JP3073181B2 - Shading material - Google Patents
Shading materialInfo
- Publication number
- JP3073181B2 JP3073181B2 JP09211396A JP21139697A JP3073181B2 JP 3073181 B2 JP3073181 B2 JP 3073181B2 JP 09211396 A JP09211396 A JP 09211396A JP 21139697 A JP21139697 A JP 21139697A JP 3073181 B2 JP3073181 B2 JP 3073181B2
- Authority
- JP
- Japan
- Prior art keywords
- light
- sheet
- shape
- water
- slit
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、遮光資材に関し、
詳しくは遮光性、通気性に優れ、シートが伸びることな
くシート上面に溜った水を排出可能でありかつシート下
面からの熱逃げを防止する遮光資材に関する。TECHNICAL FIELD The present invention relates to a light shielding material,
More specifically, the present invention relates to a light-shielding material having excellent light-shielding properties and air permeability, capable of discharging water accumulated on the upper surface of the sheet without stretching the sheet, and preventing heat from escaping from the lower surface of the sheet.
【０００２】[0002]
【従来の技術】農業用の遮光資材、特にハウス内で用い
られる遮光カーテンは、昼間の強力な太陽光線と熱を遮
光する遮光性と、夜間にハウス内の温度を逃さず保温す
る保温性が求められている。2. Description of the Related Art A light-shielding material for agriculture, particularly a light-shielding curtain used in a house, has a light-shielding property for blocking strong sunlight and heat during the day and a heat-retaining property for keeping the temperature inside the house at night without losing the temperature. It has been demanded.
【０００３】従来、このような農業用の遮光資材とし
て、熱可塑性樹脂フィルムが用いられていた。しかし熱
可塑性樹脂フィルムは保温性には優れているが、通気性
に欠けるため、日中にハウス内の温度が過度に上昇して
しまうことを防止できないという問題があった。Conventionally, thermoplastic resin films have been used as such agricultural light-shielding materials. However, although the thermoplastic resin film is excellent in heat retention, it lacks air permeability, so that there is a problem that it is impossible to prevent the temperature inside the house from excessively rising during the day.
【０００４】このため、通気性に優れた農業用の遮光資
材として、実開平６−６４４４５号では、フラッシュ紡
糸法による不織布シートを用いる例が開示されている。
フラッシュ紡糸法による不織布シートは、高い遮光効
果、通気性、透湿性、保温性を有するため、日中にハウ
ス内の気温を過度に上昇することを防止し、かつ夜間に
は保温することが可能である。For this reason, Japanese Unexamined Utility Model Publication No. 6-64445 discloses an example of using a nonwoven fabric sheet by flash spinning as an agricultural light-shielding material having excellent air permeability.
The non-woven fabric sheet made by flash spinning has a high light-shielding effect, air permeability, moisture permeability, and heat retention, so it is possible to prevent the temperature inside the house from rising excessively during the day and keep it warm at night. It is.
【０００５】一方、一般的にハウス内では内外の気温差
によって内側に凝縮した水滴が付着し、この水滴が遮光
カーテンの上に落下し、そのために遮光カーテン上に大
きな水たまりができ、水の重みによりいわゆる金魚鉢現
象と呼ばれる水溜まりが生じ、遮光カーテンの開閉を困
難にし、また遮光カーテンの耐久性を損い、水分の重さ
に耐え切れずに遮光カーテンが破れた際には農作物に損
害を与えるという問題がある。On the other hand, in a house, generally, water droplets condensed on the inside adhere to the inside due to a difference in temperature between the inside and outside, and the water drops fall on the light-shielding curtain, so that a large puddle is formed on the light-shielding curtain. This creates a pool of water, a so-called fishbowl phenomenon, making it difficult to open and close the blackout curtain, impairs the durability of the blackout curtain, and damages the crop when the blackout curtain breaks without being able to withstand the weight of moisture There is a problem.
