JP5578678B2 - Concrete for paving - Google Patents
Concrete for paving Download PDFInfo
- Publication number
- JP5578678B2 JP5578678B2 JP2011048789A JP2011048789A JP5578678B2 JP 5578678 B2 JP5578678 B2 JP 5578678B2 JP 2011048789 A JP2011048789 A JP 2011048789A JP 2011048789 A JP2011048789 A JP 2011048789A JP 5578678 B2 JP5578678 B2 JP 5578678B2
- Authority
- JP
- Japan
- Prior art keywords
- concrete
- mass
- paving
- strength
- binder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、舗装用コンクリートに関する。 The present invention relates to concrete for paving.
高速道路、幹線道路、生活道路等の舗装用材料として、舗装用コンクリート、舗装用アスファルト等が知られている。舗装用アスファルトは、舗装作業が比較的容易であって、舗装作業開始から交通開放までの期間を短縮することができるものの、舗装用コンクリートと比較すると耐久性に劣るため、路面にいわゆる「わだち掘れ」等が生じやすいという問題点がある。 As paving materials for highways, main roads, and residential roads, paving concrete, paving asphalt, and the like are known. Pavement asphalt is relatively easy to pave and can shorten the period from the start of pavement work to the opening of traffic, but it is less durable than concrete for pavement. Etc. ”is likely to occur.
一方で、舗装用コンクリートは、道路の舗装以外にも、空港、港湾、工場敷地等の重荷重用の舗装として、また、ガレージ、通路等の軽荷重用の舗装として用いられたり、さらに、橋梁等のコンクリート床版の補強を目的とした増厚用コンクリートとして用いられたり、極めて広い範囲において使用されている。 On the other hand, paving concrete is used for heavy loads such as airports, harbors, and factory sites, as well as for light loads such as garages and passages, and for bridges, etc. It is used as thickening concrete for the purpose of reinforcing concrete floor slabs, and is used in a very wide range.
舗装用コンクリートは、舗装用アスファルトと比較すると耐久性に優れるため、路面にわだち掘れが生じ難く、また当該コンクリートを使用して道路を舗装すると、路面の色が明るくなり、夜間に運転する運転者に対して疲労感を感じさせ難い等の利点を有するが、コンクリート内の温度差により発生する応力、通行車両の輪荷重により発生する応力等により疲労し、いずれはひび割れ等が発生してしまうことが知られている。 Since concrete for paving is more durable than paving asphalt, rubbing is less likely to occur on the road surface.When paving a road using the concrete, the color of the road surface becomes brighter and the driver who drives at night It has the advantage that it makes it difficult to feel fatigue, but it fatigues due to stress generated by temperature differences in the concrete, stress generated by wheel load of passing vehicles, etc., and cracks etc. will eventually occur It has been known.
舗装用コンクリートにひび割れ等が発生してしまった場合には、新たに舗装用コンクリートを構築する必要があるが、コンクリートを用いた舗装作業には、コンクリートの打設、養生等の作業が困難であること、舗装作業の開始から交通開放までの期間が長期化すること、ひび割れ等により除去したコンクリートの処分が困難である等の問題がある。そのため、道路の修復等を目的とする舗装用コンクリートを使用した舗装作業の頻度を低減すべく、寿命の極めて長い舗装用コンクリートが望まれている。 When cracks, etc. occur in paving concrete, it is necessary to construct new paving concrete. However, it is difficult to place concrete and perform curing for paving work using concrete. There are problems such as that the period from the start of paving work to the opening of traffic is prolonged, and it is difficult to dispose of the concrete removed by cracks and the like. Therefore, in order to reduce the frequency of pavement work using pavement concrete for road restoration or the like, pavement concrete having an extremely long life is desired.
このような観点から、従来、セメント、ポゾラン質微粉末、所定の粒径を有する細骨材、減水剤及び水を含む配合物を硬化させてなる舗装用コンクリートが提案されている（特許文献１参照）。 From such a viewpoint, conventionally, concrete for paving has been proposed in which a mixture containing cement, pozzolanic fine powder, fine aggregate having a predetermined particle size, a water reducing agent and water is cured (Patent Document 1). reference).
