JP5633173B2 - 冷延鋼板の製造方法 - Google Patents
冷延鋼板の製造方法 Download PDFInfo
- Publication number
- JP5633173B2 JP5633173B2 JP2010088233A JP2010088233A JP5633173B2 JP 5633173 B2 JP5633173 B2 JP 5633173B2 JP 2010088233 A JP2010088233 A JP 2010088233A JP 2010088233 A JP2010088233 A JP 2010088233A JP 5633173 B2 JP5633173 B2 JP 5633173B2
- Authority
- JP
- Japan
- Prior art keywords
- slab
- steel sheet
- rolled steel
- metallic inclusions
- surface defects
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、鋼中の非金属介在物に起因する表面欠陥に対する品質管理を行う冷延鋼板の製造方法に関する。
従来より、鋼中の非金属介在物に起因する表面欠陥は、歩留まりや生産性の低下を招くため、冷延鋼板の品質管理上の大きな問題となっている。そのため、欠陥検出装置などを用いて非金属介在物や表面欠陥を検出して鋼板の品質管理を行う種々の方法が提案されている。例えば、特許文献1には、鋼板製造ラインの各工程に表面疵(表面欠陥)検査装置を設置し、各工程における疵検査画像を前工程の同一部位の疵検査画像に順次付加して保存し、同一の疵検査部位に対応する複数の疵検査画像を並列的に表示させ、疵の履歴を把握できるようにした鋼板の品質管理方法が開示されている。また、特許文献2には、冷間圧延前の酸洗ラインにて鋼板の品質(非金属介在物や表面欠陥)を評価し、評価結果に基づき、冷間圧延後に表面欠陥となるかどうかを、過去の実績から予測して品質管理を行う冷延鋼板の製造方法が開示されている。
しかしながら、特許文献1や2に記載の品質管理では、中間製品や最終製品である鋼板の状態になって始めて非金属介在物や表面欠陥の品質評価が行われるため、評価結果に応じた中間製品や最終製品の仕様変更や向け先変更などの対応を迅速に行えず、歩留まりや生産性の低下を余儀なくされる。
本発明は、鋼中の非金属介在物に起因する表面欠陥に対する品質管理を行うにあたり、歩留まりや生産性の低下の少ない冷延鋼板の製造方法を提供することを目的とする。
本発明者等は、上記の目的を達成すべく鋭意検討を行った結果、歩留まりや生産性の低下を極力抑制するには、スラブにおける非金属介在物の存在状態と製品となった冷延鋼板の表面欠陥との関係を予め求めておくことが効果的であることを見出した。
本発明は、このような知見に基づきなされたもので、欠陥検出装置により検出されるスラブ中に存在する非金属介在物の大きさおよびスラブ表面からの深さ方向位置と、前記スラブを冷延鋼板としたときに前記非金属介在物が表面欠陥となるかどうかとの関係を予め求めておき、前記欠陥検出装置によるスラブ中の非金属介在物の検出結果を基に品質管理を行う冷延鋼板の製造方法を提供する。ここで、非金属介在物の大きさとは非金属介在物のスラブ幅方向の最大長を、非金属介在物のスラブ表面からの深さ方向位置とはスラブ表面と非金属介在物表面との最短距離を表す。
本発明により、鋼中の非金属介在物に起因する表面欠陥に対する品質管理を行うにあたり、歩留まりや生産性を大きく低下させることなく冷延鋼板を製造できるようになった。
本発明者等は、意識的に清浄度を低下させた厚み300mmのスラブを用い、超音波探傷装置により検出されるスラブ中に存在する非金属介在物のうちどのようなものが板厚1.2mmの冷延鋼板にした後に表面欠陥となるかどうかを調査したところ、図1に示すような非金属介在物の大きさおよびスラブ表面からの深さ方向位置と表面欠陥発生との関係を得た。図の領域A(図中実線の左上)を満足する非金属介在物は表面欠陥とはならず、それ以外の領域B(図中実線の右下)に入る非金属介在物は表面欠陥となる。ただし、領域Bの中の領域C(図中実線と点線の間)に入る非金属介在物は、中間製品である熱延鋼板に表面研削を施すことにより表面欠陥とはならなくなる。
図1の関係を予め求めておき、スラブ中に存在する非金属介在物を超音波探傷装置のような欠陥検出装置により検出すれば最終製品である冷延鋼板の表面欠陥に対する品質管理を行えることになる。また、スラブの段階で最終製品の品質管理を行えるので、品質に応じた中間製品や最終製品の仕様変更や向け先変更などの対応を迅速に行え、歩留まりや生産性の低下を抑制できることになる。実際、本発明の製造方法により、一般の冷延鋼板では歩留まりを0.10%、自動車外板パネル用の冷延鋼板では0.04%向上できた(いずれも、溶融亜鉛めっき鋼板を含めた歩留まりである。)。
Claims (1)
- 欠陥検出装置により検出されるスラブ中に存在する非金属介在物の大きさおよびスラブ表面からの深さ方向位置と、前記スラブを冷延鋼板とした時に前記非金属介在物が表面欠陥となるかどうかとの関係を、非金属介在物が表面欠陥とならない領域Ａ、非金属介在物は表面欠陥となるが中間製品である熱延鋼板に表面研削を施すことにより表面欠陥とはならなくなる領域Ｂ、非金属介在物が表面欠陥となり熱延鋼板に表面研削を施しても表面欠陥がなくならない領域Ｃに分類して、予め求めておき、前記欠陥検出装置によるスラブ中の非金属介在物の検出結果を基に品質管理を行う冷延鋼板の製造方法；ここで、非金属介在物の大きさとは非金属介在物のスラブ幅方向の最大長を、非金属介在物のスラブ表面からの深さ方向位置とはスラブ表面と非金属介在物表面との最短距離を表す。