JP5273710B2 - Etching agent - Google Patents

Etching agent Download PDF

Info

Publication number
JP5273710B2
JP5273710B2 JP2008190032A JP2008190032A JP5273710B2 JP 5273710 B2 JP5273710 B2 JP 5273710B2 JP 2008190032 A JP2008190032 A JP 2008190032A JP 2008190032 A JP2008190032 A JP 2008190032A JP 5273710 B2 JP5273710 B2 JP 5273710B2
Authority
JP
Japan
Prior art keywords
etching
weight
copper plating
plating layer
etching agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2008190032A
Other languages
Japanese (ja)
Other versions
JP2009149971A (en
Inventor
真美 中村
雅史 吉海
大作 秋山
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MEC Co Ltd
Original Assignee
MEC Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MEC Co Ltd filed Critical MEC Co Ltd
Priority to JP2008190032A priority Critical patent/JP5273710B2/en
Priority to TW097143843A priority patent/TWI411705B/en
Priority to CN2008101791141A priority patent/CN101445933B/en
Priority to KR1020080118152A priority patent/KR101497708B1/en
Publication of JP2009149971A publication Critical patent/JP2009149971A/en
Application granted granted Critical
Publication of JP5273710B2 publication Critical patent/JP5273710B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、硫酸、過酸化水素及び水を含む銅のエッチング剤に関する。   The present invention relates to an etchant for copper containing sulfuric acid, hydrogen peroxide and water.

プリント配線板の製造工程において、配線パターンを形成する方法としてセミアディティブ法がある。このセミアディティブ法では、電気絶縁層上に0.5〜2μｍ程度の無電解銅めっき層からなるシード層を形成し、その上に導体回路を電解銅めっきにて形成した後、不要な無電解銅めっき層をエッチングによって除去して配線パターンを形成している。このような無電解銅めっき層を除去するためのエッチング液としては、アゾール類を含むエッチング液が知られており、例えば過硫酸塩系エッチング液、過酸化水素−硫酸−アルコール系エッチング液、塩化銅エッチング液、塩化鉄エッチング液などにアゾール類を添加して使用されている（特許文献１〜４参照）。   There is a semi-additive method as a method of forming a wiring pattern in a manufacturing process of a printed wiring board. In this semi-additive method, a seed layer composed of an electroless copper plating layer of about 0.5 to 2 μm is formed on an electrical insulating layer, and a conductor circuit is formed thereon by electrolytic copper plating, followed by unnecessary electroless copper plating. The layer is removed by etching to form a wiring pattern. Etching solutions containing azoles are known as etching solutions for removing such electroless copper plating layers, such as persulfate-based etching solutions, hydrogen peroxide-sulfuric acid-alcohol etching solutions, and chlorides. An azole is added to a copper etching solution, an iron chloride etching solution, or the like (see Patent Documents 1 to 4).

しかし、これら従来技術に例示されているアゾール類の添加では無電解銅めっき層に対するエッチング速度と電解銅めっき層に対するエッチング速度の差が小さいため、導体回路間の不要な無電解銅めっき層を除去する際に、エッチング液により電解銅めっき層が腐食するおそれがある。このため、配線の幅が減少したり（パターン細り）、配線の厚みが減少したりする問題があった。   However, the addition of azoles exemplified in these prior arts removes the unnecessary electroless copper plating layer between conductor circuits because the difference between the etching rate for the electroless copper plating layer and the etching rate for the electrolytic copper plating layer is small. In doing so, the electrolytic copper plating layer may be corroded by the etching solution. For this reason, there existed a problem that the width | variety of wiring reduced (pattern thinning) and the thickness of wiring reduced.

また、上記従来技術では、無電解銅めっき層のエッチング速度を制御するのが困難であるため、不要な無電解銅めっき層を除去する間に、必要な無電解銅めっき層についても除去してしまうおそれがある。この点について、図１を参照しながら説明する。図１は、電気絶縁層１上に配線２が複数形成されたプリント配線板の概略断面図である。配線２は、シード層である無電解銅めっき層３と、無電解銅めっき層３上に形成された電解銅めっき層４とを含む。図１では、電解銅めっき層４の直下の必要な無電解銅めっき層３についてもエッチングにより一部が除去されており、アンダーカットＵＣが生じている。特に、ライン／スペースが20μｍ／20μｍを下回るような細線パターンの場合では、わずかでもアンダーカットＵＣが生じると、配線２の幅Ｗに対するアンダーカット長さＵＣＬの割合が大きくなるため、配線パターンの寸法精度の低下や、断線、欠落等が生じるおそれがあった。   Further, in the above prior art, it is difficult to control the etching rate of the electroless copper plating layer. Therefore, while removing the unnecessary electroless copper plating layer, the necessary electroless copper plating layer is also removed. There is a risk that. This point will be described with reference to FIG. FIG. 1 is a schematic cross-sectional view of a printed wiring board in which a plurality of wirings 2 are formed on an electrical insulating layer 1. The wiring 2 includes an electroless copper plating layer 3 as a seed layer and an electrolytic copper plating layer 4 formed on the electroless copper plating layer 3. In FIG. 1, a part of the necessary electroless copper plating layer 3 immediately below the electrolytic copper plating layer 4 is also removed by etching, resulting in an undercut UC. In particular, in the case of a fine line pattern in which the line / space is less than 20 μm / 20 μm, if even a slight undercut UC occurs, the ratio of the undercut length UCL to the width W of the wiring 2 increases. There was a risk that accuracy would drop, disconnection, or loss.

