JP3211175B2 - Decorative sheet for building materials - Google Patents

Decorative sheet for building materials

Info

Publication number
JP3211175B2
JP3211175B2 JP12204893A JP12204893A JP3211175B2 JP 3211175 B2 JP3211175 B2 JP 3211175B2 JP 12204893 A JP12204893 A JP 12204893A JP 12204893 A JP12204893 A JP 12204893A JP 3211175 B2 JP3211175 B2 JP 3211175B2
Authority
JP
Japan
Prior art keywords
pattern
layer
printing
glitter
decorative sheet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP12204893A
Other languages
Japanese (ja)
Other versions
JPH06305104A (en
Inventor
義昭 根津
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dai Nippon Printing Co Ltd
Original Assignee
Dai Nippon Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=14826320&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=JP3211175(B2) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Dai Nippon Printing Co Ltd filed Critical Dai Nippon Printing Co Ltd
Priority to JP12204893A priority Critical patent/JP3211175B2/en
Publication of JPH06305104A publication Critical patent/JPH06305104A/en
Application granted granted Critical
Publication of JP3211175B2 publication Critical patent/JP3211175B2/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【産業上の利用分野】本発明は、建物の内装やドア、住
器などに用いられる木目調の化粧シートに関するもので
ある。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a wood-grain decorative sheet used for interiors of buildings, doors, household appliances and the like.

【0002】[0002]

【従来の技術】従来より、木目柄などの化粧シートに関
して、例えば、ポリ塩化ビニルフィルムなどのような熱
可塑性樹脂フィルムに絵柄を印刷したもの、或いは、そ
の上に直接、又は熱可塑性透明フィルムを介してエンボ
スなどの方法により木目に相当するパターンの凹部を設
け、更にその凹部にインキを充填したものなどがある。
また、これらの化粧シートを、より本物に近い外観や手
触りにするために、透明性を有する艶消し剤を添加した
インキを用いたり、また、天然木の板材が具備する照り
を表現するために印刷絵柄層の下に光輝性インキ層を付
加し、これと微細凹凸模様を組み合わせたりする方法も
行われている。
2. Description of the Related Art Conventionally, for decorative sheets such as wood grain patterns, for example, a pattern is printed on a thermoplastic resin film such as a polyvinyl chloride film or the like, or a transparent thermoplastic film is directly formed thereon. There is a method in which a concave portion having a pattern corresponding to a grain is provided by a method such as embossing through an intervening portion, and the concave portion is further filled with ink.
Also, in order to make these decorative sheets look and feel closer to the real thing, using ink with a transparent matting agent added, or to express the shine of natural wood board material There is also a method in which a glitter ink layer is added under a printed picture layer, and this is combined with a fine uneven pattern.

【0003】只、この照りの表現については、これまで
の技術では、未だ、見る角度の変化による照りの移動パ
ターンと絵柄とが同調しないとか、照りの強弱のコント
ロールができず、単調なものとなるなどの欠点が残され
ている。
[0003] However, the expression of the illuminance is a monotonous one with the conventional technology, because the movement pattern of the illuminance due to the change of the viewing angle is not synchronized with the pattern, or the intensity of the illuminance cannot be controlled. Some disadvantages remain.

【0004】[0004]

【発明が解決しようとする課題】本発明は、前記のよう
な木目調の化粧シートの照りに関連する欠点を改善し、
天然木の板材表面が具備する質感および照りの状況をよ
り忠実に再現し、より高い意匠性の化粧シートを提供す
ることを目的とする。
SUMMARY OF THE INVENTION The present invention has been made to solve the above-mentioned drawbacks associated with the luster of a wood-grained decorative sheet,
It is an object of the present invention to more faithfully reproduce the texture and illuminance of a natural wooden board surface, and to provide a decorative sheet with a higher design.

【0005】[0005]

【課題を解決するための手段】上記の目的に鑑み、種々
研究の結果、以下に説明する方法により本発明の完成に
至ったものである。即ち、本請求項1の発明は、透明な
熱可塑性樹脂フィルムの一方の面に、第1の光輝性印刷
層、複数の絵柄印刷層、第2の光輝性印刷層、隠蔽性印
刷層を順次積層し、更に、その面に微細凹凸模様をエン
ボス方式により設け、少なくとも隠蔽性印刷層の透明熱
可塑性樹脂フィルム側の界面にまで達するように微細凹
凸模様が設けられた化粧シートからなる。
Means for Solving the Problems In view of the above objects, the present invention has been completed by the following method as a result of various studies. That is, the first aspect of the present invention provides a transparent thermoplastic resin film in which a first glitter print layer, a plurality of picture print layers, a second glitter print layer, and a concealment print layer are sequentially formed on one surface of a transparent thermoplastic resin film. The decorative sheet is laminated and further provided with a fine uneven pattern on its surface by an embossing method, and is provided with a fine uneven pattern so as to reach at least the interface of the opaque print layer on the transparent thermoplastic resin film side.

