JP2022136331A - Foamed wallpaper and method of manufacturing the same - Google Patents

Foamed wallpaper and method of manufacturing the same Download PDF

Info

Publication number
JP2022136331A
JP2022136331A JP2022122835A JP2022122835A JP2022136331A JP 2022136331 A JP2022136331 A JP 2022136331A JP 2022122835 A JP2022122835 A JP 2022122835A JP 2022122835 A JP2022122835 A JP 2022122835A JP 2022136331 A JP2022136331 A JP 2022136331A
Authority
JP
Japan
Prior art keywords
foamed
layer
resin layer
foamed resin
surface protective
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2022122835A
Other languages
Japanese (ja)
Other versions
JP7388498B2 (en
Inventor
武志 由良
Takeshi Yura
菜月 山村
Natsuki Yamamura
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toppan Inc
Original Assignee
Toppan Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toppan Printing Co Ltd filed Critical Toppan Printing Co Ltd
Priority to JP2022122835A priority Critical patent/JP7388498B2/en
Publication of JP2022136331A publication Critical patent/JP2022136331A/en
Application granted granted Critical
Publication of JP7388498B2 publication Critical patent/JP7388498B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a foamed wallpaper that is applicable to a plastic wallpaper and maintains antimicrobial properties even after heating and cleaning, as well as a method of manufacturing the foamed wallpaper.
SOLUTION: A foamed wallpaper 1 comprises: a substrate 2; a foamed resin layer 4 stacked on the substrate 2; a pattern printed layer 6 stacked on the foamed resin layer 4; and a surface protective layer 8 stacked on the pattern printed layer 6. The foamed resin layer 4 is formed using an aqueous emulsion resin as a main component, and contains a water-soluble antimicrobial agent. A mass ratio of the antimicrobial agent to the foamed resin layer 4 is within a range of 0.1% or more and 1.0% or less. A method of manufacturing the foamed wallpaper comprises a step of forming the foamed resin layer in which the foamed resin layer 4 is formed so that the aqueous emulsion resin, or the main component of the foamed resin layer 4, contains the water-soluble antimicrobial agent, and a mass ratio of the antimicrobial agent to the foamed resin layer 4 is within a range of 0.1% or more and 1.0% or less.
SELECTED DRAWING: Figure 1
COPYRIGHT: (C)2022,JPO&INPIT

Description

本発明は、建築物の壁面装飾等に用いる、発泡壁紙と、発泡壁紙の製造方法に関する。 TECHNICAL FIELD The present invention relates to a foamed wallpaper used for wall decoration of buildings and a method for producing the foamed wallpaper.

従来、店舗や病院等の衛生面を重視する建築物に対し、抗菌性を有する壁紙が適用されているが、抗菌剤を化粧層等の最表層に存在させなければ、効果を発揮させることが困難である。
しかしながら、壁紙に用いる抗菌剤の主流である銀系の抗菌剤は、ハロゲンとの反応性が高いため、塩素系の洗浄剤や塩素を多く含む水で清掃すると、失活する可能性がある。また、有機系の抗菌剤は耐熱性が低いため、最表層に添加した場合は、製品加工時に発生する熱で失活する可能性がある。
Conventionally, wallpaper with antibacterial properties has been applied to buildings such as shops and hospitals where hygiene is important, but the effect cannot be exhibited unless the antibacterial agent is present in the outermost layer such as the cosmetic layer. Have difficulty.
However, silver-based antibacterial agents, which are the most common antibacterial agents used in wallpaper, are highly reactive with halogens, and may be deactivated when cleaned with chlorine-based detergents or water containing a large amount of chlorine. In addition, since organic antibacterial agents have low heat resistance, if they are added to the outermost layer, they may be deactivated by the heat generated during product processing.

これに対し、例えば、特許文献1に開示されているように、化粧層を形成する材料に混合される薬剤に非昇華性の薬剤を用いることで、徐放性を有する抗菌剤を添加した壁紙の技術が提案されている。 On the other hand, for example, as disclosed in Patent Document 1, by using a non-sublimation drug as a drug mixed in the material forming the decorative layer, wallpaper added with an antibacterial agent having sustained release properties technology has been proposed.

特開2015-168677号公報JP 2015-168677 A

しかしながら、特許文献1に開示されている技術では、技術を適用可能な範囲が塩化ビニル系の壁紙と紙系の壁紙に限定されており、非塩化ビニル系の壁紙等、プラスチック系の壁紙への適用が困難であるという問題があった。
本発明は、上記事情に鑑みてなされたものであり、プラスチック系の壁紙への適用が可能であるとともに、加熱や清掃の後であっても抗菌性を維持することが可能な、発泡壁紙と、発泡壁紙の製造方法を提供することを目的とする。
However, in the technology disclosed in Patent Document 1, the applicable range of the technology is limited to vinyl chloride wallpaper and paper wallpaper, and it is applicable to plastic wallpaper such as non-vinyl chloride wallpaper. There was a problem that application was difficult.
The present invention has been made in view of the above circumstances, and is a foamed wallpaper that can be applied to plastic wallpaper and can maintain antibacterial properties even after heating and cleaning. , for the purpose of providing a method for producing foamed wallpaper.

上記課題を解決するために、本発明の一態様は、基材と、基材に積層した発泡樹脂層と、発泡樹脂層に積層した絵柄印刷層と、絵柄印刷層に積層した表面保護層と、を備える発泡壁紙である。そして、発泡樹脂層は、水性エマルジョン樹脂を主成分として形成され、且つ水溶性の抗菌剤を含有し、抗菌剤の発泡樹脂層に対する質量比は、0.1%以上1.0%以下の範囲内であり、表面保護層は、表面保護層を構成する固形成分のうち質量比10%以上30%以下の範囲内でシリコン系樹脂を含む。 In order to solve the above problems, one aspect of the present invention provides a substrate, a foamed resin layer laminated on the substrate, a pattern printed layer laminated on the foamed resin layer, and a surface protective layer laminated on the pattern printed layer. is a foamed wallpaper comprising: The foamed resin layer is formed mainly of an aqueous emulsion resin and contains a water-soluble antibacterial agent, and the mass ratio of the antibacterial agent to the foamed resin layer is in the range of 0.1% or more and 1.0% or less. The surface protective layer contains a silicon-based resin within a range of 10% or more and 30% or less by mass of the solid components constituting the surface protective layer.

