JP3122486U - Gas barrier film and multi-chamber bag - Google Patents
Gas barrier film and multi-chamber bag Download PDFInfo
- Publication number
- JP3122486U JP3122486U JP2006002383U JP2006002383U JP3122486U JP 3122486 U JP3122486 U JP 3122486U JP 2006002383 U JP2006002383 U JP 2006002383U JP 2006002383 U JP2006002383 U JP 2006002383U JP 3122486 U JP3122486 U JP 3122486U
- Authority
- JP
- Japan
- Prior art keywords
- chamber
- barrier film
- gas barrier
- layer
- sealant layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
【課題】薬剤を外部から明確に視認することができ、誤った投与の発生がなく、かつ、対環境性が良好で安価な複室バッグを提供する。
【解決手段】薬剤収容室1の一端側に弱シール部2を介して希釈液室3が連設される一方、薬剤収容室1の他端側に弱シール部2を介して口部4を有する空室5が連設される複室バッグであって、薬剤収容室1、希釈液室3及び空室5は、透明なフィルム材からなり、かつ、薬剤収容室1の外側が、透明なガスバリアフィルム6で覆われており、ガスバリアフィルム6は、樹脂材にCaO及び/又はAlOX 等の粉末を練り込んだシーラント層を備えている。
【選択図】図2[Problem] To provide a multi-chamber bag in which a drug can be clearly visually recognized from the outside, does not cause erroneous administration, has good environmental properties, and is inexpensive.
A diluent chamber 3 is connected to one end side of a medicine storage chamber 1 via a weak seal portion 2, and a mouth portion 4 is connected to the other end side of the medicine storage chamber 1 via a weak seal portion 2. It is a multi-chamber bag in which the vacant chambers 5 are continuously provided, and the drug containing chamber 1, the diluent chamber 3 and the vacant chamber 5 are made of a transparent film material, and the outside of the drug containing chamber 1 is transparent. The gas barrier film 6 is covered with a gas barrier film 6 and includes a sealant layer in which a powder of CaO and / or AlO x is kneaded into a resin material.
[Selection] Figure 2
Description
本考案はガスバリアフィルム及び薬剤収容室を備えた複室バッグに関する。 The present invention relates to a multi-chamber bag provided with a gas barrier film and a medicine storage chamber.
薬剤収容室と希釈液室の間に弱シール部を設け、使用時に薬剤と希釈液とを混合させるようにした複室バッグで、吸湿性や易酸化性を有する薬剤等を乾燥剤や脱酸素剤を使用することなく薬剤収容室に収容できるようにしたものは提案されている(例えば、特許文献1参照)。この例では、図示は省略するが、薬剤収容室の両側は、例えば、アルミ加工フィルムを含む多層フィルムで覆われ前面側のアルミ加工フィルムを剥離可能として、口部のある希釈液室を薬剤収容室の下に配置して吊した状態で希釈した薬剤を投与するように構成されている。
しかし、上述のように、薬剤収容室が、アルミ加工フィルムを含む多層フィルムで覆われていると、外部から薬剤を視認することができないという難点がある。また、薬剤を希釈した際にその混合状態を確認するために前面側のアルミ加工フィルムを剥がす作業も面倒である。そして、希釈液室に口部が設けられていると、薬剤が希釈液に混合されない状態で投与されてしまうようなトラブルの発生も懸念される。さらに、アルミ加工フィルムが含まれているため、高価になるだけでなく、そのまま投棄できないという対環境性の問題もあった。 However, as described above, when the medicine storage chamber is covered with a multilayer film including an aluminum processed film, there is a problem that the medicine cannot be visually recognized from the outside. Moreover, in order to confirm the mixing state when the drug is diluted, the work of removing the aluminum processed film on the front side is also troublesome. If the mouth portion is provided in the diluent chamber, there is a concern that a trouble may occur such that the medicine is administered without being mixed with the diluent. Furthermore, since an aluminum processed film is included, not only is it expensive, but there is also an environmental problem that it cannot be discarded as it is.
本願考案は、このような実情に鑑みてなされ、透明性があり対環境性が良好でガスバリア性が高くバリアフィルム層が少なくて安価なガスバリアフィルム及び薬剤を外部から明確に視認することができ、誤った投与の発生がなく、かつ、対環境性が良好で安価な複室バッグを提供することを目的とする。 The present invention was devised in view of such circumstances, and it is possible to clearly see gas barrier films and chemicals that are transparent, have good environmental properties, have high gas barrier properties, have few barrier film layers, and are inexpensive, An object of the present invention is to provide an inexpensive multi-chamber bag that does not cause erroneous administration and that is good for the environment and inexpensive.
