JP6159408B2 - 感光性樹脂組成物、硬化膜の製造方法、硬化膜、液晶表示装置および有機el表示装置 - Google Patents
感光性樹脂組成物、硬化膜の製造方法、硬化膜、液晶表示装置および有機el表示装置 Download PDFInfo
- Publication number
- JP6159408B2 JP6159408B2 JP2015535454A JP2015535454A JP6159408B2 JP 6159408 B2 JP6159408 B2 JP 6159408B2 JP 2015535454 A JP2015535454 A JP 2015535454A JP 2015535454 A JP2015535454 A JP 2015535454A JP 6159408 B2 JP6159408 B2 JP 6159408B2
- Authority
- JP
- Japan
- Prior art keywords
- group
- resin composition
- photosensitive resin
- structural unit
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明者が検討した結果、特許文献1に記載されている化学増幅型感光性樹脂組成物は、感度に優れるが保存安定性が充分ではないことがわかった。このように、化学増幅型感光性樹脂組成物において、感度を維持しつつ、耐薬品性と保存安定性とを両立させる手段は知られていない。
<1>(A)下記(1)および(2)の少なくとも一方を満たす重合体を含む重合体成分、
(1)(a1)酸基がアセタール基で保護された基を有する構成単位、および(a2)架橋性基を有する構成単位を有する重合体、
(2)構成単位(a1)を有する重合体および構成単位(a2)を有する重合体、
(B)光酸発生剤、ならびに
(C)エーテル結合および/またはエステル結合を有し、アルコール性水酸基を有さない溶剤を含み、
全溶剤量に対するアルコール性水酸基を有する溶剤の含有量が1〜50ppmである感光性樹脂組成物。
<2>アルコール性水酸基を有する溶剤の1atmにおける沸点が、95℃以上である、<1>に記載の感光性樹脂組成物。
<3>(C)溶剤が、エーテル結合を有する溶剤である、<1>または<2>に記載の感光性樹脂組成物。
<4>(C)溶剤が、ジエチレングリコール誘導体を含む、<1>〜<3>のいずれかに記載の感光性樹脂組成物。
<5>(C)溶剤が、ジエチレングリコールエチルメチルエーテル、および/またはジエチレングリコールジメチルエーテルを含む、<1>〜<4>のいずれかに記載の感光性樹脂組成物。
<6>(C)溶剤が、エーテル結合を有する溶剤、およびエステル結合を有する溶剤を含む、<1>〜<2>、<4>〜<5>のいずれかに記載の感光性樹脂組成物。
<7>構成単位(a1)が、下記一般式(A2’)で表される構成単位である、<1>〜<6>のいずれかに記載の感光性樹脂組成物;
一般式(A2’):
<8>(a2)構成単位における架橋性基が、エポキシ基、オキセタニル基、および−NH−CH2−ORから選ばれる少なくとも1種である、<1>〜<7>のいずれかに記載の感光性樹脂組成物;但し、Rは炭素数1〜20のアルキル基を示す。
<9>(C)溶剤が、全溶剤の50質量%以上である、<1>〜<8>のいずれかに記載の感光性樹脂組成物。
<10>(B)光酸発生剤が、オキシムスルホネート化合物および/またはオニウム塩化合物である、<1>〜<9>のいずれかに記載の感光性樹脂組成物。
<11>(1)<1>〜<10>のいずれかに記載の感光性樹脂組成物を基板上に塗布する工程、
(2)塗布された感光性樹脂組成物から溶剤を除去する工程、
(3)溶剤が除去された感光性樹脂組成物を活性放射線で露光する工程、
(4)露光された感光性樹脂組成物を水性現像液で現像する工程、および、
(5)現像された感光性樹脂組成物を熱硬化するポストベーク工程、を含む、硬化膜の製造方法。
<12><1>〜<10>のいずれかに記載の感光性樹脂組成物を硬化してなる硬化膜。
<13>層間絶縁膜である、<12>に記載の硬化膜。
<14><12>または<13>に記載の硬化膜を有する、液晶表示装置または有機EL表示装置。
なお、本明細書における基(原子団)の表記において、置換及び無置換を記していない表記は、置換基を有さないものと共に置換基を有するものをも包含するものである。例えば「アルキル基」とは、置換基を有さないアルキル基(無置換アルキル基)のみならず、置換基を有するアルキル基(置換アルキル基)をも包含するものである。
本発明の組成物は、(A)下記(1)および(2)の少なくとも一方を満たす重合体を含む重合体成分、
(1)(a1)酸基がアセタール基で保護された基を有する構成単位、および(a2)架橋性基を有する構成単位を有する重合体、
(2)上記構成単位(a1)を有する重合体および上記構成単位(a2)を有する重合体、
(B)光酸発生剤、ならびに
(C)エーテル結合および/またはエステル結合を有し、アルコール性水酸基を有さない溶剤を含み、全溶剤量に対するアルコール性水酸基を有する溶剤の含有量が1〜50ppmであることを特徴とする。
全溶剤量に対するアルコール性水酸基を有する溶剤の含有量を50ppm以下とすることで、アセタール基の分解を促進して、架橋反応が促進しすぎることを効果的に抑制することができ、耐薬品性を向上させると考えられる。一方、上記含有量を1ppm以上とすることで、アセタール基の脱保護を促進させ、感度をより向上させることができると考えられる。このようにアセタール基の脱保護は、組成物の他の成分の影響を受けやすいが、このように微量なアルコール性水酸基を有する溶剤を配合することによって、保存安定性を維持することができると考えられる。さらに、アルコール性水酸基を有する溶剤の含有量を50ppm以下とすることで、いわゆる低分子の不純物の割合が減少するため、得られる硬化膜のパターン形成性が向上するというメリットもある。
以下、本発明の組成物について詳細に説明する。なお、本発明の着色感光性組成物は、化学増幅ポジ型であることが好ましい。
本発明の組成物は、重合体成分として、(a1)酸基がアセタール基で保護された基を有する構成単位、および(a2)架橋性基を有する構成単位を有する重合体(1)、上記構成単位(a1)を有する重合体および上記構成単位(a2)を有する重合体(2)、の少なくとも一方を含む。さらに、これら以外の重合体を含んでいてもよい。本発明における(A)重合体成分は、特に述べない限り、上記重合体(1)および/または上記重合体(2)に加え、必要に応じて添加される他の重合体を含めたものを意味する。
(2)(a1)酸基がアセタール基で保護された基を有する構成単位を有する重合体および(a2)架橋性基を有する構成単位を有する重合体を含む場合には、(a1)酸基がアセタール基で保護された基を有する構成単位を有する重合体と(a2)架橋性基を有する構成単位を有する重合体との割合(モル比)は、95:5〜5:95が好ましく、80:20〜20:80がより好ましく、70:30〜30:70がさらに好ましい。このような範囲とすることにより、本発明の効果がより効果的に発揮される。
(A)重合体成分は、酸基がアセタール基で保護された基を有する構成単位(a1)を少なくとも有する。(A)重合体成分が構成単位(a1)を有することにより、極めて高感度な感光性樹脂組成物とすることができる。
本発明における酸基は、公知のものを使用でき、特に限定されない。具体的な酸基としては、カルボキシル基、および、フェノール性水酸基が好ましく挙げられる。
以下、アセタール基で保護された保護カルボキシル基を有する構成単位(a1−1)、アセタール基で保護された保護フェノール性水酸基を有する構成単位(a1−2)、およびアセタール基について、順にそれぞれ説明する。
構成単位(a1−1)は、カルボキシル基を有する構成単位のカルボキシル基が、以下で詳細に説明するアセタール基によって保護された保護カルボキシル基を有する構成単位である。
上記構成単位(a1−1)に用いることができる上記カルボキシル基を有する構成単位としては、特に制限はなく公知の構成単位を用いることができる。例えば、不飽和モノカルボン酸、不飽和ジカルボン酸、不飽和トリカルボン酸などの、分子中に少なくとも1個のカルボキシル基を有する不飽和カルボン酸等に由来する構成単位(a1−1−1)が挙げられる。
以下、上記カルボキシル基を有する構成単位として用いられる、構成単位(a1−1−1)について説明する。
本発明で用いられる不飽和カルボン酸としては、以下に挙げるようなものが用いられる。
すなわち、不飽和モノカルボン酸としては、例えば、アクリル酸、メタクリル酸、クロトン酸、α−クロロアクリル酸、けい皮酸、2−(メタ)アクリロイロキシエチル-コハク酸、2−(メタ)アクリロイロキシエチルヘキサヒドロフタル酸、2−(メタ)アクリロイロキシエチル-フタル酸、などが挙げられる。
また、不飽和ジカルボン酸としては、例えば、マレイン酸、フマル酸、イタコン酸、シトラコン酸、メサコン酸などが挙げられる。
また、カルボキシル基を有する構成単位を得るために用いられる不飽和多価カルボン酸は、その酸無水物であってもよい。具体的には、無水マレイン酸、無水イタコン酸、無水シトラコン酸などが挙げられる。また、不飽和多価カルボン酸は、多価カルボン酸のモノ(2−メタクリロイロキシアルキル)エステルであってもよく、例えば、コハク酸モノ(2−アクリロイロキシエチル)、コハク酸モノ(2−メタクリロイロキシエチル)、フタル酸モノ(2−アクリロイロキシエチル)、フタル酸モノ(2−メタクリロイロキシエチル)などが挙げられる。さらに、不飽和多価カルボン酸は、その両末端ジカルボキシポリマーのモノ(メタ)アクリレートであってもよく、例えば、ω−カルボキシポリカプロラクトンモノアクリレート、ω−カルボキシポリカプロラクトンモノメタクリレートなどが挙げられる。また、不飽和カルボン酸としては、アクリル酸−2−カルボキシエチルエステル、メタクリル酸−2−カルボキシエチルエステル、マレイン酸モノアルキルエステル、フマル酸モノアルキルエステル、4−カルボキシスチレン等も用いることができる。
中でも、現像性の観点から、上記構成単位(a1−1−1)を形成するためには、アクリル酸、メタクリル酸、2−(メタ)アクリロイロキシエチル-コハク酸、2−(メタ)アクリロイロキシエチルヘキサヒドロフタル酸、2−(メタ)アクリロイロキシエチル-フタル酸、または不飽和多価カルボン酸の無水物等を用いることが好ましく、アクリル酸、メタクリル酸、2-(メタ)アクリロイロキシエチルヘキサヒドロフタル酸、を用いることがより好ましい。
構成単位(a1−1−1)は、1種単独で構成されていてもよいし、2種以上で構成されていてもよい。
R1およびR2がアルキル基の場合、炭素数は1〜10のアルキル基が好ましい。R1およびR2がアリール基の場合、フェニル基が好ましい。R1およびR2は、それぞれ、水素原子または炭素数1〜4のアルキル基が好ましい。
R3は、アルキル基またはアリール基を表し、炭素数1〜10のアルキル基が好ましく、1〜6のアルキル基がより好ましい。
