JP5822636B2 - Laminated polyester film - Google Patents

Description

  The present invention relates to a laminated polyester film, for example, having a surface functional layer such as a hard coat on both surfaces of a transparent electrode such as a touch panel or an electromagnetic wave shielding film, and further conducting on at least one surface on the surface functional layer. In applications that have a polymer conductive layer, it has good adhesion to a surface functional layer such as a hard coat layer that has excellent adhesion to the conductive layer, and reflects outside light at the interface with the surface functional layer such as a hard coat layer. It is related with the laminated polyester film which can reduce the interference nonuniformity by.

  In recent years, polyester films have been used for various optical films, and are also used as substrates for transparent conductive films such as touch panels, flat panel displays, electroluminescent elements, and electromagnetic shielding films. As a transparent conductive film, conventionally, a technique in which ITO (indium tin oxide) or the like is formed by a dry process such as vacuum deposition or sputtering has been the mainstream. However, the dry process needs to be evacuated, and the dry process has a drawback that the processing speed is slow and the productivity is low. Furthermore, since the ITO film formed by this process has a large number of irregularities on the surface immediately after formation, problems may occur when applied to an element or the like due to poor flatness (Patent Document 1). ). In addition, since the film is not sufficiently flexible, there is a problem in that defects such as cracks are generated during the post-processing step or the punching step, and the surface conductivity is not sufficient.

  In order to overcome these drawbacks of the dry process, a method of forming a transparent conductive layer by a wet process (a method of applying a conductive material solution) has been proposed (Patent Document 2). Since the wet process does not need to be evacuated and the processing speed can be increased, productivity can be improved. Moreover, since it is excellent in a flexibility, there also exists an advantage that generation | occurrence | production of a crack etc. is suppressed.

  Examples of wet processes include transparent conductive films using conductive polymers such as polythiophene and polyaniline (Patent Documents 2 and 3). It is known that the conductive polymer wet process is simpler than the dry process of metals such as ITO, and ITO is a rare metal and expensive, whereas the conductive polymer is transparent because of its relatively low cost. Application to conductive films has been made. However, the adhesion between the conductive polymer and the polyester film may not be sufficient.

  By the way, the side opposite to the side where the conductive layer of the conductive polymer of the transparent conductive film is formed is often hard-coated to improve performance such as scratch prevention and surface hardness. Since the polyester film and the hard coat layer used as the base material may not be excellent in adhesion, an easy-adhesion coating layer is generally provided as an intermediate layer in order to improve adhesion. For this reason, interference unevenness occurs unless the refractive index of the three layers of the polyester film, the easily adhesive coating layer, and the hard coat layer is taken into consideration.

  When a film with interference unevenness is used for a display such as a touch panel, the visibility becomes poor and it is difficult to use. Therefore, it is required to take measures against interference unevenness. In general, the refractive index of the coating layer for reducing interference unevenness is considered to be around the geometric mean of the refractive index of the polyester film of the substrate and the refractive index of the hard coat layer, and is adjusted to the refractive index around this. Ideally. Since the refractive index of the polyester film is high, it is generally necessary to design the coating layer with a high refractive index.

  An example of improving interference unevenness by increasing the refractive index of the coating layer is, for example, a method of combining a metal chelate compound having a high refractive index and a resin in the coating layer. In this case, the stability of the coating solution may not be sufficient depending on the combination due to the instability of the metal chelate in the aqueous solution, which may lead to an increase in the liquid exchange work when producing for a long time. . Moreover, when using a metal chelate compound, the adhesiveness with a hard-coat layer may fall if it carries out moisture-proof heat processing (patent document 4). Moreover, since a high refractive index material usually used is inferior in adhesion to a surface functional layer such as a hard coat layer, a coating layer that can effectively improve adhesion even when combined with a high refractive index material is required. Yes.

JP 2010-118488 A Japanese Patent Laid-Open No. 1-313521 JP 2006-294455 A JP 2005-97571 A

  The present invention has been made in view of the above circumstances, and the problem to be solved is that when a surface functional layer excellent in adhesion to a conductive layer of a conductive polymer is laminated on a film, interference unevenness due to reflection of external light is caused. Is to provide a laminated polyester film having excellent adhesion to the surface functional layer.

  As a result of intensive studies in view of the above circumstances, the present inventors have found that the use of a laminated polyester film having a specific configuration can easily solve the above-described problems, and have completed the present invention.

That is, the gist of the present invention is a coating layer formed from a coating solution containing a metal oxide and two or more kinds of crosslinking agents, and the absolute reflectance of the coating layer surface is minimal within a wavelength range of 400 to 800 nm. It has one value, has a coating layer Ri der absolute reflectance at the minimum value is 4.0% or more, and metal oxides are present as particles below an average particle size of 50nm on both surfaces of the polyester film, It exists in the laminated polyester film for electroconductive films characterized by having a surface functional layer on both application layers, and a conductive polymer layer being formed on at least one surface of the surface functional layer.

  According to the laminated polyester film of the present invention, when various surface functional layers such as a hard coat layer are laminated, interference unevenness due to reflection of external light is small, and adhesiveness with various surface functional layers is excellent. A base film for forming a structure of a surface functional layer such as a conductive layer / a hard surface layer such as a hard coat layer / a base film / a hard surface layer such as a hard coat layer can be provided, and its industrial value is high.

  The polyester film constituting the laminated polyester film in the present invention may have a single layer structure or a multilayer structure, and may have four or more layers as long as it does not exceed the gist of the present invention other than a two-layer or three-layer structure. It may be a multilayer, and is not particularly limited.

