JP2020118028A - Artificial lawn and artificial lawn-made athletic field - Google Patents
Artificial lawn and artificial lawn-made athletic field Download PDFInfo
- Publication number
- JP2020118028A JP2020118028A JP2020008534A JP2020008534A JP2020118028A JP 2020118028 A JP2020118028 A JP 2020118028A JP 2020008534 A JP2020008534 A JP 2020008534A JP 2020008534 A JP2020008534 A JP 2020008534A JP 2020118028 A JP2020118028 A JP 2020118028A
- Authority
- JP
- Japan
- Prior art keywords
- coconut shell
- artificial turf
- filling layer
- layer
- filling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、充填層の充填物としてヤシ殻を使用し、充填層を有機天然材により構成した人工芝および人工芝製運動競技場に関する。 The present invention relates to an artificial turf in which coconut shells are used as a filling material for the filling layer, and the filling layer is made of an organic natural material, and an athletic field made of the artificial turf.
従来、人工芝製運動競技場は、人工芝を砕石舗装等の基礎層の上に敷くことにより施工・造成するものであるが、従来の人工芝製運動競技場は、次のような不具合が発生していたのである。 Conventionally, an artificial grass athletic stadium is constructed and constructed by laying artificial grass on a foundation layer such as crushed stone pavement, but the conventional artificial grass athletic stadium has the following problems. It was happening.
即ち、従来の人工芝製運動競技場は、そのクッション性を担保するために、天然芝では土にあたる部分を、他の素材を転用した充填材として、芝の目の間に詰めていく必要があった。そして、日本及びその他諸外国では、古タイヤを粉砕した黒ゴムチップを、充填材として使用していたのである。 That is, in the conventional artificial grass athletic stadium, in order to ensure its cushioning property, it is necessary to fill the part of the natural grass that corresponds to the soil between the eyes of the grass as a filling material that is diverted from another material. there were. In Japan and other foreign countries, black rubber chips obtained by crushing old tires are used as a filler.
多くの改良点や改善要望がユーザーからありながらも、特段の理由もなく、黒ゴムチップの使用が、当たり前として認識されていたのである。このような状況において、黒ゴムチップの発がん性が疑われることとなり、それをきっかけに、黒ゴムチップのネガティブな面が大きくクローズアップされてきたのである。 The use of black rubber chips was recognized as a matter of course for many reasons and requests from users for no particular reason. In such a situation, the carcinogenicity of the black rubber chip was suspected, and the negative side of the black rubber chip has been greatly highlighted as a trigger.
黒ゴムチップにより靴やボールなどが汚れ、さらに汚れが落ちにくく、真夏では温度が７０℃に達するなど、高温となり熱中症の誘発の可能性があることが問題視されてきた。
また、上記の問題を解決する充填材として、従来にも、ヤシ殻は使用されていたが、性能面において改善の余地があった。
It has been regarded as a problem that black rubber chips stain shoes, balls and the like, and stains are hard to remove, and the temperature reaches 70° C. in the middle of summer, which may cause heat stroke.
Further, coconut shells have been conventionally used as a filler for solving the above problems, but there is room for improvement in terms of performance.
本発明においては、人工芝製運動競技場に敷設される人工芝において、充填剤としてヤシ殻を構成する内果皮や中果皮や外果皮の全てを１００％使用し、有機天然素材により構成したものである。即ち、該ヤシ殻充填層は、ヤシ殻を乾燥した成分と、ヤシ殻を炭化させたヤシ殻活性炭を混合した充填物により構成したものである。 In the present invention, an artificial turf laid in an athletic field made of artificial turf is made of an organic natural material by using 100% of all inner fruit skin, mesocarp, and outer fruit skin that constitute coconut shells as a filler. Is. That is, the coconut shell filling layer is composed of a mixture of a dried coconut shell component and a coconut shell carbonized coconut shell activated carbon.
また、ヤシ殻の乾燥した成分は、粉末とチップと繊維により構成したものである。また、ヤシ殻の乾燥した成分は、粉末とチップと繊維とを、乾燥時においては分離し、施工時においては、該乾燥した成分を再度混合することにより構成したものである。これらのヤシ殻構成成分のブレンドにより、天然素材であるヤシ殻が、人工芝製運動競技場の温度上昇を抑制し、夏場の人工芝製運動競技場の不快な暑さを抑制するものである。 The dried component of coconut shell is composed of powder, chips and fibers. The dried component of the coconut shell is formed by separating the powder, the chips, and the fiber at the time of drying, and re-mixing the dried component at the time of construction. By blending these coconut shell constituents, the natural coconut shell suppresses the temperature rise in the artificial grass sports stadium and suppresses the uncomfortable heat of the artificial grass sports stadium in the summer. ..
また、細かい繊維が人工芝製運動競技場に降った雨水等の必要な水分を保水確保し、ヤシ殻の粗い繊維は余分な水分を排水し、ヤシ殻活性炭は、防臭・抗菌の効果をも発揮するのである。また、これらの作用により人工芝製運動競技場を常にベストな状態に保ち、快適なプレーの環境を整えることができるのである。 In addition, the fine fibers secure necessary water such as rainwater that fell on the artificial turf sports field, the coarse fiber of the coconut shell drains excess water, and the coconut shell activated carbon also has deodorant and antibacterial effects. It works. Also, by these actions, the artificial grass athletic stadium can always be kept in the best condition and a comfortable playing environment can be prepared.
そして、人工芝製運動競技場におけるプレイヤーは自身のプレーに專念することができて、チームのパーフォーマンスのみに集中できるようになるのである。また、ヤシ殻は、プランテーションで収穫されたヤシの実の殻だけを使用しているので、環境保護の面からしても、無駄な森林伐採が一切なく、地球環境への負荷が少ないエコロジーな人工芝製運動競技場及びその施工方法となるのである。 And, the players on the artificial turf arena will be able to focus on their own play and focus only on the performance of the team. In addition, as the palm shells, only palm shells harvested from plantations are used, so even from the perspective of environmental protection, there is no wasteful deforestation and there is little ecological impact on the global environment. It is an artificial turf sports stadium and its construction method.
