JP5353954B2 - Circuit member and semiconductor device - Google Patents

Circuit member and semiconductor device Download PDF

Info

Publication number
JP5353954B2
JP5353954B2 JP2011126491A JP2011126491A JP5353954B2 JP 5353954 B2 JP5353954 B2 JP 5353954B2 JP 2011126491 A JP2011126491 A JP 2011126491A JP 2011126491 A JP2011126491 A JP 2011126491A JP 5353954 B2 JP5353954 B2 JP 5353954B2
Authority
JP
Japan
Prior art keywords
die pad
lead
plating layer
circuit member
lead portion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2011126491A
Other languages
Japanese (ja)
Other versions
JP2011171770A (en
Inventor
洋 島崎
啓之 齋藤
正親 増田
健司 松村
勝 福地
孝夫 池澤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dai Nippon Printing Co Ltd
Original Assignee
Dai Nippon Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dai Nippon Printing Co Ltd filed Critical Dai Nippon Printing Co Ltd
Priority to JP2011126491A priority Critical patent/JP5353954B2/en
Publication of JP2011171770A publication Critical patent/JP2011171770A/en
Application granted granted Critical
Publication of JP5353954B2 publication Critical patent/JP5353954B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

<P>PROBLEM TO BE SOLVED: To provide a circuit member having increased adhesion strength with sealing resin. <P>SOLUTION: A frame raw material 2, which is used for the circuit member and has a die pad part 3 for mounting a semiconductor chip 11 on its upper face and lead parts 8 each of which is to be connected to the semiconductor chip 11, is formed by pattern-machining a rolled copper sheet or a rolled copper-alloy sheet, and the upper surfaces and side surfaces of the die pad part 3 and the lead parts 8 are formed as to be rough surfaces 3A, 3B, 8A, and 8B, respectively, and the under surfaces of the die pad part 3 and the lead parts 8 are formed as to be smooth, and a plated layer 10 to form a rough surface is formed on the rough portions of the die pad part 3 and the lead parts 8, and the lead parts 8 are buried in a sealing resin 15 so that their under surfaces can be exposed. <P>COPYRIGHT: (C)2011,JPO&amp;INPIT

Description

本発明は、回路部材表面の積層構造や、回路部材の一つとしてのリードフレームの表面処理技術やその回路部材を用いた半導体装置に関し、さらに詳しくは、半導体パッケージのタイプに対応して、リードフレームと封止樹脂との密着強度を高める技術に関する。   The present invention relates to a laminated structure on a surface of a circuit member, a surface treatment technique of a lead frame as one of circuit members, and a semiconductor device using the circuit member, and more particularly, a lead corresponding to a type of a semiconductor package. The present invention relates to a technique for increasing the adhesion strength between a frame and a sealing resin.

半導体装置としては、リードフレームにＩＣチップ、ＬＳＩチップなどの半導体チップが搭載され、絶縁性樹脂で封止された構造をもつ半導体パッケージがある。このような半導体装置では、高集積化及び小型化が進むに従ってパッケージの構造が、ＳＯＪ（Small Outline J-Leaded Package）やＱＦＰ（Quad Flat Package）のような樹脂パッケージの側壁から外部リードが外側に突出したタイプを経て、外部リードが外側に突出せずに樹脂パッケージの裏面に外部リードが露出するように埋設された、ＱＦＮ（Quad Flat Non-leaded package）やＳＯＮ（Small Outline Noneleaded Package）などの薄型で実装面積の小さいタイプに進展している。   As a semiconductor device, there is a semiconductor package having a structure in which a semiconductor chip such as an IC chip or an LSI chip is mounted on a lead frame and sealed with an insulating resin. In such a semiconductor device, as the integration and miniaturization progress, the structure of the package is such that the external leads are outward from the side walls of the resin package such as SOJ (Small Outline J-Leaded Package) and QFP (Quad Flat Package). Through the projecting type, the external leads are not projected to the outside and are embedded so that the external leads are exposed on the back of the resin package, such as QFN (Quad Flat Non-leaded package) and SON (Small Outline None Leaded Package) Progressing to a thin type with a small mounting area.

リードフレームとしては、絶縁性樹脂で封止されるフレーム素材の表面に粗面化処理が施され、この表面に順次、ニッケル（Ｎｉ）層、パラジウム（Ｐｄ）層がめっき法にて積層された構造のものが知られている（例えば、特許文献１参照。）。上述した粗面化処理の方法としては、リードフレームの素材表面を、有機酸系のエッチング液で化学研磨している。   As a lead frame, the surface of a frame material sealed with an insulating resin is roughened, and a nickel (Ni) layer and a palladium (Pd) layer are sequentially laminated on the surface by a plating method. The thing of a structure is known (for example, refer patent document 1). As the surface roughening method described above, the material surface of the lead frame is chemically polished with an organic acid etching solution.

他のリードフレームとしては、フレーム素材の表面を、表面側が粗面化されたＮｉめっき層で被覆したものが知られている（例えば、特許文献２参照。）。このような粗面化されたＮｉめっき層は、めっき法の条件を調整することにより形成することができる。   Other lead frames are known in which the surface of a frame material is coated with a Ni plating layer whose surface is roughened (see, for example, Patent Document 2). Such a roughened Ni plating layer can be formed by adjusting the conditions of the plating method.

このように、リードフレームの全面にＮｉめっき層を形成し、その上にＰｄめっきやＡｕめっきを施すことは、製造工程の簡素化、及び環境対応のはんだ工程のＰｂフリー化の目的のために広く行われている。   In this way, the Ni plating layer is formed on the entire surface of the lead frame, and the Pd plating or Au plating is performed on the Ni plating layer for the purpose of simplifying the manufacturing process and making the environment-friendly solder process Pb-free. Widely done.

また、絶縁性樹脂と密着させる回路部材としては、リードフレームの他に、車両の供給電源を車載用補器へ分配する電気接続箱に用いられるコネクタの導電板やバスバーなどがある。   In addition to the lead frame, the circuit member to be in close contact with the insulating resin includes a connector conductive plate and a bus bar used for an electrical connection box that distributes the vehicle power supply to on-vehicle auxiliary devices.

特開平１１−４０７２０号公報（第４頁、図１）Japanese Patent Laid-Open No. 11-40720 (page 4, FIG. 1) 特開２００４−３４９４９７号公報（第７頁、図３）JP 2004-349497 A (page 7, FIG. 3)

しかしながら、上述した特許文献１に記載された有機酸系のエッチング液は、めっき法で形成した銅の表面に対しては有効であるものの、リードフレームの素材である圧延銅板の表面の粗面化に対してはあまり有効でないという問題点がある。因みに、このような有機酸系のエッチング液で圧延銅素材の表面を処理した場合、表面粗度は上がるものの、表面プロファイルが針状にならない。このため、有機酸系のエッチング液で粗面化処理を行ったリードフレームでは、パッケージを構成する絶縁性樹脂との密着性に対しては大きな効果が得られないものであった。加えて、有機酸系のエッチング液を用いた粗面化では、表面粗度（Ｒａ）を０．１５μｍとするのに、銅表面から深さ３μｍに至るまでエッチングしなければならず、それ以上の表面粗度を得るにはさらに深くエッチングする必要がある。したがって、この処理方法では、エッチングに時間を要するため実際のリードフレームの生産には適さないものであった。   However, the organic acid-based etching solution described in Patent Document 1 described above is effective for the surface of copper formed by plating, but the surface of the rolled copper plate that is the material of the lead frame is roughened. There is a problem that it is not very effective. Incidentally, when the surface of the rolled copper material is treated with such an organic acid-based etching solution, the surface roughness is increased, but the surface profile does not become needle-like. For this reason, a lead frame that has been subjected to a surface roughening treatment with an organic acid-based etching solution cannot obtain a great effect on the adhesion to the insulating resin constituting the package. In addition, in roughening using an organic acid-based etchant, the surface roughness (Ra) must be 0.15 μm, and etching must be performed from the copper surface to a depth of 3 μm. In order to obtain the surface roughness, it is necessary to etch deeper. Therefore, this processing method is not suitable for production of an actual lead frame because etching takes time.

