JP2013257359A - Antidazzle hard coat film - Google Patents

Antidazzle hard coat film Download PDF

Info

Publication number
JP2013257359A
JP2013257359A JP2012131660A JP2012131660A JP2013257359A JP 2013257359 A JP2013257359 A JP 2013257359A JP 2012131660 A JP2012131660 A JP 2012131660A JP 2012131660 A JP2012131660 A JP 2012131660A JP 2013257359 A JP2013257359 A JP 2013257359A
Authority
JP
Japan
Prior art keywords
hard coat
film
antiglare
coat film
resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2012131660A
Other languages
Japanese (ja)
Inventor
Kimiyoshi Sakanochi
公善 阪後
Takeshi Hotta
武史 堀田
Yusuke Sugiyama
祐介 杉山
Sho Karizume
翔 狩集
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Paper Industries Co Ltd
Jujo Paper Co Ltd
Original Assignee
Nippon Paper Industries Co Ltd
Jujo Paper Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Paper Industries Co Ltd, Jujo Paper Co Ltd filed Critical Nippon Paper Industries Co Ltd
Priority to JP2012131660A priority Critical patent/JP2013257359A/en
Publication of JP2013257359A publication Critical patent/JP2013257359A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide an antidazzle hard coat film, which has high transmittance, a low haze value, excellent transparency and high image sharpness, suppresses glare of an image, reduces whiteness (white blur) of a coating film, suppresses decrease in contrast and improves visibility of a display, compared to a conventional antidazzle film, without imparting an excessive antidazzle property than a required degree to the film, and which is also excellent in an antifouling property and scratch resistance.SOLUTION: An antidazzle hard coat film includes an antidazzle hard coat layer containing fine particles, a resin and a fluorine-containing polymerizable compound, formed on a transparent film. The antidazzle hard coat film has a maximum cross-sectional height of 1.0 to 3.0 μm and an average inclination angle of 1 degree or less on the film surface, and shows a transmissive sharpness of 70% or more in each measurement using four types of optical combs (with widths of 2 mm, 1 mm, 0.5 mm and 0.125 mm).

Description

本発明は、液晶ディスプレイ、プラズマディスプレイ、有機ELディスプレイに代表される各種ディスプレイの表面に用いられる視認性の低下を防止するために好適な防眩ハードコートフィルムに関する。   The present invention relates to an antiglare hard coat film suitable for preventing a reduction in visibility used on the surface of various displays represented by liquid crystal displays, plasma displays, and organic EL displays.

ノートパソコン、液晶モニタなどのディスプレイは、表示面で外景の映り込みを防止するため、通常有機または無機の微粒子とバインダー樹脂または硬化性樹脂の混合物を基材に塗布し、表面に凹凸を形成することにより、防眩性を発現させている。防眩性を高めるには前記凹凸形状を大きくする、あるいは凹凸の頻度を増やす必要がある。しかし、凹凸が大きく、あるいは頻度が増えると、防眩層のヘイズ値(霞度)が上昇し防眩性が得られるものの外光の映り込みにより画面が白ボケることや、ヘイズ値の上昇に伴い像鮮明度が低下し、表示画像の視認性を悪化させるという問題があった。さらに、従来の防眩ハードコートフィルムの一般的な評価である表面のヘイズ値を低くすると、外光の映り込みにより画面が白ボケる程度は抑制できるものの、フィルム表面に、いわゆるシンチレーション(ギラツキ、面ぎら)と呼ばれるキラキラ光る輝きが強くなり、これを解消する手法としては防眩層内部のヘイズ値を高くする方法が用いられていたが、微粒子と樹脂の屈折率差に起因した内部ヘイズにより、透過率の低下が生じ、表示装置の表示輝度を低下させ、同時に内部ヘイズにより塗膜が白っぽくなるため、コントラストの低下が著しかった。   In order to prevent reflection of outside scenes on the display surface of notebook PCs, LCD monitors, etc., usually a mixture of organic or inorganic fine particles and a binder resin or curable resin is applied to the substrate to form irregularities on the surface. As a result, antiglare properties are exhibited. In order to improve the antiglare property, it is necessary to increase the uneven shape or increase the frequency of the unevenness. However, if the irregularities are large or the frequency increases, the haze value (degree) of the anti-glare layer increases and anti-glare properties can be obtained, but the screen is blurred due to the reflection of external light, or the haze value increases. As a result, there has been a problem that the image definition is lowered and the visibility of the display image is deteriorated. Furthermore, when the haze value of the surface, which is a general evaluation of conventional anti-glare hard coat films, is lowered, the degree of white blurring due to the reflection of external light can be suppressed, but so-called scintillation (glare, As a technique to eliminate this, a method of increasing the haze value inside the antiglare layer was used, but due to the internal haze caused by the difference in refractive index between the fine particles and the resin The transmittance was lowered, the display brightness of the display device was lowered, and at the same time, the coating film became whitish due to the internal haze, so that the contrast was greatly lowered.

例えば、特開平11−326608号公報(特許文献1)には、平均粒子径が0.5〜5.0μmであり、透過性樹脂との屈折率の差が0.02〜0.20である透光性微粒子を配合した防眩性フィルムが開示されている。防眩層を構成する透光性樹脂と、これに含まれる透光性微粒子の屈折率の差を0.02〜0.20とすることによって、拡散・防眩性を低下させることなく、像鮮明度を向上させ、また、この場合、ヘイズ値を高くしてギラツキを低減させても、像鮮明度を高く維持することができるとしている。しかしながら、具体的に得られるフィルムのヘイズは10%以上と高く防眩性を有する一方、塗膜が白っぽくなり、透過率とコントラストの低下が著しい。   For example, in Japanese Patent Application Laid-Open No. 11-326608 (Patent Document 1), the average particle diameter is 0.5 to 5.0 μm, and the difference in refractive index from the transparent resin is 0.02 to 0.20. An antiglare film containing translucent fine particles is disclosed. By setting the difference in refractive index between the translucent resin constituting the antiglare layer and the translucent fine particles contained therein to 0.02 to 0.20, an image can be obtained without reducing diffusion and antiglare properties. In this case, the image definition can be maintained high even if the haze value is increased to reduce glare. However, the haze of the film specifically obtained is as high as 10% or more and has an antiglare property, while the coating film becomes whitish and the transmittance and contrast are remarkably reduced.

