JP4056258B2 - 酸素ラジカル含有カルシウムアルミネートの製造方法 - Google Patents
酸素ラジカル含有カルシウムアルミネートの製造方法 Download PDFInfo
- Publication number
- JP4056258B2 JP4056258B2 JP2002030742A JP2002030742A JP4056258B2 JP 4056258 B2 JP4056258 B2 JP 4056258B2 JP 2002030742 A JP2002030742 A JP 2002030742A JP 2002030742 A JP2002030742 A JP 2002030742A JP 4056258 B2 JP4056258 B2 JP 4056258B2
- Authority
- JP
- Japan
- Prior art keywords
- calcium aluminate
- terms
- mass
- powder
- calcium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Links
- XFWJKVMFIVXPKK-UHFFFAOYSA-N calcium;oxido(oxo)alumane Chemical compound [Ca+2].[O-][Al]=O.[O-][Al]=O XFWJKVMFIVXPKK-UHFFFAOYSA-N 0.000 title claims description 57
- 229910052760 oxygen Inorganic materials 0.000 title claims description 56
- 239000001301 oxygen Substances 0.000 title claims description 56
- 238000004519 manufacturing process Methods 0.000 title claims description 15
- 239000000843 powder Substances 0.000 claims description 45
- 239000002994 raw material Substances 0.000 claims description 36
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 claims description 30
- 239000011575 calcium Substances 0.000 claims description 25
- 229910052782 aluminium Inorganic materials 0.000 claims description 17
- 229910052791 calcium Inorganic materials 0.000 claims description 17
- 229910018072 Al 2 O 3 Inorganic materials 0.000 claims description 14
- 229910004298 SiO 2 Inorganic materials 0.000 claims description 13
- 229910010413 TiO 2 Inorganic materials 0.000 claims description 12
- 238000002844 melting Methods 0.000 claims description 11
- 230000008018 melting Effects 0.000 claims description 11
- OYPRJOBELJOOCE-UHFFFAOYSA-N Calcium Chemical compound [Ca] OYPRJOBELJOOCE-UHFFFAOYSA-N 0.000 claims description 10
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims description 10
- 238000010298 pulverizing process Methods 0.000 claims description 8
- 238000010438 heat treatment Methods 0.000 claims description 6
- 238000000465 moulding Methods 0.000 claims description 6
- 150000004645 aluminates Chemical class 0.000 claims description 2
- 238000006243 chemical reaction Methods 0.000 claims description 2
- ULGYAEQHFNJYML-UHFFFAOYSA-N [AlH3].[Ca] Chemical compound [AlH3].[Ca] ULGYAEQHFNJYML-UHFFFAOYSA-N 0.000 claims 1
- ODINCKMPIJJUCX-UHFFFAOYSA-N Calcium oxide Chemical compound [Ca]=O ODINCKMPIJJUCX-UHFFFAOYSA-N 0.000 description 24
- 239000000292 calcium oxide Substances 0.000 description 12
- 235000012255 calcium oxide Nutrition 0.000 description 12
- 239000007789 gas Substances 0.000 description 12
- 150000001875 compounds Chemical class 0.000 description 11
- 238000000034 method Methods 0.000 description 11
- 230000035699 permeability Effects 0.000 description 11
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 description 9
- 230000003647 oxidation Effects 0.000 description 7
- 238000007254 oxidation reaction Methods 0.000 description 7
- 238000002441 X-ray diffraction Methods 0.000 description 6
- 239000003054 catalyst Substances 0.000 description 6
- 230000000052 comparative effect Effects 0.000 description 6
- 239000000126 substance Substances 0.000 description 6
- VTYYLEPIZMXCLO-UHFFFAOYSA-L Calcium carbonate Chemical compound [Ca+2].[O-]C([O-])=O VTYYLEPIZMXCLO-UHFFFAOYSA-L 0.000 description 4
- MCMNRKCIXSYSNV-UHFFFAOYSA-N Zirconium dioxide Chemical compound O=[Zr]=O MCMNRKCIXSYSNV-UHFFFAOYSA-N 0.000 description 4
- 239000000203 mixture Substances 0.000 description 4
- 238000001069 Raman spectroscopy Methods 0.000 description 3
