Pressure-sensitive adhesive sheet having sheet material, as well as it

Info

Publication number
JP5052711B2
JP5052711B2 JP34097599A JP34097599A JP5052711B2 JP 5052711 B2 JP5052711 B2 JP 5052711B2 JP 34097599 A JP34097599 A JP 34097599A JP 34097599 A JP34097599 A JP 34097599A JP 5052711 B2 JP5052711 B2 JP 5052711B2
Authority
JP
Grant status
Grant
Patent type
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP34097599A
Other languages
Japanese (ja)
Other versions
JP2001152102A (en )
Inventor
伸児 井口
由紀 長谷川
Original Assignee
日東電工株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Grant date

Description

【0001】 [0001]
【発明の属する技術分野】 BACKGROUND OF THE INVENTION
本発明は、感圧性接着シートなどの材料として好適なシート材、およびそのシート材を有する感圧性接着シートに関する。 The present invention is suitable sheet material as a material such as pressure-sensitive adhesive sheet, and a pressure-sensitive adhesive sheet having the sheet material. 本明細書において、シート材、感圧性接着シートは、それぞれテープ材、感圧性接着テープを包含するものである。 In this specification, the sheet material, the pressure-sensitive adhesive sheet, tape material respectively, is intended to encompass a pressure-sensitive adhesive tape.
【0002】 [0002]
【従来の技術】 BACKGROUND OF THE INVENTION
感圧性接着シートは、剥離剤を硬化させてなる層のみを有するシート材または当該層を最外層として有する剥離機能を有するシート材と、該シート材に接する感圧性接着剤層とを有し、シート材と感圧性接着剤層との間で剥離させることができる。 Pressure-sensitive adhesive sheet has a sheet material having a release function with the sheet material or the layer having only a layer formed by curing a release agent as the outermost layer, and a pressure-sensitive adhesive layer in contact with said sheet material, it can be detached between the sheet material and the pressure-sensitive adhesive layer. 前記シート材は、剥離剤のみを硬化させるか、あるいは剥離シート基材の少なくとも感圧性接着剤層に接することを意図する側の層に剥離剤を塗布し硬化させることによって形成される。 The sheet material is formed by either cure the only release agent, or release agent is applied in a layer on the side intended to contact at least a pressure-sensitive adhesive layer of the release sheet base material curing. 前記剥離剤としては、たとえばシリコーン系の剥離剤が知られている。 As the release agent, for example a silicone release agent are known. 感圧性接着剤層は、たとえばアクリル系の感圧性接着剤を用いて、シート材に接するように形成される。 Pressure-sensitive adhesive layer, for example using a pressure sensitive acrylic adhesive, is formed in contact with the sheet material.
【0003】 [0003]
このような感圧性接着シートは、シート材と感圧性接着剤層との間の剥離時に、シート材に含有されるシリコーン化合物が感圧性接着剤層に付着してしまう。 Such pressure-sensitive adhesive sheet, at the time of peeling between the sheet material and the pressure-sensitive adhesive layer, a silicone compound contained in the sheet material adheres to the pressure-sensitive adhesive layer. シリコーン化合物が付着した感圧性接着剤層は、シリコーン化合物が付着しない感圧性接着剤層と比較して、接着強さが著しく低下してしまう。 Pressure-sensitive adhesive layer silicone compound is attached, as compared to the pressure-sensitive adhesive layer silicone compound does not adhere, adhesive strength is remarkably decreased.
【0004】 [0004]
また上述した感圧性接着シートを電子機器の部品の固定などに用いると、一般に電子機器内部の腐食または電子機器の誤動作が起こりやすくなる。 Also the use of pressure-sensitive adhesive sheet described above in such a fixed component of the electronic device, made generally likely to occur corrosion or malfunction of electronic equipment inside the electronic device. このような腐食または誤動作は、前記シートがハードディスクドライブ(HDD)など電子機器の内部に用いられた場合に特に起こりやすい。 Such corrosion or malfunction, especially likely to occur when the sheet is used in the interior of the electronic device such as a hard disk drive (HDD). これは、シート材と感圧性接着剤層との間の剥離時に感圧性接着剤層に付着したシリコーン化合物がシロキサンガスを発生するためであると考えられている。 This silicone compound adhered to the pressure-sensitive adhesive layer at the time of peeling between the sheet material and the pressure-sensitive adhesive layer is believed to be due to generation of siloxane gas.
【0005】 [0005]
また特公昭51−20205号公報には、シリコーン系以外の剥離剤を用いて形成したシート材が開示されている。 Further, Japanese Patent Publication 51-20205, a sheet material formed by using a release agent other than silicone are disclosed. このシート材では、低密度ポリエチレン樹脂が用いられる。 In this sheet material, low-density polyethylene resin is used. 前記シート材は、剥離シート基材の表面上に、その表面の酸化を抑制しながら低密度ポリエチレン樹脂を積層することによって形成される。 The sheet material is on the surface of the release sheet base material, is formed by laminating a low-density polyethylene resin while suppressing the oxidation of the surface.
【0006】 [0006]
さらにまた特公昭57−45790号公報にも、シリコーン系以外の剥離剤を用いて形成したシート材が開示されている。 Furthermore in Japanese Patent Publication No. Japanese Patent Publication 57-45790, a sheet material formed by using a release agent other than silicone are disclosed. このシート材は、低密度ポリエチレン樹脂とエチレン−プロピレン共重合体とによる混合樹脂または低密度ポリエチレン樹脂とエチレン−1−ブテンランダム共重合体とによる混合樹脂が用いられる。 The sheet material is low density polyethylene resin and ethylene - mixing by a propylene copolymer resin or a low density polyethylene resin and an ethylene-1-butene random copolymer and by mixing resin is used.
【0007】 [0007]
このようなシート材と感圧性接着剤層とを有する感圧性接着シートは、感圧性接着剤層が比較的高い接着強さを有する場合に、剥離性が低下する。 Such pressure-sensitive adhesive sheet having a sheet member and the pressure-sensitive adhesive layer, when the pressure-sensitive adhesive layer has a relatively high adhesive strength, peelability decreases. 剥離性が低下した感圧性接着シートは、感圧性接着剤層とシート材との間の剥離時に接着剤がシート材に付着したり、剥離後の感圧性接着剤層の表面の形状がパルス状となるスティックスリップなどと呼ばれる不所望な剥離を引き起こしたりする。 Pressure-sensitive adhesive sheet releasability is lowered, the pressure-sensitive adhesive layer and the adhesive during peeling or adheres to the sheet material between the sheet material, the pulse shape of the surface of the pressure-sensitive adhesive layer after peeling or cause unwanted peeling called such stick-slip to be. これによって感圧性接着剤層とシート材との間の剥離で露出した感圧性接着剤層の表面粗さが大きくなってしまう。 This surface roughness of the pressure-sensitive adhesive layer exposed by peeling between the pressure-sensitive adhesive layer and the sheet material increases. このような感圧性接着シートでは、感圧性接着剤層が本来備えている接着強さを充分に発揮することができず、接着性がよくない。 In such a pressure-sensitive adhesive sheet can not be pressure-sensitive adhesive layer is sufficiently exhibit the adhesive strength that is originally provided, poor adhesion.
【0008】 [0008]
またこれらのシート材は、低密度ポリエチレン樹脂を含有しているので、液状の感圧性接着剤に対する膨潤度が大きく、さらに加熱によって変形しやすい。 Also these sheet material, because it contains a low-density polyethylene resins, a large degree of swelling pressure sensitive adhesive of a liquid, easily deformed further by heating. このためこれらのシート材を有する感圧性接着シートの製造において、たとえば予め溶剤で希釈された液状の感圧性接着剤をシート材に直接塗布し乾燥することによって感圧性接着剤層を形成すると、感圧性接着剤の塗布時にシート材が膨潤を起こしてしまったり、あるいは乾燥時にシート材が収縮してしまう。 In the manufacture of this for a pressure-sensitive adhesive sheet having these sheet materials, for example to form a pressure-sensitive adhesive layer by pre-solvents in diluted the pressure sensitive adhesive of a liquid directly applied to the sheet material drying, sensitive or sheet material is gone cause swelling at the time of application of pressure sensitive adhesive, or sheet material at the time of drying may shrink. これによって感圧性接着シートが不所望に変形してしまうか、または変形しなかったとしても感圧性接着シートの剥離性が低下してしまう。 This would also decrease the peeling of the pressure-sensitive adhesive sheet as either a pressure-sensitive adhesive sheet is deformed undesirably, or not deformed. したがってこれらの感圧性接着シートは、支持基材の一表面に感圧性接着剤層を形成し、かつ剥離シート基材の一表面にシート材を形成した後、これらを感圧性接着剤層がシート材に接するように貼り合わせる方法で作製しなければならない。 Thus, these pressure-sensitive adhesive sheet on one surface of the supporting substrate to form a pressure-sensitive adhesive layer, and after forming the sheet material on one surface of the release sheet base material, these pressure-sensitive adhesive layer sheet It must manufactured by the method of bonding in contact with the wood. このような感圧性接着シートの作製方法は、液状の感圧性接着剤をシート材に直接塗布し乾燥させる方法と比較して製造効率が低く、またコストがかかる。 Such sensitive method for manufacturing the pressure sensitive adhesive sheet, a pressure-sensitive adhesive of the liquid sheet material to lower the production efficiency compared with the method of directly coating and drying, also costly.