Xは単結合またはアリーレン基を表し、単結合が好ましい。
一般式(1−12)
R121は水素原子またはメチル基が好ましい。
L1はカルボニル基が好ましい。
R122〜R128は、水素原子が好ましい。
構成単位(a1−2)は、フェノール性水酸基を有する構成単位が、以下で詳細に説明するアセタール基によって保護された保護フェノール性水酸基を有する構成単位(a1−2−1)である。
上記フェノール性水酸基を有する構成単位としては、ヒドロキシスチレン系構成単位やノボラック系の樹脂における構成単位が挙げられるが、これらの中では、ヒドロキシスチレン、またはα−メチルヒドロキシスチレンに由来する構成単位が、感度の観点から好ましい。またフェノール性水酸基を有する構成単位として、下記一般式(a1−20)で表される構成単位も、感度の観点から好ましい。
また、R221は単結合または二価の連結基を示す。単結合である場合には、感度を向上させることができ、さらに硬化膜の透明性を向上させることができるので好ましい。R221の二価の連結基としてはアルキレン基が例示でき、R221がアルキレン基である具体例としては、メチレン基、エチレン基、プロピレン基、イソプロピレン基、n−ブチレン基、イソブチレン基、tert−ブチレン基、ペンチレン基、イソペンチレン基、ネオペンチレン基、ヘキシレン基等が挙げられる。中でも、R221が単結合、メチレン基、エチレン基であることが好ましい。また、上記二価の連結基は、置換基を有していてもよく、置換基としては、ハロゲン原子、水酸基、アルコキシ基等が挙げられる。また、aは1〜5の整数を表すが、本発明の効果の観点や、製造が容易であるという点から、aは1または2であることが好ましく、aが1であることがより好ましい。
また、ベンゼン環における水酸基の結合位置は、R221と結合している炭素原子を基準(1位)としたとき、4位に結合していることが好ましい。
R222はハロゲン原子または炭素数1〜5の直鎖または分岐鎖状のアルキル基である。具体的には、フッ素原子、塩素原子、臭素原子、メチル基、エチル基、プロピル基、イソプロピル基、n−ブチル基、イソブチル基、tert−ブチル基、ペンチル基、イソペンチル基、ネオペンチル基等が挙げられる。中でも製造が容易であるという点から、塩素原子、臭素原子、メチル基またはエチル基であることが好ましい。
また、bは0または1〜4の整数を表す。
本発明では、酸により比較的分解し易い基としてアセタール基を用いる。本発明では、例えば、カルボキシル基がアセタールの形で保護された保護カルボキシル基、およびフェノール性水酸基がアセタールで保護された保護フェノール性水酸基であることが、感光性樹脂組成物の基本物性、特に感度やパターン形状、コンタクトホールの形成性、感光性樹脂組成物の保存安定性の観点から好ましい。さらに、カルボキシル基およびフェノール性水酸基が下記一般式(a1−10)で表されるアセタールの形で保護された保護カルボキシル基およびフェノール性水酸基であることが、感度の観点からより好ましい。なお、カルボキシル基が下記一般式(a1−10)で表されるアセタールの形で保護された保護カルボキシル基である場合、保護カルボキシル基の全体としては、−(C=O)−O−CR101R102(OR103)の構造となっている。また、フェノール性水酸基が下記一般式(a1−10)で表されるアセタールの形で保護された保護フェノール性水酸基である場合、保護フェノール性水酸基の全体としては、−Ar−O−CR101R102(OR103)の構造となっている。なお、Arはアリーレン基を表す。
フェノール性水酸基のアセタールエステル構造の好ましい例は、R101=R102=R103=メチル基やR101=R102=メチル基でR103=ベンジル基の組み合わせが例示できる。
上記直鎖状または分岐鎖状のアルキル基としては、炭素数1〜12であることが好ましく、炭素数1〜6であることがより好ましく、炭素数1〜4であることがさらに好ましい。具体的には、メチル基、エチル基、n−プロピル基、i−プロピル基、n−ブチル基、i−ブチル基、sec−ブチル基、tert−ブチル基、n−ペンチル基、ネオペンチル基、n−ヘキシル基、テキシル基(2,3−ジメチル−2−ブチル基)、n−ヘプチル基、n−オクチル基、2−エチルヘキシル基、n−ノニル基、n−デシル基等を挙げることができる。
上記直鎖状または分岐鎖状のアルキル基としては、炭素数1〜12であることが好ましく、炭素数1〜6であることがより好ましく、炭素数1〜4であることがさらに好ましい。具体的には、メチル基、エチル基、n−プロピル基、i−プロピル基、n−ブチル基、i−ブチル基、sec−ブチル基、tert−ブチル基、n−ペンチル基、ネオペンチル基、n−ヘキシル基、テキシル基(2,3−ジメチル−2−ブチル基)、n−ヘプチル基、n−オクチル基、2−エチルヘキシル基、n−ノニル基、n−デシル基等を挙げることができる。
上記環状アルキル基としては、炭素数3〜12であることが好ましく、炭素数4〜8であることがより好ましく、炭素数4〜6であることがさらに好ましい。上記環状アルキル基としては、例えばシクロプロピル基、シクロブチル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基、シクロオクチル基、ノルボルニル基、イソボルニル基等を挙げることができる。
上記ハロゲン原子としては、フッ素原子、塩素原子、臭素原子、ヨウ素原子が例示され、これらの中でもフッ素原子または塩素原子が好ましい。
また、上記アリール基としては、炭素数6〜20のアリール基が好ましく、より好ましくは炭素数6〜12であり、具体的には、フェニル基、α−メチルフェニル基、ナフチル基等が例示でき、アリール基で置換されたアルキル基全体、すなわち、アラルキル基としては、ベンジル基、α−メチルベンジル基、フェネチル基、ナフチルメチル基等が例示できる。
上記アルコキシ基としては、炭素数1〜6のアルコキシ基が好ましく、より好ましくは炭素数1〜4であり、メトキシ基またはエトキシ基がより好ましい。
また、上記アルキル基がシクロアルキル基である場合、上記シクロアルキル基は、置換基として炭素数1〜10の直鎖状または分岐鎖状のアルキル基を有していてもよく、アルキル基が直鎖状または分岐鎖状のアルキル基である場合には、置換基として炭素数3〜12のシクロアルキル基を有していてもよい。
これらの置換基は、上記置換基でさらに置換されていてもよい。
なお、上記一般式(a1−10)において、R101およびR102のいずれか一方が、水素原子またはメチル基であることが好ましい。
これらの中でも、4−ヒドロキシフェニルメタクリレートの1−アルコキシアルキル保護体、4−ヒドロキシフェニルメタクリレートのテトラヒドロピラニル保護体が透明性の観点から好ましい。
上記構成単位(a1)を含有する重合体が、実質的に、構成単位(a2)を含まない場合、構成単位(a1)の含有量は、重合体中、20〜100モル%が好ましく、30〜90モル%がより好ましい。
上記構成単位(a1)を含有する重合体が、構成単位(a2)を含有する場合、構成単位(a1)の含有量は、重合体中、感度の観点から3〜70モル%が好ましく、10〜60モル%がより好ましい。また、特に上記構成単位(a1)に用いることができる上記アセタール基が、カルボキシル基がアセタールの形で保護された保護カルボキシル基を有する構成単位である場合、20〜50モル%が好ましい。
(A)重合体成分は、架橋性基を有する構成単位(a2)を有する。本発明では、構成単位(a2)を含むため、耐薬品性に優れる。上記架橋性基は、加熱処理で硬化反応を起こす基であれば特に限定はされない。好ましい架橋性基を有する構成単位の態様としては、エポキシ基、オキセタニル基、−NH−CH2−O−R(Rは水素原子または炭素数1〜20のアルキル基)で表される基およびエチレン性不飽和基よりなる群から選ばれた少なくとも1つを含む構成単位が挙げられ、エポキシ基、オキセタニル基、および、−NH−CH2−O−R(Rは水素原子または炭素数1〜20のアルキル基)で表される基から選ばれる少なくとも1種であることが好ましい。その中でも、本発明の感光性樹脂組成物は、(A)重合体成分が、エポキシ基およびオキセタニル基のうち少なくとも1つを含む構成単位を含むことが好ましい。より詳細には、以下のものが挙げられる。
上記(A−1)重合体成分は、エポキシ基および/またはオキセタニル基を有する構成単位(以下、構成単位(a2−1)ともいう。)を含有することが好ましい。
上記構成単位(a2−1)は、1つの構成単位中にエポキシ基またはオキセタニル基を少なくとも1つ有していればよく、1つ以上のエポキシ基および1つ以上オキセタニル基、2つ以上のエポキシ基、または、2つ以上のオキセタニル基を有していてもよく、特に限定されないが、エポキシ基および/またはオキセタニル基を合計1〜3つ有することが好ましく、エポキシ基および/またはオキセタニル基を合計1または2つ有することがより好ましく、エポキシ基またはオキセタニル基を1つ有することがさらに好ましい。
オキセタニル基を有する構成単位を形成するために用いられるラジカル重合性単量体の具体例としては、例えば、特開2001−330953号公報の段落番号0011〜0016に記載のオキセタニル基を有する(メタ)アクリル酸エステルや、特開2012−088459公報の段落番号0027に記載されている化合物などが挙げられ、これらの内容は本願明細書に組み込まれる。
上記エポキシ基および/またはオキセタニル基を有する構成単位(a2−1)を形成するために用いられるラジカル重合性単量体の具体例としては、メタクリル酸エステル構造を含有するモノマー、アクリル酸エステル構造を含有するモノマーであることが好ましい。
上記架橋性基を有する構成単位(a2)の1つとして、エチレン性不飽和基を有する構成単位(a2−2)が挙げられる。上記構成単位(a2−2)としては、側鎖にエチレン性不飽和基を有する構成単位が好ましく、末端にエチレン性不飽和基を有し、炭素数3〜16の側鎖を有する構成単位がより好ましい。
その他、構成単位(a2−2)については、特開2011−215580号公報の段落番号0072〜0090の記載および特開2008−256974の段落番号0013〜0031に記載の化合物等が好ましいものとして挙げられ、これらの内容は本願明細書に組み込まれる。
本発明で用いる(A)重合体成分は、−NH−CH2−O−R(Rは水素原子または炭素数1〜20のアルキル基)で表される基を有する構成単位(a2−3)も好ましい。構成単位(a2−3)を有することで、緩やかな加熱処理で硬化反応を起こすことができ、諸特性に優れた硬化膜を得ることができる。ここで、Rは炭素数1〜9のアルキル基が好ましく、炭素数1〜4のアルキル基がより好ましい。また、アルキル基は、直鎖、分岐または環状のアルキル基のいずれであってもよいが、好ましくは、直鎖または分岐のアルキル基である。構成単位(a2−3)は、より好ましくは、下記一般式(a2−30)で表される基を有する構成単位である。
一般式(a2−30)
