JP3160405B2 - Roll for transporting high-temperature steel - Google Patents
Roll for transporting high-temperature steelInfo
- Publication number
- JP3160405B2 JP3160405B2 JP01090993A JP1090993A JP3160405B2 JP 3160405 B2 JP3160405 B2 JP 3160405B2 JP 01090993 A JP01090993 A JP 01090993A JP 1090993 A JP1090993 A JP 1090993A JP 3160405 B2 JP3160405 B2 JP 3160405B2
- Authority
- JP
- Japan
- Prior art keywords
- roll
- layer
- heat
- coating layer
- cermet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、高温鋼材搬送用ロール
に関し、特に、高い温度での処理が必要とされるステン
レス鋼板用熱処理炉内に設置されるロールに、耐熱性と
断熱性とを付与するために溶射被覆層を形成してなる搬
送用ロールについての提案である。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a roll for transporting high-temperature steel materials, and more particularly, to a roll installed in a heat treatment furnace for stainless steel sheets requiring high-temperature treatment, which is provided with heat resistance and heat insulation. This is a proposal for a transport roll having a thermal spray coating layer formed thereon for application.
【０００２】[0002]
【従来の技術】高温鋼材、例えば熱処理ラインで処理す
る高温のステンレス鋼板などを搬送するための熱処理炉
用ハースロールとしては、表面に耐熱性材料を被覆した
ロールが用いられている。ところで、このような熱処理
炉用ハースロール（搬送用ロール）, とくに温度が1200
℃を超えるような熱処理炉内の加熱帯後半部や均熱帯に
設置されている搬送用ロールというのは、搬送すべき材
料（ステンレス鋼板) が軟化しているために、ロール表
面のわずかな変化でも、それが原因となって、かかる搬
送材（ステンレス鋼板）に疵を発生させやすいという傾
向がある。それゆえに表面の状態が長期にわたって安定
していることが重要である。2. Description of the Related Art As a hearth roll for a heat treatment furnace for transporting a high-temperature steel material, for example, a high-temperature stainless steel plate to be processed in a heat treatment line, a roll having a surface coated with a heat-resistant material is used. By the way, such heat treatment furnace hearth rolls (transport rolls), especially when the temperature is 1200
The transport rolls installed in the latter half of the heating zone in the heat treatment furnace or in the solitary zone where the temperature exceeds ℃ are slightly changed due to the softness of the material (stainless steel plate) to be transported. However, due to this, there is a tendency that a flaw is easily generated in such a conveying material (stainless steel plate). Therefore, it is important that the surface condition is stable for a long time.
【０００３】一方、ロールそれ自体に着目すると、この
搬送用ロールの本体部分は、高温の雰囲気下で使用され
るものであるから、その中心部分が水冷されているのが
普通である。したがって、通板面となるこのロール表面
は、断熱材料などで被覆されることが必要であり、この
断熱材料によって搬送材の温度低下を防ぐようにしてい
る。しかも、このような目的の下に使用される断熱被覆
材料は、ロールに上述した疵をつけない物質であること
が必要である。例えば、アスベストとかシリカ・アルミ
ナ繊維などが代表的な被覆材料であった。このような搬
送用被覆ロールの例としては、従来、特開平１−290712
号公報や特開平１−301818号公報に開示されているよう
なものがある。これらの従来ロールは、いわゆるロール
軸芯のまわりに、円板状の耐熱性断熱シートを軸方向に
積層して断熱層とし、この断熱層の構造を工夫すること
により、耐久性や耐ビルドアップ特性を改善することと
したものである。しかしながら、上記の従来搬送用ロー
ルは、以下に説明するような各種の問題点を抱えてい
た。On the other hand, when attention is paid to the roll itself, since the main body of the transport roll is used in a high-temperature atmosphere, its central portion is usually water-cooled. Therefore, it is necessary that the surface of the roll, which becomes the plate passing surface, be covered with a heat insulating material or the like, and the heat insulating material prevents the temperature of the conveying material from lowering. Moreover, the heat insulating coating material used for such a purpose needs to be a substance which does not cause the above-mentioned flaw on the roll. For example, asbestos or silica / alumina fiber was a typical coating material. As an example of such a transporting coating roll, a conventional coating roll is disclosed in JP-A-1-290712.