【0009】 [0009]
【発明が解決しようとする課題】 [Problems that the Invention is to Solve
本発明は、上記の問題点を解決しようとするものであり、その目的は、液状の感圧性接着剤をシート材に直接塗布し乾燥することによって感圧性接着剤層を形成することができる感圧性接着シート用の剥離機能を有するシート材、ならびにそのシート材と感圧性接着剤層とを有しかつ感圧性接着剤層とシート材との間の剥離性にすぐれる感圧性接着シートを提供することである。 Sensitive present invention is intended to solve the above problems, and an object, which can form a pressure-sensitive adhesive layer by directly coating and drying the pressure-sensitive adhesive of the liquid to the sheet material sheet material having a release function for pressure sensitive adhesive sheet, as well as provide a pressure-sensitive adhesive sheet excellent in releasability between and pressure-sensitive adhesive layer and the sheet material has its sheet material and pressure-sensitive adhesive layer It is to be.
【0010】 [0010]
【課題を解決するための手段】 In order to solve the problems]
本発明者らは、上記課題を解決するため鋭意研究を行った結果、密度、メルトフローインデックスおよび結晶化度が特定の範囲内の物性値を示す直鎖状エチレン系共重合体を主として含有することによって、液状の感圧性接着剤をシート材に直接塗布し乾燥する方法で感圧性接着剤層を形成することができる感圧性接着シート用の剥離機能を有するシート材、ならびにそのシート材と感圧性接着剤層とを有しかつ感圧性接着剤層とシート材との間の剥離性にすぐれる感圧性接着シートが得られることを見出し、本発明を完成するに至った。 The present inventors have made intensive studies to solve the above problems, the density, melt flow index and degree of crystallinity containing mainly linear ethylene copolymer shows the physical properties of a specific range by, sheet material having a release function for a pressure-sensitive adhesive sheet the pressure-sensitive adhesive liquid capable of forming a pressure-sensitive adhesive layer in a method of directly coating and drying the sheet material and the sheet material and sensitive that It found that pressure-sensitive adhesive sheet excellent in releasability between and pressure-sensitive adhesive layer and a pressure sensitive adhesive layer and the sheet material is obtained, and have completed the present invention.
【0011】 [0011]
即ち、本発明は以下のとおりである。 That is, the present invention is as follows.
(1)単層または積層のシート材であって、単層の場合には当該シート材自体が、また積層の場合にはその少なくとも一方の最外層が、密度が0.910〜0.935g/cm 3 、メルトフローインデックスが15g/10min以下、かつ結晶化度が30〜60%である直鎖状エチレン系共重合体を主として含有することを特徴とする感圧性接着シート用の剥離機能を有するシート材。 (1) A sheet material of a single layer or stacked, in the case of a single layer is the sheet material itself, in the case of lamination is at least one of the outermost layers, density 0.910 to 0.935 g / cm 3, melt flow index 15 g / 10min or less, and having a release function for a pressure-sensitive adhesive sheet, wherein a degree of crystallinity mainly comprising linear ethylene copolymer is 30% to 60% sheet material.
(2)直鎖状エチレン系共重合体のメルトフローインデックスが0.1g/10min以上であることを特徴とする上記(1)記載のシート材。 (2) linear the melt flow index of the ethylene copolymer is characterized in that it is 0.1 g / 10min or more (1) sheet according.
(3)少なくとも感圧性接着剤層に接することを意図する側の表面の算術平均粗さが1.0μm以下であることを特徴とする上記(1)記載のシート材。 (3) at least the arithmetic average roughness of the pressure-sensitive adhesive layer intended to contact the side surface and wherein the at 1.0μm or less (1) sheet according.
(4)上記表面の算術平均粗さが0.01μm以上であることを特徴とする上記(3)記載のシート材。 (4) above (3) sheet material, wherein the arithmetic average roughness of the surface and wherein the at 0.01μm or more.
(5)前記直鎖状エチレン系共重合体は、プロピレン、1−ブテン、1−ヘキセン、4−メチル−1−ペンテンならびに1−オクテンのうちの少なくとも1種以上のコモノマーとエチレンとの共重合体であることを特徴とする上記(1)記載のシート材。 (5) the linear ethylene copolymer is propylene, 1-butene, 1-hexene, 4-methyl-1-copolymerizing with at least one or more comonomers and ethylene of pentene and 1-octene sheet material as described in (1) above, which is a polymer.
(6)上記(1)〜(5)のいずれかに記載のシート材と感圧性接着剤層とを有することを特徴とする感圧性接着シート。 (6) above (1) to (5) pressure-sensitive adhesive sheet characterized by having a sheet material and a pressure-sensitive adhesive layer according to any one of the.
【0012】 [0012]
【発明の実施の形態】 DETAILED DESCRIPTION OF THE INVENTION
以下、本発明を詳細に説明する。 The present invention will be described in detail.
本発明の感圧性接着シート用の剥離機能を有するシート材は、密度、メルトフローインデックスおよび結晶化度が下記の特定の範囲内の物性値を示す直鎖状エチレン系共重合体を主として含有する。 Sheet material having a release function for the pressure-sensitive adhesive sheet of the present invention, the density, melt flow index and degree of crystallinity mainly comprising linear ethylene copolymer shows the physical properties of the specific range described below .
【0013】 [0013]
前記直鎖状エチレン系共重合体は、JIS K−6760に規定されている測定方法によって測定される密度が0.910〜0.935g/cm 3であり、好ましくは0.915〜0.930g/cm 3である。 The linear ethylene copolymer is a density of 0.910 to 0.935 g / cm 3 as measured by the measuring method prescribed in JIS K-6760, preferably 0.915~0.930g a / cm 3. 密度が0.910g/cm 3未満である場合、液状の感圧性接着剤をシート材に直接塗布し乾燥して感圧性接着剤層を形成すると、感圧性接着剤の塗布時にシート材が膨潤を起こしてしまったり、あるいは乾燥時にシート材が収縮してしまうなどの問題がある。 If the density is less than 0.910 g / cm 3, when the pressure-sensitive adhesive liquid to form a pressure-sensitive adhesive layer was applied and dried directly on the sheet material, the sheet material when the pressure sensitive adhesive coating is a swelling or wake, or sheet material at the time of drying, there is a problem, such as shrinks. また密度が0.935g/cm 3を超える場合、剥離後の感圧性接着剤層の表面の形状がパルス状となったり、シート材と感圧性接着層との間が剥離しにくいなどというようにシート材の剥離性が低下する問題がある。 Also if the density exceeds 0.935 g / cm 3, it may become the shape of the surface of the pressure-sensitive adhesive layer after peeling a pulsed, between the sheet material and the pressure-sensitive adhesive layer so that such is not easily peeled off there is a problem of peeling of the sheet material is reduced.
【0014】 [0014]
前記直鎖状エチレン系共重合体は、JIS K−6760に規定されている測定方法によって測定されるメルトフローインデックスが15g/10min以下であり、好ましくは12g/10min以下である。 The linear ethylene copolymer has a melt flow index measured by the measuring method prescribed in JIS K-6760 is not more than 15 g / 10min, preferably not more than 12 g / 10min. またメルトフローインデックスの下限値は通常0.1g/10min以上、好ましくは0.2g/10min以上である。 The lower limit of the melt flow index is typically 0.1 g / 10min or more, preferably 0.2 g / 10min or more. メルトフローインデックスが15g/10minを超える場合、液状の感圧性接着剤をシート材に直接塗布すると、シート材が膨潤を起こしてしまう問題がある。 If the melt flow index is more than 15 g / 10min, when applied directly to pressure-sensitive adhesive of the liquid to the sheet material, there is a problem that the sheet material will undergo swelling.
