JP5750247B2 - Organic thin film transistor and manufacturing method thereof - Google Patents

Description

  The present invention relates to an organic thin film transistor and a manufacturing method thereof, an organic thin film transistor substrate including an organic thin film transistor, and a display device including the organic thin film transistor substrate.

Thin film transistors can be broadly classified into organic thin film transistors and inorganic semiconductor transistors. An organic thin film transistor is provided with an organic semiconductor layer in an active layer, and an inorganic thin film transistor is provided with an inorganic semiconductor layer in an active layer. These two types of thin film transistors differ in their manufacturing methods.
Since an inorganic thin film transistor generally forms an active layer in a vacuum atmosphere, the formation of the active layer requires a vacuum atmosphere.
On the other hand, an organic thin film transistor can form an active layer by a coating method that does not require a vacuum atmosphere, and the formation of the active layer does not necessarily require a vacuum atmosphere. For example, in an organic thin film transistor, an active layer can be easily formed by applying and forming a coating solution in which an active layer material is dissolved or dispersed in any suitable solvent. By adopting the coating method in this manner, a vacuum atmosphere is not required, and a plurality of transistors can be formed at once in a wide range, thereby reducing the manufacturing cost.

  Various studies for improving the electrical characteristics of the organic thin film transistor having the advantages in the manufacturing process have been conducted. For example, an organic field effect transistor including an n-type organic semiconductor layer formed by coating a C60 fullerene derivative having a long-chain alkyl group is known (see Patent Document 1). In addition, an organic thin film transistor is known in which electrical characteristics are improved by providing a buffer layer made of lithium fluoride (LiF) between a source electrode and a drain electrode and an active layer (see Non-Patent Document 1). .)

JP 2006-060169 A

Microelectronics Journal Volume 38, Issues 4-5, April-May 2007, Pages 632-636

  Lithium fluoride or the like used for the buffer layer easily reacts with moisture and oxygen in an air atmosphere and oxidizes quickly. When the buffer layer is oxidized, the electrical characteristics of the organic thin film transistor are degraded.

  In order to prevent such oxidation of the buffer layer in the atmosphere, the conventional technique produces an organic thin film transistor without exposing the buffer layer to the atmosphere during and after the formation of the buffer layer. For example, in a high vacuum atmosphere, a buffer layer made of lithium fluoride or the like is formed by vapor deposition, and further, source / drain electrodes are formed on the buffer layer while maintaining this high vacuum atmosphere. Thus, the buffer layer is prevented from being exposed to the atmosphere. As described above, since the conventional technique requires a high vacuum atmosphere, not only a large-scale facility including a vacuum pump and a vacuum chamber which are unnecessary in the film forming process by the coating method is required. Since a process for loading into the chamber, a process for unloading from the vacuum chamber, a pressurizing process, a depressurizing process and the like are required, the manufacturing process becomes complicated and the manufacturing cost increases.

  The present invention has been made in view of the above problems, and an object of the present invention is to provide a charge injection layer using a material that is difficult to be oxidized and functionally difficult to be deteriorated even under an atmosphere of normal pressure. It is to provide an organic thin film transistor having excellent electrical characteristics, and further to provide a simple method for producing an organic thin film transistor including a step of forming a charge injection layer that can be carried out under an atmosphere of normal pressure. .

The inventors of the present invention have made extensive studies on ionic polymers and electronic devices using the ionic polymers, and are not only excellent in electrical characteristics but also difficult to oxidize even if produced in an atmosphere at atmospheric pressure, and are functional. The present inventors have found that the above problems can be solved by using an ionic polymer that hardly deteriorates, and have completed the present invention.
That is, according to the present invention, the following is provided.
[1] A gate electrode, a first source / drain electrode, a second source / drain electrode, and an organic semiconductor layer provided between the first and second source / drain electrodes and the gate electrode A charge injection layer disposed between the first and second source / drain electrodes and the organic semiconductor layer and in contact with the first and second source / drain electrodes; The injection layer is an organic thin film transistor containing an ionic polymer having charge injection characteristics.
[2] The organic thin film transistor according to [1], wherein the conductivity type charge injection layer is n-type and the organic semiconductor layer is n-type.
[3] The semiconductor device according to [2], further including a gate insulating layer disposed in contact with the gate electrode between the organic semiconductor layer and the gate electrode, wherein the gate electrode is formed of an n-type semiconductor substrate. Organic thin film transistor.
[4] An organic thin film transistor substrate comprising the organic thin film transistor according to any one of [1] to [3].
[5] A display device comprising the organic thin film transistor substrate according to [4] as a drive substrate.
[6] A gate electrode, a first source / drain electrode, a second source / drain electrode, an organic semiconductor layer provided between the first and second source / drain electrodes and the gate electrode, An organic thin film transistor that forms a charge injection layer disposed in contact with the first and second source / drain electrodes between the first and second source / drain electrodes and the organic semiconductor layer, respectively. In the manufacturing method of
A method for producing an organic thin film transistor, comprising a step of forming a charge injection layer containing an ionic polymer having charge injection characteristics.
[7] In the step of forming the charge injection layer, the charge injection layer is formed by coating and forming a coating liquid containing an ionic polymer under an atmospheric pressure atmosphere. Manufacturing method of organic thin-film transistor.
[8] The method for producing an organic thin film transistor according to [6] or [7], wherein the first and second source / drain electrodes are formed by applying and forming a coating solution in an atmospheric pressure atmosphere. .
[9] The method for producing an organic thin film transistor according to any one of [6] to [8], wherein the organic semiconductor layer is formed by applying and forming a coating solution in an atmospheric pressure.

The organic thin film transistor of the present invention has excellent charge injection characteristics, and an ionic polymer that can maintain good charge injection characteristics in an atmosphere of about normal pressure, or even in an air atmosphere, is used as a material for the charge injection layer. Therefore, the performance of the organic thin film transistor of the present invention is unlikely to deteriorate even in an atmosphere of about normal pressure, or even in an air atmosphere.
In addition, according to the method for producing an organic thin film transistor of the present invention, an ionic polymer that is not easily oxidized even in an atmosphere of about normal pressure or even in an air atmosphere is used as a material for the charge injection layer. Therefore, the formation process of the charge injection layer can be performed by a coating method in an atmosphere of about normal pressure, and further in an air atmosphere, so that the organic thin film transistor can be manufactured more easily and the manufacturing cost is remarkably increased. Can be reduced.

FIG. 1 is a cross-sectional view schematically showing an example of the configuration of the organic thin film transistor of the first embodiment. FIG. 2 is a cross-sectional view schematically showing an example of the configuration of the organic thin film transistor of the second embodiment. FIG. 3 is a graph illustrating the electrical characteristics of the ionic polymer.

  Hereinafter, embodiments of the present invention will be described with reference to the drawings. In addition, each figure has shown only the shape of the component, the magnitude | size, and arrangement | positioning to such an extent that an invention can be understood. The present invention is not limited to the following description, and each component can be appropriately changed without departing from the gist of the present invention. In the drawings used for the following description, the same components are denoted by the same reference numerals, and redundant description may be omitted. The organic EL device of the present invention is not necessarily manufactured or used in the illustrated arrangement. In the following description, in particular, one in the thickness direction of the substrate may be referred to as “up” or “upper”, and the other in the thickness direction may be referred to as “down” or “lower”.

<Configuration of organic thin film transistor>
The organic thin film transistor includes a gate electrode, a first source / drain electrode, a second source / drain electrode, and an organic semiconductor layer provided between the first and second source / drain electrodes and the gate electrode. And a charge injection layer disposed in contact with the first and second source / drain electrodes between the first and second source / drain electrodes and the organic semiconductor layer. This organic thin film transistor has a function of controlling a current flowing between the first source / drain electrode and the second source / drain electrode by adjusting a voltage applied to the gate electrode.

  The charge injection layer of the organic thin film transistor of the present invention contains an ionic polymer having charge injection characteristics.

The conductivity type of the charge injection layer and the conductivity type of the organic semiconductor layer are preferably the same. That is, if the charge injection layer is n-type, the organic semiconductor layer is preferably n-type. If the charge injection layer is p-type, the organic semiconductor layer is preferably p-type.
In the present specification, the term “source / drain electrode” means one electrode used as a source electrode or a drain electrode, and one of the first and second source / drain electrodes is a source when an organic thin film transistor is used. Used as an electrode, the other is used as a drain electrode.

  The organic thin film transistor of the present invention is characterized by an ionic polymer constituting the charge injection layer. For this reason, the ionic polymer will be described first.

(Ionic polymer)
Examples of the ionic polymer that can be used in the present invention include structural units containing one or more groups selected from the group consisting of a group represented by the following formula (1) and a group represented by the following formula (2). The polymer which has is mentioned. As one form of the ionic polymer, a structural unit containing one or more groups selected from the group consisting of the group represented by the formula (1) and the group represented by the formula (2), The polymer which has 15-100 mol% is mentioned.

− (Q ¹ ) _n1 −Y ¹ (M ¹ ) a ₁ (Z ¹ ) _{b 1} (1)
(In formula (1), Q ¹ represents a divalent organic group, Y ¹ represents —CO ₂ ⁻ , —SO ₃ ⁻ , —SO ₂ ^— or —PO ₃ ²⁻ , and M ¹ represents a metal cation. Or an ammonium cation with or without a substituent, and Z ¹ is F ⁻ , Cl ⁻ , Br ⁻ , I ⁻ , OH ⁻ , R ^a SO ₃ ⁻ , R ^a COO ⁻ , ClO ⁻ , ClO ₂ ^−. , ClO ₃ ⁻ , ClO ₄ ⁻ , SCN ⁻ , CN ⁻ , NO ₃ ⁻ , SO ₄ ²⁻ , HSO ₄ ⁻ , PO ₄ ³⁻ , HPO ₄ ²⁻ , H ₂ PO ₄ ⁻ , BF ₄ ⁻ or PF ₆ ^- , N1 represents an integer of 0 or more, a1 represents an integer of 1 or more, b1 represents an integer of 0 or more, provided that a1 and b1 represent the charge of the group represented by the formula (1) 0 is chosen to be, R ^a is -C not have or have an alkyl group or a substituent having 1 to 30 carbon atoms which does not have or have a substituent having 6 to 50 It represents an aryl group, Q ^1, each of M ¹ and Z ¹ when a plurality, may be the same or different.)

_{^{- (Q 2) n2 -Y 2}} (M 2) a2 (Z 2) b2 (2)
(In the formula (2),
Q ² represents a divalent organic group,
Y ² represents a carbo cation, an ammonium cation, a phosphonyl cation or a sulfonyl cation or an iodonium cation, and M ² represents F ⁻ , Cl ⁻ , Br ⁻ , I ⁻ , OH ⁻ , R ^b SO ₃ ⁻ , R ^b COO ⁻ , ClO ⁻ , ClO ₂ ⁻ , ClO ₃ ⁻ , ClO ₄ ⁻ , SCN ⁻ , CN ⁻ , NO ₃ ⁻ , SO ₄ ²⁻ , HSO ₄ ⁻ , PO ₄ ³⁻ , HPO ₄ ²⁻ , H ₂ PO ₄ ⁻ , BF ₄ ^- or PF ₆ ^- represents, Z ² represents an ammonium cation which does not have or have a metal cation or a substituent, n2 represents an integer of 0 or more, a2 represents an integer of 1 or more, b2 is Represents an integer of 0 or more, provided that a2 and b2 are selected such that the charge of the group represented by the formula (2) is 0, and ^Rb has 1 or no carbon atoms. Charcoal with or without -30 alkyl groups or substituents It represents an aryl group having the number of atoms of 6-50, each of Q ^2, M ² and Z ² are when a plurality, may be the same or different. )

  One form of the ionic polymer used in the present invention further includes a polymer having a group represented by the following formula (3). When the ionic polymer has a group represented by the formula (3), the group represented by the formula (3) may be contained in the structural unit of the ionic polymer, and is represented by the formula (1). And may be contained in the same structural unit as the structural unit containing one or more groups selected from the group consisting of the group represented by formula (2), or may be contained in another different structural unit. It may be. Furthermore, as one form of the ionic polymer, a structural unit containing at least one of a group represented by the formula (1), a group represented by the formula (2), and a group represented by the formula (3) Is a polymer having 15 to 100 mol% in all structural units.

− (Q ³ ) _n3 −Y ³ (3)
(In formula (3),
Q ³ represents a divalent organic group, Y ³ represents —CN or a group represented by any one of formulas (4) to (12), and n3 represents an integer of 0 or more.
-O- (R'O) _a3 -R '' (4)

-S- (R'S) _a4 -R '' (6)
-C (= O)-(R'-C (= O)) _a4 -R '' (7)
-C (= S)-(R'-C (= S)) _a4 -R '' (8)
-N {(R ′) _a4 R ″} ₂ (9)
—C (═O) O— (R′—C (═O) O) _a4 —R ″ (10)
-C (= O) O- (R'O) _a4- R "(11)
—NHC (═O) — (R′NHC (═O)) _a4 —R ″ (12)

(In the formulas (4) to (12), R ′ represents a divalent hydrocarbon group with or without a substituent, and R ″ represents a hydrogen atom, a monovalent with or without a substituent. Or —COOH, —SO ₃ H, —OH, —SH, —NR ^c ₂ , —CN or —C (═O) NR ^c ₂ , wherein R ′ ″ has a substituent, or Represents a trivalent hydrocarbon group not having, a3 represents an integer of 1 or more, a4 represents an integer of 0 or more, and R ^c is an alkyl having 1 to 30 carbon atoms with or without a substituent. An aryl group having 6 to 50 carbon atoms, with or without a group or substituent, may be the same or different when there are a plurality of R ′, R ″ and R ′ ″. ))

  The ionic polymer is composed of a structural unit represented by formula (13), a structural unit represented by formula (15), a structural unit represented by formula (17), and a structural unit represented by formula (20). It is preferable that 15-100 mol% of 1 or more types of structural units chosen from a group are included in all the structural units.

(In the formula (13), R ¹ is a monovalent group including a group represented by the formula (14), and Ar ¹ has a (2 + n4) -valent fragrance with or without a substituent other than R ^1. Represents a group, n4 represents an integer of 1 or more, and when there are a plurality of R ^{1 s} , they may be the same or different.

(In the formula (14), R ² represents a (1 + m1 + m2) -valent organic group, and Q ¹ , Q ³ , Y ¹ , M ¹ , Z ¹ , Y ³ , n1, a1, b1, and n3 have the same meaning as described above. M1 and m2 each independently represent an integer of 1 or more, and when Q ¹ , Q ³ , Y ¹ , M ¹ , Z ¹ , Y ³ , n1, a1, b1 and n3 are plural, May be the same or different.))

(In the formula (15), R ³ is a monovalent group including a group represented by the formula (16), and Ar ² has a (2 + n5) -valent fragrance with or without a substituent other than R ^3. Represents a group, n5 represents an integer of 1 or more, and when there are a plurality of R ^{3 s} , they may be the same or different.

(In the formula (16), R ⁴ represents a (1 + m3 + m4) -valent organic group, and Q ² , Q ³ , Y ² , M ² , Z ² , Y ³ , n 2, a 2, b 2 and n 3 have the same meaning as described above. M3 and m4 each independently represents an integer greater than or equal to 1. When there are a plurality of Q ² , Q ³ , Y ² , M ² , Z ² , Y ³ , n 2, a 2, b 2 and n 3, May be the same or different.))

(In the formula (17), R ⁵ is a monovalent group containing a group represented by the formula (18), R ⁶ is a monovalent group containing a group represented by the formula (19), Ar ³ represents a (2 + n6 + n7) -valent aromatic group having or not having a substituent other than R ⁵ and R ⁶ , n6 and n7 each independently represents an integer of 1 or more, and each of R ⁵ and R ⁶ May be the same or different when there are multiple.
^{-R 7 - {(Q 1)} n1 -Y 1 (M 1) a1 (Z 1) b1} m5 (18)

(In formula (18), R ⁷ represents a direct bond or a (1 + m5) -valent organic group, Q ¹ , Y ¹ , M ¹ , Z ¹ , n1, a1, and b1 represent the same meaning as described above, and m5 represents Represents an integer of 1 or more, and when there are a plurality of Q ¹ , Y ¹ , M ¹ , Z ¹ , n ¹ , a 1 and b ¹ , they may be the same or different.
^{-R 8 - {(Q 3)} n3 -Y 3} m6 (19)

(In Formula (19), R ⁸ represents a single bond or a (1 + m6) -valent organic group, Y ³ and n3 represent the same meaning as described above, m6 represents an integer of 1 or more, provided that R ⁸ is a single group. M6 represents 1 when bonded, and when there are a plurality of Q ³ , Y ³ and n3, they may be the same or different.))

(In the formula (20), R ⁹ is a monovalent group containing a group represented by the formula (21), R ¹⁰ is a monovalent group containing a group represented by the formula (22), Ar ⁴ represents a (2 + n8 + n9) -valent aromatic group having or not having a substituent other than R ⁹ and R ¹⁰ , n8 and n9 each independently represents an integer of 1 or more, and each of R ⁹ and R ¹⁰ May be the same or different when there are multiple.
^{-R 11 - {(Q 2)} n2 -Y 2 (M 2) a2 (Z 2) b2} m7 (21)

(In the formula (21), R ¹¹ represents a single bond or a (1 + m7) -valent organic group, Q ² , Y ² , M ² , Z ² , n ² , a 2 and b 2 represent the same meaning as described above, and m 7 represents Represents an integer of 1 or more, provided that when R ¹¹ is a single bond, m7 represents 1, and when there are a plurality of Q ² , Y ² , M ² , Z ² , n ² , a 2 and b ² , they are the same or different. May be.)
^{-R 12 - {(Q 3)} n3 -Y 3} m8 (22)

(In the formula (22), R ¹² represents a single bond or a (1 + m8) -valent organic group, Y ³ and n3 represent the same meaning as described above, m8 represents an integer of 1 or more, provided that R ¹² is a single group. When bonded, m8 represents 1, and when there are a plurality of Q ³ , Y ³ and n3, they may be the same or different.))

  The structural unit in the ionic polymer may contain two or more groups represented by the formula (1), may contain two or more groups represented by the formula (2), Two or more groups represented by 3) may be included.

-Group represented by Formula (1)-
In formula (1), examples of the divalent organic group represented by Q ¹ include a methylene group, an ethylene group, a 1,2-propylene group, a 1,3-propylene group, a 1,2-butylene group, 1,3. -Butylene group, 1,4-butylene group, 1,5-pentylene group, 1,6-hexylene group, 1,9-nonylene group, 1,12-dodecylene group, at least one hydrogen in these groups A divalent saturated hydrocarbon group having 1 to 50 carbon atoms, which may or may not have a substituent, such as a group in which an atom is substituted with a substituent; an ethenylene group, a propenylene group, a 3-butenylene group, a 2-butenylene group , 2-pentenylene group, 2-hexenylene group, 2-nonenylene group, 2-dodecenylene group, and a group having or having a substituent such as a group in which at least one hydrogen atom in these groups is substituted with a substituent. An alkenylene group having 2 to 50 carbon atoms, And a divalent unsaturated hydrocarbon group having 2 to 50 carbon atoms, including or not having a substituent, including an ethynylene group; a cyclopropylene group, a cyclobutylene group, a cyclopentylene group, a cyclohexylene group, 3 to 50 carbon atoms having or not having a substituent, such as a cyclononylene group, a cyclododecylene group, a norbornylene group, an adamantylene group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. Divalent cyclic saturated hydrocarbon group: 1,3-phenylene group, 1,4-phenylene group, 1,4-naphthylene group, 1,5-naphthylene group, 2,6-naphthylene group, biphenyl-4,4 An arylene group having 6 to 50 carbon atoms, which may or may not have a substituent, such as a '-diyl group, a group obtained by substituting at least one hydrogen atom of these groups with a substituent; a methyleneoxy group; Echi Having a substituent such as a nonoxy group, a propyleneoxy group, a butyleneoxy group, a pentyleneoxy group, a hexyleneoxy group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. An alkyleneoxy group having 1 to 50 carbon atoms; an imino group having a substituent containing a carbon atom; a silylene group having a substituent containing a carbon atom, and a monomer (hereinafter, “ From the viewpoint of ease of synthesis of the “raw material monomer”, a divalent saturated hydrocarbon group, an arylene group, and an alkyleneoxy group are preferable.

  Examples of the substituent include an alkyl group, an alkoxy group, an alkylthio group, an aryl group, an aryloxy group, an arylthio group, an arylalkyl group, an arylalkoxy group, an arylalkylthio group, an arylalkenyl group, an arylalkynyl group, an amino group, and a substituted amino group. Group, silyl group, substituted silyl group, halogen atom, acyl group, acyloxy group, imine residue, amide group, acid imide group, monovalent heterocyclic group, hydroxy group, carboxyl group, substituted carboxyl group, cyano group and nitro Group, etc., and when a plurality of the substituents are present, they may be the same or different. Of these, substituents other than amino groups, silyl groups, halogen atoms, hydroxy groups, and nitro groups contain carbon atoms.

Hereinafter, the substituent will be described. The term “C _{m to} C _n ” (m, n is a positive integer satisfying m <n) represents that the organic group described together with this term has m to n carbon atoms. . For _example, if C m -C _n alkyl group represents the number of carbon atoms in the alkyl group is from m to _n, as long as C m -C _n alkyl aryl group, the number of carbon atoms in the alkyl group m~ If it is an aryl-Cm-Cn alkyl group, it represents that the carbon atom number of an alkyl group is _{m- n} .

The alkyl group may be linear or branched, and may be a cycloalkyl group. The number of carbon atoms in the alkyl group is usually from 1 to 20, and preferably from 1 to 10. As the alkyl group, methyl group, ethyl group, propyl group, isopropyl group, butyl group, isobutyl group, s-butyl group, t-butyl group, pentyl group, hexyl group, cyclohexyl group, heptyl group, octyl group, nonyl group Decyl group, lauryl group and the like. A hydrogen atom in the alkyl group may be substituted with a fluorine atom. Examples of the fluorine atom-substituted alkyl group include a trifluoromethyl group, a pentafluoroethyl group, a perfluorobutyl group, a perfluorohexyl group, and a perfluorooctyl group. Examples of the C _{1 to} C ₁₂ alkyl group include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an s-butyl group, a t-butyl group, a pentyl group, an isoamyl group, and a hexyl group. Cyclohexyl group, heptyl group, octyl group, nonyl group, decyl group and lauryl group.

The alkoxy group may be linear or branched, may be a cycloalkyloxy group, and may have a substituent. The number of carbon atoms of the alkoxy group is usually from 1 to 20, and preferably from 1 to 10. As the alkoxy group, methoxy group, ethoxy group, propyloxy group, isopropyloxy group, butoxy group, isobutoxy group, s-butoxy group, t-butoxy group, pentyloxy group, hexyloxy group, cyclohexyloxy group, heptyloxy group Octyloxy group, nonyloxy group, decyloxy group, lauryloxy group and the like. A hydrogen atom in the alkoxy group may be substituted with a fluorine atom. Examples of the fluorine atom-substituted alkoxy group include a trifluoromethoxy group, a pentafluoroethoxy group, a perfluorobutoxy group, a perfluorohexyloxy group, and a perfluorooctyloxy group. The alkoxy group also includes a methoxymethyloxy group and a 2-methoxyethyloxy group. Examples of the C _{1 to} C ₁₂ alkoxy group include a methoxy group, an ethoxy group, a propyloxy group, an isopropyloxy group, a butoxy group, an isobutoxy group, an s-butoxy group, a t-butoxy group, a pentyloxy group, and a hexyloxy group. Group, cyclohexyloxy group, heptyloxy group, octyloxy group, 2-ethylhexyloxy group, nonyloxy group, decyloxy group, 3,7-dimethyloctyloxy group, lauryloxy group.

  The alkylthio group may be linear or branched, may be a cycloalkylthio group, and may have a substituent. The number of carbon atoms of the alkylthio group is usually 1-20, and preferably 1-10. As the alkylthio group, methylthio group, ethylthio group, propylthio group, isopropylthio group, butylthio group, isobutylthio group, s-butylthio group, t-butylthio group, pentylthio group, hexylthio group, cyclohexylthio group, heptylthio group, octylthio group , Nonylthio group, decylthio group, laurylthio group and the like. A hydrogen atom in the alkylthio group may be substituted with a fluorine atom. Examples of the fluorine atom-substituted alkylthio group include a trifluoromethylthio group.

An aryl group is an atomic group obtained by removing one hydrogen atom bonded to a carbon atom constituting an aromatic ring from an aromatic hydrocarbon, and is a group having a benzene ring, a group having a condensed ring, an independent benzene ring or A group in which two or more fused rings are bonded via a single bond or a divalent organic group, for example, an alkenylene group such as a vinylene group is also included. The aryl group usually has 6 to 60 carbon atoms and preferably 7 to 48 carbon atoms. Examples of the aryl group include a phenyl group, C ₁ -C ₁₂ alkoxyphenyl group, C ₁ -C ₁₂ alkylphenyl group, 1-naphthyl, 2-naphthyl, 1-anthracenyl group, 9-anthracenyl group Etc. A hydrogen atom in the aryl group may be substituted with a fluorine atom. Examples of the fluorine atom-substituted aryl group include a pentafluorophenyl group. Among the aryl groups, a C _{1 to} C ₁₂ alkoxyphenyl group and a C _{1 to} C ₁₂ alkylphenyl group are preferable.

Among the aryl groups, the C _{1 to} C ₁₂ alkoxyphenyl group includes a methoxyphenyl group, an ethoxyphenyl group, a propyloxyphenyl group, an isopropyloxyphenyl group, a butoxyphenyl group, an isobutoxyphenyl group, an s-butoxyphenyl group, t-butoxyphenyl group, pentyloxyphenyl group, hexyloxyphenyl group, cyclohexyloxyphenyl group, heptyloxyphenyl group, octyloxyphenyl group, 2-ethylhexyloxyphenyl group, nonyloxyphenyl group, decyloxyphenyl group, 3, Examples include 7-dimethyloctyloxyphenyl group, lauryloxyphenyl group, and the like.

Wherein one aryl group, the C ₁ -C ₁₂ alkylphenyl group include a methylphenyl group, ethylphenyl group, dimethylphenyl group, propylphenyl group, mesityl group, methylethylphenyl group, isopropylphenyl group, butylphenyl group, isobutyl Examples include phenyl group, t-butylphenyl group, pentylphenyl group, isoamylphenyl group, hexylphenyl group, heptylphenyl group, octylphenyl group, nonylphenyl group, decylphenyl group, dodecylphenyl group and the like.

The aryloxy group usually has 6 to 60 carbon atoms and preferably 7 to 48 carbon atoms. The aryloxy group is a phenoxy group, C ₁ -C ₁₂ alkoxy phenoxy group, C ₁ -C ₁₂ alkylphenoxy group, 1-naphthyloxy group, 2-naphthyloxy group, a pentafluorophenyl group and the like. Among the aryloxy groups, C ₁ -C ₁₂ alkoxy phenoxy group, and a C ₁ -C ₁₂ alkylphenoxy group are preferable.

Among the aryloxy group, the C ₁ -C ₁₂ alkoxy phenoxy group, methoxyphenoxy group, ethoxyphenoxy group, propyloxy phenoxy group, isopropyloxy phenoxy group, butoxyphenoxy group, isobutoxyphenoxy phenoxy group, s- butoxyphenoxy group , T-butoxyphenoxy group, pentyloxyphenoxy group, hexyloxyphenoxy group, cyclohexyloxyphenoxy group, heptyloxyphenoxy group, octyloxyphenoxy group, 2-ethylhexyloxyphenoxy group, nonyloxyphenoxy group, decyloxyphenoxy group, 3 , 7-dimethyloctyloxyphenoxy group, lauryloxyphenoxy group, and the like.

Among the aryloxy groups, the C _{1 to} C ₁₂ alkylphenoxy group includes methylphenoxy group, ethylphenoxy group, dimethylphenoxy group, propylphenoxy group, 1,3,5-trimethylphenoxy group, methylethylphenoxy group, isopropyl Phenoxy group, butylphenoxy group, isobutylphenoxy group, s-butylphenoxy group, t-butylphenoxy group, pentylphenoxy group, isoamylphenoxy group, hexylphenoxy group, heptylphenoxy group, octylphenoxy group, nonylphenoxy group, decylphenoxy group And dodecylphenoxy group.

The arylthio group is, for example, a group in which a sulfur element is bonded to the aforementioned aryl group. The arylthio group may have a substituent on the aromatic ring of the aryl group. The arylthio group usually has 6 to 60 carbon atoms, and preferably 6 to 30 carbon atoms. The arylthio group, a phenylthio group, C ₁ -C ₁₂ alkoxyphenyl-thio group, C ₁ -C ₁₂ alkyl phenylthio group, 1-naphthylthio group, 2-naphthylthio group, pentafluorophenylthio group and the like.

The arylalkyl group is, for example, a group in which the above alkyl group is bonded to the above aryl group. The arylalkyl group may have a substituent. The arylalkyl group usually has 7 to 60 carbon atoms, and preferably 7 to 30 carbon atoms. The aryl alkyl group, a phenyl -C ₁ -C ₁₂ alkyl group, C ₁ -C ₁₂ alkoxyphenyl -C ₁ -C ₁₂ alkyl group, C ₁ -C ₁₂ alkylphenyl -C ₁ -C ₁₂ alkyl group, 1- naphthyl -C ₁ -C ₁₂ alkyl group, 2-naphthyl -C ₁ -C ₁₂ alkyl group, and the like.

The arylalkoxy group is, for example, a group in which the above alkoxy group is bonded to the above aryl group. The arylalkoxy group may have a substituent. The arylalkoxy group usually has 7 to 60 carbon atoms, and preferably 7 to 30 carbon atoms. The arylalkoxy group, a phenyl -C ₁ -C ₁₂ alkoxy group, C ₁ -C ₁₂ alkoxyphenyl -C ₁ -C ₁₂ alkoxy group, C ₁ -C ₁₂ alkylphenyl -C ₁ -C ₁₂ alkoxy group, 1- naphthyl -C ₁ -C ₁₂ alkoxy groups, 2-naphthyl -C ₁ -C ₁₂ alkoxy groups and the like.

