JP5444818B2 - 反射防止フィルム - Google Patents
反射防止フィルム Download PDFInfo
- Publication number
- JP5444818B2 JP5444818B2 JP2009107989A JP2009107989A JP5444818B2 JP 5444818 B2 JP5444818 B2 JP 5444818B2 JP 2009107989 A JP2009107989 A JP 2009107989A JP 2009107989 A JP2009107989 A JP 2009107989A JP 5444818 B2 JP5444818 B2 JP 5444818B2
- Authority
- JP
- Japan
- Prior art keywords
- refractive index
- layer
- fine particles
- silica fine
- colloidal silica
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
〔反射防止フィルム〕
反射防止フィルムは、PETフィルム上にPETフィルム表面から順に接着層、ハードコート層および低屈折率層がこの順で積層されて形成されている。そして、前記低屈折率層はバインダーと平均粒子径1〜50nmの変性コロイダルシリカ微粒子とを含む屈折率が1.43〜1.50の層であり、バインダーの硬化物と変性コロイダルシリカ微粒子との屈折率差が0.04以下に設定され、かつハードコート層の屈折率は低屈折率層の屈折率よりも0.13以上0.24以下に設定されている。
<PETフィルム>
本発明の反射防止フィルムに用いる基材フィルムは、ポリエチレンテレフタラート(PET、n=1.65)である。PETフィルムの厚みは、好ましくは25〜400μm、さらに好ましくは50〜200μmである。加えて、PETフィルムには、各種の添加剤が含有されていても良い。そのような添加剤として例えば紫外線吸収剤、帯電防止剤、安定剤、可塑剤、滑剤、難燃剤等が挙げられる。
<接着層>
本発明において接着層は、光学的な悪影響を及ぼすことなく、PETフィルムと後述するハードコート層との密着性を高める機能を有している。PETフィルムとハードコート層との密着性を高めることができる限り、接着層として任意の屈折率を有する公知の樹脂層が適用可能である。接着層の膜厚は1〜50nmとすることが好ましく、10〜30nmとすることがさらに好ましい。
<ハードコート層>
本発明においてハードコート層は、表面硬度や耐擦傷性を向上できる限り、ハードコート層に用いられる公知の全ての樹脂が使用可能であり、特に電離放射線硬化型樹脂と金属酸化物微粒子とを含有する材料から形成されることが好ましい。
<低屈折率層>
本発明における低屈折率層は、低屈折率塗布液を塗布し、重合硬化させたものでバインダーと平均粒子径1〜50nmの変性コロイダルシリカ微粒子とを含み、屈折率が1.43〜1.50の層である。この低屈折率層の屈折率は、変性コロイダルシリカ微粒子を原料とした場合、その性質上1.43未満となるように設定することは困難である。一方、屈折率が1.50を超える場合、反射防止フィルムの反射防止性が悪化する。
〔式中、Zは(メタ)アクリロイルオキシ基であり、R1は炭素数1〜4のアルキレン基であり、R2はメチル基またはエチル基である。〕
変性コロイダルシリカ微粒子はコロイダルシリカ微粒子表面のシラノール基とシランカップリング剤との加水分解反応により、コロイダルシリカ微粒子表面にオルガノシリル基(モノオルガノシリル基、ジオルガノシリル基またはトリオルガノシリル基)が結合すると共に、その表面に多数の珪素原子に直接結合した有機基を有する。
<反射防止フィルムの用途>
本発明の反射防止性フィルムは、例えばショーウィンドウやショーケースなどの建築材料としてのディスプレイケース表面に貼り合わせることによって、背景からの映り込みを少なくすることができる。従って、視認性を向上させることができるため、ディスプレイケース内の展示物をくっきり見せることができる。
<評価方法>
1)屈折率の測定
次の(1)〜(4)の工程に従って塗布液の屈折率を測定した。
