JP5169093B2 - Anti-counterfeit laminate, anti-counterfeit transfer foil, anti-counterfeit seal, anti-counterfeit medium, and methods for producing these - Google Patents
Anti-counterfeit laminate, anti-counterfeit transfer foil, anti-counterfeit seal, anti-counterfeit medium, and methods for producing these Download PDFInfo
- Publication number
- JP5169093B2 JP5169093B2 JP2007236334A JP2007236334A JP5169093B2 JP 5169093 B2 JP5169093 B2 JP 5169093B2 JP 2007236334 A JP2007236334 A JP 2007236334A JP 2007236334 A JP2007236334 A JP 2007236334A JP 5169093 B2 JP5169093 B2 JP 5169093B2
- Authority
- JP
- Japan
- Prior art keywords
- counterfeit
- relief structure
- relief
- layer
- laminate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、偽造、改ざん、貼り替え、又は、秘密にされるべき情報の盗み読み、等の不正の防止対策や、万一そのような不正が心配されても不正の有無の判別を容易とする対策、これらの対策を必要とされる技術分野に関する。より詳しくは、例えば、商品券やクレジットカード等の有価証券類の偽造防止対策とか、ブランド品や高級品等の一般に高価なものへ適用希望が多い真正品であることの証明の為の偽造防止対策、これらのニーズに好適な技術、また、デザインによっては装飾性にも優れた視覚効果を得られる技術であって、レリーフ構造を含む光学素子を利用した、視認性の高い、偽造防止積層体、偽造防止転写箔、偽造防止シール、偽造防止媒体、及びこれらの製造方法並びに偽造防止積層体の製造装置に関する。 The present invention facilitates fraud prevention measures such as counterfeiting, falsification, replacement, or theft of information that should be kept secret, and the determination of the presence or absence of fraud even if such fraud is a concern. Measures, and technical fields that require these measures. More specifically, for example, forgery prevention measures to prevent counterfeiting of securities such as gift certificates and credit cards, and to prove that it is a genuine product that is often desired to be applied to generally expensive items such as branded goods and luxury goods. Countermeasures, technology suitable for these needs, and technology that can achieve a visual effect with excellent decorativeness depending on the design, and is a highly visible anti-counterfeit laminate using an optical element including a relief structure The present invention relates to an anti-counterfeit transfer foil, an anti-counterfeit seal, an anti-counterfeit medium, a manufacturing method thereof, and an apparatus for manufacturing an anti-counterfeit laminate.
近年、電子写真技術を利用した複写機が普及し、これを利用して誰でも簡単に紙などに印刷された文字や画像を複写することができるようになった。特に、最近のカラーデジタル複写機によれば、原稿か複写物か見分けが極めて困難な複写物でさえも容易に作成することができるようになった。 In recent years, copying machines using electrophotographic technology have become widespread, and anyone can easily copy characters and images printed on paper using this. In particular, with recent color digital copying machines, it has become possible to easily create even a copy that is extremely difficult to distinguish between a manuscript and a copy.
一般的なカラーデジタル複写機の原理は、原稿に光を照射し、反射光をＣＣＤラインセンサで検知する。ＣＣＤラインセンサでは、反射光の強度に応じたデジタル信号を生成し、複写機内のメモリに送信する。この読み取り過程をレッド（Ｒ）、グリーン（Ｇ）、ブルー（Ｂ）の３色について行い、それぞれの場合のデジタル信号をメモリに格納する。次に格納されたデジタル信号に基づいて、レーザ光を感光体ドラムの表面に照射し、イエロー（Ｙ）、マゼンタ（Ｍ）、シアン（Ｃ）、ブラック（Ｂｋ）のトナーを感光体ドラムの上に順次静電吸着し、これらのトナーを順次紙などのシート上に転写して定着させる。これにより、カラーの画像が形成された精巧な複写物を得ることができる。 The principle of a general color digital copying machine is to irradiate a document with light and detect reflected light with a CCD line sensor. In the CCD line sensor, a digital signal corresponding to the intensity of the reflected light is generated and transmitted to a memory in the copying machine. This reading process is performed for three colors of red (R), green (G), and blue (B), and the digital signal in each case is stored in the memory. Next, based on the stored digital signal, the surface of the photosensitive drum is irradiated with laser light, and yellow (Y), magenta (M), cyan (C), and black (Bk) toners are applied to the photosensitive drum. The toner is sequentially electrostatically adsorbed, and these toners are sequentially transferred and fixed on a sheet such as paper. Thereby, an elaborate copy on which a color image is formed can be obtained.
かかるカラー複写は便利である反面、株券、債券、約束手形、小切手などの有価証券や、入場券、搭乗券などの印刷物などが容易に偽造されるという問題が増加している。このため、容易に複写できないように印刷物に複製防止対策を施す提案が種々なされている。 While such color copying is convenient, there is an increasing problem that securities such as stock certificates, bonds, promissory notes and checks, and printed materials such as admission tickets and boarding passes are easily forged. For this reason, various proposals have been made to take anti-duplication measures on printed matter so that they cannot be easily copied.
例えば、カラー複写による複写物の色が原稿の色と異なるようにする技術が提案されている。その例として原稿とされうる有価証券などに非常に淡い色で着色すると、複写物では淡い色の部分が正確に再現できないもの、また、原稿に大きさの異なる網点を形成しておくと複写しても小さい網点の再現性が悪化するもの、さらにカラー複写機のトナーにない色である緑、紫、橙、金、銀等を印刷することで複写物の色の再現性が悪化するもの、また、人間の視認度が低い領域、例えば３８０ｎｍ〜４５０ｎｍおよび６５０〜７８０ｎｍあたりの波長域に特徴をもたせた２種類のインキを用いることで見た目には同色であるが、カラー複写機での複写物は異なる色に再現するものなどがある。 For example, a technique has been proposed in which the color of a color copy is different from the color of an original. For example, if a securities that can be used as a manuscript is colored with a very light color, the copied material cannot reproduce the light color part accurately, and if the manuscript is formed with halftone dots of different sizes, However, the reproducibility of small halftone dots deteriorates, and the color reproducibility of copies is deteriorated by printing colors such as green, purple, orange, gold, and silver that are not found in color copier toners. In addition, it is the same color by using two types of inks that are characterized by regions with low human visibility, for example, wavelength regions around 380 nm to 450 nm and 650 nm to 780 nm. Some reproductions are reproduced in different colors.
しかし、カラー複写機では、３色に分解されてメモリに格納されたデジタルデータを変更することによって、出力する色を補正することが可能である。また、カラー複写機と同様の原理を利用してカラースキャナーで読み込んだデジタルデータをコンピュータで補正し、カラープリンタまたはカラー複写機で出力するようなデジタルプレスが普及しつつある。従って、現在多少の手間をかければ、原稿の色を精巧に再現することが可能であり、上記のような技術では偽造を完全に防止することは困難である。 However, in a color copying machine, it is possible to correct the color to be output by changing the digital data separated into three colors and stored in the memory. In addition, a digital press that uses a principle similar to that of a color copying machine to correct digital data read by a color scanner by a computer and outputs the digital data by a color printer or a color copying machine is becoming widespread. Accordingly, it is possible to precisely reproduce the color of the original with a little effort at present, and it is difficult to completely prevent forgery with the above-described technique.
また、例えばカラー複写機では再現不可能な特殊部分を有価証券などに設けておく技術も提案されている。このうち、ホログラム箔などのＯＶＤ（Ｏｐｔｉｃａｌ Ｖａｒｉａｂｌｅ Ｄｅｖｉｃｅ）箔（特許文献１、２参照）を有価証券などの表面上に設ける技術はすでに実用化されている。これによれば、ホログラムの銀面の光が鏡面反射するため、ＣＣＤラインセンサに反射光が入射せず、原稿で銀面だった部分が複写物では黒色に再現されるもの、あるいは、屈折率の異なるセラミックを適当な膜厚を持つ複数層に積層すると、見る角度によって色が変化する特殊な光学薄膜が形成され（特許文献３参照）、かかる性質は、複写物では得ることができないので、容易に真偽判定が可能であるもの、さらにまた、この方法で形成された薄膜を細かく砕き、破片をインキに混入して印刷を行う方法も提案されている。 In addition, for example, a technique has been proposed in which a special part that cannot be reproduced by a color copying machine is provided in securities. Among these, a technique of providing an OVD (Optical Variable Device) foil (refer to Patent Documents 1 and 2) such as a hologram foil on the surface of securities or the like has already been put into practical use. According to this, since the light on the silver surface of the hologram is specularly reflected, the reflected light is not incident on the CCD line sensor, and the portion that was the silver surface in the original is reproduced in black on the copy, or the refractive index. When the ceramics with different thicknesses are laminated in a plurality of layers having an appropriate film thickness, a special optical thin film whose color changes depending on the viewing angle is formed (see Patent Document 3), and such a property cannot be obtained with a copy. Proposals have also been made of a method that can easily determine authenticity, and a method in which a thin film formed by this method is finely crushed and fragments are mixed with ink for printing.
