JP6157868B2 - Self-adhesive sheet

Info

Publication number: JP6157868B2
Application number: JP2013023595A
Authority: JP
Inventors: 真資芦田; 康介佐伯; 松井　哲也; 哲也松井
Original assignee: Zeon Corp; Toyo Aluminium Ekco Products Co Ltd
Current assignee: Zeon Corp; Toyo Aluminium Ekco Products Co Ltd
Priority date: 2013-02-08
Filing date: 2013-02-08
Publication date: 2017-07-05
Anticipated expiration: 2033-02-08
Also published as: JP2014151563A

Description

本発明は、ガラス板等の被着体に貼り付けることができる自着性シートに関する。 The present invention relates to a self-adhesive sheet that can be attached to an adherend such as a glass plate.

近年、省エネルギー等の観点から、建物の窓に赤外線等の透過を抑制するシートが用いられている。このようなシートは、通常、一方の面に粘着性を備えさせ、この粘着性を有する側の面を窓ガラス等に貼り付けることによって利用されている。 In recent years, from the viewpoint of energy saving or the like, a sheet that suppresses transmission of infrared rays or the like is used for a window of a building. Such a sheet is usually used by providing one surface with adhesiveness and sticking the adhesive surface to a window glass or the like.

このような粘着性を有するシート（以下、「粘着シート」ということがある。）を窓ガラス等に貼り付ける際、粘着シートと窓ガラスとの間に空気が噛み込まれて残留することがあった。このような問題を解決するための技術として、例えば特許文献１には、基材と、基材の一方の側に設けられた装飾層と、基材の他方の側に設けられた粘着剤層とを備え、一方の面から他方の面に貫通する貫通孔が複数形成されている粘着シートであって、貫通孔の基材、装飾層および粘着剤層における孔径は０．１〜３００μｍであり、孔密度は３０〜５０，０００個／１００ｃｍ^２であることを特徴とする粘着シートが開示されている。 When a sheet having such an adhesive property (hereinafter sometimes referred to as an “adhesive sheet”) is attached to a window glass or the like, air may be trapped and remain between the adhesive sheet and the window glass. It was. As a technique for solving such a problem, for example, Patent Document 1 discloses a base material, a decoration layer provided on one side of the base material, and an adhesive layer provided on the other side of the base material. And a plurality of through holes penetrating from one surface to the other surface are formed, and the hole diameters of the through holes in the base material, the decorative layer, and the pressure-sensitive adhesive layer are 0.1 to 300 μm. A pressure-sensitive adhesive sheet is disclosed in which the pore density is 30 to 50,000 / 100 cm ² .

また、特許文献２には、窓ガラス等の平滑な被貼着体に貼り付けて使用する貼着シートであって、合成樹脂フィルムよりなるシート体と、シート体の一方面に形成され、被貼着体に貼り付けられる貼着層と、シート体及び貼着層を貫通するように形成されたスリットとを備え、スリットの少なくとも全体は、その一端とその他端とを結ぶ直線に重ならない、貼着シートが開示されている。 Patent Document 2 discloses an adhesive sheet that is used by being attached to a smooth adherend such as a window glass, and is formed on a sheet body made of a synthetic resin film and one surface of the sheet body. Provided with an adhesive layer to be attached to the adhesive body, and a slit formed so as to penetrate the sheet body and the adhesive layer, at least the whole of the slit does not overlap with a straight line connecting one end and the other end, An adhesive sheet is disclosed.

特開２００５−７５９５３号公報JP 2005-75953 A 特開２０１２−１２６８５５号公報JP 2012-126855 A

上記特許文献１や特許文献２に開示されている技術によれば、粘着シートと窓ガラスなどの被着体との間の空気を、粘着シートの厚さ方向に貫通して設けられた孔やスリットを介して排出することができるため、粘着シートと窓ガラスとの間に空気が残留することを抑制できると考えられる。 According to the techniques disclosed in Patent Document 1 and Patent Document 2, air between the pressure-sensitive adhesive sheet and an adherend such as a window glass is provided with a hole provided through the thickness direction of the pressure-sensitive adhesive sheet. Since it can discharge | emit through a slit, it is thought that it can suppress that air remains between an adhesive sheet and a window glass.

しかしながら、上記従来技術のように粘着シートに貫通孔やスリットを設けると、外観が悪くなる虞があった。すなわち、上記従来の粘着シートを窓ガラスに貼り付けたとすると、該窓ガラスに照射された光が粘着シートに設けられた貫通孔やスリットによって散乱されることにより、外観が悪くなる虞があった。 However, when a through-hole or a slit is provided in the pressure-sensitive adhesive sheet as in the prior art, the appearance may be deteriorated. That is, if the conventional adhesive sheet is attached to a window glass, the light applied to the window glass may be scattered by the through holes and slits provided in the adhesive sheet, which may deteriorate the appearance. .

そこで本発明は、ガラス板等の被着体に貼り付けた際の外観の悪化を抑制できる自着性シートを提供することを課題とする。 Then, this invention makes it a subject to provide the self-adhesive sheet which can suppress the deterioration of the external appearance at the time of affixing on adherends, such as a glass plate.

本発明者らは、ガラス板等の被着体に貼り付けた際の剥離力が適切に調整されたシートを用いることによって、従来の粘着シートのような貫通孔やスリットを設けなくとも、又は貫通孔やスリットの数を減らしたり大きさを小さくしたりしても、被着体との間に空気が残留することを抑制できることを知見した。
本発明は上記知見に基づいて完成された。 The present inventors can use a sheet in which the peeling force when it is attached to an adherend such as a glass plate is appropriately adjusted, or without providing a through-hole or a slit like a conventional pressure-sensitive adhesive sheet, or It has been found that even if the number of through holes and slits is reduced or the size is reduced, air can be prevented from remaining between the adherend.
The present invention has been completed based on the above findings.