(1)屈折率1.49のアクリル樹脂板〔旭化成工業(株)製、商品名:「デラグラスA」〕上に、ディップコーター〔杉山元理化学機器(株)製〕により、低屈折率層塗布液を実膜厚が100nm程度になるように層の厚みを調整して塗布した。
(2)低屈折率層塗布液中の溶媒乾燥後、必要に応じて紫外線照射装置〔岩崎電気(株)製〕により120W高圧水銀灯を用いて、出力400mJの紫外線を照射して低屈折率層塗布液を硬化させた。
(3)アクリル樹脂板の裏面をサンドペーパーで荒らし、黒色塗料で塗りつぶしたものを分光光度計〔「U−best50」、日本分光(株)製〕により、400〜650nmにおける5°、−5°正反射率を測定し、その反射率の極小値または極大値を読み取った。
(4)反射率の極値より以下の式を用いて屈折率を計算した。
但し、アクリル樹脂の屈折率は1.49および空気の屈折率は1.00である。
2)平均粒子径の測定
粒子径分布測定装置〔大塚電子(株)製、PAR−III〕を使用して、レーザー光による動的光散乱法により平均粒子径を測定した。
3)ヘイズ値の測定
日本電飾工業(株)製NDH−2000を使用し、光学特性としてのヘイズ値(%)を測定した。
4)白ボケの評価
機能層を設けた面と反対側の面からフロートガラスを貼合し、サンプルを作製した。暗室内でハロゲンランプを光源としてサンプルからの反射光を目視し、下記の評価基準で白ボケを評価した。
○:白ボケはないが、ヘイズ値が高い。
×:白ボケもあり、ヘイズ値も高い。
5)視感度反射率の測定
測定面の裏面反射を除くため、裏面をサンドペーパーで粗し、黒色塗料で塗りつぶしたものを分光光度計〔日本分光(株)製、商品名:U−best560〕により、光の波長380〜780nmの5°、−5°正反射スペクトルを測定した。得られる380〜780nmの分光反射率と、CIE標準イルミナントD65の相対分光分布を用いて、JIS Z8701で規定されているXYZ表色系における、反射による物体色の三刺激値Yを視感度反射率とした。
<塗布液の製造例>
(ハードコート層塗布液の製造)
アンチモンドープ酸化錫の30%メチルエチルケトン分散液〔石原産業(株)製、アンチモンドープ酸化錫の平均粒子径98nm、SNS−10M〕250質量部、多官能アクリレート化合物〔6官能のジペンタエリスリトールヘキサアクリレートと5官能のジペンタエリスリトールペンタアクリレートとの混合物、平均官能基数5.5、日本化薬(株)製、DPHA、硬化物の屈折率:1.49〕25質量部およびUVラジカル開始剤〔チバスペシャリティケミカルズ(株)製、イルガキュア184〕5質量部を攪拌混合し、ハードコート層塗布液とした。このハードコート層塗布液を重合硬化したハードコート層の屈折率は1.65であった。
(変性コロイダルシリカ粒子Aの製造)
フラスコにコロイダルシリカ微粒子〔日産化学工業(株)製、商品名:IPA−ST、平均粒子径は15nm〕200部とγ‐アクリロイルオキシプロピルトリメトキシシラン〔信越化学工業(株)製、商品名:KBM5103〕37.7部を投入して混合した。次いで、十分に撹拌しながら78℃で4時間加熱を行った。加熱終了後、反応液を常温まで冷却して変性コロイダルシリカ微粒子Aを得た。変性コロイダルシリカ微粒子Aの屈折率は1.45であった。
(変性コロイダルシリカ微粒子Bの製造)
コロイダルシリカ微粒子〔日産化学工業(株)製、商品名:IPA−ST−L、平均粒子径は50nm〕200部を用いた以外は、変性コロイダルシリカ微粒子Aの製造例に準じて変性コロイダルシリカ微粒子Bを得た。変性コロイダルシリカ微粒子Bの屈折率は1.45であった。
(変性コロイダルシリカ微粒子Cの製造)
コロイダルシリカ微粒子〔日産化学工業(株)製、商品名:IPA−ST−ZL、平均粒子径は100nm〕200部を用いた以外は、変性コロイダルシリカ微粒子Aの製造例に準じて変性コロイダルシリカ微粒子Cを得た。変性コロイダルシリカ微粒子Cの屈折率は1.45であった。
(変性中空シリカ微粒子の製造)
