JP2021074495A - 記念品用組成物、記念品、記念品の使用方法および多層温熱懐炉 - Google Patents
記念品用組成物、記念品、記念品の使用方法および多層温熱懐炉 Download PDFInfo
- Publication number
- JP2021074495A JP2021074495A JP2020101476A JP2020101476A JP2021074495A JP 2021074495 A JP2021074495 A JP 2021074495A JP 2020101476 A JP2020101476 A JP 2020101476A JP 2020101476 A JP2020101476 A JP 2020101476A JP 2021074495 A JP2021074495 A JP 2021074495A
- Authority
- JP
- Japan
- Prior art keywords
- derived
- souvenir
- composition
- waste
- naturally
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明に係る記念品用組成物は、塩化ナトリウムと1種又は2種以上の廃棄物由来、自然由来又は動物由来材料とを含む。本明細書において、「記念品用組成物」とは、記念品に使用される組成物を意味する。本明細書において、「記念品」とは、使用者の思いに寄り添い、記憶を呼び起こし、癒やし、しばしの幸福感を与える効果を有する物品を意味する。このような物品としては、例えば、旅先のお土産品として取り扱われる物品、旅先や故郷の特産品を含む物品、血縁の有無を問わず何らかの縁のあった人間または動物由来の成分を含む物品等が挙げられ、これには、温熱懐炉、お守り、造形物が含まれる。なお、本明細書においては、特に断らない限り、温熱懐炉といえば、温熱懐炉を2個以上組み合わせた多層温熱懐炉を含む。
(1)同じ混合割合での冷めにくさの観点では、リン酸カルシウム>>珪砂>珊瑚砂の傾向があり、同混合割合でのレンジ取り出し直後の温度は、概ね珊瑚砂>珪砂>リン酸カルシウムの傾向がある(図1)。
(2)塩化ナトリウムと珪砂の混合物は、珪砂の混合割合にして10重量%〜25重量%という比較的広範囲で、冷めにくさに変わりがない傾向がある。
(3)塩化ナトリウムと珊瑚砂の混合物は、塩80珊瑚20または塩75珊瑚25の混合割合が特に冷めにくい性質がある(図2)。
(4)塩化ナトリウムとリン酸カルシウムの混合物は、リン酸カルシウムの割合が増えるにつれ、冷めにくくなる傾向がある。
タッパー(縦12cm×横8cm×高さ3cm)に食用塩を220g、すりきり一杯、タッパー内での高さにして約3cm(かさ密度0.76g/cm3、真密度:2.16g/cm3、気孔率:64.8%)になるまで敷き詰め、表面に霧吹きで50回水を噴霧した(噴霧量にして10cc、食用塩重量に対して4.5重量%)のち、900Wの電子レンジで2分加熱した。その後、タッパーの蓋を開けた状態で、表面から約2cmの深さを中心部温度とし、表面から約1cmの深さを表面温度とみなして市販のデジタル温度計(ドリテック DRETEC O-274IV クッキング温度計)で温度の時間変化を計測した。結果を表1に示す。
塩に代えて炭酸カルシウムを主成分とする珊瑚砂を220g、タッパー内での高さにして約2.6cm(かさ密度0.88g/cm3、真密度:2.7〜2.9g/cm3、気孔率:67.4%〜70.0%)になるまで敷き詰め、水を50回(噴霧量にして10cc、珊瑚砂重量に対して4.5重量%)噴霧したほかは実施例1と同様にして温度の時間変化を計測した。結果を表1に示す。
塩に代えて珊瑚砂を220g、タッパー内での高さにして約2.6cmになるまで敷き詰め、水を200回以上噴霧して全体を湿らせたほかは実施例1と同様にして温度の時間変化を計測した。結果を表1に示す。
塩に代えて与論島で採取した海辺の砂を220g、タッパー内での高さにして約2.8cm(かさ密度0.82g/cm3、真密度:2.5g/cm3、気孔率:67.2%)になるまで敷き詰め、水を噴霧したほかは実施例1と同様にして温度の時間変化を計測した。結果を表1に示す。
