JP5677778B2 - 光学フィルム、位相差フィルム、偏光板及び液晶表示装置 - Google Patents
光学フィルム、位相差フィルム、偏光板及び液晶表示装置 Download PDFInfo
- Publication number
- JP5677778B2 JP5677778B2 JP2010163448A JP2010163448A JP5677778B2 JP 5677778 B2 JP5677778 B2 JP 5677778B2 JP 2010163448 A JP2010163448 A JP 2010163448A JP 2010163448 A JP2010163448 A JP 2010163448A JP 5677778 B2 JP5677778 B2 JP 5677778B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- optical film
- compound
- liquid crystal
- retardation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
即ち、本発明は下記の手段により達成することができる。
繰り返し単位を有する化合物、レタデーションの耐久性を向上させる化合物、及びセルロースエステルを含む光学フィルムであって、
該繰り返し単位を有する化合物が該セルロースエステルに対して30質量%より多く含まれ、
前記光学フィルムは、60℃90%RHで1日処理した場合の寸法変化率が3%以下であり、
前記光学フィルムの波長590nmで測定した下記式(I)及び式(II)にて定義されるRe及びRthが下記式(IIIa)及び(IVa)を満たすことを特徴とする光学フィルム。
式(I) Re=(nx―ny)×d(nm)
式(II) Rth={(nx+ny)/2−nz}×d(nm)
式(IIIa) Re<10
式(IVa) |Rth|<25
(式中、nxはフィルム面内の遅相軸方向の屈折率であり、nyはフィルム面内の進相軸方向の屈折率であり、nzはフィルムの厚み方向の屈折率であり、dはフィルムの厚さ(nm)である。)
<2>
前記レタデーションの耐久性を向上させる化合物が、分子内に塩基性の官能基を有する化合物であることを特徴とする<1>に記載の光学フィルム。
<3>
前記繰り返し単位を有する化合物が、多価アルコールと多塩基酸との縮合物、多価エーテルアルコールと多塩基酸との縮合物、多価アルコールと多塩基酸との縮合物とイソシアナート化合物との縮合物からなる群より選択される少なくとも1種の化合物であることを特徴とする<1>又は<2>に記載の光学フィルム。
<4>
前記繰り返し単位を有する化合物が、アクリル酸エステルの付加物、メタクリル酸エステルの付加物からなる群より選択される少なくとも1種の化合物であることを特徴とする<1>又は<2>に記載の光学フィルム。
<5>
前記繰り返し単位を有する化合物が、多価アルコールと多塩基酸との縮合物、及び多価エーテルアルコールと多塩基酸との縮合物からなる群より選択される少なくとも1種の化合物を含有しており、該縮合物の水酸基価が40mgKOH/g未満であることを特徴とする<1>〜<3>のいずれか一項に記載の光学フィルム。
<6>
前記光学フィルムが、60℃90%RHで1日処理した場合の寸法変化率が0.05〜1%であることを特徴とする<1>〜<5>のいずれか一項に記載の光学フィルム。
<7>
前記セルロースエステルが、セルロースの水酸基へのアシル置換度が2.80〜3.00のセルロースアシレートであることを特徴とする<1>〜<6>のいずれか一項に記載の光学フィルム。
<8>
少なくとも、<1>〜<7>のいずれか一項に記載の光学フィルムを含む位相差フィルム。
<9>
少なくとも、<1>〜<7>のいずれか一項に記載の光学フィルム、または<8>に記載の位相差フィルムを含む偏光板。
<10>
少なくとも、<1>〜<7>のいずれか一項に記載の光学フィルム、又は<8>に記載の位相差フィルム、又は<9>に記載の偏光板を含むことを特徴とする画像表示装置。
なお、本発明は上記<1>〜<10>に関するものであるが、参考のためその他の事項(例えば下記1〜9に記載の事項など)についても記載した。
1.
繰り返し単位を有する化合物、レタデーションの耐久性を向上させる化合物、及びセルロースエステルを含む光学フィルムであって、
該繰り返し単位を有する化合物が該セルロースエステルに対して30質量%以上含まれることを特徴とする光学フィルム。
2.
前記レタデーションの耐久性を向上させる化合物が、分子内に塩基性の官能基を有する化合物であることを特徴とする上記1に記載の光学フィルム。
3.
前記繰り返し単位を有する化合物が、多価アルコールと多塩基酸との縮合物、多価エーテルアルコールと多塩基酸との縮合物、多価アルコールと多塩基酸との縮合物とイソシアナート化合物との縮合物からなる群より選択される少なくとも1種の化合物であることを特徴とする上記1又は2に記載の光学フィルム。
4.
前記繰り返し単位を有する化合物が、アクリル酸エステルの付加物、メタクリル酸エステルの付加物からなる群より選択される少なくとも1種の化合物であることを特徴とする上記1〜3のいずれか一項に記載の光学フィルム。
5.
前記繰り返し単位を有する化合物が、多価アルコールと多塩基酸との縮合物、及び多価エーテルアルコールと多塩基酸との縮合物からなる群より選択される少なくとも1種の化合物を含有しており、該縮合物の水酸基価が40mgKOH/g未満であることを特徴とする上記1〜4のいずれか一項に記載の光学フィルム。
6.
前記光学フィルムが、60℃90%RHで1日処理した場合の寸法変化率が3%以下であることを特徴とする上記1〜5のいずれか一項に記載の光学フィルム。
7.
少なくとも、上記1〜6のいずれか一項に記載の光学フィルムを含む位相差フィルム。
8.
少なくとも、上記1〜6のいずれか一項に記載の光学フィルム、又は上記7に記載の位相差フィルムを含む偏光板。
9.
少なくとも、上記1〜6のいずれか一項に記載の光学フィルム、又は上記7に記載の位相差フィルム、又は上記8に記載の偏光板を含むことを特徴とする画像表示装置。
本発明の光学フィルムは、繰り返し単位を有する化合物をセルロースエステルに対して上記の量含有させることで、フィルムの弾性率、光弾性、膜厚、吸湿率を適切に調整することができ、液晶表示装置の光ムラを改善することができる。
繰り返し単位を有する化合物の含有量は、セルロースエステルに対して30質量%以上200質量%以下が好ましく、35質量%以上150質量%以下がより好ましく、40質量%以上100質量%以下が更に好ましい。含有量が30質量%以上であれば光ムラを改善することができるため好ましく、200質量%以下であれば、フィルムからのブリードアウトを抑制しやすく好ましい。
なお、繰り返し単位を有する化合物を2種以上含有させる場合には、本発明の光学フィルムでは該2種以上の繰り返し単位を有する化合物の合計の含有量が上記範囲に収まればよい。
本発明で用いられる繰り返し単位を有する化合物について説明する。
本発明の光学フィルムは、繰り返し単位を有する化合物を含有し、繰り返し単位を有する化合物の分子量は特に限定されないが、好ましくは600〜5000であり、セルロースエステルとの相溶性を悪化させない範囲で繰り返し単位を有する化合物の分子量を増加させることでフィルムを湿熱環境下で保持した場合のレタデーション変化を抑制することができ、液晶表示装置を過酷な環境下で使用した場合にも、表示特性の変化が起こらないパネルを製造することができる。
本発明における繰り返し単位を有する化合物の数平均分子量(Mn)は、600〜3000であることが好ましく、650〜2800がより好ましく、800〜2000が更に好ましい。繰り返し単位を有する化合物の数平均分子量は600以上であれば揮発性が低くなる。本発明の光学フィルムを製膜したり、延伸した時の高温条件下における揮散によるフィルム故障や工程汚染を生じにくくなると同時に、分子量を上昇させることによって湿熱環境下で保持した場合のレタデーション変化を抑制することができる。
本発明における繰り返し単位を有する化合物の数平均分子量はゲルパーミエーションクロマトグラフィーによって測定、評価することができる。
また、本発明の繰り返し単位を有する化合物は使用する環境温度あるいは湿度下で(一般には室温状況、所謂25℃、相対湿度60%)、液体であっても固体であっても良い。また、その色味は少ないほど良好であり特に無色であることが好ましい。熱的にはより高温において安定であることが好ましく、分解開始温度が150℃以上、更に200℃以上が好ましい。
以下、本発明に用いられる繰り返し単位を有する化合物について、その具体例を挙げながら詳細に説明するが、本発明で用いることができる繰り返し単位を有する化合物はこれらに限定されるものではない。
本発明の光学フィルムに用いることのできる繰り返し単位を有する化合物としては、特に限定されないが、縮合物若しくは付加物を挙げることができ、縮合物としては、多価アルコールと多塩基酸との縮合物、多価エーテルアルコールと多塩基酸との縮合物、多価アルコールと多塩基酸との縮合物とイソシアナート化合物との縮合物を好ましく挙げることができ、付加物としては、アクリル酸エステルの付加物、メタクリル酸エステルの付加物を好ましく挙げることができる。また、ポリエーテル系化合物、ポリウレタン系化合物、ポリエーテルポリウレタン系化合物、ポリアミド系化合物、ポリスルフォン系化合物、ポリスルフォンアミド系化合物、後述するその他の高分子系化合物から選択される少なくとも1種の数平均分子量が600以上の化合物を用いることもできる。