他方、配線パターン表面を粗化することによって絶縁樹脂などとの密着性を改善するための銅のエッチング液として、硫酸、過酸化水素及びアゾールを主成分とするエッチング液が知られている（特許文献５〜７参照）。   On the other hand, an etching solution containing sulfuric acid, hydrogen peroxide and azole as main components is known as a copper etching solution for improving adhesion to an insulating resin by roughening the surface of the wiring pattern (patent) References 5-7).

特開２００３−１３８３８９号公報JP 2003-138389 A 特開２００５−５３４１号公報Japanese Patent Laid-Open No. 2005-5341 特開２００６−９１２２号公報Japanese Patent Laid-Open No. 2006-9122 特開２００６−１３３４０号公報JP 2006-13340 A 特開２００５−２１３５２６号公報JP 2005-213526 A 特開２００２−１９４５７３号公報JP 2002-194573 A 特開２００２−７６６１０号公報JP 2002-76610 A

しかし、特許文献５〜７のエッチング液を無電解銅めっき層の除去に使用した場合には、配線パターンの表面を粗化してしまうため、特に細線パターンを形成する場合には、寸法精度の低下等が生じるおそれがあった。   However, when the etching solutions of Patent Documents 5 to 7 are used for removing the electroless copper plating layer, the surface of the wiring pattern is roughened, so that the dimensional accuracy is lowered particularly when a fine line pattern is formed. Etc. may occur.

本発明は、上記実情に鑑みてなされたものであり、セミアディティブ法において無電解銅めっき層を除去する際に、配線パターンの寸法精度の低下を防止できるエッチング剤を提供する。   This invention is made | formed in view of the said situation, and provides the etching agent which can prevent the fall of the dimensional accuracy of a wiring pattern, when removing an electroless copper plating layer in a semiadditive method.

上記目的を達成するため、本発明の第１のエッチング剤は、硫酸、過酸化水素及び水を含む銅のエッチング剤であって、カルボキシル基及びヒドロキシル基の少なくとも一方を分子中に２以上有するベンゾトリアゾール誘導体を含むことを特徴とする。   In order to achieve the above object, a first etching agent of the present invention is a copper etching agent containing sulfuric acid, hydrogen peroxide and water, and a benzoic acid having at least one of a carboxyl group and a hydroxyl group in the molecule. It includes a triazole derivative.

同じく上記目的を達成するため、本発明の第２のエッチング剤は、硫酸、過酸化水素及び水を含む銅のエッチング剤であって、環内にある異原子として窒素原子のみを有するアゾール類と、カルボシキル基を２以上有する多塩基酸又はその塩とを含むことを特徴とする。   In order to achieve the above object, the second etching agent of the present invention is a copper etching agent containing sulfuric acid, hydrogen peroxide and water, and azoles having only nitrogen atoms as hetero atoms in the ring, and And a polybasic acid having two or more carboxyl groups or a salt thereof.

なお、上記第１及び第２のエッチング剤は、いずれも銅のエッチング剤であるが、この「銅」には、純銅だけでなく銅合金も含まれる。また、本明細書において「銅」は、純銅又は銅合金を指す。   The first and second etching agents are both copper etching agents, but this “copper” includes not only pure copper but also copper alloys. In the present specification, “copper” refers to pure copper or a copper alloy.

本発明のエッチング剤によれば、電解銅めっき層の腐食を防止する機能と、無電解銅めっき層のエッチングを促進させる機能とを有するため、配線パターンの寸法精度の低下を防止することができる。   According to the etching agent of the present invention, since it has a function of preventing the corrosion of the electrolytic copper plating layer and a function of promoting the etching of the electroless copper plating layer, it is possible to prevent a reduction in the dimensional accuracy of the wiring pattern. .

本発明の第１のエッチング剤は、硫酸、過酸化水素及び水を含む銅のエッチング剤であって、カルボキシル基及びヒドロキシル基の少なくとも一方を分子中に２以上有するベンゾトリアゾール誘導体を含む。第１のエッチング剤では、ベンゾトリアゾールが電解銅めっき層の腐食を防止する機能を有し、カルボキシル基及びヒドロキシル基の少なくとも一方が無電解銅めっき層のエッチングを促進させる機能を有していると考えられる。よって、無電解銅めっき層に対するエッチング速度（以下、「ＥＲ１」という）を速くすると共に、電解銅めっき層に対するエッチング速度（以下、「ＥＲ２」という）を遅くすることができるため、ＥＲ１とＥＲ２との差を適切な範囲内にすることができる。これにより、セミアディティブ法において無電解銅めっき層を除去する際に、アンダーカットやパターン細りを防止できるため、配線パターンの寸法精度の低下を防止できる。   The first etching agent of the present invention is a copper etching agent containing sulfuric acid, hydrogen peroxide and water, and includes a benzotriazole derivative having at least one of a carboxyl group and a hydroxyl group in the molecule. In the first etching agent, benzotriazole has a function of preventing corrosion of the electrolytic copper plating layer, and at least one of a carboxyl group and a hydroxyl group has a function of promoting etching of the electroless copper plating layer. Conceivable. Therefore, the etching rate for the electroless copper plating layer (hereinafter referred to as “ER1”) can be increased, and the etching rate for the electrolytic copper plating layer (hereinafter referred to as “ER2”) can be decreased. Can be within an appropriate range. Thereby, when removing the electroless copper plating layer in the semi-additive method, undercutting and pattern thinning can be prevented, so that reduction in the dimensional accuracy of the wiring pattern can be prevented.

