JP3945086B2 - Light-shielding packaging material - Google Patents
Light-shielding packaging material Download PDFInfo
- Publication number
- JP3945086B2 JP3945086B2 JP27614999A JP27614999A JP3945086B2 JP 3945086 B2 JP3945086 B2 JP 3945086B2 JP 27614999 A JP27614999 A JP 27614999A JP 27614999 A JP27614999 A JP 27614999A JP 3945086 B2 JP3945086 B2 JP 3945086B2
- Authority
- JP
- Japan
- Prior art keywords
- light
- packaging material
- ink layer
- printing ink
- shielding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】
【発明の属する技術分野】
本発明は、一般食品、医薬品、トイレタリー商品その他の生活資材や各種産業資材等またはレトルト食品の包装材料に関するものであり、さらに詳しくは、包装材料の脱アルミニウムによる環境負荷を減らし、かつガスバリアー性や遮光性を高めることによって内容物の保存性を高める遮光性包装材に関する。
【０００２】
【従来の技術】
従来、酸素や水分等の影響を受けて食品その他の内容物の品質が低下することを防ぐため、包装材料にガスバリアー性を持たせた包装材が利用されている。このガスバリアー性包装材としては、ポリビニルアルコールとエチレンビニルアルコールとの共重合体やポリ塩化ビニリデン系の樹脂からなるフィルム、あるいはこれらの樹脂をコーティングしたフィルム等があるが、焼却処理での塩素ガス発生やダイオキシン発生の問題から使用されなくなった。
【０００３】
これに対し、ガスバリアー性の点で最も優れているのはプラスチックフィルムにアルミ箔をラミネートしたものやアルミ蒸着層を設けた積層フィルムを利用したいわゆるアルミ包装材があった。
【０００４】
ところが、上記アルミ包装材では、昨今の廃棄物に係わる環境問題即ち廃棄物の焼却処理において、アルミニウムインゴットが焼却炉を傷めたり焼却効率の低下をもたらしたり、あるいはその焼却灰の埋め立て処分時に、雨等と反応し有害ガスが発生するなどの問題から、包装材の脱アルミ化への要求が高まってきており、その代わりに酸化珪素等の金属化合物の薄膜層を有するフィルムを利用した透明ガスバリアフィルムが利用され始めている。これは従来の透明バリアーフィルムであるポリビニルアルコールや塩化ビニリデン系のフィルムよりガスバリアー性に優れ、しかも上記アルミ系の包装材に近いガスバリア性を実現しているものである。
【０００５】
また、従来レトルト用のパウチ包装材としても、アルミニウム箔を含む構成の包装材が使用されている。それは、レトルト食品が６ヶ月から１年という長期間保存されることから、酸素による酸化を防止するため脱気包装されるので、包装材にガスバリア性が要求されるからである。また、光による劣化を防止するための遮光性の要求をも満足するアルミニウム箔を含む包装材が広く使用されていた。しかし前述のように、廃棄物に係わる環境問題発生の理由と、さらにレトルトパウチごと電子レンジに入れたいという要求と、内容物充填時に金属探知機による検査を可能にするものとして、脱アルミ化の要求が高まっており、上記の金属化合物の薄膜層を有する透明ガスバリアフィルムが利用され始めている。
【０００６】
【発明が解決しようとする課題】
しかしながら、これらの金属酸化物の薄膜層を有する透明バリアー包装材は遮光性がないため、アルミ系の包装材に比べて内容物が光による劣化を受けやすいという欠点がある。すなわち内容物の油脂成分の酸化あるいは色素や香り成分の分解等のように光による劣化を受けやすいという欠点があり、内容物によっては、保存性を高めるために、さらに遮光性を付加したバリア性包装材が要望されていた。さらに、できれば透明性の維持が可能なことや見た目に黒ずんでいないデザイン効果を有する遮光性包装材も望まれている。
【０００７】
本発明は、かかる従来技術の問題点および要望点を解決するものであり、その課題とするところは、透明バリアーフィルムに遮光性を付与することによって、アルミニウム箔を含む包装材に見られる廃棄物に係わる環境負荷が軽減され、かつガスバリアー性と遮光性の両方を有し、さらにデザイン効果を有しできれば透明性も付与した遮光性包装材を提供することにある。
【０００８】
【課題を解決するための手段】
本発明において上記課題を達成するために、まず請求項１の発明では、少なくとも外側からガスバリアー性を有する透明バリアーフィルム、少なくとも第一印刷インキ層、第二印刷インキ層の２層以上のインキ層からなる印刷インキ層、熱融着樹脂層が順に積層してなる遮光性包装材であって、上記印刷インキ層の第一印刷インキ層を白色グラビアインキ層、第二印刷インキ層を墨グラビアインキ層としたことを特徴とする遮光性包装材としたものである。
【０００９】
また、請求項２の発明では、少なくとも外側からガスバリアー性を有する透明バリアーフィルム、少なくとも第一印刷インキ層、第二印刷インキ層の２層以上のインキ層からなる印刷インキ層、熱融着樹脂層が順に積層してなる遮光性包装材であって、上記印刷インキ層の第一印刷インキ層を有機系の紫外線吸収インキ層、第二印刷インキ層を藍色グラビアインキ層としたことを特徴とする遮光性包装材としたものである。
【００１０】
また、請求項３の発明では、前記熱融着樹脂層と印刷インキ層の間に、ナイロンフィルムが積層されていることを特徴とする請求項１記載の遮光性包装材としたものである。
【００１８】
【発明の実施の形態】
以下本発明の実施の形態を図面を用いながら説明する。
本発明は、一般食品、医薬品等またはレトルト食品の包装材料、特に脱アルミニウムによる環境負荷を減らし、かつガスバリアー性や遮光性を高めて内容物の保存性を高める遮光性包装材に関するもので、その基本構成は、図１の積層側断面図に示すように、少なくとも外側からガスバリアー性を有する透明バリアーフィルム（３０）、印刷インキ層（１０）、熱融着樹脂層（２０）が順に積層している遮光性包装材（１）である。
【００１９】
そこで、まず請求項２の発明では、図２の積層側断面図に示すように、例えば最外層の基材フィルム（３２）とガスバリア層（３４）でなるガスバリアー性を有する透明バリアーフィルム（３０）と最内層のシーラントとなる熱融着樹脂層（２０）の間に、１層以上（一事例である図面では第一印刷インキ層（１２）と第二印刷インキ層（１４）からなる）の印刷インキ層（１０）を形成した遮光性包装材（１）とするものであって、その印刷インキ層（１０）を含めた包装材が３００ｎｍ〜４００ｎｍの波長域および６００ｎｍ〜７００ｎｍの波長域の光を遮断するものである。
