JP2015066135A

JP2015066135A - Wiper package

Info

Publication number: JP2015066135A
Application number: JP2013202585A
Authority: JP
Inventors: 拓郎安藤; Takuro Ando
Original assignee: Nippon Paper Crecia Co Ltd
Current assignee: Nippon Paper Crecia Co Ltd
Priority date: 2013-09-27
Filing date: 2013-09-27
Publication date: 2015-04-13
Anticipated expiration: 2033-09-27
Also published as: JP5598881B1

Abstract

PROBLEM TO BE SOLVED: To provide a wiper and a wiper package having high productivity when folding processing a colored wiper, using a folding machine having a rotary cylinder type inter holder.SOLUTION: A wiper is formed from a nonwoven fabric. The wiper is applied with coloring, and has a basis weight of 35 g/mor more and 65 g/mor less, and MD direction bending resistance in compliance with a 45° cantilever method, having 5.0 cm or more and 11.5 cm or less. A wiper package is provided by alternately overlapping the wipers followed by folding and laminating in a pop-up type, and storing them in a storage box having a take-out port on the upper surface part.

Description

本発明は、ワイパー及びワイパー包装体に関する。 The present invention relates to a wiper and a wiper package.

医療現場、実験室、精密部品工場、食品加工場といった様々な場所で、機材・備品の拭き取りや現場の清掃に、低発塵性及び吸液性に優れるワイパーが用いられている。ワイパーの基材としては、様々なものが使用されているが、風合いや拭き取り性に優れることから、パルプ繊維等の天然繊維から形成される紙製のシートやパルプ繊維等の天然繊維あるいはポリプロピレン等の合成繊維の混抄から形成される不織布シートが重用されている。 In various places such as medical sites, laboratories, precision parts factories, and food processing plants, wipers with excellent dust generation and liquid absorption are used for wiping off equipment and equipment and cleaning the site. A variety of wiper base materials are used, but because of excellent texture and wiping properties, paper sheets formed from natural fibers such as pulp fibers, natural fibers such as pulp fibers, polypropylene, etc. A nonwoven fabric sheet formed from a blend of synthetic fibers is heavily used.

これらのシートから製造される市販用ワイパーの製品形態としては、通常、シートを数回折り畳んで積層し、上面に取出部を有する収納箱に収納し、使用時に取出部から一枚を取り出すと、次の一枚の一部が取出部の外に露出する、いわゆるポップアップタイプや、シートを４つ折りにして束状に包装する４つ折りタイプや、シートをロール状に巻取ったロールタイプ等がある（特許文献１〜３参照）。ポップアップタイプの製品を製造する加工装置としては、ロータリーシリンダー式やマルチスタンド式の各種インターホルダーが知られているが、特に、ロータリーシリンダー式インターホルダーと呼ばれる折り畳み装置では、２つの原反ロールから切り出したシートを互い違いに連続的に折り畳みながら積層し、幅方向での所定の間隔での切断を経ることでワイパー積層体を形成することができる。このワイパー積層体を上部に取出口を有する収納箱内に収納することにより、ポップアップタイプを製造することができ、既存の技術として一般的に広く知られている。 As a product form of a commercially available wiper manufactured from these sheets, the sheets are usually folded several times and stacked, stored in a storage box having an extraction part on the upper surface, and when one piece is taken out from the extraction part at the time of use, There is a so-called pop-up type in which a part of the next sheet is exposed outside the take-out part, a four-fold type in which the sheet is folded in four and wrapped in a bundle, a roll type in which the sheet is wound into a roll, etc. (See Patent Documents 1 to 3). Various rotary cylinder and multi-stand type inter-holders are known as processing equipment for manufacturing pop-up type products. In particular, folding devices called rotary cylinder-type inter-holders are cut out from two raw rolls. The sheets can be laminated while being alternately folded, and a wiper laminate can be formed by cutting at predetermined intervals in the width direction. A pop-up type can be manufactured by storing this wiper laminate in a storage box having an outlet at the top, and is generally widely known as an existing technique.

このロータリーシリンダー式インターホルダーは、マルチスタンド式インターホルダーと比較して、加工速度は遅いものの、比較的小型で、原反ロールの切り替えが容易であり、また、シートの折り品質が良いことから、紙や不織布などの多様な基材を加工対象とすることができ、ポップアップタイプの小ロット製造に用いられている。 Although this rotary cylinder type inter-holder is slower in processing speed than the multi-stand type inter-holder, it is relatively small and easy to switch between the raw rolls, and the sheet folding quality is good. Various base materials such as paper and non-woven fabric can be processed, and are used for manufacturing pop-up type small lots.

ここで、インターホルダーの一例として、ロータリーシリンダー式インターホルダーによるワイパー積層体及びワイパー包装体の製造方法について、説明する。 Here, as an example of an inter holder, a method for manufacturing a wiper laminate and a wiper package using a rotary cylinder inter holder will be described.

図２（ａ）及び（ｂ）は、ロータリーシリンダー式インターホルダーを備える折り機１００の説明図である。折機１００は、原反ロールＲ及びＬと、原反ロールＲ及びＬから繰り出された原反ウエブ５にナーリング加工やエンボス加工を施すフェルトロール３１と、シート７を通過させるフィードロール３２と、シート７を折り畳みながら積層するフォールディング部６０と、を備えている。 FIGS. 2A and 2B are explanatory views of the folding machine 100 including a rotary cylinder type inter-holder. The folding machine 100 includes an original roll R and L, a felt roll 31 for knurling and embossing the original web 5 fed from the original roll R and L, a feed roll 32 for passing the sheet 7, And a folding unit 60 that stacks the sheets 7 while being folded.

フォールディング部６０は、対向配置された１対のフォールディング（折り）ロール６１と、フォールディングロール６１の上方にシート７を進行方向に一定間隔でカットするためのナイフ受け６２と、左右１対のフォールディングバー６１ｅと、フォールディングロール６１の下方に落下しつつ折り畳み積層されるワイパー積層体９を取り出す積層体取出し装置９１と、を備える。 The folding unit 60 includes a pair of folding rolls 61 arranged opposite to each other, a knife receiver 62 for cutting the sheet 7 at regular intervals in the traveling direction above the folding roll 61, and a pair of left and right folding bars. 61e, and a laminate take-out device 91 that takes out the wiper laminate 9 that is folded and laminated while falling below the folding roll 61.

