JP4291642B2 - Method for manufacturing aluminum alloy plate for packaging container lid - Google Patents

Description

The present invention relates to a method for producing an aluminum alloy plate excellent in formability and stress relaxation properties, which is suitable for packaging container lids such as cans and bottle cans.

  A typical example of an aluminum alloy packaging container is a can for drinking water. Usually, this is a body (can barrel) made of a 3000 series aluminum alloy plate having excellent formability and a high strength 5000 series aluminum. It is composed of an end (can lid) made of an alloy plate.

In recent years, the aluminum alloy bottle cans have attracted attention as an alternative to PET (Polyethylene Terephthalate) bottles, which include the following.
(1) Similar to conventional cans, the can body and the bottom of the can are made of a single body of a 3000 series aluminum alloy plate having excellent formability, and a cap section made of a 3000 series or 5000 series aluminum alloy plate is provided on this. An aluminum alloy bottle can (hereinafter referred to as “two-piece type bottle can”, which is described as a one-piece type bottle can in Patent Document 1) is disclosed (for example, Patent Document 1). 1).

(2) Further, it is composed of a can body portion made of a 3000 series aluminum alloy plate excellent in formability, a can bottom portion made of a high strength 5000 series aluminum alloy plate, and a cap portion made of a 3000 series or 5000 series aluminum alloy plate. An aluminum alloy bottle can (hereinafter referred to as “three-piece type bottle can”, which is described as a two-piece type bottle can in Patent Document 1) is disclosed (for example, Patent Document 1). reference).

Here, a general manufacturing process for manufacturing a packaging container lid (referring to a can lid part of a can and a can bottom part of a three-piece bottle can) as described above and a packaging container will be described.
<Packing container lid (can lid)>
(1) Pretreatment process Chromate treatment is applied to the aluminum alloy plate for the packaging container lid to ensure corrosion resistance.
(2) Painting / baking process The surface after chromating is painted and baked.
(3) Shell forming step After blanking into a predetermined shape from a painted, baked or laminated aluminum alloy plate, shell forming is performed.
(4) Curling forming process A can body part and a winding part (curl part) for winding are formed.
(5) Compound drying process Rubber is injected into the winding part.
(6) Conversion molding process (the following is molded by the same press)
(i) Rivet molding (bubble molding and button molding)
(ii) Score shaping (groove in the mouth / score processing)
(iii) Bead emboss molding (processing of irregularities, letters, etc.)
(iv) Stake molding (with tabs)
<Packing container>
(7) Contents filling process (can body part)
(8) Winding process of can body part and can lid part (9) The packaging container lid and the packaging container are manufactured through each process of cleaning / sterilization treatment process.

In the coating / baking step (2) in the above process, since the coating / baking is continuously performed in a continuous heat treatment furnace, the coating / baking is performed in the oven at a peak temperature of around 250 ° C. for about 20 seconds. The process is being performed.
However, since it is necessary to ensure the reliability of the packaging container such that the packaging container is not deformed by handling or the contents do not leak, excessive strength reduction due to the coating / baking process is not allowed.

Furthermore, there is a strong demand for cost reduction for such aluminum alloy packaging containers, and there is a demand for further thinner packaging containers. Similarly, reducing the thickness of the packaging container lid is also under consideration. To reduce the thickness of the packaging container lid, it is necessary to increase the strength after the painting / baking process or laminating process in order to maintain the necessary rigidity as the packaging container lid. In addition, the aluminum alloy itself needs to have a certain degree of pressure resistance when it is thinned. In order to have such pressure resistance, the packaging container lid material has a proof stress of 220 N / mm ² (220 MPa) after heat treatment for about 20 seconds at about 250 ° C., which is the highest temperature that the aluminum alloy plate for packaging container lid receives. ) There is a need for an aluminum alloy plate that is above.
JP 2002-256366 A (paragraph numbers 0018 to 0029, FIGS. 1 to 3)

In the packaging container formed from the aluminum alloy plate which consists of a conventional composition component, in the sterilization process of said (9), as above-mentioned in retort drinks and dairy products, after temperature filling at temperature conditions of 100-125 degreeC. Although it is carried out for about 30 minutes, depending on the filled contents, a pressure exceeding 5 kg / cm ² (500 kPa) may be applied to the inner wall of the packaging container and the packaging container lid. In such a case, the packaging container lid swells in the outer direction of the packaging container due to the pressure of the contents, and is in a deformed state. Such deformation amount in the deformed state of the packaging container lid is referred to as a bulge deformation amount. However, when the bulge deformation amount increases, problems such as the lid being caught on the conveyor during reverse conveyance and the production line stagnating. In addition, after the heat applied to the aluminum alloy plate is removed after the sterilization treatment, it is necessary to return to the steady state before the deformation, but the deformed packaging container lid remains in a deformed state. Some of them do not return to their original shape.

  In addition, when the product is kept warm at about 50 to 70 ° C. in a hot-compatible product in winter or when it is left in a car at high temperatures in summer and exposed to direct sunlight, the temperature of the packaging container exceeds 60 ° C. In some cases, the buckling exceeds the pressure strength, or even the buckling portion or the countersink portion (can lid groove portion) breaks in addition to the buckling.