本発明は、可撓性を有する基材層と、該基材層上に形成された、シリコーン樹脂を含む吸着層とを有し、該吸着層は、被着体に貼り付けた後に剥がすときの剥離力が０．００１Ｎ／ｃｍ以上０．００５Ｎ／ｃｍ以下である、自着性シートである。 The present invention has a flexible substrate layer and an adsorption layer containing a silicone resin formed on the substrate layer, and the adsorption layer is peeled off after being attached to an adherend. The self-adhesive sheet has a peel strength of 0.001 N / cm or more and 0.005 N / cm or less.

本発明において、「基材層上に形成された」とは、基材層上に直接形成されている形態に限定されず、他の層を介して基材層上に形成された形態も含む概念である。例えば、基材層の表面に易接着層が形成されている場合、当該易接着層を介して形成される形態も含む。 In the present invention, the term “formed on the base material layer” is not limited to the form directly formed on the base material layer, and includes a form formed on the base material layer via another layer. It is a concept. For example, when the easily bonding layer is formed in the surface of a base material layer, the form formed through the said easily bonding layer is also included.

本発明の自着性シートは、吸着層がシリコーン樹脂を含む組成物を基材層上に塗工してキャスト成形して得られる層であることが好ましい。 In the self-adhesive sheet of the present invention, the adsorbing layer is preferably a layer obtained by applying a composition containing a silicone resin onto a base material layer and cast molding.

本発明において、「基材層上に塗工して」とは、基材層上に直接塗工する場合に限定されず、他の層を介して基材層上に塗工する場合も含む概念である。例えば、基材層の表面に易接着層が形成されている場合、当該易接着層上に塗工する場合も含む。 In the present invention, “coating on the base material layer” is not limited to the case of direct application on the base material layer, but also includes the case of coating on the base material layer via another layer. It is a concept. For example, when the easily bonding layer is formed in the surface of a base material layer, the case where it coats on the said easily bonding layer is also included.

また、本発明の自着性シートは、吸着層に含まれるシリコーン樹脂が付加反応型であることが好ましい。 In the self-adhesive sheet of the present invention, the silicone resin contained in the adsorption layer is preferably an addition reaction type.

また、本発明の自着性シートは、基材層の吸着層が備えられる側とは反対の面側に、赤外線または紫外線の透過を抑制する層を備えていることが好ましい。 Moreover, it is preferable that the self-adhesive sheet of the present invention includes a layer that suppresses transmission of infrared rays or ultraviolet rays on the side of the base material layer opposite to the side on which the adsorption layer is provided.

上記において、本発明の自着性シートは、基材層の吸着層が備えられる側とは反対の面側に、赤外線の透過を抑制する層および紫外線の透過を抑制する層をそれぞれ備えていることがより好ましい。また、本発明の自着性シートは、基材層の吸着層が備えられる側とは反対の面側に、赤外線および紫外線の透過を抑制する層を備えていることがより好ましい。すなわち、上述した、赤外線の透過を抑制する層、および、紫外線の透過を抑制する層は、それぞれ別の層として存在してもよく、また、赤外線および紫外線の透過を抑制する機能を一層に備えさせていてもよい。 In the above, the self-adhesive sheet of the present invention is provided with a layer for suppressing the transmission of infrared rays and a layer for suppressing the transmission of ultraviolet rays, respectively, on the side opposite to the side where the adsorption layer of the base material layer is provided. It is more preferable. Moreover, it is more preferable that the self-adhesive sheet of the present invention includes a layer that suppresses transmission of infrared rays and ultraviolet rays on the side of the base material layer opposite to the side on which the adsorption layer is provided. That is, the above-described layer for suppressing the transmission of infrared light and the layer for suppressing the transmission of ultraviolet light may exist as separate layers, and further have a function of suppressing the transmission of infrared light and ultraviolet light. It may be allowed.

また、本発明の自着性シートは、厚さ方向に貫通した孔またはスリットが複数形成されていることが好ましい。 The self-adhesive sheet of the present invention preferably has a plurality of holes or slits penetrating in the thickness direction.

本発明の自着性シートによれば、上述した従来技術のような貫通孔やスリットを設けなくとも被着体との間に空気が噛み込まれて残留することを抑制できる。ただし、貫通孔やスリットを設けることによって、被着体との間に空気が残留することをより抑制しやすくなる。この場合、従来技術よりも貫通孔やスリットの数を減らしたり大きさを小さくしたりすることができるので、ガラス板等の被着体に貼り付けた際の外観の悪化を抑制できる。 According to the self-adhesive sheet of the present invention, it is possible to prevent air from being caught and remaining between the adherend without providing the through-holes and slits as in the prior art described above. However, by providing the through hole and the slit, it becomes easier to suppress the air from remaining between the adherend and the body. In this case, since the number of through-holes and slits can be reduced or the size can be reduced as compared with the prior art, it is possible to suppress the deterioration of the appearance when pasted on an adherend such as a glass plate.

本発明の自着性シートによれば、ガラス板等の被着体に貼り付けた際の外観の悪化を抑制できる。 According to the self-adhesive sheet of the present invention, it is possible to suppress the deterioration of the appearance when it is attached to an adherend such as a glass plate.

自着性シート１０の構成を概略的に示す断面図である。1 is a cross-sectional view schematically showing a configuration of a self-adhesive sheet 10.

本発明の上記した作用及び利得は、次に説明する発明を実施するための形態から明らかにされる。以下本発明を図面に示す実施形態に基づき説明する。ただし本発明は当該実施形態に限定されるものではない。 The above-described operation and gain of the present invention will be clarified from embodiments for carrying out the invention described below. Hereinafter, the present invention will be described based on embodiments shown in the drawings. However, the present invention is not limited to the embodiment.

図１は本発明の自着性シートの一つの実施形態例である自着性シート１０の構成を概略的に示す断面図である。なお、図１は自着性シート１０の層構成を説明するための図であり、各層の厚さや形状を正確に表わすものではない。 FIG. 1 is a cross-sectional view schematically showing a configuration of a self-adhesive sheet 10 which is one embodiment of the self-adhesive sheet of the present invention. FIG. 1 is a view for explaining the layer structure of the self-adhesive sheet 10, and does not accurately represent the thickness and shape of each layer.

