JP7388498B2 - Foam wallpaper, foam wallpaper manufacturing method - Google Patents
Foam wallpaper, foam wallpaper manufacturing method Download PDFInfo
- Publication number
- JP7388498B2 JP7388498B2 JP2022122835A JP2022122835A JP7388498B2 JP 7388498 B2 JP7388498 B2 JP 7388498B2 JP 2022122835 A JP2022122835 A JP 2022122835A JP 2022122835 A JP2022122835 A JP 2022122835A JP 7388498 B2 JP7388498 B2 JP 7388498B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- foamed
- foamed resin
- resin layer
- surface protective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、建築物の壁面装飾等に用いる、発泡壁紙と、発泡壁紙の製造方法に関する。 The present invention relates to foamed wallpaper used for wall decoration of buildings, etc., and a method for manufacturing foamed wallpaper.
従来、店舗や病院等の衛生面を重視する建築物に対し、抗菌性を有する壁紙が適用されているが、抗菌剤を化粧層等の最表層に存在させなければ、効果を発揮させることが困難である。
しかしながら、壁紙に用いる抗菌剤の主流である銀系の抗菌剤は、ハロゲンとの反応性が高いため、塩素系の洗浄剤や塩素を多く含む水で清掃すると、失活する可能性がある。また、有機系の抗菌剤は耐熱性が低いため、最表層に添加した場合は、製品加工時に発生する熱で失活する可能性がある。
Traditionally, wallpaper with antibacterial properties has been applied to buildings where hygiene is important, such as stores and hospitals, but if antibacterial agents are not present in the outermost layer, such as the makeup layer, it will not be effective. Have difficulty.
However, silver-based antibacterial agents, which are the main type of antibacterial agents used in wallpaper, are highly reactive with halogens, so if they are cleaned with chlorine-based cleaning agents or water containing a lot of chlorine, they may be deactivated. Furthermore, since organic antibacterial agents have low heat resistance, if they are added to the outermost layer, they may be deactivated by the heat generated during product processing.
これに対し、例えば、特許文献１に開示されているように、化粧層を形成する材料に混合される薬剤に非昇華性の薬剤を用いることで、徐放性を有する抗菌剤を添加した壁紙の技術が提案されている。 On the other hand, for example, as disclosed in Patent Document 1, wallpaper with a sustained-release antibacterial agent is added by using a non-sublimable agent in the agent that is mixed into the material forming the decorative layer. technology has been proposed.
しかしながら、特許文献１に開示されている技術では、技術を適用可能な範囲が塩化ビニル系の壁紙と紙系の壁紙に限定されており、非塩化ビニル系の壁紙等、プラスチック系の壁紙への適用が困難であるという問題があった。
本発明は、上記事情に鑑みてなされたものであり、プラスチック系の壁紙への適用が可能であるとともに、加熱や清掃の後であっても抗菌性を維持することが可能な、発泡壁紙と、発泡壁紙の製造方法を提供することを目的とする。
However, with the technology disclosed in Patent Document 1, the applicable scope of the technology is limited to vinyl chloride-based wallpaper and paper-based wallpaper, and it cannot be applied to plastic-based wallpaper such as non-vinyl chloride-based wallpaper. There was a problem that it was difficult to apply.
The present invention was made in view of the above circumstances, and provides a foamed wallpaper that can be applied to plastic-based wallpaper and maintains antibacterial properties even after heating and cleaning. , an object of the present invention is to provide a method for producing foam wallpaper.
上記課題を解決するために、本発明の一態様は、基材と、基材に積層した発泡樹脂層と、発泡樹脂層に積層した絵柄印刷層と、絵柄印刷層に積層した表面保護層と、を備える発泡壁紙である。そして、発泡樹脂層は、水性エマルジョン樹脂を主成分として形成され、且つ水溶性の抗菌剤を含有し、抗菌剤の発泡樹脂層に対する質量比は、０．１％以上１．０％以下の範囲内であり、表面保護層は、表面保護層を構成する固形成分のうち質量比１０％以上３０％以下の範囲内でシリコン系樹脂を含む。 In order to solve the above problems, one embodiment of the present invention includes a base material, a foamed resin layer laminated on the base material, a pattern printing layer laminated on the foamed resin layer, and a surface protection layer laminated on the pattern printing layer. It is a foam wallpaper comprising . The foamed resin layer is formed mainly from an aqueous emulsion resin and contains a water-soluble antibacterial agent, and the mass ratio of the antibacterial agent to the foamed resin layer is in the range of 0.1% to 1.0%. The surface protective layer contains a silicone resin in a mass ratio of 10% to 30% of the solid components constituting the surface protective layer.
また、上記課題を解決するために、本発明の一態様は、基材と、基材に積層した発泡樹脂層と、発泡樹脂層に積層した絵柄印刷層と、絵柄印刷層に積層した表面保護層と、を備える発泡壁紙の製造方法であり、発泡樹脂層を形成する発泡樹脂層形成工程と、表面保護層を形成する表面保護層形成工程とを備える。発泡樹脂層形成工程では、発泡樹脂層の主成分とする水性エマルジョン樹脂に水溶性の抗菌剤を含有させるとともに、抗菌剤の発泡樹脂層に対する質量比を０．１％以上１．０％以下の範囲内として発泡樹脂層を形成する。表面保護層形成工程では、表面保護層を構成する固形成分のうち質量比１０％以上３０％以下の範囲内でシリコン系樹脂を含んで表面保護層を形成する。 Further, in order to solve the above problems, one aspect of the present invention includes a base material, a foamed resin layer laminated on the base material, a pattern printing layer laminated on the foamed resin layer, and a surface protection layer laminated on the pattern printing layer. A foamed wallpaper manufacturing method includes a foamed resin layer forming step of forming a foamed resin layer, and a surface protective layer forming step of forming a surface protective layer. In the foamed resin layer forming step, a water-soluble antibacterial agent is contained in the aqueous emulsion resin that is the main component of the foamed resin layer, and the mass ratio of the antibacterial agent to the foamed resin layer is 0.1% or more and 1.0% or less. A foamed resin layer is formed within this range. In the surface protective layer forming step, the surface protective layer is formed by including a silicone resin in a mass ratio of 10% to 30% of the solid components constituting the surface protective layer.
