JP5998264B2 - チオール基含有有色化合物、金属ナノワイヤー、分散液、透明導電膜、情報入力装置、及び、電子機器 - Google Patents
チオール基含有有色化合物、金属ナノワイヤー、分散液、透明導電膜、情報入力装置、及び、電子機器 Download PDFInfo
- Publication number
- JP5998264B2 JP5998264B2 JP2015196023A JP2015196023A JP5998264B2 JP 5998264 B2 JP5998264 B2 JP 5998264B2 JP 2015196023 A JP2015196023 A JP 2015196023A JP 2015196023 A JP2015196023 A JP 2015196023A JP 5998264 B2 JP5998264 B2 JP 5998264B2
- Authority
- JP
- Japan
- Prior art keywords
- group
- metal nanowire
- conductive film
- dye
- transparent conductive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
さらに、金属ナノワイヤーを用いた透明導電膜を表示パネルの表示面側に設けた場合、金属ナノワイヤーの表面で外光が乱反射することにより、表示パネルの黒表示がほのかに明るく表示される、いわゆる黒浮き現象が発生する。黒浮き現象は、コントラスト低下による表示特性の劣化を招く要因になる。
また、金属ナノワイヤーと二次導電性媒体(CNT(カーボンナノチューブ)、導電性ポリマー、ITO等)とを併用して、光散乱を防止する手法が提案されている(例えば、特許文献2参照)。
また、後者の方法では、CNT、導電性ポリマー、ITO等の二次導電性媒体(着色材料)を金属ナノワイヤーネットワークの開口部に配置するため、透明性が損なわれる虞があるという問題がある。
この金属ナノワイヤーと該金属ナノワイヤーに吸着された有色化合物(染料)とを含む透明導電膜は、金属ナノワイヤーに吸着された有色化合物に可視光が吸収されて、金属ナノワイヤーの表面での光の乱反射が防止される。前記透明導電膜は、例えば、発色団Rと吸着官能基Xで構成されたR−Xで表わされる有色化合物(染料)を金属ナノワイヤーに吸着させているので、有色化合物(染料)の添加による透明性の低下を抑制することができる。
<1> 可視光領域に吸収を持つ発色団と、チオール基と、前記発色団と前記チオール基との間に設けられたスペーサとを有し、前記スペーサは、炭素数2〜30の鎖状アルキレン基又は炭素数3〜30の環状アルキレン基、或いは、前記アルキレン基への付加構造の炭素数が前記アルキレン基の炭素数以下である前記アルキレン基の誘導体であり、(i)酸性基含有染料と、(ii)チオール基、スペーサ−、及び塩基性基を有する塩基性基含有分子との反応物であり、前記酸性基含有染料が、下記構造式(1)で表される金属錯体塩酸性染料であり、前記塩基性基含有分子が、2−アミノエタンチオール塩酸塩、6−アミノ−1−ヘキサンチオール塩酸塩、11−アミノ−1−ウンデカンチオール塩酸塩、及び16−アミノ−1−ヘキサデカンチオール塩酸塩、からなる群から選択された少なくとも1種であることを特徴とするチオール基含有有色化合物である。
また、下記一般式(1)で表わされるチオール基含有有色化合物が、水溶液中で、下記式(2)のように解離した場合において、スペーサWが発色団Rのチオール基由来のアニオン(S-)に対する影響を低減し、プロトン(H+)の生成を抑制するので、酸性度を低くして、有色化合物を金属ナノワイヤー本体を溶解することなく、金属ナノワイヤー本体に吸着させて(金属ナノワイヤー本体を有色化合物で表面処理して)、外光散乱を抑制可能な、シート抵抗の小さい透明導電膜を製造することができる。
R−W−SH・・・・・・・(1)
(但し、Rは可視光領域に吸収を持つ発色団であり、Wは炭素数2〜30の鎖状アルキレン基又は炭素数3〜30の環状アルキレン基、或いは、前記アルキレン基への付加構造の炭素数が前記アルキレン基の炭素数以下である前記アルキレン基の誘導体である。)
H++RWS-・・・・・・・(2)
<2> 金属ナノワイヤー本体を有し、前記金属ナノワイヤー本体の表面の少なくとも一部が、前記<1>に記載のチオール基含有有色化合物で表面処理されたことを特徴とする金属ナノワイヤーである。
該<2>に記載の金属ナノワイヤーにおいて、金属ナノワイヤー本体を有し、前記金属ナノワイヤー本体の表面の少なくとも一部が、前記チオール基含有有色化合物で表面処理されたので、金属ナノワイヤーが分断されて長さが短くなくなるのを防止することができると共に、外光散乱を抑制して、黒浮き防止性(明所コントラスト)及び電極パターン非視認性を向上させることができる情報入力装置乃至電子機器を製造することができる。
<3> 前記金属ナノワイヤー本体は、Ag、Au、Ni、Cu、Pd、Pt、Rh、Ir、Ru、Os、Fe、Co、Sn、Al、Tl、Zn、Nb、Ti、In、W、Mo、Cr、Fe、V、Taからなる群から選択される少なくとも1種の元素で構成される前記<2>に記載の金属ナノワイヤーである。
<4> 前記<2>又は<3>に記載の金属ナノワイヤーと、溶剤と、バインダーと、を含むことを特徴とする分散液である。
該<4>に記載の分散液において、前記<2>又は<3>に記載の金属ナノワイヤーと、溶剤と、バインダーと、を含むので、外光散乱を抑制して、黒浮き防止性(明所コントラスト)及び電極パターン非視認性を向上させることができる情報入力装置乃至電子機器を製造することができる。
<5> 前記<2>又は<3>に記載の金属ナノワイヤーを含むことを特徴とする透明導電膜である。
該<5>に記載の透明導電膜において、前記<2>又は<3>に記載の金属ナノワイヤーを含むので、外光散乱を抑制して、黒浮き防止性(明所コントラスト)及び電極パターン非視認性を向上させることができる情報入力装置乃至電子機器を製造することができる。
<6> 前記金属ナノワイヤーが、透明なバインダーに分散されている前記<5>に記載の透明導電膜である。
<7> 反射L値が9以下である前記<5>又は<6>に記載の透明導電膜である。
<8> 前記チオール基含有有色化合物で表面処理されていない金属ナノワイヤー本体をさらに含む前記<5>から<7>のいずれかに記載の透明導電膜である。
<9> 透明基材と、前記透明基材上に設けられた前記<5>から<8>のいずれかに記載の透明導電膜と、を備えることを特徴とする情報入力装置である。
該<9>に記載の情報入力装置において、透明基材と、前記透明基材上に設けられた前記<5>から<8>のいずれかに記載の透明導電膜と、を備えるので、外光散乱を抑制して、黒浮き防止性(明所コントラスト)及び電極パターン非視認性を向上させることができる。
<10> 表示パネルと、前記表示パネル上に設けられた前記<5>から<8>のいずれかに記載の透明導電膜と、を備えることを特徴とする電子機器である。
該<10>に記載の電子機器において、表示パネルと、前記表示パネル上に設けられた前記<5>から<8>のいずれかに記載の透明導電膜と、を備えるので、外光散乱を抑制して、黒浮き防止性(明所コントラスト)及び電極パターン非視認性を向上させることができる。
本発明のチオール基含有有色化合物は、少なくとも、発色団と、チオール基(SH基、メルカプト基、スルフヒドリル基)と、スペーサとを有し、さらに必要に応じて、その他の部位を有する。即ち、前記チオール基含有有色化合物は、発色団の数、チオール基の数が、それぞれ1個に限定されるものではなく、2個以上としてもよい。また、前記チオール基含有有色化合物は、前記その他の部位として、チオール基以外の吸着官能基を1種以上有していてもよい。