上記エッチング剤中の硫酸の濃度は、1〜25重量％が好ましく、3〜18重量％がより好ましく、さらに好ましくは7〜15重量％の範囲である。１重量％以上の場合は、エッチング速度が速くなるため、無電解銅めっき層を速やかに除去できる上、銅を溶解するのに充分な酸濃度を有しているため、頻繁に液交換をする必要がなくなりコスト面で有利である。一方、25重量％以下の場合は、溶解した銅が硫酸銅として析出するのを防止できるため、被処理面に銅が再付着したり、硫酸銅の結晶が導体配線を損傷したりする不具合を防止できる。   The concentration of sulfuric acid in the etching agent is preferably 1 to 25% by weight, more preferably 3 to 18% by weight, and still more preferably 7 to 15% by weight. In the case of 1% by weight or more, since the etching rate is increased, the electroless copper plating layer can be removed quickly, and the acid concentration is sufficient to dissolve copper, so the liquid is frequently exchanged. This eliminates the need and is advantageous in terms of cost. On the other hand, in the case of 25% by weight or less, it is possible to prevent the dissolved copper from precipitating as copper sulfate. Can be prevented.

上記エッチング剤中の過酸化水素の濃度は、0.5〜15重量％が好ましく、1〜10重量％がより好ましく、さらに好ましくは2〜5重量％の範囲である。0.5重量％以上の場合は、エッチング速度が速くなるため、無電解銅めっき層を速やかに除去できる。一方、15重量％以下の場合は、反応熱が過剰に発生しない程度のエッチング速度とすることができるため、アンダーカットの発生を防止できる。   The concentration of hydrogen peroxide in the etching agent is preferably 0.5 to 15% by weight, more preferably 1 to 10% by weight, and still more preferably 2 to 5% by weight. In the case of 0.5% by weight or more, the etching rate is increased, so that the electroless copper plating layer can be quickly removed. On the other hand, in the case of 15% by weight or less, the etching rate can be set to such an extent that the reaction heat is not excessively generated, so that undercutting can be prevented.

カルボキシル基及びヒドロキシル基の少なくとも一方を分子中に２以上有するベンゾトリアゾール誘導体（以下、「Ａ成分」という）の例としては、1-(1’,2’-ジカルボキシエチル）ベンゾトリアゾール（以下、「ＤＣＥＢＴＡ」という）、1-(2,3-ジカルボキシプロピル)ベンゾトリアゾール（以下、「ＤＣＰＢＴＡ」という）、1-(2’,3’-ジヒドロキシプロピル)ベンゾトリアゾール（以下、「ＤＨＰＢＴＡ」という）などが挙げられる。この中でもＤＣＥＢＴＡを使用した場合は、ＥＲ１とＥＲ２との差を適切な範囲内に容易に保つことができる。よって、アンダーカットやパターン細りを効果的に防止できる。   Examples of a benzotriazole derivative having at least one of a carboxyl group and a hydroxyl group in the molecule (hereinafter referred to as “component A”) include 1- (1 ′, 2′-dicarboxyethyl) benzotriazole (hereinafter referred to as “component A”). "DCEBTA"), 1- (2,3-dicarboxypropyl) benzotriazole (hereinafter referred to as "DCPBTA"), 1- (2 ', 3'-dihydroxypropyl) benzotriazole (hereinafter referred to as "DHPBTA") Etc. Among these, when DCEBTA is used, the difference between ER1 and ER2 can be easily kept within an appropriate range. Therefore, undercut and pattern thinning can be effectively prevented.

上記エッチング剤中のＡ成分の濃度は、0.0001〜10重量％が好ましく、0.0002〜5重量％がより好ましく、さらに好ましくは0.0005〜1重量％の範囲である。0.0001重量％以上の場合は、ＥＲ１とＥＲ２との差を適切な範囲内に容易に保つことができる。よって、アンダーカットやパターン細りを効果的に防止できる。一方、10重量％以下の場合は、Ａ成分の使用量を低減できるため、コスト面で有利である。   The concentration of the component A in the etching agent is preferably 0.0001 to 10% by weight, more preferably 0.0002 to 5% by weight, and still more preferably 0.0005 to 1% by weight. In the case of 0.0001% by weight or more, the difference between ER1 and ER2 can be easily maintained within an appropriate range. Therefore, undercut and pattern thinning can be effectively prevented. On the other hand, when the amount is 10% by weight or less, the amount of component A used can be reduced, which is advantageous in terms of cost.

上記エッチング剤では、ＥＲ１とＥＲ２のエッチング速度比（ＥＲ１／ＥＲ２）が３〜７となるように上記各成分を調整するのが好ましく、４〜６．８となるように上記各成分を調整するのがより好ましい。この範囲内であれば、アンダーカットやパターン細りを効果的に防止できる。エッチング速度比を上記範囲内とするための各成分の濃度は、被処理材における無電解銅めっき層及び電解銅めっき層の状態や、用いる成分などにより適宜調整すればよい。なお、後述する実施例において、エッチング速度比を上記範囲内とするための各成分の濃度の具体例を例示している。   In the etching agent, it is preferable to adjust the components so that the etching rate ratio (ER1 / ER2) of ER1 and ER2 is 3 to 7, and the components are adjusted to be 4 to 6.8. Is more preferable. Within this range, undercuts and pattern thinning can be effectively prevented. What is necessary is just to adjust suitably the density | concentration of each component for making an etching rate ratio into the said range according to the state of the electroless copper plating layer and electrolytic copper plating layer in a to-be-processed material, the component to be used, etc. In the examples described later, specific examples of the concentration of each component for making the etching rate ratio within the above range are illustrated.

