JP2560580B2 - Method for manufacturing high silicon steel sheet having high magnetic permeability - Google Patents

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a high silicon steel sheet by a diffusion and infiltration treatment method of Si, which is a method for producing a high silicon steel sheet having a high magnetic permeability.

[0002]

2. Description of the Related Art Since silicon steel sheets have excellent soft magnetic properties,
Widely used as a core material for transformers and motors. It is known that this type of silicon steel sheet exhibits excellent magnetic properties such that the iron loss is reduced as the Si content increases, and the magnetostriction becomes 0 and the maximum magnetic permeability reaches a peak when the Si content is 6.5 wt%. There is. However, the Si content in the steel is 4.0
If it exceeds wt%, the ductility is drastically reduced, and it is difficult to manufacture it by ordinary rolling. As a method of manufacturing a high-silicon steel sheet that does not cause such a problem, a manufacturing method by a diffusion and penetration treatment method of Si is known. According to this method, a low silicon steel is melted and thinned by rolling, and then a high silicon steel sheet is manufactured by infiltrating Si from the surface. According to this method, Si is contained without causing a problem of workability. Amount 4.
A high silicon steel plate of 0 wt% or more can be obtained.

The production of high silicon steel sheets by this diffusion infiltration treatment method is generally performed by using ordinary steel sheets or low silicon steel sheets (usually Si:
4.0 wt% or less) is subjected to Si infiltration treatment (siliconization treatment) in an atmosphere of non-oxidizing gas containing Si compound such as SiCl ₄ to infiltrate Si from the surface of the steel sheet, and then Si compound Diffusion heat treatment is performed on a steel sheet in a non-oxidizing gas atmosphere containing no oxygen to diffuse the infiltrated Si into the steel sheet to obtain a high silicon steel sheet containing Si uniformly. Regarding such a diffusion and penetration treatment method, for example,
JP-B-45-21181 and JP-A-62-227078
No. etc. have been proposed.

Conventionally, with respect to this type of manufacturing method, various conditions for continuously processing a steel sheet have not been sufficiently examined, and the processing time is as long as 30 minutes or more, the processing temperature is extremely high, and the edge portion is very high. However, there is a problem in that the processing conditions cannot be applied to a continuous line in fact, and stable production in a continuous line of steel sheets cannot be expected. On the other hand, in the above-mentioned Japanese Patent Laid-Open No. 62-227078, etc., a steel sheet is heated and continuously subjected to a siliconizing treatment in an atmosphere of non-oxidizing gas containing SiCl _4, and then a non-oxidizing gas containing no SiCl ₄ is used. We have proposed a method for efficiently manufacturing silicon steel sheets by making into a continuous line a series of processes in which Si is homogenized by diffusion heat treatment in an atmosphere, then cooled and wound into a coil. The reaction gas concentration, reaction time, soaking diffusion treatment time, treatment temperature, and the like were examined and specified in detail, and it became possible to manufacture a high silicon steel sheet by diffusion permeation treatment in a continuous line.

[0005]

However, although such conventional techniques have examined diffusion permeation conditions and methods, no consideration has been given to production conditions of materials that control magnetic properties and their structures. Not done. According to the studies by the present inventors, the structure (texture, crystal grain size) that controls the magnetic permeability of the steel sheet manufactured by this type of manufacturing method is largely controlled by the hot rolling-cold rolling conditions, and the magnetic permeability is In order to improve, it was found that it is essential to optimize the rolling conditions of the raw steel sheet, and thereby to adequately optimize the structure of the raw steel sheet.