以下に、本発明で好ましく用いられる繰り返し単位を有する化合物について種類別に記述する。
以下、本発明における多価アルコールと多塩基酸との縮合物の合成に好ましく用いることができる二塩基酸及びグリコールについて説明する。
脂肪族ジカルボン酸としては、例えば、シュウ酸、マロン酸、コハク酸、マレイン酸、フマル酸、グルタル酸、アジピン酸、スベリン酸、アゼライン酸、シクロヘキサンジカルボン酸、セバシン酸、ドデカンジカルボン酸等が挙げられる。なかでも、コハク酸及びアジピン酸が相溶性向上の観点から好ましい。
芳香族ジカルボン酸としては、例えば、フタル酸、テレフタル酸、イソフタル酸、1,5―ナフタレンジカルボン酸、1,4―ナフタレンジカルボン酸等が挙げられる。なかでも、フタル酸及びテレフタル酸が好ましく、テレフタル酸が特に好ましい。
本発明に用いる二塩基酸の炭素数は、4〜12であることが好ましく、4〜8であることがより好ましく、4〜6であることが好ましい。本発明では2種以上の二塩基酸の混合物を用いてもよく、この場合、2種以上の二塩基酸の平均炭素数が上記範囲となることが好ましい。二塩基酸の炭素数が上記範囲であれば、光ムラの改良に加えて、セルロースエステルとの相溶性に優れ、光学フィルムの製膜時及び加熱延伸時においてもブリードアウトを生じにくいため好ましい。
脂肪族ジカルボン酸と芳香族ジカルボン酸とを併用することも好ましい。具体的には、アジピン酸とフタル酸との併用、アジピン酸とテレフタル酸との併用、コハク酸とフタル酸との併用、コハク酸とテレフタル酸のとの併用が好ましく、コハク酸とフタル酸との併用、コハク酸とテレフタル酸との併用がより好ましい。脂肪族ジカルボン酸と芳香族ジカルボン酸とを併用する場合、両者の比率(モル比)は特に限定されないが、95:5〜40:60が好ましく、55:45〜45:55がより好ましい。
脂肪族ジオールとしては、アルキルジオール又は脂環式ジオール類を挙げることができ、例えば、エチレングリコール、1,2−プロパンジオール、1,3−プロパンジオール、1,2−ブタンジオール、1,3−ブタンジオール、2−メチル−1,3−プロパンジオール、1,4−ブタンジオール、1,5−ペンタンジオール、2,2−ジメチル−1,3−プロパンジオール(ネオペンチルグリコール)、2,2−ジエチル−1,3−プロパンジオール(3,3−ジメチロ−ルペンタン)、2−n−ブチル−2−エチル−1,3−プロパンジオール(3,3−ジメチロールヘプタン)、3−メチル−1,5−ペンタンジオール、1,6−ヘキサンジオール、1,4−シクロヘキサンジオール、1,4−シクロヘキサンジメタノール、2,2,4−トリメチル−1,3−ペンタンジオール、2−エチル−1,3−ヘキサンジオール、2−メチル−1,8−オクタンジオール、1,9−ノナンジオール、1,10−デカンジオール、ジエチレングリコールなどが挙げられる。
好ましい脂肪族ジオールとしては、エチレングリコール、1,2−プロパンジオール、及び1,3−プロパンジオールの少なくとも1種であり、特に好ましくは、エチレングリコール及び1,2−プロパンジオールの少なくとも1種である。2種用いる場合は、エチレングリコール及び1,2−プロパンジオールを用いることが好ましい。
グリコールの炭素数は、2〜10であることが好ましく、2〜6であることがより好ましく、2〜4であることが特に好ましい。2種以上のグリコールを用いる場合には、該2種以上の平均炭素数が上記範囲となることが好ましい。グリコールの炭素数が上記範囲であれば、光ムラの改良に加えて、セルロースエステルとの相溶性に優れ、フィルムの製膜時及び加熱延伸時においてもブリードアウトを生じにくいため好ましい。
次に、本発明で用いられる多価エーテルアルコールと多塩基酸との縮合物について説明する。本発明の多価エーテルアルコールと多塩基酸との縮合物とは、ジカルボン酸とポリエーテルジオールとの縮合ポリマーを示すものである。ジカルボン酸としては、多価アルコールと多塩基酸との縮合物で記述した炭素数4〜12の脂肪族ジカルボン酸残基又は炭素数8〜12の芳香族ジカルボン酸残基をそのまま使用するものである。
更に、本発明で用いられる多価アルコールと多塩基酸との縮合物とイソシアナート化合物との縮合物について説明する。該縮合物は、多価アルコールと多塩基酸との縮合物とイソシアナート化合物の縮合で得ることができる。まず、多価アルコールと多塩基酸との縮合物としては、前記の両末端を封止する前の多価アルコールと多塩基酸との縮合物をそのまま使用でき、多価アルコールと多塩基酸との縮合物で前述した素材を好ましく利用できる。
本発明においては、前述した縮合物だけでなく、その他の高分子系添加剤も使用し得るものである。該高分子系添加剤としては、脂肪族炭化水素系ポリマー、脂環式炭化水素系ポリマー、ポリアクリル酸エステル、ポリメタクリル酸エステル等のアクリル系ポリマー(エステル基としては、メチル基、エチル基、プロピル基、ブチル基、イソブチル基、ペンチル基、ヘキシル基、シクロヘキシル基、オクチル基、2−エチルヘキシル基、ノニル基、イソノニル基、tert−ノニル基、ドデシル基、トリデシル基、ステアリル基、オレイル基、ベンジル基、フェニル基など)、ポリビニルイソブチルエーテル、ポリN−ビニルピロリドン等のビニル系ポリマー、ポリスチレン、ポリ4−ヒドロキシスチレン等のスチレン系ポリマー、ポリエチレンオキシド、ポリプロピレンオキシド等のポリエーテル、ポリアミド、ポリウレタン、ポリウレア、フェノール−ホルムアルデヒド縮合物、尿素−ホルムアルデヒド縮合物、酢酸ビニル、等が挙げられる。
本発明の光学フィルムは、レタデーションの耐久性を向上させる化合物を含む。このような化合物の添加量は特に限定されないが、セルロースエステルに対し0.001〜20質量%であることが好ましく、0.01〜10質量%が好ましく、0.05〜5質量%が好ましく、0.1〜3質量%が最も好ましい。レタデーションの耐久性には、フィルムを湿熱環境下で保持した場合のレタデーション変化として観測される耐久性と、フィルムを偏光板形態にした上で湿熱環境下で保持した場合のレタデーション変化とがある。前者に関しては、後述の寸法変化率を制御することで改善させることができる。また、後者に関しては、下記レタデーションの耐久性を向上させる化合物を添加することで改善させることができ、このような化合物として、分子内に塩基性の官能基を有する化合物を用いることができる。塩基性の官能基としては、例えば、1級アミノ基、2級アミノ基、3級アミノ基、4級アンモニウム基、ピリジン、ピリミジン、ピラジン等の含窒素ヘテロ環、グアニジノ基、イミノ基、イミダゾイル基、インドール基、プリン基、ピリミジン基等が挙げられる。例えば下記のような化合物を具体例として挙げることができる。
次に、本発明におけるセルロースエステルについて説明する。
本発明の光学フィルムはセルロースエステルを含むことを特徴であり、セルロースエステル含有率が30〜77質量%であることが好ましく、40〜75質量%であることがより好ましく、50〜75質量%であることが更に好ましく、このことにより、偏光板加工性に優れた光学フィルムを製造することができる。
本発明の光学フィルムに用いられるセルロースエステルは、原料のセルロースと酸とのエステルであり、炭素数2〜22程度のカルボン酸エステル(所謂セルロースアシレート)であることが好ましく、炭素数6以下の低級脂肪酸エステルであることがより好ましい。本発明のセルロースアシレートにおいて、セルロースの水酸基に置換する酢酸及び/又は炭素原子数3〜22の脂肪酸の置換度の測定方法としては、ASTMのD−817−91に準じた方法や、NMR法を挙げることができる。そして、炭素数2〜22程度のセルロースアシレートである場合には、繰り返し単位を有する縮合物を用い、特に炭素数2のセルロースアセテートである場合には、これに加え、繰り返し単位を有する付加物も好ましく用いることによって液晶表示装置の光ムラを改善することができる。
本発明に用いられるセルロースエステルの原料のセルロースとしては、綿花リンタや木材パルプ(広葉樹パルプ,針葉樹パルプ)などがあり、何れの原料セルロースから得られるセルロースエステルでも使用でき、場合により混合して使用してもよい。これらの原料セルロースについての詳細な記載は、例えばプラスチック材料講座(17)繊維素系樹脂(丸澤、宇田著、日刊工業新聞社、1970年発行)や発明協会公開技報2001−1745(7頁〜8頁)に記載のセルロースを用いることができ、本発明の光学フィルムに対しては特に限定されるものではない。
本発明の光学フィルムの光学異方性は、先述のポリエステル系オリゴマーの添加によってによって制御されるが、目的のレタデーションに応じて、更に異なる光学異方性調整剤を加えてもよい。例えば、公開特許公報 特開2006−30937号23ページから72ページに記載のRthを低減させる化合物を添加することもできるし、Rthを上昇させる化合物、具体的には、芳香環を1個以上有する化合物が好ましく、2〜15個有することがより好ましく、3〜10個有することが更に好ましい。化合物中の芳香環以外の各原子は、芳香環と同一平面に近い配置であることが好ましく、芳香環を複数有している場合には、芳香環同士も同一平面に近い配置であることが好ましい。また、Rthを選択的に上昇させるため、添加剤のフィルム中での存在状態は、芳香環平面がフィルム面と平行な方向に存在していることが好ましい。
前記添加剤は、単独で使用しても良いし、2種類以上の添加剤を組み合わせて使用しても良い。
Rthを上昇させる効果のある添加剤としては、具体的には、特開2005−104148号公報の33〜34頁に記載の可塑剤や、特開2005−104148号公報の38〜89頁に記載の光学異方性のコントロール剤などが挙げられる。