本発明の一態様によれば、最表層ではない発泡樹脂層に抗菌剤を添加するため、プラスチック系の壁紙への適用が可能であるとともに、加熱や清掃の後であっても抗菌性を維持することが可能な、発泡壁紙と、発泡壁紙の製造方法を提供することが可能となる。 According to one aspect of the present invention, since an antibacterial agent is added to the foamed resin layer that is not the outermost layer, it is possible to apply it to plastic-based wallpaper and maintain antibacterial properties even after heating and cleaning. It becomes possible to provide foamed wallpaper and a method for manufacturing foamed wallpaper that can be used to produce foamed wallpaper.
図面を参照して、本発明の第一実施形態を以下において説明する。以下の説明で参照する図面の記載において、同一または類似の部分には、同一または類似の符号を付している。ただし、図面は模式的なものであり、厚さと平面寸法との関係や、各層の厚さの比率等は、現実のものとは異なることに留意すべきである。したがって、具体的な厚さや寸法は、以下の説明を参酌して判断すべきものである。また、図面相互間においても、互いの寸法の関係や比率が異なる部分が含まれていることは勿論である。 A first embodiment of the invention will be described below with reference to the drawings. In the description of the drawings referred to in the following description, the same or similar parts are denoted by the same or similar symbols. However, it should be noted that the drawings are schematic and that the relationship between thickness and planar dimensions, the ratio of the thickness of each layer, etc. are different from the actual one. Therefore, specific thickness and dimensions should be determined with reference to the following explanation. Furthermore, it goes without saying that the drawings include portions with different dimensional relationships and ratios.
さらに、以下に示す第一実施形態は、本発明の技術的思想を具体化するための構成を例示するものであって、本発明の技術的思想は、構成部品の材質や、それらの形状、構造、配置等を下記のものに特定するものでない。本発明の技術的思想は、特許請求の範囲に記載された請求項が規定する技術的範囲内において、種々の変更を加えることが可能である。また、以下の説明における「左右」や「上下」の方向は、単に説明の便宜上の定義であって、本発明の技術的思想を限定するものではない。よって、例えば、紙面を９０度回転すれば「左右」と「上下」とは交換して読まれ、紙面を１８０度回転すれば「左」が「右」になり、「右」が「左」になることは勿論である。 Furthermore, the first embodiment shown below exemplifies a configuration for embodying the technical idea of the present invention, and the technical idea of the present invention is based on the materials of the component parts, their shapes, The structure, arrangement, etc. are not specified as shown below. The technical idea of the present invention can be modified in various ways within the technical scope defined by the claims. Further, the directions "left and right" and "up and down" in the following description are simply defined for convenience of explanation, and do not limit the technical idea of the present invention. Therefore, for example, if you rotate the page 90 degrees, "left and right" and "top and bottom" will be read interchangeably, and if you rotate the page 180 degrees, "left" becomes "right" and "right" becomes "left." Of course it will become.
（第一実施形態）
以下、本発明の第一実施形態について、図面を参照しつつ説明する。
（発泡壁紙）
図１を参照して、発泡壁紙１の構成について説明する。
発泡壁紙１は、図１中に表すように、基材２と、発泡樹脂層４と、絵柄印刷層６と、表面保護層８を、この順で備える。
発泡壁紙１の透湿度は、４００［ｇ／ｍ２・ｈｒ］以上１０００［ｇ／ｍ２・ｈｒ］以下の範囲内である。
(First embodiment)
Hereinafter, a first embodiment of the present invention will be described with reference to the drawings.
(foam wallpaper)
The structure of foam wallpaper 1 will be described with reference to FIG. 1.
As shown in FIG. 1, the foamed wallpaper 1 includes a
The moisture permeability of the foamed wallpaper 1 is within the range of 400 [g/m 2 ·hr] or more and 1000 [g/m 2 ·hr] or less.
（基材）
基材２は、火に接しても燃え難い紙材を用いて形成されたシート状の層である。
基材２を形成する紙材としては、壁紙用の裏打紙等、紙基材として通常使用されている材料であれば、特に限定されずに使用することが可能である。したがって、基材２を形成する紙材としては、例えば、水溶性難燃剤を含浸させたパルプ主体の難燃紙や、無機質剤を混抄した無機質紙等を用いることが可能である。
(Base material)
The
The paper material forming the
第一実施形態では、一例として、基材２の材料として、水溶性難燃剤を含浸させた紙等、木質系の材料とした場合について説明する。これは、基材２を木質系の基材とすることで、基材２の構成が発泡壁紙に適切な構成となるとともに、基材２を形成する材料の入手が容易となるためである。
ここで、水溶性難燃剤としては、例えば、スルファミン酸グアニジン、リン酸グアニジン等を用いることが可能である。また、無機質剤としては、例えば、炭酸マグネシウム、水酸化アルミニウム、水酸化マグネシウム等を用いることが可能である。
In the first embodiment, as an example, a case will be described in which the material of the
Here, as the water-soluble flame retardant, for example, guanidine sulfamate, guanidine phosphate, etc. can be used. Further, as the inorganic agent, for example, magnesium carbonate, aluminum hydroxide, magnesium hydroxide, etc. can be used.