R2は、炭素数1〜9のアルキル基が好ましく、炭素数1〜4のアルキル基がさらに好ましい。また、アルキル基は、直鎖、分岐または環状のアルキル基のいずれであってもよいが、好ましくは、直鎖または分岐のアルキル基である。
R2の具体例としては、メチル基、エチル基、n−ブチル基、i−ブチル基、シクロヘキシル基、およびn−ヘキシル基を挙げることができる。中でもi−ブチル基、n−ブチル基、メチル基が好ましい。
耐薬品性をさらに優れたものとする観点から、構成単位(a2)のうち、エポキシ基および/またはオキセタニル基が、50質量%以上が好ましく、70質量%以上がより好ましく、80質量%以上がさらに好ましく、90質量%以上が特に好ましい。
本発明では、重合体成分に含まれる架橋性基の70モル%以上がエポキシ基であることがさらに好ましく、架橋性基の80モル%以上がエポキシ基であることがさらに好ましい。架橋性基としてエポキシ基を採用することにより、耐薬品性がより向上する傾向にある。
上記構成単位(a2)を含有する重合体が、上記構成単位(a1)を含有する場合、構成単位(a2)の含有量は、上記重合体中、薬品耐性の観点から3〜70モル%が好ましく、10〜60モル%がより好ましい。
本発明では、さらに、いずれの態様にかかわらず、(A)重合体成分の全構成単位中、構成単位(a2)の含有量が3〜70モル%であることが好ましく、10〜60モル%であることがより好ましい。
上記の数値の範囲内とすることで、諸特性に優れる硬化膜を形成できる。
本発明において、(A)重合体成分は、上記構成単位(a1)および/または構成単位(a2)に加えて、これら以外の他の構成単位(a3)として、少なくとも酸基を有する構成単位を有することが好ましい。構成単位(a3)は、上記重合体(1)および/または(2)が含んでいてもよい。また、上記重合体(1)または(2)とは別に、実質的に構成単位(a1)および構成単位(a2)を含まずに他の構成単位(a3)を有する重合体を有していてもよい。
本発明で用いられる酸基としては、カルボン酸基由来のもの、スルホンアミド基に由来のもの、ホスホン酸基に由来のもの、スルホン酸基に由来のもの、フェノール性水酸基に由来するもの、スルホンアミド基、スルホニルイミド基等が例示され、カルボン酸基由来のものおよび/またはフェノール性水酸基に由来のものが好ましい。
本発明で用いられる酸基を含む構成単位は、スチレンに由来する構成単位や、ビニル化合物に由来する構成単位、(メタ)アクリル酸および/またはそのエステルに由来する構成単位であることがより好ましい。例えば、特開2012−88459号公報の段落番号0021〜0023および段落番号0029〜0044記載の化合物を用いることができ、この内容は本願明細書に組み込まれる。なかでも、p−ヒドロキシスチレン、(メタ)アクリル酸、マレイン酸、無水マレイン酸に由来する構成単位が好ましい。
このような重合体としては、側鎖にカルボキシル基を有する樹脂が好ましい。例えば、特開昭59−44615号、特公昭54−34327号、特公昭58−12577号、特公昭54−25957号、特開昭59−53836号、特開昭59−71048号の各公報に記載されているような、メタクリル酸共重合体、アクリル酸共重合体、イタコン酸共重合体、クロトン酸共重合体、マレイン酸共重合体、部分エステル化マレイン酸共重合体等、並びに側鎖にカルボキシル基を有する酸性セルロース誘導体、水酸基を有するポリマーに酸無水物を付加させたもの等が挙げられ、さらに側鎖に(メタ)アクリロイル基を有する高分子重合体も好ましいものとして挙げられる。
その他にも、特開平7−207211号公報、特開平8−259876号公報、特開平10−300922号公報、特開平11−140144号公報、特開平11−174224号公報、特開2000−56118号公報、特開2003−233179号公報、特開2009−52020号公報等に記載の公知の高分子化合物を使用することができ、これらの内容は本願明細書に組み込まれる。
これらの重合体は、1種類のみ含んでいてもよいし、2種類以上含んでいてもよい。
また、重合体成分は、その他の構成単位(a3)として、オキサゾリン基を有する構成単位をさらに有していてもよい。
(第1の実施形態)
重合体(1)が、さらに、1種または2種以上のその他の構成単位(a3)を有する態様。
(第2の実施形態)
重合体(2)における、(a1)酸基がアセタール基で保護された基を有する構成単位を有する重合体が、さらに、1種または2種以上のその他の構成単位(a3)を有する態様。
(第3の実施形態)
重合体(2)における、(a2)架橋性基を有する構成単位を有する重合体が、さらに、1種または2種以上のその他の構成単位(a3)を有する態様。
(第4の実施形態)
上記重合体(1)または(2)とは別に、さらに、実質的に構成単位(a1)および構成単位(a2)を含まずに他の構成単位(a3)を有する重合体を有する態様。
(第5の実施形態)
上記第1〜第4の実施形態の2以上の組み合わせからなる形態。
本発明の組成物は、固形分の70質量%以上が(A)重合体成分であることが好ましい。
(A)重合体の分子量は、ポリスチレン換算重量平均分子量で、好ましくは1,000〜200,000、より好ましくは2,000〜50,000の範囲である。上記の数値の範囲内であると、諸特性が良好である。数平均分子量と重量平均分子量の比(分散度)は1.0〜5.0が好ましく1.5〜3.5がより好ましい。
また、(A)重合体成分の合成法についても、様々な方法が知られているが、一例を挙げると、少なくとも上記(a1)および上記(a3)で表される構成単位を形成するために用いられるラジカル重合性単量体を含むラジカル重合性単量体混合物を有機溶剤中、ラジカル重合開始剤を用いて重合することにより合成することができる。また、いわゆる高分子反応で合成することもできる。
(A)重合体は、(メタ)アクリル酸および/またはそのエステルに由来する構成単位を、全構成単位に対し、50モル%以上含有することが好ましく、80モル%以上含有することがより好ましい。
本発明の感光性樹脂組成物は、(B)光酸発生剤を含有する。本発明で使用される光酸発生剤としては、波長300nm以上、好ましくは波長300〜450nmの活性光線に感応し、酸を発生する化合物が好ましいが、その化学構造に制限されるものではない。また、波長300nm以上の活性光線に直接感応しない光酸発生剤についても、増感剤と併用することによって波長300nm以上の活性光線に感応し、酸を発生する化合物であれば、増感剤と組み合わせて好ましく用いることができる。本発明で使用される光酸発生剤としては、pKaが4以下の酸を発生する光酸発生剤が好ましく、pKaが3以下の酸を発生する光酸発生剤がより好ましく、2以下の酸を発生する光酸発生剤が最も好ましい。
一般式(B1−1)
R21のアルキル基としては、炭素数1〜10の、直鎖状または分岐状アルキル基が好ましい。R21のアルキル基は、ハロゲン原子、炭素数6〜11のアリール基、炭素数1〜10のアルコキシ基、または、シクロアルキル基(7,7−ジメチル−2−オキソノルボルニル基などの有橋式脂環基を含む、好ましくはビシクロアルキル基等)で置換されてもよい。
R21のアリール基としては、炭素数6〜11のアリール基が好ましく、フェニル基またはナフチル基がより好ましい。R21のアリール基は、低級アルキル基、アルコキシ基あるいはハロゲン原子で置換されてもよい。
一般式(B1−2)
Xとしてのアルキル基は、炭素数1〜4の直鎖状または分岐状アルキル基が好ましい。また、Xとしてのアルコキシ基は、炭素数1〜4の直鎖状または分岐状アルコキシ基が好ましい。また、Xとしてのハロゲン原子は、塩素原子またはフッ素原子が好ましい。
m4は、0または1が好ましい。上記一般式(B2)中、m4が1であり、Xがメチル基であり、Xの置換位置がオルト位であり、R42が炭素数1〜10の直鎖状アルキル基、7,7−ジメチル−2−オキソノルボルニルメチル基、またはp−トルイル基である化合物が特に好ましい。
一般式(B1−3)
X1としては、炭素数1〜5のアルコキシ基が好ましく、メトキシ基がより好ましい。
n4としては、0〜2が好ましく、0〜1が特に好ましい。
上記一般式(B1−3)で表される化合物の具体例および好ましいオキシムスルホネート化合物の具体例としては、特開2012−163937号公報の段落番号0080〜0082の記載を参酌でき、この内容は本願明細書に組み込まれる。
X101は−O−、−S−、−NH−、−NR105−、−CH2−、−CR106H−、または、−CR105R107−を表し、R105〜R107はアルキル基、または、アリール基を表す。
R121〜R124は、それぞれ独立に、水素原子、ハロゲン原子、アルキル基、アルケニル基、アルコキシ基、アミノ基、アルコキシカルボニル基、アルキルカルボニル基、アリールカルボニル基、アミド基、スルホ基、シアノ基、または、アリール基を表す。R121〜R124のうち2つは、それぞれ互いに結合して環を形成してもよい。
R121〜R124としては、水素原子、ハロゲン原子、および、アルキル基が好ましく、また、R121〜R124のうち少なくとも2つが互いに結合してアリール基を形成する態様もまた、好ましく挙げられる。中でも、R121〜R124がいずれも水素原子である態様が感度の観点から好ましい。
既述の官能基は、いずれも、さらに置換基を有していてもよい。
上記一般式(OS−1)で表される化合物は、例えば、特開2012−163937号公報の段落番号0087〜0089に記載されている一般式(OS−2)で表される化合物であることが好ましく、この内容は本願明細書に組み込まれる。
本発明では、上記一般式(B1−1)で表されるオキシムスルホネート構造を含有する化合物としては、下記一般式(OS−3)、下記一般式(OS−4)または下記一般式(OS−5)で表されるオキシムスルホネート化合物であることが好ましい。
上記一般式(OS−3)〜(OS−5)については、例えば、特開2012−163937号公報の段落番号0098〜0115の記載を参酌でき、この内容は本願明細書に組み込まれる。
上記一般式(OS−6)〜(OS−11)における好ましい範囲は、特開2011−221494号公報の段落番号0110〜0112に記載される(OS−6)〜(OS−11)の好ましい範囲と同様であり、この内容は本願明細書に組み込まれる。
上記一般式(OS−3)〜上記一般式(OS−5)で表されるオキシムスルホネート化合物の具体例としては、特開2011−221494号公報の段落番号0114〜0120に記載の化合物が挙げられ、この内容は本願明細書に組み込まれる。本発明は、これらに限定されるものではない。
一般式(B1−4)
アルキル基の炭素数は、好ましくは3〜10である。特にアルキル基が分岐構造を有する場合、炭素数3〜6のアルキル基が好ましく、環状構造を有する場合、炭素数5〜7のアルキル基が好ましい。
アルキル基としては、例えば、プロピル基、イソプロピル基、n−ブチル基、s−ブチル基、イソブチル基、tert−ブチル基、ペンチル基、イソペンチル基、ネオペンチル基、1,1−ジメチルプロピル基、ヘキシル基、2−エチルヘキシル基、シクロヘキシル基、オクチル基などが挙げられ、好ましくは、イソプロピル基、tert−ブチル基、ネオペンチル基、シクロヘキシル基である。