また、上記課題を解決するために、本発明の一態様は、基材と、基材に積層した発泡樹脂層と、発泡樹脂層に積層した絵柄印刷層と、絵柄印刷層に積層した表面保護層と、を備える発泡壁紙の製造方法であり、発泡樹脂層を形成する発泡樹脂層形成工程と、表面保護層を形成する表面保護層形成工程とを備える。発泡樹脂層形成工程では、発泡樹脂層の主成分とする水性エマルジョン樹脂に水溶性の抗菌剤を含有させるとともに、抗菌剤の発泡樹脂層に対する質量比を0.1%以上1.0%以下の範囲内として発泡樹脂層を形成する。表面保護層形成工程では、表面保護層を構成する固形成分のうち質量比10%以上30%以下の範囲内でシリコン系樹脂を含んで表面保護層を形成する。 In order to solve the above problems, one aspect of the present invention includes a substrate, a foamed resin layer laminated on the substrate, a pattern printed layer laminated on the foamed resin layer, and a surface protective layer laminated on the pattern printed layer. A foamed wallpaper manufacturing method comprising: a foamed resin layer forming step for forming a foamed resin layer; and a surface protective layer forming step for forming a surface protective layer. In the foamed resin layer forming step, a water-soluble antibacterial agent is added to the aqueous emulsion resin that is the main component of the foamed resin layer, and the mass ratio of the antibacterial agent to the foamed resin layer is 0.1% or more and 1.0% or less. A foamed resin layer is formed within the range. In the surface protective layer forming step, the surface protective layer is formed by containing a silicon-based resin within a range of 10% or more and 30% or less by mass of the solid components constituting the surface protective layer.

本発明の一態様によれば、最表層ではない発泡樹脂層に抗菌剤を添加するため、プラスチック系の壁紙への適用が可能であるとともに、加熱や清掃の後であっても抗菌性を維持することが可能な、発泡壁紙と、発泡壁紙の製造方法を提供することが可能となる。 According to one aspect of the present invention, since the antibacterial agent is added to the foamed resin layer that is not the outermost layer, it can be applied to plastic wallpaper and maintains antibacterial properties even after heating and cleaning. It is possible to provide a foamed wallpaper and a method for producing the foamed wallpaper that can be used.

本発明の第一実施形態における発泡壁紙の構成を表す断面図である。1 is a cross-sectional view showing the configuration of a foamed wallpaper according to a first embodiment of the present invention; FIG.

図面を参照して、本発明の第一実施形態を以下において説明する。以下の説明で参照する図面の記載において、同一または類似の部分には、同一または類似の符号を付している。ただし、図面は模式的なものであり、厚さと平面寸法との関係や、各層の厚さの比率等は、現実のものとは異なることに留意すべきである。したがって、具体的な厚さや寸法は、以下の説明を参酌して判断すべきものである。また、図面相互間においても、互いの寸法の関係や比率が異なる部分が含まれていることは勿論である。 A first embodiment of the invention is described below with reference to the drawings. In the description of the drawings referred to in the following description, the same or similar parts are given the same or similar reference numerals. However, it should be noted that the drawings are schematic, and the relationship between thickness and planar dimension, the ratio of thickness of each layer, and the like are different from the actual ones. Therefore, specific thicknesses and dimensions should be determined with reference to the following description. In addition, it goes without saying that there are portions with different dimensional relationships and ratios between the drawings.

さらに、以下に示す第一実施形態は、本発明の技術的思想を具体化するための構成を例示するものであって、本発明の技術的思想は、構成部品の材質や、それらの形状、構造、配置等を下記のものに特定するものでない。本発明の技術的思想は、特許請求の範囲に記載された請求項が規定する技術的範囲内において、種々の変更を加えることが可能である。また、以下の説明における「左右」や「上下」の方向は、単に説明の便宜上の定義であって、本発明の技術的思想を限定するものではない。よって、例えば、紙面を90度回転すれば「左右」と「上下」とは交換して読まれ、紙面を180度回転すれば「左」が「右」になり、「右」が「左」になることは勿論である。 Furthermore, the first embodiment shown below exemplifies the configuration for embodying the technical idea of the present invention, and the technical idea of the present invention is the material of the component parts, their shape, The structure, arrangement, etc. are not specified to the following. Various changes can be made to the technical idea of the present invention within the technical scope defined by the claims. Further, the directions of "left and right" and "up and down" in the following description are merely definitions for convenience of description, and do not limit the technical idea of the present invention. Therefore, for example, if the page is rotated 90 degrees, "left and right" and "up and down" are read interchangeably, and if the page is rotated 180 degrees, "left" becomes "right" and "right" becomes "left." It goes without saying that

(第一実施形態)
以下、本発明の第一実施形態について、図面を参照しつつ説明する。
(発泡壁紙)
図1を参照して、発泡壁紙1の構成について説明する。
発泡壁紙1は、図1中に表すように、基材2と、発泡樹脂層4と、絵柄印刷層6と、表面保護層8を、この順で備える。
発泡壁紙1の透湿度は、400[g/m・hr]以上1000[g/m・hr]以下の範囲内である。
(First embodiment)
A first embodiment of the present invention will be described below with reference to the drawings.
(Foam wallpaper)
The configuration of the foamed wallpaper 1 will be described with reference to FIG.
The foamed wallpaper 1 comprises a substrate 2, a foamed resin layer 4, a pattern printed layer 6, and a surface protective layer 8 in this order, as shown in FIG.
The moisture permeability of the foamed wallpaper 1 is within the range of 400 [g/m 2 ·hr] or more and 1000 [g/m 2 ·hr] or less.

(基材)
基材2は、火に接しても燃え難い紙材を用いて形成されたシート状の層である。
基材2を形成する紙材としては、壁紙用の裏打紙等、紙基材として通常使用されている材料であれば、特に限定されずに使用することが可能である。したがって、基材2を形成する紙材としては、例えば、水溶性難燃剤を含浸させたパルプ主体の難燃紙や、無機質剤を混抄した無機質紙等を用いることが可能である。
(Base material)
The base material 2 is a sheet-like layer formed using a paper material that does not easily burn even when exposed to fire.
As the paper material forming the base material 2, any material that is normally used as a paper base material, such as backing paper for wallpaper, can be used without particular limitation. Therefore, as the paper material forming the base material 2, for example, flame-retardant paper mainly composed of pulp impregnated with a water-soluble flame retardant, inorganic paper mixed with an inorganic agent, or the like can be used.

第一実施形態では、一例として、基材2の材料として、水溶性難燃剤を含浸させた紙等、木質系の材料とした場合について説明する。これは、基材2を木質系の基材とすることで、基材2の構成が発泡壁紙に適切な構成となるとともに、基材2を形成する材料の入手が容易となるためである。
ここで、水溶性難燃剤としては、例えば、スルファミン酸グアニジン、リン酸グアニジン等を用いることが可能である。また、無機質剤としては、例えば、炭酸マグネシウム、水酸化アルミニウム、水酸化マグネシウム等を用いることが可能である。
In the first embodiment, as an example, a case where a wood-based material such as paper impregnated with a water-soluble flame retardant is used as the material of the base material 2 will be described. This is because by using a wood-based base material as the base material 2, the structure of the base material 2 becomes a structure suitable for the foamed wallpaper, and the material for forming the base material 2 is easily available.
Here, as the water-soluble flame retardant, for example, guanidine sulfamate, guanidine phosphate, or the like can be used. As the inorganic agent, for example, magnesium carbonate, aluminum hydroxide, magnesium hydroxide, etc. can be used.