図２（ｂ）は（ａ）で示す状態からフォールディングロール６１が矢印の方向に１２０度回転した状態を示す図である。 FIG. 2B is a diagram showing a state in which the folding roll 61 is rotated 120 degrees in the direction of the arrow from the state shown in FIG.

図２（ａ）及び（ｂ）に示すように、フォールディングロール６１は、周方向に３等分した位置にバキュームゾーン６１ａを有し、シート７を吸引保持できるようになっている。また、フォールディングロール６１の周方向に沿って３等分した位置に溝６１ｃが形成され、溝６１ｃ内にはシート７の折り部を掴む鉤爪状のジョー６１ｂが配置され、ジョー６１ｂと相対する位置にナイフ６１ｄが配置されている。ジョー６１ｂは溝６１ｃ内で周方向に回動し、溝６１ｃの側壁に接した際に側壁との間に製品シート７ａ、７ｂの折り部を挟持するようになっている。さらに、各フォールディングロール６１の下方には、ジョー６１ｂによって折り畳まれた積層体を各フォールディングロール６１から剥離する左右一対のフォールディングバー６１ｅが配置されている。 As shown in FIGS. 2A and 2B, the folding roll 61 has a vacuum zone 61a at a position equally divided into three in the circumferential direction so that the sheet 7 can be sucked and held. Further, a groove 61c is formed at a position equally divided into three along the circumferential direction of the folding roll 61. A claw-like jaw 61b for gripping a folded portion of the sheet 7 is disposed in the groove 61c, and a position facing the jaw 61b. A knife 61d is disposed on the surface. The jaw 61b rotates in the circumferential direction within the groove 61c, and when the jaw 61b comes into contact with the side wall of the groove 61c, the folded portions of the product sheets 7a and 7b are sandwiched between the jaw 61b. Further, a pair of left and right folding bars 61e for peeling the laminated body folded by the jaws 61b from each folding roll 61 is disposed below each folding roll 61.

そして、フォールディング部６０に導入されたシート７は、ナイフ６１ｄとナイフ受け６２の接触によりシートの進行方向に一定間隔でカットされたのち、バキュームゾーン６１ａで吸引保持されつつ左右のフォールディングロール６１の間に移動する。そして、例えば左側のフォールディングロール６１のジョー６１ｂにより保持された製品シート７ｂが、右側のフォールディングロール６１のナイフ６１ｄに対向したとき、右側のフォールディングロール６１に保持された製品シート７ａの端部と、製品シート７ｂの折り返し部とを同時に挟持する。さらに各フォールディングロール６１が回転してフォールディングバー６１ｅに差し掛かると、フォールディングバー６１ｅが上下運動により溝６１ｃに入ってジョー６１ｂを開放しつつ、製品シート７ａ、７ｂの折り部を下方に押出し、折り畳まれたワイパー積層体９を順次形成する。折り畳まれたワイパー積層体９が所定の組数になると、積層体取出し装置９１によって取り出される。 The sheet 7 introduced into the folding unit 60 is cut at regular intervals in the sheet traveling direction by contact between the knife 61d and the knife receiver 62, and is then sucked and held between the left and right folding rolls 61 while being held in the vacuum zone 61a. Move to. For example, when the product sheet 7b held by the jaw 61b of the left folding roll 61 faces the knife 61d of the right folding roll 61, the end of the product sheet 7a held by the right folding roll 61; The folded part of the product sheet 7b is held at the same time. Further, when each folding roll 61 rotates and reaches the folding bar 61e, the folding bar 61e is moved up and down to enter the groove 61c to release the jaw 61b, and the product sheet 7a, 7b is pushed down and folded. The wiper laminates 9 thus formed are sequentially formed. When the number of folded wiper laminates 9 reaches a predetermined number, the laminate take-out device 91 takes them out.

図３（ａ）ないし（ｅ）は、フォールディング部６０の拡大図である。ロータリーシリンダー式インターホルダーによるワイパー積層体９の折り畳み方法について、さらに説明する。まず、左側のフォールディングロール６１には、製品シート７ａの折り部が鉤爪状のジョー６１ｂによって掴まれており、右側のフォールディングロール６１には、バキュームゾーン６１ａで吸引保持された製品シート７ｂが保持されている（図３（ａ））。左側のフォールディングバー６１ｅ（図示せず）がジョー６１ｂを開放し、製品シート７ａは、製品シート７ｂを巻き込みながら製品シート７ａの折り部を下方に押出し、折れ７１が入る（図３（ｂ））。右側のフォールディングバー６１ｅ（図示せず）がジョー６１ｂを開放し、製品シート７ｂは、製品シート７ｃを巻き込みながら製品シート７ｂの折り部を下方に押出し、折れ７１が入る（図３（ｃ））。同様に、製品シート７ｃは製品シート７ｄを巻き込みながら折れ７１が入り（図３（ｄ））、製品シート７ｄは製品シート７ｅを巻き込みながら折れ７１が入る（図３（ｅ））。この繰り返しにより、ワイパー積層体９は形成されていく。 3A to 3E are enlarged views of the folding unit 60. FIG. A method for folding the wiper laminate 9 using the rotary cylinder type inter-holder will be further described. First, the folded portion of the product sheet 7a is gripped by the claw-shaped jaw 61b on the left folding roll 61, and the product sheet 7b sucked and held in the vacuum zone 61a is held on the right folding roll 61. (FIG. 3A). The left folding bar 61e (not shown) opens the jaw 61b, and the product sheet 7a pushes the folded portion of the product sheet 7a downward while winding the product sheet 7b, so that the fold 71 enters (FIG. 3 (b)). . The right folding bar 61e (not shown) opens the jaw 61b, and the product sheet 7b pushes the folded portion of the product sheet 7b downward while winding the product sheet 7c, so that the fold 71 enters (FIG. 3 (c)). . Similarly, the product sheet 7c is folded 71 while winding the product sheet 7d (FIG. 3 (d)), and the product sheet 7d is folded 71 while winding the product sheet 7e (FIG. 3 (e)). By repeating this, the wiper laminate 9 is formed.