しかしながら、上記特許文献１に記載の舗装用コンクリートは、コンクリート打設後の長期における強度（例えば、材齢２８日以降の強度（曲げ強度、圧縮強度））の発現性に優れ、寿命の長いものであるものの、コンクリート打設後の極めて初期における強度（例えば、材齢１日程度の強度（曲げ強度、圧縮強度））の発現性に劣るものであるため、舗装用コンクリートにおける舗装作業開始からの早期交通開放という課題を解決するには至っていなかった。 However, the concrete for paving described in Patent Document 1 has excellent long-term strength after concrete placement (for example, strength after 28 days of age (bending strength, compressive strength)) and has a long life. Although it is inferior in the expression of strength in the very early stage after concrete placement (for example, strength of about one day of age (bending strength, compressive strength)) The problem of opening up traffic has not been solved.
上記問題点に鑑みて、本発明は、長期強度の発現性に優れるとともに、初期強度の発現性にも優れ、寿命が長く、かつ舗装作業の開始から極めて早期に交通開放をすることができる舗装用コンクリートを提供することを目的とする。 In view of the above problems, the present invention is excellent in long-term strength development, initial strength development, long life, and can open traffic very early from the start of paving work. The purpose is to provide concrete.
上記課題を解決するために、ＢＥＴ比表面積が５〜２５ｍ２／ｇのポゾラン質微粉末、ブレーン比表面積が５０００〜１２０００ｃｍ２／ｇの高炉スラグ粉末、ブレーン比表面積が３０００〜１２０００ｃｍ２／ｇの無水石膏、及びセメントを含む結合材を少なくとも含有するコンクリート組成物を硬化させてなり、材齢１日における曲げ強度が、３．５Ｎ／ｍｍ２以上であることを特徴とする舗装用コンクリートを提供する（請求項１）。 In order to solve the above problems, BET specific surface area of pozzolanic substance fine powder 5~25m 2 / g, the Blaine specific surface area of blast furnace slag powder 5000~12000cm 2 / g, the Blaine specific surface area of 3000~12000cm 2 / g Provided is a concrete for paving, which is obtained by curing a concrete composition containing at least a binder containing anhydrous gypsum and cement, and has a bending strength of 3.5 N / mm 2 or more at a material age of 1 day. (Claim 1).
さらに、前記コンクリート組成物は、水結合比が１２〜３５質量％となるように、前記結合材と水とを含有する前記の舗装用コンクリートを提供する（請求項２）。 Furthermore, the concrete composition provides the pavement concrete containing the binder and water so that the water bonding ratio is 12 to 35% by mass (Claim 2).
舗装用コンクリートの設計基準強度は、曲げ強度で４．５Ｎ／ｍｍ２と規定されており、舗装用コンクリートの打設後、交通開放可能となる曲げ強度は、配合強度の７割以上の曲げ強度（３．４７Ｎ／ｍｍ２以上）と規定されているが（２００７年制定舗装標準示方書、土木学会舗装工学委員会編，２００７年３月）、上記発明（請求項１）によれば、材齢１日において交通開放可能な曲げ強度以上の強度発現性を有するため、初期強度発現性に優れたものとすることができる。よって、上記発明（請求項１）に係る舗装用コンクリートを用いることで、舗装作業の開始から極めて早期に交通開放することが可能となる。 The design standard strength of paving concrete is stipulated as 4.5 N / mm 2 in terms of bending strength, and the bending strength at which traffic can be opened after placing paving concrete is bending strength that is 70% or more of the blend strength. According to the above invention (Claim 1), the material is defined as (3. 47 N / mm 2 or more) (pavement standard specifications established in 2007, edited by the Japan Society of Civil Engineers, Pavement Engineering Committee, March 2007). Since it has a strength expression that is higher than the bending strength at which traffic can be opened at the age of one day, it can be excellent in initial strength expression. Therefore, by using the concrete for paving according to the above invention (invention 1), it becomes possible to open the traffic very early from the start of the paving work.
上記発明（請求項１）においては、前記コンクリート組成物が、水結合材比が１２〜３５質量％となるように、前記結合材と水とを含有するのが好ましい（請求項２）。かかる発明（請求項２）のように水結合材比を低く設定することで、長期強度の発現性がより優れた舗装用コンクリートとすることができ、舗装用コンクリート（当該コンクリートで舗装された道路等）の寿命を長くすることができる。 In the said invention (invention 1), it is preferable that the said concrete composition contains the said binder and water so that a water binder ratio may be 12-35 mass% (invention 2). By setting the water binder ratio low as in this invention (invention 2), it is possible to obtain a concrete for paving that exhibits better long-term strength, and a concrete for paving (a road paved with the concrete). Etc.) can be extended.