(1)本考案のガスバリアフィルムは、ポリエチレンテレフタレート(PET)、ポリビニルアルコール(PVA)及び/又はエチレン・ビニルアルコール共重合体(EVOH)にシリカ及び/又はアルミナを蒸着してなるバリアフィルム層と、透明な樹脂材に水分吸収剤を練り込んでなるシーラント層と、を備えたことを特徴とする。 (1) The gas barrier film of the present invention comprises a barrier film layer formed by vapor-depositing silica and / or alumina on polyethylene terephthalate (PET), polyvinyl alcohol (PVA) and / or ethylene / vinyl alcohol copolymer (EVOH), And a sealant layer in which a moisture absorbent is kneaded into a transparent resin material.
このようなシーラント層を備えたガスバリアフィルムは水分吸収能が高いため、例えば、これを薬剤収容室に被覆することで、乾燥剤や脱酸素剤を使用することなく、薬剤が水分や酸素の影響を受けないように保護することができる。また、そのシーラント層は透明であるため、外部から薬剤収容室の内部を透視することができ、収容された薬剤の状態や薬剤収容室に希釈液を導入して薬剤に混合したときに不溶性異物の有無等を明確に確認することができるため、誤った投与の発生を抑えることができる。そして、このようなシーラント層を備えたガスバリアフィルムは、特に水蒸気バリア性が顕著に向上するため、バリアフィルム層の層数を少なくすることができ安価に提供することができる。 Since the gas barrier film provided with such a sealant layer has a high moisture absorption capacity, for example, by coating this in a drug storage chamber, the drug can be influenced by moisture and oxygen without using a desiccant or oxygen scavenger. Can be protected from being affected. In addition, since the sealant layer is transparent, the inside of the medicine container can be seen through from the outside. When the diluent is introduced into the medicine container and mixed with the medicine, it is insoluble. Since it is possible to clearly confirm the presence or absence, etc., the occurrence of erroneous administration can be suppressed. And since the gas barrier film provided with such a sealant layer improves water vapor | steam barrier property notably, the number of layers of a barrier film layer can be decreased and it can provide at low cost.
(2)前記水分吸収剤は、無機物では、酸化カルシウム、酸化アルミニウム(AlOX )、ゼオライト、シリカゲル、焼明礬、硫酸マグネシウム、塩化カルシウム、硫酸カリウム、五酸化リン、炭酸ナトリウム、炭酸カリウム、有機物では、ポリ(メタ)アクリル酸塩、カルボキシメチルセルローズ、ポリエチレングリコール、及び、これらの誘導体、の中から選択された1種の材料、上記無機物同士、有機物同士の組み合わせ、あるいは、上記無機物と有機物相互の組み合わせ、の何れかであってもよい。このような水分吸収剤を樹脂材に練り込むことによって安定したシーラント層を形成することができる。 (2) The moisture absorbent is inorganic, calcium oxide, aluminum oxide (AlO x ), zeolite, silica gel, shochu liquor, magnesium sulfate, calcium chloride, potassium sulfate, phosphorus pentoxide, sodium carbonate, potassium carbonate, organic , Poly (meth) acrylate, carboxymethyl cellulose, polyethylene glycol, and derivatives thereof, one material selected from among the above-mentioned inorganic materials, a combination of organic materials, or a combination of the above-mentioned inorganic materials and organic materials. Any of the combinations may be used. A stable sealant layer can be formed by kneading such a moisture absorbent into the resin material.
(3)前記樹脂材は、直鎖状低密度ポリエチレン(LLDPE)、低密度ポリエチレン(LDPE)、ポリプロピレン(PP)、エチレン・酢酸ビニル共重合体(EVA)、酸コポリマー、酸エステルコポリマー、及び、アイオノマー、の中から選択された1種の材料、又は、上記材料同士の組み合わせであってもよい。このような樹脂材に酸化カルシウム(CaO)及び/又は酸化アルミニウム(AlOX )等の水分吸収剤の粉末を練り込んで形成したシーラントフィルムは、良好な接着性(ヒートシール、接着等)が得られるため、他のフィルム材に容易に積層することができる。 (3) The resin material is linear low density polyethylene (LLDPE), low density polyethylene (LDPE), polypropylene (PP), ethylene / vinyl acetate copolymer (EVA), acid copolymer, acid ester copolymer, and One kind of material selected from ionomers, or a combination of the above materials may be used. A sealant film formed by kneading a powder of a moisture absorbent such as calcium oxide (CaO) and / or aluminum oxide (AlO x ) into such a resin material has good adhesion (heat seal, adhesion, etc.). Therefore, it can be easily laminated on other film materials.
(4)前記シーラント層は、前記水分吸収剤を練り込んだ透明な樹脂材の片側又は両側に前記水分吸収剤を練り込んでいない透明な樹脂材が配設されて2層又は3層構成に形成されてもよい。このようにすれば、シーラント層を保護することができ、かつ、他のフィルム材への積層が容易となる。なお、シーラント層を2層にした場合、内容物に接する側を(水分吸収剤を練り込まない)透明樹脂とするのが好ましい。 (4) The sealant layer has a two-layer or three-layer structure in which a transparent resin material not kneaded with the moisture absorbent is disposed on one side or both sides of the transparent resin material kneaded with the moisture absorbent. It may be formed. If it does in this way, a sealant layer can be protected and lamination to other film materials will become easy. In addition, when a sealant layer is made into two layers, it is preferable to make the side which touches the contents into a transparent resin (a water absorbent is not kneaded).
