JP3060307U - Tiled mortar layered concrete structure - Google Patents
Tiled mortar layered concrete structureInfo
- Publication number
- JP3060307U JP3060307U JP1998008071U JP807198U JP3060307U JP 3060307 U JP3060307 U JP 3060307U JP 1998008071 U JP1998008071 U JP 1998008071U JP 807198 U JP807198 U JP 807198U JP 3060307 U JP3060307 U JP 3060307U
- Authority
- JP
- Japan
- Prior art keywords
- tile
- concrete structure
- mortar layer
- mortar
- joined
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
(57)【要約】
【目的】 美観を有するタイル状モルタル層接合コ
ンクリート構造体
【構成】 コンクリートに高硬度、高強度、高耐磨、色
彩美観を有するタイル状モルタル層を形成せしめ、高強
度に接合してなるタイル状モルタル層コンクリート構造
体。
(57) [Abstract] [Purpose] Tile-like mortar layer-bonded concrete structure with aesthetic appearance [Construction] Tile-like mortar layer with high hardness, high strength, high abrasion resistance, and color aesthetic appearance is formed on concrete to achieve high strength. Tile-like mortar layer concrete structure joined.
Description
【0001】[0001]
本考案は既設又は新設コンクリートの表面にタイル状モルタル層を形成硬化度 、高強度、高耐磨でかつ美観を呈する構造体に広く利用されるものである。 INDUSTRIAL APPLICABILITY The present invention forms a tile-like mortar layer on the surface of existing or new concrete, and is widely used for structures having a high degree of hardening, high strength, high abrasion resistance and aesthetic appearance.
【0002】[0002]
従来はコンクリートに高温でしょう焼成したセラミックタイルをエポキシ系な どの接着剤で貼付け、外観上美観をよくすることを主体とするものが多く見られ るが、コンクリートとタイルとの接合強度が弱く剥離現象が多く見られるなど大 きな問題となっている。また、かかるセラミックタイルは高温で焼成するときC O2が発生し、省エネルギーでクリーンな環境を整備する上で甚だしく逆行する ものとなり好ましくない。これに対して本考案のタイル状モルタル層接合コンク リート構造体は常温硬化型で高接合強度、高硬度、高強度、高耐磨性を有すると ともに、外観状セラミックタイルに匹敵する美観を有し、しかも低価格であるこ とが特徴である。本考案は地球環境にやさしいタイル状モルタル層接合コンクリ ート構造体を提供するものである。Conventionally, ceramic tiles that have been fired at high temperatures are mainly attached with epoxy or other adhesives to improve the appearance of the tiles. This is a major problem with many phenomena. In addition, such ceramic tiles generate CO 2 when fired at a high temperature, and are extremely unfavorable in terms of energy conservation and maintenance of a clean environment. On the other hand, the tile-type mortar layer-joined concrete structure of the present invention is of a room temperature curing type, has high bonding strength, high hardness, high strength, and high abrasion resistance, and has an aesthetic appearance comparable to the appearance of ceramic tiles. It is also characterized by its low price. The present invention provides a tile-like mortar layer-joined concrete structure that is environmentally friendly.
【0003】[0003]
上述したように地球環境にやさしい高接合強度を有する高硬度のタイル状モル タル層接合コンクリート構造体を提供することにある。 As described above, it is an object of the present invention to provide a high-hardness tile-like mortar layer-joined concrete structure having a high joining strength that is friendly to the global environment.
【0004】[0004]
課題を解決するための手段としてタイル状モルタル層接合コンクリート構造体 について説明する。 コンクリートの表面を清浄化した後、エマルジョン型のアクリル系高分子 エマルジョン接合用プライマーを塗布し乾燥した後、セメント、砂利、フライ アッシュ、顔料、けい酸塩水溶液、水とからなる配合体をよく混練りした生モル タルを作り、これを所定の寸法に塗布し表面を平円滑にした後、常温で自然乾 燥せしめ硬化させると高硬度、高強度、高耐磨、高耐環境、色彩美観を有する タイル状モルタル層接合コンクリート構造体となる。即ちこのタイル状モルタル 層が接合した状態でコンクリート構造耐が形成されることになる。このような手 段でタイル状モルタル層接合コンクリート構造体が調整される。 A tile-like mortar layer-joined concrete structure will be described as a means for solving the problem. After cleaning the concrete surface, apply an emulsion-type acrylic polymer primer for emulsion bonding and dry it, then mix well with a mixture of cement, gravel, fly ash, pigment, aqueous silicate solution, and water. After preparing a kneaded raw mortar, applying it to the specified dimensions and smoothing the surface, it is naturally dried at room temperature and cured to obtain high hardness, high strength, high abrasion resistance, high environmental resistance, and color beautiful appearance. It becomes a tile-like mortar layer joint concrete structure. That is, concrete structure resistance is formed in a state where the tile-like mortar layers are joined. The tile-like mortar layer-joined concrete structure is adjusted by such means.
【0005】[0005]
コンクリートに高硬度、高強度、高耐磨、高耐環境、色彩美観を有するタイル 状モルタル層はセメントとフライアッシュやけい酸塩との化学反応作用によるも ので、このタイル状モルタル層とコンクリートとの高接合強度は接合用プライマ ーの接合促進作用によるものと考えられるかくしてタイル状モルタル層接合コン クリート構造体ができることになる。 The tile-like mortar layer, which has high hardness, high strength, high abrasion resistance, high resistance to environment, and color aesthetics, is due to the chemical reaction between cement and fly ash or silicate. It is considered that the high bonding strength is due to the bonding promoting effect of the bonding primer, and thus a tile-like mortar layer bonding concrete structure can be obtained.