【０００６】この問題を解決するために、遮光カーテン
に丸穴を開ける技術が実公平１−１１４６１号に開示さ
れている。この技術によると、熱可塑性樹脂フィルムに
直径１〜６mmの丸穴を開けた例が開示されている。しか
し、同公報第５欄１１〜１３行に記載のように、丸穴の
設置位置は限定されている訳ではなく、また、水平張り
フィルムであっても通常はフィルムにたわみが生じてい
る。従ってフィルムに落ちた水はフィルム全面に均一に
広がることはありえず、水みちができると考えられるの
で、丸穴の一部は水でふさがれるかもしれないが、大部
分の丸穴は水でふさがれることはない。このため、丸穴
の大部分は夜間のシート下面からの熱逃げ防止には寄与
していなかったのである。このことは、上述の実開平６
−６４４４５号に開示された不織布シートを用いても丸
穴である以上、同様の問題が起こる。In order to solve this problem, a technique for making a circular hole in a light-shielding curtain is disclosed in Japanese Utility Model Publication No. 1-11461. According to this technique, an example in which a round hole having a diameter of 1 to 6 mm is formed in a thermoplastic resin film is disclosed. However, as described in the fifth column, lines 11 to 13, the positions of the circular holes are not limited, and the film is usually bent even with a horizontally stretched film. Therefore, the water that has fallen on the film cannot spread evenly over the entire surface of the film, and it is thought that water will form, so some of the round holes may be blocked with water, but most of the round holes will be filled with water. It will not be blocked. For this reason, most of the round holes did not contribute to preventing heat from escaping from the lower surface of the seat at night. This is due to the above-mentioned
Even if the nonwoven fabric sheet disclosed in JP-A-64445 is used as a round hole, the same problem occurs.
【０００７】また、実開昭６０−２２１５８号には熱可
塑性樹脂フィルムにフタ付の透孔を設ける例が開示され
ている。このフィルムが用いられるハウス外張以外の被
覆用途で農業用として用いられている熱可塑性樹脂フィ
ルムとしては、軟質の塩化ビニルフィルム（いわゆる農
ビ）とポリオレフィン系フィルム（農ポリ、農酢ビ、農
ＰＯ）であり、その厚みは５０〜７５μm程度が一般的
であり、この５０〜７５μm程度の厚みの熱可塑性樹脂
フィルムのようにいわゆる「腰のない軟質もの」では、
水がフィルム上部に溜ると伸びてしまい、たとえフタ付
の透孔であっても使用するにつれ透孔が開いたまま閉じ
なくなるという問題がある。Japanese Utility Model Application Laid-Open No. 60-22158 discloses an example in which a thermoplastic resin film is provided with a through hole with a lid. As thermoplastic resin films used for agriculture in coating applications other than house lining where this film is used, soft vinyl chloride films (so-called agricultural plastics) and polyolefin-based films (agricultural plastics, agricultural vinegars, agricultural plastics, etc.) PO), the thickness of which is generally about 50 to 75 μm, and in a so-called “soft body without rigidity” such as a thermoplastic resin film having a thickness of about 50 to 75 μm,
When water accumulates on the upper part of the film, the water elongates, and there is a problem that even if the through hole is provided with a lid, the through hole is open and cannot be closed as it is used.
【０００８】[0008]
【発明が解決しようとする課題】そこで、本発明は、遮
光性、通気性に優れ、シートが伸びることなくシート上
面に溜った水を排出可能でありかつシート下面からの熱
逃げを防止する遮光資材を提供することを課題とする。SUMMARY OF THE INVENTION Accordingly, the present invention is directed to a light-shielding device which is excellent in light-shielding properties and air permeability, can discharge water accumulated on the upper surface of the sheet without stretching, and prevents heat from escaping from the lower surface of the sheet. The task is to provide materials.
【０００９】[0009]
【課題を解決するための手段】上記課題を解決する本発
明に係る遮光資材は、フラッシュ紡糸法により形成され
た不透水性の不織布シートにおいて、該不織布シートに
スリットを複数設けてなり、該スリットは、シート展張
時には実質的に間隙が生じておらず太陽光線の透過及び
該シート下面からの熱逃げを防止し、かつ該シート上面
に水が溜った際に水を排出可能である細い切線からなる
ことを特徴とする。Means for Solving the Problems] shielding materials according to the present invention for solving the above problems is the water-impermeable nonwoven fabric sheet formed by flash spinning, the nonwoven fabric sheet
A plurality of slits are provided, and the slits
Sometimes there is virtually no gap and sunlight transmission and
To prevent heat from escaping from the lower surface of the seat, and
<Tb> ____________________________________________________________________________________________________________________________________________________________________________________________________________________________________________________________________________________________________________________________________________ Rightling can be able to discharge water when water accumulates .