【0015】 [0015]
また、さらに前記直鎖状エチレン系共重合体は、公知の方法である広角X線回折法によって測定される結晶化度が30〜60%、好ましくは35〜55%である。 Moreover, further the linear ethylene copolymer is 30% to 60% crystallinity as measured by wide angle X-ray diffraction method is a known method, preferably 35 to 55%. 結晶化度が30%未満である場合液状の感圧性接着剤をシート材に直接塗布すると、シート材が変形してしまう問題があり、60%を超える場合シート材の変形は起きないが、シート材の剥離性が低下する問題がある。 When the crystallinity is directly applying the pressure-sensitive adhesive liquid is less than 30% to the sheet material, there is a problem that the sheet material is deformed, but the deformation of the sheet material does not occur when it exceeds 60%, the sheet there is a problem of peeling of the wood is reduced.
【0016】 [0016]
本発明のシート材は、密度、メルトフローインデックスおよび結晶化度の各値がそれぞれ上述の範囲から選ばれる直鎖状エチレン系共重合体を用いているので、このシート材に液状の感圧性接着剤を直接塗布し乾燥することによって、感圧性接着剤層を形成することができる。 Sheet material of the present invention, the density, the values ​​of melt flow index and degree of crystallinity are used linear ethylene copolymer selected from the above range, respectively, pressure-sensitive adhesive liquid to the sheet material agent by direct application to be dried to form a pressure-sensitive adhesive layer. またこのようにして感圧性接着剤層を形成しても、シート材が不所望に変形したり剥離機能が低下してしまうことがなく、上述したシート材と感圧性接着剤層とを有する感圧性接着シートは、シート材と感圧性接着剤層との間において良好な剥離性を有する。 Also formed a pressure-sensitive adhesive layer in this manner, deformed or peeled functional sheet material undesirably have without lowered sensitive with the sheet material and the pressure-sensitive adhesive layer described above pressure sensitive adhesive sheet has good peelability between the sheet material and the pressure-sensitive adhesive layer.
【0017】 [0017]
直鎖状エチレン系共重合体の密度、メルトフローインデックスおよび結晶化度のうちの少なくともいずれかが上述の範囲を逸脱した場合、液状の感圧性接着剤の塗布によってシート材が膨潤したり、あるいは乾燥によってシート材が収縮したりしてしまう。 If the density of the linear ethylene copolymer has a melt flow of at least one of the index and crystallinity were departing from the scope of the above, or the sheet material is swollen by applying a pressure-sensitive adhesive liquid, or sheet material resulting in or contracted by the drying. これによって本発明のシート材を有する感圧性接着シートは、不所望に変形してしまうか、または変形しなかったとしても剥離性が著しく低下してしまう。 This pressure-sensitive adhesive sheet having a sheet material of the present invention, or deformed undesirably, or peelability as not to deform significantly decreases.
【0018】 [0018]
上述したように本発明のシート材は、液状の感圧性接着剤を直接塗布し乾燥することによって感圧性接着剤層を形成することができる。 Sheet material of the present invention as described above, can form a pressure-sensitive adhesive layer by coating and drying the pressure-sensitive adhesive liquid directly. したがって低密度ポリエチレン樹脂を含有する従来のシート材と異なり、予め支持基材の表面に形成した感圧性接着剤層をシート材に接するように貼り合わせて作製しなくてもよい。 Therefore unlike the conventional sheet materials containing low density polyethylene resin, it is not manufactured by bonding the pressure-sensitive adhesive layer formed on the surface of the pre-supporting substrate in contact with the sheet material. これによって従来と比較して、高い製造効率でかつ低いコストで感圧性接着シートを製造することができる。 This compared with conventional, it is possible to produce a pressure-sensitive adhesive sheet with a high production efficiency and low cost.
【0019】 [0019]
また本発明のシート材は、少なくとも感圧性接着剤層に接することを意図する側の表面の算術平均粗さ(Ra)が1.0μm以下、好ましくは0.7μm以下、より好ましくは0.5μm以下である。 The sheet material of the present invention has an arithmetic average roughness of the side surface intended to contact at least a pressure-sensitive adhesive layer (Ra) is 1.0μm or less, preferably 0.7μm or less, more preferably 0.5μm less. このような算術平均粗さは、JIS B−0601に規定されている測定方法によって測定される。 Such arithmetic average roughness is measured by a measuring method defined in JIS B-0601. 前記算術平均粗さが1.0μmを超えると、剥離性が低下してしまい、剥離時に感圧性接着シートが伸びたり、あるいは剥離後の感圧性接着剤層の表面形状が荒れたりしてしまう。 Wherein the arithmetic average roughness exceeds 1.0 .mu.m, it will peelability decreases, or elongation pressure-sensitive adhesive sheet, or the surface shape of the pressure-sensitive adhesive layer after peeling would or rough at the time of peeling. また前記算術平均粗さは、好ましくは0.01μm以上であり、より好ましくは0.03μm以上であり、特に好ましくは0.05μm以上である。 Also, the arithmetic mean roughness is preferably 0.01μm, more preferably at least 0.03 .mu.m, particularly preferably 0.05μm or more.
【0020】 [0020]
上述のように、本発明のシート材は、前記算術平均粗さが特定の範囲内に選ばれる。 As described above, the sheet material of the present invention, the arithmetic average roughness is chosen within the specified range. これによって本発明のシート材と感圧性接着剤層とを有する感圧性接着シートは、剥離時にシート材が伸びたりあるいは剥離後の感圧性接着剤層の表面形状が荒れたりしてしまうことがなく、シート材と感圧性接着剤層との間の剥離性を良好に保つことができる。 This pressure-sensitive adhesive sheet having a sheet member and the pressure-sensitive adhesive layer of the present invention, without the surface shape of the stretch sheet material or alternatively the pressure-sensitive adhesive layer after peeling ends up or rough at the time of peeling , it is possible to maintain the releasability between the sheet material and the pressure-sensitive adhesive layer satisfactorily. したがって前記感圧性接着シートは、剥離時において接着剤がシート材に付着しにくく、かつシート材に含有される物質が感圧性接着剤層に付着しにくい。 Thus the pressure-sensitive adhesive sheet does not easily adhesive adheres to the sheet material at the time of peeling, and substance contained in the sheet material is less likely to adhere to the pressure-sensitive adhesive layer. これによって剥離後の感圧性接着剤層の表面の粗さを小さくすることができ、感圧性接着剤層は本来備えている接着強さを充分に発揮することができる。 This makes it possible to reduce the roughness of the surface of the pressure-sensitive adhesive layer after peeling, the pressure-sensitive adhesive layer can be sufficiently exhibited an adhesive strength that originally provided.
【0021】 [0021]
またさらに本発明のシート材に主として含有される直鎖状エチレン系共重合体は、プロピレン、1−ブテン、1−ヘキセン、4−メチル−1−ペンテンならびに1−オクテンのうちの少なくとも1種以上のコモノマーとエチレンとの共重合体であり、好ましくはエチレン−1−ヘキセン共重合体またはエチレン−1−オクテン共重合体である。 The linear ethylene-based copolymer contained predominantly further sheet material of the present invention, propylene, 1-butene, 1-hexene, 4-methyl-1 at least one or more of pentene and 1-octene a copolymer of comonomer and ethylene, preferably ethylene-1-hexene copolymer or an ethylene-1-octene copolymer. このような直鎖状エチレン系共重合体は、公知の方法によって共重合の条件、精製の条件、および分別の条件を適宜選択すれば容易に得ることが可能である。 Such linear ethylene-based copolymer may be obtained easily be properly selected conditions copolymerization conditions purification, and fractionation conditions by known methods. また、市販品を試験して、本発明で特定する特性を有する直鎖状エチレン系共重合体を選択することによって得ることができる。 Also be obtained by selecting a linear ethylene copolymer having the characteristics tested commercial products, specified in the present invention.