And Japanese Patent Application Laid-Open No. 1-31818. These conventional rolls are made by laminating a disc-shaped heat-resistant heat-insulating sheet around the roll axis in the axial direction to form a heat-insulating layer. By devising the structure of this heat-insulating layer, durability and build-up resistance are improved. This is to improve the characteristics. However, the above-mentioned conventional transport roll has various problems as described below.
【０００４】一般に、従来の搬送用ロールというのは、
水冷ロールのロール軸芯まわりに装着する耐熱性断熱部
材の被覆層が、ドーナツ状のアスベストや耐熱性無機質
繊維をロールの軸方向に嵌め入れて積層し、かつ圧縮し
て所定の外径寸法に仕上げたもので構成されている。と
ころが、このようなドーナツ状シート状物をロールに嵌
挿する作業は、多大の労力と時間とが必要であった。し
かも、この従来搬送ロールを、実際の熱処理炉で使用し
た結果によれば、ロール表面を形造る被覆層がシート状
物の積層構造であるために、被覆構成物であるアスベス
トや無機質繊維の劣化や硬化が激しく、短期間のうちに
ロールから脱落する現象が見られ、そのため短時間で使
用不能になって操業を停止しなければならないという問
題点があった。さらに、この従来搬送ロールについて
は、ステンレス鋼板の表面に発生するスケールがロール
の表面に付着し、そのロール表面への付着スケールによ
って、後続の搬送材料（ステンレス鋼板）の表面が傷つ
けられるという、いわゆるビルドアップの弊害が、依然
として解消されていないという課題も残していた。[0004] In general, a conventional transport roll is
The coating layer of the heat-resistant heat-insulating member attached around the roll axis of the water-cooled roll is made by inserting doughnut-shaped asbestos or heat-resistant inorganic fiber in the axial direction of the roll, laminating, and compressing to a specified outer diameter. It is composed of finished products. However, the work of inserting such a donut-shaped sheet into a roll requires a great deal of labor and time. In addition, according to the results of using this conventional transport roll in an actual heat treatment furnace, the coating layer forming the roll surface has a laminated structure of sheet-like materials, so that the asbestos and inorganic fibers that are the coating components deteriorate. There was a problem that the hardener was hardened and the rolls fell off in a short period of time, so that they could not be used in a short time and the operation had to be stopped. Furthermore, in this conventional transport roll, the scale generated on the surface of the stainless steel plate adheres to the surface of the roll, and the scale attached to the roll surface damages the surface of the subsequent transport material (stainless steel plate). The problem that the evil effects of the build-up have not yet been solved remains.
【０００５】[0005]
【発明が解決しようとする課題】ところで、発明者ら
は、かつて特願平２−211691号（特開平４−99813 号公
報) において、ロール被覆層として、従来の無機質繊維
を主材とするシート材を積層していく構造のものに代
え、被削性のよいサーメットを溶射被覆する技術を提案
した。By the way, the inventors have previously disclosed in Japanese Patent Application No. 2-116991 (Japanese Patent Application Laid-Open No. 4-99813) a conventional sheet mainly composed of inorganic fibers as a roll coating layer. We proposed a technique to spray-coat a cermet with good machinability instead of a structure in which materials are laminated.
【０００６】かかるサーメット溶射被覆層を有する高温
鋼材搬送用ロールは、ロール表面性状が長期間に亘って
常に安定していてビルドアップが発生しにくいという優
れた特性を有しているが、時として溶射被覆層の剥離が
起こるという、なお解決を必要とする課題を残してい
た。A roll for transporting a high-temperature steel material having such a cermet sprayed coating layer has an excellent property that the roll surface properties are always stable for a long period of time and build-up hardly occurs. The problem that the thermal spray coating layer is peeled off still needs to be solved.
【０００７】本発明の目的は、発明者らが先行提案した
上記従来技術が抱えていた解決課題を有利に克服するこ
とにある。即ち、搬送用水冷ロール外周に形成する溶射
被覆層の密着性を向上させることができると共に、一層
良好な断熱性を有する高温鋼材搬送用ロールを開発し提
案することにある。An object of the present invention is to advantageously overcome the problems of the prior art proposed by the inventors in advance. That is, an object of the present invention is to develop and propose a high-temperature steel material transfer roll that can improve the adhesion of a thermal spray coating layer formed on the outer periphery of a transfer water-cooled roll and has better heat insulating properties.