前記チオール基含有有色化合物は、可視光領域に吸収を持ち、かつ後述する金属ナノワイヤー本体に吸着する。ここで、本明細書における「可視光領域」とは、およそ360nm以上830nm以下の波長帯域である。
前記チオール基含有有色化合物としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、下記一般式(1)で表わされる化合物、などが挙げられる。
R−W−SH・・・・・・・(1)
(但し、Rは可視光領域に吸収を持つ発色団であり、Wは炭素数2〜30の鎖状アルキレン基又は炭素数3〜30の環状アルキレン基、或いは、前記アルキレン基への付加構造の炭素数が前記アルキレン基の炭素数以下である前記アルキレン基の誘導体である。)
前記発色団Rとしては、可視光領域に吸収を持つものである限り、特に制限はなく、目的に応じて適宜選択することができ、例えば、不飽和アルキル基、芳香族、複素環、金属イオン、などが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
これらの中でも、シアニン、キノン、フェロセン、トリフェニルメタン、キノリンが、透明性が向上した透明導電膜を製造することができる点で好ましい。
また、前記発色団Rの具体例としては、例えば、ニトロソ基、ニトロ基、アゾ基、メチン基、アミノ基、ケトン基、チアゾリル基、ナフトキノン基、インドリン基、スチルベン誘導体、インドフェノール誘導体、ジフェニルメタン誘導体、アントラキノン誘導体、トリアリールメタン誘導体、ジアジン誘導体、インジゴイド誘導体、キサンテン誘導体、オキサジン誘導体、フタロシアニン誘導体、アクリジン誘導体、チアジン誘導体、硫黄原子含有化合物、金属イオン含有化合物、などが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
これらの中でも、Cr錯体、Cu錯体、Co錯体、Ni錯体、Fe錯体、アゾ基、インドリン基が、透明性が向上した透明導電膜を製造することができる点で好ましい。
前記スペーサWは、前記発色団Rと前記チオール基との間に設けられた、炭素数2〜30の鎖状アルキレン基又は炭素数3〜30の環状アルキレン基、或いは、前記アルキレン基への付加構造の炭素数が前記アルキレン基の炭素数以下である前記アルキレン基の誘導体である。なお、前記スペーサWは、チオール基の酸性度が高くならない限り、主鎖に、不飽和結合、エーテル結合、カルボニル結合、エステル結合、アミド結合、ウレタン結合、水素結合、芳香族、及び複素環からなる群から選択される少なくとも1種を有していてもよい。
ここで、前記スペーサWは、前記チオール基含有有色化合物の共役塩基を不安定化させ、チオール基の酸性度を低くする役割を担う。
前記スペーサWは、電子供与性であることが好ましい。これにより、チオール基に電子を供与することができ、もって、チオール基の酸性度を低減させることができる。
前記鎖状アルキレン基としては、炭素数が2〜30である限り、特に制限はなく、目的に応じて適宜選択することができ、例えば、エチレン基、ノルマルプロピレン基、ノルマルブチレン基、ノルマルヘキシレン基等の直鎖状アルキレン基;イソプロピレン基、イソブチレン基、2−メチルプロピレン基等の枝分かれ状アルキレン基;などが挙げられる。
前記鎖状アルキレン基の炭素数としては、2〜30である限り、特に制限はなく、目的に応じて適宜選択することができるが、2〜16が好ましい。
前記環状アルキレン基としては、炭素数3〜30である限り、特に制限はなく、目的に応じて適宜選択することができ、例えば、モノシクロ、ビシクロ、トリシクロ、テトラシクロ、ペンタシクロ構造等を有する基(下記構造式(a)〜(s)で表わされる脂環式部分を有する脂環式脂肪族基)、などを挙げることができる。
前記環状アルキレン基の炭素数としては、3〜30である限り、特に制限はなく、目的に応じて適宜選択することができるが、3〜16が好ましい。
前記アルキレン基の誘導体としては、前述したアルキレン基(炭素数2〜30の鎖状アルキレン基又は炭素数3〜30の環状アルキレン基)への付加構造の炭素数が前記アルキレン基の炭素数以下である限り、特に制限はなく、目的に応じて適宜選択することができ、例えば、2−アミノエチレン基、6−アミノへキシレン基、11−アミノウンデシレン基、16−アミノヘキサデシレン基、アミノプロピレン基、アミノブチレン基、アミノペンチレン基、アミノオクチレン基、などが挙げられる。
なお、4−ピリジンエチレン基(後述する実施例における染料EにおけるスペーサW)は、アルキレン基(エチレン基)への付加構造(4−ピリジン)の炭素数(5)が、アルキレン基(エチレン基)の炭素数(2)以下ではないので、本明細書における「アルキレン基の誘導体」に含まれない。
前記その他の部位としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、チオール基以外の吸着官能基、などが挙げられる。
前記チオール基以外の吸着官能基としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、スルホ基(スルホン酸塩含む)、スルホニル基、スルホンアミド基、カルボン酸基(カルボン酸塩含む)、アミノ基、アミド基、リン酸基(リン酸塩、リン酸エステル含む)、フォスフィノ基、シラノール基、エポキシ基、イソシアネート基、シアノ基、ビニル基、カルビノール基、水酸基、金属ナノワイヤー本体を構成する金属に配位可能な原子(例えば、N(窒素)、S(イオウ)、O(酸素)等)、などが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
前記反応物は、(i)前記酸性基含有染料における、スルホ基、カルボキシル基、スルホン酸塩基、カルボン酸塩基等の酸性基と、(ii)前記塩基性基含有分子におけるアミノ基等の塩基性基とが反応して得られるものである。
前記酸性基含有染料としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、市販の酸性染料、金属錯体塩酸性染料、直接染料、などが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
前記塩基性基含有分子としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、2−アミノエタンチオール、2−アミノエタンチオール塩酸塩、2−ジメチルアミノエタンチオール塩酸塩、2−(ジエチルアミノ)エタンチオール塩酸塩、2−ジイソプロピルアミノエタンチオール塩酸塩、4−ピリジンエタンチオール塩酸塩、6−アミノ−1−ヘキサンチオール塩酸塩、8−アミノ−1−オクタンチオール塩酸塩、11−アミノ−1−ウンデカンチオール塩酸塩、16−アミノ−1−ヘキサデカンチオール塩酸塩、アミノ−EG6−ウンデカンチオール塩酸塩、アミノ−EG6−ヘキサデカンチオール塩酸塩、などが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
前記反応物は、(i)前記塩基性基含有染料におけるアミノ基等の塩基性基と、(ii)前記酸性基含有分子における、スルホ基、カルボキシル基、スルホン酸塩基、カルボン酸塩基等の酸性基とが反応して得られるものである。
前記塩基性基含有染料としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、市販のカチオン染料、などが挙げられる。