【0006】更に、本請求項の発明は、上記成に
いて、少なくとも第1の光輝性印刷層が、一部の絵柄印
刷層のパターンに同調するように設けられた化粧シート
からなる。
Furthermore, the invention is the claims 1 and have your <br/> above configuration, at least a first bright print layer, provided to tune to a pattern of a part of the picture-printed layer It consists of a decorative sheet.

【0007】そして、本請求項の発明は、本請求項
発明の構成による化粧シートにおいて、微細凹凸模様
が平行曲線群、もしくは平行曲線群と平行直線群を組み
合わせたパターンから成り、且つその凹部と凸部の高さ
の差が3〜50μmの範囲にあり、また、その間隔が1
〜1000μmの範囲にある化粧シートからなってい
る。
[0007] Then, the invention of the claims 2, present claim 1
In the decorative sheet according to the configuration of the invention, the fine uneven pattern is formed of a pattern formed by combining a parallel curve group or a parallel curve group and a parallel straight line group, and the difference in height between the concave portion and the convex portion is in the range of 3 to 50 μm. Yes, and the interval is 1
It consists of a decorative sheet in the range of 〜1000 μm.

【0008】次に、図面を用いて本発明を更に詳細に説
明する。図1は、本発明の化粧シートの実施例の構成を
示す模式断面図である。即ち、本発明の化粧シートは、
透明熱可塑性樹脂フィルム1の一方の面に、第1の光輝
性印刷層2、一部の絵柄印刷層3、その他の絵柄印刷層
4、4′、第2の光輝性印刷層5、隠蔽性印刷層6を順
次積層し、その印刷面に熱エンボス等により、微細凹凸
模様7を設けた構成を基本部分とし、更に、透明熱可塑
性樹脂フィルムのもう一方の面に、必要により艶調整透
明樹脂層8、導管柄印刷層9を順に設けた構成である。
尚、この構成は、主要絵柄印刷層や光輝性印刷層を透明
熱可塑性樹脂フィルムを通して見る形式であり、通常、
フィルム印刷で裏刷りと呼ばれている印刷方法を主体と
するものである。
Next, the present invention will be described in more detail with reference to the drawings. FIG. 1 is a schematic sectional view showing the configuration of an embodiment of the decorative sheet of the present invention. That is, the decorative sheet of the present invention,
On one surface of the transparent thermoplastic resin film 1, a first glitter print layer 2, a part of the pattern print layer 3, other pattern print layers 4, 4 ', a second glitter print layer 5, a concealing property A printing layer 6 is sequentially laminated, and a fine uneven pattern 7 is provided on the printing surface by heat embossing or the like as a basic part. Further, on the other surface of the transparent thermoplastic resin film, if necessary, a gloss adjusting transparent resin is provided. This is a configuration in which a layer 8 and a conduit pattern printing layer 9 are provided in this order.
In addition, this constitution is a form in which a main pattern printing layer or a glittering printing layer is viewed through a transparent thermoplastic resin film.
The main method is a printing method called back printing in film printing.

【0009】また、図2の(イ)、(ロ)は、それぞれ
本発明の化粧シートの印刷面に設ける微細凹凸模様のパ
ターンの実施例を示す模式平面図であり、(イ)は平行
曲線群によるパターンの一実施例、(ロ)は平行曲線群
と平行直線群の組み合わせによるパターンの一実施例を
示している。
FIGS. 2 (a) and 2 (b) are schematic plan views showing examples of fine uneven patterns provided on the printing surface of the decorative sheet according to the present invention, wherein (a) is a parallel curve. (B) shows an embodiment of a pattern by a combination of a parallel curve group and a parallel straight line group.