[0006]

[Means for Solving the Problems] From the above viewpoints, the present inventors have examined the relationship between the hot-rolled structure of the material steel sheet in the Si diffusion infiltration treatment method, the texture after the Si diffusion infiltration treatment, and the grain size. I went. As a result, in order to stabilize the texture and crystal grain size effective for obtaining the high magnetic permeability of the final product after the diffusion permeation treatment, that is, the (100) plane which is the easy axis of magnetization and the coarsening of the crystal grain size. In addition, the hot rolling finish temperature of the raw steel sheet is 700 ° C or less, and the
It has been found that it is effective to make 0% or more a layered structure which is a non-recrystallized structure. In this case, the winding temperature is 700
No significant difference was observed in the magnetic properties at temperatures below ℃.
In addition, it is possible to confirm that the structure obtained in the material stage is predominantly formed after the siliconizing / diffusion heat treatment by the structure evaluation after the siliconizing / diffusion heat treatment performed in the processing temperature range of 1023 to 1250 ° C. It was The present invention has been made on the basis of such findings, and the constitution thereof is as follows.

(1) Si: 4.0 wt% or less, Sol.
Al: Steel containing 0.1 wt% or less is hot-rolled and cold-rolled to form a thin plate.
In a method for producing a high-silicon steel sheet having Si: 4.0 wt% or more by performing a siliconizing treatment for infiltrating Si, and then diffusing Si in the sheet thickness direction, the hot rolling finishing temperature of the material is set to 7
70% of the hot rolled structure in the plate thickness direction by setting the temperature below 00 ° C
A method for producing a high-silicon steel sheet having high magnetic permeability, which is characterized in that the above has a layered structure that is a non-recrystallized structure, has a predetermined plate thickness by cold rolling, and is then subjected to siliconizing treatment and Si diffusion heat treatment. .

(2) Manufacture of a high silicon steel sheet having a high magnetic permeability according to the above (1), which is characterized in that during the siliconizing treatment, the Si concentration on the surface layer of the steel sheet is always kept to 14.3 wt% or less. Method.

[0009]

In the production of high silicon steel sheet by the Si diffusion and infiltration treatment method, the relationship between the hot rolling conditions and the hot rolling structure of the raw steel sheet and the influence of these on the magnetic properties of the final product were investigated. First, Si: 3 wt%, Sol. Al: 110 pp
The slab of the component of m is heated to 1150 ° C and the finishing temperature is 6
Hot rolling was performed at a plate thickness of about 2 mm at 00 to 860 ° C. and a coiling temperature of 500 to 700 ° C., and the relationship between the hot rolling finish temperature and the hot rolled sheet structure was investigated. As a result, it was found that in the hot-rolled sheet structure having a finishing temperature of 700 ° C. or less, 70% or more in the sheet thickness direction has a layered structure. The photograph in Fig. 1 shows that the finishing temperature is 65
The hot-rolled microstructures in the thickness direction of the hot-rolled sheets at 0 ° C, 700 ° C, 800 ° C, and 860 ° C are shown, and the hot-rolled structure in the thickness direction is 70% or more when the finishing temperature is 700 ° C or lower. It has a layered structure.

Next, the hot rolled sheet is cold-rolled to a sheet thickness of 0.35 mm and then subjected to a siliconizing treatment-diffusion heat treatment to produce a high silicon steel sheet having an average Si content of 6.4 to 6.6 wt%. ,
The relationship between the magnetic permeability and the hot rolling finish temperature of the raw steel sheet was investigated. FIG. 2 shows the results, and the material having a hot rolling finish temperature of 700 ° C. or less of the material steel sheet shows particularly high magnetic permeability. The reason for this is that, as shown in Example 1 to be described later, at a hot rolling finishing temperature of 700 ° C. or less, most of the hot rolled sheet structure becomes a layered structure as described above, so that the grains become coarse and cold rolled-Si diffusion. It is considered that this is because the (100) plane strength after the permeation treatment becomes strong. When the hot rolling finishing temperature is higher than 700 ° C., grain coarsening is not observed and the (111) plane and (211) plane strengths are high, and it is considered that excellent magnetic properties cannot be obtained.

For the above reasons, the present invention has the condition that the hot rolling finish temperature of the raw steel sheet is 700 ° C. or lower so that 70% or more of the hot rolled structure in the sheet thickness direction has a layered structure.