前記酸性基含有分子としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、2−メルカプトエタンスルホン酸ナトリウム、3−メルカプト−1−プロパンスルホン酸ナトリウム、2,3−ジメルカプトプロパンスルホン酸ナトリウム、4−[(5−メルカプト−1,3,4−チアジアゾール−2−イル)チオ]−1−ブタンスルホン酸ナトリウム、メルカプト酢酸ナトリウム、2−(5−メルカプト−1H−テトラゾール−1−イル)酢酸ナトリウム、5−カルボキシ−1−ペンタンチオール、7−カルボキシ−1−ヘプタンチオール、10−カルボキシ−1−デカンチオール、15−カルボキシ−1−ペンタデカンチオール、カルボキシ−EG6−ウンデカンチオール、カルボキシ−EG6−ヘキサデカンチオール、などが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
前記反応物は、(i)前記反応性基含有染料における、スルファートエチルスルホニル基、ビニルスルホニル基、モノクロロトリアジニル基、モノフルオロトリアジニル基、モノピリジニオトリアジニル基、ジクロロトリアジニル基、ジフルオロモノクロロピリミジニル基、トリクロロピリミジニル基等の反応性基と、(ii)前記水酸基含有分子における水酸基とが反応して得られるものである。
前記反応性基含有染料としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、市販の反応染料、などが挙げられる。
前記水酸基含有分子としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、2−メルカプトエタノール、3−メルカプト−1−プロパノール、1−メルカプト−2−プロパノール、4−メルカプト−1−ブタノール、6−メルカプト−1−ヘキサノール、3−メルカプト−1−ヘキサノール、8−メルカプト−1−オクタノール、9−メルカプト−1−ノナノール、11−メルカプト−1−ウンデカノール、1−チオグリセロール、などが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
本発明の金属ナノワイヤーは、金属ナノワイヤー本体(金属フィラー)を有し、該金属ナノワイヤー本体の表面の少なくとも一部が、本発明のチオール基含有有色化合物で表面処理されたものである。
ここで、「有色化合物で表面処理された」とは、「有色化合物が金属ナノワイヤー本体に接触(吸着)していること(例えば、図1参照)」を意味する。また、前記有色化合物(染料)は、凝集した状態で金属ナノワイヤーに接触(吸着)していてもよい。
図1は、本発明の金属ナノワイヤーを説明するための模式図である。
図1において、金属ナノワイヤー1における金属ナノワイヤー本体2の表面2aの少なくとも一部は、有色化合物(染料)3により被覆(表面処理)されている。これにより、金属ナノワイヤー本体2の表面2aの少なくとも一部に被覆された有色化合物(染料)3に可視光が吸収され、金属ナノワイヤー本体2の表面2aでの光の乱反射が防止される。
前記金属ナノワイヤー本体は、金属を用いて構成されたものであって、nmオーダーの径を有する微細なワイヤーである。
これらの中でも、AgやCuが、導電性が高い点で、好ましい。
前記金属ナノワイヤー本体の平均短軸径が、1nm以下であると、金属ナノワイヤー本体の導電率が劣化して、該金属ナノワイヤー本体が表面処理された金属ナノワイヤーを含む透明導電膜が導電膜として機能しにくいことがあり、500nm超であると、前記金属ナノワイヤー本体が表面処理された金属ナノワイヤーを含む透明導電膜の全光線透過率やヘイズ(Haze)が劣化することがある。一方、前記金属ナノワイヤー本体の平均短軸径が前記より好ましい範囲内であると、前記金属ナノワイヤー本体が表面処理された金属ナノワイヤーを含む透明導電膜の導電性が高く、且つ透明性が高い点で有利である。
前記金属ナノワイヤー本体の平均長軸長としては、特に制限はなく、目的に応じて適宜選択することができるが、1μm超且つ1000μm以下が好ましく、10μm〜300μmがより好ましい。
前記金属ナノワイヤー本体の平均長軸長が、1μm以下であると、金属ナノワイヤー本体同士がつながりにくく、該金属ナノワイヤー本体が表面処理された金属ナノワイヤーを含む透明導電膜が導電膜として機能しにくいことがあり、1000μm超であると、前記金属ナノワイヤー本体が表面処理された金属ナノワイヤーを含む透明導電膜の全光線透過率やヘイズ(Haze)が劣化したり、透明導電膜を形成する際に用いる分散液における金属ナノワイヤー本体が表面処理された金属ナノワイヤーの分散性が劣化することがある。一方、前記金属ナノワイヤー本体の平均長軸長が前記より好ましい範囲内であると、前記金属ナノワイヤー本体が表面処理された金属ナノワイヤーを含む透明導電膜の導電性が高く、且つ透明性が高い点で有利である。
なお、金属ナノワイヤー本体の平均短軸径及び平均長軸長は、走査型電子顕微鏡により測定可能な、数平均短軸径及び数平均長軸長である。より具体的には、金属ナノワイヤー本体を少なくとも100本以上測定し、電子顕微鏡写真から画像解析装置を用いて、それぞれのナノワイヤーの投影径及び投影面積を算出する。投影径を、短軸径とした。また、下記式に基づき、長軸長を算出した。
長軸長=投影面積/投影径
平均短軸径は、短軸径の算術平均値とした。平均長軸長は、長軸長の算術平均値とした。
さらに、前記金属ナノワイヤー本体は、金属ナノ粒子が数珠状に繋がってワイヤー形状を有しているものでもよい。この場合、長さは限定されない。
前記金属ナノワイヤー本体の目付量が、0.001g/m2未満であると、金属ナノワイヤー本体が十分に金属ナノワイヤー層中に存在せず、透明導電膜の導電性が劣化することがあり、目付量が1.000g/m2超であると、透明導電膜の全光線透過率やヘイズ(Haze)が劣化することがある。一方、前記金属ナノワイヤー本体の目付量が前記より好ましい範囲内であると、透明導電膜の導電性が高く、且つ透明性が高い点で有利である。
前記金属ナノワイヤーは、金属ナノワイヤー本体分散溶液とチオール基含有有色化合物(染料)分散溶液とを混合することによって得られる。より詳細には、金属ナノワイヤー本体分散溶液とチオール基含有有色化合物(染料)分散溶液とを混合し、その後、室温〜100℃にて1分間〜48時間攪拌を行いながら、金属ナノワイヤー本体へのチオール基含有有色化合物(染料)の吸着(表面処理)を行う。また、表面処理を行った後、遠心分離やフィルタリング等を活用して、未吸着のチオール基含有有色化合物(染料)を除去する操作を行ってもよい。
前記金属ナノワイヤー本体分散溶液は、少なくとも、金属ナノワイヤー本体と、溶剤とを含有してなり、必要に応じて、分散剤、界面活性剤等のその他の成分を含有してなる。
前記溶剤は、特に制限はなく、金属ナノワイヤー本体を所定濃度に分散可能な材料を適宜選択することができ、例えば、本発明の分散液の説明で後述するものが挙げられる。
また、前記金属ナノワイヤー本体は、前述した通りであり、前記分散剤は、本発明の分散液の説明で後述するものと同様である。
前記チオール基含有有色化合物(染料)分散溶液は、少なくとも、チオール基含有有色化合物(染料)と、溶剤とを含有してなり、必要に応じて、分散剤、界面活性剤等のその他の成分を含有してなる。