本発明の光学フィルムは、波長590nmで測定したRe及びRth(下記式(I)及び式(II)にて定義される)を、用途に応じて適切に調整することが重要であり、この値は、セルロースエステルの置換基の種類や置換度、前述の繰り返し単位を有する化合物の種類や添加量、フィルムの膜厚、製膜時の工程条件、延伸工程などにより制御することができる。
本発明の光学フィルムのレタデーションを低減させ、例えば、IPSモードの液晶パネル用途で使用する場合には、下記式(IIIa)及び(IVa)を満たすことが好ましく、更に保護フィルムとして用いられる光学フィルムを支持体として、後述の機能層を設けることもできる。これにより、例えば、液晶表示装置の表示画面のコントラストを向上させたり、視野角特性や色味を改善したりすることができる。
式(I) Re=(nx―ny)×d(nm)
式(II) Rth={(nx+ny)/2−nz}×d(nm)
式(IIIa) Re<10
式(IVa) |Rth|<25
(式中、nxはフィルム面内の遅相軸方向の屈折率であり、nyはフィルム面内の進相軸方向の屈折率であり、nzはフィルムの厚み方向の屈折率であり、dはフィルムの厚さ(nm)である。)
この場合、面内の遅相軸の方位は特に限定されないが、面内でフィルムの弾性率が最大となる方位に対して略並行若しくは略直交であることが好ましい。Reは0〜5nmがより好ましい。また、Rthは−15〜5nmがより好ましく、−10〜0nmが更に好ましい。本発明のセルロースアシレートフィルムを液晶表示装置の偏光板の液晶セル側保護フィルムとして用いる場合に、Re及びRthが上記範囲にあると、斜め方向からの光漏れがより改良され、表示品位を向上させることができる。
式(IIIb): 30≦Re≦85
式(IVb): 80≦Rth≦300
この場合、面内の遅相軸の方位は特に限定されないが、面内でフィルムの弾性率が最大となる方位に対して略並行若しくは略直交であることが好ましく、略並行であることがより好ましい。
式(IIIc): 60≦Re≦400
式(IVc): −0.5≦Rth/Re≦0.5
この場合、面内の遅相軸の方位は特に限定されないが、面内でフィルムの弾性率が最大となる方位に対して略並行若しくは略直交であることが好ましい。
(レタデーション)
本明細書において、Re、Rth(単位;nm)は次の方法に従って求めたものである。まず、フィルムを25℃、相対湿度60%にて24時間調湿後、プリズムカップラー(MODEL2010 Prism Coupler:Metricon製)を用い、25℃、相対湿度60%において、532nmの固体レーザーを用いて下記式(2)で表される平均屈折率(n)を求める。
式(2): n=(nTE×2+nTM)/3
[式中、nTEはフィルム平面方向の偏光で測定した屈折率であり、nTMはフィルム面法線方向の偏光で測定した屈折率である。]
測定されるフィルムが一軸又は二軸の屈折率楕円体で表されるものである場合には、以下の方法によりRth(λnm)は算出される。
Rth(λnm)は前記Re(λnm)を、面内の遅相軸(KOBRA 21ADH又はWRにより判断される)を傾斜軸(回転軸)として(遅相軸がない場合にはフィルム面内の任意の方向を回転軸とする)のフィルム法線方向に対して法線方向から片側50°まで10°ステップで各々その傾斜した方向から波長λnmの光を入射させて全部で6点測定し、その測定されたレタデーション値と平均屈折率及び入力された膜厚値を基にKOBRA 21ADH又はWRが算出する。
上記において、λに関する記載が特になく、Re、Rthとのみ記載されている場合は、波長590nmの光を用いて測定した値のことを表す。また、法線方向から面内の遅相軸を回転軸として、ある傾斜角度にレタデーションの値がゼロとなる方向をもつフィルムの場合には、その傾斜角度より大きい傾斜角度でのレタデーション値はその符号を負に変更した後、KOBRA 21ADH又はWRが算出する。
なお、遅相軸を傾斜軸(回転軸)として(遅相軸がない場合にはフィルム面内の任意の方向を回転軸とする)、任意の傾斜した2方向からレタデーション値を測定し、その値と平均屈折率及び入力された膜厚値を基に、以下の式(3)及び式(4)よりRthを算出することもできる。
式(4): Rth=((nx+ny)/2−nz)×d
測定されるフィルムが一軸や二軸の屈折率楕円体で表現できないもの、いわゆる光学軸(optic axis)がないフィルムの場合には、以下の方法によりRth(λnm)は算出される。
Rth(λnm)は前記Re(λnm)を、面内の遅相軸(KOBRA 21ADH又はWRにより判断される)を傾斜軸(回転軸)としてフィルム法線方向に対して−50度から+50度まで10度ステップで各々その傾斜した方向から波長λnmの光を入射させて11点測定し、その測定されたレタデーション値と平均屈折率及び入力された膜厚値を基にKOBRA 21ADH又はWRが算出する。これら平均屈折率と膜厚を入力することで、KOBRA 21ADH又はWRはnx、ny、nzを算出する。この算出されたnx、ny、nzよりNz=(nx−nz)/(nx−ny)が更に算出される。
また、上記の測定において、平均屈折率は、ポリマーハンドブック(JOHN WILEY&SONS,INC)、各種光学フィルムのカタログの値を使用することもできる。平均屈折率の値が既知でないものについては、前述の方法で測定することができる。主な光学フィルムの平均屈折率の値を以下に例示する:セルロースアシレート(1.48)、シクロオレフィンポリマー(1.52)、ポリカーボネート(1.59)、ポリメチルメタクリレート(1.49)、ポリスチレン(1.59)である。
本発明において、Reの湿度依存性(ΔRe)及びRthの湿度依存性(ΔRth)は、相対湿度がH(単位;%)であるときの面内方向及び膜厚方向のレタデーション値:Re(H%)及びRth(H%)から、下記式に基づいて算出される。
ΔRe=Re(10%)−Re(80%)
ΔRth=Rth(10%)−Rth(80%)
Re(H%)及びRth(H%)は、フィルムを25℃、相対湿度H%にて24時間調湿後、25℃、相対湿度H%において、前記方法と同様にして、相対湿度H%における測定波長が590nmであるときのレタデーション値を測定、算出したものである。なお、相対湿度を明記せずに単にReと表記されている場合は、相対湿度60%で測定した値である。
本発明のセルロースアシレートフィルムの湿度を変化させた場合のレタデーション値は、以下の関係式を満たすことが好ましい。
|ΔRe|<30、かつ、
|ΔRth|<30
また以下の関係式を満たすことがより好ましい。
|ΔRe|<15、かつ、
|ΔRth|<15
また以下の関係式を満たすことが更に好ましい。
|ΔRe|<10、かつ、
|ΔRth|<10
また以下の関係式を満たすことが最も好ましい。
|ΔRe|<5、かつ、
|ΔRth|<5
上記湿度を変化させた場合のレタデーション値を制御することにより、外部環境が変化した場合のレタデーション変化を低下させることができ、信頼性の高い液晶表示装置を提供することができる。
また、本発明の光学フィルムのΔRthを低減させることによって、特定の条件で液晶表示装置を表示面の斜めから観察した際に視認される円形状の色ムラが改善されるという好ましい効果も得られる。ΔReやΔRthを効果的に低減させるために、湿度依存性低減剤を併用することが好ましい。湿度依存性低減剤としては、例えば、水素結合性基を有しており、かつ分子量あたりの水素結合性基密度が高い化合物を挙げることができる。水素結合性基としては、少なくとも1つの−OH基又は−NH基を含有する基であるのが好ましく、例えば、ヒドロキシル基(−OH)、カルボキシル基(−COOH)、カルバモイル基(−CONHR)、スルファモイル基(−SONHR)、ウレイド基(−NHCONHR)、アミノ基(−NHR)、ウレタン基(−NHCOOR)、アミド基(−NHCOR)がより好ましい。ただし、Rは水素原子、ヒドロキシ基、アミノ基、炭素数1〜10のアルキル基、炭素数6〜15のアリール基又はヘテロ環基を表すが、好ましくは、水素原子を表す。より好ましくは、アミノ基、ヒドロキシル基、カルボキシル基、カルバモイル基、スルファモイル基又はウレイド基であり、更に好ましくはアミノ基、ヒドロキシル基である。そしてヒドロキシル基のうち、少なくとも1つはフェノール性水酸基であることが更にまた好ましい。
本発明の光学フィルムの寸法変化率は、60℃、90%RHの条件下に24時間静置した場合(高湿)の寸法変化を初期長で除した値として測定することができ、これを低減させることによって、湿熱環境下で保持した場合のレタデーション変化を抑制できることが判明した。したがって、本発明の光学フィルムの寸法変化は3%以下であることが好ましく、0.05〜3%であることがより好ましく、0.05〜1%であることが更に好ましく、0.05〜0.5%であることがもっとも好ましい。寸法変化率を小さくすることによって、フィルムを湿熱環境下で保持した場合のレタデーション変化を抑制することができるが、この効果は寸法変化率を0.05%まで小さくすると、十分に得ることができる。
本発明の光学フィルムの寸法変化率は、具体的には下記の方法で測定することができる。まず、フィルムの弾性率が最大となる方向を長手方向として切り出した長さ25cm(測定方向)、幅5cmのフィルム試料を用意し、該試料に20cmの間隔でピン孔を空け、25℃、相対湿度60%にて24時間調湿後、ピン孔の間隔をピンゲージで測長する(測定値をL0とする)。次いで、試料を60℃、相対湿度90%の湿熱環境下で24時間保持した後、25℃、相対湿度60%にて2時間調湿後、ピン孔の間隔をピンゲージで測長する(測定値をL1とする)。これらの測定値を用いて下記式により湿度膨張係数を算出する。