また、材料が１００％天撚有機質素材であり、添加物は一切含んでいないので、プレイヤーの人体に対して悪影響を与えることがなく、健康上からも安全な素材となっているのである。また、施工後の降雨などで水分を含んだ後は、ヤシ殻により構成した充填材が、人工芝に絡み付くために保水し、雨水と共に流れ出すことが少なく、排水管等を詰まらせるリスクを軽減することができるのである。もし仮に充填材が下水道に流れ出したとしても、公害の原因となることもないのである。 In addition, the material is 100% twisted organic material and does not contain any additives, so it does not adversely affect the human body of the player and is a safe material for health. In addition, after it contains water such as rain after construction, the filler made up of coconut shell retains water because it entangles with the artificial turf and does not flow out with rainwater, reducing the risk of clogging drainage pipes etc. It is possible. Even if the filling material flows into the sewer, it does not cause pollution.
また、ヤシ殻製の充填材は、クッション性やボールバウンド性の面においても良好であり、プレー感は天然芝に極めて近いものとなる。また、ヤシ殻は腐食等による劣化が遅いので、多くの効果効用を長時間持続させることができるのである。 Further, the filler made of coconut shell is also good in terms of cushioning property and ball-bound property, and the feeling of play becomes very close to that of natural grass. In addition, since the coconut shell is slowly deteriorated due to corrosion and the like, many effects can be maintained for a long time.
また、ヤシ殻製の充填材に、さらに同じく１００％天然有機質素材であるコルクチップを混合することにより、コルクチップの熱伝導率が極めて低い特性を備えつつ、ヤシ殻活性炭の保水性を備えた人工芝が提供できるのである。このような人工芝を敷設することで、コルクチップの熱伝導率が極めて低い特性を利用して、夏場の人工芝製運動競技場の不快な暑さを効果的に抑制するものである。また、ヤシ殻よりも衝撃吸収性に優れたコルクチップを混合することにより、クッション性やボールバウンド性の面においてもさらに良好となり、プレー感が向上する。また、ヤシ殻活性炭とコルクチップを混合することにより、コルクチップのみを充填した場合と比べて保水性が向上する。これにより、乾いたコルクチップ同士で発生しやすい静電気による浮き上がりを防止することができるのである。 In addition, by mixing cork chips, which is also a 100% natural organic material, with the filler made of palm shell, the cork chips have the extremely low thermal conductivity and the water retention of the palm shell activated carbon. Artificial grass can be provided. By laying such artificial grass, it is possible to effectively suppress the uncomfortable heat of the sports field made of artificial grass in the summer by utilizing the characteristic that the cork chip has extremely low thermal conductivity. Further, by mixing cork chips, which are more shock-absorbent than palm shells, cushioning properties and ball-bound properties are further improved, and a feeling of play is improved. Further, by mixing the coconut shell activated carbon and the cork chips, the water retention property is improved as compared with the case where only the cork chips are filled. As a result, it is possible to prevent floating due to static electricity that is likely to occur between dry cork chips.
次に、上記課題を解決するための手段について説明する。 Next, means for solving the above problems will be described.
請求項１においては、基布２３より人工芝葉２１を間隔を置いて上方へ突出させ、前記人工芝葉２１の間に充填物を充填する構成した人工芝であって、前記充填物の上部をヤシ殻充填層２２により構成し、前記ヤシ殻充填層２２は、ヤシ殻の乾燥した成分と、ヤシ殻を炭化させたヤシ殻活性炭Ｄを混合した充填物としたものである。 The artificial turf according to claim 1, wherein artificial turf leaves (21) are protruded upward from the base cloth (23) at intervals, and a filling material is filled between the artificial turf leaves (21). Is constituted by a coconut shell filling layer 22, and the coconut shell filling layer 22 is a filling material in which a dried component of the coconut shell and coconut shell activated carbon D obtained by carbonizing the coconut shell are mixed.
請求項２においては、請求項１記載の人工芝において、ヤシ殻の乾燥した成分は、粉末ＣとチップＥと繊維Ａ・・を乾燥時には分離し、施工時において、前記分離した成分を再度混合するものである。 According to a second aspect, in the artificial turf according to the first aspect, the dried components of the coconut shell separate the powder C, the chips E, and the fibers A... When drying, and then remix the separated components during the construction. To do.
請求項３においては、請求項１記載の人工芝において、ヤシ殻の乾燥した成分は、ヤシ殻Ｙを構成する部分において、中果皮Ｎと外果皮Ｔの部分を選別して取り出し、粉末ＣとチップＥと繊維Ａ・・とにより構成したものである。 According to a third aspect, in the artificial turf according to the first aspect, the dried component of the coconut shell is selected from the mesocarp N and the epicarp T in the portion constituting the coconut shell Y, and the powder C is obtained. It is composed of a chip E and fibers A.
請求項４においては、請求項１記載の人工芝において、ヤシ殻活性炭Ｄは、ヤシ殻Ｙの中の、内果皮Ｓの部分を取り出して焼成し炭化させたものである。 According to a fourth aspect, in the artificial turf according to the first aspect, the coconut shell activated carbon D is obtained by taking out a portion of the inner skin S in the coconut shell Y and firing and carbonizing it.
請求項５においては、請求項１に記載の人工芝において、前記充填物のうち下部の充填層を珪砂２５とし、上部充填層をヤシ殻充填層２２により構成したものである。 According to a fifth aspect, in the artificial turf according to the first aspect, the lower filling layer of the filling is silica sand 25 and the upper filling layer is a coconut shell filling layer 22.
請求項６においては、請求項５記載の人工芝において、ヤシ殻充填層２２と珪砂２５の間にゴムチップ層２４を介装したものである。 According to a sixth aspect, in the artificial turf according to the fifth aspect, a rubber chip layer 24 is interposed between the coconut shell filling layer 22 and the silica sand 25.
請求項７においては、請求項１に記載の人工芝において、前記充填物の上部を、前記ヤシ殻充填層と、コルクチップから構成されるコルクチップ充填層とを含む構成としたものである。 According to a seventh aspect of the present invention, in the artificial turf according to the first aspect, an upper portion of the filling material is configured to include the coconut shell filling layer and a cork chip filling layer composed of cork chips.