霧吹きではなく、直接水を通してから水を切ることによって得られた、含水率としては実施例3の珊瑚砂2よりも高い「雨の砂浜状」の珊瑚砂3を使用し、900Wの電子レンジによる加熱時間を変えて、レンジ取り出し直後の温度を測ってみた。結果を表2に示す。
実施例2,実施例3の結果と表2から、珊瑚砂は、水分を含ませすぎると温度が上がりにくく、水分がなくなるとそれ以上上昇しない傾向があり、温熱懐炉の中心部が湿らない程度に表面に水を噴霧することが重要であることがわかった。この結果は、噴霧回数が少ない方が簡便であるので好都合である。
実施例5の結果に鑑み、実施例2において、レンジ取り出し直後に表面が水の沸点付近に達している一方、深層部が水の沸点を超えて上昇した理由は、深層部の水がほとんどない状態では、水の比熱(4189J/Kg/℃)に比べて、炭酸カルシウムや空気の比熱(石灰岩の値で920J/Kg/℃、空気は1000J/Kg/℃程度)が約4分の1程度と低いことにより、急激に温度上昇したものと考えられる。
リン酸カルシウム含有成分として、市販の天然骨灰(メーカー名:株式会社竹昇精工、品番:商品コードTO804013)をタッパー(縦12cm×横8cm×高さ3cm)に110g、タッパー内での高さにして約2.5cm(かさ密度0.46g/cm3、真密度:3.14g/cm3、気孔率:85.4%)まで敷き詰め、表面に霧吹きで50回(実施例6−1)または230回(実施例6−2)水を噴霧したのち、900Wの電子レンジで2分加熱した。その後、タッパーの蓋を開けた状態で、中心部辺りと表面付近に市販のデジタル温度計(ドリテック DRETEC O-274IV クッキング温度計)を差し込み、温度Tの時間変化を計測し、性状を目視観察した。結果を表3に示す。なお、温度の時間変化は、暫定的に以下のモデル式でT0およびBを変数として最小二乗法によりカーブフィッティングした。(以下、特に断らない限り、T0はレンジ取り出し直後の深層温度値,T∞は、一定に管理された室内温度、Bは下記式の係数を意味し、σ2は誤差分散である)。なお、Bは冷めにくさの指標として使用した。
T=T∞+(T0−T∞)exp(−Bt)
実施例6−2
表面に霧吹きで230回水を噴霧し、深層部まで湿らせたほかは実施例6−1と同様にして、温度の時間変化を計測し、性状を目視観察した。結果を表3に示す。
実施例6−3
表面に霧吹きしなかったほかは実施例6−1と同様にして、温度の時間変化を計測し、性状を目視観察した。結果を表3に示す。
縦約17cm×横約11.5cmの不織布にあら塩(産地:瀬戸内のあら塩、メーカー名:ソルトカンパニー株式会社)とリン酸カルシウムとを合計100gになるように入れて、縦真半分に折り(縦約8.5cm×横約11.5cm)、900Wの電子レンジで1分間、加熱した。図6に示すように、取り出して新聞紙の上に置き、縦半分に折り曲げた所を再び戻し、温度計を指し込んだ。温度の経時変化の測定結果を表4に示す。
縦約17cm×横約11.5cmの不織布に塩と珊瑚とを合計100gになるように入れて、50回霧吹きをかけ、縦真半分に折り(縦約8.5cm×横約11.5cm)、500Wの電子レンジで1分30秒間、加熱した。図6に示すように、取り出して新聞紙の上に置き、縦半分に折り曲げた所を再び戻し、温度計を指し込んだ。温度の経時変化の測定結果を表5に示す。なお、周囲環境は、室温25度、湿度51%であった。
150ccビーカーに純粋な珊瑚砂100g、または、あら塩と珊瑚砂とを所定の割合でよく混合して得られた組成物を合計100gになるように入れ、紙皿を2枚重ねで敷いた900Wの電子レンジで1分間加熱した。加熱後、図7に示すように中心部に料理温度計(DAISO製C008、ガラス製、指示液:ケロシン)を立てて差し込み、ビーカーの注ぎ口部分にはめるように倒した。温度計を倒した際にできる内容部の隙間はかぶせて埋めた。このような操作により、温度計の位置が変わらず、温度計の位置がほぼ同じにセットでき、不織布に水分がにじんだりせず、一ミリも動かさないで観察できる状態となった。温度の経時変化の測定結果を表6に示す。なお、周囲環境は、エアコンの設定温度が22度、湿度35%とした。