アリール基の炭素数は、好ましくは6〜12であり、より好ましくは6〜8であり、さらに好ましくは6〜7である。上記アリール基としては、フェニル基、ナフチル基などが挙げられ、好ましくは、フェニル基である。
R1が表すアルキル基およびアリール基は、置換基を有していてもよい。置換基としては、例えばハロゲン原子(フッ素原子、クロロ原子、臭素原子、ヨウ素原子)、直鎖、分岐または環状のアルキル基(例えばメチル基、エチル基、プロピル基など)、アルケニル基、アルキニル基、アリール基、アシル基、アルコキシカルボニル基、アリールオキシカルボニル基、カルバモイル基、シアノ基、カルボキシル基、水酸基、アルコキシ基、アリールオキシ基、アルキルチオ基、アリールチオ基、ヘテロ環オキシ基、アシルオキシ基、アミノ基、ニトロ基、ヒドラジノ基、ヘテロ環基などが挙げられる。また、これらの基によってさらに置換されていてもよい。好ましくは、ハロゲン原子、メチル基である。
かさ高い置換基の中でも、イソプロピル基、tert−ブチル基、ネオペンチル基、シクロヘキシル基が好ましく、tert−ブチル基、シクロヘキシル基がより好ましい。
アリール基としては、炭素数6〜10のアリール基が好ましい。上記アリール基としては、フェニル基、ナフチル基、p−トルイル基(p−メチルフェニル基)などが挙げられ、好ましくは、フェニル基、p−トルイル基である。
ヘテロアリール基としては、例えば、ピロール基、インドール基、カルバゾール基、フラン基、チオフェン基などが挙げられる。
R2が表すアルキル基、アリール基、およびヘテロアリール基は、置換基を有していてもよい。置換基としては、R1が表すアルキル基およびアリール基が有していてもよい置換基と同義である。
R2は、アルキル基またはアリール基が好ましく、アリール基がより好ましく、フェニル基がより好ましい。フェニル基の置換基としてはメチル基が好ましい。
R3〜R6のうち、R3とR4、R4とR5、またはR5とR6が結合して環を形成してもよく、環としては、脂環または芳香環を形成していることが好ましく、ベンゼン環がより好ましい。
R3〜R6は、水素原子、アルキル基、ハロゲン原子(フッ素原子、クロロ原子、臭素原子)、または、R3とR4、R4とR5、またはR5とR6が結合してベンゼン環を構成していることが好ましく、水素原子、メチル基、フッ素原子、クロロ原子、臭素原子またはR3とR4、R4とR5、またはR5とR6が結合してベンゼン環を構成していることがより好ましい。
R3〜R6の好ましい態様は以下の通りである。
(態様1)少なくとも2つは水素原子である。
(態様2)アルキル基、アリール基、またはハロゲン原子の数は、1つ以下である。
(態様3)R3とR4、R4とR5、またはR5とR6が結合してベンゼン環を構成している。
(態様4)上記態様1と2を満たす態様、および/または、上記態様1と3を満たす態様。
Xは、−O−またはS−を表す。
本発明の組成物は、(C)エーテル結合および/またはエステル結合を有し、アルコール性水酸基を有さない溶剤((C)溶剤)を含む。
エーテル結合を有する溶剤とは、分子中に1以上のエーテル結合を有する溶剤のことをいい、エステル結合を有する溶剤とは、分子中に1以上のエステル結合を有する溶剤のことをいう。エステル結合を有する溶剤には、分子内にエステル結合およびエーテル結合の両方を含む溶剤も含む趣旨である。
具体例として、プロピレングリコールモノメチルエーテルアセテート、3−エトキシプロピオン酸エチル、ジプロピレングリコールメチルエーテルアセテート、3−メトキシブチルエーテルアセテート、ジエチレングリコールモノエチルエーテルアセテート、1,3−ブチレングリコールジアセテート、エチレングリコールモノメチルエーテルアセテート、プロピレングリコールモノメチルエーテルプロピオネート、プロピレングリコールジアセテート、γーブチロラクトン等が例示できる。
具体例として、プロピレングリコールメチル−n−ブチルエーテル、プロピレングリコールメチル−n−プロピルエーテル、ジエチレングリコールメチルエチルエーテル、ジエチレングリコールジメチルエーテル、ジエチレングリコールジエチエルエーテル、ジプロピレングリコールジメチルエーテル、ジプロピレングリコールジメチルエーテル、ジエチレングリコールイソプロピルメチルエーテル、トリプロピレングリコールジメチルエーテル、トリエチレングリコールジメチルエーテル等が例示できる。
感度向上の観点から、(C)溶剤は全溶剤中、50質量%以上が好ましく、70質量%以上がより好ましく、90質量%以上が特に好ましい。(C)溶剤は1種類のみ含んでいても良いし、2種類以上含んでいても良い。2種類以上含む場合は、合計量が上記範囲となることが好ましい。
本発明の組成物は、アルコール性水酸基を有する溶剤を、全溶剤量に対し、1〜50ppmの割合で含む。アルコール性水酸基を有する溶剤の全溶剤量に対する含有量は、1〜30ppmであることが好ましく、1〜10ppmであることがより好ましい。
アルコール性水酸基を有する溶剤の含有量を1ppm以上とすることでアセタールの脱保護を促進させ、感度をより向上させることができる。アルコール性水酸基を有する溶剤の含有量を50ppm以下とすることで、アセタールの分解を抑制し、架橋反応が促進してしまうことを効果的に抑制することができる。すなわち、アルコール性水酸基を有する溶剤の含有量が50ppmを超えると、(a1)酸基がアセタール基で保護された基が不必要な段階で脱保護され、感光性樹脂組成物の粘度が増加し、安定的に製造することが困難になる。また、不必要な段階で脱保護されることにより、(a2)架橋性基が不必要な段階で架橋し、感光性樹脂組成物を硬化してなる硬化膜の耐薬品性がやや劣る傾向となる。
アルコール性水酸基を有する溶剤の1atmにおける沸点の上限は、300℃以下であることが好ましく、180℃以下であることがより好ましい。アルコール性水酸基を有する溶剤の1atmにおける沸点が300℃以下であると、ポストベークなどの処理において架橋反応後に溶剤が硬化膜から揮発されることにより、硬化膜の膜物性が良好に保たれるため好ましい
アルコール性水酸基を有する溶剤の分子量は40〜400であることが好ましく、50〜300であることがより好ましい。この範囲で、本発明の効果がより効果的に発揮されるため、好ましい。
本発明の感光性樹脂組成物には、上記成分に加えて、必要に応じて、増感剤、アルコキシシラン化合物、塩基性化合物、界面活性剤、酸化防止剤を好ましく加えることができる。さらに本発明の感光性樹脂組成物には、酸増殖剤、現像促進剤、可塑剤、熱ラジカル発生剤、熱酸発生剤、紫外線吸収剤、増粘剤、および、有機または無機の沈殿防止剤などの公知の添加剤を加えることができる。また、これらの化合物としては、例えば特開2012−88459号公報の段落番号0201〜0224の記載の化合物を使用することができ、これらの内容は本願明細書に組み込まれる。これらの成分は、それぞれ、1種類のみでもよいし、2種類以上であってもよい。
本発明の感光性樹脂組成物は、光酸発生剤との組み合わせにおいて、その分解を促進させるために、増感剤を含有することが好ましい。増感剤は、活性光線を吸収して電子励起状態となる。電子励起状態となった増感剤は、光酸発生剤と接触して、電子移動、エネルギー移動、発熱などの作用が生じる。これにより光酸発生剤は化学変化を起こして分解し、酸を生成する。好ましい増感剤の例としては、以下の化合物類に属しており、かつ350nmから450nmの波長域のいずれかに吸収波長を有する化合物を挙げることができる。
これら増感剤の中でも、多核芳香族類、アクリドン類、スチリル類、ベーススチリル類、クマリン類が好ましく、多核芳香族類がより好ましい。多核芳香族類の中でもアントラセン誘導体が最も好ましい。
本発明の感光性樹脂組成物は、必要に応じ、架橋剤を含有してもよい。架橋剤を添加することにより、本発明の感光性樹脂組成物により得られる硬化膜をより強固な膜とすることができる。
架橋剤としては、熱によって架橋反応が起こるものであれば制限は無い。例えば、以下に述べる分子内に2個以上のエポキシ基またはオキセタニル基を有する化合物、アルコキシメチル基含有架橋剤、または、少なくとも1個のエチレン性不飽和二重結合を有する化合物、ブロックイソシアネート化合物等を添加することができる。
本発明の組成物に用いることができる架橋剤の市販品としては、例えばKAYARAD DPHA(日本化薬株式会社製)などが挙げられる。
本発明の組成物が架橋剤を有する場合、架橋剤の含有量は、感光性組成物中の全固形分100質量部に対して、0.01〜50質量部であることが好ましく、0.1〜30質量部であることがより好ましく、0.5〜20質量部であることがさらに好ましい。この範囲で添加することにより、機械的強度および耐溶剤性に優れた硬化膜が得られる。架橋剤は複数を併用することもでき、その場合は架橋剤を全て合算して含有量を計算する。
分子内に2個以上のエポキシ基を有する化合物の具体例としては、ビスフェノールA型エポキシ樹脂、ビスフェノールF型エポキシ樹脂、フェノールノボラック型エポキシ樹脂、クレゾールノボラック型エポキシ樹脂、脂肪族エポキシ樹脂等を挙げることができる。
これらの中でも、ビスフェノールA型エポキシ樹脂、ビスフェノールF型エポキシ樹脂、フェノールノボラック型エポキシ樹脂および脂肪族エポキシ樹脂がより好ましく挙げられ、ビスフェノールA型エポキシ樹脂が特に好ましく挙げられる。
分子内に2個以上のオキセタニル基を有する化合物の具体例としては、アロンオキセタンOXT−121、OXT−221、OX−SQ、PNOX(以上、東亞合成(株)製)を用いることができる。
また、オキセタニル基を含む化合物は、単独でまたはエポキシ基を含む化合物と混合して使用することが好ましい。
本発明の感光性樹脂組成物では、架橋剤として、ブロックイソシアネート系化合物も好ましく採用できる。ブロックイソシアネート化合物は、特に制限はないが、硬化性の観点から、1分子内に2以上のブロックイソシアネート基を有する化合物であることが好ましい。
なお、本発明におけるブロックイソシアネート基とは、熱によりイソシアネート基を生成することが可能な基であり、例えば、ブロック剤とイソシアネート基とを反応させイソシアネート基を保護した基が好ましく例示できる。また、上記ブロックイソシアネート基は、90℃〜250℃の熱によりイソシアネート基を生成することが可能な基であることが好ましい。
