JP2018520022A - 耐衝撃性アンダーボディシールド材及び物品、ならびにそれらの使用方法 - Google Patents
耐衝撃性アンダーボディシールド材及び物品、ならびにそれらの使用方法 Download PDFInfo
- Publication number
- JP2018520022A JP2018520022A JP2017564567A JP2017564567A JP2018520022A JP 2018520022 A JP2018520022 A JP 2018520022A JP 2017564567 A JP2017564567 A JP 2017564567A JP 2017564567 A JP2017564567 A JP 2017564567A JP 2018520022 A JP2018520022 A JP 2018520022A
- Authority
- JP
- Japan
- Prior art keywords
- film
- core layer
- resin
- fiber
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本出願は、2015年6月12日出願の米国特許仮出願第62/175,004号に関連し、また同出願の利益及び優先権を主張するものであり、その開示内容全体は、あらゆる目的において参照として本明細書に組み込まれる。
特定の実施形態について、以下の添付図面を参照しながら説明する。
小石を板の表面に対して90度、すなわち垂直で、板へと射出した。使用した小石は、8〜16mmの大きさの水で侵食した沖積層の路面砂利であった。小石を、空気圧70psi、8±2秒の間隔で、気流にのせて供給した。観察用に、10サイクル毎に試験片を取り出した。外表面全体において、亀裂、膨れ、デラミネーション、または侵食のいずれかがあれば、失敗であることを示す。上記の失敗のいずれかが観察されるまで試験を続けた。それぞれのサンプルについて、2つの試験片を試験した。失敗時のサイクル数は、2つの試験片の平均値とした。試験板の坪量は、1平方メートルあたり約1250g(gsm)であった。スクリム(0.1〜0.2mmの厚み)、フィルム(50〜500ミクロンの厚み)、及びそれらの間のポリプロピレン樹脂/ガラス繊維コアを含む試験板の総厚みは、約2mmであった。
試験したLWRTは、2つの主要な構成要素、チョップドガラス繊維及びポリプロピレン(PP)樹脂で構成された。ガラス繊維は高弾性率補強材の役割を果たし、PP樹脂は、補強材を所定の位置に固定し、負荷を受けた状態で変形して補強材へと応力を分散させるマトリックスである。2つの主要な構成要素の充填速度を変化させることにより、最終作製物におけるガラス繊維/PP樹脂の比率が変化し得る。LWRTのグラベロメーター性能に対するガラス/樹脂比率の影響を、表1に示す。
PPホモポリマーフィルムをコア材料上に一体化させたLWRT成形品について試験した。このスキンフィルムは、複合材料構造体に耐湿性、塩水噴霧耐性、及びストーンチッピング耐性を付与する。石材衝突試験では、スキンフィルムがコアから剥離した場合、またはフィルム内に亀裂が現れた場合、アンダーボディパネルは、グラベロメーター試験に失敗したとみなされる。本試験では、同一組成だが厚みの異なるフィルムについて試験して、UBSパネルの石材衝突性能に対するスキンフィルムの厚みの影響を確認した。表2に、異なる厚みのスキンフィルムを備えた成形済みLWRTシートにおけるグラベロメーター試験の結果を示す。
コア内の樹脂におけるメルトフローインデックス(MFI)の影響を測定して、コア樹脂のMFIを変化させた場合に衝撃性能が変化するかを確認した。MFIは、例えば、2013年付けのASTM D1238,condition Lを用いて測定してもよく、例えば、単位は通常省略するが、g/10分で示してもよい。樹脂MFIは、オーブン内での乾燥プロセス中にどれだけ速く樹脂が流動可能であるかに、またガラス繊維にいかに良好にウェットアウト可能であるかに影響を与え得る。優れたウェットアウト性は通常、複合材料に優れた機械的強度を付与する。MFIの異なる2種類のPP樹脂について試験した。高MFI樹脂は、例えば、約300のMFI値を有し、低MFI樹脂、例えば、約100の約3倍であった。それらに対するグラベロメーター試験の結果における比較を表3に示す。