寸法変化率[%]={(L1−L0)/L0}×100
なお、フィルムの寸法変化率を低減させるためには、後述のフィルムの熱処理や水蒸気接触処理が有効である。
本発明の光学フィルムには、マット剤として微粒子を加えることが好ましい。本発明に使用される微粒子としては、二酸化珪素、二酸化チタン、酸化アルミニウム、酸化ジルコニウム、炭酸カルシウム、タルク、クレイ、焼成カオリン、焼成珪酸カルシウム、水和ケイ酸カルシウム、ケイ酸アルミニウム、ケイ酸マグネシウム及びリン酸カルシウムを挙げることができる。微粒子はケイ素を含むものが濁度が低くなる点で好ましく、特に二酸化珪素が好ましい。二酸化珪素の微粒子は、1次平均粒子径が20nm以下であり、かつ見かけ比重が70g/リットル以上であるものが好ましい。1次粒子の平均径が5〜16nmと小さいものがフィルムのヘイズを下げることができより好ましい。見かけ比重は90〜200g/リットル以上が好ましく、100〜200g/リットル以上が更に好ましい。見かけ比重が大きい程、高濃度の分散液を作ることが可能になり、ヘイズ、凝集物が良化するため好ましい。
最終的なセルロースアシレートのドープ溶液中でのマット剤の添加量は1m2あたり0.01〜1.0gが好ましく、0.03〜0.3gが更に好ましく、0.08〜0.16gが最も好ましい。また、セルロースアシレートフィルムが例えば共流延のような製膜方法で多層から形成される場合、内層への添加はせず、表層側のみに添加することが好ましく、この場合は、表層のマット剤の添加量としては0.001質量%以上0.2質量%以下が好ましく、0.01質量%以上0.1質量%以下がより好ましい。
前述の繰り返し単位を有する化合物、レタデーション調整剤、マット粒子の他に、本発明の光学フィルムには、種々の添加剤(例えば、可塑剤、紫外線吸収剤、劣化防止剤、剥離剤、赤外線吸収剤、波長分散調整剤など)を加えることができ、それらは固体でもよく油状物でもよい。すなわち、その融点や沸点において特に限定されるものではない。例えば20℃以下と20℃以上の紫外線吸収材料の混合や、同様に可塑剤の混合などであり、例えば特開2001−151901号などに記載されている。更にまた、赤外吸収染料としては例えば特開2001−194522号に記載されている。またその添加する時期はドープ作製工程において何れで添加しても良いが、ドープ調製工程の最後の調製工程に添加剤を添加し調製する工程を加えて行ってもよい。更にまた、各素材の添加量は機能が発現する限りにおいて特に限定されない。また、光学フィルムが多層から形成される場合、各層の添加物の種類や添加量が異なってもよい。例えば特開2001−151902号などに記載されているが、これらは従来から知られている技術である。これらの詳細は、発明協会公開技報(公技番号2001−1745、2001年3月15日発行、発明協会)にて16頁〜22頁に詳細に記載されている素材が好ましく用いられる。
本発明の光学フィルムにおいては、前述の繰り返し単位を有する化合物に加えてこれら他の添加剤を添加する場合、添加剤の総量は、使用されるポリマーの総量に対して30質量%以上200質量%以下であることが好ましく、35質量%以上150質量%以下であることが好ましい。
(セルロースアシレート溶液の有機溶媒)
本発明では、ソルベントキャスト法によりセルロースアシレートを含むフィルムを製造することが好ましく、セルロースアシレートを含むポリマーを有機溶媒に溶解した溶液(ドープ)を用いてフィルムは製造される。本発明の主溶媒として好ましく用いられる有機溶媒は、セルロースアシレートを含むポリマーが溶解するものであれば特に限定されないが、炭素原子数が3〜12のエステル、ケトン、エーテル、及び炭素原子数が1〜7のハロゲン化炭化水素から選ばれる溶媒が好ましい。エステル、ケトン及び、エーテルは、環状構造を有していてもよい。エステル、ケトン及びエーテルの官能基(すなわち、−O−、−CO−及び−COO−)のいずれかを二つ以上有する化合物も、主溶媒として用いることができ、たとえばアルコール性水酸基のような他の官能基を有していてもよい。
本発明のセルロースアシレート溶液(ドープ)の調製は、その溶解方法は特に限定されず、室温でもよく、更には冷却溶解法あるいは高温溶解方法、更にはこれらの組み合わせで実施される。本発明におけるセルロースアシレート溶液の調製、更には溶解工程に伴う溶液濃縮、ろ過の各工程に関しては、発明協会公開技報(公技番号 2001−1745、2001年3月15日発行、発明協会)にて22頁〜25頁に詳細に記載されている製造工程が好ましく用いられる。
次に、本発明のセルロースアシレート溶液を用いたフィルムの製造方法について述べる。本発明の光学フィルムを製造する方法及び設備は、従来セルローストリアセテートフィルム製造に供する溶液流延製膜方法及び溶液流延製膜装置を用いることができる。溶解機(釜)から調製されたドープ(セルロースアシレート溶液)を貯蔵釜で一旦貯蔵し、ドープに含まれている泡を脱泡して最終調製をする。ドープをドープ排出口から、例えば回転数によって高精度に定量送液できる加圧型定量ギヤポンプを通して加圧型ダイに送り、ドープを加圧型ダイの口金(スリット)からエンドレスに走行している流延部の金属支持体の上に均一に流延され、金属支持体がほぼ一周した剥離点で、生乾きのドープ膜(ウェブとも呼ぶ)を金属支持体から剥離する。得られるウェブの両端をクリップで挟み、幅保持しながらテンターで搬送して乾燥し、続いて得られたフィルムを乾燥装置のロール群で機械的に搬送し乾燥を終了して巻き取り機でロール状に所定の長さに巻き取る。テンターとロール群の乾燥装置との組み合わせはその目的により変わる。別の態様としては、先述の金属支持体を0℃以下に冷却したドラムとし、ドラム上にダイから流延したドープをゲル化してから約1周した時点で剥ぎ取り、ピン状のテンターで延伸しながら搬送し、乾燥する方法など、ソルベントキャスト法で製膜する様々な方法をとることが可能である。
本発明の光学フィルムの主な用途である、電子ディスプレイ用の光学部材である機能性偏光板保護フィルムやハロゲン化銀写真感光材料に用いる溶液流延製膜方法においては、溶液流延製膜装置の他に、下引層、帯電防止層、ハレーション防止層、保護層等のフィルムへの表面加工のために、塗布装置が付加されることが多い。これらについては、発明協会公開技報(公技番号 2001−1745、2001年3月15日発行、発明協会)にて25頁〜30頁に詳細に記載されており、流延(共流延を含む),金属支持体,乾燥,剥離などに分類され、本発明において好ましく用いることができる。
本発明の光学フィルムの製造方法においては、必要に応じて、前記光学フィルムを、更に熱処理する工程を適用することもできる。熱処理工程の効果は特に限定されることはないが、光学フィルムが熱エネルギーを得るため、セルロースアシレート分子の高次構造がより安定な構造に遷移しやすくなる結果、フィルムの寸法変化率や、フィルムを湿熱環境下で保持した場合のレタデーション変化を、抑制することができると考えられる。熱処理工程においては、フィルムの種類に応じて温度と張力を適切に制御することが重要であり、温度は後述の示差走査型熱量計を用いて測定したガラス転移温度より高いほうが短時間の熱処理で実施できるため好ましく、張力は低いほうが熱処理工程で期待される効果を十分に得ることができるため好ましい。
本発明の光学フィルムの製造方法においては、必要に応じて、前記光学フィルムに、更に後述の接触気体を接触させる状態を維持する工程(水蒸気接触工程)を適用することもできる。水蒸気接触工程の効果は限定されることはないが、フィルムの寸法変化率や、フィルムを湿熱環境下で保持した場合のレタデーション変化を、短時間の処理で抑制することができる。いかなる理論に拘泥するものでもないが、このことは、光学フィルムに後述の接触気体を接触させると、光学フィルムが接触気体の分子を吸収し、フィルムのガラス転移温度が減少することになり、熱エネルギーを得るため、セルロースアシレートを含む光学フィルムにおける接触気体の分子の拡散が促進され、そのことにより、セルロースアシレート分子の高次構造がより安定な構造に遷移しやすくなる結果、単なる熱処理に比べ、セルロースアシレート分子の構造安定化を短時間で行うことができることに起因すると考えられる。なお、水蒸気接触工程は本発明の製造方法において任意の場所で実施することができるが、前述の延伸工程又は熱処理工程や、後述の有機溶媒接触工程の終了した後に実施されることが好ましく、前述の延伸工程又は熱処理工程又は有機溶媒接触工程の後に実施されることがより好ましく、前述の延伸工程又は熱処理工程の後に実施されることが更に好ましい。また、水蒸気接触工程の前や後に、適宜、後述の表面処理を併用してもよい。以下において、セルロースアシレートフィルムに水蒸気を含む気体を接触させる状態を維持する工程(水蒸気接触工程)について説明する。
水蒸気接触工程における光学フィルムに接触される気体(接触気体)としては、液体状態の溶媒を気体状態にした気体であれば特に限定されることはないが、水蒸気を含む気体であることが好ましく、水蒸気を主たる成分として含む気体であることがより好ましく、水蒸気であることが更に好ましい。ここで、主たる成分として含む気体とは、単一の気体からなる場合には、その気体のことを示し、複数の気体からなる場合には、構成する気体のうち、最も質量分率の高い気体のことを示す。
