JP5413129B2 - Solid battery manufacturing method - Google Patents
Solid battery manufacturing method Download PDFInfo
- Publication number
- JP5413129B2 JP5413129B2 JP2009250412A JP2009250412A JP5413129B2 JP 5413129 B2 JP5413129 B2 JP 5413129B2 JP 2009250412 A JP2009250412 A JP 2009250412A JP 2009250412 A JP2009250412 A JP 2009250412A JP 5413129 B2 JP5413129 B2 JP 5413129B2
- Authority
- JP
- Japan
- Prior art keywords
- active material
- material layer
- electrode active
- positive electrode
- negative electrode
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、電極同士の接触を未然に防止する固体電池の製造方法に関する。
The present invention relates to a method for manufacturing a solid battery that prevents the electrodes from contacting each other.
二次電池は、化学反応に伴う化学エネルギーの減少分を電気エネルギーに変換し、放電を行うことができる他に、放電時と逆方向に電流を流すことにより、電気エネルギーを化学エネルギーに変換して蓄積(充電)することが可能な電池のことである。二次電池の中でも、リチウム二次電池は、エネルギー密度が高いため、ノート型のパーソナルコンピューターや、携帯電話機等の電源として幅広く応用されている。 The secondary battery can convert the decrease in chemical energy associated with the chemical reaction into electrical energy and perform discharge. In addition, the secondary battery converts electrical energy into chemical energy by flowing current in the opposite direction to that during discharge. A battery that can be stored (charged). Among secondary batteries, lithium secondary batteries are widely used as power sources for notebook personal computers, mobile phones, and the like because of their high energy density.
リチウム二次電池においては、負極活物質としてグラファイト(C6と表現する)を用いた場合、放電時において、負極では(1)式の反応が進行する。
C6Li → C6 + Li+ + e− (1)
(1)式で生じる電子は、外部回路を経由し、外部の負荷で仕事をした後、正極に到達する。そして、(1)式で生じたリチウムイオン(Li+)は、負極と正極に挟持された電解質内を、負極側から正極側に電気浸透により移動する。
In the lithium secondary battery, when graphite (expressed as C 6 ) is used as the negative electrode active material, the reaction of the formula (1) proceeds at the negative electrode during discharge.
C 6 Li → C 6 + Li + + e − (1)
The electrons generated by the equation (1) reach the positive electrode after working with an external load via an external circuit. Then, lithium ions (Li + ) generated in the formula (1) move from the negative electrode side to the positive electrode side by electroosmosis in the electrolyte sandwiched between the negative electrode and the positive electrode.
また、正極活物質としてコバルト酸リチウム(Li0.4CoO2)を用いた場合、放電時において、正極では(2)式の反応が進行する。
Li0.4CoO2 + 0.6Li+ + 0.6e− → LiCoO2 (2)
充電時においては、負極及び正極において、それぞれ上記式(1)及び式(2)の逆反応が進行し、負極においてはグラファイトインターカレーションによりリチウムが入り込んだグラファイト(C6Li)が、正極においてはコバルト酸リチウム(Li0.4CoO2)が再生するため、再放電が可能となる。
Further, when lithium cobaltate (Li 0.4 CoO 2 ) is used as the positive electrode active material, the reaction of the formula (2) proceeds at the positive electrode during discharge.
Li 0.4 CoO 2 + 0.6 Li + + 0.6e − → LiCoO 2 (2)
At the time of charging, the reverse reactions of the above formulas (1) and (2) proceed in the negative electrode and the positive electrode, respectively, and in the negative electrode, graphite (C 6 Li) into which lithium has entered by graphite intercalation is present in the positive electrode. Since lithium cobaltate (Li 0.4 CoO 2 ) is regenerated, re-discharge is possible.
一般に電池の技術において、正極−負極間の絶縁の確保は、電池の高耐久性及び長寿命化を図る上で最も重要な課題の一つである。特に電池にとって、電極同士の接触による短絡は、発電性能を大幅に損なう致命的な欠陥となりやすい。
このような電極間の接触回避を図る技術は、これまでにも開発されている。特許文献1には、互いに向い合う第1および第2の表面をそれぞれ有し、積層された第1および第2の集電体と、前記第1の表面上に形成され、正極および負極のいずれか一方をなす第1の活物質層と、前記第2の表面上に形成され、前記第1の活物質層と対向し、正極および負極のいずれか他方をなす第2の活物質層と、前記第1の活物質層と前記第2の活物質層との間に配置された固体電解質とを備え、前記固体電解質の端部は、前記第1の表面上に接触し、前記第1の活物質層は、前記固体電解質によって覆われている、積層型電池の技術が開示されている。
In general, in battery technology, securing insulation between a positive electrode and a negative electrode is one of the most important issues for achieving high durability and long life of the battery. In particular, for a battery, a short circuit due to contact between electrodes tends to be a fatal defect that greatly impairs power generation performance.
Techniques for avoiding such contact between electrodes have been developed so far.
特許文献1に開示された積層型電池は、当該文献の明細書中の25段落及び図2に記載されているように、実際には、第1および第2の集電体の間に絶縁部材を必要とする構成である。したがって、このような従来技術の電池を製造するためには、絶縁部材を形成する工程が別途必要であり、生産性が悪いという問題点があった。
本発明は、上記実状を鑑みて成し遂げられたものであり、電極同士の接触を未然に防止する固体電池、及び当該固体電池の製造方法を提供することを目的とする。
The stacked battery disclosed in
The present invention has been accomplished in view of the above circumstances, and an object of the present invention is to provide a solid battery that prevents contact between electrodes and a method for manufacturing the solid battery.
本発明の固体電池の製造方法は、少なくとも外周縁部の一部又は全部の厚さが最も厚く、且つ、外周縁部以外の部位に厚さが最も薄い部位を有する固体電解質膜を作製する工程、前記固体電解質膜の厚さが最も薄い部位を含み、且つ、前記固体電解質膜の厚さが最も厚い部位を含まない部分の一面側に正極活物質層を形成し、当該部分の他面側に負極活物質層を形成する工程、並びに、前記電極活物質層を両面に形成した前記固体電解質膜を、集電体で挟持する工程を有することを特徴とする。 The method for producing a solid state battery of the present invention is a process for producing a solid electrolyte membrane having at least a part of or the entire thickness of the outer peripheral edge and the thinnest part at a portion other than the outer peripheral edge. A positive electrode active material layer is formed on one side of a portion including the portion where the thickness of the solid electrolyte membrane is the smallest and the portion where the thickness of the solid electrolyte membrane is not the thickest; Forming a negative electrode active material layer, and sandwiching the solid electrolyte membrane having the electrode active material layer formed on both sides with a current collector.
