JP2015530485A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2015530485A5 JP2015530485A5 JP2015524434A JP2015524434A JP2015530485A5 JP 2015530485 A5 JP2015530485 A5 JP 2015530485A5 JP 2015524434 A JP2015524434 A JP 2015524434A JP 2015524434 A JP2015524434 A JP 2015524434A JP 2015530485 A5 JP2015530485 A5 JP 2015530485A5
- Authority
- JP
- Japan
- Prior art keywords
- weight percent
- fiber
- less
- modacrylic
- rayon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
表１
*縦／横
次に、本発明の態様を示す。
1. （ａ）３０重量パーセントを超えるアラミド繊維と、
（ｂ）２０〜３５重量パーセントのモダクリル繊維と、
（ｃ）２１以下の限界酸素指数を有し、且つ、デニール当り３グラム以上の乾燥引張り強度を有するレーヨン繊維２０〜３５重量パーセントと、
（ｄ）０〜３重量パーセントの帯電防止繊維と、
を含むアーク及び火炎防護布地に使用するための繊維のブレンドであって、前記パーセンテージは成分（ａ）、（ｂ）、（ｃ）、及び（ｄ）に基づき、前記ブレンドに存在する前記モダクリル繊維及び前記レーヨン繊維の量の違いが、１０重量パーセント以下である、繊維のブレンド。
2. 前記アラミド繊維が５９重量パーセント以下の量で存在する、上記１に記載のブレンド。
3. 前記アラミド繊維がメタ−アラミド繊維を含む、上記１に記載のブレンド。
4. 前記アラミド繊維が少なくとも２パーセントのパラ−アラミド繊維を含む、上記１に記載のブレンド。
5. （ａ）の前記アラミド繊維が、２〜２０重量パーセントのパラ−アラミド繊維及び１０〜５７重量パーセントのメタ−アラミド繊維として分配され、前記メタ−アラミドは、ポリ（メタフェニレンイソフタルアミド）であり、且つ、前記パラ−アラミドは、ポリ（パラフェニレンテレフタルアミド）である、上記１に記載のブレンド。
6. 前記レーヨン繊維の量が前記モダクリル繊維の量を超える、上記１に記載のブレンド。
7. 糸条の形態における上記１に記載のブレンド。
8. （ａ）３０重量パーセントを超えるアラミド繊維と、
（ｂ）２０〜３５重量パーセントのモダクリル繊維と、
（ｃ）２１以下の限界酸素指数を有し、且つ、デニール当り３グラム以上の乾燥引張り強度を有するレーヨン繊維２０〜３５重量パーセントと、
（ｄ）０〜３重量パーセントの帯電防止繊維と、
を含む糸条を含むアーク及び火炎防護に使用するのに適する布地であって、前記パーセンテージは成分（ａ）、（ｂ）、（ｃ）、及び（ｄ）に基づき、前記糸条に存在する前記モダクリル繊維及び前記レーヨン繊維の量の違いは、１０重量パーセント以下であり、且つ、
前記布地は、１３５〜４０７グラム毎平方メートル（４〜１２オンス毎平方ヤード）の範囲における坪量を有する、布地。
9. アラミド繊維が５９重量パーセント以下の量で前記糸条に存在する、上記８に記載の布地。
10. 前記アラミド繊維がメタ−アラミド繊維を含む、上記９に記載の布地。
11. 前記アラミド繊維が少なくとも２パーセントのパラ−アラミド繊維を含む、上記８に記載の布地。
12. （ａ）の前記アラミド繊維が２〜２０重量パーセントのパラ−アラミド繊維及び１０〜５７重量パーセントのメタ−アラミド繊維として分配され、前記メタ−アラミドは、ポリ（メタフェニレンイソフタルアミド）であり、且つ、前記パラ−アラミドは、ポリ（パラフェニレンテレフタルアミド）である、上記８に記載の布地。
13. 前記レーヨン繊維の量が前記モダクリル繊維の量を超える、上記８に記載のブレンド。
14. ＡＳＴＭ Ｄ−６４１３−０８による４インチ未満の炭化長を有する、上記８に記載の布地。
15. ＡＳＴＭ Ｆ−１９５９−０６による布地の１．２カロリー毎平方センチメートル毎オンス毎平方ヤードを超える耐アーク性を有する、上記８に記載の布地。
16. （ａ）３０重量パーセントを超えるアラミド繊維と、
（ｂ）２０〜３５重量パーセントのモダクリル繊維と、