The arylalkylthio group is, for example, a group in which the aforementioned alkylthio group is bonded to the aforementioned aryl group. The arylalkylthio group may have a substituent. The arylalkylthio group usually has 7 to 60 carbon atoms, and preferably 7 to 30 carbon atoms. Arylalkylthio group, phenyl -C ₁ -C ₁₂ alkylthio group, C ₁ -C ₁₂ alkoxyphenyl -C ₁ -C ₁₂ alkylthio group, C ₁ -C ₁₂ alkylphenyl -C ₁ -C ₁₂ alkylthio group, 1- naphthyl -C ₁ -C ₁₂ alkylthio group, 2-naphthyl -C ₁ -C ₁₂ alkylthio groups and the like.

The arylalkenyl group is, for example, a group in which an alkenyl group is bonded to the aforementioned aryl group. The arylalkenyl group usually has 8 to 60 carbon atoms, and preferably 8 to 30 carbon atoms. Arylalkenyl group, a phenyl -C ₂ -C ₁₂ alkenyl group, C ₁ -C ₁₂ alkoxyphenyl -C ₂ -C ₁₂ alkenyl group, C ₁ -C ₁₂ alkylphenyl -C ₂ -C ₁₂ alkenyl group, 1- naphthyl -C ₂ -C ₁₂ alkenyl group, 2-naphthyl -C ₂ -C ₁₂ alkenyl groups and the like, C ₁ -C ₁₂ alkoxyphenyl -C ₂ -C ₁₂ alkenyl group, C ₂ -C ₁₂ alkylphenyl - C ₂ -C ₁₂ alkenyl groups are preferred. As the C ₂ -C ₁₂ alkenyl group include a vinyl group, 1-propenyl, 2-propenyl, 1-butenyl, 2-butenyl, 1-pentenyl group, 2-pentenyl group, 1-hexenyl Group, 2-hexenyl group and 1-octenyl group.

The arylalkynyl group is, for example, a group in which an alkynyl group is bonded to the aforementioned aryl group. The arylalkynyl group usually has 8 to 60 carbon atoms, and preferably 8 to 30 carbon atoms. The arylalkynyl group, a phenyl -C ₂ -C ₁₂ alkynyl group, C ₁ -C ₁₂ alkoxyphenyl -C ₂ -C ₁₂ alkynyl group, C ₁ -C ₁₂ alkylphenyl -C ₂ -C ₁₂ alkynyl group, 1- naphthyl -C ₂ -C ₁₂ alkynyl group, 2-naphthyl -C ₂ -C ₁₂ alkynyl groups and the like, C ₁ -C ₁₂ alkoxyphenyl -C ₂ -C ₁₂ alkynyl group, C ₁ -C ₁₂ alkylphenyl - C ₂ -C ₁₂ alkynyl group are preferable. Examples of the C _{2 to} C ₁₂ alkynyl group include ethynyl group, 1-propynyl group, 2-propynyl group, 1-butynyl group, 2-butynyl group, 1-pentynyl group, 2-pentynyl group and 1-hexynyl. Group, 2-hexynyl group, 1-octynyl group.

As the substituted amino group, at least one hydrogen atom in the amino group is substituted with one or two groups selected from the group consisting of an alkyl group, an aryl group, an arylalkyl group, and a monovalent heterocyclic group. The amino group formed is preferred. The alkyl group, aryl group, arylalkyl group or monovalent heterocyclic group may have a substituent. The number of carbon atoms of the substituted amino group is usually 1 to 60 without including the number of carbon atoms of the substituent that the alkyl group, aryl group, arylalkyl group or monovalent heterocyclic group may have, 2 to 48 are preferred. Examples of substituted amino groups include methylamino group, dimethylamino group, ethylamino group, diethylamino group, propylamino group, dipropylamino group, isopropylamino group, diisopropylamino group, butylamino group, isobutylamino group, and s-butylamino. Group, t-butylamino group, pentylamino group, hexylamino group, cyclohexylamino group, heptylamino group, octylamino group, 2-ethylhexylamino group, nonylamino group, decylamino group, 3,7-dimethyloctylamino group, lauryl amino group, cyclopentylamino group, dicyclopentylamino group, cyclohexylamino group, dicyclohexylamino group, ditrifluoromethylamino group, phenylamino group, diphenylamino group, (C ₁ -C ₁₂ alkoxyphenyl) amino group Di (C ₁ -C ₁₂ alkoxyphenyl) amino group, di (C ₁ -C ₁₂ alkylphenyl) amino groups, 1-naphthylamino group, 2-naphthylamino group, pentafluorophenylamino group, pyridylamino group, Piridajini arylamino group, pyrimidylamino group, pyrazinylamino group, triazinylamino group, (phenyl -C ₁ -C ₁₂ alkyl) amino group, (C ₁ -C ₁₂ alkoxyphenyl -C ₁ -C ₁₂ alkyl) amino group, (C _{1 to} C ₁₂ alkylphenyl-C _{1 to} C ₁₂ alkyl) amino group, di (C _{1 to} C ₁₂ alkoxyphenyl-C _{1 to} C ₁₂ alkyl) amino group, di (C _{1 to} C ₁₂ alkylphenyl-C ₁ to C ₁₂ alkyl) amino group, 1-naphthyl-C ₁ -C ₁₂ alkylamino group, 2-naphthyl-C ₁ -C ₁₂ alkylamino group and the like.

As the substituted silyl group, at least one hydrogen atom in the silyl group is substituted by 1 to 3 groups selected from the group consisting of an alkyl group, an aryl group, an arylalkyl group and a monovalent heterocyclic group Silyl group formed. The alkyl group, aryl group, arylalkyl group or monovalent heterocyclic group may have a substituent. The number of carbon atoms of the substituted silyl group is usually 1 to 60 without including the number of carbon atoms of the substituent that the alkyl group, aryl group, arylalkyl group or monovalent heterocyclic group may have, 3 to 48 are preferred. The substituted silyl groups include trimethylsilyl, triethylsilyl, tripropylsilyl, triisopropylsilyl, isopropyldimethylsilyl, isopropyldiethylsilyl, t-butyldimethylsilyl, pentyldimethylsilyl, hexyldimethylsilyl. group, heptyl dimethylsilyl group, octyldimethylsilyl group, 2-ethylhexyl-dimethylsilyl group, nonyldimethylsilyl group, decyldimethylsilyl group, a 3,7-dimethyl silyl group, lauryl dimethyl silyl group, (phenyl -C ₁ ~ C ₁₂ alkyl) silyl group, (C ₁ -C ₁₂ alkoxyphenyl-C ₁ -C ₁₂ alkyl) silyl group, (C ₁ -C ₁₂ alkylphenyl-C ₁ -C ₁₂ alkyl) silyl group, (1-naphthyl- C ₁ -C ₁₂ alkyl) silyl , (2-naphthyl -C ₁ -C ₁₂ alkyl) silyl group, (phenyl -C ₁ -C ₁₂ alkyl) dimethyl silyl group, a triphenylsilyl group, tri (p- xylyl) silyl group, tribenzylsilyl group, diphenyl Examples thereof include a methylsilyl group, a t-butyldiphenylsilyl group, and a dimethylphenylsilyl group.

  Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.

  The acyl group usually has 2 to 20 carbon atoms, and preferably 2 to 18 carbon atoms. Examples of the acyl group include an acetyl group, a propionyl group, a butyryl group, an isobutyryl group, a pivaloyl group, a benzoyl group, a trifluoroacetyl group, and a pentafluorobenzoyl group.

  The acyloxy group usually has 2 to 20 carbon atoms, and preferably 2 to 18 carbon atoms. Examples of the acyloxy group include an acetoxy group, a propionyloxy group, a butyryloxy group, an isobutyryloxy group, a pivaloyloxy group, a benzoyloxy group, a trifluoroacetyloxy group, and a pentafluorobenzoyloxy group.

The imine residue means a residue obtained by removing one hydrogen atom in this structure from an imine compound having a structure represented by at least one of the formula: HN═C <and the formula: —N═CH—. To do. Examples of such imine compounds include compounds in which a hydrogen atom bonded to a nitrogen atom in aldimine, ketimine, and aldimine is substituted with an alkyl group, aryl group, arylalkyl group, arylalkenyl group, arylalkynyl group, or the like. It is done. The number of carbon atoms in the imine residue is usually 2-20, and 2-18 is preferred. Examples of the imine residue include a general formula: —CR ^β = N—R ^γ or a general formula: —N═C (R ^γ ) ₂ (wherein R ^β is a hydrogen atom, an alkyl group, an aryl group, an arylalkyl) Group, an arylalkenyl group, or an arylalkynyl group, and R ^γ independently represents an alkyl group, an aryl group, an arylalkyl group, an arylalkenyl group, or an arylalkynyl group, provided that two R ^γ are present. Two R ^γ are bonded to each other to form a divalent group, for example, an alkylene group having 2 to 18 carbon atoms such as ethylene group, trimethylene group, tetramethylene group, pentamethylene group, hexamethylene group, etc. As a ring may be formed.). Examples of the imine residue include the following groups.

  (In the formula, Me represents a methyl group, and the same shall apply hereinafter.)

  The amide group usually has 1 to 20 carbon atoms, and preferably 2 to 18 carbon atoms. As the amide group, formamide group, acetamide group, propioamide group, butyroamide group, benzamide group, trifluoroacetamide group, pentafluorobenzamide group, diformamide group, diacetamide group, dipropioamide group, dibutyroamide group, dibenzamide group, ditrifluoro Examples include an acetamide group and a dipentafluorobenzamide group.

  The acid imide group is a residue obtained by removing a hydrogen atom bonded to the nitrogen atom from an acid imide, and usually has 4 to 20 carbon atoms, and preferably 4 to 18 carbon atoms. Examples of the acid imide group include the following groups.

The monovalent heterocyclic group refers to the remaining atomic group obtained by removing one hydrogen atom from a heterocyclic compound. Here, the heterocyclic compound is not only a carbon atom but also an oxygen atom, a sulfur atom, a nitrogen atom, a phosphorus atom, a boron atom, a silicon atom as an element constituting a ring among organic compounds having a cyclic structure. , An organic compound containing a hetero atom such as a selenium atom, a tellurium atom or an arsenic atom. The monovalent heterocyclic group may have a substituent. The monovalent heterocyclic group usually has 3 to 60 carbon atoms, and preferably 3 to 20 carbon atoms. The number of carbon atoms of the monovalent heterocyclic group does not include the number of carbon atoms of the substituent. Examples of such a monovalent heterocyclic group, for example, thienyl group, C ₁ -C ₁₂ alkyl thienyl group, a pyrrolyl group, a furyl group, a pyridyl group, C ₁ -C ₁₂ alkyl pyridyl group, pyridazinyl group, pyrimidyl group, pyrazinyl group, triazinyl group, pyrrolidyl group, piperidyl group, quinolyl group and isoquinolyl group, and among them, a thienyl group, C ₁ -C ₁₂ alkyl thienyl group, pyridyl group and C ₁ -C ₁₂ alkyl pyridyl group are preferable. The monovalent heterocyclic group is preferably a monovalent aromatic heterocyclic group.

The substituted carboxyl group is a group in which a hydrogen atom in the carboxyl group is substituted with an alkyl group, an aryl group, an arylalkyl group or a monovalent heterocyclic group, that is, the formula: —C (═O) OR ^* is ( In the formula, R ^* is a group represented by an alkyl group, an aryl group, an arylalkyl group, or a monovalent heterocyclic group. The substituted oxycarbonyl group usually has 2 to 60 carbon atoms, and preferably 2 to 48 carbon atoms. The alkyl group, aryl group, arylalkyl group or monovalent heterocyclic group may have a substituent. The number of carbon atoms does not include the number of carbon atoms of the substituent that the alkyl group, aryl group, arylalkyl group, or monovalent heterocyclic group may have. Examples of the substituted carboxyl group include methoxycarbonyl group, ethoxycarbonyl group, propoxycarbonyl group, isopropoxycarbonyl group, butoxycarbonyl group, isobutoxycarbonyl group, s-butoxycarbonyl group, t-butoxycarbonyl group, pentyloxycarbonyl group, hexyl group. Siloxycarbonyl group, cyclohexyloxycarbonyl group, heptyloxycarbonyl group, octyloxycarbonyl group, 2-ethylhexyloxycarbonyl group, nonyloxycarbonyl group, decyloxycarbonyl group, 3,7-dimethyloctyloxycarbonyl group, dodecyloxycarbonyl Group, trifluoromethoxycarbonyl group, pentafluoroethoxycarbonyl group, perfluorobutoxycarbonyl group, perfluorohexyloxycarbonyl group Perfluorooctyl group, phenoxycarbonyl group, naphthoxycarbonyl group, pyridyloxycarbonyl group and the like.

In Formula (1), Y ^{1 _{is, -CO 2 -, -SO 3 -}} , -SO 2 -, -PO 3 -, or -B ^(R _{a) 3} ^- represents a monovalent group such as, Y ¹ the, -CO ₂ from the viewpoint of the acidity of the ionic polymer ^-, -SO ₂ ^-, -PO ₃ ^- is more preferred, from the viewpoint of the stability of the ionic polymer, ^- preferably, -CO ₂ - CO ₂ ⁻ , —SO ₃ ⁻ , —SO ₂ ^— or —PO ₃ ^— is preferable.

In formula (1), M ¹ represents a metal cation or an ammonium cation with or without a substituent. As the metal cation, monovalent, divalent or trivalent ions are preferable, and Li, Na, K, Cs, Be, Mg, Ca, Ba, Ag, Al, Bi, Cu, Fe, Ga, Mn, Pb, Examples include ions such as Sn, Ti, V, W, Y, Yb, Zn, and Zr, and Li ⁺ , Na ⁺ , K ⁺ , Cs ⁺ , Ag ⁺ , Mg ²⁺ , and Ca ²⁺ are preferable. Examples of the substituent that the ammonium ion may have include 1 to 10 carbon atoms such as methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, i-butyl group, and t-butyl group. Of the alkyl group.

In the formula (1), Z ¹ is F ⁻ , Cl ⁻ , Br ⁻ , I ⁻ , OH ⁻ , R ^a SO ₃ ⁻ , R ^a COO ⁻ , ClO ⁻ , ClO ₂ ⁻ , ClO ₃ ⁻ , ClO ₄ ⁻ , SCN ⁻ , CN ⁻ , NO ₃ ⁻ , SO ₄ ²⁻ , HSO ₄ ⁻ , PO ₄ ³⁻ , HPO ₄ ²⁻ , H ₂ PO ₄ ⁻ , BF ₄ ⁻ or PF ₆ ⁻ are represented.

  In the formula (1), n1 represents an integer of 0 or more, and is preferably an integer of 0 to 8, more preferably an integer of 0 to 2, from the viewpoint of synthesis of raw material monomers.

  In formula (1), a1 represents an integer of 1 or more, and b1 represents an integer of 0 or more.

a1 and b1 are selected so that the charge of the group represented by the formula (1) is zero. For example, Y ¹ is —CO ₂ ⁻ , —SO ₃ ⁻ , —SO ₂ ⁻ , —PO ₃ ⁻ , or —B (R ^a ) ₃ ^— , and M ¹ has a monovalent metal cation or substituent. An ammonium cation with or without Z ¹ being F ⁻ , Cl ⁻ , Br ⁻ , I ⁻ , OH ⁻ , R ^a SO ₃ ⁻ , R ^a COO ⁻ , ClO ⁻ , ClO ₂ ⁻ , ClO ₃ ⁻ , When ClO ₄ ⁻ , SCN ⁻ , CN ⁻ , NO ₃ ⁻ , HSO ₄ ⁻ , H ₂ PO ₄ ⁻ , BF ₄ ⁻ or PF ₆ ⁻ is selected, it is selected so as to satisfy a1 = b1 + 1. Y ¹ is —CO ₂ ⁻ , —SO ₃ ⁻ , —SO ₂ ⁻ , —PO ₃ ⁻ , or —B (R ^a ) ₃ ^— , M ¹ is a divalent metal cation, and Z ¹ is F ⁻ , Cl ⁻ , Br ⁻ , I ⁻ , OH ⁻ , R ^a SO ₃ ⁻ , R ^a COO ⁻ , ClO ⁻ , ClO ₂ ⁻ , ClO ₃ ⁻ , ClO ₄ ⁻ , SCN ⁻ , CN ⁻ , NO ₃ ⁻ , In the case of HSO ₄ ⁻ , H ₂ PO ₄ ⁻ , BF ₄ ⁻ or PF ₆ ⁻ , it is selected so as to satisfy b1 = 2 × a1-1. Y ¹ is —CO ₂ ⁻ , —SO ₃ ⁻ , —SO ₂ ⁻ , —PO ₃ ⁻ , or —B (R ^a ) ₃ ^— , M ¹ is a trivalent metal cation, and Z ¹ is F ⁻ , Cl ⁻ , Br ⁻ , I ⁻ , OH ⁻ , R ^a SO ₃ ⁻ , R ^a COO ⁻ , ClO ⁻ , ClO ₂ ⁻ , ClO ₃ ⁻ , ClO ₄ ⁻ , SCN ⁻ , CN ⁻ , NO ₃ ⁻ , In the case of HSO ₄ ⁻ , H ₂ PO ₄ ⁻ , BF ₄ ⁻ or PF ₆ ⁻ , it is selected so as to satisfy b1 = 3 × a1-1. Y ¹ is —CO ₂ ⁻ , —SO ₃ ⁻ , —SO ₂ ⁻ , —PO ₃ ⁻ , or —B (R ^a ) ₃ ^— , and M ¹ has a monovalent metal cation or substituent, or When it is an ammonium cation that does not have it and Z ¹ is SO ₄ ²⁻ or HPO ₄ ^2−, it is selected so as to satisfy a1 = 2 × b1 + 1. In any of the above formulas representing the relationship between a1 and b1, a1 is preferably an integer of 1 to 5, more preferably 1 or 2.

R ^a represents an alkyl group having 1 to 30 carbon atoms with or without a substituent or an aryl group having 6 to 50 carbon atoms with or without a substituent, and these groups have Examples of the substituent which may be included include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of substituents are present, they may be the same or different. As R ^a , methyl group, ethyl group, propyl group, isopropyl group, butyl group, isobutyl group, s-butyl group, t-butyl group, pentyl group, hexyl group, cyclohexyl group, heptyl group, octyl group, nonyl group , Decyl group, lauryl group, etc., C1-C20 alkyl group, phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl group, 9-anthracenyl group, etc. A 6-30 aryl group etc. are mentioned.

  Examples of the group represented by the formula (1) include the following groups.

-Group represented by Formula (2)-
In the formula (2), the divalent organic group represented by Q ^2, include the same groups as those exemplified for the divalent organic group represented by Q ¹ described above, the raw material monomers for synthesis From the viewpoint of ease, a divalent saturated hydrocarbon group, an arylene group, and an alkyleneoxy group are preferable.

The group exemplified as the example of the divalent organic group represented by Q ² may have a substituent, and the substituent is the same as the substituent exemplified in the description of Q ¹ described above. A substituent is mentioned. When a plurality of substituents are present, they may be the same or different.

In formula (2), Y ² represents a carbocation, an ammonium cation, a phosphonyl cation, a sulfonyl cation, or an iodonium cation.

As the carbocation, for example,
-C ⁺ R ₂
(Wherein, R is the same or different and represents an alkyl group or an aryl group).
Examples of ammonium cations include:
-N ⁺ R ₃
(Wherein, R is the same or different and represents an alkyl group or an aryl group).
Examples of phosphonyl cations include:
-P ⁺ R ₃
(Wherein, R is the same or different and represents an alkyl group or an aryl group).
Examples of the sulfonyl cation include:
-S ⁺ R ₂
(Wherein, R is the same or different and represents an alkyl group or an aryl group).
As an iodonium cation, for example,
-I ⁺ R ₂
(Wherein, R is the same or different and represents an alkyl group or an aryl group).

In the formula (2), Y ² represents a carbocation, an ammonium cation, a phosphonyl cation, a sulfonyl cation from the viewpoint of ease of synthesis of the raw material monomer and stability of the raw material monomer and the ionic polymer against air, moisture or heat. Are preferred, and ammonium cations are more preferred.

In formula (2), Z ² represents a metal cation or an ammonium cation with or without a substituent. As the metal cation, monovalent, divalent or trivalent ions are preferable, and Li, Na, K, Cs, Be, Mg, Ca, Ba, Ag, Al, Bi, Cu, Fe, Ga, Mn, Pb, Examples include ions such as Sn, Ti, V, W, Y, Yb, Zn, and Zr. In addition, examples of the substituent that the ammonium cation may have include alkyl having 1 to 10 carbon atoms such as methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, isobutyl group, and t-butyl group. Groups.

In the formula (2), M ² represents F ⁻ , Cl ⁻ , Br ⁻ , I ⁻ , OH ⁻ , R ^b SO ₃ ⁻ , R ^b COO ⁻ , ClO ⁻ , ClO ₂ ⁻ , ClO ₃ ⁻ , ClO ₄ ⁻ , SCN ⁻ , CN ⁻ , NO ₃ ⁻ , SO ₄ ²⁻ , HSO ₄ ⁻ , PO ₄ ³⁻ , HPO ₄ ²⁻ , H ₂ PO ₄ ⁻ , BF ₄ ⁻ or PF ₆ ⁻ are represented.

  In formula (2), n2 represents an integer of 0 or more, preferably an integer of 0 to 6, and more preferably an integer of 0 to 2.

  In formula (2), a2 represents an integer of 1 or more, and b2 represents an integer of 0 or more.

a2 and b2 are selected such that the charge of the group represented by the formula (2) is zero. For example, M ² is F ⁻ , Cl ⁻ , Br ⁻ , I ⁻ , OH ⁻ , R ^b SO ₃ ⁻ , R ^b COO ⁻ , ClO ⁻ , ClO ₂ ⁻ , ClO ₃ ⁻ , ClO ₄ ⁻ , SCN ⁻ , CN _{^{-, nO 3 -, HSO 4}} -, H 2 PO 4 -, BF 4 - or PF ₆ ^- if it is, if an ammonium ion Z ² has no or have a monovalent metal ion or a substituent , A2 = b2 + 1 is selected and Z ² is a divalent metal ion, a2 = 2 × b2 + 1 is selected and Z ² is a trivalent metal ion, a2 = 3 Xb2 + 1 is selected to satisfy. When M ² is SO ₄ ²⁻ , HPO ₄ ²⁻ , if Z ² is a monovalent metal ion or an ammonium ion with or without a substituent, b2 = 2 × a2-1 is satisfied. If Z ² is a trivalent metal ion, it is selected so as to satisfy the relationship of 2 × a2 = 3 × b2 + 1. In any of the above mathematical expressions representing the relationship between a2 and b2, a2 is preferably an integer of 1 to 3, more preferably 1 or 2.

R ^b represents an alkyl group having 1 to 30 carbon atoms with or without a substituent or an aryl group having 6 to 50 carbon atoms with or without a substituent, and these groups have Examples of the substituent that may be included include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of substituents are present, they may be the same or different. As R ^b , methyl group, ethyl group, propyl group, isopropyl group, butyl group, isobutyl group, s-butyl group, t-butyl group, pentyl group, hexyl group, cyclohexyl group, heptyl group, octyl group, nonyl group , Decyl group, lauryl group, etc., C1-C20 alkyl group, phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl group, 9-anthracenyl group, etc. A 6-30 aryl group etc. are mentioned.

  Examples of the group represented by the formula (2) include the following groups.

-Group represented by Formula (3)-
In the formula (3), examples of the divalent organic group represented by Q ³ include the same groups as those exemplified for the divalent organic group represented by Q ¹ described above. From the viewpoint of ease, a divalent saturated hydrocarbon group, an arylene group, and an alkyleneoxy group are preferable.

The group mentioned as an example of the divalent organic group represented by Q ³ may have a substituent, and the substituent is the same as the substituent exemplified in the description of Q ¹ described above. A substituent is mentioned. When a plurality of substituents are present, they may be the same or different.

The divalent organic group represented by Q ³ is preferably a group represented by — (CH ₂ ) —.

  n3 represents an integer of 0 or more, preferably an integer of 0 to 20, and more preferably an integer of 0 to 8.

In formula (3), Y ³ represents —CN or a group represented by any one of formulas (4) to (12).

  In the formulas (4) to (12), the divalent hydrocarbon group represented by R ′ includes a methylene group, an ethylene group, a 1,2-propylene group, a 1,3-propylene group, and a 1,2-butylene. Group, 1,3-butylene group, 1,4-butylene group, 1,5-pentylene group, 1,6-hexylene group, 1,9-nonylene group, 1,12-dodecylene group, among these groups A divalent saturated hydrocarbon group having 1 to 50 carbon atoms, which has or does not have a substituent, such as a group in which at least one hydrogen atom is substituted with a substituent; ethenylene group, propenylene group, 3-butenylene group Substituents such as 2-butenylene group, 2-pentenylene group, 2-hexenylene group, 2-nonenylene group, 2-dodecenylene group, a group in which at least one hydrogen atom in these groups is substituted with a substituent, etc. With or without carbon atoms A divalent unsaturated hydrocarbon group having 2 to 50 carbon atoms, which may or may not have a substituent, including a kenylene group and an ethynylene group; a cyclopropylene group, a cyclobutylene group, a cyclopentylene group, a cyclohexene Number of carbon atoms with or without a substituent, such as a xylene group, cyclononylene group, cyclododecylene group, norbornylene group, adamantylene group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. 3-50 divalent cyclic saturated hydrocarbon groups; 1,3-phenylene group, 1,4-phenylene group, 1,4-naphthylene group, 1,5-naphthylene group, 2,6-naphthylene group, biphenyl- An arylene group having 6 to 50 carbon atoms, which may or may not have a substituent, such as a 4,4′-diyl group or a group in which at least one hydrogen atom in these groups is substituted with a substituent; Substituents such as an oxy group, an ethyleneoxy group, a propyleneoxy group, a butyleneoxy group, a pentyleneoxy group, a hexyleneoxy group, a group in which at least one hydrogen atom in these groups is substituted with a substituent, etc. Examples thereof include an alkyleneoxy group having 1 to 50 carbon atoms which may or may not be included.

Examples of the substituent include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of substituents are present, they may be the same or different.

In the formulas (4) to (12), as the monovalent hydrocarbon group represented by R ″, methyl group, ethyl group, propyl group, isopropyl group, butyl group, isobutyl group, s-butyl group, t -Butyl group, pentyl group, hexyl group, cyclohexyl group, heptyl group, octyl group, nonyl group, decyl group, lauryl group, a group in which at least one hydrogen atom in these groups is substituted with a substituent, and the like, An alkyl group having 1 to 20 carbon atoms, which may or may not have a substituent; phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl group, 9-anthracenyl group, these groups And an aryl group having 6 to 30 carbon atoms which may or may not have a substituent, such as a group in which at least one hydrogen atom is substituted with a substituent. From the viewpoint of solubility of the ionic polymer, a methyl group, an ethyl group, a phenyl group, a 1-naphthyl group, and a 2-naphthyl group are preferable. Examples of the substituent include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of substituents are present, they may be the same or different.

In the formula (5), the trivalent hydrocarbon group represented by R ′ ″ includes a methanetriyl group, an ethanetriyl group, a 1,2,3-propanetriyl group, a 1,2,4-butanetriyl group, 1 , 2,5-pentanetriyl group, 1,3,5-pentanetriyl group, 1,2,6-hexanetriyl group, 1,3,6-hexanetriyl group, at least of these groups An alkyltriyl group having 1 to 20 carbon atoms, which may or may not have a substituent, such as a group in which one hydrogen atom is substituted with a substituent; 1,2,3-benzenetriyl group, 1,2 , 4-benzenetriyl group, 1,3,5-benzenetriyl group, or a group obtained by substituting at least one hydrogen atom of these groups with a substituent. Examples thereof include aryl groups having 6 to 30 carbon atoms. From the viewpoint of solubility of the ionic polymer, a methanetriyl group, an ethanetriyl group, a 1,2,4-benzenetriyl group, and a 1,3,5-benzenetriyl group are preferable. Examples of the substituent include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of substituents are present, they may be the same or different.

In formulas (4) to (12), R ^c is preferably a methyl group, an ethyl group, a phenyl group, a 1-naphthyl group, or a 2-naphthyl group from the viewpoint of solubility of the ionic polymer.

  In Formula (4) and Formula (5), a3 represents an integer of 1 or more, and an integer of 3 to 10 is preferable. In formulas (6) to (12), a4 represents an integer of 0 or more. In Formula (6), a4 is preferably an integer of 0 to 30, and more preferably an integer of 3 to 20. In formulas (7) to (10), a4 is preferably an integer of 0 to 10, and more preferably an integer of 0 to 5. In the formula (11), a4 is preferably an integer of 0 to 20, and more preferably an integer of 3 to 20. In the formula (12), a4 is preferably an integer of 0 to 20, and more preferably an integer of 0 to 10.

As Y ³ , from the viewpoint of ease of synthesis of the raw material monomer, —CN, a group represented by the formula (4), a group represented by the formula (6), a group represented by the formula (10), A group represented by the formula (11) is preferable, a group represented by the formula (4), a group represented by the formula (6), a group represented by the formula (11) are more preferable, and the following groups are particularly preferable: preferable.

-Structural units in ionic polymers-
The ionic polymer used in the present invention includes a structural unit represented by the formula (13), a structural unit represented by the formula (15), a structural unit represented by the formula (17), and the formula (20). It is preferable that it is an ionic polymer which has 15-100 mol% of said structural units in all the structural units.

Structural unit represented by formula (13) In formula (13), R ¹ is a monovalent group including a group represented by formula (14), and Ar ¹ has a substituent other than R ^1. Alternatively, it represents a (2 + n4) -valent aromatic group that does not exist, and n4 represents an integer of 1 or more.