The present invention has been made in view of the above-described problems, and is excellent in moldability for a packaging container lid, and exposed to a high temperature after the contents are filled, and the internal pressure of the packaging container is increased and buckled. Even if it is a case, it is difficult to break, and even if the shape is deformed, the shape returns to the original steady state with the removal of heat, that is, manufacture of an aluminum alloy plate for a packaging container lid that is excellent in stress relaxation properties It aims to provide a method.

  As a result of diligent research and experiments to solve the above problems, the present inventors have controlled the composition components (Cu, Mn, Mg, Si, Fe) contained in the aluminum alloy to an appropriate range and appropriately manufactured them. The above-mentioned problem is achieved by regulating the aluminum alloy plate produced and produced by the method so that the breaking limit elongation of the parallel bending tensile test after baking at a temperature equivalent to 250 ° C. for 20 seconds is appropriate. The inventors have found that the present invention can be solved, and have created the present invention.

The invention described in 請 Motomeko 1, 0.05 to 0.3 wt% of Cu, 0.2 to 0.6 wt% of Mn, and containing 2.0 to 5.5 mass% of Mg, further, An aluminum alloy plate having a composition in which Si is regulated to 0.05 to 0.3 mass%, Fe is regulated to 0.05 to 0.4 mass%, and the balance is composed of Al and inevitable impurities, and is composed of the above composition After the aluminum alloy plate is baked for 20 seconds under a temperature condition of 250 ° C. with a salt bath, the direction parallel to the rolling direction of the aluminum alloy plate is the longitudinal direction. A test piece having a length of 100 mm and a width of 20 mm was prepared, and this was bent into a 90-degree V-shape with a tip R0.1 mm punch so that the tensile direction was perpendicular to the rolling line of the test piece. Two flat test plates are folded A flat plate with a crease is formed by returning the flat plate to a flat plate, and the breaking limit displacement is measured by pulling the flat plate in the longitudinal direction. The gage distance is 50 mm, and {(breaking limit displacement (mm) / 50 ( mm)) × 100} is a method for producing an aluminum alloy plate for a packaging container lid for producing an aluminum alloy plate for a packaging container lid such that the elongation at break determined by 2) is at least 2% , A first step of performing a homogenization heat treatment of an ingot made of an aluminum alloy, a second step of performing a hot rolling treatment on the ingot subjected to the homogenization heat treatment in the first step, and a hot rolling treatment in the second step. A third step of cold rolling the rolled sheet, a fourth step of annealing the rolled sheet cold-rolled in the third step, and a cold rolled sheet rolled in the fourth step. A fifth step of rolling, and A sixth step of winding the aluminum alloy plate cold-rolled in five steps around a coil, and the annealing rate in the fourth step is a heating rate of 100 ° C./min or more for the cold-rolled rolled plate In the fifth step, and a step of cooling the rolled plate heated immediately after the heat treatment to 200 ° C. or less at a cooling rate of 100 ° C./min or more. The cold rolling process is performed once so that the rolling rate of the cold rolling process is 50 to 80%, and the coiling temperature in the sixth step is 120 to 150 ° C. It is a manufacturing method of the aluminum alloy plate for packaging container lids characterized by being.

Furthermore, the invention of claim 2 contains 0.05 to 0.3% by mass of Cu, 0.2 to 0.6% by mass of Mn, 2.0 to 5.5% by mass of Mg, An aluminum alloy having a composition in which Si is regulated to 0.05 to 0.3 mass%, Fe is regulated to 0.05 to 0.4 mass%, and the balance is composed of Al and inevitable impurities, and is composed of the above composition A plate is manufactured with a plate thickness of 0.30 mm, and the aluminum alloy plate is baked with a salt bath at a temperature of 250 ° C. for 20 seconds, and then the direction parallel to the rolling direction of the aluminum alloy plate is the longitudinal direction. Thus, a test piece having a length of 100 mm and a width of 20 mm was prepared, and this was bent into a 90-degree V-shape with a tip R0.1 mm punch so that the tensile direction was perpendicular to the rolling line of the test piece, Two folded test plates A flat plate with a flattened surface and a creased flat plate, the critical displacement is measured by pulling the flat plate in the longitudinal direction, and the gauge distance is 50 mm, {(the critical displacement (mm) / 50 (mm)) × 100} is a method for producing an aluminum alloy plate for a packaging container lid for producing an aluminum alloy plate for a packaging container lid such that the elongation at break required for breaking is 2% or more , A first step of performing a homogenization heat treatment of an ingot made of an aluminum alloy having the above composition, a second step of hot rolling the ingot that has been subjected to the homogenization heat treatment in the first step, and hot in the second step A third step of cold rolling the rolled sheet, a fourth step of annealing the cold rolled sheet in the third step, and a rolled sheet annealed in the fourth step 5th process of cold rolling And a sixth step of winding the aluminum alloy plate cold-rolled in the fifth step around a coil, and the annealing in the fourth step is performed at a temperature of 100 ° C./min or more on the cold-rolled rolled plate. A step of heat-treating at a heating rate, a step of heating and holding the rolled plate heat-treated in the step at 400 to 550 ° C. within 10 minutes, and a temperature of 100 ° C./min or more of the rolled plate heated and held in the step And performing the cold rolling process once so that the rolling rate of the cold rolling process in the fifth process is 50 to 80%. Further, in the sixth process, the coil winding temperature is 120 to 150 ° C., and the method for producing an aluminum alloy plate for a packaging container lid is provided.

