JP3344170B2 - PC grout material - Google Patents
PC grout materialInfo
- Publication number
- JP3344170B2 JP3344170B2 JP18390295A JP18390295A JP3344170B2 JP 3344170 B2 JP3344170 B2 JP 3344170B2 JP 18390295 A JP18390295 A JP 18390295A JP 18390295 A JP18390295 A JP 18390295A JP 3344170 B2 JP3344170 B2 JP 3344170B2
- Authority
- JP
- Japan
- Prior art keywords
- cement
- inorganic filler
- grout
- weight
- grout material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、ＰＣグラウト材、
即ち、ポストテンション方式のプレストレストコンクリ
ート（ＰＣ）構造物において、シース内に挿入され緊張
定着されたＰＣ鋼材を腐食から保護すると共に、コンク
リートとシース内のＰＣ鋼材に付着性を付与して両者を
一体化することを目的として、シースとＰＣ鋼材との隙
間に充填されるグラウト材に関する。The present invention relates to a PC grout material,
That is, in a post-tensioned prestressed concrete (PC) structure, the PC steel material inserted into the sheath and tensioned and fixed is protected from corrosion, and the concrete and the PC steel material in the sheath are imparted with adhesion to integrate the two. The present invention relates to a grout material to be filled in a gap between a sheath and a PC steel material for the purpose of forming a material.
【０００２】[0002]
【従来の技術】従来、ＰＣグラウト材としては、次のよ
うな材料構成のものが提供されている。2. Description of the Related Art Heretofore, the following grout materials have been provided as PC grout materials.
【０００３】 セメント、水及び減水剤（一般には遅
延型減水剤）及び膨張剤（通常、アルミニウム粉）より
なるＰＣグラウト材。 セメント、水及び混和剤（粉末状の市販品）よりな
るＰＣグラウト材。[0003] PC grout material consisting of cement, water and a water reducing agent (generally a delayed water reducing agent) and a swelling agent (usually aluminum powder). PC grout material consisting of cement, water and an admixture (powder commercial product).
【０００４】なお、のＰＣグラウト材の混和剤は、基
本的にはのＰＣグラウト材の減水剤及び膨張剤などか
らなるものであるが、主成分として、これらの他、増粘
剤が添加されているもの（ノンブリーディングタイプ）
もある。[0004] The admixture of the PC grout material is basically composed of a water reducing agent and a swelling agent of the PC grout material. However, in addition to these, as a main component, a thickener is added. What (non-bleeding type)
There is also.
【０００５】これらのＰＣグラウト材は、通常、水セメ
ント比４５％以下で使用される。[0005] These PC grout materials are usually used at a water cement ratio of 45% or less.
【０００６】[0006]
【発明が解決しようとする課題】上記従来のＰＣグラウ
ト材のうち、のＰＣグラウト材では、可使時間が短
く、例えば、混練後３０分を超えると流動性の低下が大
きくなり、注入作業に支障をきたすことから、注入作業
時間が制約されるという欠点がある。Among the above-mentioned conventional PC grout materials, the PC grout material has a short pot life and, for example, when it exceeds 30 minutes after kneading, a decrease in fluidity becomes large, so that the grouting operation is difficult. There is a disadvantage in that the injection work time is restricted because of the hindrance.
【０００７】また、のＰＣグラウト材では、増粘剤を
含まない混和剤を使用した場合にも、上記欠点がある。
増粘剤を含む混和剤を使用した場合には、ブリーディン
グの発生は防止されるが、この場合には、粘性が高くな
り、注入速度が低下するため、作業性が大幅に低下する
という欠点がある。In the case of the PC grout material, there is also the above-mentioned disadvantage when an admixture containing no thickener is used.
When an admixture containing a thickener is used, the occurrence of bleeding is prevented.However, in this case, the viscosity is increased, and the injection speed is reduced. is there.
【０００８】本発明は上記従来の問題点を解決し、流動
性が良好で、可使時間が長く、また、ブリーディングが
発生しない範囲で粘性を低く抑え、注入作業性に優れる
ＰＣグラウト材を提供することを目的とする。The present invention solves the above-mentioned conventional problems, and provides a PC grout material having good flowability, a long pot life, a low viscosity within a range where bleeding does not occur, and excellent workability in pouring. The purpose is to do.