珊瑚砂に代えてリン酸カルシウム粉末を使用した他は実施例9と同様にして、温度の経時変化を観察した。結果を表7に示す。なお、周囲環境は、エアコンの設定温度が22度、湿度35%であった。
リン酸カルシウム粉末に代えて珪砂を使用した他は実施例9と同様にして、温度の経時変化を観察した。結果を表8に示す。なお、周囲環境は、エアコンの設定温度が22度、湿度35%であった。
上記実施例9ないし11の検討結果に基づき、表9に記載した3成分系および4成分系の組成で実施例9と同様の条件の放熱試験を行った。結果を表9に示す。なお、周囲環境は、エアコンの設定温度が22度、湿度35%であった。
図8および図9に示すように、ポリエチレン製の食品棚クッションシートを4回巻き付けた他は、実施例12と同様の条件で放熱試験を行った。結果を表10に示す。なお、周囲環境は、エアコンの設定温度が22度、湿度35%であった。
150ccビーカーに合計100gのあら塩を入れた普通のビーカー1と、周りをポリエチレン製の食品棚クッションシートで包んだビーカー2の2パターンを使い、紙皿を2枚重ねで敷いた900Wの電子レンジで1分間加熱した。加熱後、図7に示すように中心部に料理温度計(DAISO製C008、ガラス製、指示液:ケロシン)を立てて差し込み、ビーカーの注ぎ口部分にはめるように倒した。温度計を倒した際にできる内容部の隙間はかぶせて埋め、温度の経時変化を測定した。ここで、「湿っている」ものとしては、何も手を加えないあら塩を使用し、「乾いている」ものとしては、900Wで1分電子レンジ加熱する操作を4回繰り返した結果、水分が1%抜けて99gになったものを使用した。結果を表11に示す。なお、周囲環境は、エアコンの設定温度が22度、湿度35%であった。
いずれも乾いているあら塩99gを150ccのビーカー1,2に入れ、霧吹きを5回(1cc相当)した場合と10回(2cc相当)した場合とでレンジ取り出し直後の温度を比較した。結果を表12に示す。なお、周囲環境は、エアコンの設定温度が22度、湿度35%であった。
実施例13と同様の条件で放熱試験を行った。結果を表13に示す。なお、周囲環境は、エアコンの設定温度が22度、湿度35%であった。
不織布でできた袋に塩・珊瑚砂・リン酸カルシウム・珪砂を合計100gになるように詰め、紙皿を2枚重ねで敷いた900Wの電子レンジで1分間加熱した。加熱後、取り出したら直ちに図10に示すように料理温度計(DAISO製C008、ガラス製、指示液:ケロシン)を不織布内の中心部に差し込むとともに、もう1つの温度計を不織布の表面に当て、ガムテープで固定し、表面の温度計の上に不織布をかけておき、放熱試験を行った。結果を表14に示す。なお、周囲環境は、エアコンの設定温度が22度、湿度35%であった。
不織布でできた袋に塩・珊瑚砂・リン酸カルシウム・珪砂を合計100gになるように詰め、紙皿を2枚重ねで敷いた900Wの電子レンジで1分間加熱した。加熱後、取り出したら直ちに袋を手に持ち、図11に示すように料理温度計(DAISO製C008、ガラス製、指示液:ケロシン)を袋内の中心部に差し込み、袋の口の部分と温度計とを一緒に手で握って閉じ、混合物の入っている部分を触り、何度でどんな体感かを記録した。なお、触れる際は、左右の手でなるべく暖まっていないほうの手を使用した。結果を表15に示す。なお、周囲環境は、エアコンの設定温度が22度、湿度35%であった。
塩(品名:「日本海水食塩」(瀬戸内)、株式会社日本海水、赤穂工場製)と、御影石粉(岡崎産、岡崎の灯籠店から入手)と、でんぷんのり(フエキABのり、不易糊工業株式会社製)を準備し、塩については、ミルで予め粉末化したうえで、塩10:御影石粉2:澱粉のり2:水0.4の割合でよく混ぜ、造形した。頭部については、ストローを縦に切って断面半円形にし、押して目を描いた。その後、自然放置で最低1日以上乾燥させ、頬を赤いポスターカラーで色付けすることによって、図12のような造形物(お地蔵様)を得た。なお、お地蔵様に持たせたハートの飾り物は、紙粘土製で、乾かし、ポスターカラーで色付けをし、再度乾かし、1日以上乾かしたお地蔵様に、でんぷんのりでくっつけてある。この造形物は、紙粘土を除けば、軽くて、ボンドや石膏等を使用していないことから、水に入れれば容易に溶けてなくなるという特徴があることがわかった。