なお、基材２の表面のうち、樹脂層２を積層する側の面（図１中では、基材２の上側の面）に対し、易接着処理を施すことで、基材２の表面を易接着処理面としてもよい。易接着処理としては、例えば、表面に対しコロナ放電処理、プラズマ処理、オゾン処理等を用いることが可能である。また、易接着処理面とする代わりに、プライマー層を形成してもよい。
Note that the surface of the
（発泡樹脂層）
発泡樹脂層４は、基材２に積層されている。具体的には、発泡樹脂層４は、図１中において、基材２の上側の面に積層されている。
また、発泡樹脂層４は、樹脂成分と、充填剤と、発泡剤と、発泡助剤と、樹脂分と、有機系抗菌剤と、添加剤と、抗菌剤を含有しており、発泡剤が発泡することで形成されている。
発泡樹脂層４が含有する樹脂成分は、主成分として水性エマルジョン樹脂を含有する。すなわち、発泡樹脂層４は、水性エマルジョン樹脂を主成分として形成されている。
(foamed resin layer)
The
Further, the
The resin component contained in the
発泡樹脂層４が含有する充填剤としては、例えば、無機充填剤を用いることが可能である。また、無機充填剤は、一種を単独で用いることも、二種類以上を併用して用いることも可能である。
無機充填剤としては、例えば、炭酸カルシウム、二酸化チタン、カオリン等を用いることが可能である。
発泡樹脂層４が含有する発泡剤（揮発性膨張剤）は、熱膨張性マイクロカプセルの形で発泡樹脂層４が含有する樹脂成分に添加することが、性能（発泡倍率、強度）の観点から好ましい。また、発泡樹脂層４が含有する発泡剤としては、アゾ系、ヒドラジッド系、ニトロソ系等を用いることが可能である。
As the filler contained in the
As the inorganic filler, for example, calcium carbonate, titanium dioxide, kaolin, etc. can be used.
From the viewpoint of performance (expansion ratio, strength), it is recommended that the foaming agent (volatile expansion agent) contained in the
また、発泡樹脂層４には、必要に応じて、顔料等を添加して着色してもよい。
顔料の添加による着色は、透明であってもよいし、半透明であってもよいし、不透明であってもよい。
顔料としては、例えば、酸化鉄、カーボンブラック等を用いることが可能である。
顔料の添加量は、樹脂層全量を基準として、５［質量％］以上５０［質量％］以下の範囲内が好ましく、１０［質量％］以上３０［質量％］以下の範囲内がより好ましい。
発泡樹脂層４が含有する抗菌剤としては、水に可溶であること（水溶性）が条件となるため、例えば、チアゾール系を用いることが可能である。
Further, the foamed
Coloring by adding a pigment may be transparent, translucent, or opaque.
As the pigment, for example, iron oxide, carbon black, etc. can be used.
The amount of the pigment added is preferably within the range of 5 [mass%] or more and 50 [mass%] or less, and more preferably within the range of 10 [mass%] or more and 30 [mass%] or less, based on the total amount of the resin layer.
Since the antibacterial agent contained in the foamed
また、発泡樹脂層４が含有する抗菌剤としては、水溶性を有していれば、ニトリル系、イミダゾール系、アルコール系、アルデヒド系、（カルボン酸系、エステル系）、ジスルフィド系、チオカーバメート系、フェノール系等を用いることが可能である。
さらに、発泡樹脂層４が含有する抗菌剤としては、水溶性を有していれば、ピリジン・キノリン系、トリアジン系、イソチアゾロン系、アニリド系、カルボン酸系、エーテル系、過酸化物・エポキシ系、ビグアナイド系、界面活性剤系等を用いることが可能である。
In addition, the antibacterial agent contained in the foamed
Furthermore, the antibacterial agent contained in the foamed
第一実施形態では、一例として、発泡樹脂層４が含有する抗菌剤を、有機窒素硫黄系の抗菌剤とした場合について説明する。
抗菌剤の発泡樹脂層４に対する質量比は、０．１［％］以上１．０［％］以下の範囲内である。
発泡樹脂層４が含有する添加剤としては、必要に応じて、難燃剤、セル調整剤、安定剤、滑剤等、周知の添加剤を用いることが可能である。
難燃剤としては、例えば、水酸化マグネシウム、水酸化アルミニウム等の金属酸化物系難燃剤、リン酸エステル系等のリン系難燃剤、テトラブロモビスフェノールＡ等の臭素系難燃剤等を用いることが可能である。
In the first embodiment, as an example, a case will be described in which the antibacterial agent contained in the foamed
The mass ratio of the antibacterial agent to the foamed
As the additives contained in the foamed
As the flame retardant, for example, metal oxide flame retardants such as magnesium hydroxide and aluminum hydroxide, phosphorus flame retardants such as phosphate esters, bromine flame retardants such as tetrabromobisphenol A, etc. can be used. It is.
（絵柄印刷層）
絵柄印刷層６は、発泡樹脂層４に積層されている。具体的には、絵柄印刷層６は、図１中において、発泡樹脂層４の上側の面に積層されている。
また、絵柄印刷層６は、発泡壁紙１へ、所望の絵柄による意匠性を付与するものであり、絵柄の種類等は、特に限定的されるものではない。
絵柄としては、例えば、木目模様、石目模様、砂目模様、タイル貼模様、煉瓦積模様、布目模様、皮絞模様、幾何学図形、文字、記号、抽象模様等、発泡壁紙１を用いる箇所に適した絵柄を選択することが可能である。
(Picture printing layer)
The pattern printing layer 6 is laminated on the foamed
Further, the pattern printing layer 6 imparts a desired pattern design to the foamed wallpaper 1, and the type of pattern etc. is not particularly limited.
Patterns include, for example, wood grain patterns, stone grain patterns, sand grain patterns, tiling patterns, brickwork patterns, fabric patterns, leather drawing patterns, geometric figures, letters, symbols, abstract patterns, etc. where the foam wallpaper 1 is used. It is possible to select a suitable pattern.
