JP5282564B2 - Organic electroluminescence device - Google Patents

Abstract

The present invention can equalize film thicknesses of organic EL thin films among effective optical region picture elements and within respective picture elements in manufacturing of an organic EL device to form an organic EL layer by ejecting and coating organic EL materials using an ink jet printing method. Surrounding of a display picture element region, dummy bank 43 groups having the same shape and the same pitch as those of the display picture elements 42 are installed, and an organic EL material ink composition 41 is also coated on the surroundings of the display picture element region, and an organic EL thin film is formed.

Description

  The present invention relates to an organic electroluminescence (referred to as EL throughout this specification) device and a manufacturing method thereof.

  In recent years, the development of light-emitting elements using organic substances has been accelerated as a spontaneous emission type display that replaces a liquid crystal display. As an organic electroluminescence element (referred to as EL throughout this specification) using an organic substance as a light emitting material, a method of forming a low molecular organic EL material (light emitting material) by a vapor deposition method (see Non-Patent Document 1), A method of applying a polymer organic EL material (see Non-Patent Document 2) has been mainly reported.

  As a means for colorization, in the case of a low molecular weight material, a method of depositing and forming a different light emitting material on a desired pixel through a mask is performed. On the other hand, coloration by fine patterning using an ink-jet method is attracting attention for polymer materials. A method for forming an organic EL element by an inkjet method has been proposed (see Patent Documents 1 to 7).

JP-A-7-235378 Japanese Patent Laid-Open No. 10-12377 JP-A-10-153967 Japanese Patent Laid-Open No. 11-40358 Japanese Patent Laid-Open No. 11-54270 Japanese Patent Laid-Open No. 11-339957 U.S. Pat. No. 006087196 Appl. Phys. Lett. 51 (12), 21 September (1987) 913. Appl. Phys. Lett. 71 (1), 7 July (1997) 34.

  The ink jet method can discharge and apply droplets having a diameter of the order of μm with high resolution, and thus enables high-definition patterning of organic EL materials. However, the drying of the micro liquid applied on the substrate is very fast, and the solvent molecules evaporated from the micro liquid applied to the pixel area at the ends (upper end, lower end, right end, left end) of the application area on the substrate. Due to the low pressure, it generally begins to dry quickly. In addition, when active driving is performed using a TFT element, the pixel arrangement may not be equally spaced in the X and Y directions due to the shape and arrangement of the TFT element region, wiring, and the like. A local evaporation solvent molecular partial pressure difference occurs around the droplet. Such a difference in the drying time of the organic material liquid applied on the pixel causes unevenness of the film thickness of the organic thin film within the pixel and between the pixels. Such film thickness unevenness causes display unevenness such as luminance unevenness and emission color unevenness.

  Accordingly, an object of the present invention is to manufacture an organic EL device in which an organic EL material is discharged and applied onto an electrode to form an organic EL layer, and the environment surrounding the organic EL material solution applied to the pixel region, drying It is to provide a uniform organic EL device in which the luminance and emission color are not uneven between the pixels in the effective optical region and within the pixels.

An organic electroluminescence device according to an embodiment of the present invention includes an effective optical region contributing to display, and a dummy region provided in a region outside the effective optical region, and the effective optical region and the dummy region Includes a bank, and the effective optical region includes a first electrode partitioned by the bank, a second electrode disposed to face the first electrode, the first electrode, A first light emitting film including a light emitting material disposed between the second electrode and the first light emitting film including the light emitting material on the bank of the dummy region; Is provided with a different second light emitting film.
An organic electroluminescence device according to an embodiment of the present invention includes an effective optical region contributing to display, and a dummy region provided in a region outside the effective optical region, and the effective optical region and the dummy region , A bank is provided, and in the effective optical region, a first electrode partitioned by the bank, a second electrode disposed to face the first electrode, the first electrode, A light emitting film disposed between the second electrode and the second electrode, and an organic film is provided on the bank in the dummy region.
An organic electroluminescence device according to an embodiment of the present invention includes an effective optical region, and a dummy region that is an outer region of the effective optical region and is disposed around the effective optical region. The optical region includes a first electrode partitioned by a partition wall, a second electrode disposed to face the first electrode, and a first organic material disposed between the first electrode and the second electrode. And a TFT element connected to the first electrode, the dummy area has a plurality of second organic substances disposed around the effective optical area, and the TFT element is formed The first organic substance and the plurality of second organic substances are light emitting materials.

The organic electroluminescence device according to an embodiment of the present invention is characterized in that a TFT element connected to the first electrode is provided, and the TFT element is not formed in the dummy region. To do.
The organic electroluminescence device according to an embodiment of the present invention is characterized in that a plurality of the organic films are provided.
The organic electroluminescence device according to an embodiment of the present invention is characterized in that the organic film includes the light emitting film.
The organic electroluminescence device according to one embodiment of the present invention is characterized in that the organic film includes a hole injecting material.
The organic electroluminescence device according to an embodiment of the present invention is characterized in that the first electrode is not provided in the dummy region.
The organic electroluminescence device according to an embodiment of the present invention is characterized in that the second electrode is provided in the dummy region.
The organic electroluminescence device according to an embodiment of the present invention is characterized in that the light emitting layer and the organic film are formed at the same pitch.
The organic electroluminescence device according to one embodiment of the present invention is characterized in that the first light emitting film and the second light emitting film are formed at the same pitch.
Moreover, the organic electroluminescence device according to an embodiment of the present invention is characterized in that the second organic material is planarly arranged on the upper, lower, left and right sides of the effective optical region.

  The organic electroluminescence device according to an embodiment of the present invention includes a plurality of organic substances formed at a first pitch in a first direction and at a second pitch in a second direction intersecting the first direction, and a partition wall. A plurality of first electrodes partitioned from each other, a second electrode formed at a position facing the plurality of first electrodes, and a plurality of TFT elements connected to the plurality of first electrodes, The plurality of TFT elements are arranged in a matrix in the effective optical region, and the TFT elements are formed in a dummy region located outside the effective optical region and around the effective optical region. The plurality of first electrodes are arranged at positions corresponding to the plurality of TFT elements, and the plurality of organic substances are located in the dummy optical area and the plurality of first organic substances located in the effective optical area. A plurality of second organic substances, wherein one of the plurality of first organic substances is disposed between one first electrode of the plurality of first electrodes and the second electrode, The second organic material is disposed around the effective optical region, and the first organic material and the second organic material are light emitting materials.

  The organic electroluminescence device according to an embodiment of the present invention is characterized in that the plurality of second organic substances are arranged in a plane on the upper, lower, left and right sides of the effective optical region.

  An organic electroluminescence device according to an embodiment of the present invention includes an effective optical region, and a dummy region disposed outside the effective optical region and around the effective optical region, The effective optical region includes a first electrode partitioned by a partition wall, a second electrode disposed opposite to the first electrode, and a first electrode disposed between the first electrode and the second electrode. 1 organic substance, the dummy area has a plurality of second organic substances arranged around the effective optical area, the first electrode is not formed, and the first organic substance is formed. The plurality of second organic substances is a light emitting material.