  The polyester used in the present invention may be a homopolyester or a copolyester. In the case of a homopolyester, those obtained by polycondensation of an aromatic dicarboxylic acid and an aliphatic glycol are preferred. Examples of the aromatic dicarboxylic acid include terephthalic acid and 2,6-naphthalenedicarboxylic acid, and examples of the aliphatic glycol include ethylene glycol, diethylene glycol, and 1,4-cyclohexanedimethanol. Typical polyester includes polyethylene terephthalate and the like. On the other hand, the dicarboxylic acid component of the copolyester includes isophthalic acid, phthalic acid, terephthalic acid, 2,6-naphthalenedicarboxylic acid, adipic acid, sebacic acid, oxycarboxylic acid (for example, p-oxybenzoic acid, etc.), etc. 1 type or 2 types or more are mentioned, As a glycol component, 1 type or 2 types or more, such as ethylene glycol, diethylene glycol, propylene glycol, butanediol, 4-cyclohexane dimethanol, neopentyl glycol, is mentioned.

  There is no restriction | limiting in particular as a polymerization catalyst of polyester, A conventionally well-known compound can be used, For example, an antimony compound, a titanium compound, a germanium compound, a manganese compound, an aluminum compound, a magnesium compound, a calcium compound etc. are mentioned.

  In the polyester film of the present invention, it is necessary to contain an ultraviolet absorber in order to improve the weather resistance of the film and to prevent deterioration of the liquid crystal or the like of a liquid crystal display used for a touch panel or the like. The ultraviolet absorber is not particularly limited as long as it is a compound that absorbs ultraviolet rays and can withstand the heat applied in the production process of the polyester film.

  As the ultraviolet absorber, there are an organic ultraviolet absorber and an inorganic ultraviolet absorber. From the viewpoint of transparency, an organic ultraviolet absorber is preferable. Although it does not specifically limit as an organic type ultraviolet absorber, For example, a cyclic imino ester type, a benzotriazole type, a benzophenone type etc. are mentioned. From the viewpoint of durability, a cyclic imino ester type and a benzotriazole type are more preferable. It is also possible to use two or more ultraviolet absorbers in combination.

  In the polyester layer of the film of the present invention, it is preferable to blend particles mainly for the purpose of imparting slipperiness and preventing scratches in each step. The kind of the particle to be blended is not particularly limited as long as it is a particle capable of imparting slipperiness. Specific examples thereof include silica, calcium carbonate, magnesium carbonate, barium carbonate, calcium sulfate, calcium phosphate, and phosphoric acid. Examples include inorganic particles such as magnesium, kaolin, aluminum oxide, and titanium oxide, and organic particles such as acrylic resin, styrene resin, urea resin, phenol resin, epoxy resin, and benzoguanamine resin. Furthermore, precipitated particles obtained by precipitating and finely dispersing a part of a metal compound such as a catalyst during the polyester production process can also be used.

The shape of the particles to be used is not particularly limited, and any of a spherical shape, a block shape, a rod shape, a flat shape, and the like may be used. Moreover, there is no restriction | limiting in particular also about the hardness, specific gravity, a color, etc.
These series of particles may be used in combination of two or more as required.

  Moreover, the average particle diameter of particle | grains is 0.01-5 micrometers normally, Preferably it is the range of 0.01-3 micrometers. If the average particle size is less than 0.01 μm, the slipperiness may not be sufficiently imparted, or the particles may be aggregated to make the dispersibility insufficient, thereby reducing the transparency of the film. On the other hand, when it exceeds 5 μm, the surface roughness of the film becomes too rough, and there may be a problem when various surface functional layers and the like are applied in a subsequent process.

  Further, the content of particles in the polyester layer is usually less than 5% by weight, preferably in the range of 0.0003 to 3% by weight. When there are no or few particles, the transparency of the film becomes high and the film becomes a good film, but the slipperiness may be insufficient. There are cases where improvement is required. Further, when the particle content exceeds 5% by weight, the transparency of the film may be insufficient.

  The method for adding particles to the polyester layer is not particularly limited, and a conventionally known method can be adopted. For example, it can be added at any stage for producing the polyester constituting each layer, but it is preferably added after completion of esterification or transesterification.

  Also, a method of blending a slurry of particles dispersed in ethylene glycol or water with a vented kneading extruder and a polyester raw material, or a blending of dried particles and a polyester raw material using a kneading extruder. It is done by methods.

  In addition to the above-mentioned particles, conventionally known antioxidants, antistatic agents, thermal stabilizers, lubricants, dyes, pigments, and the like can be added to the polyester film in the present invention as necessary.

  Although the thickness of the polyester film in this invention will not be specifically limited if it can be formed into a film as a film, Usually, 10-300 micrometers, Preferably it is the range of 25-250 micrometers.

  Next, although the manufacture example of the polyester film in this invention is demonstrated concretely, it is not limited to the following manufacture examples at all. That is, a method of using the polyester raw material described above and cooling and solidifying a molten sheet extruded from a die with a cooling roll to obtain an unstretched sheet is preferable. In this case, in order to improve the flatness of the sheet, it is preferable to improve the adhesion between the sheet and the rotary cooling drum, and an electrostatic application adhesion method or a liquid application adhesion method is preferably employed. Next, the obtained unstretched sheet is stretched in the biaxial direction. In that case, first, the unstretched sheet is stretched in one direction by a roll or a tenter type stretching machine. The stretching temperature is usually 70 to 120 ° C., preferably 80 to 110 ° C., and the stretching ratio is usually 2.5 to 7 times, preferably 3.0 to 6 times. Next, the film is stretched in the direction perpendicular to the first stretching direction. In that case, the stretching temperature is usually 70 to 170 ° C., and the stretching ratio is usually 3.0 to 7 times, preferably 3.5 to 6 times. is there. Subsequently, heat treatment is performed at a temperature of 180 to 270 ° C. under tension or under relaxation within 30% to obtain a biaxially oriented film. In the above-described stretching, a method in which stretching in one direction is performed in two or more stages can be employed. In that case, it is preferable to carry out so that the draw ratios in the two directions finally fall within the above ranges.