  As described above, the heating rate, the holding time, and the cooling rate are regulated in the annealing process step (fourth step) after the cold rolling in the manufacturing method of the aluminum alloy plate. Formability and stress relaxation properties can be improved. Moreover, since a rolling rate is controlled in the cold rolling treatment process (5th process) after annealing, the intensity | strength of the aluminum alloy plate for packaging container lids can be raised efficiently. Furthermore, since the coiling temperature is regulated in the coiling process after the cold rolling (sixth process), the elongation of the parallel bending tensile test after baking the aluminum alloy sheet can be kept within an appropriate range. And no grain boundary embrittlement occurs.

As described above, the manufacturing method of the aluminum alloy plate according to claim 1 and 2 of the present invention, since the production of aluminum alloy plate by the particular composition ingredients and manufacturing conditions, specific for the aluminum alloy plate test It can form so that the breaking limit elongation rate in the parallel bending tensile test performed on condition may be 2% or more. As a result, it has excellent moldability for packaging container lids, and is exposed to high temperatures after filling the contents, resulting in a state where the internal pressure of the packaging container is increased, and even when buckled, it is difficult to break and heat removal. the shape of the packaging container closure that has been in a deformed state with the excellent stress relaxation properties that return to the original steady state, further, to produce aluminum alloy sheet for better packaging container lid in can opening property.

  Hereinafter, embodiments of the present invention will be described in detail. It should be noted that the present invention is not limited to this embodiment, and can be appropriately changed as long as it is based on the technical idea of the present invention.

The present inventors were in a deformed state along with the removal of the stress even when stress corresponding to the formability as an aluminum alloy plate for packaging container lid, crack resistance, and internal pressure at high temperature was applied. Focusing on the stress relaxation required for the packaging container lid to return to its original steady state, various experimental studies were conducted on the relationship between these and the components of the aluminum alloy and the manufacturing process.
As a result, it has been found that the formability, crack resistance and stress relaxation properties are closely related to the components of the aluminum alloy and the annealing conditions after cold rolling.

That is, in the present invention, the content of the compositional components of Cu, Mn, Mg, Si, Fe contained in the aluminum alloy and the breaking limit elongation of the parallel bending tensile test after baking (the aluminum alloy plate having a specific composition) After manufacturing with a thickness of 0.30 mm and baking the aluminum alloy plate for 20 seconds under a temperature condition of 250 ° C. with a salt bath, the direction parallel to the rolling direction of the aluminum alloy plate is the longitudinal direction. A test piece having a length of 100 mm and a width of 20 mm was prepared, and this was bent into a 90-degree V-shape with a tip R0.1 mm punch so that the tensile direction was perpendicular to the rolling line of the test piece. The test plate is returned to the flat plate with two flat plates to make a creased flat plate, and the flat plate is pulled in the longitudinal direction to obtain the breaking limit displacement. Measured, the gage length as 50 mm, to regulate the {(fracture limit displacement (mm) / 50 (mm) ) × 100} refers to the fracture limit elongation sought. Hereinafter the same.) Within the appropriate range ing. Therefore, the reason why the contents of these components are limited numerically and the reason why the breaking limit elongation in the parallel bending tensile test after baking is specified will be described.

≪Composition ingredients≫
[Reason for setting Cu to 0.05 to 0.3% by mass]
Cu contained in the aluminum alloy plate for packaging container lids according to the present invention coexists with Mg and exhibits a bake hard effect due to aging precipitation. For this reason, precipitation hardenability is provided in the painting / baking or laminating process, and the rigidity as a packaging container lid is maintained. Moreover, stress relaxation property is improved.
When Cu is less than 0.05% by mass, sufficient bake hard effect and stress relaxation cannot be obtained, and when the content exceeds 0.3% by mass, ingot cracking and cracking during hot rolling are likely to occur. In addition, the corrosion resistance of the obtained aluminum alloy plate is significantly deteriorated.
Therefore, Cu is 0.05 to 0.3 mass%.

[Reason for setting Mn to 0.2 to 0.6% by mass]
Mn contained in the aluminum alloy plate for a packaging container lid according to the present invention is effective in maintaining the rigidity of the packaging container lid by improving the strength. Further, the refinement of aluminum alloy crystal grains is effective in improving formability.
When Mn is less than 0.2% by mass, the above-mentioned effect is small, and when it exceeds 0.6% by mass, a coarse Al—Fe—Mn-based intermetallic compound is produced, and the starting point of cracking during molding or buckling Therefore, it is not preferable.
Therefore, Mn is 0.2 to 0.6 mass%, more preferably 0.3 to 0.5 mass%.