(5)本考案の複室バッグは、薬剤収容室の一端側に弱シール部を介して希釈液室が連設される一方、前記薬剤収容室の他端側に弱シール部を介して口部を有する空室が連設される複室バッグであって、
前記薬剤収容室、希釈液室及び空室は透明なフィルム材からなり、かつ、前記薬剤収容室を透明なガスバリアフィルムで被覆してなり、該ガスバリアフィルムは、透明な樹脂材に水分吸収剤を練り込んでなるシーラント層を備えたことを特徴とする。
(5) In the multi-chamber bag of the present invention, a diluent chamber is connected to one end side of the drug storage chamber via a weak seal portion, and a mouth is connected to the other end side of the drug storage chamber via a weak seal portion. A multi-chamber bag in which vacancies having a portion are provided,
The drug storage chamber, the diluent chamber and the vacant chamber are made of a transparent film material, and the drug storage chamber is covered with a transparent gas barrier film, and the gas barrier film is formed by applying a moisture absorbent to a transparent resin material. It is characterized by having a kneaded sealant layer.
このような構成によれば、水分吸収能が高いシーラント層を備えた透明なガスバリアフィルムで薬剤収容室を被覆することで、乾燥剤や脱酸素剤を使用することなく、薬剤が水分や酸素の影響を受けないように保護することができる。そして、そのガスバリアフィルムが透明であることから、外部から薬剤収容室の内部を透視することができ、収容された薬剤の状態及び弱シール部を破断して希釈液室から薬剤収容室に希釈液を導入して薬剤に混合したときに不溶性異物の有無等を明確に確認することができるため、誤った投与の発生を抑えることができる。 According to such a configuration, the drug containing chamber is covered with a transparent gas barrier film having a sealant layer having a high moisture absorption capacity, so that the drug can be made of water or oxygen without using a desiccant or an oxygen scavenger. It can be protected from being affected. And since the gas barrier film is transparent, the inside of the medicine storage chamber can be seen through from the outside, the state of the stored medicine and the weak seal portion are broken, and the diluent is supplied from the diluent chamber to the medicine storage chamber. Since the presence or absence of insoluble foreign matter and the like can be clearly confirmed when is introduced and mixed with a drug, the occurrence of erroneous administration can be suppressed.
また、薬剤収容室を透明なガスバリアフィルムで被覆するので、製造工程においても異物の混入等を明確に検出することができる。そして、例えば、両面印刷したラベルを希釈液室の片面に貼り付ければ、薬剤収容室と希釈液室を弱シール部で2つ折りにした状態でも、そのラベルを外部から透視して判読できる利点もある。 In addition, since the drug storage chamber is covered with a transparent gas barrier film, contamination of foreign matters can be clearly detected in the manufacturing process. For example, if a double-sided printed label is attached to one side of the diluent chamber, the label can be seen through from the outside even when the drug storage chamber and the diluent chamber are folded in two at the weak seal portion. is there.
さらに、その薬剤収容室と弱シール部を介して口部を有する空室を連設しているため、必ず薬剤が希釈液で希釈された状態で空室を経て投与されるため、誤った投与の発生を防ぐことができる。また、ガスバリアフィルムで覆われた薬剤収容室と弱シール部を介して口部を有する空室を連設しているため、口部及びその周辺においてはガスバリア性であることが要件とされず、その分材料費を低減することができる。さらに、従来のようなアルミ加工フィルムを用いていないため、安価に提供することができ、かつ、対環境性も向上し廃棄処分が容易となる利点もある。 In addition, since the drug storage chamber and a vacant chamber having a mouth portion are connected through a weak seal portion, the drug is always administered through the vacant chamber in a state diluted with a diluent, so that erroneous administration Can be prevented. In addition, since the medicine containing chamber covered with the gas barrier film and the vacant chamber having the mouth portion through the weak seal portion are continuously provided, it is not a requirement that the mouth portion and its surroundings have gas barrier properties, Accordingly, the material cost can be reduced. Furthermore, since the conventional aluminum processed film is not used, there is an advantage that it can be provided at a low cost, is environmentally friendly, and is easily disposed of.