しかしながら、ホログラムはエンボス技術が発達したためレリーフ型の回折光を用いた反射層の形成が以前より低難易度化していること、及び多層薄膜フィルムが一般の包装用フィルムとして販売され始めたことなどから、偽造防止効果が低化してきた。 However, because of the development of embossing technology for holograms, the formation of reflective layers using relief-type diffracted light has become more difficult than before, and multilayer thin film has begun to be sold as a general packaging film. The forgery prevention effect has been reduced.
この為、近年のホログラムでは、回折光を発生させる領域を部分的に備え、例えば、ホログラムによるのマイクロ文字やマイクロパターンを表現することで、偽造防止効果を向上させる方法が提案されている。（特許文献４参照）
このような、回折光を発生させる領域を部分的に備えるホログラムは、一般的に、レリーフ型の回折構造に対し、パターン状の金属等の反射層を設ける方法で製造される。金属等の反射層のパターン化は、下記の４種の方法が一般的である。（特許文献５参照）
１）水洗インキを基材上にネガパターンで印刷しておき、その上から蒸着やスパッタリングを用いて全面に金属反射層を形成し、印刷されてある水洗インキを水で洗い流すと同時にその上の金属反射層を取り除くことによりパターンを形成する水洗シーライト加工。
For this reason, in recent holograms, a method has been proposed in which a region for generating diffracted light is partially provided and, for example, micro characters and micro patterns are expressed by the hologram to improve the forgery prevention effect. (See Patent Document 4)
Such a hologram partially provided with a region for generating diffracted light is generally manufactured by a method in which a reflective layer such as a patterned metal is provided on a relief type diffractive structure. The following four methods are generally used for patterning a reflective layer of metal or the like. (See Patent Document 5)
1) A washing ink is printed on the substrate in a negative pattern, a metal reflective layer is formed on the entire surface by vapor deposition or sputtering, and the printed washing ink is washed away with water and at the same time. Washed sea light processing to form a pattern by removing the metal reflective layer.
２）金属反射層上にマスク材をポジパターンで印刷し、マスク剤で印刷されていない部分を腐食剤で腐食させることによりパターンを形成するエッチング加工。 2) An etching process in which a mask material is printed as a positive pattern on a metal reflective layer, and a pattern is formed by corroding a portion not printed with a mask agent with a corrosive agent.
３）金属反射層の除去したい部分に強いレーザを当てて金属等の反射層を選択的に破壊することによりパターンを形成するレーザ加工。 3) Laser processing for forming a pattern by selectively destroying the reflective layer of metal or the like by applying a strong laser to the portion of the metal reflective layer to be removed.
４）金属反射層上にフォトレジスト剤を全面に印刷し、ポジパターンでフォトレジストした後、ネガパターン部のフォトレジスト剤を溶解除去し、同時に、又は別工程で金属反射層を腐食させることによりパターンを形成するフォトレジスト加工。 4) By printing a photoresist agent on the entire surface of the metal reflection layer and photoresist with a positive pattern, dissolving and removing the photoresist agent in the negative pattern portion, and corroding the metal reflection layer at the same time or in another process. Photoresist processing to form a pattern.
しかしながら、上記のいずれの方法においても、回折光によるホログラムの絵柄パターンと、反射層のパターンの位置合わせが必要となる為、良品率の低下を招く。また、僅かではあるものの、水洗インキ、マスク材、レーザー加工、フォトレジスト加工時の位置ズレ（見当ズレ）が生じることから、高品質で、偽造防止効果の高いホログラムを作ることは困難であった。 However, in any of the above-described methods, it is necessary to align the pattern pattern of the hologram by the diffracted light and the pattern of the reflective layer, which leads to a decrease in the yield rate. In addition, although it is slight, positional deviation (registration deviation) at the time of washing ink, mask material, laser processing, and photoresist processing occurs, so it was difficult to make a high-quality hologram with high anti-counterfeiting effect. .
回折光によるホログラムの絵柄パターンに対し、金属反射層のパターンを位置精度良く設ける方法としては、電子制御により左右に稼働するステージと、該ステージと連動する描写機械を使用する方法が提案されている。（特許文献６参照）この方法に依れば、割と見当精度のよい製品が安定して製造可能であることが推測され、文献に記載の通り、「少量生産に特に大きなメリットがある」ことは考えられるが、生産性が低く、大量生産には向かない。また、製造工程は前記の４方法と比べ基本的な発想は変わらず、煩雑なままである。また、同文献にて、スプレーによるエッチング剤、エッチングレジスト、又は洗い流しマスク描画の製造方法が提案されているが、単純に平坦なフィルム上にスプレーするだけでは、スプレーインキのハネが生じることや、スプレーインキの塗布量が多くなった
際に液だれ、滲みが生じる。
As a method of providing a metal reflection layer pattern with high positional accuracy with respect to a hologram pattern pattern by diffracted light, a method using a stage that moves to the left and right by electronic control and a drawing machine that is linked to the stage has been proposed. . (Refer to Patent Document 6) According to this method, it is presumed that a product with relatively high registration accuracy can be stably manufactured, and as described in the document, “particularly significant advantage is in small-volume production”. However, productivity is low and it is not suitable for mass production. In addition, the basic concept of the manufacturing process is not changed as compared with the above four methods, and it remains complicated. In addition, in the same document, a manufacturing method of an etching agent by etching, an etching resist, or a washing mask drawing is proposed, but simply spraying on a flat film may cause splash of ink, When the amount of spray ink applied increases, dripping and bleeding occur.
下記に公知文献を記す。
本発明は、上記技術的背景を考慮してなされたものであって、レリーフ構造とレリーフ効果層を設計図柄通りのパターンで形成し、そのレリーフ構造とレリーフ効果層を精度良く配置した、レリーフ構造を含む光学素子からなる、安価で生産性が高く、装飾性にも優れた視覚効果を得られる、高品質の、偽造防止積層体、偽造防止転写箔、偽造防止シール、偽造防止媒体、及びこれらの製造方法並びにその製造装置を提供することを課題とする。 The present invention has been made in consideration of the above technical background, wherein a relief structure and a relief effect layer are formed in a pattern as designed, and the relief structure and the relief effect layer are accurately arranged. High-quality, anti-counterfeit laminate, anti-counterfeit transfer foil, anti-counterfeit seal, anti-counterfeit medium, and the like, which are inexpensive, highly productive, and have a decorative effect. An object of the present invention is to provide a manufacturing method and a manufacturing apparatus thereof.
上記課題を達成するための解決手段として、
まず、請求項１に係る発明は、少なくとも、レリーフ構造形成層（イ）と、
前記レリーフ構造形成層（イ）の片側に、部分的に設けられたレリーフ構造部（ロ）と、前記レリーフ構造部（ロ）と重ならないように、同一面上に、部分的に設けられた土手部（ハ）と、
前記土手部（ハ）に囲われ、レリーフ構造部（ロ）を含むレリーフ構造囲われ部（ニ）と、
前記レリーフ構造囲われ部（ニ）のみを覆うように配置された光学薄膜からなり、前記レリーフ構造形成層（イ）を透過した光の少なくとも一部を反射させるレリーフ効果層（ホ）と、
を順次積層して具備してなることを特徴とする偽造防止積層体である。
As a solution to achieve the above problems,
First, the invention according to claim 1 includes at least a relief structure forming layer (a),
A relief structure part (b) provided partially on one side of the relief structure formation layer (a) and a part provided on the same surface so as not to overlap the relief structure part (b) Bank part (C),
A relief structure surrounded part (d) surrounded by the bank part (c) and including a relief structure part (b);
A relief effect layer (e) that consists of an optical thin film arranged so as to cover only the relief structure surrounded part (d), and reflects at least part of the light transmitted through the relief structure forming layer (a);
Is a forgery-preventing laminate comprising the following layers.
請求項２に係る発明は、少なくとも、前記レリーフ構造囲われ部（ニ）上のレリーフ効果層（ホ）を覆うように配置されたエッチングマスク層（ヘ）を具備してなることを特徴とする請求項１に記載の偽造防止積層体である。 The invention according to claim 2 comprises at least an etching mask layer (f) disposed so as to cover the relief effect layer (e) on the relief structure surrounding part (d). It is a forgery prevention laminated body of Claim 1.
請求項３に係る発明は、前記レリーフ構造部（ロ）のレリーフ構造が、レリーフ型光学素子、もしくは、前記レリーフ構造部（ロ）のレリーフ構造とレリーフ効果層（ホ）との組み合わせにより光学効果をもたらすレリーフ型光学素子であることを特徴とする請求項１または２に記載の偽造防止積層体である。 In the invention according to claim 3, the relief structure of the relief structure part (b) is an optical effect by a relief type optical element or a combination of the relief structure of the relief structure part (b) and a relief effect layer (e). The anti-counterfeit laminate according to claim 1 or 2, wherein the anti-counterfeit laminate is a relief-type optical element.
請求項４に係る発明は、少なくとも、前記レリーフ構造囲われ部（ニ）が、前記土手部（ハ）により１ｍｍ2以下の任意のパターンにブロック化されているレリーフ構造囲われブロック部（ト）を具備してなることを特徴とする請求項１ないし３のいずれか１項に記載の偽造防止積層体である。 In the invention according to claim 4, at least the relief structure surrounding portion (d) is blocked into an arbitrary pattern of 1 mm 2 or less by the bank portion (c). The anti-counterfeit laminate according to any one of claims 1 to 3, wherein the forgery-preventing laminate is provided.