[Reason for setting Mg to 2.0 to 5.5% by mass]
Mg contained in the aluminum alloy plate for a packaging container lid according to the present invention is an element that contributes to the material strength like Cu.
If the Mg content is less than 2.0% by mass, sufficient strength cannot be obtained as an aluminum alloy plate for packaging container lids. If the Mg content exceeds 5.5% by mass, ingot cracking and hot rolling It is easy to cause cracking.
Therefore, in the present invention, the Mg content is set to 2.0 to 5.5% by mass.

[Reason for setting Si to 0.05 to 0.3% by mass]
Si contained in the aluminum alloy plate for packaging container lids according to the present invention is an element that has an effect on the formation of Mg-Si intermetallic compounds that improve the openability and the stabilization of the structure.
If the Si content is less than 0.05% by mass, not only the production amount of Mg-Si intermetallic compounds is small and the effect on the openability is low, but also the purity of the Al ingot needs to be increased. This is inappropriate.
Further, if the Si content exceeds 0.3% by mass, the formability is reduced due to excessive formation of Mg-Si intermetallic compounds, and the material strength and bake hardness due to the decrease in solid solution Mg are more than necessary. It is unsuitable because it decreases.
Accordingly, Si is set to 0.05 to 0.3% by mass.

[Reason for setting Fe to 0.05 to 0.4 mass%]
Fe contained in the aluminum alloy plate for packaging container lid according to the present invention affects the crystal grain size of the aluminum alloy. If the Fe content is less than 0.05% by mass, the crystal grains become coarse, and the purity of the Al metal needs to be increased, resulting in an increase in cost.
On the other hand, when the Fe content exceeds 0.4% by mass, a huge Al—Fe—Mn-based intermetallic compound having a maximum length exceeding 20 μm is generated, and the formability is lowered.
For this reason, in this invention, content of Fe shall be 0.05 to 0.4 mass%.

[Inevitable impurities]
As unavoidable impurities contained in the aluminum alloy plate for packaging container lids according to the present invention, Zn: 0.2% by mass or less, Ti: 0.1% by mass or less, Zr: 0.1% by mass or less, B: 0.0. Inclusion of 1% by mass or less does not hinder the effects of the present invention, and such inevitable impurities are allowed to be contained.

[Reason why the elongation at break in the parallel bending tensile test after baking was 2% or more]
The elongation at break in the parallel bending tensile test after baking for 20 seconds under a temperature condition of 250 ° C. can be used to evaluate physical properties such as malleability and ductility of the aluminum alloy sheet, particularly stress relaxation properties in the present invention. it can.
When the critical elongation at break in the parallel bending tensile test after baking is less than 2%, the ductility decreases when the severed bending deformation is applied to the tightened portion in the tightening process after the end forming, and the material is broken or filled.・ If the end counter sink part (bending part) is rapidly reversed in a form where the internal pressure is applied beyond the pressure strength after winding and buckling occurs and the end counter sink part (bending part) is bent back, it will break near the counter sink part. It is unsuitable because it causes defects.
Therefore, in the present invention, the breaking limit elongation in the parallel bending tensile test after baking is set to 2% or more.
This characteristic is an index indicating the formability and cracking susceptibility of the bend-formed part, and is achieved by defining and optimizing the manufacturing process including components and rolling coiling temperature.

[Method for producing aluminum alloy sheet for packaging container lid]
Next, the manufacturing method of the aluminum alloy plate for packaging container lids of this invention is demonstrated with reference to the flowchart shown in FIG.
The method for producing an aluminum alloy plate for a packaging container lid according to the present invention, first, after performing a homogenization heat treatment step (S1) of an aluminum alloy ingot (slab) containing the composition component defined in claim 1 of the present invention. , A hot rolling treatment step (S2) and a cold rolling treatment step (S3) are performed, and the cold-rolled rolled plate is heated at a heating rate of 100 ° C./min or more, and this step is performed through 400 to After heating to 550 ° C. and immediately after heating, annealing step (S4) having a step of cooling to 200 ° C. or less at a cooling rate of 100 ° C./min or more, or after heating to the temperature of 400 to 550 ° C., An annealing treatment step (S4) is performed which includes a step of heating and holding within 10 minutes and a step of cooling the rolled plate held at a high temperature by such a step to 200 ° C. or less at a cooling rate of 100 ° C./min or more. A cold rolling treatment step (S5) is performed so that the rolling rate of the rolled plate after the annealing treatment in the step is 50 to 80%, and the cold-rolled aluminum alloy plate is wound at 120 to 150 ° C. A winding process (S6) for winding the coil at a temperature is performed. By using the manufacturing method described above, it is possible to obtain an aluminum alloy plate for a packaging container lid that is excellent in formability and stress relaxation properties as intended by the present invention.
In addition, among each said process, it can carry out by a conventionally well-known method about a homogenization heat treatment process (S1), a hot rolling process process (S2), and a cold rolling process process (S3).
The reason why the production conditions are limited in the production method of the present invention will be described below.