なお、基材2の表面のうち、樹脂層2を積層する側の面(図1中では、基材2の上側の面)に対し、易接着処理を施すことで、基材2の表面を易接着処理面としてもよい。易接着処理としては、例えば、表面に対しコロナ放電処理、プラズマ処理、オゾン処理等を用いることが可能である。また、易接着処理面とする代わりに、プライマー層を形成してもよい。 In addition, of the surface of the base material 2, the surface of the base material 2 on which the resin layer 2 is laminated (the upper surface of the base material 2 in FIG. 1) is subjected to an easy-adhesion treatment, so that the surface of the base material 2 is The surface may be treated for easy adhesion. As the adhesion-facilitating treatment, for example, corona discharge treatment, plasma treatment, ozone treatment, etc. can be used on the surface. Also, a primer layer may be formed instead of the easy-adhesion treated surface.

(発泡樹脂層)
発泡樹脂層4は、基材2に積層されている。具体的には、発泡樹脂層4は、図1中において、基材2の上側の面に積層されている。
また、発泡樹脂層4は、樹脂成分と、充填剤と、発泡剤と、発泡助剤と、樹脂分と、有機系抗菌剤と、添加剤と、抗菌剤を含有しており、発泡剤が発泡することで形成されている。
発泡樹脂層4が含有する樹脂成分は、主成分として水性エマルジョン樹脂を含有する。すなわち、発泡樹脂層4は、水性エマルジョン樹脂を主成分として形成されている。
(foamed resin layer)
The foamed resin layer 4 is laminated on the substrate 2 . Specifically, the foamed resin layer 4 is laminated on the upper surface of the substrate 2 in FIG.
The foamed resin layer 4 contains a resin component, a filler, a foaming agent, a foaming aid, a resin component, an organic antibacterial agent, an additive, and an antibacterial agent. It is formed by foaming.
The resin component contained in the foamed resin layer 4 contains an aqueous emulsion resin as a main component. That is, the foamed resin layer 4 is formed mainly of an aqueous emulsion resin.

発泡樹脂層4が含有する充填剤としては、例えば、無機充填剤を用いることが可能である。また、無機充填剤は、一種を単独で用いることも、二種類以上を併用して用いることも可能である。
無機充填剤としては、例えば、炭酸カルシウム、二酸化チタン、カオリン等を用いることが可能である。
発泡樹脂層4が含有する発泡剤(揮発性膨張剤)は、熱膨張性マイクロカプセルの形で発泡樹脂層4が含有する樹脂成分に添加することが、性能(発泡倍率、強度)の観点から好ましい。また、発泡樹脂層4が含有する発泡剤としては、アゾ系、ヒドラジッド系、ニトロソ系等を用いることが可能である。
As the filler contained in the foamed resin layer 4, for example, an inorganic filler can be used. Inorganic fillers can be used singly or in combination of two or more.
Examples of inorganic fillers that can be used include calcium carbonate, titanium dioxide, kaolin, and the like.
From the viewpoint of performance (expansion ratio, strength), the foaming agent (volatile expansion agent) contained in the foamed resin layer 4 may be added to the resin component contained in the foamed resin layer 4 in the form of thermally expandable microcapsules. preferable. As the foaming agent contained in the foamed resin layer 4, azo-based, hydrazide-based, nitroso-based, etc. can be used.

また、発泡樹脂層4には、必要に応じて、顔料等を添加して着色してもよい。
顔料の添加による着色は、透明であってもよいし、半透明であってもよいし、不透明であってもよい。
顔料としては、例えば、酸化鉄、カーボンブラック等を用いることが可能である。
顔料の添加量は、樹脂層全量を基準として、5[質量%]以上50[質量%]以下の範囲内が好ましく、10[質量%]以上30[質量%]以下の範囲内がより好ましい。
発泡樹脂層4が含有する抗菌剤としては、水に可溶であること(水溶性)が条件となるため、例えば、チアゾール系を用いることが可能である。
Further, the foamed resin layer 4 may be colored by adding a pigment or the like as necessary.
Coloration by adding a pigment may be transparent, translucent, or opaque.
Examples of pigments that can be used include iron oxide and carbon black.
The amount of pigment added is preferably in the range of 5 [mass %] to 50 [mass %], more preferably 10 [mass %] to 30 [mass %], based on the total amount of the resin layer.
As the antibacterial agent contained in the foamed resin layer 4, it is possible to use, for example, a thiazole-based agent because it must be soluble in water (water-soluble).

また、発泡樹脂層4が含有する抗菌剤としては、水溶性を有していれば、ニトリル系、イミダゾール系、アルコール系、アルデヒド系、(カルボン酸系、エステル系)、ジスルフィド系、チオカーバメート系、フェノール系等を用いることが可能である。
さらに、発泡樹脂層4が含有する抗菌剤としては、水溶性を有していれば、ピリジン・キノリン系、トリアジン系、イソチアゾロン系、アニリド系、カルボン酸系、エーテル系、過酸化物・エポキシ系、ビグアナイド系、界面活性剤系等を用いることが可能である。
Further, as the antibacterial agent contained in the foamed resin layer 4, nitrile, imidazole, alcohol, aldehyde, (carboxylic acid, ester), disulfide, thiocarbamate, etc., as long as they are water-soluble. , phenol-based, etc. can be used.
Furthermore, as the antibacterial agent contained in the foamed resin layer 4, pyridine/quinoline, triazine, isothiazolone, anilide, carboxylic acid, ether, peroxide/epoxy, etc., as long as they are water-soluble. , biguanides, surfactants, and the like can be used.

第一実施形態では、一例として、発泡樹脂層4が含有する抗菌剤を、有機窒素硫黄系の抗菌剤とした場合について説明する。
抗菌剤の発泡樹脂層4に対する質量比は、0.1[%]以上1.0[%]以下の範囲内である。
発泡樹脂層4が含有する添加剤としては、必要に応じて、難燃剤、セル調整剤、安定剤、滑剤等、周知の添加剤を用いることが可能である。
難燃剤としては、例えば、水酸化マグネシウム、水酸化アルミニウム等の金属酸化物系難燃剤、リン酸エステル系等のリン系難燃剤、テトラブロモビスフェノールA等の臭素系難燃剤等を用いることが可能である。
In the first embodiment, as an example, the case where the antibacterial agent contained in the foamed resin layer 4 is an organic nitrogen-sulfur antibacterial agent will be described.
The mass ratio of the antibacterial agent to the foamed resin layer 4 is within the range of 0.1 [%] or more and 1.0 [%] or less.
As additives contained in the foamed resin layer 4, known additives such as flame retardants, cell regulators, stabilizers, and lubricants can be used as necessary.
Examples of flame retardants that can be used include metal oxide flame retardants such as magnesium hydroxide and aluminum hydroxide, phosphorus flame retardants such as phosphate esters, and brominated flame retardants such as tetrabromobisphenol A. is.