また、特開2008−286878号公報(特許文献2)には、防眩性フィルムにおいては、バインダーの硬化物と透光性微粒子との屈折率差が0〜0.05という小さい範囲に抑えられるため、防眩性ハードコート層の内部における光の透過性を向上させることができ、防眩性ハードコート層の表面におけるJIS B 0601−1994に準拠して測定される算術平均粗さ(Ra)が0.01〜0.30μm及び凹凸の平均間隔(Sm)が10〜300μmという小さい範囲に抑えられているため、防眩性ハードコート層の表面(外面)における光の拡散を発揮しつつ、光の透過性を維持することができ、該防眩性フィルムは、ぎらつきの抑制と、透過鮮明性の向上とをバランス良く発揮することができるとしている。しかしながら、算術平均粗さ(Ra)が0.01〜0.30μm及び凹凸の平均間隔(Sm)が10〜300μmという範囲は小さくなく、現在市場で製品化されている防眩フィルムのほとんどがこの範囲に該当する。また、具体的に得られるフィルムは算術平均粗さ(Ra)が0.1μm以上で、2mmの幅を有する光学櫛を通して測定される像鮮明度の値が70%未満で、かつ60°反射で測定される像鮮明度の値が60%以下では、防眩性を有する一方、高精細パネルでのギラツキ防止は不十分で、塗膜の白っぽさは考慮されておらず、透過率とコントラストの低下が著しいという問題が残る。   Japanese Patent Application Laid-Open No. 2008-286878 (Patent Document 2) discloses that, in an antiglare film, the difference in refractive index between a cured binder and a light-transmitting fine particle is as small as 0 to 0.05. Therefore, the light transmittance in the antiglare hard coat layer can be improved, and the arithmetic average roughness (Ra) measured in accordance with JIS B 0601-1994 on the surface of the antiglare hard coat layer. Is suppressed to a small range of 0.01 to 0.30 μm and the average interval of unevenness (Sm) of 10 to 300 μm, while diffusing light on the surface (outer surface) of the antiglare hard coat layer, Light transmittance can be maintained, and the anti-glare film is said to be able to exhibit a good balance between suppression of glare and improvement of transmission clarity. However, the arithmetic average roughness (Ra) is 0.01 to 0.30 μm and the average interval of unevenness (Sm) is not so small as 10 to 300 μm, and most of the antiglare films currently on the market are Applicable to the range. In addition, the film obtained specifically has an arithmetic average roughness (Ra) of 0.1 μm or more, an image sharpness value measured through an optical comb having a width of 2 mm is less than 70%, and 60 ° reflection. When the measured image sharpness value is 60% or less, the antiglare property is not sufficient, but glare prevention on the high-definition panel is insufficient, and the whiteness of the coating film is not taken into consideration. The problem remains that the contrast is significantly reduced.

特開平11−326608号公報JP 11-326608 A 特開2008−286878号公報JP 2008-286878 A

従来技術においては防眩性を考慮するあまり、ギラツキ防止の観点からヘイズ値を高くすること、また像鮮明度を十分に高くできないことから、透過率の低さと塗膜の白っぽさが解消できておらず画像を表示すると画面が白っぽくなり、特に、黒表示で画像品位が低下する問題があった。   In the conventional technology, considering the antiglare property, the haze value is increased from the viewpoint of preventing glare, and the image clarity cannot be sufficiently increased, so the low transmittance and the whitishness of the coating are eliminated. If the image is not formed and the image is displayed, the screen becomes whitish, and there is a problem that the image quality is deteriorated particularly in the black display.

そこで、本発明の目的は、このような従来の防眩フィルムに比べ、必要以上の防眩性を付与することなく、透過率が高く、ヘイズ値が低く透明性に優れ、像鮮映性が高く、画像のギラツキを抑制し、塗膜の白っぽさ(白ぼけ)を低減しコントラスト低下を抑え、ディスプレイの視認性を向上させるとともに、防汚性、耐擦傷性に優れた表面保護用の防眩ハードコートフィルムを提供することである。   Therefore, the object of the present invention is to provide a high transmittance, a low haze value, excellent transparency, and image clarity, without imparting an antiglare property more than necessary, compared to such a conventional antiglare film. High, suppresses glare in the image, reduces the whitishness of the paint film, suppresses contrast deterioration, improves the visibility of the display, and is for surface protection with excellent antifouling and scratch resistance. It is providing an anti-glare hard coat film.

本発明は、以下の[1]〜[3]を提供するものである。
[1] 透明フィルム上に、微粒子、樹脂及び含フッ素重合性化合物を含有する防眩ハードコート層を設けてなる防眩ハードコートフィルムであって、該防眩ハードコートフィルムの表面の評価領域内の高さの平均値をゼロ(零)としたときの、評価領域内の高さ最大値と評価領域内の高さ最小値との差で表わす最大断面高さが1.0〜3.0μmであるとともに、該防眩ハードコートフィルム表面の凹凸の平均傾斜角が1度以下であり、かつ該防眩ハードコートフィルムのJIS K 7105−1981に基づく透過鮮明度測定装置を用いて4つの光学櫛(巾2mm、1mm、0.5mm、0.125mm)を通して測定される透過鮮明度の値が各々70%以上であることを特徴とする防眩ハードコートフィルム。
[2] 前記含フッ素重合性化合物が、フッ素フルオロ脂肪族基及び親水性基を有することを特徴とする[1]記載の防眩ハードコートフィルム。
[3] 前記含フッ素重合性化合物の含有量がハードコート層中の樹脂100重量部に対して、0.1〜1.0重量部(固形分)であることを特徴とする[1]〜[2]記載の防眩ハードコートフィルム。
The present invention provides the following [1] to [3].
[1] An antiglare hard coat film in which an antiglare hard coat layer containing fine particles, a resin and a fluorine-containing polymerizable compound is provided on a transparent film, wherein the antiglare hard coat film is within the evaluation region on the surface of the antiglare hard coat film The maximum cross-sectional height expressed by the difference between the maximum height value in the evaluation region and the minimum height value in the evaluation region when the average value of the heights is zero (zero) is 1.0 to 3.0 μm. In addition, the average inclination angle of the unevenness on the surface of the antiglare hard coat film is 1 degree or less, and the optical clarity is measured using a transmission sharpness measuring device based on JIS K 7105-1981 of the antiglare hard coat film. An anti-glare hard coat film characterized by having a transmission sharpness value measured through a comb (width 2 mm, 1 mm, 0.5 mm, 0.125 mm) of 70% or more.
[2] The antiglare hard coat film according to [1], wherein the fluorine-containing polymerizable compound has a fluorine fluoroaliphatic group and a hydrophilic group.
[3] The content of the fluorine-containing polymerizable compound is 0.1 to 1.0 part by weight (solid content) with respect to 100 parts by weight of the resin in the hard coat layer. [2] The antiglare hard coat film according to [2].