上記エッチング剤のエッチング速度は、ＥＲ１については０．３〜２．０μm/minの範囲が好ましく、ＥＲ２については０．０５〜０．５μm/minの範囲が好ましい。この範囲内であれば、生産性を保ちつつ、エッチングの制御が容易となる。   The etching rate of the etching agent is preferably in the range of 0.3 to 2.0 μm / min for ER1, and in the range of 0.05 to 0.5 μm / min for ER2. Within this range, etching can be easily controlled while maintaining productivity.

上記エッチング剤には、ポリアリルアミン系カチオン性ポリマーが含まれていてもよい。パターン細りを効果的に防止できるからである。なお、上記「ポリアリルアミン系カチオン性ポリマー」とは、構成単位中にアリルアミン骨格を有するカチオン性ポリマーを指す。   The etching agent may contain a polyallylamine-based cationic polymer. This is because pattern thinning can be effectively prevented. The “polyallylamine-based cationic polymer” refers to a cationic polymer having an allylamine skeleton in a structural unit.

上記ポリアリルアミン系カチオン性ポリマーのエッチング剤中における濃度は、0.000005〜0.1重量％が好ましく、0.00005〜0.05重量％がより好ましく、さらに好ましくは0.000075〜0.015重量％の範囲である。0.000005重量％以上の場合は、パターン細りをより効果的に防止できる。一方、0.1重量％以下の場合は、エッチング速度の低下を抑制できるため、無電解銅めっき層を速やかに除去できる。更にコスト面でも有利である。   The concentration of the polyallylamine cationic polymer in the etching agent is preferably 0.000005 to 0.1% by weight, more preferably 0.00005 to 0.05% by weight, and still more preferably 0.000075 to 0.015% by weight. When it is 0.000005% by weight or more, pattern thinning can be more effectively prevented. On the other hand, in the case of 0.1% by weight or less, since the decrease in etching rate can be suppressed, the electroless copper plating layer can be quickly removed. Further, it is advantageous in terms of cost.

上記ポリアリルアミン系カチオン性ポリマーの重量平均分子量は、１００〜２０万が好ましく、５００〜１５万がより好ましく、８００〜１０万がさらに好ましい。重量平均分子量が上記範囲内であれば、パターン細りを効果的に防止できる。   The weight average molecular weight of the polyallylamine-based cationic polymer is preferably 100 to 200,000, more preferably 500 to 150,000, and still more preferably 800 to 100,000. If the weight average molecular weight is within the above range, pattern thinning can be effectively prevented.

上記ポリアリルアミン系カチオン性ポリマーの例としては、ポリアリルアミン、アリルアミン・ジメチルアリルアミン共重合体、ジアリルアミン酢酸塩・二酸化硫黄共重合体、ジアリルメチルエチルアンモニウムエチルサルフェイト・二酸化硫黄共重合体、ポリアリルアミンアミド硫酸塩、アリルアミン酢酸塩・ジアリルアミン酢酸塩共重合体、メチルジアリルアミンアミド硫酸塩重合体、ジアリルアミンアミド硫酸塩・マレイン酸共重合体などが挙げられる。この中でも、ポリアリルアミン、ジアリルアミン酢酸塩・二酸化硫黄共重合体、ジアリルメチルエチルアンモニウムエチルサルフェイト・二酸化硫黄共重合体を使用した場合は、パターン細りをより効果的に防止できるため好ましい。   Examples of the polyallylamine-based cationic polymer include polyallylamine, allylamine / dimethylallylamine copolymer, diallylamine acetate / sulfur dioxide copolymer, diallylmethylethylammonium ethyl sulfate / sulfur dioxide copolymer, polyallylamine amide Examples thereof include sulfates, allylamine acetate / diallylamine acetate copolymers, methyl diallylamine amide sulfate polymers, diallylamine amide sulfate / maleic acid copolymers, and the like. Among these, the use of polyallylamine, diallylamine acetate / sulfur dioxide copolymer, diallylmethylethylammonium ethyl sulfate / sulfur dioxide copolymer is preferable because pattern thinning can be more effectively prevented.

また、上記エッチング剤には、過酸化水素の安定剤としてフェノールスルホン酸、ベンゼンスルホン酸、クレゾールスルホン酸などの芳香族スルホン酸類や、メタンスルホン酸、エタンスルホン酸などのアルカンスルホン酸類や、有機アミン類など、あるいは微細配線間における濡れ性改善のための界面活性剤などが含まれていてもよい。これらの添加剤のエッチング剤中における濃度は、例えば０．０５〜１重量％程度の範囲である。さらに、エッチング速度を安定させるために、上記エッチング剤に銅イオンを溶解させてもよい。溶解させる銅イオンの濃度は、例えば10〜40g/L程度の範囲である。   In addition, the above etchants include aromatic sulfonic acids such as phenol sulfonic acid, benzene sulfonic acid, and cresol sulfonic acid as stabilizers for hydrogen peroxide, alkane sulfonic acids such as methane sulfonic acid and ethane sulfonic acid, and organic amines. Or a surfactant for improving wettability between fine wirings. The concentration of these additives in the etching agent is, for example, in the range of about 0.05 to 1% by weight. Furthermore, in order to stabilize the etching rate, copper ions may be dissolved in the etching agent. The concentration of copper ions to be dissolved is, for example, in the range of about 10 to 40 g / L.