  Moreover, the organic electroluminescence device according to an embodiment of the present invention is characterized in that the second organic material is planarly arranged on the upper, lower, left and right sides of the effective optical region.

  An organic electroluminescence device according to an embodiment of the present invention includes an effective optical region, a dummy region disposed around the effective optical region, the outer region of the effective optical region, and a first direction. A plurality of organic substances formed at a second pitch in a second direction intersecting the first direction at a first pitch, a plurality of first electrodes partitioned from each other by a partition, and opposed to the plurality of first electrodes A plurality of first organic substances located in the effective optical region, wherein the plurality of first electrodes are disposed in the effective optical region. And a plurality of second organic substances located in the dummy region, wherein one of the plurality of first organic substances is a first electrode of the plurality of first electrodes and the second electrode. Arranged between the plurality of second organic substances, Wherein is disposed around the effective optical area, the first organic and second organic material characterized in that it is a light-emitting material.

  The organic electroluminescence device according to an embodiment of the present invention is characterized in that the plurality of second organic substances are arranged in a plane on the upper, lower, left and right sides of the effective optical region.

  An organic electroluminescence device according to an embodiment of the present invention includes an effective optical region, a dummy region disposed outside the effective optical region, around the effective optical region, and the effective optical device. A partition formed in the region and the dummy region, and in the effective optical region, a first electrode partitioned by the partition, a second electrode disposed to face the first electrode, A first organic material disposed between the first electrode and the second electrode, and the dummy region has a plurality of second organic materials disposed around the effective optical region, and The second organic material is formed on the partition, and the first organic material and the plurality of second organic materials are light emitting materials.

  Moreover, the organic electroluminescence device according to an embodiment of the present invention is characterized in that the second organic material is planarly arranged on the upper, lower, left and right sides of the effective optical region.

  The organic electroluminescence device according to an embodiment of the present invention includes a plurality of organic substances formed at a first pitch in a first direction and at a second pitch in a second direction intersecting the first direction, and a partition wall. A plurality of first electrodes partitioned from each other; and a second electrode formed at a position facing the plurality of first electrodes, wherein the plurality of first electrodes are disposed in an effective optical region. The plurality of organic materials includes a plurality of first organic materials located in the effective optical region and a plurality of second organic materials located in the dummy region. One of the plurality of first organic materials is the plurality of the plurality of organic materials. One of the first electrodes is disposed between the first electrode and the second electrode, and the plurality of second organic substances are formed on the partition wall around the effective optical region, and 1 organic matter and the second organic matter are luminescent materials And wherein the Rukoto.

  The organic electroluminescence device according to an embodiment of the present invention is characterized in that the plurality of second organic substances are arranged in a plane on the upper, lower, left and right sides of the effective optical region.

  In the method for manufacturing an organic electroluminescence device of the present invention, an organic electroluminescence device forming region including an effective optical region in which a plurality of display pixels related to display are arranged and a first dummy region not related to display has a plurality of effective optics. In a method for manufacturing an organic electroluminescence device using a substrate for an organic electroluminescence device having a region group, a second dummy region is formed around the effective optical region group so as to surround the plurality of organic electroluminescence device formation regions A step of forming a composition containing an organic electroluminescent material in the first dummy region, the second dummy region, and the display pixel, and the organic electroluminescence device along the periphery of the organic electroluminescent device forming region. Cut the electroluminescent device formation area Characterized in that it comprises a to step.

  According to the above manufacturing method, in the effective optical region, the environment and drying around the organic EL material liquid applied in the effective optical region can be made uniform, and the film thickness between and within each pixel can be made uniform. The organic electroluminescence layer refers to a layer that contributes to light emission, and includes a hole injection layer, a light emitting layer, an electron injection layer, and the like. The effective optical region indicates, for example, an effective optical region when the organic EL device is a display device, and a region that contributes to illumination when the organic EL device is a lighting device.

  By the above manufacturing method, the surrounding environment of the applied organic EL material liquid is made uniform even in the pixels at the end of the effective optical region, and the droplets in the pixel at the end of the effective optical region are dried. It is possible to prevent the organic EL thin film layer from becoming extremely faster than drying and to make the film thickness of the organic EL thin film layer uniform between the pixels in the effective optics.

  Here, the dummy area is an area not related to display or illumination. Therefore, the organic EL layer formed in the dummy region may not emit light, but may emit light as long as it does not affect display and illumination.

  According to the above manufacturing method, even when two or more effective optical regions are provided on one substrate and each effective optical region is separated in the final process to manufacture two or more organic EL devices, pixels at the end of the effective optical region The surrounding environment of the organic EL material liquid applied to the liquid crystal is made uniform in the same way as other pixels, and the drying of the inner pixel droplets is prevented from becoming extremely faster than the inner pixel droplet drying. And the film thickness of the organic EL thin film layer between the pixels can be made uniform. As a result, a plurality of organic EL devices having no unevenness in luminance and emission color can be manufactured at a time from one substrate between pixels and within each pixel.

  In the method of manufacturing an organic electroluminescent device according to the present invention, the step of forming the composition may be performed by using a composition in which an organic electroluminescent material is dissolved or dispersed in a solvent to form a second composition in a part of the first dummy region. A first application step of applying an object; a second application step of applying a first composition to the display region; and a third application step of applying a second composition to the remaining portion of the first dummy region; It is characterized by including.

  In the method for producing an organic electroluminescence device of the present invention, in the step of forming the composition, the third coating step is continuously performed from the first coating step, and the third coating step is performed from the first coating step. It has the process of apply | coating a 3rd composition to the said 2nd dummy area | region before or after a process.

  According to the manufacturing method described above, the application of the organic electroluminescent material solution starts from the dummy area and ends in the dummy area, so that the application in the effective optical area can be stably performed.

  By the above manufacturing method, in the effective optical region, the environment and drying of the organic EL material liquid applied in the effective optical region are made uniform, and the film thickness of the organic EL thin film layer is uniform between and within each pixel. can do.

  In the organic electroluminescence device manufacturing method of the present invention, the display pixel includes a transparent electrode connected to a TFT, and the first dummy region and the second dummy region include dummy pixels not related to display. It is characterized by being arranged in plural.

  Further, in the method for manufacturing an organic electroluminescence device of the present invention, each of the display pixels is partitioned by a partition, the first composition is formed in a region partitioned by the partition, and each of the dummy pixels is It is partitioned off by partition walls, and the second composition or the third composition is formed in a region partitioned by the partition walls.