(6)前記水分吸収剤は、無機物では、酸化カルシウム、酸化アルミニウム(AlOX )、ゼオライト、シリカゲル、焼明礬、硫酸マグネシウム、塩化カルシウム、硫酸カリウム、五酸化リン、炭酸ナトリウム、炭酸カリウム、有機物では、ポリ(メタ)アクリル酸塩、カルボキシメチルセルローズ、ポリエチレングリコール、及び、これらの誘導体、の中から選択された1種の材料、上記無機物同士、有機物同士の組み合わせ、あるいは、上記無機物と有機物相互の組み合わせ、の何れかであってもよい。このような水分吸収剤を樹脂材に練り込むことによって安定したシーラント層を形成することができる。 (6) The water absorbent is inorganic, calcium oxide, aluminum oxide (AlO x ), zeolite, silica gel, shochu liquor, magnesium sulfate, calcium chloride, potassium sulfate, phosphorus pentoxide, sodium carbonate, potassium carbonate, organic , Poly (meth) acrylate, carboxymethyl cellulose, polyethylene glycol, and derivatives thereof, one material selected from among the above-mentioned inorganic materials, a combination of organic materials, or a combination of the above-mentioned inorganic materials and organic materials. Any of the combinations may be used. A stable sealant layer can be formed by kneading such a moisture absorbent into the resin material.
(7)前記樹脂材は、直鎖状低密度ポリエチレン(LLDPE)、低密度ポリエチレン(LDPE)、ポリプロピレン(PP)、エチレン・酢酸ビニル共重合体(EVA)、酸コポリマー、酸エステルコポリマー、及び、アイオノマー、の中から選択された1種の材料、又は、上記材料同士の組み合わせであってもよい。このような樹脂材に酸化カルシウム(CaO)及び/又は酸化アルミニウム(AlOX )等の水分吸収剤の粉末を練り込んで形成したシーラントフィルムは、良好な接着性(ヒートシール、接着等)が得られるため、他のフィルム材に容易に積層することができる。 (7) The resin material is linear low density polyethylene (LLDPE), low density polyethylene (LDPE), polypropylene (PP), ethylene / vinyl acetate copolymer (EVA), acid copolymer, acid ester copolymer, and One kind of material selected from ionomers, or a combination of the above materials may be used. A sealant film formed by kneading a powder of a moisture absorbent such as calcium oxide (CaO) and / or aluminum oxide (AlO x ) into such a resin material has good adhesion (heat seal, adhesion, etc.). Therefore, it can be easily laminated on other film materials.
(8)前記ガスバリアフィルムは、前記シーラント層を最内層に有し、該シーラント層の外側に、ポリエチレンテレフタレート(PET)、ポリビニルアルコール(PVA)又はエチレン・ビニルアルコール共重合体(EVOH)にシリカ及び/又はアルミナを蒸着してなるバリアフィルム層を配設してなるものであってもよい。このようにすれば、シーラント層によって水分吸収能が顕著に向上するため、バリアフィルム層の積層数を減じることができ、これによりコストの低減化が可能となる。 (8) The gas barrier film has the sealant layer as an innermost layer, and on the outside of the sealant layer, polyethylene terephthalate (PET), polyvinyl alcohol (PVA), or ethylene / vinyl alcohol copolymer (EVOH) with silica and Alternatively, a barrier film layer formed by vapor deposition of alumina may be provided. In this way, the water absorption capacity is remarkably improved by the sealant layer, so that the number of laminated barrier film layers can be reduced, thereby reducing the cost.
(9)前記シーラント層は、前記水分吸収剤を練り込んだ透明な樹脂材の片側又は両側に前記水分吸収剤を練り込んでいない透明な樹脂材が配設されて2層又は3層構成に形成されてもよい。このようにすれば、シーラント層を保護することができ、かつ、他のフィルム材への積層が容易となる。なお、シーラント層を2層にした場合、内容物に接する側を(水分吸収剤を練り込まない)透明樹脂とするのが好ましい。 (9) The sealant layer has a two-layer or three-layer structure in which a transparent resin material not kneaded with the moisture absorbent is disposed on one or both sides of the transparent resin material kneaded with the moisture absorbent. It may be formed. If it does in this way, a sealant layer can be protected and lamination to other film materials will become easy. In addition, when a sealant layer is made into two layers, it is preferable to make the side which touches the contents into a transparent resin (a water absorbent is not kneaded).
(10)前記シーラント層の外側に配設されるバリアフィルム層の層数は1層乃至10層に設定されてもよい。このような広い範囲内で、薬剤の種類等に応じて適切な層数を選択することにより、所望のガスバリア性を確保することができる。 (10) The number of barrier film layers disposed outside the sealant layer may be set to 1 to 10 layers. Within such a wide range, a desired gas barrier property can be ensured by selecting an appropriate number of layers according to the type of the drug.