請求項５に係る発明は、シート状支持体上に、請求項１ないし４のいずれか１項に記載の偽造防止積層体を、転写の際に前記支持体から剥離し被転写体に移行可能とするように積層配置し、該偽造防止積層体を覆うようにして、少なくとも、前記支持体から最も遠い位置に接着層を積層してなることを特徴とする偽造防止転写箔である。 The invention according to claim 5 is capable of transferring the anti-counterfeit laminate according to any one of claims 1 to 4 from the support during transfer to a sheet-like support on the sheet-like support. The anti-counterfeit transfer foil is characterized in that an adhesive layer is laminated at least at a position farthest from the support so as to be laminated and cover the anti-counterfeit laminate.
請求項６に係る発明は、シート状支持体上に、少なくとも、請求項１ないし４のいずれか１項に記載の偽造防止積層体を配置し、該偽造防止積層体を覆うようにして、少なくとも、前記支持体から最も遠い位置に、熱又は圧力によって接着性を呈する接着層を積層してなることを特徴とする偽造防止シールである。 The invention according to claim 6 is arranged such that at least the anti-counterfeit laminate according to any one of claims 1 to 4 is disposed on the sheet-like support and covers the anti-counterfeit laminate. The anti-counterfeit seal is formed by laminating an adhesive layer exhibiting adhesiveness by heat or pressure at a position farthest from the support.
請求項７に係る発明は、請求項１ないし４に記載のいずれか１項に記載の偽造防止積層体それ自体、または、シート状支持体上に、請求項１ないし６のいずれか１項に記載の、偽造防止積層体、偽造防止転写箔、偽造防止シールの少なくとも１つ以上を積層してなることを特徴とする偽造防止媒体である。 The invention according to claim 7 is the anti-counterfeit laminate according to any one of claims 1 to 4 or the sheet-like support body according to any one of claims 1 to 6. An anti-counterfeit medium characterized by laminating at least one of the forgery-preventing laminate, the anti-counterfeit transfer foil, and the anti-counterfeit seal.
請求項８に係る発明は、少なくとも、（イ）レリーフ構造形成層の片側に、（ロ）レリーフ構造形成部、（ハ）土手部を成形した後、前記土手部（ハ）を利用し、該土手部に囲われたレリーフ構造囲われ部（ニ）にのみ、前記（イ）レリーフ構造形成層を透過した光の少なくとも一部を反射させる材料からなるレリーフ効果層（ホ）を液滴法により設けるか、もしくは、少なくとも、前記土手部に囲われたレリーフ構造囲われ部（ニ）にのみ、液滴法によりエッチングマスク層（へ）を形成した後、エッチング処理により、レリーフ構造囲われ部（ニ）以外の部分上に配置された、レリーフ効果層（ホ）を除去することを特徴とする請求項１に記載の偽造防止積層体の製造方法である。 The invention according to claim 8, at least, using (i) on one side of the relief structure-forming layer, (ii) a relief structure-forming portion, after forming the (c) bank portion, the bank portion (c), the The relief effect layer (e) made of a material that reflects at least part of the light transmitted through the relief structure forming layer (e) is applied to the relief structure surrounded by the bank part (d) only by the droplet method. I Ri設 Keru or, or, at least, the relief structure enclosed portion surrounded the bank portion (d) only, after forming an etching mask layer (to) by the droplet method, by etching, the relief structure circumference The method for producing an anti-counterfeit laminate according to claim 1, wherein the relief effect layer (e) disposed on a portion other than the crack portion (d) is removed.
請求項９に係る発明は、シート状の支持体上に、請求項１ないし４のいずれか１項に記載の偽造防止積層体を、転写の際に前記支持体から剥離し被転写体に移行可能とするように積層配置し、該偽造防止積層体を覆うようにして、少なくとも、前記支持体から最も遠い位置に接着層を積層することを特徴とする偽造防止転写箔の製造方法である。 According to a ninth aspect of the present invention, the anti-counterfeit laminate according to any one of the first to fourth aspects is peeled off from the support during transfer and transferred to a transfer target on a sheet-like support. It is a method for producing a forgery-preventing transfer foil, characterized in that the anti-counterfeit laminate is disposed so as to be capable of being covered and an adhesive layer is laminated at least at a position furthest from the support.
請求項１０に係る発明は、シート状支持体上に、少なくとも、請求項１ないし４のいずれか１項に記載の偽造防止積層体を配置し、該偽造防止積層体を覆うようにして、少なくとも、前記支持体から最も遠い位置に、熱又は圧力によって接着性を呈する接着層を積層することを特徴とする偽造防止シールの製造方法である。 According to a tenth aspect of the present invention, at least the anti-counterfeit laminate according to any one of the first to fourth aspects is disposed on the sheet-like support, and at least the anti-counterfeit laminate is covered. A method for producing a forgery-preventing seal, comprising: laminating an adhesive layer exhibiting adhesiveness by heat or pressure at a position farthest from the support.
請求項１１に係る発明は、シート状支持体上に、請求項１ないし６のいずれか１項に記載の偽造防止積層体、偽造防止転写箔、偽造防止シールの少なくとも１つ以上を積層することを特徴とする偽造防止媒体の製造方法である。 According to an eleventh aspect of the present invention, at least one of the anti-counterfeit laminate, the anti-counterfeit transfer foil, and the anti-counterfeit seal according to any one of the first to sixth aspects is laminated on a sheet-like support. This is a method for manufacturing a forgery prevention medium.
本発明によれば、レリーフ構造とレリーフ効果層を設計図柄通りのパターンで形成し、そのレリーフ構造とレリーフ効果層を精度良く配置した、レリーフ構造を含む光学素子からなる、安価で生産性が高く、装飾性にも優れた視覚効果を得られる、高品質の、偽造防止積層体、偽造防止転写箔、偽造防止シール、偽造防止媒体、及びこれらの製造方法並びにその製造装置を提供することが出来る。 According to the present invention, the relief structure and the relief effect layer are formed in a pattern as designed, and the relief structure and the relief effect layer are arranged with high precision. The optical element including the relief structure is inexpensive and highly productive. It is possible to provide a high-quality, anti-counterfeit laminate, anti-counterfeit transfer foil, anti-counterfeit seal, anti-counterfeit medium, and a production method thereof and an apparatus for producing the same, which can obtain a visual effect excellent in decorativeness. .
以下、本発明に係る、偽造防止積層体、偽造防止転写箔、偽造防止シール、又は、偽造防止媒体の実施形態を、図面を参照して詳細に説明する。図１は、本発明に係る偽造防止積層体の断面図である。この偽造防止積層体（１）は少なくとも、レリーフ構造形成層（２）の片面に、レリーフ構造部（３）、土手部（４）が設けられており、土手部に囲われ、レリーフ構造部分を含む、レリーフ構造囲われ部（５）という領域が存在する。前記、レリーフ構造囲われ部分のみを覆うように配置されており、レリーフの凹凸に密着して設けられた、レリーフ効果層（６）を順次積層した構造を有する。 Hereinafter, embodiments of the anti-counterfeit laminate, the anti-counterfeit transfer foil, the anti-counterfeit seal, or the anti-counterfeit medium according to the present invention will be described in detail with reference to the drawings. FIG. 1 is a cross-sectional view of a forgery-preventing laminate according to the present invention. The anti-counterfeit laminate (1) is provided with a relief structure part (3) and a bank part (4) on at least one side of the relief structure forming layer (2). The relief structure part is surrounded by the bank part. There is an area called the relief structure enclosing part (5). The relief structure is disposed so as to cover only the portion surrounded by the relief structure, and has a structure in which relief effect layers (6) provided in close contact with the relief irregularities are sequentially laminated.
図２は、本発明に係る第２の偽造防止積層体の断面図である。この偽造防止積層体（７）は少なくとも、レリーフ構造形成層（８）の片面に、レリーフ構造部（９）、土手部（１０）が設けられており、土手部に囲われ、レリーフ構造部分を含む、レリーフ構造囲われ部（１１）という領域が存在する。前記、レリーフ構造囲われ部分のみを覆うように配置された、レリーフ効果層（１２）、及び、エッチングマスク層（１３）を順次積層した構造を有する。 FIG. 2 is a cross-sectional view of a second anti-counterfeit laminate according to the present invention. The anti-counterfeit laminate (7) is provided with a relief structure part (9) and a bank part (10) on at least one side of the relief structure forming layer (8). The relief structure part is surrounded by the bank part. A region called the relief structure surrounding portion (11) is present. The relief structure has a structure in which a relief effect layer (12) and an etching mask layer (13) are sequentially laminated so as to cover only the portion surrounded by the relief structure.
図３は、本発明に係る第３の偽造防止積層体（１４）であって少なくとも、土手部（１５）により、１ｍｍ2以下の任意のパターンにブロック化されている、レリーフ構造囲われブロック部（１６）という領域を有する。この偽造防止積層体を、レリーフ構造部分側から見た正面図である。 FIG. 3 shows a third structure for preventing forgery (14) according to the present invention, wherein at least a bank portion (15) is formed into an arbitrary pattern of 1 mm 2 or less, and the block portion is surrounded by a relief structure. (16). It is the front view which looked at this forgery prevention laminated body from the relief structure part side.