【０００８】[0008]
【課題を解決するための手段】上述した従来技術が抱え
ている課題の解決について鋭意研究した結果、下記の如
き構成のロールにすることが有効であることが判った。
すなわち、本発明は、外周に耐熱性断熱材料の溶射被覆
層を形成してなる水冷ロールにおいて、このロール基材
の外周に粗化面を設け、このロール粗化面上には、基材
側に形成された耐熱合金溶射層とその上層に形成された
ジルコニア溶射層とからなる二層下地溶射被覆層を設
け、そしてこの下地溶射被覆層上には被削性を有するサ
ーメット溶射被覆層を設けてなる高温鋼材搬送用ロール
である。As a result of diligent research into solving the above-mentioned problems of the prior art, it has been found that a roll having the following structure is effective.
That is, the present invention provides a water-cooled roll having a heat-resistant heat-insulating material spray-coated layer formed on the outer periphery, wherein a roughened surface is provided on the outer periphery of the roll base material, A two-layer base thermal spray coating layer consisting of a heat-resistant alloy spray layer formed on the upper layer and a zirconia spray layer formed thereon is provided, and a cermet spray coating layer having machinability is provided on the base thermal spray coating layer. It is a roll for conveying high-temperature steel.
【０００９】[0009]
【作用】本発明にかかるステンレス鋼等高温鋼材搬送用
（ハース）ロールというのは、中空水冷構造とした耐熱
鋼製ロールの外周に、耐熱性と断熱性とに優れると共
に、被削性（被覆した前記溶射皮膜が接触する相手材
（搬送材）によって容易に摩滅していく性質を具えてい
ること）を具えるサーメット材料を溶射被覆して被削性
に優れた溶射被覆層を設けた構造を有するものである。The (hearth) roll for transporting high-temperature steel such as stainless steel according to the present invention has excellent heat resistance and heat insulation properties, and has excellent machinability (coating) on the outer periphery of a heat-resistant steel roll having a hollow water-cooled structure. A cermet material having a property that the sprayed coating is easily worn away by a mating material (transporting material) with which the sprayed coating comes into contact with the cermet material and provided with a sprayed coating layer having excellent machinability. It has.
【００１０】そして、本発明の構成の特徴は、中空水冷
構造の耐熱鋼製ロール基材の表面をブラスト処理して粗
化面とし、このロール粗化面に熱の衝撃に強く熱膨張,
収縮に追随できる耐熱合金（下層）と断熱性に優れたセ
ラミックスとして高温で熱的に安定したジルコニア（上
層）とを順次溶射被覆してなる二重構造の下地（アンダ
ーコート）層を形成し、このアンダーコート層上に被削
性に優れたサーメット材料を溶射被覆した多層被覆層と
した点の構造にある。The structure of the present invention is characterized in that the surface of a heat-resistant steel roll base material having a hollow water-cooled structure is blasted to a roughened surface.
Forming a double-layered undercoat (undercoat) layer, which is formed by successively thermal spray coating a heat-resistant alloy (lower layer) that can follow shrinkage and zirconia (upper layer) that is thermally stable at high temperatures as ceramics with excellent heat insulating properties. The undercoat layer has a structure in which a cermet material having excellent machinability is spray-coated to form a multilayer coating layer.
【００１１】さて、アンダーコートの下層を形成する上
記耐熱合金の例としては、“ＭCrAlＹ”と呼ばれるNi−
Cr−Al−Ｙ合金, Co−Cr−Al−Ｙ合金, Co−Ni−Cr−Al
−Ｙ合金などがよく適合し、一方、アンダーコートの上
層を形成する上記ジルコニアの例としては、ZrO2−Y2O3
やZrO2−CeＯなどの部分安定化ジルコニアがよく適合す
る。An example of the above-mentioned heat-resistant alloy for forming the lower layer of the undercoat is a Ni-alloy called “MCrAlY”.
Cr-Al-Y alloy, Co-Cr-Al-Y alloy, Co-Ni-Cr-Al
-Y alloy or the like is well suited, while ZrO 2 -Y 2 O 3 is an example of the zirconia forming the upper layer of the undercoat.
And partially stabilized zirconia such as ZrO 2 -CeO are well suited.