【０００９】[0009]
【課題を解決するための手段】請求項１のＰＣグラウト
材は、セメント、高性能減水剤、増粘剤、遅延剤及びブ
レーン比表面積が２０００〜５０００ｃｍ２／ｇの無機
質フィラーを下記配合となるように水と混練してなるこ
とを特徴とする。セメント ：１００重量部 無機質フィラー：１０〜４０重量部 遅延剤 ：セメント及び無機質フィラーの合計に
対して０．０３ 〜０．１２重量％ 増粘剤 ：セメント及び無機質フィラーの合計に
対して０．０５ 〜０．３重量％ 高性能減水剤 ：セメント及び無機質フィラーの合計に
対して０．５〜 １．５重量％ A PC grout according to claim 1
Materials include cement, high performance water reducing agents, thickeners, retarders and
Lane specific surface area 2000-5000cm2/ G inorganic
Quality fillerSo that it has the following compositionKneaded with water
And features.cement : 100 parts by weight Inorganic filler: 10 to 40 parts by weight Retarder ： To the total of cement and inorganic filler
0.03 ~ 0.12% by weight Thickener ： To the total of cement and inorganic filler
0.05 for ~ 0.3% by weight High performance water reducing agent ： To the total of cement and inorganic filler
0.5 ~ 1.5% by weight
【００１０】ブレーン比表面積２０００〜５０００ｃｍ
2 ／ｇの無機質フィラーは、材料の粘性を低減してサラ
サラした状態にする作用を奏し、さらに、このような無
機質フィラーを配合することにより、可使時間の延長を
図ることができる。また、粘性の低減により、注入圧を
下げることができ、注入速度が向上し、注入作業性が改
善される。[0010] Brain specific surface area 2000-5000cm
The 2 / g inorganic filler has the effect of reducing the viscosity of the material to make it smooth, and the use of such an inorganic filler can extend the pot life. Further, by reducing the viscosity, the injection pressure can be reduced, the injection speed is improved, and the injection workability is improved.
【００１１】遅延剤は、凝結を遅延することで、可使時
間を延長する作用を奏する。The retarder has the effect of extending the pot life by delaying the setting.
【００１２】増粘剤及び高性能減水剤を配合すること
で、増粘剤によるブリーディングの抑制効果が得られ、
また、高性能減水剤による流動性向上効果が得られる。By blending a thickener and a high-performance water reducing agent, the effect of suppressing bleeding by the thickener is obtained.
Further, an effect of improving fluidity by the high-performance water reducing agent can be obtained.
【００１３】無機質フィラーとしては石灰石の粉末が好
適である。Limestone powder is suitable as the inorganic filler.
【００１４】[0014]
【発明の実施の形態】以下に本発明を詳細に説明する。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below in detail.
【００１５】本発明のＰＣグラウト材は、特に、ブレー
ン比表面積が２０００〜５０００ｃｍ2 ／ｇの無機質フ
ィラーを配合したことに特徴を有する。この無機質フィ
ラーのブレーン比表面積が２０００ｃｍ2 ／ｇ未満で
は、得られるＰＣグラウト材の材料分離が起こり易くな
り、ブリーディングが発生し易くなる。無機質フィラー
のブレーン比表面積が５０００ｃｍ2 ／ｇを超えると、
得られるＰＣグラウト材の流動性が悪くなる。The PC grout material of the present invention is particularly characterized in that an inorganic filler having a Blaine specific surface area of 2000 to 5000 cm 2 / g is blended. If the Blaine specific surface area of the inorganic filler is less than 2000 cm 2 / g, material separation of the obtained PC grout material easily occurs, and bleeding easily occurs. When the Blaine specific surface area of the inorganic filler exceeds 5000 cm 2 / g,
The fluidity of the obtained PC grout material becomes poor.
【００１６】この無機質フィラーとしては、高炉スラ
グ、フライアッシュ、石灰石（炭酸カルシウム）、シリ
カフューム等を用いることができるが、特に、石灰石粉
末が好適である。As the inorganic filler, blast furnace slag, fly ash, limestone (calcium carbonate), silica fume and the like can be used, and limestone powder is particularly preferable.
【００１７】本発明のＰＣグラウト材は、このような無
機質フィラーとセメントと高性能減水剤、増粘剤及び遅
延剤とを下記配合となるように水に混練してなるもので
ある。The PC grout of the present invention, such inorganic filler and cement and superplasticizer, in which the thickener and retardant obtained by kneading the water so that the lower SL formulation.
