JP4408750B2 - 合成皮革 - Google Patents
合成皮革 Download PDFInfo
- Publication number
- JP4408750B2 JP4408750B2 JP2004162893A JP2004162893A JP4408750B2 JP 4408750 B2 JP4408750 B2 JP 4408750B2 JP 2004162893 A JP2004162893 A JP 2004162893A JP 2004162893 A JP2004162893 A JP 2004162893A JP 4408750 B2 JP4408750 B2 JP 4408750B2
- Authority
- JP
- Japan
- Prior art keywords
- synthetic leather
- thermoplastic polyurethane
- polyurethane elastomer
- flame retardant
- polyisocyanate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
表1に示す成分を常温で混合し、バンバリーを用いて160℃で5分間加熱混練して動的架橋反応させた。次いで混練物をウォーミングロール上に温度が下がらないようにストックし、ロール温度150℃でカレンダー加工して、厚さ0.25mmのシートに成形した。得られたシートと基布とをアクリル系接着剤を用いて積層し、表面にマーブルプリント、艶調整処理剤コーティング処理、エンボス処理を施して合成皮革を得た。上記基布は、レーヨン65%とポリエステル35%の20番手混紡糸で編成したスムースメリヤスに、丸菱油化工業製のノンネン109(リン酸カルバメートをイソプロピルアルコールと水の混合液に分散させた窒素−リン系難燃剤)を固形分で35g/m2になるように塗布し、乾燥させたものを使用した。
得られた合成皮革について、カレンダー加工性、耐摩耗性、難燃性、柔軟性を調べた。その結果も併せて表1に示す。
カレンダー加工性:150℃ロール温度で良好に加工できたものを「良好」と評価した。バンバリーで混練加工時硬化して、カレンダー加工できないものを「加工不可」と評価した。
耐摩耗性:JIS K6404−16(1999)に規定する学振型摩擦試験機を用い、JIS L3102(1978)に定める6号帆布を横向きに取付けた。荷重1kgで破れるまでの回数で評価した。80未満では座面に使用した場合、耐用期間が不十分になる。
難燃性:JIS D1201(1998)に依った。合格は、燃焼速度が100mm/分未満を意味する。
柔軟性:発泡ウレタンの座面として使用した場合の硬さを官能評価した。
表1の実施例1〜7は車両座席表皮材に適する。特に、実施例1〜3は柔軟性も良く好適である。また、実施例8は二輪車のサドルの座面の表皮材に適する。
Claims (5)
- 基布の少なくとも片面に熱可塑性ポリウレタン系エラストマー層を設けた合成皮革であって、該熱可塑性ポリウレタン系エラストマー層は、熱可塑性ポリウレタン系エラストマーにポリイソシアネートを配合し、加熱混練して動的架橋させた熱可塑性ポリウレタン系エラストマーをカレンダーでシート状に成形したものであることを特徴とする合成皮革。
- ポリイソシアネートとしてメチレンビス(4,1−フェニレン)ジイソシアネートを用い、熱可塑性ポリウレタン系エラストマー100質量部に対し、0.1〜2質量部を配合した請求項1記載の合成皮革。
- 熱可塑性ポリウレタン系エラストマー層が、リン系可塑剤を含有する請求項1又は2記載の合成皮革。
- 基布が、窒素−リン系難燃剤で難燃加工されている請求項1〜3のいずれかに記載の合成皮革。
- 窒素−リン系難燃剤が、縮合リン酸アンモニウム、縮合リン酸メラミン、縮合リン酸アミドアンモニウム及びリン酸カルバメートから選ばれた難燃剤である請求項4記載の合成皮革。