JP2564195Y2 - Blast furnace tapping lining - Google Patents
Blast furnace tapping liningInfo
- Publication number
- JP2564195Y2 JP2564195Y2 JP7057391U JP7057391U JP2564195Y2 JP 2564195 Y2 JP2564195 Y2 JP 2564195Y2 JP 7057391 U JP7057391 U JP 7057391U JP 7057391 U JP7057391 U JP 7057391U JP 2564195 Y2 JP2564195 Y2 JP 2564195Y2
- Authority
- JP
- Japan
- Prior art keywords
- lining
- blast furnace
- gutter
- furnace tapping
- silicon carbide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【0001】[0001]
【産業上の利用分野】この考案は、高炉出銑樋のライニ
ングに関するものである。BACKGROUND OF THE INVENTION This invention relates to a lining of a blast furnace tapping gutter.
【0002】[0002]
【従来の技術】従来、高炉出銑樋の内張りは、不定形耐
火物の一体構造のライニングであったが、修理の際、溶
損部および周囲の材質劣化部を取り壊す場合、図3のよ
うにブレーカー3で壊した場合、該当箇所以外の場所ま
で崩壊してしまい、修理範囲が拡大し、修理材料が増加
することが多かった。また、特開昭49−9580号公
報に開示されている溶融金属用樋の造築材は、樋のスタ
ンプ材の解体屑の再利用であり、樋の施工および修理方
法は従来の方法であった。特公昭59−1052号公報
に開示されている高炉樋の熱間吹き付け補修方法は、高
炉樋の高温状態のライニングに対して、不定形耐火物を
吹き付ける方法であり、また熱間であるため完全には修
理できなかった。2. Description of the Related Art Conventionally, the lining of a blast furnace tapping gutter has been a lining having an integral structure of an irregular refractory. When it was broken by the breaker 3, it collapsed to a place other than the applicable place, and the repair range was expanded, and the repair material often increased. Further, the construction material of the gutter for molten metal disclosed in Japanese Patent Application Laid-Open No. 49-9580 is to reuse the scrap debris of the stamp material of the gutter, and the construction and repair method of the gutter is a conventional method. Was. A hot blast furnace gutter repair method disclosed in Japanese Patent Publication No. 59-1052 is a method of spraying an amorphous refractory on a lining of a blast furnace gutter in a high temperature state. Could not be repaired.
【0003】[0003]
【考案が解決しようとする課題】本考案が解決しようと
する課題を以下に述べる。 図2に示すように、高炉出銑樋のライニングの溶損箇
所5は、ひょうたん状になり、スラグライン部6のライ
ニングの溶損が極端に大きく、壊す範囲が拡大してしま
う。このため溶損していない部位も壊さざるを得ない。 また図3に示すようにブレーカー3でライニングを壊
そうとするとブレーカーで壊されたライニングのブロッ
ク4のように、内張り煉瓦の境まで損壊してしまう。 本考案は、これらの課題を解決するためになされたもの
である。Problems to be solved by the present invention Problems to be solved by the present invention are described below. As shown in FIG. 2, the erosion site 5 of the lining of the blast furnace tapping gutter has a gourd shape, and the lining of the slag line portion 6 is extremely large in erosion, and the range to be broken is enlarged. For this reason, the parts that have not been damaged must be destroyed. When the lining is broken by the breaker 3 as shown in FIG. 3, the lining block 4 is damaged as in the lining block 4 broken by the breaker. The present invention has been made to solve these problems.
【0004】[0004]
【課題を解決するための手段】本考案は、高炉出銑樋の
不定形耐火物のライニングにおいて、出銑樋側壁のライ
ニングの施工厚みの中間部かつ樋の深さ方向に向かって
埋め込み施工された炭化珪素質煉瓦板を有することを特
徴とする高炉出銑樋のライニングである。SUMMARY OF THE INVENTION The present invention relates to a lining of an irregular refractory for a blast furnace tapping gutter, which is buried in the middle of the thickness of the lining of the tapping gutter side wall and in the depth direction of the gutter. A blast furnace tapping gutter lining characterized by having a silicon carbide brick plate.
