JP5424127B2 - Method of attaching an anticorrosion electrode to a concrete structure, and concrete structure - Google Patents

Method of attaching an anticorrosion electrode to a concrete structure, and concrete structure Download PDF

Info

Publication number
JP5424127B2
JP5424127B2 JP2010213591A JP2010213591A JP5424127B2 JP 5424127 B2 JP5424127 B2 JP 5424127B2 JP 2010213591 A JP2010213591 A JP 2010213591A JP 2010213591 A JP2010213591 A JP 2010213591A JP 5424127 B2 JP5424127 B2 JP 5424127B2
Authority
JP
Japan
Prior art keywords
electrode
sheet body
concrete
concrete structure
anticorrosion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2010213591A
Other languages
Japanese (ja)
Other versions
JP2012067360A (en
Inventor
敏和 峰松
三紀夫 若杉
浩司 山田
康弘 鈴木
山本  誠
篤志 鹿島
和也 本田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sumitomo Osaka Cement Co Ltd
Original Assignee
Sumitomo Osaka Cement Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sumitomo Osaka Cement Co Ltd filed Critical Sumitomo Osaka Cement Co Ltd
Priority to JP2010213591A priority Critical patent/JP5424127B2/en
Publication of JP2012067360A publication Critical patent/JP2012067360A/en
Application granted granted Critical
Publication of JP5424127B2 publication Critical patent/JP5424127B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、コンクリート構造物の電気防食に関し、特にコンクリート表面への電気防食電極の取り付け方法および電気防食電極が取り付けられたコンクリート構造物に関する。   The present invention relates to an anticorrosion of a concrete structure, and more particularly to a method for attaching an anticorrosion electrode to a concrete surface and a concrete structure to which an anticorrosion electrode is attached.

従来より、コンクリート構造物中の鉄筋などの鋼材の腐食を防止するために、コンクリート構造物にチタン等の耐食性金属からなる電気防食電極を設置し、電気防食電極を陽極、鋼材を陰極として鋼材に防食電流を供給する方法が知られている。   Conventionally, in order to prevent corrosion of steel materials such as reinforcing bars in concrete structures, an anticorrosion electrode made of corrosion-resistant metal such as titanium has been installed in the concrete structure, with the anticorrosion electrode as the anode and the steel material as the cathode. A method for supplying an anticorrosion current is known.

前記電気防食電極をコンクリートへの設置する方法としては下記特許文献1から5に記載されているような各種方法が知られている。
例えば、コンクリート表面に溝を切削し、該溝内に電極を設置して、モルタルなどのグラウト材で被覆する方法(特許文献1および2)や、溝内に設置した電極を絶縁材で保護する方法(特許文献3)などが知られている。
Various methods as described in Patent Documents 1 to 5 below are known as methods for installing the anticorrosion electrode on concrete.
For example, a groove is cut on a concrete surface, an electrode is placed in the groove, and a grout material such as mortar is coated (Patent Documents 1 and 2), or an electrode placed in the groove is protected with an insulating material. A method (Patent Document 3) is known.

あるいは、コンクリート表面に、陽極を設置した電極ホルダーをピンなどで固定するなどの方法がある(特許文献4および5)。   Or there exists a method of fixing the electrode holder which installed the anode on the concrete surface with a pin etc. (patent documents 4 and 5).

しかし、前記のようなコンクリート表面に溝を切削する方法では、まず、溝を形成してから、該溝内に電極を設置し、さらに電極の周囲にグラウトを充填して固定したり、電極を絶縁材で保護したりする工程が必要となり作業に手間がかかる。
特に、電極を設置する溝が横向きや下向きに開口している場合、つまり、天井や壁にあたる位置に電極を設置しようとすると、モルタルで電極を固定するまでの間、電極が溝から落下しないよう、電極を溝の内部に仮止めする必要があり、作業性がさらに悪いという問題がある。
However, in the method of cutting a groove on the concrete surface as described above, first, after forming the groove, an electrode is installed in the groove, and further, grout is filled around the electrode and fixed, A process of protecting with an insulating material is required, and work is troublesome.
In particular, if the groove where the electrode is installed opens sideways or downwards, that is, if the electrode is installed at a position corresponding to the ceiling or wall, the electrode will not fall from the groove until the electrode is fixed with mortar. There is a problem that it is necessary to temporarily fix the electrode inside the groove, and the workability is further deteriorated.

また、コンクリート表面に溝を形成する場合には、溝部においては鋼材までのコンクリートの厚みが薄くなるため、短絡を防止するためにコンクリートの厚みを増す作業が必要となる場合もある。   In addition, when grooves are formed on the concrete surface, the thickness of the concrete up to the steel material is reduced in the groove portion, and therefore it may be necessary to increase the thickness of the concrete to prevent a short circuit.