このような構成の製造方法によって、上述した固体電池を製造することができる。
また、本発明の製造方法においては、前記正極活物質層及び前記負極活物質層を形成する工程において、前記固体電解質膜の厚さが最も薄い部位を含み、且つ、当該固体電解質膜の厚さが最も厚い部位を含まない部分を、前記正極活物質層及び前記負極活物質層で挟持するように、前記正極活物質層及び前記負極活物質層を形成することが好ましい。
The above-described solid battery can be manufactured by the manufacturing method having such a configuration.
Further, in the production method of the present invention, in the step of forming the positive electrode active material layer and the negative electrode active material layer, the solid electrolyte membrane includes the thinnest portion, and the thickness of the solid electrolyte membrane It is preferable to form the positive electrode active material layer and the negative electrode active material layer so that a portion not including the thickest portion is sandwiched between the positive electrode active material layer and the negative electrode active material layer.
本発明によれば、前記固体電解質の外周縁部の厚さが、前記正極活物質層及び前記負極活物質層の間に介在する前記固体電解質の厚さよりも厚いことにより、前記正極活物質層又は前記負極活物質層の端部が折れ曲がることによる電極同士の接触や、振動等による端部の滑落に伴う反対極への混入等を防止できる。 According to the present invention, the thickness of the outer peripheral edge of the solid electrolyte is thicker than the thickness of the solid electrolyte interposed between the positive electrode active material layer and the negative electrode active material layer. Alternatively, it is possible to prevent contact between the electrodes due to the end of the negative electrode active material layer being bent, mixing into the opposite electrode due to sliding of the end due to vibration or the like.
1.固体電池
本発明の固体電池は、固体電解質の一面側に正極活物質層を有し、他面側に負極活物質層を有する積層体と、当該積層体を挟持する一対の集電体とを備える固体電池であって、前記正極活物質層及び前記負極活物質層のうち少なくとも一方は、前記固体電解質及び前記集電体よりも一回り小さい寸法及び形状を有し、且つ、前記正極活物質層及び/又は前記負極活物質層の外周からはみ出した一対の前記集電体の外周縁部の間に介在する前記固体電解質の厚さが、前記正極活物質層及び前記負極活物質層の間に介在する前記固体電解質の厚さよりも厚いことを特徴とする。
1. Solid Battery The solid battery of the present invention comprises a laminate having a positive electrode active material layer on one side of a solid electrolyte and a negative electrode active material layer on the other side, and a pair of current collectors sandwiching the laminate. A positive electrode active material layer, wherein at least one of the positive electrode active material layer and the negative electrode active material layer has a size and shape that is slightly smaller than the solid electrolyte and the current collector. The thickness of the solid electrolyte interposed between the outer peripheral edges of the pair of current collectors protruding from the outer periphery of the layer and / or the negative electrode active material layer is between the positive electrode active material layer and the negative electrode active material layer. The solid electrolyte is thicker than the thickness of the solid electrolyte.
本発明でいう「固体電池」とは、電極、電解質等の各要素がすべて固体である電池のことを指す。したがって、例えば、電解質として液体電解質を用いた電池は、本発明には含まれない。
なお、本発明の固体電池の典型例としては、全固体リチウム二次電池を挙げることができる。以下、本発明が全固体リチウム二次電池の場合について詳細に述べる。
The “solid battery” in the present invention refers to a battery in which all elements such as electrodes and electrolytes are solid. Therefore, for example, a battery using a liquid electrolyte as the electrolyte is not included in the present invention.
A typical example of the solid state battery of the present invention is an all-solid lithium secondary battery. Hereinafter, the case where the present invention is an all-solid lithium secondary battery will be described in detail.
市販のリチウム二次電池は、電解質として可燃性の有機電解液を用いているため、安全対策による厳格な電圧、温度管理が求められている。一方、電解質として、安全性が高く取り扱い容易な固体電解質を用いる全固体リチウム二次電池においては、電池内の安全装置の簡素化が図れ、電池全体の省体積化が可能となる。 Since a commercially available lithium secondary battery uses a flammable organic electrolyte as an electrolyte, strict voltage and temperature management by safety measures is required. On the other hand, in an all-solid lithium secondary battery using a solid electrolyte that is safe and easy to handle as an electrolyte, the safety device in the battery can be simplified, and the volume of the entire battery can be reduced.
全固体リチウム二次電池においては、一般的に、正極集電層、正極活物質層、固体電解質層、負極活物質層、負極集電層を積層することで、単電池が構成される。
このような単電池の製造方法としては、以下の方法が挙げられる。まず、集電体の一方の面に電極活物質層が形成された電極に、さらに固体電解質層を形成することにより単電池を作製する方法があり、当該製造方法の代表例としては、2積層塗工法等が例示できる。しかし、当該方法により電池を精確に製造することは一般的に難しく、安定的に塗工するためには、従来技術よりもより高い精度が求められている。別の単電池の製造方法としては、固体電解質自体を膜化して、その膜を正極及び負極の間に挟んで積層することにより、単電池を作製する方法が挙げられる。当該方法は、固体電解質を支持体に含浸させて膜とすることで、固体電解質単体でシートとして取り扱うことができ、簡便な方法である。
In an all solid lithium secondary battery, a single battery is generally formed by laminating a positive electrode current collecting layer, a positive electrode active material layer, a solid electrolyte layer, a negative electrode active material layer, and a negative electrode current collecting layer.
The following method is mentioned as a manufacturing method of such a unit cell. First, there is a method of producing a unit cell by further forming a solid electrolyte layer on an electrode in which an electrode active material layer is formed on one surface of a current collector. A coating method etc. can be illustrated. However, it is generally difficult to accurately manufacture a battery by this method, and higher accuracy than that of the prior art is required for stable coating. As another method for manufacturing a unit cell, there is a method in which a unit cell is manufactured by forming a solid electrolyte into a film and stacking the film between a positive electrode and a negative electrode. This method is a simple method in which a solid electrolyte is impregnated into a film to form a membrane, so that the solid electrolyte alone can be handled as a sheet.