前記接触気体は、湿潤気体供給装置によって生成される気体であることが好ましい。具体的には、液体状態の溶媒をボイラで加熱して気体状態とした後、ブロアによって送られるものであり、接触気体には、適宜空気を混合させてもよく、ブロアによって送られた後に加熱装置を経由させて更に加熱してもよい。ここで、該空気は加熱されたものであることが好ましい。このようにして生成された接触気体の温度は、70〜200℃であることが好ましく、80〜160℃であることがより好ましく、100〜140℃であることが最も好ましい。上限温度よりも高いとフィルムのカールが強くなり、好ましくなく、下限温度よりも低いと十分な効果が得られないことがある。接触気体が水を含む場合には、その相対湿度は、20〜100%であることが好ましく、40〜100%であることがより好ましく、60〜100%であることが特に好ましい。
前記液体状態の溶媒は、水や有機溶媒や無機溶媒を含む溶媒を示す。水を用いる場合には、軟水、硬水や純水などを用いることができ、ボイラの保護の観点から軟水を用いることが好ましい。光学フィルムへの異物混入は、製品としての光学フィルムの光学特性や機械特性の劣化の原因となるため、できるだけ異物の少ない水を用いることが好ましい。したがって、光学フィルムへの異物混入を防ぐためには、軟水や純水を用いることが好ましく、純水を用いることがより好ましい。ここで、純水とは、電気抵抗率が少なくとも1MΩ以上であり、特にナトリウム、カリウム、マグネシウム、カルシウムなどの金属イオンの含有濃度は1ppm未満、塩素、硝酸などのアニオンは0.1ppm未満の含有濃度を指す。純水は、逆浸透膜、イオン交換樹脂、蒸留などの単体、あるいは組み合わせによって、容易に得ることができる。有機溶媒を用いる場合には、メタノール、アセトンやメチルエチルケトンなどが挙げられる。なお、前記液体状態の溶媒は、接触気体を回収した回収気体を凝縮して得られた凝縮液を含んでいてもよい。
水蒸気接触工程における光学フィルムと前述の接触気体との接触方法としては、前記接触気体を光学フィルムに当てる方法、接触気体で満たされた空間に光学フィルムを配置する方法、又は接触気体で満たされた空間を通過させる方法を用いることができ、接触気体を光学フィルムに当てる方法、又は接触気体で満たされた空間を通過させる方法が好ましい。また、光学フィルムと接触気体との接触は、光学フィルムを千鳥状に配置された複数のローラで案内しながら実施されることが好ましい。
接触気体との接触時間は、特に限定されないが、本発明の効果が発揮される範囲内であれば、生産効率の点から出来るだけ短いほうが好ましい。処理時間の上限値として、例えば、60分以下であることが好ましく、10分以下であることがより好ましい。一方、処理時間の下限値として、例えば、10秒以上であることが好ましく、30秒以上であることがより好ましい。
接触気体との接触するときの光学フィルムの温度は特に限定されないが、50〜150℃であることが好ましい。
また、前記水蒸気接触前の光学フィルムの残留溶媒量は特に限定されないが、セルロースアシレート分子の流動性がほとんど消失していることが好ましく、0〜5質量%であることが好ましく、0〜0.3質量%であることがより好ましい。
光学フィルムと接触した接触気体は、冷却装置が接続された凝縮装置に送られ、加熱気体と凝縮液とに分けられてもよい。
このようにして接触気体と接触した光学フィルムは、そのまま略室温まで冷却してもよいし、フィルム中に残存した接触気体分子の量を調整するために、続いて乾燥ゾーンへ搬送してもよい。乾燥ゾーンへ搬送する場合、前述の有機溶媒接触工程における乾燥工程の記載と同様の乾燥方法を好ましく用いることができる。なお、水蒸気接触工程が前記延伸工程や熱処理工程や、後述の有機溶媒接触工程の前に実施される場合には、それらの工程を乾燥工程とすることもできる。
本発明の光学フィルムの製造方法においては、場合により、光学フィルム表面に有機溶媒を接触させた後、該有機溶媒を乾燥させることにより、光学フィルムの密着層を形成させることもできる。したがって、光学フィルムの片面だけに有機溶媒を接触させた場合、該光学フィルムを偏光膜と直接貼合する場合には、有機溶媒に接触させた面を偏光膜との貼合面とすることが好ましい。有機溶媒接触工程における光学フィルムと有機溶媒との接触方法としては、一般的に知られた接触方法、例えばディップコート法、エアーナイフコート法、カーテンコート法、ローラーコート法、ワイヤーバーコート法、グラビアコート法、スライドコート法、スプレー法、ダイコート法、或いは、米国特許第2681294号明細書に記載のホッパーを使用するエクストルージョンコート法、マイクログラビアコート法を用いることができる。また、前記水蒸気接触工程における主溶媒である水の代わりに有機溶媒を用いることにより、接触させることもできる。この際、密着層を効果的に形成させるために、光学フィルムに接触させる有機溶媒の濃度は、有機溶媒接触前の光学フィルム中の溶媒濃度よりも高濃度であることが好ましい。
本発明の、光学フィルムの厚さは20〜120μmが好ましく、30〜90μmが更に好ましく、35〜80μmが特に好ましい。また、液晶パネルに貼合する偏光子保護フィルムとして用いる場合は、光ムラを改良する上で、30〜80μmが好ましく、35〜65μmがより好ましく、35〜45μmであることが特に好ましい。更に、この範囲にあると温湿度変化に伴うパネルの反りが小さくすることができる。
光学フィルムとしてフィルムの透明性は重要であり、本発明の光学フィルムのヘイズは、小さいほうが好ましく、0.01〜2.0%であることが好ましい。より好ましくは1.0%以下、更に好ましくは0.5%以下である。ヘイズの測定は、本発明の光学フィルム試料40mm×80mmを、25℃,60%RHでヘイズメーター(HGM−2DP、スガ試験機)などを用いて、JIS K−6714に従って測定することができる。
光学フィルムの試料13mm×40mmを、25℃、60%RHで分光光度計“U−3210”{(株)日立製作所}にて、波長300〜450nmにおける透過率を測定することができる。傾斜幅は72%の波長−5%の波長で求めることができる。限界波長は、(傾斜幅/2)+5%の波長で表し、吸収端は、透過率0.4%の波長で表すことができる。これより380nm及び350nmの透過率を評価することができる。
本発明の光学フィルムは、偏光板の液晶セルに面した保護フィルムの対向側に用いる場合には、上記方法により測定した波長380nmにおける分光透過率が45%以上95%以下であり、かつ波長350nmにおける分光透過率が10%以下であることが好ましい。
ガラス転移温度は、示差走査型熱量計(DSC)を用いて昇温速度10℃/分で測定したときにフィルムのガラス転移に由来するベースラインが変化しはじめる温度と再びベースラインに戻る温度との平均値として求めることができる。
また、ガラス転移温度の測定は、以下の動的粘弾性測定装置を用いて求めることもできる。本発明のセルロースアシレートフィルム試料(未延伸)5mm×30mmを、25℃60%RHで2時間以上調湿した後に動的粘弾性測定装置(バイブロン:DVA−225(アイティー計測制御(株)製))で、つかみ間距離20mm、昇温速度2℃/分、測定温度範囲30℃〜250℃、周波数1Hzで測定し、縦軸に対数軸で貯蔵弾性率、横軸に線形軸で温度(℃)をとった時に、貯蔵弾性率が固体領域からガラス転移領域へ移行する際に見受けられる貯蔵弾性率の急激な減少を固体領域で直線1を引き、ガラス転移領域で直線2を引いたときの直線1と直線2の交点を、昇温時に貯蔵弾性率が急激に減少しフィルムが軟化し始める温度であり、ガラス転移領域に移行し始める温度であるため、ガラス転移温度Tg(動的粘弾性)とする。
本発明の光学フィルムの含水率(平衡含水率)は、偏光板の保護フィルムとして用いる際、ポリビニルアルコールなどの水溶性ポリマーとの接着性を損なわないために、膜厚のいかんに関わらず、25℃、80%RHにおける含水率が、0〜4質量%であることが好ましい。0.1〜3.5質量%であることがより好ましく、1〜3質量%であることが特に好ましい。平衡含水率が4質量%以下であれば、位相差フィルムの支持体として用いる際に、レタデーションの湿度変化による依存性が大きくなりすぎることがなく好ましい。
含水率の測定法は、本発明の光学フィルム試料7mm×35mmを水分測定器、試料乾燥装置“CA−03”及び“VA−05”{共に三菱化学(株)製}にてカールフィッシャー法で測定した。水分量(g)を試料質量(g)で除して算出した。
フィルムの透湿度は、JIS Z−0208をもとに、60℃、95%RHの条件において測定される。本発明の光学フィルムの透湿度は、400〜5000g/m2・24hであることが好ましい。400〜4000g/m2・24hであることがより好ましく、400〜3500g/m2・24hであることが特に好ましい。透湿度がこの範囲であれば、偏光板加工性と、湿度若しくは湿熱に対する偏光板の耐久性とを両立することができ、好ましい。
本発明の光学フィルムの引っ張り弾性率は、3.0GPa未満であることが好ましく、より好ましくは1.0〜3.0GPaであり、更に好ましくは1.2〜2.8GPaである。具体的な測定方法としては、東洋ボールドウィン(株)製万能引っ張り試験機“STM T50BP”を用い、25℃、60RH%雰囲気中、引張速度10%/分で0.1%伸びと0.5%伸びにおける応力を測定し、その傾きから弾性率を求めた。弾性率の測定において、サンプルを切り出す方位を変化させることによって、弾性率の異方性を求めることができ、製造時の搬送方向と弾性率が最大となる方位とがなす角θは、特に限定されることはないが、0±10°若しくは90±10°であることが好ましい。なお、弾性率が最大となる方位は、後述の音波伝播速度が最大となる方向として評価することもできる。