【0010】以下に本発明の化粧シートに使用する材料
及び加工方法等について説明する。基材である透明熱可
塑性樹脂フィルムは、ポリ塩化ビニルフィルムが主に使
用でき、厚さは0.06〜0.30mmが取扱も容易で
好ましい。その他セルロース系樹脂、ポリオレフィン系
樹脂、ポリエステル系樹脂、ポリスチレン系樹脂、ポリ
カーボネート樹脂などのフィルムが使用できる。
The materials used for the decorative sheet of the present invention, the processing method and the like will be described below. As the transparent thermoplastic resin film as the base material, a polyvinyl chloride film can be mainly used, and the thickness is preferably 0.06 to 0.30 mm because of easy handling. In addition, films of cellulose resin, polyolefin resin, polyester resin, polystyrene resin, polycarbonate resin and the like can be used.

【0011】光輝性印刷層は、光輝性顔料を含有するイ
ンキで希望する照りの形状を含むパターンの版を用いて
印刷により設ける。印刷は、グラビア印刷、フレキソ印
刷、スクリーン印刷等の公知の方法を利用できる。ま
た、光輝性顔料としては、例えば二酸化チタン被覆雲
母、魚鱗箔、酸塩化ビスマス等の真珠光沢や干渉光沢を
有するパール顔料、或いは、アルミニウム粉、銅粉、真
鍮粉等の金属粉顔料、そして、アルミニウム等の光輝性
物質を蒸着したフィルムの粉砕物等も使用できる。尚、
光輝性印刷層の印刷に用いるインキ(以下光輝性イン
キ)への添加量は、インキ全量に対して5〜10重量%
程度であり、第1の光輝性印刷層に使用する光輝性イン
キへの光輝性顔料の添加量は、第2の光輝性印刷層に使
用する光輝性インキへの光輝性顔料の添加量よりも、若
干少なめにすることが好ましい。
The glitter print layer is provided by printing using a plate having a pattern containing a desired shine shape with an ink containing a glitter pigment. For the printing, a known method such as gravure printing, flexographic printing, or screen printing can be used. Further, as the brilliant pigment, for example, titanium dioxide-coated mica, fish scale foil, pearl pigment having pearl luster or interference luster such as bismuth oxychloride, or aluminum powder, copper powder, metal powder pigment such as brass powder, and A pulverized film of a film on which a glittering substance such as aluminum is deposited can also be used. still,
The amount added to the ink used for printing the glitter print layer (hereinafter referred to as glitter ink) is 5 to 10% by weight based on the total amount of the ink.
The amount of the glitter pigment added to the glitter ink used for the first glitter print layer is larger than the amount of the glitter pigment added to the glitter ink used for the second glitter print layer. However, it is preferable to make it slightly smaller.

【0012】また、インキのベヒクルには、ビニル系樹
脂、アクリル系樹脂、アミノアルキッド系樹脂、ブチラ
ール樹脂等が使用でき、これらの中から適宜選択する。
As the vehicle of the ink, a vinyl resin, an acrylic resin, an amino alkyd resin, a butyral resin, and the like can be used.

【0013】絵柄印刷層は、通常の化粧シート用インキ
の印刷により設けられ、インキの顔料は無機或いは有機
の公知の顔料を使用できる。また、ベヒクルは、前記の
光輝性インキと同じで上記の中から選択できる。また、
印刷の版式も光輝性印刷層と同様グラビア印刷、フレキ
ソ印刷、スクリーン印刷等公知のものを利用できるが、
光輝性印刷層と同じ方法を用いるのが合理的である。版
の絵柄は木目の柾、板等特に限定はされない。色数は、
通常2色〜3色の範囲で行える。
The pattern printing layer is provided by printing an ordinary ink for a decorative sheet, and the pigment of the ink may be a known inorganic or organic pigment. In addition, the vehicle can be selected from the same as the glitter ink described above. Also,
As for the printing plate type, a known one such as gravure printing, flexographic printing, or screen printing can be used similarly to the glittering printing layer.
It is reasonable to use the same method as for the glitter print layer. The design of the plate is not particularly limited, such as wood grain straight and board. The number of colors is
Usually, it can be performed in a range of two to three colors.

【0014】尚、隠蔽性印刷層については、インキ顔料
に酸化チタン等の隠蔽性に優れたものを使用するが、ベ
ヒクルは絵柄用インキと同じものが使用でき、全ベタ版
を用いて絵柄印刷層などと同じ方式で印刷するのが良
い。隠蔽力自体は被膜の厚さにも左右されるため、必要
があれば印刷方式以外にロールコーティングなどで厚塗
りすることもできる。
For the concealable printing layer, an ink pigment having excellent concealing properties, such as titanium oxide, is used, but the same vehicle as the picture ink can be used. It is good to print in the same method as the layer. The hiding power itself is also affected by the thickness of the film, so if necessary, thick coating can be performed by roll coating or the like in addition to the printing method.