【0005】[0005]
【作用】本考案の構成および作用を図面に従って以下に
説明する。 図1に示すように、まず高炉出銑樋に内枠7をセット
し、樋の内張り煉瓦8と内枠7との間に流し込み樋材を
施工する。 流し込み樋材が硬化するまえに壁の上部から炭化珪素
質煉瓦板2を図1のように押し込みセットする。炭化珪
素質煉瓦板の下端は、図2に示すスラグライン部6に位
置するようにする。煉瓦板の上端は、壁の天端より50
mmほど突き出すような位置にする。 使用する炭化珪素質煉瓦板の一例を表1に示す。The structure and operation of the present invention will be described below with reference to the drawings. As shown in FIG. 1, first, the inner frame 7 is set in the blast furnace tapping gutter, and a cast gutter material is constructed between the inner brick 8 and the inner frame 7 of the gutter. Before the pouring gutter material is hardened, the silicon carbide-based brick plate 2 is pushed in from the upper part of the wall as shown in FIG. 1 and set. The lower end of the silicon carbide brick plate is located at the slag line section 6 shown in FIG. The top of the brick plate is 50 from the top of the wall
mm. Table 1 shows an example of the silicon carbide brick plate used.
【表1】 図2に示すように、高炉出銑樋のライニングの溶損箇
所5はひょうたん状になり、特にスラグライン部はスラ
グによって大きく壁を侵食されるが、高耐蝕性の炭化珪
素質煉瓦板で侵食は阻止される。 高炉出銑樋のライニングの修理の場合、先ず図2に示
すようにブレーカー3で炭化珪素質煉瓦板2の内側に沿
って壊すと、壊す範囲は少なくなり簡単に修理ができ
る。[Table 1] As shown in FIG. 2, the erosion site 5 of the lining of the blast furnace tapping gutter becomes a gourd shape, and particularly the slag line portion is greatly eroded by the slag, but is eroded by the highly corrosion-resistant silicon carbide brick plate. Is blocked. In the case of repairing the lining of the blast furnace tapping gutter, if the blast furnace is first broken along the inside of the silicon carbide brick plate 2 with the breaker 3 as shown in FIG.
【0006】[0006]
【実施例】本考案を高炉出銑樋に使用した結果、ライニ
ングの解体箇所も少なく、解体が不必要な場所を壊すこ
ともなく短時間で終了した。EXAMPLE As a result of using the present invention for a blast furnace tapping gutter, the lining was dismantled in a small number of places, and the dismantling was completed in a short time without breaking unnecessary places.
【0007】[0007]
【考案の効果】本考案を高炉出銑樋に使用した結果、ラ
イニングの解体箇所も少なく、解体が不必要な箇所を壊
すことなく短時間で終了し、またライニングの修理費も
減少し、かつ修理が短時間で終了したため、高炉の稼働
率が向上し生産性を高めた。[Effects of the invention] As a result of using the present invention for a blast furnace tapping gutter, the lining is dismantled in a small number of places, the dismantling is completed in a short time without breaking unnecessary parts, and the lining repair cost is reduced, and Since the repair was completed in a short time, the operation rate of the blast furnace was improved and the productivity was increased.
【0008】[0008]
【図1】本考案の施工説明図FIG. 1 is a diagram illustrating the construction of the present invention.
【図2】本考案の修理方法の説明図FIG. 2 is an explanatory view of the repair method of the present invention.
【図3】従来の修理方法の説明図FIG. 3 is an explanatory view of a conventional repair method.
1 高炉出銑樋のライニング 2 炭化珪素質煉瓦板 3 ブレーカー 4 ブレーカーで壊されたライニングのブロック 5 高炉出銑樋のライニングの溶損箇所 6 スラグライン部 7 内枠 8 内張り煉瓦 DESCRIPTION OF SYMBOLS 1 Lining of blast furnace tapping gutter 2 Silicon carbide-based brick plate 3 Breaker 4 Blocking of lining broken by breaker 5 Blast furnace tapping pit lining damaged part 6 Slag line part 7 Inner frame 8 Lining brick
Claims (1)
において、出銑樋側壁のライニングの施工厚みの中間部
かつ樋の深さ方向に向かって埋め込み施工された炭化珪
素質煉瓦板を有することを特徴とする高炉出銑樋のライ
ニング。1. A lining of an irregular-shaped refractory for a blast furnace tapping gutter, comprising a silicon carbide-based brick plate buried in the middle of the thickness of the lining of the tapping gutter side wall and in the depth direction of the gutter. The lining of a blast furnace tapping gutter characterized by that.