JP3193540B2 - Thermoplastic fluororesin / rubber adhesive composite and method for producing the same - Google Patents
Thermoplastic fluororesin / rubber adhesive composite and method for producing the sameInfo
- Publication number
- JP3193540B2 JP3193540B2 JP22351893A JP22351893A JP3193540B2 JP 3193540 B2 JP3193540 B2 JP 3193540B2 JP 22351893 A JP22351893 A JP 22351893A JP 22351893 A JP22351893 A JP 22351893A JP 3193540 B2 JP3193540 B2 JP 3193540B2
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- fluororesin
- thermoplastic fluororesin
- rubber composition
- butadiene copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は熱可塑性弗素樹脂とゴム
との接着複合体及びその製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an adhesive composite of a thermoplastic fluororesin and rubber and a method for producing the same.
【０００２】[0002]
【従来の技術】熱可塑性弗素樹脂（以下、弗素樹脂と略
す）は、耐薬品性，耐候性，耐ガスバリア性，耐油性，
食品安全性等多くの優れた物性を有する柔軟な加工し易
い熱可塑性樹脂であり、耐蝕機器分野，食品・衛生分
野，電気・電線分野等で用途開発が進んでいる。一方、
ゴムは、弗素樹脂に比べると高い弾性を有し、しかも安
価である。2. Description of the Related Art Thermoplastic fluororesins (hereinafter abbreviated as fluororesins) are chemically resistant, weather resistant, gas barrier resistant, oil resistant, and so on.
It is a flexible and easy-to-process thermoplastic resin with many excellent physical properties such as food safety. Applications are being developed in the fields of corrosion-resistant equipment, food and sanitation, and electric and electric wires. on the other hand,
Rubber has higher elasticity than fluororesin and is inexpensive.
【０００３】したがって、弗素樹脂とゴムを接合して接
着複合体にすることができれば、弗素樹脂と各ゴムのそ
れぞれ特長を保有する工業的メリットの大きい材料にす
ることが可能である。たとえば、ゴム製ホースの外表面
に弗素樹脂層を接合すれば、優れた耐候性，耐熱劣化
性、耐ガスバリア性等を付与することが可能になる。ま
たゴム製ベルトの表面に弗素樹脂層を接着すれば、耐油
性や耐薬品性を向上させることが可能になる。[0003] Therefore, if a fluororesin and rubber can be joined to form an adhesive composite, it is possible to obtain a material having great industrial merits which retains the characteristics of the fluororesin and each rubber. For example, if a fluorine resin layer is bonded to the outer surface of a rubber hose, excellent weather resistance, heat deterioration resistance, gas barrier resistance, and the like can be imparted. If a fluorine resin layer is adhered to the surface of the rubber belt, oil resistance and chemical resistance can be improved.
【０００４】しかしながら、弗素樹脂とゴムとは、接着
性に乏しく、強固に接着することができなかった。従
来、弗素樹脂の接着剤としてイソシアナート系接着剤が
知られているが、この接着剤は、静的接着性は良好であ
るものの、動的接着性に劣るため屈曲等の曲げ変形を受
けると容易に剥離し、耐久性のある接着力が得られるも
のではなかった。[0004] However, the fluororesin and rubber have poor adhesiveness and cannot be firmly bonded. Conventionally, an isocyanate-based adhesive is known as an adhesive for a fluororesin, but this adhesive has good static adhesiveness, but is inferior in dynamic adhesiveness, and is subject to bending deformation such as bending. It was not easy to peel off and durable adhesive strength was obtained.
【０００５】[0005]
【課題を解決するための手段】このような目的を達成す
る本発明の弗素樹脂／ゴム接着複合体は、弗素ゴムから
なる幹ポリマーに結晶性の弗素樹脂をグラフト共重合し
た弗素樹脂と、水素添加アクリロニトリル−ブタジエン
共重合体ゴム（以下、水素添加ＮＢＲと略す）にメタク
リル酸と酸化亜鉛との混合物又はメタクリル酸亜鉛及び
有機過酸化物を配合したゴム組成物（以下変性ＮＢＲゴ
ム組成物と称する）とを接着一体化したことを特徴とす
る。SUMMARY OF THE INVENTION The fluororesin / rubber adhesive composite of the present invention which achieves the above object is made of fluororubber.