請求項８においては、基布より人工芝葉を間隔を置いて上方へ突出させ、前記人工芝葉の間に充填物を充填するように構成した人工芝であって、
前記充填物の上層部をヤシ殻−コルクチップ混合充填層により構成し、
前記ヤシ殻−コルクチップ混合充填層は、ヤシ殻を乾燥した成分と、ヤシ殻を炭化させたヤシ殻活性炭と、コルクチップとを混合した充填物により構成したものである。
In Claim 8, artificial turf leaves are projected from a base cloth at intervals, and the artificial turf is configured to be filled with a filling material between the artificial turf leaves,
The upper layer portion of the filling is constituted by a coconut shell-cork chip mixed filling layer,
The coconut shell-cork chip mixed packing layer is composed of a packing material in which a component of dried coconut shell, coconut shell activated carbon obtained by carbonizing the coconut shell, and cork chips are mixed.
請求項９においては、請求項１から請求項８のいずれか一項に記載の人工芝を基礎層の上に敷設して構成する人工芝製運動競技場である。 A ninth aspect of the present invention is an athletic stadium made of artificial turf, which is constructed by laying the artificial turf according to any one of the first to eighth aspects on a base layer.
本発明は、次のような効果を奏するものである。 The present invention has the following effects.
まず、ヤシ殻充填層２２には雨水が長時間保水されるので、長時間にわたり蒸発作用が行われ、気化熱が冷却機構として作用し真夏日の人工芝製運動競技場の温度上昇を抑制する効果がある。従来のゴムチップ仕様の人工芝製運動競技場においては、表面の温度が約７０℃であったが、本発明の人工芝製運動競技場においては、表面の温度が４５℃前後となっているのである。 First, since rainwater is retained for a long time in the coconut shell filling layer 22, evaporation is performed for a long time, and heat of vaporization acts as a cooling mechanism to suppress a temperature rise in an artificial turf sports field on a midsummer day. effective. In the conventional artificial grass sports field with rubber chips, the surface temperature was about 70°C, but in the artificial grass sports field of the present invention, the surface temperature is around 45°C. is there.
次に、ヤシ殻充填層がクッション機構として、適度なクッション性を持ち、競技者の膝や腰への負担を軽減する効果がある。また、ボールバウンドなど、使用感は天然芝に極めて近いものにする効果がある。 Next, the coconut shell filling layer has an appropriate cushioning property as a cushioning mechanism, and has an effect of reducing the burden on the athlete's knees and waist. In addition, it has the effect of making the feeling of use, such as ball bound, extremely close to that of natural grass.
また、排水、保水、防臭、抗菌機構として、繊維の中の細かい繊維が必要な水分を確保し、粗い繊維は余分な水分を排水することができるのである。また、適度にブレンドされたヤシ活性炭は防臭、抗菌に作用する効果があり、従来から使用されてきたヤシ殻製の充填材に比べて機能面で優れているのである。 In addition, as a drainage, water retention, deodorization, and antibacterial mechanism, fine fibers in the fibers can secure necessary moisture, and coarse fibers can drain excess moisture. In addition, the appropriately blended coconut activated carbon has the effect of deodorizing and antibacterial action, and is superior in function to the conventionally used coconut shell filler.
また、ヤシ殻充填層が塩水を濾過するので、塩害予防機構として作用し、水による洗浄を実施するため、施設建造物への塩害を防止する効果がある。また、ヤシ製品であるヤシ殻充填層は、腐食などの劣化が遅く、多くの効果効能が長く持続するのである。 In addition, since the palm shell filling layer filters salt water, it acts as a salt damage prevention mechanism, and since washing is performed with water, there is an effect of preventing salt damage to the facility structure. In addition, the palm shell filling layer, which is a palm product, is slowly deteriorated due to corrosion and many effects and effects last long.
また、１００％有機質天然素材であるため、公害リスクを軽減して作用し、仮に下水道に流れ出したとしても公害になることがないのである。 In addition, since it is a 100% organic natural material, it acts by reducing the risk of pollution, and even if it flows into the sewer, it does not cause pollution.
また、ヤシ殻製の充填材に、さらに同じく１００％天然有機質素材であるコルクチップを混合することにより、コルクチップの熱伝導率が極めて低い特性を備えつつ、ヤシ殻活性炭の保水性を備えた人工芝が提供できるのである。 In addition, by mixing cork chips, which is also a 100% natural organic material, with the filler made of palm shell, the cork chips have the extremely low thermal conductivity and the water retention of the palm shell activated carbon. Artificial grass can be provided.
ヤシ殻を充填層２２として人工芝葉２１の間に充填する人工芝製運動競技場について説明する。 An athletic field made of artificial grass in which palm shells are filled between the artificial grass leaves 21 as the filling layer 22 will be described.
図１は、人工芝製運動競技場の第一実施例を示す側面断面図である。人工芝製運動競技場においては、人工芝２を支持するための基礎層１として、砕石舗装を施工している。また、該基礎層１は一般的なコンクリート舗装であってもよい。 FIG. 1 is a side sectional view showing a first embodiment of an artificial turf sports field. In an athletic field made of artificial grass, crushed stone pavement is constructed as a base layer 1 for supporting the artificial grass 2. Further, the foundation layer 1 may be general concrete pavement.
該基礎層１の表面に人工芝２を敷設・施工するのである。人工芝製運動競技場を構成する人工芝２は、第一実施例においては、下から順番に、基礎層１の上に、基布２３と、珪砂２５と、ヤシ殻充填層２２が層積みされており、その間に基布２３に縫込み固定された人工芝葉２１が突出されている。 The artificial grass 2 is laid and constructed on the surface of the base layer 1. In the first embodiment, the artificial turf 2 constituting the athletic stadium made of artificial turf is layered with the base cloth 23, the silica sand 25, and the coconut shell filling layer 22 on the base layer 1 in order from the bottom. The artificial turf leaf 21 sewn and fixed to the base cloth 23 is projected between them.
該人工芝葉２１は基布２３に対して列状に間隔を置いて縫込み固定されている。該人工芝葉２１の条の間隔は約１５ｍｍ程度である。そして、該１条に沿って約１０本の単位人口芝葉２１が、一束としてまとめて５ｍｍから８ｍｍの間隔を置いて株状に突出し、全体として人工芝葉２１を構成している。 The artificial turf leaf 21 is sewn and fixed to the base cloth 23 at intervals in rows. The spacing between the strips of the artificial turf leaf 21 is about 15 mm. Then, about 10 unit artificial turf blades 21 are bundled together along the one line and are projected in a stock form at intervals of 5 mm to 8 mm to constitute the artificial turf blade 21 as a whole.