(絵柄印刷層)
絵柄印刷層6は、発泡樹脂層4に積層されている。具体的には、絵柄印刷層6は、図1中において、発泡樹脂層4の上側の面に積層されている。
また、絵柄印刷層6は、発泡壁紙1へ、所望の絵柄による意匠性を付与するものであり、絵柄の種類等は、特に限定的されるものではない。
絵柄としては、例えば、木目模様、石目模様、砂目模様、タイル貼模様、煉瓦積模様、布目模様、皮絞模様、幾何学図形、文字、記号、抽象模様等、発泡壁紙1を用いる箇所に適した絵柄を選択することが可能である。
(Pattern printed layer)
The pattern printed layer 6 is laminated on the foamed resin layer 4 . Specifically, the pattern printed layer 6 is laminated on the upper surface of the foamed resin layer 4 in FIG.
Further, the pattern printed layer 6 imparts a desired design to the foamed wallpaper 1, and the type of pattern is not particularly limited.
Examples of patterns include wood grain patterns, stone grain patterns, sand grain patterns, tile patterns, brickwork patterns, texture patterns, leather tie patterns, geometric figures, letters, symbols, abstract patterns, etc., where the foamed wallpaper 1 is used. It is possible to select a pattern suitable for

絵柄印刷層6を形成する印刷インキについては、壁紙として一般的に求められるような耐光性、発色性、使用される成分の安全性の用件(顔料や添加剤として、重金属や硫黄化合物を含まない等)を満たしていれば特に限定されるものではない。
第一実施形態では、一例として、絵柄印刷層6を形成する印刷インキを、アクリル重合体をベースレジンとする水系のインキとした場合について説明する。
絵柄印刷層6を形成する印刷インキは、上記のような水性エマルジョンから構成され、印刷後に乾燥させることで、絵柄印刷層6の塗膜となる。
また、インキには、絵柄模様を構成する公知の顔料が含まれる。
As for the printing ink that forms the pattern printing layer 6, the requirements for light resistance, color development, and safety of the components used (including heavy metals and sulfur compounds as pigments and additives), which are generally required for wallpaper, are satisfied. etc.) is not particularly limited.
In the first embodiment, as an example, the case where the printing ink forming the pattern printed layer 6 is a water-based ink using an acrylic polymer as a base resin will be described.
The printing ink for forming the pattern printed layer 6 is composed of the aqueous emulsion as described above, and becomes a coating film of the pattern printed layer 6 by drying after printing.
Further, the ink contains a known pigment that forms a pattern.

また、絵柄印刷層6を形成する印刷インキに、顔料を組み合わせて配合することで、絵柄の表現を豊かにすることが可能となる。また、絵柄印刷層6を形成する印刷インキに、紫外線吸収剤や光安定剤等を添加することで、耐候性を良好にすることも可能となる。
絵柄の印刷方法としては、例えば、グラビア印刷、オフセット印刷、シルクスクリーン印刷、インクジェット印刷等、既知の印刷方法を用いることが可能である。
特に、全面を同一に着色する場合には、上述した印刷方法の他に、コーティングの手法や装置を用いてもよい。
Further, by blending a pigment in combination with the printing ink forming the pattern printed layer 6, it is possible to enrich the expression of the pattern. Moreover, by adding an ultraviolet absorber, a light stabilizer, or the like to the printing ink that forms the pattern printed layer 6, it is possible to improve the weather resistance.
As a method for printing the pattern, for example, known printing methods such as gravure printing, offset printing, silk screen printing, and inkjet printing can be used.
In particular, in the case of uniformly coloring the entire surface, a coating technique or apparatus may be used in addition to the printing method described above.

(表面保護層)
表面保護層8は、絵柄印刷層6に積層されており、コート層(コーティング層)とも呼称される層である。具体的には、表面保護層8は、図1中において、絵柄印刷層6の上側の面に積層されている。
また、表面保護層8は、層(表面保護層8)を構成する固形成分のうち、質量比10%以上30%以下の範囲内で、シリコン系樹脂を含む。
(Surface protective layer)
The surface protective layer 8 is laminated on the pattern printed layer 6 and is a layer also called a coat layer (coating layer). Specifically, the surface protective layer 8 is laminated on the upper surface of the pattern printed layer 6 in FIG.
Moreover, the surface protective layer 8 contains a silicon-based resin in a mass ratio of 10% or more and 30% or less of the solid components constituting the layer (surface protective layer 8).

また、表面保護層8は、シリコン系樹脂以外の樹脂成分として、アクリル酸(CH=CHCOOH)及びメタクリル酸(CH=C(CH)COOH)、ないしはそれらのエステルのうちから選択した一種以上のモノマーから形成される重合体、または、重合体に対してスチレン、酢酸ビニル、エチレン及びα-オレフィンのうち一種以上のモノマーないしはブロックコポリマーを共重合させることによって得られる重合体を含むことが好ましい。
なお、表面保護層8の構成は、シリコン系樹脂以外の樹脂成分として、ポリ塩化ビニル等の樹脂を含む構成とすることも可能である。
In addition, the surface protective layer 8 is made of acrylic acid (CH 2 =CHCOOH), methacrylic acid (CH 2 =C(CH 3 )COOH), or one selected from esters thereof as a resin component other than silicone resin. Polymers formed from the above monomers, or polymers obtained by copolymerizing monomers or block copolymers of one or more of styrene, vinyl acetate, ethylene and α-olefins with the polymer. preferable.
The structure of the surface protective layer 8 can also be a structure containing a resin such as polyvinyl chloride as a resin component other than the silicon-based resin.