上記エッチング剤は、上記の各成分を水に溶解させることにより、容易に調製することができる。上記水としては、イオン性物質や不純物を除去した水が好ましく、例えばイオン交換水、純水、超純水などが好ましい。   The said etching agent can be easily prepared by dissolving said each component in water. As the water, water from which ionic substances and impurities have been removed is preferable. For example, ion exchange water, pure water, ultrapure water, and the like are preferable.

上記エッチング剤は、各成分を使用時に所定の濃度になるように配合してもよく、濃縮液を調製しておき使用直前に希釈して使用してもよい。上記エッチング剤の使用方法は、特に限定されず、浸漬処理、スプレー処理等の方法を採用できるが、無電解銅めっき層を速やかに除去するためには、スプレー処理が好ましい。スプレー処理の場合は、スプレー圧を０．０５〜０．２ＭＰａの範囲に設定することが好ましい。これにより、アンダーカットの抑制が容易となる。また、エッチング時のエッチング剤の温度は、特に制限はないが、生産性の観点及びアンダーカット抑制の観点から15℃〜40℃で使用することが好ましい。   The etching agent may be blended so that each component has a predetermined concentration at the time of use, or a concentrated solution may be prepared and diluted immediately before use. The method of using the etching agent is not particularly limited, and methods such as immersion treatment and spray treatment can be adopted. However, spray treatment is preferable in order to quickly remove the electroless copper plating layer. In the case of spray treatment, it is preferable to set the spray pressure in the range of 0.05 to 0.2 MPa. Thereby, suppression of undercut becomes easy. Further, the temperature of the etching agent during etching is not particularly limited, but it is preferably used at 15 to 40 ° C. from the viewpoint of productivity and suppression of undercut.

上記エッチング剤の管理方法は、例えば遊離酸および過酸化水素の濃度については滴定等により定量し、適時補給を行うことにより適正濃度を維持しながら使用すればよい。また、その他の成分については、各々の特性に適した分析方法（例えば、Ａ成分の分析方法としては高速液体クロマトグラフィー等）を用いて定量し、適時補給を行うことにより適正濃度を維持しながら使用すればよい。この時のＡ成分の補給には、当該化合物の高濃度水溶液を用いるのが好ましい。   The management method of the etching agent may be used, for example, by quantifying the concentration of free acid and hydrogen peroxide by titration or the like, and maintaining the appropriate concentration by performing timely replenishment. In addition, other components are quantified using an analysis method suitable for each characteristic (for example, high performance liquid chromatography as an analysis method for the component A), and the appropriate concentration is maintained while maintaining the appropriate concentration. Use it. For replenishment of component A at this time, it is preferable to use a high concentration aqueous solution of the compound.

次に、本発明の第２のエッチング剤について説明する。なお、上述した本発明の第１のエッチング剤と重複する内容については記載を省略し、以下の説明では、第１のエッチング剤と異なる内容についてのみ記載する。   Next, the second etching agent of the present invention will be described. In addition, description is abbreviate | omitted about the content which overlaps with the 1st etching agent of this invention mentioned above, and only the content different from a 1st etching agent is described in the following description.

本発明の第２のエッチング剤は、硫酸、過酸化水素及び水を含む銅のエッチング剤であって、環内にある異原子として窒素原子のみを有するアゾール類（以下、単に「アゾール成分」という）と、カルボシキル基を２以上有する多塩基酸又はその塩（以下、「Ｂ成分」という）とを含む。第２のエッチング剤では、アゾール成分が電解銅めっき層の腐食を防止する機能を有し、Ｂ成分が無電解銅めっき層のエッチングを促進させる機能を有していると考えられる。よって、ＥＲ１を速くすると共に、ＥＲ２を遅くすることができるため、ＥＲ１とＥＲ２との差を適切な範囲内にすることができる。これにより、セミアディティブ法において無電解銅めっき層を除去する際に、アンダーカットやパターン細りを防止できるため、配線パターンの寸法精度の低下を防止できる。   The second etching agent of the present invention is a copper etching agent containing sulfuric acid, hydrogen peroxide and water, and azoles having only nitrogen atoms as hetero atoms in the ring (hereinafter simply referred to as “azole component”). And a polybasic acid having two or more carboxy groups or a salt thereof (hereinafter referred to as “component B”). In the second etching agent, it is considered that the azole component has a function of preventing corrosion of the electrolytic copper plating layer, and the B component has a function of promoting etching of the electroless copper plating layer. Therefore, since ER1 can be increased and ER2 can be decreased, the difference between ER1 and ER2 can be within an appropriate range. Thereby, when removing the electroless copper plating layer in the semi-additive method, undercutting and pattern thinning can be prevented, so that reduction in the dimensional accuracy of the wiring pattern can be prevented.

アゾール成分としては、イミダゾール、アルキルイミダゾール類、ベンゾイミダゾール類、アルキルベンゾイミダゾール類などのイミダゾール及びその誘導体や、トリアゾール、アルキルトリアゾール類、ベンゾトリアゾール類、アルキルベンゾトリアゾール類などのトリアゾール及びその誘導体や、テトラゾール、アルキルテトラゾール類などのテトラゾール及びその誘導体などが例示できる。電解銅めっき層の腐食をより効果的に防止するには、トリアゾール及びその誘導体が好ましく、中でもベンゾトリアゾールが好ましい。   Examples of the azole component include imidazoles such as imidazole, alkyl imidazoles, benzimidazoles, and alkyl benzimidazoles, and derivatives thereof, triazoles such as triazole, alkyl triazoles, benzotriazoles, alkyl benzotriazoles, and derivatives thereof, and tetrazole. And tetrazole such as alkyltetrazole and derivatives thereof. In order to more effectively prevent corrosion of the electrolytic copper plating layer, triazole and derivatives thereof are preferable, and benzotriazole is particularly preferable.