本発明によれば、従来の防眩フィルムに比べ、必要以上の防眩性を付与することなく、透過率が高く、ヘイズ値が低く透明性に優れ、像鮮映性が高く、画像のギラツキを抑制し、塗膜の白っぽさ(白ぼけ)を低減しコントラスト低下を抑え、ディスプレイの視認性を向上させるとともに、防汚性、耐擦傷性に優れた表面保護用の防眩ハードコートフィルムを提供することができる。すなわち、本発明の防眩ハードコートフィルムによれば、防汚性、耐擦傷性に優れ、塗膜の白っぽさを低減しコントラストを低下させずに、実用上問題ないレベルの防眩性と高い透過率、高い像鮮明度、画像のギラツキを抑制し、ディスプレイの視認性を向上させることができる。   According to the present invention, the transmittance is high, the haze value is low, the transparency is excellent, the image clarity is high, and the image is not glaring, as compared with the conventional antiglare film. , Anti-glare hard coat for surface protection with excellent antifouling and scratch resistance as well as improving the visibility of the display by reducing the whitishness of the paint film A film can be provided. That is, according to the antiglare hard coat film of the present invention, the antiglare property is excellent in antifouling property and scratch resistance, and the antiglare property has a practically no problem level without reducing the whiteness of the coating film and reducing the contrast. High transmittance, high image definition, and image glare can be suppressed, and the visibility of the display can be improved.

以下、本発明の実施の形態について詳細に説明する。   Hereinafter, embodiments of the present invention will be described in detail.

本発明の防眩ハードコートフィルムは、透明フィルム上に、微粒子、樹脂及び含フッ素重合性化合物を含有する防眩ハードコート層を設けてなる防眩ハードコートフィルムであって、該防眩ハードコートフィルムの表面の評価領域内の高さの平均値をゼロ(零)としたときの、評価領域内の高さ最大値と評価領域内の高さ最小値との差で表わす最大断面高さが1.0〜3.0μmであり、かつ該防眩ハードコートフィルム表面の凹凸の平均傾斜角が1度以下であることを特徴としている。   The antiglare hard coat film of the present invention is an antiglare hard coat film in which an antiglare hard coat layer containing fine particles, a resin and a fluorine-containing polymerizable compound is provided on a transparent film, the antiglare hard coat The maximum cross-sectional height represented by the difference between the maximum height in the evaluation area and the minimum height in the evaluation area when the average value of the height in the evaluation area on the surface of the film is zero. It is 1.0-3.0 micrometers, and the average inclination | tilt angle of the unevenness | corrugation on this anti-glare hard coat film surface is 1 degree or less, It is characterized by the above-mentioned.

ここで、「最大断面高さ」とは上記の定義のとおりであるが、JIS B0601にも定義されているように、測定対象であるフィルム表面の断面曲線(測定曲線)から算出される値である。本発明のような微粒子および樹脂を含有する防眩ハードコート層を設けてなる防眩ハードコートフィルムの表面は、微細な凹凸形状だけでなく、うねりが存在している。表面粗さ測定機で測定した測定曲線(通常、断面曲線とも呼ばれる。)は、うねり曲線および粗さ曲線との間で、
断面曲線=うねり曲線+粗さ曲線
の関係がある。従って、本発明における「最大断面高さ」は、「表面うねり成分」を含む断面曲線を評価している。なお、2001年版のJISでは、最大断面高さは記号「Pt」で表す。
Here, “maximum cross-sectional height” is as defined above, but as defined in JIS B0601, it is a value calculated from the cross-sectional curve (measurement curve) of the film surface that is the object of measurement. is there. The surface of the antiglare hard coat film provided with the antiglare hard coat layer containing the fine particles and the resin as in the present invention has not only fine irregular shapes but also undulations. A measurement curve (usually called a cross-section curve) measured with a surface roughness measuring machine is between a waviness curve and a roughness curve.
There is a relationship of cross-sectional curve = waviness curve + roughness curve. Therefore, the “maximum cross-sectional height” in the present invention evaluates a cross-sectional curve including a “surface waviness component”. In the 2001 version of JIS, the maximum cross-sectional height is represented by the symbol “Pt”.

また、上記の「平均傾斜角」とは、測定対象であるフィルム表面の断面曲線(測定曲線)を一定間隔ΔXで横方向に区切り、各区間内における断面曲線の終始点を結ぶ線分の傾き(傾斜角:傾斜角は、tan−1(ΔYi/ΔXで求められる。)の絶対値を求め、その値を平均したもの(θa)をいう(図1参照)。すなわち、平均傾斜角(θa)は、下記式で定義される値である。 In addition, the above “average inclination angle” refers to the slope of a line segment that divides a cross-sectional curve (measurement curve) of the film surface to be measured at a constant interval ΔX and connects the start points of the cross-sectional curves in each section. (Inclination angle: The inclination angle is obtained by calculating the absolute value of tan −1 (determined by ΔYi / ΔX) and averaging the values (θa) (see FIG. 1), that is, the average inclination angle (θa ) Is a value defined by the following formula.