【００２０】
上記のような印刷インキ層（１０）を施すことによって、外光の近紫外線と近赤外線が遮断され、例えば抹茶キャンディのような内容物の色素や香り成分の劣化のない遮光性包装材（１）とすることができる。さらにこの効果に加えて、内容物が透けて見えることも可能な遮光性包装材（１）とすることができる。
【００２１】
また、請求項１の発明の遮光性包装材では、図２に示す構成の印刷インキ層（１０）が１層以上で、その印刷インキ層（１０）を含む包装材が、３００ｎｍ〜８００ｎｍの波長域の光を遮断するものである。
【００２２】
上記のような印刷インキ層（１０）を施すことによって、外光全域が遮断され、アルミニウム包装材の場合と同様に内容物が透けて見える効果はないが、例えばポテトチップスや粉末海苔をまぶしてあるタイプのポテトチップスのような内容物の油脂の酸化のない遮光性包装材（１）とすることができる。
【００２３】
また、本発明の参考例としての遮光性包装材は、図２に示す構成の前記印刷インキ層（１０）が１層以上で、その印刷インキ層（１０）を含めた包装材が３００ｎｍ〜５００ｎｍの波長域の光を遮断するものである。
【００２４】
上記のような印刷インキ層（１０）を施すことによって、外光の短波長側が遮断され、例えば粉末海苔をまぶしてあるタイプのポテトチップスのような内容物の油脂の酸化を防ぐことはできないが、ポテトチップスのような内容物の油脂の酸化のない遮光性包装材（１）とすることができ、かつ外面から見た目には、黒ずんで見えず比較的明るいデザイン効果のある遮光性包装材（１）とすることができる。
【００２５】
また、請求項３の発明の遮光性包装材では、図３の積層側断面図に示すように、熱融着樹脂層（２０）と印刷インキ層（１０）との間に、ナイロンフィルム（４０）が積層され、その印刷インキ層（１０）が２層以上（図面では第一印刷インキ層（１２）と第二印刷インキ層（１４）としてある）でなる遮光性包装材とするものである。
【００２６】
上記のように、厚さ５０μｍ程度のナイロンフィルム（４０）を積層することによって、加熱滅菌等に耐性のあるレトルト用の遮光性包装材（１）とすることができ、２層以上の印刷インキ層（１０）とすることによって遮光性付与に加え、透明バリアーフィルム（３０）のガスバリアー性を補完することができる。
【００２７】
また、本発明の参考例としての発明の遮光性包装材では、例えば図３に示す２層でなる印刷インキ層（１０）を含む遮光性包装材（１）が、３００ｎｍ〜５００ｎｍの波長域の光を遮断するようにしたものである。
【００２８】
上記のような印刷インキ層（１０）を施すことによって、外光の短波長側が遮断され、例えばレトルト食品であるビーフシチューのような内容物の油脂の酸化を防ぐことができ、またレトルト食品としてのパンプキンスープのような内容物の褪色をある程度防ぐ遮光性包装材（１）とすることができ、かつ外面から見た目には、黒ずんで見えず比較的明るいデザイン効果のあるレトルト食品用の遮光性包装材（１）とすることができる。
【００２９】
また、本発明の参考例としての発明の遮光性包装材では、例えば図３に示す２層でなる印刷インキ層（１０）を含めた遮光性包装材（１）が、３００ｎｍ〜５５０ｎｍの波長域の光を遮断するようにしたものである。
【００３０】
上記のような印刷インキ層（１０）を施すことによって、外光の短波長側が遮断され、例えばレトルト食品であるビーフシチューのような内容物の油脂の酸化を防ぐことができ、またレトルト食品としてのパンプキンスープのような内容物の褪色をある程度防ぐ遮光性包装材（１）とすることができ、かつ外面から見た目には、黒ずんで見えずやや茶色系であるが比較的明るいデザイン効果のあるレトルト食品用の遮光性包装材（１）とすることができる。
【００３１】
また、本発明の参考例としての発明の遮光性包装材では、例えば図３に示す２層でなる印刷インキ層（１０）を含めた遮光性包装材（１）が、少なくとも３００ｎｍ〜７００ｎｍの波長域の光を遮断するようにしたものである。
【００３２】
上記のような印刷インキ層（１０）を施すことによって、略外光全域が遮断され、例えばレトルト食品であるビーフシチューのような内容物の油脂の酸化を従来のアルミニウム箔と同程度防ぐことができ、またレトルト食品としてのパンプキンスープのような内容物の褪色も略完全に防ぐ遮光性包装材（１）とすることができるが、外面から見た目には、黒ずんで見え、デザイン効果に少々劣るレトルト食品用の遮光性包装材（１）が得られる。
【００３３】
【実施例】
以下に本発明における遮光性包装材を用いて、ポテトチップス、粉末海苔をまぶしてあるタイプのポテトチップス（以下のり塩ポテトチップスという）、抹茶キャンディーをそれぞれ包装し、またレトルト食品としてのビーフシチュー、パンプキンスープをそれぞれ加熱殺菌後包装し、光照射下で保存したときの内容物品質低下の度合いを、実施例に示す包装材を用いて、比較例の包装材と比較しながら具体的に説明する。
【００３４】
実施例に使用する内容物として油分を含むポテトチップスやのり塩ポテトチップス、ビーフシチューなどは、光の影響で油脂の酸化を受けやすく、また、抹茶キャンディーなどは特定波長域の光の影響で色素や香り成分の分解等があり、レトルト食品としてのパンプキンスープなどは光の影響で褪色して食品としての付加価値が劣るものがあり、これが品質劣化の大きな要因となっており、これを防ぐため現状ではほとんどアルミニウム系の包装材が用いられている。本発明は廃棄物処理に係わる環境問題のあるアルミニウムを用いずに、そのアルミニウム系包装材と同等の保存性を持つ遮光性包装材を提供するものであり、よって本実施例ではアルミ系包材との比較の試験例を示すが、本発明による遮光性包材の保存性能がアルミニウム系包装材の保存性と同等であれば十分にその目的に達するものである。
【００３５】
また、本実施例では特定波長域の光の透過を遮断するのに特定の色のインキ及びその組み合わせを例示したが、本発明はその目的とする特定波長域の光の遮断を実現できれば、例示した色のインキおよびその組み合わせに限定されない。また例示した内容物も限定されるものでなく、それぞれの包材の光遮断波長の範囲に内容物の劣化に関与する光波長が含まれていれば効果を発揮する。
【００３６】
〈実施例１〉
図２に示すように、基材フィルム（３２）として厚さ１２μｍのポリエチレンテレフタレートフィルムにガスバリアー層（３４）として酸化アルミニウムの薄膜層を蒸着させた透明バリアーフィルム（３０）とし、これに第一印刷インキ層（１２）に白色グラビアインキを、第二印刷インキ層（１４）として墨グラビアインキを、それぞれベタ（日本印刷学会編：印刷事典よれば、印刷面に濃淡の差や白く抜けた部分がなく、印刷インキで完全に覆われている部分）印刷した印刷インキ層（１０）を設け、さらにシーラントとなる熱融着樹脂層（２０）として厚さ３０μｍの無延伸ポリプロピレンフィルムをドライラミネートによって張り合わせ、遮光性包装材（１）とした。本包装材（１）は３００ｎｍから８００ｎｍの波長域の光の透過は完全に遮断するものであった。