絵柄印刷層６を形成する印刷インキについては、壁紙として一般的に求められるような耐光性、発色性、使用される成分の安全性の用件（顔料や添加剤として、重金属や硫黄化合物を含まない等）を満たしていれば特に限定されるものではない。
第一実施形態では、一例として、絵柄印刷層６を形成する印刷インキを、アクリル重合体をベースレジンとする水系のインキとした場合について説明する。
絵柄印刷層６を形成する印刷インキは、上記のような水性エマルジョンから構成され、印刷後に乾燥させることで、絵柄印刷層６の塗膜となる。
また、インキには、絵柄模様を構成する公知の顔料が含まれる。
Regarding the printing ink that forms the pattern printing layer 6, the requirements for light resistance, color development, and safety of the ingredients used (including heavy metals and sulfur compounds as pigments and additives), which are generally required for wallpaper, must be met. There is no particular limitation as long as the conditions (such as no) are met.
In the first embodiment, as an example, a case will be described in which the printing ink forming the pattern printing layer 6 is a water-based ink using an acrylic polymer as the base resin.
The printing ink forming the pattern printing layer 6 is composed of the aqueous emulsion as described above, and becomes a coating film of the pattern printing layer 6 by drying it after printing.
Further, the ink contains a known pigment that forms the picture pattern.
また、絵柄印刷層６を形成する印刷インキに、顔料を組み合わせて配合することで、絵柄の表現を豊かにすることが可能となる。また、絵柄印刷層６を形成する印刷インキに、紫外線吸収剤や光安定剤等を添加することで、耐候性を良好にすることも可能となる。
絵柄の印刷方法としては、例えば、グラビア印刷、オフセット印刷、シルクスクリーン印刷、インクジェット印刷等、既知の印刷方法を用いることが可能である。
特に、全面を同一に着色する場合には、上述した印刷方法の他に、コーティングの手法や装置を用いてもよい。
Further, by blending a combination of pigments into the printing ink forming the pattern printing layer 6, it becomes possible to enrich the expression of the pattern. Further, by adding an ultraviolet absorber, a light stabilizer, etc. to the printing ink forming the pattern printing layer 6, it is also possible to improve the weather resistance.
As a method for printing the pattern, for example, known printing methods such as gravure printing, offset printing, silk screen printing, and inkjet printing can be used.
In particular, when the entire surface is to be colored uniformly, a coating method or apparatus may be used in addition to the above-described printing method.
（表面保護層）
表面保護層８は、絵柄印刷層６に積層されており、コート層（コーティング層）とも呼称される層である。具体的には、表面保護層８は、図１中において、絵柄印刷層６の上側の面に積層されている。
また、表面保護層８は、層（表面保護層８）を構成する固形成分のうち、質量比１０％以上３０％以下の範囲内で、シリコン系樹脂を含む。
(Surface protective layer)
The
Furthermore, the surface
また、表面保護層８は、シリコン系樹脂以外の樹脂成分として、アクリル酸（ＣＨ２＝ＣＨＣＯＯＨ）及びメタクリル酸（ＣＨ２＝Ｃ（ＣＨ３）ＣＯＯＨ）、ないしはそれらのエステルのうちから選択した一種以上のモノマーから形成される重合体、または、重合体に対してスチレン、酢酸ビニル、エチレン及びα-オレフィンのうち一種以上のモノマーないしはブロックコポリマーを共重合させることによって得られる重合体を含むことが好ましい。
なお、表面保護層８の構成は、シリコン系樹脂以外の樹脂成分として、ポリ塩化ビニル等の樹脂を含む構成とすることも可能である。
In addition, the surface
Note that the surface
表面保護層８の坪量は、熱や塩素からの保護、表面強度、耐汚染性等の物性を付与する観点から、５．０［ｇ／ｍ２］以上３０．０［ｇ／ｍ２］以下の範囲内であることが好ましい。さらに、表面保護層８の坪量は、１５．０［ｇ／ｍ２］以上２５．０［ｇ／ｍ２］以下の範囲内であることがより好ましい。
また、表面保護層８の絵柄印刷層６と対向する面と反対の面（図１中における、表面保護層８の上側の面）には、エンボス加工による凹凸形状１０が形成されている。
エンボス加工による凹凸形状１０としては、例えば、布目、木目板導管溝、石板表面凹凸、布表面テクスチャー、梨地、砂目、ヘアライン、万線条溝等を用いることが可能であり、適宜選択が可能である。
The basis weight of the surface
Further, on the surface of the
As the
（発泡壁紙１の製造方法）
以下、図１を参照して、第一実施形態の発泡壁紙１の製造方法を説明する。
発泡壁紙１の製造方法は、基材２と、発泡樹脂層４と、絵柄印刷層６と、表面保護層８を備える発泡壁紙１の製造方法であり、発泡樹脂層４を形成する発泡樹脂層形成工程と、表面保護層８を形成する表面保護層形成工程とを備える。
(Method for manufacturing foam wallpaper 1)
Hereinafter, with reference to FIG. 1, a method for manufacturing foamed wallpaper 1 according to the first embodiment will be described.