上述した特許文献２に記載されためっき法で粗面化されたＮｉめっき層を形成する方法では、表面粗度を大きくするにはＮｉめっき層を厚くする必要があり、１μｍ以上でないと安定した効果が得られない。最近はめっき層を薄くする傾向があり、Ｎｉめっき層の厚みとして０．５μｍ程度が要望されている。   In the method of forming the Ni plating layer roughened by the plating method described in Patent Document 2 described above, it is necessary to increase the Ni plating layer in order to increase the surface roughness. The effect is not obtained. Recently, there is a tendency to make the plating layer thinner, and the thickness of the Ni plating layer is demanded to be about 0.5 μm.

ところで、上述したＱＦＮやＳＯＮなどのような薄型で実装面積の小さいタイプの半導体装置に用いられるリードフレームでは、外部リードの下面が樹脂パッケージの下面に露出しているため、外部リードと絶縁性樹脂とが接触する面積が小さい。このため、リードフレームと絶縁性樹脂との密着強度を更に高める必要がある。近年では、車載用途向けの半導体装置の需要が高まり、このような用途に用いた場合、振動や温度変化に晒されるため、リードフレームと封止樹脂との密着強度を従来以上に強化させることが必要になっている。   By the way, in the lead frame used for the thin semiconductor device having a small mounting area such as QFN or SON described above, the lower surface of the external lead is exposed on the lower surface of the resin package. The contact area is small. For this reason, it is necessary to further increase the adhesion strength between the lead frame and the insulating resin. In recent years, the demand for semiconductor devices for in-vehicle applications has increased, and when used in such applications, it is exposed to vibration and temperature changes, so that the adhesion strength between the lead frame and the sealing resin can be strengthened more than before. It is necessary.

また、内部リードにおけるワイヤーボンディングを施す領域や、外部リードにおける実装基板（プリント配線基板）へ半田付けする領域などを考慮すると共に、パッケージのタイプに対応した機能を有するリードフレームが要望されている。   In addition, there is a demand for a lead frame having a function corresponding to the type of package while considering a region for wire bonding in the internal lead and a region in the external lead to be soldered to a mounting board (printed wiring board).

そこで、本発明の主たる目的は、封止樹脂との密着強度を高めることができるリードフレーム、及びその製造方法、並びに半導体装置を提供することにある。   Therefore, a main object of the present invention is to provide a lead frame capable of increasing the adhesion strength with a sealing resin, a manufacturing method thereof, and a semiconductor device.

また、本発明の他の目的は、ＱＦＮやＳＯＮなどのパッケージタイプに用いることのできるリードフレーム、及びその製造方法、並びに半導体装置を提供することにある。   Another object of the present invention is to provide a lead frame that can be used for a package type such as QFN or SON, a manufacturing method thereof, and a semiconductor device.

さらに、本発明の他の目的は、絶縁性樹脂に対する密着強度を高めることができる回路部材の表面積層構造を提供することにある。   Furthermore, the other object of this invention is to provide the surface lamination structure of the circuit member which can raise the adhesive strength with respect to insulating resin.

本発明の第１の特徴は、上面に半導体チップを搭載するダイパッド部と、半導体チップに電気的に接続されるリード部とを備えたフレーム素材を、圧延銅板もしくは圧延銅合金板をパターン加工して形成した回路部材であって、ダイパッド部及び前記リード部の上面及び側壁面に粗面が形成されると共に、ダイパッド部及びリード部の下面が平滑面とされ、ダイパッド部及びリード部の表面に粗面が形成された部分は粗面となるめっき層が形成され、リード部の下面が露出するように封止樹脂に埋設されることを要旨とする。   A first feature of the present invention is that a frame material having a die pad portion for mounting a semiconductor chip on an upper surface and a lead portion electrically connected to the semiconductor chip is patterned on a rolled copper plate or a rolled copper alloy plate. A rough surface is formed on the upper surface and the side wall surface of the die pad portion and the lead portion, and the lower surface of the die pad portion and the lead portion is a smooth surface, and the surface of the die pad portion and the lead portion is formed. A gist is that a portion where the rough surface is formed is provided with a plating layer that becomes a rough surface, and is embedded in the sealing resin so that the lower surface of the lead portion is exposed.

本発明の第２の特徴は、上面に半導体チップを搭載するダイパッド部と、半導体チップに電気的に接続されるリード部とを備えたフレーム素材を、圧延銅板もしくは圧延銅合金板をパターン加工して形成した回路部材であって、ダイパッド部の上面と、リード部の上面におけるボンディングワイヤが接続される部分と、が平滑面とされると共に、これら平滑面にめっき層が積層され、めっき層が形成された領域及びダイパッド部及びリード部の下面を除く領域に粗面が形成されていることを要旨とする。   A second feature of the present invention is that a frame material including a die pad portion on which a semiconductor chip is mounted on an upper surface and a lead portion electrically connected to the semiconductor chip is patterned on a rolled copper plate or a rolled copper alloy plate. The upper surface of the die pad portion and the portion to which the bonding wires are connected on the upper surface of the lead portion are smooth surfaces, and a plating layer is laminated on these smooth surfaces, The gist is that a rough surface is formed in the formed region and the region excluding the lower surface of the die pad portion and the lead portion.

なお、本発明においては、上述した粗面の表面粗度（Ｒａ）が、０．３μｍ以上であることが好ましく、さらに積層されるめっき層としては、厚さが０．５〜２μｍのＮｉめっき層、厚さが０．００５〜０．２μｍのＰｄめっき層、厚さが０．００３〜０．０１μｍのＡｕめっき層が順次積層されていることが好ましい。また、上述した粗面は、過酸化水素と硫酸を主成分とするマイクロエッチング液で処理によって形成されていることが好ましい。ここで、マイクロエッチング液とは、金属の表面を僅かに溶かし、微細な凹凸からなる粗面を形成する表面処理剤を言う。   In the present invention, the surface roughness (Ra) of the rough surface described above is preferably 0.3 μm or more, and as a plating layer to be further laminated, a Ni plating having a thickness of 0.5 to 2 μm It is preferable that a Pd plating layer having a thickness of 0.005 to 0.2 μm and an Au plating layer having a thickness of 0.003 to 0.01 μm are sequentially laminated. The rough surface described above is preferably formed by treatment with a microetching liquid mainly composed of hydrogen peroxide and sulfuric acid. Here, the micro-etching solution refers to a surface treatment agent that slightly dissolves the metal surface and forms a rough surface composed of fine irregularities.

本発明の第３の特徴は、回路部材の製造方法であって、圧延銅板もしくは圧延銅合金板をパターン加工して、ダイパッド部とリード部とを有するフレーム素材を作製する工程と、フレーム素材の下面をマスク材で覆った状態で、フレーム素材の上面及び側壁面を、過酸化水素と硫酸を主成分とするマイクロエッチング液を用いて粗面化処理する工程と、マスク材を剥離した後、フレーム素材の表面にめっき層を積層する工程と、を備えることを要旨とする。   A third feature of the present invention is a method for manufacturing a circuit member, in which a rolled copper plate or a rolled copper alloy plate is patterned to produce a frame material having a die pad portion and a lead portion; In a state where the lower surface is covered with a mask material, the upper surface and the side wall surface of the frame material are roughened using a microetching liquid mainly composed of hydrogen peroxide and sulfuric acid, and after the mask material is peeled off, And a step of laminating a plating layer on the surface of the frame material.

本発明の第４の特徴は回路部材の製造方法であって、圧延銅板もしくは圧延銅合金板をパターン加工して、ダイパッド部とリード部とを有するフレーム素材を作製する工程と、ダイパッド部の上面と、リード部におけるボンディングワイヤが接続される部分にめっき層を積層する工程と、めっき層を積層したフレーム素材の下面をマスク材で覆った状態で、フレーム素材を、過酸化水素と硫酸を主成分とするマイクロエッチング液を用いて粗面化処理する工程と、マスク材を剥離する工程と、を備えることを要旨とする。   A fourth feature of the present invention is a method for manufacturing a circuit member, which includes a step of patterning a rolled copper plate or a rolled copper alloy plate to produce a frame material having a die pad portion and a lead portion, and an upper surface of the die pad portion. And the step of laminating the plating layer on the part where the bonding wire is connected in the lead part, and with the mask material covering the lower surface of the frame material on which the plating layer is laminated, the frame material is mainly composed of hydrogen peroxide and sulfuric acid. The gist is to include a step of roughening using a microetching solution as a component and a step of peeling the mask material.