さらに、コンクリート表面に溝を形成する場合では溝を切削するためのコンクリートカッターやコンクリートチッパーなどの切削工具が必要であり、電極ホルダーをピンなどの固定具を用いて電極をコンクリ−ト表面に取り付ける場合では固定具を取り付ける孔をコンクリート表面に開けるためのコンクリートドリルなどの工具が必要であり、いずれにしても、電気またはエアー工具を使用する必要がある。
しかし、例えば、桁端部などのような作業スペースが狭い場所に電極を設置する場合には作業間隔が小さく、工具での施工が困難となることや電源の確保が困難であり、また切削のための工具を使用するためのコードやホースが邪魔になり作業性が非常に悪いという問題もある。
Furthermore, when a groove is formed on the concrete surface, a cutting tool such as a concrete cutter or a concrete chipper for cutting the groove is required, and the electrode holder is attached to the concrete surface using a fixture such as a pin. In some cases, a tool such as a concrete drill is required to open a hole for attaching the fixture in the concrete surface, and in any case, an electric or pneumatic tool must be used.
However, for example, when electrodes are installed in a narrow work space such as the end of a girder, the work interval is small, making it difficult to work with tools or securing a power source, and cutting. There is also a problem that the workability is very bad because the cord and the hose for using the tool for the purpose become an obstacle.

特開平4−116184号公報JP-A-4-116184 特開2002−371391号公報JP 2002-371391 A 特開2005−256132号公報JP 2005-256132 A 特開2006−322043号公報JP 2006-322043 A 特開2005−298940号公報JP 2005-298940 A

そこで、本発明は、設置作業が容易なコンクリート構造物への電気防食電極の取り付け方法、およびコンクリート構造物を提供することを課題とする。   Then, this invention makes it a subject to provide the attachment method of the anti-corrosion electrode to the concrete structure with easy installation work, and a concrete structure.

前記課題を解決するための手段として、内部に鋼材が設置されたコンクリート構造物の表面に、電気防食電極とシート体とを、前記電気防食電極が前記コンクリート構造物の表面に接触し、且つ前記シート体が、前記電気防食電極の外側を被覆するように固定し、 前記シート体とコンクリート構造物の表面との間にグラウトを注入することで、前記電気防食電極をコンクリート構造物に設置することを特徴とするコンクリート構造物への電気防食電極の取り付け方法を提供する。   As means for solving the above-mentioned problems, the surface of the concrete structure in which the steel material is installed is connected to the surface of the anticorrosion electrode and the sheet body, the electrode of the anticorrosion electrode is in contact with the surface of the concrete structure, and A sheet body is fixed so as to cover the outer side of the electrode protection electrode, and a grout is injected between the sheet body and the surface of the concrete structure, thereby installing the electrode protection electrode on the concrete structure. A method of attaching an anticorrosive electrode to a concrete structure characterized by the above.

本発明のコンクリート構造物への電気防食電極の取り付け方法は、前記のようにコンクリート表面に電気防食電極をシート体で被覆した状態でグラウトを注入して電気防食電極を固定するため、コンクリートの表面に溝を形成する必要がない。
よって、切削などによって溝を形成する工程が不要となり、簡単に電気防食電極の取り付け作業が行える。また、切削時に発生する粉塵などによる作業環境の悪化も防止できる。
The method of attaching the anticorrosion electrode to the concrete structure of the present invention is as described above, in which grout is injected in a state where the anticorrosion electrode is coated on the concrete surface with the sheet body to fix the anticorrosion electrode. It is not necessary to form a groove in.
Therefore, a step of forming a groove by cutting or the like is not necessary, and the work for attaching the anticorrosion electrode can be easily performed. In addition, it is possible to prevent deterioration of the work environment due to dust generated during cutting.

さらに、電気防食電極をグラウトで完全に固定するまでの間、シート体によってコンクリート表面に電気防食電極が固定されているため、たとえコンクリート面が下方を向いている面あるいは斜面や地面に対して垂直な側面であっても、電気防食電極が落下することがないため、どのような設置面に対しても作業が容易に行える。
また、コンクリート表面に溝を形成する必要がないため、鋼材が露出するおそれがなく、鋼材と電気防食電極との十分な距離を確保でき、電気分布が良好で、分極性にすぐれたコンクリート構造物が得られる。
Furthermore, since the anticorrosion electrode is fixed to the concrete surface by the sheet body until the electrocorrosion electrode is completely fixed with the grout, even if the concrete surface faces downward or is perpendicular to the slope or the ground. Even if it is a simple side surface, the anticorrosion electrode does not fall, so that it can be easily performed on any installation surface.
In addition, since there is no need to form grooves on the concrete surface, there is no risk of exposing the steel material, a sufficient distance between the steel material and the anti-corrosion electrode can be secured, the electrical distribution is good, and the polarizability is excellent. Is obtained.

また、前記シート体が、一面側に接着部を有するシート体であり、前記電気防食電極を前記シート体の接着部の一部に接着によって固定し、前記電気防食電極が接着によって固定されていない前記接着部によって前記コンクリート構造物の表面に前記シート体を設置することが好ましい。   In addition, the sheet body is a sheet body having an adhesive portion on one surface side, the electrocorrosion electrode is fixed to a part of the adhesive portion of the sheet body by adhesion, and the electrocorrosion electrode is not fixed by adhesion. It is preferable to install the sheet body on the surface of the concrete structure by the adhesive portion.