図7は、このような固体電解質シートを有する従来の全固体リチウム二次電池の一例を示す図であって、積層方向に切断した断面を模式的に示した図である。
図7(a)に示すように、従来の全固体リチウム二次電池500は、正極活物質層22及び正極集電体24を有する正極26と、負極活物質層23及び負極集電体25を有する負極27と、前記正極26及び前記負極27に挟持されるリチウムイオン伝導性固体電解質21を有する。
通常、正極及び負極の短絡を防ぐ観点から、正極活物質層22及び/又は負極活物質層23は、集電体24又は集電体25よりも一回り小さい寸法及び形状を有している。また、固体電解質21の、正極活物質層22及び負極活物質層23の間に介在する部位(一点鎖線28a上に存在する部位)の厚さは、正極活物質層22及び/又は負極活物質層23の外周からはみ出した集電体24又は集電体25の外周縁部の間に介在する部位(一点鎖線28b上に存在する部位)の厚さと略等しくなっている。
このような構造の電池においては、図7(a)において破線円で示すように、集電体と固体電解質との間に隙間が生じる。このような隙間がある場合、図7(b)に示すような、電極の端部の折れ曲がりによる集電体同士の接触や、図7(c)に示すような、振動などにより端部の滑落が起こった場合の電極同士の接触等が考えられ、いずれの場合も短絡につながる恐れがある。
このような短絡の問題の解決法の1つとして、上述した特許文献1に開示された技術のように、絶縁部材等を用いて電極の端部を保護する方法が挙げられる。しかし、上述したように、このような方法を採用した場合には、絶縁部材を形成する工程が別途必要となるため、生産性が悪いという問題点があった。
FIG. 7 is a view showing an example of a conventional all-solid lithium secondary battery having such a solid electrolyte sheet, and schematically showing a cross section cut in the stacking direction.
As shown in FIG. 7A, a conventional all solid lithium
Usually, from the viewpoint of preventing a short circuit between the positive electrode and the negative electrode, the positive electrode active material layer 22 and / or the negative electrode
In the battery having such a structure, a gap is generated between the current collector and the solid electrolyte as indicated by a broken-line circle in FIG. When there is such a gap, the ends slide down due to contact between the current collectors caused by bending of the ends of the electrodes as shown in FIG. 7B, or vibration as shown in FIG. 7C. In such a case, contact between electrodes may occur, and in either case, there is a risk of short circuit.
As one of solutions for such a short circuit problem, there is a method of protecting an end portion of an electrode using an insulating member or the like as in the technique disclosed in
発明者らは、鋭意努力の結果、固体電解質に電極の端部保護の機能を持たせることで、新たな部材を追加する必要なく、短絡を防止できることを見出した。従来技術においては、固体電解質層の厚さが積層体全面で同じ厚さであったため、固体電解質層が電極の端部保護の機能を持つことができなかったが、本発明においては、正極活物質層及び/又は負極活物質層の外周からはみ出した一対の集電体の外周縁部の間に介在する固体電解質の厚さを、正極活物質層及び負極活物質層の間に介在する固体電解質の厚さよりも厚く設定することで、固体電解質による端部保護機能を発揮させることができ、その結果、端部が折れ曲がることによる電極同士の接触や、振動等による端部の滑落による反対極への混入等を防止できる。 As a result of diligent efforts, the inventors have found that it is possible to prevent a short circuit without adding a new member by providing the solid electrolyte with a function of protecting the end of the electrode. In the prior art, since the thickness of the solid electrolyte layer was the same on the entire surface of the laminate, the solid electrolyte layer could not have the function of protecting the end of the electrode. The solid electrolyte interposed between the positive electrode active material layer and the negative electrode active material layer is defined as the thickness of the solid electrolyte interposed between the outer peripheral edges of the pair of current collectors protruding from the outer periphery of the material layer and / or the negative electrode active material layer. By setting the thickness thicker than the electrolyte thickness, the end protection function by the solid electrolyte can be exerted. Can be prevented.
以下、本発明の典型例について説明する。
図1は、本発明の固体電池の典型例を示す図であって、積層方向に切断した断面を模式的に示した図、及び、積層方向上部からみた模式図を並べて示したものである。
図1中の断面模式図に示すように、本発明の固体電池の典型例100は、正極活物質層2及び正極集電体4を有する正極6と、負極活物質層3及び負極集電体5を有する負極7と、前記正極6及び前記負極7に挟持されるリチウムイオン伝導性固体電解質1を有する。
図1中の積層方向上部からみた模式図には、正極集電体4及び負極集電体5の形状及び面積(実線)、リチウムイオン伝導性固体電解質1の形状及び面積(一点鎖線)、正極活物質層2及び負極活物質層3の形状及び面積(二点鎖線)をそれぞれ示している。この図から分かるように、本典型例においては、正極活物質層2及び負極活物質層3のいずれも、固体電解質1、正極集電体4及び負極集電体5よりも一回り小さい寸法及び形状を有し、且つ、両電極活物質層は、互いに略等しい寸法及び形状を有している。
図1中の断面模式図から分かるように、本典型例においては、固体電解質1の、正極活物質層2及び負極活物質層3の外周からはみ出した正極集電体4及び負極集電体5の外周縁部の間に介在する部位(一点鎖線8b上に存在する部位)の厚さ9bは、正極活物質層2及び負極活物質層3の間に介在する部位(一点鎖線8a上に存在する部位)の厚さ9aよりも厚くなっている。
このように、端部において固体電解質の厚さを厚くすることによって、特に正極活物質層及び負極活物質層の端部を保護し、電極同士の接触を防ぐことができる。
Hereinafter, typical examples of the present invention will be described.
FIG. 1 is a diagram showing a typical example of the solid state battery of the present invention, and shows a diagram schematically showing a cross section cut in the stacking direction and a schematic diagram viewed from the top in the stacking direction.
As shown in the schematic cross-sectional view of FIG. 1, a typical example 100 of the solid state battery of the present invention includes a
1 schematically shows the shape and area of the positive electrode current collector 4 and the negative electrode current collector 5 (solid line), the shape and area of the lithium ion conductive solid electrolyte 1 (dashed line), the positive electrode The shapes and areas (two-dot chain lines) of the active material layer 2 and the negative electrode
As can be seen from the schematic cross-sectional view in FIG. 1, in this typical example, the positive electrode current collector 4 and the negative electrode
In this way, by increasing the thickness of the solid electrolyte at the end portion, particularly the end portions of the positive electrode active material layer and the negative electrode active material layer can be protected and contact between the electrodes can be prevented.