本発明において音波伝播速度が最大となる方向は、フィルムを25℃、相対湿度60%にて24時間調湿後、配向性測定機(SST−2500:野村商事(株)製)を用いて、超音波パルスの縦波振動の伝搬速度が最大となる方向として求めた。
本発明の光学フィルムを偏光板保護フィルムとして使用した場合には、偏光子の収縮による応力などにより複屈折(Re、Rth)が変化する場合がある。このような応力に伴う複屈折の変化は光弾性係数として測定できるが、その範囲は、15×1012Pa−1以下(15Br以下)であることが好ましく、−5×1012Pa−1〜12×1012Pa−1であることがより好ましく、−2×1012Pa−1〜11×1012Pa−1であることが更に好ましい。
本発明の光学フィルムはセルロースアシレートを含むため、偏光板保護フィルムとして用いる場合の表面処理の有効な手段の1つとしてアルカリ鹸化処理が挙げられる。この場合、アルカリ鹸化処理後のフィルム表面の接触角が55°以下であることが好ましい。より好ましくは50°以下であり、45°以下であることが更に好ましい。
光学フィルムは、場合により表面処理を行うことによって、光学フィルムと各機能層(例えば、下塗層及びバック層)との接着の向上を達成することができる。例えばグロー放電処理、紫外線照射処理、コロナ処理、火炎処理、酸又はアルカリ処理を用いることができる。ここでいうグロー放電処理とは、10−3〜20Torrの低圧ガス下でおこる低温プラズマでもよく、更にまた大気圧下でのプラズマ処理も好ましい。プラズマ励起性気体とは上記のような条件においてプラズマ励起される気体をいい、アルゴン、ヘリウム、ネオン、クリプトン、キセノン、窒素、二酸化炭素、テトラフルオロメタンの様なフロン類及びそれらの混合物などがあげられる。これらについては、詳細が発明協会公開技報(公技番号 2001−1745、2001年3月15日発行、発明協会)にて30頁〜32頁に詳細に記載されており、本発明において好ましく用いることができる。
本発明の光学フィルムは、その用途として、例えば、光学用途と写真感光材料に適用される。特に光学用途が液晶表示装置であることが好ましく、液晶表示装置が、二枚の電極基板の間に液晶を担持してなる液晶セル、その両側に配置された二枚の偏光素子、及び該液晶セルと該偏光素子との間に少なくとも一枚の光学補償シートを配置した構成であることが更に好ましい。これらの液晶表示装置としては、TN、IPS、FLC、AFLC、OCB、STN、ECB、VA及びHANが好ましい。
その際に前述の光学用途に本発明の光学フィルムを用いるに際し、各種の機能層を付与することが実施される。それらは、例えば、帯電防止層、硬化樹脂層(透明ハードコート層)、反射防止層、易接着層、防眩層、光学補償層、配向層、液晶層などである。これらの機能層及びその材料としては、界面活性剤、滑り剤、マット剤、帯電防止層、ハードコート層などが挙げられ、発明協会公開技報(公技番号 2001−1745、2001年3月15日発行、発明協会)にて32頁〜45頁に詳細に記載されており、本発明において好ましく用いることができる。
本発明の位相差フィルムは本発明の光学フィルムを少なくとも一枚含有する。
また、本発明の光学フィルムは、位相差フィルムとして用いることができる。なお、「位相差フィルム」とは、一般に液晶表示装置等の表示装置に用いられ、光学異方性を有する光学材料のことを意味し、位相差板、光学補償フィルム、光学補償シートなどと同義である。液晶表示装置において、位相差フィルムは表示画面のコントラストを向上させたり、視野角特性や色味を改善したりする目的で用いられる。
本発明の光学フィルムを用いることで、レタデーションが自在に制御され、偏光膜との密着性に優れた位相差フィルムを作製することができる。
前記液晶性化合物としては、ディスコティック液晶性化合物又は棒状液晶性化合物が好ましい。
本発明において前記液晶性化合物として使用可能なディスコティック液晶性化合物の例には、様々な文献(例えば、C.Destrade et al.,Mol.Crysr.Liq.Cryst.,vol.71,page 111(1981);日本化学会編、季刊化学総説、No.22、液晶の化学、第5章、第10章第2節(1994);B.Kohne et al.,Angew.Chem.Soc.Chem.Comm.,page 1794(1985);J.Zhang etal.,J.Am.Chem.Soc.,vol.116,page 2655(1994))に記載の化合物が含まれる。
本発明において前記液晶性化合物として使用可能な棒状液晶性化合物の例には、アゾメチン類、アゾキシ類、シアノビフェニル類、シアノフェニルエステル類、安息香酸エステル類、シクロヘキサンカルボン酸フェニルエステル類、シアノフェニルシクロヘキサン類、シアノ置換フェニルピリミジン類、アルコキシ置換フェニルピリミジン類、フェニルジオキサン類、トラン類及びアルケニルシクロヘキシルベンゾニトリル類が含まれる。また、前記棒状液晶性化合物としては、以上のような低分子液晶性化合物だけではなく、高分子液晶性化合物も用いることができる。
本発明の偏光板は、本発明の光学フィルム又は本発明の位相差フィルムを少なくとも一枚含有する。
本発明の光学フィルム又は位相差フィルムは、偏光板(本発明の偏光板)の保護フィルムとして用いることができる。本発明の偏光板は、偏光膜とその両面を保護する二枚の偏光板保護フィルム(光学フィルム)からなり、本発明の光学フィルム又は位相差フィルムは少なくとも一方の偏光板保護フィルムとして用いることが特に好ましい。
本発明の光学フィルムを前記偏光板保護フィルムとして用いる場合、本発明の光学フィルムには前記表面処理(特開平6−94915号公報、同6−118232号公報にも記載)を施して親水化しておくことが好ましく、例えば、グロー放電処理、コロナ放電処理、又は、アルカリ鹸化処理などを施すことが好ましい。前記表面処理としてはアルカリ鹸化処理が最も好ましく用いられる。
偏光板は偏光子及びその両面を保護する保護フィルムで構成されており、更に該偏光板の一方の面にプロテクトフィルムを、反対面にセパレートフィルムを貼合して構成される。プロテクトフィルム及びセパレートフィルムは偏光板出荷時、製品検査時等において偏光板を保護する目的で用いられる。この場合、プロテクトフィルムは、偏光板の表面を保護する目的で貼合され、偏光板を液晶板へ貼合する面の反対面側に用いられる。又、セパレートフィルムは液晶板へ貼合する接着層をカバーする目的で用いられ、偏光板を液晶板へ貼合する面側に用いられる。
液晶表示装置には通常2枚の偏光板の間に液晶を含む基板が配置されているが、本発明の光学フィルムを適用した偏光板保護フィルムはどの部位に配置しても優れた表示性が得られる。特に液晶表示装置の表示側最表面の偏光板保護フィルムには透明ハードコート層、防眩層、反射防止層等が設けられるため、該偏光板保護フィルムをこの部分に用いることが特に好ましい。
本発明の光学フィルム、位相差フィルム及び偏光板は、様々な表示モードの液晶表示装置に用いることができる。以下にこれらのフィルムが用いられる各液晶モードについて説明する。これらのモードのうち、本発明の光学フィルム、位相差フィルム及び偏光板は、全てのモードにおいて好ましく用いることができるが、特にVAモード及びIPSモードの液晶表示装置に好ましく用いられる。これらの液晶表示装置は、透過型、反射型及び半透過型のいずれでもよい。
本発明の光学フィルムは、TNモードの液晶セルを有するTN型液晶表示装置の位相差フィルムの支持体として好ましく用いられる。TNモードの液晶セルとTN型液晶表示装置とについては、古くからよく知られている。TN型液晶表示装置に用いる位相差フィルムについては、特開平3−9325号、特開平6−148429号、特開平8−50206号及び特開平9−26572号の各公報の他、モリ(Mori)他の論文(Jpn.J.Appl.Phys.Vol.36(1997)p.143や、Jpn.J.Appl.Phys.Vol.36(1997)p.1068)に記載がある。
本発明の光学フィルムは、STNモードの液晶セルを有するSTN型液晶表示装置の位相差フィルムの支持体として用いてもよい。一般的にSTN型液晶表示装置では、液晶セル中の棒状液晶性分子が90〜360度の範囲にねじられており、棒状液晶性分子の屈折率異方性(Δn)とセルギャップ(d)との積(Δnd)が300〜1500nmの範囲にある。STN型液晶表示装置に用いる位相差フィルムについては、特開2000−105316号公報に記載がある。
本発明の光学フィルムは、VAモードの液晶セルを有するVA型液晶表示装置の位相差フィルムや位相差フィルムの支持体として特に有利に用いられる。VA型液晶表示装置は、例えば特開平10−123576号公報に記載されているような配向分割された方式であっても構わない。これらの態様において本発明の光学フィルムを用いた偏光板は視野角拡大、コントラストの良化に寄与する。
本発明の光学フィルムは、IPSモード及びECBモードの液晶セルを有するIPS型液晶表示装置及びECB型液晶表示装置の位相差フィルムや位相差フィルムの支持体、又は偏光板の保護フィルムとして特に有利に用いられる。これらのモードは黒表示時に液晶材料が略平行に配向する態様であり、電圧無印加状態で液晶分子を基板面に対して平行配向させて、黒表示する。これらの態様において本発明の光学フィルムを用いた偏光板は視野角拡大、コントラストの良化に寄与する。
また、|Rth|<25が好ましいが、更に450〜650nmの領域において、Rthが0nm以下であることが、色味の変化が小さく、特に好ましい。