  In the present invention, the simultaneous biaxial stretching method can be adopted for the production of the polyester film constituting the laminated polyester film. The simultaneous biaxial stretching method is a method in which the above-mentioned unstretched sheet is usually stretched and oriented in the machine direction and the width direction at a temperature controlled normally at 70 to 120 ° C., preferably 80 to 110 ° C. Is 4 to 50 times, preferably 7 to 35 times, and more preferably 10 to 25 times in terms of area magnification. Subsequently, heat treatment is performed at a temperature of 170 to 250 ° C. under tension or under relaxation within 30% to obtain a stretched oriented film. With respect to the simultaneous biaxial stretching apparatus that employs the above-described stretching method, a conventionally known stretching method such as a screw method, a pantograph method, or a linear driving method can be employed.

  Next, formation of the coating layer which comprises the laminated polyester film in this invention is demonstrated. Regarding the coating layer, it may be provided by in-line coating which treats the film surface during the process of forming a polyester film, or offline coating which is applied outside the system on a once produced film may be adopted. Since the coating can be performed simultaneously with the film formation, the production can be handled at a low cost, and therefore in-line coating is preferably used.

  The in-line coating is not limited to the following, but for example, in the sequential biaxial stretching, the coating treatment can be performed particularly before the lateral stretching after the longitudinal stretching is finished. When the coating layer is provided on the polyester film by in-line coating, it is possible to apply at the same time as the film formation, and the coating layer can be processed at a high temperature in the heat treatment process of the polyester film after stretching. Performances such as adhesion to various surface functional layers that can be formed on the layer and heat-and-moisture resistance can be improved. Moreover, when coating before extending | stretching, the thickness of an application layer can also be changed with a draw ratio, and compared with offline coating, thin film coating can be performed more easily. That is, a film suitable as a polyester film can be produced by in-line coating, particularly coating before stretching.

  The coating layer of the film of the present invention is designed to reduce interference unevenness due to external light after forming a surface functional layer such as a hard coat layer, and is provided to improve adhesion to the surface functional layer.

  The metal oxide used for forming the coating layer of the film of the present invention is mainly used for adjusting the refractive index of the coating layer. In particular, since the refractive index of the resin used in the coating layer is low, it is preferable to use a metal oxide having a high refractive index, and it is preferable to use a refractive index of 1.7 or more. Specific examples of the metal oxide include, for example, zirconium oxide, titanium oxide, tin oxide, yttrium oxide, antimony oxide, indium oxide, zinc oxide, antimontin oxide, indium tin oxide, and the like. You may use 2 or more types. Among these, zirconium oxide and titanium oxide are more preferably used. In particular, zirconium oxide is more preferably used from the viewpoint of weather resistance.

  The metal oxide is preferably used in the form of particles because there is a concern that the adhesion may be lowered depending on the use form, and the average particle size is preferably 100 nm or less, more preferably from the viewpoint of transparency. It is 50 nm or less, more preferably 25 nm or less.

  In the present invention, the coating liquid for forming the coating layer contains two or more types of crosslinking agents, but these have adhesion with a surface functional layer such as a hard coat layer provided on the coating layer. Can be improved. We have found that even one type of cross-linking agent can improve adhesion, but by using two or more types of cross-linking agents together, it is possible to further improve the adhesion, particularly improving the adhesion after the wet heat test. I found what I could do.

  Examples of the crosslinking agent used for forming the coating layer of the film of the present invention include oxazoline compounds, epoxy compounds, melamine compounds, isocyanate compounds, carbodiimide compounds, and silane coupling compounds. Among these crosslinking agents, from the viewpoint of good adhesion, it is particularly preferable to use an oxazoline compound or an epoxy compound, and it is more preferable to use an oxazoline compound and an epoxy compound in combination.

  The oxazoline compound used for the formation of the coating layer of the film of the present invention is a compound having an oxazoline group in the molecule, and a polymer containing an oxazoline group is particularly preferred, and an addition polymerizable oxazoline group-containing monomer alone or other It can be made by polymerization with monomers. Addition polymerizable oxazoline group-containing monomers include 2-vinyl-2-oxazoline, 2-vinyl-4-methyl-2-oxazoline, 2-vinyl-5-methyl-2-oxazoline, 2-isopropenyl-2-oxazoline, 2-isopropenyl-4-methyl-2-oxazoline, 2-isopropenyl-5-ethyl-2-oxazoline, and the like can be mentioned, and one or a mixture of two or more thereof can be used. Among these, 2-isopropenyl-2-oxazoline is preferred because it is easily available industrially. The other monomer is not limited as long as it is a monomer copolymerizable with an addition polymerizable oxazoline group-containing monomer. For example, alkyl (meth) acrylate (the alkyl group includes a methyl group, an ethyl group, an n-propyl group, an isopropyl group, (meth) acrylic acid esters such as n-butyl group, isobutyl group, t-butyl group, 2-ethylhexyl group, cyclohexyl group); acrylic acid, methacrylic acid, itaconic acid, maleic acid, fumaric acid, crotonic acid, styrene Unsaturated carboxylic acids such as sulfonic acid and its salts (sodium salt, potassium salt, ammonium salt, tertiary amine salt, etc.); Unsaturated nitriles such as acrylonitrile, methacrylonitrile; (meth) acrylamide, N-alkyl ( (Meth) acrylamide, N, N-dialkyl (meth) acrylamide, As the alkyl group, unsaturated amides such as methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, isobutyl group, t-butyl group, 2-ethylhexyl group and cyclohexyl group); vinyl acetate Vinyl esters such as vinyl propionate; vinyl ethers such as methyl vinyl ether and ethyl vinyl ether; α-olefins such as ethylene and propylene; halogen-containing α, β-unsaturated monomers such as vinyl chloride, vinylidene chloride and vinyl fluoride And α, β-unsaturated aromatic monomers such as styrene and α-methylstyrene, and the like, and one or more of these monomers can be used.

