JP3095108B2 - Fixing roll cleaning sheet and cleaning device using the same - Google Patents
Fixing roll cleaning sheet and cleaning device using the sameInfo
- Publication number
- JP3095108B2 JP3095108B2 JP29593094A JP29593094A JP3095108B2 JP 3095108 B2 JP3095108 B2 JP 3095108B2 JP 29593094 A JP29593094 A JP 29593094A JP 29593094 A JP29593094 A JP 29593094A JP 3095108 B2 JP3095108 B2 JP 3095108B2
- Authority
- JP
- Japan
- Prior art keywords
- fiber
- fixing roll
- cleaning sheet
- cleaning
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は定着ロール用クリーニン
グシート、及びこれを用いたクリーニング装置に関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a fixing roll cleaning sheet and a cleaning apparatus using the same.
【０００２】[0002]
【従来の技術】従来から、電子写真複写機などに含まれ
る、トナーを紙などに定着するために使用する定着ロー
ルのクリーニングシートとして、芳香族ポリアミド系樹
脂からなる繊維を４０％以上含む不織布に、シリコーン
オイルなどのオイルを含浸したものが使用されてきた。
しかしながら、このクリーニングシートは含浸されたオ
イル量の２０％程度しか定着ロールに塗布できず、オイ
ルを有効に利用できないものであった。2. Description of the Related Art Conventionally, as a cleaning sheet for a fixing roll used for fixing toner on paper or the like, which is included in an electrophotographic copying machine or the like, a nonwoven fabric containing at least 40% of fibers made of an aromatic polyamide resin has been used. And those impregnated with oil such as silicone oil have been used.
However, this cleaning sheet could only be applied to the fixing roll by about 20% of the amount of impregnated oil, and the oil could not be used effectively.
【０００３】そのため、本願出願人は特開平６−１６７
９０３号公報において、定着ロールとの接触時に溶融し
ない繊維を含み、厚さ０.１〜１.０mmで、見掛密度０.
０５〜０.４０g/cm3の不織布からなる定着ロール用クリ
ーニングシート、具体的には、融点が２１０℃以上の熱
可塑性繊維を３０〜７０重量％含む繊維ウエブを部分的
に熱圧着した不織布を開示した。このクリーニングシー
トは従来よりも嵩高で、疎な構造を有しているため、定
着ロールにクリーニングシートを押しつけ、押圧ロール
で押し潰されて、保持していたオイルを定着ロールに塗
布しやすく、オイルを有効に利用できるものであった
が、熱圧着されておらず、繊維密度が低くて、繊維の自
由度の高い部分を有するものであるため、特に、熱可塑
性繊維の比率を高くした場合には、定着ロールの熱によ
り熱可塑性繊維が著しく収縮し、安定してクリーニング
できないものであった。[0003] For this reason, the present applicant has disclosed in Japanese Patent Application Laid-open No. Hei 6-167.
No. 903, which contains fibers that do not melt when in contact with a fixing roll, has a thickness of 0.1 to 1.0 mm, and an apparent density of 0.1.
A fixing roll cleaning sheet made of a non-woven fabric of 0.5 to 0.40 g / cm 3 , specifically, a non-woven fabric obtained by partially thermocompressing a fiber web containing 30 to 70% by weight of a thermoplastic fiber having a melting point of 210 ° C. or more. Disclosed. Since this cleaning sheet is bulkier and has a sparse structure than before, the cleaning sheet is pressed against the fixing roll, crushed by the pressing roll, and the retained oil is easily applied to the fixing roll, and the oil is removed. Although it was possible to effectively use, but is not thermocompression bonded, the fiber density is low, because it has a high degree of freedom of the fiber, especially when the ratio of thermoplastic fibers is increased In the case of No. 2, the thermoplastic fibers were significantly shrunk by the heat of the fixing roll, and could not be stably cleaned.
【０００４】[0004]
【発明が解決しようとする課題】本発明は上記の問題点
を解決するためになされたものであり、オイルの定着ロ
ールへの移行性に優れ、しかも安定してクリーニングで
きる定着ロール用クリーニングシート、及びこれを用い
たクリーニング装置を提供することにある。SUMMARY OF THE INVENTION The present invention has been made in order to solve the above-mentioned problems, and has an excellent transferability of oil to a fixing roll, and can further stably clean a fixing roll cleaning sheet. And a cleaning device using the same.
【０００５】[0005]
【課題を解決するための手段】本発明の定着ロール用ク
リーニングシートは、定着ロール設置箇所の雰囲気温度
以上で、かつ定着ロールの表面温度よりも１００℃高い
温度以下で、軟化する繊維（以下、「軟化繊維」という
ことがある）を７０重量％を越えて含む繊維ウエブが、
全面的に圧着された層を有し、前記軟化繊維としてポリ
アミド系繊維、ポリエステル系繊維、アクリル系繊維、
ビニロン系繊維、ポリフェニレンサルファイド繊維から
選ばれる繊維と、未延伸ポリエステル繊維、未延伸ポリ
フェニレンサルファイド繊維から選ばれる繊維とを含む
ものである。なお、軟化繊維がポリエステル系繊維と未
延伸ポリエステル繊維であると、融点が２５５℃程度と
高く、定着ロール設置箇所の雰囲気温度では軟化又は溶
融しにくいため好適に使用でき、更に、２００℃におけ
る収縮率が２％以下の繊維を、５重量％以上含んでいる
と、定着ロールをクリーニングする際に収縮しにくいた
め、定着ロールを傷つけたり、巻き長さが短くなって、
使用期間が短くなることもない。また、前記軟化繊維を
７０重量％を越えて含む繊維ウエブが、表面層を構成し
ていると効率的にオイルを塗布でき、前記２００℃にお
ける収縮率が２％以下の繊維を主体とする層を含んでい
ると、安定してクリーニングすることができる。 The fixing roll cleaning sheet of the present invention has a fiber (hereinafter, referred to as "softening fiber") which is softened at a temperature not lower than the ambient temperature of the fixing roll installation location and not higher than 100 ° C. higher than the surface temperature of the fixing roll. A fiber web containing more than 70% by weight of a softened fiber)
It has a layer that is entirely pressed, and the softening fiber is made of poly
Amide fiber, polyester fiber, acrylic fiber,
From vinylon fiber and polyphenylene sulfide fiber
Selected fiber, undrawn polyester fiber, undrawn poly
Including fibers selected from phenylene sulfide fibers
Things. In addition, the softened fiber is not
The drawn polyester fiber has a high melting point of about 255 ° C. and is not easily softened or melted at the ambient temperature of the fixing roll installation location, so that it can be suitably used. Further, a fiber having a shrinkage rate of 2% or less at 200 ° C. If it is contained by weight or more, it is difficult to shrink when cleaning the fixing roll, so that the fixing roll is damaged or the winding length is shortened.
The period of use is not shortened. Further, the softened fiber
The fiber web containing more than 70% by weight constitutes the surface layer
Oil can be applied efficiently,
Including a layer mainly composed of fibers with a shrinkage of 2% or less
Then, cleaning can be performed stably.