The method for manufacturing foamed wallpaper 1 is a method for manufacturing foamed wallpaper 1 that includes a
発泡樹脂層形成工程では、発泡樹脂層４の主成分とする水性エマルジョン樹脂に水溶性の抗菌剤を含有させるとともに、抗菌剤の発泡樹脂層４に対する質量比を０．１［％］以上１．０［％］以下の範囲内として、発泡樹脂層４を形成する。
発泡樹脂層形成工程において、発泡樹脂層４の主成分とする水性エマルジョン樹脂に水溶性の抗菌剤を含有させることで、抗菌剤を、他の物性に悪影響が無い範囲で、経時変化によりブリードさせることが可能となる。
これにより、抗菌剤を含有する発泡樹脂層４を表面保護層８が保護する構成となるため、ふき取り清掃や洗剤との接触による抗菌剤の除去や、抗菌剤の揮発・昇華による喪失を抑制することが可能となる。
In the foamed resin layer forming step, a water-soluble antibacterial agent is contained in the aqueous emulsion resin that is the main component of the foamed
In the foamed resin layer forming step, by incorporating a water-soluble antibacterial agent into the aqueous emulsion resin that is the main component of the foamed
As a result, the surface
表面保護層形成工程では、表面保護層８を構成する固形成分のうち質量比１０％以上３０％以下の範囲内でシリコン系樹脂を含んで、表面保護層８を形成する。
なお、上述した第一実施形態は、本発明の一例であり、本発明は、上述した第一実施形態に限定されることはなく、この実施形態以外の形態であっても、本発明に係る技術的思想を逸脱しない範囲であれば、設計等に応じて種々の変更が可能である。
In the surface protective layer forming step, the surface
Note that the first embodiment described above is an example of the present invention, and the present invention is not limited to the first embodiment described above, and even forms other than this embodiment are applicable to the present invention. Various changes can be made according to the design, etc., as long as they do not deviate from the technical concept.
（第一実施形態の効果）
第一実施形態の発泡壁紙１であれば、以下に記載する効果を奏することが可能となる。
（１）基材２と、基材２に積層した発泡樹脂層４と、発泡樹脂層４に積層した絵柄印刷層６と、絵柄印刷層６に積層した表面保護層８を備える。これに加え、発泡樹脂層４は、水性エマルジョン樹脂を主成分として形成され、且つ水溶性の抗菌剤を含有し、抗菌剤の発泡樹脂層４に対する質量比は、０．１［％］以上１．０［％］以下の範囲内である。さらに、表面保護層８は、前記表面保護層を構成する固形成分のうち質量比１０［％］以上３０［％］以下の範囲内でシリコン系樹脂を含む。
(Effects of first embodiment)
The foamed wallpaper 1 of the first embodiment can achieve the effects described below.
(1) It includes a
このため、最表層ではない発泡樹脂層４に抗菌剤を添加することで、抗菌剤を含有する発泡樹脂層４を表面保護層８が保護する構成となり、ふき取り清掃や洗剤との接触による抗菌剤の除去や、抗菌剤の揮発・昇華による喪失を抑制することが可能となる。
その結果、プラスチック系の壁紙への適用が可能であるとともに、加熱や清掃の後であっても抗菌性を維持することが可能な、発泡壁紙１を提供することが可能となる。
Therefore, by adding an antibacterial agent to the foamed
As a result, it is possible to provide foamed wallpaper 1 that can be applied to plastic-based wallpaper and maintains antibacterial properties even after heating and cleaning.
（２）抗菌剤が、有機窒素硫黄系の抗菌剤である。
その結果、抗菌性に加え、防カビ効果を有することが可能となる。また、長期間に亘り、安定した効力を持続することが可能となる。
（３）表面保護層８の坪量が、５．０［ｇ／ｍ２］以上３０．０［ｇ／ｍ２］以下の範囲内である。
その結果、表面保護層８による発泡樹脂層４の保護力を向上させることが可能となる。
(2) The antibacterial agent is an organic nitrogen sulfur-based antibacterial agent.
As a result, it becomes possible to have an antifungal effect in addition to antibacterial properties. Moreover, it becomes possible to maintain stable efficacy over a long period of time.
(3) The basis weight of the surface
As a result, it becomes possible to improve the protection power of the foamed
（４）透湿度が４００［ｇ／ｍ２・ｈｒ］以上１０００［ｇ／ｍ２・ｈｒ］以下の範囲内である。
その結果、発泡壁紙１の構成を、壁紙として適切な透湿度を有する構成とすることが可能となる。
（５）表面保護層８の絵柄印刷層６と対向する面と反対の面に、エンボス加工による凹凸形状１０が形成されている。
その結果、絵柄印刷層６によって発泡壁紙１へ付与する意匠性を向上させることが可能となる。
また、第一実施形態の発泡壁紙１の製造方法であれば、以下に記載する効果を奏することが可能となる。
(4) Moisture permeability is within the range of 400 [g/m 2 ·hr] or more and 1000 [g/m 2 ·hr] or less.
As a result, it becomes possible to configure the foamed wallpaper 1 to have moisture permeability suitable for wallpaper.
(5) An
As a result, it becomes possible to improve the design quality imparted to the foamed wallpaper 1 by the pattern printing layer 6.
Moreover, if it is the manufacturing method of the foamed wallpaper 1 of 1st embodiment, it will become possible to show|play the effect described below.
（６）発泡樹脂層４の主成分とする水性エマルジョン樹脂に水溶性の抗菌剤を含有させるとともに、抗菌剤の発泡樹脂層４に対する質量比を０．１［％］以上１．０［％］以下の範囲内として発泡樹脂層４を形成する、発泡樹脂層形成工程を備える。これに加え、表面保護層８を構成する固形成分のうち質量比１０［％］以上３０［％］以下の範囲内でシリコン系樹脂を含んで表面保護層８を形成する、表面保護層形成工程を備える。
このため、最表層ではない発泡樹脂層４に抗菌剤を添加することで、抗菌剤を含有する発泡樹脂層４を表面保護層８が保護する構成となり、ふき取り清掃や洗剤との接触による抗菌剤の除去や、抗菌剤の揮発・昇華による喪失を抑制することが可能となる。
その結果、プラスチック系の壁紙への適用が可能であるとともに、加熱や清掃の後であっても抗菌性を維持することが可能な、発泡壁紙１の製造方法を提供することが可能となる。
(6) Contain a water-soluble antibacterial agent in the aqueous emulsion resin that is the main component of the foamed
Therefore, by adding an antibacterial agent to the foamed
As a result, it is possible to provide a method for producing foamed wallpaper 1 that can be applied to plastic-based wallpaper and maintains antibacterial properties even after heating and cleaning.