図４は、図３の破線（１７）部分の断面図である。この偽造防止積層体（１４）は少なくとも、レリーフ構造形成層（１８）の片面に、レリーフ構造部（１９）、土手部（２０）が設けられている。前記の土手部により、１ｍｍ2以下の任意のパターンにブロック化されている、レリーフ構造囲われブロック部（２１）という領域が存在する。そして、前記、レリーフ構造囲われブロック部（２１）のみを覆うように配置された、レリーフ効果層（２２）を順次積層した構造を有する。 4 is a cross-sectional view taken along a broken line (17) in FIG. In this anti-counterfeit laminate (14), a relief structure part (19) and a bank part (20) are provided at least on one side of the relief structure forming layer (18). There is an area called a relief-structure-enclosed block portion (21) that is blocked into an arbitrary pattern of 1 mm 2 or less by the bank portion. And it has the structure which laminated | stacked the relief effect layer (22) sequentially arrange | positioned so that only the said relief structure surrounding block part (21) might be covered.
図５は、本発明に係る偽造防止転写箔の断面図である。この偽造防止転写箔（２３）は少なくとも、支持体（２４）、偽造防止積層体（２５）、接着剤（２６）を順次積層した構造を有しており、偽造防止積層体（２５）と接着剤（２６）によって構成される転写層（２７）は、支持体（２４）より剥離し被転写体に移行可能である。図６は、本発明に係る偽造防止シールの断面図である。この偽造防止シール（２８）は少なくとも、支持体（２９）、偽造防止積層体（３０）、接着剤（３１）を順次積層した構造を有する。図７は、本発明に係る第２の偽造防止媒体の断面図である。この偽造防止媒体（３２）は、支持体（３３）上に、積層体、又は転写箔、又はシール（３４）の少なくとも１つ以上を貼付し、積層した構造を有する。 FIG. 5 is a cross-sectional view of the forgery-preventing transfer foil according to the present invention. This anti-counterfeit transfer foil (23) has a structure in which at least a support (24), an anti-counterfeit laminate (25), and an adhesive (26) are sequentially laminated, and is bonded to the anti-counterfeit laminate (25). The transfer layer (27) composed of the agent (26) can be peeled off from the support (24) and transferred to the transfer target. FIG. 6 is a cross-sectional view of the forgery prevention seal according to the present invention. The anti-counterfeit seal (28) has a structure in which at least a support (29), an anti-counterfeit laminate (30), and an adhesive (31) are sequentially laminated. FIG. 7 is a cross-sectional view of a second anti-counterfeit medium according to the present invention. This anti-counterfeit medium (32) has a structure in which at least one of a laminate, a transfer foil, or a seal (34) is stuck on a support (33) and laminated.
以下、本発明の転写シートを構成する各部材についてより詳細に説明する。 Hereafter, each member which comprises the transfer sheet of this invention is demonstrated in detail.
本発明の偽造防止積層体に使用される、レリーフ構造形成層（２）、（８）、（１８）は、その表面にレリーフ構造と、土手部（４）、（１０）、（２０）が形成される。これらの形状は、プレス成形法、又はフォトポリマー法等の公知の加工法によって形成される。加工方法によって、レリーフ構造形成層としての材料の要求特性が異なるため、以下に詳細を記す。 The relief structure forming layers (2), (8) and (18) used in the forgery-preventing laminate of the present invention have a relief structure and a bank (4), (10) and (20) on the surface. It is formed. These shapes are formed by a known processing method such as a press molding method or a photopolymer method. Since the required characteristics of the material as the relief structure forming layer differ depending on the processing method, details will be described below.
プレス方法による成形では、その表面にプレス版（レリーフ型）にて凹凸面を成形できるという性能が要求される。レリーフ構造形成層（２）、（８）、（１８）の主材料は、熱可塑性樹脂、熱硬化性樹脂、紫外線または電子線硬化性樹脂のいずれでもよい。たとえばアクリル系樹脂、エポキシ系樹脂、セルロース系樹脂、ビニル系樹脂などの熱可塑性樹脂や、反応性水酸基を有するアクリルポリオールやポリエステルポリオールなどにポリイ
ソシアネートを架橋剤として添加して架橋したウレタン樹脂や、メラミン系樹脂、フェノール系樹脂などの熱硬化樹脂や、エポキシ（メタ）アクリレート、ウレタン（メタ）アクリレートなどの紫外線または電子線硬化樹脂などが挙げられる。これらは、単独で用いてもよいし、２種以上を混合して用いてもよい。また、これら以外のものであっても、その表面に凹凸面を形成できれば適宜使用することができる。プレス成形の場合、平板状のホットコールドプレス法とロールエンボス法が挙げられる。これらの方法では、レリーフ構造形成層の樹脂を融点以上に加熱溶融した後、成型したいレリーフ形状、及び土手形状のネガパターンを有するレリーフ型を押し当てて形状を転写する。その後、レリーフ構造形成層の樹脂をガラス転移温度以下まで下げて樹脂を固化し、レリーフ型から離型する事で、所望のレリーフ形状、及び土手形状を得ることができる。なお、熱硬化樹脂、紫外線硬化樹脂、電子線硬化樹脂を使用する場合、レリーフ形状、及び土手形状を形成し、レリーフ型から離型した後に、熱、紫外線、電子線により樹脂を硬化させることで、耐性の良いレリーフ形状を有する塗膜が得ることもできる。
In the molding by the pressing method, the performance that the uneven surface can be molded on the surface with a press plate (relief type) is required. The main material of the relief structure forming layers (2), (8), (18) may be any of a thermoplastic resin, a thermosetting resin, an ultraviolet ray or an electron beam curable resin. For example, thermoplastic resins such as acrylic resins, epoxy resins, cellulose resins, vinyl resins, urethane resins that are crosslinked by adding polyisocyanate as a crosslinking agent to acrylic polyols or polyester polyols having reactive hydroxyl groups, Examples thereof include thermosetting resins such as melamine resins and phenolic resins, and ultraviolet or electron beam curable resins such as epoxy (meth) acrylate and urethane (meth) acrylate. These may be used alone or in combination of two or more. Moreover, even if it is a thing other than these, if an uneven surface can be formed in the surface, it can be used suitably. In the case of press molding, a flat hot cold press method and a roll embossing method are exemplified. In these methods, after the resin of the relief structure forming layer is heated and melted to a temperature equal to or higher than the melting point, a relief mold having a relief pattern to be molded and a bank-shaped negative pattern is pressed to transfer the shape. Thereafter, the resin of the relief structure forming layer is lowered to the glass transition temperature or lower to solidify the resin, and then released from the relief mold, whereby a desired relief shape and bank shape can be obtained. When using thermosetting resin, ultraviolet curable resin, or electron beam curable resin, the relief shape and bank shape are formed, and after releasing from the relief mold, the resin is cured by heat, ultraviolet light, or electron beam. A coating film having a relief shape with good resistance can also be obtained.
一方、フォトポリマー法（２Ｐ法、感光性樹脂法）は、放射線硬化性樹脂をレリーフ型（復製用型）と平担な基材（プラスチックフィルム等）との間に流し込み放射線で硬化させた後、この硬化膜を基板ごと、複製用型から剥離する方法により、レリーフ構造部、及び土手部を備えた、レリーフ構造形成層（２）、（８）、（１８）を得る事が出来る。この２Ｐ法では、スタンパと基板との間に樹脂を広げる際に、樹脂の中から気泡を除去することが重要である。気泡が残存すると、レリーフ上に欠損部分ができ、期待する光学効果が得られず、不良品となるおそれがあるからである。使用される放射線硬化樹脂としては、一般的な紫外線硬化型樹脂が使用される。また、これら以外のものであっても、その表面に凹凸面を形成できる感光性樹脂を含むワニスであれば適宜使用することができる。 On the other hand, in the photopolymer method (2P method, photosensitive resin method), a radiation curable resin is poured between a relief mold (reproduction mold) and a flat substrate (plastic film, etc.) and cured with radiation. The relief structure forming layers (2), (8), and (18) having the relief structure portion and the bank portion can be obtained by peeling the cured film from the replication mold together with the substrate. In the 2P method, it is important to remove bubbles from the resin when the resin is spread between the stamper and the substrate. If air bubbles remain, a defective portion is formed on the relief, the expected optical effect cannot be obtained, and a defective product may be obtained. As the radiation curable resin to be used, a general ultraviolet curable resin is used. Moreover, even if it is a thing other than these, if it is a varnish containing the photosensitive resin which can form an uneven surface on the surface, it can be used suitably.