ここで、ダイパット部とリード部のボンディングワイヤが接続される部分に積層されるめっき層としては、２〜１５μｍのＡｇめっき層、もしくはフレーム素材上にＮｉめっき層、Ｐｄめっき層を順次積層しためっき層である。   Here, as a plating layer to be laminated on the portion where the bonding wire of the die pad part and the lead part is connected, plating of 2 to 15 μm Ag plating layer, or Ni plating layer and Pd plating layer sequentially laminated on the frame material Is a layer.

本発明の第５の特徴は、半導体装置であって、圧延銅板もしくは圧延銅合金板でなる、ダイパッド部とリード部とを備え、ダイパッド部及びリード部の上面及び側壁面に粗面が形成され、且つダイパッド部及びリード部の下面が平滑面とされると共に、ダイパッド部及びリード部表面に粗面が形成された部分は粗面となるにめっき層が積層された回路部材と、ダイパッド部の上面に搭載された半導体チップと、この半導体チップとリード部とを接続するボンディングワイヤと、リード部の下面を露出させるように、回路部材及び半導体チップ及びボンディングワイヤを封止する電気絶縁性の封止樹脂と、を備えることを要旨とする。   A fifth feature of the present invention is a semiconductor device comprising a die pad portion and a lead portion made of a rolled copper plate or a rolled copper alloy plate, and a rough surface is formed on the upper surface and side wall surface of the die pad portion and the lead portion. In addition, the lower surface of the die pad portion and the lead portion is a smooth surface, and the portion where the rough surface is formed on the surface of the die pad portion and the lead portion is a rough surface, and the circuit member in which the plating layer is laminated and the die pad portion A semiconductor chip mounted on the upper surface, a bonding wire for connecting the semiconductor chip and the lead portion, and an electrically insulating seal for sealing the circuit member, the semiconductor chip and the bonding wire so as to expose the lower surface of the lead portion. And a stop resin.

本発明の第６の特徴は、半導体装置であって、圧延銅板もしくは圧延銅合金板でなる、ダイパッド部とリード部とを備え、ダイパッド部の上面と、リード部の表面におけるボンディングワイヤが接続される部分と、が平滑面とされると共に、これら平滑面にめっき層が積層され、このめっき層が形成された領域及びダイパッド部及びリード部の裏面を除く領域に粗面が形成された回路部材と、ダイパッド部の上面に搭載された半導体チップと、半導体チップとリード部とを接続するボンディングワイヤと、リード部の下面を露出させるように、回路部材及び半導体チップ及びボンディングワイヤを封止する電気絶縁性の封止樹脂と、を備えることを要旨とする。   A sixth feature of the present invention is a semiconductor device comprising a die pad portion and a lead portion made of a rolled copper plate or a rolled copper alloy plate, wherein the bonding wire is connected to the upper surface of the die pad portion and the surface of the lead portion. A circuit member in which a plating layer is laminated on these smooth surfaces and a rough surface is formed in a region excluding the back surface of the die pad portion and the lead portion. A semiconductor chip mounted on the upper surface of the die pad portion, a bonding wire for connecting the semiconductor chip and the lead portion, and an electric for sealing the circuit member, the semiconductor chip and the bonding wire so as to expose the lower surface of the lead portion. And an insulating sealing resin.

本発明の第７の特徴は、絶縁性樹脂と接合される回路部材の表面積層構造であって、圧延銅板もしくは圧延銅合金板でなる導電性素材の表面に、表面粗度（Ｒａ）が０．３μｍ以上の粗面が形成され、この粗面に、順次、Ｎｉめっき層、Ｐｄめっき層が積層されてなり、Ｎｉめっき層の厚さが０．５〜２μｍ、Ｐｄめっき層の厚さが０．００５〜０．２μｍであることを要旨とする。   A seventh feature of the present invention is a surface laminated structure of a circuit member joined to an insulating resin, and the surface roughness (Ra) is 0 on the surface of a conductive material made of a rolled copper plate or a rolled copper alloy plate. A rough surface of 3 μm or more is formed, and a Ni plating layer and a Pd plating layer are sequentially laminated on the rough surface. The thickness of the Ni plating layer is 0.5 to 2 μm, and the thickness of the Pd plating layer is It is summarized as being 0.005-0.2 μm.

また、必要に応じ前記Ｐｄめっき層の上に厚さ０．００３〜０．０１μｍのＡｕめっき層もしくはシラン防錆層を有することを特徴とする。   In addition, an Au plating layer or a silane rust prevention layer having a thickness of 0.003 to 0.01 μm is provided on the Pd plating layer as necessary.

本発明によれば、封止樹脂との密着強度が高く、リード部の裏面が封止樹脂から露出するタイプのパッケージに用いることのできるリードフレーム、及びその製造方法、並びに半導体装置を実現可能とする。   According to the present invention, it is possible to realize a lead frame, a manufacturing method thereof, and a semiconductor device that can be used for a type of package that has high adhesion strength with the sealing resin and the back surface of the lead portion is exposed from the sealing resin. To do.

また、本発明によれば、絶縁性樹脂に対する密着強度を高めることができる回路部材の表面積層構造を見いだしたことにより、絶縁性樹脂と接合する各種の回路部材を用いた電子機器などの耐久性を高めることができる。   In addition, according to the present invention, by finding the surface laminated structure of the circuit member that can increase the adhesion strength to the insulating resin, durability of electronic equipment using various circuit members bonded to the insulating resin is found. Can be increased.

本発明の第１の実施の形態に係るリードフレームを示す平面図である。1 is a plan view showing a lead frame according to a first embodiment of the present invention. 本発明の第１の実施の形態に係るリードフレームの製造方法を示す工程断面図である。FIG. 6 is a process cross-sectional view illustrating the lead frame manufacturing method according to the first embodiment of the invention. 本発明の第１実施の形態に係るリードフレームの製造方法を示す工程断面図である。It is process sectional drawing which shows the manufacturing method of the lead frame which concerns on 1st Embodiment of this invention. 本発明の第１の実施の形態に係るリードフレームの製造方法を示す工程断面図である。FIG. 6 is a process cross-sectional view illustrating the lead frame manufacturing method according to the first embodiment of the invention. 本発明の第１の実施の形態に係るリードフレームの製造方法を示す工程断面図である。FIG. 6 is a process cross-sectional view illustrating the lead frame manufacturing method according to the first embodiment of the invention. 本発明の第１の実施の形態に係るリードフレームの製造方法を示す工程断面図である。FIG. 6 is a process cross-sectional view illustrating the lead frame manufacturing method according to the first embodiment of the invention. 本発明の第１の実施の形態に係る半導体装置の製造方法を示す工程断面図である。It is process sectional drawing which shows the manufacturing method of the semiconductor device which concerns on the 1st Embodiment of this invention. 本発明の第１実施の形態に係る半導体装置の製造方法を示す工程断面図である。It is process sectional drawing which shows the manufacturing method of the semiconductor device which concerns on 1st Embodiment of this invention. 本発明の第１の実施の形態に係る半導体装置を示す断面図である。1 is a cross-sectional view showing a semiconductor device according to a first embodiment of the present invention. 本発明の実施の形態に係るリードフレームの粗面化部分の拡大断面図である。It is an expanded sectional view of the roughened part of the lead frame concerning an embodiment of the invention. 密着強度試験の概要を示す斜視図である。It is a perspective view which shows the outline | summary of an adhesive strength test. （ａ）〜（ｄ）は、本発明の第２の実施の形態に係るリードフレームの製造工程を示す断面図である。(A)-(d) is sectional drawing which shows the manufacturing process of the lead frame which concerns on the 2nd Embodiment of this invention. （ａ）〜（ｄ）は、本発明の第２の実施の形態に係る半導体装置の製造工程を示す工程断面図である。(A)-(d) is process sectional drawing which shows the manufacturing process of the semiconductor device which concerns on the 2nd Embodiment of this invention. 本発明のその他の実施の形態に係るリードフレームの粗面化部分の拡大断面図である。It is an expanded sectional view of the roughened part of the lead frame concerning other embodiments of the present invention. （ａ）〜（ｅ）は、本発明の第３の実施の形態に係るリードフレームの製造工程を示す工程断面図である。(A)-(e) is process sectional drawing which shows the manufacturing process of the lead frame which concerns on the 3rd Embodiment of this invention. （ａ）〜（ｅ）は、本発明の第３の実施の形態に係る半導体装置の製造工程を示す断面図である。(A)-(e) is sectional drawing which shows the manufacturing process of the semiconductor device which concerns on the 3rd Embodiment of this invention.