Graft copolymerization of a crystalline fluororesin on the base polymer
Rubber composition obtained by blending a mixture of methacrylic acid and zinc oxide or zinc methacrylate and an organic peroxide with a fluorinated resin and a hydrogenated acrylonitrile-butadiene copolymer rubber (hereinafter abbreviated as hydrogenated NBR) NBR rubber composition).
【０００６】[0006]
【課題を解決するための手段】このような目的を達成す
る本発明の弗素樹脂／ゴム接着複合体は、弗素樹脂と、
水素添加アクリロニトリル−ブタジエン共重合体ゴム
（以下、水素添加ＮＢＲと略す）にメタクリル酸と酸化
亜鉛との混合物又はメタクリル酸亜鉛及び有機過酸化物
を配合したゴム組成物（以下、変性ＮＢＲゴム組成物と
称する）とを接着一体化したことを特徴とする。The fluororesin / rubber adhesive composite of the present invention that achieves the above object has the following features.
Rubber composition obtained by blending a mixture of methacrylic acid and zinc oxide or zinc methacrylate and an organic peroxide with hydrogenated acrylonitrile-butadiene copolymer rubber (hereinafter, abbreviated as hydrogenated NBR) (hereinafter, modified NBR rubber composition) (Hereinafter referred to as “integrated”).
【０００７】また、本発明の他の弗素樹脂／ゴム接着複
合体は、弗素ゴムからなる幹ポリマーに結晶性の弗素樹
脂をグラフト共重合した弗素樹脂と、ブチルゴム（以
下、ＩＩＲと略す）、アクリロニトリル−ブタジエンゴ
ム共重合体ゴム（以下、ＮＢＲと略す）、アクリルゴム
（以下、ＡＣＭと略す）、クロロスルホン化ポリエチレ
ンゴム（以下、ＣＳＭと略す）、ヒドリンゴム（以下、
ＣＨＣと略す）からなる群から選ばれたゴムを主成分と
するゴム組成物とを、接着層として変性ＮＢＲゴム組成
物を介して接着一体化したことを特徴とするものであ
る。Further, another fluororesin / rubber composite according to the present invention is obtained by adding a crystalline fluorine resin to a backbone polymer comprising fluororubber.
A fluorine resin fat graft copolymer, butyl rubber (hereinafter abbreviated to IIR), acrylonitrile - butadiene rubber copolymer rubber (hereinafter abbreviated as NBR), acrylic rubber (hereinafter, abbreviated as ACM), chlorosulfonated polyethylene rubber (Hereinafter abbreviated as CSM), hydrin rubber (hereinafter, referred to as CSM)
CHC) and a rubber composition mainly composed of rubber selected from the group consisting of CHC) and bonded and integrated as an adhesive layer via a modified NBR rubber composition.
【０００８】本発明の弗素樹脂／ゴム接着複合体の製造
方法は、弗素ゴムからなる幹ポリマーに結晶性の弗素樹
脂をグラフト共重合した弗素樹脂と、ＩＩＲ、ＮＢＲ、
ＡＣＭ、ＣＳＭ、ＣＨＣからなる群から選ばれたゴムを
主成分とする未加硫ゴム組成物との間に、未加硫の変性
ＮＢＲゴム組成物を介在させて、前記未加硫ゴム組成物
を双方ともに加硫すると同時に、接着一体化することを
特徴とするものである。[0008] Production method of fluorine resin / rubber bonded composite of the present invention, crystalline fluorine tree stem polymer consisting of fluorine rubber
A fluororesin graft-copolymerized with a fat , IIR, NBR,
An unvulcanized modified NBR rubber composition interposed between an unvulcanized rubber composition mainly containing a rubber selected from the group consisting of ACM, CSM and CHC, Are both vulcanized and bonded and integrated at the same time.