The group represented by the formula (14) may be directly bonded to Ar ^{1, and} includes a methylene group, an ethylene group, a propylene group, a butylene group, a pentylene group, a hexylene group, a nonylene group, a dodecylene group, a cyclopropylene group, Substitution, such as a cyclobutylene group, a cyclopentylene group, a cyclohexylene group, a cyclononylene group, a cyclododecylene group, a norbornylene group, an adamantylene group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent An alkylene group having 1 to 50 carbon atoms with or without a group; oxymethylene group, oxyethylene group, oxypropylene group, oxybutylene group, oxypentylene group, oxyhexylene group, oxynonylene group, oxide decylene Group, cyclopropyleneoxy group, cyclobutyleneoxy group, cyclopentyleneoxy group, Chlohexyleneoxy group, cyclononyleneoxy group, cyclododecyleneoxy group, norbornyleneoxy group, adamantyleneoxy group, groups in which at least one hydrogen atom in these groups is substituted with a substituent, etc. An oxyalkylene group having 1 to 50 carbon atoms with or without a substituent; an imino group with or without a substituent; a silylene group with or without a substituent; with a substituent An ethynylene group; an ethynylene group; a methanetriyl group with or without a substituent; and an Ar ¹ through a heteroatom such as an oxygen atom, a nitrogen atom, or a sulfur atom.

Ar ¹ may have a substituent other than R ¹ . Examples of the substituent include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of the substituents are present, they may be the same or different.

The substituent other than R ¹ possessed by Ar ¹ is preferably an alkyl group, an alkoxy group, an aryl group, an aryloxy group, a carboxyl group, or a substituted carboxyl group from the viewpoint of ease of synthesis of the raw material monomer.

  In formula (13), n4 represents an integer of 1 or more, preferably an integer of 1 to 4, and more preferably an integer of 1 to 3.

Examples of the (2 + n4) -valent aromatic group represented by Ar ¹ in formula (13) include a (2 + n4) -valent aromatic hydrocarbon group and a (2 + n4) -valent aromatic heterocyclic group. Or a (2 + n4) -valent aromatic group consisting of carbon atoms and one or more atoms selected from the group consisting of hydrogen atoms, nitrogen atoms and oxygen atoms. Examples of the (2 + n4) -valent aromatic group include a benzene ring, a pyridine ring, a 1,2-diazine ring, a 1,3-diazine ring, a 1,4-diazine ring, a 1,3,5-triazine ring, and a furan ring. , A (2 + n4) -valent group obtained by removing (2 + n4) hydrogen atoms from a monocyclic aromatic ring such as pyrrole ring, pyrazole ring, imidazole ring, oxazole ring, azadiazole ring, etc .; selected from the group consisting of the monocyclic aromatic ring A (2 + n4) -valent group obtained by removing (2 + n4) hydrogen atoms from a condensed polycyclic aromatic ring in which two or more rings are condensed; from the group consisting of the monocyclic aromatic ring and the condensed polycyclic aromatic ring A (2 + n4) -valent group obtained by removing (2 + n4) hydrogen atoms from an aromatic ring assembly formed by connecting two or more selected aromatic rings with a single bond, an ethenylene group or an ethynylene group; the condensed polycyclic aromatic ring Or two adjacent aromatic ring assemblies A (2 + n4) -valent group obtained by removing (2 + n4) hydrogen atoms from a bridged polycyclic aromatic ring having a bridge in which the aromatic ring is bridged by a divalent group such as a methylene group, an ethylene group, or a carbonyl group. Can be mentioned.

  Examples of the monocyclic aromatic ring include the following rings.

  Examples of the condensed polycyclic aromatic ring include the following rings.

  Examples of the aromatic ring assembly include the following rings.

  Examples of the bridged polycyclic aromatic ring include the following rings.

  The (2 + n4) -valent aromatic group includes (2 + n4) hydrogen atoms from the ring represented by the formulas 1 to 14, 26 to 29, 37 to 39, or 41 from the viewpoint of ease of synthesis of the raw material monomer. The group removed is preferred, and the group obtained by removing (2 + n4) hydrogen atoms from the ring represented by the formulas 1 to 6, 8, 13, 26, 27, 37 or 41 is more preferred, represented by the formula 1, 37 or 41. More preferred is a group in which (2 + n4) hydrogen atoms have been removed from the ring formed.

In formula (14), examples of the (1 + m1 + m2) -valent organic group represented by R ² include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which (m1 + m2) hydrogen atoms are removed from an alkyl group having 1 to 20 carbon atoms with or without: phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl An aryl group having 6 to 30 carbon atoms, which may or may not have a substituent, such as a group, a 9-anthracenyl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent; (M1 + m2) groups excluding hydrogen atoms; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyl Substitution, such as an oxy group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, a group in which at least one hydrogen atom in these groups is substituted with a substituent, etc. A group obtained by removing (m1 + m2) hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms with or without a group; removing (m1 + m2) hydrogen atoms from an amino group having a substituent containing a carbon atom A group obtained by removing (m1 + m2) hydrogen atoms from a silyl group having a substituent containing a carbon atom. From the viewpoint of ease of synthesis of the raw material monomer, a group in which (m1 + m2) hydrogen atoms are removed from an alkyl group, a group in which (m1 + m2) hydrogen atoms are removed from an aryl group, and an alkoxy group (m1 + m2) Groups in which one hydrogen atom has been removed are preferred.

Examples of the substituent include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of the substituents are present, they may be the same or different.

Structural unit represented by formula (15) In formula (15), R ³ is a monovalent group including a group represented by formula (16), and Ar ² has a substituent other than R ^3. Alternatively, it represents a (2 + n5) -valent aromatic group not present, and n5 represents an integer of 1 or more.

The group represented by the formula (16) may be directly bonded to Ar ² and is a methylene group, ethylene group, propylene group, butylene group, pentylene group, hexylene group, nonylene group, dodecylene group, cyclopropylene group, Substitution, such as a cyclobutylene group, a cyclopentylene group, a cyclohexylene group, a cyclononylene group, a cyclododecylene group, a norbornylene group, an adamantylene group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent An alkylene group having 1 to 50 carbon atoms with or without a group; oxymethylene group, oxyethylene group, oxypropylene group, oxybutylene group, oxypentylene group, oxyhexylene group, oxynonylene group, oxide decylene Group, cyclopropyleneoxy group, cyclobutyleneoxy group,
Cyclopentyleneoxy group, cyclohexyleneoxy group, cyclononyleneoxy group, cyclododecyleneoxy group, norbornyleneoxy group, adamantyleneoxy group, and at least one hydrogen atom in these groups is substituted An oxyalkylene group having 1 to 50 carbon atoms, with or without a substituent, such as a group substituted with a group; an imino group with or without a substituent; a silylene with or without a substituent An ethenylene group with or without a substituent; an ethynylene group; a methanetriyl group with or without a substituent; bonded to Ar ² through a heteroatom such as an oxygen atom, a nitrogen atom, or a sulfur atom May be.

Ar ² may have a substituent other than R ³ . Examples of the substituent include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of the substituents are present, they may be the same or different.

The substituent other than R ^{3 in} Ar ² is preferably an alkyl group, an alkoxy group, an aryl group, an aryloxy group, a carboxyl group, or a substituted carboxyl group from the viewpoint of ease of synthesis of the raw material monomer.

  In formula (15), n5 represents an integer of 1 or more, preferably an integer of 1 to 4, and more preferably an integer of 1 to 3.

Examples of the (2 + n5) -valent aromatic group represented by Ar ² in the formula (15) include a (2 + n5) -valent aromatic hydrocarbon group and a (2 + n5) -valent aromatic heterocyclic group. Or a (2 + n5) -valent aromatic group consisting of carbon atoms and one or more atoms selected from the group consisting of hydrogen atoms, nitrogen atoms and oxygen atoms. Examples of the (2 + n5) -valent aromatic group include a benzene ring, a pyridine ring, a 1,2-diazine ring, a 1,3-diazine ring, a 1,4-diazine ring, a 1,3,5-triazine ring, and a furan ring. , A (2 + n5) -valent group obtained by removing (2 + n5) hydrogen atoms from a monocyclic aromatic ring such as pyrrole ring, pyrazole ring, imidazole ring, oxazole ring, azadiazole ring, etc .; selected from the group consisting of the monocyclic aromatic ring A (2 + n5) -valent group obtained by removing (2 + n5) hydrogen atoms from a condensed polycyclic aromatic ring in which two or more rings are condensed; from the group consisting of the monocyclic aromatic ring and the condensed polycyclic aromatic ring A (2 + n5) -valent group obtained by removing (2 + n5) hydrogen atoms from an aromatic ring assembly formed by linking two or more selected aromatic rings with a single bond, ethenylene group or ethynylene group; the condensed polycyclic aromatic ring Or two adjacent aromatic ring assemblies A (2 + n5) -valent group obtained by removing (2 + n5) hydrogen atoms from a bridged polycyclic aromatic ring having a bridge in which the aromatic ring is bridged by a divalent group such as a methylene group, an ethylene group, or a carbonyl group. Can be mentioned.

  As a monocyclic aromatic ring, the ring represented by Formula 1-12 illustrated in the description regarding the structural unit represented by Formula (13) is mentioned, for example.

  Examples of the condensed polycyclic aromatic ring include rings represented by Formulas 13 to 27 exemplified in the description of the structural unit represented by Formula (13).

  Examples of the aromatic ring assembly include rings represented by formulas 28 to 36 exemplified in the description of the structural unit represented by formula (13).

  Examples of the bridged polycyclic aromatic ring include rings represented by the formulas 37 to 44 exemplified in the description of the structural unit represented by the formula (13).

  The (2 + n5) -valent aromatic group includes (2 + n5) hydrogen atoms from the ring represented by the formulas 1 to 14, 26 to 29, 37 to 39, or 41 from the viewpoint of ease of synthesis of the raw material monomer. The group removed is preferred, and the group obtained by removing (2 + n5) hydrogen atoms from the ring represented by the formulas 1 to 6, 8, 13, 26, 27, 37 or 41 is more preferred, and represented by the formula 1, 37 or 41 And more preferably a group in which (2 + n5) hydrogen atoms have been removed from the ring.

  In formula (16), m3 and m4 each independently represents an integer of 1 or more.

In the formula (16), examples of the (1 + m3 + m4) -valent organic group represented by R ⁴ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group obtained by removing (m3 + m4) hydrogen atoms from an alkyl group having 1 to 20 carbon atoms with or without: phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl An aryl group having 6 to 30 carbon atoms, which may or may not have a substituent, such as a group, a 9-anthracenyl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent; (M3 + m4) groups excluding hydrogen atoms; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyl Substitution, such as an oxy group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, a group in which at least one hydrogen atom in these groups is substituted with a substituent, etc. A group obtained by removing (m3 + m4) hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms with or without a group; removing (m3 + m4) hydrogen atoms from an amino group having a substituent containing a carbon atom A group obtained by removing (m3 + m4) hydrogen atoms from a silyl group having a substituent containing a carbon atom. From the viewpoint of ease of synthesis of the raw material monomer, a group obtained by removing (m3 + m4) hydrogen atoms from an alkyl group, a group obtained by removing (m3 + m4) hydrogen atoms from an aryl group, and an alkoxy group (m3 + m4) Groups in which one hydrogen atom has been removed are preferred.

Examples of the substituent include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of the substituents are present, they may be the same or different.

Structural unit represented by formula (17) In formula (17), R ⁵ is a monovalent group including a group represented by formula (18), and R ⁶ is a group represented by formula (19). Ar ³ represents a (2 + n6 + n7) -valent aromatic group having or not having a substituent other than R ⁵ and R ⁶ , and n6 and n7 are each independently an integer of 1 or more Represents.

The group represented by the formula (18) and the group represented by the formula (19) may be directly bonded to Ar ^{3, and} include a methylene group, an ethylene group, a propylene group, a butylene group, a pentylene group, a hexylene group, Nonylene group, dodecylene group, cyclopropylene group, cyclobutylene group, cyclopentylene group, cyclohexylene group, cyclononylene group, cyclododecylene group, norbornylene group, adamantylene group, and at least one hydrogen atom in these groups An alkylene group having 1 to 50 carbon atoms, which may or may not have a substituent, such as a group substituted by a substituent; an oxymethylene group, an oxyethylene group, an oxypropylene group, an oxybutylene group, an oxypentylene group, an oxy Hexylene, oxynonylene, oxide decylene, cyclopropyleneoxy, cyclobutyleneoxy, Lopentyleneoxy group, cyclohexyleneoxy group, cyclononyleneoxy group, cyclododecyleneoxy group, norbornyleneoxy group, adamantyleneoxy group, and at least one hydrogen atom in these groups is substituted An oxyalkylene group having 1 to 50 carbon atoms, with or without a substituent, such as a group substituted with a group; an imino group with or without a substituent; a silylene with or without a substituent An ethenylene group with or without a substituent; an ethynylene group; a methanetriyl group with or without a substituent; and bonded to Ar ³ through a heteroatom such as an oxygen atom, a nitrogen atom, or a sulfur atom May be.

Ar ³ may have a substituent other than R ⁵ and R ⁶ . Examples of the substituent include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of the substituents are present, they may be the same or different.

The substituent other than R ⁵ and R ⁶ possessed by Ar ³ is an alkyl group, an alkoxy group, an aryl group, an aryloxy group, a carboxyl group or a substituted carboxyl group from the viewpoint of ease of synthesis of the raw material monomer. Is preferred.

  In formula (17), n6 represents an integer of 1 or more, preferably an integer of 1 to 4, and more preferably an integer of 1 to 3.

  In formula (17), n7 represents an integer of 1 or more, preferably an integer of 1 to 4, more preferably an integer of 1 to 3.

Examples of the (2 + n6 + n7) -valent aromatic group represented by Ar ³ in the formula (17) include a (2 + n6 + n7) -valent aromatic hydrocarbon group, a (2 + n6 + n7) -valent aromatic heterocyclic group, and a carbon atom. Or a (2 + n6 + n7) -valent aromatic group consisting of carbon atoms and one or more atoms selected from the group consisting of hydrogen atoms, nitrogen atoms and oxygen atoms. Examples of the (2 + n6 + n7) -valent aromatic group include a benzene ring, a pyridine ring, a 1,2-diazine ring, a 1,3-diazine ring, a 1,4-diazine ring, a furan ring, a pyrrole ring, a pyrazole ring, and an imidazole ring. A (2 + n6 + n7) -valent group obtained by removing (2 + n6 + n7) hydrogen atoms from a monocyclic aromatic ring such as an oxazole ring; a condensed polycycle in which two or more rings selected from the group consisting of the monocyclic aromatic rings are condensed A (2 + n6 + n7) -valent group obtained by removing (2 + n6 + n7) hydrogen atoms from the formula aromatic ring; two or more aromatic rings selected from the group consisting of the monocyclic aromatic ring and the condensed polycyclic aromatic ring are bonded to a single bond , A (2 + n6 + n7) -valent group obtained by removing (2 + n6 + n7) hydrogen atoms from an aromatic ring assembly linked by an ethenylene group or an ethynylene group; the condensed polycyclic aromatic ring or two adjacent aromatic ring assemblies (2 + n6 + n7) -valent groups obtained by removing (2 + n6 + n7) hydrogen atoms from a bridged polycyclic aromatic ring having a bridge formed by bridging an aromatic ring with a divalent group such as a methylene group, an ethylene group, or a carbonyl group. It is done.

  As a monocyclic aromatic ring, the ring represented by the formula 1-5 illustrated in the description regarding the structural unit represented by Formula (13), and the formula 7-10 is mentioned, for example.

  Examples of the condensed polycyclic aromatic ring include rings represented by Formulas 13 to 27 exemplified in the description of the structural unit represented by Formula (13).

  Examples of the aromatic ring assembly include rings represented by formulas 28 to 36 exemplified in the description of the structural unit represented by formula (13).

  Examples of the bridged polycyclic aromatic ring include rings represented by the formulas 37 to 44 exemplified in the description of the structural unit represented by the formula (13).

  The (2 + n6 + n7) -valent aromatic group is a ring represented by the formula 1 to 5, 7 to 10, 13, 14, 26 to 29, 37 to 39, or 41 from the viewpoint of ease of synthesis of the raw material monomer. A group obtained by removing (2 + n6 + n7) hydrogen atoms from the ring is preferred, and a group obtained by removing (2 + n6 + n7) hydrogen atoms from the ring represented by formula 1, 37 or 41 is more preferred, represented by formula 1, 38 or 42 A group obtained by removing (2 + n6 + n7) hydrogen atoms from the ring is more preferable.

In Formula (18), R ⁷ represents a single bond or a (1 + m5) -valent organic group, and is preferably a (1 + m5) -valent organic group.

In formula (18), examples of the (1 + m5) -valent organic group represented by R ⁷ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which an m5 hydrogen atom is removed from an alkyl group having 1 to 20 carbon atoms, which may or may not have; phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl group, M5-hydrogen from an aryl group having 6-30 carbon atoms, with or without a substituent, such as a 9-anthracenyl group or a group in which at least one hydrogen atom in these groups is substituted with a substituent original A group except for: methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyloxy group, cyclohexyloxy group Having or having a substituent, such as a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent A group obtained by removing m5 hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms; a group obtained by removing m5 hydrogen atoms from an amino group having a substituent containing carbon atoms; having a substituent containing carbon atoms Examples include groups in which m5 hydrogen atoms have been removed from a silyl group. From the viewpoint of ease of synthesis of raw material monomers, A group in which m5 hydrogen atoms have been removed, a group in which m5 hydrogen atoms have been removed from an aryl group, and a group in which m5 hydrogen atoms have been removed from an alkoxy group are preferred.

Examples of the substituent include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of the substituents are present, they may be the same or different.

In formula (18), m5 represents an integer of 1 or more, provided that m5 represents 1 when R ⁷ is a single bond.

In Formula (19), R ⁸ represents a single bond or a (1 + m6) -valent organic group, and is preferably a (1 + m6) -valent organic group.

In the formula (19), examples of the (1 + m6) -valent organic group represented by R ⁸ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which an m6 hydrogen atom is removed from an alkyl group having 1 to 20 carbon atoms with or without: phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl group, M6-hydrogen from an aryl group having 6 to 30 carbon atoms, which may or may not have a substituent, such as a 9-anthracenyl group or a group in which at least one hydrogen atom in these groups is substituted with a substituent. original A group except for: methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyloxy group, cyclohexyloxy group Having or having a substituent, such as a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent A group obtained by removing m6 hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms; a group obtained by removing m6 hydrogen atoms from an amino group having a substituent containing carbon atoms; having a substituent containing carbon atoms Examples include groups in which m6 hydrogen atoms have been removed from a silyl group. From the viewpoint of ease of synthesis of raw material monomers, And a group in which m6 hydrogen atoms have been removed from an aryl group, and a group in which m6 hydrogen atoms have been removed from an alkoxy group.

Examples of the substituent include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of the substituents are present, they may be the same or different.

In formula (19), m6 represents an integer of 1 or more, provided that m6 represents 1 when R ⁸ is a single bond.

Structural unit represented by formula (20) In formula (20), R ⁹ is a monovalent group including a group represented by formula (21), and R ¹⁰ is a group represented by formula (22). Ar ⁴ represents a (2 + n8 + n9) -valent aromatic group having or not having a substituent other than R ⁹ and R ¹⁰ , and n8 and n9 are each independently an integer of 1 or more Represents.

The group represented by the formula (21) and the group represented by the formula (22) may be directly bonded to Ar ^{4, and} include a methylene group, an ethylene group, a propylene group, a butylene group, a pentylene group, a hexylene group, Nonylene group, dodecylene group, cyclopropylene group, cyclobutylene group, cyclopentylene group, cyclohexylene group, cyclononylene group, cyclododecylene group, norbornylene group, adamantylene group, and at least one hydrogen atom in these groups An alkylene group having 1 to 50 carbon atoms, which may or may not have a substituent, such as a group substituted by a substituent; an oxymethylene group, an oxyethylene group, an oxypropylene group, an oxybutylene group, an oxypentylene group, an oxy Hexylene, oxynonylene, oxide decylene, cyclopropyleneoxy, cyclobutyleneoxy, Lopentyleneoxy group, cyclohexyleneoxy group, cyclononyleneoxy group, cyclododecyleneoxy group, norbornyleneoxy group, adamantyleneoxy group, and at least one hydrogen atom in these groups is substituted An oxyalkylene group having 1 to 50 carbon atoms, with or without a substituent, such as a group substituted with a group; an imino group with or without a substituent; a silylene with or without a substituent An ethenylene group with or without a substituent; an ethynylene group; a methanetriyl group with or without a substituent; and bonded to Ar ⁴ through a heteroatom such as an oxygen atom, a nitrogen atom, or a sulfur atom. May be.

Ar ⁴ may have a substituent other than R ⁹ and R ¹⁰ . Examples of the substituent include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of the substituents are present, they may be the same or different.

The substituent other than R ⁹ and R ^{10 of} Ar ⁴ is an alkyl group, an alkoxy group, an aryl group, an aryloxy group, a carboxyl group, or a substituted carboxyl group from the viewpoint of ease of synthesis of the raw material monomer. Is preferred.

  In formula (20), n8 represents an integer of 1 or more, preferably an integer of 1 to 4, and more preferably an integer of 1 to 3.

  In formula (20), n9 represents an integer of 1 or more, preferably an integer of 1 to 4, and more preferably an integer of 1 to 3.

Examples of the (2 + n8 + n9) -valent aromatic group represented by Ar ⁴ in the formula (20) include a (2 + n8 + n9) -valent aromatic hydrocarbon group and a (2 + n8 + n9) -valent aromatic heterocyclic group. Or a (2 + n8 + n9) -valent aromatic group consisting of carbon atoms and one or more atoms selected from the group consisting of hydrogen atoms, nitrogen atoms and oxygen atoms. Examples of the (2 + n8 + n9) -valent aromatic group include a benzene ring, a pyridine ring, a 1,2-diazine ring, a 1,3-diazine ring, a 1,4-diazine ring, a furan ring, a pyrrole ring, a pyrazole ring, and an imidazole ring. A (2 + n8 + n9) -valent group obtained by removing (2 + n8 + n9) hydrogen atoms from a monocyclic aromatic ring such as a condensed polycyclic aromatic ring obtained by condensing two or more rings selected from the group consisting of the monocyclic aromatic rings A (2 + n8 + n9) -valent group obtained by removing (2 + n8 + n9) hydrogen atoms from the above; two or more aromatic rings selected from the group consisting of the monocyclic aromatic ring and the condensed polycyclic aromatic ring are bonded to a single bond or an ethenylene group Or a (2 + n8 + n9) -valent group obtained by removing (2 + n8 + n9) hydrogen atoms from an aromatic ring assembly formed by linking with an ethynylene group; the condensed polycyclic aromatic ring or two adjacent aromatic rings in the aromatic ring assembly are methylated. Group, an ethylene group, and a divalent hydrogen atoms from a bridged polycyclic aromatic ring having a bridged crosslinked with groups (2 + n8 + n9) pieces remaining after removing (2 + n8 + n9) valent group such as a carbonyl group.

  As a monocyclic aromatic ring, the ring represented by the formula 1-5 illustrated in the description regarding the structural unit represented by Formula (13), and the formula 7-10 is mentioned, for example.

  Examples of the condensed polycyclic aromatic ring include rings represented by Formulas 13 to 27 exemplified in the description of the structural unit represented by Formula (13).

  Examples of the aromatic ring assembly include rings represented by formulas 28 to 36 exemplified in the description of the structural unit represented by formula (13).

  Examples of the bridged polycyclic aromatic ring include rings represented by the formulas 37 to 44 exemplified in the description of the structural unit represented by the formula (13).

  The (2 + n8 + n9) -valent aromatic group is a ring represented by the formula 1 to 5, 7 to 10, 13, 14, 26 to 29, 37 to 39, or 41 from the viewpoint of ease of synthesis of the raw material monomer. Is preferably a group in which (2 + n8 + n9) hydrogen atoms are removed from the ring, more preferably a group in which (2 + n8 + n9) hydrogen atoms are removed from the ring represented by formulas 1-6, 8, 14, 27, 28, 38 or 42, A group obtained by removing (2 + n8 + n9) hydrogen atoms from the ring represented by formula 1, 37 or 41 is more preferable.

In Formula (21), R ¹¹ represents a single bond or a (1 + m7) -valent organic group, and is preferably a (1 + m7) -valent organic group.

In formula (21), examples of the (1 + m7) -valent organic group represented by R ¹¹ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which an m7 hydrogen atom is removed from an alkyl group having 1 to 20 carbon atoms with or without a phenyl group; a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, M7 hydrogen from an aryl group having 6 to 30 carbon atoms, which may or may not have a substituent, such as a 9-anthracenyl group or a group in which at least one hydrogen atom in these groups is substituted with a substituent. original Groups except for: methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyloxy group, cyclohexyloxy group Having or having a substituent, such as a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent A group obtained by removing m7 hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms; a group obtained by removing m7 hydrogen atoms from an amino group having a substituent containing carbon atoms; having a substituent containing carbon atoms Examples include groups in which m7 hydrogen atoms have been removed from a silyl group. From the viewpoint of ease of synthesis of raw material monomers, alkyl groups Et m7 groups excluding the hydrogen atom, a group remaining after removing m7 hydrogen atoms from an aryl group, a group obtained by removing m7 hydrogen atoms from an amino group.

Examples of the substituent include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of the substituents are present, they may be the same or different.

In formula (21), m7 represents an integer of 1 or more, provided that m7 represents 1 when R ¹¹ is a single bond.

In Formula (22), R ¹² represents a single bond or a (1 + m8) valent organic group, and is preferably a (1 + m8) valent organic group.

In the formula (22), examples of the (1 + m8) -valent organic group represented by R ¹² include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which an m8 hydrogen atom is removed from an alkyl group having 1 to 20 carbon atoms, which may or may not have; phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl group, M8 hydrogen from an aryl group having 6 to 30 carbon atoms, with or without a substituent, such as a 9-anthracenyl group, a group in which at least one hydrogen atom in these groups is substituted with a substituent, and the like original Groups except for: methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyloxy group, cyclohexyloxy group Having or having a substituent, such as a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent A group obtained by removing m8 hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms; a group obtained by removing m8 hydrogen atoms from an amino group having a substituent containing carbon atoms; having a substituent containing carbon atoms Examples include groups in which m8 hydrogen atoms have been removed from a silyl group. From the viewpoint of ease of synthesis of raw material monomers, alkyl groups Et m8 groups excluding the hydrogen atom, a group remaining after removing m8 hydrogen atoms from an aryl group, a group obtained by removing m8 hydrogen atoms from an amino group.

Examples of the substituent include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of the substituents are present, they may be the same or different.

In formula (22), m8 represents an integer of 1 or more, provided that m8 represents 1 when R ¹² is a single bond.

Examples of the structural unit represented by the formula (13) As the structural unit represented by the formula (13), from the viewpoint of the electron transport property of the obtained ionic polymer, the structural unit represented by the formula (23), The structural unit represented by Formula (24) is preferable, and the structural unit represented by Formula (24) is more preferable.

（式（２３）中、Ｒ^1３は（１＋ｍ９＋ｍ１０）価の有機基を表し、Ｒ^１４は１価の有機基を表し、Ｑ¹、Ｑ^３、Ｙ^１、Ｍ¹、Ｚ¹、Ｙ^３、ｎ１、ａ１、ｂ１及びｎ３は前述と同じ意味を表し、ｍ９及びｍ１０はそれぞれ独立に１以上の整数を表し、Ｑ¹、Ｑ^３、Ｙ^１、Ｍ¹、Ｚ¹、Ｙ^３、ｎ１、ａ１、ｂ１及びｎ３のおのおのは複数個ある場合、同一でも異なっていてもよい。）

(In the formula (23), R ¹³ represents a (1 + m9 + m10) valent organic group, R ¹⁴ represents a monovalent organic group, and Q ¹ , Q ³ , Y ¹ , M ¹ , Z ¹ , Y ³ , n1 , A1, b1, and n3 represent the same meaning as described above, m9 and m10 each independently represent an integer of 1 or more, and Q ¹ , Q ³ , Y ¹ , M ¹ , Z ¹ , Y ³ , n1, a1, When there are a plurality of b1 and n3, they may be the same or different.)

In formula (23), examples of the (1 + m9 + m10) -valent organic group represented by R ¹³ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which (m9 + m10) hydrogen atoms are removed from an alkyl group having 1 to 20 carbon atoms, which may or may not have; phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl An aryl group having 6 to 30 carbon atoms, which may or may not have a substituent, such as a group, a 9-anthracenyl group, or a group obtained by substituting at least one hydrogen atom of these groups with a substituent. A group in which (m9 + m10) hydrogen atoms have been removed from the group; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy Groups, cyclopentyloxy groups, cyclohexyloxy groups, cyclononyloxy groups, cyclododecyloxy groups, norbornyloxy groups, adamantyloxy groups, groups in which at least one hydrogen atom in these groups is substituted with a substituent, etc. A group obtained by removing (m9 + m10) hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms with or without a substituent; (m9 + m10) hydrogens from an amino group having a substituent containing a carbon atom A group excluding atoms; (m9 + m10) hydrogen atoms from a silyl group having a substituent containing a carbon atom; From the viewpoint of ease of synthesis of the raw material monomer, a group obtained by removing (m9 + m10) hydrogen atoms from an alkyl group, a group obtained by removing (m9 + m10) hydrogen atoms from an aryl group, an alkoxy group To (m9 + m10) hydrogen atoms are preferably removed.