表面保護層8の坪量は、熱や塩素からの保護、表面強度、耐汚染性等の物性を付与する観点から、5.0[g/m]以上30.0[g/m]以下の範囲内であることが好ましい。さらに、表面保護層8の坪量は、15.0[g/m]以上25.0[g/m]以下の範囲内であることがより好ましい。
また、表面保護層8の絵柄印刷層6と対向する面と反対の面(図1中における、表面保護層8の上側の面)には、エンボス加工による凹凸形状10が形成されている。
エンボス加工による凹凸形状10としては、例えば、布目、木目板導管溝、石板表面凹凸、布表面テクスチャー、梨地、砂目、ヘアライン、万線条溝等を用いることが可能であり、適宜選択が可能である。
The basis weight of the surface protective layer 8 is 5.0 [g/m 2 ] or more and 30.0 [g/m 2 ] from the viewpoint of providing physical properties such as protection from heat and chlorine, surface strength, and stain resistance. It is preferably within the following range. Furthermore, the basis weight of the surface protective layer 8 is more preferably in the range of 15.0 [g/m 2 ] to 25.0 [g/m 2 ].
On the surface of the surface protective layer 8 opposite to the surface facing the pattern printed layer 6 (the upper surface of the surface protective layer 8 in FIG. 1), an embossed uneven shape 10 is formed.
As the uneven shape 10 by embossing, for example, it is possible to use cloth grain, wood grain plate conduit groove, stone plate surface unevenness, cloth surface texture, satin finish, sand grain, hairline, parallel groove, etc., and it is possible to select appropriately. is.

(発泡壁紙1の製造方法)
以下、図1を参照して、第一実施形態の発泡壁紙1の製造方法を説明する。
発泡壁紙1の製造方法は、基材2と、発泡樹脂層4と、絵柄印刷層6と、表面保護層8を備える発泡壁紙1の製造方法であり、発泡樹脂層4を形成する発泡樹脂層形成工程と、表面保護層8を形成する表面保護層形成工程とを備える。
(Method for producing foamed wallpaper 1)
Hereinafter, a method for manufacturing the foamed wallpaper 1 of the first embodiment will be described with reference to FIG.
The method for producing the foamed wallpaper 1 is a method for producing the foamed wallpaper 1 including the substrate 2, the foamed resin layer 4, the pattern printed layer 6, and the surface protective layer 8, and the foamed resin layer forming the foamed resin layer 4. A forming step and a surface protective layer forming step for forming the surface protective layer 8 are provided.

発泡樹脂層形成工程では、発泡樹脂層4の主成分とする水性エマルジョン樹脂に水溶性の抗菌剤を含有させるとともに、抗菌剤の発泡樹脂層4に対する質量比を0.1[%]以上1.0[%]以下の範囲内として、発泡樹脂層4を形成する。
発泡樹脂層形成工程において、発泡樹脂層4の主成分とする水性エマルジョン樹脂に水溶性の抗菌剤を含有させることで、抗菌剤を、他の物性に悪影響が無い範囲で、経時変化によりブリードさせることが可能となる。
これにより、抗菌剤を含有する発泡樹脂層4を表面保護層8が保護する構成となるため、ふき取り清掃や洗剤との接触による抗菌剤の除去や、抗菌剤の揮発・昇華による喪失を抑制することが可能となる。
In the foamed resin layer forming step, a water-soluble antibacterial agent is added to the aqueous emulsion resin that is the main component of the foamed resin layer 4, and the mass ratio of the antibacterial agent to the foamed resin layer 4 is set to 0.1% or more. The foamed resin layer 4 is formed within the range of 0 [%] or less.
In the step of forming the foamed resin layer, by adding a water-soluble antimicrobial agent to the water-based emulsion resin that is the main component of the foamed resin layer 4, the antimicrobial agent is allowed to bleed out over time as long as it does not adversely affect other physical properties. becomes possible.
As a result, the foamed resin layer 4 containing the antibacterial agent is protected by the surface protective layer 8, so the removal of the antibacterial agent due to wiping or contact with detergent and the loss of the antibacterial agent due to volatilization and sublimation are suppressed. becomes possible.

表面保護層形成工程では、表面保護層8を構成する固形成分のうち質量比10%以上30%以下の範囲内でシリコン系樹脂を含んで、表面保護層8を形成する。
なお、上述した第一実施形態は、本発明の一例であり、本発明は、上述した第一実施形態に限定されることはなく、この実施形態以外の形態であっても、本発明に係る技術的思想を逸脱しない範囲であれば、設計等に応じて種々の変更が可能である。
In the surface protective layer forming step, the surface protective layer 8 is formed by containing a silicon-based resin in a mass ratio of 10% or more and 30% or less of the solid components constituting the surface protective layer 8 .
The first embodiment described above is an example of the present invention, and the present invention is not limited to the first embodiment described above. Various modifications are possible according to the design and the like within the scope of not departing from the technical idea.

(第一実施形態の効果)
第一実施形態の発泡壁紙1であれば、以下に記載する効果を奏することが可能となる。
(1)基材2と、基材2に積層した発泡樹脂層4と、発泡樹脂層4に積層した絵柄印刷層6と、絵柄印刷層6に積層した表面保護層8を備える。これに加え、発泡樹脂層4は、水性エマルジョン樹脂を主成分として形成され、且つ水溶性の抗菌剤を含有し、抗菌剤の発泡樹脂層4に対する質量比は、0.1[%]以上1.0[%]以下の範囲内である。さらに、表面保護層8は、前記表面保護層を構成する固形成分のうち質量比10[%]以上30[%]以下の範囲内でシリコン系樹脂を含む。
(Effect of the first embodiment)
With the foamed wallpaper 1 of the first embodiment, it is possible to achieve the effects described below.
(1) A substrate 2 , a foamed resin layer 4 laminated on the substrate 2 , a pattern printed layer 6 laminated on the foamed resin layer 4 , and a surface protective layer 8 laminated on the pattern printed layer 6 . In addition, the foamed resin layer 4 is formed mainly of an aqueous emulsion resin and contains a water-soluble antibacterial agent, and the mass ratio of the antibacterial agent to the foamed resin layer 4 is 0.1 [%] or more. 0 [%] or less. Further, the surface protective layer 8 contains a silicone-based resin in a mass ratio of 10% or more and 30% or less of the solid components constituting the surface protective layer.

このため、最表層ではない発泡樹脂層4に抗菌剤を添加することで、抗菌剤を含有する発泡樹脂層4を表面保護層8が保護する構成となり、ふき取り清掃や洗剤との接触による抗菌剤の除去や、抗菌剤の揮発・昇華による喪失を抑制することが可能となる。
その結果、プラスチック系の壁紙への適用が可能であるとともに、加熱や清掃の後であっても抗菌性を維持することが可能な、発泡壁紙1を提供することが可能となる。
Therefore, by adding an antibacterial agent to the foamed resin layer 4 which is not the outermost layer, the foamed resin layer 4 containing the antibacterial agent is protected by the surface protective layer 8, and the antibacterial agent is removed by wiping off or contacting with the detergent. It is possible to suppress the removal of the antibacterial agent and the loss of the antibacterial agent due to volatilization and sublimation.
As a result, it is possible to provide a foamed wallpaper 1 that can be applied to plastic-based wallpaper and that can maintain antibacterial properties even after heating and cleaning.