  As described above, according to the present invention, in the manufacture of an organic EL device in which an organic EL material is ejected and applied onto a substrate by an inkjet method to form an organic EL layer, dummy ejection and application are performed around the display pixel region. By introducing the region and arranging the application droplets at the same interval in the effective optical region, the organic EL material solution applied to the pixel region is uniformly dried, and the luminance between the effective optical region pixels or within each pixel. Further, it is possible to provide a uniform display device with no unevenness in emission color and a method for manufacturing the display device.

  Hereinafter, embodiments of the present invention will be described with reference to the drawings. An example in which an organic EL device is used as a display device is shown.

  An organic EL device manufacturing method using an inkjet method is a method in which an ink composition in which a hole injection layer material composed of an organic material forming a pixel and a light emitting material are dissolved or dispersed in a solvent is ejected from an inkjet head onto a transparent electrode. In this method, patterning is applied to form a hole injection / transport layer and a light emitting layer. In order to pattern and apply the ejected ink droplets to a predetermined pixel area with high accuracy, it is usual to provide partition walls (hereinafter referred to as banks) that partition the pixel area.

FIG. 1 shows a cross-sectional view of an example of a substrate structure used for manufacturing an organic EL display by an ink jet method. A circuit element portion 11 ′ having a thin film transistor (TFT) 11 is formed on a glass substrate 10, and a transparent electrode 12 made of ITO is patterned on the circuit element portion 11 ′. Further, an SiO ₂ bank 13 and an organic bank 14 made of an ink-repellent or ink-repellent organic substance are laminated in a region partitioning the transparent electrode 12. The shape of the bank, that is, the opening shape of the pixel may be any of a circle, an ellipse, and a square. However, since the ink composition has surface tension, it is preferable that the square corners are rounded. The material of the organic bank 14 is not particularly limited as long as it has excellent heat resistance, liquid repellency, ink solvent resistance, and adhesion to the base substrate. Organic bank 14, the materials originally provided with liquid repellency, for example, be non-fluorine-based resins, usually used, an organic resin such as acrylic resin or polyimide resin is patterned, surface by CF ₄ plasma treatment May be made liquid repellent. The bank is not limited to the one in which the inorganic material and the organic material are laminated as described above. For example, when the transparent electrode 14 is made of ITO, the SiO ₂ bank 13 is used in order to improve the adhesion with the transparent electrode 14. Some are preferred. It is sufficient that the height of the organic bank 14 is about 1 to 2 μm.

  Next, with reference to FIG. 2, an example of a method for manufacturing an organic EL device by an ink jet method will be described along the cross-sectional structure of each step.

  In FIG. 2A, a solution (ink composition) containing an organic EL material is applied to a pixel substrate having a bank structure by an inkjet method to form an organic EL thin film. The organic EL material ink composition 15 is ejected from the inkjet head 16 and landed as shown in FIG. After coating, the solvent is removed by a flow of vacuum and / or heat treatment or nitrogen gas, and the organic EL thin film layer 17 is formed (FIG. 3C). The organic EL thin film layer 17 is a laminated film composed of, for example, a hole injection layer and a light emitting layer.

  At this time, since ink droplets are not applied to the periphery of the display pixel at the end of the effective optical region (region where pixels related to display are formed), the solvent partial pressure of the ink solvent is lower than that on the inner pixel and the solvent is reduced. May dry quickly, and for example, a film thickness difference as shown in FIG. 2C may occur between display pixels.

  Therefore, in order to uniformly dry the droplets applied to each pixel, the ink composition is discharged and applied around the effective optical region, and the same environment is applied to each droplet applied to the effective optical region. It is preferable to make. In order to construct a more same environment, the application area of the organic material by inkjet is made larger than the effective optical area. For example, a dummy area having a bank structure of the same shape as the display pixel around the effective optical area (not related to display) It is more preferable to install a region where dummy pixels are formed.

  Further, in order to make the drying of the ink composition between pixels in the effective optical area more uniform, it is desirable that the individual application areas in the effective optical area are equally spaced. For this purpose, the pixels are preferably arranged at equal intervals. In the case where the pixel intervals are designed differently in the X direction and the Y direction due to the installation of TFTs, wirings, etc., ink droplets may be ejected so that the intervals between the application regions are equal between the pixels with wider intervals. It is more preferable if a dummy pixel in which a bank structure having the same shape as the pixel portion is formed between the pixels. The shape of the pixel may not be a point-symmetric shape such as a circle or a square, but may be a rectangle, a track shape, or an ellipse. When pixels such as rectangles and track shapes are arranged at different intervals in the X direction and Y direction, the application regions have the same interval in a wide pixel interval even if they do not have the same shape as the pixel portion. Even if the coating region is formed so that

  The present invention can be applied not only to display applications of organic EL devices, but also to light emitting devices and lighting devices that use organic EL elements as light emission sources.

  Hereinafter, the present invention will be described more specifically with reference to examples, but the present invention is not limited thereto.

( Example 1)
The substrate used in this example is a 2-inch TFT substrate in which circular pixels with a diameter of 30 μm are arranged at a pitch of 70.5 μm in both the X and Y directions. The TFT substrate is composed of a glass substrate 25 and a circuit element portion 26 ′ having a TFT 26 formed on the glass substrate. FIG. 3A shows a partial cross-sectional view (X direction) of the right end side of the TFT substrate. A transparent electrode 27 made of ITO is formed on the circuit element portion 26 ′, and a two-layer bank of SiO ₂ bank 28 and polyimide bank 29 is formed on the circuit element portion 26 ′ so as to partition the transparent electrode 27. Yes. The SiO ₂ bank 28 is formed by patterning TEOS (Tetraethylorthosilicate) with a thickness of 150 nm by CVD and by photoetching. Further, photosensitive polyimide is applied thereon, and a polyimide bank 29 having a thickness of 2 μm is formed by exposure and development. A non-photosensitive material may be used as a material for forming the bank.

In FIG. 3, the region where the transparent electrode 27 is formed is the effective optical region A, and the region where the transparent electrode 27 is not partitioned by the SiO ₂ bank 28 and the polyimide bank 29 is the dummy region B.

Prior to inkjet coating, the polyimide bank 29 is subjected to ink repellent treatment by atmospheric pressure plasma treatment. The atmospheric pressure plasma treatment is performed under atmospheric pressure with a power of 300 W, an electrode-substrate distance of 1 mm, an oxygen plasma treatment with an oxygen gas flow rate of 100 ml / min, a helium gas flow rate of 10 l / min, and a table transfer speed of 10 mm / s. Subsequently, the CF ₄ plasma treatment is performed in a reciprocating manner with a CF ₄ gas flow rate of 100 ml / min, a helium gas flow rate of 10 l / min, and a table transfer speed of 3 mm / s.