前記溶剤は、特に制限はなく、チオール基含有有色化合物(染料)を所定濃度に溶解可能及び/又は分散可能で、且つ、金属ナノワイヤー分散溶液の溶媒と相溶する材料を適宜選択することができ、例えば、水、アセトニトリル、3−メトキシプロピオニトリル、3,3−ジメトキシプロピオニトリルエトキシプロピオニトリル、3−エトキシプロピオニトリル、3,3’−オキシジプロピオニトリル、3−アミノプロピオニトリル、プロピオニトリル、シアノ酢酸プロピル、イソチオシアン酸3−メトキシプロピル、3−フェノキシプロピオニトリル、p−アニシジン3−(フェニルメトキシ)プロパンニトリル、メタノール、エタノール、プロパノール、イソプロピルアルコール、n−ブタノール、2−ブタノール、イソブタノール、t−ブタノール、エチレングリコール、トリエチレングリコール、1−メトキシ−エタノール、1,1−ジメチル−2−メトキシエタノール、3−メトキシ−1−プロパノール、ジメチルスルホキシド、ベンゼン、トルエン、o−キシレン、m−キシレン、p−キシレン、クロロベンゼン、ジクロロベンゼン、酢酸ブチル、酢酸エチル、ヘキサン、シクロヘキサン、シクロヘキサノン、エチルメチルケトン、アセトン、ジメチルホルムアミド、などが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。なお、「チオール基含有有色化合物(染料)が分散」とは、「チオール基含有有色化合物(染料)が凝集体として分散」している状態も含むことを意味する。
また、前記溶剤は、後述する分散液におけるバインダーを膨潤しない溶媒を選択することが好ましい。バインダーを膨潤する溶剤を使用すると、バインダー中にチオール基含有化合物(染料)が取り込まれ過ぎてしまい、透明導電膜の透明性が損なわれることがあるからである。
また、前記チオール基含有有色化合物(染料)は、前述した通りであり、前記分散剤は、本発明の分散液の説明で後述するものと同様である。
前記チオール基含有有色化合物(染料)分散溶液におけるチオール基含有有色化合物(染料)の濃度としては、特に制限はなく、目的に応じて適宜選択することができるが、金属ナノワイヤー本体に対するチオール基含有有色化合物(染料)の吸着速度を向上させる観点から、0.01質量%以上が好ましい。
本発明の分散液は、少なくとも、本発明の金属ナノワイヤーと、溶剤と、バインダーとを含有してなり、さらに必要に応じて、分散剤、その他の添加剤、などを含有してなる。
ここで、本発明の金属ナノワイヤーは、前述した通り、金属ナノワイヤー本体を有し、該金属ナノワイヤー本体の表面の少なくとも一部が、本発明のチオール基含有有色化合物(染料)で表面処理されたものである。ここで、前記チオール基含有有色化合物(染料)は、凝集した状態で金属ナノワイヤーに吸着していてもよい。
なお、後述する本発明の透明導電膜を製造するために用いられる分散液として、上記「本発明の金属ナノワイヤーと、溶剤と、バインダーとを含有する分散液」を用いる代わりに、「金属ナノワイヤー本体と、バインダーと、溶剤とを含む分散液」と「チオール基含有有色化合物(染料)分散溶液」とを併用してもよい。ここで、金属ナノワイヤー本体、チオール基含有有色化合物(染料)、は前述した通りである。
さらに、後述する本発明の透明導電膜を製造するために用いられる分散液として、上記「本発明の金属ナノワイヤーと、溶剤と、バインダーとを含有する分散液」を用いる代わりに、「金属ナノワイヤー本体と、チオール基含有有色化合物(染料)と、バインダーと、溶剤とを含む分散液」を用いてもよい。ここで、金属ナノワイヤー本体、チオール基含有有色化合物(染料)、は前述した通りである。
前記金属ナノワイヤーにおける金属ナノワイヤー本体の配合量が、0.01質量部未満であると、最終的に得られる透明導電膜において金属ナノワイヤー本体に十分な目付量(0.001〜1.000[g/m2])が得られないことがあり、10.00質量部超であると、金属ナノワイヤーの分散性が劣化することがある。
前記バインダーは、金属ナノワイヤー、及び/又は、金属ナノワイヤー本体を分散させるものである。
前記バインダーとしては、特に制限はなく、目的に応じて適宜選択することができ、例えば、既知の透明な、天然高分子樹脂、合成高分子樹脂、などが挙げられ、熱可塑性樹脂であってもよく、また、熱、光、電子線、放射線で硬化する熱(光)硬化性樹脂であってもよい。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
前記熱可塑性樹脂としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、ポリ塩化ビニル、塩化ビニル−酢酸ビニル共重合体、ポリメチルメタクリレート、ニトロセルロース、塩素化ポリエチレン、塩素化ポリプロピレン、フッ化ビニリデン、エチルセルロース、ヒドロキシプロピルメチルセルロース、ヒドロキシプロピルセルロース、ポリビニルアルコール、ポリビニルピロリドン、などが挙げられる。
前記熱(光)硬化性樹脂としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、メラミンアクリレート、ウレタンアクリレート、イソシアネート、エポキシ樹脂、ポリイミド樹脂、アクリル変性シリケート等のシリコン樹脂、アジド基やジアジリン基などの感光基を主鎖及び側鎖の少なくともいずれかに導入したポリマー、などが挙げられる。
前記溶剤としては、金属ナノワイヤー、及び/又は、金属ナノワイヤー本体が分散するものである限り、特に制限はなく、目的に応じて適宜選択することができ、例えば、水;メタノール、エタノール、n−プロパノール、i−プロパノール、n−ブタノール、i−ブタノール、sec−ブタノール、tert−ブタノール等のアルコール;シクロヘキサノン、シクロペンタノン等のアノン;N,N−ジメチルホルムアミド(DMF)等のアミド;ジメチルスルホキシド(DMSO)等のスルフィド;などが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
前記高沸点溶剤としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、ブチルセロソルブ、ジアセトンアルコール、ブチルトリグリコール、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、エチレングリコールモノエチルエーテル、エチレングリコールモノプロピルエーテル、エチレングリコールモノイソプロピルエーテル、ジエチレングリコールモノブチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノメチルエーテルジエチレングリコールジエチルエーテル、ジプロピレングリコールモノメチルエーテル、トリプロピレングリコールモノメチルエーテル、プロピレングリコールモノブチルエーテル、プロピレングリコールイソプロピルエーテル、ジプロピレングリコールイソプロピルエーテル、トリプロピレングリコールイソプロピルエーテル、メチルグリコール、などが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
前記分散剤としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、ポリビニルピロリドン(PVP);ポリエチレンイミン等のアミノ基含有化合物;スルホ基(スルホン酸塩含む)、スルホニル基、スルホンアミド基、カルボン酸基(カルボン酸塩含む)、アミド基、リン酸基(リン酸塩、リン酸エステル含む)、フォスフィノ基、シラノール基、エポキシ基、イソシアネート基、シアノ基、ビニル基、チオール基、カルビノール基等の官能基を有する化合物で金属に吸着可能なもの;などが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