Further, when Si is enriched in the steel sheet by the siliconizing treatment, Fe having a Si concentration of about 14.3 wt% is formed on the surface layer.
_{A 3} Si layer is formed. In this way, Fe ₃ Si is formed on the surface of the steel sheet.
When the layer is formed, the texture tends to decrease the (100) plane strength, and the Fe ₃ Si layer is not formed, that is, the surface Si concentration is always less than 14.3 wt% during the siliconizing treatment. The magnetic properties will be inferior. Therefore, in order to stabilize the (100) plane after the siliconizing / diffusion heat treatment, the Si concentration of the steel sheet surface layer during the siliconizing treatment is always 14.
It is preferable that the treatment be performed so as to be less than 3 wt%. Such a treatment can be realized by controlling the siliconizing treatment speed, specifically, by making the siliconizing treatment speed relatively small and avoiding the rapid siliconizing treatment.

In the present invention, the steel sheet which is the material before the siliconizing treatment is made of Si: 4 wt% or less, Sol. Al: 0.1w
Steel sheet of t% or less, which includes ordinary steel sheet and S
i: 4 wt% or less of non-oriented or grain-oriented silicon steel sheet is included. The present invention can be thinned by rolling Si: 4w
This is a technology based on obtaining a high silicon steel sheet by subjecting a steel sheet of t% or less to a raw material steel sheet and subjecting it to a siliconizing treatment. Therefore, the upper limit of the Si content of the raw material steel sheet is 4.0 wt%. . Further, since Al in the steel sheet is concentrated and segregated in the steel sheet during the siliconizing treatment, and adversely affects the magnetic properties, its upper limit must be strictly defined.

In order to investigate the influence of Al concentration and segregation, S
ol. The steel plates having different Al concentrations are subjected to siliconizing treatment, the average Si amount in the plate thickness direction is 6.4 to 6.6 wt%, and the number of remaining voids in the steel plate cross section that adversely affects the magnetic properties is 1 in the steel plate width direction.
A high silicon steel plate having 5 or less pieces per mm was manufactured. As a result of investigating the occurrence states of Al concentration and segregation in such steel sheets, the steel sheets were roughly classified into Sol. Al concentration is 10
In each case of 0 ppm or less, 0.1% or less, and more than 0.1%, differences in Al concentration and segregation were observed.

That is, according to the IMA image photographs of these steel sheets, the sol. Al concentration is 100ppm
In the following, Al was scattered sparsely and evenly in the steel sheet, and Al concentration and segregation were not observed at all. On the other hand, S
ol. In a steel sheet with an Al concentration of 0.1 wt%, Al begins to be scattered on a straight line, and a concentration tendency is recognized. However, it has not been extremely concentrated or segregated. On the other hand, So
l. In a steel sheet with an Al concentration of 0.3%, Al is connected in a straight line and is concentrated, and the concentrated and segregated portions occupy a considerable area in the steel sheet.

From the relationship between Al concentration, segregation and magnetic properties based on the results of this test, in order to obtain a high silicon steel plate with excellent magnetic properties, Al has a degree of homogeneity scattered in the steel plate. It is necessary to use Sol. It was found that the Al concentration should be 0.1% or less. In particular, in order to obtain a high-silicon steel sheet having a more uniform and excellent magnetic property such that Al is not reflected in an ion image or scattered sparsely and evenly in the steel sheet, Sol. Al concentration is 100
It must be below ppm.

In the conventional silicon steel sheet, a method of replacing a part of Si with Al is used by utilizing the effect of increasing the electric resistance of Al and the effect of improving spreadability. Average Si content easily 6.0-7.0w
Since it can be set to t%, it is not necessary to add Al for improving the magnetism. On the contrary, from the viewpoint described above, Sol. Al: 0.
1 wt% or less, desirably 100 ppm or less.

In the present invention, the impurity components other than Si and Al in the raw steel sheet are not particularly limited, but are preferably defined as follows in order to obtain excellent magnetic properties.