【０００９】このように変性ＮＢＲゴム組成物は、弗素
樹脂に対し優れた接着性を有するため、弗素樹脂との接
着複合体にすることができると共に、さらにこの変性Ｎ
ＢＲゴム組成物を接着層とすれば、ＩＩＲ，ＮＢＲ，Ａ
ＣＭ，ＣＳＭ，ＣＨＣからなる群から選ばれたゴムを主
成分とするゴム組成物との接着複合体にすることができ
る。As described above, the modified NBR rubber composition has excellent adhesiveness to the fluororesin, so that it can be used as an adhesive composite with the fluororesin, and further, this modified NBR rubber composition
If the BR rubber composition is used as the adhesive layer, IIR, NBR, A
It can be an adhesive composite with a rubber composition containing a rubber selected from the group consisting of CM, CSM and CHC as a main component.
【００１０】本発明において、熱可塑性弗素樹脂とは、
柔軟性セグメントの弗素ゴムからなる幹ポリマーに結晶
性の弗素樹脂からなる枝ポリマーをグラフト共重合した
樹脂をいう。好ましくは、弗素ゴムにポリビニリデンフ
ロライドをグラフト共重合したポリマーが挙げられる。
具体的には、セントラル硝子社から製造販売されている
“セフラルソフトＧ１５０”（商品名）を例示すること
ができる。In the present invention, the thermoplastic fluorine resin is
A resin obtained by graft copolymerizing a branch polymer made of a crystalline fluororesin with a backbone polymer made of fluororubber having a flexible segment. Preferably, a polymer obtained by graft copolymerizing polyvinylidene fluoride on a fluororubber is used.
Specifically, “Sefralsoft G150” (trade name) manufactured and sold by Central Glass Company can be exemplified.
【００１１】また、弗素樹脂と複合させるゴム組成物と
しては、ＩＩＲ，ＮＢＲ，ＡＣＭ，ＣＳＭ，ＣＨＣから
なる群から選ばれたゴムを主成分とするゴム組成物があ
る。これらゴム組成物は、いずれも特に限定されるもの
ではなく公知のものを使用することができる。本発明に
おいて、弗素樹脂の複合相手のゴムとして又は接着層と
して使用される変性ＮＢＲゴム組成物には、エチレン性
不飽和ニトリル単位を１０〜６０重量部含有し、共役ジ
エン単位を３０重量部以下を含有する水素添加ＮＢＲ１
００重量部に対し、メタクリル酸亜鉛を２０〜２００重
量部配合し、さらに有機過酸化物を０．５〜２０重量部
配合したものが挙げられる。具体的には日本ゼオン社か
ら製造販売されているＺＳＣ２２９５（商品名）があ
る。メタクリル酸亜鉛は、その原料のメタクリル酸と酸
化亜鉛を、メタクリル酸／酸化亜鉛のモル比が１／０．
５〜１／３の範囲になるように配合することもできる。
この場合、上記水素添加ＮＢＲ１００重量部に対してメ
タクリル酸を２０〜６０重量部、酸化亜鉛を１０〜６０
重量部の範囲で配合することが望ましい。As a rubber composition to be combined with a fluorine resin, there is a rubber composition containing a rubber selected from the group consisting of IIR, NBR, ACM, CSM and CHC as a main component. These rubber compositions are not particularly limited, and known rubber compositions can be used. In the present invention, the modified NBR rubber composition used as the rubber of the fluororesin composite partner or as an adhesive layer contains 10 to 60 parts by weight of an ethylenically unsaturated nitrile unit and 30 parts by weight or less of a conjugated diene unit. NBR1 containing hydrogen
For example, a mixture of 20 to 200 parts by weight of zinc methacrylate and 0.5 to 20 parts by weight of an organic peroxide, based on 00 parts by weight. Specifically, there is ZSC2295 (trade name) manufactured and sold by Zeon Corporation. Zinc methacrylate is obtained by mixing raw materials of methacrylic acid and zinc oxide at a molar ratio of methacrylic acid / zinc oxide of 1/0.
It can be blended so as to be in the range of 5 to 1/3.
In this case, 20 to 60 parts by weight of methacrylic acid and 10 to 60 parts by weight of zinc oxide are added to 100 parts by weight of the hydrogenated NBR.
It is desirable to mix in the range of parts by weight.