≪Production conditions≫
[Annealing treatment step after cold rolling (S4)]
In order to improve the formability and stress relaxation as an aluminum alloy plate for a packaging container lid, annealing is required after cold rolling.
The heating rate and cooling rate in the annealing treatment step affect the crystal size of the recrystallized aluminum alloy grains and the solid solution amount of the solid solution elements (Mg, Cu).
When the heating rate is less than 100 ° C./min, the recrystallized grain size increases and the moldability decreases. Furthermore, when the cooling rate is less than 100 ° C./min, the solid solution state of the solid solution component cannot be maintained, and the bake hard effect and the stress relaxation property cannot be obtained.
Further, if the holding temperature is less than 400 ° C, a sufficient recrystallized grain structure cannot be obtained, and if it exceeds 550 ° C, quality abnormalities such as burning on the surface of the aluminum alloy plate are caused.
Moreover, it is unsuitable for the holding time after the heat treatment to exceed 10 minutes because the productivity is significantly reduced.
Accordingly, it is necessary that the heating rate is 100 ° C./min or more, the cooling rate is 100 ° C./min or more, the holding temperature during heating is 400 to 550 ° C., and the holding time after the heat treatment is within 10 minutes. However, it is more desirable to perform a cooling process immediately after the heat treatment (that is, the retention time is 0 second) without providing a retention time.
Moreover, as an annealing process process, although a continuous annealing process is preferable, it is good also as a batch type.

[Cold rolling process step (S5) at a rolling rate of 50 to 80%]
Cold rolling after the annealing process is necessary to increase the strength of the aluminum alloy plate for the packaging container lid. At this time, if the rolling rate is less than 50%, sufficient strength cannot be obtained, and if the rolling rate exceeds 80%, the degree of thermal softening of the rolling strain exceeds the effect of the bake hard, and as a result, the packaging container lid Stress relaxation properties are reduced.
Therefore, the cold rolling rate is 50 to 80%.

[Winding step at a temperature of 120 ° C. to 150 ° C. (S6)]
If it is wound around a coil at a temperature of less than 120 ° C after cold rolling, the recovery of the processed structure by cold rolling (subgraining) is insufficient and non-uniform deformation is likely to occur, and the fracture in the parallel bending tensile test after baking Since the limit elongation is less than 2%, there is a risk that the tightening portion breaks when the packaging container is tightened, or the countersink portion of the packaging container lid is broken due to a change in internal pressure.
Further, when the coil is wound at a temperature exceeding 150 ° C., a β phase is precipitated at the crystal grain boundary and embrittlement of the grain boundary occurs, so that cracking is particularly likely to occur at the processed portion along the rolling direction.
Therefore, the coiling temperature after cold rolling needs to be 120 ° C to 150 ° C.
In addition, the temperature of the said coil was measured with the portable contact-type thermometer in two points, the circumference center part and circumference outer edge part of the coil side surface immediately after winding.

In the manufacturing method of an aluminum alloy plate for a packaging container lid according to the present invention, but it may also be performed a plurality of times as required to cold rolling treatment process S3. In addition, the manufacturing method can be variously changed as necessary, and such a modified example of the manufacturing method is also included in the method for manufacturing an aluminum alloy plate for a packaging container lid of the present invention.

Hereinafter, the Example which satisfy | fills the requirements for the aluminum alloy plate for packaging container lids concerning this invention is described concretely compared with the comparative example which does not satisfy the requirements of this invention.
Each aluminum alloy ingot having the chemical composition shown in Table 1 is subjected to a hot rolling treatment step (S2) and a cold rolling treatment step (S3) after the homogenization heat treatment step (S1), and then the conditions shown in Table 1 An annealing treatment step (S4) and a cold rolling treatment step (S5) were carried out to produce each aluminum alloy plate having a plate thickness of 0.30 mm.
In addition, the annealing process conditions of an annealing process process (S4) were set as follows.
<Annealing conditions>
Heating rate: 120 ° C / min Holding temperature: 500 ° C x 0 seconds Cooling rate: 150 ° C / min

Then, about the aluminum alloy plate produced on the said conditions, the following items (1)-(6) were evaluated.
(1) Average crystal grain size After making the surface of the aluminum alloy plate produced under each condition a mirror surface, the surface was etched, and the metal structure was observed and photographed with a metal microscope having a magnification of 100 times.
At this time, a line segment of a known length (for example, 1 mm) is drawn in a direction perpendicular to the rolling direction, and the number of crystal grains cut by the line segment is obtained and divided by the length of the line segment. The crystal grain size per one was determined (cutting method). The same measurement was repeated at different locations (5 locations), and the average value was defined as the average crystal grain size.

(2) Yield strength About the aluminum alloy plate produced on each condition, the tension test piece by JIS5 was produced so that a tension direction might become parallel with a rolling direction. After that, the packaging container is baked for 20 seconds at a maximum temperature of 250 ° C. during the manufacturing process, equivalent to coating and baking with a salt bath, and a tensile test is performed according to JIS Z 2241 (metal material tensile test method). Asked.