本発明によれば、長期強度の発現性に優れるとともに、初期強度の発現性にも優れ、寿命が長く、かつ舗装作業の開始から極めて早期に交通開放をすることができる舗装用コンクリートを提供することができる。 According to the present invention, there is provided a concrete for paving that is excellent in long-term strength development, is excellent in initial strength development, has a long life, and can open traffic very early from the start of paving work. be able to.
本発明の舗装用コンクリートは、上述のとおり、特定の混和材料とセメントを含む結合材を少なくとも含有するコンクリート組成物を硬化させてなるものである。
以下に、本発明について詳細に説明する。
As described above, the concrete for paving of the present invention is obtained by curing a concrete composition containing at least a binder containing a specific admixture and cement.
The present invention is described in detail below.
結合材について、結合材は、（１）ＢＥＴ比表面積が１５〜２５ｍ２／ｇのポゾラン質微粉末、（２）ブレーン比表面積が５０００〜１２０００ｃｍ２／ｇの高炉スラグ粉末、および、（３）ブレーン比表面積が３０００〜１２０００ｃｍ２／ｇの無水石膏（以下［混和材（Ａ）」という。）、及び、（４）セメントを含むものである。 With respect to the binder, the binder is (1) a pozzolanic fine powder having a BET specific surface area of 15 to 25 m 2 / g, (2) a blast furnace slag powder having a brain specific surface area of 5000 to 12000 cm 2 / g, and (3) It contains anhydrous gypsum (hereinafter referred to as “Admixture (A)”) having a specific surface area of 3000 to 12000 cm 2 / g, and (4) cement.
前記結合材の組成は、好ましくは、混和材（Ａ）の含有率が１０〜５０質量％、および、セメントの含有率が５０〜９０質量％であり、より好ましくは、混和材（Ａ）の含有率が２０〜４０質量％、および、セメントの含有率が６０〜８０質量％である。混和材（Ａ）の含有率が１０質量％未満で、セメントの含有率が９０質量％を超えると、舗装用コンクリートの寿命を長くすることが困難になるおそれがある。また、舗装用コンクリートの作業性も低下し、作業性を向上させるために減水剤の配合量を増やした場合は舗装用コンクリートの初期強度の発現性が低下するおそれがある。混和材（Ａ）の含有率が５０質量％を超え、セメントの含有率が５０質量％未満では、舗装用コンクリートの初期強度の発現性が低下するおそれがある。 The composition of the binder is preferably 10 to 50% by mass of the admixture (A) and 50 to 90% by mass of the cement, and more preferably of the admixture (A). The content is 20 to 40% by mass and the cement content is 60 to 80% by mass. If the content of the admixture (A) is less than 10% by mass and the content of cement exceeds 90% by mass, it may be difficult to extend the life of the concrete for paving. Moreover, the workability of the paving concrete also decreases, and when the blending amount of the water reducing agent is increased to improve the workability, the initial strength of the paving concrete may be lowered. If the content of the admixture (A) exceeds 50% by mass and the content of the cement is less than 50% by mass, the initial strength of the paving concrete may be deteriorated.
また、前記混和材（Ａ）の組成は、好ましくは、ポゾラン質微粉末の含有率が５〜５５質量％、高炉スラグ粉末の含有率が２０〜８０質量％、および、無水石膏の含有率が１５〜４０質量‰であり、より好ましくは、ポゾラン質微粉末の含有率が１０〜４０質量％、高炉スラブ粉末の含有率が３０〜６０質量％、および、無水石膏の含有率が２０〜３５質量％である。混和材（Ａ）の組成が該範囲を外れると、舗装用コンクリートの強度発現性が低下したり、寿命を長くすることが困難になるおそれがある。 The composition of the admixture (A) is preferably such that the content of pozzolanic fine powder is 5 to 55% by mass, the content of blast furnace slag powder is 20 to 80% by mass, and the content of anhydrous gypsum is More preferably, the content of pozzolanic fine powder is 10 to 40% by mass, the content of blast furnace slab powder is 30 to 60% by mass, and the content of anhydrous gypsum is 20 to 35%. % By mass. If the composition of the admixture (A) is out of this range, the strength development of the concrete for paving may be lowered or it may be difficult to extend the life.
結合材に含まれる各成分について説明する。
（１）ポゾラン質微粉末
ポゾラン質微粉末は、単独では、水硬性はないが、水酸化カルシウムがあれば、水中で反応して不溶性のゲルを生成し硬化する物質である。
そして、本発明で用いるポゾラン質微粉末として、例えば、シリカフューム、シリカダスト、フライアッシュ、スラグ、火山灰、シリカゾル、沈降性シリカなどが挙げられる。これらの中でも、シリカフュームやシリカダストは、その平均粒径が１μｍ以下であって粉砕する必要がないため好適である。ここで、粉砕手段として、ボールミルやロッドミルなどが使用できる。
Each component contained in the binder will be described.