【００１８】ＰＣグラウト材の配合割合 セメント：１００重量部 ブレーン比表面積2000〜5000ｃｍ２／ｇの無機質フィラー ：１０〜４０重量部 遅延剤：セメント及び無機質フィラーの合計に対して ０．０３〜０．１２重量％ 増粘剤：セメント及び無機質フィラーの合計に対して ０．０５〜０．３重量％ 高性能減水剤：セメント及び無機質フィラーの合計に対して ０．５〜１．５重量％ 水：セメント及び無機質フィラーの合計に対して３５〜４５重量％ なお、遅延剤としては、ピロリン酸ナトリウム等の水溶
性リン酸塩、硫酸ナトリウム、クエン酸ソーダ等を用い
ることができ、増粘剤としては、アクリル系水溶性高分
子化合物、セルロース系高分子化合物等を用いることが
できる。また、高性能減水剤としては、ナフタリンスル
ホン酸ホルマリン高縮合物、メラミンを変成した水溶性
ポリマーを主成分にしたもの等を用いることができる。[0018] Blend ratio cement PC grout: 100 parts by Blaine specific surface area 2000~5000cm 2 / g of the inorganic filler: 10 to 40 parts by weight retarder: 0.03 to 0 with respect to the sum of cement and inorganic filler 12% by weight Thickener: 0.05 to 0.3% by weight based on the total amount of cement and inorganic filler High performance water reducing agent: 0.5 to 1.5% by weight based on the total amount of cement and inorganic filler Water : 35 to 45% by weight based on the total amount of cement and inorganic filler As the retarder, a water-soluble phosphate such as sodium pyrophosphate, sodium sulfate, sodium citrate or the like can be used. For example, an acrylic water-soluble polymer compound, a cellulose-based polymer compound, or the like can be used. Examples of the high-performance water reducing agent include a high-condensation product of formalin naphthalenesulfonic acid, a water-soluble polymer modified with melamine as a main component, and the like.
【００１９】本発明のＰＣグラウト材は、各構成材料を
所定配合で撹拌機に投入して十分に混練することにより
容易に調製することができる。The PC grout material of the present invention can be easily prepared by putting each constituent material into a stirrer in a predetermined blend and sufficiently kneading.
【００２０】[0020]
【実施例】以下に実施例及び比較例を挙げて、本発明を
より具体的に説明する。The present invention will be described more specifically with reference to the following examples and comparative examples.
【００２１】実施例１，２、比較例１〜４ 表１に示す材料配合で、万能撹拌機（ラボミキサ）に、
材料投入後、羽根の回転数１０００ｒｐｍで、４分間混
練することによりＰＣグラウト材を調製した。なお、用
いた材料は次の通りである。Examples 1 and 2 and Comparative Examples 1 to 4 Using the materials shown in Table 1, a universal stirrer (lab mixer) was used.
After the introduction of the materials, the PC grout was prepared by kneading at 1,000 rpm for 4 minutes. The materials used are as follows.
【００２２】セメント：普通ポルトランドセメント（三
菱マテリアル社製） 石灰石粉末Ａ：普通炭酸カルシウム（（株）ニッチツ
製、ブレーン比表面積 ３１００ｃｍ2 ／ｇ） 石灰石粉末Ｂ：炭酸カルシウム（（株）ニッチツ製、ブ
レーン比表面積 １７５０ｃｍ2 ／ｇ） 石灰石粉末Ｃ：炭酸カルシウム（（株）ニッチツ製、ブ
レーン比表面積 ５７００ｃｍ2 ／ｇ） 高性能減水剤：マイティ１００（花王社製、ナフタリン
スルホン酸ホルマリン高縮合物が主成分） 増粘剤：シーベターＡＤ（三共化成工業製、アクリル系
高分子化合物が主成分） 遅延剤：ピロリン酸ナトリウム（Na4P2O7・10H2O)（特級
試薬）Cement: Ordinary Portland cement (Mitsubishi Materials Corporation) Limestone powder A: Ordinary calcium carbonate (Nichetz Co., Ltd., Blaine specific surface area 3100 cm 2 / g) Limestone powder B: Calcium carbonate (Nichetz Co., Brain) Specific surface area 1750 cm 2 / g) Limestone powder C: Calcium carbonate (manufactured by Nichetsu Co., Ltd., Blaine specific surface area 5700 cm 2 / g) High performance water reducing agent: Mighty 100 (manufactured by Kao Corporation, high-condensate of naphthalenesulfonic acid formalin) ) thickener: Shibeta AD (Sankyo Kasei Kogyo, acrylic polymer compound is the main component) retarder: sodium pyrophosphate (Na 4 P 2 O 7 · 10H 2 O) ( guaranteed reagent)
【００２３】[0023]
【表１】 [Table 1]
【００２４】得られたＰＣグラウト材について、下記方
法に従って特性試験を行い、結果を表３に示した。The obtained PC grout was subjected to a characteristic test according to the following method, and the results are shown in Table 3.