(11)本考案の別の複室バッグは、薬剤収容室と、口部を備えた希釈液室が、弱シール部を介して連設されてなる複室バッグであって、
前記薬剤収容室及び希釈液室は透明なフィルム材からなり、かつ、前記薬剤収容室には透明なガスバリアフィルムが被覆され、該ガスバリアフィルムは、透明な樹脂材に水分吸収剤を練り込んでなるシーラント層を備えていることを特徴とする。
(11) Another multi-chamber bag of the present invention is a multi-chamber bag in which a drug storage chamber and a diluent chamber having a mouth portion are connected via a weak seal portion,
The drug storage chamber and the diluent chamber are made of a transparent film material, and the drug storage chamber is covered with a transparent gas barrier film, and the gas barrier film is formed by kneading a moisture absorbent into a transparent resin material. A sealant layer is provided.
このような構成によれば、水分吸収能が高いシーラント層を備えた透明なガスバリアフィルムで薬剤収容室を被覆することで、乾燥剤や脱酸素剤を使用することなく、薬剤が水分や酸素の影響を受けないように保護することができる。そして、そのガスバリアフィルムが透明であることから、外部から薬剤収容室の内部を透視することができ、収容された薬剤の状態及び弱シール部を破断して希釈液室から薬剤収容室に希釈液を導入して薬剤に混合したときに不溶性異物の有無等を明確に確認することができるため、誤った投与の発生を抑えることができる。 According to such a configuration, the drug containing chamber is covered with a transparent gas barrier film having a sealant layer having a high moisture absorption capacity, so that the drug can be made of water or oxygen without using a desiccant or an oxygen scavenger. It can be protected from being affected. And since the gas barrier film is transparent, the inside of the medicine storage chamber can be seen through from the outside, the state of the stored medicine and the weak seal portion are broken, and the diluent is supplied from the diluent chamber to the medicine storage chamber. Since the presence or absence of insoluble foreign matter and the like can be clearly confirmed when is introduced and mixed with a drug, the occurrence of erroneous administration can be suppressed.
また、薬剤収容室を透明なガスバリアフィルムで被覆するので、製造工程においても異物の混入等を明確に検出することができる。そして、例えば、両面印刷したラベルを希釈液室の片面に貼り付ければ、薬剤収容室と希釈液室を弱シール部で2つ折りにした状態でも、そのラベルを外部から透視して判読できる利点もある。さらに、従来のようなアルミ加工フィルムを用いていないため、安価に提供することができ、かつ、対環境性も向上し廃棄処分が容易となる利点もある。 In addition, since the drug storage chamber is covered with a transparent gas barrier film, contamination of foreign matters can be clearly detected in the manufacturing process. For example, if a double-sided printed label is attached to one side of the diluent chamber, the label can be seen through from the outside even when the drug storage chamber and the diluent chamber are folded in two at the weak seal portion. is there. Furthermore, since the conventional aluminum processed film is not used, there is an advantage that it can be provided at a low cost, is environmentally friendly, and is easily disposed of.
(12)前記希釈液室と口部の間には空室が設けられ、該空室と前記希釈液室の間に前記弱シール部が介設されてもよい。このようにすれば、薬剤と希釈液の混合状態を確認した後、空室を経由させて薬剤を投与することができる。 (12) An empty chamber may be provided between the diluent chamber and the mouth, and the weak seal portion may be interposed between the empty chamber and the diluent chamber. If it does in this way, after checking the mixed state of a medicine and a diluent, a medicine can be administered via an empty room.
本考案のガスバリアフィルムは、透明な樹脂材に水分吸収剤を練り込んだシーラント層を備えているので、例えば、これを薬剤収容室に被覆することで、乾燥剤や脱酸素剤を使用することなく、薬剤が水分や酸素の影響を受けないように保護することができる。また、そのシーラント層は透明であるため、外部から薬剤収容室の内部を透視することができ、収容された薬剤の状態や薬剤収容室に希釈液を導入して薬剤に混合したときに不溶性異物の有無等を明確に確認することができるため、誤った投与の発生を抑えることができる。そして、このようなシーラント層を備えたガスバリアフィルムは、特に水蒸気バリア性が顕著に向上するため、バリアフィルム層の層数を少なくすることができ安価に提供することができる。 Since the gas barrier film of the present invention has a sealant layer in which a moisture absorbent is kneaded into a transparent resin material, for example, a desiccant or an oxygen scavenger can be used by covering this in a drug containing chamber. In addition, the drug can be protected from being affected by moisture and oxygen. In addition, since the sealant layer is transparent, the inside of the medicine container can be seen through from the outside. When the diluent is introduced into the medicine container and mixed with the medicine, it is insoluble. Since it is possible to clearly confirm the presence or absence, etc., the occurrence of erroneous administration can be suppressed. And since the gas barrier film provided with such a sealant layer improves remarkably water vapor barrier property especially, the number of layers of a barrier film layer can be decreased and it can provide at low cost.
