JP2702362B2 - Molten container and its repair method - Google Patents
Molten container and its repair methodInfo
- Publication number
- JP2702362B2 JP2702362B2 JP4227844A JP22784492A JP2702362B2 JP 2702362 B2 JP2702362 B2 JP 2702362B2 JP 4227844 A JP4227844 A JP 4227844A JP 22784492 A JP22784492 A JP 22784492A JP 2702362 B2 JP2702362 B2 JP 2702362B2
- Authority
- JP
- Japan
- Prior art keywords
- molten metal
- metal container
- carbon
- refractory
- locally damaged
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION
【０００１】[0001]
【産業上の利用分野】本発明は、溶湯容器及びその補修
方法に関し、詳細には、タンディッシュ、取鍋などの溶
湯容器の内張り材の構造及び該溶湯容器内張り材の局部
損傷部を補修する方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a molten metal container and a method for repairing the molten metal container, and more particularly, to a structure of a lining material of a molten metal container such as a tundish or a ladle, and repairs a locally damaged portion of the lining material of the molten metal container. About the method.
【０００２】[0002]
【従来の技術】タンディッシュ、取鍋などの溶湯容器
は、内張り材が施工されており、この内張り材は、使用
条件により異なるが、ろう石質、ジルコン質、高アルミ
ナ質などの耐火物（耐火レンガ等）が使用されている。
また、溶鋼やスラグによる損傷を防止するため、上記内
張り耐火物上に更に被覆材を設けた内張り構造の溶湯容
器も知られている。2. Description of the Related Art Molten containers such as tundishes and ladles are provided with a lining material. The lining material varies depending on the conditions of use. Refractory bricks).
Further, there is known a molten metal container having a lining structure in which a coating material is further provided on the lining refractory in order to prevent damage by molten steel or slag.
【０００３】ところで、被覆材を使用しないレンガで構
築されたタンディッシュは、通常100〜500チャ−ジ程度
耐用するが、内張りレンガ全体が均一に損傷するのでは
なく、例えば排滓側の側壁の一部や湯当り部などが局部
的に損傷する。この局部的な損傷部分を補修する場合、
この部分のレンガの積替えによる補修法や吹付け材、パ
ッチング材などの不定形耐火物による補修が従来より実
施されている。[0003] A tundish constructed of bricks that do not use a covering material is generally durable for about 100 to 500 charges, but does not damage the entire lining bricks uniformly. Some parts and hot spots are locally damaged. When repairing this localized damage,
Conventionally, a repair method by transshipment of bricks in this portion and a repair by an irregular refractory such as a spraying material and a patching material have been carried out.
【０００４】[0004]
【発明が解決しようとする課題】損傷部のみのレンガ積
替え方式の場合、例えば被覆材を使用せずレンガで内張
りしたタンディッシュでは、被熱温度が高く、また、溶
鋼やスラグが直接このレンガに接触するため、内張レン
ガの一体化現象が著しく、このため、局部損傷部のみの
レンガを解体することは、極めて困難である。[0005] In the case of a brick reloading method of only a damaged portion, for example, in a tundish lined with bricks without using a covering material, the temperature to be heated is high, and molten steel or slag is directly applied to the bricks. Because of the contact, the integration phenomenon of the lining brick is remarkable, and therefore, it is extremely difficult to disassemble the brick having only the locally damaged portion.
【０００５】従って、損傷部だけでなく、その周囲を広
範囲に解体する必要があり、場合によっては片側の側壁
全体の内張りレンガを解体する必要が生ずる。このた
め、解体作業に大きな労力と時間を要すると共に解体不
必要な部分のレンガまで解体する必要があり、極めて不
経済である欠点を有している。[0005] Therefore, it is necessary to dismantle not only the damaged part but also its surroundings over a wide area, and in some cases, it is necessary to dismantle the lining brick on the entire side wall on one side. For this reason, the dismantling operation requires a large amount of labor and time, and it is necessary to dismantle even the portion of the brick that is not necessary for dismantling, which has the disadvantage of being extremely uneconomical.