【００１０】好ましい態様としては、不織布シートが、
坪量２０〜１００g/m2、可視光線の反射率６０％以上、
可視光線の透過率２０％以下、通気性１０〜５００秒／
１００ccであることである。In a preferred embodiment, the nonwoven fabric sheet is
Basis weight 20-100 g / m 2 , visible light reflectance 60% or more,
Visible light transmittance 20% or less, air permeability 10 to 500 seconds /
It is 100cc.
【００１１】また、スリットが少なくとも一重線状、二
重線状、ノコ刃状、波型、×状又は＋状から選ばれる形
状であることが好ましい。It is preferable that the slit has a shape selected from at least a single linear shape, a double linear shape, a saw blade shape, a wave shape, a cross shape, and a + shape.
【００１２】[0012]
【発明の実施の形態】本発明の遮光資材は遮光を必要と
する場所であれば広く多用でき、農業用ハウスの外張り
材、ハウス内の遮光カーテン、トンネル栽培、マルチ栽
培その他作物の栽培以外にも広く使用できる。特に好ま
しくは、ハウス内の遮光カーテンとして使用することで
ある。BEST MODE FOR CARRYING OUT THE INVENTION The light-shielding material of the present invention can be widely used as long as light-shielding is required. Can also be widely used. Particularly preferably, it is used as a shade curtain in a house.
【００１３】以下、本発明の実施の形態を図面に基いて
説明する。Hereinafter, embodiments of the present invention will be described with reference to the drawings.
【００１４】図１は本発明の一実施例を示す斜視図であ
る。図１において、１は遮光資材であり、本実施例では
遮光カーテンである。２は不透水性の不織布シートであ
り、３は不織布シート２に設けられたスリットである。
４は遮光資材１を固定し開閉するワイヤーであり、５は
遮光資材１を支持するワイヤーである。６はワイヤー４
に遮光資材１を付ける留め具である。留め具としてはホ
チキスまたはクリップを用いることができる。７は不織
布シート２上に形成される水滞留領域である。FIG. 1 is a perspective view showing an embodiment of the present invention. In FIG. 1, reference numeral 1 denotes a light shielding material, and in this embodiment, a light shielding curtain. Reference numeral 2 denotes a water-impermeable nonwoven fabric sheet, and reference numeral 3 denotes a slit provided in the nonwoven fabric sheet 2.
Reference numeral 4 denotes a wire for fixing and opening and closing the light shielding material 1, and reference numeral 5 denotes a wire for supporting the light shielding material 1. 6 is wire 4
Is a fastener for attaching the light shielding material 1. A staple or clip can be used as the fastener. Reference numeral 7 denotes a water retention area formed on the nonwoven fabric sheet 2.
【００１５】本発明に用いられる不織布シート２はフラ
ッシュ紡糸法により形成された不織布であり、好ましく
は、坪量２０〜１００g/m2、可視光線（波長４００〜７
００nm）の反射率６０％以上、透過率２０％以下（日立
分光光度計U-3210型（積分球式）で測定）、通気性（JI
S P 8117のガーレー法による透気度）１０〜５００秒／
１００ccである不織布シートが用いられる。坪量が２０
〜１００g/m2であると不織布シートとしての強度を保持
でき、いわゆる「腰のある」シートが得られ、度重なる
使用でもスリットが開いたままになることがなく使用で
きる。また反射率の低下防止や、通気性の付与に好まし
く、コスト的にも好ましい。特に好ましい坪量は４０〜
８０g/m2の範囲である。The nonwoven fabric sheet 2 used in the present invention is a nonwoven fabric formed by a flash spinning method, and preferably has a basis weight of 20 to 100 g / m 2 and a visible light (wavelength of 400 to 7).