耐衝撃性に対する膨張剤の影響について試験した。膨張剤をLWRT配合物に添加して、その膨張性能を高めることにより、重量を抑え、また音響性能を向上させることができる。膨張剤添加の影響を表4に示す。微粒子状の膨張剤、HS1100を使用した。
ポリプロピレンホモポリマーフィルムを、約55重量パーセント以上の熱可塑性ポリマー、ガラス繊維、及び膨張剤を含むLWRTコア板上に配置することにより、アンダーボディシールドを製造することができる。不織布スクリムを板の反対側の面に接合してもよい。得られた複合材料を熱成形により更に加工し、アンダーボディシールドとして用いるのに望ましい形状及び/またはサイズとすることができる。
ポリプロピレン−ポリエチレンコポリマーフィルム(50%超のコポリマーがポリプロピレン)を、約55重量パーセント以上の熱可塑性ポリマー、ガラス繊維、及び膨張剤を含むLWRTコア板上に配置することにより、アンダーボディシールドを製造することができる。不織布スクリムを板の反対側の面に接合してもよい。得られた複合材料を熱成形により更に加工し、アンダーボディシールドとして用いるのに望ましい形状及び/またはサイズとすることができる。
ポリプロピレンホモポリマーフィルムを、約55〜60重量パーセント以上の熱可塑性ポリマー、約40〜45重量パーセントのガラス繊維、及び約0.1〜5重量パーセントの膨張剤を含むLWRTコア板上に配置することにより、アンダーボディシールドを製造することができる。不織布スクリムを板の反対側の面に接合してもよい。得られた複合材料を熱成形により更に加工し、アンダーボディシールドとして用いるのに望ましい形状及び/またはサイズとすることができる。
ポリプロピレン−ポリエチレンコポリマーフィルム(50%超のコポリマーがポリプロピレン)を、約55〜60重量パーセント以上の熱可塑性ポリマー、約40〜45重量パーセントのガラス繊維、及び約0.1〜5重量パーセントの膨張剤を含むLWRTコア板上に配置することにより、アンダーボディシールドを製造することができる。不織布スクリムを板の反対側の面に接合してもよい。得られた複合材料を熱成形により更に加工し、アンダーボディシールドとして用いるのに望ましい形状及び/またはサイズとすることができる。
ポリプロピレンホモポリマーフィルムを、約55〜60重量パーセント以上の熱可塑性ポリマー、約40〜45重量パーセントのガラス繊維、及び約0.1〜5重量パーセントの微粒子状の膨張剤を含むLWRTコア板上に配置することにより、アンダーボディシールドを製造することができる。不織布スクリムを板の反対側の面に接合してもよい。得られた複合材料を熱成形により更に加工し、アンダーボディシールドとして用いるのに望ましい形状及び/またはサイズとすることができる。
ポリプロピレン−ポリエチレンコポリマーフィルム(50%超のコポリマーがポリプロピレン)を、約55〜60重量パーセント以上の熱可塑性ポリマー、約40〜45重量パーセントのガラス繊維、及び約0.1〜5重量パーセントの微粒子状の膨張剤を含むLWRTコア板上に配置することにより、アンダーボディシールドを製造することができる。不織布スクリムを板の反対側の面に接合してもよい。得られた複合材料を熱成形により更に加工し、アンダーボディシールドとして用いるのに望ましい形状及び/またはサイズとすることができる。
表5に示す樹脂:ガラス比率を含む、2種類のLWRT板(それぞれの種類の板に対し2つの複製)を作製した。
表6に示す材料を備えた3種類のLWRT板を作製した。
Claims (110)
- アンダーボディシールド組成物であって、
熱可塑性ポリマーで互いに結合した強化繊維の不規則な交差が画定する、連続気泡構造ウェブを含む熱可塑性コア層と、前記熱可塑性コア層は更に、熱にさらした際に前記コア層の厚みを増加させて膨張後のコア層を提供可能な膨張剤を含み、
前記コア層の第1表面上に配置されたフィルムと、を含み、