【０００６】本発明のクリーニング装置は、上記定着ロ
ール用クリーニングシートの、よりオイル移行性の高い
表面が定着ロールと接触するように巻き出す手段と、ク
リーニングシートの定着ロールへの押圧手段と、クリー
ニングシートの巻き取り手段とを有するものである。[0006] The cleaning device of the present invention comprises: means for unwinding the cleaning sheet for a fixing roll so that the surface having a higher oil transferability comes into contact with the fixing roll; means for pressing the cleaning sheet against the fixing roll; Sheet winding means.
【０００７】[0007]
【作用】本発明の定着ロール用クリーニングシートは、
定着ロール設置箇所の雰囲気温度以上で、かつ定着ロー
ルの表面温度よりも１００℃高い温度以下で、軟化する
繊維を７０重量％を越えて含む繊維ウエブが、全面的に
圧着された層を有するため、定着ロールへの押圧手段に
より、この軟化繊維自体が変形し、定着ロールとの接触
面積が広くなると同時に、空隙に保持されたオイルを押
し出すため、クリーニング性及びオイル移行性に優れて
いる。また、このクリーニングシートは全面的に圧着さ
れ、緻密で繊維の自由度の低い層を有するため、軟化繊
維が軟化して変形しても、収縮しにくく、安定してクリ
ーニングできる。The fixing roll cleaning sheet of the present invention comprises:
A fiber web containing more than 70% by weight of a softening fiber at a temperature higher than the ambient temperature of the fixing roll installation location and lower than 100 ° C. higher than the surface temperature of the fixing roll has a layer which is entirely pressed. The softening fiber itself is deformed by the pressing means against the fixing roll, and the contact area with the fixing roll is increased, and at the same time, the oil held in the gap is pushed out, so that the cleaning property and the oil transfer property are excellent. Further, since the cleaning sheet is entirely pressed and has a layer having a dense and low degree of freedom of the fibers, even if the softened fibers are softened and deformed, they do not easily shrink and can be stably cleaned.
【０００８】本発明で使用する軟化繊維は、クリーニン
グシートが定着ロールと接触した際に、定着ロールによ
る熱及び定着ロールへの押圧により、軟化し、変形し
て、定着ロールと密着すると共に、クリーニングシート
の空隙に保持されているオイルを押し出す働きをする。
そのため、この軟化繊維は定着ロール設置箇所の雰囲気
温度以上で、かつ定着ロールの表面温度よりも１００℃
高い温度以下で軟化する必要がある。軟化繊維が定着ロ
ール設置箇所の雰囲気温度未満で著しく軟化すると、定
着ロールにオイルを塗布する前にオイルだれが生じ、軟
化繊維が定着ロールの表面温度よりも１００℃高い温度
を越える温度で軟化すると、上記クリーニングとオイル
塗布の作用が低下するためである。より好ましくは、定
着ロール設置箇所の雰囲気温度よりも５０℃以上で、か
つ定着ロールの表面温度よりも８０℃高い温度以下で軟
化する繊維である。When the cleaning sheet comes into contact with the fixing roll, the softening fiber is softened and deformed by the heat of the fixing roll and the pressure applied to the fixing roll, and adheres to the fixing roll. It works to push out the oil held in the gaps in the sheet.
For this reason, the softened fiber is 100 ° C. or higher than the ambient temperature of the fixing roll installation location and the surface temperature of the fixing roll.
It is necessary to soften below a high temperature. If the softening fiber softens significantly below the ambient temperature of the fixing roll installation location, oil dripping occurs before applying oil to the fixing roll, and the softening fiber softens at a temperature exceeding 100 ° C. higher than the surface temperature of the fixing roll. This is because the effects of the above cleaning and oil application are reduced. More preferably, the fiber softens at a temperature of 50 ° C. or higher than the ambient temperature of the fixing roll installation location and 80 ° C. or higher than the surface temperature of the fixing roll.
【０００９】一般的に定着ロールの表面温度は１７０〜
２００℃で、この際の定着ロール設置箇所の雰囲気温度
は１２０〜１５０℃程度であるため、例えば、定着ロー
ルの表面温度が１７０℃である場合には、１２０〜２７
０℃の範囲内で軟化する繊維、定着ロールの表面温度が
２００℃である場合には、１５０〜３００℃の範囲内で
軟化する繊維を使用する。この軟化繊維としては、６ナ
イロン繊維や６６ナイロン繊維などのポリアミド系繊
維、ポリエステル系繊維、アクリル系繊維、ビニロン系
繊維、ポリフェニレンサルファイド繊維がある。これら
の中でも、ポリエステル系繊維は融点が２５５℃程度と
高く、定着ロール設置箇所の雰囲気温度では軟化又は溶
融しにくいため、好適に使用できる。Generally, the surface temperature of the fixing roll is 170 to
At 200 ° C., since the ambient temperature of the fixing roll installation location at this time is about 120 to 150 ° C., for example, when the surface temperature of the fixing roll is 170 ° C., 120 to 27 ° C.
When the surface temperature of the fixing roll is 200 ° C, the fibers softening within the range of 150 to 300 ° C are used. This softened fiber has 6 fibers
There are polyamide fibers such as iron fibers and 66 nylon fibers, polyester fibers, acrylic fibers, vinylon fibers, and polyphenylene sulfide fibers. Among these, polyester-based fibers have a high melting point of about 255 ° C. and are not easily softened or melted at the ambient temperature of the fixing roll installation location, and thus can be suitably used.
【００１０】この軟化繊維はオイル移行性に優れるよう
に、全面的に圧着した繊維ウエブ層中、７０重量％を越
えて含まれており、好ましくは７５重量％以上、より好
ましくは８０重量％以上、最も好ましくは９０重量％以
上含まれている。[0010] The softened fiber is contained in the fiber web layer which has been completely press-bonded in an amount of more than 70% by weight, preferably 75% by weight or more, more preferably 80% by weight or more so as to have excellent oil transferability. , Most preferably 90% by weight or more.
【００１１】なお、本発明における軟化点とは、繊維に
一定荷重（０.０１g/d以下）をかけながら、１℃／分の
割合で温度を上昇させ、急激に収縮した時の温度をい
う。The softening point in the present invention refers to a temperature at which the fiber is heated at a rate of 1 ° C./min while a constant load (0.01 g / d or less) is applied to the fiber and suddenly shrinks. .
【００１２】この軟化繊維以外に、２００℃における収
縮率が２％以下の繊維（以下、低収縮性繊維ということ
がある）を含むと、クリーニングシートが定着ロールと
接触した際に、より収縮しにくいため、収縮して厚みが
増し、摩擦抵抗が大きくなって、定着ロールを傷つけた
り、収縮によりシート長が短くなり、使用期間が短くな
るといった問題を生じないので、好適に使用できる。[0012] In addition to the softened fiber, if the fiber contains a fiber having a shrinkage rate of 2% or less at 200 ° C (hereinafter sometimes referred to as a low shrinkage fiber), the cleaning sheet shrinks more when it comes into contact with the fixing roll. Since it is difficult to shrink, the film shrinks to increase the thickness and the frictional resistance increases, and there is no problem that the fixing roll is damaged or the sheet length is shortened due to the shrinkage, thereby shortening the service period.