(1) Pozzolanic fine powder Pozzolanic fine powder alone is not hydraulic, but if calcium hydroxide is present, it is a substance that reacts in water to form an insoluble gel and hardens.
Examples of the pozzolanic fine powder used in the present invention include silica fume, silica dust, fly ash, slag, volcanic ash, silica sol, and precipitated silica. Among these, silica fume and silica dust are preferable because their average particle diameter is 1 μm or less and they do not need to be pulverized. Here, a ball mill or a rod mill can be used as the pulverizing means.
また、該ポゾラン質微粉末のＢＥＴ比表面積は、通常、１５〜２５ｍ２／ｇであり、好ましくは１７〜２３ｍ２／ｇ、より好ましくは１８〜２２ｍ２／ｇである。該比表面積が１５〜２５ｍ２／ｇの範囲を外れると、舗装用コンクリートの強度発現性が低下したり、寿命を長くすることが困難になるおそれがある。 Moreover, the BET specific surface area of this pozzolanic fine powder is 15-25 m < 2 > / g normally, Preferably it is 17-23 m < 2 > / g, More preferably, it is 18-22 m < 2 > / g. If the specific surface area is out of the range of 15 to 25 m 2 / g, the strength development of the concrete for pavement may be lowered or it may be difficult to extend the life.
（２）高炉スラグ粉末
本発明で用いる高炉スラグ粉末として、「ＪＩＳ Ａ ６２０６」に規定するコンクリート用高炉スラグ微粉末のほか、さらに該微粉末を粉砕したものが用いられる。高炉スラグ粉末の粉末度は、通常、ブレーン比表面積が５０００〜１２０００ｃｍ２／ｇであり、好ましくは６０００〜１００００ｃｍ２／ｇである、該比表面積が５０００ｃｍ２／ｇ未満では潜在水硬性が低く、１２０００ｃｍ２／ｇを超えると、粉砕の手間が増大してコスト高になる。ここで、粉砕手段として、ボールミルやロッドミルなどが使用できる。
(2) Blast Furnace Slag Powder As the blast furnace slag powder used in the present invention, in addition to the blast furnace slag fine powder for concrete specified in “JIS A 6206”, a powder obtained by further pulverizing the fine powder is used. Fineness of blast furnace slag powder is usually Blaine specific surface area of 5000～12000Cm 2 / g, preferably from 6000～10000Cm 2 / g, specific surface area is 5000cm is less than 2 / g latent hydraulic low, If it exceeds 12000 cm 2 / g, the labor of pulverization increases and the cost increases. Here, a ball mill or a rod mill can be used as the pulverizing means.
（３）無水石膏
本発明で用いる無水石膏として、天然無水石膏のほか、石膏ボード等の石膏廃材を加熱処理して得られる再生無水石膏が挙げられる。
また、無水石膏の粉末度は、通常、ブレーン比表面積が３０００〜１２０００ｍ２／ｇであり、好ましくは４０００〜１００００ｍ２／ｇである。該比表面積が３０００ｍ２／ｇ未満では、舗装用コンクリートの強度発現性が低下したり、寿命を長くすることが困難になるおそれがあり、１２０００ｍ２／ｇを超えると、粉砕の手間が増大してコスト高になる。
(3) Anhydrous gypsum The anhydrous gypsum used in the present invention includes natural anhydrous gypsum and regenerated anhydrous gypsum obtained by heat treatment of gypsum waste such as gypsum board.
Further, the powder of the anhydrous gypsum is usually Blaine specific surface area of 3000~12000m 2 / g, preferably from 4000~10000m 2 / g. If the specific surface area is less than 3000 m 2 / g, the strength development of the concrete for pavement may be lowered, and it may be difficult to extend the life. If it exceeds 12000 m 2 / g, the labor of grinding increases. Cost.