人工芝２は、人工芝葉２１どうしが良く絡み合うので、人工芝葉２１の芝目が常に立っている。強く復元性のある形状をした人工芝となるように、前記人工芝葉２１の条の間隔と、株の間隔を構成している。このように構成した基布２３の上の人工芝葉２１の間に、図１に示す如く、下層に珪砂２５を充填し、その上にヤシ殻充填層２２を充填しているのである。 In the artificial turf 2, since the artificial turf leaves 21 are intertwined well with each other, the turf eyes of the artificial turf leaves 21 are always standing. The spacing between the strips of the artificial turf leaf 21 and the spacing between the plants are configured so that the artificial turf has a strong and resilient shape. As shown in FIG. 1, silica sand 25 is filled in the lower layer between the artificial turf leaves 21 on the base cloth 23 thus constructed, and the coconut shell filling layer 22 is filled thereon.
特に、珪砂２５やヤシ殻充填層２２が、人工芝葉２１の芝の目に入って行き易いように、縫い目のピッチや本数、間隔などをも工夫しているのである。また、水の浸透性なども考慮して、基布２３のコーティングや、基布２３に間隔を置いて開口している直径３乃至６ｍｍほどの水抜き穴の数、位置などをも構成しているのである。 In particular, the pitch, the number, and the spacing of the seams are also devised so that the silica sand 25 and the coconut shell filling layer 22 can easily reach the eyes of the grass of the artificial grass leaf 21. In addition, in consideration of water permeability, the coating of the base cloth 23 and the number and position of water drain holes having a diameter of 3 to 6 mm opened at intervals in the base cloth 23 are also configured. There is.
第一実施例においては、図示する如く基礎層１の上に直接的に人工芝２の基布２３を載置している。基布２３のうえに珪砂２５の層を２０乃至２５ｍｍにわたり層積みしている。さらにその上に２５乃至３０ｍｍにわたりヤシ殻充填層２２を層積みしている。そして、該ヤシ殻充填層２２の上面から人工芝葉２１の上端が５乃至１０ｍｍ程度が突出するように充填されているのである。 In the first embodiment, the base cloth 23 of the artificial grass 2 is placed directly on the base layer 1 as shown. A layer of silica sand 25 is layered on the base cloth 23 for 20 to 25 mm. Further, a coconut shell filling layer 22 is layered thereon over 25 to 30 mm. Then, the upper end of the artificial turf leaf 21 is filled so as to project from the upper surface of the palm shell filling layer 22 by about 5 to 10 mm.
この構成は、日本サッカー協会の認定を受けることも可能な人工芝製運動競技場及びその施工方法に構成されているのである。図２は、人工芝製運動競技場の第二実施例を示す側面断面図である。図２においては、充填層としてクッション性がさらに要求される場合の人工芝製運動競技場の構成を開示している。 This structure is composed of an artificial turf sports field that can be certified by the Japan Football Association and its construction method. FIG. 2 is a side sectional view showing a second embodiment of the artificial turf sports stadium. FIG. 2 discloses the structure of an athletic stadium made of artificial turf when cushioning properties are further required as the filling layer.
第二実施例の場合には、珪砂２５の充填層とヤシ殻充填層２２の充填層の間にゴムチップ層２４の充填層を介装している。珪砂２５の層は２０乃至２５ｍｍ程度と、第一実施例の場合と同じであるが、ヤシ殻充填層２２の層を１２．５乃至１５ｍｍとして、ゴムチップ層２４を１２．５乃至１５ｍｍとして、第一実施例のヤシ殻充填層２２の半分をゴムチップ層２４としている。 In the case of the second embodiment, the filling layer of the rubber chip layer 24 is interposed between the filling layer of the silica sand 25 and the filling layer of the coconut shell filling layer 22. The layer of silica sand 25 is about 20 to 25 mm, which is the same as in the first embodiment, but the layer of the coconut shell filling layer 22 is 12.5 to 15 mm and the rubber chip layer 24 is 12.5 to 15 mm. Half of the coconut shell filling layer 22 of one embodiment is a rubber chip layer 24.
ヤシ殻を充填層２２として人工芝葉２１の間に充填する人工芝製運動競技場である。そして、ヤシ殻充填層２２は、ヤシ殻成分の中の乾燥した成分と、ヤシ殻成分を焼成したヤシ殻活性炭Ｄをブレンドしたものである。ヤシ殻を乾燥した成分は、粉末Ｃと、チップＥと短い繊維Аと、長い繊維Ｂから構成されている。ヤシ殻活性炭Ｄはヤシ殻の内果皮Ｓ(シェル)の部分を１２時間程度加熱処理して炭化し炭にしたものである。 It is an athletic stadium made of artificial grass in which palm shells are packed as a packed layer 22 between the artificial grass leaves 21. The coconut shell filling layer 22 is a blend of a dried coconut shell component and a coconut shell activated carbon D obtained by burning the coconut shell component. The dried coconut shell component is composed of powder C, chips E, short fibers A, and long fibers B. The coconut shell activated carbon D is obtained by heating the inner skin S (shell) of the coconut shell for about 12 hours to carbonize it.
次に、ヤシ殻充填層２２を構成する部材の製造工程を説明する。図３は、ヤシ殻充填層２２の主要な原材料となるヤシ殻の断面図である。ヤシ殻Ｙは外側から順に、外果皮Ｔ、中果皮Ｎ、内果皮Ｓにより構成されており、内果皮Ｓはシェルとも呼ばれ、その内部にヤシ樹液が封じ込められている。ヤシ殻充填層２２は、内果皮Ｓの内部のヤシ樹液を抜いた後に、さらにヤシ殻の部分からヤシ油を搾油もした後の廃棄物であるヤシ殻Ｙを原料とするのである。 Next, the manufacturing process of the member forming the coconut shell filling layer 22 will be described. FIG. 3 is a sectional view of a coconut shell which is a main raw material of the coconut shell filling layer 22. The palm shell Y is composed of an outer skin T, a middle skin N, and an inner skin S in this order from the outside, and the inner skin S is also called a shell, and the palm sap is contained inside it. The coconut shell filling layer 22 is made of the coconut shell Y which is a waste after the coconut sap inside the endocarp S is removed and the coconut oil is further squeezed from the coconut shell.