In the formula (23), examples of the monovalent organic group represented by R ¹⁴ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a s-butyl group, a t-butyl group, It has a substituent such as a pentyl group, hexyl group, cyclohexyl group, heptyl group, octyl group, nonyl group, decyl group, lauryl group, or a group obtained by substituting at least one hydrogen atom of these groups with a substituent. Or a group obtained by removing one hydrogen atom from an alkyl group having 1 to 20 carbon atoms, which is not present; phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl group, 9- One hydrogen atom from an aryl group having 6 to 30 carbon atoms, which may or may not have a substituent, such as an anthracenyl group or a group in which at least one hydrogen atom in these groups is substituted with a substituent. Excluded group Methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyloxy group, cyclohexyloxy group, cyclononyloxy group , A cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, a group in which at least one hydrogen atom in these groups is substituted with a substituent, and the like, having 1 or less carbon atoms A group obtained by removing one hydrogen atom from 50 alkoxy groups; a group obtained by removing one hydrogen atom from an amino group having a substituent containing a carbon atom; one from a silyl group having a substituent containing a carbon atom From the viewpoint of ease of synthesis of the raw material monomer, one hydrogen atom is removed from the alkyl group. A group in which one hydrogen atom has been removed from an aryl group or a group in which one hydrogen atom has been removed from an alkoxy group is preferred.

  Examples of the structural unit represented by the formula (23) include the following structural units.

(In the formula (24), R ¹³ represents a (1 + m11 + m12) valent organic group, and Q ¹ , Q ³ , Y ¹ , M ¹ , Z ¹ , Y ³ , n1, a1, b1, and n3 have the same meaning as described above. M11 and m12 each independently represents an integer of 1 or more, and R ¹³ , m 11, m 12, Q ¹ , Q ³ , Y ¹ , M ¹ , Z ¹ , Y ³ , n1, a1, b1, and n3 (If there are several, each may be the same or different.)

In the formula (24), examples of the (1 + m11 + m12) -valent organic group represented by R ¹³ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which (m11 + m12) hydrogen atoms are removed from an alkyl group having 1 to 20 carbon atoms with or without: phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl A group having 9 to 30 carbon atoms, which may or may not have a substituent, such as a group, a 9-anthracenyl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group obtained by removing (m11 + m12) hydrogen atoms from a reel group; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy Groups, cyclopentyloxy groups, cyclohexyloxy groups, cyclononyloxy groups, cyclododecyloxy groups, norbornyloxy groups, adamantyloxy groups, groups in which at least one hydrogen atom in these groups is substituted with a substituent, etc. A group obtained by removing (m11 + m12) hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms with or without a substituent; (m11 + m12) hydrogens from an amino group having a substituent containing a carbon atom Groups excluding atoms; (m11 + m12) silyl groups having substituents containing carbon atoms From the viewpoint of ease of synthesis of the raw material monomer, a group in which (m11 + m12) hydrogen atoms have been removed from the alkyl group, and (m11 + m12) hydrogen atoms have been removed from the aryl group. A group obtained by removing (m11 + m12) hydrogen atoms from a group or alkoxy group is preferred.

  Examples of the structural unit represented by the formula (24) include the following structural units.

  As the structural unit represented by the formula (13), the structural unit represented by the formula (25) is preferable from the viewpoint of durability of the obtained ionic polymer.

(In the formula (25), R ¹⁵ represents a (1 + m13 + m14) -valent organic group, and Q ¹ , Q ³ , Y ¹ , M ¹ , Z ¹ , Y ³ , n1, a1, b1, and n3 have the same meaning as described above. the stands, m13, m14 and m15 represent each independently an integer of 1 or ^{more, R 15, m13, m14,} Q 1, Q 3, Y 1, M 1, Z 1, Y 3, n1, a1, b1 and When there are a plurality of n3s, they may be the same or different.)

In the formula (25), examples of the (1 + m13 + m14) -valent organic group represented by R ¹⁵ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which (m13 + m14) hydrogen atoms are removed from an alkyl group having 1 to 20 carbon atoms with or without: phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl A group having 9 to 30 carbon atoms, which may or may not have a substituent, such as a group, a 9-anthracenyl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group obtained by removing (m13 + m14) hydrogen atoms from a reel group; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy Groups, cyclopentyloxy groups, cyclohexyloxy groups, cyclononyloxy groups, cyclododecyloxy groups, norbornyloxy groups, adamantyloxy groups, groups in which at least one hydrogen atom in these groups is substituted with a substituent, etc. A group obtained by removing (m13 + m14) hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms with or without a substituent; (m13 + m14) hydrogens from an amino group having a substituent containing a carbon atom Groups excluding atoms; (m13 + m14) silyl groups having substituents containing carbon atoms From the viewpoint of ease of synthesis of the raw material monomer, a group in which (m13 + m14) hydrogen atoms have been removed from the alkyl group, and (m13 + m14) hydrogen atoms have been removed from the aryl group. A group obtained by removing (m13 + m14) hydrogen atoms from a group or alkoxy group is preferred.

  Examples of the structural unit represented by the formula (25) include the following structural units.

Examples of the structural unit represented by the formula (15) As the structural unit represented by the formula (15), from the viewpoint of the electron transport property of the obtained ionic polymer, the structural unit represented by the formula (26), The structural unit represented by Formula (27) is preferable, and the structural unit represented by Formula (27) is more preferable.

(In the formula (26), R ¹⁶ represents a (1 + m16 + m17) valent organic group, R ¹⁷ represents a monovalent organic group, Q ² , Q ³ , Y ² , M ² , Z ² , Y ³ , n2 , a2, b2 and n3 represent the same as defined above, m16 and represent an integer of 1 or more, respectively m17 ^{independently, Q 2, Q 3, Y} 2, M 2, Z 2, Y 3, n2, a2 , B2 and n3 may be the same or different when there are a plurality of each.

In the formula (26), examples of the (1 + m16 + m17) -valent organic group represented by R ¹⁶ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which (m16 + m17) hydrogen atoms are removed from an alkyl group having 1 to 20 carbon atoms with or without: phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl A group having 9 to 30 carbon atoms, which may or may not have a substituent, such as a group, a 9-anthracenyl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group obtained by removing (m16 + m17) hydrogen atoms from a reel group; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy Groups, cyclopentyloxy groups, cyclohexyloxy groups, cyclononyloxy groups, cyclododecyloxy groups, norbornyloxy groups, adamantyloxy groups, groups in which at least one hydrogen atom in these groups is substituted with a substituent, etc. A group obtained by removing (m16 + m17) hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms with or without a substituent; (m16 + m17) hydrogens from an amino group having a substituent containing a carbon atom Groups excluding atoms; (m16 + m17) silyl groups having substituents containing carbon atoms From the viewpoint of ease of synthesis of the raw material monomer, a group in which (m16 + m17) hydrogen atoms have been removed from the alkyl group, and (m16 + m17) hydrogen atoms have been removed from the aryl group. A group obtained by removing (m16 + m17) hydrogen atoms from a group or alkoxy group is preferred.

In the formula (26), examples of the monovalent organic group represented by R ¹⁷ include a methyl group, ethyl group, propyl group, isopropyl group, butyl group, isobutyl group, s-butyl group, t-butyl group, It has a substituent such as a pentyl group, hexyl group, cyclohexyl group, heptyl group, octyl group, nonyl group, decyl group, lauryl group, or a group obtained by substituting at least one hydrogen atom of these groups with a substituent. Or a group obtained by removing one hydrogen atom from an alkyl group having 1 to 20 carbon atoms, which is not present; phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl group, 9- One hydrogen atom from an aryl group having 6 to 30 carbon atoms, which may or may not have a substituent, such as an anthracenyl group or a group in which at least one hydrogen atom in these groups is substituted with a substituent. Excluded group Methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyloxy group, cyclohexyloxy group, cyclononyloxy Group, cyclododecyloxy group, norbornyloxy group, adamantyloxy group, or the number of carbon atoms having or not having a substituent, such as a group in which at least one hydrogen atom in these groups is substituted with a substituent A group obtained by removing one hydrogen atom from 1 to 50 alkoxy groups; a group obtained by removing one hydrogen atom from an amino group having a substituent containing a carbon atom; and a silyl group having a substituent containing a carbon atom. From the viewpoint of ease of synthesis of the raw material monomer, one hydrogen atom from the alkyl group is exemplified. Except groups, groups obtained by removing one hydrogen atom from an aryl group, a group derived by removing one hydrogen atom from an amino group.

  Examples of the structural unit represented by the formula (26) include the following structural units.

(In the formula (27), R ¹⁶ represents a (1 + m16 + m17) -valent organic group, and Q ² , Q ³ , Y ² , M ² , Z ² , Y ³ , n 2, a 2, b 2 and n 3 have the same meaning as described above. the stands, m16 and represent an integer of 1 or more each independently ^{m17, R 16, m16, m17} , Q 2, Q 3, Y 2, M 2, Z 2, Y 3, n2, a2, b2 , and n3 If there are multiple of each, they may be the same or different.)

In the formula (27), examples of the (1 + m16 + m17) -valent organic group represented by R ¹⁶ include methyl, ethyl, propyl, isopropyl, butyl, isobutyl, s-butyl, and t-butyl. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which (m16 + m17) hydrogen atoms are removed from an alkyl group having 1 to 20 carbon atoms with or without: phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl A group having 9 to 30 carbon atoms, which may or may not have a substituent, such as a group, a 9-anthracenyl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group obtained by removing (m16 + m17) hydrogen atoms from a diol group; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyl An oxy group, a cyclopentyloxy group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, or a group in which at least one of these groups is substituted with a substituent A group obtained by removing (m16 + m17) hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms with or without a substituent, such as (m16 + m17) amino groups having a substituent containing a carbon atom A group excluding a hydrogen atom; (m16 + m17) silyl groups having a substituent containing a carbon atom From the viewpoint of ease of synthesis of the raw material monomer, a group in which (m16 + m17) hydrogen atoms have been removed from the alkyl group, and (m16 + m17) hydrogen atoms have been removed from the aryl group. A group obtained by removing (m16 + m17) hydrogen atoms from a group or alkoxy group is preferred.

  Examples of the structural unit represented by the formula (27) include the following structural units.

  As the structural unit represented by the formula (15), the structural unit represented by the formula (28) is preferable from the viewpoint of durability of the obtained ionic polymer.

(In the formula (28), R ¹⁸ represents a (1 + m18 + m19) -valent organic group, and Q ² , Q ³ , Y ² , M ² , Z ² , Y ³ , n 2, a 2, b 2 and n 3 have the same meaning as described above. M18, m19 and m20 each independently represents an integer of 1 or more, and R ¹⁸ , m18, m19, Q ² , Q ³ , Y ² , M ² , Z ² , Y ³ , n2, a2, b2 and When there are a plurality of n3s, they may be the same or different.)

In the formula (28), examples of the (1 + m18 + m19) -valent organic group represented by R ¹⁸ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which (m18 + m19) hydrogen atoms are removed from an alkyl group having 1 to 20 carbon atoms with or without: phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl A group having 9 to 30 carbon atoms, which may or may not have a substituent, such as a group, a 9-anthracenyl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group obtained by removing (m18 + m19) hydrogen atoms from a reel group; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy Groups, cyclopentyloxy groups, cyclohexyloxy groups, cyclononyloxy groups, cyclododecyloxy groups, norbornyloxy groups, adamantyloxy groups, groups in which at least one hydrogen atom in these groups is substituted with a substituent, etc. A group obtained by removing (m18 + m19) hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms with or without a substituent; (m18 + m19) hydrogens from an amino group having a substituent containing a carbon atom Groups excluding atoms; (m18 + m19) silyl groups having substituents containing carbon atoms From the viewpoint of ease of synthesis of the raw material monomer, a group in which (m18 + m19) hydrogen atoms have been removed from the alkyl group, and (m18 + m19) hydrogen atoms have been removed from the aryl group. A group obtained by removing (m18 + m19) hydrogen atoms from an alkoxy group is preferred.

  Examples of the structural unit represented by the formula (28) include the following structural units.

Examples of the structural unit represented by the formula (17) As the structural unit represented by the formula (17), from the viewpoint of the electron transport property of the obtained ionic polymer, the structural unit represented by the formula (29) is preferable.

(In formula (29), R ¹⁹ represents a single bond or a (1 + m21) -valent organic group, R ²⁰ represents a single bond or a (1 + m22) -valent organic group, and Q ¹ , Q ³ , Y ¹ , M ^{1 , Z 1, Y 3, n1} , a1, b1 and n3 represent the same as defined above, represents an integer of 1 or more, respectively m21 and m22 independently, provided ^that when ^{R 19} is a single bond m21 represents 1 , R ²⁰ is a single bond, m22 represents 1, and when there are a plurality of Q ¹ , Q ³ , Y ¹ , M ¹ , Z ¹ , Y ³ , n1, a1, b1 and n3, they are the same or different May be.)

In the formula (29), examples of the (1 + m21) -valent organic group represented by R ¹⁹ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which (m21) hydrogen atoms are removed from an alkyl group having 1 to 20 carbon atoms, which may or may not include: phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl Group, 9-anthracenyl group, aryl group having 6 to 30 carbon atoms with or without a substituent such as a group in which at least one hydrogen atom in these groups is substituted with a substituent (m 21) Groups excluding one hydrogen atom; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyloxy Substituents such as a group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, a group in which at least one hydrogen atom in these groups is substituted with a substituent, and the like A group in which (m21) hydrogen atoms are removed from an alkoxy group having 1 to 50 carbon atoms with or without having; and (m21) hydrogen atoms are removed from an amino group having a substituent containing a carbon atom Group: a group obtained by removing (m21) hydrogen atoms from a silyl group having a substituent containing a carbon atom. From the viewpoint of easiness, (m21) hydrogen atoms are removed from the alkyl group, (m21) hydrogen atoms are removed from the aryl group, and (m21) hydrogen atoms are removed from the alkoxy group. The groups are preferred.

In the formula (29), examples of the (1 + m22) -valent organic group represented by R ²⁰ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which (m22) hydrogen atoms are removed from an alkyl group having 1 to 20 carbon atoms, which may or may not include: phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl Group, 9-anthracenyl group, aryl group having 6 to 30 carbon atoms with or without a substituent such as a group in which at least one hydrogen atom in these groups is substituted with a substituent (m 22) Groups excluding one hydrogen atom; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyloxy Substituents such as a group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, a group in which at least one hydrogen atom in these groups is substituted with a substituent, and the like A group in which (m22) hydrogen atoms have been removed from an alkoxy group having 1 to 50 carbon atoms with or without having; and (m22) hydrogen atoms have been removed from an amino group having a substituent containing carbon atoms Group: a group obtained by removing (m22) hydrogen atoms from a silyl group having a substituent containing a carbon atom. From the viewpoint of easiness, a group obtained by removing (m22) hydrogen atoms from an alkyl group, a group obtained by removing (m22) hydrogen atoms from an aryl group, and (m22) hydrogen atoms from an alkoxy group The groups are preferred.

  Examples of the structural unit represented by the formula (29) include the following structural units.

  The structural unit represented by the formula (17) is preferably a structural unit represented by the formula (30) from the viewpoint of durability of the obtained ionic polymer.

(In Formula (30), R ²¹ represents a single bond or a (1 + m23) -valent organic group, R ²² represents a single bond or a (1 + m24) -valent organic group, and Q ¹ , Q ³ , Y ¹ , M ^{1 , Z 1, Y 3, n1} , a1, b1 and n3 represent the same as defined above, represents an integer of 1 or more, respectively m23 and m24 independently, provided ^that when ^{R 21} is a single bond m23 represents 1 when ^{R 22} is a single bond m24 represents 1, represents an integer of 1 or more, respectively m25 and m26 ^{independently, m23, m24, R 21,} R 22, Q 1, Q 3, Y 1, M 1, When there are a plurality of Z ¹ , Y ³ , n1, a1, b1, and n3, they may be the same or different.)

In the formula (30), examples of the (1 + m23) -valent organic group represented by R ²¹ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which (m23) hydrogen atoms are removed from an alkyl group having 1 to 20 carbon atoms with or without: phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl Group, 9-anthracenyl group, aryl group having 6 to 30 carbon atoms with or without a substituent such as a group in which at least one hydrogen atom in these groups is substituted with a substituent (m 23) Groups excluding one hydrogen atom; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyloxy Substituents such as a group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, a group in which at least one hydrogen atom in these groups is substituted with a substituent, and the like A group in which (m23) hydrogen atoms are removed from an alkoxy group having 1 to 50 carbon atoms with or without having; and (m23) hydrogen atoms are removed from an amino group having a substituent containing a carbon atom Group: a group obtained by removing (m23) hydrogen atoms from a silyl group having a substituent containing a carbon atom. From the viewpoint of easiness, a group in which (m23) hydrogen atoms have been removed from an alkyl group, a group in which (m23) hydrogen atoms have been removed from an aryl group, and (m23) hydrogen atoms have been removed from an alkoxy group The groups are preferred.

In the formula (30), examples of the (1 + m24) -valent organic group represented by R ²² include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which (m24) hydrogen atoms are removed from an alkyl group having 1 to 20 carbon atoms with or without: phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl Group, 9-anthracenyl group, aryl group having 6 to 30 carbon atoms with or without a substituent such as a group in which at least one hydrogen atom in these groups is substituted with a substituent (m 24) Groups excluding one hydrogen atom; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyloxy Substituents such as a group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, a group in which at least one hydrogen atom in these groups is substituted with a substituent, and the like A group in which (m24) hydrogen atoms are removed from an alkoxy group having 1 to 50 carbon atoms with or without having; and (m24) hydrogen atoms are removed from an amino group having a substituent containing a carbon atom Group: a group obtained by removing (m24) hydrogen atoms from a silyl group having a substituent containing a carbon atom. From the viewpoint of easiness, (m24) hydrogen atoms are removed from the alkyl group, (m24) hydrogen atoms are removed from the aryl group, and (m24) hydrogen atoms are removed from the alkoxy group. The groups are preferred.

  Examples of the structural unit represented by the formula (30) include the following structural units.

Example of Structural Unit Represented by Formula (20) As the structural unit represented by Formula (20), the structural unit represented by Formula (31) is preferable from the viewpoint of the electron transport property obtained.

(In Formula (31), R ²³ represents a single bond or a (1 + m27) -valent organic group, R ²⁴ represents a single bond or a (1 + m28) -valent organic group, Q ² , Q ³ , Y ² , M ² , Z ² , Y ³ , n 2, a 2, b 2 and n 3 represent the same meaning as described above, and m 27 and m 28 each independently represent an integer of 1 or more, provided that m 27 represents 1 when R ²³ is a single bond. , When R ²⁴ is a single bond, m28 represents 1, and when Q ² , Q ³ , Y ² , M ² , Z ² , Y ³ , n 2, a 2, b 2 and n 3 are plural, they are the same or different May be.)

In formula (31), examples of the (1 + m27) -valent organic group represented by R ²³ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which (m27) hydrogen atoms are removed from an alkyl group having 1 to 20 carbon atoms, which may or may not have; phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl Group, 9-anthracenyl group, aryl group having 6 to 30 carbon atoms with or without a substituent such as a group in which at least one hydrogen atom in these groups is substituted with a substituent (m 27) Groups excluding one hydrogen atom; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyloxy Substituents such as a group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, a group in which at least one hydrogen atom in these groups is substituted with a substituent, and the like A group in which (m27) hydrogen atoms have been removed from an alkoxy group having 1 to 50 carbon atoms with or without having; and (m27) hydrogen atoms have been removed from an amino group having a substituent containing carbon atoms Group: a group obtained by removing (m27) hydrogen atoms from a silyl group having a substituent containing a carbon atom. From the viewpoint of easiness, a group in which (m27) hydrogen atoms have been removed from an alkyl group, a group in which (m27) hydrogen atoms have been removed from an aryl group, and (m27) hydrogen atoms have been removed from an alkoxy group The groups are preferred.

In the formula (31), examples of the (1 + m28) -valent organic group represented by R ²⁴ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which (m28) hydrogen atoms are removed from an alkyl group having 1 to 20 carbon atoms with or without: phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl Group, 9-anthracenyl group, aryl group having 6 to 30 carbon atoms with or without a substituent such as a group in which at least one hydrogen atom in these groups is substituted with a substituent (m 28) Groups excluding one hydrogen atom; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyloxy Substituents such as a group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, a group in which at least one hydrogen atom in these groups is substituted with a substituent, and the like A group in which (m28) hydrogen atoms have been removed from an alkoxy group having 1 to 50 carbon atoms with or without having; and (m28) hydrogen atoms have been removed from an amino group having a substituent containing a carbon atom Group: a group obtained by removing (m28) hydrogen atoms from a silyl group having a substituent containing a carbon atom. From the viewpoint of easiness, (m28) hydrogen atoms are removed from the alkyl group, (m28) hydrogen atoms are removed from the aryl group, and (m28) hydrogen atoms are removed from the alkoxy group. The groups are preferred.

  Examples of the structural unit represented by the formula (31) include the following structural units.

  As the structural unit represented by the formula (20), the structural unit represented by the formula (32) is preferable from the viewpoint of durability of the obtained ionic polymer.

(In Formula (32), R ²⁵ represents a single bond or a (1 + m29) -valent organic group, R ²⁶ represents a single bond or a (1 + m30) -valent organic group, and Q ² , Q ³ , Y ² , M ^{2 , Z 2, Y 3, n2} , a2, b2 and n3 represent the same as defined above, represents an integer of 1 or more, respectively m29 and m30 independently, provided ^that when ^{R 25} is a single bond m29 represents 1 , R ²⁶ is a single bond, m30 represents 1, m31 and m32 each independently represents an integer of 1 or more, m29, m30, R ²⁵ , R ²⁶ , Q ² , Q ³ , Y ² , M ² , When there are a plurality of Z ² , Y ³ , n 2, a 2, b 2 and n 3, they may be the same or different.)

In the formula (32), examples of the (1 + m29) -valent organic group represented by R ²⁵ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which (m29) hydrogen atoms are removed from an alkyl group having 1 to 20 carbon atoms, which may or may not include: phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl Group, 9-anthracenyl group, aryl group having 6 to 30 carbon atoms with or without a substituent such as a group in which at least one hydrogen atom in these groups is substituted with a substituent (m 29) groups excluding one hydrogen atom; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyloxy Substituents such as a group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, a group in which at least one hydrogen atom in these groups is substituted with a substituent, and the like A group in which (m29) hydrogen atoms are removed from an alkoxy group having 1 to 50 carbon atoms with or without having; and (m29) hydrogen atoms are removed from an amino group having a substituent containing a carbon atom Group: a group obtained by removing (m29) hydrogen atoms from a silyl group having a substituent containing a carbon atom. From the viewpoint of easiness, a group in which (m29) hydrogen atoms are removed from an alkyl group, a group in which (m29) hydrogen atoms are removed from an aryl group, and (m29) hydrogen atoms are removed from an alkoxy group The groups are preferred.

In the formula (32), examples of the (1 + m30) -valent organic group represented by R ²⁶ include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a s-butyl group, and a t-butyl group. A substituent such as a group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, or a group in which at least one hydrogen atom in these groups is substituted with a substituent. A group in which (m30) hydrogen atoms are removed from an alkyl group having 1 to 20 carbon atoms with or without: phenyl group, 1-naphthyl group, 2-naphthyl group, 1-anthracenyl group, 2-anthracenyl Group, 9-anthracenyl group, aryl group having 6 to 30 carbon atoms with or without a substituent such as a group in which at least one hydrogen atom in these groups is substituted with a substituent (m 30) groups excluding one hydrogen atom; methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, nonyloxy group, dodecyloxy group, cyclopropyloxy group, cyclobutyloxy group, cyclopentyloxy Substituents such as a group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, a group in which at least one hydrogen atom in these groups is substituted with a substituent, and the like A group in which (m30) hydrogen atoms are removed from an alkoxy group having 1 to 50 carbon atoms with or without having; and (m30) hydrogen atoms are removed from an amino group having a substituent containing carbon atoms Group: a group obtained by removing (m30) hydrogen atoms from a silyl group having a substituent containing a carbon atom. From the viewpoint of easiness, a group in which (m30) hydrogen atoms are removed from an alkyl group, a group in which (m30) hydrogen atoms are removed from an aryl group, and (m30) hydrogen atoms are removed from an alkoxy group The groups are preferred.

  Examples of the structural unit represented by the formula (32) include the following structural units.

-Other structural unit The ionic polymer used for this invention may have 1 or more types of structural units further represented by Formula (33).

(In formula (33), Ar ⁵ represents a divalent aromatic group having or not having a substituent, or a divalent aromatic amine residue having or not having a substituent, and X ′ represents a substituted group. Represents an imino group with or without a group, a silylene group with or without a substituent, an ethenylene group with or without a substituent, or an ethynylene group, and m33 and m34 are each independently 0 or 1 And at least one of m33 and m34 is 1.)

Examples of the divalent aromatic group represented by Ar ⁵ in formula (33) include a divalent aromatic hydrocarbon group and a divalent aromatic heterocyclic group. Examples of the divalent aromatic group include a benzene ring, a pyridine ring, a 1,2-diazine ring, a 1,3-diazine ring, a 1,4-diazine ring, a 1,3,5-triazine ring, a furan ring, and a pyrrole. A divalent group in which two hydrogen atoms are removed from a monocyclic aromatic ring such as a ring, thiophene ring, pyrazole ring, imidazole ring, oxazole ring, oxadiazole ring, azadiazole ring; the group consisting of the monocyclic aromatic ring A divalent group obtained by removing two hydrogen atoms from a condensed polycyclic aromatic ring condensed with two or more selected from: two selected from the group consisting of the monocyclic aromatic ring and the condensed polycyclic aromatic ring A divalent group obtained by removing two hydrogen atoms from an aromatic ring assembly formed by connecting the above aromatic rings with a single bond, an ethenylene group or an ethynylene group; the condensed polycyclic aromatic ring or the aromatic ring assembly adjacent to each other. Two aromatic rings are methylene, ethylene, and cal Group, and a divalent group in which two hydrogen atoms are removed from a bridged polycyclic aromatic ring having a bridged crosslinked with divalent group such as an imino group.

  In the condensed polycyclic aromatic ring, the number of monocyclic aromatic rings to be condensed is preferably 2 to 4, more preferably 2 to 3, and still more preferably 2 from the viewpoint of solubility of the ionic polymer. In the aromatic ring assembly, the number of linked aromatic rings is preferably 2 to 4, more preferably 2 to 3, and still more preferably 2 from the viewpoint of solubility. In the bridged polycyclic aromatic ring, the number of aromatic rings to be bridged is preferably 2 to 4, more preferably 2 to 3, and still more preferably 2 from the viewpoint of solubility of the ionic polymer.

  Examples of the monocyclic aromatic ring include the following rings.

  Examples of the condensed polycyclic aromatic ring include the following rings.

  Examples of the aromatic ring assembly include the following rings.

  Examples of the bridged polycyclic aromatic ring include the following rings.

From the viewpoint of either or both of the electron accepting property and hole accepting property of the ionic polymer, the divalent aromatic group represented by Ar ⁵ is represented by the formulas 45-60, 61-71, 77-80, A divalent group obtained by removing two hydrogen atoms from the ring represented by 91, 92, 93 or 96 is preferable, and the ring represented by the formulas 45 to 50, 59, 60, 77, 80, 91, 92 or 96 A divalent group in which two hydrogen atoms are removed from is more preferable.

The above divalent aromatic group may have a substituent. Examples of the substituent include the same substituents as those exemplified in the description of Q ¹ described above.

Examples of the divalent aromatic amine residue represented by Ar ⁵ in formula (33) include a group represented by formula (34).

(In the formula (34), Ar ⁶ , Ar ⁷ , Ar ⁸ and Ar ⁹ are each independently an arylene group having or not having a substituent, or a divalent heterocyclic ring having or without a substituent. Each of Ar ¹⁰ , Ar ¹¹ and Ar ¹² independently represents an aryl group with or without a substituent or a monovalent heterocyclic group with or without a substituent, n10 and m35 independently represents 0 or 1.)

  Examples of the substituent that the arylene group, aryl group, divalent heterocyclic group, and monovalent heterocyclic group may have include a halogen atom, an alkyl group, an alkyloxy group, an alkylthio group, an aryl group, and an aryloxy group. Group, arylthio group, arylalkyl group, arylalkyloxy group, arylalkylthio group, alkenyl group, alkynyl group, arylalkenyl group, arylalkynyl group, acyl group, acyloxy group, amide group, acid imide group, imine residue, substitution Amino group, substituted silyl group, substituted silyloxy group, substituted silylthio group, substituted silylamino group, cyano group, nitro group, monovalent heterocyclic group, heteroaryloxy group, heteroarylthio group, alkyloxycarbonyl group, aryloxycarbonyl Group, arylalkyloxycarbonyl group, hete And aryloxy carbonyl group and a carboxyl group. The substituent is vinyl group, acetylene group, butenyl group, acrylic group, acrylate group, acrylamide group, methacryl group, methacrylate group, methacrylamide group, vinyl ether group, vinylamino group, silanol group, small ring (cyclopropyl group) , A group having a cyclobutyl group, an epoxy group, an oxetane group, a diketene group, an episulfide group, etc.), a lactone group, a lactam group, or a group containing a siloxane derivative structure.

When n10 is 0, the carbon atom in Ar ⁶ and the carbon atom in Ar ⁸ may be directly bonded, or may be bonded through a divalent group such as —O— or —S—. .

The aryl group and monovalent heterocyclic group represented by Ar ¹⁰ , Ar ¹¹ and Ar ¹² are the same as the aryl group and monovalent heterocyclic group described and exemplified above as the substituent.