【0015】艶調整透明樹脂層は、通常、透明熱可塑性
樹脂フィルムの表面が艶のある状態に仕上げられている
ため、天然木の板材の表面状態に近づけるためシリカ等
のマット剤を含む透明樹脂塗料を印刷またはコーティン
グにより全面に塗布するものである。透明樹脂は化粧シ
ートの表面性能を良くするため2液硬化型ウレタン樹脂
等を使用するのが好ましい。また、導管柄印刷層につい
ても、艶調整透明樹脂層の上に設けることからインキの
ベヒクルには前記同様2液硬化型ウレタン樹脂等を使用
することが好ましい。
The gloss-controlling transparent resin layer is usually made of a transparent thermoplastic resin film whose surface is finished in a glossy state, so that the transparent resin layer contains a matting agent such as silica in order to approximate the surface state of a natural wood board. The paint is applied over the entire surface by printing or coating. As the transparent resin, it is preferable to use a two-component curable urethane resin or the like in order to improve the surface performance of the decorative sheet. Since the conduit pattern printing layer is also provided on the gloss adjusting transparent resin layer, it is preferable to use a two-component curable urethane resin or the like as described above for the ink vehicle.

【0016】微細凹凸模様については、ロール状金属版
を使用する熱エンボス方式等により設けるが、凹凸のパ
ターンは、凹部と凸部の高さの差が3〜50μmで、凹
部の間隔が1〜1000μmの平行曲線群、もしくは平
行曲線群と平行直線群の組み合わせからなる。そして、
平行曲線群は正弦波、サイクロイド、楕円関数、ベッセ
ル関数等の曲線を連結し、平行に配列したもの、或いは
前記関数曲線を、そのパラメーターを変化させて各曲線
間の間隔を等分し、間隔が線方向に滑らかに変化するよ
うに形成したものも含んでいる。
The fine uneven pattern is provided by a hot embossing method using a roll-shaped metal plate or the like. The uneven pattern has a height difference between the concave portion and the convex portion of 3 to 50 μm and an interval between the concave portions of 1 to 50 μm. It consists of a parallel curve group of 1000 μm or a combination of a parallel curve group and a parallel straight line group. And
The parallel curve group connects curves such as sine wave, cycloid, elliptic function, Bessel function, etc. and arranges them in parallel, or the function curve is divided into equal intervals by changing its parameters, Are formed so as to change smoothly in the line direction.

【0017】尚、天然木目板の照りは、木材の種類、木
材の部位、そして切断する方向などにより照りのパター
ンや方向が変化する。従って、印刷した木目模様の流れ
方向と凹凸曲線の流れ方向とは、例えば、直交させた場
合、現れる照りのパターンは木目模様の方向に沿った縦
の照りとなるが、天然の板では虎斑と言われる横方向の
照りなどもあり、この場合には木目模様の流れ方向と凹
凸曲線の流れ方向とを平行させる必要がある。従って、
この角度は、必ずしも限定するものではない。
The pattern and direction of illumination of a natural woodgrain board varies depending on the type of wood, the portion of the wood, and the cutting direction. Therefore, the flow direction of the printed grain pattern and the flow direction of the uneven curve are, for example, when orthogonal, the pattern of shining that appears is vertical shining along the direction of the grain pattern, but on a natural board it is a tiger spot. There is also a so-called lateral illumination, and in this case, it is necessary to make the flow direction of the grain pattern and the flow direction of the uneven curve parallel. Therefore,
This angle is not necessarily limited.

【0018】[0018]

【作用】本請求項1の発明の化粧シートは、透明な熱可
塑性樹脂フィルムを基材とし、その一方の面に、第1の
光輝性印刷層、複数の絵柄印刷層、第2の光輝性印刷
層、隠蔽性印刷層を順次積層し、更に、その面に微細凹
凸模様をエンボス方式により設けている。このため、第
1の光輝性印刷層と絵柄印刷層の下に設けた第2の光輝
性印刷層およびエンボスによる微細凹凸模様により、光
学的に凹凸模様に応じたパターンの天然木目板で言う照
りが現出し、しかも、その照りに強弱の階調ができる。
The decorative sheet according to the first aspect of the present invention comprises a transparent thermoplastic resin film as a base material, a first glitter print layer, a plurality of picture print layers, and a second glitter print on one surface. A printing layer and a concealable printing layer are sequentially laminated, and a fine uneven pattern is provided on the surface thereof by an embossing method. For this reason, the second glittering printing layer provided below the first glittering printing layer and the picture printing layer and the fine concavo-convex pattern formed by embossing provide an optical pattern having a pattern corresponding to the concavo-convex pattern optically. Appear, and furthermore, a strong gradation can be formed in the illumination.