- 238000010521 absorption reaction Methods 0.000 description 3
- 239000003242 anti bacterial agent Substances 0.000 description 3
- 239000013078 crystal Substances 0.000 description 3
- 238000001362 electron spin resonance spectrum Methods 0.000 description 3
- 238000005245 sintering Methods 0.000 description 3
- 238000003746 solid phase reaction Methods 0.000 description 3
- 238000001228 spectrum Methods 0.000 description 3
- 238000009681 x-ray fluorescence measurement Methods 0.000 description 3
- 235000019738 Limestone Nutrition 0.000 description 2
- 229910001570 bauxite Inorganic materials 0.000 description 2
- 230000015572 biosynthetic process Effects 0.000 description 2
- 229910000019 calcium carbonate Inorganic materials 0.000 description 2
- AXCZMVOFGPJBDE-UHFFFAOYSA-L calcium dihydroxide Chemical compound [OH-].[OH-].[Ca+2] AXCZMVOFGPJBDE-UHFFFAOYSA-L 0.000 description 2
- 239000000920 calcium hydroxide Substances 0.000 description 2
- 235000011116 calcium hydroxide Nutrition 0.000 description 2
- 229910001861 calcium hydroxide Inorganic materials 0.000 description 2
- 239000004568 cement Substances 0.000 description 2
- 238000002425 crystallisation Methods 0.000 description 2
- 230000008025 crystallization Effects 0.000 description 2
- 230000000694 effects Effects 0.000 description 2
- XLYOFNOQVPJJNP-UHFFFAOYSA-M hydroxide Chemical compound [OH-] XLYOFNOQVPJJNP-UHFFFAOYSA-M 0.000 description 2
- 229910052500 inorganic mineral Inorganic materials 0.000 description 2
- 239000006028 limestone Substances 0.000 description 2
- 238000005259 measurement Methods 0.000 description 2
- 235000010755 mineral Nutrition 0.000 description 2
- 239000011707 mineral Substances 0.000 description 2
- 238000004435 EPR spectroscopy Methods 0.000 description 1
- 229910052783 alkali metal Inorganic materials 0.000 description 1
- 150000001340 alkali metals Chemical group 0.000 description 1
- 150000001450 anions Chemical class 0.000 description 1
- 239000003153 chemical reaction reagent Substances 0.000 description 1
- 239000011362 coarse particle Substances 0.000 description 1
- 239000000470 constituent Substances 0.000 description 1
- 238000007796 conventional method Methods 0.000 description 1
- 238000001816 cooling Methods 0.000 description 1
- 238000001035 drying Methods 0.000 description 1
- 238000001125 extrusion Methods 0.000 description 1
- 238000010304 firing Methods 0.000 description 1
- 239000000446 fuel Substances 0.000 description 1
- 238000001746 injection moulding Methods 0.000 description 1
- 239000010416 ion conductor Substances 0.000 description 1
- 150000002500 ions Chemical class 0.000 description 1
- 230000001678 irradiating effect Effects 0.000 description 1
- 230000001590 oxidative effect Effects 0.000 description 1
- 125000004430 oxygen atom Chemical group O* 0.000 description 1
- 239000002245 particle Substances 0.000 description 1
- 238000005192 partition Methods 0.000 description 1
- 239000012071 phase Substances 0.000 description 1
- 230000005855 radiation Effects 0.000 description 1
- 239000007787 solid Substances 0.000 description 1
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Chemical compound O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 1
Landscapes
- Compositions Of Oxide Ceramics (AREA)
- Compounds Of Alkaline-Earth Elements, Aluminum Or Rare-Earth Metals (AREA)
Priority Applications (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| JP2002030742A JP4056258B2 (ja) | 2002-02-07 | 2002-02-07 | 酸素ラジカル含有カルシウムアルミネートの製造方法 |