前記膨張後のコア層及びフィルムは共に、前記フィルムへの損傷を受けずに、SAE J400の手順に従った少なくとも50個の個々の衝撃物に耐えることが可能なアンダーボディシールド物品を提供する、前記アンダーボディシールド組成物。 - 前記フィルムはホモポリマーフィルムまたはコポリマーフィルムである、請求項1に記載のアンダーボディシールド組成物。
- 前記ホモポリマーはポリオレフィンである、請求項2に記載のアンダーボディシールド組成物。
- 前記熱可塑性ポリマーは、前記コア層内において50重量パーセント以上で存在する、請求項1に記載のアンダーボディシールド組成物。
- 前記フィルムは少なくとも10ミルの厚みである、請求項4に記載のアンダーボディシールド組成物。
- 前記膨張剤は、前記コア層内において4重量パーセント以上で存在する、請求項5に記載のアンダーボディシールド組成物。
- 前記強化繊維は、ガラス繊維、炭素繊維、黒鉛繊維、合成有機繊維、無機繊維、天然繊維、鉱物繊維、金属繊維、金属無機繊維、金属合成繊維、セラミック繊維、及びこれらの組み合わせからなる群から選択される、請求項6に記載のアンダーボディシールド組成物。
- 前記熱可塑性ポリマーは、ポリオレフィン樹脂、熱可塑性ポリオレフィン配合樹脂、ポリビニルポリマー樹脂、ブタジエンポリマー樹脂、アクリルポリマー樹脂、ポリアミド樹脂、ポリエステル樹脂、ポリカーボネート樹脂、ポリエステルカーボネート樹脂、ポリスチレン樹脂、アクリロニトリルスチレンポリマー樹脂、アクリロニトリル−ブチルアクリレート−スチレンポリマー樹脂、ポリエーテルイミド樹脂、ポリフェニレンエーテル樹脂、ポリフェニレンオキサイド樹脂、ポリフェニレンサルファイド樹脂、ポリエーテル樹脂、ポリエーテルケトン樹脂、ポリアセタール樹脂、ポリウレタン樹脂、ポリベンズイミダゾール樹脂、及びコポリマー、ならびにこれらの組み合わせからなる群から選択されるポリマー樹脂である、請求項7に記載のアンダーボディシールド組成物。
- 前記熱可塑性コア層は、ポリプロピレン、ガラス繊維、及び微粒子状の膨張剤を含み、前記フィルムはポリプロピレンホモポリマーフィルムである、請求項1に記載のアンダーボディシールド組成物。
- 前記フィルムは、介在層または介在材料を何ら設けずに、前記コア層の前記第1表面上に直接配置される、請求項9に記載のアンダーボディシールド組成物。
- 前記コア層の前記第1表面の反対側にある前記コア層の第2表面上に配置されたスクリムを更に含む、請求項1に記載のアンダーボディシールド組成物。
- 前記スクリムは、ガラス繊維、アラミド繊維、黒鉛繊維、炭素繊維、無機鉱物繊維、金属繊維、金属合成繊維、及び金属無機繊維を含む、請求項11に記載のアンダーボディシールド組成物。
- 前記スクリム上に配置された別のスキン層を更に含む、請求項11に記載のアンダーボディシールド組成物。
- 前記熱可塑性コア層は、ポリプロピレン、ガラス繊維、及び微粒子状の膨張剤を含み、前記フィルムはポリプロピレンホモポリマーフィルムであり、前記スクリムはポリエステル不織布スクリムである、請求項11に記載のアンダーボディシールド組成物。
- 前記フィルムは、介在層または介在材料を何ら設けずに、前記コア層の前記第1表面上に直接配置され、前記スクリムは、介在層または介在材料を何ら設けずに、前記コア層の前記第2表面上に直接配置される、請求項14に記載のアンダーボディシールド組成物。
- 前記スクリムは、1つまたは複数のストリップとして前記コア層の前記第2表面上に配置される、請求項11に記載のアンダーボディシールド組成物。
- 前記コア層と接合した別のコア層を更に含み、前記別のコア層は、熱可塑性ポリマーで互いに結合した強化繊維の不規則な交差が画定する、連続気泡構造ウェブを含む、請求項1に記載のアンダーボディシールド組成物。
- 前記別のコア層は、前記別のコア層の厚みを増加可能な膨張剤を更に含む、請求項17に記載のアンダーボディシールド組成物。
- 前記別のコア層は、前記コア層内に存在する熱可塑性材料の量よりも低い重量パーセントの熱可塑性材料を含む、請求項17に記載のアンダーボディシールド組成物。