図１に示したように、自着性シート１０は、基材層３と、基材層３の一方の面側に形成された吸着層２と、該吸着層２が他の部材に貼りつくことを防止する離型フィルム１と、を備えている。また、基材層３の表面には易接着層４ａ、４ｂが形成されている。さらに、基材層３の吸着層２が形成された側と反対の面側には、接着層５、赤外線遮蔽層６、基材層７、およびハードコート層８が備えられている。以下、自着性シート１０に含まれるこれらの構成要素について詳細に説明する。 As shown in FIG. 1, the self-adhesive sheet 10 includes a base material layer 3, an adsorption layer 2 formed on one surface side of the base material layer 3, and the adsorption layer 2 sticks to another member. And a release film 1 for preventing this. Easy-adhesion layers 4 a and 4 b are formed on the surface of the base material layer 3. Furthermore, an adhesive layer 5, an infrared shielding layer 6, a base material layer 7, and a hard coat layer 8 are provided on the side of the base material layer 3 opposite to the side on which the adsorption layer 2 is formed. Hereinafter, these components included in the self-adhesive sheet 10 will be described in detail.

（離型フィルム１）
離型フィルム１は、吸着層２を目的とする被着体に貼り付けるまでの間に吸着層２が他の部材に貼りつくことを防止するため、吸着層２に貼り付けておくシート状の部材である。自着性シート１０を使用するとき、すなわち吸着層２を目的の被着体に貼り付けるとき、離型フィルム１を剥離する。離型フィルム１としては、従来公知の離型フィルムを特に限定することなく用いることができる。 (Release film 1)
The release film 1 is a sheet-like film that is attached to the adsorption layer 2 in order to prevent the adsorption layer 2 from adhering to other members until the adsorption layer 2 is attached to the target adherend. It is a member. When the self-adhesive sheet 10 is used, that is, when the adsorption layer 2 is attached to the target adherend, the release film 1 is peeled off. As the release film 1, a conventionally known release film can be used without any particular limitation.

（吸着層２）
吸着層２は、自着性シート１０を窓ガラス等の被着体に貼り付ける際に該被着体に吸着する層である。吸着層２は、表面が平滑なガラス板に対する剥離力が０．００１０Ｎ／ｃｍ以上０．００５０Ｎ／ｃｍ以下であり、０．００３０Ｎ／ｃｍ以上０．００４５Ｎ／ｃｍ以下であることが好ましい。
なお、「剥離力」とは、以下の条件にて測定したものである。まず、２５ｍｍ×１２５ｍｍの大きさの試験片をガラス板に吸着させた後、ローラーで２ｋｇｆ（１９．６Ｎ）の荷重をかけながら１往復させて圧着させ、その後１時間放置する。この試験片を２３℃、５０％ＲＨ環境下で、剥離速度３００ｍｍ／分にて１８０度方向に剥離させ、その時の剥離力を、株式会社島津製作所製「オートグラフＡＧ−ＩＳ」にて測定した。 (Adsorption layer 2)
The adsorbing layer 2 is a layer that adsorbs to the adherend when the self-adhesive sheet 10 is attached to the adherend such as a window glass. The adsorptive layer 2 has a peel force with respect to a glass plate having a smooth surface of 0.0010 N / cm or more and 0.0050 N / cm or less, and preferably 0.0030 N / cm or more and 0.0045 N / cm or less.
The “peeling force” is measured under the following conditions. First, after a test piece having a size of 25 mm × 125 mm is adsorbed to a glass plate, the test piece is reciprocated once while applying a load of 2 kgf (19.6 N) with a roller, and then left for 1 hour. This test piece was peeled in a 180 ° direction at a peeling speed of 300 mm / min in an environment of 23 ° C. and 50% RH, and the peeling force at that time was measured by “Autograph AG-IS” manufactured by Shimadzu Corporation. .

自着性シート１０は、吸着層２の剥離力が上記のように適切な範囲に調整されていることによって、ガラス板等の表面が平滑な被着体との間に空気が残留することを抑制しつつ、該被着体に貼り付く。すなわち、自着性シート１０によれば、上述した従来技術のような貫通孔やスリットを設けなくとも被着体との間に空気が噛み込まれて残留することを抑制できる。したがって、自着性シート１０によれば、ガラス板等の被着体に貼り付けた際の外観の悪化を抑制できる。 In the self-adhesive sheet 10, air remains between an adherend having a smooth surface such as a glass plate by adjusting the peeling force of the adsorption layer 2 to an appropriate range as described above. It sticks to this adherend while suppressing. That is, according to the self-adhesive sheet 10, it is possible to prevent air from being caught between the adherend and remaining without providing the through-holes and slits as in the prior art described above. Therefore, according to the self-adhesive sheet 10, it is possible to suppress the deterioration of the appearance when pasted on an adherend such as a glass plate.

吸着層２の剥離力が上記範囲の下限を下回ると、自着性シートを被着体に貼り付け難くなる。また、吸着層２の剥離力が上記範囲の上限を上回ると、被着体と自着性シートとの間に噛み込まれた空気が抜ける道ができにくくなり、被着体と自着性シートとの間に空気が残留しやすくなる。 When the peeling force of the adsorption layer 2 is below the lower limit of the above range, it becomes difficult to attach the self-adhesive sheet to the adherend. Moreover, if the peeling force of the adsorbing layer 2 exceeds the upper limit of the above range, it becomes difficult for the air entrained between the adherend and the self-adhesive sheet to escape, and the adherend and the self-adhesive sheet. Air tends to remain between.

また、自着性シート１０は吸着層２の剥離力が上記のように適切な範囲に調整されていることによって、被着体に貼り付けた後に剥がして再度貼り直すことが容易である。 Moreover, the self-adhesive sheet 10 can be easily peeled off after being attached to the adherend and re-attached because the peeling force of the adsorption layer 2 is adjusted to an appropriate range as described above.