  The epoxy compound is a compound having an epoxy group in the molecule, and examples thereof include condensates of epichlorohydrin with ethylene glycol, polyethylene glycol, glycerin, polyglycerin, bisphenol A and the like hydroxyl groups and amino groups, There are polyepoxy compounds, diepoxy compounds, monoepoxy compounds, glycidylamine compounds, and the like. Examples of the polyepoxy compound include sorbitol polyglycidyl ether, polyglycerol polyglycidyl ether, pentaerythritol polyglycidyl ether, diglycerol polyglycidyl ether, triglycidyl tris (2-hydroxyethyl) isocyanate, glycerol polyglycidyl ether, trimethylolpropane. Examples of the polyglycidyl ether and diepoxy compound include neopentyl glycol diglycidyl ether, 1,6-hexanediol diglycidyl ether, resorcin diglycidyl ether, ethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, and propylene glycol diglycidyl ether. , Polypropylene glycol diglycidyl ether, poly Examples of tetramethylene glycol diglycidyl ether and monoepoxy compounds include allyl glycidyl ether, 2-ethylhexyl glycidyl ether, phenyl glycidyl ether, and glycidyl amine compounds such as N, N, N ′, N′-tetraglycidyl-m-xylyl. Examples include range amine and 1,3-bis (N, N-diglycidylamino) cyclohexane.

  The melamine compound is a compound having a melamine skeleton in the compound. For example, an alkylolized melamine derivative, a compound partially or completely etherified by reacting an alcohol with an alkylolated melamine derivative, and these Mixtures can be used. As alcohol used for etherification, methyl alcohol, ethyl alcohol, isopropyl alcohol, n-butanol, isobutanol and the like are preferably used. Moreover, as a melamine compound, either a monomer or a multimer more than a dimer may be sufficient, or a mixture thereof may be used. Further, a product obtained by co-condensing urea or the like with a part of melamine can be used, and a catalyst can be used to increase the reactivity of the melamine compound.

  The isocyanate compound is a compound having an isocyanate derivative structure typified by isocyanate or blocked isocyanate. Examples of the isocyanate include aromatic isocyanates such as tolylene diisocyanate, xylylene diisocyanate, methylene diphenyl diisocyanate, phenylene diisocyanate, and naphthalene diisocyanate, and aromatic rings such as α, α, α ′, α′-tetramethylxylylene diisocyanate. Aliphatic isocyanates such as aliphatic isocyanate, methylene diisocyanate, propylene diisocyanate, lysine diisocyanate, trimethylhexamethylene diisocyanate, hexamethylene diisocyanate, cyclohexane diisocyanate, methylcyclohexane diisocyanate, isophorone diisocyanate, methylene bis (4-cyclohexyl isocyanate), isopropylidene dicyclohexyl diisocyanate Ne Alicyclic isocyanates such as bets are exemplified. Further, polymers and derivatives such as burettes, isocyanurates, uretdiones, and carbodiimide modified products of these isocyanates are also included. These may be used alone or in combination. Among the above isocyanates, aliphatic isocyanates or alicyclic isocyanates are more preferable than aromatic isocyanates in order to avoid yellowing due to ultraviolet rays.

  When used in the state of blocked isocyanate, the blocking agent includes, for example, bisulfites, phenolic compounds such as phenol, cresol, and ethylphenol, and alcohols such as propylene glycol monomethyl ether, ethylene glycol, benzyl alcohol, methanol, and ethanol. Compounds, active methylene compounds such as dimethyl malonate, diethyl malonate, methyl acetoacetate, ethyl acetoacetate and acetylacetone, mercaptan compounds such as butyl mercaptan and dodecyl mercaptan, lactam compounds such as ε-caprolactam and δ-valerolactam , Amine compounds such as diphenylaniline, aniline, ethyleneimine, acetanilide, acid amide compounds of acetic acid amide, formaldehyde, acetoald Examples include oxime compounds such as oxime, acetone oxime, methyl ethyl ketone oxime, and cyclohexanone oxime, and these may be used alone or in combination of two or more.

  In addition, the isocyanate compound in the present invention may be used alone, or may be used as a mixture or bond with various polymers. In the sense of improving the dispersibility and crosslinkability of the isocyanate compound, it is preferable to use a mixture or a bond with a polyester resin or a urethane resin.

  A carbodiimide-based compound is a compound having a carbodiimide structure, and is used for improving adhesion with a surface functional layer such as a hard coat layer that can be formed on a coating layer, and for improving wet heat resistance of the coating layer. It is what A carbodiimide compound is a compound having one or more carbodiimide structures in the molecule, but a polycarbodiimide compound having two or more in the molecule is more preferable for better adhesion and the like.

  The carbodiimide compound can be synthesized by a conventionally known technique, and generally a condensation reaction of a diisocyanate compound is used. The diisocyanate compound is not particularly limited, and any of aromatic and aliphatic compounds can be used. Specifically, tolylene diisocyanate, xylene diisocyanate, diphenylmethane diisocyanate, phenylene diisocyanate, naphthalene diisocyanate, hexa Examples include methylene diisocyanate, trimethylhexamethylene diisocyanate, cyclohexane diisocyanate, methylcyclohexane diisocyanate, isophorone diisocyanate, dicyclohexyl diisocyanate, and dicyclohexylmethane diisocyanate.

  Furthermore, in order not to lose the effect of the present invention, in order to improve the water solubility and water dispersibility of the polycarbodiimide compound, adding a surfactant, polyalkylene oxide, quaternary ammonium salt of dialkylamino alcohol, You may add and use hydrophilic monomers, such as a hydroxyalkyl sulfonate.

  These cross-linking agents are used in a design that improves the performance of the coating layer by reacting in the drying process or film forming process. It can be inferred that unreacted products of these crosslinking agents, compounds after the reaction, or mixtures thereof exist in the finished coating layer.