［粉末と長繊維の分離］
山岳地のヤシ畑で生産されたヤシの実のみを原料として採取し、ヤシの実からヤシ樹液と内果皮Ｓ（シェル）を取り除いた後に、中果皮Ｎと外果皮Ｔを繊維に沿って縦に２〜３分割し、約３ヶ月間水に漬けて柔らかくし、長い繊維Ｂを掻き取り易くする。
[Separation of powder and long fiber]
Only palm fruit produced in a palm field in a mountainous area is collected as a raw material, and after removing the palm sap and the inner skin S (shell) from the palm fruit, the mesocarp N and the epicarp T are longitudinally arranged along the fiber. Divide into 2 to 3 parts and soak in water for about 3 months to soften the long fibers B to facilitate scraping.
円筒型の回転体に剣山状に鋲をつけた繊維掻き取り機を回転させ、水を含み柔らかくなった中果皮Ｎを、その繊維に対して縦方向に鋲に押し付け、太い長い繊維Ｂから粉末Ｃ状の中果皮Ｎと、細かいチップＥを取り出す。即ち、固形上の中果皮Ｎの部位、及び短い繊維Аを掻き取り、分離するのである。 By rotating a fiber scraping machine with a sword-shaped tack on a cylindrical rotating body, the mesocarp N softened with water is pressed against the fiber in the longitudinal direction, and powdered from a thick long fiber B. C-shaped mesocarp N and fine chips E are taken out. That is, the portion of the mesocarp N on the solid and the short fibers A are scraped off and separated.
その後、約３年間野積みし、天日乾燥、及び年２回の雨季によるアク抜き後、目の粗い回転式篩い機に投入し、粉末Ｃと短い繊維Аを落下させ、残った長い繊維Ｂを取り除く。 After that, it was loaded in the open air for about 3 years, dried in the sun, and removed from the rain twice a year, then put into a coarse rotary sieving machine to drop the powder C and the short fibers A, and the remaining long fibers B. Get rid of.
［篩い掛け・水洗い洗浄・乾燥］
上記で篩い分けした粉末Ｃには、細い繊維が残っているため、目の細い回転式篩い機で長い繊維Ｂと粉末Ｃを分離させる。但し、この状態の粉末Ｃは濡れている状態で完全には長い繊維Ｂを取り除くことはできないが、乾燥効率を高めるために予め短い繊維Аを、あらかた取り除く前処理６を行う。長い繊維Ｂを取り除いた粉末Ｃを、水洗い洗浄し、２４時間真水に漬け込み、その後、水分を絞った原料をコンクリート敷きの乾燥場に敷きレーキで攪拌しながら天日乾燥する。
[Sieving/Washing/Washing/Drying]
Since the fine fibers remain in the powder C sieved above, the long fibers B and the powder C are separated with a fine mesh rotary sieving machine. However, although the powder C in this state cannot completely remove the long fibers B in a wet state, a pretreatment 6 for removing the short fibers A beforehand is performed in advance in order to improve the drying efficiency. The powder C from which the long fibers B have been removed is washed by washing with water, immersed in fresh water for 24 hours, and then the raw material whose water content has been squeezed is spread in a drying place for concrete and dried in the sun while stirring with a rake.
［再篩い掛け］
上記で篩った粉末Ｃ（ヤシ中果皮Ｎ部位）、細かいチップＥ（固形のヤシ殻中果皮Ｎ部位）と、短い繊維Аが混ざった原料を、天日乾燥後、前記の処理で取り切れなかった長い繊維Ｂを、８ｍｍ目の細い振動篩い機でさらに取り除く。
[Re-sieving]
The raw material in which the powder C sieved above (N portion of coconut rind skin), the fine chips E (N portion of coconut husk of solid coconut shell) and short fiber А are mixed is removed by the above-mentioned treatment after sun drying. The long fibers B, which were not present, are further removed with an 8 mm fine vibrating screen.
［ヤシ殻炭と混ぜる］
最初に取り除いたヤシの内果皮Ｓ（シェル）を、１２時間熱処理し、炭に加工してヤシ殻活性炭Ｄとする。該ヤシ殻活性炭Ｄを粉砕処理しながら、３ｍｍの網で篩を掛けて、約３ｍｍのヤシ殻炭を製造する。
[Mix with coconut shell charcoal]
The inner skin S (shell) of the palm that was first removed is heat-treated for 12 hours and processed into charcoal to obtain coconut shell activated carbon D. While crushing the coconut shell activated carbon D, a coconut shell charcoal of about 3 mm is produced by sieving with a 3 mm net.
前記において篩い分けした、粉末ＣとチップＥと短い繊維Аと長い繊維Ｂが混ざった原料に対し、ヤシ殻活性炭Ｄを約２０％（使用状況により配合割合は調整する）投入し、よく撹拌する。 About 20% of coconut shell activated carbon D is added to the raw material mixed with powder C, chips E, short fibers A and long fibers B, which have been sieved in the above (the mixing ratio is adjusted depending on the usage conditions), and the mixture is stirred well. ..
このようにして製造したヤシ殻活性炭Ｄは、内果皮Ｓを取り出して、炭化及び賦活工程処理によって０．８ｎｍ以下のサブミクロ孔、０．８〜２ｎｍのミクロ孔、２〜５０ｎｍのメソ孔、５０ｎｍ以上のマクロ孔をもつ炭素となる。この細孔はヤシ殻活性炭Ｄの内部で網目状に存在し、比表面積が非常に大きくなり、様々な物質を吸着するのである。 In the coconut shell activated carbon D produced in this manner, the inner skin S is taken out, and sub-micropores of 0.8 nm or less, micropores of 0.8 to 2 nm, mesopores of 2 to 50 nm, 50 nm by carbonization and activation process treatment. The carbon has the above macropores. These pores are present inside the coconut shell activated carbon D in a mesh form, have a very large specific surface area, and adsorb various substances.