本考案の複室バッグは、乾燥剤や脱酸素剤を使用することなく、薬剤が水分や酸素の影響を受けないように保護することができる。そして、外部から薬剤収容室の内部を透視することができ、収容された薬剤の状態及び弱シール部を破断して希釈液室から薬剤収容室に希釈液を導入して薬剤に混合したときに不溶性異物の有無等を明確に確認することができるため、誤った投与の発生を抑えることができる。 The multi-chamber bag of the present invention can protect the drug from being affected by moisture and oxygen without using a desiccant or an oxygen scavenger. And when the inside of the medicine storage chamber can be seen through from the outside, when the state of the stored medicine and the weak seal portion are broken and the diluent is introduced into the medicine storage chamber from the diluent chamber and mixed with the medicine Since the presence or absence of insoluble foreign matter can be clearly confirmed, the occurrence of erroneous administration can be suppressed.
また、製造工程においても異物の混入等を明確に検出することができる。そして、例えば、両面印刷したラベルを希釈液室の片面に貼り付ければ、薬剤収容室と希釈液室を弱シール部で2つ折りにした状態でもそのラベルを外部から透視して判読できる利点もある。 In addition, foreign matters can be clearly detected in the manufacturing process. For example, if a label printed on both sides is affixed to one side of the diluent chamber, there is an advantage that the label can be seen through from the outside even when the medicine storage chamber and the diluent chamber are folded in two at the weak seal portion. .
さらに、必ず薬剤が希釈液で希釈された状態で空室を経て投与されるため、誤った投与の発生を防ぐことができる。また、口部及びその周辺においてはガスバリア性であることが要件とされず、その分材料費を低減することができる。さらに、従来のようなアルミ加工フィルムを用いていないため、安価に提供することができ、かつ、対環境性も向上し廃棄処分が容易となる利点もある。 Furthermore, since the drug is always administered through the empty chamber in a state diluted with a diluent, it is possible to prevent the occurrence of erroneous administration. Further, the gas barrier property is not a requirement at the mouth and its periphery, and the material cost can be reduced accordingly. Furthermore, since the conventional aluminum processed film is not used, there is an advantage that it can be provided at a low cost, is environmentally friendly, and is easily disposed of.
本考案の別の複室バッグは、乾燥剤や脱酸素剤を使用することなく、薬剤が水分や酸素の影響を受けないように保護することができる。そして、外部から薬剤収容室の内部を透視することができ、収容された薬剤の状態及び弱シール部を破断して希釈液室から薬剤収容室に希釈液を導入して薬剤に混合したときに不溶性異物の有無等を明確に確認することができるため、誤った投与の発生を抑えることができる。 Another multi-chamber bag of the present invention can protect the drug from being affected by moisture and oxygen without using a desiccant or oxygen scavenger. And when the inside of the medicine storage chamber can be seen through from the outside, when the state of the stored medicine and the weak seal portion are broken and the diluent is introduced into the medicine storage chamber from the diluent chamber and mixed with the medicine Since the presence or absence of insoluble foreign matter can be clearly confirmed, the occurrence of erroneous administration can be suppressed.
また、製造工程においても異物の混入等を明確に検出することができる。そして、例えば、両面印刷したラベルを希釈液室の片面に貼り付ければ、薬剤収容室と希釈液室を弱シール部で2つ折りにした状態でも、そのラベルを外部から透視して判読できる利点もある。さらに、従来のようなアルミ加工フィルムを用いていないため、安価に提供することができ、かつ、対環境性も向上し廃棄処分が容易となる利点もある。 In addition, foreign matters can be clearly detected in the manufacturing process. For example, if a double-sided printed label is attached to one side of the diluent chamber, the label can be seen through from the outside even when the drug storage chamber and the diluent chamber are folded in two at the weak seal portion. is there. Furthermore, since the conventional aluminum processed film is not used, there is an advantage that it can be provided at a low cost, is environmentally friendly, and is easily disposed of.
以下に、本考案の最良の実施の形態に係るガスバリアフィルム及び複室バッグについて図面を参照しつつ詳細に説明する。
図1は複室バッグの正面図、図2は断面図、図3はフィルム材及びガスバリアフィルムの断面図である。図1及び図2にて、符号1は、抗生剤等の各種薬剤を収納する薬剤収容室、2は弱シール部、3は希釈液室、4は口部、5は空室、6はガスバリアフィルム、7は吊り孔である。この複室バッグは、薬剤収容室1の一端側に弱シール部2を介して希釈液室3が連設される一方、前記薬剤収容室1の他端側に弱シール部2を介して口部4を有する空室5が連設され、薬剤収容室1、希釈液室3及び空室5は、透明なフィルム材からなり、かつ、薬剤収容室1の外側は、透明なガスバリアフィルム6で覆われている。
Hereinafter, a gas barrier film and a multi-chamber bag according to the best mode of the present invention will be described in detail with reference to the drawings.