また、ブロックイソシアネート化合物としては、その骨格は特に限定されるものではなく、1分子中にイソシアネート基を2個有するものであればどのようなものでもよく、脂肪族、脂環族または芳香族のポリイソシアネートであってよいが、例えば2,4−トリレンジイソシアネート、2,6−トリレンジイソシアネート、イソホロンジイソシアネート、1,6−ヘキサメチレンジイソシアネート、1,3−トリメチレンジイソシアネート、1,4−テトラメチレンジイソシアネート、2,2,4−トリメチルヘキサメチレンジイソシアネート、2,4,4−トリメチルヘキサメチレンジイソシアネート、1,9−ノナメチレンジイソシアネート、1,10−デカメチレンジイソシアネート、1,4−シクロヘキサンジイソシアネート、2,2'−ジエチルエーテルジイソシアネート、ジフェニルメタン−4,4'−ジイソシアネート、o−キシレンジイソシアネート、m−キシレンジイソシアネート、p−キシレンジイソシアネート、メチレンビス(シクロヘキシルイソシアネート)、シクロヘキサン−1,3−ジメチレンジイソシアネート、シクロヘキサン−1,4−ジメチレレンジイソシアネート、1,5−ナフタレンジイソシアネート、p−フェニレンジイソシアネート、3,3'−メチレンジトリレン−4,4'−ジイソシアネート、4,4'−ジフェニルエーテルジイソシアネート、テトラクロロフェニレンジイソシアネート、ノルボルナンジイソシアネート、水素化1,3−キシリレンジイソシアネート、水素化1,4−キシリレンジイソシアネート等のイソシアネート化合物およびこれらの化合物から派生するプレポリマー型の骨格の化合物を好適に用いることができる。これらの中でも、トリレンジイソシアネート(TDI)やジフェニルメタンジイソシアネート(MDI)、ヘキサメチレンジイソシアネート(HDI)、イソホロンジイソシアネート(IPDI)が特に好ましい。
本発明の感光性樹脂組成物におけるブロックイソシアネート化合物の母構造としては、ビウレット型、イソシアヌレート型、アダクト型、2官能プレポリマー型等を挙げることができる。
上記ブロックイソシアネート化合物のブロック構造を形成するブロック剤としては、オキシム化合物、ラクタム化合物、フェノール化合物、アルコール化合物、アミン化合物、活性メチレン化合物、ピラゾール化合物、メルカプタン化合物、イミダゾール系化合物、イミド系化合物等を挙げることができる。これらの中でも、オキシム化合物、ラクタム化合物、フェノール化合物、アルコール化合物、アミン化合物、活性メチレン化合物、ピラゾール化合物から選ばれるブロック剤が特に好ましい。
上記ラクタム化合物としてはε−カプロラクタム、γ−ブチロラクタム等が例示できる。
上記フェノール化合物としては、フェノール、ナフトール、クレゾール、キシレノール、ハロゲン置換フェノール等が例示できる。
上記アルコール化合物としては、メタノール、エタノール、プロパノール、ブタノール、シクロヘキサノール、エチレングリコールモノアルキルエーテル、プロピレングリコールモノアルキルエーテル、乳酸アルキル等が例示できる。
上記アミン化合物としては、1級アミンおよび2級アミンが上げられ、芳香族アミン、脂肪族アミン、脂環族アミンいずれでもよく、アニリン、ジフェニルアミン、エチレンイミン、ポリエチレンイミン等が例示できる。
上記活性メチレン化合物としては、マロン酸ジエチル、マロン酸ジメチル、アセト酢酸エチル、アセト酢酸メチル等が例示できる。
上記ピラゾール化合物としては、ピラゾール、メチルピラゾール、ジメチルピラゾール等が例示できる。
上記メルカプタン化合物としては、アルキルメルカプタン、アリールメルカプタン等が例示できる。
本発明の感光性樹脂組成物は、密着改良剤としてアルコキシシラン化合物を含有してもよい。アルコキシシラン化合物を用いると、本発明の感光性樹脂組成物により形成された膜と基板との密着性を向上できたり、本発明の感光性樹脂組成物により形成された膜の性質を調整することができる。本発明の感光性樹脂組成物に用いることができるアルコキシシラン化合物は、基材となる無機物、例えば、シリコン、酸化シリコン、窒化シリコン等のシリコン化合物、金、銅、モリブデン、チタン、アルミニウム等の金属と絶縁膜との密着性を向上させる化合物であることが好ましい。具体的には、公知のシランカップリング剤等も有効である。
シランカップリング剤としては、例えば、γ−アミノプロピルトリメトキシシラン、γ−アミノプロピルトリエトキシシラン、γ−グリシドキシプロピルトリアルコキシシラン、γ−グリシドキシプロピルトリメトキシシラン、γ−グリシドキシプロピルジアルコキシシラン、γ−メタクリロキシプロピルトリアルコキシシラン、γ−メタクリロキシプロピルジアルコキシシラン、γ−クロロプロピルトリアルコキシシラン、γ−メルカプトプロピルトリアルコキシシラン、β−(3,4−エポキシシクロヘキシル)エチルトリアルコキシシラン、ビニルトリアルコキシシランが挙げられる。これらのうち、γ−グリシドキシプロピルトリアルコキシシランやγ−メタクリロキシプロピルトリアルコキシシランがより好ましく、γ−グリシドキシプロピルトリアルコキシシランがさらに好ましく、3−グリシドキシプロピルトリメトキシシランがよりさらに好ましい。これらは1種単独または2種以上を組み合わせて使用することができる。市販品としては、KBM−403、信越シリコーン社製等が例示される。
本発明の組成物がアルコキシシラン化合物を有する場合、アルコキシシラン化合物の含有量は、感光性樹脂組成物中の全固形分100質量部に対して、0.1〜30質量部が好ましく、0.5〜20質量部がより好ましい。
本発明の感光性樹脂組成物は、塩基性化合物を含有してもよい。塩基性化合物としては、化学増幅レジストで用いられるものの中から任意に選択して使用することができる。例えば、脂肪族アミン、芳香族アミン、複素環式アミン、第四級アンモニウムヒドロキシド、カルボン酸の第四級アンモニウム塩等が挙げられる。これらの具体例としては、特開2011−221494号公報の段落番号0204〜0207に記載の化合物が挙げられ、これらの内容は本願明細書に組み込まれる。
芳香族アミンとしては、例えば、アニリン、ベンジルアミン、N,N−ジメチルアニリン、ジフェニルアミンなどが挙げられる。
複素環式アミンとしては、例えば、ピリジン、2−メチルピリジン、4−メチルピリジン、2−エチルピリジン、4−エチルピリジン、2−フェニルピリジン、4−フェニルピリジン、N−メチル−4−フェニルピリジン、4−ジメチルアミノピリジン、イミダゾール、ベンズイミダゾール、4−メチルイミダゾール、2−フェニルベンズイミダゾール、2,4,5−トリフェニルイミダゾール、ニコチン、ニコチン酸、ニコチン酸アミド、キノリン、8−オキシキノリン、ピラジン、ピラゾール、ピリダジン、プリン、ピロリジン、ピペリジン、ピペラジン、モルホリン、4−メチルモルホリン、N−シクロヘキシル−N’−[2−(4−モルホリニル)エチル]チオ尿素、1,5−ジアザビシクロ[4.3.0]−5−ノネン、1,8−ジアザビシクロ[5.3.0]−7−ウンデセン、1,8−ジアザビシクロ[5.4.0]−7−ウンデセンなどが挙げられる。
第四級アンモニウムヒドロキシドとしては、例えば、テトラメチルアンモニウムヒドロキシド、テトラエチルアンモニウムヒドロキシド、テトラプロピルアンモニウムヒドロキシド、ベンジルトリメチルアンモニウムヒドロキシド、テトラ−n−ブチルアンモニウムヒドロキシド、テトラ−n−ヘキシルアンモニウムヒドロキシドなどが挙げられる。
カルボン酸の第四級アンモニウム塩としては、例えば、テトラメチルアンモニウムアセテート、テトラメチルアンモニウムベンゾエート、テトラ−n−ブチルアンモニウムアセテート、テトラ−n−ブチルアンモニウムベンゾエートなどが挙げられる。
本発明に用いることができる塩基性化合物は、1種単独で使用しても、2種以上を併用してもよい。
本発明の感光性樹脂組成物は、界面活性剤を含有してもよい。界面活性剤としては、アニオン系、カチオン系、ノニオン系、または、両性のいずれでも使用することができるが、好ましい界面活性剤はノニオン界面活性剤である。本発明の組成物に用いられる界面活性剤としては、例えば、特開2012−88459号公報の段落番号0201〜0205に記載のものや、特開2011−215580号公報の段落番号0185〜0188に記載のものを用いることができ、これらの記載は本願明細書に組み込まれる。
ノニオン系界面活性剤の例としては、ポリオキシエチレン高級アルキルエーテル類、ポリオキシエチレン高級アルキルフェニルエーテル類、ポリオキシエチレングリコールの高級脂肪酸ジエステル類、シリコーン系、フッ素系界面活性剤を挙げることができる。また、以下商品名で、KP−341、X−22−822(信越化学工業(株)製)、ポリフローNo.99C(共栄社化学(株)製)、エフトップ(三菱マテリアル化成社製)、メガファック(DIC(株)製)、フロラードノベックFC−4430(住友スリーエム(株)製)、サーフロンS−242(AGCセイミケミカル社製)、PolyFoxPF−6320(OMNOVA社製)、SH 8400 FLUID、SH−8400(東レ・ダウコーニングシリコーン)、フタージェントFTX−218、フタージェントFTX−218G(ネオス社製)、F−554(DIC社製)等を挙げることができる。
また、界面活性剤として、下記一般式(I−1−1)で表される構成単位Aおよび構成単位Bを含み、テトラヒドロフラン(THF)を溶媒とした場合のゲルパーミエーションクロマトグラフィーで測定されるポリスチレン換算の重量平均分子量(Mw)が1,000以上10,000以下である共重合体を好ましい例として挙げることができる。
これらの界面活性剤は、1種単独でまたは2種以上を混合して使用することができる。
本発明の組成物が界面活性剤を有する場合、界面活性剤の添加量は、感光性樹脂組成物中の全固形成分100質量部に対し、10質量部以下であることが好ましく、0.001〜10質量部であることがより好ましく、0.01〜3質量部であることがさらに好ましい。
<<酸化防止剤>>
本発明の感光性樹脂組成物は、酸化防止剤を含有してもよい。酸化防止剤としては、公知の酸化防止剤を含有することができる。酸化防止剤を添加することにより、硬化膜の着色を防止できる、または、分解による膜厚減少を低減でき、また、耐熱透明性に優れるという利点がある。
このような酸化防止剤としては、例えば、リン系酸化防止剤、アミド類、ヒドラジド類、ヒンダードアミン系酸化防止剤、イオウ系酸化防止剤、フェノール系酸化防止剤、アスコルビン酸類、硫酸亜鉛、糖類、亜硝酸塩、亜硫酸塩、チオ硫酸塩、ヒドロキシルアミン誘導体などを挙げることができる。これらの中では、硬化膜の着色、膜厚減少の観点から特にフェノール系酸化防止剤、ヒンダードアミン系酸化防止剤、リン系酸化防止剤、アミド系酸化防止剤、ヒドラジド系酸化防止剤、イオウ系酸化防止剤が好ましく、フェノール系酸化防止剤が最も好ましい。これらは1種単独で用いてもよいし、2種以上を混合してもよい。
具体例としては、特開2005−29515号公報の段落番号0026〜0031に記載の化合物、特開2011-227106号公報の段落番号0106〜0116に記載の化合物を挙げる事ができ、これらの内容は本願明細書に組み込まれる。
好ましい市販品として、アデカスタブAO−60、アデカスタブAO−20、アデカスタブAO−80、アデカスタブLA−52、アデカスタブLA−81、アデカスタブAO−412S、アデカスタブPEP−36、イルガノックス1035、イルガノックス1098、チヌビン144を挙げる事ができる。
本発明の感光性樹脂組成物は、感度向上を目的に、酸増殖剤を用いることができる。