Figure 2013257359
Figure 2013257359

かかる本発明の防眩ハードコートフィルムによれば、ヘイズ値が低く、透過率の高い、透明性に優れる理由は、本発明者の検討によると次のように推測される。 According to such an anti-glare hard coat film of the present invention, the reason why the haze value is low, the transmittance is high, and the transparency is excellent is presumed as follows according to the study of the present inventors.

防眩ハードコートフィルムのヘイズ値は、防眩ハードコート層表面の凹凸に起因し光が屈折、散乱することで発生する表面ヘイズと、防眩ハードコート層中に微粒子が存在することに起因し光が屈折、散乱することで発生する内部ヘイズがあり、防眩ハードコートフィルムの表面の評価領域内の高さの平均値をゼロ(零)としたときの、評価領域内の高さ最大値と評価領域内の高さ最小値との差で表わす最大断面高さが1.0〜3.0μmであり、かつ該防眩ハードコートフィルム表面の凹凸の平均傾斜角が1度以下である場合、特定領域のうねり、或いはなだらかな(緩やかな)表面凹凸、等の表面性が得られ、表面の凹凸に起因する光の屈折、散乱を抑制できるため、表面ヘイズが発現し難くなり、光の屈折、散乱による光のロスが抑えられるので透過率の低下を抑制できるとともに、防眩ハードコート層表面での散乱光により防眩ハードコートフィルムが白っぽく濁る現象が抑えられることから透明性に優れるものと考えられる。   The haze value of the antiglare hard coat film is attributed to the surface haze generated when light is refracted and scattered due to the irregularities on the surface of the antiglare hard coat layer and the presence of fine particles in the antiglare hard coat layer. There is an internal haze generated by light being refracted and scattered, and the maximum height in the evaluation area when the average height in the evaluation area on the surface of the antiglare hard coat film is zero. And the maximum cross-sectional height represented by the difference between the height in the evaluation region is 1.0 to 3.0 μm, and the average inclination angle of the irregularities on the surface of the antiglare hard coat film is 1 degree or less. The surface properties such as the undulation of the specific region or the gentle (gradual) surface unevenness can be obtained, and the refraction and scattering of the light caused by the surface unevenness can be suppressed, so that the surface haze is hardly expressed and the light Reduces light loss due to refraction and scattering With the decrease in transmittance can be suppressed since the by scattered light in the antiglare hard coat layer surface is considered that excellent transparency since the antiglare hard coat film is suppressed phenomenon turbid whitish.

なお、防眩ハードコートフィルムの表面の上記最大断面高さが3.0μmを超える場合、表面の凹凸に起因する光の屈折、散乱が強まるため表面ヘイズが発現し易くなり、光の屈折、散乱による光のロスにより透過率の低下が懸念されるとともに、防眩ハードコート層表面での散乱光による防眩性は得られ易くなるが、防眩ハードコートフィルムが白っぽく濁る現象を抑えられ難くなることから透明性や透過鮮明度が低下しやすい。   In addition, when the above-mentioned maximum cross-sectional height of the surface of the antiglare hard coat film exceeds 3.0 μm, the refraction and scattering of light due to the unevenness of the surface becomes strong, so that surface haze is easily developed, and the refraction and scattering of light. There is a concern about the decrease in transmittance due to the loss of light due to light, and it is easy to obtain antiglare properties due to scattered light on the surface of the antiglare hard coat layer, but it is difficult to suppress the phenomenon that the antiglare hard coat film becomes whitish and cloudy. For this reason, transparency and transmission clarity are liable to decrease.

また、上記最大断面高さの下限値については特に制約はないが、最大断面高さが1.0μm未満の場合、フィルム表面の凹凸が小さくなりすぎるため、防眩ハードコート層表面での散乱光による防眩性が得られ難くなる。   Further, the lower limit of the maximum cross-sectional height is not particularly limited, but when the maximum cross-sectional height is less than 1.0 μm, the unevenness of the film surface becomes too small, and thus the scattered light on the surface of the antiglare hard coat layer. It becomes difficult to obtain the antiglare property due to.

また、上記平均傾斜角が1度よりも大きい(1度超)場合、表面の凹凸に起因する光の屈折、散乱が強まるため表面ヘイズが発現し易くなり、光の屈折、散乱による光のロスにより透過率の低下が懸念されるとともに、防眩ハードコート層表面での散乱光による防眩性は得られ易くなるが、防眩ハードコートフィルムが白っぽく濁る現象を抑えられ難くなることから透明性や透過鮮明度が低下しやすいという問題がある。   Further, when the average inclination angle is larger than 1 degree (more than 1 degree), refraction and scattering of light due to surface unevenness is enhanced, so that surface haze is easily developed, and light loss due to refraction and scattering of light. As a result, there is concern about a decrease in transmittance, and it is easy to obtain antiglare properties due to scattered light on the surface of the antiglare hard coat layer, but it is difficult to suppress the phenomenon that the antiglare hard coat film becomes whitish and turbid. In addition, there is a problem that transmission clarity tends to decrease.

従って、本発明においては、防眩ハードコートフィルムの表面の上記最大断面高さは、1.0μm以上3.0μm以下であることが好ましく、より好ましくは上記最大断面高さが1.2μm以上2.5μm以下である。   Therefore, in the present invention, the maximum cross-sectional height of the surface of the antiglare hard coat film is preferably 1.0 μm or more and 3.0 μm or less, and more preferably the maximum cross-sectional height is 1.2 μm or more and 2 or less. .5 μm or less.

また、防眩ハードコートフィルムの表面の上記平均傾斜角は1度以下であることが好ましく、より好ましくは上記平均傾斜角が0.9度であり、更に好ましくは上記平均傾斜角が0.7度以下である。上記平均傾斜角の下限値については特に制約はないが、防眩性の観点から、0.1度以上であることが好ましい。   The average inclination angle of the surface of the antiglare hard coat film is preferably 1 degree or less, more preferably the average inclination angle is 0.9 degree, and further preferably the average inclination angle is 0.7 degree. Less than or equal to degrees. Although there is no restriction | limiting in particular about the lower limit of the said average inclination angle, From a glare-proof viewpoint, it is preferable that it is 0.1 degree or more.