【0022】 [0022]
本発明のシート材は、上述したような特定の範囲内の物性値を有する直鎖状エチレン系共重合体からなっていてもよく、また必要に応じて他の樹脂成分または添加物を含有する混合物であってもよい。 Sheet material of the present invention, contain other resin components or additives optionally may consist linear ethylene copolymer having the following physical properties within a specific range as described above, also requires it may be a mixture. ただし前記樹脂成分または添加物は、前記直鎖状エチレン系共重合体によってシート材に付加された剥離機能、成膜性、耐溶剤性および耐熱性を損なわない範囲の量で含有される。 However the resin component or additive, the appended release function to the sheet material by a linear ethylene copolymer, the film forming property is contained in an amount range that does not impair the solvent resistance and heat resistance.
【0023】 [0023]
このようなシート材は、前記直鎖状エチレン系共重合体またはその混合物を押出し成形法などの公知の成形法によってシート状に成形した剥離シートとすることによって作製される。 Such sheet material is produced by a release sheet which is formed into a sheet by a known molding method such as extrusion molding the linear ethylene copolymer or a mixture thereof. このような剥離シートの厚みは、その用途などに応じて適宜選択することができ、たとえば30〜300μm程度に選ばれる。 The thickness of such a release sheet may be appropriately selected depending on its use, for example, it is selected to about 30 to 300 [mu] m.
単層のシート材はかかる剥離シートをそのまま使用すればよい。 Sheet material of a single layer may be used as such a release sheet.
【0024】 [0024]
また本発明のシート材は、剥離シート基材の少なくとも片側に前記直鎖状エチレン系共重合体またはその混合物が積層される積層のシート材であってもよい。 The sheet material of the present invention, at least the one side linear ethylene copolymer or a mixture of the release sheet substrate may be a sheet material stacking to be laminated. このような直鎖状エチレン系共重合体またはその混合物と剥離シート基材との積層のシート材は、前記直鎖状エチレン系共重合体またはその混合物を押出しラミネーション、ドライラミネーション、ウェットラミネーションまたはホットメルトラミネーションなどの公知の積層法によって剥離シート基材の少なくとも片側に積層する。 Such linear ethylene copolymer or a sheet material laminated with its mixture with the release sheet base material, the linear ethylene copolymer or a mixture extrusion lamination, dry lamination, wet lamination or hot by a known lamination method such as melt lamination is laminated on at least one side of the release sheet substrate. このような積層のシート材の厚みは、その用途などに応じて適宜選択することができ、たとえば30〜300μm程度に選ばれる。 Such a thickness of the sheet material of the stack may be appropriately selected depending on its use, for example, it is selected to about 30 to 300 [mu] m.
【0025】 [0025]
前記剥離シート基材としては、プラスティックフィルム、金属箔または紙などが用いられる。 Examples of the release sheet base material, plastic film, metal foil or paper is used. プラスティックフィルムとしては、具体的には、高密度ポリエチレン、低密度ポリエチレン、直鎖状低密度ポリエチレン、ポリエステル、ポリプロピレン、ポリ−4−メチル−1−ペンテン、ポリスチレンまたはポリ塩化ビニルが挙げられる。 The plastic film, in particular, high density polyethylene, low density polyethylene, linear low density polyethylene, polyester, polypropylene, poly-4-methyl-1-pentene, polystyrenes or polyvinyl chloride. また前記金属箔としては、具体的には、アルミ箔またはステンレス箔が挙げられる。 Examples of the metal foil, and specific examples thereof include aluminum foil or stainless steel foil. 前記紙としては、具体的には、和紙、クラフト紙、上質紙またはクレープ紙が挙げられる。 As the paper, specifically, Japanese paper, kraft paper, and a high-quality paper or crepe paper.
【0026】 [0026]
本発明のシート材を有する感圧性接着シートが含有する感圧性接着剤層は、前記剥離シートの一表面または前記積層のシート材に溶剤系、エマルジョン系またはホットメルト系の感圧性接着剤を塗布し、乾燥することによって形成される。 Pressure-sensitive adhesive layer containing the pressure-sensitive adhesive sheet having a sheet material of the present invention is applied, one surface or solvent-based sheet material of the stack of the release sheet, the pressure-sensitive adhesive of the emulsion type or hot melt type and it is formed by drying.
感圧性接着剤層は、その厚みが1〜70μm、好ましくは20〜50μmとなるように形成される。 Pressure-sensitive adhesive layer has a thickness 1~70Myuemu, it is preferably formed to be 20 to 50 m.
【0027】 [0027]
このような感圧性接着剤層を形成するための感圧性接着剤としては特に限定されないが、好ましい一例としてポリアクリル酸エステルおよび/またはポリメタクリル酸エステルを含有するポリアクリル酸エステル系感圧性接着剤が挙げられる。 Such is not particularly restricted but includes pressure-sensitive adhesive layer a pressure sensitive adhesive for forming a polyacrylate pressure-sensitive adhesive containing a polyacrylic acid ester and / or polymethacrylic acid ester as a preferable example and the like. ポリアクリル酸エステル系感圧性接着剤は、溶液重合法またはエマルジョン重合法などの当業者が通常用いる重合法によって得られるアクリル系ポリマーを主剤とする。 Polyacrylate pressure-sensitive adhesives, those skilled in the art, such as solution polymerization or emulsion polymerization is a main agent of an acrylic polymer obtained by polymerization using normal. 前記アクリル系ポリマーは、ブチルアクリレート、2−エチルヘキシルアクリレートなどのアルキルアクリレート、あるいはブチルメタクリレート、2−エチルヘキシルメタクリレートなどのアルキルメタクリレートを主成分とする。 The acrylic polymer, butyl acrylate, alkyl acrylates such as 2-ethylhexyl acrylate or butyl methacrylate, as a main component an alkyl methacrylate such as 2-ethylhexyl methacrylate. このようなアクリル系ポリマーを得るための重合において、好ましくは、トルエン、酢酸エチルなどの溶媒が用いられ、ベンゾイルパーオキサイド、アゾビスイソブチロニトリルなどの重合開始剤が用いられる。 In the polymerization for obtaining such acrylic polymer, preferably, toluene, a solvent is used, such as ethyl acetate, benzoyl peroxide, a polymerization initiator such as azobisisobutyronitrile it is used. このようなアクリル系ポリマーは、重量平均分子量が好ましくは15万〜100万、より好ましくは25万〜80万のものが用いられる。 Such acrylic polymer has a weight average molecular weight of preferably 150,000 to 1,000,000, more preferably used are those from 250,000 to 800,000.
【0028】 [0028]
前記ポリアクリル酸エステル系接着剤は、このようなアクリル系ポリマーに、必要に応じて各種の添加剤を加えて調製される。 The polyacrylate adhesive, in such acrylic polymers are prepared by adding various additives as necessary. このような添加剤としては、架橋剤、粘着付与剤、軟化剤、老化防止剤、充填剤などが挙げられる。 Examples of such additives include crosslinking agents, tackifiers, softening agents, anti-aging agents, and fillers.
【0029】 [0029]
また前記アクリル系ポリマーは、必要に応じてアルキルアクリレートまたはアルキルメタクリレートに、2−ヒドロキシエチルアクリレート、2−ヒドロキシエチルメタクリレート、アクリル酸、メタクリル酸、スチレンおよび酢酸ビニルの内の少なくともいずれかのモノマーを共重合可能な改質用モノマーとして加えたモノマー混合物の共重合体であってもよい。 Also, the acrylic polymer, the alkyl acrylates or alkyl methacrylates as necessary, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, acrylic acid, methacrylic acid, co at least one of the monomers of styrene and vinyl acetate may be a copolymer of a monomer mixture was added as a monomer for polymerizable modification. この共重合において、好ましくは、トルエン、酢酸エチルなどの溶媒が用いられ、ベンゾイルパーオキサイド、アゾビスイソブチロニトリルなどの重合開始剤が用いられる。 In this copolymerization, preferably, toluene, a solvent is used, such as ethyl acetate, benzoyl peroxide, a polymerization initiator such as azobisisobutyronitrile is used. このような共重合体のアクリル系ポリマーから調整されるポリアクリル酸エステル系感圧性接着剤を感圧性接着剤層の形成に用いることによって、シート材と感圧性接着剤層との間の剥離性を更に向上することができる。 By using such a copolymer polyacrylate pressure-sensitive adhesives prepared from acrylic polymers for the formation of the pressure-sensitive adhesive layer, peeling property between the sheet material and the pressure-sensitive adhesive layer it can be further improved.