前記分散剤を、前記金属ナノワイヤー又は前記金属ナノワイヤー本体の表面に吸着させてもよい。これにより、前記金属ナノワイヤー又は前記金属ナノワイヤー本体の分散性を向上させることができる。
前記その他の添加剤としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、増粘剤、界面活性剤、などが挙げられる。
本発明の透明導電膜は、少なくとも、本発明の金属ナノワイヤー(即ち、(i)金属ナノワイヤー本体と、(ii)前記金属ナノワイヤー本体に吸着されたチオール基含有有色化合物と)を含んでなり、さらに必要に応じて、その他の成分を含有してなる。
また、本発明の透明導電膜は、チオール基含有有色化合物で表面処理されていない金属ナノワイヤー本体を含んでいてもよい。ここで「チオール基含有有色化合物で表面処理されていない金属ナノワイヤー本体」とは、「全く表面処理されていない金属ナノワイヤー本体」及び/又は「本発明のチオール基含有有色化合物以外の化合物で表面処理された金属ナノワイヤー本体」を意味する。
前記基材としては、特に制限はなく、目的に応じて適宜選択することができるが、無機材料、プラスチック材料等の可視光に対して透過性を有する材料で構成された透明基材が好ましい。前記透明基材は、透明導電膜を有する透明電極に必要とされる膜厚を有しており、例えばフレキシブルな屈曲性を実現できる程度に薄膜化されたフィルム状(シート状)、または適度の屈曲性と剛性を実現できる程度の膜厚を有する基板状であることとする。
前記無機材料としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、石英、サファイア、ガラス、などが挙げられる。
前記プラスチック材料としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、トリアセチルセルロース(TAC)、ポリエステル(TPEE)、ポリエチレンテレフタレート(PET)、ポリエチレンナフタレート(PEN)、ポリイミド(PI)、ポリアミド(PA)、アラミド、ポリエチレン(PE)、ポリアクリレート、ポリエーテルスルフォン、ポリスルフォン、ポリプロピレン(PP)、ジアセチルセルロース、ポリ塩化ビニル、アクリル樹脂(PMMA)、ポリカーボネート(PC)、エポキシ樹脂、尿素樹脂、ウレタン樹脂、メラミン樹脂、シクロオレフィンポリマー(COP)、などの公知の高分子材料が挙げられる。斯かるプラスチック材料を用いて透明基材を構成した場合、生産性の観点から透明基材の膜厚を5μm〜500μmとすることが好ましいが、この範囲に特に限定されるものではない。
前記オーバーコート層は、可視光に対して光透過性を有していることが重要であり、ポリアクリル系樹脂、ポリアミド系樹脂、ポリエステル系樹脂、又は、セルロース系樹脂で構成されるか、或いは、金属アルコキシドの加水分解、脱水縮合物などで構成される。またこのようなオーバーコート層は、可視光に対する光透過性が阻害されることのない膜厚で構成されていることとする。前記オーバーコート層が、ハードコート機能、防眩機能、反射防止機能、アンチニュートンリング機能、及びアンチブロッキング機能などからなる機能群より選ばれる少なくとも1種の機能を有していてもよい。
前記アンカー層としては、基材とバインダー層とをより強固に接着可能なものである限り、特に制限はなく、目的に応じて適宜選択することができる。
−−第1実施形態−−
以下、本発明の透明導電膜を製造する方法の第1実施形態を説明する。
本発明の透明導電膜を製造する方法は、少なくとも、分散膜形成工程と、硬化工程と、表面処理工程を含み、さらに、必要に応じて適宜選択した、カレンダー工程、リンス乾燥工程、オーバーコート層形成工程、パターン電極形成工程、その他の工程を含む。
本発明の透明導電膜を製造する方法の第1実施形態は、例えば、分散膜形成工程、硬化工程、カレンダー工程、表面処理工程、リンス乾燥工程の順で行われる。
前記分散膜形成工程は、金属ナノワイヤー本体と、バインダーと、溶剤とを含む分散液を用いて基材上に分散膜(金属ナノワイヤー膜)を形成する工程である。
前記金属ナノワイヤー本体、前記バインダー、前記溶剤は、いずれも、本発明の分散液の説明で前述した通りである。
前記分散膜の形成方法としては、特に制限はなく、目的に応じて適宜選択することができるが、物性、利便性、製造コスト等の点で、湿式製膜法が好ましい。
前記湿式製膜法としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、塗布法、スプレー法、印刷法、などの公知の方法が挙げられる。
前記塗布法としては、特に限定されるものではなく、目的に応じて適宜選択することができ、例えば、マイクログラビアコート法、ワイヤーバーコート法、ダイレクトグラビアコート法、ダイコート法、ディップ法、スプレーコート法、リバースロールコート法、カーテンコート法、コンマコート法、ナイフコート法、スピンコート法、などが挙げられる。
前記スプレー法としては、特に制限はなく、目的に応じて適宜選択することができる。
前記印刷法としては、特に限定されるものではなく、目的に応じて適宜選択することができ、例えば、凸版印刷、オフセット印刷、グラビア印刷、凹版印刷、ゴム版印刷、スクリーン印刷、インクジェット印刷、などが挙げられる。
前記硬化工程は、前記基材上に形成された分散膜を硬化させて、硬化物(図7における金属ナノワイヤー本体2を含有するバインダー層31)を得る工程である。
前記硬化工程において、まず、前記基材上に形成された分散膜中の溶剤を乾燥させて除去する。乾燥による溶剤の除去は、自然乾燥及び加熱乾燥のいずれであってもよい。乾燥後、未硬化のバインダーの硬化処理を行い、硬化させたバインダー中に金属ナノワイヤーを分散させた状態とする。ここで、前記硬化処理は、加熱及び/又は活性エネルギー線照射により行うことができる。
前記表面処理工程は、(i)図8に示すように、前記分散膜を硬化させて得られた硬化物70を、チオール基含有有色化合物(染料)3と溶剤とを含む有色化合物(染料)分散溶液80に浸漬する、又は、(ii)前記分散膜を硬化させて得られた硬化物に、チオール基含有有色化合物(染料)3と溶剤とを含む有色化合物(染料)分散溶液を塗布乃至印刷する工程である。
これにより、図9に示すように、硬化させたバインダー層31中に分散した金属ナノワイヤー本体2に、有色化合物(染料)分散溶液中のチオール基含有有色化合物(染料)3を吸着させた金属ナノワイヤーを含む層を形成する。ここでは、金属ナノワイヤー本体2のバインダー層31からの露出部分が優先的に表面処理される。このような表面処理では、有色化合物(染料)分散溶液中のチオール基含有有色化合物(染料)3と金属ナノワイヤー本体2を構成する金属材料とを、化学吸着(共有結合、配位結合、イオン結合、或いは水素結合)させる。
前記印刷方式を適用する場合、例えば、凸版印刷法、オフセット印刷法、グラビア印刷法、凹版印刷法、ゴム版印刷法、インクジェット法、及びスクリーン印刷法などから適宜の方法を選択し、分散膜上に有色化合物(染料)分散溶液の液膜を形成する。
前記カレンダー処理は、(i)前記硬化工程と前記表面処理工程との間、(ii)前記リンス乾燥工程の後、又は、(iii)前記オーバーコート層形成工程の後、に行われる工程であって、表面の平滑性を向上させたり、表面に光沢をつける工程である。
斯かるカレンダー処理を行うことにより、得られる透明導電膜のシート抵抗値を下げることができる。
前記リンス乾燥工程は、前記表面処理工程の後に、前記表面処理した硬化物を所定の溶媒でリンスし、その後乾燥処理する工程である。これにより、基材上に形成された、金属ナノワイヤーを含む透明導電膜の製造を完了する。なお、前記乾燥処理は、自然乾燥及び加熱乾燥のいずれであってもよい。