シート体が接着部を有するシート体である場合には、予め、電気防食電極をシート体に固定しておき、さらに電気防食電極が接着されていない接着部をコンクリート構造物表面に貼り付けることで、容易にシート体ごと電気防食電極をコンクリート表面に固定することができる。   In the case where the sheet body is a sheet body having an adhesive portion, the anticorrosion electrode is fixed to the sheet body in advance, and further, the adhesive portion to which the anticorrosion electrode is not adhered is pasted on the concrete structure surface. It is possible to easily fix the anticorrosion electrode together with the sheet body to the concrete surface.

尚、本発明における接着部は、シート体の一面側のうち、電気防食電極を固定する位置、および、コンクリート表面と接触する位置に設けられていればよく、シート体の一面側全体に接着部が設けられていることは必要ではない。
また、接着部の接着力は、少なくとも、電気防食電極をグラウトで固定するまでの間、電気防食電極をシート体に固定でき、且つシート体をコンクリート表面に固定できる程度の接着力があればよい。
In addition, the adhesion part in this invention should just be provided in the position which fixes an anti-corrosion electrode among the one surface side of a sheet | seat body, and the position which contacts a concrete surface. It is not necessary to be provided.
Also, the adhesive strength of the adhesive portion should be at least sufficient to fix the electrocorrosive electrode to the sheet body and to fix the sheet body to the concrete surface until the anticorrosive electrode is fixed by grouting. .

また、前記電気防食電極を、導電性シートを介して前記シート体に固定することが好ましい。   Moreover, it is preferable to fix the said anti-corrosion electrode to the said sheet | seat body through an electroconductive sheet.

導電性シートを介することで鋼材と電極との電流が流れやすくなるため防食効果がより高まり好ましい。   Since the electric current between the steel material and the electrode easily flows through the conductive sheet, the anticorrosion effect is further enhanced, which is preferable.

さらに、前記シート体をコンクリート表面に固定した後に、前記シート体に形成された切り込み部から前記グラウトを注入することが好ましい。   Furthermore, it is preferable to inject the grout from a cut portion formed in the sheet body after the sheet body is fixed to the concrete surface.

コンクリート表面にシート体を固定してからでも切り込み部からグラウトを注入でき、さらに作業効率がよい。   Even after fixing the sheet body to the concrete surface, grout can be injected from the cut section, and work efficiency is further improved.

また、前記グラウトが硬化した後に、前記シート体に小孔を形成することが好ましい。   Moreover, it is preferable to form a small hole in the sheet body after the grout is cured.

電極を設置した後に、電極と鋼材との電極反応によって酸素や水素などのガスが発生することがあるが、シート体に小孔を形成することで、これらのガスを逃すことができる。   After the electrodes are installed, gases such as oxygen and hydrogen may be generated by the electrode reaction between the electrodes and the steel material, but these gases can be released by forming small holes in the sheet body.

また、本発明のコンクリート構造物としては、コンクリートの内部に鋼材が設置されたコンクリート構造物であって、コンクリート表面に電気防食電極とシート体とが、前記電気防食電極が前記コンクリート構造物の表面に接触され、且つ前記シート体が、前記電気防食電極の外側を被覆するように固定され、前記シート体とコンクリート表面との間にグラウトが注入されて前記電気防食電極がコンクリート表面に設置されていることを特徴とする。   The concrete structure of the present invention is a concrete structure in which a steel material is installed inside the concrete, and the surface of the concrete structure is provided with the electrode and electrode body on the concrete surface. And the sheet body is fixed so as to cover the outer side of the electro-corrosion electrode, grout is injected between the sheet body and the concrete surface, and the electro-corrosion electrode is installed on the concrete surface. It is characterized by being.

本発明によれば、電気防食電極の設置作業を容易に行うことができる。
また、鋼材が露出するおそれがなく、鋼材と電気防食電極との十分な距離を確保でき、電気分布が良好で、分極性にすぐれたコンクリート構造物が得られる。
According to the present invention, it is possible to easily perform the installation work of the anticorrosion electrode.
Moreover, there is no possibility that the steel material is exposed, and a sufficient distance between the steel material and the anticorrosion electrode can be secured, and a concrete structure with good electrical distribution and excellent polarizability can be obtained.

(a)本発明のコンクリート構造物を示す上面図、(b)(a)のX-X断面図。(A) Top view which shows the concrete structure of this invention, (XX) XX sectional drawing of (a). (a)本発明の方法で使用される電極付きシート体を示す上面図、(b)(a)のY-Y断面図。(A) Top view which shows the sheet | seat body with an electrode used by the method of this invention, (b) YY sectional drawing of (a). (a)本発明の方法の一工程を示す上面図、(b)本発明の方法の一工程を示す上面図、(c)本発明の方法の一工程を示す一部断面図、(d)本発明の方法の一工程を示す一部断面図.(A) Top view showing one step of the method of the present invention, (b) Top view showing one step of the method of the present invention, (c) Partial sectional view showing one step of the method of the present invention, (d) The partial cross section figure which shows 1 process of the method of this invention. 実施例および比較例の分極量を示すグラフ。The graph which shows the amount of polarization of an Example and a comparative example.