(3) Breaking limit displacement amount in parallel bending tensile test The breaking limit displacement amount in the parallel bending tensile test was measured by the method shown in FIG. That is, after the aluminum alloy plate manufactured under the conditions of the present invention was subjected to coating / baking equivalent baking treatment with a salt bath at 250 ° C. for 20 seconds, a test piece 1 having a length of 100 mm and a width of 20 mm was prepared. It is bent into a 90-degree V-shape by the tip R0.1 mm punch 2 (FIG. (A)), and this is returned to a flat plate by two flat plates or the like to form a flat plate 3 (FIG. (B)). The flat plate 3 of the aluminum alloy plate test piece is creased. And the fracture | rupture limit displacement amount is measured by pulling this flat plate 3 to a longitudinal direction (the figure (c)). In the parallel bending tensile test, since the elongation of the flat plate 3 of the aluminum alloy plate test piece is smaller when the bending test is performed along the rolling line of the aluminum alloy plate, the direction is parallel to the rolling direction of the aluminum alloy plate. It implemented so that the bending part of the flat plate 3 might be formed. That is, the tensile direction of the flat plate 3 is a direction perpendicular to the rolling line of the aluminum alloy plate.

In addition, since the fracture | rupture limit displacement amount in a parallel bending tensile test changes with the size of a test piece and a gauge distance, it decided to obtain this by the fracture limit elongation rate which made the gauge distance 50mm. In other words, fracture limit elongation in the present invention can be found from Equation (1),
Breaking limit elongation (%) = (breaking limit displacement (mm) / 50 (mm)) × 100 (1)
In the present invention, since the breaking limit elongation of 2% or more is required, the breaking limit displacement in this case needs to be 1 mm or more.

(4) Ball-head overhanging formability After subjecting the aluminum alloy plate produced under the conditions shown in Table 1 to a predetermined pretreatment, an epoxy resin coating film having a thickness of 5 μm was applied on both sides, and the heating temperature Baking was performed under heating conditions of 250 ° C. and a heating time of 20 seconds.
Thereafter, as shown in FIG. 3, a ball head overhang test (ball head diameter: 6 mmφ, overhang amount: 1) is performed by subjecting the test piece 1 to overhang molding processing using a ball head punch 4. 0.5 mm), and the performance was evaluated according to the following criteria. “No” indicates that there is no crack or rough skin on the overhang, “O” indicates that there is no problem, “△” indicates that the rough surface is seen on the overhang 5, and “No” indicates that the overhang is cracked. × ”. The ball head overhang test was performed while holding the test piece 1 with the tool 6 before the ball head punch 4 was in contact with the test piece 1 of the aluminum alloy plate as the workpiece.

(5) Stress relaxation property This evaluation method was carried out by a technique (stress relaxation test; EMAS-3003) standardized by the Japan Electronic Materials Industry Association. FIG. 4 shows an outline of a method for evaluating the stress relaxation property. As a test method, a test piece 1 ′ having a plate thickness of 0.3 mm, a width of 10 mm, and a length of 100 mm was prepared after performing a baking process (heat treatment at a temperature condition of 250 ° C. for 20 seconds) corresponding to the painting and baking process. In order to simulate the deformation state of the lid material, a pre-strain of 2.5% (deflection) corresponding to the can lid groove part (counter sink part) processing step is achieved by the cantilever type described in the Japan Electronic Materials Industry Association Standard EMAS-3003. Distance (L): 30 mm, deflection height (H): 10 mm (corresponding to a load stress of 350 MPa from the relationship between deflection distance and height)), elasticity in a predetermined atmosphere at a test temperature of 120 ° C. and a holding time of 3 hours The bending height (h) after the stress was removed was measured while maintaining a state of bending deformation. In addition, it is inferior to stress relaxation property, so that the deflection height (h) of a test piece is large.
In the present invention, when the deflection height (h) is 7 mm or less, it is “◯” as being excellent in stress relaxation properties, and when the deflection height exceeds this, “x” is assumed as being inferior in stress relaxation properties. did.

(6) Can openability evaluation After applying a predetermined pretreatment to the aluminum alloy plate produced under each condition shown in Table 1, an epoxy resin coating film having a thickness of 5 μm was applied on both sides, and the temperature was 250 ° C. Baked for 20 seconds.
Then, (3) Shell molding and (6) Conversion molding explained in the general manufacturing process for the packaging container lid and packaging container described above, the thickness of 0.30 mm, the remaining score of 110 μm It shape | molded so that it might become. An SOT (Stay On Tab) type tab 9 was attached to the packaging container lid 8 formed in this manner, and a test for openability was performed (see FIG. 5).
The can opening operation was performed using a reed measuring instrument open can testing machine 7 shown in FIG. A packaging container lid 8 having a tab 9 attached thereto is attached to the can opener tester 7, and a hook 71 of the can opener tester 7 is hooked on a hooking portion P of the tab 9. At the same time that the tab 9 was loaded, the packaging container lid 8 was rotated 90 degrees in the direction of the arrow X in FIG.
The case where the score crack propagated beyond the tab lengthwise extension E shown in FIG. 5C is indicated as “◯” when the can is opened without any problem, and the score crack did not propagate until the tab lengthwise extension E (half open) "X" as a problem.
Table 2 shows the results of each evaluation.

  As shown in Table 1, Example No. 1-4 satisfy the necessary conditions defined in the present invention, that is, the composition components, heating rate, holding temperature, cooling rate, cold rolling rate, and winding temperature, and are manufactured under such conditions. The aluminum alloy sheet can give excellent results in all evaluations of average grain size, yield strength after baking, elongation rate of parallel bending tensile test, ball head overhang formability, stress relaxation and can openability. It was.

