JP3507181B2 - 骨セメントをインプラントに形成する方法 - Google Patents

骨セメントをインプラントに形成する方法

Info

Publication number
JP3507181B2
JP3507181B2 JP08120895A JP8120895A JP3507181B2 JP 3507181 B2 JP3507181 B2 JP 3507181B2 JP 08120895 A JP08120895 A JP 08120895A JP 8120895 A JP8120895 A JP 8120895A JP 3507181 B2 JP3507181 B2 JP 3507181B2
Authority
JP
Japan
Prior art keywords
implant
bone cement
cement mixture
cement
irradiation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP08120895A
Other languages
English (en)
Other versions
JPH0838588A (ja
Inventor
イー．ホーキンス マイケル
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bristol Myers Squibb Co
Original Assignee
Bristol Myers Squibb Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bristol Myers Squibb Co filed Critical Bristol Myers Squibb Co
Publication of JPH0838588A publication Critical patent/JPH0838588A/ja
Application granted granted Critical
Publication of JP3507181B2 publication Critical patent/JP3507181B2/ja
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【発明の詳細な説明】
【０００１】
【産業上の利用分野】本発明は、骨セメントを補てつイ
ンプラントに形成する方法に関し、そして骨セメントを
インプラントに形成させ、そしてそのセメントをその電
磁気スペクトル内での照射に晒すことにより重合を開始
させるための方法に特定の関連をもつ。
【０００２】
【従来の技術】骨セメントは、一般的に、補てつインプ
ラント(prosthetic implant)、例えば、股関節部幹(hip
stem)を、生骨組織、例えば、準備された大腿の骨髄内
管(prepared intramedullary canal of a femur)に付着
するために使用される。骨セメントは、典型的には、共
に十分に混合されたときに重合を経験するアクリル・ポ
リマー材料である。好ましい慣用の骨セメントは、粉
末、ポリメチル・メタクリレート(PMMA)ポリマー及び液
体、メチル・メタクリレート(MMA) モノマーから成る。
この重合は、硬化を触媒するための開始剤を必要とす
る。この開始剤は、典型的には、第三アミン、例えば、
アニリン又はトルイジンである。このアミン開始剤は、
PMMA粉末セメント中の過酸化ベンゾイルを解裂させて、
上記液体モノマーの結合を開始させるフリー・ラジカル
を作り出す。
【０００３】外科用途においては、骨セメントは、その
骨組織とインプラントとの間のインターロック(interlo
ck) を弱める血液、体液、水、及び気泡により汚染され
ることができる。そのインプラントに成形されたセメン
トの外層を含む補てつインプラントが、開発されてい
る。セメントの層をそのインプラントに制御された環境
において成形することにより、そのインプラントとセメ
ントとの間のインターロックがかなり改善される。この
インプラント手順の間に、追加量の骨セメントが、その
インプラントをその骨組織に固定するために使用され
る。この追加の骨セメントは、そのインプラントに成形
されたセメントの層と分子的に相互作用し、そしてその
骨組織とかみ合い(interdigitate) 、ポジティブ・イン
ターロックを提供する。
【０００４】
【発明が解決しようとする課題】骨セメントを金属又は
複合材補てつインプラントに成形又は適用することは、
多様な製造困難性を提示する。この骨セメントは、その
インプラントとセメントとの間のポジティブ・インター
ロックを確保するため可能な限り汚染物及び空間の数を
減少させるために、そのインプラントに適用されなけれ
ばならない。好ましい製造環境においては、そのセメン
トは、成形工程により適用される。そのインプラントを
型の中に置き、そしてそのセメントを混合し、そしてそ
の型の中に押し出し、そこで、それをそのインプラント
周りで重合させる。しかしながら、重合している骨セメ
ントを型の中に押し出すことは、問題がある。アクリル
・セメントの粘度は、上記モノマーとポリマー成分とを
混合した後にその経過時間に伴い増加する。押し出し工
程においては、混合後、その骨セメントは、直ぐに、そ
の型の中に容易に押し出されることができない程硬くな
る。さらに、重合を開始させるセメント中のアミン開始
剤は、滅菌の間に変色し、色彩において黄色又は茶色に
変化する。
【０００５】
【課題を解決するための手段】本発明に係る方法は、そ
のセメント混合物中のアミン開始剤の必要性を取り除く
ことにより骨セメントをインプラントに成形する上記の
押し出しの問題を取り除く。本方法においては、照射に
晒すことが、上記液体モノマーの重合を開始させるため
に使用される。上記アミン開始剤を取り除くことによ
り、そのセメント混合物の粘度が、照射されるまで同一
に残る。結果として、上記液体モノマー及び粉末ポリマ
ーが、プレ- ミックスされ、そしてその粘度におけるい
ずれの変化を伴わずにバッチ・コンテナからその型の中
に自由に押し出されることができる。上記アミン開始剤
を取り除くことは、そのインプラントの滅菌の間に生じ
る変色の問題をも取り除く。
【０００６】アミン開始剤のいずれをも欠くセメント混
合物は、手動において又は自動化された工程においてイ
ンプラントに適用又は成形されることができる。好まし
くは、製造環境においては、セメントが、慣用の押し出
し装置及び技術を使用して自動化された押し出し工程に
おいてそのインプラントに適用される。個々のインプラ
ントは、型の中に置かれ、そしてセメント混合物が、空
間のいずれをも取り除くために圧力下でその型の空隙中
に射出される。セメント混合物は、その型の内部のイン
プラント及びセメント混合物が照射源に晒されるまで安
定且つ粘性のまま残る。比較的低エネルギーのX-線又は
比較的高エネルギーのガンマ線により液体モノマーを照
射することが、モノマー中にフリー・ラジカルを作り出
し、これはその型の内部での重合を開始させる。一旦、
モノマーが完全に重合又は硬化されると、インプラント