フラスコにイソプロパノール(IPA)分散中空シリカゾル〔商品名:ELCOM NY−1001SIV、固形分濃度20質量%、平均粒子径60nm、屈折率1.32、触媒化成(株)製〕2000部、γ−アクリロイルオキシプロピルトリメトキシシラン〔商品名:KBM5103、信越化学工業(株)製〕70部、蒸留水80部を混合して変性中空シリカゾル用塗布液を得た。その後、4時間加熱還流(反応温度:77℃)を行い、加水分解反応および縮合反応を行い、変性中空シリカ微粒子を得た。
(低屈折率層塗布液Aの製造)
バインダーとして含フッ素モノマー(16FDA、(CH2=CHCOOCH2)2C8F16、硬化物の屈折率:1.42)80質量部と、変性コロイダルシリカ微粒子A20質量部と、光重合開始剤〔チバスペシャルティケミカルズ(株)製、イルガキュア907〕5質量部、イソプロピルアルコール3200質量部とを混合して、低屈折率層塗布液を得た。低屈折率層塗布液の塗膜(低屈折率層)の屈折率層は1.43であった。バインダーの硬化物と微粒子の屈折率差および低屈折率層塗布液を重合硬化させた低屈折率層の屈折率を表1に示す。
(低屈折率層塗布液B〜Iの製造)
変性コロイダルシリカ微粒子、バインダー、開始剤(光重合開始剤)およびIPAを表1のとおりに配合して、低屈折率層塗布液Aの製造例に準じて低屈折率層液BからIを得た。バインダーの硬化物と微粒子の屈折率差および低屈折率層塗布液を重合硬化させた低屈折率層の屈折率を表1に示す。
〔接着剤の作製〕
(共重合ポリエステル樹脂の合成)
ジメチルテレフタレート100質量部、ジメチルイソフタレート100質量部、エチレングリコール30.3質量部、ネオペンチルグリコール150質量部、酢酸亜鉛0.1質量部および三酸化アンチモン0.1質量部をエステル交換反応容器に仕込み、180℃にコントロールして加熱し4時間反応させ、エステル交換反応を行った。その後、5−ナトリウムスルホイソフタル酸5質量部を添加し、240℃で1時間エステル化反応を行った。次に、250℃まで温度を上げ、系内を1.33×102Pa(1mmHg)の減圧にして2時間重縮合反応を行ない、共重合ポリエステル樹脂を得た。
(架橋剤の合成)
フラスコにイオン交換水300質量部を仕込み、窒素気流下で60℃に加温し、過硫酸アンモニウム0.3質量部および亜硝酸水素ナトリウム0.3質量部を添加した。その後、メタクリル酸メチル20.2質量部、2−イソプロペニルー2−オキサゾリン21.2質量部、ポリエチレンオキシドメタクリル酸45.5質量部およびアクリルアミド10.2質量部の混合物を4時間かけて滴下した。滴下終了後1時間撹拌を継続し、架橋剤の25質量%水分散体を得た。
(接着剤塗布液の調製)
前記共重合ポリエステル樹脂の30質量%水分散体65質量部、前記架橋剤の25質量%水分散体40質量部およびイオン交換水450質量部を混合して接着剤とした。
〔PETフィルムの作製〕
二軸延伸ポリエステルフィルム〔片面に接着膜が設けられているポリエチレンテレフタレートフィルム、東洋紡績(株)製、コスモシャインA4100、厚み100μm、屈折率1.65〕の接着膜のない面に、前記接着剤塗布液をグラビアコート法で塗布した。フィルム断面をSEM観察したところ、接着層の厚みは乾燥膜厚で15nmであった。
(実施例1)
上記PETフィルムの接着層上にハードコート液を、実膜厚1.0μm程度になるようにスピンコート法で塗布後、紫外線照射装置(アイグラフィック社製、120W高圧水銀灯)を用いて400mJの紫外線を照射して硬化させることにより、ハードコートフィルムを作製した。このハードコートフィルムの屈折率は1.64であった。
(実施例2〜5および比較例1〜4)
実施例1において、表1に示す低屈折率層塗布液B〜Iを塗布する以外は実施例1と同様にして実施例2〜5および比較例1〜4の反射防止フィルムB〜Iを作製した。得られた反射防止フィルムB〜Iについての評価結果を表2に示した。
Claims (1)
- PETフィルム上にPETフィルム表面から順に接着層、ハードコート層、低屈折率層がこの順で積層されている反射防止フィルムであって、
低屈折率層はバインダーと平均粒子径1〜50nmの変性コロイダルシリカ微粒子とを含む屈折率が1.43〜1.50の層であり、バインダーの硬化物と変性コロイダルシリカ微粒子との屈折率差が0.04以下であり、ハードコート層と低屈折率層との屈折率差が0.13以上0.24以下であることを特徴とする反射防止フィルム。