  Using Bayer (registered trademark) of Bayer as a hole injection layer material, an ink composition 30 dispersed with isopropyl alcohol, N-methylpyrrolidone, and 1,3-dimethyl-2-imidazolidinone as polar solvents was prepared. In the X and Y directions, the ink jet head (MJ-930C manufactured by Epson) is discharged and applied at a pitch of 70.5 μm. At that time, the upper and lower lines and the left and right lines are discharged around the display pixel at the same pitch. FIG. 3B shows a partial cross-sectional view on the right end side of the substrate after the hole injection layer material ink composition 30 has been pattern-coated. In the effective optical region A, the hole injection layer material ink composition 30 is applied on the transparent electrode 27, while in the dummy region B, the hole injection layer material ink composition 30 is applied on the polyimide bank 29.

  Next, the solvent is removed in vacuum (1 torr (133.3 Pa)) at room temperature for 20 minutes, and then heat treatment is performed in nitrogen at 200 ° C. (on a hot plate) for 10 minutes. The hole injection layer 31 is formed as shown in FIG. In the effective optical region A, the hole injection layer 31 having a uniform film thickness can be formed.

  Next, using a polyfluorene-based material that emits red, green, and blue as the light emitting layer, the red light emitting layer ink composition 32, the green light emitting layer ink composition 33, and the blue light emitting layer ink composition 34 are obtained. Prepare 3 types. As the ink solvent, cyclohexylbenzene was used. As shown in FIG. 3C, these ink compositions 32, 33, and 34 were ejected from an ink jet head and applied in a pattern with a 211.5 μm pitch in the X direction and a 70.5 μm pitch in the Y direction. At this time, the upper and lower and left and right 21 lines are discharged to the dummy area B at an extra pitch.

Next, light emitting layers 35, 36, and 37 are formed by heat treatment at 80 ° C. for 5 minutes on a hot plate in an N ₂ atmosphere. In the effective optical region A, the light emitting layers 35, 36, and 37 having a uniform film thickness can be formed.

  After forming the light emitting layer, as shown in FIG. 3D, as the cathode 38, a 2 nm LiF layer, a 20 nm Ca layer and a 200 nm Al layer are stacked by vacuum heating vapor deposition, and finally sealed with an epoxy resin 39. I do.

  In this manner, an organic EL device having a uniform display in the effective optical region A and free from luminance unevenness and color unevenness could be obtained.

( Example 2)
In the present embodiment, as shown in FIG. 4, a TFT substrate in which a dummy region B is arranged around the effective optical region A is used as in the first embodiment . The TFT substrate is composed of a glass substrate 25 and a circuit element portion 26 ′ having a TFT 26 formed on the glass substrate 25. Further, a transparent electrode 27 made of ITO is formed on the circuit element portion 26 ′, and a bank consisting of two layers of an SiO ₂ bank 28 and a polyimide bank 29 is formed on the circuit element portion 26 ′ so as to partition the transparent electrode 27. Has been. In this way, the display pixel 42 is formed in the effective optical area A.

In the dummy region B, a SiO ₂ film 28 ′ extending from the SiO ₂ bank is provided, and a dummy bank 40 is provided on the SiO ₂ film 28 ′ with the same shape and pitch as the display pixels 42. Pixels 43 are formed. FIG. 4A shows a partial cross-sectional view on the right end side of the substrate.

The same as in Example 1, a hole injection layer for the ink composition 41 at 70.5μm pitch, shown in FIG. 4 (B) a state in which patterning applied to the display pixel 42 and the dummy pixels 43. As in Example 1, the thickness of the hole injection layer of the display pixel 42 formed by drying and heat treatment was uniform.

Next, a light emitting layer ink composition made of a polyfluorene material is applied to the display pixels 42 and the dummy pixels 43 by patterning in the same manner as in Example 1, and the thickness of the light emitting layer formed by drying is uniform in the display pixels 42. there were. The organic EL device completed by forming and sealing the cathode had a uniform display with no luminance unevenness and color unevenness in the effective optical region A including the display pixels 42.

Example 3
In this example, as in Example 1, a TFT substrate in which a dummy area B was disposed around the effective optical area A was used. As shown in FIG. 5A, the TFT substrate is composed of a glass substrate 25 and a circuit element portion 26 ′ having a TFT 26 formed on the glass substrate 25. Further, a transparent electrode 27 made of ITO is formed on the circuit element portion 26 ′, and a bank consisting of two layers of an SiO ₂ bank 28 and a polyimide bank 29 is formed on the circuit element portion 26 ′ so as to partition the transparent electrode 27. Has been. In this way, the display pixel 42 is formed in the effective optical area A.

  Further, on the circuit element portion 26 ′ in the dummy region B, a dummy pixel 44 in which only the polyimide bank 29 is formed with the same shape and the same pitch as the display pixel 42 is provided. FIG. 5A is a partial cross-sectional view on the right end side of the substrate.

Next, as in Example 1, the polyimide bank 29 is subjected to ink repellent treatment by atmospheric pressure plasma treatment.

Next, as shown in FIG. 5B, in the same manner as in Example 1, the ink composition 30 containing the hole injection layer material was applied to the display pixel 42 and the dummy pixel 44 at a pitch of 70.5 μm in both the X and Y directions. Apply patterning to In the effective optical region A, the hole injection layer material ink composition 30 is applied on the transparent electrode 27, while in the dummy region B, the hole injection layer material ink composition 30 is applied on the circuit element portion 26 '. Yes.

  Next, the solvent was removed in vacuum (1 torr (133.3 Pa)) at room temperature for 20 minutes, and then heat treatment was performed in nitrogen at 200 ° C. (on a hot plate) for 10 minutes. A hole injection layer 31 as shown in FIG. In the effective optical region A, the hole injection layer 31 having a uniform film thickness can be formed.

Next, as in Example 1, three types of red light emitting layer ink composition 32, green light emitting layer ink composition 33, and blue light emitting layer ink composition 34 were prepared, as shown in FIG. 5C. Then, these ink compositions 32, 33, and 34 are ejected from the ink jet head, and are applied in a pattern with a 211.5 μm pitch in the X direction and a 70.5 μm pitch in the Y direction, respectively. At that time, it is preferable that the upper and lower and left and right 21 lines are discharged to the dummy area B at an extra pitch.

Next, the light emitting layers 35, 36 and 37 are formed by heat treatment at 80 ° C. for 5 minutes in a N ₂ atmosphere on a hot plate. In the effective optical region A, the light emitting layers 35, 36, and 37 having a uniform film thickness can be formed.

  After the light emitting layer is formed, as shown in FIG. 5D, a 2 nm LiF layer, a 20 nm Ca layer and a 200 nm Al layer are stacked by vacuum heating deposition as the cathode 38 and finally sealed with an epoxy resin 39. I do.

  Thus, it is possible to obtain an organic EL device having a uniform display without luminance unevenness and color unevenness in the effective optical region A.