は、型から取り出され、そして、滅菌及び包装の準備が
される。本方法の他の変法においては、感光開始剤(pho
tosensitive initiator)が液体モノマーに添加される。
混合物は、光源に晒され、その混合物が型の中に流れる
ときに重合を開始される。その型の中へのそのセメント
混合物の導入の後にその混合物がその光源に晒されるこ
とができるように、透明な型が使用されこともできる。
【０００７】セメント混合物がインプラントに表在局所
的に適用されることができ又はインプラントにセメント
の厚い層を固定するための接着剤として使用されること
ができるであろうことを理解すべきである。従って、本
発明の利点は、骨セメントを補てつインプラントに形成
する方法であって、アミン開始剤のいずれをも欠くセメ
ント混合物がそのインプラント上に置かれ、そしてその
セメント混合物を照射源に晒すことにより重合を開始さ
せて、そのセメントをインプラントに付着させるような
方法を、提供する。他の利点は、アクリル骨セメントを
補てつインプラントに形成する方法であってそのセメン
ト混合物中のアミン開始剤の必要性を取り除く方法を提
供することである。他の利点は、アクリル・セメントを
インプラントに形成する方法であって、照射源へ晒すこ
とが重合を開始させるまでそのセメント混合物が流動性
を残しているような方法を提供することである。他の利
点は、以下の記載の説明を読む間に明らかになるであろ
う。
【０００８】本発明の好ましい態様を、説明の目的のた
めにのみ描写する。ここで:図1 は、本発明に係る補て
つインプラントのまわりで骨セメントを重合させる方法
のフロー・チャートである。図2 は、押し出し工程にお
いて使用される本発明に係る方法のフロー・チャートで
ある。図3 は、押し出し工程において使用される本発明
に係る第二変法のフロー・チャートである。
【０００９】本明細書中に記載する好ましい態様は、網
羅的なものであること又は本発明を開示された正確な形
態に限定することを意図されていない。それらは、当業
者がそれらの技術を利用することができるように、本発
明の原理並びにそれらの適用及び実施を説明するために
選択及び記載される。図1 中に示すように、本発明に係
る方法は、本明細書中の骨セメントの重合又は補てつイ
ンプラントへのそのセメントの成形を開始させるために
照射を使用する。本法は、第三アミン開始剤のいずれを
も欠く骨セメントを使用する。このセメント混合物は、
粉末ポリマー及び液体モノマーを含む。液体モノマー、
好ましくはメチル・メタクリレート(MMA) は、アミン開
始剤、例えば、アニリン又はN,N'- ジメチルp-トルイジ
ン又はジヒドロキシエチル-o- トルイジンを含むトルイ
ジンを全く含まないように配合される。粉末ポリマー
は、好ましくはポリメチル・メタクリレート(PMMA)であ
る。場合により、この粉末ポリマーは、スチレン・コポ
リマーを含むことができる。この液体モノマー及び粉末
ポリマーの混合物が安定であり、そして長い時間にわた
りその粘度を保持するであろうことは、注目すべきこと
である。
【００１０】このセメント混合物は、手動において又は
自動化された工程においてインプラントに適用されるこ
とができる。好ましくは、製造環境においては、このセ
メントが、慣用の押し出し装置及び技術を使用する押し
出し工程においてそのインプラントに適用される。補て
つインプラントについて記載したような骨セメント混合
物を押し出すのに好適な押し出し機器及び装置は、本分
野においてよく知られている。慣用の押し出し機器は、
一般的には、型、その中にセメント混合物が収納される
ホッパー、及びその型の中にそのセメント混合物を押し
つけるインジェクター、を含む。
【００１１】図2 中に示すように、インプラントを最初
に好適な型の中に挿入する。このインプラントを、セメ
ンント混合物がそのインプラントの一部をカバーするで
あろうように、その型の中にフィットさせる。この型
は、セメント混合物が仕上がったインプラントの意図さ
れた外形を形成するように、輪郭を描かれている。次
に、流動性のセメント混合物を、空間のいずれをも取り
除くように圧力下その型の空隙内に射出する。最後の段
階において、その型の中のセメント混合物を、その電磁
気スペクトルにおける照射の源、例えば、X-線又はガン
マ線に晒して、そのセメント混合物中のモノマーの重合
を開始させる。慣用の照射機器、例えば、診断のための
医療用途において及び金属成分検査のための工業用途に
おいて使用されるX-線装置を、型及びセメント混合物を
照射に直接的に晒すために使用することができる。セメ
ント混合物を照射することは、そのモノマー中にフリー
・ラジカルを作り出す。このフリー・ラジカルの作用
は、そのモノマーの重合を開始させることである。さら
にPMMA中に存在することができるいずれかの過酸化ベン
ゾイルが、フリー・ラジカルの追加の源を提供すること
ができる。照射源のエネルギー・レベル及び露出の長さ
は、そのモノマーの累積質量、そのインプラント、その
型、及び重合の所望速度に対して選択される。
【００１２】図3 は、本発明に係る方法の他の変法をダ
イアグラムにより表したものである。この変法において
は、光活性化開始剤が、歯の中の空間を満たすために歯
科用途において使用されるセメントに類似したセメント
混合物に添加される。この感光開始剤は、上記の液体モ
ノマーに添加される。重合は、その型の中で透明な型を
通して、又はセメント混合物をその型の中に押し出しな
がら、光源にその混合物を晒すことにより開始される。
この光源への露出が、上記の感光材料を活性化して、そ
の重合を開始させる。本明細書は、セメントをインプラ
ントに成形するための方法について一般的に言及してい
るけれども、用語" 成形" は、広く解釈されなければな
らないことを、理解すべきである。本セメント混合物
は、実際に、インプラントに表在局所的に適用されるこ
とができる。さらに、本セメント混合物は、そのインプ
ラントに表在局所的に適用されて、第二の成分、例え
ば、セメントの形成前固体層のための接着剤として作用
することができる。これまでの記載は、本発明をその与
えられた細目に限定するものではないが、先の請求の範
囲内で修正されることができることが、理解されよう。
【図面の簡単な説明】
【図１】図1 は、本発明に係る補てつインプラントのま
わりで骨セメントを重合させる方法のフロー・チャート
である。
【図２】図2 は、押し出し工程において使用される本発
明に係る方法のフロー・チャートである。
【図３】図3 は、押し出し工程において使用される本発
明に係る第二変法のフロー・チャートである。
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平５−139927（ＪＰ，Ａ) 特開 平４−83748（ＪＰ，Ａ) 特表 平９−511666（ＪＰ，Ａ) 米国特許4554686（ＵＳ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) A61L 24/00 - 24/12 A61L 27/00 - 27/60