(2)抗菌剤が、有機窒素硫黄系の抗菌剤である。
その結果、抗菌性に加え、防カビ効果を有することが可能となる。また、長期間に亘り、安定した効力を持続することが可能となる。
(3)表面保護層8の坪量が、5.0[g/m]以上30.0[g/m]以下の範囲内である。
その結果、表面保護層8による発泡樹脂層4の保護力を向上させることが可能となる。
(2) The antibacterial agent is an organic nitrogen-sulfur antibacterial agent.
As a result, it becomes possible to have an antifungal effect in addition to antibacterial properties. In addition, it becomes possible to maintain stable efficacy over a long period of time.
(3) The basis weight of the surface protective layer 8 is in the range of 5.0 [g/m 2 ] to 30.0 [g/m 2 ].
As a result, it is possible to improve the protection of the foamed resin layer 4 by the surface protective layer 8 .

(4)透湿度が400[g/m・hr]以上1000[g/m・hr]以下の範囲内である。
その結果、発泡壁紙1の構成を、壁紙として適切な透湿度を有する構成とすることが可能となる。
(5)表面保護層8の絵柄印刷層6と対向する面と反対の面に、エンボス加工による凹凸形状10が形成されている。
その結果、絵柄印刷層6によって発泡壁紙1へ付与する意匠性を向上させることが可能となる。
また、第一実施形態の発泡壁紙1の製造方法であれば、以下に記載する効果を奏することが可能となる。
(4) Moisture permeability is in the range of 400 [g/m 2 ·hr] to 1000 [g/m 2 ·hr].
As a result, the structure of the foamed wallpaper 1 can be configured to have a moisture permeability suitable for wallpaper.
(5) An uneven shape 10 is formed by embossing on the surface of the surface protective layer 8 opposite to the surface facing the pattern printed layer 6 .
As a result, it becomes possible to improve the design property imparted to the foamed wallpaper 1 by the pattern printed layer 6 .
Moreover, if it is the manufacturing method of the foamed wallpaper 1 of 1st embodiment, it will become possible to produce the effect described below.

(6)発泡樹脂層4の主成分とする水性エマルジョン樹脂に水溶性の抗菌剤を含有させるとともに、抗菌剤の発泡樹脂層4に対する質量比を0.1[%]以上1.0[%]以下の範囲内として発泡樹脂層4を形成する、発泡樹脂層形成工程を備える。これに加え、表面保護層8を構成する固形成分のうち質量比10[%]以上30[%]以下の範囲内でシリコン系樹脂を含んで表面保護層8を形成する、表面保護層形成工程を備える。
このため、最表層ではない発泡樹脂層4に抗菌剤を添加することで、抗菌剤を含有する発泡樹脂層4を表面保護層8が保護する構成となり、ふき取り清掃や洗剤との接触による抗菌剤の除去や、抗菌剤の揮発・昇華による喪失を抑制することが可能となる。
その結果、プラスチック系の壁紙への適用が可能であるとともに、加熱や清掃の後であっても抗菌性を維持することが可能な、発泡壁紙1の製造方法を提供することが可能となる。
(6) A water-soluble antibacterial agent is added to the aqueous emulsion resin that is the main component of the foamed resin layer 4, and the mass ratio of the antibacterial agent to the foamed resin layer 4 is 0.1 [%] or more and 1.0 [%]. A foamed resin layer forming step is provided to form the foamed resin layer 4 within the following range. In addition to this, a surface protective layer forming step of forming the surface protective layer 8 containing a silicon-based resin in a mass ratio of 10% or more and 30% or less of the solid components constituting the surface protective layer 8. Prepare.
Therefore, by adding an antibacterial agent to the foamed resin layer 4 which is not the outermost layer, the foamed resin layer 4 containing the antibacterial agent is protected by the surface protective layer 8, and the antibacterial agent is removed by wiping off or contacting with the detergent. It is possible to suppress the removal of the antibacterial agent and the loss of the antibacterial agent due to volatilization and sublimation.
As a result, it is possible to provide a method for producing the foamed wallpaper 1, which can be applied to plastic-based wallpaper and can maintain antibacterial properties even after heating and cleaning.

第一実施形態を参照しつつ、以下、実施例の発泡壁紙と、比較例の発泡壁紙について説明する。
(実施例1)
実施例1の発泡壁紙は、以下の構成とした。
また、実施例1の発泡壁紙は、透湿度を400[g/m・hr]とした。
・基材
坪量が65[g/m]の普通紙を用いて形成した。
・発泡樹脂層
エチレン・酢酸ビニル共重合樹脂(EVA樹脂)を主成分とし、充填剤として炭酸カルシウムを80部、カプセル発泡剤を10部添加した。そして、発泡倍率を5倍に設定し、坪量が100[g/m]となるように形成した。
さらに、発泡樹脂層には、抗菌剤(BC-477)を含有させ、抗菌剤の発泡樹脂層に対する質量比を0.3[%]とした。
・絵柄印刷層
アクリル樹脂系インキを用いて、塗布量が2[g/m]となるように形成した。
・表面保護層
アクリル系樹脂及びシリコン系樹脂を主成分とし、坪量が5[g/m]となるように形成した。
With reference to the first embodiment, a foamed wallpaper of an example and a foamed wallpaper of a comparative example will be described below.
(Example 1)
The foamed wallpaper of Example 1 was configured as follows.
Further, the foamed wallpaper of Example 1 had a moisture permeability of 400 [g/m 2 ·hr].
- Base material Plain paper having a basis weight of 65 [g/m 2 ] was used.
- Foamed resin layer An ethylene-vinyl acetate copolymer resin (EVA resin) was used as a main component, and 80 parts of calcium carbonate and 10 parts of a capsule foaming agent were added as fillers. Then, the expansion ratio was set to 5 times, and the basis weight was 100 [g/m 2 ].
Furthermore, the foamed resin layer contained an antibacterial agent (BC-477), and the mass ratio of the antibacterial agent to the foamed resin layer was set to 0.3 [%].
- Pattern printed layer Using an acrylic resin ink, it formed so that the amount of application might be set to 2 [g/m< 2 >].
- Surface protective layer A layer containing acrylic resin and silicone resin as main components and having a basis weight of 5 [g/m 2 ] was formed.

(実施例2)
実施例2の発泡壁紙は、透湿度を1000[g/m・hr]とした構成を除き、実施例1の発泡壁紙と同様である。
(実施例3)
実施例3の発泡壁紙は、表面保護層の構成を除き、実施例1の発泡壁紙と同様である。
・表面保護層
アクリル系樹脂及びシリコン系樹脂を主成分とし、坪量が30[g/m]となるように形成した。
(実施例4)
実施例4の発泡壁紙は、透湿度を1000[g/m・hr]とした構成と、表面保護層の構成を除き、実施例3の発泡壁紙と同様である。
(Example 2)
The foamed wallpaper of Example 2 is the same as the foamed wallpaper of Example 1 except for the structure in which the moisture permeability is set to 1000 [g/m 2 ·hr].
(Example 3)
The foamed wallpaper of Example 3 is the same as the foamed wallpaper of Example 1 except for the structure of the surface protective layer.
- Surface protective layer A surface protective layer containing acrylic resin and silicone resin as main components was formed so as to have a basis weight of 30 [g/m 2 ].
(Example 4)
The foamed wallpaper of Example 4 is the same as the foamed wallpaper of Example 3 except for the structure of the moisture permeability of 1000 [g/m 2 ·hr] and the structure of the surface protective layer.