【０００６】そこで、本発明は、従来の上記欠点を解消
することを技術的課題とし、局部損傷部を部分的に補修
することを目的とする溶湯容器及びその補修方法を提供
するにある。詳細には、本発明の目的は、局部損傷部の
みのレンガをできる限り狭い範囲で容易に解体すること
ができ、この局部損傷部のみを補修可能とする溶湯容器
及びその補修方法を提供するにある。SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide a molten metal container and a method for repairing the molten metal container, which aims at partially repairing a locally damaged portion, with the technical problem of resolving the above-mentioned conventional disadvantages. In detail, an object of the present invention is to provide a molten metal container and a method for repairing a molten metal container that can easily dismantle a brick having only a locally damaged portion within a narrowest possible range and can repair only the locally damaged portion. is there.
【０００７】[0007]
【課題を解決するための手段】そして、本発明は、タン
ディッシュ、取鍋等の溶湯容器において、局部損傷推定
部（局部的に損傷する可能性のある部分）の周辺部のみ
を予めカ−ボン系耐火物で構成することを特徴とし、こ
れによって上記目的を達成したものである。According to the present invention, in a molten metal container such as a tundish or a ladle, only a peripheral portion of a local damage estimating portion (a portion that may be locally damaged) is preliminarily cared. It is characterized by comprising a bon-based refractory, thereby achieving the above object.
【０００８】即ち、本発明の溶湯容器は、「内張り材を
施工してなる溶湯容器において、該溶湯容器内壁の局部
損傷推定部の周辺部をカ−ボン系耐火物で構成してなる
ことを特徴とする溶湯容器。」を要旨とし、また、本発
明の溶湯容器の補修方法は、「内張り材を施工してなる
溶湯容器の局部損傷部を補修する方法において、溶湯容
器内壁の局部損傷推定部の周辺部を予めカ−ボン系耐火
物で構成し、補修時に該周辺部の内側の局部的に損傷し
た内張り材を解体除去し、次に、この除去部分に定形耐
火物又は不定形耐火物を埋込み又は充填することを特徴
とする溶湯容器の補修方法。」を要旨とする。[0008] That is, the molten metal container of the present invention is characterized in that in a molten metal container provided with a lining material, a peripheral portion of a local damage estimating portion on an inner wall of the molten metal container is made of a carbon-based refractory. The method for repairing a molten metal container according to the present invention is a method for repairing a locally damaged portion of a molten metal container provided with a lining material, the method comprising: The periphery of the part is made of a carbon-based refractory in advance, and during repair, the locally damaged lining material inside the periphery is dismantled and removed. A method for repairing a molten metal container, characterized by embedding or filling an object. "
【０００９】以下、本発明を詳細に説明すると、タンデ
ィッシュ、取鍋などの溶湯容器は、前記したとおり、そ
の内張り材全体が溶鋼やスラグにより均一に損傷するも
のではなく、例えば排滓側の側壁の一部や湯当り部など
が局部的に損傷する。本発明では、このように局部的に
損傷した部分を補修することを意図して、局部損傷推定
部（局部的に損傷する可能性のある部分）の周辺部のみ
を予めカ−ボン系耐火物で構成することを特徴とするも
のである。Hereinafter, the present invention will be described in detail. As described above, a molten metal container such as a tundish or a ladle does not have its entire lining material uniformly damaged by molten steel or slag. A part of the side wall and the hot water contact part are locally damaged. In the present invention, in order to repair such a locally damaged portion, only the peripheral portion of the local damage estimating portion (portion that may be locally damaged) is previously carbon-based refractory. It is characterized by comprising.
【００１０】本発明において、カ−ボン系耐火物として
は、例えばカ−ボン又は黒鉛を５ｗｔ％以上含む耐火物
が好ましく、具体的には、カ−ボンを５ｗｔ％以上含有
するＡｌ2Ｏ3−Ｃレンガ又はＭｇＯ−Ｃレンガ等を挙げ
ることができる。また、本発明では、上記カ−ボン系耐
火物で局部損傷推定部の周辺部のみを構築するものであ
るが、この周辺部の形状としては、額縁状、丸状、楕円
状、菱形状など任意の形状とすることができ、また、こ
のカ−ボン系耐火物として、定形又は不定形耐火物を用
いることができる。しかしながら、構築作業の容易性か
ら定形耐火物を用い、額縁状に構築するのがより好まし
い。In the present invention, the carbon-based refractory is preferably, for example, a refractory containing 5% by weight or more of carbon or graphite, and specifically, Al 2 O 3 containing 5% by weight or more of carbon. -C brick or MgO-C brick. Further, in the present invention, only the peripheral portion of the local damage estimating portion is constructed with the above-mentioned carbon-based refractory, but the peripheral portion may have a frame shape, a round shape, an elliptical shape, a diamond shape, or the like. The carbon-based refractory may be any shape, and a regular or irregular refractory may be used. However, it is more preferable to use a fixed refractory and to form the frame in a frame shape from the viewpoint of easiness of the construction operation.