Claims (8)

    (57)【特許請求の範囲】
  1. 【請求項１】 骨セメント混合物を補てつインプラント
    に付着させる方法であって、以下の段階: a) その骨セメント混合物をそのインプラントに流動状
    態において適用し、その骨セメント混合物が液体モノマ
    ー成分を含み; そして b)その骨セメント混合物をその電磁気スペクトルにおい
    て照射源に晒して、その液体モノマーの重合を開始さ
    せ、それによりその骨セメント混合物をそのインプラン
    ト上で硬化させる、を含んで成る方法。
  2. 【請求項２】 段階b)における照射がガンマ線照射であ
    る、請求項１に記載の方法。
  3. 【請求項３】 段階b)における照射がX-線照射である、
    請求項１に記載の方法。
  4. 【請求項４】 骨セメント混合物をインプラントに成形
    する方法であって、以下の段階: a)空隙を有する型を提供し; b)その空隙内にそのインプラントをフィットさせ; c)流動状態におけるその骨セメント混合物をそのインプ
    ラントのまわりで上記空隙内に導入し、その骨セメント
    混合物が液体モノマーを含み; そして d)その骨セメント混合物をその電磁気スペクトルにおい
    て照射源に晒して、その液体モノマーの重合を開始さ
    せ、それによりその骨セメント混合物がそのインプラン
    トに硬化する、を含んで成る方法。
  5. 【請求項５】 段階d)における照射がガンマ線照射であ
    る、請求項４に記載の方法。
  6. 【請求項６】 段階d)における照射がX-線照射である、
    請求項４に記載の方法。
  7. 【請求項７】 骨セメント混合物が感光開始剤をさらに
    含む、請求項４に記載の方法。
  8. 【請求項８】 整形外科インプラントであって: 本体、
    並びに液体骨セメント混合物のコーティングであってそ
    のインプラントの一部の上に置かれ、そしてその液体骨
    セメント混合物をそのインプラント上で重合及び硬化せ
    しめるために電磁気照射に晒されたコーティングを、含
    んで成るインプラント。
JP08120895A 1994-04-07 1995-04-06 骨セメントをインプラントに形成する方法 Expired - Fee Related JP3507181B2 (ja)