なお、本発明において、「評価領域」とは測定領域のことである。
また、本発明の防眩ハードコートフィルムにおいては、JIS K 7105−1981に基づく透過鮮明度測定装置を用いて4つの光学櫛(巾2mm、1mm、0.5mm、0.125mm)を通して測定される透過鮮明度の合計値が280%以上であり、各光学櫛を通して測定される透過鮮明度の値が各々70%以上とすることにより、像鮮明度が高く、塗膜の白っぽさ(白ぼけ)を低減しコントラスト低下を抑え、ディスプレイの視認性を向上させることができる。
In the present invention, the “evaluation region” is a measurement region.
Moreover, in the anti-glare hard coat film of the present invention, it is measured through four optical combs (width 2 mm, 1 mm, 0.5 mm, 0.125 mm) using a transmission sharpness measuring device based on JIS K 7105-1981. The total value of the transmission definition is 280% or more, and the transmission definition value measured through each optical comb is 70% or more, so that the image definition is high and the whiteness of the coating film (white) It is possible to reduce blur and suppress a decrease in contrast and improve the visibility of the display.

本発明に用いることのできる透明フィルムは、特に限定はないが、たとえば、ポリエチレンテレフタレートフィルム(PET;屈折率1.665)、ポリカーボネートフィルム(PC;屈折率1.582)、トリアセチルセルロースフィルム(TAC;屈折率1.485)、ノルボルネンフィルム(NB;屈折率1.525)などが使用でき、フィルム厚さも特に制限はないが、25μm〜250μm程度が汎用的に使用されている。一般的な、電離放射線硬化樹脂の屈折率は、1.52程度であるので、視認性を高くするためには前記樹脂の屈折率に近いTACフィルム、NBフィルムが好ましく、また、価格的にはPETフィルムが好ましい。   The transparent film that can be used in the present invention is not particularly limited. For example, a polyethylene terephthalate film (PET; refractive index 1.665), a polycarbonate film (PC; refractive index 1.582), a triacetyl cellulose film (TAC) ; Refractive index 1.485), norbornene film (NB; refractive index 1.525) can be used, and the film thickness is not particularly limited, but about 25 μm to 250 μm is generally used. Since the refractive index of a general ionizing radiation curable resin is about 1.52, a TAC film or NB film close to the refractive index of the resin is preferable in order to increase the visibility. A PET film is preferred.

本発明に用いる樹脂は、被膜を形成する樹脂であれば特に制限なく用いることができるが、特に防眩ハードコート層表面にハード性(鉛筆硬度、耐擦傷性)を付与し、また防眩ハードコート層形成時に多量の熱を必要としないという点で、電離放射線硬化型樹脂が好ましい。   The resin used in the present invention can be used without particular limitation as long as it is a resin that forms a film. In particular, it imparts hard properties (pencil hardness, scratch resistance) to the surface of the antiglare hard coat layer, and also provides antiglare hard. An ionizing radiation curable resin is preferred in that a large amount of heat is not required when forming the coat layer.

電離放射線硬化型樹脂は、電子線または紫外線等を照射することによって硬化する透明な樹脂であれば、特に限定されるものではなく、例えば、ウレタンアクリレート系樹脂、ポリエステルアクリレート系樹脂、及びエポキシアクリレート系樹脂等の中から適宜選択することができる。電離放射線硬化型樹脂として好ましいものは、分子内に2個以上の(メタ)アクリロイル基を有する紫外線硬化可能な多官能アクリレートからなるものが挙げられる。分子内に2個以上の(メタ)アクリロイル基を有する紫外線硬化可能な多官能アクリレートの具体例としては、ネオペンチルグリコールジ(メタ)アクリレート、1,6−ヘキサンジオールジ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、ジトリメチロールプロパンテトラ(メタ)アクリレート、ペンタエリスリトールテトラ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート等のポリオールポリアクリレート、ビスフェノールAジグリシジルエーテルのジアクリレート、ネオペンチルグリコールジグリシジルエーテルのジアクリレート、1,6−ヘキサンジオールジグリシジルエーテルのジ(メタ)アクリレートなどのエポキシ(メタ)アクリレート、多価アルコールと多価カルボン酸及び/またはその無水物とアクリル酸とをエステル化することによって得ることができるポリエステル(メタ)アクリレート、多価アルコール、多価イソシアネート及び水酸基含有(メタ)アクリレートを反応させることによって得られるウレタン(メタ)アクリレート、ポリシロキサンポリ(メタ)アクリレート等を挙げることができる。   The ionizing radiation curable resin is not particularly limited as long as it is a transparent resin that is cured by irradiation with an electron beam or ultraviolet rays. For example, a urethane acrylate resin, a polyester acrylate resin, and an epoxy acrylate resin It can select suitably from resin etc. Preferred examples of the ionizing radiation curable resin include those composed of an ultraviolet curable polyfunctional acrylate having two or more (meth) acryloyl groups in the molecule. Specific examples of the UV curable polyfunctional acrylate having two or more (meth) acryloyl groups in the molecule include neopentyl glycol di (meth) acrylate, 1,6-hexanediol di (meth) acrylate, and trimethylol. Polyol polyacrylates such as propane tri (meth) acrylate, ditrimethylolpropane tetra (meth) acrylate, pentaerythritol tetra (meth) acrylate, pentaerythritol tri (meth) acrylate, dipentaerythritol hexa (meth) acrylate, bisphenol A diglycidyl Epoxys such as diacrylate of ether, diacrylate of neopentyl glycol diglycidyl ether, di (meth) acrylate of 1,6-hexanediol diglycidyl ether ( A) Polyester (meth) acrylate, polyhydric alcohol, polyisocyanate and hydroxyl group-containing (meta) which can be obtained by esterifying acrylate, polyhydric alcohol and polyhydric carboxylic acid and / or anhydride and acrylic acid ) Urethane (meth) acrylate obtained by reacting acrylate, polysiloxane poly (meth) acrylate, and the like.