【００１２】本発明の接着複合体において、変性ＮＢＲ
ゴム組成物は、それ自身が弗素樹脂との複合体のゴム層
を構成できるばかりでなく、弗素樹脂に対してＩＩＲ，
ＮＢＲ，ＡＣＭ，ＣＳＭ，ＣＨＣからなる群から選ばれ
たゴムを主成分とするゴム組成物を接着させる接着剤と
しての機能を有する。すなわち、ＩＩＲ，ＮＢＲ，ＡＣ
Ｍ，ＣＳＭ，ＣＨＣを主成分とするゴム組成物は、いず
れも弗素樹脂に直接接着させることはできないが、変性
ＮＢＲゴム組成物を介して接着させることが可能になる
のである。In the adhesive composite of the present invention, the modified NBR
The rubber composition not only can itself constitute a rubber layer of a composite with a fluororesin, but also has a IIR,
It has a function as an adhesive for bonding a rubber composition mainly composed of rubber selected from the group consisting of NBR, ACM, CSM and CHC. That is, IIR, NBR, AC
Although none of the rubber compositions containing M, CSM, and CHC as main components can be directly bonded to a fluororesin, they can be bonded via a modified NBR rubber composition.
【００１３】本発明の接着複合体の製造方法において、
変性ＮＢＲゴム組成物は未加硫状態で接着処理に供す
る。未加硫状態であることにより、これを加熱下に加硫
させると、未加硫の変性ＮＢＲゴム組成物が架橋反応を
起こして弗素樹脂との間、ゴム組成物同士の間で強固に
接着するようになる。この変性ＮＢＲゴム組成物を接着
剤として使用するときは、厚さ１０μｍ〜１．０ｍｍの
フィルム状にして使用することが望ましい。その厚さを
１０μｍ以上にすることにより接着強度を高めることが
できる。しかし、接着強度は１．０ｍｍ以上の厚さで飽
和するようになるので、上限を１．０ｍｍにするのが経
済的である。In the method for producing an adhesive composite of the present invention,
The modified NBR rubber composition is subjected to an adhesive treatment in an unvulcanized state. When it is unvulcanized, when it is vulcanized under heating, the unvulcanized modified NBR rubber composition undergoes a cross-linking reaction and adheres firmly to the fluororesin and between the rubber compositions. I will be. When using this modified NBR rubber composition as an adhesive, it is desirable to use it in the form of a film having a thickness of 10 μm to 1.0 mm. By setting the thickness to 10 μm or more, the adhesive strength can be increased. However, since the adhesive strength becomes saturated at a thickness of 1.0 mm or more, it is economical to set the upper limit to 1.0 mm.
【００１４】他方、ＩＩＲ，ＮＢＲ，ＣＳＭ，ＡＣＭ，
ＣＨＣを主成分とするゴム組成物も接着処理するとき
は、それぞれ未加硫状態で使用する。加硫済みのときは
変性ＮＢＲゴム組成物に対する接着性が低下するからで
ある。接着条件としては、未加硫の変性ＮＢＲゴム組成
物及び上記ＩＩＲ，ＮＢＲ，ＣＳＭ，ＡＣＭ，ＣＨＣを
主成分とするゴム組成物がそれぞれ加硫する条件下、好
ましくは１６０〜１８０℃、１５〜３０分間、プレス下
に加熱するのがよい。On the other hand, IIR, NBR, CSM, ACM,
When the rubber composition containing CHC as a main component is also subjected to the bonding treatment, each is used in an unvulcanized state. This is because when vulcanized, the adhesion to the modified NBR rubber composition decreases. The bonding conditions are such that the unvulcanized modified NBR rubber composition and the rubber composition containing IIR, NBR, CSM, ACM, and CHC as main components are each vulcanized, preferably at 160 to 180 ° C and 15 to 15 ° C. It is good to heat under a press for 30 minutes.