( Example 4)
In this example, as in Example 1, a TFT substrate in which a dummy area B was disposed around the effective optical area A was used. As shown in FIG. 6A, the TFT substrate is composed of a glass substrate 25 and a circuit element portion 26 ′ having a TFT 26 formed on the glass substrate 25. Further, a transparent electrode 27 made of ITO is formed on the circuit element portion 26 ′, and a bank composed of two layers of an SiO ₂ bank 28 and a polyimide bank 29 is formed so as to partition the transparent electrode 27. In this way, the display pixel 42 is formed in the effective optical area A.

A dummy pixel 45 is provided on the circuit element portion 26 ′ in the dummy region B by laminating the SiO ₂ bank 28 and the polyimide bank 29 with the same shape and the same pitch as the display pixel 42. FIG. 6A is a partial cross-sectional view on the right end side of the substrate.

Next, as in Example 1, the polyimide bank 29 is subjected to ink repellent treatment by atmospheric pressure plasma treatment, and an ink composition 30 containing a hole injection layer material is further displayed on the display pixel 42 as shown in FIG. 6B. In addition, patterning is applied to the dummy pixels 45. In the effective optical region A, the hole injection layer material ink composition 30 is applied on the transparent electrode 27, while in the dummy region B, the hole injection layer material ink composition 30 is applied on the circuit element portion 26 '. .

Next, Example 1 under the same conditions of the hole injection layer material ink composition 30 solvent and removed, further Example 1 was heat-treated under the same conditions, a hole injection layer as shown in FIG. 6 (C) 31 Form. In the effective optical region A, the hole injection layer 31 having a uniform film thickness can be formed.

Next, as in Example 1, a red light emitting layer ink composition 32, a green light emitting layer ink composition 33, and a blue light emitting layer ink composition 34 were prepared. As shown in FIG. Each ink composition 32, 33, 34 is ejected from an inkjet head to apply a pattern. At this time, the upper and lower and left and right 21 lines are discharged to the dummy area B at an extra pitch.

Next, the light emitting layers 35, 36 and 37 are formed by heat treatment at 80 ° C. for 5 minutes in a N ₂ atmosphere on a hot plate. In the effective optical region A, the light emitting layers 35, 36, and 37 having a uniform film thickness can be formed.

  After forming the light emitting layer, as shown in FIG. 6D, a 2 nm LiF layer, a 20 nm Ca layer, and a 200 nm Al layer are stacked by vacuum heating deposition as the cathode 38, and finally sealed with an epoxy resin 39. I do.

  Thus, it is possible to obtain an organic EL device having a uniform display without luminance unevenness and color unevenness in the effective optical region A.

( Example 5)
In this example, as in Example 1, a TFT substrate in which a dummy area B was disposed around the effective optical area A was used. As shown in FIG. 7A, the TFT substrate is composed of a glass substrate 25 and a circuit element portion 26 ′ having a TFT 26 formed on the glass substrate 25. Further, a transparent electrode 27 made of ITO is formed on the circuit element portion 26 ′, and a bank consisting of two layers of an SiO ₂ bank 28 and a polyimide bank 29 is formed on the circuit element portion 26 ′ so as to partition the transparent electrode 27. Has been. In this way, the display pixel 42 is formed in the effective optical area A.

A dummy pixel 46 is provided on the circuit element portion 26 ′ in the dummy region B by laminating the SiO ₂ bank 28 and the polyimide bank 29 with the same shape and the same pitch as the display pixel 42. Note that the TFT 26 is not provided in the circuit element portion 26 ′ in the dummy region B. FIG. 7A shows a partial cross-sectional view on the right end side of the substrate.

Next, in the same manner as in Example 1, the polyimide bank 29 is subjected to ink repellent treatment by atmospheric pressure plasma treatment, and an ink composition 30 containing a hole injection layer material is further displayed on the display pixel 42 as shown in FIG. In addition, patterning is applied to the dummy pixel 46. In the effective optical region A, the hole injection layer material ink composition 30 is applied on the transparent electrode 27, while in the dummy region B, the hole injection layer material ink composition 30 is applied on the circuit element portion 26 '. Yes.

The solvent was then removed hole injection layer material ink composition 30 under the same conditions as in Example 1, further subjected to heat treatment under the same conditions as in Example 1, a hole injection layer as shown in FIG. 7 (C) 31 is formed. In the effective optical region A, the hole injection layer 31 having a uniform film thickness can be formed.

Next, as in Example 1, a red light emitting layer ink composition 32, a green light emitting layer ink composition 33, and a blue light emitting layer ink composition 34 were prepared, and as shown in FIG. Each ink composition 32, 33, 34 is ejected from an inkjet head to apply a pattern. At that time, it is preferable that the upper and lower and left and right 21 lines are discharged to the dummy area B at an extra pitch.

Next, the light emitting layers 35, 36 and 37 are formed by heat treatment at 80 ° C. for 5 minutes in a N ₂ atmosphere on a hot plate. In the effective optical region A, the light emitting layers 35, 36, and 37 having a uniform film thickness can be formed.

  After the light emitting layer is formed, as shown in FIG. 7D, a 2 nm LiF layer, a 20 nm Ca layer and a 200 nm Al layer are stacked by vacuum heating deposition as the cathode 38, and finally sealed with an epoxy resin 39. I do.

  Thus, it is possible to obtain an organic EL device having a uniform display without luminance unevenness and color unevenness in the effective optical region A.

Further, the dummy pixel 46 is configured by providing the transparent electrode 27, the SiO ₂ bank 28 and the polyimide bank 29 that partition the transparent electrode 27, and is the same as the display pixel 42 except that the TFT 26 is not provided. Because of the configuration, the hole injection layer material ink composition 30 applied to the dummy pixel 46 can be dried under the same conditions as when applied to the display pixel 42, and thus the effective optical region A has a greater film thickness. A uniform hole injection layer 31 can be formed, and a uniform display organic EL device free from luminance unevenness and color unevenness can be obtained.

( Example 6)
FIG. 8A shows part of the display pixel region and the dummy pixel region of the substrate used in this example. FIG. 8A is a plan view of the substrate, and the TFT element is not shown here. Circular pixels 50 having a diameter of 60 μm are arranged at a pitch of 80 μm in the horizontal (X) direction and at a pitch of 240 μm in the vertical (Y) direction. There is a dummy bank pixel 51 having a diameter of 80 μm and a diameter of 60 μm between the display pixels in the vertical direction line. Around the effective optical region, dummy pixels 52 having the same shape are vertically, right and left, 30 lines, and the same pitch of 80 μm. It is formed with. The display pixels are divided by the stacked banks of the SiO ₂ bank 53 and the polyimide bank 54 as before, and the basic cross-sectional structure other than the pixel diameter and pitch is the same as in the first or second embodiment .