【００１２】また、表面被覆層（トップコート層）を形
成する溶射被覆層としては、耐熱性と断熱特性に優れ、
かつ搬送ステンレスのかじりを起こさないように被削性
に優れたサーメット溶射被覆層が好適であり、そのよう
なサーメット溶射被覆層としては、ＢＮを４〜10wt％含
み残部がNi, Co, Cr, Fe, Alを含む各種の耐熱合金より
なる溶射材料、あるいは焼成ベントナイトを15〜30wt％
含み残部が同じく耐熱合金からなる溶射材料が好適であ
り、そしてそのサーメット溶射被覆層の厚さは0.5〜５m
mの層厚にすることが好適であると言える。なお、サー
メット中に混合する耐熱合金としては、上記アンダーコ
ート層の耐熱合金と共金のものを用いることも有効な手
段の１つである。The thermal spray coating layer for forming the surface coating layer (top coat layer) has excellent heat resistance and heat insulating properties.
Further, a cermet sprayed coating layer excellent in machinability so as not to cause galling of the transported stainless steel is preferable. As such a cermet sprayed coating layer, 4 to 10 wt% of BN is contained, and the balance is Ni, Co, Cr, Sprayed material composed of various heat-resistant alloys containing Fe and Al, or calcined bentonite 15 to 30 wt%
The thermal spraying material, the remainder of which is also made of a heat-resistant alloy, is suitable, and the thickness of the cermet sprayed coating layer is 0.5 to 5 m.
It can be said that a layer thickness of m is preferable. It is to be noted that, as the heat-resistant alloy to be mixed into the cermet, the use of a heat-resistant alloy of the above-mentioned undercoat layer and a common metal is one of the effective means.
【００１３】このような構成を有する本発明の高温鋼材
搬送用ロールは、 ロール基材表面がブラストによる粗化処理がされてい
るから、アンダーコート層の特に下層の耐熱合金層との
密着強度が高い。 アンダーコート層の下層を構成する耐熱合金の存在
は、その上層を構成する断熱皮膜（部分安定化ジルコニ
ア）との結合力に優れており、それ故にこのアンダーコ
ート層が上層であっても密着強度の向上は却って向上す
る。 アンダーコート層を二重構造とすることにより、ロー
ル基材と被削性を具える溶射被覆層との両方に対する密
着性を向上させると同時に、断熱性をより一層向上させ
るという効果を発揮する。In the roll for transporting a high-temperature steel material of the present invention having the above structure, since the surface of the roll base material has been subjected to a roughening treatment by blasting, the adhesion strength of the undercoat layer, particularly to the lower heat-resistant alloy layer, is low. high. The presence of the heat-resistant alloy constituting the lower layer of the undercoat layer has excellent bonding strength with the heat-insulating coating (partially stabilized zirconia) constituting the upper layer, and therefore, the adhesion strength of the undercoat layer even when the undercoat layer is the upper layer The improvement is rather improved. When the undercoat layer has a double structure, the adhesiveness to both the roll base material and the sprayed coating layer having machinability is improved, and at the same time, the heat insulating property is further improved.
【００１４】上記ロール基材表面の粗化は、ブラスト処
理により粗さRa：10〜30μｍ程度にする。この粗さRa：
10μｍ未満ではアンカー効果が劣り、密着性が低下して
剥離する危険があり、一方Ra：30μｍを超えると皮膜に
切り欠き作用を起こしクラックの発生がある。The surface of the roll substrate is roughened by blasting to a roughness Ra of about 10 to 30 μm. This roughness Ra:
If it is less than 10 μm, the anchor effect is inferior, and there is a danger of peeling due to a decrease in adhesion. On the other hand, if it exceeds Ra: 30 μm, a notch action occurs in the film and cracks occur.
【００１５】上記アンダーコート層は、上層, 下層とも
いずれもプラズマ方式による溶射によって被覆形成する
が、それぞれの溶射被覆層の厚みは、下層の耐熱合金層
の場合、0.05〜0.5 mmとし、上層のジルコニア層の場合
0.2〜2.5 mmとする。これらの厚みはそれぞれの下限を
下回ると緩衝効果, 断熱効果が劣り、また、それぞれの
上限値を上回ると皮膜内応力が強くなり剥離するので、
上記のように限定した。Both the upper layer and the lower layer are formed by thermal spraying using a plasma method. The thickness of each thermal spray coating layer is 0.05 to 0.5 mm for the lower heat-resistant alloy layer. For zirconia layer
0.2 to 2.5 mm. If the thickness is below the lower limit, the buffering effect and the heat insulating effect are inferior, and if the thickness exceeds the upper limit, the stress in the film increases and the film peels off.