以下、本発明に係る実施形態について説明する。
まず、本発明の電気防食電極が設置されたコンクリート構造物について、図1に基づいて説明する。
本実施形態のコンクリート構造物10は、図1(a)(b)に示すように、コンクリート1の表面に長尺状の電気防食電極2の一面側が接触するように配置されており、該電気防食電極2の他面側には導電性シート3を介してシート体4が設けられている。
該シート体4は、前記電気防食電極2および導電性シート3よりも幅の広い長尺状であり、前記電気防食電極2および導電性シート3を外側から覆うようにコンクリート1表面に接着部によって接着されている。
前記該シート体4とコンクリート1表面の間であって、前記電気防食電極2の幅方向の側部には、グラウト5が充填され、前記電気防食電極2を固定している。
Embodiments according to the present invention will be described below.
First, a concrete structure in which the anticorrosion electrode of the present invention is installed will be described with reference to FIG.
As shown in FIGS. 1 (a) and 1 (b), the concrete structure 10 of the present embodiment is disposed so that one surface side of the long anticorrosive electrode 2 is in contact with the surface of the concrete 1, A sheet body 4 is provided on the other surface side of the anticorrosive electrode 2 via a conductive sheet 3.
The sheet body 4 has an elongated shape that is wider than the cathodic protection electrode 2 and the conductive sheet 3, and is attached to the surface of the concrete 1 by an adhesive portion so as to cover the cathodic protection electrode 2 and the conductive sheet 3 from the outside. It is glued.
A grout 5 is filled between the sheet body 4 and the surface of the concrete 1 and in the width direction of the electrode 2 to fix the electrode 2.

前記電気防食電極2としては金属からなる陽極電極が用いられ、材質としては、陽極として用いられ且つ耐食性を有する金属であれば特に限定されるものではなく、例えば、白金メッキチタン製電極、高珪素鋳鉄製電極、黒鉛製電極、フェライト製電極または金属酸化物製電極等を使用することができる。   An anode electrode made of metal is used as the anticorrosion electrode 2, and the material is not particularly limited as long as it is a metal that is used as an anode and has corrosion resistance. For example, a platinum-plated titanium electrode, high silicon A cast iron electrode, a graphite electrode, a ferrite electrode, a metal oxide electrode, or the like can be used.

また、前記電気防食電極2は、棒状あるいは帯状などの長尺状のものが好ましく使用できるが、特にエキスパンドメタル状の網目を有する金属体を用いることが好ましい。
尚、エキスパンドメタル状とは、JIS G 3351に規定されたエキスパンドメタルの形状、またはこれと同様の形状をいう。
In addition, the cathodic electrode 2 can be preferably used in a long shape such as a rod shape or a belt shape, but it is particularly preferable to use a metal body having an expanded metal mesh.
The expanded metal shape refers to the expanded metal shape defined in JIS G 3351 or a shape similar thereto.

前記シート体4は、一面側に接着層4aを備えており、該一面側に前記導電性シート3が前記接着層4aを介して固定されている。
シート体4の材質は特に限定されるものではないが、前記電気防食電極2をコンクリート1表面に固定し、さらにその後、シート体4の内部にグラウトを充填するためある程度の伸縮性と、コンクリート構造物の外面に配置されるため防水性とを備えていることが好ましい。具体的には、例えば、アイオノマー樹脂製のフィルムやブチルゴムテープなどが好ましい。
The sheet body 4 includes an adhesive layer 4a on one surface side, and the conductive sheet 3 is fixed to the one surface side via the adhesive layer 4a.
Although the material of the sheet body 4 is not particularly limited, a certain degree of stretchability and a concrete structure are provided to fix the electrocorrosive electrode 2 to the concrete 1 surface and then fill the interior of the sheet body 4 with grout. Since it is arranged on the outer surface of the object, it is preferable to have waterproofness. Specifically, for example, an ionomer resin film or a butyl rubber tape is preferable.

前記シート体4には、複数の小孔(図示せず)が設けられており、電気防食電極2とコンクリート内部の鋼材との間で電流が流れることによる電極反応によって水素や酸素ガスが発生した場合に、外部にガスを逃がすことができる。   The sheet body 4 is provided with a plurality of small holes (not shown), and hydrogen or oxygen gas is generated by an electrode reaction caused by an electric current flowing between the anticorrosive electrode 2 and the steel material inside the concrete. In some cases, gas can escape to the outside.

前記シート体4の接着層4aは図2(b)に示すようにシート体4の一面側の全面に設けられていてもよく、一部に設けられていてもよいが、少なくとも前記導電性シート3を接着する部分、および、それ以外の場所であってコンクリート1表面と接する部分(本実施形態では、幅方向の両端部の位置4b)に接着層が形成され、該接着層によってシート体4がコンクリート1表面に取り付けられるように接着層が形成されることが必要である。   The adhesive layer 4a of the sheet body 4 may be provided on the entire surface on one side of the sheet body 4 as shown in FIG. 2B, or may be provided on a part thereof, but at least the conductive sheet. 3 and an adhesive layer is formed in a part other than that and in contact with the surface of the concrete 1 (in this embodiment, positions 4b at both ends in the width direction), and the sheet body 4 is formed by the adhesive layer. It is necessary that an adhesive layer be formed so that can be attached to the concrete 1 surface.