ヤシ殻活性炭Ｄは上記の性質により、臭いを吸い取る脱臭作用、空気や水や油等を浄化する浄化作用、空気中の水分を調湿する調湿作用を行うのである。その他に、静電気除去や、電磁波吸収、遠赤外線放射等の作用も行うのである。これらの作用により前述した人工芝製運動競技場に対する効果を奏することができるのである．とくに、ヤシ殻活性炭Ｄが、ヤシ殻充填層２２を構成する成分の中で、重量比率において１０〜３０％であると、従来のヤシ殻製の充填材に比べて、ヤシ殻活性炭Ｄに基づく脱臭作用等の効果が顕著に得られて好ましい。 Owing to the above properties, the coconut shell activated carbon D exerts a deodorizing action for absorbing odor, a purifying action for purifying air, water, oil, etc., and a humidity controlling action for controlling moisture in the air. In addition, it also works to remove static electricity, absorb electromagnetic waves, and radiate far infrared rays. By these actions, the above-mentioned effects on the artificial turf sports arenas can be achieved. In particular, when the coconut shell activated carbon D is 10 to 30% by weight in the components constituting the coconut shell filled layer 22, the coconut shell activated carbon D is based on the coconut shell activated carbon D as compared with the conventional coconut shell-made filler. It is preferable because the effects such as deodorizing action are remarkably obtained.
次に、本発明のヤシ殻充填層２２を構成する主たる成分の大きさと、それらの体積比率の最適な数値は次のとおりである。
粉末Ｃ ： １−８ｍｍ、 ４０％
チップＥ ： １−５ｍｍ、 １０％
短い繊維А ： １−３ｍｍ、 １５％
長い繊維Ｂ ： １−８ｍｍ、 １５％
ヤシ殻活性炭Ｄ ： ３ｍｍ、 ２０％
また、重量比率は以下のとおりである。
粉末Ｃ ： １−８ｍｍ、６０％
チップＥ ： １−５ｍｍ、 ４％
短い繊維А ： １−３ｍｍ、 ３％
長い繊維Ｂ ： １−８ｍｍ、 ３％
ヤシ殻活性炭Ｄ ： ３ｍｍ、 ３０％
Next, the optimum numerical values of the sizes of the main components constituting the coconut shell filling layer 22 of the present invention and their volume ratios are as follows.
Powder C: 1-8 mm, 40%
Chip E: 1-5 mm, 10%
Short fiber А: 1-3mm, 15%
Long fiber B: 1-8 mm, 15%
Coconut shell activated carbon D: 3mm, 20%
The weight ratio is as follows.
Powder C: 1-8 mm, 60%
Chip E: 1-5 mm, 4%
Short fiber А: 1-3mm, 3%
Long fiber B: 1-8 mm, 3%
Coconut shell activated carbon D: 3mm, 30%
［圧縮ポリ袋包装］
次に、原料のヤシ殻成分の、篩掛けの状況を検査し、圧縮包装機のホッパーに投入する。ホッパーに投入された原料は、予めポリ袋が装填されている圧縮包装機の圧縮チューブにスクリューコンベアーで投入され、ポリ袋内で圧縮される。ポリ袋の開口部をヒートシーラーで留め圧縮機から取り出しコンテナに積み出荷する。
[Compressed plastic bag packaging]
Next, the state of sieving of the raw material coconut shell component is inspected and put into the hopper of the compression packaging machine. The raw material put into the hopper is put into a compression tube of a compression packaging machine in which a plastic bag is loaded in advance by a screw conveyor and compressed in the plastic bag. The opening of the plastic bag is fixed with a heat sealer, removed from the compressor, and loaded into a container for shipment.
次に、本発明の基本的な施工工程について説明する。まず、砕石舗装の基礎層１の上に人工芝２を載置する。次に、人工芝２を構成する人工芝葉２１の間に、珪砂２５を充填する。珪砂２５の充填作業は、大型のタンクと開閉シャッターを具備し、トラクターで牽引される散布充填機により行う。そして、人工芝葉２１の間に充填した珪砂２５の表面をブラッシングしてならす。ブラッシング施工はトラクターにより牽引する牽引型のブラシにより行う。該ブラシは鉄板の下面に人工芝葉２１の条列に合致するように突起を突出した構成となっている。 Next, the basic construction process of the present invention will be described. First, the artificial grass 2 is placed on the foundation layer 1 of the crushed stone pavement. Next, silica sand 25 is filled between the artificial turf leaves 21 constituting the artificial turf 2. The filling work of the silica sand 25 is performed by a spray filling machine equipped with a large tank and an opening/closing shutter and pulled by a tractor. Then, the surface of the silica sand 25 filled between the artificial turf leaves 21 is brushed and smoothed. Brushing is performed with a traction brush that is pulled by a tractor. The brush has a structure in which projections are projected on the lower surface of the iron plate so as to match the rows of the artificial turf leaf 21.
珪砂２５をブラッシングして人工芝葉２１の間に押し込んだ後に、さらにヤシ殻充填層２２を充填する。ヤシ殻充填層２２の充填作業は大型のタンクと開閉シャッターを具備し、トラクターで牽引される散布充填機により行う。該ヤシ殻充填層２２の充填後に、前記した牽引型のブラシによりヤシ殻充填層２２の表面をブラッシングして、ヤシ殻充填層２２を人工芝葉２１の間に押し込みを行う。第二実施例の場合には、ゴムチップ層２４の充填とブラッシング施工を追加するものである。 After the silica sand 25 is brushed and pushed between the artificial turf leaves 21, the coconut shell filling layer 22 is further filled. The filling work of the palm shell filling layer 22 is performed by a spray filling machine equipped with a large tank and an opening/closing shutter and pulled by a tractor. After the coconut shell filling layer 22 is filled, the surface of the coconut shell filling layer 22 is brushed by the above-mentioned traction type brush to push the coconut shell filling layer 22 between the artificial turf leaves 21. In the case of the second embodiment, filling of the rubber chip layer 24 and brushing are added.