【0019】本請求項の発明の化粧シートは、更に上
記構成において、少なくとも第1の光輝性印刷層が、一
部の絵柄印刷層のパターンに同調するように設けている
ため、前記の照りのパターンとその移動が絵柄に同調す
るようになる。
The decorative sheet according to the first aspect of the present invention further comprises
In Ki構 formed, at least a first photoluminescent printing layer, since the provided to tune to a pattern of a part of the picture-printed layer, the pattern and the movement of said shine is to tune to the picture.

【0020】また、本請求項の発明の化粧シートは、
請求項1の構成の化粧シートにおいて、微細凹凸模様を
平行曲線群、もしくは平行曲線群と平行直線群を組み合
わせたパターンとし、更に、凹部と凸部の高さの差を3
〜50μmの範囲に、また、凹部の線の間隔を1〜10
00μmの範囲にあるようにしたものである。これによ
り、照りのパターン自体が天然木目板に見られる照りの
形状に近いものを表現できるようになり、同時に見る角
度による照りの移動が絵柄に同調し、しかも、照りに強
弱の階調が付くようになる。
Further, the decorative sheet according to the second aspect of the present invention
2. The decorative sheet according to claim 1, wherein the fine uneven pattern is a pattern formed by combining a parallel curve group or a parallel curve group and a parallel straight line group.
To 50 μm, and the interval between the concave lines is 1 to 10 μm.
The thickness is in the range of 00 μm. As a result, the illuminated pattern itself can express a shape close to the illuminated shape seen on a natural woodgrain board, and at the same time, the movement of the illuminated light according to the viewing angle is synchronized with the pattern, and the intensity of the illuminated light has a strong gradation. Become like

【0021】[0021]

【実施例】以下に実施例により本発明を詳細に説明す
る。 (実施例1)印刷する木目の絵柄はメイプル柄とし、印
刷する基材は透明な塩化ビニルフィルム(三宝樹脂製
DH−1)で厚さ0.15mmとした。そして、このフ
ィルムの一方の面に、前記の絵柄の一部と同調するよう
に光輝性インキ(化Xパール 昭和インク工業製)を
用いて、グラビア印刷により第1の光輝性印刷層をパタ
ーンAで印刷した。
The present invention will be described below in detail with reference to examples. (Example 1) The wood pattern to be printed is a maple pattern, and the substrate to be printed is a transparent vinyl chloride film (manufactured by Sanbo Resin).
DH-1) and a thickness of 0.15 mm. Then, on one surface of this film, a first glitter print layer was formed by gravure printing using a glitter ink (manufactured by Kasei X Pearl Showa Ink Kogyo Co., Ltd.) so as to synchronize with a part of the above-mentioned pattern. Printed with.

【0022】次に、絵柄用インキ(化X 昭和インク工
業製)を用いてメイプル柄をグラビア印刷により印刷
し、更に、この絵柄と同調するように、光輝性インキ
(化Xパール 昭和インク工業製)を用いてグラビア
印刷により前記のパターンAと異なるパターンBで第2
の光輝性印刷層を印刷した。尚、パターンAはメイプル
柄に特徴的な放射繊維によって得られる横照りを表現す
るため、照りを強調する部分(主に春材の明るい部分)
にインキがのるパターンとし、パターンBは、パターン
Aほど強調しなくてもよい部分にインキが乗るように設
定した。
Next, a maple pattern is printed by gravure printing using a picture ink (manufactured by Showa Ink Industries, Ltd.), and a glittering ink (manufactured by Showa Ink Industries, Ltd.) is synchronized with the picture. ) By gravure printing using a second pattern B different from the above-described pattern A.
Was printed. In addition, the pattern A expresses the side shine obtained by the radiation fiber characteristic of the maple pattern, and therefore, the portion that emphasizes the shine (mainly the bright portion of the spring material)
The pattern B is set so that the ink is applied to a portion that does not need to be emphasized as much as the pattern A.