以下、本発明の実施の形態に係る回路部材、回路部材の製造方法、半導体装置、及び回路部材の表面積層構造の詳細を図面に基づいて説明する。本実施の形態では、回路部材としてリードフレームに本発明を適用して説明する。但し、図面は模式的なものであり、各材料層の厚みやその比率などは現実のものとは異なることに留意すべきである。したがって、具体的な厚みや寸法は以下の説明を参酌して判断すべきものである。また、図面相互間においても互いの寸法の関係や比率が異なる部分が含まれていることは勿論である。   DESCRIPTION OF THE PREFERRED EMBODIMENTS Details of a circuit member, a method for manufacturing a circuit member, a semiconductor device, and a surface laminated structure of the circuit member according to embodiments of the present invention will be described below with reference to the drawings. In the present embodiment, the present invention is applied to a lead frame as a circuit member. However, it should be noted that the drawings are schematic, and the thicknesses and ratios of the material layers are different from actual ones. Therefore, specific thicknesses and dimensions should be determined in consideration of the following description. Moreover, it is a matter of course that portions having different dimensional relationships and ratios are included between the drawings.

〔第１の実施の形態〕
図１〜図９は、本発明の第１の実施の形態を示している。図１はリードフレームの平面図、図２〜図９は、図１のＡ−Ａ断面に着目したリードフレーム及び半導体装置の製造方法を示す工程図である。 [First Embodiment]
1 to 9 show a first embodiment of the present invention. FIG. 1 is a plan view of a lead frame, and FIGS. 2 to 9 are process diagrams showing a method of manufacturing a lead frame and a semiconductor device, focusing on the AA cross section of FIG.

（リードフレームの構成）
本実施の形態に係るリードフレーム１は、細長いリボン状の圧延銅板もしくは圧延銅合金板でなるフレーム素材２を、エッチングや金型打ち抜きなどにより、パターン形成して、複数の単位パターンが連続した状態で製造される。なお、図１はリードフレーム１における１単位パターンを示している。 (Lead frame configuration)
In the lead frame 1 according to the present embodiment, a frame material 2 made of an elongated ribbon-like rolled copper plate or rolled copper alloy plate is formed by patterning by etching or die punching, and a plurality of unit patterns are continuous. Manufactured by. FIG. 1 shows one unit pattern in the lead frame 1.

図１に示すように、リードフレーム１の１単位パターンは、中央に形成された、半導体チップを搭載するための矩形状のダイパッド部３と、このダイパッド部３を取り囲むように形成されたリード部８と、ダイパッド部３をフレーム素材２に連結しているタイバー６と、リード部８を横方向に連結するタイバー７と、を備えている。このリード部８は、後述するように、封止樹脂１５の側壁から外側へ向けて突出しない程度の寸法に設定されている。なお、本実施の形態では、リード部８を横方向に連結するタイバー７を形成しているが、タイバー７を省略してリード部８がフレーム２の外枠部からダイパッド部３の周縁に向けて延在されるパターンに形成してもよい。   As shown in FIG. 1, one unit pattern of the lead frame 1 includes a rectangular die pad portion 3 for mounting a semiconductor chip formed at the center, and a lead portion formed so as to surround the die pad portion 3. 8, a tie bar 6 that connects the die pad portion 3 to the frame material 2, and a tie bar 7 that connects the lead portion 8 in the lateral direction. As will be described later, the lead portion 8 is set to a size that does not protrude outward from the side wall of the sealing resin 15. In the present embodiment, the tie bar 7 that connects the lead portions 8 in the lateral direction is formed, but the tie bar 7 is omitted and the lead portions 8 are directed from the outer frame portion of the frame 2 toward the periphery of the die pad portion 3. It may be formed in a pattern extending in the direction.

本実施の形態に係るリードフレーム１の上面（半導体チップを搭載する側の面）及び各パターンの側壁面は、図４及び図５に示すように、過酸化水素と硫酸を主成分とするマイクロエッチング液を用いて粗面化処理が施された粗面３Ａ，３Ｂ、８Ａ，８Ｂとなっている。これら粗面３Ａ，３Ｂ、８Ａ，８Ｂにおける表面粗度（Ｒａ）は、０．３μｍ以上に設定されており、表面プロファイルは針状に突出した凹凸面となっている。フレーム素材２の下面（半導体チップ搭載面の反対側の面）は平滑面に形成されている。   As shown in FIGS. 4 and 5, the upper surface (surface on which the semiconductor chip is mounted) of the lead frame 1 according to the present embodiment and the side wall surface of each pattern are formed of microparticles mainly composed of hydrogen peroxide and sulfuric acid. The rough surfaces 3A, 3B, 8A, and 8B are subjected to the roughening treatment using the etching solution. The surface roughness (Ra) of these rough surfaces 3A, 3B, 8A, 8B is set to 0.3 μm or more, and the surface profile is an uneven surface protruding like a needle. The lower surface of the frame material 2 (the surface opposite to the semiconductor chip mounting surface) is formed as a smooth surface.

また、ダイパッド部３及びリード部８などを含むフレーム素材２の表面には、図６に示すように、めっき層１０が形成されている。なお、本実施の形態におけるめっき層１０は、図１０に示すように、フレーム素材２の表面に、順次、Ｎｉめっき層１７、Ｐｄめっき層１８が積層されてなる。そして、Ｎｉめっき層１７の厚さは０．５〜２μｍに設定され、Ｐｄめっき層１８の厚さは０．００５〜０．２μｍに設定されている。なお、Ｐｄめっき層１８は、ボンディングワイヤ及び半田ペーストとの接続性の良好な金属層であり、図７に示すようなボンディングワイヤ１３を接続するワイヤボンディングや、図示しない実装基板（プリント配線基板）への半田付けを確実に行うことができる。   A plating layer 10 is formed on the surface of the frame material 2 including the die pad portion 3 and the lead portion 8 as shown in FIG. As shown in FIG. 10, the plating layer 10 in the present embodiment is formed by sequentially laminating a Ni plating layer 17 and a Pd plating layer 18 on the surface of the frame material 2. The thickness of the Ni plating layer 17 is set to 0.5 to 2 μm, and the thickness of the Pd plating layer 18 is set to 0.005 to 0.2 μm. The Pd plating layer 18 is a metal layer having good connectivity with bonding wires and solder paste, such as wire bonding for connecting the bonding wires 13 as shown in FIG. 7 or a mounting board (printed wiring board) not shown. Soldering to can be performed reliably.

このような構成のリードフレーム１では、粗面３Ａ，３Ｂ、８Ａ，８Ｂの表面粗度（Ｒａ）を０．３μｍ以上に設定し、めっき層１０を構成するＮｉめっき層１７及びＰｄめっき層１８の厚さ範囲を設定したことにより、粗面３Ａ，３Ｂ、８Ａ，８Ｂの表面プロファイルを崩すことなく針状の突起の表面をめっき層１０でコーティングした形状を保つことができる。このため、このリードフレーム１を樹脂封止したときに、めっき層１０を含めた微細突起が封止樹脂に食い込むアンカー効果を奏しているものと考えられる。   In the lead frame 1 having such a configuration, the surface roughness (Ra) of the rough surfaces 3A, 3B, 8A, 8B is set to 0.3 μm or more, and the Ni plating layer 17 and the Pd plating layer 18 constituting the plating layer 10 are formed. By setting the thickness range, the shape in which the surface of the needle-like protrusion is coated with the plating layer 10 can be maintained without destroying the surface profile of the rough surfaces 3A, 3B, 8A, 8B. For this reason, when this lead frame 1 is resin-sealed, it is considered that the fine protrusion including the plating layer 10 has an anchor effect that bites into the sealing resin.

（リードフレームの製造方法）
次に、図２〜図６を用いて本実施の形態に係るリードフレームの製造方法について説明する。 (Lead frame manufacturing method)
Next, the manufacturing method of the lead frame according to the present embodiment will be described with reference to FIGS.