First, the non-metal element will be described. C: C lowers the initial permeability and the maximum permeability, increases Hc, and increases iron loss. It is known that this effect becomes remarkable when it exceeds 0.01 wt%, as shown in FIG. 10. Therefore, it is preferable that C be 0.01 wt% or less. However, in order to improve the crystal orientation, it is possible to contain more than 0.01 wt% of C in the steelmaking stage and roll it. In this case, decarburization annealing is performed to prevent aging and property deterioration. However, it is preferable that C is 0.01 wt% or less. That is, the C concentration may be adjusted at the smelting stage or by performing decarburizing annealing.

O: O is known as an element which enhances iron loss and, when present as colloidal fine particles such as SiO ₂ , significantly deteriorates magnetic properties. O is C
The magnetic characteristics are changed depending on the degree of coexistence with. In particular, as shown in FIG. 11, it is also known that the iron loss value becomes the minimum when the O content and the C content are almost equal to each other, and the O content is similar to the appropriate range of the C content. Is 0.
It is preferable that the content be 01 wt% or less.

N and S: Since both cause aging, it is preferable to reduce them as much as possible.
It is preferable that the content be 01 wt% or less. P: P has a function of reducing magnetic deterioration due to oxygen and reducing iron loss, but when added in a large amount, there is a problem of deteriorating hot workability, and its upper limit is 0.02 wt.
% Is preferable. H: Since H makes the steel sheet extremely brittle, aggressive inclusion such as H under high pressure should be avoided (usually p
pm level). As described above, it is preferable to minimize C, O, N, S, etc., and optimize the ratio of C and O for the nonmetallic elements.

Next, the metal element will be described. Mn: M in consideration of improvement of ductility at the time of hot rolling and improvement of magnetism in desulfurization action and order-disorder transformation.
n is preferably added in a range of 0.5 wt% or less. Ca: If Ca is contained in a large amount, the magnetic permeability is reduced. Therefore, the content is preferably not more than 0.3 wt%.

V: By adding a slight amount of V, Hc
Are known to be improved. That is, V is 0.
Addition of about 05 wt% promotes the development of crystal grains and improves magnetism. Therefore, V is 0.1 wt
% Can be added up to the upper limit. By adding about 0.05 wt% of Ti, the same effect as V can be expected, so that 0.1 wt% can be added as an upper limit. Be, As: A slight magnetic property improving effect can be expected, and 0.1 wt% of each can be added as an upper limit.

Cu: Up to about 0.7 wt%, the magnetism is not significantly deteriorated, but if it exceeds 0.7 wt%, iron loss increases. Therefore, Cu is 0.7 wt.
% Or less, preferably 0.1 wt% or less. Cr: tends to increase iron loss, and is preferably set to 0.03 wt% or less. Ni: To significantly deteriorate magnetic properties, it is preferable to reduce the Ni as much as possible, and it is preferable to set the content to 0.01 wt% or less.

In the present invention, the cold rolling rate is not particularly limited, and the same effect can be obtained in a wide range of 60 to 93%.

[0026]

【Example】

[Example 1] A 3% Si steel having the composition shown in Table 1 was vacuum melted to form a slab, which was hot rolled to a finish temperature of 600 to 86.
Hot rolling at 0 ° C. and coiling temperature: 550 ° C. to 700 ° C. to obtain a hot rolled sheet having a sheet thickness of about 2 mm, and then cold rolling to a sheet thickness of 0.35 mm, and then in a N ₂ or Ar gas atmosphere. Siliconization / diffusion heat treatment was performed to produce a high silicon steel sheet having an average Si amount of 6.4 to 6.6 wt%. In this example, the siliconizing / diffusion heat treatment gave the same result regardless of the atmosphere of N ₂ or Ar. Therefore, the following is a representative example of the case of performing the siliconizing / diffusion heat treatment in the Ar atmosphere. Show.