ロータリーシリンダー式インターホルダーで折り畳む場合、その折り畳み方向は、原反ウエブ５の繊維方向（ＭＤ方向）５１に対して直角方向であるため、硬いシートは折り畳みにくく、良好な折り畳み性能を得るにはシートに適当な柔らかさが要求される。 When folding with a rotary cylinder type inter-holder, the folding direction is a direction perpendicular to the fiber direction (MD direction) 51 of the original web 5, so that a hard sheet is difficult to fold, and a sheet for obtaining good folding performance. Is required to have a suitable softness.

なお、フォールディング部６０により製造されるワイパー積層体９は、原反ロールＲ及びＬの進行方向に対してナイフ６１ｄとナイフ受け６２でワイパーの製品長にカットされた後、最終的な組数（例えば１００組）の積層体になり、このワイパー積層体９を、図示しないカッターでワイパーの製品幅（折り畳み線と垂直な方向）にカットした後、収納箱に箱詰めしてワイパー包装体となる。 In addition, the wiper laminated body 9 manufactured by the folding unit 60 is cut into the product length of the wiper with the knife 61d and the knife receiver 62 in the traveling direction of the raw rolls R and L, and then the final number of sets ( For example, the wiper laminate 9 is cut into the product width of the wiper (direction perpendicular to the folding line) with a cutter (not shown), and then packed in a storage box to form a wiper package.

ところで、食品加工場、給食センター、飲食店といった食品関係の現場では、清掃用として不織布ワイパーが使用されているが、ワイパーに付着した塵や埃、糸屑等が目視しやすく、また、ワイパーの食品への混入を発見しやすいように、着色したワイパーを使用することが多い。そして、このようなワイパーで汚れのふき取りや消毒をする際には、水やアルコール等を含有する洗浄液にワイパーを浸してから使用している場合が少なくない。 By the way, non-woven wipers are used for cleaning at food-related sites such as food processing plants, lunch centers, restaurants, etc., but dust, dust, lint, etc. adhering to the wipers are easy to see. Often colored wipes are used to help detect food contamination. When wiping or disinfecting dirt with such a wiper, the wiper is often used after being immersed in a cleaning solution containing water, alcohol, or the like.

このような水やアルコール等に浸しても色落ちしにくいワイパーを製造するには、色落ち防止用として、一定量のアクリル系バインダー等の各種バインダーを添加する必要がある。 In order to produce a wiper that does not easily lose its color even when immersed in water, alcohol, or the like, it is necessary to add a certain amount of various binders such as an acrylic binder to prevent discoloration.

特開２０１０−２０９４８２号公報JP 2010-209482 A 特開２００８−１２７６８８号公報JP 2008-127688 A 特開２００５−２４５７５２号公報JP 2005-245752 A

しかしながら、このバインダーの添加により作成した不織布のシートは、一般的にシートが硬化することが知られている。特に、前述のロータリーシリンダー式インターホルダーによりワイパー積層体９を製造する工程では、シート７が硬い場合、シート７を湾曲したフォールディングロール６１表面を添うように通紙・保持しにくく、結果、以降の工程でシート皺発生の原因となる。図４（ａ）に示すように、ワイパー積層体９は、折れ７１がきちんと入ることで、シートが反れることなく、整然と積層され、収納箱２０に正しく収納したものとなるが、シート７が硬くなると、ジョー６１ｂがシート７を挟持しにくくなるとともに、折り部での折り目付けが不十分になるために、ジョー６１ｂが製品シート７ａないし７ｅを開放するときに、開放直後に折り部でのシートの反発力を招き、結果、収納箱２０に収納できたとしても、整然としたワイパー積層体９が得られなくなる（図４（ｂ）参照）。このようにシートが硬くなると、ワイパー積層体９の製造に不具合が生じやすく、生産性が低いという問題があった。 However, it is known that a sheet of a nonwoven fabric prepared by adding this binder is generally cured. In particular, in the process of manufacturing the wiper laminate 9 by the above-described rotary cylinder type inter-holder, when the sheet 7 is hard, it is difficult to pass and hold the sheet 7 so as to follow the curved folding roll 61 surface. It may cause sheet flaws in the process. As shown in FIG. 4 (a), the wiper laminate 9 is configured such that the sheets 71 are neatly stacked and properly stored in the storage box 20 when the folds 71 are properly inserted. If it becomes hard, the jaw 61b becomes difficult to pinch the sheet 7 and the crease at the folding portion becomes insufficient. Therefore, when the jaw 61b opens the product sheets 7a to 7e, Even if the sheet is repelled and can be stored in the storage box 20, an orderly wiper laminate 9 cannot be obtained (see FIG. 4B). When the sheet becomes hard in this way, there is a problem in that the production of the wiper laminate 9 is liable to occur and the productivity is low.

そこで、本発明はこのような課題に鑑みてなされたものであり、その目的は生産性の高いワイパー及びワイパー包装体を提供することにある。 Then, this invention is made | formed in view of such a subject, The objective is to provide the wiper and wiper package which have high productivity.

上記課題を解決するために、本発明は、以下の構成によって把握される。
（１）本発明のワイパーは、不織布から形成されるワイパーであって、前記ワイパーは、着色が施され、３５ｇ／ｍ^２以上６５ｇ／ｍ^２以下の坪量と、５．０ｃｍ以上１１．５ｃｍ以下の４５°カンチレバー法に準拠したＭＤ方向の剛軟度とを有することを特徴とする。 In order to solve the above problems, the present invention is grasped by the following configuration.
(1) The wiper of the present invention is a wiper formed from a nonwoven fabric, and the wiper is colored, and has a basis weight of 35 g / m ² or more and 65 g / m ² or less, and 5.0 cm or more and 11.5 cm. It has a bending resistance in the MD direction based on the following 45 ° cantilever method.

（２）本発明のワイパーは、（１）の構成において、前記ワイパーが０.２３ｍｍ以上０．７０ｍｍ以下の厚さを有することを特徴とする。 (2) The wiper of the present invention is characterized in that, in the configuration of (1), the wiper has a thickness of 0.23 mm to 0.70 mm.