前記導電性シート3は導電性を有するシート材であり、一面側に接着層(図示せず)を備えており、該接着層を介して前記電気防食電極2と接着されており、他面側が前記シート体4の接着層4aによってシート体4と接着されている。   The conductive sheet 3 is a sheet material having conductivity, and is provided with an adhesive layer (not shown) on one surface side, and is bonded to the anticorrosion electrode 2 via the adhesive layer, and the other surface side is The sheet body 4 is bonded to the sheet body 4 by the adhesive layer 4 a of the sheet body 4.

本発明のコンクリート構造物において導電性シートのような導電層が用いられることは条件ではないが、このような導電層を介して前記電気防食電極2とコンクリート1の表面が接触されることで、防食電流の供給がより良好になるため好ましい。   In the concrete structure of the present invention, it is not a condition that a conductive layer such as a conductive sheet is used, but the surface of the anticorrosion electrode 2 and the concrete 1 is contacted through such a conductive layer, This is preferable because the supply of the anticorrosion current becomes better.

導電性シートの材質は特に限定されるものではないが、例えば、炭素、ニッケル、錫、銀などからなる基材をシート状に加工したものなどが好ましい。   Although the material of a conductive sheet is not specifically limited, For example, what processed the base material which consists of carbon, nickel, tin, silver etc. in the sheet form etc. are preferable.

前記グラウト材5は、前記電気防食電極2を固定するためにシート体4とコンクリート1の表面との間に充填されている。
前記グラウト材5としては、モルタルやセメントペースト等のグラウト材の充填性が良好であるため好適に用いられるが、特に限定されるものではない。
The grout material 5 is filled between the sheet body 4 and the surface of the concrete 1 in order to fix the cathodic protection electrode 2.
The grout material 5 is preferably used because it has good filling properties of grout materials such as mortar and cement paste, but is not particularly limited.

次に、電気防食電極2をコンクリート表面に取り付ける方法について説明する。
まず、前記のような網目状の電気防食電極2を、導電性シート3を介して長尺状のシート体4の一面側の幅方向の中央部に配置して、図2に示すような形成する。
Next, a method for attaching the anticorrosion electrode 2 to the concrete surface will be described.
First, the mesh-like cathodic protection electrode 2 as described above is arranged at the center in the width direction on the one surface side of the long sheet body 4 via the conductive sheet 3 to form as shown in FIG. To do.

本実施形態のシート体4の幅は、前記電気防食電極2の幅よりも広く形成されており、且つ一面側には接着層4aが設けられている。
前記導電性シート3はシート体4の中央部の接着層4a上に配置され、さらに導電性シート3の接着層の上面に前記電気防食電極2が接着される。
前記のようにシート体4の幅は、電気防食電極2の幅よりも広く形成されているため、電気防食電極2の幅方向の側部にはシート体4の両端部4bに接着層4aが露出している、図2(a)に示すような電極付きシート20が形成される。
The width | variety of the sheet | seat body 4 of this embodiment is formed wider than the width | variety of the said anti-corrosion electrode 2, and the contact bonding layer 4a is provided in the one surface side.
The conductive sheet 3 is disposed on the adhesive layer 4 a at the center of the sheet body 4, and the anticorrosion electrode 2 is bonded to the upper surface of the adhesive layer of the conductive sheet 3.
As described above, since the width of the sheet body 4 is formed wider than the width of the cathodic protection electrode 2, the adhesive layer 4 a is attached to both end portions 4 b of the sheet body 4 on the side in the width direction of the cathodic protection electrode 2. The exposed sheet | seat 20 with an electrode as shown to Fig.2 (a) is formed.

次に前記電極付きシート20をコンクリート1の表面に設置する。
まず、コンクリート1の表面を、洗浄し、必要に応じてコンクリートサンダーなどを用いて粗化する。
このような洗浄や粗化などの前処理を行うことは必ずしも条件ではないが、前記シート体4を接着しやすくなるという利点がある。
Next, the electrode-attached sheet 20 is installed on the surface of the concrete 1.
First, the surface of the concrete 1 is washed and roughened using a concrete sander or the like as necessary.
It is not always necessary to perform such pretreatments such as washing and roughening, but there is an advantage that the sheet body 4 can be easily adhered.

前記前処理を施したコンクリート1の表面に、前記電極付きシート20を図1(b)に示すように、前記電気防食電極2がコンクリート1表面に接触するように貼り付ける。この時、前記電気防食電極2の両側に露出している接着層4bをコンクリート1の表面に接触させてシート体4を固定する。   As shown in FIG. 1 (b), the electrode-attached sheet 20 is attached to the surface of the concrete 1 that has been subjected to the pretreatment so that the electrode 2 is in contact with the concrete 1 surface. At this time, the sheet body 4 is fixed by bringing the adhesive layers 4 b exposed on both sides of the anticorrosion electrode 2 into contact with the surface of the concrete 1.