【００３７】
〈参考例１〉
図２に示す第二印刷インキ層（１４）を朱色グラビアインキとした以外は、実施例１と同様にして遮光性包装材（１）を得た。本包装材（１）は３００ｎｍから５５０ｎｍの波長域の光の透過は完全に遮断するものであった。
【００３８】
〈参考例２〉
図２に示す第二印刷インキ層（１４）を黄色グラビアインキとした以外は、実施例１と同様にして遮光性包装材（１）を得た。本包装材（１）は３００ｎｍから５００ｎｍの波長域の光の透過は完全に遮断するものであった。
【００３９】
〈実施例２〉
図２に示す基材フィルム（３２）として、厚さ１２μｍの延伸ポリプロピレンフィルムに、ガスバリアー層（３４）として水溶性高分子と金属アルコキシドまたはその加水分解物を含む層をコーティングにより形成させた透明バリアーフィルム（３０）とし、これに第一印刷インキ層（１２）として有機系の紫外線吸収インキ（東洋インキ製造社製、ＮＥＷ-ＬＰスーパーＶ白）を、第二印刷インキ層（１４）として藍色グラビアインキをそれぞれベタ印刷した印刷インキ層（１０）を設けた以外は、実施例１と同様にして遮光性包装材（１）を得た。本包装材は３００ｎｍから４００ｎｍおよび５８０から７３０の波長域の光の透過は完全に遮断するものであった。
【００４０】
〈比較例１〉
印刷インキ層（１０）を施さない以外は、実施例１と同様にしてバリアー包装材を得た。本包装材は、３００ｎｍ以上の波長の光はほとんど透過するものであった。
【００４１】
〈比較例２〉
ガスバリアー層（３４）としてアルミニウムの薄膜層を蒸着させた層とした以外は、比較例１と同様にしてバリアー包装材を得た。本包装材は、３００ｎｍから８００ｎｍの波長域の光の透過は完全に遮断するものであった。
【００４２】
実施例１、２、参考例１、２および比較例１、２の包装材を用いて、ポテトチップス、のり塩ポテトチップスおよび抹茶キャンディーをそれぞれ包装し、１５００ＬＸ蛍光灯照射、室温下で保存した時の品質の劣化度合いを、ポテトチップおよびのり塩ポテトチップスについては油脂の酸化度（過酸化物価）の分析値で、抹茶キャンディーについては色の変化を外観で評価した。そのポテトチップスでの結果を表１に、のり塩ポテトチップスでの結果を表２に、抹茶キャンディーでの結果を表３に示した。
【００４３】
【表１】
【表２】
【表３】
上記表１より、内容物がポテトチップの場合では、すなわち少なくとも３００〜５００ｎｍの波長域の光を遮断する実施例１、参考例１、２の遮光性バリアー包装材（１）を用いることで比較例１の包装材よりも格段に内容物保存性が向上することがわかる。中でも３００〜８００ｎｍの波長域を遮断する実施例１の遮光性バリアー包装材（１）では比較例２のアルミニウム系包装材と完全に同等の内容物保存性（油脂の酸化度の少ない）を示した。
【００４７】
また、上記表２より、内容物がのり塩ポテトチップの場合では、３００〜８００ｎｍの波長域を遮断する実施例１の遮光性バリアー包装材（１）で比較例２のアルミニウム系包装材と同等の保存性（油脂の酸化度の少ない）を示した。
【００４８】
また、内容物が抹茶キャンディーの場合では、３００〜４００ｎｍおよび６００〜７００ｎｍの波長域を遮断する実施例２の遮光性バリアー包装材で、３００〜８００ｎｍの波長域を遮断する実施例１の遮光性バリアー包装材と同様に比較例２のアルミニウム系包装材とほとんど遜色の無い内容物保存性（色素や香り成分の分解のない）を示した。さらに実施例４の遮光性バリアー包装材では、内容物が透けて見える効果（すなわち内容物の確認可能な効果）を有するものであった。
【００４９】
〈参考例３〉
図３に示すように、基材フィルム（３２）として厚さ１２μｍのポリエチレンテレフタレートフィルムに、ガスバリアー層（３４）として酸化アルミニウムの薄膜層を蒸着させた透明バリアーフィルム（３０）とし、これに第一印刷インキ層（１２）に白色グラビアインキを、第二印刷インキ層（１４）として黄色グラビアインキを、それぞれベタ印刷した印刷インキ層（１０）を設け、その上に、厚さ６０μｍのナイロンフィルム（４０）を、さらにシーラントとなる熱融着樹脂層（２０）として厚さ３０μｍの無延伸ポリプロピレンフィルムをドライラミネートによって張り合わせ、レトルト用の遮光性包装材（１）とした。本包装材（１）は３００ｎｍから５００ｎｍの波長域の光の透過は完全に遮断するものであった。
【００５０】
〈参考例４〉
図３に示す第二印刷インキ層（１４）を茶色グラビアインキとした以外は、実施例５と同様にしてレトルト用の遮光性包装材（１）とした。本包装材（１）は３００ｎｍから５５０ｎｍの波長域の光の透過は完全に遮断するものであった。
【００５１】
〈実施例３〉
図３に示す第二印刷インキ層（１４）を墨グラビアインキとした以外は、参考例３と同様にしてレトルト用の遮光性包装材（１）とした。本包装材（１）は３００ｎｍから８００ｎｍの波長域の光の透過は完全に遮断するものであった。
【００５２】
〈比較例３〉
厚さ１２μｍのポリエチレンテレフタレートフィルムに、厚さ６０μｍのナイロンフィルム、厚さ７μｍのアルミニウム箔、厚さ３０μｍの無延伸ポリプロピレンフィルムを順にドライラミネートによって張り合わせ、レトルト用の遮光性包装材とした。本包装材（１）は３００ｎｍから８００ｎｍの波長域の光の透過は完全に遮断するものであった。
【００５３】
〈比較例４〉
図３に示す第二印刷インキ層（１４）を白色グラビアインキ即ち第一、第二印刷インキ層（１２，１４）とも白色グラビアインキとした以外は、実施例５と同様にしてレトルト用の遮光性包装材（１）とした。本包装材（１）は３００ｎｍから４００ｎｍの波長域の光の透過は完全に遮断するものであった。
【００５４】
〈比較例５〉
図３に示す印刷インキ層（１０）を除外した以外は、参考例３と同様にしてレトルト用の透明な包装材とした。本包装材は３２０ｎｍ以上の波長の光の透過はほとんど透過するものであった。
【００５５】
〈比較例６〉
厚さ１２μｍのポリエチレンテレフタレートフィルムに、厚さ＊＊μｍのナイロンフィルム、厚さ３０μｍの無延伸ポリプロピレンフィルムを順にドライラミネートによって張り合わせ、レトルト用の透明な包装材とした。本包装材は３２０ｎｍ以上の波長の光はほとんど透過するものであった。
【００５６】
上記実施例３、参考例３、４および比較例３〜６の包装材を用いて、レトルト食品としてのビーフシチューおよびパンプキンスープを包装し、１２５℃、６０分の加熱殺菌後、１５００ＬＸ蛍光灯下で照射しながら室温下で保存、６ヵ月後の品質劣化度合いを、ビーフシチューについては油脂の酸化度（過酸化物価）の分析値で、パンプキンスープについては色の変化を外観で評価し、その結果を表４、５に示した。