本発明に用いることができる酸増殖剤は、酸触媒反応によってさらに酸を発生して反応系内の酸濃度を上昇させることができる化合物であり、酸が存在しない状態では安定に存在する化合物である。
このような酸増殖剤の具体例としては、特開2011−221494号公報の段落番号0226〜0228に記載の酸増殖剤が挙げられ、この内容は本願明細書に組み込まれる。
本発明の感光性樹脂組成物は、現像促進剤を含有することができる。
現像促進剤としては、特開2012−042837号公報の段落番号0171〜0172に記載されているものを参酌でき、この内容は本願明細書に組み込まれる。
現像促進剤は、1種を単独で用いてもよいし、2種以上を併用することも可能である。
本発明の感光性樹脂組成物における現像促進剤の添加量は、感度と残膜率の観点から、感光性組成物の全固形分100質量部に対し、0〜30質量部が好ましく、0.1〜20質量部がより好ましく、0.5〜10質量部であることが最も好ましい。
また、その他の添加剤としては特開2012−8223号公報の段落番号0120〜0121に記載の熱ラジカル発生剤、WO2011/136074A1に記載の窒素含有化合物および熱酸発生剤も用いることができ、これらの内容は本願明細書に組み込まれる。
各成分を所定の割合でかつ任意の方法で混合し、撹拌溶解して感光性樹脂組成物を調製する。例えば、成分を、それぞれ予め溶剤に溶解させた溶液とした後、これらを所定の割合で混合して樹脂組成物を調製することもできる。以上のように調製した組成物溶液は、例えば孔径0.2μmのフィルター等を用いてろ過した後に、使用することもできる。
本発明の硬化膜の製造方法は、以下の(1)〜(5)の工程を含むことが好ましい。
(1)本発明の感光性樹脂組成物を基板上に塗布する工程;
(2)塗布された感光性樹脂組成物から溶剤を除去する工程;
(3)溶剤が除去された感光性樹脂組成物を活性光線により露光する工程;
(4)露光された感光性樹脂組成物を水性現像液により現像する工程;
(5)現像された感光性樹脂組成物を熱硬化するポストベーク工程。
以下に各工程を順に説明する。
上記の基板としては、無機基板、樹脂、樹脂複合材料などが挙げられる。
無機基板としては、例えばガラス、石英、シリコーン、シリコンナイトライド、および、それらのような基板上にモリブデン、チタン、アルミ、銅などを蒸着した複合基板が挙げられる。
樹脂としては、ポリブチレンテレフタレート、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリブチレンナフタレート、ポリスチレン、ポリカーボネート、ポリスルホン、ポリエーテルスルホン、ポリアリレート、アリルジグリコールカーボネート、ポリアミド、ポリイミド、ポリアミドイミド、ポリエーテルイミド、ポリベンズアゾール、ポリフェニレンサルファイド、ポリシクロオレフィン、ノルボルネン樹脂、ポリクロロトリフルオロエチレン等のフッ素樹脂、液晶ポリマー、アクリル樹脂、エポキシ樹脂、シリコーン樹脂、アイオノマー樹脂、シアネート樹脂、架橋フマル酸ジエステル、環状ポリオレフィン、芳香族エーテル、マレイミドーオレフィン、セルロース、エピスルフィド化合物等の合成樹脂からなる基板が挙げられる。
これらの基板は、上記の形態のまま用いられる場合は少なく、通常、最終製品の形態によって、例えばTFT素子のような多層積層構造が形成されている。
基板への塗布方法は特に限定されず、例えば、スリットコート法、スプレー法、ロールコート法、回転塗布法、流延塗布法、スリットアンドスピン法等の方法を用いることができる。
塗布したときの湿潤膜厚は特に限定されるものではなく、用途に応じた膜厚で塗布することができるが、通常は0.5〜10μmの範囲で使用される。
さらに、基板に本発明で用いられる組成物を塗布する前に、特開2009−145395号公報に記載されているような、所謂プリウェット法を適用することも可能である。
活性光線による露光光源としては、低圧水銀灯、高圧水銀灯、超高圧水銀灯、ケミカルランプ、LED光源、エキシマレーザー発生装置などを用いることができ、i線(365nm)、h線(405nm)、g線(436nm)などの波長300nm以上450nm以下の波長を有する活性光線が好ましく使用できる。また、必要に応じて長波長カットフィルター、短波長カットフィルター、バンドパスフィルターのような分光フィルターを通して照射光を調整することもできる。露光量は好ましくは1〜500mJ/cm2である。
露光装置としては、ミラープロジェクションアライナー、ステッパー、スキャナー、プロキシミティ、コンタクト、マイクロレンズアレイ、レンズスキャナ、レーザー露光、など各種方式の露光機を用いることができる。
酸触媒の生成した領域において、上記の加水分解反応を加速させるために、露光後加熱処理:Post Exposure Bake(以下、「PEB」ともいう。)を行うことができる。PEBにより、アセタール基からのカルボキシル基またはフェノール性水酸基の生成を促進させることができる。PEBを行う場合の温度は、30℃以上130℃以下であることが好ましく、40℃以上110℃以下がより好ましく、50℃以上100℃以下が特に好ましい。
ただし、本発明におけるアセタール基は、酸分解の活性化エネルギーが低く、露光による酸発生剤由来の酸により容易に分解し、カルボキシル基またはフェノール性水酸基を生じるため、必ずしもPEBを行うことなく、現像によりポジ画像を形成することもできる。
現像工程で使用する現像液には、塩基性化合物が含まれることが好ましい。塩基性化合物としては、例えば、水酸化リチウム、水酸化ナトリウム、水酸化カリウムなどのアルカリ金属水酸化物類;炭酸ナトリウム、炭酸カリウムなどのアルカリ金属炭酸塩類;重炭酸ナトリウム、重炭酸カリウムなどのアルカリ金属重炭酸塩類;テトラメチルアンモニウムヒドロキシド、テトラエチルアンモニウムヒドロキシド、コリンヒドロキシド等のアンモニウムヒドロキシド類;ケイ酸ナトリウム、メタケイ酸ナトリウムなどの水溶液を使用することができる。また、上記アルカリ類の水溶液にメタノールやエタノールなどの水溶性有機溶剤や界面活性剤を適当量添加した水溶液を現像液として使用することもできる。
好ましい現像液として、テトラメチルアンモニウムヒドロキシドの0.4〜2.5%水溶液を挙げる事ができる。
現像液のpHは、好ましくは10.0〜14.0である。
現像時間は、好ましくは30〜500秒間であり、また、現像の手法は液盛り法(パドル法)、シャワー法、ディップ法等の何れでもよい。
現像の後に、リンス工程を行うこともできる。リンス工程では、現像後の基板を純水などで洗うことで、付着している現像液除去、現像残渣除去を行う。リンス方法は公知の方法を用いることができる。例えばシャワーリンスやディップリンスなどを挙げる事ができる。
ポストベークの前に、比較的低温でベークを行った後にポストベークすることもできる(ミドルベーク工程の追加)。ミドルベークを行う場合は、90〜150℃で1〜60分加熱した後に、200℃以上の高温でポストベークすることが好ましい。また、ミドルベーク、ポストベークを3段階以上の多段階に分けて加熱する事もできる。このようなミドルベーク、ポストベークの工夫により、パターンのテーパー角を調整することができる。これらの加熱は、ホットプレート、オーブン、赤外線ヒーターなど、公知の加熱方法を使用することができる。
なお、ポストベークに先立ち、パターンを形成した基板に活性光線により全面再露光(ポスト露光)した後、ポストベークすることにより未露光部分に存在する光酸発生剤から酸を発生させ、架橋工程を促進する触媒として機能させることができ、膜の硬化反応を促進することができる。ポスト露光工程を含む場合の好ましい露光量としては、100〜3,000mJ/cm2が好ましく、100〜500mJ/cm2が特に好ましい。
本発明の硬化膜は、上述した本発明の組成物を硬化して得られた硬化膜である。
本発明の硬化膜は、層間絶縁膜として好適に用いることができる。また、本発明の硬化膜は、上述した本発明の硬化膜の形成方法により得られた硬化膜であることが好ましい。
本発明の感光性樹脂組成物により、絶縁性に優れ、高温でベークされた場合においても高い透明性を有する層間絶縁膜が得られる。本発明の感光性樹脂組成物を用いてなる層間絶縁膜は、高い透明性を有し、硬化膜物性に優れるため、液晶表示装置や有機EL表示装置の用途に有用である。
本発明の液晶表示装置は、本発明の硬化膜を具備することを特徴とする。
本発明の液晶表示装置としては、上記本発明の感光性樹脂組成物を用いて形成される平坦化膜や層間絶縁膜を有すること以外は特に制限されず、様々な構造をとる公知の液晶表示装置を挙げることができる。
例えば、本発明の液晶表示装置が具備するTFT(Thin−Film Transistor)の具体例としては、アモルファスシリコン−TFT、低温ポリシリコンーTFT、酸化物半導体TFT等が挙げられる。本発明の硬化膜は電気特性に優れるため、これらのTFTに組み合わせて好ましく用いることができる。
また、本発明の液晶表示装置が取りうる液晶駆動方式としてはTN(TwistedNematic)方式、VA(Virtical Alignment)方式、IPS(In−Place−Switching)方式、FFS(Frings Field Switching)方式、OCB(Optical Compensated Bend)方式などが挙げられる。
パネル構成においては、COA(Color Filter on Allay)方式の液晶表示装置でも本発明の硬化膜を用いることができ、例えば、特開2005−284291の有機絶縁膜(115)や、特開2005−346054の有機絶縁膜(212)として用いることができる。また、本発明の液晶表示装置が取りうる液晶配向膜の具体的な配向方式としてはラビング配向法、光配向方などが挙げられる。また、特開2003−149647号公報や特開2011−257734号公報に記載のPSA(Polymer Sustained Alignment)技術によってポリマー配向支持されていてもよい。
また、本発明の感光性樹脂組成物および本発明の硬化膜は、上記用途に限定されず種々の用途に使用することができる。例えば、平坦化膜や層間絶縁膜以外にも、カラーフィルターの保護膜や、液晶表示装置における液晶層の厚みを一定に保持するためのスペーサーや固体撮像素子においてカラーフィルター上に設けられるマイクロレンズ等に好適に用いることができる。
図1は、アクティブマトリックス方式の液晶表示装置10の一例を示す概念的断面図である。このカラー液晶表示装置10は、背面にバックライトユニット12を有する液晶パネルであって、液晶パネルは、偏光フィルムが貼り付けられた2枚のガラス基板14,15の間に配置されたすべての画素に対応するTFT16の素子が配置されている。ガラス基板上に形成された各素子には、硬化膜17中に形成されたコンタクトホール18を通して、画素電極を形成するITO透明電極19が配線されている。ITO透明電極19の上には、液晶20の層とブラックマトリックスを配置したRGBカラーフィルター22が設けられている。