【００１３】この低収縮性繊維として、例えば、メタ型
又はパラ型の芳香族ポリアミド、ポリアミドイミド、ポ
リテトラフルオロエチレン、芳香族ポリエーテルアミ
ド、ポリベンツイミダゾール、ポリフェニレンサルファ
イドなどの樹脂成分からなる繊維、或いは、前記の軟化
繊維を弛緩熱処理により既に収縮した繊維などを単独
で、或いは混合して使用できる。これらの中でも、弛緩
熱処理した軟化繊維を使用すれば、軟化繊維量を多くで
き、オイル移行性を低下させることなく、収縮を抑える
ことができるので、より好適である。As the low shrinkage fiber, for example, a fiber comprising a resin component such as meta-type or para-type aromatic polyamide, polyamide imide, polytetrafluoroethylene, aromatic polyetheramide, polybenzimidazole, polyphenylene sulfide, etc. Alternatively, the above-mentioned softened fibers which have already shrunk by relaxation heat treatment can be used alone or in combination. Of these, the use of softened fibers subjected to relaxation heat treatment is more preferable because the amount of softened fibers can be increased, and shrinkage can be suppressed without lowering oil transferability.
【００１４】この低収縮性繊維は、クリーニングシート
が収縮しにくいように、全面的に圧着した繊維ウエブ層
中、５重量％以上含まれているのが好ましく、より好ま
しくは１０重量％以上、最も好ましくは、１５重量％以
上含まれている。なお、メタ型又はパラ型の芳香族ポリ
アミドなどの剛性のある繊維を低収縮性繊維として使用
する場合には、これら繊維の剛性により、軟化繊維の変
形を妨げないように、３０重量％未満とする。The low-shrinkage fiber is preferably contained at 5% by weight or more, more preferably at least 10% by weight, most preferably in the fiber web layer which has been completely pressed to prevent the cleaning sheet from shrinking. Preferably, the content is 15% by weight or more. When rigid fibers such as meta-type or para-type aromatic polyamides are used as the low-shrinkage fibers, the rigidity of these fibers should be less than 30% by weight so as not to hinder the deformation of the softened fibers. I do.
【００１５】なお、収縮率は、繊維に一定荷重（０.０
１g/d以下）をかけ、２００℃の雰囲気下で２０分間放
置した場合の寸法変化率をいう。The shrinkage rate is determined by applying a constant load (0.0) to the fiber.
(1 g / d or less) and a dimensional change rate when left in an atmosphere of 200 ° C. for 20 minutes.
【００１６】本発明の軟化繊維及び低収縮性繊維の断面
形状は、例えば、略円形状や、略三角形状、略四角形、
略五角形、略六角形などの略多角形状や、略Ｉ形状、略
Ｋ形状、略Ｔ形状、略Ｖ形状、略Ｗ形状、略Ｘ形状、略
Ｙ形状などの略アルファベット形状や、略楕円形状、略
長円形状などであっても良い。The cross-sectional shapes of the softened fiber and the low-shrinkable fiber of the present invention are, for example, substantially circular, substantially triangular, substantially square,
Substantially polygonal shapes such as approximately pentagons and approximately hexagons, approximately alphabetical shapes such as approximately I shapes, approximately K shapes, approximately T shapes, approximately V shapes, approximately W shapes, approximately X shapes, approximately Y shapes, and approximately elliptical shapes , A substantially elliptical shape or the like.
【００１７】以上のような軟化繊維や低収縮性繊維は、
繊度０.１〜２０デニールのものを使用するのが好まし
い。繊度が０.１デニール未満では、単繊維強度が不足
し、定着ロールとの摩擦により破断しやすく、他方、２
０デニールを越えると、オイルの保持性が悪いためであ
る。より好ましい繊度は０.５〜７デニールである。ま
た、繊維長は特に限定するものではなく、５〜１５０mm
程度のものを使用すれば良い。The above softened fibers and low-shrinkage fibers are
It is preferable to use a fineness of 0.1 to 20 denier. If the fineness is less than 0.1 denier, the strength of the single fiber is insufficient, and the fiber is easily broken by friction with the fixing roll.
If it exceeds 0 denier, oil retention is poor. A more preferred fineness is 0.5 to 7 denier. The fiber length is not particularly limited, and is 5 to 150 mm
What is necessary is just to use something.
【００１８】以上のような繊維を使用して繊維ウエブを
形成した後、全面的に圧着して、全面的に圧着された層
を形成する。この繊維ウエブの形成方法として、例え
ば、カード法、エアレイ法などの乾式法や、湿式法など
がある。これらの中でも、カード法による一方向性の繊
維ウエブと、この一方向性の繊維ウエブと交差するよう
に、クロスレイヤーなどによって得た交差繊維ウエブと
を積層すると、全方向の強度に優れたクリーニングシー
トとすることができる。なお、この積層繊維ウエブから
得られるクリーニングシートの交差繊維ウエブ面が定着
ロールと接触するように巻き出すと、トナーを線的に払
拭できるので、よりクリーニング性に優れるという特長
もある。After forming a fiber web using the above-described fibers, the fiber web is entirely pressed to form a layer that is entirely pressed. As a method of forming the fiber web, for example, there are a dry method such as a card method and an air lay method, and a wet method. Among these, when a unidirectional fiber web formed by the card method and a crossed fiber web obtained by a cross layer or the like are laminated so as to intersect with the unidirectional fiber web, cleaning having excellent strength in all directions is performed. It can be a sheet. In addition, if the crossed fiber web surface of the cleaning sheet obtained from the laminated fiber web is unwound so as to be in contact with the fixing roll, the toner can be wiped off linearly, so that there is a feature that the cleaning property is more excellent.
【００１９】なお、２層以上からなる繊維ウエブの場
合、少なくとも１層が軟化繊維を７０重量％を越えて含
む繊維ウエブであれば良いが、効率的にオイルを塗布で
きるように、表面層に軟化繊維を７０重量％を越えて含
んでいるのが、最も好ましい。なお、２層以上からな
り、クリーニングシートの両面を使用する場合には、ク
リーニングシートの両表面層に、軟化繊維を７０重量％
を越えて含んでいるのが、より好適である。なお、軟化
繊維を７０重量％を越えて含んでいる層以外の層は、前
記軟化繊維及び低収縮性繊維を自由に配合すれば良い
が、低収縮性繊維を主体（５０重量％以上）とすれば、
この層によって、より収縮しにくく、安定してクリーニ
ングすることができる。In the case of a fiber web comprising two or more layers, at least one layer may be a fiber web containing more than 70% by weight of softened fibers. Most preferably, it contains more than 70% by weight of softened fibers. When the cleaning sheet is composed of two or more layers and both surfaces of the cleaning sheet are used, 70% by weight of the softened fiber is added to both surface layers of the cleaning sheet.