本発明のレリーフ構造（３）、（９）、（１９）は、レリーフの形状自体、又は、レリーフ構造形成層を透過した光を反射させるレリーフ効果層を設ける事によって何らかの光学効果をもたらす光学素子であり、プリズム、凸レンズ、凹レンズ、凸シリンドリカルレンズ、凹シリンドリカルレンズ、レンチキュラーレンズ、フレネルレンズ、回折格子、正弦回折格子、ブレーズ格子、サブ波長格子、偏光子等のレリーフ形状を有する。また、上記以外の形状でも、公知の光学素子の形状であれば適宜、レリーフ形状として使用できる。本発明の積層体において、例えば、レリーフ構造部に、回折光を発生させる為の凹凸からなるレリーフ構造を設け、そのレリーフ構造部の凹凸面に沿ってレリーフ効果層が設置された場合には、レリーフ効果層の凹凸表面で屈折、反射され、回折光は互いに干渉して色鮮やかな構造色を呈する。この回折現象によって得られる構造色は、観察者の位置によって異なる色彩を示す。 The relief structures (3), (9), and (19) of the present invention are optical elements that provide a certain optical effect by providing a relief effect layer that reflects the relief shape itself or light that has passed through the relief structure forming layer. And a relief shape such as a prism, a convex lens, a concave lens, a convex cylindrical lens, a concave cylindrical lens, a lenticular lens, a Fresnel lens, a diffraction grating, a sine diffraction grating, a blazed grating, a sub-wavelength grating, and a polarizer. In addition, shapes other than those described above can be appropriately used as a relief shape as long as the shape is a known optical element. In the laminate of the present invention, for example, when the relief structure is provided with a relief structure composed of irregularities for generating diffracted light, and a relief effect layer is installed along the irregular surface of the relief structure, It is refracted and reflected by the uneven surface of the relief effect layer, and the diffracted light interferes with each other to exhibit a colorful structural color. The structural color obtained by this diffraction phenomenon shows different colors depending on the position of the observer.
本発明の土手部（４）、（１０）、（２０）は、レリーフ効果層用の液状インキ又はエッチングマスク層用の液状インキを液滴法によって塗工する際に、液状インキのはみ出しを防止する効果がある。土手部は、液状インキを溜める堰である。この為、レリーフ構造部と、レリーフ効果層の位置制度を向上させるには、レリーフ構造部と、土手部を同時に成型する事が好ましい。成型方法については、前記のレリーフ構造と同様に、プレス成形法、フォトポリマー法等が挙げられる。 The banks (4), (10) and (20) of the present invention prevent the liquid ink from protruding when the liquid ink for the relief effect layer or the liquid ink for the etching mask layer is applied by the droplet method. There is an effect to. The bank is a weir for storing liquid ink. For this reason, in order to improve the position system of the relief structure part and the relief effect layer, it is preferable to mold the relief structure part and the bank part simultaneously. As for the molding method, a press molding method, a photopolymer method, and the like can be used as in the relief structure.
土手部の形状については、液状インキの堰き止め効果、及び成型性を考慮しデザインする必要が有る。 The shape of the bank portion needs to be designed in consideration of the liquid ink damming effect and moldability.
プレス成形法、又はフォトポリマー法のいずれの方法においても、成形される形状のアスペクト比が大きくなるほど、また、土手部の底面部分の面積に対する、先端部分の面積比率が大きくなればなるほど、土手部の成形が困難であり、また仮に成形されたとしても欠損が生じやすい。欠損を防止する為には、土手部のアスペクト比を下げるほか、土手部
をブロック状（任意の連続形状や、格子形状）にする事で、土手部の連続面積を増やし、構造的に土手部の強度を上げる手法が挙げられる。なお、土手高さについては、必要なインキの塗工量から算出し適宜決定すれば良い。図３、及び図４は、このような土手部の、液状インキの堰き止め効果、及び成型性を考慮したデザインの例である。
In either the press molding method or the photopolymer method, the bank portion increases as the aspect ratio of the shape to be molded increases, and as the area ratio of the tip portion to the area of the bottom surface portion of the bank portion increases. Is difficult to form, and even if it is formed, defects are likely to occur. In order to prevent defects, in addition to reducing the aspect ratio of the bank part, the bank part is made into a block shape (arbitrary continuous shape or lattice shape) to increase the continuous area of the bank part and structurally the bank part. A technique for increasing the strength of the material is mentioned. The bank height may be determined appropriately by calculating from the required ink coating amount. FIG. 3 and FIG. 4 are examples of the design of the bank portion in consideration of the liquid ink damming effect and moldability.
本発明のレリーフ効果層（６）、（１２）、（２２）は、レリーフ構造囲われ部（５）、（１１）、（２１）のみを覆うように配置された光学薄膜からなり、レリーフ構造形成層を透過した光を反射させる事を特徴とする。この為、レリーフ構造形成層よりも屈折率が高い高屈折率材料を使用することによって光学効果を得ることもできる。この場合、両層の屈折率の差は、０．２以上であることが好ましい。屈折率の差を０．２以上にすることによって、レリーフ構造形成層とレリーフ効果層との界面で屈折および反射が起こり、レリーフ形状による光学効果を得ることができる。なお、レリーフ効果層は少なくとも一部分、又は全体が複層であっても良く、又、部分的に異なる材料を使用しても良い。 The relief effect layers (6), (12), and (22) of the present invention are formed of an optical thin film disposed so as to cover only the relief structure surrounding portions (5), (11), and (21), and have a relief structure. It is characterized by reflecting light transmitted through the formation layer. For this reason, the optical effect can also be obtained by using a high refractive index material having a higher refractive index than the relief structure forming layer. In this case, the difference in refractive index between the two layers is preferably 0.2 or more. By setting the difference in refractive index to 0.2 or more, refraction and reflection occur at the interface between the relief structure forming layer and the relief effect layer, and the optical effect due to the relief shape can be obtained. The relief effect layer may be at least partly or entirely multilayered, or partially different materials may be used.
レリーフ効果層（６）、（１２）、（２２）を液適法で設ける場合には、アルミニウム、銀、ニッケル、金、銅、錫、インジウム、コバルトなどの微細な金属粉または金属ナノ粒子などを水、有機溶剤、及び有機高分子樹脂に分散して得られる高輝性光反射インキや、有機ポリマーの微粒子を水、有機溶剤、及び有機高分子樹脂に分散して得られる微粒子樹脂反射インキを使用することもできる。さらに、高輝性反射インキ、又は微粒子樹脂反射インキに使用可能である、高屈折率微粒子材料の例を以下に挙げる。以下に示す化学式または化合物名の後に続くカッコ内の数値は屈折率ｎを示す。セラミックスとしては、Ｓｂ2Ｏ3（３．０）、Ｆｅ2Ｏ3（２．７）、ＴｉＯ2（２．６）、ＣｄＳ（２．６）、ＣｅＯ２（２．３）、ＺｎＳ（２．３）、ＰｂＣｌ2（２．３）、ＣｄＯ（２．２）、Ｓｂ2Ｏ3（２．０）、ＷＯ3（２．０）、ＳｉＯ（２．０）、Ｓｉ2Ｏ3（２．５）、Ｉｎ2Ｏ3（２．０）、ＰｂＯ（２．６）、Ｔａ2Ｏ3（２．４）、ＺｎＯ（２．１）、ＺｒＯ2（２．０）、ＭｇＯ（１．６）、Ｓｉ2Ｏ2（１．５）、ＭｇＦ2（１．４）、ＣｅＦ3（１．６）、ＣａＦ2（１．３〜１．４）、ＡｌＦ3（１．６）、Ａｌ2Ｏ3（１．６）、ＧａＯ（１．７）などが挙げられる。有機ポリマーとしては、ポリエチレン（１．５１）、ポリプロピレン（１．４９）、ポリテトラフルオロエチレン（１．３５）、ポリメチルメタクリレート（１．４９）、ポリスチレン（１．６０）などが挙げられるが、これらに限定されない。これらの材料の微粒子は、屈折率、反射率、透過率などの光学特性や、耐候性、層間密着性などに基づいて適宜選択され、水、有機溶剤などの各種溶媒に分散されるほか、少量のバインダーを入れる事も可能である。なお、使用する微粒子は２種以上の粒子を組み合わせても良い。また、液適法によりレリーフ効果層を設ける場合は、レリーフ構造形成層のレリーフ形成面を溶剤によりアタックさせないようにする注意が必要である。また、乾燥後の膜厚は０．００１〜１０μｍ程度になるように調整すればよい。 When the relief effect layers (6), (12) and (22) are provided by a liquid suitable method, fine metal powder or metal nanoparticles such as aluminum, silver, nickel, gold, copper, tin, indium and cobalt are used. Uses high-brightness light reflection ink obtained by dispersing in water, organic solvent, and organic polymer resin, and fine particle resin reflection ink obtained by dispersing fine particles of organic polymer in water, organic solvent, and organic polymer resin You can also Furthermore, the example of the high refractive index fine particle material which can be used for high gloss reflective ink or fine particle resin reflective ink is given below. The numerical value in parentheses following the chemical formula or compound name shown below indicates the refractive index n. As ceramics, Sb 2 O 3 (3.0), Fe 2 O 3 (2.7), TiO 2 (2.6), CdS (2.6), CeO 2 (2.3), ZnS (2. 3), PbCl 2 (2.3), CdO (2.2), Sb 2 O 3 (2.0), WO 3 (2.0), SiO (2.0), Si 2 O 3 (2. 5), In 2 O 3 (2.0), PbO (2.6), Ta 2 O 3 (2.4), ZnO (2.1), ZrO 2 (2.0), MgO (1.6 ), Si 2 O 2 (1.5), MgF 2 (1.4), CeF 3 (1.6), CaF 2 (1.3 to 1.4), AlF 3 (1.6), Al 2 O 3 (1.6), GaO (1.7) and the like can be mentioned. Examples of the organic polymer include polyethylene (1.51), polypropylene (1.49), polytetrafluoroethylene (1.35), polymethyl methacrylate (1.49), polystyrene (1.60), and the like. It is not limited to these. The fine particles of these materials are appropriately selected based on optical properties such as refractive index, reflectance, and transmittance, weather resistance, interlayer adhesion, and the like, and are dispersed in various solvents such as water and organic solvents. It is also possible to add a binder. The fine particles to be used may be a combination of two or more kinds. Further, when the relief effect layer is provided by a liquid suitable method, care must be taken not to attack the relief forming surface of the relief structure forming layer with a solvent. Moreover, what is necessary is just to adjust so that the film thickness after drying may be set to about 0.001-10 micrometers.