【００５７】
【表４】
【表５】
表１より、ビーフシチューの酸化度は、参考例３の白色、黄色インキを施した比較的明るい包装材でも３００ｎｍ〜５００ｎｍの波長の波長域の光を遮断することができ、印刷インキ層を施さない包装材よりは言うまでもなく、白色、白色インキを施した包装材よりも格段に抑えられるものであった。すなわち少なくとも３００ｎｍ〜５００ｎｍの波長の波長域の光を遮断すれば、従来のアルミニウム箔が積層された遮光性包装材と比較しても殆ど遜色のない内容物の保存性を示した。
【００６０】
また、表２より、パンプキンスープの変色（褪色）度は、３００ｎｍ〜８００ｎｍの波長域を遮断する白色、墨インキを施した灰色の包装材では従来のアルミニウム箔が積層された包装材と同等で、殆ど遜色のない内容物の保存性を示した。また、白色、黄色インキでなる比較的明るい、あるいは白色、茶色インキでなる黒ずんでいない印刷インキ層では、印刷インキ層のないものに比較すれば変色抑制効果はあるが、大きな効果ではなかった。
【００６１】
【発明の効果】
本発明は以上の構成であるから、下記に示す如き効果がある。
即ち、基材フィルムとガスバリア層でなる透明バリアーフィルムとシーラントとなる熱融着樹脂層の間に、第一印刷インキ層、第二印刷インキ層の２層の印刷インキ層を形成した遮光性バリアー包装材であって、第一印刷インキ層を有機系の紫外線吸収インキ層、第二印刷インキ層を藍色グラビアインキ層とすることによって、該印刷インキ層を含む包装材が３００ｎｍ〜４００ｎｍの波長域および６００ｎｍ〜７００ｎｍの波長域の光を遮断する遮光性バリアー包装材とすることができ、従来のアルミニウム箔が積層された遮光性包装材と異なり、廃棄物に係わる環境問題がなく、しかも内容物が透けて見え、例えば抹茶キャンディのような内容物の色素や香り成分の劣化のない遮光性包装材とすることができる。
【００６２】
また、基材フィルムとガスバリア層でなる透明バリアーフィルムとシーラントとなる熱融着樹脂層の間に、第一印刷インキ層、第二印刷インキ層の２層の印刷インキ層を形成した遮光性バリアー包装材であって、第一印刷インキ層を白色グラビアインキ層、第二印刷インキ層を墨グラビアインキ層とすることによって、該印刷インキ層を含む包装材が３００ｎｍ〜８００ｎｍの波長域の光を遮断する遮光性包装材とすることができ、外光が遮断され、アルミニウム箔が積層された包装材の場合と同様に内容物が透けて見える効果はないが、例えばポテトチップスや粉末海苔をまぶしてあるタイプのポテトチップスのような内容物の油脂の酸化のない遮光性包装材とすることができる。
【００６３】
さらに、前記印刷インキ層を含む包装材が３００ｎｍ〜５００ｎｍの波長域の光を遮断する比較的明るい色でデザイン効果のある遮光性包装材とすることによって、外光の短波長側が遮断され、例えば粉末海苔をまぶしたポテトチップスのような内容物の油脂の酸化を防ぐことはできないが、ポテトチップスのような内容物の油脂の酸化のない遮光性包装材とすることができる。
【００６４】
また、第一印刷インキ層を白色グラビアインキ層、第二印刷インキ層を墨グラビアインキ層とし、該前記印刷インキ層と熱融着樹脂層との間にナイロンフィルムを積層し、該印刷インキ層が２層以上の包装材とし、この印刷インキ層を含む包装材が３００ｎｍ〜５００ｎｍの波長域の光を遮断する比較的明るい色でデザイン効果のある遮光性包装材とすることによって、外光の短波長側が遮断され、例えばビーフシチューのようなレトルト食品の油脂の酸化を防ぐができ、パンプキンスープのようなレトルト食品の変色（褪色）をある程度防ぐレトルト用の遮光性包装材とすることができる。
【００６５】
また、前記印刷インキ層を含む包装材が３００ｎｍ〜５５０ｎｍの波長域の光を遮断するあまり黒ずんでいない茶系統の色で比較的デザイン効果のある遮光性包装材とすることによって、外光の短波長側が遮断され、例えばビーフシチューのようなレトルト食品の油脂の酸化を防ぐができ、パンプキンスープのようなレトルト食品の変色（褪色）をある程度防ぐレトルト用の遮光性包装材とすることができる。
【００６６】
また、前記印刷インキ層を含む包装材が少なくとも３００ｎｍ〜７００ｎｍの波長域の光を遮断する灰色でデザイン効果は比較的ない遮光性包装材とすることによって、外光がほぼ遮断され、例えばビーフシチューのようなレトルト食品の油脂の酸化やパンプキンスープのようなレトルト食品の変色（褪色）を従来のアルミニウム箔と同程度に防ぐレトルト用の遮光性包装材とすることができる。
【００６７】
さらにまた、前記ガスバリアー性を有する透明バリアーフィルムが、金属酸化物等の薄膜、あるいは水溶性高分子と金属アルコキシドまたは加水分解物を含む被覆層を有するので、従来のアルミニウム箔に匹敵するガスバリアー性を有し、かつ廃棄物に係わる環境負荷の低減に寄与する遮光性包装材とすることができる。
【００６８】
従って本発明は、廃棄物に係わる環境負荷の低減に寄与し、内容物の保存性に合致した遮光性包装材として、優れた実用上の効果を発揮する。
【図面の簡単な説明】
【図１】本発明の遮光性包装材の基本構成の一実施の形態を側断面で表した説明図である。
【図２】本発明の遮光性包装材の一実施の形態を側断面で表した説明図である。
【図３】本発明の遮光性包装材のうちのレトルト用の一実施の形態を側断面で表した説明図である。
【符号の説明】
１‥‥遮光性バリアー包装材
１０‥‥印刷インキ層
１２‥‥第一印刷インキ層
１４‥‥第二印刷インキ層
２０‥‥熱融着樹脂層
３０‥‥透明バリアーフィルム
３２‥‥基材フィルム
３４‥‥ガスバリアー層
４０‥‥ナイロンフィルム[0001]
BACKGROUND OF THE INVENTION
The present invention relates to packaging materials for general foods, pharmaceuticals, toiletry products, other living materials, various industrial materials, etc., or retort foods. More specifically, the present invention reduces the environmental burden caused by dealumination of packaging materials, and gas barrier properties. The present invention also relates to a light-shielding packaging material that enhances the storage stability of contents by increasing the light-shielding property.