1 is a front view of a multi-chamber bag, FIG. 2 is a cross-sectional view, and FIG. 3 is a cross-sectional view of a film material and a gas barrier film. 1 and 2,
薬剤収容室1、希釈液室3及び空室5を形成するフィルム材は、例えば、図3(a)に示すように、内面側のポリエチレン(PE)とポリプロピレン(PP)の混合樹脂層(厚さ20μm)11、ポリエチレン(PE)層(厚さ60μm)12、シクロオレフィンコポリマー(COC)層又はシクロオレフィンポリマー(COP)層(厚さ20μm)13、ポリエチレン(PE)層(厚さ50μm)12からなる多層構成で、2枚のフィルム材の周縁部同士が溶着され、かつ、その薬剤収容室1と希釈液室3の間、及び、薬剤収容室1と空室5の間には、それぞれ弱シール部2,2が形成されている。
For example, as shown in FIG. 3A, the film material forming the
一方、薬剤収容室1の外側を覆う透明なガスバリアフィルム6は、例えば、図3(b)に示すように、その内面側にシーラント層6Aを配設し、その外側にバリアフィルム層6Bを配設するように構成される。シーラント層6Aは、直鎖状低密度ポリエチレン(LLDPE)(本考案の樹脂材)層65,65の間に酸化カルシウム(CaO)及び/又は酸化アルミニウム(AlOX )等の粉末を直鎖状低密度ポリエチレン(LLDPE)に練り込んだ層64を挟み込んでなる3層構成とし、バリアフィルム層6Bは、シーラント層6Aに対してドライラミネート用接着剤層63を介して、ポリエチレンテレフタレート(PET)(厚さ12μm)62にシリカ蒸着層6aを蒸着したものを2層積層している。
On the other hand, the transparent
上述のバリアフィルム層6Bは、図3(c)に示すように6層であってもよく、その他、1層乃至10層の範囲で適宜に選択されればよい。また、バリアフィルム層6Bのシーラント層6Aへの積層は、上記のドライラミネート法によるほか、加熱溶融樹脂を間に挟んで積層するサンドイッチラミネーション法を採用することもできる。この場合、バリアフィルム層6Bとシーラント層6Aの間に挟む樹脂としては、接着性に優れたポリオレフィン系樹脂を用いるのが好ましく、シーラント層6Aに用いた樹脂と同系統の樹脂を用いることが、接着性の点から好ましい。さらに、ガスバリアフィルム6には、ガスバリア性を向上させる目的で、ポリビニルアルコール(PVA)又はエチレン・ビニルアルコール共重合体(EVOH)などのガスバリア性に優れるフィルムをさらに積層してもよい。
The above-described
このように、水分吸収能が高いシーラント層6Aを最内層に備えた透明なガスバリアフィルム6で薬剤収容室1を被覆することで、乾燥剤や脱酸素剤を使用することなく、薬剤が水分や酸素の影響を受けないように保護することができ、そのシーラント層6Aの外側に配設されるバリアフィルム層6Bの積層数を減じることもでき、これによりコストの低減化が可能となる。ちなみに、このようなシーラント層6Aを備えたガスバリアフィルム6の酸素透過度は1cc/m2 ・day・atm以下、水分透過度は1g/m2 ・day(40℃,90%)以下であることが好ましい。
In this way, by covering the
そして、そのガスバリアフィルム6が透明であることから、外部から薬剤収容室1の内部を透視することができ、収容された薬剤の状態及び弱シール部2を破断して希釈液室3から薬剤収容室1に希釈液を導入して薬剤に混合したときに不溶性異物の有無等を明確に確認することができるため、誤った投与の発生を抑えることができる。また、薬剤収容室1を透明なガスバリアフィルム6で被覆するので、製造工程においても異物の混入等を明確に検出することができる。そして、例えば、両面印刷したラベルを希釈液室3の片面に貼り付ければ、薬剤収容室1と希釈液室3を弱シール部2で2つ折りにした状態でも、そのラベルを外部から透視して判読できる利点もある。
Since the
さらに、その薬剤収容室1と弱シール部2を介して口部4を有する空室5を連設しているため、必ず薬剤が希釈液で希釈された状態で空室5を介して投与されるため、誤った投与の発生を防ぐことができる。また、ガスバリアフィルム6で覆われた薬剤収容室1と弱シール部2を介して口部4を有する空室5を連設しているため、口部4及びその周辺においては、バリア性であることが要件とされず、その分材料費を低減することができる。さらに、従来のようなアルミ加工フィルムを用いていないため、安価に提供することができ、かつ、対環境性も向上し廃棄処分が容易となる利点もある。
Furthermore, since the
上述のようなシーラント層6Aを形成するためには、CaO粉末又はAlOX 粉末の何れかを直鎖状低密度ポリエチレン(LLDPE)に練り込めばよいがCaO粉末とAlOX 粉末の両者を混ぜて練り込んでもよい。また、その直鎖状低密度ポリエチレン(LLDPE)に代えて、低密度ポリエチレン(LDPE)、ポリプロピレン(PP)、エチレン・酢酸ビニル共重合体(EVA)、酸コポリマー、酸エステルコポリマー及び/又はアイオノマー等にCaO粉末及び/又はAlOX 粉末を練り込んでもよい。
In order to form the
また、図3(b)(c)の例では、シーラント層6Aを最内層に配設しているが、これに限定されることなく、シーラント層6Aの内側に保護フィルム層やバリアフィルム層が積層されてもよい。また、図3(b)(c)の例では、シーラント層6Aを3層構成としているが、CaO及び/又はAlOX 粉末の粉末を直鎖状低密度ポリエチレン(LLDPE)に練り込んだ層64のみであってもよく、その層64に直鎖状低密度ポリエチレン(LLDPE)層65を積層した2層構成のシーラント層6Aであってもよい。
3B and 3C, the