00 nm) with a reflectance of 60% or more and a transmittance of 20% or less (measured with a Hitachi spectrophotometer U-3210 type (integrating sphere type)), air permeability (JI
Gurley air permeability of SP 8117) 10 to 500 seconds /
A nonwoven sheet of 100 cc is used. 20 basis weight
When it is １００100 g / m 2 , the strength as a nonwoven fabric sheet can be maintained, and a so-called “stiff” sheet can be obtained, which can be used without repeatedly keeping the slit open even after repeated use. Further, it is preferable for preventing a decrease in reflectance and for providing air permeability, and is also preferable in terms of cost. Particularly preferred basis weight is 40 to
It is in the range of 80 g / m 2 .
【００１６】また、可視光線の反射率が６０％以上であ
ると、遮光資材下の気温を３０℃以下に保つことができ
好ましい。好ましい反射率は７５〜１００％である。更
に、可視光線の透過率が２０％以下であると昼間の強力
な太陽光線から作物を守り、作物の育成に好ましい環境
を与えることができる。更に好ましい透過率は１０％以
下である。It is preferable that the visible light reflectance is 60% or more because the temperature under the light-shielding material can be kept at 30 ° C. or less. The preferred reflectance is 75-100%. Further, if the visible light transmittance is 20% or less, the crop can be protected from strong sunlight in the daytime and a favorable environment for growing the crop can be provided. Further preferred transmittance is 10% or less.
【００１７】更にまた、通気性が１０〜５００秒／１０
０ccであると、不織布シート自体の強度を保持でき、高
反射率を維持する上で好ましい。また、水分蒸発による
放熱効果も期待できる。好ましい通気性は５０〜１００
秒／１００ccである。Furthermore, the air permeability is 10 to 500 seconds / 10
When it is 0 cc, the strength of the nonwoven fabric sheet itself can be maintained, and this is preferable in maintaining a high reflectance. In addition, a heat radiation effect by water evaporation can be expected. Preferred breathability is 50-100
Seconds / 100 cc.
【００１８】本発明の不織布シート２としては、熱可塑
性樹脂を原料としてフラッシュ紡糸法により形成された
ものが好ましく用いられる。不織布シートをフラッシュ
紡糸法により形成すると、高密度で強度保持に優れたシ
ートが得られる。本発明において好ましいシートの強度
としてはJIS L 1906による引張強度が２〜１００kgfの
範囲である。As the nonwoven fabric sheet 2 of the present invention, a nonwoven fabric sheet formed by a flash spinning method using a thermoplastic resin as a raw material is preferably used. When the nonwoven fabric sheet is formed by flash spinning, a sheet having high density and excellent strength retention can be obtained. The preferred sheet strength in the present invention is a tensile strength according to JIS L 1906 in the range of 2 to 100 kgf.
【００１９】熱可塑性樹脂としては、ポリエチレン（特
に高密度ポリエチレン）、ポリプロピレン、ポリエステ
ル、ポリアミド等およびこれらの共重合体等の熱可塑性
樹脂を用いることができる。これらの樹脂は単独で、ま
たは混合して使用することができる。強度、耐久性、価
格の点では高密度ポリエチレンが望ましい。As the thermoplastic resin, thermoplastic resins such as polyethylene (especially high-density polyethylene), polypropylene, polyester, polyamide, and copolymers thereof can be used. These resins can be used alone or as a mixture. High-density polyethylene is desirable in terms of strength, durability, and price.
【００２０】不織布の繊維の太さは特に限定されない
が、反射率を向上させるには出来るだけ細い方がよい。
一般的には0.1〜１０μm程度、望ましくは0.1〜0.5μm
程度が適当である。The thickness of the fibers of the nonwoven fabric is not particularly limited, but it is preferable that the fibers be as thin as possible to improve the reflectance.
Generally about 0.1 to 10 μm, desirably 0.1 to 0.5 μm
The degree is appropriate.