(比較例1)
比較例1の発泡壁紙は、以下の構成とした。
また、比較例1の発泡壁紙は、透湿度を400[g/m・hr]とした。
・基材
坪量が65[g/m]の普通紙を用いて形成した。
・発泡樹脂層
エチレン・酢酸ビニル共重合樹脂(EVA樹脂)を主成分とし、充填剤として炭酸カルシウムを80部、カプセル発泡剤を10部添加した。そして、発泡倍率を5倍に設定し、坪量が100[g/m]となるように形成した。
・絵柄印刷層
アクリル樹脂系インキを用いて、塗布量が2[g/m]となるように形成した。
・表面保護層
アクリル系樹脂及びシリコン系樹脂を主成分とし、坪量が30[g/m]となるように形成した。
さらに、表面保護層には、抗菌剤(ゼオミック AV-10D)を含有させ、抗菌剤の表面保護層に対する質量比を0.3[%]とした。
(Comparative example 1)
The foamed wallpaper of Comparative Example 1 had the following structure.
Further, the foamed wallpaper of Comparative Example 1 had a moisture permeability of 400 [g/m 2 ·hr].
- Base material Plain paper having a basis weight of 65 [g/m 2 ] was used.
- Foamed resin layer An ethylene-vinyl acetate copolymer resin (EVA resin) was used as a main component, and 80 parts of calcium carbonate and 10 parts of a capsule foaming agent were added as fillers. Then, the expansion ratio was set to 5 times, and the basis weight was 100 [g/m 2 ].
- Pattern printed layer Using an acrylic resin ink, it formed so that the amount of application might be set to 2 [g/m< 2 >].
- Surface protective layer A surface protective layer containing acrylic resin and silicone resin as main components was formed so as to have a basis weight of 30 [g/m 2 ].
Furthermore, the surface protective layer contained an antibacterial agent (Zeomic AV-10D), and the mass ratio of the antibacterial agent to the surface protective layer was set to 0.3 [%].

(比較例2)
比較例2の発泡壁紙は、透湿度を1000[g/m・hr]とした構成を除き、比較例1の発泡壁紙と同様である。
(比較例3)
比較例3の発泡壁紙は、表面保護層の構成を除き、比較例2の発泡壁紙と同様である。
・表面保護層
アクリル系樹脂及びシリコン系樹脂を主成分とし、坪量が30[g/m]となるように形成した。
さらに、表面保護層には、抗菌剤(ゼオミック AV-10D)を含有させ、抗菌剤の表面保護層に対する質量比を2.0[%]とした。
(Comparative example 2)
The foamed wallpaper of Comparative Example 2 is the same as the foamed wallpaper of Comparative Example 1 except for the structure in which the moisture permeability is set to 1000 [g/m 2 ·hr].
(Comparative Example 3)
The foamed wallpaper of Comparative Example 3 is the same as the foamed wallpaper of Comparative Example 2 except for the structure of the surface protective layer.
- Surface protective layer A surface protective layer containing acrylic resin and silicone resin as main components was formed so as to have a basis weight of 30 [g/m 2 ].
Furthermore, the surface protective layer contained an antibacterial agent (Zeomic AV-10D), and the mass ratio of the antibacterial agent to the surface protective layer was set to 2.0 [%].

(比較例4)
比較例4の発泡壁紙は、以下の構成とした。
また、比較例4の発泡壁紙は、透湿度を1000[g/m・hr]とした。
・基材
坪量が65[g/m]の普通紙を用いて形成した。
・発泡樹脂層
エチレン・酢酸ビニル共重合樹脂(EVA樹脂)を主成分とし、充填剤として炭酸カルシウムを80部、カプセル発泡剤を10部添加した。そして、発泡倍率を5倍に設定し、坪量が100[g/m]となるように形成した。
さらに、発泡樹脂層には、抗菌剤(ゼオミック AV-10D)を含有させ、抗菌剤の発泡樹脂層に対する質量比を2.0[%]とした。
・絵柄印刷層
アクリル樹脂系インキを用いて、塗布量が2[g/m]となるように形成した。
・表面保護層
アクリル系樹脂及びシリコン系樹脂を主成分とし、坪量が30[g/m]となるように形成した。
(Comparative Example 4)
The foamed wallpaper of Comparative Example 4 was configured as follows.
The foamed wallpaper of Comparative Example 4 had a moisture permeability of 1000 [g/m 2 ·hr].
- Base material Plain paper having a basis weight of 65 [g/m 2 ] was used.
- Foamed resin layer An ethylene-vinyl acetate copolymer resin (EVA resin) was used as a main component, and 80 parts of calcium carbonate and 10 parts of a capsule foaming agent were added as fillers. Then, the expansion ratio was set to 5 times, and the basis weight was 100 [g/m 2 ].
Furthermore, the foamed resin layer contained an antibacterial agent (Zeomic AV-10D), and the mass ratio of the antibacterial agent to the foamed resin layer was set to 2.0 [%].
- Pattern printed layer Using an acrylic resin ink, it formed so that the amount of application might be set to 2 [g/m< 2 >].
- Surface protective layer A surface protective layer containing acrylic resin and silicone resin as main components was formed so as to have a basis weight of 30 [g/m 2 ].

(比較例5)
比較例5の発泡壁紙は、発泡樹脂層の構成を除き、比較例4の発泡壁紙と同様である。
・発泡樹脂層
エチレン・酢酸ビニル共重合樹脂(EVA樹脂)を主成分とし、充填剤として炭酸カルシウムを80部、カプセル発泡剤を10部添加した。そして、発泡倍率を5倍に設定し、坪量が100[g/m]となるように形成した。
さらに、発泡樹脂層には、抗菌剤(BC-477)を含有させ、抗菌剤の発泡樹脂層に対する質量比を2.0[%]とした。
(比較例6)
比較例6の発泡壁紙は、透湿度を100[g/m・hr]とした構成を除き、比較例5の発泡壁紙と同様である。
(Comparative Example 5)
The foamed wallpaper of Comparative Example 5 is the same as the foamed wallpaper of Comparative Example 4 except for the structure of the foamed resin layer.
- Foamed resin layer An ethylene-vinyl acetate copolymer resin (EVA resin) was used as a main component, and 80 parts of calcium carbonate and 10 parts of a capsule foaming agent were added as fillers. Then, the expansion ratio was set to 5 times, and the basis weight was 100 [g/m 2 ].
Further, the foamed resin layer contained an antibacterial agent (BC-477), and the mass ratio of the antibacterial agent to the foamed resin layer was set to 2.0 [%].
(Comparative Example 6)
The foamed wallpaper of Comparative Example 6 is the same as the foamed wallpaper of Comparative Example 5 except for the structure in which the moisture permeability is set to 100 [g/m 2 ·hr].