【0023】ここで、パターンAおよびパターンBのグ
ラビア版の製版方法について、概略の補足説明をする。
先ず、メイプルの天然木目板を原稿とし、これをカメラ
の正面に置き、照りが効果的に観察される角度に光源を
設置してネガフィルムにより撮影する。この陰画の反射
光部のみを抽出して図3の(イ)にそのパターンを模型
図として示したような照り全体の陰画を作成する。次
に、この陰画を基に、スキャナーにより濃度の略中間値
を基準として、照りの強い部分と弱い部分の二つに分け
て読み込ませて、図3の(ロ)、(ハ)にそのパターン
の模型図を示したような二種類の黒パターンのフィルム
を作成する。(ロ)は照りの強い部分のパターンで第1
の光輝性印刷層の絵柄とし、(ハ)は照りの弱い部分の
パターンで第2の光輝性印刷層の絵柄とするものであ
る。このようにして作成した二種類の黒パターンのフィ
ルムを用いて、それぞれ木目の絵柄版と見当合わせし、
通常のカーボンティッシュを使用する刷版方式で、露
光、現像、エッチング、メッキ、研磨を行い、パターン
AおよびパターンBの印刷用の版を作成した。尚、前記
の第1および第2の光輝性印刷層のパターンの形状は本
実施例において用いたものであり、これに限定されるも
のではない。例えば、第2の光輝性印刷層の絵柄パター
ンとして図3の(イ)に示した照り全体のパターンを使
用することもできる。
Here, a brief supplementary explanation will be given of a method of making a gravure plate of the pattern A and the pattern B.
First, a maple natural wood grain board is used as a document, placed in front of a camera, and a light source is installed at an angle at which illuminance can be effectively observed, and photographing is performed using a negative film. Only the reflected light portion of this negative image is extracted, and a negative image of the entire illuminated light whose pattern is shown as a model diagram in FIG. 3A is created. Next, based on the negative image, a scanner is read into two parts, a bright part and a weak part, on the basis of a substantially intermediate value of the density, and the patterns are shown in (b) and (c) of FIG. A film with two types of black patterns as shown in the model drawing of FIG. (B) is the pattern of the strong shining part.
(C) is a pattern of the second bright print layer, which is a pattern of a weakly illuminated portion. Using the two types of black pattern films created in this way, register each with the wood grain pattern plate,
Exposure, development, etching, plating, and polishing were performed by a printing plate method using a normal carbon tissue to prepare printing plates for pattern A and pattern B. The shapes of the patterns of the first and second glitter print layers are used in the present embodiment, and are not limited thereto. For example, the entire pattern shown in FIG. 3A can be used as the picture pattern of the second glittering print layer.

【0024】続いて、二酸化チタン等の隠蔽性に優れた
顔料を含んだインキで、パターンBの上にグラビア印刷
により、全面ベタ版を使用して隠蔽性印刷層を印刷し
た。
Subsequently, a concealing printing layer was printed on the pattern B by gravure printing using an ink containing a pigment having excellent concealing properties such as titanium dioxide, using a solid printing plate on the entire surface.

【0025】このようにして得た印刷シートの印刷面
に、加熱温度165℃、スピード10m/min 、エンボ
ス圧4kgf/cm2 で、サインカーブ状の平行曲線群よりな
るパターンの微細な凹凸模様を設けたエンボス版を使用
し、木目の方向とサインカーブ状のエンボスラインとが
平行するように位置合わせしてエンボス加工を施した。
このエンボス版の線状の凸部の高さは12μmであり、
凸部と凸部の間隔は70μmである。尚、このエンボス
加工により、印刷シートに設けられた凹凸模様は、図1
に示したように、各印刷層を通して第1の光輝性印刷層
と透明熱可塑性樹脂フィルムの界面にまで達していた。
この状態は、照りを発現させるために最も好ましい状態
である。
On the printing surface of the printing sheet thus obtained, a fine irregular pattern of a pattern consisting of a group of sine-curved parallel curves was formed at a heating temperature of 165 ° C., a speed of 10 m / min, and an embossing pressure of 4 kgf / cm 2. Using the provided embossing plate, embossing was performed by aligning the grain direction and the sine curve-shaped embossing line so as to be parallel.
The height of the linear projections of this embossing plate is 12 μm,
The interval between the convex portions is 70 μm. In addition, the uneven pattern provided on the print sheet by this embossing is shown in FIG.
As shown in the above, the ink reached the interface between the first glittering printing layer and the transparent thermoplastic resin film through each printing layer.
This state is the most preferable state for expressing illuminance.

