JP4067972B2 - 防弾用途向け擬似一方向布帛 - Google Patents
防弾用途向け擬似一方向布帛 Download PDFInfo
- Publication number
- JP4067972B2 JP4067972B2 JP2002587883A JP2002587883A JP4067972B2 JP 4067972 B2 JP4067972 B2 JP 4067972B2 JP 2002587883 A JP2002587883 A JP 2002587883A JP 2002587883 A JP2002587883 A JP 2002587883A JP 4067972 B2 JP4067972 B2 JP 4067972B2
- Authority
- JP
- Japan
- Prior art keywords
- fabric
- yarn
- ballistic
- yarns
- fabric according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
また、前記布帛は、前記第2のヤーンが、前記防弾性ヤーンの直径の14%以下の直径、好ましくは、前記防弾性ヤーンの直径の2.5%の直径を有することを特徴とする。
また、前記布帛は、前記第2のヤーンが、最大引張弾性率1777グラム/texを有することを特徴とする。
また、前記布帛は、前記第2のヤーンが、3%伸び時に、前記防弾性ヤーンの0.31%である最大強度を有することを特徴とする。
また、前記布帛は、前記防弾性ヤーンの1インチ当たりのヤーン数が、同じサイズの防弾性ヤーンですべて構成して平織布帛として織ることのできる最大タイトネスの40〜85%、好ましくは50%±1本であることを特徴とする。
また、前記防弾性布帛は、貫入抵抗が、前記複数層のすべてを貫通して前記布帛を縫い合わせることにより、改良されていることを特徴とする。
また、前記防弾性布帛は、前記複数層が、二重に積層された擬似一方向布帛で構成されていることを特徴とする。
本発明の目的は、防弾用途向けの布帛を提供することである。この布帛は、第2の織布内で安定化され、一方向に引揃えられた高性能防弾性経糸および緯糸ヤーンを有する。平織布帛および一方向に引揃えられた布帛がそれぞれ、図1および図2に図示されている。図1は、緯糸ヤーン12および経糸または緯糸ヤーン14を織り交ぜて有する平織10を示している。図2は、本発明によるいわゆる擬似一方向布帛20を示している。経糸および緯糸ヤーン22および24は、一方向に引揃えられて配置されており、織込まれたり、組み合わせられたりしていない。布帛20は、第2の布帛のヤーン26、28を織込んで具備している。
(実施例1)
実験用の布帛を、1330デシテックスのSpectra(登録商標)(伸びきり鎖ポリエチレン)経糸および緯糸ヤーンと、78デシテックスのナイロン経糸および緯糸ヤーンとから作製した。Spectra(登録商標)ヤーンは捻ったが、ナイロンヤーンは捻らなかった。Spectra(登録商標)ヤーンを第1の緒巻きから織機内に給送し、ナイロンヤーンを第2の緒巻きから給送した。
実験用の布帛を、1330デシテックスのSpectra(登録商標)経糸および緯糸ヤーンと、78デシテックスのナイロン経糸および緯糸ヤーンとから作製した。Spectra(登録商標)ヤーンは捻ったが、ナイロンヤーンは捻らなかった。Spectra(登録商標)を第1の緒巻きから織機内に給送し、ナイロンヤーンを第2の緒巻きから給送した。
実験用の布帛を、1330デシテックスのSpectra(登録商標)経糸および緯糸ヤーンと、78デシテックスのナイロン経糸および緯糸ヤーンとから作製した。Spectra(登録商標)ヤーンは捻ったが、ナイロンヤーンは捻らなかった。Spectra(登録商標)を第1の緒巻きから織機内に給送し、ナイロンヤーンを第2の緒巻きから給送した。異なる経糸ヤーンを布帛内に交互に配置した。すなわち、Spectra(登録商標)ヤーンの次にナイロンヤーンを配置して、これを布帛全体に繰返した。緯糸ヤーンも、Spectra(登録商標)ヤーンとナイロンヤーンとで交互にした。この布帛を平織布帛として織った。強度、弾性率および直径の違いを反映させるため、Spectra(登録商標)ヤーンを一方向に引揃え、ナイロンヤーンで、Spectra(登録商標)ヤーンを支持している、捲縮を設けた布帛を形成した。この布帛では、経糸方向においても緯糸方向においても、1インチ当たりSpectra(登録商標)ヤーンを10.5本、ナイロンヤーンを10.5本配置した。平織に織ることのできる1200デニールヤーンの最大数は、1インチ当たり25本である。防弾性ヤーンに対する包囲ヤーンの直径の割合は5.4%であった。仕上った布帛に、実施例1と同じ20重量%の熱可塑性エラストマをコーティングして、プリプレグを形成した。このプリプレグの25層を、230psiにて30分間、250°F(121℃)の温度でプレスした。このパネルを圧力下で200°F(93℃)まで冷却し、その後、圧力を解放した。こうして得られたパネルを、冷却用金属プレートに押付けて直ちに冷却した。このパネルの面積密度は、実施例1による比較パネルの面積密度とほぼ一致した。