一方、液適法によってエッチングマスク層を設ける場合、レリーフ効果層は前述の液適法以外の方法で設けても良い。例えば、、Ａｌ、Ｓｎ、Ｃｒ、Ｎｉ、Ｃｕ、Ａｕ、Ａｇなどの金属材料の単体、またはこれらの化合物を、公知の真空蒸着またはスパッタリングにより成膜してもよい。 On the other hand, when the etching mask layer is provided by a liquid suitable method, the relief effect layer may be provided by a method other than the liquid suitable method described above. For example, a single metal material such as Al, Sn, Cr, Ni, Cu, Au, and Ag, or a compound thereof may be formed by known vacuum deposition or sputtering.
上記以外の材料の例を以下に挙げる。以下に示す化学式または化合物名の後に続くカッコ内の数値は屈折率ｎを示す。セラミックスとしては、Ｓｂ２Ｏ３（３．０）、Ｆｅ２Ｏ３（２．７）、ＴｉＯ2（２．６）、ＣｄＳ（２．６）、ＣｅＯ2（２．３）、ＺｎＳ（２．３）、ＰｂＣｌ2（２．３）、ＣｄＯ（２．２）、Ｓｂ2Ｏ3（２．０）、ＷＯ3（２．０）、ＳｉＯ（２．０）、Ｓｉ2Ｏ3（２．５）、Ｉｎ2Ｏ3（２．０）、ＰｂＯ（２．６）、Ｔａ2Ｏ3（２．４）、ＺｎＯ（２．１）、ＺｒＯ2（２．０）、ＭｇＯ（１．６）、Ｓｉ2Ｏ2（１．５）、ＭｇＦ2（１．４）、ＣｅＦ3（１．６）、ＣａＦ2（１．３〜１．４）、ＡｌＦ3（１．６）、Ａｌ2Ｏ3（１．６）、ＧａＯ（１．７）などが挙げられる。有機ポリマーとしては、ポリエチレン（１．５１）、ポリプロピレン（１．４９）、ポリテトラフルオロエチレン（１．３５）、ポリメチルメタクリレート（１．４９）、ポリスチレン（１．６０）などが挙げられるが、これらに限定されない。これらの材料は、屈折率、反射率、透過率などの光学特性や、耐候性、層間密着性などに基づいて適宜選択され、薄膜の形態で形成される。形成方法としては、膜厚、成膜速度、積層数、光学膜厚などの制御が可能な、真空蒸着法、スパッタリング法、ＣＶＤ法など公知の方法を適宜使用することができる。なお、本発明において光学膜厚とは、ｎ・ｄ（ここで、ｎは屈折率、ｄは膜厚である）で与えられる量を意味する。 Examples of materials other than the above are given below. The numerical value in parentheses following the chemical formula or compound name shown below indicates the refractive index n. The ceramics, Sb2O3 (3.0), Fe2O3 ( 2.7), TiO 2 (2.6), CdS (2.6), CeO 2 (2.3), ZnS (2.3), PbCl 2 (2.3), CdO (2.2), Sb 2 O 3 (2.0), WO 3 (2.0), SiO (2.0), Si 2 O 3 (2.5), In 2 O 3 (2.0), PbO (2.6), Ta 2 O 3 (2.4), ZnO (2.1), ZrO 2 (2.0), MgO (1.6), Si 2 O 2 (1.5), MgF 2 (1.4), CeF 3 (1.6), CaF 2 (1.3 to 1.4), AlF 3 (1.6), Al 2 O 3 (1. 6) and GaO (1.7). Examples of the organic polymer include polyethylene (1.51), polypropylene (1.49), polytetrafluoroethylene (1.35), polymethyl methacrylate (1.49), polystyrene (1.60), and the like. It is not limited to these. These materials are appropriately selected based on optical characteristics such as refractive index, reflectance, and transmittance, weather resistance, interlayer adhesion, and the like, and are formed in the form of a thin film. As a formation method, a known method such as a vacuum evaporation method, a sputtering method, or a CVD method capable of controlling the film thickness, the film formation speed, the number of stacked layers, the optical film thickness, and the like can be appropriately used. In the present invention, the optical film thickness means an amount given by n · d (where n is the refractive index and d is the film thickness).
本発明のエッチングマスク層（１３）は、レリーフ効果層をエッチングする際のエッチングマスクであり、酸やアルカリに対する耐久性を持っていることが好ましい。一般的な、アルミ反射膜のエッチング手法を一例を挙げると、４０〜５０℃程度に熱した１．５ＮのＮａＯＨ溶液中に、１０〜２０秒浸すものであるため、２倍の４０秒程度浸して塗膜に変化なければ十分な耐性があると判断される。また、エッチングマスクに耐熱性を持たせる事で、レリーフ形状に耐熱性を付与する事が可能である。この場合、特開２００５−９９０９０号公報に記載の公知の耐熱樹脂材料をエッチングマスクに用いれば良い。但し、本発明では、液滴法によりパターンが形成される。 The etching mask layer (13) of the present invention is an etching mask for etching the relief effect layer, and preferably has durability against acids and alkalis. An example of a general aluminum reflective film etching method is to immerse in a 1.5N NaOH solution heated to about 40 to 50 ° C. for 10 to 20 seconds. If the coating film does not change, it is judged that there is sufficient resistance. In addition, heat resistance can be imparted to the relief shape by imparting heat resistance to the etching mask. In this case, a known heat-resistant resin material described in JP-A-2005-99090 may be used for the etching mask. However, in the present invention, the pattern is formed by the droplet method.
本発明の偽造防止転写箔（２３）における、支持体（２４）は、厚みが安定しており、かつ耐熱性の高いポリエチレンテレフタレート樹脂フィルムを用いるのが一般的であるが、その材料は特に限定されない。その他のフィルム材料として、高い耐熱性を示すポリエチレンナフタレート樹脂フィルム、ポリイミド樹脂フィルムなどを同様の目的で使用することができる。また、他のフィルム材料、たとえばポリエチレン、ポリプロピレン、耐熱塩化ビニルなども、塗液の塗工条件（乾燥条件）、蒸着加工、スパッタ加工、レリーフ成型時のプレス加工等における熱条件、張力条件、プレス条件が許せば使用できる。 The support (24) in the forgery-preventing transfer foil (23) of the present invention is generally a polyethylene terephthalate resin film having a stable thickness and high heat resistance, but the material is particularly limited. Not. As other film materials, a polyethylene naphthalate resin film, a polyimide resin film, or the like exhibiting high heat resistance can be used for the same purpose. In addition, other film materials such as polyethylene, polypropylene, heat-resistant vinyl chloride, etc. can also be used for coating conditions (drying conditions) for coating liquids, vapor deposition, spattering, thermal conditions, tension conditions, press conditions during relief molding, etc. Can be used if conditions permit.
本発明の偽造防止転写箔（２３）において、積層体（２５）は支持体（２４）から剥離可能であってもよい。なお、支持体（２４）と積層体（２５）との間に、支持体から剥離可能な剥離保護層、又は、支持体から剥離しない離型層と呼ばれる層が設けられる場合があるが、これらの層はいずれも必須ではない。すなわち、これらの層は、転写された積層体（２５）の表面を保護する意図で、又は安定した剥離強度を得る事で、転写する際の転写性能を高める意図で、設計により適宜設けてもよい。 In the forgery-preventing transfer foil (23) of the present invention, the laminate (25) may be peelable from the support (24). A layer called a release protective layer that can be peeled off from the support or a release layer that does not peel off from the support may be provided between the support (24) and the laminate (25). None of these layers are required. That is, these layers may be appropriately provided by design with the intention of protecting the surface of the transferred laminate (25) or with the intention of improving the transfer performance during transfer by obtaining a stable peel strength. Good.