（３）本発明のワイパーは、（１）または（２）の構成において、前記ワイパーが０．０５重量％以上０．５０重量％以下のバインダーを含有することを特徴とする。 (3) The wiper of the present invention is characterized in that, in the constitution of (1) or (2), the wiper contains 0.05% by weight or more and 0.50% by weight or less of a binder.

（４）本発明のワイパーは、（１）ないし（３）のいずれかの構成において、ロータリーシリンダー式インターホルダーを用いて折り畳まれることを特徴とする。 (4) The wiper of the present invention is characterized by being folded using a rotary cylinder type inter-holder in any one of the constitutions (1) to (3).

（５）本発明のワイパー包装体は、（４）の構成のワイパーが、交互に重ねられてポップアップ式に折り畳まれて積層され、上部に取出口を有する収納箱に収納されていることを特徴とする。 (5) The wiper package of the present invention is characterized in that the wipers having the configuration of (4) are alternately stacked, folded in a pop-up manner and stacked, and stored in a storage box having an outlet at the top. And

本発明のワイパー及びワイパー包装体によれば、上記の様な構成にすることにより、生産性を向上させるという効果が生じる。 According to the wiper and wiper package of the present invention, the above-described configuration produces an effect of improving productivity.

本発明に係るワイパー包装体の外観を示す斜視図。The perspective view which shows the external appearance of the wiper package which concerns on this invention. （ａ）及び（ｂ）は、ロータリーシリンダー式インターホルダーを備える折機の説明図。(A) And (b) is explanatory drawing of a folding machine provided with a rotary cylinder type inter holder. （ａ）ないし（ｅ）は、フォールディング部の拡大図。(A) thru | or (e) are the enlarged views of a folding part. 本発明に係るワイパーを積層したワイパー積層体の断面図。Sectional drawing of the wiper laminated body which laminated | stacked the wiper which concerns on this invention.

以下、添付図面を参照して、本発明を実施するための形態（以下、実施形態）について詳細に説明する。なお、実施形態の説明の全体を通して同じ要素には同じ番号を付している。 DESCRIPTION OF EMBODIMENTS Hereinafter, embodiments for carrying out the present invention (hereinafter referred to as embodiments) will be described in detail with reference to the accompanying drawings. Note that the same number is assigned to the same element throughout the description of the embodiment.

本実施形態の一例として、ワイパーを収納するワイパー包装体について説明する。図１は、本発明に係るワイパー包装体の外観を示す斜視図である。ワイパー包装体１は、ワイパー３が積層されたワイパー積層体（図示せず）と、ワイパー包装体１表面のほぼ中央部の長手方向に、取出口２１を有する略直方体形状の収納箱２０で構成されている。ワイパー包装体１を使用する際は、取出口２１から収納箱２０内に指を挿入して、最上部にあるワイパー３を摘み、外部に引き出すこととなる。なお、ロータリーシリンダー式インターホルダーによる折り畳みの場合には、ワイパーの取出し方向は、引張強度の高いワイパーの縦方向（ＭＤ方向）にあたる。 As an example of this embodiment, a wiper package that houses a wiper will be described. FIG. 1 is a perspective view showing an appearance of a wiper package according to the present invention. The wiper package 1 includes a wiper stack (not shown) in which the wipers 3 are stacked, and a substantially rectangular parallelepiped storage box 20 having an outlet 21 in the longitudinal direction of the substantially central portion of the surface of the wiper package 1. Has been. When the wiper package 1 is used, a finger is inserted into the storage box 20 from the outlet 21, and the wiper 3 at the top is picked and pulled out. In addition, in the case of folding with a rotary cylinder type inter-holder, the removal direction of the wiper corresponds to the longitudinal direction (MD direction) of the wiper having a high tensile strength.

ワイパーの基材である不織布については特に限定されず、例えば、レーヨン繊維、ポリエステル繊維、ポリプロピレン繊維、ポリアミド繊維、ポリエチレン繊維、アクリル繊維、綿、ウール等を積層し、一体化したものがあげられる。一体化方法としては、ウォータージェットやニードルパンチを用いる方法等、ワイパーとして使用する際に糸屑等が発生しない程度の強度を保持できる方法であれば限定されない。 The nonwoven fabric that is the base material of the wiper is not particularly limited, and examples thereof include those obtained by laminating and integrating rayon fibers, polyester fibers, polypropylene fibers, polyamide fibers, polyethylene fibers, acrylic fibers, cotton, wool, and the like. The integration method is not limited as long as it is a method that can maintain a strength that does not cause lint or the like when used as a wiper, such as a method using a water jet or a needle punch.

ワイパーを着色する着色剤としては、特に限定されず、一般に繊維・紙の着色に用いられる直接染料、カチオン染料、塩基性染料、酸性染料等の染料、天然色素、食用色素、染料ベースもしくは顔料ベースのインキ等をあげることができる。これらの中でも、染着性及び耐候性の観点からは、直接染料、カチオン染料及び顔料ベースのインキが好ましい。色は、赤・青・黄・等特に限定されず、その配合量は色落ちを起こさない程度であれば適宜適当量決めることができる。 The colorant for coloring the wiper is not particularly limited, and is generally a direct dye, a cationic dye, a basic dye, an acid dye or the like, which is used for coloring fibers and paper, a natural dye, a food dye, a dye base or a pigment base. Can be used. Among these, direct dyes, cationic dyes, and pigment-based inks are preferable from the viewpoints of dyeability and weather resistance. The color is not particularly limited, such as red, blue, yellow, and the like, and the blending amount can be appropriately determined as long as it does not cause discoloration.

着色剤によるワイパーの着色方法は、公知の着色方法を採ることができる。着色面は、ワイパーの片面でも両面でも特に限定はないが、毛羽を抑制する観点から、両面を着色することが好ましい。 As a method for coloring the wiper with the colorant, a known coloring method can be adopted. The coloring surface is not particularly limited on one side or both sides of the wiper, but it is preferable to color both sides from the viewpoint of suppressing fluff.