[0002]
[Prior art]
Conventionally, in order to prevent the quality of food and other contents from being deteriorated due to the influence of oxygen, moisture, etc., a packaging material having a gas barrier property for a packaging material has been used. Examples of the gas barrier packaging material include a film made of a copolymer of polyvinyl alcohol and ethylene vinyl alcohol, a polyvinylidene chloride resin film, or a film coated with these resins. No longer used due to generation and dioxin generation problems.
[0003]
On the other hand, what is most excellent in terms of gas barrier properties is a so-called aluminum packaging material using a laminate film in which an aluminum foil is laminated on a plastic film or an aluminum vapor deposition layer.
[0004]
However, in the above aluminum packaging material, in recent environmental problems related to waste, that is, incineration of waste, the aluminum ingot damages the incinerator or reduces the incineration efficiency, or when the incineration ash is disposed of in the landfill, The demand for dealumination of packaging materials has increased due to problems such as the generation of harmful gases by reacting with other materials. Instead, a transparent gas barrier film using a film having a thin film layer of a metal compound such as silicon oxide Has begun to be used. This is superior in gas barrier properties to conventional transparent barrier films such as polyvinyl alcohol and vinylidene chloride-based films, and realizes gas barrier properties close to those of the aluminum-based packaging material.
[0005]
Moreover, the packaging material of the structure containing aluminum foil is also used as a conventional pouch packaging material for retorts. This is because the retort food is stored for a long period of 6 months to 1 year and is deaerated and packaged to prevent oxidation by oxygen, so that the packaging material is required to have a gas barrier property. In addition, a packaging material including an aluminum foil that satisfies the requirement of light shielding for preventing deterioration due to light has been widely used. However, as mentioned above, the reason for the environmental problems related to waste, the requirement to put the retort pouch in the microwave oven, and the inspection with a metal detector when filling the contents, There is an increasing demand, and transparent gas barrier films having a thin film layer of the above-described metal compound have begun to be used.
[0006]
[Problems to be solved by the invention]
However, transparent barrier packaging materials having these metal oxide thin film layers are not light-shielding, and therefore have the disadvantage that the contents are more susceptible to light degradation than aluminum-based packaging materials. In other words, there is a drawback that it is susceptible to deterioration due to light such as oxidation of the fat component of the contents or decomposition of pigments and fragrance components, and depending on the contents, barrier properties with additional light shielding properties to enhance storage A packaging material was desired. Furthermore, if possible, a light-shielding packaging material that can maintain transparency and has a design effect that does not darken the appearance is also desired.
[0007]
The present invention solves the problems and demands of the prior art, and the problem is that wastes found in packaging materials containing aluminum foil by imparting light shielding properties to the transparent barrier film. It is an object of the present invention to provide a light-shielding packaging material that has reduced environmental burden, has both gas barrier properties and light-shielding properties, and also has transparency if it has a design effect.
[0008]
[Means for Solving the Problems]
In order to achieve the above object in the present invention, first, in the invention of claim 1, a transparent barrier film having gas barrier properties at least from the outside, Consists of at least two ink layers, a first printing ink layer and a second printing ink layer A printing ink layer and a heat-sealing resin layer are laminated in order. A light-shielding packaging material, wherein the first printing ink layer of the printing ink layer is a white gravure ink layer, and the second printing ink layer is a black gravure ink layer. It is set as the light-shielding packaging material characterized by this.
[0009]
In the invention of claim 2, Transparent barrier film having gas barrier properties from at least the outside, at least a first printing ink layer, a printing ink layer composed of two or more ink layers of a second printing ink layer, and a light shielding property obtained by laminating a heat-sealing resin layer in order A packaging material, wherein the first printing ink layer of the printing ink layer is an organic ultraviolet absorbing ink layer, and the second printing ink layer is an indigo gravure ink layer. It is characterized by Shield It is a light packaging material.
[0010]
In the invention of claim 3, A nylon film is laminated between the heat sealing resin layer and the printing ink layer. The light-shielding packaging material according to claim 1.
[0018]
DETAILED DESCRIPTION OF THE INVENTION
Embodiments of the present invention will be described below with reference to the drawings.
The present invention relates to a packaging material for general foods, pharmaceuticals, etc. or retort foods, in particular to a light-shielding packaging material that reduces the environmental burden due to dealumination and increases the gas barrier properties and light-shielding properties to increase the storage stability of the contents. As shown in the cross-sectional side view of FIG. 1, the basic structure is that a transparent barrier film (30) having a gas barrier property, a printing ink layer (10), and a heat-sealing resin layer (20) are laminated in order from at least the outside. The light-shielding packaging material (1).
[0019]
Therefore, in the invention of claim 2, as shown in the laminated side sectional view of FIG. 2, for example, a transparent barrier film (30) having a gas barrier property comprising, for example, an outermost base film (32) and a gas barrier layer (34). ) And the heat-sealing resin layer (20) serving as the innermost sealant (in the drawing which is an example, the first printing ink layer (12) and the second printing ink layer (14)). The light-shielding packaging material (1) in which the printing ink layer (10) is formed, and the packaging material including the printing ink layer (10) has a wavelength range of 300 nm to 400 nm and a wavelength range of 600 nm to 700 nm. The light is blocked.