【００２１】本発明においてスリットとは、不織布シー
ト２上面に溜った水を排出可能でありかつ不織布シート
２下面からの熱逃げを防止するものであり、不織布シー
ト２に複数設けられている。スリット３は太陽光線や熱
を通すことのない細い切線であり、遮光資材をハウス内
カーテンとして展張した場合には、実質的に間隙が生じ
ていない。従って、本発明の不織布シート２の上面にハ
ウス天井から水分が落下すると、不織布シート２上で水
滞留領域７が形成されるが、水は界面張力によって水膜
を形成し、スリット３を閉塞する。しかし、更に水滞留
領域７が大きくなった時にはスリット３から水分が排出
可能であり、この状況を繰り返すことによっていわゆる
金魚鉢現象は回避される。一方、水滞留領域７が形成さ
れないスリット３は実質的に間隙が生じていないので、
不織布シート２下面からの熱逃げは防止される。In the present invention, a plurality of slits are provided on the nonwoven fabric sheet 2 so as to discharge water accumulated on the upper surface of the nonwoven fabric sheet 2 and to prevent heat from escaping from the lower surface of the nonwoven fabric sheet 2. The slit 3 is a thin cut line that does not allow sunlight or heat to pass through, and substantially no gap is formed when the light-shielding material is extended as a curtain in a house. Accordingly, when water drops from the house ceiling onto the upper surface of the nonwoven fabric sheet 2 of the present invention, a water retention area 7 is formed on the nonwoven fabric sheet 2, but water forms a water film due to interfacial tension and closes the slit 3. . However, when the water retention area 7 is further enlarged, moisture can be discharged from the slit 3, and the so-called fishbowl phenomenon can be avoided by repeating this situation. On the other hand, since the slit 3 in which the water retention region 7 is not formed has substantially no gap,
Heat escape from the lower surface of the nonwoven fabric sheet 2 is prevented.
【００２２】スリット３から不織布シート２上面に溜っ
た水、即ち水滞留領域７の水を排出する方法としては、
前述したように自然に排出する方法以外にも、不織布シ
ート２に衝撃を与えることによって人為的に排出する方
法もある。具体的には、展張しているハウス内カーテン
を開閉する時にスリット３の両側にずれが生じて開口を
形成し水を排出する方法や、展張している不織布シート
２を下方から棒等で揺さぶることである。As a method of discharging water accumulated on the upper surface of the nonwoven fabric sheet 2 from the slit 3, that is, water in the water retaining area 7,
In addition to the method of naturally discharging as described above, there is also a method of artificially discharging the nonwoven fabric sheet 2 by giving an impact to the nonwoven sheet 2. Specifically, when opening and closing the curtain of the house that is being extended, a gap occurs on both sides of the slit 3 to form an opening and drain water, or the extending nonwoven fabric sheet 2 is shaken from below with a stick or the like. That is.
【００２３】このため、本発明の遮光資材は、昼間は、
太陽光線を反射し、光と熱を遮断し、かつ通気性に優れ
ているので、過度に内部の温度を上昇させることがな
く、夜間には内部の熱を放出することなく保温性に優れ
ているのである。For this reason, the light-shielding material of the present invention
Reflects sunlight, blocks light and heat, and has excellent ventilation, so it does not excessively raise the internal temperature and excels in heat retention without releasing internal heat at night. It is.
【００２４】本発明におけるスリット３としては、一重
線状、二重線状、ノコ刃状、波型、×状又は＋状から選
ばれる形状であることが好ましい。なお、これらの形状
の２種以上を組み合わせてもよい。The slit 3 in the present invention preferably has a shape selected from a single linear shape, a double linear shape, a saw blade shape, a wave shape, a cross shape, and a + shape. Note that two or more of these shapes may be combined.
【００２５】スリット３が一重又は二重の線状の場合に
は、その長さは５〜５０mmが好ましい。スリット３が上
記の範囲内の長さであると、水滞留領域７の水を排出可
能でありかつ不織布シート２下面からの熱逃げの防止が
可能であり好ましい。スリット３が線状の場合には、ス
リット３の方向は特に限定されず遮光部材１の開閉方向
に対し、平行、直角、斜めのいずれの方向でもよい。図
１の例では、スリット３の長手方向は、遮光部材１の開
閉方向と同じ方向に設けられている。When the slit 3 has a single or double linear shape, its length is preferably 5 to 50 mm. When the length of the slit 3 is within the above range, it is preferable because the water in the water retaining area 7 can be discharged and the heat can be prevented from escaping from the lower surface of the nonwoven fabric sheet 2. When the slit 3 is linear, the direction of the slit 3 is not particularly limited, and may be any direction parallel, perpendicular, or oblique to the opening and closing direction of the light shielding member 1. In the example of FIG. 1, the longitudinal direction of the slit 3 is provided in the same direction as the opening and closing direction of the light shielding member 1.