上記のような吸着層２はシリコーン樹脂を含む組成物で構成されている。また、吸着層２は、シリコーン樹脂を含む組成物を基材層３上に塗工してキャスト成形（シリコーン樹脂を溶剤に溶かした組成物を塗工して乾燥させて硬化）して得られる層であることが好ましい。また、吸着層２に含まれるシリコーン樹脂は付加反応型であることが好ましい。付加反応型のシリコーン樹脂は、加熱することにより短時間で硬化反応を進めることができ、また、硬化収縮がほとんどないためキャスト成形に好適に使用できる。 The adsorption layer 2 as described above is composed of a composition containing a silicone resin. The adsorption layer 2 is obtained by coating a composition containing a silicone resin on the base material layer 3 and cast molding (coating a composition in which a silicone resin is dissolved in a solvent and drying and curing). A layer is preferred. Moreover, it is preferable that the silicone resin contained in the adsorption layer 2 is an addition reaction type. The addition reaction type silicone resin can be cured in a short time by heating, and can be suitably used for cast molding because there is little curing shrinkage.

吸着層２の厚さは特に限定されないが、１０μｍ以上５０μｍ以下であることが好ましく、２０μｍ以上３０μｍ以下であることがより好ましい。吸着層２の厚さを１０μｍ以上にすることによって、自着性シート１０を被着体に貼り付けたまま保持できるだけの剥離力を吸着層２に備えさせやすくなる。また、吸着層２の厚さを５０μｍ以下にすることによって、吸着層２の厚さを均一にしやすくなる。 The thickness of the adsorption layer 2 is not particularly limited, but is preferably 10 μm or more and 50 μm or less, and more preferably 20 μm or more and 30 μm or less. By making the thickness of the adsorbing layer 2 10 μm or more, it becomes easy to provide the adsorbing layer 2 with a peeling force that can hold the self-adhesive sheet 10 while being adhered to the adherend. Moreover, it becomes easy to make the thickness of the adsorption layer 2 uniform by making the thickness of the adsorption layer 2 50 μm or less.

（基材層３）
基材層３は吸着層２を形成するための基材となる層である。基材層３は可撓性を有する樹脂製のシートで構成されている。基材層３を構成する材料としては、例えば、アクリル、スチレン、ポリカーボネート、ポリエチレンテレフタレート、アクリロニトリル等のうちの１つ以上を主成分とする透明樹脂や、エポキシアクリレートやウレタンアクリレート系の反応性樹脂（電離放射線硬化型樹脂等）を挙げることができる。なお、「主成分」とは、材料全体に対して５０質量％以上含有されている成分を意味する（以下、同様とする。）。また、基材層３には各種添加剤を適宜添加してもよい。一般的な添加剤としては、フェノール系等の酸化防止剤、ラクトン系等の安定剤等を挙げることができる。 (Base material layer 3)
The base material layer 3 is a layer serving as a base material for forming the adsorption layer 2. The base material layer 3 is composed of a resin sheet having flexibility. As a material constituting the base material layer 3, for example, a transparent resin mainly composed of one or more of acrylic, styrene, polycarbonate, polyethylene terephthalate, acrylonitrile, etc., an epoxy acrylate or urethane acrylate reactive resin ( Ionizing radiation curable resins). The “main component” means a component contained in an amount of 50% by mass or more based on the whole material (hereinafter the same). Various additives may be appropriately added to the base material layer 3. Examples of general additives include phenol-based antioxidants, lactone-based stabilizers, and the like.

基材層３の厚さは特に限定されないが、１０μｍ以上１００μｍ以下であることが好ましい。基材層３の厚さを１０μｍ以上とすることによって、自着性シート１０に必要とされる強度を確保しやすくなる。また、基材層３の厚さを１００μｍ以下とすることによって、自着性シート１０に適度な柔軟性を備えさせやすくなる。 Although the thickness of the base material layer 3 is not specifically limited, It is preferable that they are 10 micrometers or more and 100 micrometers or less. By setting the thickness of the base material layer 3 to 10 μm or more, it is easy to ensure the strength required for the self-adhesive sheet 10. Moreover, by making the thickness of the base material layer 3 100 μm or less, the self-adhesive sheet 10 can be easily provided with appropriate flexibility.

（易接着層４ａ、４ｂ）
易接着層４ａ、４ｂは、基材層３と吸着層２や接着層５とを密着させやすくするために基材層３の表面に薄く形成された樹脂層である。通常、易接着層４ａ、４ｂには、基材層３に対して親和性を有するバインダが含まれる。当該バインダとしては、ポリエステル系樹脂、ポリウレタン系樹脂、アクリル系樹脂、ポリオレフィン系樹脂などが挙げられる。基材層３を構成する材料の主成分がポリエチレンテレフタレート（ＰＥＴ）の場合、易接着層４ａ、４ｂにはポリエステル系樹脂が含まれることが好ましい。また、当該バインダは有機溶剤に溶解したものを用いてもよく、水分散物を用いてもよい。ただし、環境負荷を抑える観点からは、水分散物を用いて水系塗布することが好ましい。易接着層４ａ、４ｂの形成は、例えば易接着層４ａ、４ｂを構成するシートを基材層３に貼合する方法や、易接着層４ａ、４ｂを構成する塗布液を基材層３の表面に塗工する方法が挙げられる。塗布液の調製に用いる溶媒には、水や、トルエン、メチルエチルケトン等の有機溶媒を挙げることができる。易接着層４ａ、４ｂの層厚は通常、２０ｎｍ以上３００ｎｍ以下程度である。 (Easily adhesive layers 4a, 4b)
The easy-adhesion layers 4 a and 4 b are resin layers formed thinly on the surface of the base material layer 3 in order to make the base material layer 3 and the adsorption layer 2 and the adhesive layer 5 easily adhere to each other. Usually, the easily adhesive layers 4 a and 4 b include a binder having affinity for the base material layer 3. Examples of the binder include polyester resins, polyurethane resins, acrylic resins, and polyolefin resins. When the main component of the material constituting the base material layer 3 is polyethylene terephthalate (PET), it is preferable that the easily adhesive layers 4a and 4b include a polyester resin. Further, the binder may be dissolved in an organic solvent, or an aqueous dispersion may be used. However, from the viewpoint of reducing the environmental load, it is preferable to use an aqueous dispersion to apply water. The easy-adhesion layers 4a and 4b are formed by, for example, a method of bonding the sheets constituting the easy-adhesion layers 4a and 4b to the base material layer 3 and the coating liquid constituting the easy-adhesion layers 4a and 4b. The method of coating on the surface is mentioned. Examples of the solvent used for preparing the coating liquid include water and organic solvents such as toluene and methyl ethyl ketone. The layer thickness of the easy-adhesion layers 4a and 4b is usually about 20 nm to 300 nm.