[0020]
By applying the printing ink layer (10) as described above, outside light near-infrared rays and near-infrared rays are blocked, for example, a light-shielding packaging material (1) that does not deteriorate the contents of pigments and fragrance components such as matcha candy. ). Furthermore, in addition to this effect, it is possible to provide a light-shielding packaging material (1) in which the contents can be seen through.
[0021]
Claims 1 In the light-shielding packaging material of the invention, the printing ink layer (10) having the configuration shown in FIG. 2 is one or more layers, and the packaging material including the printing ink layer (10) blocks light in the wavelength region of 300 nm to 800 nm. To do.
[0022]
By applying the printing ink layer (10) as described above, the entire outside light is blocked, and there is no effect of seeing through the contents in the same manner as in the case of the aluminum packaging material. For example, potato chips or powdered laver is applied. It can be set as the light-shielding packaging material (1) which does not oxidize the fats and oils of the content like a certain type of potato chip.
[0023]
Also ,Book Invention As a reference example The light-shielding packaging material is one in which the printing ink layer (10) having the configuration shown in FIG. 2 is one or more layers, and the packaging material including the printing ink layer (10) blocks light in a wavelength range of 300 nm to 500 nm. It is.
[0024]
By applying the printing ink layer (10) as described above, the short wavelength side of external light is blocked, and for example, it is not possible to prevent the oxidation of fats and oils of contents such as potato chips of a type covered with powdered laver. It is possible to obtain a light-shielding packaging material (1) that does not oxidize the oils and fats of the contents, such as potato chips, and is a light-shielding packaging material that has a relatively bright design effect that does not appear blackish when viewed from the outside ( 1).
[0025]
Claims 3 In the light-shielding packaging material of the invention, a nylon film (40) is laminated between the heat-sealing resin layer (20) and the printing ink layer (10) as shown in the laminated side sectional view of FIG. The printing ink layer (10) is a light-shielding packaging material comprising two or more layers (in the drawing, the first printing ink layer (12) and the second printing ink layer (14)).
[0026]
As described above, by laminating a nylon film (40) having a thickness of about 50 μm, it is possible to obtain a light-shielding packaging material (1) for retort that is resistant to heat sterilization and the like, and two or more layers of printing ink By setting it as a layer (10), in addition to light-shielding provision, the gas barrier property of a transparent barrier film (30) can be supplemented.
[0027]
Also ,Book Invention As a reference example invention Light shielding packaging material Then, for example, the light-shielding packaging material (1) including the two-layer printing ink layer (10) shown in FIG. 3 is configured to block light in the wavelength region of 300 nm to 500 nm.
[0028]
By applying the printing ink layer (10) as described above, the short wavelength side of outside light is blocked, and for example, the oxidation of fats and oils of contents such as beef stew which is a retort food can be prevented. Can be used as a light-shielding packaging material (1) that prevents some of the contents such as pumpkin soup from fading to a certain extent, and it does not look dark from the outside, but it has a relatively bright design effect. It can be set as a packaging material (1).
[0029]
Also ,Book Invention As a reference example In the light-shielding packaging material of the invention, for example, the light-shielding packaging material (1) including the two-layer printing ink layer (10) shown in FIG. 3 blocks light in the wavelength range of 300 nm to 550 nm. It is.
[0030]
By applying the printing ink layer (10) as described above, the short wavelength side of outside light is blocked, and for example, the oxidation of fats and oils of contents such as beef stew which is a retort food can be prevented. It can be used as a light-shielding packaging material (1) that prevents the fading of contents such as pumpkin soup to some extent, and it has a relatively bright design effect although it looks dark from the outside and is slightly brownish. It can be set as the light-shielding packaging material (1) for retort food.
[0031]
Also ,Book Invention As a reference example In the light-shielding packaging material of the invention, for example, the light-shielding packaging material (1) including the two-layer printing ink layer (10) shown in FIG. 3 blocks light in the wavelength region of at least 300 nm to 700 nm. Is.
[0032]
By applying the printing ink layer (10) as described above, almost the entire area of external light is blocked, and for example, the oxidation of fats and oils of contents such as beef stew which is a retort food can be prevented to the same extent as a conventional aluminum foil. It can also be used as a light-shielding packaging material (1) that almost completely prevents discoloration of the contents such as pumpkin soup as a retort food, but looks dark from the outside and is slightly inferior in design effect. A light-shielding packaging material (1) for retort food is obtained.
[0033]
【Example】
Using the light-shielding packaging material according to the present invention, potato chips, a type of potato chips coated with powdered seaweed (hereinafter referred to as “ritsuri potato chips”), green tea candy, and beef stew as a retort food, Each of the pumpkin soups is packaged after heat sterilization, and the degree of content quality deterioration when stored under light irradiation is specifically described using the packaging materials shown in the examples and comparing with the packaging materials of the comparative examples. .
[0034]
Potato chips, oil paste potato chips, beef stew, etc. that contain oil as the contents used in the examples are susceptible to oxidation of fats and oils due to the influence of light, and matcha candy and the like are dyes due to the influence of light in a specific wavelength range In order to prevent this, the pumpkin soup as a retort food is fading due to the effect of light and has poor value added as a food. At present, aluminum-based packaging materials are mostly used. The present invention provides a light-shielding packaging material having a storage stability equivalent to that of the aluminum-based packaging material without using aluminum which has environmental problems related to waste treatment. Therefore, in this embodiment, the aluminum-based packaging material is provided. A comparative test example is shown, but if the storage performance of the light-shielding packaging material according to the present invention is equivalent to the storage stability of the aluminum-based packaging material, the purpose is sufficiently achieved.
[0035]
Further, in the present embodiment, the ink of a specific color and the combination thereof are illustrated to block the transmission of light in a specific wavelength range, but the present invention is illustrated as long as it can achieve the light blocking of the specific wavelength range of interest. It is not limited to the ink of the color and its combination. Further, the exemplified contents are not limited, and the effect is exhibited if the light wavelength involved in the deterioration of the contents is included in the range of the light blocking wavelength of each packaging material.