図1に示したような典型例の他にも、異なる形状の固体電解質を用いた本発明の変形例について、以下に示す。
図2は、本発明の固体電池の第1の変形例を示す図であって、積層方向に切断した断面を模式的に示した図、及び、積層方向上部からみた模式図を並べて示したものである。
図2中の断面模式図に示すように、本発明の固体電池の第1の変形例200aの構成は、固体電解質1の形状以外は、上述した典型例100と同様である。
図2中の断面模式図から分かるように、本第1の変形例においては、固体電解質1の、正極活物質層2及び負極活物質層3の外周からはみ出した正極集電体4及び負極集電体5の外周縁部の間に介在する部位(一点鎖線8b上に存在する部位)の厚さ9bが、正極活物質層2及び負極活物質層3の間に介在する部位(一点鎖線8a上に存在する部位)の厚さ9aよりも厚くなっている。しかし、上述した典型例100とは異なり、本第1の変形例においては、厚さ9bは正極集電体4及び負極集電体5間の距離よりも短く設定され、且つ、固体電解質1の外周縁部の角の形状が丸みを帯び、このことにより本第1の変形例においては、電池の外周縁部において、固体電解質1と、各電極活物質層及び各集電体との間に隙間が生じている。
このように、たとえ固体電解質1と、各電極活物質層及び各集電体との間に隙間が生じていても、固体電解質が十分に正極活物質層及び負極活物質層の端部を保護できる形状を有していれば、電極同士の接触を防ぐことができる。
In addition to the typical example shown in FIG. 1, a modification of the present invention using a solid electrolyte having a different shape will be described below.
FIG. 2 is a diagram showing a first modification of the solid state battery of the present invention, which is a diagram schematically showing a cross section cut in the stacking direction, and a schematic diagram viewed from the top in the stacking direction. It is.
As shown in the schematic cross-sectional view in FIG. 2, the configuration of the first modification 200 a of the solid battery of the present invention is the same as that of the above-described typical example 100 except for the shape of the
As can be seen from the schematic cross-sectional view in FIG. 2, in the first modification, the positive electrode current collector 4 and the negative electrode current collector of the
Thus, even if a gap is generated between the
図3は、本発明の固体電池の第2の変形例を示す図であって、積層方向に切断した断面を模式的に示した図、及び、積層方向上部からみた模式図を並べて示したものである。
図3中の断面模式図に示すように、本発明の固体電池の第2の変形例200bの構成は、各電極活物質層の面積が異なること及び固体電解質1の形状以外は、上述した典型例100と同様である。
図3中の積層方向上部からみた模式図には、正極集電体4及び負極集電体5の形状及び面積(実線)、リチウムイオン伝導性固体電解質1の形状及び面積(一点鎖線)、正極活物質層2の形状及び面積(二点鎖線)、負極活物質層3の形状及び面積(破線)をそれぞれ示している。この図から分かるように、本第2の変形例においては、正極活物質層2及び負極活物質層3のいずれも、固体電解質1、正極集電体4及び負極集電体5よりも一回り小さい寸法及び形状を有し、且つ、負極活物質層3の面積は、正極活物質層2の面積よりもさらに小さい寸法及び形状を有している。
このように、たとえ正極活物質層2及び負極活物質層3の面積及び形状が互いに異なっていたとしても、固体電解質1の、正極活物質層2及び負極活物質層3の外周からはみ出した正極集電体4及び負極集電体5の外周縁部の間に介在する部位(一点鎖線8b上に存在する部位)の厚さ9bが、正極活物質層2及び負極活物質層3の間に介在する部位(一点鎖線8a上に存在する部位)の厚さ9aよりも厚くなっていれば、電極同士の接触を防ぐことができる。
FIG. 3 is a view showing a second modification of the solid state battery of the present invention, which is a diagram schematically showing a cross section cut in the stacking direction, and a schematic view seen from the top in the stacking direction. It is.
As shown in the schematic cross-sectional view in FIG. 3, the configuration of the
3 schematically shows the shape and area of the positive electrode current collector 4 and the negative electrode current collector 5 (solid line), the shape and area of the lithium ion conductive solid electrolyte 1 (dashed line), and the positive electrode. The shape and area (two-dot chain line) of the active material layer 2 and the shape and area (dashed line) of the negative electrode
Thus, even if the areas and shapes of the positive electrode active material layer 2 and the negative electrode
図4は、本発明の固体電池の第3の変形例の第三角法による正投影図であり、積層方向上部からみた模式図を正面図とした図である。
図4中の平面図(電池の断面の模式図に相当する図)に示すように、本発明の固体電池の第3の変形例200cの構成は、各電極活物質層の面積が異なること及び固体電解質1の形状以外は、上述した典型例100と同様である。
図4中の正面図には、正極集電体4及び負極集電体5の形状及び面積(実線)、リチウムイオン伝導性固体電解質1の形状及び面積(一点鎖線)、正極活物質層2の形状及び面積(二点鎖線)、負極活物質層3の形状及び面積(破線)をそれぞれ示している。この図から分かるように、本第3の変形例においては、正極活物質層2及び負極活物質層3のいずれも、固体電解質1、正極集電体4及び負極集電体5よりも一回り小さい寸法及び形状を有し、且つ、負極活物質層3の面積は、正極活物質層2の面積よりもさらに小さい寸法及び形状を有している。また、図4中の側面図から分かるように、正極活物質層2の1つの辺は、固体電解質1の1つの辺と略等しい長さである。
このように、たとえ正極活物質層2及び負極活物質層3の面積及び形状が互いに異なり、且つ、いずれかの電極活物質層の1つの辺が、固体電解質1の1つの辺と略等しい長さであったとしても、固体電解質1の、負極活物質層3の外周からはみ出した正極集電体4及び負極集電体5の外周縁部の間に介在する部位(一点鎖線8b上に存在する部位)の厚さ9b、及び、正極活物質層2及び負極活物質層3の外周からはみ出した正極集電体4及び負極集電体5の外周縁部の間に介在する部位(一点鎖線8c上に存在する部位)の厚さ9cのいずれの厚さも、正極活物質層2及び負極活物質層3の間に介在する部位(一点鎖線8a上に存在する部位)の厚さ9aよりも厚くなっていれば、電極同士の接触を防ぐことができる。
FIG. 4 is an orthographic projection view of the third modification of the solid state battery according to the present invention by the trigonometric method, and is a front view of a schematic view seen from the upper part in the stacking direction.
As shown in the plan view in FIG. 4 (a diagram corresponding to a schematic diagram of the cross section of the battery), the configuration of the
In the front view in FIG. 4, the shape and area (solid line) of the positive electrode current collector 4 and the negative electrode
Thus, even if the areas and shapes of the positive electrode active material layer 2 and the negative electrode
以下、全固体リチウム二次電池の構成要素である、正極及び負極、固体電解質、並びにその他の構成要素(セパレータ等)について、項を分けて説明する。 Hereinafter, the positive and negative electrodes, the solid electrolyte, and other components (separator and the like), which are components of the all-solid lithium secondary battery, will be described separately.