また、第三実施例においては、図示する如く基礎層１の上に直接的に人工芝２の基布２３を載置している。基布２３のうえに珪砂２５の層を１０乃至１５ｍｍにわたり層積みしている。さらにその上に、１０乃至１５ｍｍにわたりコルクチップ充填層２６を層積みしている。さらにその上に１０乃至１５ｍｍにわたりヤシ殻充填層２２を層積みしている。コルクチップ充填層２６は、コルクチップFが充填されている。コルクチップＦは、コルクガシの樹皮を剥離して加工した粉粒であり、弾力性に富み空気を豊富に含む。また、ヤシ殻充填層２２は、粉末Ｃと、チップＥと短い繊維Аと、長い繊維Ｂから構成されるヤシ殻成分の中の乾燥した成分と、ヤシ殻成分を焼成したヤシ殻活性炭Ｄをブレンドしたもので構成されている。そして、ヤシ殻充填層２２の上面から人工芝葉２１の上端が２０乃至３０ｍｍ程度が突出するように充填されているのである。 In the third embodiment, the base cloth 23 of the artificial grass 2 is placed directly on the base layer 1 as shown in the figure. A layer of silica sand 25 is layered on the base cloth 23 for 10 to 15 mm. Further thereon, a cork chip filling layer 26 is laminated in a thickness of 10 to 15 mm. Further, a palm shell filling layer 22 is layered thereon over 10 to 15 mm. The cork chip filling layer 26 is filled with the cork chips F. The cork chips F are powder particles obtained by peeling and processing cork oak bark, and are rich in elasticity and rich in air. In addition, the coconut shell filling layer 22 includes a powder C, a chip E, a short fiber А, a dried component of a coconut shell component composed of a long fiber B, and a coconut shell activated carbon D obtained by firing the coconut shell component. It is composed of blended materials. Then, the upper end of the artificial turf leaf 21 is filled so as to project from the upper surface of the palm shell filling layer 22 by about 20 to 30 mm.
ヤシ殻活性炭Ｄは臭いを吸い取る脱臭作用、空気や水や油等を浄化する浄化作用、空気中の水分を調湿する調湿作用を行うのである。また、コルクチップ充填層２６のコルクチップFは、ガスのような空気を含んだ独特の細胞構造により、熱伝導率が極めて低く、衝撃吸収性、耐水性、温度上昇の抑制に優れている。
これらの作用により前述した人工芝製運動競技場に対する効果を奏することができるのである。
The coconut shell activated carbon D has a deodorizing action for absorbing odor, a purifying action for purifying air, water, oil, etc., and a humidity controlling action for controlling moisture in the air. Further, the cork chip F of the cork chip filling layer 26 has an extremely low thermal conductivity due to the unique cell structure containing air such as gas, and is excellent in shock absorption, water resistance, and suppression of temperature rise.
By these actions, the above-mentioned effect on the artificial turf sports stadium can be achieved.
また、第四実施例においては、図示する如く基礎層１の上に直接的に人工芝２の基布２３を載置している。基布２３の上に珪砂２５の層を１０乃至１５ｍｍにわたり層積みしている。さらにその上に１０乃至１５ｍｍにわたりヤシ殻−コルクチップ混合充填層２７を層積みしている。ヤシ殻−コルクチップ混合充填層２７には、ヤシ殻由来の成分の他に、コルクチップＦが混合されている。ヤシ殻−コルクチップ混合充填層２７において、粉末Ｃと、チップＥと短い繊維Аと、長い繊維Ｂから構成されるヤシ殻成分の中の乾燥した成分と、ヤシ殻成分を焼成したヤシ殻活性炭Ｄと、コルクチップFとを混合している。コルクチップＦは、コルクガシの樹皮を剥離して加工した粉粒であり、弾力性に富み空気を豊富に含む。そして、該ヤシ殻−コルクチップ混合充填層２７の上面から人工芝葉２１の上端が２０乃至３０ｍｍ程度が突出するように充填されているのである。 In the fourth embodiment, the base cloth 23 of the artificial grass 2 is placed directly on the base layer 1 as shown in the figure. A layer of silica sand 25 is layered on the base cloth 23 for 10 to 15 mm. Further, a coconut shell-cork chip mixed filling layer 27 is layered thereon over 10 to 15 mm. In the coconut shell-cork chip mixed filling layer 27, a cork chip F is mixed in addition to the components derived from the coconut shell. In the coconut shell-cork chip mixed packed layer 27, a dry component in the coconut shell component composed of the powder C, the chip E, the short fiber A, and the long fiber B, and the coconut shell activated carbon obtained by burning the coconut shell component. D and cork chip F are mixed. The cork chips F are powder particles obtained by peeling and processing cork oak bark, and are rich in elasticity and rich in air. The artificial turf leaf 21 is filled so that the upper end of the artificial turf leaf 21 projects from the upper surface of the coconut shell-cork chip mixed and filled layer 27 by about 20 to 30 mm.
次に、本発明のヤシ殻−コルクチップ混合充填層２７を構成する主たる成分の大きさと、それらの重量比率の最適な数値は次のとおりである。
ヤシ殻：コルクチップ＝１：２
また、ヤシ殻とコルクチップそれぞれの粒径は次のとおりである。
ヤシ殻 ： １−８ｍｍ
コルクチップ ： １−２ｍｍ
Next, the optimum numerical values of the sizes of the main components constituting the coconut shell-cork chip mixed and packed layer 27 of the present invention and their weight ratios are as follows.
Palm shell: cork chip = 1:2
The particle sizes of palm shell and cork chips are as follows.
Palm shell: 1-8mm
Cork chip: 1-2mm
ヤシ殻活性炭Ｄは臭いを吸い取る脱臭作用、空気や水や油等を浄化する浄化作用、空気中の水分を調湿する調湿作用を行うのである。また、コルクチップＦは、ガスのような空気を含んだ独特の細胞構造により、熱伝導率が極めて低く、衝撃吸収性、耐水性、温度上昇の抑制に優れている。一方、コルク単体で充填物を構成した場合には、乾いたコルクチップ同士の接触で静電気が発生し、当該静電気によってコルクチップＦが人工芝から浮き上がりやすくなるという問題があった。そこで、ヤシ殻素材、とくに粉末ＣやチップＥにおける保水性を利用することで、コルクチップを適度に保湿し、静電気の発生を起こり難くすることで浮き上がりを防止することができるのである。
これらの作用により前述した人工芝製運動競技場に対する効果を奏することができるのである。
The coconut shell activated carbon D has a deodorizing action for absorbing odor, a purifying action for purifying air, water, oil, etc., and a humidity controlling action for controlling moisture in the air. Further, the cork chip F has an extremely low thermal conductivity due to the unique cell structure containing air such as gas, and is excellent in shock absorption, water resistance, and suppression of temperature rise. On the other hand, in the case where the filling material is composed of only the cork, there is a problem that static electricity is generated due to the contact between the dry cork chips, and the cork chip F is easily lifted from the artificial grass by the static electricity. Therefore, by utilizing the water retention property of the coconut shell material, especially the powder C and the chip E, the cork chips can be appropriately moisturized and the generation of static electricity can be made less likely to prevent floating.