【００２６】図１の例において、同列のスリット３、３
・・・・・におけるその一つのスリット３とこれに隣接
するスリット３の間隔は５ｃｍ〜５０ｃｍ（各々のスリ
ットの中心間の距離Ｌ1）の範囲が好ましい。In the example shown in FIG.
It is preferable that the distance between the one slit 3 and the slit 3 adjacent to the slit 3 in 5... Is in the range of 5 cm to 50 cm (distance L 1 between the centers of the slits).
【００２７】また、一つの列に存するスリットと他の隣
接する列に存するスリットの距離（列間距離Ｌ2）は、
５〜５０ｃｍが好ましい。The distance between the slits in one row and the slits in another adjacent row (inter-row distance L 2 ) is:
5 to 50 cm is preferred.
【００２８】図１の例は一重線状のスリットについて示
しているが、二重線状のスリットの場合も同様に中心間
距離、列間距離を設けることが好ましい。尚、二重線間
の距離は、５〜２０ｍｍの範囲が好ましい。Although the example of FIG. 1 shows a single-line slit, it is preferable to provide a center-to-center distance and a column-to-row distance also for a double-line slit. The distance between the double lines is preferably in the range of 5 to 20 mm.
【００２９】一重線状あるいは二重線状のスリットを形
成する場合、図２のように千鳥状にすることも好ましい
ことである。When forming a single-line or double-line slit, it is preferable that the slit is formed in a staggered shape as shown in FIG.
【００３０】スリット３がノコ刃状（図３）、波型（図
４）である場合、ノコ刃の数や波の数は特に限定されな
いが、１つのスリットにおいて２〜５個が好ましい。When the slit 3 has a saw blade shape (FIG. 3) and a wave shape (FIG. 4), the number of saw blades and the number of waves are not particularly limited, but two to five slit blades are preferable.
【００３１】スリット３が×状（図５）または＋状（図
６）である場合には、その１本の切目の長さは２０mm以
下であることが好ましい。When the slit 3 has an X shape (FIG. 5) or a + shape (FIG. 6), the length of one cut is preferably 20 mm or less.
【００３２】スリット３は上述した形状以外に、本発明
の課題を解決する範囲において他の形状であってもよ
く、Ｔ字形、三角形、半円等でもよい。In addition to the above-mentioned shape, the slit 3 may have another shape as long as the object of the present invention is solved, and may be a T-shape, a triangle, a semicircle, or the like.
【００３３】不織布シート２にスリット３を設ける方法
としては、適当な刃型具により突刺切開したり、持具を
加熱して溶開したり、持具の摺り合わせ（ハサミの原
理）を利用して切開する等の方法がある。The slits 3 are provided in the nonwoven fabric sheet 2 by piercing and incising with an appropriate blade, by heating and melting the holding tool, or by rubbing the holding tool (scissors principle). And incision.
【００３４】スリット３は一定の間隔で設けられてもよ
いし、ランダムに設けられてもよい。好ましくは、１m2
に付き１個以上のスリットがあることであり、より好ま
しくは、１m2に付き１０〜１００個である。The slits 3 may be provided at regular intervals or may be provided at random. Preferably, 1 m 2
It is that there is one or more slits per, more preferably 10 to 100 per 1 m 2.
【００３５】本発明の遮光資材１は、遮光効果を更に高
めるために、内側になる面を光吸収性のある色に印刷等
により着色することもできる。光吸収性のある色とは、
黒、青、緑等であるが、好ましくは遮光性に優れた黒色
である。In the light-shielding material 1 of the present invention, in order to further enhance the light-shielding effect, the inner surface can be colored by printing or the like to have a light-absorbing color. What is a light-absorbing color?
The color is black, blue, green, or the like, and is preferably black having excellent light-shielding properties.
【００３６】また、遮光資材１の内面側を銀色印刷やア
ルミ蒸着によりシルバー色面にすると、夜間の保温効果
を向上することができる。When the inner surface of the light-shielding material 1 is made silver by silver printing or aluminum deposition, the heat retention effect at night can be improved.