前記オーバーコート層形成工程は、分散液の硬化物が形成された後に、前記硬化物上にオーバーコート層を形成する工程である。前記オーバーコート層形成工程は、リンス乾燥後に行ってもよい。
前記オーバーコート層は、例えば、前記硬化物上に、所定の材料を含むオーバーコート層形成用塗布液を塗布して、硬化させることにより形成することができる。
前記パターン電極形成工程は、前記リンス乾燥工程の後に、公知のフォトリソグラフィープロセスを適用して、パターン電極を形成する工程である。これにより、本発明の透明導電膜を静電容量タッチパネル用センサー電極に適用させることができる。なお、前記硬化工程における硬化処理が活性エネルギー線照射を含む場合、前記硬化処理をマスク露光/現像としてパターン電極を形成してもよい。
以下、本発明の透明導電膜を製造する方法の第2実施形態を説明する。ここで、本発明の透明導電膜を製造する方法の第1実施形態の説明と重複する部分は省略する。
本発明の透明導電膜を製造する方法は、少なくとも、分散膜形成工程と、硬化工程とを含み、さらに、必要に応じて適宜選択した、カレンダー工程、オーバーコート層形成工程、パターン電極形成工程、その他の工程を含む。
本発明の透明導電膜の製造方法の第2実施形態は、例えば、分散膜形成工程、硬化工程、カレンダー工程の順で行われる。
前記分散膜形成工程は、(i)金属ナノワイヤーと、バインダーと、溶剤とを含む分散液、又は、(ii)チオール基含有有色化合物(染料)と、金属ナノワイヤー本体と、バインダーと、溶剤とを含む分散液を用いて基材上に分散膜を形成する工程である。
前記金属ナノワイヤー、前記チオール基含有有色化合物(染料)、前記金属ナノワイヤー本体、前記バインダー、前記溶剤は、いずれも、本発明の分散液の説明で前述した通りである。
前記硬化工程は、前記基材上に形成された分散膜を硬化させて、硬化物を得る工程である。
前記カレンダー工程は、(i)前記硬化工程後、又は、(ii)前記オーバーコート層形成工程の後に行われる工程である。
前記オーバーコート層形成工程は、分散膜の硬化物が形成された後に、前記硬化物上にオーバーコート層を形成する工程である。
前記パターン電極形成工程は、透明導電膜を基材上に形成した後、公知のフォトリソグラフィープロセスを適用して、パターン電極を形成する工程である。これにより、本発明の透明導電膜を静電容量タッチパネル用センサー電極に適用させることができる。なお、前記硬化工程における硬化処理が活性エネルギー線照射を含む場合、前記硬化処理をマスク露光/現像としてパターン電極を形成してもよい。
本発明の情報入力装置は、少なくとも、公知の透明基材と、本発明の透明導電膜とを備え、さらに必要に応じて、その他の公知の部材(例えば、特許第4893867号参照)を備える。
前記情報入力装置としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、特許第4893867号に示されるような、タッチパネル、などが挙げられる。
本発明の電子機器は、少なくとも、公知の表示パネルと、本発明の透明導電膜とを備え、さらに必要に応じて、その他の公知の部材(例えば、特許第4893867号参照)を備える。
前記電子機器としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、特許第4893867号に示されるような、テレビ、デジタルカメラ、ノート型パーソナルコンピュータ、ビデオカメラ、携帯端末装置、などが挙げられる。
金属錯体塩酸性染料Lanyl Black BG E/C(下記構造式(1)、株式会社岡本染料店製)の水溶液100mL(濃度:0.00564モル/L)に対して、2モル当量の2−アミノエタンチオール塩酸塩(下記構造式(2))水溶液100mLを加えた。混合後、超音波を1時間〜2時間照射し、約12時間静置した。その後、ろ過により固体を回収し、この固体を純水で洗浄後、真空乾燥することで、黒色の染料Aを合成した。
合成例1において、2−アミノエタンチオール塩酸塩(上記構造式(2))を用いる代わりに、6−アミノ−1−ヘキサンチオール塩酸塩(下記構造式(3))を用いたこと以外は、合成例1と同様にして、黒色の染料Bを合成した。
合成例1において、2−アミノエタンチオール塩酸塩(上記構造式(2))を用いる代わりに、11−アミノ−1−ウンデカンチオール塩酸塩(下記構造式(4))を用いたこと以外は、合成例1と同様にして、黒色の染料Cを合成した。
合成例1において、2−アミノエタンチオール塩酸塩(上記構造式(2))を用いる代わりに、16−アミノ−1−ヘキサデカンチオール塩酸塩(下記構造式(5))を用いたこと以外は、合成例1と同様にして、黒色の染料Dを合成した。
合成例1において、2−アミノエタンチオール塩酸塩(上記構造式(2))を用いる代わりに、4−ピリジンエタンチオール塩酸塩(下記構造式(6))を用いたこと以外は、合成例1と同様にして、黒色の染料Eを合成した。
合成例1において、2モル当量の2−アミノエタンチオール塩酸塩(上記構造式(2))を用いる代わりに、1モル当量の2,5−ジアミノ−1,4−ベンゼンジチオール二塩酸塩(下記構造式(7))を用いたこと以外は、合成例1と同様にして、黒色の染料Fを合成した。
<銀ナノワイヤーインク(分散液)の作製>
下記の配合にて、銀ナノワイヤーインクを作製した。
(1)金属ナノワイヤー:銀ナノワイヤー(Seashell Technology社製、AgNW−25、平均径25nm、平均長さ23μm):配合量0.065質量部
(2)バインダー:水溶性感光性樹脂(東洋合成工業株式会社製、BIOSURFINE−AWP):配合量0.13質量部
(3)溶媒:(i)水:配合量89.805質量部、(ii)1−プロパノール:配合量10質量部
<銀ナノワイヤー透明電極(銀ナノワイヤー透明導電膜)の作製>
以下の手順で、銀ナノワイヤー透明電極を作製した。
まず、作製した銀ナノワイヤーインク(分散液)を、コイルバー(番手10)で透明基材(PET:東レ株式会社製、U34、膜厚125μm)上に塗布して銀ナノワイヤー分散膜を形成した。ここで、銀ナノワイヤーの目付量を約0.015g/m2とした。
次いで、大気中において、塗布面にドライヤーで温風をあて、銀ナノワイヤー分散膜中の溶媒を乾燥除去した。
その後、メタルハライドランプを用いて、大気中にて透明導電膜(銀ナノワイヤー層)側から積算光量200mJ/cm2で紫外線を照射して、バインダーを硬化させた。
その後、円柱状のプレスロール及びバックロールを備えるカレンダー処理装置(図14参照)を使用して、カレンダー処理(ニップ幅1mm、荷重4kN、速度1m/min)を行った。
シート抵抗を、銀ナノワイヤー分散膜表面に、手動式非破壊抵抗測定器(ナプソン株式会社製、EC−80P)の測定プローブを接触させて、透明導電膜(銀ナノワイヤー層)表面上の任意の3箇所で測定を行い、その平均値をシート抵抗とした。シート抵抗は、100Ω/□であった。
合成例1で合成した染料Aの0.2質量%エタノール溶液を調製した。このエタノール溶液に、比較例1で作製した銀ナノワイヤー透明電極を80℃で30分間浸漬した。その後、銀ナノワイヤー透明電極を取り出し、エタノールでリンスし、エアブローで乾燥させ、染料Aで表面処理された銀ナノワイヤー透明電極を作製した。さらに、比較例1と同様に、シート抵抗値を測定した(表1)。
実施例1において、合成例1で合成した染料Aを用いる代わりに、合成例2で合成した染料Bを用いたこと以外は、実施例1と同様にして、染料Bで表面処理された銀ナノワイヤー透明電極を作製し、シート抵抗値を測定した(表1)。