直接染料としては、例えば、アニオン性直接染料、カチオン性直接染料等があげられる。なかでも、ワイパーの基材に対する染着性、着色コスト及び色落ちを抑制する効果が大きいことから、アニオン性直接染料がより好ましい。原料中に染料を配合する場合、カチオン性柔軟剤（必要ならばカチオン性紙力剤）を原料パルプに添加してから、アニオン性染料を添加すると、柔らかな風合いを持たせることができるため好ましい。 Examples of direct dyes include anionic direct dyes and cationic direct dyes. Among these, an anionic direct dye is more preferable because it has a great effect of suppressing the dyeing property of the wiper to the base material, the coloring cost, and the color fading. When a dye is blended in the raw material, it is preferable to add an anionic dye after adding a cationic softening agent (a cationic paper strength agent if necessary) to the raw material pulp, because it can give a soft texture. .

カチオン染料は、第四アンモニウム化合物型のカチオンとしてパルプ中の酸性基と結合して染着するものであり、例えば、ポリメチン系、アゾ系、アザメチン系、アントラキノン系をあげることができる。 The cationic dye is dyed by binding to an acidic group in pulp as a quaternary ammonium compound type cation, and examples thereof include polymethine series, azo series, azamethine series, and anthraquinone series.

顔料ベースのインキとしては、例えば、無機顔料、有機顔料及びレーキ顔料のインキをあげることができる。ワイパーの基材への定着性の観点から、無機顔料のインキを用いることが好ましい。 Examples of pigment-based inks include inorganic pigments, organic pigments, and lake pigment inks. From the viewpoint of fixability of the wiper to the substrate, it is preferable to use an ink of an inorganic pigment.

バインダーは、着色剤により染色したワイパーに対して、水やアルコール等による色落ちを防止するものであれば特に限定はなく、例えば、アクリル系、酢酸ビニル系、合成ゴム系のバインダーがあげられる。バインダー量とは、原反に対する重量割合を示すもので、０．０１％以上０．５０％以下であり、０．０５％以上０．４０％以下が好ましい。０．０１％未満であると色落ちが発生することが多く、逆に０．５０％を超えるとワイパーの吸収性が低下する。 The binder is not particularly limited as long as the wiper dyed with the colorant is prevented from being discolored by water or alcohol, and examples thereof include acrylic, vinyl acetate and synthetic rubber binders. The binder amount indicates a weight ratio with respect to the original fabric, and is 0.01% or more and 0.50% or less, preferably 0.05% or more and 0.40% or less. If it is less than 0.01%, color fading often occurs. Conversely, if it exceeds 0.50%, the absorbability of the wiper is lowered.

さらに、必要に応じて、本発明の目的を損なわない範囲で、ワイパーに耐熱安定剤、滑剤等を配合することができる。耐熱安定剤としては、例えば、ＢＨＴ（２，６−ジ−ｔ−ブチル−４−メチルフェノール）等のフェノール系安定剤等があげられる。 Furthermore, if necessary, a heat stabilizer, a lubricant and the like can be blended in the wiper within a range not impairing the object of the present invention. Examples of the heat resistant stabilizer include phenol-based stabilizers such as BHT (2,6-di-t-butyl-4-methylphenol).

ワイパーの坪量は、ＪＩＳＰ８１２４に準拠した方法で測定し、３５ｇ／ｍ^２以上６５ｇ／ｍ^２以下であり、３５ｇ／ｍ^２以上５０ｇ／ｍ^２以下が好ましい。３５ｇ／ｍ^２未満であるとワイパーの形成が難しく、逆に、６５ｇ／ｍ^２を超えると製品にする際のカットが困難になる。 The basis weight of the wiper is measured by a method according to JIS P 8124, 35g / ^{m 2} or more 65 g / ^{m 2} or less, 35 g / ^{m 2} or more 50 g / ^{m 2} or less. If it is less than 35 g / m ^2, it is difficult to form a wiper. Conversely, if it exceeds 65 g / m ² , it becomes difficult to cut the product.

ワイパーのＭＤ方向の剛軟度は、ＪＩＳＬ１０９６（１９９９）４５°カンチレバー法に準拠し、試料を幅２.５ｃｍ×長さ１５ｃｍとして測定した際のシート表裏面における平均値を意味し、５．０ｃｍ以上１１．５ｃｍである。 The bending resistance in the MD direction of the wiper means an average value on the front and back surfaces of the sheet when the sample is measured as 2.5 cm wide × 15 cm long according to JIS L 1096 (1999) 45 ° cantilever method. 0.0 cm or more and 11.5 cm.

不織布から形成されたワイパーにおいて、坪量３５ｇ／ｍ^２以上６５ｇ／ｍ^２以下及び剛軟度５．０ｃｍ以上１１．５ｃｍにすることにより、着色されたワイパーの柔軟性が向上し、かつ、生産性が向上する。 A wiper formed from a non-woven fabric has a basis weight of 35 g / m ² or more and 65 g / m ² or less and a bending resistance of 5.0 cm or more and 11.5 cm, thereby improving the flexibility of the colored wiper and producing it. Improves.

ワイパーの厚さはＪＩＳＰ８１１８に準拠した方法で測定し、０．２３ｍｍ以上０．７０ｍｍ以下である。０．２３ｍｍ未満であると、破れやすくなり、逆に、０．７０ｍｍを超えると、取扱い性が低下する。 The thickness of the wiper is measured by a method according to JIS P 8118 and is not less than 0.23 mm and not more than 0.70 mm. If it is less than 0.23 mm, it is easy to break, and conversely if it exceeds 0.70 mm, the handleability is lowered.

ワイパーは、交互に重ねられロータリーシリンダー式インターホルダーにより折り畳まれて積層され、上面部に取出口を有する収納箱に収納されている。折り畳み方法は、使用時に開口部から一枚を取り出すと、次の一枚の一部が開口部の外に露出する、いわゆるポップアップタイプや、シングルホールドタイプ等、特に限定はないが、片手で取り出しやすいポップアップ形式が好ましい。 The wipers are alternately stacked, folded and stacked by a rotary cylinder type inter-holder, and stored in a storage box having an outlet on the upper surface. The folding method is not particularly limited, such as a so-called pop-up type or single hold type, in which a part of the next piece is exposed outside the opening when one piece is taken out from the opening during use, but it is taken out with one hand. Easy pop-up format is preferred.