[0036]
<Example 1>
As shown in FIG. 2, a transparent barrier film (30) is obtained by depositing a thin film layer of aluminum oxide as a gas barrier layer (34) on a polyethylene terephthalate film having a thickness of 12 μm as a base film (32). White gravure ink for the printing ink layer (12), black gravure ink for the second printing ink layer (14), solid (edited by the Japan Printing Society: According to the Printing Encyclopedia, the difference in shading and white areas on the printed surface There is no part that is completely covered with printing ink) A printed printing ink layer (10) is provided, and an unstretched polypropylene film with a thickness of 30 μm is formed by dry lamination as a heat-sealing resin layer (20) serving as a sealant. Lamination and light-shielding packaging material (1) was obtained. This packaging material (1) completely blocked the transmission of light in the wavelength range of 300 nm to 800 nm.
[0037]
< reference Example 1 >
A light-shielding packaging material (1) was obtained in the same manner as in Example 1 except that the second printing ink layer (14) shown in FIG. This packaging material (1) completely blocked the transmission of light in the wavelength range of 300 nm to 550 nm.
[0038]
< reference Example 2 >
A light-shielding packaging material (1) was obtained in the same manner as in Example 1 except that the second printing ink layer (14) shown in FIG. This packaging material (1) completely blocked the transmission of light in the wavelength range of 300 nm to 500 nm.
[0039]
<Example 2 >
As a base film (32) shown in FIG. 2, a transparent polypropylene film having a thickness of 12 μm and a layer containing a water-soluble polymer and a metal alkoxide or a hydrolyzate thereof as a gas barrier layer (34) is formed by coating. A barrier film (30) is used, and an organic ultraviolet absorbing ink (NEW-LP Super V White, manufactured by Toyo Ink Co., Ltd.) is used as the first printing ink layer (12), and indigo is used as the second printing ink layer (14). A light-shielding packaging material (1) was obtained in the same manner as in Example 1 except that a printing ink layer (10) in which each color gravure ink was solid-printed was provided. This packaging material completely blocked the transmission of light in the wavelength ranges of 300 nm to 400 nm and 580 to 730.
[0040]
<Comparative example 1>
A barrier packaging material was obtained in the same manner as in Example 1 except that the printing ink layer (10) was not applied. This packaging material almost transmits light with a wavelength of 300 nm or more.
[0041]
<Comparative example 2>
A barrier packaging material was obtained in the same manner as in Comparative Example 1, except that an aluminum thin film layer was deposited as the gas barrier layer (34). This packaging material completely blocked the transmission of light in the wavelength range of 300 nm to 800 nm.
[0042]
Example 1 2, Reference Examples 1 and 2 Using the packaging materials of Comparative Examples 1 and 2, potato chips, glue salt potato chips and green tea candy were each packaged, and the degree of quality deterioration when stored at 1500 LX fluorescent light irradiation and at room temperature was measured. The salt potato chips were evaluated by the analysis value of the oxidation degree (peroxide value) of fats and oils, and the color change of the matcha candy was evaluated by appearance. Table 1 shows the results with the potato chips, Table 2 shows the results with the paste potato chips, and the results with the matcha candy. table It was shown in 3.
[0043]
[Table 1]
[Table 2]
[Table 3]
From Table 1 above, when the content is a potato chip, that is, Example 1 that blocks light in the wavelength region of at least 300 to 500 nm. Reference examples 1 and 2 It can be seen that the use of the light-shielding barrier packaging material (1) significantly improves the content storage stability as compared with the packaging material of Comparative Example 1. Among them, the light-shielding barrier packaging material (1) of Example 1 that blocks the wavelength range of 300 to 800 nm shows completely the same content preservation (less oxidation degree of fats and oils) as the aluminum-based packaging material of Comparative Example 2. It was.
[0047]
Moreover, from the said Table 2, when the content is a paste salt potato chip | tip, it is equivalent to the aluminum-type packaging material of the comparative example 2 with the light-shielding barrier packaging material (1) of Example 1 which interrupts | blocks the wavelength range of 300-800 nm. Storage stability (low degree of oxidation of fats and oils).
[0048]
In the case where the content is matcha candy, the embodiment blocks the wavelength range of 300 to 400 nm and 600 to 700 nm. 2 In the same light-shielding barrier packaging material as in Example 1, which blocks the wavelength region of 300 to 800 nm, the aluminum-based packaging material of Comparative Example 2 and the content preservability (pigments and fragrances) almost the same as those of Comparative Example 2 No decomposition of the components). Furthermore, the light-shielding barrier packaging material of Example 4 had an effect of seeing through the contents (that is, an effect of confirming the contents).
[0049]
< reference Example 3 >
As shown in FIG. 3, a transparent barrier film (30) is obtained by depositing a thin film layer of aluminum oxide as a gas barrier layer (34) on a polyethylene terephthalate film having a thickness of 12 μm as a base film (32). A white gravure ink is provided on one printing ink layer (12), a yellow gravure ink is provided as a second printing ink layer (14), and a solid printing ink layer (10) is provided thereon, and a nylon film having a thickness of 60 μm is provided thereon. (40) was further laminated with a non-stretched polypropylene film having a thickness of 30 μm as a heat-sealing resin layer (20) serving as a sealant by dry lamination to obtain a light-shielding packaging material (1) for retort. This packaging material (1) completely blocked the transmission of light in the wavelength range of 300 nm to 500 nm.
[0050]
< reference Example 4 >
A light-shielding packaging material (1) for retort was obtained in the same manner as in Example 5 except that the second printing ink layer (14) shown in FIG. 3 was a brown gravure ink. This packaging material (1) completely blocked the transmission of light in the wavelength range of 300 nm to 550 nm.
[0051]
<Example 3 >
Except that the second printing ink layer (14) shown in FIG. reference Example 3 In the same manner as described above, a light-shielding packaging material (1) for retort was obtained. This packaging material (1) completely blocked the transmission of light in the wavelength range of 300 nm to 800 nm.
[0052]
<Comparative Example 3>
A polyethylene terephthalate film having a thickness of 12 μm, a nylon film having a thickness of 60 μm, an aluminum foil having a thickness of 7 μm, and an unstretched polypropylene film having a thickness of 30 μm were sequentially laminated together by dry lamination to obtain a light-shielding packaging material for retort. This packaging material (1) completely blocked the transmission of light in the wavelength range of 300 nm to 800 nm.
[0053]
<Comparative example 4>
The second printing ink layer (14) shown in FIG. 3 is a white gravure ink, that is, the first and second printing ink layers (12, 14) are both white gravure inks. Packaging material (1). This packaging material (1) completely blocked the transmission of light in the wavelength range of 300 nm to 400 nm.
[0054]
<Comparative Example 5>
Except for excluding the printing ink layer (10) shown in FIG. reference Example 3 In the same manner, a transparent packaging material for retort was obtained. This packaging material was almost transparent to light having a wavelength of 320 nm or longer.