  In the laminated polyester film of the coating layer of the present invention, improvement of coating appearance, reduction of interference unevenness when various surface functional layers such as a hard coat layer are laminated on the coating surface, improvement of transparency and adhesion, etc. Therefore, it is preferable to use various polymers.

  Specific examples of the polymer include polyester resin, acrylic resin, urethane resin, polyvinyl (polyvinyl alcohol, polyvinyl chloride, vinyl chloride vinyl acetate copolymer, etc.), polyalkylene glycol, polyalkyleneimine, methylcellulose, hydroxycellulose, starches. Etc. Among these, it is preferable to use a polyester resin, an acrylic resin, or a urethane resin from the viewpoint of improving adhesion with a surface functional layer such as a hard coat layer and improving the appearance of coating. In addition, a polyester resin is particularly preferable from the viewpoint that a large number of aromatic compounds such as a benzene ring can be contained in the molecule, thereby increasing the refractive index.

  Further, in order to make it easier to adjust the refractive index of the coating layer, naphthalene, anthracene, phenanthrene, naphthacene, benzo [a] anthracene, benzo [a] phenanthrene, pyrene, benzo [c It is preferable to use a compound having a condensed polycyclic aromatic structure such as phenanthrene or perylene.

  In consideration of applicability on the polyester film, the compound having a condensed polycyclic aromatic is preferably a polymer compound such as a polyester resin, an acrylic resin, or a urethane resin. In particular, polyester resins are more preferable because more condensed polycyclic aromatics can be introduced.

  As a method of incorporating the condensed polycyclic aromatic into the polyester resin, for example, two or more hydroxyl groups are introduced into the condensed polycyclic aromatic as a substituent to form a diol component or a polyvalent hydroxyl component, or There is a method in which two or more acid groups are introduced to prepare a dicarboxylic acid component or a polyvalent carboxylic acid component.

  In the laminated polyester film production process, the condensed polycyclic aromatic contained in the coating layer is preferably a compound having a naphthalene skeleton in that it is difficult to be colored. In addition, a resin in which a naphthalene skeleton is incorporated as a polyester component is suitably used in terms of good adhesion to various surface functional layers formed on the coating layer and transparency. Representative examples of the naphthalene skeleton include 1,5-naphthalenedicarboxylic acid, 2,6-naphthalenedicarboxylic acid, and 2,7-naphthalenedicarboxylic acid.

  In addition to the hydroxyl group and the carboxylic acid group, the condensed polycyclic aromatic has a refractive index of a refractive index by introducing a substituent containing a sulfur element, an aromatic substituent such as a phenyl group, a halogen element group, and the like. Improvements can be expected, and substituents such as alkyl groups, ester groups, amide groups, sulfonic acid groups, carboxylic acid groups, and hydroxyl groups may be introduced from the viewpoint of coating properties and adhesion.

  Moreover, this invention may contain particle | grains other than the above-mentioned metal oxide for the purpose of the adhesiveness of an application layer, and slipperiness improvement in an application layer. The average particle size is preferably in the range of 1.0 μm or less, more preferably 0.5 μm or less, particularly preferably 0.2 μm or less from the viewpoint of the transparency of the film. Specific examples of the particles include silica, alumina, kaolin, calcium carbonate, and organic particles.

  Furthermore, as long as it does not impair the gist of the present invention, the coating layer has an antifoaming agent, a coating property improving agent, a thickener, an organic lubricant, an antistatic agent, an ultraviolet absorber, an antioxidant, foaming as necessary. Agents, dyes, pigments and the like may be contained.

  As a ratio with respect to all the non-volatile components in the coating liquid which forms the coating layer which comprises the laminated polyester film in this invention, a metal oxide is the range of 3-70 weight% normally, Preferably it is the range of 5-50 weight%, Furthermore, Preferably it is the range of 5-40 weight%, Most preferably, it is the range of 8-30 weight%. When the amount of the metal oxide is less than 3% by weight, the refractive index of the coating layer cannot be made sufficiently high, so that interference unevenness may not be reduced. When it exceeds 70% by weight, the coating layer is transparent. Sexuality may worsen.

  As a ratio with respect to all the non-volatile components in the coating liquid which forms the coating layer which comprises the laminated polyester film in this invention, 2 or more types of crosslinking agents are 2-80 weight% normally, More preferably, it is 4-60 weight%. More preferably, it is the range of 10 to 40 weight%. If it is out of these ranges, there is a concern that the adhesion with the surface functional layer such as the hard coat layer may be lowered, if the coating appearance deteriorates, interference after the formation of the surface functional layer such as the hard coat layer The visibility may not be good due to unevenness.

  When using an oxazoline compound as a cross-linking agent, the content of the oxazoline compound is usually in the range of 1 to 50% by weight, more preferably 1 to 30% by weight, as a ratio to the total nonvolatile components in the coating liquid forming the coating layer. More preferably, it is in the range of 3 to 20% by weight. If the amount is less than 1% by weight, there is a concern that the adhesion to the surface functional layer such as a hard coat layer may be lowered. If the amount exceeds 50% by weight, the refractive index of the coating layer is lowered, thereby causing a hard coat layer or the like. Visibility may not be good due to interference unevenness after the surface functional layer is formed.

  When using an epoxy compound as a cross-linking agent, the content of the epoxy compound is usually in the range of 1 to 50% by weight, more preferably 3 to 30% by weight, as a ratio to the total nonvolatile components in the coating liquid forming the coating layer. More preferably, it is the range of 5 to 20 weight%. If it is out of these ranges, there is a possibility that the adhesion with the surface functional layer such as the hard coat layer may be lowered, or the coating appearance may be deteriorated.