（接着層５）
接着層５は、基材層３と赤外線遮蔽層６とを接着するための層である。ただし、本実施形態では上述したように基材層３の表面に易接着層４ａが形成されているため、正確には易接着層４ａおよび接着層５を介して基材層３と赤外線遮蔽層６とを接着する。 (Adhesive layer 5)
The adhesive layer 5 is a layer for adhering the base material layer 3 and the infrared shielding layer 6. However, in this embodiment, since the easy-adhesion layer 4a is formed on the surface of the base material layer 3 as described above, the base material layer 3 and the infrared shielding layer are accurately interposed via the easy-adhesion layer 4a and the adhesive layer 5. 6 is bonded.

接着層５を構成する材料は、基材層３と赤外線遮蔽層６とを接着できるものであれば特に限定されない。接着層５には、例えば、ドライラミネート接着剤を用いることができる。ドライラミネート接着剤としては、例えば、ポリ酢酸ビニル系接着剤、アクリル酸エチル、アクリル酸ブチル、２−エチルヘキシルエステル等のホモポリマー、または、これらとメタクリル酸メチル、アクリロニトリル、スチレン等との共重合体等からなるポリアクリル酸エステル系接着剤、シアノアクリレート系接着剤、エチレンと酢酸ビニル、アクリル酸エチル、（メタ）アクリル酸等のモノマーとの共重合体等からなるエチレン共重合体系接着剤、セルロース系接着剤、ポリエステル系接着剤、ポリアミド系接着剤、ポリイミド系接着剤、尿素樹脂またはメラミン樹脂等からなるアミノ樹脂系接着剤、フェノール樹脂系接着剤、エポキシ系接着剤、ポリウレタン系接着剤、反応型（メタ）アクリル系接着剤、クロロプレンゴム、ニトリルゴム、スチレン−ブタジエンゴム等からなるゴム系接着剤、シリコーン系接着剤、アルカリ金属シリケート、低融点ガラス等からなる無機系接着剤等を挙げることができる。 The material which comprises the contact bonding layer 5 will not be specifically limited if the base material layer 3 and the infrared shielding layer 6 can be adhere | attached. For the adhesive layer 5, for example, a dry laminate adhesive can be used. Examples of the dry laminate adhesive include polyvinyl acetate adhesive, homopolymers such as ethyl acrylate, butyl acrylate, and 2-ethylhexyl ester, or copolymers of these with methyl methacrylate, acrylonitrile, styrene, and the like. Polyacrylic acid ester adhesive, cyanoacrylate adhesive, ethylene copolymer adhesive made of copolymer of ethylene and vinyl acetate, ethyl acrylate, (meth) acrylic acid, etc., cellulose Adhesive, polyester adhesive, polyamide adhesive, polyimide adhesive, amino resin adhesive made of urea resin or melamine resin, phenolic resin adhesive, epoxy adhesive, polyurethane adhesive, reaction Mold (meth) acrylic adhesive, chloroprene rubber, Nitori Rubber, styrene - rubber adhesive comprising a butadiene rubber, a silicone-based adhesive, an alkali metal silicate, may be mentioned inorganic adhesive or the like made of a low-melting-point glass or the like.

上記の接着剤は、水性型、溶液型、エマルジョン型、分散型のいずれの組成物形態でもよく、その形状についても、フィルム・シート状、粉末状、固形状等のいずれの形態でもよい。また、その接着機構についても、化学反応型、溶剤揮発型、熱溶融型、熱圧型等のいずれの形態でもよい。 The adhesive may be in the form of an aqueous type, solution type, emulsion type, or dispersion type, and the shape may be any of film / sheet type, powder type, solid type, and the like. The bonding mechanism may be any form such as a chemical reaction type, a solvent volatilization type, a heat melting type, and a hot pressure type.

本実施形態では、赤外線遮蔽層６の表面に上記接着剤を、例えば、ロールコート法、グラビアロールコート法、キスコート法等のコート法、または、印刷法等によって塗工し、次いで、溶剤等を乾燥させることで、接着層５を形成することができる。 In the present embodiment, the adhesive is applied to the surface of the infrared shielding layer 6 by, for example, a coating method such as a roll coating method, a gravure roll coating method, a kiss coating method, or a printing method, and then a solvent or the like is applied. The adhesive layer 5 can be formed by drying.

（赤外線遮蔽層６）
赤外線遮蔽層６は赤外線の透過を抑制する層である。このような赤外線遮蔽層６は、例えば、基材層７の一方の面にアルミニウムを蒸着することによって形成できる。また、公知の赤外線吸収剤を基材層７の一方の面に塗布したり、当該赤外線吸収剤を添加した樹脂組成物を層状に形成したりすることによっても、赤外線遮蔽層６を形成できる。なお、公知の赤外線吸収剤としては、アンチモンドープ酸化スズ（ＡＴＯ）またはスズドープ酸化インジウム（ＩＴＯ）、フタロシアニン化合物などの金属酸化物超微粒子などが挙げられる。 (Infrared shielding layer 6)
The infrared shielding layer 6 is a layer that suppresses infrared transmission. Such an infrared shielding layer 6 can be formed, for example, by vapor-depositing aluminum on one surface of the base material layer 7. The infrared shielding layer 6 can also be formed by applying a known infrared absorber on one surface of the base material layer 7 or by forming a resin composition to which the infrared absorber is added in a layer shape. In addition, as a well-known infrared absorber, metal oxide ultrafine particles, such as antimony dope tin oxide (ATO) or tin dope indium oxide (ITO), a phthalocyanine compound, etc. are mentioned.