FIG. 8B shows a state in which the same hole injection layer material ink composition 55 as that of Example 1 is applied to the display pixel 50 and the dummy pixels 51 and 52 in a pattern with a pitch of 80 μm. In the same manner as in Example 1, a hole injection layer was formed, and in the light emitting layer, the same three types of light emitting layer compositions 56, 57, and 58 as in Example 1 were coated at a pitch of 80 μm in length and 240 μm in width. A light emitting layer was laminated and formed by drying. FIG. 8C shows the pattern application of the light emitting layer ink composition. The organic EL device completed by forming and sealing the cathode had a uniform display with no luminance unevenness and color unevenness in the effective optical region.

( Example 7)
FIG. 9A shows part of the effective optical region and the dummy region of the substrate used in this example. FIG. 9A is a plan view of the substrate, and the TFT element is not shown here. Rectangular (rounded corners) -shaped pixels 60 having a horizontal width of 50 μm and a vertical width of 200 μm are arranged at a pitch of 80 μm in the horizontal (X) direction and at a pitch of 290 μm in the vertical (Y) direction. The interpixel spacing in the horizontal direction is 30 μm, and the interpixel spacing in the vertical direction is 90 μm. Around the display pixels 60..., Dummy pixels 61 having the same shape are formed at the same pitch of 80 μm and 290 μm for up and down, left and right, and 30 lines. The display pixel 60 is partitioned by a stacked bank of SiO ₂ 62 and polyimide 63 as before, and the basic cross-sectional structure other than the pixel diameter and pitch is the same as in the first or second embodiment .

The hole injection layer material ink composition 64 similar to that in Example 1 was applied to all the display pixels 60 and dummy pixels 61 in a pattern, and the composition was also applied to the center between the pixels in the vertical direction as shown in FIG. 9B. 64 was applied in a pattern. After drying, the hole injection layer in the formed pixel showed a uniform film thickness, but if it was not applied at the center between the pixels in the vertical direction, the film thickness was extremely thick at both ends in the vertical direction of the pixel. It got thick.

After forming the hole injection layer, the same light emitting layer composition 65, 66, and 67 as in Example 1 was applied to the light emitting layer by pattern coating at pitches of 240 μm and 290 μm, respectively. Similarly to the case, the light emitting layer ink compositions 65, 66, and 67 were also applied in a pattern at the center between the pixels in the vertical direction as shown in FIG. 9C. As a result, the thickness of the dried light emitting layer was uniform within and between pixels. The organic EL device completed by forming and sealing the cathode had a uniform display with no luminance unevenness and color unevenness in the effective optical region.

( Example 8)
FIG. 10A shows a plan view of a substrate used in this embodiment. FIG. 10B is a partial cross-sectional view taken along line MM ′ of FIG. As shown in FIGS. 10A and 10B, this substrate 101 is a substrate before the formation of the hole injection layer and the light emitting layer, and the circuit element portion 103 formed on the glass substrate 102; The light emitting element unit 104 is formed on the circuit element unit 103. The light emitting element section 104 is provided with display pixels and dummy pixels, which will be described later, and the light emitting element section 104 further includes an effective optical area A composed of display pixel groups and a dummy disposed around the effective optical area A. It is partitioned into a dummy area B consisting of a pixel group.

The circuit element unit 103 includes a plurality of TFT elements 105 formed on the glass substrate 102 and first and second interlayer insulating films 106 and 107 covering the TFT elements 105. The TFT elements 105 are arranged in a matrix, and transparent electrodes 108 made of ITO are connected to the TFT elements 105.
The transparent electrodes 108 are formed on the second interlayer insulating film 107 and are disposed at positions corresponding to the TFT elements 105. The transparent electrode 108 only needs to be formed in a shape such as a substantially circular shape, a rectangular shape, or a rectangular shape having a square arc shape in plan view.

  The TFT element 105 and the transparent electrode 108 are formed only at positions corresponding to the effective optical region A of the light emitting element unit 104.

Next, the SiO ₂ bank 109 and the polyimide bank 110 are laminated in the effective optical region A of the light emitting element portion 104. The SiO ₂ bank 109 and the polyimide bank 110 are provided between the transparent electrodes 108. Thereby, an opening 111 surrounding the transparent electrode 108 is provided.

In addition, the dummy region B of the light emitting element portion 104 is provided with a SiO ₂ thin film 109 ′ formed on the second interlayer insulating film 107 and a polyimide bank 110 ′ formed on the SiO ₂ thin film 109 ′. Yes. A dummy pixel 111 ′ having substantially the same shape as the display pixel 111 in the display pixel region A is provided by the polyimide bank 110 ′ in the dummy region B.

  Regarding the number of dummy pixels 111 ′ provided in the dummy region B, there are 10 or more sets of three dummy pixels of R, G, and B between the width X ′ along the X direction shown in FIG. It is preferable to provide it. Further, it is preferable to provide 10 or more columns of a large number of R, G, and B dummy pixels between the widths Y ′ along the Y direction shown in FIG. More preferably, the dummy pixels are arranged so that the widths X ′ and Y ′ are equal. By doing so, the drying condition of the composition ink in the pixels near the boundary with the dummy area B can be made more consistent with the drying conditions in the pixels near the center of the effective optical area A. In order to make the width X ′ and the width Y ′ equal, for example, each pixel (both display pixel and dummy pixel) is arranged at a pitch of 70.5 μm in the X direction and a pitch of 211.5 μm in the Y direction. When formed, 30 lines parallel to the Y direction between the width X ′ (lines consisting of three pairs of three dummy pixels R, G, B) and X between the width Y ′ A dummy pixel having 10 lines parallel to the direction may be formed. Accordingly, since the pitch in the Y direction is three times the pitch in the X direction, the widths X ′ and Y ′ are substantially equal. The number of dummy pixels is not limited to this, but if the number of dummy pixels 111 ′ is excessive, the frame not related to display becomes large, that is, the display module becomes large.

The substrate 101 is subjected to atmospheric pressure plasma processing as in Example 1 to perform ink repellent treatment on the polyimide banks 110 and 110 ′, and an ink composition containing a hole injection layer material is ejected from the inkjet head for display. Patterning is applied to the pixel 111 and the dummy pixel 111 ′. In the display pixel 111, the hole injection layer material ink composition is applied on the transparent electrode 108, while in the dummy 111 ′, the hole injection layer material ink composition is applied on the SiO ₂ thin film 109 ′.

  When the ink composition containing the hole injection layer material is ejected by the ink jet head, for example, an ink jet head having a nozzle row having a width approximately equal to the width direction (X direction in the drawing) of the display element unit 104 is prepared. It is preferable to carry out the inkjet head while moving it on the substrate 101 along the arrow Y direction in the figure from the lower side of FIG. As a result, the ejection order of the ink composition is in the order of the lower dummy area B in the figure, the effective optical area A, and the upper dummy area B in the figure, and the ink composition is ejected from the dummy area B to the dummy area. You can end with B. Since the composition ink is ejected in the dummy area B and then ejected in the effective optical area A, the ink composition in the effective optical area A can be uniformly dried.