- 前記フィルムは、前記コア層の厚みを減少させる場合に、より多くの衝撃物に耐えるように構成されている、請求項1に記載のアンダーボディシールド組成物。
- アンダーボディシールド組成物であって、
熱可塑性ポリマーで互いに結合した強化繊維の不規則な交差が画定する、連続気泡構造ウェブを含む熱可塑性コア層と、前記熱可塑性コア層は更に、熱にさらした際に前記コア層の厚みを増加させて膨張後のコア層を提供可能な膨張剤を含み、
前記コア層の第1表面上に配置されたホモポリマーポリオレフィンフィルムまたはコポリマーポリオレフィンフィルムと、
前記コア層の第2表面上に配置されたスクリムと、を含み、
前記膨張後のコア層、フィルム、及びスクリムは共に、前記フィルムへの損傷を受けずに、SAE J400の手順に従った少なくとも50個の個々の衝撃物に耐えることが可能なアンダーボディシールド物品を提供する、前記アンダーボディシールド組成物。 - 前記スクリム上に配置された装飾層を更に含む、請求項21に記載のアンダーボディシールド組成物。
- 前記熱可塑性コア層は、5%超〜最大約95%の空隙率を含む、請求項21に記載のアンダーボディシールド組成物。
- 前記熱可塑性ポリマーは、前記コア層内において50重量パーセント以上で存在する、請求項21に記載のアンダーボディシールド組成物。
- 前記フィルムは少なくとも10ミルの厚みである、請求項24に記載のアンダーボディシールド組成物。
- 前記膨張剤は、前記コア層内において4重量パーセント以上で存在する、請求項25に記載のアンダーボディシールド組成物。
- 前記強化繊維は、ガラス繊維、炭素繊維、黒鉛繊維、合成有機繊維、無機繊維、天然繊維、鉱物繊維、金属繊維、金属無機繊維、金属合成繊維、セラミック繊維、及びこれらの組み合わせからなる群から選択される、請求項26に記載のアンダーボディシールド組成物。
- 前記熱可塑性ポリマーは、ポリオレフィン樹脂、熱可塑性ポリオレフィン配合樹脂、ポリビニルポリマー樹脂、ブタジエンポリマー樹脂、アクリルポリマー樹脂、ポリアミド樹脂、ポリエステル樹脂、ポリカーボネート樹脂、ポリエステルカーボネート樹脂、ポリスチレン樹脂、アクリロニトリルスチレンポリマー樹脂、アクリロニトリル−ブチルアクリレート−スチレンポリマー樹脂、ポリエーテルイミド樹脂、ポリフェニレンエーテル樹脂、ポリフェニレンオキサイド樹脂、ポリフェニレンサルファイド樹脂、ポリエーテル樹脂、ポリエーテルケトン樹脂、ポリアセタール樹脂、ポリウレタン樹脂、ポリベンズイミダゾール樹脂、及びコポリマー、ならびにこれらの組み合わせからなる群から選択されるポリマー樹脂である、請求項27に記載のアンダーボディシールド組成物。
- 前記熱可塑性コア層は、ポリプロピレン、ガラス繊維、及び微粒子状の膨張剤を含み、前記フィルムはポリプロピレンホモポリマーフィルムである、請求項21に記載のアンダーボディシールド組成物。
- 前記フィルムは、介在層または介在材料を何ら設けずに、前記コア層の前記第1表面上に直接配置される、請求項29に記載のアンダーボディシールド組成物。
- プリプレグであって、
熱可塑性ポリマー、強化繊維、及び膨張剤を含む第1層と、前記第1層は、前記第1層の硬化により連続気泡構造ウェブを含む層を形成可能であり、前記連続気泡構造ウェブは、前記ウェブの前記連続気泡構造内部に捕捉された前記膨張剤を用いて、前記熱可塑性ポリマーで互いに結合した前記強化繊維の不規則な交差により画定され、前記膨張剤は、熱にさらした後に前記第1層の厚みを増加させて、膨張後の第1層を提供可能であり、
前記第1層の第1表面上に配置されたフィルムと、を含み、
前記膨張後の第1層及びフィルムは共に、前記フィルムへの損傷を受けずに、SAE J400の手順に従った少なくとも50個の個々の衝撃物に耐えることが可能な、前記プリプレグ。 - 前記フィルムはホモポリマーフィルムである、請求項31に記載のプリプレグ。
- 前記ホモポリマーはポリオレフィンである、請求項32に記載のプリプレグ。
- 前記熱可塑性ポリマーは、前記第1層内において50重量パーセント以上で存在する、請求項31に記載のプリプレグ。
- 前記フィルムは少なくとも10ミルの厚みである、請求項34に記載のプリプレグ。