（４）セメント
本発明で用いるセメントとしては、ポルトランドセメント、普通エコセメント、フライアッシュセメントやシリカセメントが挙げられる。ポルトランドセメントは、例えば、普通ポルトランドセメント、早強ポルトランドセメント、超早強ポルトランドセメント、中庸熱ポルトランドセメント、低熱ポルトランドセメント、耐硫酸塩ポルトランドセメント等から選ばれる、少なくとも１種以上が挙げられる。これらの中でも、普通ポルトランドセメント、早強ポルトランドセメント、または、超早強ポルトランドセメントは、早期に強度を発現することができる。また、中庸熱ポルトランドセメントは、化学抵抗性や長期の強度が向上する。
(4) Cement Examples of the cement used in the present invention include Portland cement, ordinary eco cement, fly ash cement and silica cement. Examples of the Portland cement include at least one selected from ordinary Portland cement, early-strength Portland cement, ultra-early strong Portland cement, moderately hot Portland cement, low heat Portland cement, sulfate-resistant Portland cement, and the like. Among these, ordinary Portland cement, early-strength Portland cement, or ultra-early-strength Portland cement can develop strength at an early stage. In addition, medium heat Portland cement improves chemical resistance and long-term strength.
また、前記ポルトランドセメントは、３ＣａＯ・ＳｉＯ２を４５〜８０質量％、および、３ＣａＯ・Ａ１２Ｏ３を４〜２０質量％含むものが、より好ましく、３ＣａＯ・ＳｉＯ２を５０〜７５質量‰、および、３ＣａＯ・Ａｌ２Ｏ３を５〜１５質量％含むものが、更に好ましい。３ＣａＯ・ＳｉＯ２の含有率が４５〜８０質量‰、および、３ＣａＯ・Ａ１２Ｏ３の含有率が４〜２０質量％の範囲を外れると、舗装用コンクリートの強度発現性が低下するおそれがある。 Further, the Portland cement preferably contains 3CaO · SiO 2 in an amount of 45 to 80% by mass and 3CaO · A1 2 O 3 in an amount of 4 to 20% by mass, more preferably 3CaO · SiO 2 in an amount of 50 to 75% by mass, and those containing 3CaO · Al 2 O 3 5~15 wt% is more preferable. If the content ratio of 3CaO · SiO 2 is 45 to 80 mass% and the content ratio of 3CaO · A1 2 O 3 is out of the range of 4 to 20 mass%, the strength development property of the concrete for pavement may be lowered. .
結合材以外の材料について説明する。
結合材以外の材料としては、細骨材、粗骨材、減水剤及び水が挙げられる。細骨材としては、特に限定されず、例えば、川砂、山砂、陸砂、海砂、砕砂、珪砂、スラグ細骨材、軽量細骨材等、または、これらの混合物が挙げられる。
細骨材の配合量は、舗装用コンクリートの作業性や強度発現性、寿命などから、結合材１００質量部に対して、１〜２５０質量部、より好ましくは３０〜２２０質量部である。
Materials other than the binder will be described.
Examples of materials other than the binder include fine aggregate, coarse aggregate, water reducing agent, and water. The fine aggregate is not particularly limited, and examples thereof include river sand, mountain sand, land sand, sea sand, crushed sand, quartz sand, slag fine aggregate, lightweight fine aggregate, and a mixture thereof.
The blending amount of the fine aggregate is 1 to 250 parts by mass, more preferably 30 to 220 parts by mass with respect to 100 parts by mass of the binder because of the workability, strength development, and life of the paving concrete.
粗骨材としては、特に限定されず、例えば、砂利、砕石、スラグ粗骨材、軽量粗骨材等、または、これらの混合物が挙げられる。
粗骨材の配合量は、舗装用コンクリートの作業性や強度発現性、寿命などから、結合材１００質量部に対して、８０〜４２０質量部、より好ましくは１２０〜３２０質量部である。なお、粗骨材や細骨材は、天然骨材のほか再生骨材も用いることができる。
The coarse aggregate is not particularly limited, and examples thereof include gravel, crushed stone, slag coarse aggregate, lightweight coarse aggregate, or a mixture thereof.
The blending amount of the coarse aggregate is 80 to 420 parts by mass, more preferably 120 to 320 parts by mass with respect to 100 parts by mass of the binder because of the workability, strength development, and life of the paving concrete. In addition, as the coarse aggregate and the fine aggregate, regenerated aggregate can be used in addition to natural aggregate.
水も特に限定されず、水道水やスラッジ水等を用いることができる。
水結合材比（Ｗ／Ｐ：１００×水の質量／結合材の質量）は、通常１２〜３５質量％であり、好ましくは１３〜３０質量％である。水結合材比が１２質量％未満では、舗装用コンクリートの作業性が低下し、作業性を向上させるために減水剤の配合量を増やした場合は舗装用コンクリートの初期強度の発現性が低下するおそれがある。水結合材比が３５質量％を超えると、舗装用コンクリートの初期強度の発現性が低下するおそれがある。
Water is not particularly limited, and tap water, sludge water, or the like can be used.
