JP2021172771A - 中空粒子の製造方法 - Google Patents
中空粒子の製造方法 Download PDFInfo
- Publication number
- JP2021172771A JP2021172771A JP2020079415A JP2020079415A JP2021172771A JP 2021172771 A JP2021172771 A JP 2021172771A JP 2020079415 A JP2020079415 A JP 2020079415A JP 2020079415 A JP2020079415 A JP 2020079415A JP 2021172771 A JP2021172771 A JP 2021172771A
- Authority
- JP
- Japan
- Prior art keywords
- monomer
- hollow particles
- solvent
- mass
- organic solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明の中空粒子の製造方法において、前記懸濁安定剤(D)が、ノニオニックアニオン系界面活性剤を含むものであることが好ましい。
本発明の中空粒子の製造方法において、前記ノニオニックアニオン系界面活性剤として、ポリオキシエチレンアルキルエーテル硫酸塩を用いることが好ましい。
本発明の中空粒子の製造方法において、前記懸濁安定剤(D)の使用量が、前記油相を構成する全成分100質量部に対して0.015〜3.0質量部であることが好ましい。
本発明の中空粒子の製造方法において、前記単量体(A)が、親水性基含有単量体を含むことが好ましい。
本発明の中空粒子の製造方法において、前記単量体(A)が、親水性基含有単量体として、酸基含有単量体を含むことが好ましい。
本発明の中空粒子の製造方法において、前記単量体(A)が、前記酸基含有単量体として、(メタ)アクリル酸単量体を含むことが好ましい。
本発明の中空粒子の製造方法において、前記単量体(A)100質量%中における、前記酸基含有単量体の量が、0.5〜15質量%であることが好ましい。
本発明の中空粒子の製造方法において、前記貫通孔の孔径が、50〜500nmであることが好ましい。
本発明の中空粒子の製造方法において、前記中空粒子の個数平均粒子径が、1〜13μmであることが好ましい。
貫通孔を有する中空粒子の製造方法であって、
単量体(A)、油溶性重合開始剤(B)、有機溶剤(C)、懸濁安定剤(D)、および水系媒体(E)を含む混合液を懸濁させることにより、前記水系媒体(E)に、前記単量体(A)、前記油溶性重合開始剤(B)、および前記有機溶剤(C)を含む油相が分散した懸濁液を調製する懸濁工程と、
前記懸濁液中の前記単量体(A)を重合することにより、前記有機溶剤(C)を内包するとともに、貫通孔を有する前駆体粒子を含む前駆体分散液を調製する重合工程と、
前記前駆体分散液から前記有機溶剤(C)を除去することにより、貫通孔を有する中空粒子を得る除去工程と、を備え、
前記有機溶剤(C)が、10℃における水100gに対する溶解度が1g/100g以下の疎水性溶剤と、10℃における水100gに対する溶解度が1g/100g超、100g/100g未満の親水性溶剤と、を含むものであり、
前記親水性溶剤の使用量が、前記単量体(A)100質量部に対して0.5〜40質量部であるものである。
以下、本発明の製造方法の各工程について説明する。
懸濁工程は、単量体(A)、油溶性重合開始剤(B)、有機溶剤(C)、懸濁安定剤(D)、および水系媒体(E)を含む混合液を懸濁させることにより、水系媒体(E)に、単量体(A)、油溶性重合開始剤(B)、および有機溶剤(C)を含む油相が分散した懸濁液を調製する工程である。
本発明で用いる単量体(A)としては、特に限定されないが、たとえば、ビニル官能基を1つ有する化合物であるモノビニル単量体や、重合可能な官能基を2つ以上有する架橋性単量体を挙げることができる。