【００２５】流動性試験：土木学会規準「ＰＣグラウト
試験方法 -JSCE-F531-1993」に準拠。なお、後掲の比較
例５についてはＪＡロートで、その他はＪ14ロートを使
用した。経時変化の測定では、グラウト混練後静置し、
測定前約１０秒程度、手練りで撹拌した。Fluidity test: Based on the Japan Society of Civil Engineers standard "PC grout test method -JSCE-F531-1993". In JA funnel for Comparative Example 5 given later, and the other was used J 14 funnel. In the measurement of the change over time, the grout was kneaded and allowed to stand,
The mixture was manually mixed for about 10 seconds before the measurement.
【００２６】ブリーディング試験：土木学会規準「ＰＣ
グラウト試験方法 -JSCE-F531-1993」 圧縮強度試験：土木学会規準「ＰＣグラウト試験方法 -
JSCE-F531-1993」 レオロジー（塑性粘度）試験：円筒型回転粘度計を使
用。Bleeding test: PCS standard "PC
Grout test method -JSCE-F531-1993 "Compressive strength test: JSCE standard" PC grout test method-
JSCE-F531-1993 ”Rheology (plastic viscosity) test: Using a cylindrical rotational viscometer.
【００２７】比較例５〜７ 表２に示す材料配合で、万能撹拌機（ラボミキサ）に、
材料投入後、羽根の回転数１０００ｒｐｍで混練するこ
とによりＰＣグラウト材を調製した。混練時間は比較例
５，６では３分間、また、比較例７ではセメント及び水
を３分間混練した後、混和剤を投入し、更に３分間、合
計６分間混練した。なお、用いた材料は次の通りであ
る。Comparative Examples 5 to 7 With the material formulations shown in Table 2, a universal stirrer (lab mixer) was used.
After the introduction of the material, a PC grout material was prepared by kneading at a blade rotation speed of 1000 rpm. The kneading time was 3 minutes in Comparative Examples 5 and 6, and in Comparative Example 7, cement and water were kneaded for 3 minutes, then an admixture was added, and kneading was further performed for 3 minutes, for a total of 6 minutes. The materials used are as follows.
【００２８】セメント：普通ポルトランドセメント（三
菱マテリアル社製） 減水剤：ポゾリス No.８（ＮＭＢ社製、リグニンスルホ
ン酸化合物が主成分） 膨張剤：アルミニウム粉末 混和剤Ｉ：ポゾリスＧＦ−１７００（ＮＭＢ社製） 混和剤II：コンベックス２０８（極東鋼弦コンクリート
振興社製）Cement: ordinary Portland cement (manufactured by Mitsubishi Materials Corporation) Water reducing agent: pozzolith No. 8 (manufactured by NMB, mainly composed of ligninsulfonic acid compound) Swelling agent: aluminum powder Admixture I: pozzolith GF-1700 (manufactured by NMB) Admixture II: Convex 208 (manufactured by Far East Steel String Concrete Co., Ltd.)
【００２９】[0029]
【表２】 [Table 2]
【００３０】得られたＰＣグラウト材について、実施例
１と同様にして特性試験を行い、結果を表３に示した。The obtained PC grout was subjected to a characteristic test in the same manner as in Example 1, and the results are shown in Table 3.
【００３１】[0031]
【表３】 [Table 3]
【００３２】表３より次のことが明らかである。The following is clear from Table 3.