【００１１】上記局部損傷推定部の周辺部以外の内張り
材としては、通常タンディッシュや取鍋などの溶湯容器
用内張り材として使用されている定形耐火物又は不定形
耐火物を任意に適用することができる。これを例示すれ
ば、ろう石質、ジルコン質、高アルミナ質などの定形耐
火物又は不定形耐火物を挙げることができる。As the lining material other than the peripheral portion of the local damage estimating portion, a fixed refractory or an irregular-shaped refractory usually used as a lining material for a molten metal container such as a tundish or a ladle may be arbitrarily applied. Can be. For example, a fixed refractory or an amorphous refractory such as pyroxene, zircon, or high alumina may be used.
【００１２】次に、補修方法について説明すると、溶湯
容器の内張り材が局部的に損傷した場合、この周辺部に
施工されているカ−ボン系耐火物の範囲内の内張り材の
みを解体除去した後、この除去部分に内張り材を新たに
施工する。この施工手段としては、定形耐火物（定形耐
火レンガ）を埋込むか或いは不定形耐火物を充填するこ
とができる。Next, a repair method will be described. When the lining material of the molten metal vessel is locally damaged, only the lining material within the range of the carbon-based refractory applied to the periphery is dismantled and removed. Thereafter, a new lining material is applied to the removed portion. As this construction means, a fixed refractory (a fixed refractory brick) can be embedded or an irregular refractory can be filled.
【００１３】なお、類似の従来技術として、“スラグラ
イン部をカ−ボン5〜30ｗｔ％含有する塩基性レンガと
し、他の部分を石灰質レンガとした取鍋の内張り構造”
が提案されている（実公昭61−42672号公報参照）。し
かしながら、この従来技術は、取鍋のスラグライン部分
の耐用性を改良することを目的としたものであり、本発
明のように局部損傷部を部分的に補修することを意図し
たものではなく、また、本発明のように局部損傷推定部
の周辺部のみをカ−ボン系耐火物で構成したものでな
く、従って、本発明の補修には適用できないものであ
る。[0013] As a similar prior art, a "ladder lining structure in which the slag line portion is made of basic brick containing 5 to 30 wt% of carbon and the other portion is made of calcareous brick"
(See Japanese Utility Model Publication No. 61-42672). However, this prior art is intended to improve the durability of the slag line portion of the ladle, and is not intended to partially repair a locally damaged portion as in the present invention, Further, unlike the present invention, only the peripheral portion of the local damage estimating portion is not made of a carbon-based refractory, and therefore cannot be applied to the repair of the present invention.
【００１４】[0014]
【作用】カ−ボン系耐火物は、耐熱性、耐付着性、耐ヌ
レ性に優れた耐火物であるから、溶湯容器内張り材が局
部的に損傷又は溶損したとしても、また、この内張り材
が前記した一体化現象が生じたとしても、その周辺部に
構築したカ−ボン系耐火物によりこれらの現象が制限さ
れ、全体に波及することがなく、局部的にとどまること
になる。そこで、この部分を補修する場合、周辺部に構
築したカ−ボン系耐火物内の局部損傷部のみの内張り材
が容易に解体除去することができ、従来の局部補修法に
比して補修範囲、補修時間とも改善することができる。[Function] Since carbon-based refractories are excellent in heat resistance, adhesion resistance, and wetting resistance, even if the lining material of the molten metal vessel is locally damaged or melted, this lining is also used. Even if the above-described unification phenomenon occurs in the material, these phenomena are limited by the carbon-based refractory material constructed in the peripheral portion thereof, so that the refractory does not spread to the whole and stays locally. Therefore, when repairing this part, the lining material of only the locally damaged part in the carbon-based refractory constructed in the peripheral part can be easily dismantled and removed, and the repair range is smaller than the conventional local repair method. And the repair time can be improved.
