JP2898104B2 - Striped steel sheet and manufacturing method thereof - Google Patents

Striped steel sheet and manufacturing method thereof

Info

Publication number
JP2898104B2
JP2898104B2 JP2401049A JP40104990A JP2898104B2 JP 2898104 B2 JP2898104 B2 JP 2898104B2 JP 2401049 A JP2401049 A JP 2401049A JP 40104990 A JP40104990 A JP 40104990A JP 2898104 B2 JP2898104 B2 JP 2898104B2
Authority
JP
Japan
Prior art keywords
striped
steel sheet
temperature
steel
low carbon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2401049A
Other languages
Japanese (ja)
Other versions
JPH04210807A (en
Inventor
祥之 高橋
圀彦 片岡
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JFE Steel Corp
Original Assignee
Kawasaki Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kawasaki Steel Corp filed Critical Kawasaki Steel Corp
Priority to JP2401049A priority Critical patent/JP2898104B2/en
Publication of JPH04210807A publication Critical patent/JPH04210807A/en
Application granted granted Critical
Publication of JP2898104B2 publication Critical patent/JP2898104B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【産業上の利用分野】本発明は、極低炭素鋼素材スラブ
を用いた、熱延鋼帯縞鋼板とその製造方法に関する。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a hot-rolled steel striped steel sheet using a very low carbon steel material slab and a method for producing the same.

【0002】[0002]

【従来の技術】縞鋼板に要求される化学成分・機械的性
質は、日本工業規格一般構造用圧延鋼材(JISG310
1)が一般に適用されているが、炭素含有量の低い極低
炭素鋼素材スラブでは、引張強さを満足できず製造でき
ないという問題があった。従って従来炭素含有量が0.04
〜0.08重量%の低炭素鋼素材スラブを用いて製造されて
いた。
2. Description of the Related Art The chemical composition and mechanical properties required for striped steel sheets are based on Japanese Industrial Standards rolled steel for general structures (JIS G310).
Although 1) is generally applied, there is a problem that a very low carbon steel slab having a low carbon content cannot satisfy the tensile strength and cannot be manufactured. Therefore, the conventional carbon content is 0.04
It was manufactured using low carbon steel slabs of ~ 0.08 wt%.

【0003】[0003]

【発明が解決しようとする課題】前述のように従来に低
炭素鋼のみでしか縞鋼板を製造できないため、製鋼段階
の出鋼チャンスや連続鋳造チャンスが制約され、製造工
程期間が長くなるという問題があった。
As described above, since a striped steel sheet can be manufactured only with low-carbon steel in the past, the chance of tapping at the steel making stage and the chance of continuous casting are restricted, and the manufacturing process period is lengthened. was there.

【0004】極低炭素鋼でも縞鋼板を製造できる場合に
は、製鋼の工程期間の短縮がはかられる他に、さらに素
材スラブの適用範囲拡大により省資源がはかれるという
メリットもあるので、本発明は、極低炭素鋼素材スラブ
を用いた縞鋼板とその製造技術を提供するためになされ
たものである。
When striped steel sheets can be manufactured even with extremely low carbon steel, the steelmaking process period can be shortened, and furthermore, there is an advantage that resources can be saved by expanding the applicable range of the material slab. Has been made to provide a striped steel plate using an ultra-low carbon steel material slab and a manufacturing technique thereof.

【0005】[0005]

【課題を解決するための手段】本発明は、熱延鋼帯縞鋼
板とその製造方法において、C含有量が 0.001〜 0.010
重量%の極低炭素鋼素材スラブを用いて、加熱温度:12
00±50℃,仕上ミル出側温度: 900±30℃,巻取り温
度: 450±50℃の圧延温度条件で、製造することを特徴
とする縞鋼板の製造方法である。
According to the present invention, there is provided a striped hot-rolled steel strip and a method for producing the same, wherein the C content is 0.001 to 0.010.
Heating temperature: 12% by weight using ultra low carbon steel slab
This is a method for manufacturing a striped steel sheet, which is manufactured under a rolling temperature condition of 00 ± 50 ° C., a finish mill exit side temperature of 900 ± 30 ° C., and a winding temperature of 450 ± 50 ° C.