布帛を、1330デシテックスのSpectra(登録商標)経糸および緯糸ヤーンと、78デシテックスのナイロン経糸および緯糸ヤーンとから作製した。Spectra(登録商標)経糸ヤーンは捻ったが、Spectra(登録商標)緯糸ヤーンは捻らなかった。ナイロンヤーンも捻らなかった。Spectra(登録商標)を第1の緒巻きから織機内に給送し、ナイロンヤーンを第2の緒巻きから給送した。異なる経糸ヤーンを布帛内に交互に配置した。すなわち、Spectra(登録商標)ヤーンの次にナイロンヤーンを配置して、これを布帛全体に繰返した。緯糸ヤーンも、Spectra(登録商標)ヤーンとナイロンヤーンとで交互にした。
3000デニールのKevlar(アラミド)擬似一方向布帛を、70デニールナイロンヤーンを安定化ヤーンとして用いて織った。このナイロンヤーンは、1インチ当たり2.5回捻られた、70デニール、34フィラメントでテクスチャのあるダルナイロン(dull nylon)であった。Kevlarヤーンの1インチ当たりのピック数は9であった。平織に織ることのできる3000デニールヤーンの最大数は、1インチ当たり18本である。防弾性ヤーンに対する包囲ヤーンの直径の割合は2.6%であった。この布帛を、実施例1と同じ熱可塑性エラストマをコーティングして、ハード防護具パネルとしてプレスした。こうして得られたパネルは、ヤーン0.88ポンド/平方フィートであった。このパネルに9mmの銃弾を射撃したところ、そのV50性能は、3000デニールのKevlarで織られた最良布帛の場合を35m/秒(16%)上回った。この布帛は11×11平織布帛である。防弾性パネルの重量は0.93ポンド/平方フィートであり、同じ樹脂系でプレスした。
840デニールのアラミド(Twaron)擬似一方向布帛を、70デニールナイロンヤーンを包囲ヤーンとして用いて織った。このナイロンヤーンは、1インチ当たり2.5回捻られた、70デニール、34フィラメントでテクスチャのあるダルナイロンであった。このアラミドヤーンの1インチ当たりのピック数は17であった。平織に織ることのできる840デニールヤーンの最大数は、1インチ当たり34本である。防弾性ヤーンに対する包囲ヤーンの直径の割合は9.4%であった。この布帛を積層して、それぞれ22層からなる布帛パネルを2セット形成した。第1のセットは縫い合わせず、第2のセットは、1.5インチ間隔の斜めステッチラインで縫い合わせた。縫い合わせたパネルに9mm銃弾を射撃したところ、そのV50性能は、縫い合わせなかったパネルの射撃結果を80メートル(35%)上回った。縫い合わせなかったパネルの射撃結果は一定せず、縫い合わせたパネルに対するV50の結果が、最低で81メートル下回った。
840デニールのアラミド(Twaron)擬似一方向布帛を、70デニールナイロンヤーンを包囲ヤーンとして用いて織った。このナイロンヤーンは、1インチ当たり2.5回捻られた、70デニール、34フィラメントでテクスチャのあるダルナイロンであった。このアラミドヤーンの1インチ当たりのピック数は17であった。平織に織ることのできる840デニールヤーンの最大数は、1インチ当たり34本である。防弾性ヤーンに対する包囲ヤーンの直径の割合は9.4%であった。得られた布帛の2層を、実施例1と同じ熱可塑性エラストマを用いて積層した。この樹脂の重量は、36g/m2であった。積層した布帛を、11層ずつからなる布帛パネルの2セットとして重ねた。第1のセットは縫い合わせず、第2のセットは、1.5インチ間隔の斜めステッチラインで縫い合わせた。縫い合わせたパネルに9mm銃弾を射撃したところ、そのV50性能は、縫い合わせなかったパネルの射撃結果を62メートル(15%)上回った。
840デニールのアラミド(Twaron)擬似一方向布帛を、40デニールヤーンを包囲ヤーンとして用いて織った。この包囲ヤーンは、40デニールのポリエステルヤーンであった。このアラミドヤーンの1インチ当たりのピック数は17であった。平織に織ることのできる840デニールヤーンの最大数は、1インチ当たり34本である。防弾性ヤーンに対する包囲ヤーンの直径の割合は5.4%であった。この布帛を、2つの布帛パネルとして縫い合わせた。パネル周囲をステッチラインで縫い合わせてパネルを形成した。これらのパネルのV50試験結果は、比較布帛から加工したパネルと同じであった。このパネルの面積密度(重量/単位面積)は、実験用パネルの面積密度と同じであった。コーティングを施したこの布帛は、27×27平織布帛であった。0.2%伸び時のポリエステルヤーンの割線弾性係数は、1777g/texであり、3%伸び時の最大強度は、防弾性ヤーンの0.31%であった。