上記エッチング剤中のアゾール成分の濃度は、0.001〜5重量％が好ましく、0.005〜3重量％がより好ましく、さらに好ましくは0.01〜2重量％の範囲である。上記範囲内であれば、無電解銅めっき層のエッチングを妨げない程度に、電解銅めっき層の腐食を防止する効果が発揮される。   The concentration of the azole component in the etching agent is preferably 0.001 to 5% by weight, more preferably 0.005 to 3% by weight, and still more preferably 0.01 to 2% by weight. If it is in the said range, the effect which prevents the corrosion of an electrolytic copper plating layer will be exhibited to such an extent that the etching of an electroless copper plating layer is not prevented.

Ｂ成分としては、蓚酸、マロン酸、コハク酸などの脂肪族ジカルボン酸又はその塩や、フタル酸、イソフタル酸、フェニルマロン酸などの芳香族ジカルボン酸又はその塩や、リンゴ酸、酒石酸、クエン酸、イソクエン酸などのカルボシキル基を２以上有するヒドロキシ酸又はその塩が挙げられる。無電解銅めっき層に対するエッチング促進効果の観点から、芳香族ジカルボン酸又はその塩が好ましく、中でもフェニルマロン酸又はその塩が好ましい。   B component includes aliphatic dicarboxylic acids such as succinic acid, malonic acid and succinic acid or salts thereof, aromatic dicarboxylic acids such as phthalic acid, isophthalic acid and phenylmalonic acid or salts thereof, malic acid, tartaric acid and citric acid. And hydroxy acids having two or more carboxy groups such as isocitric acid or salts thereof. From the viewpoint of the etching promoting effect on the electroless copper plating layer, an aromatic dicarboxylic acid or a salt thereof is preferable, and among them, phenylmalonic acid or a salt thereof is preferable.

上記エッチング剤中のＢ成分の濃度は、0.005〜10重量％が好ましく、0.01〜7重量％がより好ましく、さらに好ましくは0.05〜5重量％の範囲である。0.005重量％以上の場合は、無電解銅めっき層を速やかに除去できる。一方、10重量％以下の場合はコスト面で有利である。   The concentration of the B component in the etching agent is preferably 0.005 to 10% by weight, more preferably 0.01 to 7% by weight, and still more preferably 0.05 to 5% by weight. In the case of 0.005% by weight or more, the electroless copper plating layer can be quickly removed. On the other hand, when it is 10% by weight or less, it is advantageous in terms of cost.

アゾール成分とＢ成分の混合比率は、モル比で、アゾール成分１に対しＢ成分１〜５の範囲であることが好ましい。この範囲内であれば、電解銅めっき層の腐食抑制効果と無電解銅めっき層のエッチング促進効果のバランスがとれるため、アンダーカットやパターン細りを効果的に防止できる。   The mixing ratio of the azole component and the B component is preferably in the range of B components 1 to 5 relative to the azole component 1 in terms of molar ratio. Within this range, a balance between the corrosion inhibition effect of the electrolytic copper plating layer and the etching acceleration effect of the electroless copper plating layer can be balanced, and undercuts and pattern thinning can be effectively prevented.

次に、本発明に係るエッチング剤の実施例について比較例と併せて説明する。なお、本発明は下記の実施例に限定して解釈されるものではない。   Next, examples of the etching agent according to the present invention will be described together with comparative examples. In addition, this invention is limited to a following example and is not interpreted.

表１〜４に示す組成のエッチング剤を用いて、下記に示す測定方法により各項目について評価した。表１及び表２に示す実施例１〜２３は、上述した本発明の第１のエッチング剤の実施例であり、表３に示す実施例２４〜３３は、上述した本発明の第２のエッチング剤の実施例である。また、表４には、比較例を示した。各エッチング剤は、まず、硫酸及び過酸化水素をイオン交換水に溶解させた溶液に対し、金属銅を25g/Lの割合で溶解させた後、残りの成分を添加して調製した。なお、表１〜４に示す各成分の配合量は、銅イオンの重量を除いた各エッチング剤全重量に対する各成分の重量比率を示す。   Using the etching agents having the compositions shown in Tables 1 to 4, each item was evaluated by the measurement method shown below. Examples 1 to 23 shown in Table 1 and Table 2 are examples of the first etching agent of the present invention described above, and Examples 24 to 33 shown in Table 3 are the second etching of the present invention described above. It is an example of an agent. Table 4 shows a comparative example. Each etching agent was prepared by first dissolving copper metal at a rate of 25 g / L in a solution in which sulfuric acid and hydrogen peroxide were dissolved in ion-exchanged water, and then adding the remaining components. In addition, the compounding quantity of each component shown to Tables 1-4 shows the weight ratio of each component with respect to each etchant total weight except the weight of the copper ion.