Limited as described above.
【００１６】上記サーメット溶射被覆層は、ガス燃焼方
式溶射被覆によって形成する。その被覆の厚さは 0.5〜
５mmとする。0.5 mm未満では摩滅期間が短く、寿命延長
が図れないし、５mmを超えると皮膜内応力が強くなり剥
離することから、上記範囲内の厚みに限定した。The cermet spray coating layer is formed by a gas combustion type spray coating. The coating thickness is 0.5 ~
5 mm. If the thickness is less than 0.5 mm, the abrasion period is short and the life cannot be extended. If the thickness exceeds 5 mm, the stress in the film increases and the film peels off. Therefore, the thickness is limited to the above range.
【００１７】なお、上記サーメット溶射被覆層の表面に
ついては、さらに表面粗度Ra：10μｍ以内となるように
研磨することが望ましい。The surface of the sprayed cermet coating layer is desirably polished so that the surface roughness Ra is within 10 μm.
【００１８】[0018]
【実施例】生産能力24,000トン／月のステンレス鋼板用
熱処理炉に、本発明にかかる図１に示すような搬送用ロ
ールを適用設置し、主として寿命についての試験を行っ
た。その結果を表１にまとめて示す。EXAMPLE A transfer roll as shown in FIG. 1 according to the present invention was applied to a heat treatment furnace for stainless steel plates having a production capacity of 24,000 tons / month, and a life test was mainly performed. The results are summarized in Table 1.
【００１９】(1) 比較に供した従来アスベスト被覆ロー
ル（No.1) は、生産量が6000トンになると、表面を覆う
アスベストが脱落した。また、シリカ・アルミナ繊維の
被覆ロール(No.2)も、6000トンを処理した段階でビルド
アップが発生し、ステンレス鋼板の疵が心配されたの
で、取り外した。(1) In the conventional asbestos-coated roll (No. 1) used for comparison, asbestos covering the surface dropped off when the production amount reached 6000 tons. Also, the silica-alumina fiber coating roll (No. 2) was removed because build-up occurred at the stage of processing 6000 tons and there was concern about flaws on the stainless steel plate.
【００２０】(2) 一方、本発明例については、アンダー
コートの下層としてNiCoCrAlY 合金を、そしてその上層
としてZrO2−Y2Ｏ部分安定化ジルコニアを溶射被覆し、
またトップコート層としてＢＮと耐熱合金（Ni Cr Fe
Al合金）とからなるサーメットを溶射被覆したロール
(No.３）の例では、27,000トン処理した段階（約１カ月
使用した段階）で摩耗してしまったので取り外したが、
それでも従来ロールよりも著しく寿命延長が達成でき
た。また、アンダーコート中の下層としてNiCrAlY 合金
を、そしてその上層としてZrO2−CeＯ部分安定化ジルコ
ニアを溶射被覆し、またトップコート層としてベントナ
イトと耐熱合金（Ni Cr Al合金）とからなるサーメッ
トを溶射被覆したロール(No.４）は、36,000トン処理し
た段階（約１.3カ月使用した段階）で摩耗してしまった
ので取り外したが、それでも従来ロールよりも大幅な寿
命延長を達成した。(2) On the other hand, in the case of the present invention, a NiCoCrAlY alloy is spray-coated as a lower layer of the undercoat, and ZrO 2 —Y 2 O partially stabilized zirconia is spray-coated as an upper layer thereof,
BN and a heat-resistant alloy (NiCrFe
Roll coated with a cermet consisting of Al alloy)
In the example of (No. 3), it was worn out at the stage where it was processed for 27,000 tons (when it was used for about one month), so it was removed,
Nevertheless, the service life was significantly extended compared to the conventional roll. In addition, a NiCrAlY alloy is applied as a lower layer in the undercoat, and ZrO 2 -CeO partially stabilized zirconia is applied as a thermal spray coating as an upper layer, and a cermet made of bentonite and a heat-resistant alloy (NiCrAl alloy) is applied as a top coat layer. The coated roll (No. 4) was worn out at the stage where it was treated at 36,000 tons (approximately 1.3 months of use) and was removed, but still achieved a much longer life than the conventional roll.