1−1.正極及び負極
本発明に係る全固体リチウム二次電池の正極は、好ましくは正極活物質を有する正極活物質層を有するものであり、通常、これに加えて、正極集電体、及び当該正極集電体に接続された正極リードを有するものである。
本発明に係る全固体リチウム二次電池の負極は、上述した本発明に係る負極用積層体を有するものであり、通常、これに加えて、当該負極用積層体の負極集電体に接続された負極リードを有するものである。
1-1. Positive electrode and negative electrode The positive electrode of the all-solid-state lithium secondary battery according to the present invention preferably has a positive electrode active material layer having a positive electrode active material, and in addition to this, a positive electrode current collector and the positive electrode current collector are usually added. It has a positive electrode lead connected to an electric body.
The negative electrode of the all-solid-state lithium secondary battery according to the present invention has the negative electrode laminate according to the present invention described above, and is usually connected to the negative electrode current collector of the negative electrode laminate in addition to this. It has a negative electrode lead.
(正極活物質層)
以下、正極として、正極活物質層を有する正極を採用した場合について説明する。
本発明に用いられる正極活物質としては、具体的には、LiCoO2、LiNi1/3Mn1/3Co1/3O2、LiNiPO4、LiMnPO4、LiNiO2、LiMn2O4、LiCoMnO4、Li2NiMn3O8、Li3Fe2(PO4)3及びLi3V2(PO4)3等を挙げることができる。これらの中でも、本発明においては、LiCoO2を正極活物質として用いることが好ましい。
(Positive electrode active material layer)
Hereinafter, the case where the positive electrode which has a positive electrode active material layer as a positive electrode is employ | adopted is demonstrated.
Specific examples of the positive electrode active material used in the present invention include LiCoO 2 , LiNi 1/3 Mn 1/3 Co 1/3 O 2 , LiNiPO 4 , LiMnPO 4 , LiNiO 2 , LiMn 2 O 4 , LiCoMnO 4. , Li 2 NiMn 3 O 8 , Li 3 Fe 2 (PO 4 ) 3, Li 3 V 2 (PO 4 ) 3 and the like. Among these, in the present invention, LiCoO 2 is preferably used as the positive electrode active material.
本発明に用いられる正極活物質層の厚さは、目的とするリチウム二次電池の用途等により異なるものであるが、10μm〜250μmの範囲内であるのが好ましく、20μm〜200μmの範囲内であるのが特に好ましく、特に30μm〜150μmの範囲内であることが最も好ましい。 The thickness of the positive electrode active material layer used in the present invention varies depending on the intended use of the lithium secondary battery, but is preferably in the range of 10 μm to 250 μm, and in the range of 20 μm to 200 μm. It is particularly preferred that it is most preferably in the range of 30 μm to 150 μm.
正極活物質の平均粒径としては、例えば1μm〜50μmの範囲内、中でも1μm〜20μmの範囲内、特に3μm〜5μmの範囲内であることが好ましい。正極活物質の平均粒径が小さすぎると、取り扱い性が悪くなる可能性があり、正極活物質の平均粒径が大きすぎると、平坦な正極活物質層を得るのが困難になる場合があるからである。なお、正極活物質の平均粒径は、例えば走査型電子顕微鏡(SEM)により観察される活物質担体の粒径を測定して、平均することにより求めることができる。 The average particle diameter of the positive electrode active material is, for example, preferably in the range of 1 μm to 50 μm, more preferably in the range of 1 μm to 20 μm, and particularly preferably in the range of 3 μm to 5 μm. If the average particle size of the positive electrode active material is too small, the handleability may be deteriorated. If the average particle size of the positive electrode active material is too large, it may be difficult to obtain a flat positive electrode active material layer. Because. The average particle diameter of the positive electrode active material can be determined by measuring and averaging the particle diameter of the active material carrier observed with, for example, a scanning electron microscope (SEM).
正極活物質層は、必要に応じて導電化材および結着材等を含有していても良い。
本発明において用いられる正極活物質層が有する導電化材としては、正極活物質層の導電性を向上させることができれば特に限定されるものではないが、例えばアセチレンブラック、ケッチェンブラック等のカーボンブラック等を挙げることができる。また、正極活物質層における導電化材の含有量は、導電化材の種類によって異なるものであるが、通常1質量%〜10質量%の範囲内である。
The positive electrode active material layer may contain a conductive material, a binder, and the like as necessary.
The conductive material included in the positive electrode active material layer used in the present invention is not particularly limited as long as the conductivity of the positive electrode active material layer can be improved. For example, carbon black such as acetylene black and ketjen black Etc. Moreover, although content of the electrically conductive material in a positive electrode active material layer changes with kinds of electrically conductive material, it is in the range of 1 mass%-10 mass% normally.
本発明において用いられる正極活物質層が有する結着材としては、例えばポリビニリデンフロライド(PVDF)、ポリテトラフルオロエチレン(PTFE)等を挙げることができる。また、正極活物質層における結着材の含有量は、正極活物質等を固定化できる程度の量であれば良く、より少ないことが好ましい。結着材の含有量は、通常1質量%〜10質量%の範囲内である。 Examples of the binder included in the positive electrode active material layer used in the present invention include polyvinylidene fluoride (PVDF) and polytetrafluoroethylene (PTFE). Further, the content of the binder in the positive electrode active material layer may be an amount that can fix the positive electrode active material or the like, and is preferably smaller. The content of the binder is usually in the range of 1% by mass to 10% by mass.
(正極集電体)
本発明において用いられる正極集電体は、上記の正極活物質層の集電を行う機能を有するものである。上記正極集電体の材料としては、例えばアルミニウム、SUS、ニッケル、鉄およびチタン等を挙げることができ、中でもアルミニウムおよびSUSが好ましい。また、正極集電体の形状としては、例えば、箔状、板状、メッシュ状等を挙げることができ、中でも箔状が好ましい。
(Positive electrode current collector)
The positive electrode current collector used in the present invention has a function of collecting the positive electrode active material layer. Examples of the material for the positive electrode current collector include aluminum, SUS, nickel, iron, and titanium. Of these, aluminum and SUS are preferable. Moreover, as a shape of a positive electrode electrical power collector, foil shape, plate shape, mesh shape etc. can be mentioned, for example, Foil shape is preferable.