【0030】 [0030]
またポリアクリル酸エステル系感圧性接着剤以外で、感圧性接着剤層の形成に好適な感圧性接着剤としては、ポリエステル系感圧性接着剤が挙げられる。 In addition polyacrylate pressure-sensitive adhesives, as pressure-sensitive adhesives suitable for forming pressure sensitive adhesive layer, a polyester-based pressure-sensitive adhesive. 中でも特に、脂肪族系ポリカーボネートジオールをポリオールの成分として有するポリエステル系感圧性接着剤が好ましい。 Inter alia, polyester pressure-sensitive adhesives having aliphatic polycarbonate diol as a component of the polyol is preferred. 脂肪族系ポリカーボネートジオールとは、下記式【0031】 The aliphatic polycarbonate diol, the following formula [0031]
【化1】 [Formula 1]

【0032】 [0032]
〔式中、Rは炭素数2〜20の直鎖状または分枝鎖状の炭化水素基である。 [Wherein, R is a straight-chain or branched hydrocarbon group having 2 to 20 carbon atoms. 〕で示される繰返し単位を有する脂肪族系ポリカーボネート構造を有するジオールである。 A diol having aliphatic polycarbonate structure having a repeating unit represented by]. このようなジオールは、たとえばブタンジオールなどのジオール成分とエチレンカーボネートなどのカーボネート化合物との反応によって得られる。 Such diols are for example obtained by reaction of a carbonate compound such as a diol component and ethylene carbonate, such as butanediol. 前記ポリエステル系重合体は、重量平均分子量が好ましくは1万以上、より好ましくは3万以上(通常30万以下)のものが用いられる。 The polyester-based polymer has a weight average molecular weight of preferably 10,000 or more, more preferably one having 30,000 or more (usually 300,000 or less) is used.
【0033】 [0033]
上述の脂肪族系ポリカーボネートジオール以外の好適な前記ポリオール成分としては、エチレングリコール、プロピレングリコール、ブタンジオール、ヘキサンジオール、オクタンジオール、デカンジオールまたはオクタデカンジオールなどの直鎖状のジオール成分などが挙げられる。 Suitable the polyol component other than the aliphatic polycarbonate diols described above, ethylene glycol, propylene glycol, butanediol, hexanediol, octanediol, etc. linear diol component such as decanediol or octadecane diol. このようなジオール成分と反応させる多塩基性酸成分は、炭素数が2〜20個の脂肪族または脂環族の炭化水素基を分子骨格としたものが好ましい。 Such polybasic acid component to be reacted with the diol component is preferably one carbon atoms and from 2 to 20 aliphatic or alicyclic hydrocarbon group as the molecular skeleton. 前記脂肪族炭化水素基は直鎖状であってもよく、また分枝鎖状であってもよい。 The aliphatic hydrocarbon groups may be may be linear, also branched. このような多塩基性酸成分として、具体的には、マロン酸、コハク酸、メチルコハク酸、アジピン酸、セバシン酸、1,2−ドデカン二酸、1,14−テトラデカン二酸、n−ヘキシルアジピン酸、テトラヒドロフタル酸またはエンドメチレンテトラヒドロフタル酸、あるいはそれらの酸無水物またはエステルなどの誘導体が用いられる。 Such polybasic acid component such as malonic acid, succinic acid, methyl succinic acid, adipic acid, sebacic acid, 1,2-dodecanedioic acid, 1,14-tetradecane diacid, n- hexyl adipate acid, tetrahydrophthalic acid or endomethylene tetrahydrophthalic acid or derivatives such as their anhydrides or esters, are used.
【0034】 [0034]
前記脂肪族系カーボネートジオールをポリオールの成分として有するポリエステル系感圧性接着剤は、上述したような脂肪族系ポリカーボネート構造を有するジオールに、必要に応じて各種の添加剤を加えて調製される。 The polyester-based pressure sensitive adhesive having a aliphatic carbonate diol as a component of the polyol, the diol having an aliphatic polycarbonate structure as described above, are prepared by adding various additives as necessary. このような添加剤としては、架橋剤、粘着付与剤、軟化剤、老化防止剤、充填剤などが挙げられる。 Examples of such additives include crosslinking agents, tackifiers, softening agents, anti-aging agents, and fillers.
【0035】 [0035]
上述した感圧性接着剤層の形成に好適な感圧性接着剤は、その調製過程でいかなる形態をも取り得るけれども、溶剤系、エマルジョン系およびホットメルト系のうちのいずれかの形態で用いられるのが取り扱いの上で好ましい。 The pressure sensitive adhesive suitable for forming pressure sensitive adhesive layer described above, although may take any form in the preparation process, the solvent system used either in the form of an emulsion system and hot-melt There preferable in terms of handling. また上述した感圧性接着剤は、本発明の範囲を逸脱しない限り、あるいは感圧性接着剤としての接着性を損なわないならば単独で用いてもよく、また従来からの公知の混合方法または撹拌方法によって混合物として用いてもよい。 The pressure-sensitive adhesive described above, unless departing from the scope of the present invention, or if not impair the adhesiveness of the pressure-sensitive adhesive may be used singly, known mixing methods or agitation conventional methods it may be used as a mixture with.
【0036】 [0036]
また本発明のシート材と感圧性接着剤層とを有する感圧性接着シートは、好ましくは、前記感圧性接着剤層のシート材に接する側とは反対側に接する支持基材を備える。 The pressure-sensitive adhesive sheet having a sheet member and the pressure-sensitive adhesive layer of the present invention preferably comprises a supporting substrate in contact with the opposite side to the side in contact with the sheet material of the pressure-sensitive adhesive layer. 支持基材は、その厚みが30〜300μm、好ましくは50〜200μmに選ばれる。 Supporting substrate has a thickness of 30 to 300 [mu] m, it is preferably selected to 50 to 200 [mu] m. 支持基材としては、プラスティックフィルム、金属箔または紙などが用いられる。 As the supporting substrate, plastic film, metal foil or paper is used. プラスティックフィルムとしては、具体的には、高密度ポリエチレン、低密度ポリエチレン、直鎖状低密度ポリエチレン、ポリエステル、ポリプロピレン、ポリ−4−メチル−1−ペンテン、ポリスチレンまたはポリ塩化ビニルが挙げられる。 The plastic film, in particular, high density polyethylene, low density polyethylene, linear low density polyethylene, polyester, polypropylene, poly-4-methyl-1-pentene, polystyrenes or polyvinyl chloride. また前記金属箔としては、具体的には、アルミ箔またはステンレス箔が挙げられる。 Examples of the metal foil, and specific examples thereof include aluminum foil or stainless steel foil. 前記紙としては、具体的には、和紙、クラフト紙、上質紙またはクレープ紙が挙げられる。 As the paper, specifically, Japanese paper, kraft paper, and a high-quality paper or crepe paper.
【0037】 [0037]
上述のように本発明のシート材を有する感圧性接着シートは、シート材に感圧性接着剤を直接塗布し乾燥することによって感圧性接着剤層を形成することができるので、シート材に感圧性接着剤層を積層した後、感圧性接着剤層のシート材に接する側とは反対側に接するように支持基材を貼り合わせて設けることができる。 Pressure-sensitive adhesive sheet having a sheet material of the present invention as described above, it is possible to form a pressure-sensitive adhesive layer by directly coating and drying the pressure sensitive adhesive sheet, pressure sensitive sheet material after the adhesive layer is laminated, the side in contact with the sheet material of the pressure-sensitive adhesive layer can be provided by bonding a supporting substrate in contact with the opposite side. したがって本発明では支持基材の材料として熱に弱い材料でも用いることができ、従来のシート材と比較して支持基材の材料の選択範囲を広くすることができる。 Accordingly the present invention also can be used in a sensitive material to heat as the material of the supporting substrate, in comparison with the conventional sheet widening the selection range of the material of the supporting substrate.
【0038】 [0038]
また本発明のシート材を有する感圧性接着シートは、従来と同様に公知の方法によって、支持基材の一表面に感圧性接着剤層を形成し、かつシート材を形成した後、これらを感圧性接着剤層とシート材とが接するように貼り合わせて製造してもよい。 The pressure-sensitive adhesive sheet having a sheet material of the present invention, by methods known in a conventional manner on one surface of the supporting substrate to form a pressure-sensitive adhesive layer, and after forming the sheet material, sensitive to these may be prepared by bonding to the pressure sensitive adhesive layer and the sheet material is in contact.