- 前記膨張剤は、前記第1層内において4重量パーセント以上で存在する、請求項35に記載のプリプレグ。
- 前記強化繊維は、ガラス繊維、炭素繊維、黒鉛繊維、合成有機繊維、無機繊維、天然繊維、鉱物繊維、金属繊維、金属無機繊維、金属合成繊維、セラミック繊維、及びこれらの組み合わせからなる群から選択される、請求項36に記載のプリプレグ。
- 前記熱可塑性ポリマーは、ポリオレフィン樹脂、熱可塑性ポリオレフィン配合樹脂、ポリビニルポリマー樹脂、ブタジエンポリマー樹脂、アクリルポリマー樹脂、ポリアミド樹脂、ポリエステル樹脂、ポリカーボネート樹脂、ポリエステルカーボネート樹脂、ポリスチレン樹脂、アクリロニトリルスチレンポリマー樹脂、アクリロニトリル−ブチルアクリレート−スチレンポリマー樹脂、ポリエーテルイミド樹脂、ポリフェニレンエーテル樹脂、ポリフェニレンオキサイド樹脂、ポリフェニレンサルファイド樹脂、ポリエーテル樹脂、ポリエーテルケトン樹脂、ポリアセタール樹脂、ポリウレタン樹脂、ポリベンズイミダゾール樹脂、及びコポリマー、ならびにこれらの組み合わせからなる群から選択されるポリマー樹脂である、請求項37に記載のプリプレグ。
- 前記第1層は、ポリプロピレン、ガラス繊維、及び微粒子状の膨張剤を含み、前記フィルムはポリプロピレンホモポリマーフィルムである、請求項31に記載のプリプレグ。
- 前記フィルムは、介在層または介在材料を何ら設けずに、前記第1層の前記第1表面上に直接配置される、請求項39に記載のプリプレグ。
- 前記第1層の前記第1表面の反対側にある前記第1層の第2表面上に配置されたスクリムを更に含む、請求項31に記載のプリプレグ。
- 前記スクリムは、ガラス繊維、アラミド繊維、黒鉛繊維、炭素繊維、無機鉱物繊維、金属繊維、金属合成繊維、及び金属無機繊維を含む、請求項41に記載のプリプレグ。
- 前記スクリム上に配置された別のスキン層を更に含む、請求項41に記載のプリプレグ。
- 前記第1層は、ポリプロピレン、ガラス繊維、及び微粒子状の膨張剤を含み、前記フィルムはポリプロピレンホモポリマーフィルムであり、前記スクリムはポリエステル不織布スクリムである、請求項41に記載のプリプレグ。
- 前記フィルムは、介在層または介在材料を何ら設けずに、前記第1層の前記第1表面上に直接配置され、前記スクリムは、介在層または介在材料を何ら設けずに、前記第1層の前記第2表面上に直接配置される、請求項44に記載のプリプレグ。
- 前記スクリムは、1つまたは複数のストリップとして前記第1層の前記第2表面上に配置される、請求項41に記載のプリプレグ。
- 前記第1層と接合した別の層を更に含み、前記別の層は、熱可塑性ポリマーで互いに結合した強化繊維の不規則な交差が画定する、連続気泡構造ウェブを含む、請求項31に記載のプリプレグ。
- 前記別の層は、前記別の層の厚みを増加可能な膨張剤を更に含む、請求項47に記載のプリプレグ。
- 前記別の層は、前記第1層内に存在する熱可塑性材料の量よりも低い重量パーセントの熱可塑性材料を含む、請求項47に記載のプリプレグ。
- 前記フィルムは、前記第1層の厚みを減少させる場合に、より多くの衝撃物に耐えるように構成されている、請求項31に記載のプリプレグ。
- アンダーボディシールドであって、
熱可塑性ポリマーで互いに結合した強化繊維の不規則な交差が画定する、連続気泡構造ウェブを含む熱可塑性コア層と、前記熱可塑性コア層は更に、熱にさらした際に前記コア層の厚みを増加させて膨張後のコア層を提供可能な膨張剤を含み、
前記コア層の第1表面上に配置されたフィルムと、を含み、
前記膨張後のコア層及びフィルムは共に、前記フィルムへの損傷を受けずに、SAE J400の手順に従った少なくとも50個の個々の衝撃物に耐えることが可能な前記アンダーボディシールドを提供し、前記アンダーボディシールドは、車両の底面に連結させるための1ヵ所または複数ヵ所の取り付け領域を含む、前記アンダーボディシールド。 - 前記アンダーボディシールドは、前記アンダーボディシールドが前記車両に連結する際に、車両の抵抗係数を減少させるような形状となっている、請求項51に記載のアンダーボディシールド。