  In the compound having a condensed polycyclic aromatic that can be used in the coating layer constituting the laminated polyester film in the present invention, the proportion of the condensed polycyclic aromatic in the compound is preferably in the range of 5 to 80% by weight. More preferably, it is in the range of 10 to 60% by weight. Further, the content of the compound having a condensed polycyclic aromatic in all the non-volatile components in the coating liquid forming the coating layer is preferably in the range of 80% by weight or less, more preferably in the range of 5 to 70% by weight, More preferably, it is the range of 10-50 weight%. By using within these ranges, the refractive index of the coating layer can be easily adjusted, and interference unevenness after forming a surface functional layer such as a hard coat layer can be easily reduced. The ratio of the condensed polycyclic aromatic can be determined by, for example, dissolving and extracting the coating layer with an appropriate solvent or warm water, separating by chromatography, analyzing the structure by NMR or IR, and further pyrolyzing GC-MS (gas It can be determined by analyzing by chromatography mass spectrometry) or optical analysis.

  Analysis of the components in the coating layer can be performed by analysis of TOF-SIMS, ESCA, fluorescent X-rays, and the like, for example.

  When providing a coating layer by in-line coating, the above-mentioned series of compounds is applied as an aqueous solution or dispersion, and the coating solution adjusted to a solid content concentration of about 0.1 to 50% by weight as a guide is applied onto the polyester film. It is preferable to produce a laminated polyester film. Moreover, in the range which does not impair the main point of this invention, a small amount of organic solvents may be contained in the coating liquid for the purpose of improving dispersibility in water, improving film-forming properties, and the like. Only one type of organic solvent may be used, or two or more types may be used as appropriate.

  Regarding the laminated polyester film in the present invention, the thickness of the coating layer provided on the polyester film is usually in the range of 0.04 to 0.20 μm, preferably 0.07 to 0.15 μm. When the film thickness is out of the above range, visibility may deteriorate due to interference unevenness after the surface functional layer is laminated.

  In the present invention, as a method for providing the coating layer, a conventionally known coating method such as reverse gravure coating, direct gravure coating, roll coating, die coating, bar coating, curtain coating or the like can be used.

  In the present invention, the drying and curing conditions for forming the coating layer on the polyester film are not particularly limited. For example, when the coating layer is provided by off-line coating, it is usually 3 to 40 at 80 to 200 ° C. The heat treatment may be performed for 2 seconds, preferably 100 to 180 ° C. for 3 to 40 seconds.

  On the other hand, when the coating layer is provided by in-line coating, heat treatment is usually performed at 70 to 280 ° C. for 3 to 200 seconds as a guide.

  Further, irrespective of off-line coating or in-line coating, heat treatment and active energy ray irradiation such as ultraviolet irradiation may be used in combination as required. The polyester film constituting the laminated polyester film in the present invention may be subjected to surface treatment such as corona treatment or plasma treatment in advance.

  The coating layer in the present invention has a refractive index adjusted to suppress the occurrence of interference unevenness, and the refractive index is in the vicinity of the geometric mean of the surface functional layer such as the base material polyester film and the hard coat layer. Designed. The refractive index of the coating layer and the reflectance of the coating layer are closely related. The absolute reflectance of the film of the present invention is a graph in which the horizontal axis indicates the wavelength and the vertical axis indicates the reflectance, and the minimum value of the reflectance needs to be one in the wavelength range of 400 to 800 nm. Is 4.0% or more. In the range of the absolute reflectance of the present invention, if the minimum value appears at the same wavelength, the reflectance of the minimum value is a high value when the refractive index is high, and a low value when the refractive index is low.

  In the present invention, the absolute reflectance of the coating layer has one minimum value in the wavelength range of 400 to 800 nm, more preferably one minimum value in the wavelength range of 500 to 700 nm. The minimum value is preferably in the range of 4.0 to 6.5%, more preferably 4.5 to 6.2%. If the minimum value in the wavelength range of 400 to 800 nm is not one, and if the absolute reflectance of the minimum value deviates from the above value, interference unevenness occurs after the surface functional layer such as a hard coat layer is formed. The visibility of the film may be reduced.

  In the polyester film of the present invention, a surface functional layer such as a hard coat layer is generally provided on the coating layer, and a conductive layer made of a conductive polymer is further provided thereon. Although it does not specifically limit as a material used for a hard-coat layer, For example, hardened | cured materials, such as reactive silicon compounds, such as monofunctional (meth) acrylate, polyfunctional (meth) acrylate, and tetraethoxysilane, are mentioned. Among these, from the viewpoint of achieving both productivity and hardness, a polymerization cured product of a composition containing an ultraviolet curable polyfunctional (meth) acrylate is particularly preferable.

  It does not specifically limit as a composition containing a ultraviolet curable polyfunctional (meth) acrylate. For example, a mixture of one or more known ultraviolet curable polyfunctional (meth) acrylates, a commercially available ultraviolet curable hard coat material, or a range that does not impair the purpose of this embodiment other than these, What added the other component further can be used.

  The UV-curable polyfunctional (meth) acrylate is not particularly limited. For example, dipentaerythritol hexa (meth) acrylate, tetramethylolmethanetetra (meth) acrylate, tetramethylolmethanetri (meth) acrylate, (Meth) acryl derivatives of polyfunctional alcohols such as trimethylolpropane tri (meth) acrylate, 1,6-hexanediol di (meth) acrylate, 1,6-bis (3-acryloyloxy-2-hydroxypropyloxy) hexane And polyethylene glycol di (meth) acrylate and polyurethane (meth) acrylate.

  Other components contained in the composition containing an ultraviolet curable polyfunctional (meth) acrylate are not particularly limited. Examples thereof include inorganic or organic fine particles, polymerization initiators, polymerization inhibitors, antioxidants, antistatic agents, dispersants, surfactants, light stabilizers and leveling agents. In addition, when the film is dried after film formation in the wet coating method, an arbitrary amount of solvent can be added.

  As a method for forming the hard coat layer, when an organic material is used, a general wet coat method such as a roll coat method or a die coat method is employed. The formed hard coat layer can be subjected to a curing reaction by heating, irradiation with active energy rays such as ultraviolet rays and electron beams as necessary.