【００３７】更に、本発明の遮光資材は、基本的に白色
で可視部反射性が大変大きく、本質的に紫外線の反射率
も高いために、有翅アブラムシ、ミナミキイロアザミウ
マ等の飛来が少なく、ウイルス性病害発生等を最小限に
抑止する効果も具備している。また、本発明の遮光資材
は不透水性であるので、シートが水分を吸収し、こけが
発生することはほとんどない。Further, the light-shielding material of the present invention is basically white, has a very large visible portion reflectivity, and has essentially a high reflectance of ultraviolet rays, so that winged aphids and Thrips palmi are less likely to fly. It also has the effect of minimizing the occurrence of viral diseases and the like. Further, since the light-shielding material of the present invention is water-impermeable, the sheet absorbs moisture and moss is hardly generated.
【００３８】本発明に用いられる不織布シートに撥水処
理を行ってもよく、撥水処理を行う方法は特に限定され
ない。また、本発明の遮光資材は、不織布シートに各種
熱可塑性樹脂製のフィルムやネット等を積層してもよ
い。The nonwoven fabric sheet used in the present invention may be subjected to a water-repellent treatment, and the method for performing the water-repellent treatment is not particularly limited. The light-shielding material of the present invention may be formed by laminating various thermoplastic resin films or nets on a nonwoven fabric sheet.
【００３９】[0039]
【実施例】本発明の実施例について説明する。かかる実
施例によって本発明が限定されるものではない。An embodiment of the present invention will be described. The present invention is not limited by such embodiments.
【００４０】実施例１本発明の遮光資材の製造 高密度ポリエチエレンを用い、フラッシュ紡糸法により
不織布シートを製造した。このシートは坪量７０g/m2、
可視光線の反射率９５％、可視光線の透過率１％、通気
性９５秒／１００ccの不透水性の不織布シートである。
またこのシートの引張強度（JIS L 1906）は、縦１４kg
f/５cm、横１１．２kgf/５cmであった。このシートの面
積は１００m2となるようにし、１m2あたり２５個の線状
のスリットを打抜刃型を用いて形成した。スリットの長
さは１５mmとなるようにした。Example 1 Production of a light-shielding material of the present invention A nonwoven fabric sheet was produced by flash spinning using high-density polyethylene. This sheet has a basis weight of 70 g / m 2 ,
It is a water-impermeable nonwoven sheet having a visible light reflectance of 95%, a visible light transmittance of 1%, and air permeability of 95 seconds / 100 cc.
The tensile strength (JIS L 1906) of this sheet is 14 kg in length.
f / 5 cm, width 11.2 kgf / 5 cm. The area of this sheet was set to 100 m 2, and 25 linear slits per 1 m 2 were formed using a punch blade. The length of the slit was set to 15 mm.
【００４１】この不織布シートを試供シート１としてハ
ウス内カーテンとして展張し、ハウス内の夜間の気温変
化について調査した。調査は１２月５日から１２月１５
日まで行った。The nonwoven fabric sheet was spread as a curtain in a house as a sample sheet 1, and the nighttime temperature change in the house was investigated. The survey is from December 5 to December 15
I went until the day.
【００４２】夜間の気温は、夕方５時から測定開始し、
連続記録計で記録し、１０日間測定した。１日のうち温
度が最低になった時の温度を読み取り、１０日間の平均
値を表１に示す。The temperature at night starts to be measured from 5:00 in the evening,
It was recorded on a continuous recorder and measured for 10 days. The temperature when the temperature became the lowest in one day was read, and the average value for 10 days is shown in Table 1.
【００４３】比較のために、スリットの代わりに丸穴
（直径３mm）を１m2あたり２５個設けた以外は本発明と
同様に製造した不織布シートを比較シート１として、同
様の実験を行い、その結果を表１に示す。[0043] For comparison, as a comparative sheet 1 the nonwoven sheet produced in the same manner as in the present invention except that the round hole (diameter 3mm) was provided 25 per 1 m 2 in place of the slits, the same experiment, the Table 1 shows the results.
【００４４】同じく、比較のために丸穴加工をしない不
織布シートを参考シートとして、同様の実験を行い、そ
の結果を表１に示す。For comparison, a similar experiment was conducted using a non-woven sheet without round hole processing as a reference sheet, and the results are shown in Table 1.