(性能評価)
実施例の発泡壁紙と、比較例の発泡壁紙に対し、それぞれ、通常の状態における抗菌性と、拭き取り後の抗菌性に対する性能評価を行った。
通常の状態における抗菌性は、壁装問屋協議会の規格である「抗菌壁紙性能規定」の試験方法に基づき、「生菌数が0.63以下」の場合を合格として評価し、「生菌数が0.63を超える」場合を不合格として評価した。
拭き取り後の抗菌性は、壁装問屋協議会の規格である「抗菌壁紙性能規定」の試験方法に基づき、「生菌数が0.63以下」の場合を合格として評価し、「生菌数が0.63を超える」場合を不合格として評価した。
評価結果は表1中に表す。
(performance evaluation)
The foamed wallpaper of the example and the foamed wallpaper of the comparative example were evaluated for antibacterial properties under normal conditions and antibacterial properties after wiping.
The antibacterial property under normal conditions is evaluated as passing when the number of viable bacteria is 0.63 or less, based on the test method of the "antibacterial wallpaper performance regulations", which is the standard of the Wallcovering Wholesalers Association. A number greater than 0.63” was evaluated as a failure.
The antibacterial property after wiping is evaluated as passing if the number of viable bacteria is 0.63 or less based on the test method of the "antibacterial wallpaper performance regulation", which is the standard of the Wallcovering Wholesalers Association. is more than 0.63" was evaluated as fail.
Evaluation results are shown in Table 1.

Figure 2022136331000002
Figure 2022136331000002

(評価結果)
表1中に表されるように、実施例の発泡壁紙は、比較例の発泡壁紙と比較して、通常の状態における抗菌性と、拭き取り後の抗菌性が高いことが確認された。
(Evaluation results)
As shown in Table 1, it was confirmed that the foamed wallpaper of the example had higher antibacterial properties in normal conditions and higher antibacterial properties after wiping than the foamed wallpaper of the comparative example.

1…発泡壁紙、2…基材、4…発泡樹脂層、6…絵柄印刷層、8…表面保護層、10…凹凸形状 DESCRIPTION OF SYMBOLS 1... Foam wallpaper, 2... Base material, 4... Foam resin layer, 6... Pattern printing layer, 8... Surface protection layer, 10... Concavo-convex shape

Claims (5)

基材と、前記基材に積層した発泡樹脂層と、前記発泡樹脂層に積層した絵柄印刷層と、前記絵柄印刷層に積層した表面保護層と、を備え、
前記発泡樹脂層は、水性エマルジョン樹脂を主成分として形成され、且つ水溶性の抗菌剤を含有し、
前記抗菌剤の前記発泡樹脂層に対する質量比は、0.1%以上1.0%以下の範囲内であり、
前記表面保護層は、前記表面保護層を構成する固形成分のうち質量比10%以上30%以下の範囲内でシリコン系樹脂を含むことを特徴とする発泡壁紙。
A substrate, a foamed resin layer laminated on the substrate, a pattern printed layer laminated on the foamed resin layer, and a surface protective layer laminated on the pattern printed layer,
The foamed resin layer is formed mainly of an aqueous emulsion resin and contains a water-soluble antibacterial agent,
The mass ratio of the antibacterial agent to the foamed resin layer is in the range of 0.1% or more and 1.0% or less,
The foamed wallpaper, wherein the surface protective layer contains a silicon-based resin in a mass ratio of 10% or more and 30% or less of the solid components constituting the surface protective layer.
前記抗菌剤は、有機窒素硫黄系の抗菌剤であることを特徴とする請求項1に記載した発泡壁紙。 2. The foamed wallpaper according to claim 1, wherein the antibacterial agent is an organic nitrogen-sulfur antibacterial agent. 前記表面保護層の坪量は、5.0g/m以上30.0g/m以下の範囲内であることを特徴とする請求項1または請求項2に記載した発泡壁紙。 The foamed wallpaper according to claim 1 or 2, wherein the basis weight of the surface protective layer is in the range of 5.0 g/ m2 to 30.0 g/ m2 . 前記表面保護層の前記絵柄印刷層と対向する面と反対の面には、エンボス加工による凹凸形状が形成されていることを特徴とする請求項1から請求項3のうちいずれか1項に記載した発泡壁紙。 4. The surface protective layer according to any one of claims 1 to 3, wherein a surface opposite to the surface facing the pattern printed layer of the surface protective layer is formed with an uneven shape by embossing. foam wallpaper. 基材と、前記基材に積層した発泡樹脂層と、前記発泡樹脂層に積層した絵柄印刷層と、前記絵柄印刷層に積層した表面保護層と、を備える発泡壁紙の製造方法であって、
前記発泡樹脂層を形成する発泡樹脂層形成工程と、前記表面保護層を形成する表面保護層形成工程と、を備え、
前記発泡樹脂層形成工程では、前記発泡樹脂層の主成分とする水性エマルジョン樹脂に水溶性の抗菌剤を含有させるとともに、前記抗菌剤の前記発泡樹脂層に対する質量比を0.1%以上1.0%以下の範囲内として前記発泡樹脂層を形成し、
前記表面保護層形成工程では、前記表面保護層を構成する固形成分のうち質量比10%以上30%以下の範囲内でシリコン系樹脂を含んで前記表面保護層を形成することを特徴とする発泡壁紙の製造方法。
A method for producing a foamed wallpaper comprising a base material, a foamed resin layer laminated on the base material, a pattern printed layer laminated on the foamed resin layer, and a surface protective layer laminated on the pattern printed layer,
A foamed resin layer forming step of forming the foamed resin layer and a surface protective layer forming step of forming the surface protective layer,
In the foamed resin layer forming step, a water-soluble antibacterial agent is added to the aqueous emulsion resin that is the main component of the foamed resin layer, and the mass ratio of the antibacterial agent to the foamed resin layer is 0.1% or more. Forming the foamed resin layer within the range of 0% or less,
In the step of forming the surface protective layer, the surface protective layer is formed by containing a silicon-based resin in a mass ratio of 10% or more and 30% or less of the solid components constituting the surface protective layer. How wallpaper is made.
JP2022122835A 2017-11-01 2022-08-01 Foam wallpaper, foam wallpaper manufacturing method Active JP7388498B2 (en)