【００１５】[0015]
実施例 市販の弗素樹脂（セントラル硝子社製“セフラルソフト
Ｇ１５０”）からなる樹脂板を切断して１５０ｍｍ×５
０ｍｍ×２. ５ｍｍの樹脂板を製作した。水素添加ＮＢ
Ｒとメタクリル酸亜鉛を主成分として含有するゴム組成
物（日本ゼオン社製ＺＳＣ−２２９５）８５重量％に、
水素添加ＮＢＲ（日本ゼオン社製ＺＥＴＰＯＬ２０２
０）１５重量％を添加混練した後、この混合物１００重
量部に対して４，４−ビス（α，α−ジメチルベンジ
ル）ジフェニルアミン（老化防止剤，Ｎａｕｇａｒｄ−
４４５）１．５重量部、１，３−ビスターシャリーブチ
ルパーオキシ−イソプロピルベンゼン（化薬アクゾ社製
有機過酸化物“パーカドックス１４／４０“）５重量部
を、それぞれ添加配合して未加硫の変性ＮＢＲゴム組成
物を調製し、このゴム組成物から１５０ｍｍ×５０ｍｍ
×０．５ｍｍのフィルムを作製した。EXAMPLE A resin plate made of a commercially available fluororesin (“Cefralsoft G150” manufactured by Central Glass Co., Ltd.) was cut into 150 mm × 5 mm.
A resin plate of 0 mm × 2.5 mm was manufactured. Hydrogenated NB
85% by weight of a rubber composition (ZSC-2295 manufactured by Zeon Corporation) containing R and zinc methacrylate as main components,
Hydrogenated NBR (ZEPOL202 manufactured by Zeon Corporation)
0) After 15% by weight of the mixture was added and kneaded, 4,4-bis (α, α-dimethylbenzyl) diphenylamine (an antioxidant, Naugard-
445) 1.5 parts by weight, and 5 parts by weight of 1,3-Vistaly-butylperoxy-isopropylbenzene (organic peroxide "Percadox 14/40" manufactured by Kayaku Akzo Co., Ltd.) were added and blended, respectively. A sulfur-modified NBR rubber composition was prepared, and a 150 mm × 50 mm
A film of × 0.5 mm was produced.
【００１６】表１に示す配合組成のＡＣＭ，ＮＢＲ，Ｃ
ＨＣ，ＩＩＲ，ＣＳＭをそれぞれ含有する５種類の未加
硫ゴム組成物１〜５を調製し、これらゴム組成物１〜５
を用いて、それぞれ１５０ｍｍ×５０ｍｍ×２. ５ｍｍ
の未加硫ゴムシートに成形した。 表１中の数値は、いずれも重量部である。ACM, NBR, C having the composition shown in Table 1
Five types of unvulcanized rubber compositions 1 to 5 containing HC, IIR and CSM, respectively, were prepared, and these rubber compositions 1 to 5 were prepared.
Using 150mm x 50mm x 2.5mm
Into an unvulcanized rubber sheet. All numerical values in Table 1 are parts by weight.
【００１７】＊１：日本ゼオン社製ＮＩＰＯＬ ＡＲ
７２ＬＳ ＊２：日本ゼオン社製ＧＥＣＨＲＯＮ ３１０２ ＊３：ハイパロン−４０ ＊４：Ｐb3Ｏ4 （レビタルマスター） ＊５：４，４−ビス（α，α−ジメチルベンジル）ジフ
ェニルアミン（老化防止剤４４５） ＊６：ジブチルジチオカルバミン酸ニッケル（老化防止
剤ＮＢＣ） ＊７：Ｎ−フェニル−Ｎ’−イソプロピル−ｐ−フェニ
レンジアミン（老化防止剤３Ｃ） ＊８：脂肪酸ソーダ石鹸（ノンサールＳＮ−１） ＊９：脂肪酸カリ石鹸（ノンサールＴＫ−１） ＊10：エチレンチオウレアのマスター（レビタルマスタ
ー＃２２） ＊11：ベンゾチアジルジスルフィド ＊12：ジペンタメチレンチウラムテトラサルファイド ＊13：Ｎ−ｔ−ブチル−２−ベンゾチアゾールスルフェ
ンアミド ＊14：テトラメチルチウラムモノスルフィド 上記弗素樹脂板に、それぞれ変性ＮＢＲゴム組成物から
なる未加硫ゴムフィルムを積層し、１７０℃，２０分間
加熱して加硫すると同時に接着させた。また、上記弗素
樹脂板と上記５種類のゴム組成物１〜５からなる未加硫
ゴムシートとの間に、それぞれ前記変性ＮＢＲゴム組成
物の未加硫ゴムフィルムを介在させ、上記と同条件下に
加熱して加硫すると同時に接着させた。得られた５種類
の接着複合体の接着性を下記の方法により評価した結
果、いずれも接着性良好（○）であった。* 1: NIPOL AR manufactured by Zeon Corporation