Then, under the same conditions as in Example 1 the solvent was removed hole injection layer material ink composition was heat-treated further in Example 1 under the same conditions, the hole injection layer 131, as shown in FIG. 11 (A) Form.

  A dummy pixel 111 ′ is provided outside the effective optical region A, and the composition ink is discharged and dried in the same manner as the display pixel 111 on the dummy pixel 111 ′. The drying conditions of the composition ink in the display pixels 111 in the vicinity can be made to substantially coincide with the drying conditions in the display pixels 111 in the vicinity of the center of the effective optical area A, and thereby the display pixels in the vicinity of the boundary with the dummy area B 111 can form the hole injection layer 131 having a uniform film thickness. Therefore, the hole injection layer 131 having a uniform film thickness can be formed over the entire effective optical region A.

Next, in the same manner as in Example 1, the red, green, and blue light emitting layer ink compositions were ejected from the inkjet head and applied to the display pixels 111 and the dummy pixels 111 ′, and the N ₂ atmosphere was applied on the hot plate. The light emitting layers 135, 136, and 137 are formed by heat treatment at 80 ° C. for 5 minutes. In the effective optical region A, the light emitting layers 135, 136, and 137 having a uniform film thickness can be formed in the same manner as in the case of the hole injection layer 131.

  In the formation of the light emitting layer, the inkjet head is moved from the lower side of FIG. 10A onto the substrate 101 along the arrow Y direction in the same manner as in the case of the hole injection layer. The ink composition is discharged in the order of the lower dummy area B in the figure, the effective optical area A, and the upper dummy area B in the figure, whereby the ink composition is discharged from the dummy area B in the dummy area B. It is preferable to end the process. Thereby, in the whole effective optical area A, the ink composition containing a light emitting layer was able to be dried uniformly.

  After the light emitting layer is formed, as shown in FIG. 11B, a 2 nm LiF layer, a 20 nm Ca layer and a 200 nm Al layer are stacked by vacuum heating deposition as a cathode 138, and finally sealed with an epoxy resin 139. I do.

  Thus, it is possible to obtain an organic EL device having a uniform display without luminance unevenness and color unevenness in the effective optical region A.

Example 9
FIG. 12 shows a plan view of the substrate used in this embodiment. As shown in FIG. 12, the substrate 201 is mainly composed of a circuit element portion (not shown) formed on the glass substrate 202 and a plurality of light emitting element portions 204... Formed on the circuit element portion. ing. On the substrate 201 of FIG. 12, 16 light emitting element portions 204 are arranged in a matrix of 4 columns and 4 rows. Each light emitting element portion 204 is provided with display pixels and dummy pixels not shown in the same manner as in the eighth embodiment, and each light emitting element portion 204... Has an effective optical region A composed of display pixel groups, and effective optical elements. The area is divided into a dummy area B including dummy pixel groups arranged around the area A.

The configuration of the display pixel in the effective optical region A and the configuration of the dummy pixel in the dummy region B are the same as the configuration of the display pixel 111 and the dummy pixel 111 ′ described in the eighth embodiment . The configuration of the circuit element unit (not shown) is the same as the configuration of the circuit element unit 103 of the eighth embodiment .

  Thus, the substrate 201 is formed with an effective optical region group C composed of a plurality of effective optical regions A.

  The substrate 201 is finally cut along a one-dot chain line in the figure and cut into 16 small substrates. Thereby, a plurality of organic EL devices can be manufactured simultaneously from one substrate.

  Further, another dummy region D is formed around the effective optical region group C on the substrate 201.

  Regarding the number of dummy pixels provided in the dummy region D, it is preferable to provide 10 or more sets of three dummy pixels of R, G, and B between the width X ′ along the X direction shown in FIG. Further, it is preferable to provide 10 or more columns of a large number of R, G, and B dummy pixels between the width Y ′ along the Y direction shown in FIG.

The substrate 201 is subjected to ink repellent treatment in the same manner as in Example 8, and an ink composition containing a hole injection layer material is ejected from an ink jet head and is applied to display pixels and dummy pixels by patterning.

  When the ink composition containing the hole injection layer material is ejected by the ink jet head, for example, an ink jet head having a nozzle row having the same width as one display element portion 204 in the width direction (X direction in the drawing) is used. It is preferable that the inkjet head is prepared and moved while moving from the lower side in the drawing of FIG. 12 to the upper side in the drawing along the arrow Y direction in the drawing. The width of the inkjet head is not limited to this, and may be an integer multiple of the width of one display element unit 204.

  The locus of the inkjet head at this time is a zigzag locus in which, for example, as shown in FIG. 13 (A), the inkjet head H is moved to the upper side in the drawing and then runs obliquely to the lower side and then moved upward again. Alternatively, as shown in FIG. 13B, it may be a folded trajectory that moves upward, then slides (runs idle) in the horizontal direction, and then moves downward.

  In any of the above cases, the ejection order of the ink composition is dummy areas D and B, effective optical area A, dummy areas B and D, dummy areas D and B, effective optical areas A,..., Dummy areas B and D In this order, the ejection of the ink composition can be started from the dummy area D and ended in the dummy area D.

Further, as in Example 8, an ink jet head having a nozzle row having a width approximately the same as the width direction (X direction in the drawing) of the effective optical region group C is prepared, and this ink jet head is arranged on the lower side in FIG. The display element unit 204 may be moved to the upper side in the figure along the arrow Y direction in the figure. In this case, the ejection order of the ink composition is the order of the dummy areas D and B, the effective optical area A, and the dummy areas B and D. The ejection of the ink composition starts from the dummy area D and ends in the dummy area D. Can do.

  Therefore, in any case, since the ink composition is ejected from the dummy area D and then ejected from the effective optical area A, the ink composition can be uniformly dried in the entire effective optical area A.

  In addition, when the inkjet head takes a zigzag trajectory or a zigzag trajectory, the ink is always discharged from the dummy area D after the idle run, so the state of the ink filled in the inkjet head changes during the idle run. Even in this case, preliminary ejection is performed in the dummy area D and then ejection is performed in the effective optical area A, and ejection in the effective optical area A can be performed stably.

Next, in the same manner as in Example 1, the solvent of the hole injection layer material ink composition is removed and heat treatment is performed to form the hole injection layer 131.

  Since the dummy pixels of the dummy area B are provided outside the effective optical area A and the dummy pixels of another dummy area D are further provided outside the effective optical area A, the display pixels in the vicinity of the boundary with the dummy area B The drying conditions of the composition ink can be made to substantially coincide with the drying conditions of the display pixels near the center of the effective optical region A, so that even a display pixel near the boundary with the dummy region B has a uniform thickness. An injection layer can be formed. Therefore, a hole injection layer having a uniform film thickness can be formed over the entire effective optical region A.

  In particular, since the dummy region D is provided around the effective optical region group C, a hole injection layer having a uniform thickness can be formed even when a large number of display devices are manufactured from one substrate.