【００１５】[0015]
【実施例】次に、本発明の実施例を図１に基づいて詳細
に説明する。図１は、本発明の実施例を説明するための
図であって、このうち(A)は、タンディッシュの一部切
開部を示す断面図であり、(B)は、(A)の一部切開部の部
分拡大詳細図である。Next, an embodiment of the present invention will be described in detail with reference to FIG. FIG. 1 is a view for explaining an embodiment of the present invention, in which (A) is a cross-sectional view showing a partially cut portion of a tundish, and (B) is a sectional view of (A). It is a partial enlarged detailed view of a partial incision.
【００１６】タンディッシュ１の内張り材の材質として
通常使用されているレンガ２（例えばＡｌ2Ｏ3が85％ク
ラスの高アルミナレンガ）で内張りすると共に局部的に
損傷する部位の周囲をカ−ボン含有定形レンガ３（例え
ばカ−ボン10〜15％を含むアルミナ・カ−ボンレンガ）
で額縁状に築炉する。タンディッシュ１のレンガ２ａが
予測したとおり局部的に損傷すると、その周囲がカ−ボ
ン含有定形レンガ３で額縁状に築炉されているため、そ
の周囲外のレンガ２と一体化することがなく、容易にこ
の損傷したレンガ２ａの部分のみを解体することができ
る。The tundish 1 is lined with a brick 2 (for example, high-alumina brick of 85% class of Al 2 O 3 ) which is usually used as a material of a lining material, and carbon is wound around a locally damaged portion. Content brick 3 (for example, alumina carbon brick containing 10 to 15% carbon)
The furnace is built in a frame shape. If the brick 2a of the tundish 1 is locally damaged as predicted, the surroundings are built in a frame shape with the carbon-containing shaped bricks 3, so that the bricks 2a of the tundish 1 are not integrated with the bricks 2 outside the surroundings. Thus, only the damaged brick 2a can be easily dismantled.
【００１７】この部分を補修する時は、まず、カ−ボン
含有定形レンガ３の額縁を境として、損傷したレンガ２
ａ部分のみを抜掘り解体し、次に、この解体除去部分を
再度定形レンガ２ａで築炉するか或いは不定形耐火物で
補修する。この実施例によれば、局部損傷部のみのレン
ガ２ａをできるだけ狭い範囲で容易に解体除去すること
ができ、そして、この部分のみの補修で足りるメリット
を有する。When repairing this part, first, the damaged brick 2
Only part a is excavated and dismantled, and then the dismantled removed part is rebuilt with a fixed brick 2a or repaired with an irregular refractory. According to this embodiment, it is possible to easily disassemble and remove the brick 2a having only the locally damaged portion in the narrowest possible range, and there is an advantage that repairing only this portion is sufficient.
【００１８】なお、本実施例では、タンディッシュ１に
適用した例について説明したが、本発明は、これのみに
限定されるものでなく、取鍋やそのＳＬ（スラグライ
ン）、その他の溶湯容器にも適用することができる。更
に、本実施例では、局部損傷推定部（局部的に損傷する
可能性のある部分）の周辺部をカ−ボン含有定形レンガ
３で額縁状に築炉することについて説明したが、これ以
外にカ−ボン含有不定形耐火物を用い、額縁状以外の形
状に築炉することもでき、これらも本発明に包含される
ものである。In this embodiment, an example in which the present invention is applied to the tundish 1 has been described. However, the present invention is not limited to this, and a ladle, its SL (slag line), and other molten metal containers are used. Can also be applied. Furthermore, in the present embodiment, a description has been given of a case where the peripheral portion of the local damage estimating portion (portion that is likely to be locally damaged) is built in a frame shape with the carbon-containing shaped bricks 3. Furnace shapes other than picture frames can also be constructed using carbon-containing amorphous refractories, and these are also included in the present invention.