（ｃ）２１以下の限界酸素指数を有し、且つ、デニール当り３グラム以上の乾燥引張り強度を有するレーヨン繊維２０〜３５重量パーセントと、
（ｄ）０〜３重量パーセントの帯電防止繊維と、
を含む布地を含むアーク及び火炎防護に使用するのに適する衣類であって、前記パーセンテージは成分（ａ）、（ｂ）、（ｃ）、及び（ｄ）に基づき、前記布地に存在する前記モダクリル繊維及び前記レーヨン繊維の量の違いは、１０重量パーセント以下であり、且つ、
前記布地は、１５０〜２９０グラム毎平方メートル（４．５〜８．５オンス毎平方ヤード）の範囲における坪量を有する、衣類。
17. 前記アラミド繊維が５９重量パーセント以下の量で前記布地に存在する、上記１６に記載の衣類。
18. 前記アラミド繊維がメタ−アラミド繊維を含む、上記１６に記載の衣類。
19. 前記アラミド繊維が少なくとも２パーセントのパラ−アラミド繊維を含む、上記１６に記載の衣類。
20. （ａ）の前記アラミド繊維が、２〜２０重量パーセントのパラ−アラミド繊維及び１０〜５７重量パーセントのメタ−アラミド繊維として分配され、前記メタ−アラミドは、ポリ（メタフェニレンイソフタルアミド）であり、且つ、前記パラ−アラミドは、ポリ（パラフェニレンテレフタルアミド）である、上記１６に記載の衣類。
21. ＡＳＴＭ Ｆ１９５９及びＮＦＰＡ ７０Ｅによるカテゴリー２のアーク等級を維持しながら、ＡＳＴＭ Ｆ１９３０による４秒の火災への曝露において体の火傷が６５％未満に等しい熱防護性を提供する、上記１６に記載の衣類。
22. 前記布地は、ＡＳＴＭ Ｆ−１９５９−０６による布地の１．２カロリー毎平方センチメートル毎オンス毎平方ヤードを超える耐アーク性を有する、上記１６に記載の衣類。
*縦／横
次に、本発明の態様を示す。
1. （ａ）３０重量パーセントを超えるアラミド繊維と、
（ｂ）２０〜３５重量パーセントのモダクリル繊維と、
（ｃ）２１以下の限界酸素指数を有し、且つ、デニール当り３グラム以上の乾燥引張り強度を有するレーヨン繊維２０〜３５重量パーセントと、
（ｄ）０〜３重量パーセントの帯電防止繊維と、
を含むアーク及び火炎防護布地に使用するための繊維のブレンドであって、前記パーセンテージは成分（ａ）、（ｂ）、（ｃ）、及び（ｄ）に基づき、前記ブレンドに存在する前記モダクリル繊維及び前記レーヨン繊維の量の違いが、１０重量パーセント以下である、繊維のブレンド。
2. 前記アラミド繊維が５９重量パーセント以下の量で存在する、上記１に記載のブレンド。
3. 前記アラミド繊維がメタ−アラミド繊維を含む、上記１に記載のブレンド。
4. 前記アラミド繊維が少なくとも２パーセントのパラ−アラミド繊維を含む、上記１に記載のブレンド。
5. （ａ）の前記アラミド繊維が、２〜２０重量パーセントのパラ−アラミド繊維及び１０〜５７重量パーセントのメタ−アラミド繊維として分配され、前記メタ−アラミドは、ポリ（メタフェニレンイソフタルアミド）であり、且つ、前記パラ−アラミドは、ポリ（パラフェニレンテレフタルアミド）である、上記１に記載のブレンド。
6. 前記レーヨン繊維の量が前記モダクリル繊維の量を超える、上記１に記載のブレンド。
7. 糸条の形態における上記１に記載のブレンド。
8. （ａ）３０重量パーセントを超えるアラミド繊維と、
（ｂ）２０〜３５重量パーセントのモダクリル繊維と、
（ｃ）２１以下の限界酸素指数を有し、且つ、デニール当り３グラム以上の乾燥引張り強度を有するレーヨン繊維２０〜３５重量パーセントと、
（ｄ）０〜３重量パーセントの帯電防止繊維と、
を含む糸条を含むアーク及び火炎防護に使用するのに適する布地であって、前記パーセンテージは成分（ａ）、（ｂ）、（ｃ）、及び（ｄ）に基づき、前記糸条に存在する前記モダクリル繊維及び前記レーヨン繊維の量の違いは、１０重量パーセント以下であり、且つ、
前記布地は、１３５〜４０７グラム毎平方メートル（４〜１２オンス毎平方ヤード）の範囲における坪量を有する、布地。
9. アラミド繊維が５９重量パーセント以下の量で前記糸条に存在する、上記８に記載の布地。
10. 前記アラミド繊維がメタ−アラミド繊維を含む、上記９に記載の布地。
11. 前記アラミド繊維が少なくとも２パーセントのパラ−アラミド繊維を含む、上記８に記載の布地。
12. （ａ）の前記アラミド繊維が２〜２０重量パーセントのパラ−アラミド繊維及び１０〜５７重量パーセントのメタ−アラミド繊維として分配され、前記メタ−アラミドは、ポリ（メタフェニレンイソフタルアミド）であり、且つ、前記パラ−アラミドは、ポリ（パラフェニレンテレフタルアミド）である、上記８に記載の布地。