【0039】 [0039]
また本発明のシート材を有する感圧性接着シートは、支持基材の両面に感圧性接着剤層とシート材との積層構造を備える両面の感圧性接着シートであってもよい。 The pressure-sensitive adhesive sheet having a sheet material of the present invention, on both sides of the supporting substrate may be a double-sided pressure-sensitive adhesive sheet comprising a laminated structure of a pressure-sensitive adhesive layer and the sheet material. 換言すると、支持基材の両面にそれぞれ接する各感圧性接着剤層と、各感圧性接着剤層にそれぞれ接する単層または積層のシート材とを備えてもよい。 In other words, each pressure-sensitive adhesive layer in contact with the both surfaces of the supporting substrate may be a sheet material of a single layer or a laminate in contact with the respective pressure-sensitive adhesive layer.
【0040】 [0040]
また本発明の感圧性接着シートは、たとえば支持基材の一方の表面に感圧性接着剤層が接し、かつ支持基材の他方の表面(背面)に前記剥離シートの一表面または前記積層体のシート材が接するような構造であってもよい。 The pressure-sensitive adhesive sheet of the present invention, for example against one pressure-sensitive adhesive layer on the surface of the supporting substrate, and the other of the supporting substrate surface (back surface) on one surface or the laminate of the release sheet it may have a structure such as the sheet material is in contact. これによって自背面との剥離性にすぐれる感圧性接着シートを製造することができる。 This makes it possible to produce a pressure-sensitive adhesive sheet excellent in releasability between the own back.
【0041】 [0041]
上述した本発明のシート材を有する感圧性接着シートの各形態は、感圧性接着テープにおいても好適である。 Each form of pressure-sensitive adhesive sheet having a sheet material of the present invention described above is also suitable in the pressure-sensitive adhesive tape. すなわち本発明のシート材を有する感圧性接着テープは、両面の感圧性接着テープであってもよく、また自背面との剥離性にすぐれる感圧性接着テープであってもよい。 That pressure-sensitive adhesive tape having a sheet material of the present invention may be a double-sided pressure-sensitive adhesive tape, or may be a pressure-sensitive adhesive tape excellent in peeling property from a self back.
【0042】 [0042]
【実施例】 【Example】
以下に実施例を挙げて本発明をさらに詳細に説明するが、これらは単なる例示であり、本発明は、これらにより何ら限定されるものではない。 Although described in Example to the present invention further detail by way of the following, these are merely illustrative, the present invention is not intended to be limited thereto.
【0043】 [0043]
実施例1 Example 1
密度0.919g/cm 3 、メルトフローインデックス2.0g/10minのエチレン−1−ヘキセン共重合体である直鎖状低密度ポリエチレン樹脂(日本ポリオレフィン社製、ジェイレクス LL AC−404A)を、40φ1軸混練り押出機を用いて200℃の押出し温度で押出成形を行い、厚みが100μmの剥離シートを単層のシート材として作製した。 Density 0.919 g / cm 3, melt flow index 2.0 g / 10min of the ethylene-1-hexene copolymer and a linear low density polyethylene resin (Nippon Polyolefin Co., Jeirekusu LL AC-404A) and, 40Fai1 axis performed extruded at 200 ° C. extrusion temperature using kneading extruder, a thickness to prepare a 100μm release sheet as a sheet material of a single layer. X線発生装置(理学電機工業社製、RU−200B)を用い広角X線回折法によって、この剥離シートの結晶化度を算出したところ、45.2%であった。 X-ray generator (Rigaku Kogyo Co., Ltd., RU-200B) by wide angle X-ray diffraction method using, calculation of crystallinity of the release sheet was 45.2%. また前記剥離シートの表面の算術平均粗さは、0.18μmであった。 The arithmetic average roughness of the surface of the release sheet was 0.18 .mu.m.
またn−ブチルアクリレート100重量部およびアクリル酸5重量部を、トルエンを溶媒として、当業者が通常用いる方法によって重合させた。 The addition n- butyl acrylate 100 parts by weight 5 parts by weight of acrylic acid, toluene as the solvent, those skilled in the art were polymerized by a method ordinarily used. 重合開始剤としては、ベンゾイルパーオキサイドを用いた。 As the polymerization initiator, it was used benzoyl peroxide. このような重合反応によって、重量平均分子量が50万のアクリル系ポリマーの溶液(固形分:30%)を得た。 Such polymerization reactions, weight average molecular weight of 500,000 of acrylic polymer solution (solid content: 30%). このようなアクリル系ポリマーに、アクリル系ポリマー100重量部あたりメラミン系架橋剤を1.5重量部、イソシアネート系架橋剤を3重量部配合して、ポリアクリル酸エステル系感圧性接着剤を調製した。 Such acrylic polymers, 1.5 parts by weight of acrylic polymer 100 parts by weight per melamine crosslinking agent, by blending 3 parts by weight of isocyanate crosslinking agent to prepare a polyacrylate pressure-sensitive adhesive .
このポリアクリル酸エステル系感圧性接着剤を、乾燥後の厚みが30μmになるように上述のように作製した剥離シート上に塗布し、120℃で3分間乾燥して、感圧性接着剤層を形成した。 The polyacrylate pressure-sensitive adhesive to a thickness after drying on a release sheet prepared as described above so that the 30 [mu] m, and dried for 3 minutes at 120 ° C., a pressure-sensitive adhesive layer the formed. 前記感圧性接着剤層に、支持基材として厚みが25μmのポリエステルフィルムを貼り合わせることによって、感圧性接着シートを作製した。 The pressure-sensitive adhesive layer, the thickness as the supporting base material by laminating the polyester film of 25 [mu] m, to prepare a pressure-sensitive adhesive sheet.
【0044】 [0044]
実施例2 Example 2
実施例1と同様に調製したポリアクリル酸エステル系感圧性接着剤を、乾燥後の厚みが30μmとなるように、厚み25μmのポリエステルフィルムの一表面上に塗布し、120℃で3分間乾燥して、感圧性接着剤層を形成した。 The polyacrylate pressure-sensitive adhesive was prepared as in Example 1, so that the thickness after drying became 30 [mu] m, was applied onto one surface of a polyester film having a thickness of 25 [mu] m, and dried for 3 minutes at 120 ° C. Te, to form a pressure-sensitive adhesive layer. このように形成した感圧性接着剤層に接するように実施例1と同様に作製した剥離シートを貼り合わせることによって、感圧性接着シートを作製した。 By attaching the release sheet was prepared in the same manner as in Example 1 so as to contact the so-formed pressure-sensitive adhesive layer to prepare a pressure-sensitive adhesive sheet.
【0045】 [0045]
実施例3 Example 3
直鎖状エチレン系共重合体として、密度が0.925g/cm 3 、メルトフローインデックスが3.5g/10minのエチレン−1−ヘキセン共重合体(日本ポリオレフィン社製、ハーモレックス LL NC−479A)を用いた以外は実施例1と同様にして感圧性接着シートを作製した。 As the linear ethylene copolymer, a density of 0.925 g / cm 3, melt flow index ethylene-1-hexene copolymer 3.5 g / 10min (Nippon Polyolefin Co., harmonization Rex LL NC-479A) to prepare a pressure-sensitive adhesive sheet in the same manner as in example 1 except for using. このエチレン−1−ヘキセン共重合体の結晶化度を算出したところ、46.1%であった。 Was calculated crystallinity of the ethylene-1-hexene copolymer was 46.1%. またこの剥離シートの表面の算術平均粗さは、0.12μmであった。 The arithmetic average roughness of the surface of the release sheet was 0.12 .mu.m.
【0046】 [0046]
実施例4 Example 4
直鎖状エチレン系共重合体として、密度が0.919g/cm 3 、メルトフローインデックスが2.3g/10minのエチレン−1−オクテン共重合体(ダウケミカル社製、ダウレックス 2047AC)を用いた以外は実施例1と同様にして感圧性接着シートを作製した。 As the linear ethylene copolymer, density 0.919 g / cm 3, melt flow index was used ethylene-1-octene copolymer of 2.3 g / 10min (the Dow Chemical Co., Dow Rex 2047AC) except to prepare a pressure-sensitive adhesive sheet in the same manner as in example 1. このエチレン−1−オクテン共重合体の結晶化度を算出したところ、41.5%であった。 Was calculated crystallinity of the ethylene-1-octene copolymer was 41.5%. またこの剥離シートの表面の算術平均粗さは、0.21μmであった。 The arithmetic average roughness of the surface of the release sheet was 0.21 [mu] m.