本発明で用いる油溶性重合開始剤(B)は、10℃の水100gに対する溶解度が0.2g/100g以下の親油性のものであれば特に制限されない。油溶性重合開始剤(B)としては、たとえば、ベンゾイルペルオキシド、ラウロイルペルオキシド、t−ブチルペルオキシド−2−エチルヘキサノエート、オルソクロロベンゾイルペルオキシド、オルソメトキシベンゾイルペルオキシド、3,5,5−トリメチルヘキサノイルペルオキシド、ジ−t−ブチルペルオキシド等の有機過酸化物;2,2’−アゾビス(2,4−ジメチルバレロニトリル)、2,2’−アゾビスイソブチロニトリル、1,1’−アゾビスシクロヘキサンカルボニトリル等のアゾ系化合物等が挙げられる。
本発明で用いる有機溶剤(C)は、10℃における水100gに対する溶解度が1g/100g以下の疎水性溶剤と、10℃における水100gに対する溶解度が1g/100g超、100g/100g未満の親水性溶剤と、を含むものである。
ヘプタン(1.9)、シクロヘキサン(2.0)、ベンゼン(2.3)、トルエン(2.4)。
懸濁安定剤(D)は、後述する懸濁重合法における懸濁液中の懸濁状態を安定化させる作用を奏する。本発明においては、懸濁安定剤(D)としては、ノニオニックアニオン系界面活性剤を含むものとすることが好ましく、このような懸濁安定剤(D)の作用により、後述する懸濁重合法において、単量体(A)、油溶性重合開始剤(B)、および、有機溶剤(C)を内包するミセルを形成することができる。
R1−O−(CR2R3CR4R5)n−SO3M (1)
(上記一般式(1)中、R1は、炭素数6〜16のアルキル基、または炭素数1〜25のアルキル基で置換されていてもよい炭素数6〜14のアリール基、R2〜R5は、水素およびメチル基よりなる群からそれぞれ独立して選ばれる基、Mは、アルカリ金属原子またはアンモニウムイオン、nは3〜40である。)
水系媒体(E)としては、通常、水が用いられるが、水に加えて、10℃における水100gに対する溶解度が、100g/100g以上の溶媒を併用してもよい。
重合工程は、上述した懸濁工程において得られた懸濁液を重合させることにより、有機溶剤(C)を内包した前駆体粒子を含む前駆体分散液を調製する工程である。ここで、前駆体粒子とは、単量体(A)を重合させることにより形成される粒子である。
除去工程は、前駆体粒子に内包される有機溶剤(C)を除去することにより、貫通孔を有する中空粒子を得る工程である。
空隙率(%)=[使用する疎水性溶剤の体積(ml)/{使用する単量体の体積(ml)+使用する疎水性溶剤の体積(ml)}]×100
なお、中空粒子の空隙率は、たとえば、疎水性溶剤の使用量を調整すること等により、調製することができる。
中空粒子の空隙率は、中空粒子を製造する際の、使用する疎水性溶剤の体積および使用する単量体の体積から、以下の式を用いて算出した。
空隙率(%)=[使用する疎水性溶剤の体積(ml)/{使用する単量体の体積(ml)+使用する疎水性溶剤の体積(ml)}]×100
(疎水性溶剤として使用したシクロヘキサンの体積は、シクロヘキサンの比重を0.779g/mlとして計算し、使用した単量体の体積は、単量体の比重を1.0g/mlとして計算した。)
レーザー回析式粒度分布測定器(商品名「SALD−2000」、島津製作所社製)を用いて各中空粒子の粒子径を測定し、その個数平均をそれぞれ算出し、得られた値をその中空粒子の個数平均粒子径とした。
中空粒子のシェル厚は、上記にて算出した中空粒子の空隙率と、個数平均粒子径とから算出した。
貫通孔の孔径は、以下のようにして求めた。すなわち、まず、走査型電子顕微鏡により、無作為に選択された100個の中空粒子を観察し、それぞれの中空粒子における最大の貫通孔の孔径を測定した。そして、それぞれの中空粒子における、最大の貫通孔の孔径の個数平均を算出し、得られた値を、中空粒子の貫通孔の孔径とした。
以下の式により、中空粒子内の残留溶剤量を算出した。残留溶剤量が少ないほど、中空粒子の中空中の溶剤の残存量が効果的に低減されたものと判断できる。
残留溶剤量(%)=100×(全固形分量−理論固形分量)/全固形分量
(全固形分量は、中空粒子を105℃で2時間加熱した後の固形分の全量の実測値(g)であり、理論固形分量は、溶剤を含まない中空粒子の質量の理論値(g)である。)