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| JP2002030742A JP4056258B2 (ja) | 2002-02-07 | 2002-02-07 | 酸素ラジカル含有カルシウムアルミネートの製造方法 |
Publications (3)
| Publication Number | Publication Date |
|---|---|
| JP2003226571A JP2003226571A (ja) | 2003-08-12 |
| JP2003226571A5 JP2003226571A5 (https=) | 2005-07-14 |
| JP4056258B2 true JP4056258B2 (ja) | 2008-03-05 |
Family
ID=27750398
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| JP2002030742A Expired - Fee Related JP4056258B2 (ja) | 2002-02-07 | 2002-02-07 | 酸素ラジカル含有カルシウムアルミネートの製造方法 |
Country Status (1)
| Country | Link |
|---|---|
| JP (1) | JP4056258B2 (https=) |
Cited By (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JPWO2013051576A1 (ja) * | 2011-10-07 | 2015-03-30 | 旭硝子株式会社 | 導電性マイエナイト化合物焼結体、スパッタリング用ターゲット、および導電性マイエナイト化合物焼結体の製造方法 |
Families Citing this family (8)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JP4010414B2 (ja) * | 2003-01-21 | 2007-11-21 | 電気化学工業株式会社 | 酸素ラジカル含有カルシウムアルミネート膜の製造方法と積層体 |
| TWI283234B (en) | 2004-02-13 | 2007-07-01 | Asahi Glass Co Ltd | Method for preparing electroconductive Mayenite type compound |
| JP4708857B2 (ja) * | 2005-05-16 | 2011-06-22 | 電気化学工業株式会社 | 成形体、その製造方法とそれを用いた酸化反応促進方法 |
| JP5061427B2 (ja) * | 2005-05-27 | 2012-10-31 | 旭硝子株式会社 | 導電性マイエナイト型化合物の製造方法 |
| EP1900689B1 (en) * | 2005-05-30 | 2016-03-30 | Asahi Glass Company, Limited | Process for producing electroconductive mayenite compound |
| KR101245943B1 (ko) | 2005-05-30 | 2013-03-21 | 도오쿄 인스티튜드 오브 테크놀로지 | 도전성 마이에나이트형 화합물의 제조 방법 |
| JP2008013396A (ja) * | 2006-07-05 | 2008-01-24 | Kansai Paint Co Ltd | 複合金属酸化物及び導電性複合金属酸化物の製造方法 |
| JP5058880B2 (ja) * | 2007-06-19 | 2012-10-24 | 日本碍子株式会社 | 導電性セラミックス材料 |
-
2002
- 2002-02-07 JP JP2002030742A patent/JP4056258B2/ja not_active Expired - Fee Related
Cited By (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JPWO2013051576A1 (ja) * | 2011-10-07 | 2015-03-30 | 旭硝子株式会社 | 導電性マイエナイト化合物焼結体、スパッタリング用ターゲット、および導電性マイエナイト化合物焼結体の製造方法 |
Also Published As
| Publication number | Publication date |
|---|---|
| JP2003226571A (ja) | 2003-08-12 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Salomão et al. | Mechanism of pore generation in calcium hexaluminate (CA6) ceramics formed in situ from calcined alumina and calcium carbonate aggregates | |
| Ganesh et al. | Formation and densification behavior of magnesium aluminate spinel: the influence of CaO and moisture in the precursors | |
| US8173085B2 (en) | Process for producing an oxide | |
| Rashad et al. | Characteristics of porous mullite developed from clay and AlF3· 3H2O | |
| Ganesh et al. | Effect of fuel type on morphology and reactivity of combustion synthesised MgAl2O4 powders | |
| Abbass et al. | From dolomite waste to katoite-based binder: synthesis, performance and characterization | |
| Yang et al. | Properties and microstructure of CO2 activated binder produced by recycling phosphorous slag | |
| Peyne et al. | Feasibility of producing geopolymer binder based on a brick clay mixture | |
| JP4056258B2 (ja) | 酸素ラジカル含有カルシウムアルミネートの製造方法 | |
| Maheswaran et al. | Low-temperature preparation of belite from lime sludge and nanosilica through solid-state reaction | |
| Ganesh et al. | Formation and densification behavior of MgAl2O4 spinel: the influence of processing parameters | |
| Gineika et al. | Synthesis and characterisation of wollastonite with aluminium and fluoride ions | |