Examples of the arylene group represented by Ar ⁶ , Ar ⁷ , Ar ⁸ , Ar ⁹ include the remaining atomic groups obtained by removing two hydrogen atoms bonded to a carbon atom constituting an aromatic ring from an aromatic hydrocarbon, A group having a benzene ring, a group having a condensed ring, a group in which two or more independent benzene rings or condensed rings are bonded through a single bond or a divalent organic group, for example, an alkenylene group such as a vinylene group, etc. . The arylene group usually has 6 to 60 carbon atoms, and preferably 7 to 48 carbon atoms. Specific examples of the arylene group, phenylene group, biphenylene group, C ₁ -C ₁₇ alkoxy phenylene group, C ₁ -C ₁₇ alkyl phenylene group, 1-naphthylene group, 2-naphthylene group, 1-anthracenylene group, 2- anthracenylene Group and 9-anthracenylene group. A hydrogen atom in the aryl group may be substituted with a fluorine atom. Examples of the fluorine atom-substituted aryl group include a tetrafluorophenylene group. Among the aryl groups, a phenylene group, a biphenylene group, a C _{1 to} C ₁₂ alkoxyphenylene group, and a C _{1 to} C ₁₂ alkylphenylene group are preferable.

Examples of the divalent heterocyclic group represented by Ar ⁶ , Ar ⁷ , Ar ⁸ , Ar ⁹ include the remaining atomic groups obtained by removing two hydrogen atoms from a heterocyclic compound. Here, the heterocyclic compound is not only a carbon atom but also an oxygen atom, a sulfur atom, a nitrogen atom, a phosphorus atom, a boron atom, a silicon atom as an element constituting a ring among organic compounds having a cyclic structure. , An organic compound containing a hetero atom such as a selenium atom, a tellurium atom or an arsenic atom. The divalent heterocyclic group may have a substituent. The divalent heterocyclic group usually has 4 to 60 carbon atoms, and preferably 4 to 20 carbon atoms. The number of carbon atoms of the divalent heterocyclic group does not include the number of carbon atoms of the substituent. Examples of such a divalent heterocyclic group include a thiophene diyl group, a C ₁ -C ₁₂ alkylthiophene diyl group, a pyrrole diyl group, a furandiyl group, a pyridinediyl group, a C ₁ -C ₁₂ alkylpyridine diyl group, and a pyridazine. diyl group, a pyrimidine-diyl group, a pyrazinediyl group, a triazine-diyl group, pyrrolidinediyl group, piperidine-diyl group, quinolinediyl group, and isoquinoline-diyl group, among others, a thiophene-diyl group, C ₁ -C ₁₂ alkyl thiophenediyl group, pyridinediyl group and C ₁ -C ₁₂ alkyl pyridinediyl group are more preferable.

  The ionic polymer containing a divalent aromatic amine residue as a structural unit may further have another structural unit. Examples of other structural units include arylene groups such as a phenylene group and a fluorenediyl group. Of these ionic polymers, those containing a crosslinking group are preferred.

  Moreover, as a bivalent aromatic amine residue represented by Formula (34), the group remove | excluding two hydrogen atoms from the aromatic amine represented by following formula 101-110 is illustrated.

The aromatic amines represented by Formulas 101 to 110 may have a substituent within a range that can form a divalent aromatic amine residue, and as the substituent, in the description of Q ¹ described above, The same substituents as the exemplified substituents are exemplified, and when a plurality of substituents are present, they may be the same or different.

  In formula (33), X ′ represents an imino group with or without a substituent, a silylene group with or without a substituent, an ethenylene group with or without a substituent, or an ethynylene group. Examples of the substituent that the imino group, silyl group or ethenylene group may have include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a s-butyl group, a t-butyl group, and a pentyl group. Alkyl groups having 1 to 20 carbon atoms such as hexyl group, cyclohexyl group, heptyl group, octyl group, 2-ethylhexyl group, nonyl group, decyl group, 3,7-dimethyloctyl group, lauryl group; phenyl group, 1 -A naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, an aryl group having 6 to 30 carbon atoms such as a 9-anthracenyl group, and the like, and when there are a plurality of substituents, They may be the same or different.

  From the viewpoint of the stability of the ionic polymer against air, moisture or heat, X 'is preferably an imino group, an ethenylene group or an ethynylene group.

  From the viewpoint of electron acceptability and hole acceptability of the ionic polymer, m33 is preferably 1 and m34 is preferably 0.

  The structural unit represented by the formula (33) is preferably the structural unit represented by the formula (35) from the viewpoint of electron accepting property of the ionic polymer.

(In the formula (35), Ar ¹³ is a pyridinediyl group with or without a substituent, a pyrazinediyl group with or without a substituent, a pyrimidinediyl group with or without a substituent, Represents a pyridazinediyl group with or without a group or a triazinediyl group with or without a substituent.

Examples of the substituent that the pyridinediyl group may have include the same substituents as the substituents exemplified in the description regarding Q ¹ described above. When a plurality of substituents are present, they may be the same or different.
Examples of the substituent that the pyrazinediyl group may have include the same substituents as those exemplified in the description regarding Q ¹ described above. When a plurality of substituents are present, they may be the same or different.
Examples of the substituent that the pyrimidinediyl group may have include the same substituents as the substituents exemplified in the description of Q ¹ described above. When a plurality of substituents are present, they may be the same or different.
Examples of the substituent that the pyridazinediyl group may have include the same substituents as those exemplified in the description of Q ¹ described above. When a plurality of substituents are present, they may be the same or different.
Examples of the substituent that the triazinediyl group may have include the same substituents as those exemplified in the description regarding Q ¹ described above. When a plurality of substituents are present, they may be the same or different.

-Ratio of structural unit Structural unit represented by formula (13), structural unit represented by formula (15), structural unit represented by formula (17), and ionic polymer used in the present invention, From the viewpoint of the light emission efficiency of the organic EL device, the total proportion of the structural units represented by the formula (20) is 30 to 100 mol% in all the structural units contained in the ionic polymer excluding the terminal structural unit. It is more preferable that

-Terminal structural unit As the terminal structural unit (terminal group) of the ionic polymer used in the present invention, a hydrogen atom, methyl group, ethyl group, propyl group, isopropyl group, butyl group, isobutyl group, s- Butyl group, t-butyl group, pentyl group, isoamyl group, hexyl group, cyclohexyl group, heptyl group, octyl group, nonyl group, decyl group, lauryl group methoxy group, ethoxy group, propyloxy group, isopropyloxy group, butoxy group , Isobutoxy group, s-butoxy group, t-butoxy group, pentyloxy group, hexyloxy group, cyclohexyloxy group, heptyloxy group, octyloxy group, 2-ethylhexyloxy group, nonyloxy group, decyloxy group, 3,7- Dimethyloctyloxy group, lauryloxy group, methylthio group, ethylthio O, propylthio, isopropylthio, butylthio, isobutylthio, s-butylthio, t-butylthio, pentylthio, hexylthio, cyclohexylthio, heptylthio, octylthio, nonylthio, decylthio, laurylthio Group, methoxyphenyl group, ethoxyphenyl group, propyloxyphenyl group, isopropyloxyphenyl group, butoxyphenyl group, isobutoxyphenyl group, s-butoxyphenyl group, t-butoxyphenyl group, pentyloxyphenyl group, hexyloxyphenyl group Cyclohexyloxyphenyl group, heptyloxyphenyl group, octyloxyphenyl group, 2-ethylhexyloxyphenyl group, nonyloxyphenyl group, decyloxyphenyl group, 3,7-dimethyloxy Tyloxyphenyl group, lauryloxyphenyl group, methylphenyl group, ethylphenyl group, dimethylphenyl group, propylphenyl group, mesityl group, methylethylphenyl group, isopropylphenyl group, butylphenyl group, isobutylphenyl group, t-butylphenyl Group, pentylphenyl group, isoamylphenyl group, hexylphenyl group, heptylphenyl group, octylphenyl group, nonylphenyl group, decylphenyl group, dodecylphenyl group, methylamino group, dimethylamino group, ethylamino group, diethylamino group, propyl Amino group, dipropylamino group, isopropylamino group, diisopropylamino group, butylamino group, isobutylamino group, s-butylamino group, t-butylamino group, pentylamino group, hexylamino , Cyclohexylamino group, heptylamino group, octylamino group, 2-ethylhexylamino group, nonylamino group, decylamino group, 3,7-dimethyloctylamino group, laurylamino group, cyclopentylamino group, dicyclopentylamino group, cyclohexylamino group , dicyclohexylamino group, ditrifluoromethylamino group, phenylamino group, diphenylamino group, (C ₁ -C ₁₂ alkoxyphenyl) amino group, di (C ₁ -C ₁₂ alkoxyphenyl) amino group, di (C ₁ -C ₁₂ alkylphenyl) amino group, 1-naphthylamino group, 2-naphthylamino group, pentafluorophenylamino group, pyridylamino group, pyridazinylamino group, pyrimidylamino group, pyrazinylamino group, triazinylamino group, (phenyl- C ₁ ~ C ₁₂ alkyl) amino group, (C ₁ -C ₁₂ alkoxyphenyl-C ₁ -C ₁₂ alkyl) amino group, (C ₁ -C ₁₂ alkylphenyl-C ₁ -C ₁₂ alkyl) amino group, di (C _1- C ₁₂ alkoxyphenyl-C ₁ -C ₁₂ alkyl) amino group, di (C ₁ -C ₁₂ alkylphenyl-C ₁ -C ₁₂ alkyl) amino group, 1-naphthyl-C ₁ -C ₁₂ alkylamino group, 2- naphthyl -C ₁ -C ₁₂ alkylamino group, a trimethylsilyl group, triethylsilyl group, tripropylsilyl group, triisopropylsilyl group, isopropyl dimethylsilyl group, isopropyl diethyl silyl group, t- butyl dimethyl silyl group, pentyl dimethylsilyl group, Hexyldimethylsilyl group, heptyldimethylsilyl group, octyldimethylsilyl group, 2-ethylhexyldimethylsilyl Group, nonyldimethylsilyl group, decyldimethylsilyl group, a 3,7-dimethyl silyl group, lauryl dimethyl silyl group, (phenyl -C ₁ -C ₁₂ alkyl) silyl group, (C ₁ -C ₁₂ alkoxyphenyl -C ₁ -C ₁₂ alkyl) silyl group, (C ₁ -C ₁₂ alkylphenyl -C ₁ -C ₁₂ alkyl) silyl group, (1-naphthyl -C ₁ -C ₁₂ alkyl) silyl group, (2-naphthyl -C ₁ -C ₁₂ alkyl) silyl group, (phenyl -C ₁ -C ₁₂ alkyl) dimethyl silyl group, a triphenylsilyl group, tri (p- xylyl) silyl group, tribenzylsilyl group, diphenylmethylsilyl group, t- butyl diphenyl silyl group, dimethylphenyl silyl group, a thienyl group, C ₁ -C ₁₂ alkyl thienyl group, a pyrrolyl group, a furyl group, a pyridyl group, C ₁ ~ ₁₂ alkylpyridyl group, a pyridazinyl group, pyrimidyl group, pyrazinyl group, triazinyl group, pyrrolidyl group, piperidyl group, quinolyl group, isoquinolyl group, hydroxy group, a mercapto group, a fluorine atom, a chlorine atom, a bromine atom, an iodine atom . When a plurality of the terminal structural units are present, they may be the same or different.

-Characteristics of ionic polymers-
The ionic polymer used in the present invention is preferably a conjugated compound. The ionic polymer used in the present invention is a conjugated compound when the ionic polymer has a multiple bond (for example, double bond, triple bond) or a nitrogen atom, oxygen atom, etc. in the main chain. It means that the pair includes a region that is continuous with one single bond. When the ionic polymer is a conjugated compound, from the viewpoint of electron transport properties of the conjugated compound,
{(The number of atoms on the main chain contained in a region where multiple bonds or unshared electron pairs of nitrogen atoms, oxygen atoms, etc. are connected across one single bond) / (the number of all atoms on the main chain) )} × 100% calculated ratio is preferably 50% or more, more preferably 60% or more, more preferably 70% or more, and more preferably 80% or more, More preferably, it is 90% or more.

The ionic polymer used in the present invention is preferably a polymer compound, more preferably a conjugated polymer compound. Here, the polymer compound means a compound having a polystyrene-equivalent number average molecular weight of 1 × 10 ³ or more. Moreover, the ionic polymer used in the present invention being a conjugated polymer compound means that the ionic polymer is a conjugated compound and a polymer compound.

From the viewpoint of film formability by application of the ionic polymer used in the present invention, the ionic polymer preferably has a polystyrene-equivalent number average molecular weight of 1 × 10 ³ to 1 × 10 ⁸ , preferably 2 × 10 ³ to 1 × 10 ⁷ is more preferable, 3 × 10 ³ to 1 × 10 ⁷ is more preferable, and 5 × 10 ³ to 1 × 10 ⁷ is even more preferable. From the viewpoint of the purity of the ionic polymer preferably has a weight average molecular weight in terms of polystyrene is ^{1 × 10 3 ~5 × 10 7} , more preferably ^{1 × 10 3 ~1 × 10 7} , 1 It is more preferable that it is * 10 < ³ > -5 * 10 < ⁶ >. Further, from the viewpoint of solubility of the ionic polymer, it is preferred that the number average molecular weight in terms of polystyrene is ^{1 × 10 3 ~5 × 10 5} , more preferably ^{1 × 10 3 ~5 × 10 4} , More preferably, it is 1 × 10 ^{3 to} 3 × 10 ³ . The polystyrene-equivalent number average molecular weight and weight average molecular weight of the ionic polymer used in the present invention can be determined using, for example, gel permeation chromatography (GPC).

  From the viewpoint of the purity of the ionic polymer used in the present invention, the number of all structural units (ie, the degree of polymerization) contained in the ionic polymer excluding the terminal structural unit is preferably 1 or more and 20 or less. It is more preferably 10 or less and more preferably 1 or more and 5 or less.

  From the viewpoint of electron acceptability and hole acceptability of the ionic polymer used in the present invention, the orbital energy of the lowest unoccupied molecular orbital (LUMO) of the ionic polymer is −5.0 eV or more and −2.0 eV or less. It is preferable that it is -4.5 eV or more and -2.0 eV or less. From the same viewpoint, the orbital energy of the highest occupied molecular orbital (HOMO) of the ionic polymer is preferably −6.0 eV or more and −3.0 eV or less, and −5.5 eV or more and −3.0 eV or less. Is more preferable. However, the orbital energy of HOMO is lower than that of LUMO. The orbital energy of the highest occupied molecular orbital (HOMO) of the ionic polymer is obtained by measuring the ionization potential of the ionic polymer and using the obtained ionization potential as the orbital energy. On the other hand, the orbital energy of the lowest unoccupied molecular orbital (LUMO) of the ionic polymer is obtained by calculating the energy difference between HOMO and LUMO and using the sum of the value and the ionization potential measured above as the orbital energy. . A photoelectron spectrometer is used to measure the ionization potential. Further, the energy difference between HOMO and LUMO is obtained from the absorption terminal by measuring the absorption spectrum of the ionic polymer using an ultraviolet / visible / near infrared spectrophotometer.

The polymer used in the present invention is preferably substantially non-luminescent when used in an electroluminescent device. Here, the fact that a certain polymer is substantially non-luminous means as follows. First, an electroluminescent element A having a layer containing a certain polymer is produced. On the other hand, the electroluminescent element 2 which does not have the layer containing a polymer is produced. Although the electroluminescent element A has a layer containing a polymer, the electroluminescent element 2 is different from the electroluminescent element 2 only in that it does not have a layer containing a polymer. Next, a forward voltage of 10 V is applied to the electroluminescent element A and the electroluminescent element 2 to measure an emission spectrum. The wavelength λ that gives the maximum peak in the emission spectrum obtained for the electroluminescent element 2 is obtained. The emission spectrum at the wavelength λ is set to 1, the emission spectrum obtained for the electroluminescent element 2 is normalized, and the normalized emission amount S ₀ is calculated by integrating the wavelength. On the other hand, assuming that the emission intensity at the wavelength λ is 1, the emission spectrum obtained for the electroluminescent element A is also normalized, and the normalized emission amount S is calculated by integrating the wavelength. When the value calculated by (S−S ₀ ) / S ₀ × 100% is 30% or less, that is, compared with the normalized light emission amount of the electroluminescent element 2 having no polymer-containing layer, the polymer When the increase in the normalized light emission amount of the electroluminescent device A having a layer containing is 30% or less, the polymer used is substantially non-light-emitting, and (S−S ₀ ) / S _The value calculated by ₀ × 100 is preferably 15% or less, and more preferably 10% or less.

  As the ionic polymer containing the group represented by the formula (1) and the group represented by the formula (3), an ionic polymer consisting only of the group represented by the formula (23), a formula (23) One or more selected from the group consisting of groups represented by formulas 45 to 50, 59, 60, 77, 80, 91, 92, 96, and 101 to 110, wherein two hydrogen atoms are removed An ionic polymer comprising only a group represented by formula (24), a group represented by formula (24) and formulas 45-50, 59, 60, 77, 80, 91, 92 96, 101-110, an ionic polymer comprising at least one group selected from the group consisting of groups obtained by removing two hydrogen atoms, an ion comprising only the group represented by formula (25) Polymer, group represented by formula (25) and formula 45- An ionic polymer comprising one or more groups selected from the group consisting of groups obtained by removing two hydrogen atoms from groups represented by 0, 59, 60, 77, 80, 91, 92, 96, 101-110, An ionic polymer comprising only a group represented by the formula (29), a group represented by the formula (29), and a group represented by the formulas 45 to 50, 59, 60, 77, 80, 91, 92, 96, 101 to 110 An ionic polymer composed of one or more groups selected from the group consisting of a group obtained by removing two hydrogen atoms from the group represented by formula (30), an ionic polymer composed only of the group represented by formula (30), One or more selected from the group consisting of groups represented by formulas 45 to 50, 59, 60, 77, 80, 91, 92, 96, and 101 to 110, wherein two hydrogen atoms are removed An ionic polymer composed of the following group is exemplified.

  Examples of the ionic polymer containing the group represented by the formula (1) and the group represented by the formula (3) include the following polymer compounds. Among these, in the polymer compound represented by the formula in which two types of structural units are separated by a slash “/”, the proportion of the left structural unit is p mol% and the proportion of the right structural unit is (100− p) mol%, and these structural units are randomly arranged. In the following formula, n represents the degree of polymerization.

  (In the formula, p represents a number of 15 to 100.)

  As an ionic polymer containing the group represented by the formula (2) and the group represented by the formula (3), an ionic polymer consisting only of the group represented by the formula (26), the formula (26) 1 or more types selected from the group consisting of groups represented by formulas 45 to 50, 59, 60, 77, 80, 91, 92, 96, 101 to 110 and two hydrogen atoms removed An ionic polymer comprising only the group represented by formula (27), an ionic polymer comprising only the group represented by formula (27), a group represented by formula (27), and formulas 45 to 50, 59, 60, 77, 80, 91, 92. 96, 101-110, an ionic polymer comprising at least one group selected from the group consisting of groups obtained by removing two hydrogen atoms, an ion comprising only the group represented by formula (28) Polymer, group represented by formula (28) and formula 45 An ionic polymer comprising one or more groups selected from the group consisting of groups obtained by removing two hydrogen atoms from the groups represented by 50, 59, 60, 77, 80, 91, 92, 96, 101-110, An ionic polymer comprising only the group represented by the formula (31), the group represented by the formula (31), and the formula 45 to 50, 59, 60, 77, 80, 91, 92, 96, 101 to 110 An ionic polymer comprising at least one group selected from the group consisting of groups obtained by removing two hydrogen atoms from the group to be produced, an ionic polymer comprising only the group represented by formula (32), and formula (32) 1 or more types selected from the group consisting of groups represented by formulas 45 to 50, 59, 60, 77, 80, 91, 92, 96, 101 to 110 and two hydrogen atoms removed An ionic polymer consisting of .

  Examples of the ionic polymer containing the group represented by the formula (2) and the group represented by the formula (3) include the following polymer compounds. Among these, in the polymer compound represented by the formula in which two types of structural units are separated by a slash “/”, the proportion of the left structural unit is p mol% and the proportion of the right structural unit is (100− p) mol%, and these structural units are randomly arranged. In the following formula, n represents the degree of polymerization.

  (In the formula, p represents a number of 15 to 100.)

-Method for producing ionic polymer-
Next, a method for producing the ionic polymer used in the present invention will be described. As a suitable method for producing the ionic polymer used in the present invention, for example, a compound represented by the following general formula (36) is selected and used as one of the raw materials. ) in -A _a - compound is a structural unit represented by the formula (13), said -A _a - compound is a structural unit represented by the formula (15), said -A _a - is the formula ( 17) A method in which at least one of a compound which is a structural unit represented by formula (17) and a compound in which -A _a -is a structural unit represented by formula (20) is contained as an essential raw material, and this is subjected to condensation polymerization Can be mentioned.
Y ⁴ -A _a -Y ⁵ (36)

(In Formula (36), A _a is represented by Formula (3) and one or more groups selected from the group consisting of the group represented by Formula (1) and the group represented by Formula (2). A repeating unit containing a group of at least species is represented, and Y ⁴ and Y ⁵ each independently represent a group involved in condensation polymerization.)

When the ionic polymer used in the present invention contains a structural unit represented by -A _a- in the above formula (36) and another structural unit other than -A _a- , If a compound having two substituents involved in condensation polymerization, which is another structural unit other than -A _a- , is used together with the compound represented by the formula (36), the condensation polymerization is performed. Good.

Examples of the compound having two condensation-polymerizable substituents used to contain such other structural units include compounds represented by the formula (37). Thus, in addition to the compound represented by Y ⁴ -A _a -Y ⁵ , the structural unit represented by -A _b- is obtained by condensation polymerization of the compound represented by Formula (37). Furthermore, the ionic polymer used in the present invention can be produced.
Y ⁶ -A _b -Y ⁷ (37)

(In the formula (37), _Ab is a structural unit represented by the general formula (33) or a structural unit represented by the general formula (35), and Y ⁶ and Y ⁷ are each independently a condensation polymerization. Represents a group involved in

Examples of groups (Y ⁴ , Y ⁵ , Y ⁶ and Y ⁷ ) involved in such condensation polymerization include a hydrogen atom, a halogen atom, an alkyl sulfonate group, an aryl sulfonate group, an aryl alkyl sulfonate group, a boric acid ester residue, Examples include a sulfonium methyl group, a phosphonium methyl group, a phosphonate methyl group, a monohalogenated methyl group, -B (OH) ₂ , a formyl group, a cyano group, and a vinyl group.

  Examples of the halogen atom that can be selected as a group involved in such condensation polymerization include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.

  Examples of the alkyl sulfonate group that can be selected as a group involved in the condensation polymerization include a methane sulfonate group, an ethane sulfonate group, and a trifluoromethane sulfonate group. Examples of the aryl sulfonate group include a benzene sulfonate group and a p-toluene sulfonate group. Is exemplified.

  Examples of the arylalkyl sulfonate group that can be selected as the group involved in the condensation polymerization include a benzyl sulfonate group.

  Examples of the boric acid ester residue that can be selected as a group involved in the condensation polymerization include groups represented by the following formulae.

Furthermore, the sulfonium methyl group that can be selected as a group involved in the condensation polymerization includes the following formula:
_{^{-CH 2 S + Me 2 E -}} , _{^{or, -CH 2 S + Ph 2 E}} -

  (Wherein E represents a halogen atom, Ph represents a phenyl group, and the same shall apply hereinafter).

In addition, as a phosphonium methyl group that can be selected as a group involved in the condensation polymerization,
Following formula:
-CH ₂ P ⁺ Ph ₃ E ^-

  (Wherein E represents a halogen atom).

In addition, as a phosphonate methyl group that can be selected as a group involved in the condensation polymerization,
Following formula:
-CH ₂ PO (OR ^d) ₂

(Wherein, R ^d represents an alkyl group, an aryl group, or an arylalkyl group).

  Furthermore, examples of the monohalogenated methyl group that can be selected as the group involved in the condensation polymerization include a methyl fluoride group, a methyl chloride group, a methyl bromide group, and a methyl iodide group.

Further, a group suitable as a group involved in condensation polymerization varies depending on the type of polymerization reaction. For example, when a zero-valent nickel complex such as a Yamamoto coupling reaction is used, a halogen atom, an alkyl sulfonate group, an aryl sulfonate group And arylalkyl sulfonate groups. In addition, when a nickel catalyst or palladium catalyst such as Suzuki coupling reaction is used, an alkyl sulfonate group, a halogen atom, a boric acid ester residue, -B (OH) _{2 and the} like can be mentioned, and an oxidizing agent or electrochemically In the case of oxidative polymerization, a hydrogen atom is exemplified.

  When producing the ionic polymer used in the present invention, for example, if necessary, the compound (monomer) represented by the general formula (36) or (37) having a plurality of groups involved in condensation polymerization may be used. You may employ | adopt the polymerization method which melt | dissolves in an organic solvent, and makes it react at the temperature below the melting | fusing point of an organic solvent below a boiling point using an alkali and a suitable catalyst. Such polymerization methods include, for example, “Organic Reactions”, Vol. 14, pages 270-490, John Wiley & Sons, Inc., 1965, “Organic Synthesis”. Syntheses), Collective Volume 6 (Collective Volume VI), 407-411, John Wiley & Sons, Inc., 1988, Chemical Review (Vol. 95, 2457). 1995), Journal of Organometallic Chemistry (J. Organomet. Chem.), 576, 147 (1999), Macromore. Yura Chemistry Macromolecular Symposium (Macromol.Chem., Macromol.Symp.), Vol. 12, it is possible to employ a known method described in page 229 (1987).

Moreover, when manufacturing the ionic polymer used for this invention, you may employ | adopt a known condensation polymerization reaction according to the group which participates in condensation polymerization. Examples of such a polymerization method include a method of polymerizing a corresponding monomer by a Suzuki coupling reaction, a method of polymerizing by a Grignard reaction, a method of polymerizing by a Ni (0) complex, a method of polymerizing by an oxidizing agent such as FeCl ₃ , Examples thereof include a method of electrochemically oxidative polymerization and a method of decomposing an intermediate polymer having an appropriate leaving group. Among such polymerization reactions, a polymerization method using a Suzuki coupling reaction, a polymerization method using a Grignard reaction, and a polymerization method using a nickel zero-valent complex are preferable because the structure of the resulting ionic polymer can be easily controlled.

  One aspect of a preferred method for producing the ionic polymer used in the present invention is a group selected from the group consisting of a halogen atom, an alkyl sulfonate group, an aryl sulfonate group, and an aryl alkyl sulfonate group as a group involved in condensation polymerization. This is a method for producing an ionic polymer by condensation polymerization in the presence of a nickel zero-valent complex using a starting material monomer. Examples of the raw material monomer used in such a method include dihalogenated compounds, bis (alkyl sulfonate) compounds, bis (aryl sulfonate) compounds, bis (aryl alkyl sulfonate) compounds, halogen-alkyl sulfonate compounds, and halogen-aryl sulfonates. Compounds, halogen-aryl alkyl sulfonate compounds, alkyl sulfonate-aryl sulfonate compounds, alkyl sulfonate-aryl alkyl sulfonate compounds and aryl sulfonate-aryl alkyl sulfonate compounds.

In another aspect of the preferred production method of the ionic polymer, as the group involved in the condensation polymerization, a halogen atom, an alkyl sulfonate group, an aryl sulfonate group, an aryl alkyl sulfonate group, —B (OH) ₂ , and a boric acid ester residue The total number of moles of halogen atoms, alkyl sulfonate groups, aryl sulfonate groups and aryl alkyl sulfonate groups (J), and -B (OH) ₂ and Using a raw material monomer in which the ratio of the total number of moles of boric acid ester residues (K) is substantially 1 (usually K / J is in the range of 0.7 to 1.2), the nickel catalyst or palladium catalyst It is a method for producing an ionic polymer by condensation polymerization in the presence.

  As the organic solvent, although it varies depending on the compound and reaction used, it is generally preferable to use an organic solvent that has been sufficiently deoxygenated to suppress side reactions. When manufacturing an ionic polymer, it is preferable to advance reaction in inert atmosphere using such an organic solvent. In the organic solvent, it is preferable to perform a dehydration process in the same manner as the deoxygenation process. However, this is not the case in the case of reaction in a two-phase system with water such as Suzuki coupling reaction.

  Such organic solvents include saturated hydrocarbons such as pentane, hexane, heptane, octane, cyclohexane, unsaturated hydrocarbons such as benzene, toluene, ethylbenzene, xylene, carbon tetrachloride, chloroform, dichloromethane, chlorobutane, bromobutane, chloro Halogenated saturated hydrocarbons such as pentane, bromopentane, chlorohexane, bromohexane, chlorocyclohexane and bromocyclohexane, halogenated unsaturated hydrocarbons such as chlorobenzene, dichlorobenzene and trichlorobenzene, methanol, ethanol, propanol, isopropanol, butanol, Alcohols such as t-butyl alcohol, carboxylic acids such as formic acid, acetic acid, propionic acid, dimethyl ether, diethyl ether, methyl t-butyl ether, teto Ethers such as hydrofuran, tetrahydropyran and dioxane, trimethylamine, triethylamine, N, N, N ′, N′-tetramethylethylenediamine, amines such as pyridine, N, N-dimethylformamide, N, N-dimethylacetamide, N Amides such as N, diethylacetamide and N-methylmorpholine oxide. These organic solvents may be used alone or in combination of two or more. Among these organic solvents, ethers are more preferable from the viewpoint of reactivity, tetrahydrofuran and diethyl ether are more preferable, and toluene and xylene are preferable from the viewpoint of reaction rate.

  In producing the ionic polymer, it is preferable to add an alkali or an appropriate catalyst in order to react the raw material monomers. What is necessary is just to select such an alkali or a catalyst according to the superposition | polymerization method etc. to employ | adopt. Such an alkali or catalyst is preferably one that is sufficiently dissolved in the solvent used in the reaction. Further, as a method of mixing the alkali or catalyst, the alkali or catalyst solution is slowly added while stirring the reaction liquid under an inert atmosphere such as argon or nitrogen, or the reaction liquid is added to the alkali or catalyst solution. The method of adding slowly is illustrated.