本開示内容をまとめると、本発明は、一方向に引揃えられた防弾性ヤーンを、破断応力および引張弾性率がそれより実質的に低いヤーンで形成された第2の布帛内に織込むことにより安定化され、互いに90±5度をなす少なくとも2層として含む独自の布帛を提供するものである。本発明の範囲内で、さまざまな修正を加えることが可能である。
12 緯糸ヤーン
14 経糸ヤーン
20 擬似一方向布帛
22 緯糸ヤーン
24 経糸ヤーン
26 布帛のヤーン
28 布帛のヤーン
Claims (21)
- 布帛であって、一方向に引揃えられた防弾性ヤーンを、互いに90±5度で交差する少なくとも2層として有し、経方向及び緯方向において、前記防弾性ヤーンと、該防弾性ヤーンより破断応力および引張弾性率が実質的に低い第2のヤーンとを交互に配置して製織したことを特徴とする布帛。
- 前記防弾性ヤーンが、高性能防弾性ヤーンであることを特徴とする、請求項1に記載の布帛。
- 前記防弾性ヤーンが、少なくとも15グラム/デニールの破断応力を有し、その引張弾性率が少なくとも400グラム/デニールであることを特徴とする、請求項1または2に記載の布帛。
- 前記防弾性ヤーンが、アラミド繊維、伸びきり鎖ポリエチレン繊維、ポリ(p−フェニレン−2,6−ベンゾビスオキサゾール)(PBO)繊維およびガラス繊維からなる群から選択されることを特徴とする、請求項1から3のいずれかに記載の布帛。
- 前記第2のヤーンが、20〜1000デニールであることを特徴とする、請求項1から4のいずれかに記載の布帛。
- 前記第2のヤーンが、天然繊維、合成繊維及びガラス繊維からなる群から選択されることを特徴とする、請求項1から5のいずれかに記載の布帛。
- 前記天然繊維が、綿、羊毛、サイザル繊維、亜麻繊維、ジュートおよび絹から選択される請求項6に記載の布帛。
- 前記合成繊維が、再生セルロース、レーヨン、ポリノジックレーヨン、セルロースエステル、アクリル、モダクリル、ポリアミド、ポリオレフィン、ポリエステル、ゴム、合成ゴムおよびサラン繊維から選択される請求項6に記載の布帛。
- 前記合成繊維が、ポリアクリロニトリル、アクリロニトリル−塩化ビニルコポリマー、ポリヘキサメチレンアジポアミド、ポリカプラミド、ポリウンデカンアミド、ポリエチレン、ポリプロピレンおよびポリエチレンテレフタレート繊維から選択される請求項6に記載の布帛。
- 前記第2のヤーンが、高い伸びを有するものであることを特徴とする、請求項1から6のいずれかに記載の布帛。
- 前記第2のヤーンが、前記布帛に対する投射物による衝撃により、前記防弾性ヤーンより早く破断するものであることを特徴とする請求項10に記載の布帛。
- コーティングされているかまたは積層されたフィルムを有していることを特徴とする、
請求項1から11のいずれかに記載の布帛。 - 前記第2のヤーンが、前記防弾性ヤーンの直径の14%以下の直径を有することを特徴とする請求項1から12のいずれかに記載の布帛。
- 前記第2のヤーンが、前記防弾性ヤーンの直径の2.5%の直径を有することを特徴とする請求項13に記載の布帛。
- 前記第2のヤーンが、最大引張弾性率1777グラム/texを有することを特徴とする、請求項1から14のいずれかに記載の布帛。
- 前記第2のヤーンが、3%伸び時に、前記防弾性ヤーンの0.31%である最大強度を
有することを特徴とする、請求項1から15のいずれかに記載の布帛。 - 前記防弾性ヤーンの1インチ当たりのヤーン数が、同じサイズの防弾性ヤーンですべて構成して平織布帛として織ることができるときの最大ヤーン数である最大タイトネスの40〜85%であることを特徴とする、請求項1から16のいずれかに記載の布帛。
- 前記防弾性ヤーンの1インチ当たりのヤーン数が、前記最大タイトネスの50%±1本であることを特徴とする、請求項17に記載の布帛。
- 請求項1から18のいずれかに記載した布帛を複数層有することを特徴とする防弾性布帛。
- 貫入抵抗が、前記複数層のすべてを貫通して前記布帛を縫い合わせることにより、改良されていることを特徴とする、請求項19に記載の防弾性布帛。
- 前記複数層が、二重に積層された擬似一方向布帛で構成されていることを特徴とする請求項19または20に記載の防弾性布帛。