JP2017530234A - パイプ用プロピレン系共重合体組成物 - Google Patents
パイプ用プロピレン系共重合体組成物 Download PDFInfo
- Publication number
- JP2017530234A JP2017530234A JP2017517239A JP2017517239A JP2017530234A JP 2017530234 A JP2017530234 A JP 2017530234A JP 2017517239 A JP2017517239 A JP 2017517239A JP 2017517239 A JP2017517239 A JP 2017517239A JP 2017530234 A JP2017530234 A JP 2017530234A
- Authority
- JP
- Japan
- Prior art keywords
- propylene
- weight
- component
- polyolefin composition
- ethylene copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
A)90.0重量%〜99.0重量%のプロピレンホモポリマーであって:
(i)多分散指数が5〜10であり、
(ii)25℃でのキシレン可溶物が4.0重量%〜1.0重量%であり;
(iii)メルトフローレート(230℃/5kg、ISO1133)が0.2g/10分〜3.5g/10分である、プロピレンホモポリマーと;
B)1.0重量%〜10.0重量%のプロピレン、エチレン共重合体組成物であって:
b1)エチレン誘導単位の含有量が0.1重量%〜4.5重量%であり;25℃で測定したキシレン可溶物の含有量が10重量%よりも少なく;メルトフローレート(230℃/2.16kg、ISO1133)が50g/10分〜120g/10分である;14重量%〜52重量%のプロピレンホモポリマーまたはプロピレン/エチレン共重合体;
b2)エチレン誘導単位の含有量が20.0重量%〜55.0重量%である48重量%〜86重量%のプロピレンエチレン共重合体を含んでいる、プロピレン、エチレン共重合体組成物とを含む、ポリオレフィン組成物であって;
仕上がったポリオレフィン組成物は、メルトフローレート(230℃/5kg、ISO1133)が0.2g/10分〜4.0g/10分であり;A+Bの合計量は100であり、b1+b2の合計量は100である、ポリオレフィン組成物である。
A)90.0重量%〜99.0重量%;好ましくは93.0重量%〜98.5.0重量%、さらに好ましくは98.5重量%〜95.0重量%のプロピレンホモポリマーであって:
(i)多分散指数が5〜10であり、
(ii)25℃でのキシレン可溶物が4.0重量%〜1.0重量%;好ましくは3.0重量%〜2.0重量%であり;
(iii)メルトフローレート(230℃/5kg、ISO1133)が0.2g/10分〜3.5g/10分;好ましくは0.6g/10分〜2.0g/10分である、プロピレンホモポリマーと;
B)1.0重量%〜10.0重量%;好ましくは1.5重量%〜7.0重量%;さらに好ましくは1.5重量%〜5.0重量%のプロピレン、エチレン共重合体組成物であって:
b1)エチレン誘導単位の含有量が0.1重量%〜4.5重量%であり;25℃で測定したキシレン可溶物の含有量が10重量%よりも少なく;好ましくは8重量%よりも少なく;さらに好ましくは7重量%よりも少なく;メルトフローレート(230℃/2.16kg、ISO1133)が50g/10分〜120g/10分;好ましくは72g/10分〜115g/10分;さらに好ましくは80g/10分〜95g/10分である;14重量%〜52重量%;好ましくは18重量%〜44重量%;さらに好ましくは22重量%〜38重量%のプロピレンホモポリマーまたはプロピレン/エチレン共重合体;
b2)エチレン誘導単位の含有量が20.0重量%〜55.0重量%;好ましくは28重量%〜45重量%;さらに好ましくは32重量%〜40重量%である;48重量%〜86重量%;好ましくは56重量%〜82重量%;さらに好ましくは62重量%〜78重量%のプロピレンエチレン共重合体を含む、プロピレン;エチレン共重合体組成物とを含む、ポリオレフィン組成物であって:
仕上がったポリオレフィン組成物は、メルトフローレート(230℃/5kg、ISO1133)が0.2g/10分〜4.0g/10分;好ましくは0.4g/10分〜3.0g/10分;さらに好ましくは0.5g/10分〜2g/10分であり;A+Bの合計量は100であり;b1+b2の合計量は100である、ポリオレフィン組成物である。
アイソタクチックまたは主にアイソタクチックのアイソタクチックプロピレンホモポリマー;
エチレンおよび/または1−ブテン、1−ヘキセン、1−オクテン、4−メチル−1−ペンテンなどのC4−C8α−オレフィンを含み、全体のコモノマー含有量が0.05%〜20重量%である、プロピレンのランダムな共重合体およびテルポリマー、またはアイソタクチックまたは主にアイソタクチックのプロピレンホモポリマーを含む前記ポリマーの混合物;
(a)プロピレンホモポリマーおよび/または項目の共重合体およびテルポリマーのうちの1つ(2)と、プロピレンを含むエチレンの共重合体およびテルポリマーおよび/またはC4−C8α−オレフィンを含むエラストマー部分(b)とを含み、必要に応じてそれよりも少ない量のジエンを含有し、異相ポリマーのブレンド(これをポリマー(2)(a)として開示する);
フッ素化ポリマー、ポリビニルジフルオライド(PVDF)などの非結晶質ポリマー、などである。