In FIG. 1, the hot rolling finishing temperature is 650, respectively.
The microscopic enlarged photograph of the sheet thickness direction hot rolled structure of each hot rolled sheet which is ℃, 700 ℃, 800 ℃, 860 ℃ is shown. According to this, in the hot rolled sheet having a hot rolling finishing temperature of 860 ° C., the entire cross section in the sheet thickness direction has a recrystallized structure, and the hot rolling finishing temperature is 800 ° C.
Even in the hot-rolled sheet of No. 3, a recrystallized structure is recognized in a portion (surface layer portion) exceeding 30%. On the other hand, in the hot-rolled sheet having a finishing temperature of 700 ° C. or less, the layered structure which is a non-recrystallized structure accounts for 70% or more. FIG. 2 shows the magnetic properties of the steel sheets (Si content: 6.4 to 6.6 wt%) after the above-mentioned siliconizing / diffusion heat treatment in relation to their hot rolling finishing temperatures. When a raw material steel sheet having a layered structure occupying 70% or more at a temperature of not higher than 0 ° C. is used, a high silicon steel sheet having a high magnetic permeability is obtained.

Further, FIG. 3 shows the relationship between the average grain size of the steel sheet after the siliconizing / diffusion heat treatment and the hot rolling finishing temperature of the raw steel sheet, and FIG. 4 shows the hot rolling finishing temperatures of 650 ° C. and 860 ° C., respectively. The texture of the steel sheet after siliconizing / diffusion heat treatment is shown. The P value shown in FIG. 4 is an evaluation index according to the evaluation method of the texture using X-ray diffraction, and the peaks (7 peaks) of the low-order crystal planes are assumed to be typical crystal orientations. Then, the distribution of crystal planes is statistically shown. Conceptually speaking, the powder sample is taken as a standard sample with a totally random texture, whereby the surface strength is normalized. In this case, each plane direction is 7
Each surface has a value of 1. On the other hand, the plane orientation of an anisotropic texture has a value of 1 or more. In an extreme case, if the material takes only one plane orientation, only that orientation takes a value of 7 and all other planes are 0.
Will be taken. FIG. 4 shows the evaluation of the texture using such an evaluation method.

According to these, when a raw steel sheet in which the layered structure occupies 70% or more is used, the (100) plane texture is stabilized and the crystal grain size tends to be coarse. And, by such improvement of the material structure, siliconization
It is considered that the magnetic properties of the steel sheet after the diffusion treatment can be improved.

Example 2 3% S of the composition of components shown in Table 1
i Steel is vacuum melted to form a slab, which is hot rolled to a finishing temperature of 6
After hot rolling under each condition of 50 ° C. and 860 ° C., and then cold rolling to a plate thickness of 0.35 mm, silicon carbide / diffusion heat treatment was performed at 1150 ° C. in N ₂ or Ar atmosphere to obtain an average Si content of 6 A high silicon steel sheet of 4 to 6.6 wt% was manufactured, and the texture of the steel sheet before and after the siliconizing / diffusion heat treatment was examined. In the siliconizing treatment conditions of this example, the Si concentration in the surface layer reached about 14.3 wt%, and Fe ₃ was added to the surface layer portion.
2 when the Si layer is formed (rapid siliconization treatment: treatment time 3 minutes 30 seconds) and when the Si concentration of the surface layer is always less than 14.3 wt% (slow siliconization treatment: treatment time 10 minutes) Conducted at the standard. Also in this example, the same results were obtained in the siliconizing / diffusion heat treatment regardless of the atmosphere of N ₂ or Ar. Therefore, the following is a representative example of the case of performing the siliconizing / diffusion heat treatment in an Ar atmosphere. Show.

As a result of the above test, similar to the result of Example 1,
If the Si concentration in the surface layer during the siliconizing treatment is always less than 14.3 wt%, the hot rolling finishing temperature is 650.
No change in the texture was observed before and after the siliconizing / diffusion heat treatment for each of the steel sheets at ℃ and 860 ℃.