収納箱の基材は特に限定されないが、紙箱、樹脂フィルム、プラスチック箱、ハンドタオルディスペンサーをあげることができる。また、包装材の高さ、幅、長さ等の大きさは特に限定されない。収納箱の一部に粘着用の治具、例えば、磁石や両面テープ、接着剤を取り付け、壁掛けタイプとしてもよい。 Although the base material of a storage box is not specifically limited, A paper box, a resin film, a plastic box, and a hand towel dispenser can be mentioned. Further, the size, such as the height, width, and length of the packaging material is not particularly limited. A sticking jig, for example, a magnet, a double-sided tape, or an adhesive, may be attached to a part of the storage box so as to be a wall hanging type.

紙箱は、例えば、木材パルプ、古紙、段ボール紙、コートボール紙等の平面紙を用いて形成することができ、強度の観点から、コートボール紙が好ましい。 The paper box can be formed using, for example, flat paper such as wood pulp, waste paper, corrugated paper, and coated cardboard, and coated cardboard is preferred from the viewpoint of strength.

平面紙の坪量は、ＪＩＳＰ８１２４に準じて測定され、２００ｇ／ｍ^２以上５５０ｇ／ｍ^２以下が好ましく、２５０ｇ／ｍ^２以上５００ｇ／ｍ^２以下がより好ましく、３００ｇ／ｍ^２以上５００ｇ／ｍ^２以下が最も好ましい。坪量が、２００ｇ／ｍ^２未満であると、強度が不十分となり、一方、５５０ｇ／ｍ^２を超えると、平面紙を折り曲げ、立体形状に形成する際に、加工性が低下する。 The basis weight of the flat sheet is measured in accordance with JIS P8124, 200g / ^m is preferably ² or more 550 g / ^{m 2} or less, 250 g / ^m, more preferably ² or more 500 g / ^{m 2} or less, 300 g / ^{m 2} or more 500 g / m Most preferred is ² or less. When the basis weight is less than 200 g / m ² , the strength becomes insufficient. On the other hand, when the basis weight exceeds 550 g / m ² , workability is lowered when the flat paper is bent and formed into a three-dimensional shape.

樹脂フィルムは、例えば、ポリエチレンフィルム、ポリプロピレンフィルム、ポリエチレンテレフタレートフィルム、ポリビニルアルコールフィルム、ポリスチレンフィルム、エチレン−ビニルアルコール共重合体フィルムをあげることができる。なかでも、透明性が高く、ミシン目での裂開性にも優れることから、直鎖状低密度ポリエチレンフィルムが好ましい。樹脂フィルムの厚さは、４０μｍ以上８０μｍ以下であることが好ましい。４０μｍ未満のであると、折り畳んで積層したワイパーの形状維持力が低く、自身の強度も不足する。逆に、８０μｍを超えると、剛性が高すぎるため、取り扱い性及びシール性が悪化する。 Examples of the resin film include a polyethylene film, a polypropylene film, a polyethylene terephthalate film, a polyvinyl alcohol film, a polystyrene film, and an ethylene-vinyl alcohol copolymer film. Of these, a linear low density polyethylene film is preferred because of its high transparency and excellent tearing ability at the perforation. The thickness of the resin film is preferably 40 μm or more and 80 μm or less. When the thickness is less than 40 μm, the shape maintaining force of the folded and laminated wipers is low, and the strength of the wiper itself is insufficient. On the other hand, when it exceeds 80 μm, the rigidity is too high, and the handleability and the sealing performance deteriorate.

以下に、実施例及び比較例を挙げて本発明を更に具体的に説明する。 Hereinafter, the present invention will be described more specifically with reference to Examples and Comparative Examples.

（坪量）
ＪＩＳＰ８１２４に準拠した方法で測定した。 (Basis weight)
It measured by the method based on JISP8124.

（ＭＤ方向の剛軟度）
ＪＩＳＬ１０９６（１９９９）４５°カンチレバー法に準拠し、試料を幅２.５ｃｍ×長さ１５ｃｍとして測定し、シート表裏面での平均値を用いた。剛軟度は数値が小さいほど柔らかいことを示す。 (Flexibility in MD direction)
In accordance with JIS L 1096 (1999) 45 ° cantilever method, the sample was measured as 2.5 cm wide × 15 cm long, and the average value on the front and back surfaces of the sheet was used. The lower the numerical value, the softer the softness.

（厚さ）
ＪＩＳＰ８１１８に準拠した方法で測定した。 (thickness)
It measured by the method based on JISP8118.

（実施例１）
レーヨン１００％を配合した不織布をワイパーの基材として用い、顔料及び０．５０重量％のアクリルバインダーの混合液をロールアプリケートにて塗布・乾燥させ、坪量３５ｇ／ｍ^２、厚さ０．２３ｍｍのワイパーを作製した。このワイパーのＭＤ方向の剛軟度を測定したところ、９．６ｃｍであることがわかった。次に、図２に示すロータリーシリンダー式インターホルダーを用いてワイパーの原反に折り加工を行い、ワイパー積層体を作製した。これらの結果を表１に示す。 Example 1
Using a non-woven fabric blended with 100% rayon as a base material for the wiper, a mixed solution of pigment and 0.50% by weight acrylic binder was applied and dried with a roll applicator, and the basis weight was 35 g / m ² and the thickness was 0.00. A 23 mm wiper was produced. When the bending resistance in the MD direction of this wiper was measured, it was found to be 9.6 cm. Next, the raw material of the wiper was folded using the rotary cylinder type inter-holder shown in FIG. 2 to produce a wiper laminate. These results are shown in Table 1.

（実施例２〜７）
実施例２〜７については、表１に示す坪量、バインダー量で実施例１とまったく同様にして、ワイパーを作製し、ワイパーのＭＤ方向の剛軟度を測定した。次に、実施例１とまったく同様にして、ワイパー積層体を作製した。これらの結果を表１に示す。 (Examples 2 to 7)
For Examples 2 to 7, wipers were prepared in the same manner as in Example 1 with the basis weight and binder amount shown in Table 1, and the bending resistance of the wiper in the MD direction was measured. Next, a wiper laminate was produced in exactly the same manner as in Example 1. These results are shown in Table 1.