【0047】 [0047]
実施例5 Example 5
直鎖状エチレン系共重合体として、密度が0.920g/cm 3 、メルトフローインデックスが4.0g/10minのエチレン−1−ヘキセン共重合体(三井化学社製、エボリュー SP2040)を用いた以外は実施例2と同様にして感圧性接着シートを作製した。 As the linear ethylene copolymer, density 0.920 g / cm 3, except that the melt flow index is used ethylene-1-hexene copolymer 4.0 g / 10min (manufactured by Mitsui Chemicals, Inc., EVOLUE SP2040) and to prepare a pressure-sensitive adhesive sheet in the same manner as in example 2. このエチレン−1−ヘキセン共重合体の結晶化度を算出したところ、39.1%であった。 Was calculated crystallinity of the ethylene-1-hexene copolymer was 39.1%. またこの剥離シートの表面の算術平均粗さは、0.13μmであった。 The arithmetic average roughness of the surface of the release sheet was 0.13 [mu] m.
【0048】 [0048]
実施例6 Example 6
直鎖状エチレン系共重合体として、密度が0.912g/cm 3 、メルトフローインデックスが3.5g/10minのエチレン−1−ヘキセン共重合体(日本ポリオレフィン社製、ハーモレックス LL NC−544A)を用いた以外は実施例1と同様にして感圧性接着シートを作製した。 As the linear ethylene copolymer, density 0.912 g / cm 3, melt flow index ethylene-1-hexene copolymer 3.5 g / 10min (Nippon Polyolefin Co., harmonization Rex LL NC-544A) to prepare a pressure-sensitive adhesive sheet in the same manner as in example 1 except for using. このエチレン−1−ヘキセン共重合体の結晶化度を算出したところ、36.4%であった。 Was calculated crystallinity of the ethylene-1-hexene copolymer was 36.4%. またこの剥離シートの表面の算術平均粗さは、0.33μmであった。 The arithmetic average roughness of the surface of the release sheet was 0.33 .mu.m.
【0049】 [0049]
実施例7 Example 7
直鎖状エチレン系共重合体として、密度が0.912g/cm 3 、メルトフローインデックスが10.0g/10minのエチレン−1−ヘキセン共重合体(日本ポリオレフィン社製、ハーモレックス LL NH−744A)を用いた以外は実施例1と同様にして感圧性接着シートを作製した。 As the linear ethylene copolymer, density 0.912 g / cm 3, melt flow index ethylene-1-hexene copolymer 10.0 g / 10min (Nippon Polyolefin Co., harmonization Rex LL NH-744A) to prepare a pressure-sensitive adhesive sheet in the same manner as in example 1 except for using. このエチレン−1−ヘキセン共重合体の結晶化度を算出したところ、33.2%であった。 Was calculated crystallinity of the ethylene-1-hexene copolymer was 33.2%. またこの剥離シートの表面の算術平均粗さは、0.42μmであった。 The arithmetic average roughness of the surface of the release sheet was 0.42 .mu.m.
【0050】 [0050]
実施例8 Example 8
直鎖状エチレン系共重合体として、密度が0.935g/cm 3 、メルトフローインデックスが3.5g/10minのエチレン−1−ヘキセン共重合体(日本ポリオレフィン社製、ハーモレックス LL NC−499A)を用いた以外は実施例1と同様にして感圧性接着シートを作製した。 As the linear ethylene copolymer, density 0.935 g / cm 3, melt flow index ethylene-1-hexene copolymer 3.5 g / 10min (Nippon Polyolefin Co., harmonization Rex LL NC-499A) to prepare a pressure-sensitive adhesive sheet in the same manner as in example 1 except for using. このエチレン−1−ヘキセン共重合体の結晶化度を算出したところ、53.8%であった。 Was calculated crystallinity of the ethylene-1-hexene copolymer was 53.8%. またこの剥離シートの表面の算術平均粗さは、0.38μmであった。 The arithmetic average roughness of the surface of the release sheet was 0.38 .mu.m.
【0051】 [0051]
実施例9 Example 9
直鎖状エチレン系共重合体として、密度が0.921g/cm 3 、メルトフローインデックスが0.5g/10minのエチレン−(4−メチル−1−ペンテン)−(1−ブテン)共重合体(三井化学社製、ウルトゼックス 2005H)を用いた以外は実施例1と同様にして感圧性接着シートを作製した。 As the linear ethylene copolymer, density 0.921 g / cm 3, a melt flow index of 0.5 g / 10min ethylene - (4-methyl-1-pentene) - (1-butene) copolymer ( manufactured by Mitsui Chemicals, Inc., to prepare a pressure-sensitive adhesive sheet except that a ULTZEX 2005H) in the same manner as in example 1. このエチレン−(4−メチル−1−ペンテン)−(1−ブテン)共重合体の結晶化度を算出したところ、46.4%であった。 The ethylene - (4-methyl-1-pentene) - (1-butene) was calculated crystallinity of the copolymer was 46.4%. またこの剥離シートの表面の算術平均粗さは、0.29μmであった。 The arithmetic average roughness of the surface of the release sheet was 0.29 .mu.m.
【0052】 [0052]
比較例1 Comparative Example 1
直鎖状エチレン系共重合体として、密度が0.902g/cm、メルトフローインデックスが3.0g/10minのエチレン−1−オクテン共重合体(ダウケミカル社製、アフィニティー PL1850)を用いた以外は実施例1と同様にして感圧性接着シートを作製した。 As the linear ethylene copolymer, except that the density was used 0.902 g / cm, ethylene-1-octene copolymer of melt flow index 3.0 g / 10min (Dow Chemical Co., affinity PL1850) to the to prepare a pressure-sensitive adhesive sheet in the same manner as in example 1. このエチレン−1−オクテン共重合体の結晶化度を測定したところ、28.6%であった。 The measured crystallinity of the ethylene-1-octene copolymer was 28.6%.
【0053】 [0053]
比較例2 Comparative Example 2
直鎖状エチレン系共重合体として、密度が0.905g/cm 3 、メルトフローインデックスが3.5g/10minのエチレン−1−ヘキセン共重合体(日本ポリオレフィン社製、ハーモレックス LL NC524A)を用いた以外は実施例1と同様にして感圧性接着シートを作製した。 Use a linear ethylene-based copolymer, a density of 0.905 g / cm 3, ethylene-1-hexene copolymer melt flow index 3.5 g / 10min (Nippon Polyolefin Co., harmonization Rex LL NC524A) a except that had was prepared a pressure-sensitive adhesive sheet in the same manner as in example 1. このエチレン−1−ヘキセン共重合体の結晶化度を測定したところ、31.1%であった。 The measured crystallinity of the ethylene-1-hexene copolymer was 31.1%.
【0054】 [0054]
比較例3 Comparative Example 3
直鎖状エチレン系共重合体として、密度が0.940g/cm 3 、メルトフローインデックスが1.0g/10minのエチレン−1−オクテン共重合体(ダウケミカル社製、ダウレックス 2740E)を用いた以外は実施例2と同様にして感圧性接着シートを作製した。 As the linear ethylene copolymer, a density of 0.940 g / cm 3, melt flow index was used ethylene-1-octene copolymer of 1.0 g / 10min (the Dow Chemical Co., Dow Rex 2740E) except to prepare a pressure-sensitive adhesive sheet in the same manner as in example 2.
【0055】 [0055]
<感圧性接着剤の塗布および乾燥による剥離シートの形状変化> <Shape change of the release sheet by coating and drying of pressure-sensitive adhesive>
実施例1,3,4,6〜9および比較例1,2で作製した各感圧性接着シートについて、剥離シートに感圧性接着剤を塗布し乾燥させて感圧性接着剤層を形成する際の剥離シートの形状の変化を判定した。 For each pressure-sensitive adhesive sheet prepared in Examples 1,3,4,6~9 and Comparative Examples 1 and 2, for forming the pressure-sensitive adhesive layer of the pressure sensitive adhesive is coated and dried to a release sheet and determine a change in the shape of the release sheet. 感圧性接着剤層を形成しても特に問題がなかったものを○とした。 Those be formed a pressure-sensitive adhesive layer had no particular problem was ○. 感圧性接着剤層の形成において、感圧性接着剤の塗布によって剥離シートが膨れたりしわが発生したもの、あるいは前記塗布の時点では問題がなくても乾燥時に剥離シートが収縮したものを×とした。 In the formation of the pressure-sensitive adhesive layer, those wrinkles or blisters release sheet by applying the pressure sensitive adhesive occurs, or was × those even in drying the release sheet is contracted no problems at the time of the coating .