中空粒子の重合時安定性は、重合後の前駆体分散液を、80メッシュの金網により濾過し、濾過残渣として得られる凝集物の有無を確認し、凝集物が見られなかったものを○、凝集物が見られたものを×として評価した。凝集物が見られないものであれば、重合時安定性に優れていると判断できる。
中空粒子の潰れ割合は、中空粒子を、走査型電子顕微鏡で100個の中空粒子を観察し、観察した中空粒子中における、潰れた中空粒子および割れた中空粒子の個数の割合を算出することにより求めた。
(懸濁工程)
まず、メタクリル酸5部、エチレングリコールジメタクリレート95部、2,2’−アゾビス(2,4−ジメチルバレロニトリル)(油溶性重合開始剤、商品名「V−65」、和光純薬社製)3.33部、メチルエチルケトン(親水性溶剤、10℃における水100gに対する溶解度:35g/100g)3部、およびシクロヘキサン563.7部(疎水性溶剤、10℃における水100gに対する溶解度:0.36g/100g)を混合し、これを油相とした。
次いで、イオン交換水1300部に、ポリオキシエチレンアルキル硫酸ナトリウム(ノニオニックアニオン系界面活性剤、商品名「ラテムルE−118B」、花王社製)0.10部(油相100部に対して0.015部)を混合し、これを水相とした。
そして、水相と油相とを混合することにより、混合液を調製した。
懸濁工程にて得られた懸濁液を、65℃に昇温した後、65℃の温度条件を3時間維持し、重合反応を行った。この重合反応により、シクロヘキサンを内包した前駆体粒子を含む前駆体分散液を得た。得られた前駆体分散液について、重合時安定性を評価した。結果を表1に示す。
まず、重合工程で得られた前駆体分散液につき、冷却高速遠心機(商品名「H−9R」、コクサン社製)により、ローターMN1、回転数3,000rpm、遠心分離時間20分間の条件で遠心分離を行い、固形分を脱水した(固液分離)。脱水後の固形分を乾燥機にて40℃の温度で乾燥させ、シクロヘキサンを内包した前駆体粒子を得た。
シクロヘキサンの使用量を、563.7部から556.7部に、メチルエチルケトンの使用量を、3部から10部に、それぞれ変更した以外は、実施例1と同様にして、中空粒子(2)を得て、同様に評価を行った。結果を表1に示す。
シクロヘキサンの使用量を、556.7部から275.0部に変更した以外は、実施例2と同様にして、中空粒子(3)を得て、同様に評価を行った。結果を表1に示す。
メチルエチルケトンを使用しなかった以外は、実施例2と同様にして、中空粒子(4)を得て、同様に評価を行った。結果を表1に示す。また、中空粒子(4)を走査型電子顕微鏡により観察して得た画像を、図2に示す。
シクロヘキサンの使用量を、563.7部から516.7部に、メチルエチルケトンの使用量を、3部から50部に、それぞれ変更した以外は、実施例1と同様にして、中空粒子(5)を得て、同様に評価を行った。なお、比較例2においては、重合時安定性に劣るものであり、重合後の前駆体分散液の段階で、多量の凝集物が発生してしまい、中空粒子を得ることができなかった。
メチルエチルケトン10部に代えて、ドデカン(疎水性溶剤、10℃における水100gに対する溶解度:0.1g/100g未満)10部を使用した以外は、実施例2と同様にして、中空粒子(6)を得て、同様に評価を行った。結果を表1に示す。
(懸濁工程)
まず、メタクリル酸41部、エチレングリコールジメタクリレート59部、2,2’−アゾビス(2,4−ジメチルバレロニトリル)(油溶性重合開始剤、商品名「V−65」、和光純薬社製)3.33部、リノール酸3部、およびシクロヘキサン563.7部を混合し、これを油相とした。
次いで、イオン交換水1300部に、ドデシルベンゼンスルホン酸ナトリウム(商品名「ネオペレックスG−15」、花王社製)0.50部(油相100部に対し0.075部)を混合し、これを水相とした。
そして、水相と油相とを混合することにより、混合液を調製した。
懸濁工程にて得られた懸濁液を、65℃に昇温した後、65℃の温度条件を3時間維持し、重合反応を行った。この重合反応により、シクロヘキサンを内包した前駆体粒子を含む前駆体分散液を得た。得られた前駆体分散液について、重合時安定性を評価した。結果を表1に示す。