まず、本実施の形態では、図２に示すように、ダイパッド部３やリード部８などの所定のパターン形成がされているフレーム素材２を用意する。このフレーム素材２（圧延銅合金板）の構成材料は、例えば、三菱電機メテックス製，低すず，Ｎｉ銅合金ＭＦ２０２を用いる。   First, in the present embodiment, as shown in FIG. 2, a frame material 2 on which a predetermined pattern is formed such as a die pad portion 3 and a lead portion 8 is prepared. As a constituent material of the frame material 2 (rolled copper alloy plate), for example, a low tin, Ni copper alloy MF202 manufactured by Mitsubishi Electric Metex is used.

次に、図３に示すように、フレーム素材２の下面（一方の主面）に、マスク材としての保護フィルム９をラミネートする。そして、フレーム素材２の保護フィルム９で覆われていない部分を、過酸化水素と硫酸とを主成分とするマイクロエッチング液に浸漬させて、約９０秒のマイクロエッチングを行って、図４に示すような粗面３Ａ，３Ｂ、８Ａ，８Ｂを形成する。これら粗面３Ａ，３Ｂ、８Ａ，８Ｂの表面プロファイルは、急峻な針状の凹凸となる。このような粗面化処理を行った結果、粗面３Ａ，３Ｂ、８Ａ，８Ｂのエッチング量が２μｍで、表面粗さ（Ｒａ）が０．３３μｍ、Ｓｒａｔｉｏが２．０８であった。なお、エッチング量とは、エッチングで掘り下げた平均の深さを表す。Ｓｒａｔｉｏは、凹凸面の表面積を、測定範囲の平面の面積で割った値である。   Next, as shown in FIG. 3, a protective film 9 as a mask material is laminated on the lower surface (one main surface) of the frame material 2. Then, the portion of the frame material 2 that is not covered with the protective film 9 is immersed in a microetching solution containing hydrogen peroxide and sulfuric acid as main components, and microetching is performed for about 90 seconds, as shown in FIG. Such rough surfaces 3A, 3B, 8A, 8B are formed. The surface profiles of these rough surfaces 3A, 3B, 8A, 8B are steep needle-like irregularities. As a result of such roughening treatment, the etching amount of the rough surfaces 3A, 3B, 8A and 8B was 2 μm, the surface roughness (Ra) was 0.33 μm, and the Sratio was 2.08. Note that the etching amount represents an average depth dug by etching. Sratio is a value obtained by dividing the surface area of the uneven surface by the area of the plane of the measurement range.

その後、図５に示すように、保護フィルム（マスク材）９を剥離し、図６に示すようなめっき層１０を形成する。なお、このめっき層１０は、上述したように、フレーム素材２の表面に、順次、Ｎｉめっき層１７、Ｐｄめっき層１８が積層されてなる。なお、めっき層１０の形成方法は、電解めっき法や無電解めっき法など周知の方法を用いることができる。ここで、Ｎｉめっき層１７の厚さが０．５〜２μｍ、Ｐｄめっき層１８の厚さが０．００５〜０．２μｍの範囲となるようにめっき層の成長を制御する。このようにして、リードフレームの製造が完了する。   Then, as shown in FIG. 5, the protective film (mask material) 9 is peeled off to form a plating layer 10 as shown in FIG. As described above, the plating layer 10 is formed by sequentially laminating the Ni plating layer 17 and the Pd plating layer 18 on the surface of the frame material 2. In addition, the formation method of the plating layer 10 can use well-known methods, such as an electrolytic plating method and an electroless plating method. Here, the growth of the plating layer is controlled so that the thickness of the Ni plating layer 17 is in the range of 0.5 to 2 μm and the thickness of the Pd plating layer 18 is in the range of 0.005 to 0.2 μm. In this way, the manufacture of the lead frame is completed.

本実施の形態に係るリードフレームの製造方法では、エッチング時間が短く生産性を高めることができる。また、めっき層１０の厚さが薄いため、高価なめっき液の消費を抑えることができる。   In the lead frame manufacturing method according to the present embodiment, the etching time is short and the productivity can be improved. Moreover, since the thickness of the plating layer 10 is thin, consumption of an expensive plating solution can be suppressed.

次に、図７〜図９を用いて半導体装置の製造方法及び半導体装置の構成について説明する。   Next, a method for manufacturing a semiconductor device and a configuration of the semiconductor device will be described with reference to FIGS.

図７に示すように、上述した製造方法で作製したリードフレーム１のダイパッド部３の上面に、半導体チップ１１をペースト剤１２を介して搭載する。その後、ワイヤボンディングを行って、リード部８の先端部と半導体チップ１１の対応する電極との間をボンディングワイヤ１３で接続する。次に、図８に示すように、リードフレーム１の下面に樹脂もれ防止用保護フィルム１４をラミネートした後、全体を例えばエポキシ樹脂でなる封止樹脂１５でモールドする。その後、所望の形状となるように、封止樹脂１５及びリードフレーム１を一括して切断（個片化）することにより、図９に示す半導体装置（半導体パッケージ）１６が完成する。   As shown in FIG. 7, the semiconductor chip 11 is mounted via the paste agent 12 on the upper surface of the die pad portion 3 of the lead frame 1 manufactured by the manufacturing method described above. Thereafter, wire bonding is performed to connect the tip of the lead portion 8 and the corresponding electrode of the semiconductor chip 11 with the bonding wire 13. Next, as shown in FIG. 8, after the resin leak prevention protective film 14 is laminated on the lower surface of the lead frame 1, the whole is molded with a sealing resin 15 made of, for example, an epoxy resin. Thereafter, the sealing resin 15 and the lead frame 1 are collectively cut (separated) so as to have a desired shape, whereby the semiconductor device (semiconductor package) 16 shown in FIG. 9 is completed.

本実施の形態の半導体装置１６では、リード部８及びダイパッド部３の下面が封止樹脂１５の下面側で露出するようになっている。この露出したリード部８は、図示しない実装基板（プリント配線基板）側に半田付けにより接続される。   In the semiconductor device 16 of the present embodiment, the lower surfaces of the lead portion 8 and the die pad portion 3 are exposed on the lower surface side of the sealing resin 15. The exposed lead portion 8 is connected to a mounting board (printed wiring board) (not shown) by soldering.

このような構成の半導体装置１６では、リードフレーム１のダイパッド部３及びリード部８の下面を除く表面が粗面化されているため、封止樹脂１５との密着強度が高く、振動や温度変化に対する耐久性を発揮することができる。   In the semiconductor device 16 having such a configuration, since the surface of the lead frame 1 excluding the lower surface of the die pad portion 3 and the lead portion 8 is roughened, the adhesion strength with the sealing resin 15 is high, and vibration and temperature change occur. It is possible to demonstrate durability against.

ここで、圧延銅合金板に本実施の形態の粗面化処理を行った場合と、有機酸系の処理を行った場合の比較を行った。   Here, the case where the roughening process of this Embodiment was performed to the rolled copper alloy board, and the case where an organic acid type process were performed were compared.

下表１は、本実施の形態のように過酸化水素と硫酸とを主成分とするマイクロエッチング液を用いて粗面化処理を施した例と、従来のように有機酸系（この例では商品名がＣＺ８１００を用いた）を用いた比較例におけるエッチング量、表面粗度（Ｒａ）、Ｓｒａｔｉｏ、エッチング時間を比較したものである。比較例においては、エッチング量が１μｍ，２μｍ，３μｍの場合を挙げている。

Figure 0005353954
Table 1 below shows an example of surface roughening using a micro-etching solution mainly composed of hydrogen peroxide and sulfuric acid as in the present embodiment, and an organic acid system (in this example, This is a comparison of the etching amount, surface roughness (Ra), Sratio, and etching time in a comparative example using a product name of CZ8100. In the comparative example, the etching amounts are 1 μm, 2 μm, and 3 μm.
Figure 0005353954

上記表１より、有機酸系を用いた比較例では、０．１５μｍの粗さを得るのに、深さ３μｍにエッチングしなければならないことがわかる。このため、それ以上の粗さを得たい場合は、さらに深くエッチングする必要があり、このエッチングに時間を要するため、実際のリードフレームの生産には適さないことがわかる。これに対して、本実施の形態の粗面化処理を行うと、エッチング深さが２μｍで、比較例の２倍以上の粗さを得ることができる。本実施の形態では、過酸化水素と硫酸とを主成分とするマイクロエッチング液を用いて粗面化処理を施したことにより、細かい針状の凹凸を持った表面形状が得られる。この形状が、数値で表されるパラメータ以上にアンカー効果を奏するのに有効であると考えられる。   From Table 1 above, it can be seen that in the comparative example using the organic acid system, it is necessary to etch to a depth of 3 μm in order to obtain a roughness of 0.15 μm. For this reason, when it is desired to obtain a roughness higher than that, it is necessary to etch deeper, and this etching takes time, and it is understood that it is not suitable for production of an actual lead frame. On the other hand, when the roughening treatment of the present embodiment is performed, the etching depth is 2 μm, and a roughness twice or more that of the comparative example can be obtained. In the present embodiment, a surface shape having fine needle-like irregularities can be obtained by performing the roughening treatment using a micro-etching solution containing hydrogen peroxide and sulfuric acid as main components. This shape is considered to be more effective for achieving the anchor effect than the numerical value parameter.