On the other hand, Comparative Example No. 1 to 16 do not satisfy any of the necessary conditions defined in the present invention.
That is, Comparative Example No. 1 has a result that the stress relaxation property evaluation is inferior because the Cu content is out of the lower limit value of the necessary condition defined in the present invention, so that sufficient bake hard effect and stress relaxation property cannot be obtained. (X).
Comparative Example No. No. 2 is because the Cu content deviates from the upper limit of the necessary conditions defined in the present invention, the resulting aluminum alloy sheet is prone to ingot cracking and cracking during hot rolling, and the corrosion resistance is remarkably deteriorated. To do. That is, the obtained aluminum alloy plate was manufactured as an alloy plate with weak mechanical strength, the elongation rate of the parallel bending tensile test was low, and cracks occurred in the overhanging part for ball head overhanging formability. (X).

Comparative Example No. No. 3 has a problem in can openability because the Mn content deviates from the lower limit of the necessary conditions defined in the present invention, and the effect of maintaining the rigidity of the aluminum alloy sheet due to strength improvement is thin (×) .
Comparative Example No. No. 4, because the Mn content deviates from the upper limit of the necessary conditions defined in the present invention, a coarse Al-Fe-Mn intermetallic compound is generated, and the starting point of cracking during molding or buckling Therefore, the elongation rate in the parallel bending tensile test was low, and cracking occurred in the overhanging portion for the ball head overhanging formability (×).

Comparative Example No. 5, since the Mg content deviates from the lower limit of the requirements defined in the present invention, sufficient strength as an aluminum alloy plate for a packaging container lid cannot be obtained. In addition, the results of the can openability were inferior (×).
Comparative Example No. No. 6, because the Mg content deviates from the upper limit of the necessary conditions defined in the present invention, ingot cracking and cracking during hot rolling are likely to occur, and due to this, parallel bending The elongation rate of the tensile test was low, and cracking occurred in the overhanging portion with respect to the ball head overhanging formability (×).

Comparative Example No. No. 7, since the Si content is outside the lower limit of the necessary conditions defined in the present invention, the production amount of the Mg-Si intermetallic compound for improving the can openability is small, and the effect on the can openability Was low, and there was a problem in the can openability evaluation (×).
Comparative Example No. 8 is because the Si content deviates from the upper limit of the necessary conditions defined in the present invention, the material strength and the As a result of the Bakehard effect being lowered more than necessary, the elongation rate in the parallel bending tensile test was low, and cracks occurred in the overhanging portion in terms of ball head overhanging formability (×).

Comparative Example No. No. 9, since the Fe content deviates from the lower limit of the necessary conditions defined in the present invention, the crystal grains of the aluminum alloy contained in the aluminum alloy plate for the packaging container lid are coarsened, so the formability is reduced. To do. Therefore, rough skin was seen in the overhanging part (Δ). There was also a problem with can openability (×).
Comparative Example No. No. 10, since the Fe content deviates from the upper limit of the necessary conditions defined in the present invention, a huge Al—Fe—Mn intermetallic compound having a maximum length exceeding 20 μm is generated, and the formability Therefore, the elongation rate in the parallel bending tensile test was low, and cracking occurred in the ball head overhanging formability (×).

Comparative Example No. No. 11, because the cold rolling rate is out of the lower limit of the necessary conditions defined in the present invention, sufficient strength cannot be obtained as an aluminum alloy plate for a packaging container lid, and the proof strength after baking is low. Due to its weakness, the stress relaxation property was also inferior (x), the propagation of score cracks stopped in the middle, and there was a problem in the openability (×).
Comparative Example No. No. 12, because the cold rolling rate is out of the upper limit of the necessary conditions defined in the present invention, the degree of thermal softening of the rolling strain exceeds the effect of the bake hard, and the elongation rate in the parallel bending tensile test is low. As a result, the stress relaxation amount increased due to this, resulting in poor stress relaxation properties (×).

  Comparative Example No. No. 13, because the coiling temperature deviates from the lower limit value of the necessary conditions defined in the present invention, the elongation rate of the parallel bending tensile test after baking is low, so that the packaging container changes due to the change in the internal pressure of the packaging container. The winding part of the lid may be broken, making it unsuitable for use as a packaging container lid.

  Comparative Example No. No. 14, because the heating rate deviates from the lower limit value of the necessary conditions defined in the present invention, the crystal grain size of the aluminum alloy recrystallized grains is increased, the formability is lowered, and the ball head overhang formability is increased. Rough skin was seen at the exit (△).

  Comparative Example No. No. 15, since the holding temperature and the coiling temperature are out of the lower limit values of the necessary conditions defined in the present invention, a sufficient recrystallized grain structure of the aluminum alloy recrystallized grains cannot be obtained. The strength required for an aluminum alloy plate could not be obtained. Since the elongation rate of the parallel bending tensile test was low, the ball head overhanging formability and the stress relaxation property were also inferior (x).