本発明の光学フィルムは、OCBモードの液晶セルを有するOCB型液晶表示装置或いはHANモードの液晶セルを有するHAN型液晶表示装置の位相差フィルムの支持体としても有利に用いられる。OCB型液晶表示装置或いはHAN型液晶表示装置に用いる位相差フィルムには、レタデーションの絶対値が最小となる方向が位相差フィルムの面内にも法線方向にも存在しないことが好ましい。OCB型液晶表示装置或いはHAN型液晶表示装置に用いる位相差フィルムの光学的性質も、光学的異方性層の光学的性質、支持体の光学的性質及び光学的異方性層と支持体との配置により決定される。OCB型液晶表示装置或いはHAN型液晶表示装置に用いる位相差フィルムについては、特開平9−197397号公報に記載がある。また、モリ(Mori)他の論文(Jpn.J.Appl.Phys.Vol.38(1999)p.2837)に記載がある。
本発明の光学フィルムは、TN型、STN型、HAN型、GH(Guest−Host)型の反射型液晶表示装置の位相差フィルムとしても有利に用いられる。これらの表示モードは古くからよく知られている。TN型反射型液晶表示装置については、特開平10−123478号、国際公開第98/48320号パンフレット、特許第3022477号公報に記載がある。反射型液晶表示装置に用いる位相差フィルムについては、国際公開第00/65384号パンフレットに記載がある。
本発明の光学フィルムは、ASM(Axially Symmetric Aligned Microcell)モードの液晶セルを有するASM型液晶表示装置の位相差フィルムの支持体としても有利に用いられる。ASMモードの液晶セルは、セルの厚さが位置調整可能な樹脂スペーサーにより維持されているとの特徴がある。その他の性質は、TNモードの液晶セルと同様である。ASMモードの液晶セルとASM型液晶表示装置とについては、クメ(Kume)他の論文(Kume et al.,SID 98 Digest 1089(1998))に記載がある。
更に、本発明の光学フィルムは、3D立体映像表示を表示することができる映像表示パネルで好ましく用いられる位相差フィルムや、位相差フィルムの支持体として用いることもできる。具体的には、本発明の光学フィルムの全面にλ/4層を形成させたり、例えばライン状に交互に複屈折率が異なるパターン化された位相差層を形成させたりすることができる。本発明の光学フィルムは、従来のセルロースアシレートフィルムと比較して、湿度変化に対する寸法変化率が小さいため、特に後者において好ましく用いることができる。
本発明の光学フィルムは、ハードコートフィルム、防眩フィルム、反射防止フィルムへ適用することができる。LCD、PDP、CRT、EL等のフラットパネルディスプレイの視認性を向上する目的で、本発明の光学フィルムの片面又は両面にハードコート層、防眩層、反射防止層の何れかあるいは全てを付与することができる。このような防眩フィルム、反射防止フィルムとしての望ましい実施態様は、発明協会公開技報(公技番号2001−1745、2001年3月15日発行、発明協会)の54頁〜57頁に詳細に記載されており、本発明の光学フィルムを好ましく用いることができる。
本発明の光学フィルムは光学的異方性をゼロに近く作ることができ、優れた透明性を持っており、かつ湿熱環境下で保持してもレタデーション変化が小さいことから、液晶表示装置の液晶セルガラス基板の代替、すなわち駆動液晶を封入する透明基板としても用いることもできる。
液晶を封入する透明基板はガスバリア性に優れる必要があることから、必要に応じて本発明の光学フィルムの表面にガスバリアー層を設けてもよい。ガスバリアー層の形態や材質は特に限定されないが、本発明の光学フィルムの少なくとも片面にSiO2等を蒸着したり、あるいは塩化ビニリデン系ポリマーやビニルアルコール系ポリマーなど相対的にガスバリアー性の高いポリマーのコート層を設けたり、これら無機層と有機層とを積層する方法が考えられ、これらを適宜使用できる。
また液晶を封入する透明基板として用いるには、電圧印加によって液晶を駆動するための透明電極を設けてもよい。透明電極としては特に限定されないが、本発明の光学フィルムの少なくとも片面に、金属膜、金属酸化物膜などを積層することによって透明電極を設けることができる。中でも透明性、導電性、機械的特性の点から、金属酸化物膜が好ましく、なかでも酸化スズを主として酸化亜鉛を2〜15%含む酸化インジウムの薄膜が好ましく使用できる。これら技術の詳細は例えば、特開2001−125079や特開2000−227603などに公開されている。
まず、特性の測定法及び評価法を以下に示す。
セルロースアシレートのアシル置換度は、Carbohydr.Res.273(1995)83−91(手塚他)に記載の方法で13C−NMRにより求めた。
フィルムの幅方向5点(フィルムの中央部、端部(両端からそれぞれ全幅の5%の位置)、及び中央部と端部の中間部2点)とを長手方向に100mごとにサンプリングし、5cm□の大きさのサンプルを取り出し、前述の方法に従って評価した各点の平均値を算出し、それぞれRe、Rth、ΔRe、ΔRthを求めた。
レタデーション測定時と同じサンプリングを実施し、サンプルを25℃、相対湿度60%にて24時間調湿後、ヘイズメーター(NDH 2000:日本電色工業(株)製)を用いて測定し、平均値をヘイズとした。
作製したセルロースアシレートフィルムから1cm×5cmのサンプルを切り出し、分光エリプソメーター(M−220、日本分光株式会社製)を用いて、サンプルに25℃で応力をかけながら、フィルム面内のレタデーション値を測定し、レタデーション値と応力の関数の傾きから算出した。
東洋ボールドウィン(株)製万能引っ張り試験機“STM T50BP”を用い、25℃、60RH%雰囲気中、引張速度10%/分で0.1%伸びと0.5%伸びにおける応力を測定し、その傾きから弾性率を求めた。
作製したセルロースアシレートフィルムから7mm×35mmのサンプルを切り出し、25℃、相対湿度60%にて24時間調湿後、水分測定器、試料乾燥装置“CA−03”及び“VA−05”{共に三菱化学(株)製}にてカールフィッシャー法で含水率を測定した。
作製した2枚の偏光板を吸収軸を平行に重ね合わせた場合の透過率(Tp)及び吸収軸を直交させて重ね合わせた場合の透過率(Tc’)を測定し、下記式から偏光度(P)を算出した。
偏光度P = ((Tp−Tc’)/(Tp+Tc’))0.5
(ポリマー溶液の調製)
1〕セルロースアシレート
下記のセルロースアシレートAを使用した。各セルロースアシレートは120℃に加熱して乾燥し、含水率を0.5質量%以下とした後、20質量部を使用した。
置換度が2.86のセルロースアセテートの粉体を用いた。セルロースアシレートAの粘度平均重合度は300、6位のアセチル基置換度は0.89、アセトン抽出分は7質量%、質量平均分子量/数平均分子量比は2.3、含水率は0.2質量%、6質量%ジクロロメタン溶液中の粘度は305mPa・s、残存酢酸量は0.1質量%以下、Ca含有量は65ppm、Mg含有量は26ppm、鉄含有量は0.8ppm、硫酸イオン含有量は18ppm、イエローインデックスは1.9、遊離酢酸量は47ppmであった。粉体の平均粒子サイズは1.5mm、標準偏差は0.5mmであった。
下記の溶媒Aを使用した。各溶媒の含水率は0.2質量%以下であった。
・溶媒A ジクロロメタン/メタノール/ブタノール/水=81.0/17.5/1.0/0.5(質量比)
下記の添加剤群の中から表1に記載されるものを選択し、加えて下記の添加剤Mを使用した。但し、表1中、量は、セルロースアシレートを100質量%としたときの質量%を表す。
(繰り返し単位を有する化合物)
・A−1: エタンジオール/アジピン酸(1/1モル比)との縮合物、数平均分子量1000、水酸基価112
・A−2: エタンジオール/アジピン酸(1/1モル比)との縮合物、数平均分子量550、水酸基価187
・A−3: エタンジオール/アジピン酸(1/1モル比)との縮合物の両末端のメチルエステル体、数平均分子量1000、水酸基価0
・A−4: 1,3−プロパンジオール/アジピン酸(1/1モル比)との縮合物の両末端のメチルエステル体、数平均分子量1000、水酸基価0
・A−5: エタンジオール/1,3−プロパンジオール/アジピン酸(1/1/2モル比)との縮合物の両末端のメチルエステル体、数平均分子量1000、水酸基価0
・A:下記構造の化合物
・M:
二酸化ケイ素微粒子(粒子サイズ20nm、モース硬度約7)(0.02質量部)
下記の溶解工程Aを使用して膨潤、溶解を行った。
・溶解工程A
攪拌羽根を有し外周を冷却水が循環する400リットルのステンレス製溶解タンクに、前記溶媒及び添加剤を投入して撹拌、分散させながら、前記セルロースアシレートを徐々に添加した。投入完了後、室温にて2時間撹拌し、3時間膨潤させた後に再度撹拌を実施し、セルロースアシレート溶液を得た。
なお、攪拌には、15m/sec(剪断応力5×104kgf/m/sec2〔4.9×105N/m/sec2〕)の周速で攪拌するディゾルバータイプの偏芯攪拌軸及び中心軸にアンカー翼を有して周速1m/sec(剪断応力1×104kgf/m/sec2〔9.8×104N/m/sec2〕)で攪拌する攪拌軸を用いた。膨潤は、高速攪拌軸を停止し、アンカー翼を有する攪拌軸の周速を0.5m/secとして実施した。
膨潤した溶液をタンクから、ジャケット付配管で50℃まで加熱し、更に2MPaの加圧化で90℃まで加熱し、完全溶解した。加熱時間は15分であった。この際、高温にさらされるフィルター、ハウジング、及び配管はハステロイ合金製で耐食性の優れたものを利用し保温加熱用の熱媒を流通させるジャケットを有する物を使用した。
次に36℃まで温度を下げ、セルロースアシレート溶液を得た。