本実施の形態における封止樹脂と密着強度を測定するため、図１１に示すようなカップせん断強度を測定した。銅合金（ＭＦ２０２）の圧延銅合金板の上に、上記と同様のめっき層の形成、及び変色防止処理を施して密着強度試験片２０を作製した。この密着強度試験片２０をホットプレート上で２２０℃、６０秒間加熱した後、更にホットプレート上で２２０℃、６０秒間の加熱を行い、更にホットプレート上で２４０℃、８０秒間の加熱を行った。成型は、１２５ｋｇ／ｃｍの圧力下で１７５℃、１２０秒間の加熱を行った。その後、更に１７５℃、５時間の加熱を行ってエポキシ樹脂２１を硬化させた。   In order to measure the sealing resin and adhesion strength in the present embodiment, cup shear strength as shown in FIG. 11 was measured. On the rolled copper alloy plate of copper alloy (MF202), the same plating layer formation and discoloration prevention treatment as described above were performed to produce an adhesion strength test piece 20. The adhesion strength test piece 20 was heated on a hot plate at 220 ° C. for 60 seconds, further heated on the hot plate at 220 ° C. for 60 seconds, and further heated on the hot plate at 240 ° C. for 80 seconds. . Molding was performed by heating at 175 ° C. for 120 seconds under a pressure of 125 kg / cm. Thereafter, the epoxy resin 21 was cured by further heating at 175 ° C. for 5 hours.

このように成型したエポキシ樹脂２１と密着強度試験片２０に、図１１に示す矢印方向に荷重をかけ、剥離したときの荷重を接着面の面積で割って単位面積当たりの荷重（ｋＮ／ｃｍ２）を求めた。 A load is applied to the molded epoxy resin 21 and the adhesion strength test piece 20 in the direction of the arrow shown in FIG. 11 and the load when peeled is divided by the area of the adhesive surface (kN / cm 2). )

この結果、せん断強度の値として次の値が得られ、本実施の形態の粗面処理を行うことにより、封止樹脂との密着強度を高める効果が得られた。   As a result, the following values were obtained as shear strength values, and the effect of increasing the adhesion strength with the sealing resin was obtained by performing the rough surface treatment of the present embodiment.

（１）粗面化なしの場合、０．０４ｋＮ／ｃｍ２
（２）粗面化あり、防錆処理なしの場合、０．４２ｋＮ／ｃｍ２
（３）粗面化あり、シラン系防錆処理ありの場合、０．５４ｋＮ／ｃｍ２
〔第２の実施の形態〕
図１２及び図１３を用いて、本発明の第２の実施の形態を説明する。なお、本実施の形態において上述の第１の実施の形態と同一の部分には同一の符号を付して説明を省略する。 (1) 0.04 kN / cm 2 in the case of no roughening
(2) 0.42 kN / cm 2 with roughening and without rust prevention treatment
(3) In the case of roughening and silane-based antirust treatment, 0.54 kN / cm 2
[Second Embodiment]
A second embodiment of the present invention will be described with reference to FIGS. In the present embodiment, the same parts as those in the first embodiment described above are denoted by the same reference numerals and description thereof is omitted.

第２の実施の形態に係る回路部材は、リードフレーム表面のうち樹脂封止用金型と接する部分を平滑な面とし、その他の部分を粗面化したリードフレームで、封止樹脂成形時の樹脂バリの発生や、樹脂もれを防ぐ効果を有する。図１２（ａ）は、図２と同様にパターン形成されたフレーム素材２の断面を示す。部分粗化の方法としては、図１２（ｂ）に示すように、図３で説明したフレーム素材２の下面に保護フィルムをラミネートする方法の代わりにフレーム素材２をゴムパッキン２７、２８を介して上下一対のエッチング用の冶具２９、３０で挟み、エッチング用冶具２９に付設されたノズル３１からマイクロエッチング液３２をフレーム素材２に所定時間噴射してマイクロエッチングして粗面を形成する。   The circuit member according to the second embodiment is a lead frame having a smooth surface on the surface of the lead frame that is in contact with the resin sealing mold and a roughened surface on the other portion. It has the effect of preventing the occurrence of resin burrs and resin leakage. FIG. 12A shows a cross section of the frame material 2 patterned in the same manner as FIG. As a method of partial roughening, as shown in FIG. 12 (b), instead of the method of laminating a protective film on the lower surface of the frame material 2 described in FIG. A rough surface is formed by sandwiching a pair of upper and lower etching jigs 29 and 30 and micro-etching a micro-etching liquid 32 from a nozzle 31 attached to the etching jig 29 onto the frame material 2 for a predetermined time.

このとき、ゴムパッキン２８はフレーム素材２の下面、ゴムパッキン２７はフレーム素材２の上面のうち樹脂封止用金型の接する部分を覆ってマスク材の役割を果たし、マイクロエッチングから保護してフレーム素材２の平滑な面が残る。   At this time, the rubber packing 28 serves as a mask material by covering the lower surface of the frame material 2 and the rubber packing 27 covers the portion of the upper surface of the frame material 2 that is in contact with the resin sealing mold, and protects the frame from microetching. The smooth surface of the material 2 remains.

図１２（ｃ）は、エッチング後に、エッチング用の冶具からフレーム素材２を取り出した状態を示しており、下面２３及び上面のうちゴムパッキン２７で覆われた部分（樹脂封止用金型に接する部分）２４が平滑な面として残り、それ以外の表面は粗面３Ａ、３Ｂ、８Ａ、８Ｂとなっている。   FIG. 12C shows a state in which the frame material 2 is taken out from the etching jig after the etching, and the lower surface 23 and the portion covered with the rubber packing 27 on the upper surface (in contact with the resin sealing mold). Part) 24 remains as a smooth surface, and the other surfaces are rough surfaces 3A, 3B, 8A, and 8B.

次に、図１２（ｄ）に示すように、ダイパッド部３及びリード部８を含むフレーム素材２の表面に、上記第１の実施の形態と同様にめっき層１０を形成し、リードフレーム１Ａとして完成する。   Next, as shown in FIG. 12D, a plating layer 10 is formed on the surface of the frame material 2 including the die pad portion 3 and the lead portion 8 in the same manner as in the first embodiment, and the lead frame 1A is formed. Complete.

図１３に上記リードフレーム１Ａを用いて半導体装置を製造する工程を示す。リードフレーム１Ａに、図１３（ａ）に示すように、ダイパッド部上面にペースト剤１２を介して半導体チップ１１を搭載した後、ワイヤボンディングを行ってリード部８と半導体チップ１１の対応する電極同士をボンディングワイヤ１３で接続する。   FIG. 13 shows a process of manufacturing a semiconductor device using the lead frame 1A. As shown in FIG. 13A, after the semiconductor chip 11 is mounted on the upper surface of the die pad portion via the paste agent 12 on the lead frame 1A, wire bonding is performed to connect the corresponding electrodes of the lead portion 8 and the semiconductor chip 11 to each other. Are connected by a bonding wire 13.

次に、図１３（ｂ）に示すように、樹脂封止用金型２５を用いて封止樹脂１５でモールドする。樹脂モールド後、リードフレームを樹脂封止用金型２５から取り出した状態を図１３（ｃ）に示す。この状態でリード部の不要な個所を所望の形状に切断し、半導体装置（半導体パッケージ）図１３（ｄ）が完成する。なお、本実施の形態では、個別モールドを例示しているため、一括モールド時のような個片化のためのダイサーカットの工程は無い。   Next, as shown in FIG. 13 (b), the resin sealing mold 15 is used to mold with a sealing resin 15. FIG. 13C shows a state in which the lead frame is taken out from the resin sealing die 25 after the resin molding. In this state, unnecessary portions of the lead portion are cut into a desired shape, and the semiconductor device (semiconductor package) FIG. 13D is completed. In addition, in this Embodiment, since the separate mold is illustrated, there is no dicer cut process for individualization like the batch molding.