実施例1において、合成例1で合成した染料Aを用いる代わりに、合成例3で合成した染料Cを用いたこと以外は、実施例1と同様にして、染料Cで表面処理された銀ナノワイヤー透明電極を作製し、シート抵抗値を測定した(表1)。
実施例1において、合成例1で合成した染料Aを用いる代わりに、合成例4で合成した染料Dを用いたこと以外は、実施例1と同様にして、染料Dで表面処理された銀ナノワイヤー透明電極を作製し、シート抵抗値を測定した(表1)。
実施例1において、合成例1で合成した染料Aを用いる代わりに、合成例5で合成した染料Eを用いたこと以外は、実施例1と同様にして、染料Eで表面処理された銀ナノワイヤー透明電極を作製し、シート抵抗値を測定した(表1)。
実施例1において、合成例1で合成した染料Aを用いる代わりに、合成例6で合成した染料Fを用いたこと以外は、実施例1と同様にして、染料Fで表面処理された銀ナノワイヤー透明電極を作製し、シート抵抗値を測定した(表1)。
<銀ナノワイヤーインク(分散液)の作製>
下記の配合にて、銀ナノワイヤーインクを作製した。
(1)金属ナノワイヤー:銀ナノワイヤー(Seashell Technology社製、AgNW−25、平均径25nm、平均長さ23μm):配合量0.045質量部
(2)バインダー:ヒドロキシプロピルメチルセルロース(アルドリッチ社製、2%水溶液の20℃における粘度80cP〜120cP(文献値)):配合量0.09質量部
(3)架橋剤:有機チタン化合物(マツモトファインケミカル株式会社製、オルガチックスTC−400):配合量0.009質量部
(4)溶媒:(i)水:配合量88.965質量部、(ii)1−プロパノール:配合量10質量部、(iii)イソプロパノール:配合量0.891質量部
<銀ナノワイヤー透明電極の作製>
以下の手順で、銀ナノワイヤー透明電極を作製した。
まず、作製した銀ナノワイヤーインク(分散液)を、コイルバー(番手10)で透明基材(PET:東レ株式会社製、U34、膜厚125μm)上に塗布して銀ナノワイヤー分散膜を形成した。ここで、銀ナノワイヤーの目付量を約0.01g/m2とした。
次いで、大気中において、塗布面にドライヤーで温風をあて、銀ナノワイヤー分散膜中の溶媒を乾燥除去した。
その後、オーブン中で120℃5分間の加熱硬化処理を行った。
その後、円柱状のプレスロール及びバックロールを備えるカレンダー処理装置(図14参照)を使用して、カレンダー処理(ニップ幅1mm、荷重4kN、速度1m/min)を行った。
シート抵抗を、銀ナノワイヤー分散膜表面に、手動式非破壊抵抗測定器(ナプソン株式会社製、EC−80P)の測定プローブを接触させて、透明導電膜(銀ナノワイヤー層)表面上の任意の3箇所で測定を行い、その平均値をシート抵抗とした。シート抵抗は、100Ω/□であった。
合成例1で合成した染料Aの0.2質量%エタノール溶液を調製した。このエタノール溶液に、比較例4で作製した銀ナノワイヤー透明電極を80℃で30分間浸漬した。その後、銀ナノワイヤー透明電極を取り出し、エタノールでリンスし、エアブローで乾燥させ、染料Aで表面処理された銀ナノワイヤー透明電極を作製した。さらに、比較例4と同様に、シート抵抗値を測定した(表1)。
実施例5において、合成例1で合成した染料Aを用いる代わりに、合成例2で合成した染料Bを用いたこと以外は、実施例5と同様にして、染料Bで表面処理された銀ナノワイヤー透明電極を作製し、シート抵抗値を測定した(表1)。
実施例5において、合成例1で合成した染料Aを用いる代わりに、合成例3で合成した染料Cを用いたこと以外は、実施例5と同様にして、染料Cで表面処理された銀ナノワイヤー透明電極を作製し、シート抵抗値を測定した(表1)。
実施例5において、合成例1で合成した染料Aを用いる代わりに、合成例4で合成した染料Dを用いたこと以外は、実施例5と同様にして、染料Dで表面処理された銀ナノワイヤー透明電極を作製し、シート抵抗値を測定した(表1)。
実施例5において、合成例1で合成した染料Aを用いる代わりに、合成例5で合成した染料Eを用いたこと以外は、実施例5と同様にして、染料Eで表面処理された銀ナノワイヤー透明電極を作製し、シート抵抗値を測定した(表1)。
実施例5において、合成例1で合成した染料Aを用いる代わりに、合成例6で合成した染料Fを用いたこと以外は、実施例5と同様にして、染料Fで表面処理された銀ナノワイヤー透明電極を作製し、シート抵抗値を測定した(表1)。
<銀ナノワイヤーインク(分散液)の作製>
下記の配合にて、銀ナノワイヤーインクを作製した。
(1)金属ナノワイヤー:銀ナノワイヤー(Seashell Technology社製、AgNW−25、平均径25nm、平均長さ23μm):配合量0.05質量部
(2)染料:合成例1で合成した染料A:配合量0.015質量部
(3)バインダー:ヒドロキシプロピルメチルセルロース(アルドリッチ社製、2%水溶液の20℃における粘度80cP〜120cP(文献値)):配合量0.1質量部
(3)架橋剤:有機チタン化合物(マツモトファインケミカル株式会社製、オルガチックスTC−400):配合量0.01質量部
(4)溶媒:(i)水:配合量88.835質量部、(ii)1−プロパノール:配合量10質量部、(iii)イソプロパノール:配合量0.99質量部
<銀ナノワイヤー透明電極の作製>
以下の手順で、銀ナノワイヤー透明電極を作製した。
まず、作製した銀ナノワイヤーインク(分散液)を、コイルバー(番手10)で透明基材(PET:東レ株式会社製、U34、膜厚125μm)上に塗布して銀ナノワイヤー分散膜を形成した。ここで、銀ナノワイヤーの目付量を約0.011g/m2とした。
次いで、大気中において、塗布面にドライヤーで温風をあて、銀ナノワイヤー分散膜中の溶媒を乾燥除去した。
その後、オーブン中で120℃5分間の加熱硬化処理を行った。
その後、円柱状のプレスロール及びバックロールを備えるカレンダー処理装置(図14参照)を使用して、カレンダー処理(ニップ幅1mm、荷重4kN、速度1m/min)を行った。
シート抵抗を、銀ナノワイヤー分散膜表面に、手動式非破壊抵抗測定器(ナプソン株式会社製、EC−80P)の測定プローブを接触させて、透明導電膜(銀ナノワイヤー層)表面上の任意の3箇所で測定を行い、その平均値をシート抵抗とした。シート抵抗は、90Ω/□であった。
実施例9において、合成例1で合成した染料Aを用いる代わりに、合成例2で合成した染料Bを用いたこと以外は、実施例9と同様にして、染料Bで表面処理された銀ナノワイヤー透明電極を作製し、シート抵抗値を測定した(表1)。
実施例9において、合成例1で合成した染料Aを用いる代わりに、合成例3で合成した染料Cを用いたこと以外は、実施例9と同様にして、染料Cで表面処理された銀ナノワイヤー透明電極を作製し、シート抵抗値を測定した(表1)。
実施例9において、合成例1で合成した染料Aを用いる代わりに、合成例4で合成した染料Dを用いたこと以外は、実施例9と同様にして、染料Dで表面処理された銀ナノワイヤー透明電極を作製し、シート抵抗値を測定した(表1)。
以上の実施例1〜12及び比較例1〜6で作製した透明電極について、A)反射L値の評価、B)黒浮きの評価、C)電極パターン非視認性の評価を行った。各評価は、次のように行った。
得られた透明電極について、透明導電膜(銀ナノワイヤー層)側に黒色のビニールテープ(ニチバン株式会社製VT−50)を貼合し、透明導電膜(銀ナノワイヤー層)とは反対側から、JIS Z8722に従い、エックスライト社製カラーi5で評価した。任意の3箇所で測定を行い、その平均値を反射L値とした。
