JP4483328B2 - 偏光フィルムの製造方法 - Google Patents
偏光フィルムの製造方法 Download PDFInfo
- Publication number
- JP4483328B2 JP4483328B2 JP2004037792A JP2004037792A JP4483328B2 JP 4483328 B2 JP4483328 B2 JP 4483328B2 JP 2004037792 A JP2004037792 A JP 2004037792A JP 2004037792 A JP2004037792 A JP 2004037792A JP 4483328 B2 JP4483328 B2 JP 4483328B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- treatment
- boric acid
- water
- acid treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
本発明におけるポリビニルアルコール系フィルムを形成するポリビニルアルコール系樹脂は、通常、ポリ酢酸ビニル系樹脂をケン化したものが例示される。ポリビニルアルコール系樹脂のケン化度は、約85モル%以上、好ましくは約90モル%以上、より好ましくは約99モル%〜100モル%である。ポリ酢酸ビニル系樹脂としては、酢酸ビニルの単独重合体であるポリ酢酸ビニルのほか、酢酸ビニルとこれに共重合可能な他の単量体との共重合体、例えば、エチレン−酢酸ビニル共重合体などが挙げられる。共重合可能な他の単量体としては、例えば不飽和カルボン酸類、オレフィン類、ビニルエーテル類、不飽和スルホン酸類などが挙げられる。ポリビニルアルコール系樹脂の重合度は、約1000〜10000、好ましくは約1500〜5000程度である。
50μm 程度である。
このホウ酸処理は、架橋による耐水化や色相調整(青味がかるのを防止する等)等のために実施される。架橋による耐水化のための場合には、必要に応じて、ホウ酸以外に、またはホウ酸と共に、グリオキザール、グルタルアルデヒドなどの架橋剤も使用することができる。なお、耐水化のためのホウ酸処理を、耐水化処理、架橋処理、固定化処理などの名称で呼称する場合もある。また、色相調整のためのホウ酸処理を、補色処理、再染色処理などの名称で呼称する場合もある。
原反フィルムに膨潤、染色、ホウ酸処理を施す場合で、ホウ酸処理が架橋による耐水化を目的としているときは、水100重量部に対してホウ酸を約3〜10重量部、ヨウ化物を約1〜20重量部含有するホウ酸処理浴を使用し、通常、約50℃〜70℃、好ましくは約55℃〜65℃の温度で行われる。浸漬時間は、通常、約30〜600秒程度、好ましくは約60〜420秒、より好ましくは約90〜300秒である。
なお、予め延伸したフィルムに染色、ホウ酸処理を行う場合、ホウ酸処理浴の温度は、通常、約50℃〜85℃、好ましくは約55℃〜80℃である。
色相調整のためのホウ酸処理は、耐水化のためのホウ酸処理に比べて、通常、低いホウ酸濃度、高いヨウ化物濃度、低い温度で行われる。
ホウ酸処理工程においても、染色工程と同様にフィルムの延伸を行ってもよい。最終的な積算延伸倍率は、約4.5〜7.0倍、好ましくは約5.0〜6.5倍である。
ホウ酸処理工程が複数のホウ酸処理工程からなる場合には、最初または最初から2段目までのホウ酸処理工程で前記フィルムを延伸し、延伸処理を行ったホウ酸処理工程の次のホウ酸処理工程から水洗工程までのそれぞれの工程において張力制御を行うか、最初から3段目までのホウ酸処理工程で前記フィルムを延伸し、延伸処理を行ったホウ酸処理工程の次のホウ酸処理工程から水洗工程までのそれぞれの工程において張力制御を行うことが好ましいが、工業的には。最初または最初から2段目までのホウ酸処理工程で前記フィルムを延伸し、延伸処理を行ったホウ酸処理工程の次のホウ酸処理工程から水洗工程までのそれぞれの工程において張力制御を行うことがより好ましい。ホウ酸処理後に、上記したヨウ化物処理または亜鉛処理を行う場合には、これらの工程についても張力制御を行う。
実施例1
ポリビニルアルコールフィルムを以下のとおり膨潤槽、染色槽、第1ホウ酸処理槽、第2ホウ酸処理槽、水洗槽の順に搬送して偏光フィルムを製造した。第1ホウ酸処理槽の処理液中の全ガイドロール(5本)を直径70mm、表面粗さ0.2S、動摩擦係数が0.24のSUS製研磨ロールとし、他の気中、処理液中のガイドロールとして、直径70mm、表面粗さ0.6S、ゴム硬度(JISショアAスケール)80度、動摩擦係数が0.6であるNBRゴム製ロールを用いた。延伸は、処理槽の前後に配置したニップロールに周速差を持たせて行った。
次に、ヨウ素/ヨウ化カリウム/水が重量比で0.02/1.5/100の水溶液に浸漬して染色処理しつつ、一軸延伸(延伸倍率: 4.0倍)を行った。その後、ヨウ化カリウム/ホウ酸/水が重量比で10/5/100の60℃水溶液に浸漬して、ホウ酸処理しつつ原反からの積算延伸倍率が 5.9倍になるまで一軸延伸を行った。さらに、ヨウ化カリウム/ホウ酸/水が重量比で10/3/100の水溶液に40℃でおよそ30秒間浸漬して、第2のホウ酸処理を行った。第2のホウ酸処理後、10℃の純水で約10秒間水洗した。水洗後、60℃で2分間乾燥して、厚さ28μm のヨウ素系偏光フィルムを得た。
得られた偏光フィルムの膜厚分布を調べたところ、%ゲージ差が 26.3%であった。%ゲージ差とは以下の式によって定義されるものであり、これによって膜厚分布を規格化することができる。
%ゲージ差=100×(最大膜厚−最小膜厚)/平均膜厚
第1ホウ酸処理槽の処理液中の全ガイドロール(5本)も他のガイドロールと同じNBRゴム製ロールとした以外は、実施例1と同様にして偏光フィルムを作製した。得られた偏光フィルムの膜厚分布を調べたところ、%ゲージ差が 40.3%となり、膜厚分布の悪いものであった。
Claims (1)
- ポリビニルアルコール系フィルムを膨潤処理、染色処理、ホウ酸処理および水洗処理の順に処理し、ホウ酸処理工程および/またはその前の工程で一軸延伸を行う偏光フィルムの製造方法において、染色処理以降の処理液中の少なくとも一つのガイドロールとして、表面粗さが0.2〜1.0S、処理フィルムとの水中における動摩擦係数が0.1〜0.4であるステンレススチール製研磨ロールを用いることを特徴とする、偏光フィルムの製造方法。