（比較例１）
表２に示すように、坪量を３０ｇ／ｍ^２に変更し、バインダーを添加しない以外は実施例１とまったく同様にして、ワイパーを作製した。しかし、このワイパーのＭＤ方向の剛軟度は検出限界以下（ＮＤ）であり、ロータリーシリンダー式インターホルダーを用いた折り加工を試みたが、ワイパー積層体を作製することはできなかった。これらの結果を表２に示す。 (Comparative Example 1)
As shown in Table 2, a wiper was produced in the same manner as in Example 1 except that the basis weight was changed to 30 g / m ² and no binder was added. However, the bending resistance of the wiper in the MD direction was below the detection limit (ND), and folding was attempted using a rotary cylinder type inter-holder, but a wiper laminate could not be produced. These results are shown in Table 2.

（比較例２）
表２に示すように、坪量を５０ｇ／ｍ^２に変更したこと以外は実施例１とまったく同様にして、ワイパーを作製した。このワイパーは、実施例３と比較して坪量が高く、ＭＤ方向の剛軟度が１２．４ｃｍと硬いため、折り加工が効率よく行えず、ワイパー積層体に不具合が発生した。これらの結果を表２に示す。 (Comparative Example 2)
As shown in Table 2, a wiper was produced in the same manner as in Example 1 except that the basis weight was changed to 50 g / m ² . Since this wiper had a higher basis weight than that of Example 3 and the MD softness was as hard as 12.4 cm, folding work could not be performed efficiently, and a defect occurred in the wiper laminate. These results are shown in Table 2.

（比較例３）
表２に示すように、坪量を５５ｇ／ｍ^２に変更し、バインダー量を０．４０重量％に変更したこと以外は実施例１とまったく同様にして、ワイパーを作製した。このワイパーは、実施例５と比較してバインダーの量が少ないものの、ＭＤ方向の剛軟度は１７ｃｍと硬いため、折り加工が効率よく行えず、ワイパー積層体に不具合が発生した。これらの結果を表２に示す。 (Comparative Example 3)
As shown in Table 2, a wiper was produced in exactly the same manner as in Example 1 except that the basis weight was changed to 55 g / m ² and the binder amount was changed to 0.40% by weight. Although this wiper had a smaller amount of binder as compared with Example 5, the bending resistance in the MD direction was as hard as 17 cm, so that folding could not be performed efficiently, and a defect occurred in the wiper laminate. These results are shown in Table 2.

（比較例４）
表２に示すように、坪量を５５ｇ／ｍ^２に変更し、バインダー量を０．５０重量％に変更したこと以外は実施例１とまったく同様にして、ワイパーを作製した。このワイパーは、実施例６と比較してバインダー量が多く、ＭＤ方向の剛軟度が１３．６ｃｍと硬いため、折り加工を試みたが、ワイパー積層体を作製することはできなかった。これらの結果を表２に示す。 (Comparative Example 4)
As shown in Table 2, wipers were produced in exactly the same manner as in Example 1, except that the basis weight was changed to 55 g / m ² and the binder amount was changed to 0.50% by weight. Since this wiper had a larger binder amount than Example 6 and the bending resistance in the MD direction was as hard as 13.6 cm, folding was attempted, but a wiper laminate could not be produced. These results are shown in Table 2.

（比較例５）
表２に示すように、坪量を７０ｇ／ｍ^２に変更し、バインダー量を０．０１重量％に変更したこと以外は実施例１とまったく同様にして、ワイパーを作製した。このワイパーは、実施例７とバインダー量が同じであり、ＭＤ方向の剛軟度が５．３ｃｍとほぼ同じであるが、坪量が多いため、折り加工が効率よく行えず、ワイパー積層体に不具合が発生した。これらの結果を表２に示す。 (Comparative Example 5)
As shown in Table 2, wipers were produced in exactly the same manner as in Example 1, except that the basis weight was changed to 70 g / m ² and the binder amount was changed to 0.01% by weight. This wiper has the same binder amount as in Example 7, and the bending resistance in the MD direction is almost the same as 5.3 cm. However, since the basis weight is large, folding cannot be performed efficiently, and the wiper laminate is A malfunction occurred. These results are shown in Table 2.

以上、実施形態を用いて本発明を説明したが、本発明の技術的範囲は上記実施形態に記載の範囲には限定されないことは言うまでもない。上記実施形態に、多様な変更または改良を加えることが可能であることが当業者に明らかである。またその様な変更または改良を加えた形態も本発明の技術的範囲に含まれ得ることが、特許請求の範囲の記載から明らかである。 As mentioned above, although this invention was demonstrated using embodiment, it cannot be overemphasized that the technical scope of this invention is not limited to the range as described in the said embodiment. It will be apparent to those skilled in the art that various modifications or improvements can be added to the above-described embodiments. Further, it is apparent from the scope of the claims that the embodiments added with such changes or improvements can be included in the technical scope of the present invention.

１ワイパー包装体
３ワイパー
９ワイパー積層体
９１積層体取出し装置
２０収納箱
２１取出口
１００折機
Ｒ、Ｌ原反ロール
３１フェルトロール
３２フィードロール
５原反ウエブ
５１原反ウエブのＭＤ方向
６０フォールディング部
６１フォールディングロール
６１ａバキュームゾーン
６１ｂジョー
６１ｃ溝
６１ｄナイフ
６１ｅフォールディングバー
６２ナイフ受け
７シート
７１折れ
７ａ、７ｂ、７ｃ、７ｄ、７ｅ製品シート DESCRIPTION OF SYMBOLS 1 Wiper packaging body 3 Wiper 9 Wiper laminated body 91 Laminate take-out apparatus 20 Storage box 21 Exit 100 Folding machine R, L Original fabric roll 31 Felt roll 32 Feed roll 5 Original fabric web 51 MD direction 60 of original fabric web Folding part 61 Folding roll 61a Vacuum zone 61b Jaw 61c Groove 61d Knife 61e Folding bar 62 Knife receptacle 7 Sheet 71 Folding 7a, 7b, 7c, 7d, 7e Product sheet

上記課題を解決するために、本発明は、以下の構成によって把握される。
（１）本発明のワイパー包装体は、ワイパーとワイパー収納箱を備えるワイパー包装体であって、前記ワイパーは、不織布から形成され、着色が施され、３５ｇ／ｍ^２以上６５ｇ／ｍ^２以下の坪量と、５．０ｃｍ以上１１．５ｃｍ以下の４５°カンチレバー法に準拠したＭＤ方向の剛軟度とを有し、前記ワイパー収納箱は、上部に取出口を有し、前記ワイパーが積層されたワイパー積層体を収納し、前記ワイパーの取出し方向は、前記ワイパーの縦方向（ＭＤ方向）であることを特徴とする。
In order to solve the above problems, the present invention is grasped by the following configuration.
(1) The wiper package of the present invention is a wiper package including a wiper and a wiper storage box, wherein the wiper is formed of a nonwoven fabric and is colored, and is 35 g / m ² or more and 65 g / m ² or less. possess a basis weight, the bending resistance MD direction conforming to 11.5cm following 45 ° cantilever method or 5.0 cm, the wiper storage box has a takeout at the top, the wiper is laminated The wiper laminated body is housed, and the direction in which the wiper is taken out is the vertical direction (MD direction) of the wiper.