（ＥＲ１の測定方法）
厚み1.6mmの松下電工社製銅張積層板（製品名：ガラスエポキシマルチ R-1766）をエッチング液（硫酸200g/L、過酸化水素50g/L、残部イオン交換水）に浸漬して、当該積層板の銅箔を完全に除去し、露出したガラスエポキシ基材の一面側に、奥野製薬工業社製無電解めっき薬液（製品名：ＯＰＣカッパーＨ）を用いて厚み約1.5μｍの無電解銅めっきを全面に施し、これを50mm×50mmに切断したものをテスト基板とした。この基板に対して、表１〜４に記載の各エッチング剤を用いて、30秒間のスプレー処理（スプレー圧：0.05MPa、温度：25℃）にてエッチングを行った。そして、処理前後のテスト基板の重量から、下式によりＥＲ１（μm/min）を算出した。
ＥＲ１（μm/min）＝（処理前の重量(g)−処理後の重量(g)）÷基板面積（ｍ2）÷銅の密度（g/cｍ3）÷処理時間（min） (Measurement method of ER1)
A 1.6 mm thick copper-clad laminate (product name: Glass Epoxy Multi R-1766) manufactured by Matsushita Electric Works, Ltd. is immersed in an etching solution (sulfuric acid 200 g / L, hydrogen peroxide 50 g / L, balance ion-exchanged water). The copper foil of the laminated plate is completely removed, and an electroless copper with a thickness of about 1.5 μm is used on one side of the exposed glass epoxy substrate using an electroless plating solution (product name: OPC Copper H) manufactured by Okuno Pharmaceutical Co., Ltd. A test substrate was prepared by plating the entire surface and cutting it to 50 mm × 50 mm. Etching was performed on this substrate by spraying for 30 seconds (spray pressure: 0.05 MPa, temperature: 25 ° C.) using the etching agents described in Tables 1 to 4. And ER1 (micrometer / min) was computed by the following formula from the weight of the test board | substrate before and behind a process.
ER1 (μm / min) = (weight before processing (g) −weight after processing (g)) ÷ substrate area (m 2 ) ÷ copper density (g / cm 3 ) ÷ processing time (min)

（ＥＲ２の測定方法）
50mm×50mmの松下電工社製銅張積層板（製品名：ガラスエポキシマルチ R-1766）の電解銅箔面上に、厚み約15μｍの電解銅めっきを全面に施したテスト基板を用意した。この基板に対して、表１〜４に記載の各エッチング剤を用いて、2分間のスプレー処理（スプレー圧：0.05MPa、温度：25℃）にてエッチングを行った。そして、処理前後のテスト基板の重量から、上記式と同様にＥＲ２（μm/min）を算出した。 (Measurement method of ER2)
A test substrate was prepared by applying electrolytic copper plating of about 15 μm in thickness on the electrolytic copper foil surface of a copper-clad laminate (product name: Glass Epoxy Multi R-1766) manufactured by Matsushita Electric Works, Ltd. of 50 mm × 50 mm. Etching was performed on this substrate by spray treatment (spray pressure: 0.05 MPa, temperature: 25 ° C.) for 2 minutes using the etching agents described in Tables 1 to 4. And ER2 (micrometer / min) was computed from the weight of the test board | substrate before and behind a process similarly to the said formula.

（ジャストエッチ時間の測定方法）
厚み1.6mmの松下電工社製銅張積層板（製品名：ガラスエポキシマルチ R-1766）をエッチング液（硫酸200g/L、過酸化水素50g/L、残部イオン交換水）に浸漬して、当該積層板の銅箔を完全に除去し、露出したガラスエポキシ基材の一面側に、奥野製薬工業社製無電解めっき薬液（製品名：ＯＰＣカッパーＨ）を用いて厚み約1μｍの無電解銅めっきを全面に施し、これを50mm×50mmに切断した基板を用意した。この基板の上に旭化成エレクトロニクス社製感光性ドライフィルム（製品名：サンフォート SPG152）によりメッキレジストパターンを施し、電解銅めっきにて厚み18μｍの配線パターン（ライン/スペース＝15μｍ/15μｍ）を形成し、３重量％の水酸化ナトリウム水溶液をスプレーすることにより上記メッキレジストパターンを剥離してテスト基板を作製した。この基板に対して、表１〜４に記載の各エッチング剤を用いて、スプレー処理（スプレー圧：0.05MPa、温度：25℃）によりエッチングを行い、無電解銅めっき層が除去されて下地の樹脂面が現れるまでの処理時間（ジャストエッチ時間）を計測した。なお、無電解銅めっき層が除去されたかどうかは、配線間の樹脂表面を金属顕微鏡によって500倍に拡大して観察することにより確認した。 (Measurement method of just etch time)
A 1.6 mm thick copper-clad laminate (product name: Glass Epoxy Multi R-1766) manufactured by Matsushita Electric Works, Ltd. is immersed in an etching solution (sulfuric acid 200 g / L, hydrogen peroxide 50 g / L, balance ion-exchanged water). The copper foil of the laminated plate is completely removed, and electroless copper plating with a thickness of about 1μm is applied to one side of the exposed glass epoxy substrate using an electroless plating chemical solution (product name: OPC Copper H) manufactured by Okuno Pharmaceutical Co., Ltd. Was applied to the entire surface, and a substrate cut into 50 mm × 50 mm was prepared. On this substrate, a plating resist pattern is applied with a photosensitive dry film (product name: Sanfort SPG152) manufactured by Asahi Kasei Electronics, and a wiring pattern (line / space = 15 μm / 15 μm) with a thickness of 18 μm is formed by electrolytic copper plating. The plating resist pattern was peeled off by spraying a 3% by weight sodium hydroxide aqueous solution to prepare a test substrate. Etching is performed on this substrate by spray treatment (spray pressure: 0.05 MPa, temperature: 25 ° C.) using the etching agents shown in Tables 1 to 4, and the electroless copper plating layer is removed to form a base. The processing time (just etch time) until the resin surface appeared was measured. Whether or not the electroless copper plating layer was removed was confirmed by observing the resin surface between the wirings with a metal microscope at a magnification of 500 times.