It is more preferable to include more than. The layers other than the layer containing more than 70% by weight of the softened fiber may be freely mixed with the softened fiber and the low-shrinkable fiber. if,
With this layer, shrinkage is more difficult and cleaning can be performed stably.
【００２０】なお、繊維ウエブをニードルや水流などに
よって予め絡合すると、より緻密に絡み合った状態とす
ることができるので、後述の全面的な圧着によって、よ
り繊維の自由度が少なく、より収縮しにくいクリーニン
グシートとすることができる。If the fiber web is entangled in advance with a needle or a water stream, the fiber web can be entangled more densely. It can be a difficult cleaning sheet.
【００２１】次いで、この繊維ウエブを全面的に圧着す
れば、緻密で、繊維の自由度が少なく、収縮しにくいク
リーニングシートが得られる。この圧着方法としては、
例えば、加熱したカレンダーロール間を通す方法や、平
板プレス機により行うことができるが、前者の方が、連
続生産に適しているため、より好適な方法である。この
カレンダーロール間を通す場合、十分に圧着でき、厚み
を均一に調整できるように、温度１７０〜２５０℃、線
圧１０〜１００kg/cmであるのが好ましい。より好まし
くは、温度１９０〜２３０℃、線圧３０〜７０kg/cmで
ある。Then, if the fiber web is entirely pressed, a cleaning sheet which is dense, has a small degree of freedom of fibers, and is hardly shrunk can be obtained. As this crimping method,
For example, a method of passing between heated calender rolls or a flat plate press can be used, but the former is a more suitable method because it is more suitable for continuous production. When passing between the calender rolls, it is preferable that the temperature is 170 to 250 ° C. and the linear pressure is 10 to 100 kg / cm so that sufficient pressure can be applied and the thickness can be adjusted uniformly. More preferably, the temperature is 190 to 230 ° C and the linear pressure is 30 to 70 kg / cm.
【００２２】なお、繊維ウエブが２層以上からなる場
合、軟化繊維を７０重量％を越えて含んだ繊維ウエブの
みを全面的に圧着し、他の層は部分的に圧着したり、水
流などによって絡合しても良いが、製造上、他の層も全
面的に圧着するのが好ましい。この全面的に圧着する方
法は、低目付でも優れた強度とすることができ、しかも
厚みの制御が容易なため、好適なクリーニングシートの
製造方法である。When the fiber web is composed of two or more layers, only the fiber web containing more than 70% by weight of the softened fiber is entirely press-bonded, and the other layers are partially press-bonded or subjected to water flow or the like. Although it may be entangled, it is preferable that the other layers be completely pressed on the whole for the purpose of manufacturing. This method of pressure bonding over the entire surface is a suitable method for producing a cleaning sheet because excellent strength can be obtained even with a low basis weight and the thickness can be easily controlled.
【００２３】また、全面的に圧着しやすいように、未延
伸ポリエステル繊維や、未延伸ポリフェニレンサルファ
イド繊維を、軟化繊維を７０重量％を越えて含む繊維ウ
エブ中に混合しておく。これらの繊維は軟化繊維でもあ
り、軟化繊維の量を減らすことなく、圧着しやすい。 Further, unstretched polyester fiber and unstretched polyphenylene sulfide fiber are mixed in a fiber web containing more than 70% by weight of softened fiber so that the whole surface can be easily pressed . These fibers are also softened fibers and can be easily pressed without reducing the amount of softened fibers .
【００２４】以上のようにして得られるクリーニングシ
ートの厚さは２０〜１２０μmであるのが好ましい。２
０μm未満であると、オイル及びトナーを保持する空隙
が少なくなり、１２０μmを越えると、オイル及びトナ
ーの保持に関与しない空隙が多く、非効率的となるため
である。より好ましくは、４０〜９０μmである。ま
た、目付は強度を維持し、空隙を低下させない範囲で、
１０〜６０g/m2であるのが好ましい。The thickness of the cleaning sheet obtained as described above is preferably 20 to 120 μm. 2
If the thickness is less than 0 μm, the space for holding the oil and the toner will be small, and if it exceeds 120 μm, there will be many spaces not involved in the holding of the oil and the toner, which will be inefficient. More preferably, it is 40 to 90 μm. In addition, the basis weight maintains the strength, as long as the gap is not reduced,
It is preferably from 10 to 60 g / m 2 .
【００２５】このクリーニングシートには、よりトナー
を除去しやすくするために、ポリシロキサン系などのシ
リコーンオイルを含浸する。このオイルの含浸量はクリ
ーニングシートの厚さなどによって異なるが、１０〜４
０g/m2程度が好ましい。また、オイルの粘度は特に限定
するものではなく、１００〜５０,０００センチポアズ
のものが使用できる。This cleaning sheet is impregnated with a silicone oil such as a polysiloxane to make it easier to remove the toner. The oil impregnation amount varies depending on the thickness of the cleaning sheet and the like.
About 0 g / m 2 is preferable. The viscosity of the oil is not particularly limited, and a viscosity of 100 to 50,000 centipoise can be used.
【００２６】このオイルを含浸したクリーニングシート
を使用する、クリーニング装置について、クリーニング
装置の一例である図１をもとに説明する。オイルを含有
したクリーニングシート１は巻出しシャフト２から巻き
出され、押圧ロール４により、定着ロールに押圧され、
定着ロールの熱及び押圧ロールによる圧力により、クリ
ーニングシートが変形して、定着ロールとクリーニング
シートとの接触面積が広くなるため、よりトナーの払拭
性に優れると共に、クリーニングシート中のオイルが押
し出され、効率的にオイルを塗布することができる。そ
の後、このクリーニングシートは巻取りシャフト３によ
って巻取られる。A cleaning device using the cleaning sheet impregnated with the oil will be described with reference to FIG. 1 which is an example of the cleaning device. The cleaning sheet 1 containing oil is unwound from the unwinding shaft 2 and is pressed against the fixing roll by the pressing roll 4.
Due to the heat of the fixing roll and the pressure of the pressing roll, the cleaning sheet is deformed and the contact area between the fixing roll and the cleaning sheet is increased, so that the toner in the cleaning sheet is more excellent, and the oil in the cleaning sheet is extruded. The oil can be applied efficiently. Thereafter, the cleaning sheet is wound by the winding shaft 3.
【００２７】なお、本発明においては、クリーニングシ
ートのよりオイル移行性の高い表面が定着ロールと接触
するように巻き出し、よりオイルが押し出されやすいよ
うにする。例えば、２層からなるクリーニングシート
で、片面のみが軟化繊維を７０重量％を越えて含む繊維
ウエブの圧着層である場合には、この軟化繊維を７０重
量％を越えて含む繊維ウエブの圧着層が定着ロールと接
触するように巻き出し、３層からなるクリーニングシー
トで、中間層が軟化繊維を７０重量％を越えて含む繊維
ウエブの圧着層である場合には、クリーニングシートの
オイル移行性のより高い表面が定着ロールと接触するよ
うに巻き出す。In the present invention, the surface of the cleaning sheet having higher oil transferability is unwound so as to come into contact with the fixing roll, so that the oil is more easily extruded. For example, in the case of a two-layer cleaning sheet, in which only one side is a pressure-bonded layer of a fiber web containing more than 70% by weight of softened fiber, a pressure-bonded layer of a fiber web containing more than 70% by weight of this softened fiber Is unwound so as to come into contact with the fixing roll, and when the intermediate layer is a pressure-bonded layer of a fiber web containing more than 70% by weight of softened fibers, the oil transfer property of the cleaning sheet is increased. Unwind so that the higher surface contacts the fuser roll.