次に、図3(a)に示すように、前記シート体4の上面にグラウト注入用の孔5を形成する。
このような孔5はシート体4にカッターなどで切り込みをいれることで容易に形成できる。前記孔5を設ける数や位置は、シート体4の長さや充填するグラウトの流動性などに合わせて任意の数や位置に設定することができるが、例えば、シート体4の長手方向に1個/1m間隔程度に形成することが好ましい。
前記のようにシート体4にカッターなどで切り込みを入れる際に、内側に位置する前記導電性シート3にもカッターなどの刃が到達するようにして、同時に切り込みを入れ前記導電性シート3にも孔3aを形成する。
Next, as shown in FIG. 3A, a grouting hole 5 is formed on the upper surface of the sheet body 4.
Such holes 5 can be easily formed by cutting the sheet body 4 with a cutter or the like. The number and position of the holes 5 can be set to any number or position according to the length of the sheet body 4 or the fluidity of the grout to be filled. For example, one hole is provided in the longitudinal direction of the sheet body 4. / It is preferable to form at intervals of about 1 m.
As described above, when the sheet body 4 is cut with a cutter or the like, the blade such as a cutter also reaches the conductive sheet 3 located on the inner side, and at the same time, a cut is made into the conductive sheet 3. Hole 3a is formed.

シート体4に穿設した孔5に、図3(b)に示すように、プラグ6を取り付ける。
前記プラグ6としては、通常コンクリート構造物のひび割れにモルタルを注入するために用いられる注入プラグが使用できる。
さらに、該プラグ6から、注入ポンプ7を用いてモルタルを注入し(図3(c))、このモルタルが硬化することで電気防食電極2が固定される。
この時、前記電気防食電極2は網目状であるため、プラグ6から注入されたモルタルは、シート体4の孔5、導電性シート3の孔3aから電気防食電極2まで到達し、さらに電気防食電極2の網目の隙間を通過して、電極付きシート20とコンクリート1の表面の間にまんべんなくゆきわたって注入される。
A plug 6 is attached to the hole 5 formed in the sheet body 4 as shown in FIG.
As the plug 6, an injection plug that is usually used for injecting mortar into a crack in a concrete structure can be used.
Further, mortar is injected from the plug 6 by using an injection pump 7 (FIG. 3C), and the mortar is hardened, so that the anticorrosion electrode 2 is fixed.
At this time, since the cathodic protection electrode 2 has a mesh shape, the mortar injected from the plug 6 reaches the cathodic protection electrode 2 from the hole 5 of the sheet body 4 and the hole 3a of the conductive sheet 3, and further the cathodic protection. It passes through the gaps in the mesh of the electrode 2 and is injected evenly between the sheet 20 with electrode and the surface of the concrete 1.

さらに、グラウトが完全に硬化してから、図3(d)に示すような、スパイクローラー8を用いてシート体4にガス抜き用の小孔を複数設けてもよい。   Further, after the grout is completely cured, a plurality of small holes for degassing may be provided in the sheet body 4 using the spike roller 8 as shown in FIG.

前記方法で電気防食電極をコンクリート構造物に取り付けるので、コンクリート表面に溝などを形成することなく簡単に電気防食電極の取り付け作業が行える。
しかも、電気防食電極をグラウトで完全に固定するまでの間、シート体でコンクリート表面に固定させておくことができるので、例えば、電気防食電極を構造物の下向きの面、斜面や側面などに取り付ける場合であっても、シート体で電気防食電極を固定しておくことでき、作業性が良好である。
Since the anticorrosion electrode is attached to the concrete structure by the above-described method, it is possible to easily attach the anticorrosion electrode without forming a groove or the like on the concrete surface.
Moreover, until the electrode is completely fixed with grout, it can be fixed to the concrete surface with a sheet body. For example, the electrode is attached to the downward surface, slope or side of the structure. Even in this case, the anticorrosion electrode can be fixed by the sheet body, and the workability is good.

尚、本実施形態では、シート体4の一面側に設けられた接着層によってシート体とコンクリート表面を固定したが、シート体4とコンクリート表面の固定手段はこのような接着層に限らず、例えば、接着テープなどでコンクリート表面に止めつけてもよい。
シート体4がコンクリート表面へ固定されている状態は、少なくとも充填されたグラウトが硬化するまでの間維持されていれば、電気防食電極の設置は可能である。
但し、シート体4によって電極外面が被覆されている場合には、電極が露出することを確実に防止できるため、電極の取り付け後にもシート体4で覆われていることが好ましい。
In the present embodiment, the sheet body and the concrete surface are fixed by the adhesive layer provided on the one surface side of the sheet body 4, but the fixing means for the sheet body 4 and the concrete surface is not limited to such an adhesive layer, for example, It may be fixed to the concrete surface with an adhesive tape or the like.
If the state where the sheet body 4 is fixed to the concrete surface is maintained at least until the filled grout is hardened, it is possible to install an anticorrosion electrode.
However, when the outer surface of the electrode is covered with the sheet body 4, it is preferable that the electrode body is covered with the sheet body 4 even after the electrode is attached because the electrode can be reliably prevented from being exposed.