第一実施形態を参照しつつ、以下、実施例の発泡壁紙と、比較例の発泡壁紙について説明する。
（実施例１）
実施例１の発泡壁紙は、以下の構成とした。
また、実施例１の発泡壁紙は、透湿度を４００［ｇ／ｍ２・ｈｒ］とした。
・基材
坪量が６５［ｇ／ｍ２］の普通紙を用いて形成した。
・発泡樹脂層
エチレン・酢酸ビニル共重合樹脂（ＥＶＡ樹脂）を主成分とし、充填剤として炭酸カルシウムを８０部、カプセル発泡剤を１０部添加した。そして、発泡倍率を５倍に設定し、坪量が１００［ｇ／ｍ２］となるように形成した。
さらに、発泡樹脂層には、抗菌剤（ＢＣ－４７７）を含有させ、抗菌剤の発泡樹脂層に対する質量比を０．３［％］とした。
・絵柄印刷層
アクリル樹脂系インキを用いて、塗布量が２［ｇ／ｍ２］となるように形成した。
・表面保護層
アクリル系樹脂及びシリコン系樹脂を主成分とし、坪量が５［ｇ／ｍ２］となるように形成した。
The foamed wallpaper of Examples and the foamed wallpaper of Comparative Examples will be described below with reference to the first embodiment.
(Example 1)
The foamed wallpaper of Example 1 had the following configuration.
Further, the foamed wallpaper of Example 1 had a moisture permeability of 400 [g/m 2 ·hr].
- Base material It was formed using plain paper with a basis weight of 65 [g/m 2 ].
- Foamed resin layer The main component was ethylene/vinyl acetate copolymer resin (EVA resin), and 80 parts of calcium carbonate and 10 parts of a capsule foaming agent were added as a filler. Then, the foaming ratio was set to 5 times, and the material was formed to have a basis weight of 100 [g/m 2 ].
Further, the foamed resin layer contained an antibacterial agent (BC-477), and the mass ratio of the antibacterial agent to the foamed resin layer was set to 0.3%.
- Pattern printing layer This layer was formed using acrylic resin ink so that the coating amount was 2 [g/m 2 ].
-Surface protective layer The main components were acrylic resin and silicone resin, and the layer had a basis weight of 5 [g/m 2 ].
（実施例２）
実施例２の発泡壁紙は、透湿度を１０００［ｇ／ｍ２・ｈｒ］とした構成を除き、実施例１の発泡壁紙と同様である。
（実施例３）
実施例３の発泡壁紙は、表面保護層の構成を除き、実施例１の発泡壁紙と同様である。
・表面保護層
アクリル系樹脂及びシリコン系樹脂を主成分とし、坪量が３０［ｇ／ｍ２］となるように形成した。
（実施例４）
実施例４の発泡壁紙は、透湿度を１０００［ｇ／ｍ２・ｈｒ］とした構成と、表面保護層の構成を除き、実施例３の発泡壁紙と同様である。
(Example 2)
The foamed wallpaper of Example 2 is the same as the foamed wallpaper of Example 1, except for the configuration in which the moisture permeability is 1000 [g/m 2 ·hr].
(Example 3)
The foamed wallpaper of Example 3 is the same as the foamed wallpaper of Example 1 except for the structure of the surface protective layer.
-Surface protective layer The main components were acrylic resin and silicone resin, and the layer had a basis weight of 30 [g/m 2 ].
(Example 4)
The foamed wallpaper of Example 4 is the same as the foamed wallpaper of Example 3, except for the moisture permeability of 1000 [g/m 2 ·hr] and the structure of the surface protective layer.
（比較例１）
比較例１の発泡壁紙は、以下の構成とした。
また、比較例１の発泡壁紙は、透湿度を４００［ｇ／ｍ２・ｈｒ］とした。
・基材
坪量が６５［ｇ／ｍ２］の普通紙を用いて形成した。
・発泡樹脂層
エチレン・酢酸ビニル共重合樹脂（ＥＶＡ樹脂）を主成分とし、充填剤として炭酸カルシウムを８０部、カプセル発泡剤を１０部添加した。そして、発泡倍率を５倍に設定し、坪量が１００［ｇ／ｍ２］となるように形成した。
・絵柄印刷層
アクリル樹脂系インキを用いて、塗布量が２［ｇ／ｍ２］となるように形成した。
・表面保護層
アクリル系樹脂及びシリコン系樹脂を主成分とし、坪量が３０［ｇ／ｍ２］となるように形成した。
さらに、表面保護層には、抗菌剤（ゼオミック ＡＶ－１０Ｄ）を含有させ、抗菌剤の表面保護層に対する質量比を０．３［％］とした。
(Comparative example 1)
The foamed wallpaper of Comparative Example 1 had the following configuration.
Further, the foamed wallpaper of Comparative Example 1 had a moisture permeability of 400 [g/m 2 ·hr].
- Base material It was formed using plain paper with a basis weight of 65 [g/m 2 ].
- Foamed resin layer The main component was ethylene/vinyl acetate copolymer resin (EVA resin), and 80 parts of calcium carbonate and 10 parts of a capsule foaming agent were added as a filler. Then, the foaming ratio was set to 5 times, and the material was formed to have a basis weight of 100 [g/m 2 ].
- Pattern printing layer This layer was formed using acrylic resin ink so that the coating amount was 2 [g/m 2 ].
-Surface protective layer The main components were acrylic resin and silicone resin, and the layer had a basis weight of 30 [g/m 2 ].