【0026】更に、この印刷シートのエンボス面と反対
側の面に、艶調整透明樹脂層としてシリカ等のマット剤
を含む2液硬化型ウレタン樹脂系の塗料をロールコータ
ーで塗布し、続いて、この艶調整透明樹脂層より低い艶
となる2液硬化型ウレタン樹脂系の絵柄用インキを用い
て、木目の導管柄を印刷して本発明の化粧シートを得
た。このようにして得た化粧シートには、天然のメイプ
ルを使用した化粧材に近い階調のある横照りが見られ、
照りの移動も絵柄に同調し、これまでにない高い意匠性
が得られた。
Further, a two-part curable urethane resin-based paint containing a matting agent such as silica is applied as a gloss-adjusting transparent resin layer on a surface opposite to the embossed surface of the printed sheet by a roll coater. Using a two-component curable urethane resin-based pattern ink having a gloss lower than that of the gloss-adjusting transparent resin layer, a wood grain conduit pattern was printed to obtain a decorative sheet of the present invention. In the decorative sheet obtained in this way, there is horizontal gradation with gradation close to that of a decorative material using natural maple,
The movement of the shining was also synchronized with the pattern, and an unprecedented design was obtained.

【0027】[0027]

【発明の効果】本発明の化粧シートは、以上に説明した
ように透明な熱可塑性樹脂フィルムを基材とし、その一
方の面に、第1の光輝性印刷層、複数の色からなる絵柄
印刷層、第2の光輝性印刷層、隠蔽性印刷層を順次積層
し、更に、その面に微細凹凸模様をエンボス方式により
設けている。また、第1の光輝性印刷層と第2の光輝性
印刷層を、照りを強調したい絵柄部とそれほど強くない
照りの絵柄部とに分けて、異なるパターンでそれぞれ絵
柄に同調するように設けている。そして、エンボスによ
る微細凹凸模様を平行曲線群、もしくは平行曲線群と平
行直線群を組み合わせたパターンで構成し、凹部と凸部
の高さの差を3〜50μm、凹部を形成する線間隔を1
〜1000μmの範囲にはいるように設けた構成を採っ
ている。
As described above, the decorative sheet of the present invention comprises a transparent thermoplastic resin film as a base material, a first brilliant print layer on one surface thereof, and a pattern print comprising a plurality of colors. Layer, a second glitter print layer, and a concealment print layer are sequentially laminated, and a fine uneven pattern is provided on the surface thereof by an embossing method. In addition, the first glitter print layer and the second glitter print layer are divided into a picture part for which illumination is to be emphasized and a picture part for which illumination is not so strong, and provided so as to be synchronized with the picture in different patterns. I have. The embossed fine uneven pattern is constituted by a parallel curve group or a pattern combining the parallel curve group and the parallel straight line group, the difference in height between the concave portion and the convex portion is 3 to 50 μm, and the line interval for forming the concave portion is 1.
A configuration provided so as to be in the range of up to 1000 μm is adopted.

【0028】このような構成を採ることにより、第1の
光輝性印刷層が強い照り感を、そして第2の光輝性印刷
層がやヽ弱い照り感を現出し、絵柄に同調した階調のあ
る照りの表現を可能にした。また、これにエンボスによ
る微細凹凸模様が加わり、絵柄に同調した照りの移動と
立体感の表現が得られ、極めて天然木の化粧材に近似し
た高い意匠性の化粧シートを容易に得られると言う優れ
た効果を奏するものである。
By adopting such a configuration, the first glittering print layer gives a strong shine and the second glitter print layer gives a weak shine, and the gradation of the gradation synchronized with the picture is obtained. The expression of a certain shine was made possible. In addition, a fine uneven pattern by embossing is added to this, it is possible to obtain the movement of illuminance synchronized with the pattern and the expression of three-dimensional effect, and it is easy to obtain a decorative sheet with a high design that is extremely similar to the decorative material of natural wood. It has excellent effects.

【図面の簡単な説明】[Brief description of the drawings]

【図1】図1は、本発明の化粧シートの一実施例を示す
拡大模式断面図である。
FIG. 1 is an enlarged schematic sectional view showing one embodiment of a decorative sheet of the present invention.

【図2】図2の(イ)、(ロ)は、それぞれ本発明の化
粧シートの印刷面に、エンボスにより設ける微細凹凸模
様の実施例を示す拡大模式平面図であり、(イ)は平行
曲線群によるパターンの一実施例を示し、(ロ)は平行
曲線群と平行直線群の組み合わせによるパターンの一実
施例を示す。
FIGS. 2A and 2B are enlarged schematic plan views each showing an example of a fine uneven pattern provided by embossing on a printing surface of a decorative sheet according to the present invention, and FIGS. One example of a pattern using a curve group is shown, and (b) shows one example of a pattern using a combination of a parallel curve group and a parallel straight line group.