重合工程にて得られた、冷却後の前駆体分散液に、10%の水酸化ナトリウム水溶液を、反応容器中の混合物のpHが7.0となるまで反応容器に添加した。なお、水酸化ナトリウム水溶液の添加は、前駆体分散液をインライン型乳化分散機により攪拌しながら行った。
塩基添加工程を経た前駆体分散液100部に対し、さらに消泡剤を0.1〜0.5質量部の範囲内で添加し、窒素を流速6min/Lで吹きこみながら、70℃で6時間維持し、前駆体粒子からシクロヘキサンを除去することにより、中空粒子(6)を得た。そして、得られた中空粒子(6)について、実施例1と同様に評価を行った。結果を表1に示す。
一方、有機溶媒として親水性溶剤を使用しなかった場合は、実施例1,2と同様の空隙率および粒子径を有する中空粒子を製造しようとしても、貫通孔が適切に形成されず、有機溶剤(C)が多量に残存する結果となり、さらには、有機溶剤(C)を除去する際に、粒子の潰れが顕著に発生してしまい、良好な中空粒子を得ることができなかった(比較例1,3、図2)。
また、用いる親水性溶剤の使用量が多すぎた場合は、重合時安定性に劣るものであり、重合後の前駆体分散液の段階で、多量の凝集物が発生してしまい、中空粒子を得ることができなかった(比較例2)。
また、有機溶媒として親水性溶剤を使用せず、代わりに、リノール酸を用い、かつ、pH調整を行った場合には、貫通孔が形成されたものの、その孔径が小さく、有機溶剤(C)が、比較的多く残存する結果となり、さらには、有機溶剤(C)を除去する際に、粒子の潰れが多く発生してしまい、良好な中空粒子を得ることができなかった(比較例4)。
Claims (11)
- 貫通孔を有する中空粒子の製造方法であって、
単量体(A)、油溶性重合開始剤(B)、有機溶剤(C)、懸濁安定剤(D)、および水系媒体(E)を含む混合液を懸濁させることにより、前記水系媒体(E)に、前記単量体(A)、前記油溶性重合開始剤(B)、および前記有機溶剤(C)を含む油相が分散した懸濁液を調製する懸濁工程と、
前記懸濁液中の前記単量体(A)を重合することにより、前記有機溶剤(C)を内包するとともに、貫通孔を有する前駆体粒子を含む前駆体分散液を調製する重合工程と、
前記前駆体分散液から前記有機溶剤(C)を除去することにより、貫通孔を有する中空粒子を得る除去工程と、を備え、
前記有機溶剤(C)が、10℃における水100gに対する溶解度が1g/100g以下の疎水性溶剤と、10℃における水100gに対する溶解度が1g/100g超、100g/100g未満の親水性溶剤と、を含むものであり、
前記親水性溶剤の使用量が、前記単量体(A)100質量部に対して0.5〜40質量部である中空粒子の製造方法。 - 前記親水性溶剤の使用量が、前記単量体(A)100質量部に対して0.2〜10質量部である請求項1に記載の中空粒子の製造方法。
- 前記懸濁安定剤(D)が、ノニオニックアニオン系界面活性剤を含むものである請求項1または2に記載の中空粒子の製造方法。
- 前記ノニオニックアニオン系界面活性剤として、ポリオキシエチレンアルキルエーテル硫酸塩を用いる請求項3に記載の中空粒子の製造方法。
- 前記懸濁安定剤(D)の使用量が、前記油相を構成する全成分100質量部に対して0.015〜3.0質量部である請求項1〜4のいずれかに記載の中空粒子の製造方法。
- 前記単量体(A)が、親水性基含有単量体を含む請求項1〜5のいずれかに記載の中空粒子の製造方法。
- 前記単量体(A)が、親水性基含有単量体として、酸基含有単量体を含む請求項6に記載の中空粒子の製造方法。
- 前記単量体(A)が、前記酸基含有単量体として、(メタ)アクリル酸単量体を含む請求項7に記載の中空粒子の製造方法。
- 前記単量体(A)100質量%中における、前記酸基含有単量体の量が、0.5〜15質量%である請求項7または8に記載の中空粒子の製造方法。
- 前記貫通孔の孔径が、50〜500nmである請求項1〜9のいずれかに記載の中空粒子の製造方法。
- 前記中空粒子の個数平均粒子径が、1〜13μmである請求項1〜10のいずれかに記載の中空粒子の製造方法。