融解温度および結晶化温度:示差走査熱量測定(Differential Scanning Calorimetry、DSC)によって測定する。重さ6±1mgで、20℃/分の率で220±1℃まで加熱し、窒素流内で2分間220±1℃に保持し、その後、20℃/分の率で40±2℃まで冷却し、そのようにして2分間この温度で保持して試料を結晶化する。次に、試料を最大220℃±1まで20℃/分の温度上昇率で再度溶解させる。溶融走査を記録し、サーモグラムを取得し、そこから融解温度および結晶化温度を読み取る。
エチレン含有量を赤外分光法で測定した。圧縮フィルムの試料をASTM D5576〜00(2013)に従って製造した。ポリマーの圧縮フィルムのスペクトルを吸光度対波数(cm−1)として記録する。以下の測定を用いてC2含有量を算出する:
a)フィルム厚の分光標準化に用いられる4482〜3950cm−1の吸収帯を合わせた面積(At)。
b)アイソタクチックポリプロピレン(IPP)基準スペクトルを正確にデジタル減算した後のメチレン配列(CH2ロッキング振動)によって生じる吸収帯の面積(AC2)。範囲は660〜790cm−1。
IS018011Aに従って算出した。
試料をISO294−2に従って得た。
ISO178に従って測定算出した。
ISO527に従って算出した。
試料をISO1873−2:2007に従って得た。ただし曲げ弾性率についてはISO3167を用いた。
成分A)用の固体触媒成分の製造
機械撹拌器、ジャケットおよび熱電対を備え、窒素でパージした2000mLの5つ口ガラス製反応器に1000mLのTiCl4を導入し、反応器を−5℃で冷却した。撹拌しながら、平均粒子サイズが58μmの微小球状MgCl2・1.7C2H5OH(欧州特許第728769号の実施例1に記載の方法に従って製造)を−5℃で60.0g添加した。温度を40℃に上昇させ、Mg/コハク酸塩のモル比が13になるような量のジエーテル2,3−ジイソプロピルコハク酸を添加した。温度を100℃まで上昇させ、この値を60分間保持した。その後に撹拌を15分間停止し、固体を沈降させた。液体をサイホンで吸い上げた。サイホンで吸い上げた後、新鮮なTiCl4およびMg/ジエーテルのモル比が26になるような量量の9,9−ビス(メトキシメチル)フルオレンを添加した。その後、温度を110℃まで上昇させ、撹拌しながら30分間保持した。次に反応器を75℃で冷却し、撹拌器を15分間停止した。沈殿させサイホンで吸い上げた後、新鮮なTiCl4を添加した。次に温度を90℃まで上昇させ、懸濁液を15分間撹拌した。次に温度を75℃まで低下させ、撹拌器を15分間停止した。沈殿させサイホンで吸い上げた後、固体を無水ヘキサンを用いて60℃で6回(6x1000ml)かつヘキサンを用いて25℃で1回洗浄した。固体をロータリーエバポレーターで乾燥させた。
重合反応器に導入する前に、前述の固体触媒成分を温度15℃でアルミニウムトリエチル(TEAL)およびジシクロペンチルジメトキシシラン(DCPMS)と接触させた。
次に、触媒系を液状プロピレン中に9分間の滞留時間にわたって浮遊状態に維持して20℃で予備重合処理に供してから重合反応器に導入した。
成分B)は、連続気相重合によって得た市販の異相ポリマーであり、ポリマーの特徴を表3に記録する。
Claims (8)
- A)90.0重量%〜99.0重量%のプロピレンホモポリマーであって:
(i)多分散指数が5〜10であり、
(ii)25℃でのキシレン可溶物が4.0重量%〜1.0重量%であり;
(iii)メルトフローレート(230℃/5kg、ISO1133)が0.2g/10分〜3.5g/10分である、プロピレンホモポリマーと;
B)1.0重量%〜10.0重量%のプロピレン;エチレン共重合体組成物であって:
b1)エチレン誘導単位の含有量が0.1重量%〜4.5重量%であり;25℃で測定したキシレン可溶物の含有量が10重量%よりも少なく;メルトフローレート(230℃/2.16kg、ISO1133)が50g/10分〜120g/10分である;14重量%〜52重量%のプロピレンホモポリマーまたはプロピレン/エチレン共重合体;
b2)エチレン誘導単位の含有量が20.0重量%〜55.0重量%である48重量%〜86重量%のプロピレンエチレン共重合体を含む、プロピレン、エチレン共重合体組成物とを含む、ポリオレフィン組成物であって;
前記仕上がったポリオレフィン組成物は、メルトフローレート(230℃/5kg、ISO1133)が0.2g/10分〜4.0g/10分であり;A+Bの合計量は100であり、b1+b2の合計量は100である、ポリオレフィン組成物。 - 成分A)は98.5〜95重量%であり、成分B)は1.5重量%〜5.0重量%である、請求項1に記載のポリオレフィン組成物。
- 成分B)のb1)は、22重量%〜38重量%であり、成分b2)は62重量%〜78重量%である、請求項1または2に記載のポリオレフィン組成物。
- 前記仕上がったポリオレフィン組成物は、メルトフローレート(230℃/5kg、ISO1133)が0.5g/10分〜2g/10分である、請求項1〜3のいずれか一項に記載のポリオレフィン組成物。
- 前記成分B)の成分b1)はプロピレンホモポリマーである、請求項1〜4のいずれか一項に記載のポリオレフィン組成物。
- 前記成分B)の成分b2)は、好ましくは、25℃でのキシレン可溶画分の固有粘度が1.5dl/g〜3.9dl/gのプロピレンエチレン共重合体である、請求項1〜5のいずれか一項に記載のポリオレフィン組成物。
- 請求項1〜5に記載のポリオレフィン組成物を含むパイプ。
- 下水管である、請求項7に記載のパイプ。