【0006】[0006]
図1に基いて本考案の実施例について説明する。 コンクリート1の表面を清浄化し、この清浄面に水エマルジョン型のアク リル系高分子接合用プライマー2を含浸塗布後、常温で自然乾燥させた後、こ れにセメント、砂利、フライアッシュ、弁柄顔料、けい酸アンモニウム塩20% 水溶液、水を1、0 1、5 0、02 0、03 0、02 5、0の比で混 ぜ合わせよく混練りした生モルタル3を調整し、これを厚み3mmに塗布し表 面を平滑にした後、常温で自然乾燥させ硬化反応を進行させる。硬化せしめた 後、高硬度、高強度、高耐磨、かつ赤い色調を有し光沢のあるタイル状のモルタ ル層4が高強度に接合したコンクリート構造体に形成された。硬化反応は速やか に進行し4時間で指触できる硬度になり、1日で充分使用に耐える迄にその特性 が強化される。以後徐々にその強度は増大し一定値となる。 このタイル状モルタル層接合コンクリート構造体5をコンクリート床に適用す るべくその特性である高硬度、高強度、高耐磨、高耐環境、色彩美観について調 べた結果、セラミックタイルに匹敵することがわかった。また、タイルとコンク リートの接合強度は沸騰水(100℃)と常温水(20℃)に繰り返し1時間浸 漬する100回の熱水衝撃試験に耐え剥離破壊は生じなかった、また機械的破壊 試験においても接合面で剥離破壊をおこさず、接合面以外の領域で破壊を生じた 。このことは接合強度が母材強度以上の強度に達していることを示している。 An embodiment of the present invention will be described with reference to FIG. The surface of the concrete 1 is cleaned, and the clean surface is impregnated with a water emulsion type primer 2 for joining an acrylic polymer, and then naturally dried at room temperature, and then cement, gravel, fly ash, and red stalks are added thereto. A pigment, a 20% aqueous solution of ammonium silicate, and water are mixed in a ratio of 1,01,50,200,030,025,0 to prepare a well-kneaded raw mortar 3, which is then thickened. After applying a thickness of 3 mm to smooth the surface, it is naturally dried at room temperature to allow the curing reaction to proceed. After curing, a tile-like mortar layer 4 having high hardness, high strength, high abrasion resistance and a red color and having a gloss was formed into a concrete structure joined with high strength. The curing reaction proceeds rapidly and becomes hard enough to be touched in 4 hours, and its properties are enhanced until it can be used enough in one day. Thereafter, the intensity gradually increases to a constant value. In order to apply this tile-shaped mortar layer-joined concrete structure 5 to concrete floors, the characteristics of the concrete structure, such as high hardness, high strength, high abrasion resistance, high environment resistance and color aesthetics, were examined. all right. The bond strength between the tile and the concrete was 100 hours with hot water (100 ° C) and room temperature water (20 ° C) repeated 100 hours of hot water shock test. Also in the test, peeling failure did not occur on the joint surface, and fracture occurred in a region other than the joint surface. This indicates that the joining strength has reached a strength equal to or higher than the base material strength.
【0007】[0007]
本考案のタイル状モルタル層接合コンクリート構造体は、 1、高硬度、高強度、高耐磨、色彩美観を有するタイル状コンクリート床構造 材に適用できる。 2、色彩美観を有するコンクリート外壁材に適用できる。 3、地球環境にやさしい材料として適用できる。 The tile-type mortar layer-joined concrete structure of the present invention can be applied to a tile-type concrete floor structural material having high hardness, high strength, high abrasion resistance and color aesthetics. 2. It can be applied to concrete exterior wall materials having a beautiful color appearance. 3. Applicable as environmentally friendly materials.
【図1】タイル状モルタル層接合コンクリート構造体概
略図FIG. 1 is a schematic view of a tile-like mortar layer-joined concrete structure.
1 コンクリート 2 接合用プライマー 3 生モルタル 4 タイル状モルタル層 5 タイル状モルタル層接合コンクリート構造体 DESCRIPTION OF SYMBOLS 1 Concrete 2 Joining primer 3 Raw mortar 4 Tile-like mortar layer 5 Tile-like mortar layer joint concrete structure
Claims (2)
エマルジョン接合用プライマーを薄く塗布乾燥してなる
接合層を介して生モルタルを塗布接合硬化せしめてなる
タイル状モルタル層を接合したることを特徴とするタイ
ル状モルタル層接合コンクリート構造体。1. A tile-like mortar layer formed by applying and curing raw mortar on a concrete surface through a bonding layer formed by thinly applying and drying an acrylic polymer emulsion bonding primer. Tile-like mortar layer-joined concrete structure.
料、けい酸塩水溶液、水とからなる混合体をよく攪拌混
練りした生モルタルを所定の形状に塗布し、常温で硬化
してなる高硬度のタイル状モルタル層を形成せしめるこ
とを特徴とする請求項第1項記載のタイル状モルタル層
接合コンクリート構造体。2. A raw mortar obtained by mixing a mixture of cement, gravel, fly ash, pigment, aqueous solution of silicate and water with good stirring and kneading is applied in a predetermined shape and cured at room temperature to obtain a high hardness. The tile-like mortar layer-joined concrete structure according to claim 1, wherein a tile-like mortar layer is formed.