  In the ionic polymer used in the present invention, if the polymerization active group remains as it is in the terminal group, the light emitting characteristics and life characteristics of the resulting light emitting device may be deteriorated. Therefore, the terminal group is protected with a stable group. May be. When the terminal group is protected with such a stable group, when the ionic polymer used in the present invention is a conjugated compound, it has a conjugated bond continuous with the conjugated structure of the main chain of the ionic polymer. Preferably, the structure includes, for example, a structure bonded to an aryl group or a heterocyclic group via a carbon-carbon bond. Examples of such a stable group for protecting the end group include substituents such as a monovalent aromatic compound group represented by the structural formula of Chemical Formula 10 in JP-A-9-45478.

  As another preferable method for producing the ionic polymer containing the structural unit represented by the formula (1), an ionic polymer having no cation is polymerized in the first step, and then from the ionic polymer in the second step. The method of manufacturing the ionic polymer containing a cation is mentioned. As the method for polymerizing the ionic polymer having no cation in the first step, the above-mentioned condensation polymerization reaction may be mentioned. Examples of the reaction in the second step include a hydrolysis reaction with a metal hydroxide, an alkyl ammonium hydroxide, or the like.

As another preferred method for producing an ionic polymer containing a group represented by the formula (2), an ionic polymer having no ions is polymerized in the first step, and ions are generated from the ionic polymer in the second step. The method of manufacturing the ionic polymer containing this is mentioned. As a method for polymerizing an ionic polymer having no ions in the first step, the above-mentioned condensation polymerization reaction may be mentioned. Examples of the reaction in the second step include quaternary ammonium chlorination reaction of amine using alkyl halide, halogen abstraction reaction with SbF _{5 and the} like.

  Since the ionic polymer used in the present invention is excellent in charge generation, an element that emits light with high luminance can be obtained.

  Examples of the method for forming a layer containing an ionic polymer include a method of forming a film using a solution containing an ionic polymer.

Solvents used for film formation from such solutions include alcohols other than water, ethers, esters, nitrile compounds, nitro compounds, alkyl halides, aryl halides, thiols, sulfides Of the solvents such as sulfoxides, thioketones, amides and carboxylic acids, those having a solubility parameter of 9.3 or more are preferable. Examples of the solvent (values in parentheses represent solubility parameter values of each solvent) include methanol (12.9), ethanol (11.2), 2-propanol (11.5), 1- Butanol (9.9), t-butyl alcohol (10.5), acetonitrile (11.8), 1,2-ethanediol (14.7), N, N-dimethylformamide (11.5), dimethyl sulfoxide (12.8), acetic acid (12.4), nitrobenzene (11.1), nitromethane (11.0), 1,2-dichloroethane (9.7), dichloromethane (9.6), chlorobenzene (9.6) ), Bromobenzene (9.9), dioxane (9.8), propylene carbonate (13.3), pyridine (10.4), carbon disulfide (10.0), and a mixed solvent thereof. Be . Here, a mixed solvent obtained by mixing two kinds of solvents (solvent 1 and solvent 2) will be described. The solubility parameter (δ _m ) of the mixed solvent is δ _m = δ ₁ × φ ₁ + δ _2. Xφ ₂ (δ ₁ is the solubility parameter of solvent 1, φ ₁ is the volume fraction of solvent 1, δ ₂ is the solubility parameter of solvent 2, and φ ₂ is the volume fraction of solvent 2.) .

<First Embodiment>
(Organic thin film transistor)
With reference to FIG. 1, the structural example of the organic thin-film transistor of 1st Embodiment is demonstrated. FIG. 1 is a cross-sectional view schematically showing a configuration example of the organic thin film transistor of the first embodiment. The organic thin film transistor 10 of the first embodiment is a configuration example of a bottom gate type organic thin film transistor.

  As shown in FIG. 1, in the organic thin film transistor 10 of the first embodiment, a gate insulating layer 30 and an organic semiconductor layer 40 are stacked in this order on a gate electrode 20, and further on the organic semiconductor layer 40, The first charge injection layer 50A and the first source / drain electrode 60A are stacked in this order, and the second charge injection layer 50B and the second source / drain electrode 60B are formed on the organic semiconductor layer 40. Stacked in order. On the organic semiconductor layer 40, a laminate composed of the first charge injection layer 50A and the first source / drain electrode 60A, and a laminate composed of the second charge injection layer 50B and the second source / drain electrode 60B. Are spaced apart from each other.

  As another embodiment, the charge injection layer in which the first and second source / drain electrodes 60 </ b> A and 60 </ b> B are stacked may be continuous on the organic semiconductor layer 40. From the viewpoint of electrical characteristics, it is preferable that the charge injection layers are spaced apart as in this embodiment. In the following description, when the first charge injection layer 50A and the second charge injection layer 50B are shown without distinction, these may be simply referred to as the charge injection layer 50.

  A conductor or a semiconductor can be used for the gate electrode 20. Since the gate electrode 20 requires a predetermined conductivity, an intrinsic semiconductor can be used. However, from the viewpoint of conductivity, it is preferable to use an n-type semiconductor or a p-type semiconductor doped with impurities. More preferably, is used. For example, a substrate having a desired conductivity type by doping a silicon substrate with any suitable p-type ion or n-type ion can be used as the gate electrode 20. The thickness of the gate electrode 20 in the thickness direction Z is about 0.05 μm to 100 μm.

  The gate insulating layer 30 can be formed using an insulating material such as silicon oxide or silicon nitride. For example, the gate insulating layer 30 can be formed on the surface portion of the silicon substrate by oxidizing the surface portion of the silicon substrate used as the gate electrode 20. As a result, the gate insulating layer 30 can be formed on the gate electrode 20. The thickness in the thickness direction Z of the gate insulating layer 30 is about 50 nm to 1000 nm.

  When the organic semiconductor layer 40 is a p-type organic semiconductor layer, examples of the material thereof include anthracene, tetracene, pentacene, benzopentacene, dibenzopentacene, tetrabenzopentacene, naphthopentacene, hexacene, heptacene, and nanoacene polyacene compounds; phenanthrene, picene , Coronene compounds such as fluorene, pyrene, antanthrene, peroprene, coronene, benzocoronene, dibenzocoronene, hexabunzocoronene, benzodicoronene, vinyl coronene; perylene compounds such as perylene, terylene, diperylene, quaterylene, etc .; Violanthrone, Isoviolanthrone, Chrysene, Circumanthracene, Bisanthene, Zesulene, Heptazesulene, Pyranthrene, Viola Ten, iso Biollante down, biphenyl, triphenylene, terphenyl, Kuo terphenyl, circo biphenyl, kekulene, now becomes a polymer organic semiconductor compounds and a copolymer of phthalocyanine Ageraru.

  When the organic semiconductor layer 40 is an n-type organic semiconductor layer, the materials include perfluoropentacene, perfluorocopper phthalocyanine, TCNQ (tetracyanoquinodimethane), PTCDA (3,4,9,10-perylenetetracarboxylic dianhydride), NTCDA (Naphthalene tetracarboxylic anhydride), PTCDI-C8 (N, N'-dioctyl-3,4,9,10-perylene tetracarboxylic diimide), C60, C60MC12ne C70m12 (Phenyl C61 butyric acid methyl ester), cyano PPV (polycyanote Phthalidene), F4TCNQ (tetrafluoro-tetracyanoquinodimethane), Poly [(2,5-didecyloxy-1,4-phenylene) (2,4,6-triisopropylenephenylene) (2,4,6-triphenylphenylene) , 4,6-triisopropylphenylborane)], poly (benzobisimidazobenzophenanthroline), trifluoromethylphenyl-substituted bithiazole NTCDA (naphthalenetetracarboxylic dianhydride), TCNNQD (11,11,12,12-tetracyanonaphth-2) , 6-quinodimethane). The thickness of the organic semiconductor layer 40 is about 1 nm to 100 μm.

  The charge injection layer 50 functions as an electron injection layer when the conductivity type is n-type, and functions as a hole injection layer when the conductivity type is p-type.

The charge injection layer 50 preferably includes the ionic polymer already described, and is substantially composed of the ionic polymer. In the case of forming the charge injection layer 50 functioning as an electron injection layer, an n-type ionic polymer having electron injection characteristics may be used as a material. When the charge injection layer 50 that functions as a hole injection layer is formed, a p-type ionic polymer having hole injection characteristics may be used as a material.
As described above, the charge injection layer 50 in the present embodiment is disposed on the organic semiconductor layer 40 so as to be separated from the first charge injection layer 50A and the second charge injection layer 50B.
The thickness of the charge injection layer 50 in the thickness direction Z is about 0.5 nm to 100 nm. The distance L1 (corresponding to the channel length) between the first charge injection layer 50A and the second charge injection layer 50B is about 0.1 μm to 1000 μm. Further, the width L2 of the first charge injection layer 50A and the second charge injection layer 50B in the direction X in which the first charge injection layer 50A and the second charge injection layer 50B are separated (the left-right direction in FIG. 1) is It is about 0.1 μm to 1000 μm. In addition, a direction Y perpendicular to the direction X (left and right direction in FIG. 1) in which the first charge injection layer 50A and the second charge injection layer 50B are separated from each other and the thickness direction Z (up and down direction in FIG. 1) of the charge injection layer 50 The width of the charge injection layer 50 (corresponding to the channel width) in the direction (perpendicular to the paper surface in FIG. 1) is about 0.1 μm to 1000 μm.

The first source / drain electrode 60A is provided in contact with the first charge injection layer 50A, and the second source / drain electrode 60B is provided in contact with the second charge injection layer 50B. In the present embodiment, when viewed from one side in the thickness direction Z of the gate electrode 20 (hereinafter sometimes referred to as a plan view), the first charge injection layer 50A and the first source / drain electrode 60A have their peripheral edges. They are provided so that their shapes substantially match. In plan view, the second charge injection layer 50B and the second source / drain electrode 60B are provided so that their peripheral shapes substantially coincide.
The thicknesses in the thickness direction Z of the first and second source / drain electrodes 60A and 60B are about 0.05 μm to 1000 μm, respectively.

  As a material of the first and second source / drain electrodes 60A and 60B, any suitable conductive material can be used. However, when formed by a coating method using a coating liquid, the first and second source / drain electrodes 60A and 60B have conductivity. It is preferable to use metal fine particles. As the metal fine particles, gold, silver, aluminum or the like is preferably used. In addition to metal fine particles of gold, silver, and aluminum, carbon paste, a mixture of carbon paste and metal fine particles, and the like are preferably used.

  The conductivity types of the charge injection layer 50, the organic semiconductor layer 40, and the gate electrode 20 are appropriately selected from the optimal combination, and may be the same or different from each other. The conductivity types are preferably the same. The conductivity type of the gate electrode 20 is not particularly limited as long as it has high conductivity. However, since the n-type silicon semiconductor substrate generally has high conductivity, an n-type silicon semiconductor substrate is used for the gate electrode 20. preferable. For example, the charge injection layer 50, the organic semiconductor layer 40, and the gate electrode 20 are preferably all n-type conductivity. When the charge injection layer 50 is separated from the first charge injection layer 50A and the second charge injection layer 50B, the conductivity types of the first and second charge injection layers 50A and 50B may be different from each other. Good.

(Method for producing organic thin film transistor)
Below, the manufacturing method of the organic thin-film transistor which has the structure demonstrated with reference to FIG. 1 is demonstrated.
An organic thin film transistor manufacturing method is provided between a gate electrode, a first source / drain electrode, a second source / drain electrode, and the first and second source / drain electrodes and the gate electrode. An organic semiconductor layer and a charge injection layer disposed in contact with the first and second source / drain electrodes are formed between the first and second source / drain electrodes and the organic semiconductor layer, respectively. The method of manufacturing an organic thin film transistor includes a step of forming a charge injection layer containing an ionic polymer having charge injection characteristics. That is, the organic thin film transistor manufacturing method includes a step of forming a gate electrode, a step of forming a first source / drain electrode, a step of forming a second source / drain electrode, and the first and second sources. Between the first and second source / drain electrodes and the organic semiconductor layer, the step of forming the organic semiconductor layer provided between the / drain electrode and the gate electrode, and the first and second source / drain electrodes and the organic semiconductor layer. Forming a charge injection layer disposed in contact with the source / drain electrodes. In addition, the order of each process is suitably set according to the structure of an organic thin-film transistor. In this embodiment, the step of forming a gate electrode, the step of forming an organic semiconductor layer, the step of forming a charge injection layer, and the step of forming first and second source / drain electrodes are performed in this order.

  First, the gate electrode 20 is formed. In this step, a substrate functioning as a gate electrode may be obtained from the market. For example, a silicon substrate is prepared and an ion implantation step and an ion diffusion step are performed, so that the entire region or a partial region of the substrate is obtained. The gate electrode may be formed by using any conductivity type.

Next, the gate insulating layer 30 is formed on the surface portion of the prepared substrate. In this step, a film forming step can be performed using an insulating material as described above by a CVD method (chemical vapor deposition method) or the like.
When a silicon substrate is used as the substrate 20, the surface portion of the prepared silicon substrate is oxidized by a thermal oxidation process, and a thermal oxide film is formed on the surface portion of the silicon substrate. The layer 30 may be formed on the gate electrode 20. By using the silicon substrate as the gate electrode in this way, the gate insulating layer 30 can be easily formed by a simple process of thermally oxidizing the silicon substrate.

Next, the organic semiconductor layer 40 is formed on the gate insulating layer 30. This step can be performed by any suitable method, but can be performed by a coating method using a coating solution in which the material is dissolved or dispersed in any suitable solvent. In preparing the coating liquid, a process such as filtration using a membrane filter may be performed as necessary.
The organic semiconductor layer 40 is formed by applying the obtained coating liquid on the gate insulating layer 30 and performing any suitable heat treatment corresponding to the material.

  In the method for producing the organic thin film transistor 10 of the present invention, when the layer constituting the organic thin film transistor 10 is formed by a coating method using a coating liquid, the coating process is performed in an atmosphere of about normal pressure or in an air atmosphere. Is done.

  Here, the “atmosphere” means an atmosphere that allows the inclusion of moisture and oxygen. The “atmosphere” specifically includes an unadjusted atmosphere at normal temperature and normal pressure, and further includes an atmosphere adjusted with respect to temperature, pressure, components, etc. while allowing the inclusion of moisture and oxygen. This “adjusted atmosphere” is a process for adjusting composition components such as nitrogen, hydrogen, oxygen, carbon dioxide and the like, and a process for adjusting their composition ratios, provided that the production method of the present invention including “coating” can be carried out. The environmental conditions such as temperature, humidity, and pressure may be adjusted on condition that the production method of the present invention including “coating” can be carried out. Includes an atmosphere that may be adjusted. In the present specification, the normal pressure is usually a pressure of 1013 hPa ± 100 hPa. The atmosphere at normal pressure includes an inert gas atmosphere such as nitrogen gas or argon gas as long as the pressure is normal pressure.

  As the coating method, spin coating method, casting method, micro gravure coating method, gravure coating method, bar coating method, roll coating method, wire bar coating method, dip coating method, spray coating method, screen printing method, flexographic printing method, Examples include an offset printing method and an inkjet printing method.

  When it is necessary to form an organic semiconductor layer in a predetermined pattern shape when forming a layer by the coating method, the organic semiconductor is formed into a predetermined pattern shape by coating the coating liquid into the predetermined pattern shape in the coating process. An organic semiconductor layer may be formed in a predetermined pattern shape by performing any suitable patterning process such as a photolithography process and a subsequent etching process after the layer is formed by coating on the entire surface. Also good.

  Next, first and second charge injection layers 50A and 50B containing an ionic polymer having charge injection characteristics are formed on the organic semiconductor layer 40. In this embodiment, the first charge injection layer 50A is formed to have a pattern similar to that of the first source / drain electrode 60A formed later. In the present embodiment, the second charge injection layer 50B is formed to have the same pattern as the second source / drain electrode 60B to be formed later. This step can be performed by a coating method using a coating solution in which a material is dissolved in any suitable solvent, as in the step of forming the organic semiconductor layer 40. When the charge injection layer 50 is an n-type electron injection layer, an ionic polymer having a conductivity type of n-type is selected as the material, and when the charge injection layer 50 is a p-type hole injection layer. An ionic polymer having a p-type conductivity is selected as a material to prepare a coating solution. The coating liquid is applied to the surface of the organic semiconductor layer 40, and any suitable heat treatment corresponding to the material is performed to form the charge injection layer 50.

  Next, a first source / drain electrode 60A having the same pattern shape as the first charge injection layer 50A is formed on the first charge injection layer 50A, and has the same pattern shape as the second charge injection layer 50B. A second source / drain electrode 60B is formed on the second charge injection layer 50B.

  In this step, it is preferable to form a conductive layer using a coating liquid prepared from metal fine particles having conductivity such as gold, silver, and aluminum and any suitable solvent. When metal fine particles are used as the conductive material, polar solvents such as water, methanol, ethanol, propanol, isopropyl alcohol (IPA), and dimethyl ketone can be preferably used.

  The formation of the first and second source / drain electrodes 60A and 60B by the coating method is performed by applying the prepared coating liquid. The coating liquid is preferably applied by a spin coating method, an ink jet method or the like. Then, the first and second source / drain electrodes 60A and 60B can be formed by heat-treating the formed coating film under any suitable condition corresponding to the material.

  As described above, according to the method of manufacturing the organic thin film transistor 10 of the present invention, the charge injection layer 50 is formed because an ionic polymer that is not easily oxidized even in an atmosphere at about normal pressure or even in an air atmosphere is used as the material for the charge injection layer. And the step of forming the first and second source / drain electrodes 60A and 60B are each performed as a step including a step of applying a coating liquid in an atmosphere of about normal pressure and further in an air atmosphere. be able to. Furthermore, the step of forming the organic semiconductor layer 40 can also be a step including a step of applying a coating liquid in an atmosphere of about normal pressure, and further in an air atmosphere.

<Second Embodiment>
(Organic thin film transistor)
With reference to FIG. 2, the structural example of the organic thin-film transistor of 2nd Embodiment is demonstrated. In addition, about the same layer as the layer demonstrated in 1st Embodiment, the same number may be attached | subjected and the description may be abbreviate | omitted.

  FIG. 2 is a cross-sectional view schematically showing a configuration example of the organic thin film transistor of the second embodiment. The organic thin film transistor 10 of the second embodiment is a configuration example of a top gate type organic thin film transistor.

  As shown in FIG. 2, the organic thin film transistor 10 of the second embodiment is provided on a substrate 70. The substrate 70 may be a rigid substrate such as a glass substrate, a flexible substrate such as a plastic substrate, and may be a film. By using a flexible substrate and a film, a flexible organic thin film transistor can be formed as a whole.

  On one surface of substrate 70 in thickness direction Z, first source / drain electrode 60A and second source / drain electrode 60B are provided. The first source / drain electrode 60A and the second source / drain electrode 60B are spaced apart from each other.

  A first charge injection layer 50A patterned in the same shape as the first source / drain electrode 60A is provided on the surface of the first source / drain electrode 60A. A second charge injection layer 50B patterned in the same shape as the second source / drain electrode 60B is provided on the surface of the second source / drain electrode 60B.

  The charge injection layer 50 is made of the ionic polymer already described. In the case of forming the charge injection layer 50 functioning as an electron injection layer, an n-type ionic polymer having electron injection characteristics may be used as a material. When the charge injection layer 50 that functions as a hole injection layer is formed, a p-type ionic polymer having hole injection characteristics may be used as a material.

  The charge injection layer 50 functions as an electron injection layer when the conductivity type is n-type, and functions as a hole injection layer when the conductivity type is p-type.

  An organic semiconductor layer 40 is provided on the substrate 70 so as to cover the first and second source / drain electrodes 60A and 60B and the charge injection layer 50 formed on these electrodes. The organic semiconductor layer 40 corresponds to an active layer.

  On the organic semiconductor layer 40, the gate insulating layer 30 and the gate electrode 20A are stacked in this order.

  The dimensions of the layers and electrodes constituting the organic thin film transistor of the second embodiment are the same as those of the organic thin film transistor of the first embodiment described above, for example. In this way, if the organic thin film transistor is configured as a top gate type, a silicon substrate becomes unnecessary. Therefore, since a flexible substrate can be used, a flexible organic thin film transistor can be obtained as a whole. In addition, since the substrate can be inexpensive, manufacturing cost can be reduced.

(Method for producing organic thin film transistor)
A method for manufacturing the organic thin film transistor of the second embodiment having the configuration shown in FIG. 2 will be described. In addition, when it is the same as the manufacturing process demonstrated in 1st Embodiment, the detailed description may be abbreviate | omitted.

  The manufacturing method of the organic thin film transistor 10 of the second embodiment includes a gate electrode, a first source / drain electrode, a second source / drain electrode, the first and second source / drain electrodes, and the gate. An organic semiconductor layer provided between the electrodes, and between the first and second source / drain electrodes and the organic semiconductor layer, are disposed in contact with the first and second source / drain electrodes. In the method for manufacturing an organic thin film transistor, in which the charge injection layer is formed, the method includes a step of forming a charge injection layer containing an ionic polymer having charge injection characteristics. That is, the organic thin film transistor manufacturing method includes a step of forming a gate electrode, a step of forming a first source / drain electrode, a step of forming a second source / drain electrode, and the first and second sources. Between the first and second source / drain electrodes and the organic semiconductor layer, the step of forming the organic semiconductor layer provided between the / drain electrode and the gate electrode, and the first and second source / drain electrodes and the organic semiconductor layer. Forming a charge injection layer disposed in contact with the source / drain electrodes. In addition, the order of each process is suitably set according to the structure of an organic thin-film transistor. In this embodiment, the first and second source / drain electrodes are formed, the charge injection layer is formed, the organic semiconductor layer is formed, and the gate electrode is formed in this order.

  First, the substrate 70 is prepared, and the first and second source / drain electrodes 60 </ b> A and 60 </ b> B are formed on the substrate 70. This step is a step of forming a conductive layer or a conductive electrode pattern using a coating liquid prepared from conductive metal fine particles such as gold, silver, and aluminum and any suitable solvent. Is preferred. When metal fine particles are used as the conductive material, polar solvents such as water, methanol, ethanol, propanol, isopropyl alcohol (IPA), and dimethyl ketone can be preferably used. The coating liquid is preferably applied by a spin coating method, an ink jet method or the like.

  Next, the first charge injection layer 50A is formed on the surface of the first source / drain electrode 60A, and the second charge injection layer 50B is formed on the surface of the second source / drain electrode 60B. These first and second charge injection layers 50A and 50B contain an ionic polymer having charge injection characteristics. This step can be performed by a coating method using a coating solution as already described. In the case of forming the charge injection layer 50 that functions as an electron injection layer, an ionic polymer having a conductivity type of n type is selected as the material, and the charge injection layer 50 that functions as a hole injection layer is formed. Prepares a coating solution by selecting an ionic polymer of p-type conductivity as the material.

  The prepared coating liquid is applied onto the surfaces of the formed first and second source / drain electrodes 60A and 60B, and an appropriate heat treatment corresponding to the material is performed to form the charge injection layer 50. Is done.

  Next, the organic semiconductor layer 40 is formed on the substrate 70 so as to cover the first and second source / drain electrodes 60 </ b> A and 60 </ b> B exposed from the charge injection layer 50 and the charge injection layer 50. This step can be performed by subjecting a coating film formed by a coating method using a coating solution to any suitable heat treatment depending on the material.

  Next, the gate insulating layer 30 is formed on the organic semiconductor layer 40, and the gate electrode 20 </ b> A is further formed on the gate insulating layer 30. The gate insulating layer 30 can be formed by a CVD method (chemical vapor deposition method) or the like using an insulating material as described above. Further, the formation process of the gate electrode 20A is prepared with metal fine particles having conductivity such as gold, silver, and aluminum and any suitable solvent in the same manner as the formation process of the first and second source / drain electrodes 60A and 60B. It can be set as the process of forming a conductive layer using the coating liquid. The gate electrode 20 </ b> A is formed by a coating method by applying a coating solution to the gate insulating layer 30. The gate electrode 20A can be formed by heat-treating the formed coating film.

  According to the method for manufacturing the organic thin film transistor 10 of the present invention, since an ionic polymer that is not easily oxidized even in an atmosphere at about atmospheric pressure, or even in an air atmosphere, is used as a material for the charge injection layer, Each of the step of forming the gate electrode 20A and the step of forming the first source / drain electrode 60A and the second source / drain electrode 60B is performed by applying a coating liquid in an atmosphere of about normal pressure, and further in an air atmosphere. It can implement as a process including the process to perform. Furthermore, the step of forming the organic semiconductor layer 40 can also be a step including a step of applying a coating liquid in an air atmosphere.

  The organic thin film transistor 10 according to the first embodiment and the second embodiment can be configured as an n-type organic thin film transistor or a p-type organic thin film transistor by appropriately selecting the conductivity type of each layer.

  In addition, the organic thin film transistor 10 of the present invention can also constitute a complementary organic thin film transistor by combining an n-type organic thin film transistor and a p-type organic thin film transistor.

  When the complementary organic thin film transistor is configured in the configuration example of the first embodiment, the conductivity type of the material constituting the organic semiconductor layer and the charge injection layer is selected, and the n type organic thin film transistor, the p type organic thin film transistor, Can be formed on a single substrate 20 to form a complementary organic thin film transistor.

  When the complementary organic thin film transistor is configured in the configuration example of the second embodiment, the conductivity type of the material forming the organic semiconductor layer and the charge injection layer is selected, and the n type organic thin film transistor, the p type organic thin film transistor, Can be formed on a single substrate 70 to form a complementary organic thin film transistor.

  If a complementary organic thin film transistor is constructed, various logic circuits can be constructed. A logic circuit composed of complementary organic thin film transistors can be suitably used for an electronic tag such as an RF (Radio Frequency) tag.

The organic thin film transistor of the present invention is, for example, an organic thin film transistor substrate in which a plurality of organic thin film transistors are formed on a base material and a circuit capable of carrying a predetermined electrical function is formed by combining the plurality of organic thin film transistors. Can do.
When configured as an organic thin film transistor substrate, it can be suitably used as a drive substrate for display devices such as liquid crystal display devices and organic electroluminescence display devices.

  Hereinafter, although the present invention will be described more specifically based on experimental examples and the like, the present invention is not limited to the following experimental examples and the like.

The weight average molecular weight (Mw) and the number average molecular weight (Mn) of the polymer are determined by using gel permeation chromatography (GPC) (manufactured by Tosoh Corporation: HLC-8220GPC). As sought. The sample to be measured was dissolved in tetrahydrofuran to a concentration of about 0.5% by weight, and 50 μL was injected into GPC. Further, tetrahydrofuran was used as the mobile phase of GPC, and was allowed to flow at a flow rate of 0.5 mL / min. The structural analysis of the polymer was performed by ¹ H-NMR analysis using a 300 MHz NMR spectrometer manufactured by Varian. In addition, the measurement was performed by dissolving the sample in a soluble heavy solvent (a solvent in which a hydrogen atom in a solvent molecule was substituted with a deuterium atom) so as to have a concentration of 20 mg / mL. The orbital energy of the highest occupied molecular orbital (HOMO) of the polymer was determined by measuring the ionization potential of the polymer and using the obtained ionization potential as the orbital energy. On the other hand, the orbital energy of the lowest unoccupied molecular orbital (LUMO) of the polymer was obtained by calculating the energy difference between HOMO and LUMO and using the sum of the value and the ionization potential measured above as the orbital energy. . A photoelectron spectrometer (manufactured by Riken Keiki Co., Ltd .: AC-2) was used to measure the ionization potential. The energy difference between HOMO and LUMO was determined from the absorption terminal of the polymer by measuring the absorption spectrum of the polymer using an ultraviolet / visible / near infrared spectrophotometer (Varian: Cary 5E).

[Reference Example 1]
Synthesis of 2,7-dibromo-9,9-bis [3-ethoxycarbonyl-4- [2- [2- (2-methoxyethoxy) ethoxy] ethoxy] phenyl] -fluorene (Compound A) 2,7-dibromo -9-Fluorenone (52.5 g), ethyl salicylate (154.8 g), and mercaptoacetic acid (1.4 g) were placed in a 300 mL flask, and the atmosphere in the flask was replaced with nitrogen (hereinafter, “the atmosphere in the flask is nitrogen. "Substituted" may be simply referred to as "nitrogen substituted"). Thereto was added methanesulfonic acid (630 mL) and the mixture was stirred at 75 ° C. overnight. The mixture was allowed to cool, added to ice water and stirred for 1 hour. The resulting solid was filtered off and washed with heated acetonitrile. The washed solid was dissolved in acetone, and the solid was recrystallized from the obtained acetone solution and filtered. The resulting solid (62.7 g), 2- [2- (2-methoxyethoxy) ethoxy] -p-toluenesulfonate (86.3 g), potassium carbonate (62.6 g), and 18-crown-6 (7 2 g) was dissolved in N, N-dimethylformamide (DMF) (670 mL) and the solution was transferred to a flask and stirred at 105 ° C. overnight. The obtained mixture was allowed to cool to room temperature, ice water was added to the flask, and the mixture was stirred for 1 hour. Chloroform (300 mL) was added to the reaction solution, liquid separation extraction was performed, and the solution was concentrated, whereby 2,7-dibromo-9,9-bis [3-ethoxycarbonyl-4- [2- [2- (2 -Methoxyethoxy) ethoxy] ethoxy] phenyl] -fluorene (Compound A) (51.2 g) was obtained.

[Reference Example 2]
2,7-bis (4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl) -9,9-bis [3-ethoxycarbonyl-4- [2- [2- ( Synthesis of 2-methoxyethoxy) ethoxy] ethoxy] phenyl] -fluorene (Compound B) Compound A (15 g), bis (pinacolato) diboron (8.9 g), [1,1′-bis (diphenylphos) under nitrogen atmosphere Fino) ferrocene] dichloropalladium (II) dichloromethane complex (0.8 g), 1,1′-bis (diphenylphosphino) ferrocene (0.
5 g), potassium acetate (9.4 g), and dioxane (400 mL) were mixed, heated to 110 ° C., and heated to reflux for 10 hours. The reaction liquid was filtered after standing_to_cool and the filtrate was concentrate | evaporated under reduced pressure. The reaction mixture was washed 3 times with methanol. The precipitate was dissolved in toluene, and activated carbon was added to the solution and stirred. Then, filtration is performed and the filtrate is concentrated under reduced pressure to give 2,7-bis (4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl) -9,9-bis. [3-Ethoxycarbonyl-4- [2- [2- (2-methoxyethoxy) ethoxy] ethoxy] phenyl] -fluorene (Compound B) (11.7 g) was obtained.