【００２１】(3) これに対し、アンダーコート層として
単にNiCrAlY 耐熱合金のみを溶射被覆し、そしてすぐそ
の上にトップコートとして上記と同じベントナイト系サ
ーメットを被覆したロール(No.5)は、18,000トン処理し
た段階でロール曲がりによる偏摩耗が大きくなったので
取り外したが、それでも従来ロールよりも寿命が延びた
が、供試材No.3, 4 ほどではなかった。(3) On the other hand, a roll (No. 5) in which only the NiCrAlY heat-resistant alloy was spray-coated as an undercoat layer and the same bentonite cermet as the top coat was immediately coated thereon was 18,000. At the stage of ton treatment, the uneven wear due to the bending of the roll became large, so it was removed. However, the service life was longer than that of the conventional roll, but it was not as good as the test materials No. 3 and 4.
【００２２】[0022]
【表１】 [Table 1]
【００２３】[0023]
【発明の効果】以上説明したように、本発明にかかる高
温鋼材搬送用ロールは、その表面に形成した溶射皮膜の
特性から断熱性に優れるために過冷却現象がなく、それ
故にビルドアップが自動的に消滅するので搬送されるス
テンレス鋼板に疵をつけることもなく、しかも初期状態
のまま長時間安定した表面状態を維持して使用すること
ができる。しかも、アンダーコート層を下層の耐熱合金
と上層のジルコニア層との２層構造とし、かつロール基
材の表面を粗化したことにより、溶射皮膜の密着性が大
きくなり、そのために寿命が著しく向上する。As described above, the roll for transporting high-temperature steel according to the present invention has excellent heat insulating properties due to the characteristics of the thermal spray coating formed on the surface thereof, so that there is no supercooling phenomenon, and therefore, the build-up is automatic. The stainless steel sheet conveyed does not flaw, so that it can be used while maintaining a stable surface state for a long time in the initial state. In addition, the undercoat layer has a two-layer structure consisting of a lower heat-resistant alloy and an upper zirconia layer, and the surface of the roll substrate is roughened, so that the adhesion of the thermal spray coating is increased, thereby significantly improving the service life. I do.
【図１】本発明高温鋼材搬送用ロールの部分切欠き断面
図である。FIG. 1 is a partially cutaway sectional view of a roll for transporting a high-temperature steel material according to the present invention.
１ ロール基材 ２ 耐熱合金溶射被覆層（下層アンダーコート） ３ 部分安定化ジルコニア溶射被覆層（上層アンダーコ
ート） ４ サーメット溶射被覆層 ５ 冷却水DESCRIPTION OF SYMBOLS 1 Roll base material 2 Heat-resistant alloy spray coating layer (lower undercoat) 3 Partially stabilized zirconia spray coating layer (upper undercoat) 4 Cermet spray coating layer 5 Cooling water
フロントページの続き (56)参考文献 特開 昭62−103314（ＪＰ，Ａ) 特許2650774（ＪＰ，Ｂ２) 特許3043917（ＪＰ，Ｂ２) (58)調査した分野(Int.Cl.7，ＤＢ名) C21D 1/00 115 C21D 9/56 101 C23C 4/00 - 6/00 C23C 24/00 - 30/00 Continuation of the front page (56) References JP-A-62-103314 (JP, A) Patent 2650774 (JP, B2) Patent 3043917 (JP, B2) (58) Fields investigated (Int. Cl. 7 , DB name) C21D 1/00 115 C21D 9/56 101 C23C 4/00-6/00 C23C 24/00-30/00
Claims (1)
成してなる水冷ロールにおいて、このロール基材の外周
に粗化面を設け、このロール粗化面上には、基材側に形
成された耐熱合金溶射層とその上層に形成されたジルコ
ニア溶射層とからなる二層下地溶射被覆層を設け、そし
てこの下地溶射被覆層上には被削性を有するサーメット
溶射被覆層を設けてなる高温鋼材搬送用ロール。1. A water-cooled roll having a heat-sprayed heat-insulating material spray-coated layer formed on the outer periphery, a roughened surface is provided on the outer periphery of the roll base material, A two-layer base spray coating layer consisting of the formed heat-resistant alloy spray layer and the zirconia spray layer formed thereon is provided, and a cermet spray coating layer having machinability is provided on the base spray coating layer. Roll for transporting high-temperature steel.