【0056】 [0056]
<剥離性試験> <Peel test>
実施例1〜9および比較例2,3で作製した各感圧性接着シートそれぞれについて、20mm幅に切断した試料を2個ずつ用意した。 Each pressure-sensitive adhesive sheets prepared for in Examples 1 to 9 and Comparative Examples 2 and 3 were prepared samples were cut into 20mm width twice. これらの各試料について剥離シート側を剛性を備える板状体に貼るとともに、ポリエステルフィルム側を万能引張試験機(オリエンテック社製、RTM−100)で引っ張り、公知の試験法である180°角剥離試験によって各試料の抵抗、言い換えると剥離力を測定した。 Together put a release sheet side to the plate-like body having a rigidity for each of these samples, the polyester film side universal tensile tester (Orientec Co., RTM-100) pulled at, 180 ° angle peel is a known test method resistance of each sample by the test were measured in other words the peel force. 前記試験は、温度23℃、60%RHの雰囲気中で、万能引張試験機のクロスヘッドのスピードが300mm/minの条件で行った。 The test temperature 23 ° C., in an atmosphere of RH 60%, the speed of the crosshead of a universal tensile testing machine was carried out under the condition of 300 mm / min.
【0057】 [0057]
上述の感圧性接着剤の塗布および乾燥による剥離シートの形状変化および剥離性試験のそれぞれの結果を表1に示す。 The respective results of the shape change and peel test of peeling sheet by coating and drying the above-mentioned pressure-sensitive adhesive shown in Table 1.
【0058】 [0058]
【表1】 [Table 1]
【0059】 [0059]
表1に示されるように、密度、メルトフローインデックスおよび結晶化度が特定の範囲内の物性値を示す直鎖状エチレン系共重合体を主として含有する実施例1,3,4,6〜9の本発明の剥離シートは、感圧性接着剤を直接塗布し乾燥して感圧性接着剤層を形成しても、不所望に変形することがなかった。 As shown in Table 1, density, melt flow index and Examples crystallinity contains mainly linear ethylene copolymer shows the physical properties of a specific range 1,3,4,6~9 release sheet of the present invention the, also form a pressure-sensitive adhesive layer by applying a pressure sensitive adhesive directly drying, it had never deformed undesirably. 実施例1,3,4,6〜9と同様の方法で作製した比較例1,2の本発明でない剥離シートは、いずれも作製の過程で剥離シートが不所望な変形を起こし、比較例1に至っては剥離性試験を行うことができなかった。 The release sheet is not the present invention in Comparative Examples 1 and 2 was produced in the same manner as in Example 1,3,4,6~9 are both release sheet cause undesired deformation in manufacturing process, Comparative Example 1 it was not possible to carry out the peel test is leading to. また本発明の剥離シートを有する感圧性接着シートは、作製時に上述のような不所望な変形を起こさないとともに、すぐれた剥離性を有することが分かる。 The pressure-sensitive adhesive sheet having a release sheet of the present invention, as well as does not cause undesired deformation as described above during the production, it can be seen to have a good release property. このことは、実施例1,3,4,6〜9と比較例2との剥離性試験の結果を比較してみると明らかである。 This is evident when we compare the results of the peel test of Comparative Example 2 and Example 1,3,4,6~9.
【0060】 [0060]
また実施例2,5の感圧性接着シートは、従来と同様に、支持基材の一表面に感圧性接着剤層を形成し、かつ剥離シートを形成した後、これらを感圧性接着剤層が剥離シートに接するように貼り合わせて作製される。 The pressure-sensitive adhesive sheets of Examples 2 and 5, in a conventional manner on one surface of the supporting substrate to form a pressure-sensitive adhesive layer, and after forming the release sheet, these pressure-sensitive adhesive layer bonded in contact with the release sheet is produced. このような本発明の感圧性接着シートは、比較例3の本発明でない感圧性接着シートと比較して、よりすぐれた剥離性を有することが分かる。 Such pressure-sensitive adhesive sheet of the present invention, as compared to the pressure-sensitive adhesive sheet not according to invention Comparative Example 3, it can be seen to have a more excellent releasability. このことは実施例2,5と比較例3との剥離性試験の結果を比較してみると明らかである。 This is evident when we compare the results of the peel test of Comparative Example 3 and Examples 2, 5.
【0061】 [0061]
【発明の効果】 【Effect of the invention】
以上の説明で明らかなように、本発明によれば、液状の感圧性接着剤をシート材に直接塗布し乾燥する方法で感圧性接着剤層を形成することができる感圧性接着シート用の剥離機能を有するシート材、ならびにそのシート材と感圧性接着剤層とを有しかつ感圧性接着剤層とシート材との間の剥離性にすぐれる感圧性接着シートを提供することができる。 As apparent from the above description, according to the present invention, peeling of a pressure-sensitive adhesive sheet capable of forming a pressure-sensitive adhesive layer a pressure sensitive adhesive liquid in a way that coating and drying directly on the sheet material sheet material having the function, as well as to provide a pressure-sensitive adhesive sheet excellent in releasability between and pressure-sensitive adhesive layer and the sheet material has its sheet material and pressure-sensitive adhesive layer.

Claims (5)

  1. 単層または積層のシート材であって、単層の場合には当該シート材自体が、また積層の場合にはその少なくとも一方の最外層が、密度が0.910〜0.935g/cm 、メルトフローインデックスが0.1g/10min以上、15g/10min以下、結晶化度が30〜60%である直鎖状エチレン系共重合体製のシート材であり、少なくとも感圧性接着剤層に接することを意図する側の表面の算術平均粗さが0.01μm以上、1.0μm以下である、ことを特徴とするポリアクリル酸エステル系感圧性接着剤層を有する感圧性接着シート用の剥離シート材。 A sheet material of a single layer or a laminate, the sheet material itself in the case of the single layer is also the case of the lamination is at least one of the outermost layers, density 0.910 to 0.935 g / cm 3, melt flow index 0.1 g / 10min or more, 15 g / 10min or less, crystallinity of a linear ethylene copolymer sheet made of material which is a 30% to 60%, in contact with at least the pressure-sensitive adhesive layer intended side of the arithmetic average roughness of the surface is 0.01μm or more and 1.0μm or less, peeling sheet for pressure-sensitive adhesive sheet having a polyacrylate pressure-sensitive adhesive layer, characterized in that .
  2. 前記算術平均粗さが0.05μm以上、0.5μm以下である、請求項1記載の剥離シート材。 The arithmetic average roughness is 0.05μm or more and 0.5μm or less, according to claim 1 release sheet material according.
  3. 前記直鎖状エチレン系共重合体は、プロピレン、1−ブテン、1−ヘキセン、4−メチル−1−ペンテンならびに1−オクテンのうちの少なくとも1種以上のコモノマーとエチレンとの共重合体であることを特徴とする請求項1または2記載の剥離シート材。 The linear ethylene-based copolymer, propylene, is 1-butene, 1-hexene, a copolymer of 4-methyl-1-pentene and at least one or more comonomers and ethylene of 1-octene claim 1 or 2 release sheet material wherein a.
  4. 請求項1〜 のいずれか1項に記載の剥離シート材と前記剥離シート材に接するポリアクリル酸エステル系感圧性接着剤層とを有することを特徴とする感圧性接着シート。 Pressure-sensitive adhesive sheet characterized by having a polyacrylate pressure-sensitive adhesive layer and a release sheet in contact with the release sheet material according to any one of claims 1-3.
  5. 前記剥離シート材にポリアクリル酸エステル系感圧性接着剤の溶液を直接塗布し乾燥することで前記感圧性接着剤層を形成することを特徴とする請求項記載の感圧性接着シート。 Pressure-sensitive adhesive sheet according to claim 4, wherein the forming the pressure sensitive adhesive layer by the solution of the release sheet material polyacrylate pressure-sensitive adhesive directly applied and dried.
JP34097599A 1999-11-30 1999-11-30 Pressure-sensitive adhesive sheet having sheet material, as well as it Active JP5052711B2 (en)