バックライトの光源としては、特に限定されず公知の光源を用いることができる。例えば白色LED、青色・赤色・緑色などの多色LED、蛍光灯(冷陰極管)、有機ELなどを挙げる事ができる。
また、液晶表示装置は、3D(立体視)型のものとしたり、タッチパネル型のものとしたりすることも可能である。さらにフレキシブル型にすることも可能であり、特開2011−145686号公報に記載の第2層間絶縁膜(48)や、特開2009−258758号公報に記載の層間絶縁膜(520)として用いることができる。
本発明の有機EL表示装置は、本発明の硬化膜を具備することを特徴とする。
本発明の有機EL表示装置としては、上記本発明の感光性樹脂組成物を用いて形成される平坦化膜や層間絶縁膜を有すること以外は特に制限されず、様々な構造をとる公知の各種有機EL表示装置や液晶表示装置を挙げることができる。
例えば、本発明の有機EL表示装置が具備するTFT(Thin−Film Transistor)の具体例としては、アモルファスシリコン−TFT、低温ポリシリコンーTFT、酸化物半導体TFT等が挙げられる。本発明の硬化膜は電気特性に優れるため、これらのTFTに組み合わせて好ましく用いることができる。
図2は、有機EL表示装置の一例の構成概念図である。ボトムエミッション型の有機EL表示装置における基板の模式的断面図を示し、平坦化膜4を有している。
ガラス基板6上にボトムゲート型のTFT1を形成し、このTFT1を覆う状態でSi3N4から成る絶縁膜3が形成されている。絶縁膜3に、ここでは図示を省略したコンタクトホールを形成した後、このコンタクトホールを介してTFT1に接続される配線2(高さ1.0μm)が絶縁膜3上に形成されている。配線2は、TFT1間または、後の工程で形成される有機EL素子とTFT1とを接続するためのものである。
さらに、配線2の形成による凹凸を平坦化するために、配線2による凹凸を埋め込む状態で絶縁膜3上に平坦化膜4が形成されている。
平坦化膜4上には、ボトムエミッション型の有機EL素子が形成されている。すなわち、平坦化膜4上に、ITOからなる第一電極5が、コンタクトホール7を介して配線2に接続させて形成されている。また、第一電極5は、有機EL素子の陽極に相当する。
第一電極5の周縁を覆う形状の絶縁膜8が形成されており、この絶縁膜8を設けることによって、第一電極5とこの後の工程で形成する第二電極との間のショートを防止することができる。
さらに、図2には図示していないが、所望のパターンマスクを介して、正孔輸送層、有機発光層、電子輸送層を順次蒸着して設け、次いで、基板上方の全面にAlから成る第二電極を形成し、封止用ガラス板と紫外線硬化型エポキシ樹脂を用いて貼り合わせることで封止し、各有機EL素子にこれを駆動するためのTFT1が接続されてなるアクティブマトリックス型の有機EL表示装置が得られる。
MATHF:2−テトラヒドロフラニルメタクリレート(合成品)
MAEVE:1−エトキシエチルメタクリレート(和光純薬工業社製)
OXE−30:3−エチル−3−オキセタニルメチルメタクリレート(大阪有機化学工業社製)
NBMA:n−ブトキシメチルアクリルアミド(東京化成社製)
HEMA:ヒドロキシエチルメタクリレート(和光純薬工業社製)
MAA:メタクリル酸(和光純薬工業社製)
MMA:メチルメタクリレート(和光純薬工業社製)
St:スチレン(和光純薬工業社製)
t−BuMA:t−ブチルメタクリレート(三菱レイヨン社製)
GMA:グリシジルメタクリレート(和光純薬工業社製)
DCPM:ジシクロペンタニルメタクリレート
V−601:ジメチル 2,2’−アゾビス(2−メチルプロピオネート)(和光純薬工業社製)
V−65:2,2‘−アゾビス(2,4−ジメチルバレロニトリル)(和光純薬工業社製)
メタクリル酸(86g、1mol)を15℃に冷却しておき、カンファースルホン酸(4.6g、0.02mol)添加した。その溶液に、2−ジヒドロフラン(71g、1mol、1.0当量)を滴下した。1時間撹拌した後に、飽和炭酸水素ナトリウム(500mL)を加え、酢酸エチル(500mL)で抽出し、硫酸マグネシウムで乾燥後、不溶物を濾過後40℃以下で減圧濃縮し、残渣の黄色油状物を減圧蒸留して沸点(bp.)54〜56℃/3.5mmHg留分のメタクリル酸テトラヒドロ−2H−フラン−2−イル(MATHF)125gを無色油状物として得た(収率80%)。
3つ口フラスコに蒸留PGMEA(89g)を入れ、窒素雰囲気下において90℃に昇温した。その溶液にMAA(全単量体成分中の10mol%となる量)、MATHF(全単量体成分中の40mol%となる量)、GMA(全単量体成分中の40mol%に相当)、MMA(全単量体成分中の10mol%となる量)、V−65(全単量体成分の合計100mol%に対して4mol%に相当)をPEGMEA(89g)に室温で溶解させた溶液を、2時間かけて滴下した。滴下終了後2時間攪拌し、反応を終了させた。反応混合液の5倍容量のヘキサンに投入し白色粉体を析出させ、析出した粉体を濾過取り出しし、これをPGMEAに溶解した。再度ヘキサンに投入し白色粉体を析出させ、析出した粉体を濾過取り出しし、乾燥させて重合体P−1を得た。
モノマー種類等を下記表に示す通りに変更し、他の重合体を合成した。
下記表に記載の固形分比となるように、(A)重合体成分、(B)光酸発生剤、溶剤、塩基性化合物、界面活性剤、その他の成分から、下記表に示す各実施例・各比較例に示す成分をそれぞれ混合し、溶液とした。その口径0.2μmのポリテトラフルオロエチレン製フィルターで濾過して、実施例および比較例の感光性樹脂組成物を得た。上記表において、表中の特に単位を付していない数値はmol%を単位とする。
(エーテル結合を有する溶剤)
ハイソルブEDM:(ジエチレングリコールエチルメチルエーテル、沸点176℃、東邦化学工業社製)
ハイソルブEDM−S:(ジエチレングリコールエチルメチルエーテル、沸点176℃、東邦化学工業社製)
ハイソルブMDM:(ジエチレングリコールジメチルエーテル、沸点162℃、東邦化学工業社製)
ハイソルブMMPOM:(プロピレングリコールジメチルエーテル、沸点97℃、東邦化学工業社製)
γ-ブチロラクトン:(沸点204℃、三菱化学製)
PGMEA:(プロピレングリコールモノメチルエーテルアセテート、沸点143℃、昭和電工社製)
1,3−BGDA:(1,3−ブチレングリコールジアセテート、沸点232℃、ダイセル社製)
ハイソルブDM:ジエチレングリコールモノメチルエーテル、沸点194℃(東邦化学工業社製)
シクロヘキサノン:(沸点155℃、ダイセル社製)
例えば1Lスケールの減圧蒸留装置にハイソルブEDMを700g入れ、減圧度30mmHg、外設温度70℃にて蒸留を行い、約100gを初流として除き、蒸留物を400g得た。
DBA:9,10−ジブトキシアントラセン(川崎化成社製)
DPHA:(KAYARAD DPHA、日本化薬社製)
(アルコキシシラン化合物)
KBM−403:γ−グリシドキシプロピルトリメトキシシラン(KBM−403、信越シリコーン社製)
AO−60:(アデカスタブAO−60、アデカ社製)
(架橋剤)
JER157S70:(JER157S70、三菱ケミカルホールディングス社製)
W−1:シリコーン系界面活性剤((株)東レ・ダウコーニング製の「SH 8400 FLUID」)
W−2:フッ素系界面活性剤(ネオス社製、フタージェントFTX−218)
W−3:下記構造式で示されるパーフルオロアルキル基含有ノニオン界面活性剤(F−554,DIC社製)
B−1:PAG−103(商品名、下記に示す構造、BASF社製)
B−3:下記に示す構造(合成例を後述する。)
2−ナフトール(10g)、クロロベンゼン(30mL)の懸濁溶液に塩化アルミニウム(10.6g)、2−クロロプロピオニルクロリド(10.1g)を添加し、混合液を40℃に加熱して2時間反応させた。氷冷下、反応液に4NHCl水溶液(60mL)を滴下し、酢酸エチル(50mL)を添加して分液した。有機層に炭酸カリウム(19.2g)を加え、40℃で1時間反応させた後、2NHCl水溶液(60mL)を添加して分液し、有機層を濃縮後、結晶をジイソプロピルエーテル(10mL)でリスラリーし、ろ過、乾燥してケトン化合物(6.5g)を得た。
得られたケトン化合物(3.0g)、メタノール(30mL)の懸濁溶液に酢酸(7.3g)、50質量%ヒドロキシルアミン水溶液(8.0g)を添加し、加熱還流した。放冷後、水(50mL)を加え、析出した結晶をろ過、冷メタノール洗浄後、乾燥してオキシム化合物(2.4g)を得た。
得られたオキシム化合物(1.8g)をアセトン(20mL)に溶解させ、氷冷下トリエチルアミン(1.5g)、p−トルエンスルホニルクロリド(2.4g)を添加し、室温に昇温して1時間反応させた。反応液に水(50mL)を添加し、析出した結晶をろ過後、メタノール(20mL)でリスラリーし、ろ過、乾燥してB−3の化合物(上述の構造)(2.3g)を得た。
なお、B−3の1H−NMRスペクトル(300MHz、CDCl3)は、δ=8.3(d,1H),8.0(d,2H),7.9(d,1H),7.8(d,1H),7.6(dd,1H),7.4(dd,1H)7.3(d,2H),7.1(d.1H),5.6(q,1H),2.4(s,3H),1.7(d,3H)であった。
各組成物に配合する溶剤(2種以上用いる場合は混合物)をDMAc(ジメチルアセトアミド)で100倍または10倍に希釈したものをガスクロマトマトグラフィー装置(Agilent6890、カラム:HP−INNOWAX=30m×0.32mmID(膜厚0.25μm))にインジェクションし以下の条件下で測定した。それぞれのアルコール成分は絶対検量線法によって、試料中に含まれるそれぞれのアルコール成分量を求めた。
オーブン温度:50℃(2分保持した後10℃/分で昇温した。250℃で28分保持させた。
キャリアーガス:He=1mL/min、注入口温度:250℃、
スプリット比:10/1。FID検出器:温度300℃、
H2=40mL/min、Air=400mL/min。
注入量は1μL。
測定結果を表に示す(単位:ppm)。
A:1ppm以上10ppm以下
B:10ppmより大きく30ppm以下
C:30ppmより大きく50ppm以下
D:50ppmより大きく500ppm以下
E:500ppmより大きい
ヘキサメチルジシラザン蒸気で1分間表面処理をしたガラス基板(コーニング1737、0.7mm厚(コーニング社製))上に、各感光性樹脂組成物をスリット塗布した後(実施例37のみはスピンコート)、85℃/120秒ホットプレート上でプリベークして溶剤を揮発させ、膜厚3.0μmの感光性樹脂組成物層を形成した。
次に、得られた感光性樹脂組成物層を、キヤノン(株)製PLA−501F露光機(超高圧水銀ランプ)を用いて、4.0μmホールパターンのマスクを介して露光した。その後、アルカリ現像液(0.4質量%のテトラメチルアンモニウムヒドロキシド水溶液)で現像し(24℃、60秒)、超純水で20秒リンスした。下底の径が4.0μmのホールパターンを形成できることを確認し、またその時の最適露光量(Eopt)を感度とした。いずれの実施例も実用的な感度であった。