【0006】[0006]

【作用】極低炭素鋼素材スラブを用いて種々の熱間圧延
の温度条件で試験した結果、熱間圧延の温度条件を最適
範囲に規制することによって極低炭素鋼素材スラブを用
いても、低炭素鋼素材スラブ並みの品質特性を有する縞
鋼板を製造できるとの知見を得、この知見にもとづいて
本発明をなすに至った。
[Action] As a result of testing under various hot rolling temperature conditions using an ultra-low carbon steel material slab, even if an ultra-low carbon steel material slab is used by regulating the hot rolling temperature condition to an optimum range, The inventor has found that a striped steel sheet having a quality characteristic comparable to that of a low-carbon steel slab can be manufactured, and based on this finding, the present invention has been accomplished.

【0007】極低炭素鋼を素材スラブとして、熱間圧延
条件を表1に示す通り変化させて諸特性を調査した。結
果を表2に示す。JISG3101(日本工業規格一般構造
用圧延鋼材)SS34により縞鋼板に要求される特性を
表3に示すが、これ以外に形状、外観共に良好なものが
要求されるのはもちろんであり、試験結果の表2にはそ
の評価も加えている。
[0007] Using ultra-low carbon steel as a raw material slab, various characteristics were investigated while changing the hot rolling conditions as shown in Table 1. Table 2 shows the results. Table 3 shows the properties required for the striped steel sheet according to JIS G3101 (Japanese Industrial Standards General Rolled Steel for General Structure) SS34. Table 2 also shows the evaluation.

【0008】[0008]

【表1】 [Table 1]

【0009】[0009]

【表2】 [Table 2]

【0010】[0010]

【表3】 [Table 3]

【0011】この試験結果から次のことが明らかになっ
た。加熱温度、仕上ミル出側温度・巻取温度は低い方が
強度は上昇する。一方、仕上ミル出側温度が低い場合、
例えば860 ℃では鋼の相変態近傍のため、圧延中の鋼板
内の温度偏差から、未変態部と変態部が混在して鋼板が
湾曲する現象が表れる。
From the test results, the following has become clear. The strength increases as the heating temperature, finish mill outlet temperature, and winding temperature are lower. On the other hand, when the finish mill outlet temperature is low,
For example, at 860 ° C, since the steel is near the phase transformation, the temperature deviation in the steel sheet during rolling shows a phenomenon in which the untransformed part and the transformed part are mixed and the steel sheet curves.

【0012】しかし、仕上ミル出側温度が、 750℃では
温度が低いために表層スケール(FeO +Fe2O3 +Fe3O
4 )の成長速度が遅く、タイトなスケール被膜が生成せ
ずコイルからシートに切断時、表層スケールが剥離する
問題がある。次に巻取温度は、低い方が強度向上に寄与
する反面、歪不良を発生しやすい。試験No.2,3が
縞鋼板に要求される品質特徴を満足し、かつ形状、外観
共に良好な結果をえたものであり、それ以外の試験N
o.1、4、5、6は縞鋼板として品質特性などが不適
当なものである。次に圧延温度条件を特定した理由を述
べる。
However, when the exit temperature of the finishing mill is 750 ° C., the temperature is low, so the surface scale (FeO + Fe 2 O 3 + Fe 3 O
4 ) The growth rate is slow, and a tight scale film is not formed, and there is a problem that the surface layer scale peels when cutting from the coil to the sheet. Next, the lower the winding temperature, the better the strength, but the more likely it is to cause poor distortion. Test No. Samples No. 2 and No. 3 satisfied the quality characteristics required for the striped steel sheet and obtained good results in both shape and appearance.
o. Nos. 1, 4, 5, and 6 have unsuitable quality characteristics or the like as striped steel plates. Next, the reasons for specifying the rolling temperature conditions will be described.

【0013】加熱温度・後述する仕上ミル出側温度を達
成できる温度が必要であり、1200±50℃と限定した。仕
上ミル出側温度:Ar3 変態点(≒870 ℃)をはずせば、
Ar3 より上でも下でも、圧延は可能であるが、スケール
剥離の点からAr3 より上の 900±30℃とした。
Heating temperature: A temperature capable of achieving the finishing mill outlet temperature described later is required, and the temperature is limited to 1200 ± 50 ° C. Finishing mill outlet temperature: If the Ar 3 transformation point (≒ 870 ° C) is removed,
Even under even above the Ar 3, although rolling is possible, and a 900 ± 30 ° C. above the Ar 3 in terms of scale peeling.