自着性シート１０が赤外線遮蔽層６を備えることによって、例えば自着性シート１０を建物の採光部に設置された窓ガラスに貼り付けた場合、特に夏場における室内温度の上昇を抑制することができ、冷房の使用を控えられる等の効果を奏することができる。 When the self-adhesive sheet 10 includes the infrared shielding layer 6, for example, when the self-adhesive sheet 10 is attached to a window glass installed in a daylighting part of a building, it is possible to suppress an increase in indoor temperature particularly in summer. It is possible to achieve such an effect that the use of cooling is refrained.

（基材層７）
基材層７は、赤外線遮蔽層６およびハードコート層８を形成するための基材となる層である。基材層７は基材層３と同様に、可撓性を有する樹脂製のシートで構成されている。このような基材を構成する材料としては、基材層３と同様のものを用いることができる。 (Base material layer 7)
The base material layer 7 is a layer serving as a base material for forming the infrared shielding layer 6 and the hard coat layer 8. The base material layer 7 is composed of a flexible resin sheet, like the base material layer 3. As a material constituting such a base material, the same material as the base material layer 3 can be used.

また、本実施形態では、基材層７に紫外線を吸収する機能を持たせることが好ましい。基材層７において紫外線を吸収させるためには、基材層７に公知の紫外線吸収剤を添加または塗布することが考えられる。公知の紫外線吸収剤としては、例えば、ベンゾトリアゾール系紫外線吸収剤や、トリアジン系紫外線吸収剤、ベンゾフェノン系紫外線吸収剤、ベンゾエート系紫外線吸収剤などが挙げられる。 Moreover, in this embodiment, it is preferable to give the base material layer 7 a function of absorbing ultraviolet rays. In order to absorb ultraviolet rays in the base material layer 7, it is conceivable to add or apply a known ultraviolet absorber to the base material layer 7. Examples of known UV absorbers include benzotriazole UV absorbers, triazine UV absorbers, benzophenone UV absorbers, and benzoate UV absorbers.

自着性シート１０に紫外線を吸収する機能を付加することによって、例えば自着性シート１０を建物の採光部に設置された窓ガラスに貼り付けた場合、室内に居る人の皮膚への悪影響や室内にある家具の退色等を抑制する等の効果を奏することができる。 By adding a function of absorbing ultraviolet rays to the self-adhesive sheet 10, for example, when the self-adhesive sheet 10 is attached to a window glass installed in a daylighting part of a building, The effect of suppressing fading etc. of the furniture in a room can be produced.

基材層７の厚さは特に限定されないが、１０μｍ以上１００μｍ以下であることが好ましい。基材層７の厚さを１０μｍ以上とすることによって、自着性シート１０に必要とされる強度を確保しやすくなる。また、基材層７の厚さを１００μｍ以下とすることによって、自着性シート１０に適度な柔軟性を備えさせやすくなる。 Although the thickness of the base material layer 7 is not specifically limited, It is preferable that they are 10 micrometers or more and 100 micrometers or less. By setting the thickness of the base material layer 7 to 10 μm or more, it is easy to ensure the strength required for the self-adhesive sheet 10. Moreover, by making the thickness of the base material layer 7 100 μm or less, the self-adhesive sheet 10 can be easily provided with appropriate flexibility.

（ハードコート層８）
ハードコート層８は、自着性シート１０の表面保護を目的として、自着性シート１０のうち被着体に貼り付けられる側とは反対側の最表面に設けられる層である。ハードコート層８は透明な樹脂層として形成することができる。自着性シート１０の表面の擦り傷、表面汚染に対する耐性の観点から、ハードコート層８は硬化性樹脂が硬化してなる樹脂硬化層として形成することが好ましい。 (Hard coat layer 8)
For the purpose of protecting the surface of the self-adhesive sheet 10, the hard coat layer 8 is a layer provided on the outermost surface of the self-adhesive sheet 10 on the side opposite to the side attached to the adherend. The hard coat layer 8 can be formed as a transparent resin layer. From the viewpoint of resistance to scratches and surface contamination on the surface of the self-adhesive sheet 10, the hard coat layer 8 is preferably formed as a cured resin layer obtained by curing a curable resin.

ハードコート層８を構成する材料としては、例えば電離放射線硬化性樹脂、その他公知の硬化性樹脂等を要求性能に応じて適宜採用すればよい。ハードコート層８に用いることができる電離放射線硬化性樹脂としては、アクリレート系、オキセタン系、シリコーン系等の電離放射線硬化性樹脂が挙げられる。 As a material constituting the hard coat layer 8, for example, an ionizing radiation curable resin, other known curable resins, or the like may be appropriately employed according to the required performance. Examples of the ionizing radiation curable resin that can be used for the hard coat layer 8 include acrylate-based, oxetane-based, and silicone-based ionizing radiation curable resins.

また、ハードコート層８には、耐汚染性向上の機能を追加してもよい。これは例えばシリコーン系化合物、フッ素系化合物などを添加することにより可能となる。さらにその他の機能として帯電防止性向上、撥水性向上の機能を有するものとしてもよい。 Further, the hard coat layer 8 may be added with a function of improving the stain resistance. This can be achieved, for example, by adding a silicone compound, a fluorine compound, or the like. Further, as other functions, it may have a function of improving antistatic properties and water repellency.