【００２８】このオイル移行性のより高い表面は次のよ
うにして判断することができる。まず、一定の大きさ
（例えばＡ４サイズ）に裁断した、オイルを含有するク
リーニングシートを２枚用意する。このクリーニングシ
ートの１枚を完全に覆うことのできる２枚の紙で挟み、
温度５０℃、圧力０.１kg/cm2のロール間を通す。この
時、１枚のクリーニングシートは片面（Ａ面という）を
上向きにしてロール間を通し、他の１枚のクリーニング
シートはＡ面とは反対の面を上向きにして通す。そし
て、クリーニングシートを挟んだ２枚の紙の重量の増加
から、より増加量の大きかった面をオイル移行性の高い
表面と判断する。The surface having higher oil transferability can be determined as follows. First, two oil-containing cleaning sheets cut to a certain size (for example, A4 size) are prepared. One sheet of this cleaning sheet is sandwiched between two sheets of paper that can completely cover the sheet,
Pass between rolls at a temperature of 50 ° C. and a pressure of 0.1 kg / cm 2 . At this time, one cleaning sheet is passed between the rolls with one surface (referred to as surface A) facing upward, and another cleaning sheet is passed with the surface opposite to surface A facing upward. Then, based on the increase in the weight of the two sheets sandwiching the cleaning sheet, the surface with the larger increase is determined to be the surface with high oil transferability.
【００２９】このクリーニングシートの押圧手段として
は、図１に示すように円形状のもの、四角形、六角形な
どの多角形状のもので良いが、円形状であると、均一に
力がかかるので、より好適である。なお、この押圧手段
による押圧力は、クリーニングシートの軟化繊維を変形
させ、オイルを押し出しやすいように、０.１kg/cm2以
上であるのが好ましいが、定着ロールに傷をつけないよ
うに、０.２kg/cm2以下であるのが好ましい。また、こ
の押圧手段は、弾性及び耐熱性に優れた材料、例えば、
発泡又は無発泡のシリコンゴムなどからなるのが好まし
い。As the pressing means for the cleaning sheet, a circular one as shown in FIG. 1, a polygonal one such as a square or a hexagon may be used, but a circular one applies a uniform force. More preferred. The pressing force by this pressing means is preferably 0.1 kg / cm 2 or more so as to deform the softened fiber of the cleaning sheet and easily push out the oil. It is preferably at most 0.2 kg / cm 2 . The pressing means is made of a material having excellent elasticity and heat resistance, for example,
It is preferably made of foamed or non-foamed silicone rubber.
【００３０】以下に、本発明の実施例を記載するが、本
発明は以下の実施例に限定されるものではない。Examples of the present invention will be described below, but the present invention is not limited to the following examples.
【００３１】[0031]
（実施例１）軟化点２４０℃、収縮率６.９％のポリエ
ステル繊維（繊度１.５デニール、繊維長３８mm、断面
円形）３５重量％、軟化点２４０℃、収縮率４０％の未
延伸ポリエステル繊維（繊度５デニール、繊維長３８m
m、断面円形）４０重量％、及び軟化点なし、収縮率０.
５％のメタ型芳香族ポリアミド繊維（繊度１.５デニー
ル、繊維長３８mm、断面円形、商品名：ノーメックス、
デュポン製）２５重量％とをカード機により開繊して一
方向性の繊維ウエブを得た。次いで、この繊維ウエブ
を、温度２１０℃のスチールロールとコットンロール間
（線圧４０kg/cm）を通して圧着し、目付２５g/m2、厚
さ６０μmの不織布を得た。その後、この不織布にジメ
チルポリシロキサン（粘度１０,０００CS）を２５g/m2
コーティングして、クリーニングシートを得た。(Example 1) Unstretched polyester having a softening point of 240 ° C and a shrinkage of 6.9% (weight: 1.5 denier, fiber length: 38 mm, circular cross section) 35% by weight, a softening point of 240 ° C and a shrinkage of 40% Fiber (denier 5 denier, fiber length 38m
m, circular cross section) 40% by weight, and no softening point, shrinkage of 0,0.
5% meta-type aromatic polyamide fiber (fineness 1.5 denier, fiber length 38 mm, circular cross section, trade name: Nomex,
(Manufactured by DuPont) was opened by a carding machine to obtain a unidirectional fiber web. Next, the fiber web was pressed between a steel roll and a cotton roll at a temperature of 210 ° C. (linear pressure: 40 kg / cm) to obtain a nonwoven fabric having a basis weight of 25 g / m 2 and a thickness of 60 μm. Thereafter, 25 g / m 2 of dimethylpolysiloxane (viscosity 10,000 CS) was added to the nonwoven fabric.
After coating, a cleaning sheet was obtained.
【００３２】（実施例２）軟化点２４０℃、収縮率６.
９％のポリエステル繊維（繊度１.５デニール、繊維長
３８mm、断面円形）４５重量％、軟化点２４０℃、収縮
率４０％の未延伸ポリエステル繊維（繊度５デニール、
繊維長３８mm、断面円形）４０重量％、及び軟化点な
し、収縮率０.５％のメタ型芳香族ポリアミド繊維（繊
度１.５デニール、繊維長３８mm、断面円形、商品名：
ノーメックス、デュポン製）１５重量％とを使用した以
外は、実施例１と同様にして、目付２５g/m2、厚さ６０
μmの不織布に２５g/m2のジメチルポリシロキサンをコ
ーティングしてクリーニングシートを得た。Example 2 Softening point 240 ° C., shrinkage 6.
9% polyester fiber (fineness 1.5 denier, fiber length 38 mm, circular cross section) 45% by weight, softening point 240 ° C, unstretched polyester fiber 40% shrinkage (fineness 5 denier,
Meta-type aromatic polyamide fiber having a fiber length of 38 mm and a cross section of 40% by weight and a softening point of 0.5% and a shrinkage of 0.5% (denier 1.5 denier, fiber length 38 mm, circular cross section, trade name:
Nomex, manufactured by DuPont) in the same manner as in Example 1, except that the weight per unit area was 25 g / m 2 and the thickness was 60%.
A cleaning sheet was obtained by coating 25 μm / m 2 of dimethylpolysiloxane on a μm nonwoven fabric.
【００３３】（実施例３）軟化点２４０℃、収縮率６.