（２）本発明のワイパー包装体は、（１）の構成において、前記ワイパーが０.２３ｍｍ以上０．７０ｍｍ以下の厚さを有することを特徴とする。
(2) The wiper package of the present invention is characterized in that, in the configuration of (1), the wiper has a thickness of 0.23 mm to 0.70 mm.

（３）本発明のワイパー包装体は、（１）または（２）の構成において、前記ワイパーがアクリル系、酢酸ビニル系及び合成ゴム系から選択される０．０１重量％以上０．５０重量％以下のバインダーを含有することを特徴とする。
(3) The wiper package of the present invention is the wiper package according to (1) or (2), wherein the wiper is selected from acrylic, vinyl acetate, and synthetic rubber based on 0.01% by weight or more and 0.50% by weight. It contains the following binders.

（４）本発明のワイパー包装体は、（１）ないし（３）のいずれかの構成において、前記ワイパーが、ロータリーシリンダー式インターホルダーを用いて折り畳まれ、交互に重ねられてポップアップ式に折り畳まれて積層されることを特徴とする。
(4) The wiper package according to the present invention is the wiper package according to any one of (1) to (3), wherein the wiper is folded using a rotary cylinder type inter-holder , and alternately stacked and folded in a pop-up manner. It is characterized by being laminated .

（５）本発明のワイパー包装体は、（１）ないし（４）のいずれかの構成において、前記ワイパー収納箱は、２００ｇ／ｍ ^２以上５５０ｇ／ｍ ^２以下の坪量を有する平面紙又は４０μｍ以上８０μｍ以下の厚さを有する樹脂フィルムを基材とすることを特徴とする。
(5) The wiper package of the present invention is the wiper package according to any one of (1) to (4), wherein the wiper storage box is a flat paper having a basis weight of 200 g / m ² or more and 550 g / m ² or less, or 40 μm. A resin film having a thickness of 80 μm or less is used as a base material .

本発明は、ワイパー包装体に関する。 The present invention relates to a wiper package.

上記課題を解決するために、本発明は、以下の構成によって把握される。
（１）本発明のワイパー包装体は、ワイパーとワイパー収納箱を備えるワイパー包装体であって、ワイパーは、不織布から形成され、着色が施され、アクリル系、酢酸ビニル系及び合成ゴム系から選択される０．０１重量％以上０．５０重量％以下の色落ち防止用のバインダーを含有し、３５ｇ／ｍ^２以上６５ｇ／ｍ^２以下の坪量と、５．０ｃｍ以上１１．５ｃｍ以下の４５°カンチレバー法に準拠したＭＤ方向の剛軟度とを有し、前記ワイパー収納箱は、上部に取出口を有し、前記ワイパーが積層されたワイパー積層体を収納し、前記ワイパーの取出し方向は、ワイパーの縦方向（ＭＤ方向）であることを特徴とする。 In order to solve the above problems, the present invention is grasped by the following configuration.
(1) The wiper package of the present invention is a wiper package including a wiper and a wiper storage box. The wiper is formed from a nonwoven fabric, is colored, and is selected from acrylic, vinyl acetate, and synthetic rubber. Containing 0.01% to 0.50% by weight of a binder for preventing discoloration, a basis weight of 35 g / m ^{2 to} 65 g / m ² , and 45 of 5.0 cm to 11.5 cm ° possess a bending resistance MD direction conforming to the cantilever method, the wiper storage box has a takeout at the top, housing a wiper stack in which the wiper is stacked, take-out direction of the wiper The wiper is in the vertical direction (MD direction) .

（３）本発明のワイパー包装体は、（１）または（２）の構成において、前記ワイパーが、ロータリーシリンダー式インターホルダーを用いて折り畳まれ、交互に重ねられてポップアップ式に折り畳まれて積層されることを特徴とする。 (3) In the wiper package of the present invention, in the configuration of (1) or (2), the wipers are folded using a rotary cylinder type inter-holder, alternately stacked and folded in a pop-up manner and stacked. characterized in that that.

（４）本発明のワイパー包装体は、（１）ないし（３）のいずれかの構成において、前記ワイパー収納箱は、２００ｇ／ｍ ^２以上５５０ｇ／ｍ ^２以下の坪量を有する平面紙又は４０μｍ以上８０μｍ以下の厚さを有する樹脂フィルムを基材とすることを特徴とする。 (4) Wiper package of the present invention, (1) to in the construction of (3), before Symbol wiper storage box, flat sheet having 200 g / ^{m 2} or more 550 g / ^{m 2} or less basis weight or A resin film having a thickness of 40 μm or more and 80 μm or less is used as a base material .

Claims

A wiper formed from a nonwoven fabric,
The wiper is colored,
A basis weight of 35 g / m ² or more and 65 g / m ² or less;
A wiper characterized by having a bending resistance in the MD direction based on a 45 ° cantilever method of 5.0 cm or more and 11.5 cm or less.

The wiper according to claim 1, wherein the wiper has a thickness of 0.23 mm to 0.70 mm.

The wiper according to claim 1 or 2, wherein the wiper contains a binder of 0.01 wt% or more and 0.50 wt% or less.

The wiper according to any one of claims 1 to 3, wherein the wiper is folded using a rotary cylinder type inter-holder.

5. The wiper package according to claim 4, wherein the wipers according to claim 4 are alternately stacked, folded in a pop-up manner and stacked, and stored in a storage box having an outlet at the top.