On the other hand, the surface Si concentration is about 14.3.
When the Fe ₃ Si layer was formed in the surface layer portion, the texture did not change before and after the siliconizing / diffusion heat treatment in the material with a hot rolling finish temperature of 860 ° C., whereas the hot rolling finish temperature of 650 ° C. In the ° C material, the (100) plane strength decreased and the (111) plane strength having no easy axis of magnetization increased. Fig. 5 shows the texture after the siliconizing / diffusion heat treatment for the material with hot rolling finishing temperature of 650 ° C. The steel plates that were present are shown below. The surface Si concentration was about 14.3 during the treatment.
It can be seen that the steel sheet having a wt% of the Fe ₃ Si layer formed on the surface layer has a reduced (100) plane strength and an increased (111) plane strength.

Table 2 shows a steel sheet having a hot rolling finishing temperature of 650 ° C. and a Si layer concentration of about 14.3 wt% during the siliconizing treatment (two samples having different siliconizing conditions) and the Si concentration of the surface layer. Shows the magnetic characteristics of the steel sheets (two samples with different siliconizing conditions) whose content was always less than 14.3 wt% after siliconizing / diffusion heat treatment. According to this, the surface Si concentration is 14.3 during the siliconizing treatment.
Although the steel sheet that has reached the wt% has an effect of improving the magnetic properties due to the coarsening of the grain size, the effect is less than that of the steel sheet whose Si concentration in the surface layer during the siliconizing treatment is always less than 14.3 wt%. small.

From the above results, the surface Si concentration is always 1
It has been found that when the content is less than 4.3 wt%, the (100) plane becomes more stable even after the siliconizing / diffusion heat treatment, and a high silicon steel sheet having high magnetic permeability can be obtained.

[Example 3] In order to investigate the influence of the hot rolling coiling temperature on the hot rolled structure, 3 wt% of the component composition shown in Table 1 was used.
A Si steel slab is hot-rolled under various hot-rolling conditions, the hot-rolled sheet is cold-rolled to 0.35 mm, and then subjected to siliconizing / diffusion heat treatment to keep the surface layer Si concentration always less than 14.3 wt%. A high silicon steel sheet having an average Si amount of 6.4 to 6.7 wt% was manufactured and their magnetic properties were evaluated. Table 3 shows hot rolling conditions and magnetic properties. According to this, the winding temperature is 500 to 7
It can be seen that in the range of 00 ° C., the magnetic properties depend on the hot rolling finishing temperature and not the winding temperature.

[Embodiment 4] Sol. A
In order to investigate the effect of the concentration of Sol.
Hot rolling finishing temperature 70% for 3% Si steel slabs with different Al concentrations
After hot rolling at 0 ° C and a coiling temperature of 550 ° C, the plate thickness is 0.3.
Cold rolled to 5mm, and the Si concentration of the surface layer is always 1
The siliconizing / diffusion heat treatment is applied under the condition of less than 4.3 wt%, and the average Si amount in the plate thickness direction is 6.4 to 6.65 wt%
Manufactured high-silicon steel sheet.

FIG. 6 shows the Sol. The relationship between the Al concentration and the maximum magnetic permeability of the steel sheet after the siliconizing / soaking diffusion treatment is shown. According to this, Sol. A material having a maximum magnetic permeability of 30,000 or more has been obtained in a steel sheet having an Al concentration of 0.1 wt% or less. Al concentration is 100ppm
In the following, more excellent magnetic characteristics are obtained.

7 to 9 show Sol. Al concentration 60pp
IMA showing the state of Al concentration and segregation in the steel sheet cross section after the siliconizing / diffusion heat treatment for the respective steel sheets of m (FIG. 7), 0.1 wt% (FIG. 8) and 0.3 wt% (FIG. 9). It is an ion imaging photograph. According to this, Sol. In the steel sheet having an Al concentration of 60 ppm, Al after the siliconizing treatment / soaking diffusion is scattered at most in the steel sheet cross section (or not visible in the IMA ion imaging photograph). On the other hand, Sol. In a steel sheet with an Al concentration of 0.1 wt%, Al is a Si concentration gradient portion (especially,
Many are scattered on a straight line in the vicinity of the boundary with the Fe ₃ Si layer) and start to show a concentration tendency. Furthermore, Sol. In a steel sheet with an Al concentration of 0.3 wt%, the concentration of Al becomes severe,
It is thickened in a connected state. In addition, Sol.
Regardless of the Al concentration, the precipitate existing in the Al concentrated portion was Al ₂ O ₃ .