Furthermore, the surface protective layer contained an antibacterial agent (Zeomic AV-10D), and the mass ratio of the antibacterial agent to the surface protective layer was set to 0.3%.
（比較例２）
比較例２の発泡壁紙は、透湿度を１０００［ｇ／ｍ２・ｈｒ］とした構成を除き、比較例１の発泡壁紙と同様である。
（比較例３）
比較例３の発泡壁紙は、表面保護層の構成を除き、比較例２の発泡壁紙と同様である。
・表面保護層
アクリル系樹脂及びシリコン系樹脂を主成分とし、坪量が３０［ｇ／ｍ２］となるように形成した。
さらに、表面保護層には、抗菌剤（ゼオミック ＡＶ－１０Ｄ）を含有させ、抗菌剤の表面保護層に対する質量比を２．０［％］とした。
(Comparative example 2)
The foamed wallpaper of Comparative Example 2 is the same as the foamed wallpaper of Comparative Example 1, except for the configuration in which the moisture permeability is 1000 [g/m 2 ·hr].
(Comparative example 3)
The foamed wallpaper of Comparative Example 3 is the same as the foamed wallpaper of Comparative Example 2 except for the structure of the surface protective layer.
-Surface protective layer The main components were acrylic resin and silicone resin, and the layer had a basis weight of 30 [g/m 2 ].
Furthermore, the surface protective layer contained an antibacterial agent (Zeomic AV-10D), and the mass ratio of the antibacterial agent to the surface protective layer was set to 2.0%.
（比較例４）
比較例４の発泡壁紙は、以下の構成とした。
また、比較例４の発泡壁紙は、透湿度を１０００［ｇ／ｍ２・ｈｒ］とした。
・基材
坪量が６５［ｇ／ｍ２］の普通紙を用いて形成した。
・発泡樹脂層
エチレン・酢酸ビニル共重合樹脂（ＥＶＡ樹脂）を主成分とし、充填剤として炭酸カルシウムを８０部、カプセル発泡剤を１０部添加した。そして、発泡倍率を５倍に設定し、坪量が１００［ｇ／ｍ２］となるように形成した。
さらに、発泡樹脂層には、抗菌剤（ゼオミック ＡＶ－１０Ｄ）を含有させ、抗菌剤の発泡樹脂層に対する質量比を２．０［％］とした。
・絵柄印刷層
アクリル樹脂系インキを用いて、塗布量が２［ｇ／ｍ２］となるように形成した。
・表面保護層
アクリル系樹脂及びシリコン系樹脂を主成分とし、坪量が３０［ｇ／ｍ２］となるように形成した。
(Comparative example 4)
The foamed wallpaper of Comparative Example 4 had the following configuration.
Further, the foamed wallpaper of Comparative Example 4 had a moisture permeability of 1000 [g/m 2 ·hr].
- Base material It was formed using plain paper with a basis weight of 65 [g/m 2 ].
- Foamed resin layer The main component was ethylene/vinyl acetate copolymer resin (EVA resin), and 80 parts of calcium carbonate and 10 parts of a capsule foaming agent were added as a filler. Then, the foaming ratio was set to 5 times, and the material was formed to have a basis weight of 100 [g/m 2 ].
Further, the foamed resin layer contained an antibacterial agent (Zeomic AV-10D), and the mass ratio of the antibacterial agent to the foamed resin layer was set to 2.0%.
- Pattern printing layer This layer was formed using acrylic resin ink so that the coating amount was 2 [g/m 2 ].
-Surface protective layer The main components were acrylic resin and silicone resin, and the layer had a basis weight of 30 [g/m 2 ].
（比較例５）
比較例５の発泡壁紙は、発泡樹脂層の構成を除き、比較例４の発泡壁紙と同様である。
・発泡樹脂層
エチレン・酢酸ビニル共重合樹脂（ＥＶＡ樹脂）を主成分とし、充填剤として炭酸カルシウムを８０部、カプセル発泡剤を１０部添加した。そして、発泡倍率を５倍に設定し、坪量が１００［ｇ／ｍ２］となるように形成した。
さらに、発泡樹脂層には、抗菌剤（ＢＣ－４７７）を含有させ、抗菌剤の発泡樹脂層に対する質量比を２．０［％］とした。
（比較例６）
比較例６の発泡壁紙は、透湿度を１００［ｇ／ｍ２・ｈｒ］とした構成を除き、比較例５の発泡壁紙と同様である。
(Comparative example 5)
The foamed wallpaper of Comparative Example 5 is the same as the foamed wallpaper of Comparative Example 4 except for the structure of the foamed resin layer.
- Foamed resin layer The main component was ethylene/vinyl acetate copolymer resin (EVA resin), and 80 parts of calcium carbonate and 10 parts of a capsule foaming agent were added as a filler. Then, the foaming ratio was set to 5 times, and the material was formed to have a basis weight of 100 [g/m 2 ].
Furthermore, the foamed resin layer contained an antibacterial agent (BC-477), and the mass ratio of the antibacterial agent to the foamed resin layer was set to 2.0%.
(Comparative example 6)
The foamed wallpaper of Comparative Example 6 is the same as the foamed wallpaper of Comparative Example 5 except for the configuration in which the moisture permeability is 100 [g/m 2 ·hr].
（性能評価）
実施例の発泡壁紙と、比較例の発泡壁紙に対し、それぞれ、通常の状態における抗菌性と、拭き取り後の抗菌性に対する性能評価を行った。
通常の状態における抗菌性は、壁装問屋協議会の規格である「抗菌壁紙性能規定」の試験方法に基づき、「生菌数が０．６３以下」の場合を合格として評価し、「生菌数が０．６３を超える」場合を不合格として評価した。
拭き取り後の抗菌性は、壁装問屋協議会の規格である「抗菌壁紙性能規定」の試験方法に基づき、「生菌数が０．６３以下」の場合を合格として評価し、「生菌数が０．６３を超える」場合を不合格として評価した。
評価結果は表１中に表す。
(Performance evaluation)
The foamed wallpaper of the example and the foamed wallpaper of the comparative example were evaluated for antibacterial properties under normal conditions and antibacterial properties after wiping, respectively.