[Reference Example 3]
Synthesis of poly [9,9-bis [3-ethoxycarbonyl-4- [2- [2- (2-methoxyethoxy) ethoxy] ethoxy] phenyl] -fluorene] (Polymer A) Compound A under an inert atmosphere (0.55 g), Compound B (0.61 g), triphenylphosphine palladium (0.01 g), methyl trioctyl ammonium chloride (manufactured by Aldrich, trade name Aliquat 336 (registered trademark)) (0.20 g), and toluene ( 10 mL) and heated to 105 ° C. To this reaction solution, 2M aqueous sodium carbonate solution (6 mL) was added dropwise and refluxed for 8 hours. 4-t-butylphenylboronic acid (0.01 g) was added to the reaction solution, and the mixture was refluxed for 6 hours. Then, a sodium diethyldithiacarbamate aqueous solution (10 mL, concentration: 0.05 g / mL) was added, and the mixture was stirred for 2 hours. The mixed solution was dropped into 300 mL of methanol and stirred for 1 hour, and then the deposited precipitate was filtered, dried under reduced pressure for 2 hours, and dissolved in 20 mL of tetrahydrofuran. The obtained solution was dropped into a mixed solvent of 120 ml of methanol and 50 ml of 3% by weight acetic acid aqueous solution and stirred for 1 hour, and then the deposited precipitate was filtered and dissolved in 20 ml of tetrahydrofuran. The solution thus obtained was dropped into 200 ml of methanol and stirred for 30 minutes, and then the deposited precipitate was filtered to obtain a solid. The obtained solid was dissolved in tetrahydrofuran and purified by passing through an alumina column and a silica gel column. The tetrahydrofuran solution collected from the column was concentrated and then added dropwise to methanol (200 mL), and the precipitated solid was filtered and dried. The yield of the obtained poly [9,9-bis [3-ethoxycarbonyl-4-bis [2- [2- (2-methoxyethoxy) ethoxy] ethoxy] phenyl] -fluorene] (polymer A) was 520 mg. there were.
The number average molecular weight in terms of polystyrene of the polymer A was 5.2 × 10 ⁴ . The polymer A consists of a structural unit represented by the formula (A).

[Experimental Example 1]
Synthesis of Polymer A Cesium Salt Polymer A (200 mg) was placed in a 100 mL flask and purged with nitrogen. Tetrahydrofuran (20 mL) and ethanol (20 mL) were added and the mixture was warmed to 55 ° C. Thereto was added an aqueous solution in which cesium hydroxide (200 mg) was dissolved in water (2 mL), and the mixture was stirred at 55 ° C. for 6 hours. After the mixture was cooled to room temperature, the reaction solvent was distilled off under reduced pressure. The resulting solid was washed with water and dried under reduced pressure to obtain a pale yellow solid (150 mg). From the NMR spectrum, it was confirmed that the signal derived from the ethyl group at the ethyl ester site in the polymer A completely disappeared. The obtained cesium salt of polymer A is referred to as conjugated polymer compound 1. Conjugated polymer compound 1 is composed of a structural unit represented by formula (B) ("selected from the group consisting of a group represented by formula (1) and a group represented by formula (2) in all structural units). The ratio of structural units containing one or more groups and one or more groups represented by formula (3) "and" the formulas (13), (15), (17), ( The ratio of the structural unit represented by 20) "is 100 mol%.) The conjugated polymer compound 1 had an orbital energy of HOMO of −5.5 eV and an orbital energy of LUMO of −2.7 eV.

[Experiment 2]
Synthesis of Polymer A Potassium Salt Polymer A (200 mg) was placed in a 100 mL flask and purged with nitrogen. Tetrahydrofuran (20 mL) and methanol (10 mL) were mixed, an aqueous solution in which potassium hydroxide (400 mg) was dissolved in water (2 mL) was added to the mixed solution, and the mixture was stirred at 65 ° C. for 1 hour. 50 mL of methanol was added to the reaction solution, and the mixture was further stirred at 65 ° C. for 4 hours. After the mixture was cooled to room temperature, the reaction solvent was distilled off under reduced pressure. The resulting solid was washed with water and dried under reduced pressure to obtain a pale yellow solid (131 mg). From the NMR spectrum, it was confirmed that the signal derived from the ethyl group at the ethyl ester site in the polymer A completely disappeared. The obtained potassium salt of polymer A is referred to as conjugated polymer compound 2. Conjugated polymer compound 2 is composed of a structural unit represented by formula (C) ("selected from the group consisting of a group represented by formula (1) and a group represented by formula (2) in all structural units). The ratio of structural units containing one or more groups and one or more groups represented by formula (3) "and" the formulas (13), (15), (17), ( The ratio of the structural unit represented by 20) "is 100 mol%.) The conjugated polymer compound 2 had an orbital energy of HOMO of −5.5 eV and an orbital energy of LUMO of −2.7 eV.

[Experiment 3]
Synthesis of Polymer A Sodium Salt Polymer A (200 mg) was placed in a 100 mL flask and purged with nitrogen. Tetrahydrofuran (20 mL) and methanol (10 mL) were mixed, an aqueous solution in which sodium hydroxide (260 mg) was dissolved in water (2 mL) was added to the mixed solution, and the mixture was stirred at 65 ° C. for 1 hour. 30 mL of methanol was added to the reaction solution, and the mixture was further stirred at 65 ° C. for 4 hours. After the mixture was cooled to room temperature, the reaction solvent was distilled off under reduced pressure. The resulting solid was washed with water and dried under reduced pressure to obtain a pale yellow solid (123 mg). From the NMR spectrum, it was confirmed that the signal derived from the ethyl group at the ethyl ester site in the polymer A completely disappeared. The resulting sodium salt of polymer A is referred to as conjugated polymer compound 3. The conjugated polymer compound 3 is composed of a structural unit represented by the formula (D) (“selected from the group consisting of a group represented by the formula (1) and a group represented by the formula (2) in all structural units). The ratio of structural units containing one or more groups and one or more groups represented by formula (3) "and" the formulas (13), (15), (17), ( The ratio of the structural unit represented by 20) "is 100 mol%.) The conjugated polymer compound 3 had a HOMO orbital energy of −5.6 eV and a LUMO orbital energy of −2.8 eV.

[Experimental Example 4]
Synthesis of Polymer A Ammonium Salt Polymer A (200 mg) was placed in a 100 mL flask and purged with nitrogen. Tetrahydrofuran (20 mL) and methanol (15 mL) were mixed, an aqueous solution in which tetramethylammonium hydroxide (50 mg) was dissolved in water (1 mL) was added to the mixed solution, and the mixture was stirred at 65 ° C. for 6 hours. An aqueous solution in which tetramethylammonium hydroxide (50 mg) was dissolved in water (1 mL) was added to the reaction solution, and the mixture was further stirred at 65 ° C. for 4 hours. After the mixture was cooled to room temperature, the reaction solvent was distilled off under reduced pressure. The resulting solid was washed with water and dried under reduced pressure to obtain a pale yellow solid (150 mg). From the NMR spectrum, it was confirmed that 90% of the signal derived from the ethyl group at the ethyl ester site in the polymer A disappeared. The resulting ammonium salt of polymer A is referred to as conjugated polymer compound 4. The conjugated polymer compound 4 is composed of a structural unit represented by the formula (E) (“selected from the group consisting of a group represented by the formula (1) and a group represented by the formula (2) in all structural units). The ratio of structural units containing one or more groups and one or more groups represented by formula (3) "and" the formulas (13), (15), (17), ( The ratio of the structural unit represented by 20) "is 90 mol%.) The conjugated polymer compound 4 had a HOMO orbital energy of −5.6 eV and a LUMO orbital energy of −2.8 eV.

[Reference Example 4]
2,7-bis [7- (4-methylphenyl) -9,9-dioctylfluoren-2-yl] -9,9-bis [3-ethoxycarbonyl-4- [2- [2- (2-methoxy) Synthesis of ethoxy) ethoxy] ethoxy] phenyl] -fluorene (Polymer B) Compound A (0.52 g), 2,7-bis (1,3,2-dioxaborolan-2-yl) -9 under inert atmosphere , 9-dioctylfluorene (1.29 g), triphenylphosphine palladium (0.0087 g), methyltrioctylammonium chloride (manufactured by Aldrich, trade name Aliquat 336 (registered trademark)) (0.20 g), toluene (10 mL), and 2M aqueous sodium carbonate solution (10 mL) was mixed and heated to 80 ° C. The reaction was allowed to react for 3.5 hours. Thereafter, parabromotoluene (0.68 g) was added thereto, and the mixture was further reacted for 2.5 hours. After the reaction, the reaction solution was cooled to room temperature, 50 mL of ethyl acetate / 50 mL of distilled water was added, and the aqueous layer was removed. Distilled water (50 mL) was added again to remove the aqueous layer, magnesium sulfate was added as a desiccant, and the insoluble matter was filtered to remove the organic solvent. Thereafter, the obtained residue was dissolved again in 10 mL of THF, 2 mL of saturated aqueous sodium diethyldithiocarbamate was added and stirred for 30 minutes, and then the organic solvent was removed. Purification was performed through an alumina column (developing solvent hexane: ethyl acetate = 1: 1, v / v), and the deposited precipitate was filtrated and dried under reduced pressure for 12 hours. As a result, 2,7-bis [7- (4-methyl Phenyl) -9,9-dioctylfluoren-2-yl] -9,9-bis [3-ethoxycarbonyl-4- [2- [2- (2-methoxyethoxy) ethoxy] ethoxy] phenyl] -fluorene (heavy 524 mg of union B) was obtained.
The number average molecular weight in terms of polystyrene of the polymer B was 2.0 × 10 ³ . The polymer B is represented by the formula (F).

[Experimental Example 5]
Synthesis of Polymer B Cesium Salt Polymer B (262 mg) was placed in a 100 mL flask and purged with argon. Tetrahydrofuran (10 mL) and methanol (15 mL) were added thereto, and the mixture was heated to 55 ° C. Thereto was added an aqueous solution in which cesium hydroxide (341 mg) was dissolved in water (1 mL), and the mixture was stirred at 55 ° C. for 5 hours. After the resulting mixture was cooled to room temperature, the reaction solvent was distilled off under reduced pressure. The resulting solid was washed with water and dried under reduced pressure to obtain a pale yellow solid (250 mg). From the NMR spectrum, it was confirmed that the signal derived from the ethyl group at the ethyl ester site had completely disappeared. The obtained polymer B cesium salt is referred to as a conjugated polymer compound 5. The conjugated polymer compound 5 is represented by the formula (G) (“one type selected from the group consisting of the group represented by the formula (1) and the group represented by the formula (2) in all structural units). "Ratio of structural units containing the above groups and one or more groups represented by formula (3)" and "in formulas (13), (15), (17), (20) in all structural units" The “ratio of structural units represented” is 33.3 mol% rounded off to the second decimal place.) The conjugated polymer compound 5 had a HOMO orbital energy of −5.6 eV and a LUMO orbital energy of −2.6 eV.

[Reference Example 5]
Synthesis of Polymer C In an inert atmosphere, Compound A (0.40 g), Compound B (0.49 g), N, N′-bis (4-bromophenyl) -N, N′-bis (4-t- Butyl-2,6-dimethylphenyl) 1,4-phenylenediamine (35 mg), triphenylphosphine palladium (8 mg), methyl trioctyl ammonium chloride (manufactured by Aldrich, trade name Aliquat 336 (registered trademark)) (0.20 g), And toluene (10 mL) were mixed and heated to 105 ° C. To this reaction solution, 2M aqueous sodium carbonate solution (6 mL) was added dropwise and refluxed for 8 hours. Phenylboronic acid (0.01 g) was added to the reaction solution and refluxed for 6 hours. Then, a sodium diethyldithiacarbamate aqueous solution (10 mL, concentration: 0.05 g / mL) was added, and the mixture was stirred for 2 hours. The mixed solution was dropped into 300 mL of methanol and stirred for 1 hour, and then the deposited precipitate was filtered, dried under reduced pressure for 2 hours, and dissolved in 20 mL of tetrahydrofuran. The obtained solution was dropped into a mixed solvent of 120 mL of methanol and 50 mL of a 3% by weight acetic acid aqueous solution and stirred for 1 hour, and then the deposited precipitate was filtered and dissolved in 20 mL of tetrahydrofuran. The solution thus obtained was dropped into 200 mL of methanol and stirred for 30 minutes, and then the deposited precipitate was filtered to obtain a solid. The obtained solid was dissolved in tetrahydrofuran and purified by passing through an alumina column and a silica gel column. The tetrahydrofuran solution collected from the column was concentrated and then added dropwise to methanol (200 mL), and the precipitated solid was filtered and dried. The yield of the obtained polymer C was 526 mg.
The number average molecular weight in terms of polystyrene of the polymer C was 3.6 × 10 ⁴ . The polymer C consists of a structural unit represented by the formula (H).
N, N′-bis (4-bromophenyl) -N, N′-bis (4-t-butyl-2,6-dimethylphenyl) 1,4-phenylenediamine is disclosed in, for example, JP-A-2008-74017. It can be synthesized by the method described in the publication.

[Experimental Example 6]
Synthesis of Polymer C Cesium Salt Polymer C (200 mg) was placed in a 100 mL flask and purged with nitrogen. Tetrahydrofuran (20 mL) and methanol (20 mL) were added and mixed. An aqueous solution in which cesium hydroxide (200 mg) was dissolved in water (2 mL) was added to the mixed solution, and the mixture was stirred at 65 ° C. for 1 hour. 30 mL of methanol was added to the reaction solution, and the mixture was further stirred at 65 ° C. for 4 hours. After the mixture was cooled to room temperature, the reaction solvent was distilled off under reduced pressure. The resulting solid was washed with water and dried under reduced pressure to obtain a pale yellow solid (150 mg). From the NMR spectrum, it was confirmed that the signal derived from the ethyl group at the ethyl ester site in the polymer C had completely disappeared. The obtained cesium salt of polymer C is referred to as conjugated polymer compound 6. Conjugated polymer compound 6 is composed of a structural unit represented by formula (I) (“selected from the group consisting of a group represented by formula (1) and a group represented by formula (2) in all structural units). The ratio of structural units containing one or more groups and one or more groups represented by formula (3) "and" the formulas (13), (15), (17), ( The ratio of the structural unit represented by 20) "is 95 mol%.) The conjugated polymer compound 6 had a HOMO orbital energy of −5.3 eV and a LUMO orbital energy of −2.6 eV.

[Reference Example 6]
Synthesis of Polymer D Compound A (0.55 g), Compound B (0.67 g), N, N′-bis (4-bromophenyl) -N, N′-bis (4-t-) under an inert atmosphere Butyl-2,6-dimethylphenyl) 1,4-phenylenediamine (0.038 g), 3,7-dibromo-N- (4-n-butylphenyl) phenoxazine 0.009 g, triphenylphosphine palladium (0. 01 g), methyl trioctyl ammonium chloride (manufactured by Aldrich, trade name Aliquat 336 (registered trademark)) (0.20 g), and toluene (10 mL) were mixed and heated to 105 ° C. To this reaction solution, 2M aqueous sodium carbonate solution (6 mL) was added dropwise and refluxed for 2 hours. Phenylboronic acid (0.004 g) was added to the reaction solution and refluxed for 6 hours. Then, a sodium diethyldithiacarbamate aqueous solution (10 mL, concentration: 0.05 g / mL) was added, and the mixture was stirred for 2 hours. The mixed solution was dropped into 300 mL of methanol and stirred for 1 hour, and then the deposited precipitate was filtered, dried under reduced pressure for 2 hours, and dissolved in 20 mL of tetrahydrofuran. The obtained solution was dropped into a mixed solvent of 120 mL of methanol and 50 mL of a 3% by weight acetic acid aqueous solution and stirred for 1 hour, and then the deposited precipitate was filtered and dissolved in 20 mL of tetrahydrofuran. The solution thus obtained was dropped into 200 mL of methanol and stirred for 30 minutes, and then the deposited precipitate was filtered to obtain a solid. The obtained solid was dissolved in tetrahydrofuran and purified by passing through an alumina column and a silica gel column. The tetrahydrofuran solution collected from the column was concentrated and then added dropwise to methanol (200 mL), and the precipitated solid was filtered and dried. The yield of the obtained polymer D was 590 mg.
The number average molecular weight in terms of polystyrene of the polymer D was 2.7 × 10 ⁴ . The polymer D consists of a structural unit represented by the formula (J).
3,7-Dibromo-N- (4-n-butylphenyl) phenoxazine was synthesized by the method described in JP-A-2004-137456.

[Experimental Example 7]
Synthesis of Polymer D Cesium Salt Polymer D (200 mg) was placed in a 100 mL flask and purged with nitrogen. Tetrahydrofuran (15 mL) and methanol (10 mL) were mixed. An aqueous solution in which cesium hydroxide (360 mg) was dissolved in water (2 mL) was added to the mixed solution, and the mixture was stirred at 65 ° C. for 3 hours. 10 mL of methanol was added to the reaction solution, and the mixture was further stirred at 65 ° C. for 4 hours. After the mixture was cooled to room temperature, the reaction solvent was distilled off under reduced pressure. The resulting solid was washed with water and dried under reduced pressure to obtain a pale yellow solid (210 mg). From the NMR spectrum, it was confirmed that the signal derived from the ethyl group at the ethyl ester site in the polymer D had completely disappeared. The resulting cesium salt of polymer D is referred to as conjugated polymer compound 7. Conjugated polymer compound 7 is composed of a structural unit represented by formula (K) ("selected from the group consisting of a group represented by formula (1) and a group represented by formula (2) in all structural units). The ratio of structural units containing one or more groups and one or more groups represented by formula (3) "and" the formulas (13), (15), (17), ( The ratio of the structural unit represented by 20) "is 90 mol%.) The conjugated polymer compound 7 had a HOMO orbital energy of −5.3 eV and a LUMO orbital energy of −2.4 eV.

[Reference Example 7]
Synthesis of polymer E Under an inert atmosphere, compound A (0.37 g), compound B (0.82 g), 1,3-dibromobenzene (0.09 g), triphenylphosphine palladium (0.01 g), methyltri Octyl ammonium chloride (manufactured by Aldrich, trade name Aliquat 336 (registered trademark)) (0.20 g) and toluene (10 mL) were mixed and heated to 105 ° C. To this reaction solution, 2M aqueous sodium carbonate solution (6 mL) was added dropwise and refluxed for 7 hours. Phenylboronic acid (0.002 g) was added to the reaction solution and refluxed for 10 hours. Next, an aqueous solution of sodium diethyldithiacarbamate (10 mL, concentration: 0.05 g / mL) was added and stirred for 1 hour. The mixed solution was dropped into 300 mL of methanol and stirred for 1 hour, and then the deposited precipitate was filtered, dried under reduced pressure for 2 hours, and dissolved in 20 mL of tetrahydrofuran. The obtained solution was dropped into a mixed solvent of 120 mL of methanol and 50 mL of a 3% by weight acetic acid aqueous solution and stirred for 1 hour, and then the deposited precipitate was filtered and dissolved in 20 mL of tetrahydrofuran. The solution thus obtained was dropped into 200 mL of methanol and stirred for 30 minutes, and then the deposited precipitate was filtered to obtain a solid. The obtained solid was dissolved in tetrahydrofuran and purified by passing through an alumina column and a silica gel column. The tetrahydrofuran solution collected from the column was concentrated and then added dropwise to methanol (200 mL), and the precipitated solid was filtered and dried. The yield of the obtained polymer E was 293 mg.
The number average molecular weight in terms of polystyrene of the polymer E was 1.8 × 10 ⁴ . The polymer E consists of a structural unit represented by the formula (L).

[Experimental Example 8]
Synthesis of Polymer E Cesium Salt Polymer E (200 mg) was placed in a 100 mL flask and purged with nitrogen. Tetrahydrofuran (10 mL) and methanol (5 mL) were mixed. An aqueous solution in which cesium hydroxide (200 mg) was dissolved in water (2 mL) was added to the mixed solution, and the mixture was stirred at 65 ° C. for 2 hours. 10 mL of methanol was added to the reaction solution, and the mixture was further stirred at 65 ° C. for 5 hours. After the mixture was cooled to room temperature, the reaction solvent was distilled off under reduced pressure. The resulting solid was washed with water and dried under reduced pressure to obtain a pale yellow solid (170 mg). From the NMR spectrum, it was confirmed that the signal derived from the ethyl group at the ethyl ester site in the polymer E completely disappeared. The resulting cesium salt of polymer E is referred to as conjugated polymer compound 8. The conjugated polymer compound 8 is composed of a structural unit represented by the formula (M) (“selected from the group consisting of a group represented by the formula (1) and a group represented by the formula (2) in all structural units). The ratio of structural units containing one or more groups and one or more groups represented by formula (3) "and" the formulas (13), (15), (17), ( The ratio of the structural unit represented by 20) "is 75 mol%.) The conjugated polymer compound 8 had a HOMO orbital energy of −5.6 eV and a LUMO orbital energy of −2.6 eV.

[Reference Example 8]
Synthesis of polymer F Under an inert atmosphere, compound B (1.01 g), 1,4-dibromo-2,3,5,6-tetrafluorobenzene (0.30 g), triphenylphosphine palladium (0.02 g) , Methyltrioctylammonium chloride (manufactured by Aldrich, trade name Aliquat 336 (registered trademark)) (0.20 g), and toluene (10 mL) were mixed and heated to 105 ° C. To this reaction solution, 2M aqueous sodium carbonate solution (6 mL) was added dropwise and refluxed for 4 hours. Phenylboronic acid (0.002 g) was added to the reaction solution and refluxed for 4 hours. Next, an aqueous solution of sodium diethyldithiacarbamate (10 mL, concentration: 0.05 g / mL) was added and stirred for 1 hour. The mixed solution was dropped into 300 mL of methanol and stirred for 1 hour, and then the deposited precipitate was filtered, dried under reduced pressure for 2 hours, and dissolved in 20 mL of tetrahydrofuran. The obtained solution was dropped into a mixed solvent of 120 mL of methanol and 50 mL of a 3% by weight acetic acid aqueous solution and stirred for 1 hour, and then the deposited precipitate was filtered and dissolved in 20 mL of tetrahydrofuran. The solution thus obtained was dropped into 200 mL of methanol and stirred for 30 minutes, and then the deposited precipitate was filtered to obtain a solid. The obtained solid was dissolved in a mixed solvent of tetrahydrofuran / ethyl acetate (1/1 (volume ratio)) and purified by passing through an alumina column and a silica gel column. The tetrahydrofuran solution collected from the column was concentrated and then added dropwise to methanol (200 mL), and the precipitated solid was filtered and dried. The yield of the obtained polymer E was 343 mg.
The polystyrene equivalent number average molecular weight of the polymer F was 6.0 × 10 ⁴ . The polymer F consists of a structural unit represented by the formula (N).

[Experimental Example 9]
Synthesis of Polymer F Cesium Salt Polymer F (150 mg) was placed in a 100 mL flask and purged with nitrogen. Tetrahydrofuran (10 mL) and methanol (5 mL) were mixed. An aqueous solution in which cesium hydroxide (260 mg) was dissolved in water (2 mL) was added to the mixed solution, and the mixture was stirred at 65 ° C. for 2 hours. 10 mL of methanol was added to the reaction solution, and the mixture was further stirred at 65 ° C. for 5 hours. After the mixture was cooled to room temperature, the reaction solvent was distilled off under reduced pressure. The resulting solid was washed with water and dried under reduced pressure to obtain a pale yellow solid (130 mg). From the NMR spectrum, it was confirmed that the signal derived from the ethyl group at the ethyl ester site in the polymer E completely disappeared. The resulting cesium salt of polymer F is referred to as conjugated polymer compound 9. The conjugated polymer compound 9 is composed of a structural unit represented by the formula (O) (“selected from the group consisting of a group represented by the formula (1) and a group represented by the formula (2) in all structural units). The ratio of structural units containing one or more groups and one or more groups represented by formula (3) "and" the formulas (13), (15), (17), ( The ratio of the structural unit represented by 20) "is 75 mol%.) The conjugated polymer compound 9 had a HOMO orbital energy of −5.9 eV and a LUMO orbital energy of −2.8 eV.

[Reference Example 9]
Under an inert atmosphere, 2- [2- (2-methoxyethoxy) ethoxy] -p-toluenesulfonate (11.0 g), triethylene glycol (30.0 g), potassium hydroxide (3.3 g) were mixed, The mixture was stirred with heating at 100 ° C. for 18 hours. After allowing to cool, the reaction solution was added to water (100 mL), liquid separation extraction was performed with chloroform, and the solution was concentrated. The concentrated solution was subjected to Kugelrohr distillation (10 mm Torr, 180 ° C.) to give 2- (2- (2- (2- (2- (2-methoxyethoxy) -ethoxy) -ethoxy) -ethoxy) -ethoxy). Ethanol (6.1 g) was obtained.

[Reference Example 10]
Under an inert atmosphere, 2- (2- (2- (2- (2- (2-methoxyethoxy) -ethoxy) -ethoxy) -ethoxy) -ethoxy) ethanol (8.0 g), sodium hydroxide (1. 4 g), distilled water (2 mL) and tetrahydrofuran (2 mL) were mixed and ice-cooled. To the mixed solution, a tetrahydrofuran (6.4 mL) solution of p-tosyl chloride (5.5 g) was added dropwise over 30 minutes, and after the addition, the reaction solution was raised to room temperature and stirred for 15 hours. Distilled water (50 mL) was added to the reaction solution, and the reaction solution was neutralized with 6M sulfuric acid, followed by liquid separation extraction with chloroform. The solution was concentrated to give 2- (2- (2- (2- (2- (2-methoxyethoxy) -ethoxy) -ethoxy) -ethoxy) -ethoxy) p-toluenesulfonate (11.8 g). It was.

[Reference Example 11]
2,7-dibromo-9,9-bis [3-ethoxycarbonyl-4- [2- (2- (2- (2- (2- (2-methoxyethoxy) -ethoxy) -ethoxy) -ethoxy)- Synthesis of Ethoxy) Ethoxy] phenyl] -fluorene (Compound C) 2,7-Dibromo-9-fluorenone (127.2 g), ethyl salicylate (375.2 g), and mercaptoacetic acid (3.5 g) are placed in a 300 mL flask. And replaced with nitrogen. Thereto was added methanesulfonic acid (1420 mL) and the mixture was stirred at 75 ° C. overnight. The mixture was allowed to cool, added to ice water and stirred for 1 hour. The resulting solid was filtered off and washed with heated acetonitrile. The washed solid was dissolved in acetone, and the solid was recrystallized from the obtained acetone solution and filtered to obtain a solid (167.8 g). The resulting solid (5 g), 2- (2- (2- (2- (2- (2-methoxyethoxy) -ethoxy) -ethoxy) -ethoxy) -ethoxy) p-toluenesulfonate (10.4 g), Potassium carbonate (5.3 g) and 18-crown-6 (0.6 g) were dissolved in N, N-dimethylformamide (DMF) (100 mL), and the solution was transferred to a flask and stirred at 105 ° C. for 4 hours. The obtained mixture was allowed to cool to room temperature, added to ice water, and stirred for 1 hour. Chloroform (300 mL) was added to the reaction solution, liquid separation extraction was performed, and the solution was concentrated. The concentrate was dissolved in ethyl acetate, passed through an alumina column, and the solution was concentrated to give 2,7-dibromo-9,9-bis [3-ethoxycarbonyl-4- [2- (2- (2- ( 2- (2- (2- (2- (2-methoxyethoxy) -ethoxy) -ethoxy) -ethoxy) -ethoxy) ethoxy] phenyl] -fluorene (compound C) (4.5 g) was obtained.

[Reference Example 12]
Synthesis of Polymer G In an inert atmosphere, 200 mL of Compound C (1.0 g), 4-tert-butylphenyl bromide (0.9 mg), 2,2′-bipyridine (0.3 g), and dehydrated tetrahydrofuran (50 mL) Mix in flask. After heating the mixture to 55 ° C., bis (1,5-cyclooctadiene) nickel (0.6 g) was added, and the mixture was stirred at 55 ° C. for 5 hours. After the mixture was cooled to room temperature, the reaction solution was added dropwise to a mixture of methanol (200 mL) and 1N dilute hydrochloric acid (200 mL). The resulting precipitate was collected by filtration and redissolved in tetrahydrofuran. The solution was added dropwise to a mixture of methanol (200 mL) and 15% aqueous ammonia (100 mL), and the resulting precipitate was collected by filtration. The precipitate was redissolved in tetrahydrofuran and added dropwise to a mixed solution of methanol (200 mL) and water (100 mL), and the resulting precipitate was collected by filtration. The collected precipitate was dried under reduced pressure to obtain a polymer G (360 mg).
The number average molecular weight in terms of polystyrene of the polymer G was 6.0 × 10 ⁴ . The polymer G consists of a structural unit represented by the formula (P).