Next, in the same manner as in Example 1, the red, green, and blue light emitting layer ink compositions were ejected from the ink jet head, applied to the effective optical region and the dummy region, and then subjected to heat treatment to obtain R, G, and B A light emitting layer is formed. In the effective optical region A, a light emitting layer having a uniform thickness can be formed as in the case of the hole injection layer.

When forming the light emitting layer, the ink jet head is moved as shown in FIG. 13 (A) or FIG. 13 (B) in the same manner as in the case of the hole injection layer. The ejection order is the same as that in the case of the hole injection layer, whereby the ejection of the ink composition can be started from the dummy area D and ended in the dummy area D.
As a result, the ink composition could be uniformly dried over the entire effective optical area A.

  After the light emitting layer is formed, a 2 nm LiF layer, a 20 nm Ca layer and a 200 nm Al layer are stacked by vacuum heating deposition as a cathode, and finally sealed with an epoxy resin.

  Thus, it is possible to obtain an organic EL device having a uniform display without luminance unevenness and color unevenness in the effective optical region A.

  Although a high molecular material is used here as the organic EL layer, a low molecular material may be used. When a low molecular material is used, it is preferably formed by an evaporation method using a mask 71 as shown in FIG. At this time, the present invention can be realized by depositing a material using a mask in which an area corresponding to the effective optical area E and an area outside the area corresponding to the effective optical area E (area corresponding to the dummy area F) are opened. . Even when the vapor deposition method is used, it is possible to form a uniform organic EL layer in the entire effective optical region by providing the dummy region.

( Example 10)
Next, specific examples of the electronic apparatus including any one of the organic EL devices manufactured according to the first to ninth embodiments will be described.

  FIG. 15A is a perspective view illustrating an example of a mobile phone. In FIG. 15A, reference numeral 600 denotes a mobile phone body, and reference numeral 601 denotes a display portion using any of the organic EL devices.

  FIG. 15B is a perspective view illustrating an example of a portable information processing device such as a word processor or a personal computer. In FIG. 15B, reference numeral 700 denotes an information processing apparatus, reference numeral 701 denotes an input unit such as a keyboard, reference numeral 703 denotes an information processing apparatus body, and reference numeral 702 denotes a display unit using any one of the organic EL devices. Yes.

  FIG. 15C is a perspective view illustrating an example of a wristwatch-type electronic device. In FIG. 15C, reference numeral 800 denotes a watch body, and reference numeral 801 denotes a display unit using any of the organic EL devices.

Each of the electronic devices shown in FIGS. 15A to 15C includes a display unit using any one of the above-described organic EL devices, and the organic EL devices manufactured in Examples 1 to 9 above. Therefore, an electronic device having an effect of excellent display quality can be obtained regardless of which organic EL device is used.

Sectional drawing which shows an example of the manufacturing method of the organic electroluminescent apparatus by an inkjet system. Sectional drawing which shows an example of the manufacturing method of the organic electroluminescent apparatus by the inkjet system in connection with this invention. Process drawing explaining the manufacturing method of the organic electroluminescent apparatus of Example 1. FIG. Process drawing explaining the manufacturing method of the organic electroluminescent apparatus of Example 2. FIG. Process drawing explaining the manufacturing method of the organic electroluminescent apparatus of Example 3. FIG. Process drawing explaining the manufacturing method of the organic electroluminescent apparatus of Example 4. FIG. Process drawing explaining the manufacturing method of the organic electroluminescent apparatus of Example 5. FIG. Process drawing explaining the manufacturing method of the organic electroluminescent apparatus of Example 6. FIG. Process drawing explaining the manufacturing method of the organic electroluminescent apparatus of Example 7. FIG. It is a figure explaining the manufacturing method of the organic electroluminescent apparatus of Example 8, Comprising: (A) is a top view of the board | substrate before hole injection layer formation, (B) is the part which followed the MM 'line | wire of (A). It is sectional drawing. Process drawing explaining the manufacturing method of the organic electroluminescent apparatus of Example 8. FIG. It is a figure explaining the manufacturing method of the organic electroluminescent apparatus of Example 9, Comprising: It is a top view of the board | substrate before hole injection layer formation. It is a figure explaining the manufacturing method of the organic electroluminescent apparatus of Example 9, Comprising: It is a schematic diagram which shows the locus | trajectory of an inkjet head. It is a figure explaining the other manufacturing method of the organic electroluminescent apparatus of Example 9. FIG. FIG. 16 is a perspective view showing an electronic apparatus of Example 10.

10,25,102,202 ... glass substrate, 11 ... thin film transistor (TFT), 12,27,108 ... transparent electrode, 13,28,53,62,109 ... SiO ₂ banks, 14,29,40,54,63 , 110, 110 ′, organic matter (polyimide) bank, 15 ... organic EL material ink composition, 16 ... inkjet head, 17 ... organic EL thin film layer, 17 ... ink composition for light emitting layer, 26 ... thin film transistor (TFT), 30 , 41, 55, 64 ... hole injection layer material ink composition, 31 ... hole injection layer, 32, 56, 65 ... red light emitting material ink composition, 33, 57, 66 ... green light emitting material ink composition, 34 , 58, 67 ... blue light emitting material ink composition, 35 ... red light emitting layer, 36 ... green light emitting layer, 37 ... blue light emitting layer, 38 ... cathode, 42 ... display pixel, 43, 44 ... da -Pixel, 50 ... display pixel, 51 ... dummy pixel in display pixel region, 52 ... dummy pixel outside display pixel region, 60 ... display pixel, 61 ... dummy pixel outside display pixel region, 101, 201 ... substrate, 103 ... circuit element Department, 104, 204 ... display element unit, 105 ... TFT element, 109 '... SiO ₂ thin film, 111 ... display pixel 111' ... dummy pixels, 131 ... hole injection layer, 135, 136 ... light-emitting layer, A ... effective optical region, B, D ... dummy region, C ... effective optical region group.

Claims (5)

An effective optical area that contributes to the display;
A dummy area provided in an area outside the effective optical area,
A bank is provided in the effective optical region and the dummy region,
The effective optical region includes
A first electrode partitioned by the bank;
A second electrode disposed opposite the first electrode;
A first light-emitting film including a light-emitting material disposed between the first electrode and the second electrode,
An organic electroluminescence device , wherein a second light emitting film containing the light emitting material and different from the first light emitting film is provided on the bank in the dummy region. A TFT element connected to the first electrode is provided;
The organic electroluminescence device according to claim 1, wherein the TFT element is not formed in the dummy region. The dummy in the region, the organic electroluminescent device according to claim 1 or 2, wherein the first electrode is not provided.   The organic electroluminescent device according to claim 1, wherein the second electrode is provided in the dummy region. 5. The organic electroluminescent device according to claim 1, wherein the first light emitting film and the second light emitting film are formed at the same pitch. 6.

Images