前記の紫外線硬化可能な多官能アクリレートは単独または2種以上混合して用いてもよく、その含有量は防眩ハードコート層用塗料の樹脂固形分に対して、好ましくは50〜95重量%である。なお、上記の多官能(メタ)アクリレートの他に、防眩ハードコート層用塗料の樹脂固形分に対して、好ましくは10重量%以下の2−ヒドロキシ(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、グリシジル(メタ)アクリレート等の単官能アクリレートを添加することもできる。   The ultraviolet curable polyfunctional acrylate may be used alone or in combination of two or more, and the content thereof is preferably 50 to 95% by weight with respect to the resin solid content of the antiglare hard coat layer coating material. is there. In addition to the polyfunctional (meth) acrylate, preferably 10% by weight or less of 2-hydroxy (meth) acrylate, 2-hydroxypropyl (meth) based on the resin solid content of the antiglare hard coat layer coating. ) Monofunctional acrylates such as acrylate and glycidyl (meth) acrylate can also be added.

また、防眩ハードコート層には硬度を調整する目的で使用される重合性オリゴマーを添加することができる。このようなオリゴマーとしては、末端(メタ)アクリレートポリメチル(メタ)アクリレート、末端スチリルポリ(メタ)アクリレート、末端(メタ)アクリレートポリスチレン、末端(メタ)アクリレートポリエチレングリコール、末端(メタ)アクリレートアクリロニトリル−スチレン共重合体、末端(メタ)アクリレートスチレン−メチルメタクリレート共重合体などのマクロモノマーを挙げることができ、その含有量は防眩ハードコート用塗料中の樹脂固形分に対して、好ましくは5〜50重量%である。
本発明に用いる微粒子を形成する材料としては、特に限定はなく、例えば、シリカ(屈折率1.420〜1.460)、塩化ビニル樹脂(屈折率1.530)、アクリル樹脂(屈折率1.490)、(メタ)アクリル樹脂(屈折率1.520〜1.530)ポリスチレン樹脂(屈折率1.590)、メラミン樹脂(屈折率1.650)、ポリエチレン樹脂、ポリカーボネート樹脂、アクリル−スチレン共重合樹脂(屈折率1.490〜1.590)等が挙げることができ、微粒子は単独で用いてもよいし、或いは2種以上を併用することも可能である。また、前記微粒子の屈折率も制限はないが、本発明の効果をより一層得るには、前記微粒子は防眩ハードコート層に用いられる樹脂の屈折率に対し、屈折率の差が0.001〜0.200である微粒子を用いることが好ましく、とくに屈折率の差が0.001〜0.100である微粒子を用いることがより好ましい。
In addition, a polymerizable oligomer used for the purpose of adjusting the hardness can be added to the antiglare hard coat layer. Examples of such oligomers include terminal (meth) acrylate polymethyl (meth) acrylate, terminal styryl poly (meth) acrylate, terminal (meth) acrylate polystyrene, terminal (meth) acrylate polyethylene glycol, terminal (meth) acrylate acrylonitrile-styrene copolymer. Macromonomers such as polymers and terminal (meth) acrylate styrene-methyl methacrylate copolymers can be mentioned, and the content thereof is preferably 5 to 50 weights based on the resin solid content in the antiglare hard coat coating material. %.
The material for forming the fine particles used in the present invention is not particularly limited. For example, silica (refractive index 1.420 to 1.460), vinyl chloride resin (refractive index 1.530), acrylic resin (refractive index 1.. 490), (meth) acrylic resin (refractive index 1.520 to 1.530), polystyrene resin (refractive index 1.590), melamine resin (refractive index 1.650), polyethylene resin, polycarbonate resin, acrylic-styrene copolymer. Resin (refractive index 1.490-1.590) etc. can be mentioned, A microparticle may be used independently or it is also possible to use 2 or more types together. Further, the refractive index of the fine particles is not limited, but in order to further obtain the effects of the present invention, the fine particles have a refractive index difference of 0.001 with respect to the refractive index of the resin used for the antiglare hard coat layer. It is preferable to use fine particles having a refractive index of ˜0.200, and it is more preferable to use fine particles having a refractive index difference of 0.001 to 0.100.

また、本発明において、防眩ハードコート層の塗膜厚さは、防眩ハードコート層を構成する微粒子の平均粒径の0.5〜1.5倍であることが好ましく、より好ましくは0.8〜1.2倍である。また、好ましい微粒子の平均粒径は1.0〜4.0μmであり、高い鉛筆硬度を付与するために微粒子の平均粒径は3.0〜4.0μmであることがより好ましい。   In the present invention, the coating thickness of the antiglare hard coat layer is preferably 0.5 to 1.5 times the average particle size of the fine particles constituting the antiglare hard coat layer, more preferably 0. .8 to 1.2 times. The average particle size of the fine particles is preferably 1.0 to 4.0 μm, and the average particle size of the fine particles is more preferably 3.0 to 4.0 μm in order to impart high pencil hardness.

塗膜厚さが防眩ハードコート層を構成する微粒子の平均粒径の0.5倍未満であると、微粒子が塗膜中に固定されなくなり、塗膜表面のハード性が著しく悪くなる。
一方塗膜厚さが防眩ハードコート層を構成する微粒子の平均粒径の1.5倍を超えると防眩性が全く得られなくなる。なお、前記微粒子の平均粒径は、例えばレーザー回折散乱法で測定することができる。
When the coating film thickness is less than 0.5 times the average particle size of the fine particles constituting the antiglare hard coat layer, the fine particles are not fixed in the coating film, and the hardness of the coating film surface is remarkably deteriorated.
On the other hand, when the coating thickness exceeds 1.5 times the average particle size of the fine particles constituting the antiglare hard coat layer, no antiglare property can be obtained. The average particle diameter of the fine particles can be measured by, for example, a laser diffraction scattering method.