- 前記フィルムはホモポリマーポリオレフィンフィルムである、請求項51に記載のアンダーボディシールド。
- 前記熱可塑性ポリマーは、前記コア層内において50重量パーセント以上で存在する、請求項53に記載のアンダーボディシールド。
- 前記フィルムは少なくとも10ミルの厚みである、請求項54に記載のアンダーボディシールド。
- 前記膨張剤は、前記コア層内において4重量パーセント以上で存在する、請求項55に記載のアンダーボディシールド。
- 前記熱可塑性コア層は、ポリプロピレン、ガラス繊維、及び微粒子状の膨張剤を含み、前記フィルムはポリプロピレンホモポリマーフィルムである、請求項51に記載のアンダーボディシールド。
- 前記フィルムは、介在層または介在材料を何ら設けずに、前記コア層の前記第1表面上に直接配置される、請求項57に記載のアンダーボディシールド。
- 前記コア層の前記第1表面の反対側にある前記コア層の第2表面上に配置されたスクリムを更に含む、請求項51に記載のアンダーボディシールド。
- 前記熱可塑性コア層は、ポリプロピレン、ガラス繊維、及び微粒子状の膨張剤を含み、前記フィルムはポリプロピレンホモポリマーフィルムであり、前記スクリムはポリエステル不織布スクリムである、請求項59に記載のアンダーボディシールド。
- 複合プリプレグの形成方法であって、
熱可塑性ポリマー、強化繊維、及び膨張剤を水溶液中に混ぜ合わせることと、
前記熱可塑性ポリマー、強化繊維、及び膨張剤を含む前記水溶液を混合し、前記強化繊維及び前記膨張剤を前記熱可塑性ポリマー中に分散させて水性発泡分散液を得ることと、
前記水性発泡分散液を成形用部材上に配置することと、
前記配置した水性発泡液から水分を除去して、前記熱可塑性ポリマー、前記強化繊維、及び前記膨張剤を含むウェブを得ることと、
前記ウェブ中の前記熱可塑性ポリマーの軟化温度を超える温度で前記ウェブを加熱することと、
フィルムを前記ウェブの第1表面上に配置して、前記配置したフィルムへの損傷を受けずに、SAE J400の手順に従った少なくとも50個の個々の衝撃物に耐えることが可能な複合プリプレグを得ることと、を含む、前記複合プリプレグの形成方法。 - 前記複合プリプレグを所定の厚みまで加圧して複合物品を成形することを更に含む、請求項61に記載の方法。
- 前記複合物品を膨張させて前記複合物品の前記厚みを増加させることを更に含む、請求項62に記載の方法。
- スクリムを前記ウェブの第2表面上に配置することを更に含む、請求項61に記載の方法。
- 前記複合プリプレグを所定の厚みまで加圧して複合物品を成形することを更に含む、請求項64に記載の方法。
- 前記熱可塑性ポリマーをポリプロピレン樹脂で構成し、前記強化繊維をガラス繊維で構成し、前記膨張剤を微粒子で構成することを更に含む、請求項61に記載の方法。
- 前記フィルムをホモポリマーフィルムまたはコポリマーフィルムで構成することを更に含む、請求項66に記載の方法。
- 前記ホモポリマーフィルムにポリオレフィンフィルムを選択することを更に含む、請求項67に記載の方法。
- 前記フィルムを少なくとも10ミルの厚みを有するように構成することを更に含む、請求項67に記載の方法。
- 前記熱可塑性樹脂を、前記水溶液中において50重量パーセント以上で存在するように構成することを更に含む、請求項69に記載の方法。
- 複合物品の形成方法であって、
熱可塑性ポリマー、強化繊維、及び膨張剤を水溶液中に混ぜ合わせることと、
前記熱可塑性ポリマー、強化繊維、及び膨張剤を含む前記水溶液を混合し、前記強化繊維及び前記膨張剤を前記熱可塑性ポリマー中に分散させて水性発泡分散液を得ることと、
前記水性発泡分散液を成形用部材上に配置することと、
前記配置した水性発泡液から水分を除去して、前記熱可塑性ポリマー、前記強化繊維、及び前記膨張剤から形成されるウェブを含むコア層を得ることと、
前記コア層中の前記熱可塑性ポリマーの軟化温度を超える温度で前記コア層を加熱することと、
耐衝撃性フィルムを前記コア層の第1表面上に配置することと、
スクリムを前記コア層の第2表面上に配置して複合物品を得ることと、