The water binder ratio (W / P: 100 × mass of water / mass of binder) is usually 12 to 35% by mass, preferably 13 to 30% by mass. When the water binder ratio is less than 12% by mass, the workability of the paving concrete is lowered, and when the blending amount of the water reducing agent is increased to improve the workability, the initial strength of the paving concrete is lowered. There is a fear. If the water binder ratio exceeds 35% by mass, the initial strength of the paving concrete may be deteriorated.
減水剤としては、リグニン系、ナフタレンスルホン酸系、メラミン系、ポリカルボン酸系等の減水剤、ＡＥ減水剤、高性能減水剤または高性能ＡＥ減水剤を使用することができる。これらのうち、減水効果の大きな高性能減水剤または高性能ＡＥ減水剤を使用することが好ましく、特に、ポリカルボン酸系の高性能減水剤または高性能ＡＥ減水剤を使用することがより好ましい。
減水剤の配合量は、舗装用コンクリートの作業性や強度発現性、寿命などから、結合材１００質量部に対して、固形分換算で好ましくは０．０５〜１質量部、より好ましくは０．１〜０．８質量部である。
なお、減水剤は、液状と粉末状のいずれでも使用することができる。
As the water reducing agent, lignin-based, naphthalenesulfonic acid-based, melamine-based, polycarboxylic acid-based water reducing agents, AE water reducing agents, high-performance water reducing agents, or high-performance AE water reducing agents can be used. Among these, it is preferable to use a high-performance water reducing agent or a high-performance AE water reducing agent having a large water-reducing effect, and it is more preferable to use a polycarboxylic acid-based high-performance water reducing agent or a high-performance AE water reducing agent.
The blending amount of the water reducing agent is preferably 0.05 to 1 part by mass in terms of solid content with respect to 100 parts by mass of the binder, and more preferably 0. 1 to 0.8 parts by mass.
The water reducing agent can be used in either liquid or powder form.
なお、本発明の舗装用コンクリートには、上記材料の他に、収縮低減剤、ＡＥ剤、膨張材、顔料などを含んでもよい。 In addition to the above materials, the concrete for paving of the present invention may contain a shrinkage reducing agent, an AE agent, an expansion material, a pigment, and the like.
本実施形態に係る舗装用コンクリートは、上記コンクリート組成物を混練し、施工現場 （道路等）に敷設し、養生して硬化させることにより得られる。養生方法としては、例えば、養生シートを用いた加温養生、蒸気養生等が挙げられるが、これらに限定されるものではない。 The concrete for paving according to the present embodiment can be obtained by kneading the concrete composition, laying it on a construction site (road or the like), curing and curing it. Examples of the curing method include, but are not limited to, warm curing using a curing sheet, steam curing, and the like.
このようにして得られる舗装用コンクリートは、材齢１日において交通開放に必要な３．４７Ｎ／ｍｍ２以上の曲げ強度（初期曲げ強度）を発揮することができ、好ましくは舗装用コンクリートの設計基準強度である４．５Ｎ／ｍｍ２以上の曲げ強度を発揮することができる。また、上記舗装用コンクリートは、材齢２８日以降において８．５Ｎ／ｍｍ２以上の曲げ強度（長期曲げ強度）を発揮することができ、好ましくは９．５Ｎ／ｍｍ２以上の曲げ強度を発揮することができる。 The paving concrete thus obtained can exhibit a bending strength (initial bending strength) of 3.47 N / mm 2 or more necessary for opening traffic at the age of one day, and is preferably designed for paving concrete. A bending strength of 4.5 N / mm 2 or more, which is a reference strength, can be exhibited. The concrete for paving can exhibit a bending strength (long-term bending strength) of 8.5 N / mm 2 or more after the age of 28 days, and preferably exhibits a bending strength of 9.5 N / mm 2 or more. can do.
さらに、上記舗装用コンクリートは、材齢１日において２０Ｎ／ｍｍ２以上の圧縮強度（初期圧縮強度）を発揮することができ、好ましくは３０Ｎ／ｍｍ２以上の圧縮強度を発揮することができる。さらにまた、上記舗装用コンクリートは、材齢２８日以降において１１０〜１３５Ｎ／ｍｍ２の圧縮強度（長期圧縮強度）を発揮することができ、好ましくは１２５〜１３５Ｎ／ｍｍ２の圧縮強度を発揮することができる。 Furthermore, the paving concrete, can exhibit 20 N / mm 2 or more compression strength (initial compression strength) at 1 day age of, preferably can exhibit 30 N / mm 2 or more compression strength. Furthermore, the concrete for paving can exhibit a compressive strength (long-term compressive strength) of 110 to 135 N / mm 2 after the age of 28 days, and preferably exhibits a compressive strength of 125 to 135 N / mm 2. be able to.