また、微粒子の平均粒径が4μm以上の場合は、防眩ハードコート層の塗膜厚さを前記微粒子の平均粒径の0.5〜1.5倍と設定した場合に必要以上の防眩性が付与され塗膜表面での外光の散乱が大きくなり、光の散乱により表面が白っぽくなり、ディスプレイの視認性を著しく低下させる。一方、微粒子の平均粒径が1.0μmより小さい場合は塗膜厚さを薄くしなければならないため、ハード性に欠ける。   Further, when the average particle size of the fine particles is 4 μm or more, the antiglare is more than necessary when the coating thickness of the antiglare hard coat layer is set to 0.5 to 1.5 times the average particle size of the fine particles. And the scattering of external light on the surface of the coating film becomes large, and the surface becomes whitish due to the scattering of light, and the visibility of the display is remarkably lowered. On the other hand, when the average particle size of the fine particles is smaller than 1.0 μm, the coating film thickness must be reduced, so that the hard property is lacking.

本発明において微粒子は防眩ハードコート層中に前記樹脂100重量部に対して0.05〜3重量部配合することが好ましく、より好ましくは0.075〜1重量部配合することであり、更に好ましくは0.1〜0.5重量部配合することである。   In the present invention, the fine particles are preferably blended in the antiglare hard coat layer in an amount of 0.05 to 3 parts by weight, more preferably 0.075 to 1 part by weight based on 100 parts by weight of the resin. Preferably, 0.1 to 0.5 part by weight is blended.

微粒子の配合量が、前記樹脂100重量部に対して0.05重量部未満の場合は、防眩ハードコート層の塗膜厚さを微粒子の平均粒径の0.5〜1.5倍と設定した場合に防眩性が全く得られない。また、微粒子の配合量が、前記樹脂100重量部に対して3重量部を超えるとヘイズ値が高くなり透過率、コントラストが低下する。
本発明において、含フッ素重合性化合物とは不飽和基を有する重合型フッ素系界面活性剤またはフッ素系表面改質剤であって、これらの重合型フッ素系界面活性剤またはフッ素系表面改質剤はフルオロ脂肪族基および親水性基を有していることが好ましく、防汚性の点からパーフルオロアルキレンエーテル鎖を有していることがより好ましい。
When the amount of fine particles is less than 0.05 parts by weight with respect to 100 parts by weight of the resin, the coating thickness of the antiglare hard coat layer is 0.5 to 1.5 times the average particle size of the fine particles. When set, no antiglare property is obtained. Moreover, when the compounding quantity of microparticles exceeds 3 weight part with respect to 100 weight part of said resin, a haze value will become high and the transmittance | permeability and contrast will fall.
In the present invention, the fluorine-containing polymerizable compound is a polymerizable fluorine-based surfactant or fluorine-based surface modifier having an unsaturated group, and these polymerized fluorine-based surfactant or fluorine-based surface modifier. Preferably has a fluoroaliphatic group and a hydrophilic group, and more preferably has a perfluoroalkylene ether chain from the viewpoint of antifouling properties.

本発明の効果を変えない範囲で、レベリング剤、防汚剤(含フッ素重合性樹脂を除く)、消泡剤、滑剤、紫外線吸収剤、光安定剤、重合禁止剤、湿潤分散剤、レオロジーコントロール剤、酸化防止剤、帯電防止剤、導電剤などを必要に応じて含有してもよい。   Leveling agents, antifouling agents (excluding fluorine-containing polymerizable resins), antifoaming agents, lubricants, ultraviolet absorbers, light stabilizers, polymerization inhibitors, wetting and dispersing agents, and rheology control as long as the effects of the present invention are not changed. An agent, an antioxidant, an antistatic agent, a conductive agent and the like may be contained as necessary.

従って以上のとおり、本発明の防眩ハードコートフィルムは、透明フィルム上に、微粒子、樹脂及び含フッ素重合性化合物を含有する防眩ハードコート層を設けてなる防眩ハードコートフィルムであって、該防眩ハードコートフィルムの表面の評価領域内の高さの平均値をゼロ(零)としたときの、評価領域内の高さ最大値と評価領域内の高さ最小値との差で表わす最大断面高さが1.0〜3.0μmであり、かつ該防眩ハードコートフィルム表面の凹凸の平均傾斜角が1度以下であり、JIS K 7105−1981に基づく透過鮮明度測定装置を用いて4つの光学櫛(巾2mm、1mm、0.5mm、0.125mm)を通して測定される透過鮮明度の合計値が280%以上であり、各光学櫛を通して測定される透過鮮明度の値が各々70%以上であることを特徴とし、この場合、前記微粒子は平均粒径1.0〜4.0μmであり、且つ前記防眩ハードコート層の塗膜厚さが前記微粒子の平均粒径の0.5〜1.5倍であり、前記微粒子の配合量が前記樹脂100重量部に対して0.05〜3重量部であることが好ましい。また、該防眩ハードコートフィルムのヘイズ値は0.1〜5.0%であることが好ましく、より好ましくはヘイズ値が0.1〜3.5%であり、更に好ましくはヘイズ値が0.1〜2.0%である。さらに、前記含フッ素重合性化合物の配合量が前記樹脂100重量部に対して、0.1〜10重量部(固形分換算)であることが好ましい。   Therefore, as described above, the antiglare hard coat film of the present invention is an antiglare hard coat film in which an antiglare hard coat layer containing fine particles, a resin and a fluorine-containing polymerizable compound is provided on a transparent film, Expressed by the difference between the maximum height in the evaluation area and the minimum height in the evaluation area when the average height in the evaluation area on the surface of the antiglare hard coat film is zero. The maximum cross-sectional height is 1.0 to 3.0 μm, the average inclination angle of the irregularities on the surface of the antiglare hard coat film is 1 degree or less, and a transmission sharpness measuring device based on JIS K 7105-1981 is used. The total value of transmitted sharpness measured through four optical combs (width 2 mm, 1 mm, 0.5 mm, 0.125 mm) is 280% or more, and the transmitted sharpness values measured through each optical comb are each 7 In this case, the fine particles have an average particle size of 1.0 to 4.0 μm, and the coating thickness of the antiglare hard coat layer is 0. 0 of the average particle size of the fine particles. It is preferable that the compounding amount of the fine particles is 0.05 to 3 parts by weight with respect to 100 parts by weight of the resin. The haze value of the antiglare hard coat film is preferably 0.1 to 5.0%, more preferably the haze value is 0.1 to 3.5%, and still more preferably the haze value is 0. 0.1-2.0%. Furthermore, it is preferable that the compounding quantity of the said fluorine-containing polymeric compound is 0.1-10 weight part (solid content conversion) with respect to 100 weight part of said resin.