また、本実施形態ではシート体4にグラウト注入用の孔を設けて、該孔からグラウトを注入したが、グラウトの注入箇所は孔に限らず、例えば、シート体とコンクリート表面の接触箇所の一部を非接着にしておき、該非接着箇所からグラウトを注入してもよい。   Further, in this embodiment, the sheet body 4 is provided with a hole for grout injection, and grout is injected from the hole. However, the grout injection position is not limited to the hole, for example, one of the contact points between the sheet body and the concrete surface. The part may be left unbonded, and grout may be injected from the non-bonded portion.

以下、本発明の実施例について説明する。   Examples of the present invention will be described below.

(実施例)
長さ3m、高さ2.5m、厚さ20cmのコンクリート壁に、直径13mm(D13)の鉄筋を高さ方向に20cm間隔で複数本、壁面の表面から30mmの深さに埋設したコンクリートを試験対象とした。
実施例として、前記コンクリート壁面表面に長さ50cmの2本の電極(エルガードチタンリボンメッシュ#100、エルガード社製)を、前記壁面の中央部であって、前記鉄筋の上部に位置する付近に、高さ方向に15cm間隔で配置し、シート材(スコッチ強力防水補修テープ50mm幅、住友スリーエム株式会社製)、および導電性シート材(導電性メッシュテープ#2465RY、住友スリーエム株式会社製)を用いて、前記の方法で、シート材および導電性シート材によってコンクリート表面に前記電極を固定し、その後カッターで適宜数箇所に孔をあけ、該孔にプラグ(グラウトプラグA、日本シーカ株式会社製)からグラウト材(ハイスタッフ、日鉄セメント株式会社製)を注入して,28日放置し硬化させたものを準備した。
(Example)
Test concrete with a 3m long, 2.5m high, 20cm thick concrete wall with multiple 13mm (D13) diameter rebars at 20cm intervals in the height direction and 30mm deep from the wall surface. Targeted.
As an example, two electrodes (Elgard titanium ribbon mesh # 100, manufactured by Elgard Co., Ltd.) having a length of 50 cm are placed on the concrete wall surface in the vicinity of the central portion of the wall surface and located above the reinforcing bar. , Arranged at 15 cm intervals in the height direction, using a sheet material (50 mm wide Scotch waterproof waterproofing repair tape, manufactured by Sumitomo 3M Limited), and a conductive sheet material (conductive mesh tape # 2465RY, manufactured by Sumitomo 3M Limited) Then, the electrode is fixed to the concrete surface with the sheet material and the conductive sheet material by the above-mentioned method, and then holes are appropriately drilled with a cutter, and plugs are formed in the holes (grout plug A, manufactured by Nihon Sika Co., Ltd.). A grout material (High Stuff, manufactured by Nittetsu Cement Co., Ltd.) was poured from the ground, and left for 28 days to harden.

(比較例1)
比較例1として、前記実施例と同様のコンクリート表面の前記電極を配置した位置と略同じ位置に、深さ20mm,幅20mm、長さ50cmの溝を2本形成し、内部に実施例と同様の電極を埋設して、上からモルタル材で固定したものを準備した。
尚、この時の2本の電極の間隔は10cmであった。
(Comparative Example 1)
As Comparative Example 1, two grooves having a depth of 20 mm, a width of 20 mm, and a length of 50 cm are formed at substantially the same position as the position of the electrode on the concrete surface similar to that of the above example, and the same as in the example. The electrode was embedded and fixed with mortar from above.
At this time, the distance between the two electrodes was 10 cm.

(比較例2)
比較例2として、前記比較例1と、電極の間隔を20cmにした以外は、同様にしたものを準備した。
前記実施例、比較例1および2の分極試験(E-log I試験)をそれぞれ行った。
分極試験は、土木学会の「電気化学的防食工法設計施工指針」に記載の方法に従って行った。
(Comparative Example 2)
Comparative Example 2 was prepared in the same manner as Comparative Example 1 except that the distance between the electrodes was 20 cm.
The polarization test (E-log I test) of the above Example and Comparative Examples 1 and 2 was performed, respectively.
The polarization test was performed according to the method described in the “Design Guidelines for Electrochemical Corrosion Protection Method” of the Japan Society of Civil Engineers.

使用装置は下記のとおりであり、測定電圧、電流は表1に示すとおりである。
通電試験装置;ポテンショガルバノスタッド(HA−151A、北斗電工株式会社製)
電位測定機器;高入力抵抗マルチメータ(734、横河電気株式会社製)
照合電極;鉛照合電極(PbM−5型、日本防蝕工業株式会社製)
The apparatus used is as follows, and the measurement voltage and current are as shown in Table 1.
Energization test equipment; potentiogalvano stud (HA-151A, manufactured by Hokuto Denko Co., Ltd.)
Potential measurement equipment: High input resistance multimeter (734, manufactured by Yokogawa Electric Corporation)
Reference electrode: Lead reference electrode (PbM-5, manufactured by Nippon Corrosion Protection Co., Ltd.)