剥離保護層としては、ポリメチルメタクリレート樹脂と他の熱可塑性樹脂たとえば塩化ビニル／酢酸ビニル共重合体もしくはニトロセルロース樹脂との混合物、またはポリメチルメタクリレート樹脂とポリエチレンワックスとの混合物などが挙げられる。また、酢酸セルロース樹脂と熱硬化性樹脂たとえばエポキシ樹脂、フェノール樹脂、熱硬化型アクリル樹脂またはメラミン樹脂との混合物を塗工した後、熱により硬化させたものも好ましい例として挙げられる。又、離型層としては、シリコン樹脂、フッ素樹脂等の離型性のある樹脂が挙げられ、特に離型紙用の材料が用いられる。これらの樹脂を支持体（２４）に塗工する事で、積層体（２５）の離型性、剥離性を制御する事が可能である。 Examples of the peel protective layer include a mixture of polymethyl methacrylate resin and other thermoplastic resins such as vinyl chloride / vinyl acetate copolymer or nitrocellulose resin, or a mixture of polymethyl methacrylate resin and polyethylene wax. A preferable example is one obtained by applying a mixture of a cellulose acetate resin and a thermosetting resin such as an epoxy resin, a phenol resin, a thermosetting acrylic resin, or a melamine resin, and then curing it by heat. Examples of the release layer include resins having a release property such as a silicon resin and a fluorine resin, and a release paper material is particularly used. By applying these resins to the support (24), it is possible to control the releasability and releasability of the laminate (25).
本発明の偽造防止転写箔（２３）において、接着剤層（２６）には、様々な被転写材（例えば、紙・プラスチック）に接した状態で熱および圧力を与えられることにより、被転写材に接着する機能を有する公知の感熱樹脂（感熱性接着材料）が使用される。 In the forgery-preventing transfer foil (23) of the present invention, the adhesive layer (26) is subjected to heat and pressure in contact with various transfer materials (for example, paper and plastic), thereby transferring the transfer material. A known heat-sensitive resin (heat-sensitive adhesive material) having a function of adhering to is used.
本発明の偽造防止シール（２８）において、支持体（２９）および接着剤（３１）は、例えば、公知のステッカー製造に用いられる材料および手法を適宜用いて、製造できる。 In the anti-counterfeit seal (28) of the present invention, the support (29) and the adhesive (31) can be produced by appropriately using, for example, known materials and techniques used for producing stickers.
また、貼り付けられたステッカーを剥すと、ステッカーが破壊してしまうように、層間
に剥離する部分を設けたり、ステッカーに切れ込みを入れることも可能である。これによると、ステッカーが破壊されるので、ステッカーを別の基材に貼り替えて利用しようとする不正を図られても再利用を阻止することに有効である。また、これによると、ステッカーが破壊されるので、（ステッカーの下方に秘密の情報が設けてある場合に）秘密の情報の盗み読みした後に元の箇所にこの本物のステッカーを貼りつけたり、秘密の情報を改ざんした後に元の箇所にこの本物のステッカーを貼りつけたり、といった不正を阻止することにも有効である。
Moreover, it is also possible to provide a part to be peeled between layers or to make a notch in the sticker so that the sticker is destroyed when the sticker is affixed. According to this, since the sticker is destroyed, it is effective in preventing reuse even if an attempt is made to replace the sticker with another base material and try to use it. This also destroys the sticker, so if you have stolen the secret information (if there is secret information below the sticker), stick this real sticker to the original location, It is also effective to prevent fraud such as pasting this genuine sticker on the original part after tampering.
以上、一実施例を説明してきたが、意匠性を向上すべく各層を着色することや表面もしくは層間に印刷を施す等、使用の目的により適宜利用可能である。また、各層の接着性を鑑み、各層間に接着アンカー層を設けることや、コロナ放電処理・プラズマ処理・フレーム処理等の各種易接着処理を施すことも可能である。 Although one embodiment has been described above, it can be used as appropriate depending on the purpose of use, such as coloring each layer to improve the design or printing on the surface or between layers. Moreover, in view of the adhesiveness of each layer, it is possible to provide an adhesion anchor layer between each layer, and to perform various easy adhesion treatments such as corona discharge treatment, plasma treatment, and flame treatment.
以下、具体的な実施例に基づいて本発明を更に詳細に説明する。 Hereinafter, the present invention will be described in more detail based on specific examples.
＜実施例１＞
本発明に係る偽造防止積層体を製造するために、下記に示すように、レリーフ形成層、及びレリーフ効果層に用いるインキ組成物を用意した。
「レリーフ構造形成層インキ組成物」
ウレタン樹脂 １５．０重量部
アクリルシリコン樹脂 ５．０重量部
メチルエチルケトン ５０．０重量部
酢酸エチル ３０．０重量部
「レリーフ効果層インキ組成物」
銀粒子分散インキ（５０ｎｍ銀粒子、水分散体） １００．０重量部
厚み２３μｍの透明ポリエチレンテレフタレート（ＰＥＴ）フィルムからなる支持体上に、レリーフ構造形成層インキ組成物を膜厚２μｍとなるように塗布し、１５０℃、１０ｓｅｃの条件で焼き付け、乾燥してレリーフ構造形成層を形成した。次いで、ロールエンボス法により、レリーフ構造形成層の表面に回折格子を構成する微小凹凸のレリーフ構造部と、土手部を形成した。次に、液適法（インキジェット法）によって、レリーフ構造囲われ部のみにレリーフ効果層インキ組成物を塗工し、乾燥して所望の偽造防止積層体を得た。
<Example 1>
In order to produce the forgery-preventing laminate according to the present invention, an ink composition used for a relief forming layer and a relief effect layer was prepared as shown below.
"Relief structure forming layer ink composition"
Urethane resin 15.0 parts by weight Acrylic silicone resin 5.0 parts by weight Methyl ethyl ketone 50.0 parts by weight Ethyl acetate 30.0 parts by weight “Relief effect layer ink composition”
Silver particle-dispersed ink (50 nm silver particles, water dispersion) 100.0 parts by weight On a support made of a transparent polyethylene terephthalate (PET) film having a thickness of 23 μm, the relief structure forming layer ink composition has a thickness of 2 μm. It was applied, baked at 150 ° C. for 10 seconds, and dried to form a relief structure forming layer. Subsequently, the relief structure part of the micro unevenness | corrugation which comprises a diffraction grating and the bank part were formed in the surface of the relief structure formation layer by the roll embossing method. Next, the relief effect layer ink composition was applied only to the relief structure surrounded portion by a liquid suitable method (ink jet method) and dried to obtain a desired forgery-preventing laminate.
＜実施例２＞
本発明に係る偽造防止積層体を製造するために、下記に示すように、レリーフ形成層、及びエッチングマスク層に用いるインキ組成物を用意した。
<Example 2>
In order to produce the anti-counterfeit laminate according to the present invention, an ink composition used for a relief forming layer and an etching mask layer was prepared as shown below.
アクリルシリコン樹脂 ５．０重量部
メチルエチルケトン ５０．０重量部
酢酸エチル ３０．０重量部
「エッチングマスク層インキ組成物」
塩化ビニル酢酸ビニル共重合体 ２０．０重量部
メチルエチルケトン ５０．０重量部
酢酸エチル ３０．０重量部
厚み２３μｍの透明ポリエチレンテレフタレート（ＰＥＴ）フィルムからなる支持体上に、レリーフ構造形成層インキ組成物を膜厚２μｍとなるように塗布し、１５０℃、１０ｓｅｃの条件で焼き付け、乾燥してレリーフ構造形成層を形成した。次いで、ロールエンボス法により、レリーフ構造形成層層の表面に回折格子を構成する微小凹凸のレリーフ構造部と、土手部を形成した。次に、アルミニウムを５０ｎｍの膜厚となるように真空蒸着
して、全面にレリーフ効果層を形成した。その後、液適法（インクジェット法）によって、レリーフ構造囲われ部のみにエッチングマスク層組成物を塗布、乾燥させた。次に、５０℃に加熱された１．５ＮのＮａＯＨ溶液が入った浴槽に１０秒間浸すことにより、上記エッチングマスク層不存在部のレリーフ効果層をエッチングした後、０．１ＮのＨＣｌ溶液にて中和し、その後水洗・乾燥工程を経て、所望の偽造防止積層体を得た。
Acrylic silicone resin 5.0 parts by weight Methyl ethyl ketone 50.0 parts by weight Ethyl acetate 30.0 parts by weight “Etching mask layer ink composition”
Vinyl chloride vinyl acetate copolymer 20.0 parts by weight Methyl ethyl ketone 50.0 parts by weight Ethyl acetate 30.0 parts by weight On a support made of a transparent polyethylene terephthalate (PET) film having a thickness of 23 μm, a relief structure-forming layer ink composition was prepared. The film was applied to a thickness of 2 μm, baked at 150 ° C. for 10 seconds, and dried to form a relief structure forming layer. Subsequently, the relief structure part of the fine unevenness which comprises a diffraction grating, and the bank part were formed in the surface of the relief structure formation layer layer by the roll embossing method. Next, aluminum was vacuum-deposited to a thickness of 50 nm to form a relief effect layer on the entire surface. Then, the etching mask layer composition was applied and dried only on the portion surrounded by the relief structure by a liquid suitable method (inkjet method). Next, after the relief effect layer in the absence of the etching mask layer is etched by immersing in a bath containing 1.5N NaOH solution heated to 50 ° C. for 10 seconds, 0.1N HCl solution is used. After neutralization, a desired anti-counterfeit laminate was obtained through a washing and drying process.