これまでの本発明の説明では、離型フィルム１、吸着層２、基材層３、易接着層４ａ、４ｂ、接着層５、赤外線遮蔽層６、基材層７、ハードコート層８を備えた自着性シート１０を例示して説明したが、本発明の自着性シートは当該形態に限定されない。本発明の自着性シートは、少なくとも吸着層２および基材層３を備えていればよい。少なくとも吸着層２および基材層３を備えることによって、強度を確保しつつ、上述したようにガラス板等の被着体に貼り付けたときに空気の噛み込みを抑制することができる。 In the description of the present invention so far, the release film 1, the adsorption layer 2, the base material layer 3, the easy adhesion layers 4a and 4b, the adhesive layer 5, the infrared shielding layer 6, the base material layer 7, and the hard coat layer 8 are provided. Although the self-adhesive sheet 10 has been described as an example, the self-adhesive sheet of the present invention is not limited to this form. The self-adhesive sheet of the present invention only needs to include at least the adsorption layer 2 and the base material layer 3. By providing at least the adsorbing layer 2 and the base material layer 3, it is possible to suppress the biting of air when it is attached to an adherend such as a glass plate as described above while ensuring strength.

また、ガラス板等に貼り付けたときの空気の噛み込みをより抑制しやすくする観点からは、本発明の自着性シートは、厚さ方向に貫通した孔やスリットを複数備えている形態としてもよい。このように厚さ方向に貫通した孔やスリットを形成することによって、該孔やスリットを介して自着性シートと被着体との間の空気を排出することができる。なお、本発明の自着性シートによれば、貫通孔やスリットを設けなくとも上述したように被着体との間に空気が噛み込まれて残留することを抑制できる。ただし、貫通孔やスリットを設けることによって、被着体との間に空気が残留することをより抑制しやすくなる。この場合、従来技術よりも貫通孔やスリットの数を減らしたり大きさを小さくしたりすることができるので、ガラス板の被着体に貼り付けた際に外観の悪化を抑制できる。 Moreover, from the viewpoint of making it easier to suppress air entrainment when pasted on a glass plate or the like, the self-adhesive sheet of the present invention has a plurality of holes and slits penetrating in the thickness direction. Also good. By forming the holes and slits penetrating in the thickness direction in this way, the air between the self-adhesive sheet and the adherend can be discharged through the holes and slits. In addition, according to the self-adhesive sheet of the present invention, air can be prevented from remaining between the adherend and remaining as described above without providing a through hole or a slit. However, by providing the through hole and the slit, it becomes easier to suppress the air from remaining between the adherend and the body. In this case, since the number of through-holes and slits can be reduced or the size can be reduced as compared with the prior art, it is possible to suppress deterioration in appearance when the glass plate is attached to an adherend.

以下に、実施例にて本発明をさらに詳しく説明するが、本発明は実施例に限定されるものではない。 Hereinafter, the present invention will be described in more detail by way of examples. However, the present invention is not limited to the examples.

１．自着性シートの作製
以下に説明するようにして、自着性シートを作製した。 1. Production of self-adhesive sheet A self-adhesive sheet was produced as described below.

（実施例１）
基材層として、表面に易接着層が形成された透明なポリエチレンテレフタレートフィルム（東洋紡株式会社製、コスモシャイン（登録商標）Ａ４３００、厚さ：３８μｍ）を用意した。当該基材層の一方の面側に、以下に説明する工程を経て調整した組成物を、アプリケーター（２００μｍ）を用いて塗工した。その後、オーブンを用いて８０℃で２分間加熱した後に１２０℃で２分間加熱させ、基材層上に厚さ２７μｍの吸着層を形成した。このようにして、基材層および吸着層を備えた自着性シートを作製した。吸着層を構成する組成物の配合を表１に示した。なお、表１において配合量は質量部で示している。

Example 1
A transparent polyethylene terephthalate film (manufactured by Toyobo Co., Ltd., Cosmo Shine (registered trademark) A4300, thickness: 38 μm) having an easy-adhesion layer formed on the surface was prepared as a base material layer. The composition prepared through the steps described below was applied to one surface side of the base material layer using an applicator (200 μm). Then, after heating for 2 minutes at 80 degreeC using oven, it was made to heat for 2 minutes at 120 degreeC, and the 27-micrometer-thick adsorption layer was formed on the base material layer. Thus, the self-adhesive sheet provided with the base material layer and the adsorption layer was produced. Table 1 shows the composition of the composition constituting the adsorption layer. In Table 1, the compounding amount is shown in parts by mass.

吸着層を構成する組成物は以下の工程１〜５を経て、サンプル作製に必要な量の２倍の量を調整した。
工程１：５００ｍｌのディスポカップにシリコーン樹脂およびポットライフ延長剤を計量し、ディスパーで攪拌した。攪拌条件は、１４００ｒｐｍ、１分とした。
工程２：１００ｍｌのディスポカップに触媒および希釈溶剤を計量し、ディスパーで攪拌した。攪拌条件は、１４００ｒｐｍ、１分とした。
工程３：工程１を経て得られた組成物に工程２を経て得られた組成物を少しずつ加えながら、ディスパーで攪拌した。攪拌条件は、１４００ｒｐｍ、３分とした。
工程４：工程３を経て得られた組成物をメッシュでろ過し、５００ｍｌのディスポカップに移した。
工程５：工程４を経て得られた組成物を２時間以上静置し、自然脱泡させた。静置時間経過後、気泡が完全に抜けていることを確認した。
なお、実施例１及び実施例２、並びに、比較例１〜比較例３において使用されたシリコーン樹脂は、全て、付加反応型シリコーン樹脂である。 The composition constituting the adsorption layer was adjusted to an amount twice as large as that required for sample preparation through the following steps 1 to 5.
Step 1: Silicone resin and pot life extender were weighed in a 500 ml disposable cup and stirred with a disper. The stirring conditions were 1400 rpm and 1 minute.
Step 2: The catalyst and the diluting solvent were weighed into a 100 ml disposable cup and stirred with a disper. The stirring conditions were 1400 rpm and 1 minute.
Process 3: It stirred with the disper, adding the composition obtained through the process 2 little by little to the composition obtained through the process 1. The stirring conditions were 1400 rpm and 3 minutes.
Step 4: The composition obtained through Step 3 was filtered through a mesh and transferred to a 500 ml disposable cup.
Process 5: The composition obtained through the process 4 was allowed to stand for 2 hours or longer to be naturally degassed. After the standing time, it was confirmed that the bubbles were completely removed.
The silicone resins used in Examples 1 and 2 and Comparative Examples 1 to 3 are all addition reaction type silicone resins.