  As the conductive layer, a conductive polymer is generally used. Although it does not specifically limit as a conductive polymer, For example, polythiophene, polyaniline, polypyrrole, etc. are mentioned. Usually, a conductive polymer exhibits high conductivity when used in combination with an electron supply substance called a dopant, but the combination changes not only the conductivity but also properties such as melt processability and solution processability. Among many conductive polymer / dopant combinations, from the viewpoint of conductivity and solution processability, for example, a polythiophene system such as poly (3,4-ethylenedioxythiophene) used in combination with polystyrene sulfonic acid is preferably used. It is done.

  EXAMPLES Hereinafter, although an Example demonstrates this invention further in detail, this invention is not limited to a following example, unless the summary is exceeded. The measurement method and evaluation method used in the present invention are as follows.

(1) Method for measuring the intrinsic viscosity of polyester 1 g of polyester from which other polymer components and pigments incompatible with polyester have been removed are precisely weighed, and 100 ml of a mixed solvent of phenol / tetrachloroethane = 50/50 (weight ratio) is added. And dissolved at 30 ° C.

(2) Measuring method of average particle diameter The coating layer was observed using TEM (H-7650 manufactured by Hitachi High-Technologies Corporation, acceleration voltage 100V), and the average value of the particle diameters of 10 particles was defined as the average particle diameter. .

(3) Method for measuring film thickness of coating layer The surface of the coating layer was dyed with RuO ₄ and embedded in an epoxy resin. Thereafter, the section prepared by ultramicrotomy stained with RuO _4, a coating layer cross-section was measured by using a TEM (Hitachi High Technologies Corporation H-7650, accelerating voltage 100 V).

(4) Evaluation method of absolute reflectance from coating layer surface in polyester film A black tape (vinyl tape VT-50 manufactured by Nichiban Co., Ltd.) was previously applied to the measurement back surface of the polyester film, and a spectrophotometer (manufactured by JASCO Corporation). UV-visible spectrophotometer V-570 and automatic absolute reflectance measuring device ARM-500N), synchronous mode, incident angle 5 °, N-polarized light, response Fast, data collection interval 1.0 nm, bandwidth 10 nm, scanning The absolute reflectance of the coating layer surface in the wavelength range of 300 to 800 nm was measured at a speed of 1000 m / min, and the wavelength (bottom wavelength) and reflectance at the minimum value were evaluated.

(5) Interference unevenness evaluation method On the polyester film coating layer side, 72 parts by weight of dipentaerythritol hexaacrylate, 18 parts by weight of 2-hydroxy-3-phenoxypropyl acrylate, 10 parts by weight of antimony pentoxide, a photopolymerization initiator ( (Product name: Irgacure 184, manufactured by Ciba Specialty Chemical) 1 part by weight and 200 parts by weight of methyl ethyl ketone were applied so that the dry film thickness was 5 μm and cured by irradiating with ultraviolet rays to form a hard coat layer. The obtained film is visually observed under a three-wavelength fluorescent lamp, and interference unevenness is observed. If the interference unevenness is not confirmed, ◎, thin sparse interference unevenness is confirmed, thin, linear The case where the interference unevenness was confirmed was indicated by Δ, and the case where clear interference unevenness was confirmed was indicated by ×.

(6) Method for evaluating adhesion of coating layer In order to evaluate adhesion, 80 parts by weight of dipentaerythritol hexaacrylate, 20 parts by weight of 2-hydroxy-3-phenoxypropyl acrylate, a photopolymerization initiator (trade name: A mixed coating solution of 5 parts by weight (Irgacure 184, manufactured by Ciba Specialty Chemical) and 200 parts by weight of methyl ethyl ketone was applied to a dry film thickness of 5 μm and cured by irradiating with ultraviolet rays to form a hard coat layer. The obtained film was subjected to 10 × 10 cross-cut after 100 hours in an environment of 80 ° C. and 90% RH, and then a 18 mm wide tape (cello tape (registered trademark) CT manufactured by Nichiban Co., Ltd.). -18) is pasted and the peeled surface is observed after being peeled off rapidly at a peeling angle of 180 °. If the peeled area is less than 3%, ◎ if it is 3% or more but less than 10%, ○, 10% or more and 50%. If it was less than △, it was marked as x if it was 50% or more.

The polyester used in the examples and comparative examples was prepared as follows.
<Method for producing polyester (A)>
100 parts by weight of dimethyl terephthalate, 60 parts by weight of ethylene glycol, 30 ppm of ethyl acid phosphate with respect to the resulting polyester, and 100 ppm of magnesium acetate tetrahydrate with respect to the resulting polyester as the catalyst at 260 ° C. in a nitrogen atmosphere at 260 ° C. The reaction was allowed to proceed. Subsequently, 50 ppm of tetrabutyl titanate was added to the resulting polyester, the temperature was raised to 280 ° C. over 2 hours and 30 minutes, the pressure was reduced to 0.3 kPa in absolute pressure, and melt polycondensation was further carried out for 80 minutes. 0.63 polyester (A) was obtained.

<Method for producing polyester (B)>
100 parts by weight of dimethyl terephthalate, 60 parts by weight of ethylene glycol, and magnesium acetate tetrahydrate as a catalyst were subjected to an esterification reaction at 225 ° C. in a nitrogen atmosphere at 900 ppm with respect to the produced polyester. Subsequently, 3500 ppm of orthophosphoric acid was added to the produced polyester, and 70 ppm of germanium dioxide was added to the produced polyester. The temperature was raised to 280 ° C. over 2 hours and 30 minutes, and the pressure was reduced to an absolute pressure of 0.4 kPa. After 85 minutes of melt polycondensation, polyester (B) having an intrinsic viscosity of 0.64 was obtained.