９％のポリエステル繊維（繊度１.５デニール、繊維長
３８mm、断面円形）３０重量％、軟化点２４０℃、収縮
率１.３％（弛緩熱処理済）のポリエステル繊維（繊度
１.５デニール、繊維長３８mm、断面円形）１５重量
％、軟化点２４０℃、収縮率４０％の未延伸ポリエステ
ル繊維（繊度５デニール、繊維長３８mm、断面円形）４
０重量％、及び軟化点なし、収縮率０.５％のメタ型芳
香族ポリアミド繊維（繊度１.５デニール、繊維長３８m
m、断面円形、商品名：ノーメックス、デュポン製）１
５重量％とを使用した以外は、実施例１と同様にして、
目付２５g/m2、厚さ６０μmの不織布に２５g/m2のジメ
チルポリシロキサンをコーティングしてクリーニングシ
ートを得た。Example 3 Softening point 240 ° C., shrinkage 6.
9% polyester fiber (fineness 1.5 denier, fiber length 38 mm, circular cross section) 30% by weight, softening point 240 ° C, shrinkage 1.3% (relaxation heat treated) polyester fiber (fineness 1.5 denier, fiber Undrawn polyester fiber (length: 38 mm, cross section circular) 15% by weight, softening point 240 ° C, shrinkage ratio 40% (denier 5 denier, fiber length 38 mm, cross section circular) 4
0% by weight, no softening point, 0.5% shrinkage rate meta-type aromatic polyamide fiber (denier 1.5 denier, fiber length 38m)
m, circular section, product name: Nomex, made by Dupont) 1
Except for using 5% by weight, the same as in Example 1,
A cleaning sheet was obtained by coating 25 g / m 2 of dimethylpolysiloxane on a nonwoven fabric having a basis weight of 25 g / m 2 and a thickness of 60 μm.
【００３４】（実施例４）軟化点２４０℃、収縮率６.
９％のポリエステル繊維（繊度１.５デニール、繊維長
３８mm、断面円形）６０重量％、軟化点２４０℃、収縮
率４０％の未延伸ポリエステル繊維（繊度５デニール、
繊維長３８mm、断面円形）４０重量％とを使用した以外
は、実施例１と同様にして、目付２５g/m2、厚さ６０μ
mの不織布に２５g/m2のジメチルポリシロキサンをコー
ティングしてクリーニングシートを得た。(Example 4) Softening point 240 ° C, shrinkage 6.
60% by weight of 9% polyester fiber (denier 1.5 denier, fiber length 38mm, circular cross section), softening point 240 ° C, unstretched polyester fiber of shrinkage 40% (denier 5 denier,
Except for using a fiber length of 38 mm and a circular cross section of 40% by weight), the same as in Example 1 except that the basis weight was 25 g / m 2 and the thickness was 60 μm.
m was coated with 25 g / m 2 of dimethylpolysiloxane to obtain a cleaning sheet.
【００３５】（実施例５）軟化点２４０℃、収縮率６.
９％のポリエステル繊維（繊度１.５デニール、繊維長
３８mm、断面円形）５０重量％、軟化点２４０℃、収縮
率１.３％（弛緩熱処理済）のポリエステル繊維（繊度
１.５デニール、繊維長３８mm、断面円形）１０重量
％、及び軟化点２４０℃、収縮率４０％の未延伸ポリエ
ステル繊維（繊度５デニール、繊維長３８mm、断面円
形）４０重量％とを使用した以外は、実施例１と同様に
して、目付２５g/m2、厚さ６０μmの不織布に２５g/m2
のジメチルポリシロキサンをコーティングしてクリーニ
ングシートを得た。Example 5 Softening point 240 ° C., shrinkage 6.
9% polyester fiber (fineness 1.5 denier, fiber length 38 mm, circular cross section) 50% by weight, softening point 240 ° C, shrinkage 1.3% (relaxation heat treated) polyester fiber (fineness 1.5 denier, fiber Example 1 except that 10% by weight of a 38 mm length, circular cross section) and 40% by weight of an undrawn polyester fiber (denier 5 denier, fiber length 38 mm, circular cross section) having a softening point of 240 ° C. and a shrinkage of 40% were used. in the same manner as, basis weight 25 g / m 2, the thickness of 60μm nonwoven 25 g / m 2
Of dimethylpolysiloxane was obtained to obtain a cleaning sheet.
【００３６】（実施例６）軟化点２４０℃、収縮率６.
９％のポリエステル繊維（繊度１.５デニール、繊維長
３８mm、断面円形）４０重量％、軟化点２４０℃、収縮
率１.３％（弛緩熱処理済）のポリエステル繊維（繊度
１.５デニール、繊維長３８mm、断面円形）２０重量
％、及び軟化点２４０℃、収縮率４０％の未延伸ポリエ
ステル繊維（繊度５デニール、繊維長３８mm、断面円
形）４０重量％とを使用した以外は、実施例１と同様に
して、目付２５g/m2、厚さ６０μmの不織布に２５g/m2
のジメチルポリシロキサンをコーティングしてクリーニ
ングシートを得た。(Example 6) Softening point 240 ° C, shrinkage 6.
Polyester fiber with 9% polyester fiber (fineness 1.5 denier, fiber length 38 mm, circular cross section) 40% by weight, softening point 240 ° C, shrinkage 1.3% (relaxation heat treatment) polyester fiber (fineness 1.5 denier, fiber) Example 1 except that 20% by weight of a 38 mm long, circular cross section) and 40% by weight of an undrawn polyester fiber having a softening point of 240 ° C. and a shrinkage of 40% (denier 5 denier, fiber length 38 mm, circular cross section) were used. in the same manner as, basis weight 25 g / m 2, the thickness of 60μm nonwoven 25 g / m 2
Of dimethylpolysiloxane was obtained to obtain a cleaning sheet.
【００３７】（比較例１）軟化点２４０℃、収縮率６.
９％のポリエステル繊維（繊度１.５デニール、繊維長
３８mm、断面円形）３０重量％、軟化点２４０℃、収縮
率４０％の未延伸ポリエステル繊維（繊度５デニール、
繊維長３８mm、断面円形）４０重量％、及び軟化点な
し、収縮率０.５％のメタ型芳香族ポリアミド繊維（繊
度１.５デニール、繊維長３８mm、断面円形、商品名：
ノーメックス、デュポン製）３０重量％とを使用した以
外は、実施例１と同様にして、目付２５g/m2、厚さ６０
μmの不織布に２５g/m2のジメチルポリシロキサンをコ
ーティングしてクリーニングシートを得た。Comparative Example 1 Softening point 240 ° C., shrinkage 6.
9% polyester fiber (denier 1.5 denier, fiber length 38 mm, circular cross section) 30% by weight, softening point 240 ° C., shrinkage 40% undrawn polyester fiber (denier 5 denier,
Meta-type aromatic polyamide fiber having a fiber length of 38 mm and a cross section of 40% by weight and a softening point of 0.5% and a shrinkage of 0.5% (denier 1.5 denier, fiber length 38 mm, circular cross section, trade name:
Nomex, manufactured by DuPont) in the same manner as in Example 1, except that the weight per unit area was 25 g / m 2 and the thickness was 60.