  Comparative Example No. No. 16 has a cooling rate and a coiling temperature that are out of the lower limit values of the necessary conditions defined in the present invention, so that the solid solution state of the solid solution component cannot be maintained, and sufficient bake hard effects and stress relaxation properties are obtained. Since it could not be obtained, the stress relaxation property was inferior (x).

It is a flowchart explaining the manufacturing method of the aluminum alloy plate for packaging container lids of this invention. It is explanatory drawing of the method of a parallel bending tension test. It is a section explanatory view of a ball head overhang formability test. It is explanatory drawing of a stress relaxation test. It is explanatory drawing of a can openability test.

Claims (2)

0.05 to 0.3% by mass of Cu, 0.2 to 0.6% by mass of Mn, 2.0 to 5.5% by mass of Mg, and 0.05 to 0.3% by mass of Si %, Fe is regulated to 0.05 to 0.4% by mass, and the balance is composed of Al and inevitable impurities, and
An aluminum alloy plate having the above composition is manufactured with a thickness of 0.30 mm, and the aluminum alloy plate is baked for 20 seconds under a temperature condition of 250 ° C. with a salt bath, and then parallel to the rolling direction of the aluminum alloy plate. A test piece having a length of 100 mm and a width of 20 mm is prepared so that the direction is the longitudinal direction, and this is 90 degrees so that the tensile direction is a direction perpendicular to the rolling line of the test piece with a tip R0.1 mm punch. Bend into a V-shape, and return the folded test plate to a flat plate with two flat plates to make a creased plate. Pull the flat plate in the longitudinal direction to measure the amount of fracture limit displacement. Is 50 mm, and the packaging container lid aluminium is such that the breaking limit elongation obtained by {(breaking limit displacement (mm) / 50 (mm)) × 100} is 2% or more. A manufacturing method of an aluminum alloy plate for a packaging container lid for making no alloy plate,
A first step of performing a homogenization heat treatment of an ingot made of an aluminum alloy having the above composition;
A second step of hot-rolling the ingot subjected to the homogenization heat treatment in the first step;
A third step of cold rolling the rolled sheet hot-rolled in the second step;
A fourth step of annealing the rolled sheet that has been cold-rolled in the third step;
A fifth step of cold rolling the rolled sheet annealed in the fourth step;
A sixth step of winding the aluminum alloy plate cold-rolled in the fifth step around a coil,
In the annealing process in the fourth step, the cold-rolled rolled sheet is heated to 400 to 550 ° C. at a heating rate of 100 ° C./min or more, and the rolled sheet heated immediately after the heating process is 100 A process of cooling to 200 ° C. or lower at a cooling rate of at least C / min,
The cold rolling process is performed once so that the rolling rate of the cold rolling process in the fifth step is 50 to 80%,
Furthermore, the winding temperature to the coil in the said 6th process is 120 thru | or 150 degreeC. The manufacturing method of the aluminum alloy plate for packaging container lids characterized by the above-mentioned. 0.05 to 0.3% by mass of Cu, 0.2 to 0.6% by mass of Mn, 2.0 to 5.5% by mass of Mg, and 0.05 to 0.3% by mass of Si %, Fe is regulated to 0.05 to 0.4% by mass, and the balance is composed of Al and inevitable impurities, and
An aluminum alloy plate having the above composition is manufactured with a thickness of 0.30 mm, and the aluminum alloy plate is baked for 20 seconds under a temperature condition of 250 ° C. with a salt bath, and then parallel to the rolling direction of the aluminum alloy plate. A test piece having a length of 100 mm and a width of 20 mm is prepared so that the direction is the longitudinal direction, and this is 90 degrees so that the tensile direction is a direction perpendicular to the rolling line of the test piece with a tip R0.1 mm punch. Bend into a V-shape, and return the folded test plate to a flat plate with two flat plates to make a creased plate. Is 50 mm, and the packaging container lid aluminium is such that the breaking limit elongation obtained by {(breaking limit displacement (mm) / 50 (mm)) × 100} is 2% or more. A manufacturing method of an aluminum alloy plate for a packaging container lid for making no alloy plate,
A first step of performing a homogenization heat treatment of an ingot made of an aluminum alloy having the above composition;
A second step of hot-rolling the ingot subjected to the homogenization heat treatment in the first step;
A third step of cold rolling the rolled sheet hot-rolled in the second step;
A fourth step of annealing the rolled sheet that has been cold-rolled in the third step;
A fifth step of cold rolling the rolled sheet annealed in the fourth step;
A sixth step of winding the aluminum alloy plate cold-rolled in the fifth step around a coil,
In the annealing process in the fourth step, the cold-rolled rolled plate is heat-treated at a heating rate of 100 ° C./min or more, and the rolled plate heat-treated in the step is 400 to 550 ° C. within 10 minutes. A step of heating and holding, and a step of cooling the rolled plate heated and held in the above step to 200 ° C. or less at a cooling rate of 100 ° C./min or more,
The cold rolling process is performed once so that the rolling rate of the cold rolling process in the fifth step is 50 to 80%,
Furthermore, the winding temperature to the coil in the said 6th process is 120 thru | or 150 degreeC. The manufacturing method of the aluminum alloy plate for packaging container lids characterized by the above-mentioned.

Images