図１３（ｂ）の封止樹脂による樹脂モールド時に、樹脂封止用金型２５と接する部分のリードフレーム１Ａの表面が粗面化されていると樹脂封止用金型２５とリードフレーム１Ａとの間に隙間が生じ、封止樹脂が入り込み樹脂バリとなったり、極端な場合は金型の外に封止樹脂が漏れることになる。本実施の形態では、粗面化された部分は上記第１の実施の形態と同じ効果を奏するとともに、前記のように樹脂封止用金型２５と接する部分のリードフレーム１Ａの表面を平滑な面としているので、樹脂封止用金型２５とリードフレーム１Ａとが密着し樹脂バリや樹脂漏れを防止する効果がある。   When the surface of the lead frame 1A in contact with the resin sealing mold 25 is roughened during resin molding with the sealing resin in FIG. 13B, the resin sealing mold 25 and the lead frame 1A A gap is formed between them, and the sealing resin enters and becomes a resin burr. In an extreme case, the sealing resin leaks out of the mold. In the present embodiment, the roughened portion has the same effect as in the first embodiment, and the surface of the lead frame 1A that is in contact with the resin sealing mold 25 as described above is smooth. Since it is a surface, the resin sealing mold 25 and the lead frame 1A are in close contact with each other, and there is an effect of preventing resin burrs and resin leakage.

〔第３の実施の形態〕
図１５及び図１６を用いて本発明の第３の実施の形態に係る回路部材について説明する。なお、本実施の形態において上述した第１の実施の形態と同一の部分には同一の符号を付して説明を省略する。 [Third Embodiment]
A circuit member according to a third embodiment of the present invention will be described with reference to FIGS. In the present embodiment, the same parts as those in the first embodiment described above are denoted by the same reference numerals and description thereof is omitted.

本実施の形態では、図１５（ａ）に示すように、エッチングや金型打ち抜きによりダイパッド部３やリード部８などのリードフレームの所定のパターンが形成された圧延銅合金からなるフレーム素材２を用意する。   In the present embodiment, as shown in FIG. 15A, a frame material 2 made of a rolled copper alloy in which a predetermined pattern of a lead frame such as the die pad portion 3 and the lead portion 8 is formed by etching or die punching is used. prepare.

次に、図１５（ｂ）に示すように、フレーム素材２のダイパッド上面の半導体チップを搭載する部分及びリード上面のボンディングワイヤを接続する部分に貴金属めっき層１０Ｂを形成するとともに、図１５（ｃ）に示すように、フレーム素材２の下面に保護フィルム（マスク材）９をラミネートする。   Next, as shown in FIG. 15B, a noble metal plating layer 10B is formed on the portion of the frame material 2 where the semiconductor chip is mounted on the upper surface of the die pad and the portion of the lead upper surface where the bonding wire is connected. ), A protective film (mask material) 9 is laminated on the lower surface of the frame material 2.

次に、フレーム素材２の表面にマイクロエッチング液を噴射もしくはフレーム素材２をマイクロエッチング液に浸漬して所定時間（約９０秒）のマイクロエッチングを行って、図１５（ｄ）に示すような３Ａ、３Ｂ、８Ａ、８Ｂの粗面を形成する。ここで、フレーム素材２の表面のうち貴金属めっき層１０Ｂが施された部分と保護フィルム９がラミネートされた部分はマイクロエッチングから保護されておりフレーム素材２表面の平滑面が残る。図１５（ｅ）は、保護フィルム９を剥離し完成したリードフレーム１の断面を示す図であり、下面２３と貴金属めっき層１０Ｂは平滑な面が保存されており、それ以外の表面は粗面３Ａ、３Ｂ、８Ａ、８Ｂが形成されている。   Next, micro-etching liquid is sprayed on the surface of the frame material 2 or the frame material 2 is immersed in the micro-etching solution and micro-etching is performed for a predetermined time (about 90 seconds), and 3A as shown in FIG. The rough surfaces of 3B, 8A, and 8B are formed. Here, the portion of the surface of the frame material 2 on which the noble metal plating layer 10B is applied and the portion on which the protective film 9 is laminated are protected from microetching, and the smooth surface of the surface of the frame material 2 remains. FIG. 15 (e) is a view showing a cross section of the lead frame 1 completed by peeling off the protective film 9. The lower surface 23 and the noble metal plating layer 10B have a smooth surface, and the other surfaces are rough surfaces. 3A, 3B, 8A, and 8B are formed.

ここで、前記の貴金属めっき層１０Ｂとしては、Ａｇめっき層、もしくはフレーム素材２表面に順次Ｎｉめっき層、Ｐｄめっき層が積層されてなるめっき層である。   Here, the noble metal plating layer 10B is an Ag plating layer or a plating layer in which a Ni plating layer and a Pd plating layer are sequentially laminated on the surface of the frame material 2.

図１６は、図１５の工程で製造された本発明のリードフレームを用いてＱＦＮ（Quad Flat Non-leaded package）を製造する工程を示している。図１６（ａ）は、図１５（ｅ）に対応した単位パターンが多面付けされたリードフレームの断面図を示している。   FIG. 16 shows a process of manufacturing a QFN (Quad Flat Non-leaded package) using the lead frame of the present invention manufactured in the process of FIG. FIG. 16A shows a cross-sectional view of a lead frame in which unit patterns corresponding to FIG.

次に、図１６（ｂ）に示すように、リードフレーム下面には必要に応じて樹脂バリ防止用フィルムを貼り、ダイパッド上面にペースト剤１２を介して半導体チップ１１を搭載した後、ワイヤボンディングを行ってリード部８のめっき層１０Ｂと半導体チップ１１の対応する電極同士をボンディングワイヤ１３で接続する。   Next, as shown in FIG. 16B, a resin burr prevention film is attached to the lower surface of the lead frame as necessary, and the semiconductor chip 11 is mounted on the upper surface of the die pad via the paste agent 12, and then wire bonding is performed. Then, the plating layer 10B of the lead portion 8 and the corresponding electrodes of the semiconductor chip 11 are connected by the bonding wire 13.

その後、図１６（ｃ）のように樹脂封止用金型（一括モールド用金型）２５を用いて封止樹脂１５で一括モールド（樹脂封止）する。   After that, as shown in FIG. 16C, a resin molding die (batch molding die) 25 is used to perform a batch molding (resin sealing) with the sealing resin 15.

次に、実装時のはんだ接続性を向上させるため、図１６（ｄ）に示すように封止樹脂から露出したリード部及びダイパッド部にはんだめっき層２２を施した後、個片化の切断位置２６で一括モールドされたリードフレームをダイサーカットして図１６（ｅ）に示すように各半導体装置が完成する。   Next, in order to improve solder connectivity at the time of mounting, the solder plating layer 22 is applied to the lead portion and die pad portion exposed from the sealing resin as shown in FIG. The lead frame that is collectively molded at 26 is dicer cut to complete each semiconductor device as shown in FIG.

この第３の実施の形態においても、前述の第１の実施の形態と同様の効果を得ることができる。なお、本実施の形態では、半導体チップ搭載面やワイヤボンディング面のみにめっき層を施し、又、はんだ付けを行うリード部８の下面ははんだめっきを施しているため、高価な貴金属めっき液を節約でき、製品コストを低く抑えることができるとともに、ワイヤボンディング性や半導体チップ１１のマウント性を高めることができる。   In the third embodiment, the same effect as that of the first embodiment can be obtained. In this embodiment, the plating layer is applied only to the semiconductor chip mounting surface and the wire bonding surface, and the lower surface of the lead portion 8 to be soldered is subjected to solder plating, thus saving an expensive noble metal plating solution. In addition, the product cost can be kept low, and the wire bonding property and the mountability of the semiconductor chip 11 can be improved.