From the above results, excellent magnetic properties can be obtained as long as Al is scattered in the cross section of the steel plate in the IMA ion photograph, and for that purpose, Sol. The Al concentration must be 0.1 wt% or less, and in order to obtain more excellent magnetic properties, the Sol. Al concentration of 10
It was confirmed that it is preferable to set the content to 0 ppm or less.

[0040]

[Table 1]

[0041]

[Table 2]

[0042]

[Table 3]

[0043]

[Table 4]

[Brief description of drawings]

FIG. 1 Hot rolling finishing temperature is 650 ° C., 700 ° C., 800
Micrograph of the metallographic structure in the plate thickness direction of each hot-rolled sheet at ℃ and 860 ℃

FIG. 2 is a graph showing the magnetic properties of steel sheets after siliconizing / diffusion heat treatment in relation to their hot rolling finishing temperatures.

FIG. 3 is a graph showing the relationship between the average grain size of the steel sheet after the siliconizing / diffusion heat treatment and the hot rolling finishing temperature of the steel sheet.

FIG. 4 is a drawing showing the P-value strength in each surface direction after the siliconizing / diffusion heat treatment of each steel sheet having a hot rolling finishing temperature of 650 ° C. and 860 ° C.

[FIG. 5] Silicone treatment of a steel sheet having a surface Si concentration of about 14.3 wt% during the siliconizing treatment and a steel sheet having a thermal rolling finishing temperature of 650 ° C. that was always less than 14.3 wt% during the treatment.・ Drawing showing the texture after diffusion heat treatment with P value strength in each plane direction

[FIG. 6] Sol. Graph showing the relationship between the amount of Al and the maximum magnetic permeability after siliconizing / diffusion heat treatment

FIG. 7: Sol. Al concentration: 60ppm material silicon
IMA ion imaging photograph showing Al enrichment and segregation in the steel plate cross section after diffusion heat treatment

FIG. 8: Sol. IMA ion image photograph showing Al enrichment and segregation in the steel plate cross section after siliconizing / diffusion heat treatment of Al concentration: 0.1 wt%

FIG. 9: Sol. IMA ion photograph showing the concentration and segregation of Al in the steel plate cross section after the siliconizing / diffusion heat treatment of the material with Al concentration: 0.3 wt%

FIG. 10 is a graph showing the effect of the content of impurity elements on iron loss.

FIG. 11 is a graph showing the effect of the carbon / oxygen content ratio on iron loss.

Claims (2)

(57) [Claims] 1. Si: 4.0 wt% or less, Sol. A
1: Steel containing 0.1 wt% or less is hot-rolled and cold-rolled to form a thin plate, and this thin plate is subjected to a siliconizing treatment in which Si penetrates from its surface, and then Si is diffused in the plate thickness direction. Therefore, in the method for producing a high silicon steel sheet having Si: 4.0 wt% or more, the hot rolling finish temperature of the material is set to 70
By making the temperature 0 ° C. or less, 70% or more of the hot rolling structure in the plate thickness direction becomes a layered structure that is a non-recrystallized structure, and after cold rolling to a predetermined plate thickness, siliconizing treatment and Si diffusion heat treatment are performed. A method for producing a high silicon steel sheet having high magnetic permeability, comprising: 2. The method for producing a high silicon steel sheet having high magnetic permeability according to claim 1, wherein during the siliconizing treatment, the surface of the steel sheet is treated so that the Si concentration is always less than 14.3 wt%.