【００３３】即ち、石灰石粉末又は遅延剤を配合してい
ない比較例１，２では、短時間で流動性が乏しくなり、
可使時間が短い。また、石灰石粉末を配合したものであ
っても、そのブレーン比表面積が２０００ｃｍ2 ／ｇよ
り小さい比較例３ではブリーディングが発生し、ブレー
ン比表面積が５０００ｃｍ2 ／ｇより大きい比較例４で
は流動性が悪いものとなる。That is, in Comparative Examples 1 and 2 in which limestone powder or retarder was not blended, the fluidity became poor in a short time,
The pot life is short. Even in the case where limestone powder was blended, bleeding occurred in Comparative Example 3 having a Blaine specific surface area of less than 2000 cm 2 / g, and fluidity was observed in Comparative Example 4 having a Blaine specific surface area of more than 5000 cm 2 / g. It will be bad.
【００３４】また、従来品を再現した比較例５〜７のう
ち、混和剤を含まない比較例５では流動性が悪く、ま
た、ブリーディングが発生する。一方、混和剤を配合し
た比較例６，７ではブリーディングは防止され、特に比
較例６では流動性も良好ではあるが、いずれも粘性が高
いため、注入時の注入圧力が高くなり、注入速度が遅く
なることが予想される。Of Comparative Examples 5 to 7 in which the conventional product was reproduced, Comparative Example 5 containing no admixture had poor fluidity and caused bleeding. On the other hand, in Comparative Examples 6 and 7 in which the admixture was blended, bleeding was prevented, and especially in Comparative Example 6, the fluidity was good. However, since all of them had high viscosity, the injection pressure at the time of injection was high, and the injection speed was low. Expected to be slow.
【００３５】[0035]
【発明の効果】以上詳述した通り、本発明のＰＣグラウ
ト材は、流動性の低下が少ないため、可使時間を長く確
保することができ、しかも、粘性が低いことから、注入
時の注入圧力を低減でき、高い注入速度で効率的に注入
することができる。従って、本発明のＰＣグラウト材に
よれば、注入作業性が大幅に改善される。As described in detail above, the PC grout material of the present invention is capable of ensuring a long pot life because of a small decrease in fluidity, and has a low viscosity. Pressure can be reduced and injection can be performed efficiently at a high injection rate. Therefore, according to the PC grout material of the present invention, the injection workability is greatly improved.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ Ｃ０４Ｂ 24:22 Ｃ０４Ｂ 24:26 Ｄ 24:26 22:16 Ａ 22:16） 111:70 111:70 (72)発明者 黒岩 義仁 埼玉県大宮市北袋町１丁目297番地 三 菱マテリアル株式会社セメント研究所内 (56)参考文献 特開 平２−102162（ＪＰ，Ａ) 特開 平１−96053（ＪＰ，Ａ) 特開 平７−41352（ＪＰ，Ａ) 特開 平９−32294（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) C04B 7/00 - 28/36 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification code FI C04B 24:22 C04B 24:26 D 24:26 22:16 A 22:16) 111: 70 111: 70 (72) Inventor Kuroiwa Yoshihito 1-297 Kitabukuro-cho, Omiya City, Saitama Prefecture Cement Research Institute, Mitsubishi Materials Corporation (56) References JP-A-2-102162 (JP, A) JP-A-1-96053 (JP, A) JP-A-7 -41352 (JP, A) JP-A-9-32294 (JP, A) (58) Fields investigated (Int. Cl. 7 , DB name) C04B 7/ 00-28/36
Claims (2)
剤及びブレーン比表面積が２０００〜５０００ｃｍ２／
ｇの無機質フィラーを下記配合となるように水と混練し
てなるＰＣグラウト材。セメント ：１００重量部 無機質フィラー：１０〜４０重量部 遅延剤 ：セメント及び無機質フィラーの合計に
対して０．０３ 〜０．１２重量％ 増粘剤 ：セメント及び無機質フィラーの合計に
対して０．０５ 〜０．３重量％ 高性能減水剤 ：セメント及び無機質フィラーの合計に
対して０．５〜 １．５重量％ Claims: 1. Cement, high performance water reducing agent, thickener, delay
Agent and Blaine specific surface area 2000-5000cm2/
g of inorganic fillerSo that it has the following compositionKnead with water
PC grout material.cement : 100 parts by weight Inorganic filler: 10 to 40 parts by weight Retarder ： To the total of cement and inorganic filler
0.03 ~ 0.12% by weight Thickener ： To the total of cement and inorganic filler
0.05 for ~ 0.3% by weight High performance water reducing agent ： To the total of cement and inorganic filler
0.5 ~ 1.5% by weight
灰石の粉末であることを特徴とするＰＣグラウト材。2. The PC grout according to claim 1, wherein the inorganic filler is limestone powder.