〔回路部材の表面積層構造〕
次に、本発明に係る回路部材の表面積層構造を、図１０を用いて説明する。圧延銅板もしくは圧延銅合金板でなる導電性素材としてのフレーム素材２の表面に、表面粗度（Ｒａ）が０．３μｍ以上の粗面８Ａが形成され、この粗面８Ａに、順次、Ｎｉめっき層１７、Ｐｄめっき層１８が積層されたものであり、Ｎｉめっき層の厚さが０．５〜２μｍ、Ｐｄめっき層の厚さが０．００５〜０．２μｍであることが好ましい。このような表面積層構造とすることにより、導電性素材と絶縁性樹脂との密着強度を向上することができる。また、図１４に示すように、Ｐｄめっき層１８の上には、厚さが０．００３〜０．０１μｍのＡｕめっき層１９が積層されている構成としてもよい。このようなＡｕめっき層は、Ｐｄめっき層の表面に酸化膜が形成されることを防ぐ効果がある。 [Surface laminate structure of circuit members]
Next, the surface laminated structure of the circuit member according to the present invention will be described with reference to FIG. A rough surface 8A having a surface roughness (Ra) of 0.3 μm or more is formed on the surface of the frame material 2 as a conductive material made of a rolled copper plate or a rolled copper alloy plate, and Ni plating is sequentially applied to the rough surface 8A. It is preferable that the layer 17 and the Pd plating layer 18 are laminated, and the thickness of the Ni plating layer is 0.5 to 2 μm and the thickness of the Pd plating layer is 0.005 to 0.2 μm. By setting it as such a surface lamination structure, the adhesive strength of an electroconductive raw material and insulating resin can be improved. As shown in FIG. 14, an Au plating layer 19 having a thickness of 0.003 to 0.01 μm may be laminated on the Pd plating layer 18. Such an Au plating layer has an effect of preventing an oxide film from being formed on the surface of the Pd plating layer.

〔その他の実施の形態〕
上述した実施の形態の開示の一部をなす論述および図面はこの発明を限定するものであると理解すべきではない。この開示から当業者には様々な代替実施の形態、実施例および運用技術が明らかとなろう。 [Other Embodiments]
It should not be understood that the descriptions and drawings which form part of the disclosure of the above-described embodiments limit the present invention. From this disclosure, various alternative embodiments, examples and operational techniques will be apparent to those skilled in the art.

例えば、第１、第２及び第３の実施の形態では、めっき層１０をＡｇめっき層１層もしくは、Ｎｉめっき層１７とＰｄめっき層１８の２層を積層した構成としたが、図１４に示した回路部材の表面積層構造のように、Ｐｄめっき層１８の上にさらにＡｕめっき層１９を積層しためっき層１０Ａとしてもよい。なお、このＡｕめっき層１９の厚さは、０．００３〜０．０１μｍの範囲であることが好ましい。   For example, in the first, second, and third embodiments, the plating layer 10 has a structure in which one Ag plating layer or two layers of the Ni plating layer 17 and the Pd plating layer 18 are stacked. A plated layer 10 </ b> A in which an Au plated layer 19 is further stacked on the Pd plated layer 18 may be used as in the surface laminated structure of the circuit member shown. The thickness of the Au plating layer 19 is preferably in the range of 0.003 to 0.01 μm.

上述した第１、第２及び第３の実施の形態では、パッケージタイプとしてＱＦＮやＳＯＮなどの薄型で実装面積の小さいタイプに適用したが、ＱＦＰ、ＳＯＰ、ＦＬＧＡなどのタイプのリードフレームにも勿論適用可能であり、封止樹脂との密着強度の向上を図ることができる。   In the first, second, and third embodiments described above, the package type is applied to a thin type having a small mounting area such as QFN or SON, but of course, a lead frame of a type such as QFP, SOP, or FLGA is also used. It is applicable, and the adhesion strength with the sealing resin can be improved.

さらに、上述した第１、第２及び第３の実施の形態では、回路部材としてリードフレームを適用して説明したが、車両の供給電源を車載用補器へ分配する電気接続箱に用いられるコネクタの導電板やバスバーなど回路部材にも適用可能である。   In the first, second, and third embodiments described above, the lead frame is applied as the circuit member. However, the connector used in the electrical connection box that distributes the vehicle power supply to the on-vehicle auxiliary devices is described. It is also applicable to circuit members such as conductive plates and bus bars.

１ リードフレーム（回路部材）
２ フレーム素材
３ ダイパッド部
３Ａ，３Ｂ 粗面
８ リード部
８Ａ 粗面
９，１４ 保護フィルム
１０，１０Ａ，１０Ｂ めっき層
１１ 半導体チップ
１２ ペースト剤
１３ ボンディングワイヤ
１５ 封止樹脂
１６ 半導体装置
１７ Ｎｉめっき層
１８ Ｐｄめっき層
１９ Ａｕめっき層 1 Lead frame (circuit member)
2 Frame material 3 Die pad portion 3A, 3B Rough surface 8 Lead portion 8A Rough surface 9, 14 Protective film 10, 10A, 10B Plating layer 11 Semiconductor chip 12 Paste agent 13 Bonding wire 15 Sealing resin 16 Semiconductor device 17 Ni plating layer 18 Pd plating layer 19 Au plating layer

Claims (4)

上面に半導体チップを搭載するダイパッド部と、前記半導体チップに電気的に接続されるリード部とを備えたフレーム素材を、圧延銅板もしくは圧延銅合金板をパターン加工して形成した回路部材であって、
前記ダイパッド部及び前記リード部の上面及び側壁面に粗面が形成されると共に、前記ダイパッド部及び前記リード部の下面が平滑面とされ、前記ダイパッド部及び前記リード部の表面に前記粗面が形成された部分は粗面となるめっき層が形成され、前記リード部の下面が露出するように封止樹脂に埋設されることを特徴とする回路部材。 A circuit member formed by patterning a rolled copper plate or a rolled copper alloy plate with a frame material having a die pad portion for mounting a semiconductor chip on an upper surface and a lead portion electrically connected to the semiconductor chip. ,
A rough surface is formed on the upper surface and side wall surface of the die pad portion and the lead portion, a lower surface of the die pad portion and the lead portion is a smooth surface, and the rough surface is formed on the surfaces of the die pad portion and the lead portion. A circuit member, wherein a plated layer that is a rough surface is formed in the formed portion, and is embedded in a sealing resin so that a lower surface of the lead portion is exposed. 請求項１に記載の回路部材であって、
前記粗面の表面粗度（Ｒａ）が、０．３μｍ以上であることを特徴とする回路部材。 The circuit member according to claim 1 ,
The circuit member, wherein the rough surface has a surface roughness (Ra) of 0.3 μm or more. 請求項１又は２に記載の回路部材であって、
前記粗面は、過酸化水素と硫酸を主成分とするマイクロエッチング液で処理されてなることを特徴とする回路部材。 The circuit member according to claim 1 or 2 ,
The circuit member according to claim 1, wherein the rough surface is treated with a micro-etching solution containing hydrogen peroxide and sulfuric acid as main components. 圧延銅板もしくは圧延銅合金板でなる、ダイパッド部とリード部とを備え、前記ダイパッド部及び前記リード部の上面及び側壁面に粗面が形成され、且つ前記ダイパッド部及び前記リード部の下面が平滑面とされると共に、前記ダイパッド部及び前記リード部表面に前記粗面が形成された部分は粗面となるめっき層が積層された回路部材と、
前記ダイパッド部の上面に搭載された半導体チップと、
前記半導体チップと前記リード部とを接続するボンディングワイヤと、
前記リード部の下面を露出させるように、前記回路部材及び前記半導体チップ及び前記ボンディングワイヤを封止する電気絶縁性の封止樹脂と、
を備えることを特徴とする半導体装置。 A die pad portion and a lead portion made of a rolled copper plate or a rolled copper alloy plate are provided, rough surfaces are formed on the upper surface and side wall surface of the die pad portion and the lead portion, and the lower surfaces of the die pad portion and the lead portion are smooth. And a circuit member in which a plating layer that is a rough surface is laminated on a portion where the rough surface is formed on the surface of the die pad part and the lead part,
A semiconductor chip mounted on the upper surface of the die pad portion;
A bonding wire connecting the semiconductor chip and the lead portion;
An electrically insulating sealing resin that seals the circuit member, the semiconductor chip, and the bonding wire so as to expose the lower surface of the lead portion;
A semiconductor device comprising:
JP2011126491A 2011-06-06 2011-06-06 Circuit member and semiconductor device Active JP5353954B2 (en)