【００４５】[0045]
【表１】 [Table 1]
【００４６】表１から、本発明の試供シート１を用いた
場合には、夜間の熱逃げが防止されていることがわか
る。また、作業上問題となるような水滞留領域は存在し
なかった。Table 1 shows that when the sample sheet 1 of the present invention was used, heat escape at night was prevented. Further, there was no water stagnation area that would pose a problem in work.
【００４７】これに対し、比較シート１では、夜間丸穴
から熱がかなり放出されており、また少量の水の滞留に
より一部の丸穴が閉鎖されても大部分の丸穴は開口のま
まであるため、夜間の熱逃げは本発明と比べ大幅に劣る
ことがわかる。On the other hand, in the comparative sheet 1, much heat was released from the round holes at night, and even if some of the round holes were closed due to the accumulation of a small amount of water, most of the round holes remained open. Therefore, it can be understood that heat escape at night is significantly inferior to that of the present invention.
【００４８】また、参考シートでは、水滞留領域が大変
多くなり、いわゆる乳房状（金魚鉢現象）になり、カー
テンの開閉が完全には行えない状態になった。Further, in the reference sheet, the water stagnation area became very large, so-called breast shape (fish bowl phenomenon), and the curtain could not be completely opened and closed.
【００４９】[0049]
【発明の効果】以上の如く、本発明によれば、遮光性、
通気性に優れ、シートが伸びることなくシート上面に溜
った水を排出可能でありかつシート下面からの熱逃げを
防止する遮光資材を提供することができる。As described above, according to the present invention, light shielding properties,
It is possible to provide a light-shielding material having excellent air permeability, capable of discharging water accumulated on the upper surface of the sheet without stretching the sheet, and preventing heat from escaping from the lower surface of the sheet.
【図１】本発明の一実施例を示す斜視図FIG. 1 is a perspective view showing an embodiment of the present invention.
【図２】本発明の他の実施例を示す平面図FIG. 2 is a plan view showing another embodiment of the present invention.
【図３】本発明の他の実施例を示す平面図FIG. 3 is a plan view showing another embodiment of the present invention.
【図４】本発明の他の実施例を示す平面図FIG. 4 is a plan view showing another embodiment of the present invention.
【図５】本発明の他の実施例を示す平面図FIG. 5 is a plan view showing another embodiment of the present invention.
【図６】本発明の他の実施例を示す平面図FIG. 6 is a plan view showing another embodiment of the present invention.
１：遮光資材 ２：不織布シート ３：スリット ４：ワイヤー ５：ワイヤー ６：留め具 ７：水滞留領域 1: light shielding material 2: non-woven fabric sheet 3: slit 4: wire 5: wire 6: fastener 7: water retention area
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) A01G 13/02 A01G 9/14 A01G 9/22 ──────────────────────────────────────────────────続 き Continued on the front page (58) Field surveyed (Int.Cl. 7 , DB name) A01G 13/02 A01G 9/14 A01G 9/22
Claims (3)
性の不織布シートにおいて、該不織布シートに複数のス
リットを設けてなり、該スリットは、シート展張時には
実質的に間隙が生じておらず太陽光線の透過及び該シー
ト下面からの熱逃げを防止し、かつ該シート上面に水が
溜った際に水を排出可能である細い切線からなることを
特徴とする遮光資材。1. A water-impermeable nonwoven sheet formed by a flash spinning method, wherein the nonwoven sheet has a plurality of fibers.
The slit is provided when the sheet is extended.
There is substantially no gap, and the penetration of sunlight and the sea
To prevent heat from escaping from the underside of the
A light-shielding material comprising a thin cut line capable of discharging water when accumulated .
可視光線の反射率６０％以上、可視光線の透過率２０％
以下、通気性１０〜５００秒／１００ccであることを特
徴とする請求項１記載の遮光資材。2. A nonwoven fabric sheet having a basis weight of 20 to 100 g / m 2 ,
Visible light reflectance 60% or more, visible light transmittance 20%
2. The light-shielding material according to claim 1, wherein the air permeability is 10 to 500 seconds / 100 cc.
状、ノコ刃状、波型、×状又は＋状から選ばれる形状で
あることを特徴とする請求項１又は２記載の遮光資材。3. The light-shielding material according to claim 1, wherein the slit has a shape selected from at least a single linear shape, a double linear shape, a saw blade shape, a wavy shape, a cross shape, and a + shape.