(負極活物質層)
負極活物質層に用いられる負極活物質としては、リチウムイオンを吸蔵・放出可能なものであれば特に限定されるものではないが、例えば、金属リチウム、リチウム合金、金属酸化物、金属硫化物、金属窒化物、およびグラファイト等の炭素材料等を挙げることができる。また、負極活物質は、粉末状であっても良く、薄膜状であっても良い。
(Negative electrode active material layer)
The negative electrode active material used for the negative electrode active material layer is not particularly limited as long as it can occlude / release lithium ions. For example, metal lithium, lithium alloy, metal oxide, metal sulfide, Examples thereof include metal nitrides and carbon materials such as graphite. The negative electrode active material may be in the form of a powder or a thin film.
負極活物質層は、必要に応じて導電化材および結着材等を含有していても良い。
負極活物質層中に用いることができる結着材および上記導電化材は、正極活物質層の説明において既に述べたものを用いることができる。また、結着材および導電化材の使用量は、リチウム二次電池の用途等に応じて、適宜選択することが好ましい。また、負極活物質層の膜厚としては、特に限定されるものではないが、例えば10μm〜100μmの範囲内、中でも10μm〜50μmの範囲内であることが好ましい。
The negative electrode active material layer may contain a conductive material, a binder, and the like as necessary.
As the binder and the conductive material that can be used in the negative electrode active material layer, those already described in the description of the positive electrode active material layer can be used. Moreover, it is preferable to select the usage-amount of a binder and a electrically conductive material suitably according to the use etc. of a lithium secondary battery. Further, the film thickness of the negative electrode active material layer is not particularly limited, but for example, it is preferably in the range of 10 μm to 100 μm, and more preferably in the range of 10 μm to 50 μm.
(負極集電体)
負極集電体の材料及び形状としては、上述した正極集電体の材料及び形状と同様のものを採用することができる。
本発明に用いられる負極の製造方法としては、上述したような正極の製造方法と同様の方法を採用することができる。
(Negative electrode current collector)
As the material and shape of the negative electrode current collector, the same materials and shapes as those of the positive electrode current collector described above can be employed.
As a manufacturing method of the negative electrode used in the present invention, a method similar to the manufacturing method of the positive electrode as described above can be adopted.
前記正極及び前記負極のうち少なくとも一方の電極体の電極活物質層が、少なくとも電極活物質及び電極用電解質を含有するという構成をとることもできる。この場合、電極用電解質としては、後述する固体電解質等を用いることができる。 The electrode active material layer of at least one of the positive electrode and the negative electrode can also be configured to contain at least an electrode active material and an electrode electrolyte. In this case, a solid electrolyte described later can be used as the electrode electrolyte.
1−2.固体電解質
本発明に用いられる固体電解質としては、イオン伝導性を有し、且つ、常温(15℃〜25℃)において固体形状であれば、特に限定されない。本発明に用いられる固体電解質としては、具体的には、固体酸化物電解質、固体硫化物電解質等を用いることができる。
固体酸化物電解質としては、具体的には、LiPON(リン酸リチウムオキシナイトライド)、Li1.3Al0.3Ti0.7(PO4)3、La0.51Li0.34TiO0.74、Li3PO4、Li2SiO2、Li2SiO4、Li0.5La0.5TiO3、Li1.5Al0.5Ge1.5(PO4)3等を例示することができる。
固体硫化物電解質としては、具体的には、Li2S−P2S5、Li2S−P2S3、Li2S−P2S3−P2S5、Li2S−SiS2、LiI−Li2S−P2S5、LiI−Li2S−SiS2−P2S5、Li2S−SiS2−Li4SiO4、Li2S−SiS2−Li3PO4、Li3PS4−Li4GeS4、Li3.4P0.6Si0.4S4、Li3.25P0.25Ge0.76S4、Li4−xGe1−xPxS4、Li7P3S11等を例示することができる。
1-2. Solid electrolyte The solid electrolyte used in the present invention is not particularly limited as long as it has ionic conductivity and is in a solid form at room temperature (15 ° C to 25 ° C). Specifically, a solid oxide electrolyte, a solid sulfide electrolyte, or the like can be used as the solid electrolyte used in the present invention.
Specifically, as the solid oxide electrolyte, LiPON (lithium phosphate oxynitride), Li 1.3 Al 0.3 Ti 0.7 (PO 4 ) 3 , La 0.51 Li 0.34 TiO 0 .74 , Li 3 PO 4 , Li 2 SiO 2 , Li 2 SiO 4 , Li 0.5 La 0.5 TiO 3 , Li 1.5 Al 0.5 Ge 1.5 (PO 4 ) 3 etc. be able to.
The solid sulfide electrolyte, specifically, Li 2 S-P 2 S 5, Li 2 S-P 2
1−3.その他の構成要素
その他の構成要素として、セパレータを本発明のリチウム二次電池に用いることができる。セパレータは、上述した正極集電体及び上記負極集電体の間に配向されるものであり、通常、正極活物質層と負極活物質層との接触を防止し、固体電解質を保持する機能を有する。さらに、上記セパレータの材料としては、例えばポリエチレン(PE)、ポリプロピレン(PP)、ポリエステル、セルロースおよびポリアミド等の樹脂を挙げることができ、中でもポリエチレンおよびポリプロピレンが好ましい。また、上記セパレータは、単層構造であっても良く、複層構造であっても良い。複層構造のセパレータとしては、例えばPE/PPの2層構造のセパレータ、PP/PE/PPの3層構造のセパレータ等を挙げることができる。さらに、本発明においては、上記セパレータが、樹脂不織布、ガラス繊維不織布等の不織布等であっても良い。また、上記セパレータの膜厚は、特に限定されるものではなく、一般的なリチウム二次電池に用いられるセパレータの膜厚と同様である。
また、その他の構成要素として、本発明のリチウム二次電池を収納する電池ケースを用いることもできる。電池ケースの形状としては、上述した正極、負極、固体電解質等を収納できるものであれば特に限定されるものではないが、具体的には、円筒型、角型、コイン型、ラミネート型等を挙げることができる。
1-3. Other component As another component, a separator can be used for the lithium secondary battery of this invention. The separator is oriented between the positive electrode current collector and the negative electrode current collector described above, and usually has a function of preventing contact between the positive electrode active material layer and the negative electrode active material layer and holding the solid electrolyte. Have. Furthermore, examples of the material for the separator include resins such as polyethylene (PE), polypropylene (PP), polyester, cellulose, and polyamide. Among them, polyethylene and polypropylene are preferable. The separator may have a single layer structure or a multilayer structure. Examples of the separator having a multilayer structure include a separator having a two-layer structure of PE / PP and a separator having a three-layer structure of PP / PE / PP. Furthermore, in the present invention, the separator may be a nonwoven fabric such as a resin nonwoven fabric or a glass fiber nonwoven fabric. Moreover, the film thickness of the said separator is not specifically limited, It is the same as the film thickness of the separator used for a general lithium secondary battery.