72LS * 2: GECHRON 3102 manufactured by Zeon Corporation * 3: Hypalon-40 * 4: Pb 3 O 4 (levital master) * 5: 4,4-bis (α, α-dimethylbenzyl) diphenylamine (antiaging agent 445) * 6: Nickel dibutyldithiocarbamate (anti-aging agent NBC) * 7: N-phenyl-N'-isopropyl-p-phenylenediamine (anti-aging agent 3C) * 8: Fatty acid soda soap (Non Sear SN-1) * 9 : Fatty acid potassium soap (Non-Salle TK-1) * 10: Ethylenethiourea master (Levital master # 22) * 11: Benzothiazyl disulfide * 12: Dipentamethylenethiuram tetrasulfide * 13: Nt-butyl-2 -Benzothiazole sulfenamide * 14: Tetramethylthiuram monosulfide Fluorine tree An unvulcanized rubber film made of the modified NBR rubber composition was laminated on each of the fat plates, heated at 170 ° C. for 20 minutes, vulcanized, and simultaneously bonded. An unvulcanized rubber film of the modified NBR rubber composition was interposed between the fluororesin plate and an unvulcanized rubber sheet comprising the five types of rubber compositions 1 to 5, respectively, under the same conditions as above. It was heated and vulcanized underneath and bonded at the same time. As a result of evaluating the adhesiveness of the obtained five types of adhesive composites by the following method, all of them were good (O).
【００１８】接着性の評価方法：熱可塑性弗素樹脂接着
複合体の接着性は、接着力の大きさで評価するのは正確
ではない、。そこで、幅約２０ｍｍのサンプルを作製し
て剥離テストを行い、乾麺剥離を起こった場合は、たと
え接着力が高くても不良（×）と評価した。他方、界面
剥離を起こさなかった場合は、複合体の接着界面を中心
にして約０．５ｍｍの厚さのシートを剃刀で切り出し、
その接着界面付近に剃刀で傷を入れて剥離テストを行
い、シートが内部で凝集破壊を起こすほどに強固に接着
している場合を接着性良好 (○) と評価した。 Adhesion evaluation method : It is not accurate to evaluate the adhesion of a thermoplastic fluororesin-adhesive composite based on the magnitude of the adhesive force. Therefore, a sample having a width of about 20 mm was prepared and subjected to a peeling test. When dry noodle peeling occurred, it was evaluated as poor (x) even if the adhesive strength was high. On the other hand, if no interfacial peeling occurred, a sheet having a thickness of about 0.5 mm was cut out with a razor around the adhesive interface of the composite,
A peeling test was performed by making a scratch near the adhesive interface with a razor, and a case where the sheet was firmly adhered to the inside so as to cause cohesive failure was evaluated as good (O).
【００１９】[0019]
【発明の効果】本発明によれば、弗素樹脂に対する複合
相手として変性ＮＢＲゴム組成物を使用することによ
り、弗素樹脂と上記変性ＮＢＲゴム組成物とが強固に接
着した接着複合体を得ることができる。また、上記変性
ＮＢＲゴム組成物を接着層とすることにより、弗素樹脂
とＩＩＲ，ＮＢＲ，ＡＣＭ，ＣＳＭ，ＣＨＣとがそれぞ
れ強固に接着し、かつ優れた動的接着性を有する接着複
合体を得ることができる。According to the present invention, by using a modified NBR rubber composition as a composite partner for a fluororesin, an adhesive composite in which the fluororesin and the modified NBR rubber composition are firmly adhered can be obtained. it can. Further, by using the modified NBR rubber composition as an adhesive layer, a fluororesin and IIR, NBR, ACM, CSM, CHC are firmly adhered to each other, and an adhesive composite having excellent dynamic adhesiveness is obtained. be able to.