13. 前記レーヨン繊維の量が前記モダクリル繊維の量を超える、上記８に記載のブレンド。
14. ＡＳＴＭ Ｄ−６４１３−０８による４インチ未満の炭化長を有する、上記８に記載の布地。
15. ＡＳＴＭ Ｆ−１９５９−０６による布地の１．２カロリー毎平方センチメートル毎オンス毎平方ヤードを超える耐アーク性を有する、上記８に記載の布地。
16. （ａ）３０重量パーセントを超えるアラミド繊維と、
（ｂ）２０〜３５重量パーセントのモダクリル繊維と、
（ｃ）２１以下の限界酸素指数を有し、且つ、デニール当り３グラム以上の乾燥引張り強度を有するレーヨン繊維２０〜３５重量パーセントと、
（ｄ）０〜３重量パーセントの帯電防止繊維と、
を含む布地を含むアーク及び火炎防護に使用するのに適する衣類であって、前記パーセンテージは成分（ａ）、（ｂ）、（ｃ）、及び（ｄ）に基づき、前記布地に存在する前記モダクリル繊維及び前記レーヨン繊維の量の違いは、１０重量パーセント以下であり、且つ、
前記布地は、１５０〜２９０グラム毎平方メートル（４．５〜８．５オンス毎平方ヤード）の範囲における坪量を有する、衣類。
17. 前記アラミド繊維が５９重量パーセント以下の量で前記布地に存在する、上記１６に記載の衣類。
18. 前記アラミド繊維がメタ−アラミド繊維を含む、上記１６に記載の衣類。
19. 前記アラミド繊維が少なくとも２パーセントのパラ−アラミド繊維を含む、上記１６に記載の衣類。
20. （ａ）の前記アラミド繊維が、２〜２０重量パーセントのパラ−アラミド繊維及び１０〜５７重量パーセントのメタ−アラミド繊維として分配され、前記メタ−アラミドは、ポリ（メタフェニレンイソフタルアミド）であり、且つ、前記パラ−アラミドは、ポリ（パラフェニレンテレフタルアミド）である、上記１６に記載の衣類。
21. ＡＳＴＭ Ｆ１９５９及びＮＦＰＡ ７０Ｅによるカテゴリー２のアーク等級を維持しながら、ＡＳＴＭ Ｆ１９３０による４秒の火災への曝露において体の火傷が６５％未満に等しい熱防護性を提供する、上記１６に記載の衣類。
22. 前記布地は、ＡＳＴＭ Ｆ−１９５９−０６による布地の１．２カロリー毎平方センチメートル毎オンス毎平方ヤードを超える耐アーク性を有する、上記１６に記載の衣類。
Claims (3)
- （ａ）３０重量パーセントを超えるアラミド繊維と、
（ｂ）２０〜３５重量パーセントのモダクリル繊維と、
（ｃ）２１以下の限界酸素指数を有し、且つ、デニール当り３グラム以上の乾燥引張り強度を有するレーヨン繊維２０〜３５重量パーセントと、
（ｄ）０〜３重量パーセントの帯電防止繊維と、
を含むアーク及び火炎防護布地に使用するための繊維のブレンドであって、前記パーセンテージは成分（ａ）、（ｂ）、（ｃ）、及び（ｄ）に基づき、前記ブレンドに存在する前記モダクリル繊維及び前記レーヨン繊維の量の違いが、１０重量パーセント以下である、繊維のブレンド。 - （ａ）３０重量パーセントを超えるアラミド繊維と、
（ｂ）２０〜３５重量パーセントのモダクリル繊維と、
（ｃ）２１以下の限界酸素指数を有し、且つ、デニール当り３グラム以上の乾燥引張り強度を有するレーヨン繊維２０〜３５重量パーセントと、
（ｄ）０〜３重量パーセントの帯電防止繊維と、
を含む糸条を含むアーク及び火炎防護に使用するのに適する布地であって、前記パーセンテージは成分（ａ）、（ｂ）、（ｃ）、及び（ｄ）に基づき、前記糸条に存在する前記モダクリル繊維及び前記レーヨン繊維の量の違いは、１０重量パーセント以下であり、且つ、
前記布地は、１３５〜４０７グラム毎平方メートル（４〜１２オンス毎平方ヤード）の範囲における坪量を有する、布地。 - （ａ）３０重量パーセントを超えるアラミド繊維と、
（ｂ）２０〜３５重量パーセントのモダクリル繊維と、
（ｃ）２１以下の限界酸素指数を有し、且つ、デニール当り３グラム以上の乾燥引張り強度を有するレーヨン繊維２０〜３５重量パーセントと、
（ｄ）０〜３重量パーセントの帯電防止繊維と、
を含む布地を含むアーク及び火炎防護に使用するのに適する衣類であって、前記パーセンテージは成分（ａ）、（ｂ）、（ｃ）、及び（ｄ）に基づき、前記布地に存在する前記モダクリル繊維及び前記レーヨン繊維の量の違いは、１０重量パーセント以下であり、且つ、
前記布地は、１５０〜２９０グラム毎平方メートル（４．５〜８．５オンス毎平方ヤード）の範囲における坪量を有する、衣類。