Antibacterial properties under normal conditions are evaluated as passing if the number of viable bacteria is 0.63 or less, based on the test method of the Antibacterial Wallpaper Performance Regulations, which is the standard of the Wall Covering Wholesalers Association. If the number exceeds 0.63, it was evaluated as a failure.
The antibacterial properties after wiping are evaluated based on the test method of the "Antibacterial Wallpaper Performance Regulations", which is a standard of the Wall Covering Wholesalers Association, and a "viable bacteria count of 0.63 or less" is considered a pass; exceeds 0.63" was evaluated as a failure.
The evaluation results are shown in Table 1.
（評価結果）
表１中に表されるように、実施例の発泡壁紙は、比較例の発泡壁紙と比較して、通常の状態における抗菌性と、拭き取り後の抗菌性が高いことが確認された。
(Evaluation results)
As shown in Table 1, it was confirmed that the foamed wallpaper of the example had higher antibacterial properties under normal conditions and higher antibacterial properties after wiping, compared to the foamed wallpaper of the comparative example.
１…発泡壁紙、２…基材、４…発泡樹脂層、６…絵柄印刷層、８…表面保護層、１０…凹凸形状 DESCRIPTION OF SYMBOLS 1... Foamed wallpaper, 2... Base material, 4... Foamed resin layer, 6... Pattern printing layer, 8... Surface protection layer, 10... Uneven shape
Claims (4)
前記発泡樹脂層は、水性エマルジョン樹脂を主成分として形成され、且つ水溶性の抗菌剤を含有し、
前記抗菌剤の前記発泡樹脂層に対する質量比は、０．１％以上１．０％以下の範囲内であり、
前記表面保護層は、前記表面保護層を構成する固形成分のうち質量比１０％以上３０％以下の範囲内でシリコン系樹脂を含み、さらに、シリコン系樹脂以外の樹脂成分として、アクリル酸及びメタクリル酸、ないしはそれらのエステルのうちから選択した一種以上のモノマーから形成される重合体、または、重合体に対してスチレン、酢酸ビニル、エチレン及びα‐オレフィンのうち一種以上のモノマーないしはブロックコポリマーを共重合させることによって得られる重合体を含み、
前記抗菌剤は、有機窒素硫黄系の抗菌剤であることを特徴とする発泡壁紙。 A base material, a foamed resin layer laminated on the base material, a pattern printing layer laminated on the foamed resin layer, and a surface protection layer laminated on the pattern printing layer,
The foamed resin layer is formed mainly of a water-based emulsion resin and contains a water-soluble antibacterial agent,
The mass ratio of the antibacterial agent to the foamed resin layer is within the range of 0.1% or more and 1.0% or less,
The surface protective layer contains silicone resin in a mass ratio of 10% to 30% of the solid components constituting the surface protective layer, and further contains acrylic acid and acrylic acid as resin components other than the silicone resin. A polymer formed from one or more monomers selected from methacrylic acid or their esters, or a polymer formed from one or more monomers or block copolymers selected from styrene, vinyl acetate, ethylene and α-olefins. Including a polymer obtained by copolymerizing,
The foamed wallpaper is characterized in that the antibacterial agent is an organic nitrogen sulfur-based antibacterial agent .
前記発泡樹脂層を形成する発泡樹脂層形成工程と、前記表面保護層を形成する表面保護層形成工程と、を備え、
前記発泡樹脂層形成工程では、前記発泡樹脂層の主成分とする水性エマルジョン樹脂に水溶性且つ有機窒素硫黄系の抗菌剤を含有させるとともに、前記抗菌剤の前記発泡樹脂層に対する質量比を０．１％以上１．０％以下の範囲内として前記発泡樹脂層を形成し、
前記表面保護層形成工程では、前記表面保護層を構成する固形成分のうち質量比１０％以上３０％以下の範囲内でシリコン系樹脂を含み、さらに、シリコン系樹脂以外の樹脂成分として、アクリル酸及びメタクリル酸、ないしはそれらのエステルのうちから選択した一種以上のモノマーから形成される重合体、または、重合体に対してスチレン、酢酸ビニル、エチレン及びα‐オレフィンのうち一種以上のモノマーないしはブロックコポリマーを共重合させることによって得られる重合体を含んで前記表面保護層を形成することを特徴とする発泡壁紙の製造方法。 A method for producing foamed wallpaper comprising a base material, a foamed resin layer laminated on the base material, a pattern printing layer laminated on the foamed resin layer, and a surface protection layer laminated on the pattern printing layer,
comprising a foamed resin layer forming step of forming the foamed resin layer, and a surface protective layer forming step of forming the surface protective layer,
In the foamed resin layer forming step, a water-soluble, organic nitrogen sulfur-based antibacterial agent is contained in the aqueous emulsion resin that is the main component of the foamed resin layer, and the mass ratio of the antibacterial agent to the foamed resin layer is set to 0. Forming the foamed resin layer within a range of 1% or more and 1.0% or less,
In the surface protective layer forming step, the solid components constituting the surface protective layer contain a silicone resin in a mass ratio of 10% to 30%, and further include acrylic resin as a resin component other than the silicone resin. A polymer formed from one or more monomers selected from acid and methacrylic acid or their esters, or a polymer formed from one or more monomers or blocks selected from styrene, vinyl acetate, ethylene and α-olefin. A method for producing foamed wallpaper, characterized in that the surface protective layer includes a polymer obtained by copolymerizing a copolymer .