得られたセルロースアシレート溶液を、絶対濾過精度10μmの濾紙(#63、東洋濾紙(株)製)で濾過し、更に絶対濾過精度2.5μmの金属焼結フィルター(FH025、ポール社製)にて濾過してポリマー溶液を得た。
下記の製膜工程A−1又はA−2から表1に記載されるものを使用した。これらの製膜工程により製造されたセルロースアシレートフィルムの残留溶媒量は、全て0.3質量%以下であった。
前記ポリマー溶液を30℃に加温し、流延ギーサーを通して直径3mのドラムである鏡面ステンレス支持体上に流延した。支持体の温度は−7℃に設定し、流延スピードは50m/分、塗布幅は200cmとした。流延部全体の空間温度は、10℃に設定した。そして、流延部の終点部から50cm手前で、流延して回転してきたセルロースアシレートフィルムをドラムから剥ぎ取り、両端をピンテンターでクリップした。なお、下記式に基づいて算出した、剥ぎ取った直後のウェブの残留溶媒量は300質量%であった。
残留溶媒量(質量%)={(M−N)/N}×100
[式中、Mは、延伸ゾーンに挿入される直前のセルロースアシレートフィルムの質量、Nは、延伸ゾーンに挿入される直前のセルロースアシレートフィルムを110℃で3時間乾燥させたときの質量を表す]
続けて、ピンテンターで保持されたセルロースアシレートフィルムは、100℃で5分間乾燥した後、ピンテンターから外して両耳を切り落とし、更に70℃で15分ロール搬送しながら乾燥して、セルロースアシレートフィルムを得た。
前述の製膜工程A−1で乾燥の終了したセルロースアシレートフィルムを、更にロール搬送しながら85℃に予熱した後、フィルムの搬送張力を60N/mに設定して、85℃・相対湿度85%に調節された水蒸気に1分間接触させ、続いて70℃の乾燥ゾーンで2分間乾燥した後、3900m巻きのロール状に巻き取って、セルロースアシレートフィルムを得た。
(偏光板の作製)
1〕フィルムの鹸化
実施例及び比較例で作成した各フィルム及びフジタックTD60UL(富士フイルム(株)製)を45℃に調温した1.5mol/Lの水酸化ナトリウム水溶液(けん化液)に2分間浸漬した後、フィルムを水洗し、その後、0.1mol/Lの硫酸水溶液に35秒浸漬した後、更に水洗浴を通した。そして、エアナイフによる水切りを3回繰り返し、水を落とした後に80℃の乾燥ゾーンに15秒間滞留させて乾燥し、鹸化処理したフィルムを作製した。
特開2001−141926号公報の実施例1に従い、2対のニップロール間に周速差を与え、長手方向に延伸し、厚み20μmの偏光膜を調製した。
このようにして得た偏光膜と、前記鹸化処理したフィルムのうちから2枚選び、これらで前記偏光膜を挟んだ後、PVA((株)クラレ製、PVA−117H)3%水溶液を接着剤として、偏光軸とフィルムの長手方向とが直交するようにロールツーロールで貼り合わせて偏光板を作成した。ここで、偏光膜の一方のフィルムは、表1記載のフィルム群から選択される1枚を鹸化したフィルムとし、他方のフィルムはフジタックTD60ULを鹸化したフィルムとした。
前記偏光板の偏光度を前述した方法で算出したところ、全ての偏光板の偏光度が99.9%であった。
前記偏光板のフィルムA側を粘着剤でガラス板に貼り合わせ、60℃・相対湿度90%の条件で500時間放置し、放置後の偏光度(経時偏光度)を前述の方法で算出したところ、全ての偏光板の偏光度が99.9%であった。
前記偏光板のうち、表1記載のフィルム側に粘着剤を転写させた上でガラス板に貼合し、これを80℃、相対湿度90%の条件で144時間放置した。そして、得られた偏光板からフジタックTD60UL及び前記偏光膜を剥がし、ガラス板に残ったフィルムが透明であることを目視確認した上で、前述の方法に準じてレタデーション測定を行い、下記式にしたがって算出されるRth耐久性を算出し、表1に記載した。
Rth耐久性=(ガラス板に残ったフィルムのRth)−(製膜直後のフィルムのRth)
(IPS型液晶表示装置への実装)
市販の液晶テレビ(IPSモードのスリム型42型液晶テレビ)から、液晶セルを挟んでいる偏光板を剥がし取り、前記作製した偏光板を、表1記載のフィルム側が液晶セル側に配置されるように、粘着剤を介して液晶セルに再貼合した。組みなおした液晶テレビを、40℃・相対湿度80%の環境で1週間保持した後に、25℃・相対湿度60%の環境に移し、黒表示状態で点灯させ続け、24時間後に目視観察して、光ムラを評価した。評価結果を表1に示す。
(正面方向の光ムラレベル)
装置正面から観察した場合の黒表示時の輝度ムラを観察し、以下の基準で評価した。
○ : 照度100lxの環境下でムラがほとんど視認されない
△ : 照度100lxの環境下で淡いムラが視認される
× : 照度100lxの環境下で明確なムラが視認される
××: 照度300lxの環境下で明確なムラが視認される
表1記載のフィルム1〜13は全てヘイズ値が0.5%以下の透明性に優れるフィルムであり、光学フィルムとして好ましく用いられるものであった。そして、表1に示されるように、本発明の如く、繰り返し単位を有する化合物をセルロースエステルに対し30質量%以上含む光学フィルムを用いた偏光板を組み込んだ液晶表示装置は光漏れの改善が十分であった。更に、この偏光板を湿熱環境下で保持した場合のRth変化は、レタデーションの耐久性を向上させる化合物を添加することによって大幅に低減することができ、更に水酸基価を低減させたり、繰り返し単位を有する化合物として炭素数3以上の多価アルコールを含む縮合物を使用したり、フィルムの寸法変化を小さくしたりすることによって、更に低減することができた。そして、これらのRth変化を抑制した本発明の偏光板を用いた液晶表示装置は、湿熱環境下で保持した後でも色味変化がなく、信頼性の高いものであることが確認された。
前述の『《1》 セルロースアシレートフィルムの製造と評価』と同様に、下記フィルム14、及びフィルム15を作製した。
フィルム2の作製において、繰り返し単位を有する化合物としてA−1の代わりにA−3を用い、更に下記湿度依存性改良剤Aをセルロースアシレートに対して5質量%加えた以外はフィルム2と全く同様にフィルムを作製し、フィルム14とした。
・A:下記構造の化合物
フィルム2の作製において、繰り返し単位を有する化合物としてA−1の代わりにA−5用い、更に前述の湿度依存性改良剤Aをセルロースアシレートに対して5質量%加えた以外はフィルム2と全く同様にフィルムを作製し、フィルム15した。
装置正面からの方位角方向45度、極角方向70度における黒表示時の輝度ムラ、色味ムラを観察し、以下の基準で評価したところ、フィルム14及びフィルム15を用いた偏光板を組み込んだ液晶表示装置はともに、正面からの光ムラは○レベル、斜めからの色ムラも○レベルであった。
○ : 照度100lxの環境下でムラがほとんど視認されない
△ : 照度100lxの環境下で淡いムラが視認される
× : 照度100lxの環境下で明確なムラが視認される
××: 照度300lxの環境下で明確なムラが視認される
Claims (10)
- 繰り返し単位を有する化合物、レタデーションの耐久性を向上させる化合物、及びセルロースエステルを含む光学フィルムであって、
該繰り返し単位を有する化合物が該セルロースエステルに対して30質量%より多く含まれ、
前記光学フィルムは、60℃90%RHで1日処理した場合の寸法変化率が3%以下であり、
前記光学フィルムの波長590nmで測定した下記式(I)及び式(II)にて定義されるRe及びRthが下記式(IIIa)及び(IVa)を満たすことを特徴とする光学フィルム。
式(I) Re=(nx―ny)×d(nm)
式(II) Rth={(nx+ny)/2−nz}×d(nm)
式(IIIa) Re<10
式(IVa) |Rth|<25
(式中、nxはフィルム面内の遅相軸方向の屈折率であり、nyはフィルム面内の進相軸方向の屈折率であり、nzはフィルムの厚み方向の屈折率であり、dはフィルムの厚さ(nm)である。) - 前記レタデーションの耐久性を向上させる化合物が、分子内に塩基性の官能基を有する化合物であることを特徴とする請求項1に記載の光学フィルム。
- 前記繰り返し単位を有する化合物が、多価アルコールと多塩基酸との縮合物、多価エーテルアルコールと多塩基酸との縮合物、多価アルコールと多塩基酸との縮合物とイソシアナート化合物との縮合物からなる群より選択される少なくとも1種の化合物であることを特徴とする請求項1又は2に記載の光学フィルム。
- 前記繰り返し単位を有する化合物が、アクリル酸エステルの付加物、メタクリル酸エステルの付加物からなる群より選択される少なくとも1種の化合物であることを特徴とする請求項1又は2に記載の光学フィルム。
- 前記繰り返し単位を有する化合物が、多価アルコールと多塩基酸との縮合物、及び多価エーテルアルコールと多塩基酸との縮合物からなる群より選択される少なくとも1種の化合物を含有しており、該縮合物の水酸基価が40mgKOH/g未満であることを特徴とする請求項1〜3のいずれか一項に記載の光学フィルム。
- 前記光学フィルムが、60℃90%RHで1日処理した場合の寸法変化率が0.05〜1%であることを特徴とする請求項1〜5のいずれか一項に記載の光学フィルム。
- 前記セルロースエステルが、セルロースの水酸基へのアシル置換度が2.80〜3.00のセルロースアシレートであることを特徴とする請求項1〜6のいずれか一項に記載の光学フィルム。
- 少なくとも、請求項1〜7のいずれか一項に記載の光学フィルムを含む位相差フィルム。
- 少なくとも、請求項1〜7のいずれか一項に記載の光学フィルム、または請求項8に記載の位相差フィルムを含む偏光板。
- 少なくとも、請求項1〜7のいずれか一項に記載の光学フィルム、又は請求項8に記載の位相差フィルム、又は請求項9に記載の偏光板を含むことを特徴とする画像表示装置。