【００１９】[0019]
【発明の効果】本発明は、以上詳記したとおり、局部損
傷推定部（局部的に損傷する可能性のある部分）の周辺
部のみをカ−ボン系耐火物で構成することを特徴とする
ものであり、これにより局部損傷部のみの内張り材をで
きる限り狭い範囲で容易に解体除去することができ、こ
の局部損傷部のみを補修可能とする効果が生ずる。具体
的には、補修範囲については、従来の40〜80％減少させ
ることができ、従来の60〜20％の補修ですむものであ
り、また、補修時間も1／2以下に短縮することができる
効果が生ずる。As described in detail above, the present invention is characterized in that only the peripheral portion of the local damage estimating portion (portion that may be locally damaged) is made of a carbon-based refractory. Accordingly, it is possible to easily disassemble and remove the lining material of only the locally damaged portion in the narrowest possible range, and it is possible to repair only the locally damaged portion. Specifically, the repair area can be reduced by 40-80% compared to the conventional one, and the repair can be reduced by 60-20% compared to the conventional one, and the repair time can also be reduced to 1/2 or less. The effect occurs.
【図１】本発明の実施例を説明するための図であって、
このうち(A)は、タンディッシュの一部切開部を示す断
面図であり、(B)は、(A)の一部切開部の部分拡大詳細図
である。FIG. 1 is a diagram for explaining an embodiment of the present invention,
(A) is a cross-sectional view showing a partially cut portion of the tundish, and (B) is a partially enlarged detailed view of the partially cut portion of (A).
１ タンディッシュ ２、２ａ レンガ ３ カ−ボン含有定形レンガ DESCRIPTION OF SYMBOLS 1 Tundish 2, 2a brick 3 Carbon-containing fixed-size brick
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｆ２７Ｄ 1/04 Ｆ２７Ｄ 1/16 Ｖ 1/16 Ｃ０４Ｂ 35/52 Ｚ (56)参考文献 特開 昭54−96506（ＪＰ，Ａ) 特開 平２−103395（ＪＰ，Ａ) 特開 昭54−43804（ＪＰ，Ａ) 実開 昭63−11158（ＪＰ，Ｕ) 実開 昭64−33363（ＪＰ，Ｕ) 実開 昭56−11253（ＪＰ，Ｕ) 実公 平３−43595（ＪＰ，Ｙ２)──────────────────────────────────────────────────続 き Continuation of the front page (51) Int.Cl. 6 Identification number Agency reference number FI Technical display location F27D 1/04 F27D 1/16 V 1/16 C04B 35/52 Z (56) References JP JP-A-2-103395 (JP, A) JP-A-54-43804 (JP, A) JP-A-63-11158 (JP, U) JP-A-64-33363 (JP, A) U) Japanese Utility Model Showa 56-11253 (JP, U) Japanese Utility Model Publication No. 3-43595 (JP, Y2)
Claims (3)
て、該溶湯容器内壁の局部損傷推定部の周辺部をカ−ボ
ン系耐火物で構成してなることを特徴とする溶湯容器。1. A molten metal container provided with a lining material, wherein a peripheral portion of a local damage estimating portion of an inner wall of the molten metal container is formed of a carbon-based refractory.
状、丸状、楕円状又は菱形状であることを特徴とする請
求項１記載の溶湯容器。2. The molten metal container according to claim 1, wherein a shape of a peripheral portion of the local damage estimating portion is a frame shape, a round shape, an elliptical shape, or a rhombic shape.
損傷部を補修する方法において、溶湯容器内壁の局部損
傷推定部の周辺部を予めカ−ボン系耐火物で構成し、補
修時に該周辺部の内側の局部的に損傷した内張り材を解
体除去し、次に、この除去部分に定形耐火物又は不定形
耐火物を埋込み又は充填することを特徴とする溶湯容器
の補修方法。3. A method for repairing a locally damaged portion of a molten metal container provided with a lining material, wherein a peripheral portion of a locally damaged estimating portion of an inner wall of the molten metal container is formed of a carbon-based refractory material in advance, and the repair is performed at the time of repair. A method for repairing a molten metal container, comprising dismantling and removing a locally damaged lining material inside a peripheral portion, and then embedding or filling a fixed or irregular shaped refractory in the removed portion.