A cleaning sheet was obtained by coating 25 μm / m 2 of dimethylpolysiloxane on a μm nonwoven fabric.
【００３８】（比較例２）軟化点２４０℃、収縮率４０
％の未延伸ポリエステル繊維（繊度５デニール、繊維長
３８mm、断面円形）４０重量％、軟化点なし、収縮率
０.５％のメタ型芳香族ポリアミド繊維（繊度１.５デニ
ール、繊維長３８mm、断面円形、商品名：ノーメック
ス、デュポン製）６０重量％とを使用した以外は、実施
例１と同様にして、目付２５g/m2、厚さ６０μmの不織
布に２５g/m2のジメチルポリシロキサンをコーティング
してクリーニングシートを得た。Comparative Example 2 Softening Point 240 ° C., Shrinkage 40
% Of unstretched polyester fiber (fineness 5 denier, fiber length 38 mm, circular cross section) 40% by weight, no softening point, shrinkage 0.5% meta-type aromatic polyamide fiber (fineness 1.5 denier, fiber length 38 mm, 25 g / m 2 , 25 g / m 2 dimethylpolysiloxane on a nonwoven fabric having a basis weight of 25 g / m 2 and a thickness of 60 μm in the same manner as in Example 1 except that 60% by weight of a circular cross section, trade name: Nomex, manufactured by DuPont was used. Coating was performed to obtain a cleaning sheet.
【００３９】（比較例３）軟化点２４０℃、収縮率６.
９％のポリエステル繊維（繊度１.５デニール、繊維長
３８mm、断面円形）１５重量％、軟化点２４０℃、収縮
率４０％の未延伸ポリエステル繊維（繊度５デニール、
繊維長３８mm、断面円形）４０重量％、及び軟化点な
し、収縮率０.５％のメタ型芳香族ポリアミド繊維（繊
度１.５デニール、繊維長３８mm、断面円形、商品名：
ノーメックス、デュポン製）４５重量％とを使用した以
外は、実施例１と同様にして、目付２５g/m2、厚さ６０
μmの不織布に２５g/m2のジメチルポリシロキサンをコ
ーティングしてクリーニングシートを得た。Comparative Example 3 Softening point 240 ° C., shrinkage 6.
15% by weight of 9% polyester fiber (1.5 denier fineness, fiber length 38 mm, circular cross section), unstretched polyester fiber having a softening point of 240 ° C and a shrinkage of 40% (5 denier fineness,
Meta-type aromatic polyamide fiber having a fiber length of 38 mm and a cross section of 40% by weight and a softening point of 0.5% and a shrinkage of 0.5% (denier 1.5 denier, fiber length 38 mm, circular cross section, trade name:
Nomex, manufactured by DuPont) except that 45% by weight was used in the same manner as in Example 1 except that the basis weight was 25 g / m 2 and the thickness was 60%.
A cleaning sheet was obtained by coating 25 μm / m 2 of dimethylpolysiloxane on a μm nonwoven fabric.
【００４０】（比較例４）実施例１と同様にして得た繊
維ウエブを、温度２１０℃、圧力４０kg/cmで千鳥状
に、繊維ウエブの２８％を部分熱圧着して、目付２５g/
m2、凸部の厚さ１５０μmの不織布に２５g/m2のジメチ
ルポリシロキサンをコーティングしてクリーニングシー
トを得た。Comparative Example 4 A fiber web obtained in the same manner as in Example 1 was staggered at a temperature of 210 ° C. and a pressure of 40 kg / cm, and 28% of the fiber web was partially thermocompressed to obtain a basis weight of 25 g / g.
m 2, and to obtain a cleaning sheet by coating a dimethylpolysiloxane having a thickness of 150μm nonwoven of 25 g / m 2 protrusions.
【００４１】（オイル移行性試験）直径５０mm、回転速
度１８.８ｍ／分、表面温度２００℃の定着装置（キヤ
ノン（株）製、ＮＰ−５０２０）に、実施例１〜６及び
比較例１〜４のクリーニングシートを各々速度０.４５m
m／秒で巻き出し、発泡シリコンゴム（断面円形）から
なる押圧ロールにより、圧力０.１１kg／cm2で押圧し、
定着ロールをクリーニングすると同時に、ジメチルポリ
シロキサンを定着ロールに塗布した。なお、この時、定
着ロールとクリーニングシートとが接触した後に、クリ
ーニングシートから塗布されたジメチルポリシロキサン
を除去するために、目付７８０g/m2、厚み５.５mmの耐
熱フェルト（２×３２cm）を押しあてた。この定着ロー
ルとの接触の前後におけるクリーニングシートの重量か
ら、オイル移行量を測定し、コーティングオイル量に対
するオイル移行量の百分率を計算した。この結果は表１
に示すように、本発明のクリーニングシートはオイル移
行性に優れていることがわかる。(Oil transferability test) A fixing device (NP-5020, manufactured by Canon Inc.) having a diameter of 50 mm, a rotation speed of 18.8 m / min, and a surface temperature of 200 ° C. was applied to Examples 1 to 6 and Comparative Examples 1 to 5. 4 cleaning sheets each 0.45m speed
It is unwound at m / sec and pressed at a pressure of 0.11 kg / cm 2 by a pressing roll made of foamed silicone rubber (circular cross section).
Simultaneously with the cleaning of the fixing roll, dimethylpolysiloxane was applied to the fixing roll. At this time, after the fixing roll comes into contact with the cleaning sheet, a heat-resistant felt (2 × 32 cm) having a basis weight of 780 g / m 2 and a thickness of 5.5 mm was used to remove the dimethylpolysiloxane applied from the cleaning sheet. I pressed it. The oil transfer amount was measured from the weight of the cleaning sheet before and after the contact with the fixing roll, and the percentage of the oil transfer amount to the coating oil amount was calculated. Table 1 shows the results.
As shown in the graph, the cleaning sheet of the present invention is excellent in oil transferability.
【００４２】[0042]
【表１】 [Table 1]
【００４３】（乾熱収縮率測定）２００mm×２００mmに
裁断した、実施例１〜６及び比較例１〜４のクリーニン
グシートを２００℃のオーブン中に１時間放置した後、
クリーニングシートの寸法（ａ(mm)）を測定し、次の式
により乾熱収縮率を計算した。この結果も表１に示すよ
うに、全面的に圧着したクリーニングシート、特に、低
収縮性繊維を使用したクリーニングシートは収縮しにく
いことがわかる。 (Measurement of Dry Heat Shrinkage Ratio) After the cleaning sheets of Examples 1 to 6 and Comparative Examples 1 to 4 cut into 200 mm × 200 mm were left in an oven at 200 ° C. for 1 hour,
The dimensions (a (mm)) of the cleaning sheet were measured, and the dry heat shrinkage was calculated by the following equation. As shown in Table 1, this result also shows that the cleaning sheet completely pressed, particularly the cleaning sheet using the low-shrinkage fiber, hardly shrinks.