【図3】図3は、天然の木目板に見られる照りを表現す
るための、光輝性印刷層の絵柄パターンを示す模型図で
ある。(イ)は、照り全体のパターンを示す模型図であ
り、(ロ)は、照りの強い部分のパターンを示す模型図
で第1の光輝性印刷層の絵柄パターンに相当する。ま
た、(ハ)は、照りの弱い部分のパターンを示す模型図
で第2の光輝性印刷層の絵柄パターンに相当する。
FIG. 3 is a model diagram showing a picture pattern of a glitter print layer for expressing the shine seen on a natural wood grain board. (A) is a model diagram showing a pattern of the entire shining, and (b) is a model diagram showing a pattern of a portion having a strong shining, and corresponds to a pattern pattern of the first glitter print layer. (C) is a model diagram showing a pattern of a weakly illuminated portion, and corresponds to a picture pattern of the second glittering print layer.

【符号の説明】[Explanation of symbols]

1 透明熱可塑性樹脂フィルム 2 第1の光輝性印刷層 3 一部の絵柄印刷層 4、4′その他の絵柄印刷層 5 第2の光輝性印刷層 6 隠蔽性印刷層 7 微細凹凸模様 8 艶調整透明樹脂層 9 導管柄印刷層 10 微細凹凸模様の細線 DESCRIPTION OF SYMBOLS 1 Transparent thermoplastic resin film 2 1st glitter print layer 3 Some picture print layers 4, 4 'Other picture print layers 5 2nd glitter print layer 6 Hiding print layer 7 Fine unevenness pattern 8 Gloss adjustment Transparent resin layer 9 Conduit pattern printing layer 10 Fine lines with fine irregularities

───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平2−128843(JP,A) 特開 平3−8477(JP,A) 特開 平4−14448(JP,A) 特開 平4−135755(JP,A) 特開 昭54−103438(JP,A) 実開 昭57−76035(JP,U) 実開 平4−94440(JP,U) (58)調査した分野(Int.Cl.7,DB名) B32B 1/00 - 35/00 ────────────────────────────────────────────────── ─── Continuation of front page (56) References JP-A-2-128843 (JP, A) JP-A-3-8477 (JP, A) JP-A-4-14448 (JP, A) JP-A-4- 135755 (JP, A) JP-A-54-103438 (JP, A) JP-A-57-76035 (JP, U) JP-A-4-94440 (JP, U) (58) Fields investigated (Int. Cl. 7 , DB name) B32B 1/00-35/00

Claims (2)

(57)【特許請求の範囲】(57) [Claims] 【請求項1】 透明な熱可塑性樹脂フィルムの一方の面
に、第1の光輝性印刷層、複数の絵柄印刷層、第2の光
輝性印刷層、隠蔽性印刷層を順次積層し、少なくとも第
1の光輝性印刷層が、一部の絵柄印刷層のパターンに同
調するように設けられたことと、更に、前記隠蔽性印刷
層の面に微細凹凸模様をエンボス方式により設け、少な
くとも隠蔽性印刷層の透明熱可塑性樹脂フィルム側の界
面にまで達するように微細凹凸模様が設けられたことを
特徴とする化粧シート。
1. A first glitter print layer, a plurality of picture print layers, a second glitter print layer, and a concealment print layer are sequentially laminated on one surface of a transparent thermoplastic resin film, and at least a first glitter print layer is formed .
1 glitter print layer is identical to the pattern of some picture print layers.
And the concealable printing
The fine asperity pattern on the surface of the layer formed by the embossing method, the decorative sheet, wherein the fine asperity pattern so as to reach the interface of the transparent thermoplastic resin film side of at least concealing printing layer is provided.
【請求項2】 微細凹凸模様が平行曲線群、もしくは平
行曲線群と平行直線群を組み合わせたパターンから成
り、且つ凹部と凸部の高さの差が3〜50μmの範囲
で、その間隔が1〜1000μmの範囲にあることを特
徴とする請求項1記載の化粧シート。
2. The fine uneven pattern is composed of a parallel curve group or a pattern combining a parallel curve group and a parallel straight line group, and the difference between the height of the concave portion and the convex portion is 3 to 50 μm and the interval is 1 decorative sheet of claim 1 Symbol mounting, characterized in that the range of ~1000Myuemu.
JP12204893A 1993-04-27 1993-04-27 Decorative sheet for building materials Expired - Lifetime JP3211175B2 (en)