（パターン細り率の測定方法）
上記ジャストエッチ時間の測定方法で用いたものと同様のテスト基板を用意し、表１〜４に記載の各エッチング剤を用いて、ジャストエッチ時間に対し3倍の時間、スプレー処理（スプレー圧：0.05MPa、温度：25℃）によりエッチングを継続した。そして、エッチング処理前後の配線頂部の幅からパターン細り率を下式により求めた。なお、処理前後の配線頂部の幅は、いずれもレーザー顕微鏡（オリンパス製 OLS-1100）にて計10箇所測定し、その平均値とした。
パターン細り率（％）＝（処理前の配線幅−処理後の配線幅）÷処理前の配線幅×１００ (Measurement method of pattern thinning rate)
A test substrate similar to that used in the method for measuring the just etch time is prepared, and spray treatment (spray pressure: 3 times the just etch time) is performed using each of the etchants described in Tables 1 to 4. Etching was continued at 0.05 MPa (temperature: 25 ° C.). And the pattern thinning rate was calculated | required by the following Formula from the width | variety of the wiring top part before and behind an etching process. In addition, the width of the top part of the wiring before and after the treatment was measured with a laser microscope (OLS-1100 manufactured by Olympus) for a total of 10 points, and the average value was obtained.
Pattern thinning ratio (%) = (Wiring width before processing−Wiring width after processing) ÷ Wiring width before processing × 100

（アンダーカット長さＵＣＬの測定方法）
上記パターン細り率の測定方法により測定した後のテスト基板の一部を包埋樹脂にて包埋処理し、これを切断して断面研磨した。続いて、研磨断面を走査型電子顕微鏡（日本電子製 JSM-6390）にて観察し、配線パターン下部のアンダーカット長さＵＣＬ（図１参照）を計10箇所測定し、その平均値を算出した。 (Measurement method of undercut length UCL)
A part of the test substrate after being measured by the pattern thinning ratio measuring method was embedded with an embedding resin, and this was cut and polished in cross section. Subsequently, the polished cross section was observed with a scanning electron microscope (JSM-6390 manufactured by JEOL), and a total of 10 undercut lengths UCL (see FIG. 1) under the wiring pattern were measured, and the average value was calculated. .

Figure 0005273710
Figure 0005273710

Figure 0005273710
Figure 0005273710

Figure 0005273710
Figure 0005273710

Figure 0005273710
Figure 0005273710

表１〜４に示すように、本発明の実施例１〜３３は、いずれも比較例１〜５よりパターン細りを抑えることができた。また、アンダーカット長さＵＣＬについても、例えば比較例２と実施例３との比較、比較例３と実施例２５との比較、比較例４と実施例３０との比較、比較例５と実施例２５との比較などからも分かるように、本発明の実施例は、比較例に比べ、アンダーカット長さＵＣＬを抑えることができた。   As shown in Tables 1 to 4, Examples 1-33 of the present invention were able to suppress pattern thinning more than Comparative Examples 1-5. Further, for the undercut length UCL, for example, comparison between Comparative Example 2 and Example 3, comparison between Comparative Example 3 and Example 25, comparison between Comparative Example 4 and Example 30, Comparative Example 5 and Example As can be seen from the comparison with 25, the example of the present invention was able to suppress the undercut length UCL compared to the comparative example.

なかでも、ポリアリルアミン系カチオン性ポリマーを配合した実施例１５〜２１は、特にパターン細りを抑制できた。なお、構成単位中にアリルアミン骨格を含まないカチオン性ポリマーを添加した実施例２２及び２３では、パターン細りについては実施例４と同等であった。   Especially, Examples 15-21 which mix | blended the polyallylamine type cationic polymer were able to especially suppress pattern thinning. In Examples 22 and 23 in which a cationic polymer not containing an allylamine skeleton was added in the structural unit, pattern thinning was the same as in Example 4.

電気絶縁層上に配線が複数形成されたプリント配線板の概略断面図である。It is a schematic sectional drawing of the printed wiring board by which multiple wiring was formed on the electrical insulating layer.

符号の説明Explanation of symbols

１ 電気絶縁層
２ 配線
３ 無電解銅めっき層
４ 電解銅めっき層 1 Electrical insulation layer 2 Wiring 3 Electroless copper plating layer 4 Electrolytic copper plating layer

Claims (3)

硫酸、過酸化水素及び水を含む銅のエッチング剤であって、
カルボキシル基及びヒドロキシル基の少なくとも一方を分子中に２以上有するベンゾトリアゾール誘導体を含むことを特徴とするエッチング剤。 A copper etchant containing sulfuric acid, hydrogen peroxide and water,
An etching agent comprising a benzotriazole derivative having at least one of a carboxyl group and a hydroxyl group in a molecule. 前記ベンゾトリアゾール誘導体の濃度が、０．０００１〜１０重量％である請求項１に記載のエッチング剤。   The etching agent according to claim 1, wherein the concentration of the benzotriazole derivative is 0.0001 to 10% by weight. ポリアリルアミン系カチオン性ポリマーを更に含む請求項１又は２に記載のエッチング剤。   The etching agent according to claim 1 or 2, further comprising a polyallylamine-based cationic polymer.
JP2008190032A 2007-11-27 2008-07-23 Etching agent Active JP5273710B2 (en)