By these actions, the above-mentioned effect on the artificial turf sports stadium can be achieved.
本発明の人工芝製運動競技場は、ヤシ殻充填層２２が人工芝葉２１の目に入っていきやすいように、基布２３に対する人工芝葉２１の縫い目のピッチや本数、間隔などを開発し、水の浸透性なども考慮した基布のコーティングや、水抜き穴の数、位置などを調整して、ヤシ殻充填層２２の人工芝葉２１がよく絡みあい、芝目が常に立っているので、強く復元性のある特殊な形状をした人工芝とすることができたのである。これにより、サッカー、ラグビー、アメリカンフットボール、野球等のグラウンドとして利用することができるのである。 In the artificial turf sports field of the present invention, the pitch, the number, and the interval of the seams of the artificial turf leaf 21 with respect to the base fabric 23 are developed so that the palm shell filling layer 22 can easily enter the eyes of the artificial turf leaf 21. By adjusting the coating of the base fabric in consideration of water permeability and the number and position of drainage holes, the artificial turf leaves 21 of the coconut shell filling layer 22 are well entangled with each other, and the grass is always standing. Therefore, it was possible to obtain an artificial turf with a special shape that is strong and resilient. As a result, it can be used as a ground for soccer, rugby, American football, baseball, etc.
１ 基礎層
２ 人工芝
２１ 人工芝葉
２２ ヤシ殻充填層
２３ 基布
２４ ゴムチップ
２５ 珪砂
２６ コルクチップ層
２７ ヤシ殻−コルクチップ混合充填層
Ａ 短い繊維
Ｂ 長い繊維
Ｃ 粉末
Ｄ ヤシ殻活性炭
Ｅ 細かいチップ
Ｆ コルクチップ
Ｙ ヤシ殻
Ｔ 外果皮
Ｎ 中果皮
Ｓ 内果皮
1 Foundation layer 2 Artificial grass 21 Artificial grass leaf 22 Palm shell filling layer 23 Base cloth 24 Rubber chip 25 Silica sand 26 Cork chip layer 27 Palm shell-cork chip mixed packing layer A Short fiber B Long fiber C Powder D Palm shell activated carbon E Fine chip F Cork chip Y Palm shell T Epicarp N Mesocarpus S Inner skin
Claims (9)
前記充填物の上層部をヤシ殻充填層により構成し、
前記ヤシ殻充填層は、ヤシ殻を乾燥した成分と、ヤシ殻を炭化させたヤシ殻活性炭を混合した充填物により構成した
ことを特徴とする人工芝。 An artificial turf that is configured so that artificial turf leaves are spaced apart from a base fabric and protrude upward, and a filling material is filled between the artificial turf leaves,
The upper layer portion of the filling is constituted by a coconut shell filling layer,
The artificial turf is characterized in that the coconut shell filling layer is composed of a mixture of a dried coconut shell component and coconut shell activated carbon obtained by carbonizing the coconut shell.
ヤシ殻の乾燥した成分は、粉末とチップと繊維を乾燥時には分離し、施工時において、前記乾燥した成分を再度混合する
ことを特徴とする人工芝。 The artificial turf according to claim 1,
An artificial turf is characterized in that a dried component of coconut shell separates powder, chips and fibers at the time of drying, and mixes the dried component again at the time of construction.
ヤシ殻の乾燥した成分は、ヤシ殻を構成する部分において、中果皮と外果皮の部分を選別して取り出し、粉末とチップと繊維とにより構成した
ことを特徴とする人工芝。 The artificial turf according to claim 1,
The dried coconut shell component is an artificial turf characterized by being composed of powder, chips, and fibers by separating and extracting the mesocarp and epicarp parts in the part constituting the coconut shell.
ヤシ殻活性炭は、ヤシ殻の中の、内果皮の部分を取り出して焼成し炭化させた
ことを特徴とする人工芝。 The artificial turf according to claim 1,
Activated coconut shell charcoal is an artificial turf characterized by taking out the part of the inner skin from the coconut shell, firing and carbonizing it.
前記充填物のうち下部の充填層を珪砂とし、上部の充填層をヤシ殻充填層により構成した
ことを特徴とする人工芝。 The artificial turf according to claim 1,
An artificial turf characterized in that the lower filling layer of the filling is silica sand, and the upper filling layer is a coconut shell filling layer.
ヤシ殻充填層と珪砂の間にゴムチップ層を介装した
ことを特徴とする人工芝。 The artificial turf according to claim 5,
An artificial turf characterized by having a rubber chip layer interposed between a palm shell filling layer and silica sand.
前記充填物の上部を、前記ヤシ殻充填層と、コルクチップから構成されるコルクチップ充填層とを含む構成とした
ことを特徴とする人工芝。 The artificial turf according to claim 1,
An artificial turf characterized in that an upper part of the filling material is configured to include the palm shell filling layer and a cork chip filling layer composed of cork chips.
前記充填物の上層部をヤシ殻−コルクチップ混合充填層により構成し、
前記ヤシ殻−コルクチップ混合充填層は、ヤシ殻を乾燥した成分と、ヤシ殻を炭化させたヤシ殻活性炭と、コルクチップとを混合した充填物により構成した
ことを特徴とする人工芝。 An artificial turf that is configured so that artificial turf leaves are spaced apart from a base fabric and protrude upward, and a filling material is filled between the artificial turf leaves,
The upper layer portion of the filling is constituted by a coconut shell-cork chip mixed filling layer,
The coconut shell-cork chip mixed packing layer is composed of a packing material that is a mixture of a dried coconut shell component, a coconut shell carbonized coconut shell activated carbon, and a cork chip.