さらに、水分吸収剤は、CaOやAlOX に代えて以下のようなものであってもよい。即ち、無機物では、ゼオライト、シリカゲル、焼明礬、硫酸マグネシウム、塩化カルシウム、硫酸カリウム、五酸化リン、炭酸ナトリウム、炭酸カリウム、有機物では、ポリ(メタ)アクリル酸塩、カルボキシメチルセルローズ、ポリエチレングリコール、及び、これらの誘導体、の中から選択された1種の材料、上記無機物同士、有機物同士の組み合わせ、あるいは、上記無機物と有機物相互の組み合わせ、の何れかであってもよい。 Further, the water absorbing agent, may be as follows in place of CaO or AlO X. That is, for inorganic substances, zeolite, silica gel, shochu liquor, magnesium sulfate, calcium chloride, potassium sulfate, phosphorus pentoxide, sodium carbonate, potassium carbonate, for organic substances, poly (meth) acrylate, carboxymethylcellulose, polyethylene glycol, and One kind of material selected from these derivatives, the above inorganic materials, a combination of organic materials, or a combination of the above inorganic materials and organic materials may be used.
また、図示は省略するが、このようなシーラント層6Aとバリアフィルム層6Bを備えたガスバリアフィルム6は、例えば、薬剤収容室と、口部を備えた希釈液室が、弱シール部を介して連設される2室構成の複室バッグにも適用することができ、その薬剤収容室をガスバリアフィルム6で被覆することができる。また、その希釈液室と口部の間に空室が設けられ、該空室と前記希釈液室の間に前記弱シール部が介設される3室構成の複室バッグの場合にも、同様に、薬剤収容室をガスバリアフィルム6で被覆することができる。
Moreover, although illustration is abbreviate | omitted, the
なお、本考案は、実施の形態に限定されることなく、考案の要旨を逸脱しない限りにおいて、適宜、必要に応じて、設計変更や改良等を行うのは自由であり、また、実施の形態間での構成の組み合わせも自由であり、少なくとも薬剤収容室を備えた複室バッグであれば、本考案のガスバリアフィルムを適用することができる。 It should be noted that the present invention is not limited to the embodiment, and it is free to make design changes and improvements as necessary, as long as it does not depart from the gist of the invention. The combination of configurations between them is also free, and the gas barrier film of the present invention can be applied to a multi-chamber bag provided with at least a medicine storage chamber.
1…薬剤収容室、2…弱シール部、3…希釈液室、4…口部、5…空室、6…ガスバリアフィルム、6A…シーラント層、6B…バリアフィルム層、62…ポリエチレンテレフタレート(PET)
DESCRIPTION OF
Claims (12)
前記薬剤収容室、希釈液室及び空室は透明なフィルム材からなり、かつ、前記薬剤収容室を透明なガスバリアフィルムで被覆してなり、該ガスバリアフィルムは、透明な樹脂材に水分吸収剤を練り込んでなるシーラント層を備えたことを特徴とする複室バッグ。 A dilution chamber is connected to one end side of the drug storage chamber via a weak seal portion, while a vacant chamber having a mouth portion is connected to the other end side of the drug storage chamber via a weak seal portion. A room bag,
The drug storage chamber, the diluent chamber and the vacant chamber are made of a transparent film material, and the drug storage chamber is covered with a transparent gas barrier film, and the gas barrier film is formed by applying a moisture absorbent to a transparent resin material. A multi-chamber bag comprising a kneaded sealant layer.
前記薬剤収容室及び希釈液室は透明なフィルム材からなり、かつ、前記薬剤収容室には透明なガスバリアフィルムが被覆され、該ガスバリアフィルムは、透明な樹脂材に水分吸収剤を練り込んでなるシーラント層を備えていることを特徴とする複室バッグ。 A drug storage chamber and a diluting solution chamber provided with a mouth portion are multi-chamber bags connected continuously via a weak seal portion,
The drug storage chamber and the diluent chamber are made of a transparent film material, and the drug storage chamber is covered with a transparent gas barrier film, and the gas barrier film is formed by kneading a moisture absorbent into a transparent resin material. A multi-chamber bag comprising a sealant layer.