【００４４】[0044]
【発明の効果】本発明の定着ロール用クリーニングシー
トは、定着ロール設置箇所の雰囲気温度以上で、かつ定
着ロールの表面温度よりも１００℃高い温度以下で、軟
化する繊維を７０重量％を越えて含む繊維ウエブが、全
面的に圧着された層を有するため、オイル移行性に優
れ、しかも安定してクリーニングできるものである。The cleaning sheet for a fixing roll according to the present invention contains 70% by weight or more of a softening fiber at a temperature not lower than the ambient temperature of the fixing roll installation location and not higher than 100 ° C. higher than the surface temperature of the fixing roll. Since the fiber web contains a layer that is entirely pressed, the oil web has excellent oil transferability and can be stably cleaned.
【００４５】軟化繊維がポリエステル系繊維と未延伸ポ
リエステル繊維であると、定着ロール設置箇所の雰囲気
温度では軟化又は溶融しにくいため好適に使用でき、２
００℃における収縮率が２％以下の繊維を、５重量％以
上含んでいると、定着ロールをクリーニングする際に収
縮しにくいため、より安定してクリーニングできるクリ
ーニングシートである。更に、前記軟化繊維を７０重量
％を越えて含む繊維ウエブが、表面層を構成していると
効率的にオイルを塗布でき、前記２００℃における収縮
率が２％以下の繊維を主体とする層を含んでいると、安
定してクリーニングすることができる。 The softened fiber is made of polyester fiber and undrawn
Since it is hard to be softened or melted at the ambient temperature of the fixing roll installation place, it is preferable to use a
If the fiber contains 5% by weight or more of a fiber having a shrinkage rate of 2% or less at 00 ° C., it is difficult to shrink when the fixing roll is cleaned, so that the cleaning sheet can be more stably cleaned. Further, the softened fiber is 70 weight
% Of the fiber web constitutes the surface layer
Oil can be applied efficiently and shrink at 200 ° C
If a layer mainly composed of fibers with a rate of 2% or less is included,
Cleaning.
【００４６】本発明のクリーニング装置は、上記定着ロ
ール用クリーニングシートの、よりオイル移行性の高い
表面が定着ロールと接触するように巻き出す手段と、ク
リーニングシートの定着ロールへの押圧手段と、クリー
ニングシートの巻き取り手段とを有するため、オイル移
行性に優れ、安定してクリーニングできる装置である。The cleaning device according to the present invention comprises: means for unwinding the cleaning sheet for a fixing roll so that the surface having a higher oil transferability contacts the fixing roll; means for pressing the cleaning sheet against the fixing roll; Since the apparatus has a sheet winding means, the apparatus has excellent oil transferability and can be stably cleaned.
【図１】 クリーニング装置の一例の断面図FIG. 1 is a cross-sectional view of an example of a cleaning device.
１ クリーニングシート ２ 巻出しシャフト ３ 巻取りシャフト ４ 押圧ロール ５ 定着ロール DESCRIPTION OF SYMBOLS 1 Cleaning sheet 2 Unwinding shaft 3 Rewinding shaft 4 Press roll 5 Fixing roll
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平４−83283（ＪＰ，Ａ) 特開 平６−167903（ＪＰ，Ａ) 特開 平６−167902（ＪＰ，Ａ) 特開 平３−63683（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) G03G 13/20 G03G 15/20 D04H 1/42 D04H 1/54 ──────────────────────────────────────────────────続 き Continuation of the front page (56) References JP-A-4-83283 (JP, A) JP-A-6-167903 (JP, A) JP-A-6-167902 (JP, A) JP-A-3-167 63683 (JP, A) (58) Field surveyed (Int. Cl. 7 , DB name) G03G 13/20 G03G 15/20 D04H 1/42 D04H 1/54
Claims (6)
巻き出し、押圧手段により定着ロールに押圧して、定着
ロール表面をクリーニングすると同時にオイルを塗布
し、巻き取るクリーニング装置に使用するクリーニング
シートにおいて、定着ロール設置箇所の雰囲気温度以上
で、かつ定着ロールの表面温度よりも１００℃高い温度
以下で、軟化する繊維（以下、「軟化繊維」ということ
がある）を７０重量％を越えて含む繊維ウエブが、全面
的に圧着された層を有し、前記軟化繊維としてポリアミ
ド系繊維、ポリエステル系繊維、アクリル系繊維、ビニ
ロン系繊維、ポリフェニレンサルファイド繊維から選ば
れる繊維と、未延伸ポリエステル繊維、未延伸ポリフェ
ニレンサルファイド繊維から選ばれる繊維とを含むこと
を特徴とする定着ロール用クリーニングシート。1. A cleaning sheet for use in a cleaning device for unwinding an oil-containing cleaning sheet, pressing the fixing sheet against a fixing roll by pressing means, cleaning the fixing roll surface, and simultaneously applying and winding oil. A fiber web containing more than 70% by weight of a softening fiber (hereinafter, sometimes referred to as “softened fiber”) at a temperature equal to or higher than the ambient temperature of the installation location and equal to or lower than 100 ° C. higher than the surface temperature of the fixing roll, Having a layer which is entirely pressed, and the softening fiber is polyamide
Fiber, polyester fiber, acrylic fiber, vinyl
Ron fiber, polyphenylene sulfide fiber
Fibers, undrawn polyester fibers, undrawn
Including fibers selected from nylene sulfide fibers
Cleaning Sheets fixing roll according to claim.
ポリエステル繊維であることを特徴とする請求項１記載
の定着ロール用クリーニングシート。2. The softened fiber is not drawn with a polyester fiber.
The cleaning sheet for a fixing roll according to claim 1, wherein the cleaning sheet is a polyester fiber .
維を、繊維ウエブ中、５重量％以上含んでいることを特
徴とする請求項１又は請求項２記載の定着ロール用クリ
ーニングシート。3. The cleaning sheet for a fixing roll according to claim 1, wherein the fiber web contains 5% by weight or more of fibers having a shrinkage rate of 2% or less at 200 ° C.
繊維ウエブが、表面層を構成していることを特徴とすThe fiber web constitutes a surface layer.
る、請求項１〜３のいずれかに記載の定着ロール用クリ4. The fixing roll according to claim 1,
ーニングシート。Training sheet.
の繊維を主体とする層を含んでいることを特徴とする、Characterized by comprising a layer mainly composed of fibers of
請求項３又は請求項４に記載の定着ロール用クリーニンThe cleaning roll for a fixing roll according to claim 3.
グシート。Good sheet.
ール用クリーニングシートの、よりオイル移行性の高い
表面が定着ロールと接触するように巻き出す手段と、ク
リーニングシートの定着ロールへの押圧手段と、クリー
ニングシートの巻き取り手段とを有することを特徴とす
るクリーニング装置。 6. A means for unwinding the cleaning sheet for a fixing roll according to claim 1 so that a surface having higher oil transferability comes into contact with the fixing roll, and applying the cleaning sheet to the fixing roll. A cleaning device comprising: a pressing unit; and a cleaning sheet winding unit.