（実施例２）
吸着層を構成する組成物の配合を表１に示したように変更した以外は実施例１と同様にして自着性シートを作製した。 (Example 2)
A self-adhesive sheet was produced in the same manner as in Example 1 except that the composition of the composition constituting the adsorption layer was changed as shown in Table 1.

（比較例１）
吸着層を構成する組成物の配合を表１に示したように変更した以外は実施例１と同様にして自着性シートを作製した。 (Comparative Example 1)
A self-adhesive sheet was produced in the same manner as in Example 1 except that the composition of the composition constituting the adsorption layer was changed as shown in Table 1.

（比較例２）
吸着層を構成する組成物の配合を表１に示したように変更した以外は実施例１と同様にして自着性シートを作製した。 (Comparative Example 2)
A self-adhesive sheet was produced in the same manner as in Example 1 except that the composition of the composition constituting the adsorption layer was changed as shown in Table 1.

（比較例３）
吸着層を構成する組成物の配合を表１に示したように変更した以外は実施例１と同様にして自着性シートを作製した。 (Comparative Example 3)
A self-adhesive sheet was produced in the same manner as in Example 1 except that the composition of the composition constituting the adsorption layer was changed as shown in Table 1.

２．評価
上記のようにして作製した各例にかかる自着性シートについて、剥離力と空気の抜け易さを評価した。評価結果を表１に示した。なお、評価方法および評価基準は以下の通りである。 2. Evaluation About the self-adhesive sheet | seat concerning each example produced as mentioned above, peeling force and the ease of air removal were evaluated. The evaluation results are shown in Table 1. The evaluation method and evaluation criteria are as follows.

まず、表面が平滑なガラス板を用意し、２５ｍｍ×１２５ｍｍの大きさの自着性シートを端部から少しずつ該ガラス板に貼り付けた。空気の抜け易さの評価は、上記のようにして自着性シートをガラス板に貼り終えた後に、自着性シートとガラス板との間に空気が残っていたか否かを目視で確認して、主観的に評価した。空気がかなり残っていた場合を×、空気が少し残っていた場合を○、空気が全く残っていなかった場合を◎とした。 First, a glass plate having a smooth surface was prepared, and a self-adhesive sheet having a size of 25 mm × 125 mm was attached to the glass plate little by little from the end. The evaluation of the ease of air release was made by visually checking whether air remained between the self-adhesive sheet and the glass plate after the self-adhesive sheet was attached to the glass plate as described above. And evaluated subjectively. The case where air remained considerably was marked as x, the case where a little air was left as ◯, and the case where no air remained as ◎.

上記のようにして自着性シートをガラス板に貼り終えた後、該自着性シートの上から１９．６Ｎで押圧しながら（２ｋｇｆの荷重をかけながら）ローラーを１往復させた。その後、１時間放置した。このサンプルを２３℃、５０％ＲＨ環境下、１８０°テープピールの条件下で３００ｍｍ／分の速度で剥離させ、その時の剥離力［Ｎ／ｃｍ］を、株式会社島津製作所製「オートグラフＡＧ−ＩＳ」にて測定し、評価した。 After affixing the self-adhesive sheet on the glass plate as described above, the roller was reciprocated once while pressing at 19.6 N from above the self-adhesive sheet (loading 2 kgf). Then, it was left for 1 hour. This sample was peeled off at a speed of 300 mm / min under the conditions of a tape peel at 180 ° in an environment of 23 ° C. and 50% RH, and the peeling force [N / cm] at that time was “Autograph AG-” manufactured by Shimadzu Corporation. It was measured and evaluated by “IS”.

表１に示した結果から、実施例にかかる自着性シートのように剥離力がある程度小さい場合には、被着体に貼り付けたときの空気の噛み込みを抑制できることがわかる。 From the results shown in Table 1, it can be seen that when the peel force is small to some extent as in the self-adhesive sheet according to the example, it is possible to suppress the biting of air when it is attached to the adherend.

１離型フィルム
２吸着層
３基材層
４ａ、４ｂ易接着層
５接着層
６赤外線遮蔽層
７基材層
８ハードコート層
１０自着性シート DESCRIPTION OF SYMBOLS 1 Release film 2 Adsorption layer 3 Base material layer 4a, 4b Easy adhesion layer 5 Adhesion layer 6 Infrared shielding layer 7 Base material layer 8 Hard coat layer 10 Self-adhesive sheet

Claims

As a resin-made base material layer having a thickness of 10 μm or more and 100 μm or less, it has only the first base material layer and the second base material layer,
Further, it formed on the first base layer, and the adsorption layer comprising a silicone resin,
On a surface opposite from the first side of the adsorption layer of the base layer is provided, comprising an adhesive layer, a
The second base material layer is provided on the surface side of the adhesive layer opposite to the first base material layer side,
The adsorbing layer is a self-adhesive sheet having a peeling force of 0.001 N / cm or more and 0.005 N / cm or less when peeled off after being attached to an adherend.

The self-adhesive sheet according to claim 1, wherein the resin is polyethylene terephthalate.

The self-adhesive sheet according to claim 1 or 2, wherein the adsorption layer is a layer obtained by coating a composition containing the silicone resin on the first base material layer and cast molding.

The self-adhesive sheet according to any one of claims 1 to 3, wherein the silicone resin contained in the adsorption layer is an addition reaction type.

The self-adhesion according to any one of claims 1 to 4, further comprising a layer for suppressing transmission of infrared rays or ultraviolet rays on a surface side of the first base material layer opposite to a side on which the adsorption layer is provided. Sex sheet.

The self-adhesive sheet according to any one of claims 1 to 5, wherein a plurality of holes or slits penetrating in the thickness direction are formed.