<Method for producing polyester (C)>
In the production method of polyester (A), polyester (C) is obtained using the same method as the production method of polyester (A) except that 0.3 part by weight of silica particles having an average particle diameter of 2 μm is added before melt polymerization. It was.

Examples of compounds constituting the coating layer are as follows.
(Example compounds)
Metal oxide: (IA) Zirconium oxide particles having an average particle diameter of 15 nm Metal oxide: (IB) Titanium oxide particles having an average particle diameter of 15 nm

・ Oxazoline compounds: (IIA)
Acrylic polymer having an oxazoline group and a polyalkylene oxide chain Epocros WS-500 (manufactured by Nippon Shokubai Co., Ltd., containing about 38% by weight of 1-methoxy-2-propanol solvent)
・ Oxazoline compounds: (IIB)
Acrylic polymer having an oxazoline group and a polyalkylene oxide chain Epocros WS-700 (manufactured by Nippon Shokubai Co., Ltd., VOC-free type)

Epoxy compound: (IIIA) Denacol EX-521 (manufactured by Nagase ChemteX Corporation), which is polyglycerol polyglycidyl ether.
Epoxy compound: (IIIB) Denacol EX-1410 (manufactured by Nagase ChemteX Corporation), which is an epoxy resin.

・ Condensed polycyclic aromatic polyester resin: (IVA)
Water dispersion of polyester resin copolymerized with the following composition: Monomer composition: (acid component) 2,6-naphthalenedicarboxylic acid / 5-sodium sulfoisophthalic acid // (diol component) ethylene glycol / diethylene glycol = 92/8 // 80/20 (mol%)
・ Polyester resin: (IVB)
Water dispersion of polyester resin copolymerized with the following composition: Monomer composition: (acid component) terephthalic acid / isophthalic acid / 5-sodium sulfoisophthalic acid // (diol component) ethylene glycol / 1,4-butanediol / diethylene glycol = 56/40/4 // 70/20/10 (mol%)
Acrylic resin: (IVC) Aqueous dispersion of acrylic resin polymerized with the following composition: ethyl acrylate / n-butyl acrylate / methyl methacrylate / N-methylol acrylamide / acrylic acid = 65/21/10/2/2 (% by weight) Emulsion polymer (emulsifier: anionic surfactant)
・ Urethane resin (IVD)
Hydran AP-40 (manufactured by DIC Corporation), which is a carboxylic acid water-dispersed polyester polyurethane resin

・ Hexamethoxymethylmelamine (V)
・ Particles: (VIA) Silica particles with an average particle size of 0.07 μm ・ Particles: (VIB) Silica particles with an average particle size of 0.15 μm

Example 1:
A mixed raw material obtained by mixing polyester (A) and (B) at a ratio of 95% and 5%, respectively, is used as a raw material for the intermediate layer, and polyesters (A), (B), and (C) are 89%, 5%, and 6%, respectively. % Of the mixed raw material mixed at a ratio of 2% as the raw material of the outermost layer (surface layer), each was supplied to two extruders, melted at 285 ° C., and then on a cooling roll set at 40 ° C. Coextruded and cooled and solidified with a layer structure of layers (surface layer / intermediate layer / surface layer = 1: 35: 1 discharge amount) to obtain an unstretched sheet. Next, the film was stretched 3.4 times in the longitudinal direction at a film temperature of 85 ° C. using the difference in peripheral speed of the roll, and then the coating liquid A1 shown in Table 1 below was applied to both surfaces of the longitudinally stretched film (formation of coating layer). , Led to a tenter, stretched 4.0 times at 120 ° C in the lateral direction, heat treated at 225 ° C, relaxed 2% in the lateral direction, and the coating layer thickness (after drying) was 0.10 µm A 100 μm thick polyester film having layers on both sides of the film was obtained.

  When the absolute reflectance of the coated layer of the obtained polyester film was measured, the minimum value was 600 nm, the reflectance was 5.0%, and there was no clear interference unevenness in the film after forming the hard coat layer. Also, the adhesion was good. The properties of this film are shown in Table 2 below.

Examples 2 to 21:
In Example 1, it manufactured similarly to Example 1 except having changed the coating agent composition into the coating agent composition shown in Table 1, and obtained the polyester film. As shown in Table 2, the finished polyester film had good adhesion of the coating layer, high reflectance, and good interference unevenness level.

Comparative Examples 1-5:
In Example 1, it manufactured similarly to Example 1 except having changed the coating agent composition into the coating agent composition shown in Table 1, and obtained the polyester film. When the completed laminated polyester film was evaluated, as shown in Table 3, when clear interference unevenness could be observed, the adhesion was inferior.

  The film of the present invention has, for example, a transparent electrode such as a touch panel or an electromagnetic shielding film, and has a conductive polymer conductive layer as a surface layer, and uses with importance on adhesion and visibility with a surface functional layer such as a hard coat layer. Can be suitably used.

Claims (5)

It is a coating layer formed from a coating liquid containing a metal oxide and two or more kinds of crosslinking agents, and the absolute reflectance of the coating layer surface has one minimum value in the wavelength range of 400 to 800 nm, Ri der absolute reflectance at the minimum value is 4.0% or more, and a coating layer in which the metal oxide is present as particles below an average particle size of 50nm has on both sides of the polyester film, the surface features on both of the coating layer A laminated polyester film for a conductive film , comprising a layer, wherein a conductive polymer layer is formed on at least one surface of the surface functional layer. The laminated polyester film for a conductive film according to claim 1, wherein the content of the metal oxide in the coating layer is 3 to 70% by weight. The laminated polyester film according to claim 1 or 2, wherein the metal oxide is zirconium oxide or titanium oxide. The laminated polyester film according to any one of claims 1 to 3 , comprising a condensed polycyclic aromatic compound in the coating layer. The laminated polyester film according to any one of claims 1 to 4 , wherein the crosslinking agent is an oxazoline compound or an epoxy compound.