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 昭60−52336（ＪＰ，Ａ) 特開 平４−93244（ＪＰ，Ａ) 特開 平５−185513（ＪＰ，Ａ) 特開 平５−186609（ＪＰ，Ａ) 実開 昭60−17331（ＪＰ，Ｕ) (58)調査した分野(Int.Cl.7，ＤＢ名) B32B 1/00 - 35/00 C08J 5/12 ────────────────────────────────────────────────── ─── Continuation of the front page (56) References JP-A-60-52336 (JP, A) JP-A-4-93244 (JP, A) JP-A-5-185513 (JP, A) JP-A-5-185513 186609 (JP, A) Japanese Utility Model Showa 60-17331 (JP, U) (58) Field surveyed (Int. Cl. 7 , DB name) B32B 1/00-35/00 C08J 5/12
Claims (3)
弗素樹脂をグラフト共重合した熱可塑性弗素樹脂と、水
素添加アクリロニトリル−ブタジエン共重合体ゴムにメ
タクリル酸と酸化亜鉛との混合物又はメタクリル酸亜鉛
及び有機過酸化物を配合したゴム組成物とを接着一体化
した熱可塑性弗素樹脂／ゴム接着複合体。The present invention relates to a backbone polymer comprising a fluororubber and a crystalline polymer.
A thermoplastic fluororesin grafted with a fluororesin and a rubber composition obtained by blending a mixture of hydrogenated acrylonitrile-butadiene copolymer rubber with methacrylic acid and zinc oxide or zinc methacrylate and an organic peroxide. Thermoplastic fluororesin / rubber adhesive composite.
弗素樹脂をグラフト共重合した熱可塑性弗素樹脂と、ブ
チルゴム、アクリロニトリル−ブタジエン共重合体ゴ
ム、アクリルゴム、クロロスルホン化ポリエチレンゴム
及びヒドリンゴムからなる群から選ばれたゴムを主成分
とするゴム組成物とを、接着層として水素添加アクリロ
ニトリル−ブタジエン共重合体ゴムにメタクリル酸と酸
化亜鉛との混合物又はメタクリル酸亜鉛及び有機過酸化
物を配合したゴム組成物を介して接着一体化した熱可塑
性弗素樹脂／ゴム接着複合体。(2) A crystalline backbone polymer comprising fluororubber
A thermoplastic fluororesin graft-copolymerized with a fluororesin, and a rubber composition mainly composed of a rubber selected from the group consisting of butyl rubber, acrylonitrile-butadiene copolymer rubber, acrylic rubber, chlorosulfonated polyethylene rubber and hydrin rubber; A thermoplastic fluororesin bonded / integrated as a bonding layer via a rubber composition obtained by mixing a mixture of methacrylic acid and zinc oxide or zinc methacrylate and an organic peroxide with a hydrogenated acrylonitrile-butadiene copolymer rubber as an adhesive layer / Rubber bonded composite.
弗素樹脂をグラフト共重合した熱可塑性弗素樹脂と、ブ
チルゴム、アクリロニトリル−ブタジエン共重合体ゴ
ム、アクリルゴム、クロロスルホン化ポリエチレンゴム
及びヒドリンゴムからなる群から選ばれたゴムを主成分
とする未加硫ゴム組成物との間に、水素添加アクリロニ
トリル−ブタジエン共重合体ゴムにメタクリル酸と酸化
亜鉛との混合物又はメタクリル酸亜鉛及び有機過酸化物
を配合した未加硫ゴム組成物を介在させて、前記未加硫
のゴム組成物を双方ともに加硫すると同時に、接着一体
化する熱可塑性弗素樹脂／ゴム接着複合体の製造方法。3. A crystalline polymer is formed on a backbone polymer comprising fluororubber.
Unvulcanized rubber mainly composed of thermoplastic fluororesin grafted with fluororesin and rubber selected from the group consisting of butyl rubber, acrylonitrile-butadiene copolymer rubber, acrylic rubber, chlorosulfonated polyethylene rubber and hydrin rubber An unvulcanized rubber composition obtained by mixing a mixture of methacrylic acid and zinc oxide or zinc methacrylate and an organic peroxide with a hydrogenated acrylonitrile-butadiene copolymer rubber is interposed between the composition and the composition. A method for producing a thermoplastic fluororesin / rubber adhesive composite in which both of the vulcanized rubber compositions are vulcanized and bonded together.