このように、本実施形態に係る舗装用コンクリートは、舗装用コンクリートの要求強度 （曲げ強度：４．５Ｎ／ｍｍ２以上）を満足することができるとともに、優れた初期強度（圧縮強度及び曲げ強度）の発現性能を奏し得るため、本実施形態に係る舗装用コンクリートを用いて舗装作業を開始してから極めて早期に交通開放をすることができる。また、本実施形態に係る舗装用コンクリートは、優れた長期強度の発現性能をも奏し得るため、わだち掘れ等が生じ難く、寿命の極めて長いものとすることができる。 As described above, the concrete for paving according to the present embodiment can satisfy the required strength (bending strength: 4.5 N / mm 2 or more) of the concrete for paving and has excellent initial strength (compressive strength and bending strength). ), The traffic can be released very early after the paving work is started using the concrete for paving according to the present embodiment. Moreover, since the concrete for paving which concerns on this embodiment can also show | play the outstanding expression performance of long-term intensity | strength, rubbing etc. are hard to produce and it can be made into a thing with a very long life.
上述したように、本実施形態に係る舗装用コンクリートは、初期強度及び長期強度の発現性に優れるものである。したがって、本実施形態に係る舗装用コンクリートによれば、道路等の舗装用として十分な強度発現性能を発揮し得るとともに、舗装作業開始から交通開放までの期間を極めて短縮することができる。 As described above, the concrete for paving according to this embodiment has excellent initial strength and long-term strength. Therefore, according to the concrete for paving which concerns on this embodiment, while being able to exhibit sufficient strength expression performance for paving, such as a road, the period from the start of paving work to the opening of traffic can be shortened extremely.
以上説明した実施形態は、本発明の理解を容易にするために記載されたものであって、本発明を限定するために記載されたものではない。したがって、上記実施形態に開示された各要素は、本発明の技術的範囲に属する全ての設計変更や均等物をも含む趣旨である。 The embodiment described above is described for facilitating understanding of the present invention, and is not described for limiting the present invention. Therefore, each element disclosed in the above embodiment is intended to include all design changes and equivalents belonging to the technical scope of the present invention.
上記実施形態に係る舗装用コンクリートは、極めて初期（材齢１日程度）における強度
（曲げ強度、圧縮強度）及び長期強度の発現性に優れるため、橋梁等のコンクリート床版の補強を目的とした増厚用コンクリートとしても使用することができる。
The concrete for paving according to the above embodiment has excellent strength (bending strength, compressive strength) and long-term strength in the initial stage (about 1 day of age), and is intended to reinforce concrete slabs such as bridges. It can also be used as thickening concrete.
以下、本発明を実施例により具体的に説明するが、本発明はこれらの実施例に限定されるものではない。
1.使用した材料
（1）混和材（Ａ）
以下の３成分からなる混和材。
（ｉ）シリカフューム（ＢＥＴ比表面積２０ｍ２／ｇ）：３０質量％
（ｉｉ）高炉スラグ微粉末（ブレーン比表面積７０００ｃｍ２／ｇ）：４０質量％
（ｉｉｉ）天然無水石膏（ブレーン比表面積４０００ｃｍ２／ｇ）：３０質量％
（２）セメント
Ａ：普通ポルトランドセメント（太平洋セメント社製）
Ｃ３Ｓ：６３質量‰、Ｃ２Ｓ：１１質量％、Ｃ３Ａ：９質量％、Ｃ４ＡＦ：９質量％
Ｂ：早強ポルトランドセメント（太平洋セメント社製）
Ｃ３Ｓ：６６質量‰、Ｃ２Ｓ：８質量％、Ｃ３Ａ：１０質量％、Ｃ４ＡＦ：８質量％
Ｃ：中庸熱ポルトランドセメント（太平洋セメント社製）
Ｃ３Ｓ：４２質量‰、Ｃ２Ｓ：３５質量％、Ｃ３Ａ：３質量％、Ｃ４ＡＦ：１３質量％
（３）細骨材
静岡県掛川市産の山砂
（４）粗骨材
茨城県桜川市産の硬質砂岩砕石１３０５
（５）減水剤
ポリカルボン酸系高性能ＡＥ減水剤（ＢＡＳＦポゾリス社製、固形分２８％）
EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to these examples.