【0014】巻取温度:引張強度を保証するため、 450
±50℃とした。
Winding temperature: 450 to ensure tensile strength
± 50 ° C.

【0015】[0015]

【実施例】表4に成分を示した極低炭素鋼素材スラブ
(260 ×920 ×8300mmを用いて表5の実施例1の圧延温
度条件で、図1に示す縞板ロールを第5スタンド(F−
5)に組み入れて表6のパススケジュールで縞鋼板(コ
イル寸法: 3.1× 924×1mm)を製造した結果、機械的
性質、形状、外観等に低炭素鋼並みの良好な縞鋼板をえ
ることができた。
EXAMPLE Using a very low carbon steel material slab having the components shown in Table 4 (260 × 920 × 8300 mm, under the rolling temperature conditions of Example 1 in Table 5), the striped plate roll shown in FIG. F-
As a result of manufacturing striped steel sheets (coil dimensions: 3.1 × 924 × 1 mm) according to the pass schedule shown in Table 6 by incorporating them into 5), it is possible to obtain striped steel sheets that are as good as low carbon steel in mechanical properties, shape, appearance, etc. did it.

【0016】さらに表5の実施例2、3、4に示す圧延
温度条件で、他は実施例1と同様な条件で縞鋼板を製造
した結果も同時に良好な縞鋼板をえることができた。
Furthermore, striped steel sheets were produced under the same rolling temperature conditions as those of Examples 2, 3 and 4 in Table 5 except for the same conditions as in Example 1, and a good striped steel sheet was obtained at the same time.

【0017】[0017]

【表4】 [Table 4]

【0018】[0018]

【表5】 [Table 5]

【0019】[0019]

【表6】 [Table 6]

【0020】[0020]

【発明の効果】本発明は、従来、低炭素鋼スラブのみで
しか製造できなかった縞板鋼板を、熱間圧延の圧延温度
条件を本発明の規制に従って選定することによって、極
低炭素鋼素材スラブからも製造できるようになった。
According to the present invention, an ultra-low carbon steel material can be obtained by selecting a striped steel sheet which can be conventionally produced only with a low carbon steel slab, by selecting the rolling temperature conditions for hot rolling in accordance with the regulations of the present invention. It can also be manufactured from slabs.

【0021】したがって、製鋼段階での製造工程日数の
短縮がはかれるばかりでなく、素材スラブの適用範囲拡
大により省資源がはかれる。
Therefore, not only the number of days of the manufacturing process in the steelmaking stage can be reduced, but also the resources can be saved by expanding the applicable range of the raw material slab.

【図面の簡単な説明】[Brief description of the drawings]

【図1】縞板ロールを示す図面で(a)は平面図、
(b)はX−X視断面図である。
1A is a plan view showing a striped plate roll, FIG.
(B) is XX sectional drawing.

Claims (2)

(57)【特許請求の範囲】(57) [Claims] 【請求項1】 熱延鋼帯縞鋼板にC含有量が 0.001〜0.
010 重量%の極低炭素鋼を用いたことを特徴とする縞鋼
板。
1. A hot-rolled striped steel sheet having a C content of 0.001 to 0.
A striped steel sheet using 010% by weight of ultra-low carbon steel.
【請求項2】 熱延鋼帯縞鋼板の製造方法において、C
含有量が 0.001〜0.010重量%の極低炭素鋼素材スラブ
を用いて、加熱温度:1200±50℃,仕上ミル出側温度:
900±30℃,巻取り温度: 450±50℃の圧延温度条件
で、製造することを特徴とする縞鋼板の製造方法。
2. A method for producing a strip steel strip with hot strip, comprising the steps of:
Using a very low carbon steel slab with a content of 0.001 to 0.010% by weight, heating temperature: 1200 ± 50 ° C, finish mill outlet temperature:
900 ± 30 ° C, winding temperature: A method for producing striped steel sheets, characterized in that it is produced under rolling temperature conditions of 450 ± 50 ° C.
JP2401049A 1990-12-10 1990-12-10 Striped steel sheet and manufacturing method thereof Expired - Fee Related JP2898104B2 (en)