[Experimental Example 10]
Synthesis of Polymer G Cesium Salt Polymer G (150 mg) was placed in a 100 mL flask and purged with nitrogen. Tetrahydrofuran (15 mL) and methanol (5 mL) were mixed. An aqueous solution in which cesium hydroxide (170 mg) was dissolved in water (2 mL) was added to the mixed solution, and the mixture was stirred at 65 ° C. for 6 hours. After the mixture was cooled to room temperature, the reaction solvent was distilled off under reduced pressure. The resulting solid was washed with water and dried under reduced pressure to obtain a pale yellow solid (95 mg). From the NMR spectrum, it was confirmed that the signal derived from the ethyl group at the ethyl ester site in the polymer G had completely disappeared. The obtained cesium salt of polymer G is referred to as conjugated polymer compound 10. Conjugated polymer compound 10 is composed of a structural unit represented by formula (Q) (“selected from the group consisting of a group represented by formula (1) and a group represented by formula (2) in all structural units). The ratio of structural units containing one or more groups and one or more groups represented by formula (3) "and" the formulas (13), (15), (17), ( The ratio of the structural unit represented by 20) "is 100 mol%.) The conjugated polymer compound 10 had a HOMO orbital energy of −5.7 eV and a LUMO orbital energy of −2.9 eV.

[Reference Example 13]
Synthesis of 1,3-dibromo-5-ethoxycarbonyl-6- [2- [2- (2-methoxyethoxy) ethoxy] ethoxy] benzene 3,5-Dibromosalicylic acid (20 g), ethanol (17 mL) under inert atmosphere ), Concentrated sulfuric acid (1.5 mL) and toluene (7 mL) were mixed, and the mixture was stirred with heating at 130 ° C. for 20 hours. After allowing to cool, the reaction solution was added to ice water (100 mL), liquid separation extraction was performed with chloroform, and the solution was concentrated. The obtained solid was dissolved in isopropanol, and the solution was added dropwise to distilled water. The obtained precipitate was filtered off to obtain a solid (18 g). Under an inert atmosphere, the obtained solid (1 g), 2- [2- (2-methoxyethoxy) ethoxy] -p-toluenesulfonate (1.5 g), potassium carbonate (0.7 g), DMF (15 mL) were added. Mix and stir at 100 ° C. for 4 hours. After allowing to cool, chloroform was added to perform liquid separation and extraction, and the solution was concentrated. The concentrate was dissolved in chloroform and purified by passing through a silica gel column. The solution was concentrated to give 1,3-dibromo-5-ethoxycarbonyl-6- [2- [2- (2-methoxyethoxy) ethoxy] ethoxy] benzene (1.0 g).

[Reference Example 14]
Synthesis of Polymer H Under an inert atmosphere, Compound A (0.2 g), Compound B (0.5 g), 1,3-dibromo-5-ethoxycarbonyl-6- [2- [2- (2-methoxyethoxy) ) Ethoxy] ethoxy] benzene (0.1 g), triphenylphosphine palladium (30 mg), tetrabutylammonium bromide (4 mg), and toluene (19 mL) were mixed and heated to 105 ° C. To this reaction solution, 2M aqueous sodium carbonate solution (5 mL) was added dropwise and refluxed for 5 hours. Phenylboronic acid (6 mg) was added to the reaction solution and refluxed for 14 hours. Then, a sodium diethyldithiacarbamate aqueous solution (10 mL, concentration: 0.05 g / mL) was added, and the mixture was stirred for 2 hours. The aqueous layer was removed, the organic layer was washed with distilled water, and the solid obtained by concentration was dissolved in chloroform and purified by passing through an alumina column and a silica gel column. The eluate from the column was concentrated and dried. The yield of the obtained polymer H was 0.44 g.
The number average molecular weight in terms of polystyrene of the polymer H was 3.6 × 10 ⁴ . The polymer H consists of a structural unit represented by the formula (R).

[Experimental Example 11]
Synthesis of Polymer H Cesium Salt Polymer H (200 mg) was placed in a 100 mL flask and purged with nitrogen. Tetrahydrofuran (14 mL) and methanol (7 mL) were added and mixed. An aqueous solution in which cesium hydroxide (90 mg) was dissolved in water (1 mL) was added to the mixed solution, and the mixture was stirred at 65 ° C. for 1 hour. 5 mL of methanol was added to the reaction solution, and the mixture was further stirred at 65 ° C. for 4 hours. After the mixture was cooled to room temperature, the reaction solvent was distilled off under reduced pressure. The resulting solid was washed with water and dried under reduced pressure to obtain a pale yellow solid (190 mg). From the NMR spectrum, it was confirmed that the signal derived from the ethyl group at the ethyl ester site in the polymer H had completely disappeared. The resulting cesium salt of polymer H is referred to as conjugated polymer compound 11. The conjugated polymer compound 11 is composed of a structural unit represented by the formula (S) (“selected from the group consisting of a group represented by the formula (1) and a group represented by the formula (2) in all structural units). The ratio of structural units containing one or more groups and one or more groups represented by formula (3) "and" the formulas (13), (15), (17), ( The ratio of the structural unit represented by 20) "is 100 mol%.) The conjugated polymer compound 11 had a HOMO orbital energy of −5.6 eV and a LUMO orbital energy of −2.8 eV.

[Reference Example 15]
Synthesis of 2,7-dibromo-9,9-bis [3,4-bis [2- [2- (2-methoxyethoxy) ethoxy] ethoxy] -5-methoxycarbonylphenyl] fluorene (Compound D) -Dibromo-9-fluorenone (34.1 g), methyl 2,3-dihydroxybenzoate (101.3 g), and mercaptoacetic acid (1.4 g) were placed in a 500 mL flask and purged with nitrogen. Thereto was added methanesulfonic acid (350 mL), and the mixture was stirred at 90 ° C. for 19 hours. The mixture was allowed to cool, added to ice water and stirred for 1 hour. The resulting solid was filtered off and washed with heated acetonitrile. The washed solid was dissolved in acetone, and the solid was recrystallized from the obtained acetone solution and filtered. The resulting solid (16.3 g), 2- [2- (2-methoxyethoxy) ethoxy] -p-toluenesulfonate (60.3 g), potassium carbonate (48.6 g), and 18-crown-6 (2 4 g) was dissolved in N, N-dimethylformamide (DMF) (500 mL) and the solution was transferred to a flask and stirred at 110 ° C. for 15 hours. The obtained mixture was allowed to cool to room temperature, added to ice water, and stirred for 1 hour. Separation extraction was performed by adding ethyl acetate (300 mL) to the reaction solution, the solution was concentrated, dissolved in a mixed solvent of chloroform / methanol (50/1 (volume ratio)), and purified by passing through a silica gel column. By concentrating the solution passed through the column, 2,7-dibromo-9,9-bis [3,4-bis [2- [2- (2-methoxyethoxy) ethoxy] ethoxy] -5-methoxycarbonyl was obtained. Phenyl] fluorene (Compound D) (20.5 g) was obtained.

[Reference Example 16]
2,7-bis [7- (4-methylphenyl) -9,9-dioctylfluoren-2-yl] -9,9-bis [5-methoxycarbonyl-3,4-bis [2- [2- ( Synthesis of 2-methoxyethoxy) ethoxy] ethoxy] phenyl] -fluorene (Polymer I) Compound D (0.70 g), 2- (4,4,5,5-tetramethyl-1,2 under inert atmosphere , 3-Dioxaborane-2-yl) -9,9-dioctylfluorene (0.62 g), triphenylphosphine palladium (0.019 g), dioxane (40 mL), water (6 mL) and aqueous potassium carbonate (1.38 g) Were mixed and heated to 80 ° C. The reaction was allowed to react for 1 hour. After the reaction, 5 mL of saturated aqueous sodium diethyldithiocarbamate was added and stirred for 30 minutes, and then the organic solvent was removed. The obtained solid was purified through an alumina column (developing solvent hexane: ethyl acetate = 1: 1 (volume ratio)), and the solution was concentrated to obtain 2,7-bis [7- (4-methylphenyl)- 9,9-Dioctylfluoren-2-yl] -9,9-bis [3-ethoxycarbonyl-4- [2- [2- (2-methoxyethoxy) ethoxy] ethoxy] phenyl] -fluorene (Polymer I) 660 mg of was obtained.
The number average molecular weight in terms of polystyrene of the polymer I was 2.0 × 10 ³ . The polymer I is represented by the formula (T). In addition, 2- (4,4,5,5-tetramethyl-1,2,3-dioxaborane-2-yl) -9,9-dioctylfluorene is described in, for example, JP-A-2008-74017. It can be synthesized by the method.

[Experimental example 12]
Synthesis of Polymer I Cesium Salt Polymer I (236 mg) was placed in a 100 mL flask and purged with argon. Tetrahydrofuran (20 mL) and methanol (10 mL) were added thereto, and the mixture was heated to 65 ° C. Thereto was added an aqueous solution in which cesium hydroxide (240 mg) was dissolved in water (2 mL), and the mixture was stirred at 65 ° C. for 7 hours. After the resulting mixture was cooled to room temperature, the reaction solvent was distilled off under reduced pressure. The resulting solid was washed with water and dried under reduced pressure to obtain a pale yellow solid (190 mg). It was confirmed by NMR spectrum that the signal derived from the ethyl group at the ethyl ester site had completely disappeared. The obtained polymer I cesium salt is referred to as a conjugated polymer compound 12. The conjugated polymer compound 12 is represented by the formula (U) (“one type selected from the group consisting of a group represented by the formula (1) and a group represented by the formula (2) in all structural units). "Ratio of structural units containing the above groups and one or more groups represented by formula (3)" and "in formulas (13), (15), (17), (20) in all structural units" The “ratio of structural units represented” is 33.3 mol% rounded off to the second decimal place.) The conjugated polymer compound 12 had a HOMO orbital energy of −5.6 eV and a LUMO orbital energy of −2.8 eV.

[Production and Evaluation Results of Evaluation Device]
In order to evaluate the electron injection characteristics of the ionic polymer, an evaluation element having a diode structure in which only electrons flow was produced, and the current-voltage characteristics were evaluated.
The evaluation element was produced as follows. First, an aluminum layer (lower electrode) having a thickness of 30 nm is formed on a glass substrate, and a polymer layer having a thickness of 80 nm composed of a repeating unit represented by the following formula (I) is formed on the aluminum layer. Then, a 5 nm electron injection layer was formed, and an aluminum layer (upper electrode) having a thickness of 100 nm was further formed on the electron injection layer, thereby producing an evaluation element.

  The following three types of evaluation elements were produced by changing the material of the electron injection layer and the formation method thereof. (A) An evaluation element 1 in which the ionic polymer synthesized in Example 1 is formed in the atmosphere by a coating method. (B) An evaluation element 2 in which sodium fluoride is formed by a vapor deposition method. (C) Evaluation element 3 formed by vapor deposition of barium. A positive voltage was applied to the lower electrode of each evaluation element, a negative voltage was applied to the upper electrode, and the applied voltage was changed to gradually increase, and the electron current flowing through the evaluation element was measured.

  The results are shown in FIG. FIG. 3 is a graph for explaining the electrical characteristics of the ionic polymer. The vertical axis represents the electron current (A: Ampere), and the horizontal axis represents the applied voltage (V: Volt). In the graph of FIG. 3, (a) represents the evaluation result of the evaluation element 1, (b) represents the evaluation result of the evaluation element 2, and (c) represents the evaluation result of the evaluation element 3.

  As is clear from FIG. 3, the evaluation element 1 using the ionic polymer of the present invention for the electron injection layer is compared with the evaluation elements 2 and 3 using sodium fluoride or barium for the electron injection layer. It was found that excellent electron injection characteristics were exhibited in the entire region of 5 V or higher. As for the electron current flowing when the applied voltage is 10 V, the electron current flowing in the evaluation element 1 using the ionic polymer for the electron injection layer is the evaluation element 2 using sodium fluoride or barium for the electron injection layer. 3 was much larger than the electron current flowing through No. 3, and it was found that even in a region where the applied voltage is relatively low, the electron injection characteristic is extremely excellent.

DESCRIPTION OF SYMBOLS 10 Organic thin-film transistor 20 Board | substrate 20A Gate electrode 30 Gate insulating layer 40 Organic-semiconductor layer 50 Charge injection layer 50A 1st charge injection layer 50B 2nd charge injection layer 60A 1st source / drain electrode 60B 2nd source / drain electrode 70 substrates

Claims (9)

A gate electrode;
A first source / drain electrode;
A second source / drain electrode;
An organic semiconductor layer provided between the first and second source / drain electrodes and the gate electrode;
An organic thin film transistor comprising a charge injection layer disposed in contact with the first and second source / drain electrodes between the first and second source / drain electrodes and the organic semiconductor layer,
The charge injection layer contains an ionic polymer having charge injection characteristics to the organic semiconductor layer, and the ionic polymer is a structural unit represented by the following formula (13), represented by the following formula (15). 1 to 1 or more structural units selected from the group consisting of the structural unit represented by the structural unit represented by the following formula (17) and the structural unit represented by the following formula (20) in all structural units. An organic thin film transistor which is a polymer containing mol%.

(In the formula (13), R ¹ is a monovalent group including a group represented by the formula (14), and Ar ¹ has a (2 + n4) -valent fragrance with or without a substituent other than R ^1. Represents a group, n4 represents an integer of 1 or more, and when there are a plurality of R ^{1 s} , they may be the same or different.

(In formula (14), R ² represents a (1 + m1 + m2) -valent organic group, m1 and m2 each independently represents an integer of 1 or more, Q ¹ represents a divalent organic group, and Y ¹ represents − Represents CO ₂ ⁻ , —SO ₃ ⁻ , —SO ₂ ^— or —PO ₃ ²⁻ , M ¹ represents a metal cation or an ammonium cation with or without a substituent, and Z ¹ represents F ⁻ , Cl ^−. , Br ⁻ , I ⁻ , OH ⁻ , R ^a SO ₃ ⁻ , R ^a COO ⁻ , ClO ⁻ , ClO ₂ ⁻ , ClO ₃ ⁻ , ClO ₄ ⁻ , SCN ⁻ , CN ⁻ , NO ₃ ⁻ , SO ₄ ²⁻ , HSO ₄ ⁻ , PO ₄ ³⁻ , HPO ₄ ²⁻ , H ₂ PO ₄ ⁻ , BF ₄ ⁻ or PF ₆ ⁻ , n1 represents an integer of 0 or more, a1 represents an integer of 1 or more, b1 represents an integer of 0 or more, however, a1 and _{^{b1, - (Q 1) n1}} -Y 1 (M 1) a1 (Z 1) is selected so that the charge is zero the groups represented by _b1 , R ^a represents an aryl group having a carbon number of 6 to 50 that do not have or have an alkyl group or a substituent having 1 to 30 carbon atoms which does not have or have a substituent, Q ³ is a divalent Represents an organic group, Y ³ represents —CN or a group represented by any one of formulas (4) to (12), n3 represents an integer of 0 or more, and Q ¹ , Q ³ , Y ¹ , M ¹ , Z ¹ , Y ³ , n1, a1, b1, and n3 may be the same or different when there are a plurality of each.
-O- (R'O) _a3 -R '' (4)

-S- (R'S) _a4 -R '' (6)
-C (= O)-(R'-C (= O)) _a4 -R '' (7)
-C (= S)-(R'-C (= S)) _a4 -R '' (8)
-N {(R ′) _a4 R ″} ₂ (9)
—C (═O) O— (R′—C (═O) O) _a4 —R ″ (10)
-C (= O) O- (R'O) _a4- R "(11)
—NHC (═O) — (R′NHC (═O)) _a4 —R ″ (12)
(In the formulas (4) to (12), R ′ represents a divalent hydrocarbon group with or without a substituent, and R ″ represents a hydrogen atom, a monovalent with or without a substituent. Or —COOH, —SO ₃ H, —OH, —SH, —NR ^c ₂ , —CN or —C (═O) NR ^c ₂ , wherein R ′ ″ has a substituent, or Represents a trivalent hydrocarbon group not having, a3 represents an integer of 1 or more, a4 represents an integer of 0 or more, and R ^c is an alkyl having 1 to 30 carbon atoms with or without a substituent. An aryl group having 6 to 50 carbon atoms, with or without a group or substituent, may be the same or different when there are a plurality of R ′, R ″ and R ′ ″. ))

(In the formula (15), R ³ is a monovalent group including a group represented by the formula (16), and Ar ² has a (2 + n5) -valent fragrance with or without a substituent other than R ^3. Represents a group, n5 represents an integer of 1 or more, and when there are a plurality of R ^{3 s} , they may be the same or different.

(In Formula (16), R ⁴ represents a (1 + m3 + m4) valent organic group, Q ² represents a divalent organic group , Y ² represents a carbocation, an ammonium cation, a phosphonyl cation, a sulfonyl cation, or an iodonium cation. M ² represents F ⁻ , Cl ⁻ , Br ⁻ , I ⁻ , OH ⁻ , R ^b SO ₃ ⁻ , R ^b COO ⁻ , ClO ⁻ , ClO ₂ ⁻ , ClO ₃ ⁻ , ClO ₄ ⁻ , SCN ⁻ , CN _{^{-, NO 3 -, SO 4}} 2-, HSO 4 -, PO 4 3-, HPO 4 2-, H 2 PO 4 -, BF 4 - or PF ₆ ^- represents a Z ² is a metal cation or a substituent N2 represents an integer of 0 or more , a2 represents an integer of 1 or more , b2 represents an integer of 0 or more, provided that a2 and b2 represent-(Q ² ) _{^{n2 -Y 2 (M 2) a2}} (Z 2) so that the charge of the group represented by _b2 becomes 0 Is selected, R ^b represents an aryl group having a carbon number of 6 to 50 that do not have or have an alkyl group or a substituent having 1 to 30 carbon atoms which does not have or have a substituent, Q ^3, Y ³ and n3 represent the same meaning as described above, and m3 and m4 each independently represent an integer of 1 or more, Q ² , Q ³ , Y ² , M ² , Z ² , Y ³ , n 2, a 2, b 2 and n 3 If there are multiple of each, they may be the same or different.))

(In the formula (17), R ⁵ is a monovalent group containing a group represented by the formula (18), R ⁶ is a monovalent group containing a group represented by the formula (19), Ar ³ represents a (2 + n6 + n7) -valent aromatic group having or not having a substituent other than R ⁵ and R ⁶ , n6 and n7 each independently represents an integer of 1 or more, and each of R ⁵ and R ⁶ May be the same or different when there are multiple.
Equation ^{(18): - R 7 -} {(Q 1) n1 -Y 1 (M 1) a1 (Z 1) b1} m5 (18)
(In formula (18), R ⁷ represents a direct bond or a (1 + m5) -valent organic group, Q ¹ , Y ¹ , M ¹ , Z ¹ , n1, a1, and b1 represent the same meaning as described above, and m5 represents Represents an integer of 1 or more, and when there are a plurality of Q ¹ , Y ¹ , M ¹ , Z ¹ , n ¹ , a 1 and b ¹ , they may be the same or different.
Equation ^{(19): - R 8 -} {(Q 3) n3 -Y 3} m6 (19)
(In the formula (19), R ⁸ represents a single bond or a (1 + m6) valent organic group, Q ³ , Y ³ and n3 represent the same meaning as described above, m6 represents an integer of 1 or more, provided that R ^{When 8} is a single bond, m6 represents 1, and when there are a plurality of Q ³ , Y ³ and n3, they may be the same or different.))

(In the formula (20), R ⁹ is a monovalent group containing a group represented by the formula (21), R ¹⁰ is a monovalent group containing a group represented by the formula (22), Ar ⁴ represents a (2 + n8 + n9) -valent aromatic group having or not having a substituent other than R ⁹ and R ¹⁰ , n8 and n9 each independently represents an integer of 1 or more, and each of R ⁹ and R ¹⁰ May be the same or different when there are multiple.
Equation ^{(21): - R 11 -} {(Q 2) n2 -Y 2 (M 2) a2 (Z 2) b2} m7 (21)
(In the formula (21), R ¹¹ represents a single bond or a (1 + m7) -valent organic group, Q ² , Y ² , M ² , Z ² , n ² , a 2 and b 2 represent the same meaning as described above, and m 7 represents Represents an integer of 1 or more, provided that when R ¹¹ is a single bond, m7 represents 1, and when there are a plurality of Q ² , Y ² , M ² , Z ² , n ² , a 2 and b ² , they are the same or different. May be.)
Equation ^{(22): - R 12 -} {(Q 3) n3 -Y 3} m8 (22)
(In the formula (22), R ¹² represents a single bond or a (1 + m8) -valent organic group, Q ³ , Y ³ and n3 represent the same meaning as described above, and m8 represents an integer of 1 or more, provided that R ^{When 12} is a single bond, m8 represents 1, and when there are a plurality of Q ³ , Y ³ and n3, they may be the same or different.)) The charge injection layer is a charge injection layer whose conductivity type is n-type,
The organic thin film transistor according to claim 1, wherein the organic semiconductor layer is an n type organic semiconductor layer. Between the organic semiconductor layer and the gate electrode, having a gate insulating layer disposed in contact with the gate electrode,
The organic thin film transistor according to claim 2, wherein the gate electrode is made of an n-type semiconductor substrate.   An organic thin-film transistor substrate provided with the organic thin-film transistor as described in any one of Claims 1-3.   A display device comprising the organic thin film transistor substrate according to claim 4 as a drive substrate. A gate electrode;
A first source / drain electrode;
A second source / drain electrode;
An organic semiconductor layer provided between the first and second source / drain electrodes and the gate electrode;
An organic thin film transistor that forms a charge injection layer disposed in contact with the first and second source / drain electrodes between the first and second source / drain electrodes and the organic semiconductor layer, respectively. In the manufacturing method,
An ionic polymer having a charge injection property to the organic semiconductor layer is contained, and the ionic polymer is a structural unit represented by the following formula (13), a structural unit represented by the following formula (15), A polymer containing 15 to 100 mol% of all structural units of at least one structural unit selected from the group consisting of the structural unit represented by formula (17) and the structural unit represented by formula (20) below. A method for producing an organic thin film transistor, comprising a step of forming a certain charge injection layer.

(In the formula (13), R ¹ is a monovalent group including a group represented by the formula (14), and Ar ¹ has a (2 + n4) -valent fragrance with or without a substituent other than R ^1. Represents a group, n4 represents an integer of 1 or more, and when there are a plurality of R ^{1 s} , they may be the same or different.

(In formula (14), R ² represents a (1 + m1 + m2) -valent organic group, m1 and m2 each independently represents an integer of 1 or more, Q ¹ represents a divalent organic group, and Y ¹ represents − Represents CO ₂ ⁻ , —SO ₃ ⁻ , —SO ₂ ^— or —PO ₃ ²⁻ , M ¹ represents a metal cation or an ammonium cation with or without a substituent, and Z ¹ represents F ⁻ , Cl ^−. , Br ⁻ , I ⁻ , OH ⁻ , R ^a SO ₃ ⁻ , R ^a COO ⁻ , ClO ⁻ , ClO ₂ ⁻ , ClO ₃ ⁻ , ClO ₄ ⁻ , SCN ⁻ , CN ⁻ , NO ₃ ⁻ , SO ₄ ²⁻ , HSO ₄ ⁻ , PO ₄ ³⁻ , HPO ₄ ²⁻ , H ₂ PO ₄ ⁻ , BF ₄ ⁻ or PF ₆ ⁻ , n1 represents an integer of 0 or more, a1 represents an integer of 1 or more, b1 is an integer of 0 or more, however, a1 and _{^{b1, - (Q 1) n1}} -Y 1 (M 1) a1 (Z 1) is selected so that the charge is zero the groups represented by _b1 , R ^a represents an aryl group having a carbon number of 6 to 50 that do not have or have an alkyl group or a substituent having 1 to 30 carbon atoms which does not have or have a substituent, Q ³ is a divalent Represents an organic group, Y ³ represents —CN or a group represented by any one of formulas (4) to (12), n3 represents an integer of 0 or more, and Q ¹ , Q ³ , Y ¹ , M ¹ , Z ¹ , Y ³ , n1, a1, b1, and n3 may be the same or different when there are a plurality of each.
-O- (R'O) _a3 -R '' (4)

-S- (R'S) _a4 -R '' (6)
-C (= O)-(R'-C (= O)) _a4 -R '' (7)
-C (= S)-(R'-C (= S)) _a4 -R '' (8)
-N {(R ′) _a4 R ″} ₂ (9)
—C (═O) O— (R′—C (═O) O) _a4 —R ″ (10)
-C (= O) O- (R'O) _a4- R "(11)
—NHC (═O) — (R′NHC (═O)) _a4 —R ″ (12)
(In the formulas (4) to (12), R ′ represents a divalent hydrocarbon group with or without a substituent, and R ″ represents a hydrogen atom, a monovalent with or without a substituent. Or —COOH, —SO ₃ H, —OH, —SH, —NR ^c ₂ , —CN or —C (═O) NR ^c ₂ , wherein R ′ ″ has a substituent, or Represents a trivalent hydrocarbon group not having, a3 represents an integer of 1 or more, a4 represents an integer of 0 or more, and R ^c is an alkyl having 1 to 30 carbon atoms with or without a substituent. An aryl group having 6 to 50 carbon atoms, with or without a group or substituent, may be the same or different when there are a plurality of R ′, R ″ and R ′ ″. ))

(In the formula (15), R ³ is a monovalent group including a group represented by the formula (16), and Ar ² has a (2 + n5) -valent fragrance with or without a substituent other than R ^3. Represents a group, n5 represents an integer of 1 or more, and when there are a plurality of R ^{3 s} , they may be the same or different.

(In Formula (16), R ⁴ represents a (1 + m3 + m4) valent organic group, Q ² represents a divalent organic group , Y ² represents a carbocation, an ammonium cation, a phosphonyl cation, a sulfonyl cation, or an iodonium cation. M ² represents F ⁻ , Cl ⁻ , Br ⁻ , I ⁻ , OH ⁻ , R ^b SO ₃ ⁻ , R ^b COO ⁻ , ClO ⁻ , ClO ₂ ⁻ , ClO ₃ ⁻ , ClO ₄ ⁻ , SCN ⁻ , CN _{^{-, NO 3 -, SO 4}} 2-, HSO 4 -, PO 4 3-, HPO 4 2-, H 2 PO 4 -, BF 4 - or PF ₆ ^- represents a Z ² is a metal cation or a substituent N2 represents an integer of 0 or more , a2 represents an integer of 1 or more , b2 represents an integer of 0 or more, provided that a2 and b2 represent-(Q ² ) _{^{n2 -Y 2 (M 2) a2}} (Z 2) so that the charge of the group represented by _b2 becomes 0 Is selected, R ^b represents an aryl group having a carbon number of 6 to 50 that do not have or have an alkyl group or a substituent having 1 to 30 carbon atoms which does not have or have a substituent, Q ^3, Y ³ and n3 represent the same meaning as described above, and m3 and m4 each independently represent an integer of 1 or more, Q ² , Q ³ , Y ² , M ² , Z ² , Y ³ , n 2, a 2, b 2 and n 3 If there are multiple of each, they may be the same or different.))

(In the formula (17), R ⁵ is a monovalent group containing a group represented by the formula (18), R ⁶ is a monovalent group containing a group represented by the formula (19), Ar ³ represents a (2 + n6 + n7) -valent aromatic group having or not having a substituent other than R ⁵ and R ⁶ , n6 and n7 each independently represents an integer of 1 or more, and each of R ⁵ and R ⁶ May be the same or different when there are multiple.
Equation ^{(18): - R 7 -} {(Q 1) n1 -Y 1 (M 1) a1 (Z 1) b1} m5 (18)
(In formula (18), R ⁷ represents a direct bond or a (1 + m5) -valent organic group, Q ¹ , Y ¹ , M ¹ , Z ¹ , n1, a1, and b1 represent the same meaning as described above, and m5 represents Represents an integer of 1 or more, and when there are a plurality of Q ¹ , Y ¹ , M ¹ , Z ¹ , n ¹ , a 1 and b ¹ , they may be the same or different.
Equation ^{(19): - R 8 -} {(Q 3) n3 -Y 3} m6 (19)
(In the formula (19), R ⁸ represents a single bond or a (1 + m6) valent organic group, Q ³ , Y ³ and n3 represent the same meaning as described above, m6 represents an integer of 1 or more, provided that R ^{When 8} is a single bond, m6 represents 1, and when there are a plurality of Q ³ , Y ³ and n3, they may be the same or different.))

(In the formula (20), R ⁹ is a monovalent group containing a group represented by the formula (21), R ¹⁰ is a monovalent group containing a group represented by the formula (22), Ar ⁴ represents a (2 + n8 + n9) -valent aromatic group having or not having a substituent other than R ⁹ and R ¹⁰ , n8 and n9 each independently represents an integer of 1 or more, and each of R ⁹ and R ¹⁰ May be the same or different when there are multiple.
Equation ^{(21): - R 11 -} {(Q 2) n2 -Y 2 (M 2) a2 (Z 2) b2} m7 (21)
(In the formula (21), R ¹¹ represents a single bond or a (1 + m7) -valent organic group, Q ² , Y ² , M ² , Z ² , n ² , a 2 and b 2 represent the same meaning as described above, and m 7 represents Represents an integer of 1 or more, provided that when R ¹¹ is a single bond, m7 represents 1, and when there are a plurality of Q ² , Y ² , M ² , Z ² , n ² , a 2 and b ² , they are the same or different. May be.)
Equation ^{(22): - R 12 -} {(Q 3) n3 -Y 3} m8 (22)
(In the formula (22), R ¹² represents a single bond or a (1 + m8) -valent organic group, Q ³ , Y ³ and n3 represent the same meaning as described above, and m8 represents an integer of 1 or more, provided that R ^{When 12} is a single bond, m8 represents 1, and when there are a plurality of Q ³ , Y ³ and n3, they may be the same or different.))   The organic thin film transistor according to claim 6, wherein in the step of forming the charge injection layer, the charge injection layer is formed by coating and forming a coating liquid containing an ionic polymer under an atmospheric pressure atmosphere. Production method.   8. The method of manufacturing an organic thin film transistor according to claim 6, wherein the first and second source / drain electrodes are formed by applying and forming a coating liquid in a normal pressure atmosphere. 9.   The manufacturing method of the organic thin-film transistor as described in any one of Claims 6-8 which forms the said organic-semiconductor layer by apply | coating and forming a coating liquid in a normal-pressure atmosphere.