1. Materials used (1) Admixture (A)
An admixture consisting of the following three components.
(I) Silica fume (BET specific surface area 20 m 2 / g): 30% by mass
(Ii) Blast furnace slag fine powder (Blaine specific surface area 7000 cm 2 / g): 40% by mass
(Iii) Natural anhydrous gypsum (Brain specific surface area 4000 cm 2 / g): 30% by mass
(2) Cement A: Ordinary Portland cement (manufactured by Taiheiyo Cement)
C 3 S: 63 mass%, C 2 S: 11 mass%, C 3 A: 9 mass%, C 4 AF: 9 mass%
B: Early strong Portland cement (manufactured by Taiheiyo Cement)
C 3 S: 66 mass%, C 2 S: 8 mass%, C 3 A: 10 mass%, C 4 AF: 8 mass%
C: Moderate heat Portland cement (manufactured by Taiheiyo Cement)
C 3 S: 42 mass%, C 2 S: 35 mass%, C 3 A: 3 mass%, C 4 AF: 13 mass%
(3) Fine aggregate Mountain sand from Kakegawa City, Shizuoka Prefecture (4) Coarse aggregate Hard sandstone crushed stone 1305 from Sakuragawa City, Ibaraki Prefecture
(5) Water-reducing agent Polycarboxylic acid-based high-performance AE water-reducing agent (BASF Pozzolith, solid content 28%)
表１に、舗装用コンクリート組成物の材料組成等、表２に、その単位量とともに、スランプ値、強度データを示す。結合材とは、セメントと上記混和材（Ａ）の総称である。 Table 1 shows the material composition of the concrete composition for paving, and Table 2 shows the slump value and strength data together with the unit amount. The binder is a general term for cement and the admixture (A).
〔圧縮強度の測定〕
上述のようにして作製された舗装用コンクリート組成物（実施例１〜１２、比較例１３〜１６）について、ＪＩＳ−Ａｌ１０８に準拠して圧縮強度を測定した。
(Measurement of compressive strength)
About the concrete composition for pavements produced as mentioned above (Examples 1-12, Comparative Examples 13-16), compressive strength was measured based on JIS-Al108.
〔曲げ強度の測定〕
上述のようにして作製された舗装用コンクリート組成物（実施例１〜１２、比較例１３〜１６）について、ＪＩＳ−Ａｌ１０６に準拠して曲げ強度を測定した。
[Measurement of bending strength]
About the concrete composition for pavements produced as mentioned above (Examples 1-12, Comparative Examples 13-16), bending strength was measured based on JIS-Al106.
実験例1〜１２については、舗装用コンクリートとして、良好な施工性と強度物性が得られた。 About Experimental Examples 1-12, favorable workability and strength physical properties were obtained as concrete for paving.
長期強度の発現性に優れるとともに、初期強度の発現性にも優れ、寿命が長く、かつ舗装作業の開始から極めて早期に交通開放をすることができる舗装用コンクリートとすることができる。
It is possible to provide a concrete for paving that is excellent in long-term strength development, excellent in initial strength, has a long life, and can open traffic very early from the start of paving work.
Claims (3)
前記結合材が、ＢＥＴ比表面積が５〜２５ｍ２／ｇのシリカダスト又はシリカフューム、ブレーン比表面積が５０００〜１２０００ｃｍ２／ｇの高炉スラグ粉末、ブレーン比表面積が３０００〜１２０００ｃｍ２／ｇの無水石膏、並びに３ＣａＯ・ＳｉＯ ２ 含有量が５０〜７５質量％のポルトランドセメントのみからなり、
材齢１日における曲げ強度が、４．５Ｎ／ｍｍ２以上であることを特徴とする舗装用コンクリート。 Concrete for paving made by curing a concrete composition consisting only of binder, fine aggregate, coarse aggregate, water reducing agent and water,
The binder, silica dust or fume of BET specific surface area of 5~25m 2 / g, blast furnace slag powder Blaine specific surface area of 5000~12000cm 2 / g, the Blaine specific surface area of 3000~12000cm 2 / g anhydrous gypsum, and 3CaO · SiO 2 content is only 50 to 75% by weight of Portland cement,
A concrete for paving, wherein the bending strength at a material age of 1 day is 4.5 N / mm 2 or more.