前記複合物品を選択した厚みまで加圧することと、を含み、前記加圧済み複合物品は、前記配置したフィルムへの損傷を受けずに、SAE J400の手順に従った少なくとも50個の個々の衝撃物に耐えることが可能である、前記複合物品の形成方法。 - 前記複合物品を膨張させて前記複合物品の前記厚みを増加させることを更に含む、請求項71に記載の方法。
- 前記スクリムに、ガラス繊維、アラミド繊維、黒鉛繊維、炭素繊維、無機鉱物繊維、金属繊維、金属合成繊維、及び金属無機繊維を含むスクリムを選択することを更に含む、請求項71に記載の方法。
- 前記フィルム及び前記スクリムは、同時に前記コア層上に配置される、請求項71に記載の方法。
- 前記熱可塑性ポリマー及び前記膨張剤のそれぞれを、ほぼ同一の平均粒径を有する粒子で構成することを更に含む、請求項71に記載の方法。
- 前記熱可塑性ポリマーをポリプロピレン樹脂で構成し、前記強化繊維をガラス繊維で構成し、前記膨張剤を微粒子で構成することを更に含む、請求項71に記載の方法。
- 前記フィルムをホモポリマーフィルムまたはコポリマーフィルムで構成することを更に含む、請求項76に記載の方法。
- 前記ホモポリマーフィルムにポリオレフィンフィルムを選択することを更に含む、請求項77に記載の方法。
- 前記フィルムを少なくとも10ミルの厚みを有するように構成することを更に含む、請求項77に記載の方法。
- 前記熱可塑性樹脂を、前記水溶液中において50重量パーセント以上で存在するように構成することを更に含む、請求項79に記載の方法。
- 車両の抵抗を減少させる方法であって、前記方法は、アンダーボディシールドを前記車両に連結させることを含み、前記アンダーボディシールドは、熱可塑性ポリマーで互いに結合した強化繊維の不規則な交差が画定する、連続気泡構造ウェブを含む熱可塑性コア層を含み、前記熱可塑性コア層は更に、熱にさらした際に前記コア層の厚みを増加させて膨張後のコア層を提供可能な膨張剤、及び前記コア層の第1表面上に配置されたフィルムを含み、前記アンダーボディシールドは、前記アンダーボディシールドの前記フィルムへの損傷を受けずに、SAE J400の手順に従った少なくとも50個の個々の衝撃物に耐えることが可能である、前記方法。
- 前記アンダーボディシールドを成形するための指示書を提供することを更に含む、請求項81に記載の方法。
- 前記アンダーボディシールドの前記コア層を膨張させるための指示書を提供することを更に含む、請求項81に記載の方法。
- 前記アンダーボディシールドを前記自動車両に連結するように構成された、少なくとも1つの締結具を提供することを更に含む、請求項81に記載の方法。
- 前記アンダーボディシールドを前記自動車両に取り付けるための指示書を更に含む、請求項81に記載の方法。
- 車両の抵抗を減少させる方法であって、前記方法は、アンダーボディシールドを前記車両に連結させることを含み、前記アンダーボディシールドは、熱可塑性ポリマーで互いに結合した強化繊維の不規則な交差が画定する、連続気泡構造ウェブを含む熱可塑性コア層を含み、前記熱可塑性コア層は更に、熱にさらした際に前記コア層の厚みを増加させて膨張後のコア層を提供可能な膨張剤、前記コア層の第1表面上に配置されたフィルム、及び前記コア層の第2表面上に配置されたスクリムを含み、前記アンダーボディシールドは、前記アンダーボディシールドの前記フィルムへの損傷を受けずに、SAE J400の手順に従った少なくとも50個の個々の衝撃物に耐えることが可能である、前記方法。
- 前記プリプレグを硬化させてアンダーボディシールドを成形するための指示書を提供することを更に含む、請求項86に記載の方法。
- 前記プリプレグを成形してアンダーボディシールドを作製するための指示書を提供することを更に含む、請求項86に記載の方法。
- 前記プリプレグの前記接着剤層を架橋させるための指示書を提供することを更に含む、請求項86に記載の方法。
- 前記コア層を膨張させるための指示書を提供することを更に含む、請求項86に記載の方法。