Moreover, the battery case which accommodates the lithium secondary battery of this invention can also be used as another component. The shape of the battery case is not particularly limited as long as it can accommodate the above-described positive electrode, negative electrode, solid electrolyte, and the like. Specifically, a cylindrical shape, a square shape, a coin shape, a laminate shape, etc. Can be mentioned.
なお、本発明に係る固体電池は、上述した全固体リチウム二次電池に必ずしも限定されない。すなわち、固体電解質の一面側に正極活物質層を有し、他面側に負極活物質層を有する積層体と、当該積層体を挟持する一対の集電体とを備える固体電池であれば、本発明に係る固体電池に含まれる。
本発明に係る固体電池としては、全固体リチウム二次電池の他にも、例えば、ポリマー電池等が例示できる。
In addition, the solid battery which concerns on this invention is not necessarily limited to the all-solid-state lithium secondary battery mentioned above. That is, if it is a solid battery comprising a laminate having a positive electrode active material layer on one side of the solid electrolyte and a negative electrode active material layer on the other side, and a pair of current collectors sandwiching the laminate, It is contained in the solid battery which concerns on this invention.
Examples of the solid battery according to the present invention include a polymer battery and the like in addition to the all solid lithium secondary battery.
図5及び図6には、本発明の固体電池の応用例を示す。
図5は、本発明の固体電池を組み込んだ、バイポーラ構造電池の一例を示す断面模式図であり、図6は、本発明の固体電池を組み込んだ、モノポーラ構造電池の一例を示す断面模式図である。なお、図5及び図6には、いずれも図1に示した本発明の固体電池の典型例を単電池として組み込んだ例を示した。
バイポーラ電池300及びモノポーラ電池400は、いずれも数個の単電池11が互いに電気的に接続され、さらに外装体12によって覆われたものからなる。
バイポーラ電池300は、単電池11が直列に接続された仕様であり、単一のセルにおいて高電圧に設定することが可能であるため、高出力向け用途に用いることができる。一方、モノポーラ電池400は、単電池11が並列に接続された仕様であり、単一のセルにおいて高容量に設定することが可能であるため、電池の航続距離を長く保つことができる。ただし、このような性質は、あくまでも単一のセルにおいて観測される性質であり、これらのセルのまとまりであるパックを組み合わせることによって、高出力・高容量を両立させることは可能であるため、実用的には大きな違いはない。
5 and 6 show application examples of the solid state battery of the present invention.
FIG. 5 is a schematic cross-sectional view showing an example of a bipolar structure battery incorporating the solid battery of the present invention, and FIG. 6 is a schematic cross-sectional view showing an example of a monopolar structure battery incorporating the solid battery of the present invention. is there. 5 and 6 show examples in which the typical example of the solid battery of the present invention shown in FIG. 1 is incorporated as a unit cell.
Each of the bipolar battery 300 and the monopolar battery 400 is composed of
Since the bipolar battery 300 has a specification in which the
2.固体電池の製造方法
本発明の固体電池の製造方法は、少なくとも外周縁部の一部又は全部の厚さが最も厚く、且つ、外周縁部以外の部位に厚さが最も薄い部位を有する固体電解質膜を作製する工程、前記固体電解質膜の厚さが最も薄い部位を含み、且つ、前記固体電解質膜の厚さが最も厚い部位を含まない部分の一面側に正極活物質層を形成し、当該部分の他面側に負極活物質層を形成する工程、並びに、前記電極活物質層を両面に形成した前記固体電解質膜を、集電体で挟持する工程を有することを特徴とする。
少なくとも上記3工程を有する方法により、本発明に係る固体電池が製造できる。以下、本製造方法の各工程について詳細に述べる。
2. Solid battery manufacturing method The solid battery manufacturing method of the present invention includes a solid electrolyte having at least a part of or the entire thickness of the outer peripheral edge portion and a thinnest part at a portion other than the outer peripheral edge portion. Forming a positive electrode active material layer on one side of a portion including the portion where the thickness of the solid electrolyte membrane is the smallest and not including the portion where the thickness of the solid electrolyte membrane is the thickest, The method includes a step of forming a negative electrode active material layer on the other surface side of the portion, and a step of sandwiching the solid electrolyte film formed with the electrode active material layer on both surfaces with a current collector.
The solid battery according to the present invention can be manufactured by a method having at least the above three steps. Hereafter, each process of this manufacturing method is described in detail.
2−1.固体電解質膜作製工程
本発明に係る製造方法のうち、固体電解質膜を作製する工程は、上記「1.固体電池」の項で詳述したような、部位によって厚さの異なる固体電解質膜を作製する工程に相当する。本工程は、図1乃至図4に記載されたいずれかの固体電解質1を作製できる工程であれば、特に限定されない。
固体電解質膜の加工の具体的な方法としては、例えば、ある一定の略均一な厚さを有する固体電解質膜を、少なくとも外周縁部の一部又は全部を残して、その他の部分を薄く加工する方法、又は、寸法及び/又は形状の異なる固体電解質膜を2枚以上貼り合わせて融着させ、所望の固体電解質膜を得る方法等が挙げられる。
このうち、固体電解質膜の所定部分を薄く加工する方法としては、当該部分を削る方法、及び、当該部分を潰す方法が例示できる。
固体電解質膜を位置選択的に削る方法としては、固体電解質膜の所定の部分を研磨することにより、研磨部分を所定の膜厚に制御する方法が例示でき、固体電解質膜を位置選択的に潰す方法としては、所定の荷重をかけた圧力プレスにより加工するという方法が例示できる。
2-1. Solid Electrolyte Membrane Production Step Among the production methods according to the present invention, the step of producing a solid electrolyte membrane comprises producing solid electrolyte membranes having different thicknesses depending on the site as described in detail in the section “1. Solid battery” above. It corresponds to the process to do. This step is not particularly limited as long as it can produce any one of the
As a specific method of processing the solid electrolyte membrane, for example, a solid electrolyte membrane having a certain and substantially uniform thickness is processed by thinning the other portions, leaving at least a part or all of the outer peripheral edge. Examples thereof include a method, or a method in which two or more solid electrolyte membranes having different dimensions and / or shapes are bonded and fused to obtain a desired solid electrolyte membrane.