A:60mJ/cm2未満
B:60mJ/cm2以上80mJ/cm2未満
C:80mJ/cm2以上100mJ/cm2未満
D:100mJ/cm2以上200mJ/cm2未満
E:200mJ/cm2以上
各組成物の調整直後の粘度の測定結果をη1、気温32℃、湿度55%の環境下で経時させた後の粘度の測定結果をη2としたとき|η2−η1|/η1の変動が±8%以内に収まる期間を測定した。なお、粘度は東機産業 粘度計RE85Lを用い、25℃で測定した。変動が±8%以内に収まる期間が長いほど、保存安定性が優れる。A、B、Cが実用範囲である。
A:4週間以上
B:3週間以上、4週間未満
C:2週間以上、3週間未満
D:1週間以上、2週間未満
E:1週間未満
ガラス基板を、ヘキサメチルジシラザン(HMDS)蒸気下に30秒曝し、基板に各感光性樹脂組成物をスリットコート塗布した後(実施例37のみはスピンコート)、90℃/120秒ホットプレート上でプリベークして溶剤を揮発させ、膜厚4.0μmの感光性樹脂組成物層を形成した。続いて超高圧水銀灯を用いて積算照射量が300mJ/cm2(エネルギー強度:20mW/cm2、i線)となるように露光し、この基板をオーブンにて230℃/60分間加熱した。
得られた硬化膜の膜厚(T1)を測定した。そして、この硬化膜が形成された基板を60℃に温度制御されたジメチルスルホキシド溶剤中に10分間浸漬させた後、浸漬後の硬化膜の膜厚(t1)を測定し、浸漬による膜厚変化率{|t1−T1|/T1}×100〔%〕を算出した。結果を下記表に示す。小さいほど好ましく、C以上が実用上問題のないレベルである。
A:1%未満
B:1%以上4%未満
C:4%以上6%未満
D:6%以上10%未満
E:10%以上または溶解
一方、アルコール性水酸基を有する溶剤の含有量が50ppmを超える場合(比較例2、3、7〜10、および13)、保存安定性が顕著に劣り、耐薬品性も劣っていることが分かった。エーテル結合および/またはエステル結合を有する溶剤を含まない場合(比較例1、11、および12)、感度が劣ってしまっていた。重合体成分が、アセタール基で保護された基を有さない場合(比較例4)、感度が劣っていた。重合体成分が、架橋性基を有さない場合(比較例5)、耐薬品性が劣っていた。比較例6は、感度が悪く、パターンを形成することができなかった。
比較例1では、溶剤としてトルエンを使用しているが、他の実施例と比較して感度が劣ることがわかる。これにより、エーテル結合および/またはエステル結合を有する溶剤を用いることで感度が向上することがわかる。また、比較例4から、酸基がアセタール基で保護された基を有する構成単位を用いていないことで感度が劣ることがわかる。比較例5から、架橋性基を有する構成単位を用いていないことで耐薬品性が劣ることがわかる。
(実施例101)
薄膜トランジスタ(TFT)を用いた有機EL表示装置を以下の方法で作製した(図2参照)。
ガラス基板6上にボトムゲート型のTFT1を形成し、このTFT1を覆う状態でSi3N4から成る絶縁膜3を形成した。次に、この絶縁膜3に、ここでは図示を省略したコンタクトホールを形成した後、このコンタクトホールを介してTFT1に接続される配線2(高さ1.0μm)を絶縁膜3上に形成した。この配線2は、TFT1間または、後の工程で形成される有機EL素子とTFT1とを接続するためのものである。
さらに、配線2の形成による凹凸を平坦化するために、配線2による凹凸を埋め込む状態で絶縁膜3上へ平坦化膜4を形成した。絶縁膜3上への平坦化膜4の形成は、実施例1の感光性樹脂組成物を基板上にスリット塗布し、ホットプレート上でプリベーク(90℃×2分)した後、マスク上から高圧水銀灯を用いてi線(365nm)を45mJ/cm2(照度20mW/cm2)照射した後、アルカリ水溶液にて現像してパターンを形成し、230℃で60分間の加熱処理を行った。
感光性樹脂組成物を塗布する際の塗布性は良好で、露光、現像、焼成の後に得られた硬化膜には、しわやクラックの発生は認められなかった。さらに、配線2の平均段差は500nm、作製した平坦化膜4の膜厚は2,000nmであった。
次に、得られた平坦化膜4上に、ボトムエミッション型の有機EL素子を形成した。まず、平坦化膜4上に、ITOからなる第一電極5を、コンタクトホール7を介して配線2に接続させて形成した。その後、市販のレジストを塗布、プリベークし、所望のパターンのマスクを介して露光し、現像した。このレジストパターンをマスクとして、ITOエッチャント用いたウエットエッチングによりパターン加工を行った。その後、レジスト剥離液(リムーバ100、AZエレクトロニックマテリアルズ社製)を用いて上記レジストパターンを50℃で剥離した。こうして得られた第一電極5は、有機EL素子の陽極に相当する。
さらに、真空蒸着装置内で所望のパターンマスクを介して、正孔輸送層、有機発光層、電子輸送層を順次蒸着して設けた。次いで、基板上方の全面にAlから成る第二電極を形成した。得られた上記基板を蒸着機から取り出し、封止用ガラス板と紫外線硬化型エポキシ樹脂を用いて貼り合わせることで封止した。
以上のようにして、各有機EL素子にこれを駆動するためのTFT1が接続してなるアクティブマトリックス型の有機EL表示装置が得られた。駆動回路を介して電圧を印加したところ、良好な表示特性を示し、信頼性の高い有機EL表示装置であることが分かった。
実施例101において、実施例1の感光性樹脂組成物を実施例16の感光性樹脂組成物に換えたこと以外は、実施例101と同様に有機EL表示装置を作製した。得られた有機EL表示装置に対して、駆動電圧を印加したところ、良好な表示特性を示し、信頼性の高い有機EL表示装置であることが分かった。
実施例101において、実施例1の感光性樹脂組成物を実施例23の感光性樹脂組成物に換えたこと以外は、実施例101と同様に有機EL表示装置を作製した。得られた有機EL表示装置に対して、駆動電圧を印加したところ、良好な表示特性を示し、信頼性の高い有機EL表示装置であることが分かった。
実施例101において、実施例1の感光性樹脂組成物を実施例30の感光性樹脂組成物に換えたこと以外は、実施例101と同様に有機EL表示装置を作製した。得られた有機EL表示装置に対して、駆動電圧を印加したところ、良好な表示特性を示し、信頼性の高い有機EL表示装置であることが分かった。
実施例101において、実施例1の感光性樹脂組成物を実施例34の感光性樹脂組成物に換えたこと以外は、実施例101と同様に有機EL表示装置を作製した。得られた有機EL表示装置に対して、駆動電圧を印加したところ、良好な表示特性を示し、信頼性の高い有機EL表示装置であることが分かった。
特許第3321003号公報の図1に記載のアクティブマトリクス型液晶表示装置において、層間絶縁膜として硬化膜17を以下のようにして形成し、実施例106の液晶表示装置を得た。すなわち、実施例1の感光性樹脂組成物を用い、上記実施例101における有機EL表示装置の平坦化膜4の形成方法と同様の方法で、層間絶縁膜として硬化膜17を形成した。
得られた液晶表示装置に対して、駆動電圧を印加したところ、良好な表示特性を示し、信頼性の高い液晶表示装置であることが分かった。
実施例106において、実施例1の感光性樹脂組成物を実施例16の感光性樹脂組成物に換えたこと以外は、実施例106と同様に液晶表示装置を作製した。得られた液晶表示装置に対して、駆動電圧を印加したところ、良好な表示特性を示し、信頼性の高い液晶表示装置であることが分かった。
実施例106において、実施例1の感光性樹脂組成物を実施例23の感光性樹脂組成物に換えたこと以外は、実施例106と同様に液晶表示装置を作製した。得られた液晶表示装置に対して、駆動電圧を印加したところ、良好な表示特性を示し、信頼性の高い液晶表示装置であることが分かった。
実施例106において、実施例1の感光性樹脂組成物を実施例30の感光性樹脂組成物に換えたこと以外は、実施例106と同様に液晶表示装置を作製した。得られた液晶表示装置に対して、駆動電圧を印加したところ、良好な表示特性を示し、信頼性の高い液晶表示装置であることが分かった。
実施例106において、実施例1の感光性樹脂組成物を実施例34の感光性樹脂組成物に換えたこと以外は、実施例106と同様に液晶表示装置を作製した。得られた液晶表示装置に対して、駆動電圧を印加したところ、良好な表示特性を示し、信頼性の高い液晶表示装置であることが分
2:配線
3:絶縁膜
4:平坦化膜
5:第一電極
6:ガラス基板
7:コンタクトホール
8:絶縁膜
10:液晶表示装置
12:バックライトユニット
14,15:ガラス基板
16:TFT
17:硬化膜
18:コンタクトホール
19:ITO透明電極
20:液晶
22:カラーフィルター
Claims (11)
- (A)下記(1)および(2)の少なくとも一方を満たす重合体を含む重合体成分、
(1)(a1)酸基がアセタール基で保護された基を有する構成単位、および(a2)架橋性基を有する構成単位を有する重合体、
(2)前記構成単位(a1)を有する重合体および前記構成単位(a2)を有する重合体、
(B)光酸発生剤、ならびに
(C)エーテル結合および/またはエステル結合を有し、アルコール性水酸基を有さない溶剤、
を含み、
全溶剤量に対するアルコール性水酸基を有する溶剤の含有量が1〜50ppmである感光性樹脂組成物。 - アルコール性水酸基を有する溶剤の1atmにおける沸点が、95℃以上である、請求項1に記載の感光性樹脂組成物。
- (C)溶剤が、エーテル結合を有する溶剤を含む、請求項1または2に記載の感光性樹脂組成物。
- (C)溶剤が、ジエチレングリコール誘導体を含む、請求項1〜3のいずれか1項に記載の感光性樹脂組成物。
- (C)溶剤が、ジエチレングリコールエチルメチルエーテルおよび/またはジエチレングリコールジメチルエーテルを含む、請求項1〜4のいずれか1項に記載の感光性樹脂組成物。
- (C)溶剤が、エーテル結合を有する溶剤およびエステル結合を有する溶剤を含む、請求項1〜5のいずれか1項に記載の感光性樹脂組成物。
- 前記(a2)構成単位における架橋性基が、エポキシ基、オキセタニル基、および−NH−CH2−ORから選ばれる少なくとも1種である、請求項1〜7のいずれか1項に記載の感光性樹脂組成物;但し、Rは炭素数1〜20のアルキル基を示す。
- 前記(C)溶剤が、全溶剤の50質量%以上である、請求項1〜8のいずれか1項に記載の感光性樹脂組成物。
- (B)光酸発生剤が、オキシムスルホネート化合物および/またはオニウム塩化合物である、請求項1〜9のいずれか1項に記載の感光性樹脂組成物。
- (1)請求項1〜10のいずれか1項に記載の感光性樹脂組成物を基板上に塗布する工程、
(2)塗布された前記感光性樹脂組成物から溶剤を除去する工程、
(3)溶剤が除去された前記感光性樹脂組成物を活性放射線で露光する工程、
(4)露光された前記感光性樹脂組成物を水性現像液で現像する工程、および、
(5)現像された前記感光性樹脂組成物を熱硬化するポストベーク工程、を含む、硬化膜の製造方法。