Figure 0005424127
Figure 0005424127

測定結果を図4に示す。
図4のグラフより、実施例は電極間の距離が10cm比較例1よりも5cm電極間が広いにもかかわらず、比較例1と同程度の分極量であることが明らかである。すなわち、実施例は電流分布が良好なコンクリート構造物であるといえる。
従って、電極の設置間隔を広くとることができ、電極の設置数や設置面積を減らすことができる。
The measurement results are shown in FIG.
From the graph of FIG. 4, it is apparent that the example has the same amount of polarization as that of Comparative Example 1 although the distance between the electrodes is 5 cm longer than that of Comparative Example 1 as compared with 10 cm. That is, it can be said that an Example is a concrete structure with favorable electric current distribution.
Therefore, it is possible to widen the installation interval of the electrodes, and it is possible to reduce the number and installation area of the electrodes.

1:コンクリート、
2:電気防食電極、
3:導電性シート、
4:シート体、
5:グラウト、
10:コンクリート構造
1: Concrete,
2: Electrocorrosive electrode,
3: Conductive sheet,
4: Sheet body,
5: Grout,
10: Concrete structure

Claims (7)

内部に鋼材が設置されたコンクリート構造物の表面に、電気防食電極とシート体とを、前記電気防食電極が前記コンクリート構造物の表面に接触し、且つ前記シート体が、前記電気防食電極の外側を被覆するように固定し、
前記シート体とコンクリート構造物の表面との間にグラウトを注入することで、
前記電気防食電極をコンクリート構造物に設置することを特徴とするコンクリート構造物への電気防食電極の取り付け方法。
On the surface of the concrete structure in which steel material is installed, the anticorrosion electrode and the sheet body, the electrocorrosion electrode is in contact with the surface of the concrete structure, and the sheet body is outside the electrocorrosion electrode. Fixed to cover,
By injecting grout between the sheet body and the surface of the concrete structure,
A method of attaching an anticorrosion electrode to a concrete structure, wherein the electrocorrosion electrode is installed in the concrete structure.
前記シート体が、一面側に接着部を有するシート体であり、前記電気防食電極を前記シート体の接着部の一部に接着によって固定し、前記電気防食電極が接着によって固定されていない前記接着部によって前記コンクリート構造物の表面に前記シート体を設置する請求項1に記載のコンクリート構造物への電気防食電極の取り付け方法。   The sheet body is a sheet body having an adhesive portion on one surface side, the electro-corrosive electrode is fixed to a part of the adhesive portion of the sheet body by adhesion, and the electro-corrosion electrode is not fixed by adhesion The method of attaching an anticorrosion electrode to a concrete structure according to claim 1, wherein the sheet body is installed on the surface of the concrete structure by a portion. 前記電気防食電極を、導電性シートを介して前記シート体に固定する請求項1または請求項2に記載のコンクリート構造物への電気防食電極の取り付け方法。   The method for attaching the anticorrosion electrode to the concrete structure according to claim 1 or 2, wherein the electrocorrosion electrode is fixed to the sheet body via a conductive sheet. 前記シート体をコンクリート構造物の表面に固定した後に、前記シート体に設けられた切り込み部から前記グラウトを注入する請求項1乃至請求項3のいずれか1項に記載のコンクリート構造物への電気防食電極の取り付け方法。   The electricity to the concrete structure according to any one of claims 1 to 3, wherein the grout is injected from a cut portion provided in the sheet body after the sheet body is fixed to the surface of the concrete structure. How to install anticorrosion electrodes. 前記グラウトが硬化した後に、前記シート体に小孔を形成する請求項1乃至請求項4のいずれか1項に記載のコンクリート構造物への電気防食電極の取り付け方法。   The method of attaching an anticorrosion electrode to a concrete structure according to any one of claims 1 to 4, wherein a small hole is formed in the sheet body after the grout is cured. コンクリートの内部に鋼材が設置されたコンクリート構造物であって、コンクリート表面に電気防食電極とシート体とが、前記電気防食電極が前記コンクリート構造物の表面に接触され、且つ前記シート体が、前記電気防食電極の外側を被覆するように固定され、前記シート体とコンクリート表面との間にグラウトが注入されて前記電気防食電極がコンクリート表面に設置されていることを特徴とするコンクリート構造物。   A concrete structure in which a steel material is installed inside concrete, and the anticorrosion electrode and the sheet body are contacted with the concrete surface, the electrocorrosion electrode is in contact with the surface of the concrete structure, and the sheet body is A concrete structure which is fixed so as to cover an outer side of an electrode for anticorrosion, and in which grout is injected between the sheet body and the surface of the concrete so that the electrode for anticorrosion is installed on the surface of the concrete. 前記シート体が、一面側に接着部を有し、前記接着部の一部を介して電気防食電極とシート体が固定され、前記電気防食電極が固定されていない接着部によって前記コンクリート表面に前記シート体が固定されている請求項6に記載のコンクリート構造物。   The sheet body has an adhesive portion on one surface side, and the anticorrosion electrode and the sheet body are fixed through a part of the adhesive portion, and the concrete surface is bonded to the concrete surface by the adhesive portion to which the electrocorrosion protection electrode is not fixed. The concrete structure according to claim 6, wherein the sheet body is fixed.
JP2010213591A 2010-09-24 2010-09-24 Method of attaching an anticorrosion electrode to a concrete structure, and concrete structure Active JP5424127B2 (en)