実施例1〜8及び比較例2、3、5及び6で得られた透明電極について、表面処理を施した部分(処理部)に隣接して、表面処理を施していない部分(未処理部)を形成した。処理部と未処理部が形成された透明導電膜(銀ナノワイヤー層)側に黒色のビニールテープ(ニチバン株式会社製VT−50)を貼った状態で透明導電膜(銀ナノワイヤー層)側とは反対側に蛍光灯を映し込み、目視で黒浮きの発生を観察し、黒浮きの発生を以下の評価基準にて評価した。
−評価基準−
○:処理部と未処理部の境目がすぐに判断でき、処理部は黒浮き低減
△:処理部と非処理部の境目が角度によって確認でき、処理部は黒浮き低減
×:処理部と未処理部の境目がわからず、処理部は黒浮きあり
なお、比較例1は実施例1〜4及び比較例2及び3の未処理部と同等であり、比較例4は実施例5〜8及び比較例5及び6の未処理部と同等である。すなわち、実施例1〜4及び比較例2及び3についての三段階評価は、比較例1を基準とした評価であり、実施例5〜8及び比較例5及び6についての三段階評価は、比較例4を基準とした評価である。
実施例9〜12で得られた透明電極について、透明導電膜(銀ナノワイヤー層)側に黒色のビニールテープ(ニチバン株式会社製VT−50)を貼った状態で透明導電膜(銀ナノワイヤー層)側とは反対側に蛍光灯を映し込み、目視で黒浮きの発生を観察し、黒浮きの発生を以下の評価基準にて評価した。
−評価基準−
○:比較例4との差異がすぐに判断でき、黒浮き低減
△:比較例4との差異が角度によって確認でき、黒浮き低減
×:比較例4との差異がわからず、黒浮きあり
得られた透明電極の透明導電膜(銀ナノワイヤー層)上にレジスト層を形成した後、電極パターンが形成されたCrフォトマスクを用いて、レジスト層を露光した。この際、Crフォトマスクの電極パターンとしては、ダイヤモンドパターンを採用した。次に、レジスト層を現像してレジストパターンを形成し、このレジストパターンをマスクとして、透明導電膜(銀ナノワイヤー層)をAl用混酸エッチャントを用いてウエットエッチングした後、レジスト層をアルカリ現像液を用いて除去した。これにより、図15(図中の参照番号以外の数字の単位はmm)のような電極パターンを形成した。
電極パターン側に黒色のビニールテープ(ニチバン株式会社製VT−50)を貼合し、電極パターン側と反対側に透明両面粘着シート(日東電工株式会社製、商品名:LUCIACS CS9621T)を介してガラス板(松浪硝子工業株式会社製、MICRO SLIDE GLASS S9213)を貼合した。
ガラス面に蛍光灯を映し込み、目視で電極パターンを観察し、電極パターン非視認性を以下の評価基準にて評価した。
−評価基準−
○:パターンは視認しにくい
△:パターンが非常に視認しにくいが、角度によっては視認可能
×:パターンは容易に視認可能
なお、実施例1〜4及び比較例2及び3においては、下記の工程で電極パターンを形成しても同様の結果が得られた。
銀ナノワイヤーインク(分散液)をPET基材に塗布及び乾燥後、Crフォトマスクをソフトコンタクトし、東芝ライテック製アライメント露光装置を用いて積算光量200mJ/cm2の紫外線を照射し、露光部を硬化した。次に、100mLの20質量%酢酸水溶液をシャワー状に吹きかけ、非露光部を除去し現像した。その後、カレンダー処理(ニップ幅1mm、荷重4kN、速度1m/min)を行い、次いで、染料のエタノール溶液(0.2質量%)への浸漬(80℃、30分間)による表面処理を行い、透明パターン電極を作製した。また、カレンダー処理を、表面処理後に行っても、又は、紫外線硬化前に行っても、同様の結果であった。
また、表1における比較例2及び5の評価結果では、反射L値が低減することなく、シート抵抗が増大してしまっていた。このことから、染料Eは、銀ナノワイヤー表面に吸着するのではなく、銀ナノワイヤーを部分的に溶出してしまっているものと思われる。以上より、染料Eのスペーサ部分の「4−ピリジンエチレン基」は、チオール基の酸性度を小さくするスペーサとして不適切であることが分かった。
また、表1における比較例3及び6の評価結果では、反射L値が低減することなく或いは低減効果が少なく、シート抵抗が増大してしまっていた。このことから、染料Fは、銀ナノワイヤー表面に吸着するのではなく、銀ナノワイヤーを部分的に溶出してしまっているものと思われる。以上より、スペーサ部分がない染料Fは、有色化合物(染料)として不適切であることが分かった。
表1における比較例4と実施例5〜8との評価結果比較から、透明電極における銀ナノワイヤーを本発明のチオール基含有有色化合物(染料)で表面処理することで、黒浮き及び電極パターン非視認性を改善することができることが分かる。
表1における比較例4と実施例9〜12との評価結果比較から、本発明のチオール基含有有色化合物(染料)で表面処理された銀ナノワイヤーを含む銀ナノワイヤーインクを使用することで、黒浮き及び電極パターン非視認性を改善することができることが分かる。
2 金属ナノワイヤー本体
2a 金属ナノワイヤーの表面
3 チオール基含有有色化合物(染料)
31 バインダー層
40 基材
50 オーバーコート層
60 アンカー層
70 硬化物
80 有色化合物(染料)分散溶液
100 プレスロール
110 バックロール
120 透明導電膜
130 PET基材
200 電極部
300 絶縁部
Claims (10)
- 可視光領域に吸収を持つ発色団と、チオール基と、前記発色団と前記チオール基との間に設けられたスペーサとを有し、
前記スペーサは、炭素数2〜30の鎖状アルキレン基又は炭素数3〜30の環状アルキレン基、或いは、前記アルキレン基への付加構造の炭素数が前記アルキレン基の炭素数以下である前記アルキレン基の誘導体であり、
(i)酸性基含有染料と、(ii)チオール基、スペーサ−、及び塩基性基を有する塩基性基含有分子との反応物であり、
前記酸性基含有染料が、下記構造式(1)で表される金属錯体塩酸性染料であり、
前記塩基性基含有分子が、2−アミノエタンチオール塩酸塩、6−アミノ−1−ヘキサンチオール塩酸塩、11−アミノ−1−ウンデカンチオール塩酸塩、及び16−アミノ−1−ヘキサデカンチオール塩酸塩、からなる群から選択された少なくとも1種であることを特徴とするチオール基含有有色化合物。
- 金属ナノワイヤー本体を有し、前記金属ナノワイヤー本体の表面の少なくとも一部が、請求項1に記載のチオール基含有有色化合物で表面処理されたことを特徴とする金属ナノワイヤー。
- 前記金属ナノワイヤー本体は、Ag、Au、Ni、Cu、Pd、Pt、Rh、Ir、Ru、Os、Fe、Co、Sn、Al、Tl、Zn、Nb、Ti、In、W、Mo、Cr、Fe、V、Taからなる群から選択される少なくとも1種の元素で構成されることを特徴とする請求項2記載の金属ナノワイヤー。
- 請求項2又は3に記載の金属ナノワイヤーと、
溶剤と、
バインダーと、
を含むことを特徴とする分散液。 - 請求項2又は3に記載の金属ナノワイヤーを含むことを特徴とする透明導電膜。
- 前記金属ナノワイヤーが、透明なバインダーに分散されていることを特徴とする請求項5に記載の透明導電膜。
- 反射L値が9以下であることを特徴とする請求項5又は6に記載の透明導電膜。
- 前記チオール基含有有色化合物で表面処理されていない金属ナノワイヤー本体をさらに含む請求項5から7のいずれかに記載の透明導電膜。
- 透明基材と、
前記透明基材上に設けられた請求項5から8のいずれかに記載の透明導電膜と、
を備えることを特徴とする情報入力装置。 - 表示パネルと、
前記表示パネル上に設けられた請求項5から8のいずれかに記載の透明導電膜と、
を備えることを特徴とする電子機器。