＜比較例１＞
実施例１と同様にして、厚み２３μｍの透明ポリエチレンテレフタレート（ＰＥＴ）フィルムからなる支持体上に、レリーフ構造形成層インキ組成物を膜厚２μｍとなるように塗布し、１５０℃、１０ｓｅｃの条件で焼き付け、乾燥してレリーフ構造形成層を形成した。次いで、ロールエンボス法により、レリーフ構造形成層の表面に回折格子を構成する微小凹凸のレリーフ構造部を形成した。次に、アルミニウムを５０ｎｍの膜厚となるように真空蒸着して、全面にレリーフ効果層を形成した。その後、レリーフ構造部分と同一のパターンとなるように、液適法（インクジェット法）によって０．５μｍの厚みとなるようにエッチングマスク層組成物をパターン印刷し、エッチングマスク層を形成した。次に、５０℃に加熱された１．５ＮのＮａＯＨ溶液が入った浴槽に１０秒間浸すことにより、上記エッチングマスク層不存在部のレリーフ効果層（アルミ蒸着）をエッチングした後、０．１ＮのＨＣｌ溶液にて中和し、その後水洗・乾燥工程を経て、所望の偽造防止積層体を得た。
<Comparative Example 1>
In the same manner as in Example 1, the relief structure forming layer ink composition was applied to a thickness of 2 μm on a support made of a transparent polyethylene terephthalate (PET) film having a thickness of 23 μm, and the conditions were 150 ° C. and 10 sec. A relief structure forming layer was formed by baking and drying. Subsequently, the relief structure part of the micro unevenness | corrugation which comprises a diffraction grating was formed in the surface of the relief structure formation layer by the roll embossing method. Next, aluminum was vacuum-deposited to a thickness of 50 nm to form a relief effect layer on the entire surface. Then, the etching mask layer composition was pattern-printed so that it might become a thickness of 0.5 micrometer by the liquid suitable method (inkjet method) so that it might become the same pattern as a relief structure part, and the etching mask layer was formed. Next, after etching the relief effect layer (aluminum deposition) in the absence of the etching mask layer by immersing in a bath containing 1.5N NaOH solution heated to 50 ° C. for 10 seconds, 0.1N of The solution was neutralized with an HCl solution and then washed with water and dried to obtain a desired anti-counterfeit laminate.
実施例１、２、及び比較例１の積層体をそれぞれ２０サンプル作成し、設計図柄における、レリーフ構造部分とレリーフ効果層の位置ズレ幅について測定し、位置ズレのバラツキに関して評価した。また、液適法で発生する液ハネ、及び液ダレに起因するレリーフ効果層の面積を測定し、液ハネ液ダレ不良の発生について評価した。その評価結果を表１に示す。 Twenty samples of each of the laminates of Examples 1 and 2 and Comparative Example 1 were prepared, the positional shift widths of the relief structure portion and the relief effect layer in the design pattern were measured, and the variation in positional shift was evaluated. Moreover, the area of the relief effect layer resulting from the liquid splash generated by the liquid suitable method and the liquid dripping was measured, and the occurrence of the liquid dripping liquid deficiency was evaluated. The evaluation results are shown in Table 1.
［位置ズレの評価］
実施例１、実施例２、及び比較例１の積層体をそれぞれ２０サンプル作成し、設計図柄を基準とし、レリーフ構造部分とレリーフ効果層の位置ズレ幅について測定し、位置ズレのバラツキに関して評価した。
[Evaluation of misalignment]
Twenty samples of each of the laminates of Example 1, Example 2, and Comparative Example 1 were prepared, and the positional displacement widths of the relief structure portion and the relief effect layer were measured with reference to the design pattern, and the variation in positional displacement was evaluated. .
［液ハネ、液ダレの評価］
実施例１、実施例２、及び比較例１の積層体をそれぞれ２０サンプル作成し、液適法で発生する液ハネ、及び液ダレに起因するレリーフ効果層の面積を測定し、設計面積との比較により、液ハネ液ダレ不良の発生について評価した。なお、面積の測定は、スキャナーにて画像取り込みを実施した後に、測定したい面積部のピクセル数を計数した後、実面積に換算した。
[Evaluation of liquid splash and dripping]
20 samples of each of the laminates of Example 1, Example 2, and Comparative Example 1 were prepared, and the area of the relief effect layer caused by the liquid splash generated by the liquid appropriate method and the liquid dripping was measured, and compared with the design area. Thus, the occurrence of defective liquid dripping was evaluated. The area was measured after the image was captured by the scanner, and after counting the number of pixels in the area portion to be measured, it was converted to the actual area.
［評価基準］
○：設計面積に対し、液ダレ液ハネ不良面積が、０．０〜０．１％
△：設計面積に対し、液ダレ液ハネ不良面積が、０．２〜０．９％
×：設計面積に対し、液ダレ液ハネ不良面積が、１．０％以上
[Evaluation criteria]
○: The dripping liquid splash defective area is 0.0 to 0.1% with respect to the design area.
Δ: The dripping liquid splash defective area is 0.2 to 0.9% with respect to the design area.
X: The dripping liquid splash defective area is 1.0% or more with respect to the design area.
表１からわかるように、実施例１、２の積層体では、位置ズレ平均が０．０１ｍｍ未満で良好であるのに対し、比較例１では最大で０．２ｍｍの位置ズレが生じる。また、実施例１、及び２に対し、比較例１は、液ダレ液ハネ不良面積が多い。 As can be seen from Table 1, in the laminates of Examples 1 and 2, the average positional deviation is good at less than 0.01 mm, whereas in Comparative Example 1, a positional deviation of 0.2 mm at maximum occurs. Moreover, compared with Example 1 and 2, the comparative example 1 has many dripping liquid splash defective areas.
以上のことから、レリーフ構造とレリーフ効果層を設計図柄通りのパターンで形成し、
そのレリーフ構造とレリーフ効果層を精度良く配置した、レリーフ構造を含む光学素子からなる、安価で生産性が高く、装飾性にも優れた視覚効果を得られる、高品質の、偽造防止積層体、偽造防止転写箔、偽造防止シール、偽造防止媒体、及びこれらの製造方法並びにその製造装置を提供することが出来る。
From the above, the relief structure and relief effect layer are formed in a pattern as designed,
A high-quality, anti-counterfeit laminate that has a relief structure and a relief effect layer that are arranged with high accuracy, and that is made of an optical element including a relief structure. It is possible to provide an anti-counterfeit transfer foil, an anti-counterfeit seal, an anti-counterfeit medium, a manufacturing method thereof, and an apparatus for manufacturing the same.
１：第１の偽造防止積層体
２：レリーフ構造形成層
３：レリーフ構造部
４：土手部
５：レリーフ構造囲われ部
６：レリーフ効果層
７：第２の偽造防止積層体
８：レリーフ構造形成層
９：レリーフ構造部
１０：土手部
１１：レリーフ構造囲われ部
１２：レリーフ効果層
１３：エッチングマスク層
１４：第３の偽造防止積層体
１５：土手部
１６：レリーフ構造囲われブロック部
１７：破線
１８：レリーフ構造形成層
１９：レリーフ構造部
２０：土手部
２１：レリーフ構造囲われ部
２２：レリーフ効果層
２３：偽造防止転写箔
２４：支持体２５：偽造防止積層体
２６：接着層
２７：転写層
２８：偽造防止シール
２９：支持体
３０：偽造防止積層体
３１：接着層
３２：偽造防止媒体
３３：支持体
３４：積層体、又は転写箔、又はシール
1: First anti-counterfeit laminate 2: Relief structure forming layer 3: Relief structure portion 4: Bank portion 5: Relief structure enclosed portion 6: Relief effect layer 7: Second anti-counterfeit laminate 8: Relief structure formation Layer 9: Relief structure part 10: Bank part 11: Relief structure enclosed part 12: Relief effect layer 13: Etching mask layer 14: Third anti-counterfeit laminate 15: Bank part 16: Relief structure enclosed block part 17: Broken line 18: Relief structure forming layer 19: Relief structure part 20: Bank part 21: Relief structure enclosed part 22: Relief effect layer 23: Anti-counterfeit transfer foil 24: Support 25: Anti-counterfeit laminate 26: Adhesive layer 27: Transfer layer 28: anti-counterfeit seal 29: support 30: anti-counterfeit laminate 31: adhesive layer 32: anti-counterfeit medium 33: support 34: laminate, transfer foil, or seal
Claims (11)
前記レリーフ構造形成層（イ）の片側に、部分的に設けられたレリーフ構造部（ロ）と、前記レリーフ構造部（ロ）と重ならないように、同一面上に、部分的に設けられた土手部（ハ）と、前記土手部（ハ）に囲われ、レリーフ構造部（ロ）を含むレリーフ構造囲われ部（ニ）と、前記レリーフ構造囲われ部（ニ）のみを覆うように配置された光学薄膜からなり、前記レリーフ構造形成層（イ）を透過した光の少なくとも一部を反射させるレリーフ効果層（ホ）と、を順次積層して具備してなることを特徴とする偽造防止積層体。 At least the relief structure forming layer (I),
A relief structure part (b) provided partially on one side of the relief structure formation layer (a) and a part provided on the same surface so as not to overlap the relief structure part (b) Surrounded by the bank part (c) and the bank part (c) and arranged to cover only the relief structure part (d) including the relief structure part (b) and the relief structure enclosed part (d) Forgery prevention comprising a relief effect layer (e) that is formed by sequentially laminating the relief structure forming layer (a) and reflecting at least part of the light transmitted through the relief structure forming layer (a). Laminated body.