[0055]
<Comparative Example 6>
A 12 μm thick polyethylene terephthalate film was laminated with a nylon film with a thickness of ** μm and an unstretched polypropylene film with a thickness of 30 μm in this order by dry lamination to obtain a transparent packaging material for retort. This packaging material almost transmits light with a wavelength of 320 nm or more.
[0056]
Example above 3, Reference Example 3, 4 The beef stew and pumpkin soup as retort foods are packaged using the packaging materials of Comparative Examples 3 to 6, and after heat sterilization at 125 ° C. for 60 minutes, they are stored at room temperature while being irradiated under 1500 LX fluorescent light. The degree of deterioration in quality after a month was evaluated by the analysis value of the oxidation degree (peroxide value) of fats and oils for beef stew, and the color change was evaluated by appearance for pumpkin soup, and the results are shown in Tables 4 and 5.
[0057]
[Table 4]
[Table 5]
From Table 1, the degree of oxidation of beef stew is reference Example 3 Even relatively bright packaging materials with white and yellow inks can block light in the wavelength range of 300 nm to 500 nm, and needless to say, white and white inks are applied rather than packaging materials without a printing ink layer. It was much less constrained than the packaging material. That is, when light in a wavelength range of at least 300 nm to 500 nm was cut off, the storage stability of the content was almost the same as that of a conventional light-shielding packaging material in which an aluminum foil was laminated.
[0060]
Also, from Table 2, the degree of discoloration (fading) of the pumpkin soup is the same as that of a conventional packaging material in which aluminum foil is laminated in a white packaging ink and a gray packaging material in which black ink is applied, which blocks the wavelength range of 300 nm to 800 nm. It showed the storage stability of almost the same contents. In addition, the relatively bright or non-black printing ink layer made of white or yellow ink has a discoloration suppressing effect as compared with the non-dark printing ink layer made of white or brown ink, but not a great effect.
[0061]
【The invention's effect】
Since this invention is the above structure, there exist the following effects.
That is, between the transparent barrier film consisting of the base film and the gas barrier layer and the heat-sealing resin layer serving as the sealant, 2 of the first printing ink layer and the second printing ink layer A light-shielding barrier wrapping material on which a printing ink layer is formed, By making the first printing ink layer an organic UV absorbing ink layer and the second printing ink layer an indigo gravure ink layer, The packaging material including the printing ink layer is a light-shielding barrier packaging material that blocks light in a wavelength range of 300 nm to 400 nm and a wavelength range of 600 nm to 700 nm. It is possible Unlike conventional light-shielding packaging materials laminated with aluminum foil, there is no environmental problem related to waste, and the contents can be seen through, for example, there is no deterioration of the pigments and scent components of the contents such as matcha candy. It can be set as a light-shielding packaging material.
[0062]
Also, A light-shielding barrier packaging material in which two printing ink layers, a first printing ink layer and a second printing ink layer, are formed between a transparent barrier film comprising a base film and a gas barrier layer and a heat-sealing resin layer serving as a sealant. The first printing ink layer is a white gravure ink layer and the second printing ink layer is a black gravure ink layer, The packaging material including the printing ink layer is a light-shielding packaging material that blocks light in the wavelength range of 300 nm to 800 nm. Can As with packaging materials that are shielded from external light and laminated with aluminum foil, there is no effect of seeing through the contents, but for example, contents such as potato chips or types of potato chips covered with powdered seaweed It can be set as the light-shielding packaging material without the oxidation of the fats and oils.
[0063]
Furthermore, the packaging material containing the printing ink layer is a light-shielding packaging material having a design effect with a relatively bright color that blocks light in the wavelength range of 300 nm to 500 nm, thereby blocking the short wavelength side of external light, for example, Although it is not possible to prevent oxidation of fats and oils such as potato chips coated with powdered seaweed, it is possible to provide a light-shielding packaging material that does not oxidize fats and oils of contents such as potato chips.
[0064]
Also, The first printing ink layer is a white gravure ink layer, the second printing ink layer is a black gravure ink layer, A nylon film is laminated between the printing ink layer and the heat-sealing resin layer, the printing ink layer is a packaging material having two or more layers, and the packaging material including the printing ink layer has a wavelength region of 300 nm to 500 nm. Pumpkin soup can be used as a light-shielding packaging material with a relatively bright color that blocks light, blocking the short-wavelength side of outside light and preventing oxidation of retort foods such as beef stew. It can be set as the light-shielding packaging material for retort which prevents the discoloration (fading) of retort food like this to some extent.
[0065]
Moreover, the packaging material including the printing ink layer is a light-shielding packaging material that has a relatively dark tea color that blocks light in the wavelength range of 300 nm to 550 nm and has a relatively design effect. The light-shielding packaging material for retort that blocks the wavelength side, can prevent oxidation of fats and oils of retort food such as beef stew, and prevents discoloration (fading) of retort food such as pumpkin soup to some extent.
[0066]
In addition, since the packaging material containing the printing ink layer is a light-shielding packaging material that blocks light in the wavelength region of at least 300 nm to 700 nm and has relatively little design effect, external light is substantially blocked, for example, beef stew. It can be set as the light-shielding packaging material for retorts which prevents the oxidation of the fats and oils of retort foods and the discoloration (dark blue) of retort foods such as pumpkin soup to the same extent as conventional aluminum foil.
[0067]
Furthermore, since the transparent barrier film having the gas barrier property has a thin film such as a metal oxide, or a coating layer containing a water-soluble polymer and a metal alkoxide or a hydrolyzate, a gas barrier comparable to a conventional aluminum foil. And a light-shielding packaging material that contributes to the reduction of the environmental burden associated with waste.
[0068]
Therefore, the present invention contributes to the reduction of the environmental load related to waste, and exhibits an excellent practical effect as a light-shielding packaging material that matches the preservability of the contents.
[Brief description of the drawings]
FIG. 1 is an explanatory view showing an embodiment of the basic configuration of a light-shielding packaging material of the present invention in a side cross section.
FIG. 2 is an explanatory view showing an embodiment of the light-shielding packaging material of the present invention in a side section.
FIG. 3 is an explanatory view showing one embodiment for retort in the light-shielding packaging material of the present invention in a side section.
[Explanation of symbols]
1. Light-shielding barrier packaging material
10. Printing ink layer
12 ... 1st printing ink layer
14 ... Second printing ink layer
20 ... heat-sealing resin layer
30 ... Transparent barrier film
32 ... Base film
34 Gas barrier layer
40 Nylon film
Claims (3)