Among these, as a method of thinly processing a predetermined portion of the solid electrolyte membrane, a method of cutting the portion and a method of crushing the portion can be exemplified.
As a method of selectively cutting the solid electrolyte membrane, a method of controlling the polished portion to a predetermined film thickness by polishing a predetermined portion of the solid electrolyte membrane can be exemplified, and the solid electrolyte membrane is selectively crushed. As a method, the method of processing by the pressure press which applied the predetermined load can be illustrated.
2−2.電極活物質層形成工程
本発明に係る製造方法のうち、固体電解質膜の両面に電極活物質層を形成する工程は、図1乃至図4に記載されたいずれかの正極活物質層2及び負極活物質層3を形成できる工程であれば、特に限定されない。本工程においては、固体電解質膜の厚さが最も薄い部位を含み、且つ、固体電解質膜の厚さが最も厚い部位を含まない部分を、正極活物質層及び負極活物質層で挟持するように層を形成する条件を満たすことが必要であり、当該条件を満たせば、どのように電極活物質層を形成しても差し支えない。
なお、電極活物質層を形成した後、電極密度を向上させるために、正極活物質層をプレスしても良い。
2-2. Electrode Active Material Layer Forming Step In the production method according to the present invention, the step of forming the electrode active material layer on both surfaces of the solid electrolyte membrane is the positive electrode active material layer 2 and the negative electrode described in any of FIGS. If it is a process which can form the
In addition, after forming an electrode active material layer, in order to improve an electrode density, you may press a positive electrode active material layer.
2−3.集電体挟持工程
本発明に係る製造方法のうち、電極活物質層を形成した固体電解質膜を集電体で挟持する工程は、最終的に図1乃至図4に記載されたいずれかの固体電池を形成できる工程であれば、特に限定されない。
2-3. Current collector sandwiching step In the manufacturing method according to the present invention, the step of sandwiching the solid electrolyte membrane on which the electrode active material layer is formed with the current collector is finally one of the solids described in FIGS. If it is a process which can form a battery, it will not specifically limit.
1 リチウムイオン伝導性固体電解質
2 正極活物質層
3 負極活物質層
4 正極集電体
5 負極集電体
6 正極
7 負極
8a 正極活物質層及び負極活物質層の間に介在する固体電解質の部位を含む積層部分を示す一点鎖線
8b,8c 正極活物質層及び/又は負極活物質層の外周からはみ出した正極集電体又は負極集電体の外周縁部の間に介在する固体電解質の部位を含む積層部分を示す一点鎖線
9a 正極活物質層及び負極活物質層の間に介在する固体電解質の厚さ
9b,9c 正極活物質層及び/又は負極活物質層の外周からはみ出した正極集電体又は負極集電体の外周縁部の間に介在する固体電解質の厚さ
11 単電池
12 外装体
21 リチウムイオン伝導性固体電解質
22 正極活物質層
23 負極活物質層
24 正極集電体
25 負極集電体
26 正極
27 負極
28a 正極活物質層及び負極活物質層の間に介在する固体電解質の部位を含む積層部分を示す一点鎖線
28b 正極活物質層及び/又は負極活物質層の外周からはみ出した正極集電体又は負極集電体の外周縁部の間に介在する固体電解質の部位を含む積層部分を示す一点鎖線
100 本発明に係る固体電池の典型例
200a,200b,200c 本発明に係る固体電池の変形例
300 バイポーラ構造電池
400 モノポーラ構造電池
500 従来の全固体リチウム二次電池
DESCRIPTION OF SYMBOLS 1 Lithium ion conductive solid electrolyte 2 Positive electrode active material layer 3 Negative electrode active material layer 4 Positive electrode current collector 5 Negative electrode current collector 6 Positive electrode 7 Negative electrode 8a Part of the solid electrolyte interposed between the positive electrode active material layer and the negative electrode active material layer Dotted lines 8b and 8c indicating the laminated portion including the positive electrode active material layer and / or the portion of the solid electrolyte interposed between the outer peripheral edge portions of the negative electrode current collector that protrudes from the outer periphery of the negative electrode active material layer Alternate long and short dash line 9a indicating the laminated portion including the thickness 9b, 9c of the solid electrolyte interposed between the positive electrode active material layer and the negative electrode active material layer, and / or the positive electrode current collector protruding from the outer periphery of the positive electrode active material layer and / or the negative electrode active material layer Alternatively, the thickness of the solid electrolyte interposed between the outer peripheral edges of the negative electrode current collector 11 unit cell 12 exterior body 21 lithium ion conductive solid electrolyte 22 positive electrode active material layer 23 negative electrode active material layer 24 positive electrode current collector 25 negative electrode current collector Electrical body 26 Positive electrode 27 Negative electrode 28a A one-dot chain line 28b showing a laminated portion including a positive electrode active material layer and a solid electrolyte portion interposed between the negative electrode active material layer and a positive electrode current collector protruding from the outer periphery of the positive electrode active material layer and / or the negative electrode active material layer Or the dashed-dotted line 100 which shows the lamination | stacking part containing the site | part of the solid electrolyte interposed between the outer periphery edge parts of a negative electrode electrical power collector Typical example 200a, 200b, 200c of the solid battery which concerns on this invention The modification of the solid battery which concerns on this invention 300 Bipolar Structure Battery 400 Monopolar Structure Battery 500 Conventional All Solid Lithium Secondary Battery
Claims (2)
前記固体電解質膜の厚さが最も薄い部位を含み、且つ、前記固体電解質膜の厚さが最も厚い部位を含まない部分の一面側に正極活物質層を形成し、当該部分の他面側に負極活物質層を形成する工程、並びに、
前記電極活物質層を両面に形成した前記固体電解質膜を、集電体で挟持する工程を有することを特徴とする、固体電池の製造方法。 A step of producing a solid electrolyte membrane having at least a part of or the entire thickness of the outer peripheral edge and a thinnest part at a portion other than the outer peripheral edge;
A positive electrode active material layer is formed on one surface side of the portion including the thinnest portion of the solid electrolyte membrane and not including the thickest portion of the solid electrolyte membrane, and on the other surface side of the portion. Forming a negative electrode active material layer; and
A method for producing a solid state battery, comprising a step of sandwiching the solid electrolyte membrane having the electrode active material layer formed on both sides with a current collector.