顔を描いた後、水2:澱粉のり1程にといた水のりを刷毛で塗布しておくと、固さが増すことがわかった。
塩(品名:「日本海水食塩」(瀬戸内)、株式会社日本海水・赤穂工場製)と、御影石粉(岡崎産、岡崎の灯籠店から入手)と、珪砂粉末(岐阜県産、製造元:白井石鹸株式会社、販売元:株式会社らくらくエコショップ)、澱粉のり(フエキABのり、不易糊工業株式会社製)を準備し、塩については、ミルで予め粉末化したうえで、塩10:御影石粉1:珪砂粉末0.1:でんぷんのり1:水1の割合でよく混ぜ、造形した。その後、実施例19と同様の工程を経て、造形物を得た。得られた造形物は、密度が上がり、固く締まっていた。
2 透水性素材
3 密閉部位(ジッパー)
4 非透水性袋
5 開口辺
6 外袋
7 融着しろ
8 保温性素材
11 多層温熱懐炉
12 布製収納袋
13 第1ポケット
14a,14b 間仕切り布
15 第3ポケット
17 第2ポケット
18 耐熱性素材
22 珊瑚
Claims (14)
- 塩化ナトリウムと、廃棄物由来、自然由来もしくは動物由来のケイ酸塩含有成分、海砂、陶磁器粉砕物または宝石クズから選択される廃棄物由来もしくは自然由来のアルミノケイ酸塩含有成分、廃棄物由来、自然由来もしくは動物由来の炭酸カルシウム含有成分、および、廃棄物由来、自然由来もしくは動物由来のリン酸カルシウム含有成分から選択される1種又は2種以上の廃棄物由来、自然由来又は動物由来材料とを含む記念品用組成物。
- 塩化ナトリウムが、海水由来の塩である請求項1に記載の記念品用組成物。
- 組成物の全重量に対して塩化ナトリウムを70〜85重量%、1種または2種以上の廃棄物由来、自然由来又は動物由来材料を合計で15〜30重量%含む請求項1または請求項2に記載の記念品用組成物。
- 組成物の全重量に対して塩化ナトリウムを70〜85重量%、炭酸カルシウム、リン酸カルシウムおよびケイ酸塩から選択される1種または2種以上の成分を合計で15〜30重量%含む記念品用組成物。
- 請求項1乃至請求項4のいずれか一項に記載の記念品用組成物を透水性素材で包んだ記念品。
- さらに密閉可能な非透水性袋に収納した請求項5に記載の記念品。
- 前記密閉可能な非透水性袋を外袋に収納した請求項6に記載の記念品。
- 前記外袋と密閉可能な非透水性袋との間に保温性素材を備えた請求項7に記載の記念品。
- 請求項5に記載の記念品の中心部が湿らない程度に記念品の表面に水を噴霧することと、電子レンジまたは温熱器で加熱または保温することとを含む記念品の使用方法。
- 水を噴霧することは、記念品用組成物の合計重量に対して0.5〜5重量%の水を満遍なく噴霧することである請求項9に記載の記念品の使用方法。
- 請求項1乃至請求項4のいずれか一項に記載の記念品用組成物に水と澱粉のりとを添加して混合、造形した記念品。
- 請求項1乃至請求項4のいずれか一項に記載の記念品用組成物を袋に収納した記念品。
- 廃棄物由来、自然由来もしくは動物由来のケイ酸塩含有成分、海砂、陶磁器粉砕物または宝石クズから選択される廃棄物由来もしくは自然由来のアルミノケイ酸塩含有成分、廃棄物由来、自然由来もしくは動物由来の炭酸カルシウム含有成分、および、廃棄物由来、自然由来もしくは動物由来のリン酸カルシウム含有成分から選択される1種又は2種以上の廃棄物由来、自然由来又は動物由来材料を耐熱性素材で包囲し、請求項5乃至請求項8のいずれか一項に記載の記念品で挟んだ多層温熱懐炉。
- 前記耐熱性素材が、炭化繊維、炭素繊維、アルミ繊維、ウレタンゴム、ガラス繊維シート、シリコーンゴム、シリコーンゴムと麻布との複合材、シリコーンゴムとアラミド繊維シートとの複合材、または、ポリエステルシートである請求項13に記載の多層温熱懐炉。