| Zhang et al. | Feasibility of producing non-fired compressed masonry units from brick clay mill residues by alkali activation | |
| WO2014050900A1 (ja) | 高電子密度の導電性マイエナイト化合物の製造方法 | |
| Nagaoka et al. | Forming and sintering of porous calcium-hexaaluminate ceramics with hydraulic alumina | |
| Liu et al. | Effect of titanium chelating compound on hydration resistance of CaO material | |
| Hu et al. | CO2-induced high calcium magnesite tailings for enhanced performance of magnesium oxysulfate cement: Investigation on hydration kinetics, microstructural evolution, and chloride resistance | |
| Miao et al. | Effect of nano-TiO2 and nano-SiO2 addition on the morphological control of α-Al2O3 platelets via solid-state reaction | |
| Ribeiro et al. | Effect of water content and MgO/ADP ratio on the properties of magnesium phosphate cement | |
| Heraiz et al. | Effect of MgO addition and sintering parameters on mullite formation through reaction sintering kaolin and alumina | |
| Kurama et al. | Magnesium hydroxide recovery from magnesia waste by calcinations and hydration processes | |
| Ribeiro et al. | Effect of MgO/NH4H2PO4 ratio on the properties of magnesium phosphate cements | |
| Side et al. | Characterization of Natural Clay from Gowa Regency, South Sulawesi Province, Indonesia | |
| Mei et al. | Fabrication and characterization of porous ZnAl2O4 ceramics | |
| 長岡孝明 et al. | Fabrication of porous alumina ceramics by new eco-friendly process |
Legal Events
| Date | Code | Title | Description |
|---|---|---|---|
| A521 | Request for written amendment filed |
Free format text: JAPANESE INTERMEDIATE CODE: A523 Effective date: 20041110 |
|
| A621 | Written request for application examination |
Free format text: JAPANESE INTERMEDIATE CODE: A621 Effective date: 20041110 |
|
| A977 | Report on retrieval |
Free format text: JAPANESE INTERMEDIATE CODE: A971007 Effective date: 20071022 |
|
| A131 | Notification of reasons for refusal |
Free format text: JAPANESE INTERMEDIATE CODE: A131 Effective date: 20071030 |
|
| A521 | Request for written amendment filed |
Free format text: JAPANESE INTERMEDIATE CODE: A523 Effective date: 20071112 |
|
| TRDD | Decision of grant or rejection written | ||
| A01 | Written decision to grant a patent or to grant a registration (utility model) |
Free format text: JAPANESE INTERMEDIATE CODE: A01 Effective date: 20071211 |
|
| A61 | First payment of annual fees (during grant procedure) |
Free format text: JAPANESE INTERMEDIATE CODE: A61 Effective date: 20071211 |
|
| R150 | Certificate of patent or registration of utility model |
Free format text: JAPANESE INTERMEDIATE CODE: R150 |
|
| FPAY | Renewal fee payment (event date is renewal date of database) |
Free format text: PAYMENT UNTIL: 20101221 Year of fee payment: 3 |
|
| FPAY | Renewal fee payment (event date is renewal date of database) |
Free format text: PAYMENT UNTIL: 20111221 Year of fee payment: 4 |
|
| FPAY | Renewal fee payment (event date is renewal date of database) |
Free format text: PAYMENT UNTIL: 20111221 Year of fee payment: 4 |
|
| FPAY | Renewal fee payment (event date is renewal date of database) |
Free format text: PAYMENT UNTIL: 20121221 Year of fee payment: 5 |
|
| FPAY | Renewal fee payment (event date is renewal date of database) |
Free format text: PAYMENT UNTIL: 20121221 Year of fee payment: 5 |
|
| FPAY | Renewal fee payment (event date is renewal date of database) |
Free format text: PAYMENT UNTIL: 20131221 Year of fee payment: 6 |
|
| LAPS | Cancellation because of no payment of annual fees |