- 車両の抵抗を減少させる方法であって、前記方法は、熱可塑性ポリマーで互いに結合した強化繊維の不規則な交差が画定する、連続気泡構造ウェブを含む熱可塑性コア層を含むアンダーボディシールドを提供することを含み、前記熱可塑性コア層は更に、熱にさらした際に前記コア層の厚みを増加させて膨張後のコア層を提供可能な膨張剤、及び前記コア層の第1表面上に配置されたフィルムを含み、前記アンダーボディシールドは、前記アンダーボディシールドの前記フィルムへの損傷を受けずに、SAE J400の手順に従った少なくとも50個の個々の衝撃物に耐えることが可能である、前記方法。
- 前記アンダーボディシールドを成形するための指示書を提供することを更に含む、請求項91に記載の方法。
- 前記アンダーボディシールドの前記コア層を膨張させるための指示書を提供することを更に含む、請求項91に記載の方法。
- 前記アンダーボディシールドを前記自動車両に連結するように構成された、少なくとも1つの締結具を提供することを更に含む、請求項91に記載の方法。
- 前記アンダーボディシールドを前記自動車両に取り付けるための指示書を提供することを更に含む、請求項91に記載の方法。
- 車両の抵抗を減少させる方法であって、前記方法は、熱可塑性ポリマーで互いに結合した強化繊維の不規則な交差が画定する、連続気泡構造ウェブを含む熱可塑性コア層を含むアンダーボディシールドを提供することを含み、前記熱可塑性コア層は更に、熱にさらした際に前記コア層の厚みを増加させて膨張後のコア層を提供可能な膨張剤、前記コア層の第1表面上に配置されたフィルム、及び前記コア層の第2表面上に配置されたスクリムを含み、前記アンダーボディシールドは、前記アンダーボディシールドの前記フィルムへの損傷を受けずに、SAE J400の手順に従った少なくとも50個の個々の衝撃物に耐えることが可能である、前記方法。
- 前記プリプレグを硬化させてアンダーボディシールドを成形するための指示書を提供することを更に含む、請求項96に記載の方法。
- 前記プリプレグを成形してアンダーボディシールドを作製するための指示書を提供することを更に含む、請求項96に記載の方法。
- 前記プリプレグの前記接着剤層を架橋させるための指示書を提供することを更に含む、請求項96に記載の方法。
- 前記コア層を膨張させるための指示書を提供することを更に含む、請求項96に記載の方法。
- 繊維強化熱可塑性ポリマーコア、及び前記繊維強化熱可塑性ポリマーコアの表面上に配置されたフィルムを含む成形済み複合材料であって、前記成形済み複合材料は、前記アンダーボディシールドの前記フィルムへの損傷を受けずに、SAE J400の手順に従った少なくとも50個の個々の衝撃物に耐えることが可能である、前記成形済み複合材料。
- 前記繊維強化熱可塑性ポリマーコアは、熱可塑性ポリマーで互いに結合した強化繊維の不規則な交差が画定する、連続気泡構造ウェブを含む、請求項101に記載の成形済み複合材料。
- 前記強化繊維はガラス繊維を含む、請求項102に記載の成形済み複合材料。
- 前記フィルムは少なくとも10ミルの厚みを含む、請求項103に記載の成形済み複合材料。
- 前記熱可塑性ポリマーは50重量パーセント以上で存在し、前記ポリマーコアは膨張剤を更に含む、請求項104に記載の成形済み複合材料。
- 繊維強化熱可塑性ポリマーコア、前記繊維強化熱可塑性ポリマーコアの第1表面上に配置されたフィルム、及び前記繊維強化熱可塑性ポリマーコアの第2表面上に配置されたスクリムを含む成形済み複合材料であって、前記成形済み複合材料は、前記アンダーボディシールドの前記フィルムへの損傷を受けずに、SAE J400の手順に従った少なくとも50個の個々の衝撃物に耐えることが可能である、前記成形済み複合材料。
- 前記繊維強化熱可塑性ポリマーコアは、熱可塑性ポリマーで互いに結合した強化繊維の不規則な交差が画定する、連続気泡構造ウェブを含む、請求項106に記載の成形済み複合材料。
- 前記強化繊維はガラス繊維を含む、請求項107に記載の成形済み複合材料。
- 前記フィルムは少なくとも10ミルの厚みを含む、請求項108に記載の成形済み複合材料。
- 前記熱可塑性ポリマーは50重量パーセント以上で存在し、前記ポリマーコアは膨張剤を更に含む、請求項109に記載の成形済み複合材料。