上記防眩ハードコート層は、前記樹脂と微粒子等を溶剤に溶解、分散した塗料を透明フィルム上に塗工乾燥して形成することができる。溶媒としては、前記樹脂の溶解性に応じて適宜選択でき、少なくとも固形分(樹脂、微粒子、触媒、硬化剤、その他添加剤) を均一に溶解あるいは分散できる溶媒であればよい。そのような溶媒としては、例えば、ケトン類(アセトン、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン等)、エーテル類(ジオキサン、テトラヒドロフラン等)、脂肪族炭化水素類(ヘキサン等)、脂環式炭化水素類(シクロヘキサン等)、芳香族炭化水素類(トルエン、キシレン等)、ハロゲン化炭素類(ジクロロメタン、ジクロロエタン等) 、エステル類( 酢酸メチル、酢酸エチル、酢酸ブチル等)、アルコール類(メタノール、エタノール、イソプロパノール、ブタノール、シクロヘキサノール等)、セロソルブ類(メチルセロソルブ、エチルセロソルブ等)、セロソルブアセテート類、スルホキシド類、アミド類などが例示できる。また、溶媒は単独で使用しても混合して使用してもよい。   The antiglare hard coat layer can be formed by applying and drying a paint obtained by dissolving and dispersing the resin and fine particles in a solvent on a transparent film. The solvent can be appropriately selected depending on the solubility of the resin, and may be any solvent that can uniformly dissolve or disperse at least solids (resin, fine particles, catalyst, curing agent, and other additives). Examples of such solvents include ketones (acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, etc.), ethers (dioxane, tetrahydrofuran, etc.), aliphatic hydrocarbons (hexane, etc.), alicyclic hydrocarbons ( Cyclohexane, etc.), aromatic hydrocarbons (toluene, xylene, etc.), halogenated carbons (dichloromethane, dichloroethane, etc.), esters (methyl acetate, ethyl acetate, butyl acetate, etc.), alcohols (methanol, ethanol, isopropanol, Butanol, cyclohexanol, etc.), cellosolves (methyl cellosolve, ethyl cellosolve, etc.), cellosolve acetates, sulfoxides, amides and the like. Further, the solvents may be used alone or in combination.

防眩ハードコート層の塗工方法については特に限定しないが、グラビア塗工、マイクログラビア塗工、バー塗工、スライドダイ塗工、スロットダイ塗工、デイップコートなど、塗膜厚さの調整が容易な方式で塗工が可能である。なお、塗工した防眩ハードコート層の膜厚は、防眩フィルム断面写真を顕微鏡等で観察し、塗膜界面から表面までを実測することにより測定可能である。   The coating method of the anti-glare hard coat layer is not particularly limited, but the coating thickness can be adjusted by gravure coating, micro gravure coating, bar coating, slide die coating, slot die coating, dip coating, etc. Coating is possible with an easy method. The film thickness of the coated antiglare hard coat layer can be measured by observing a cross-sectional photograph of the antiglare film with a microscope or the like and actually measuring from the coating film interface to the surface.

また、本発明の防眩ハードコートフィルムにおいては、60度鏡面光沢度が70%以上95%以下であり、かつ20度鏡面光沢度が30%以上90%以下であることが好ましく、さらに視感透過率(透過Y値)が92.00以上であることが好ましい。   In the antiglare hard coat film of the present invention, the 60 ° specular gloss is preferably 70% or more and 95% or less, and the 20 ° specular gloss is preferably 30% or more and 90% or less. The transmittance (transmission Y value) is preferably 92.00 or more.

なお、本発明の防眩ハードコートフィルムにおいては、透明フィルム上に、微粒子および樹脂を含有する防眩ハードコート層以外に、反射防止層や帯電防止層のような機能層を設けることも可能である。但し、このような機能層を設けることにより、表面の起伏がキャンセルされ、所望の防眩性が得られなくなる可能性があるので、微粒子を含有した防眩ハードコート層の上に機能層を設ける場合は、機能層の膜厚は0.5μm以下とすることが望ましい。   In the antiglare hard coat film of the present invention, a functional layer such as an antireflection layer or an antistatic layer can be provided on the transparent film in addition to the antiglare hard coat layer containing fine particles and a resin. is there. However, by providing such a functional layer, surface undulations may be canceled and the desired anti-glare property may not be obtained, so a functional layer is provided on the anti-glare hard coat layer containing fine particles. In this case, the thickness of the functional layer is desirably 0.5 μm or less.

また、防眩ハードコート層の下に機能層を設けることも可能である。この機能層としては、例えば、反射防止機能を向上するための屈折率制御層、基材と防眩ハードコート層の密着性を得るための易接着層、帯電防止層などである。   It is also possible to provide a functional layer under the antiglare hard coat layer. Examples of the functional layer include a refractive index control layer for improving the antireflection function, an easy adhesion layer for obtaining adhesion between the base material and the antiglare hard coat layer, and an antistatic layer.

また、本発明の防眩ハードコートフィルムにおいては、透明フィルム上に、微粒子および樹脂を含有する防眩ハードコート層以外に、反射防止層や帯電防止層のような機能層を、微粒子を含有した防眩ハードコート層の上に設ける場合、防眩ハードコート層の塗膜厚さを、防眩ハードコート層を構成する微粒子の平均粒径以下に設定した場合は、防眩ハードコート層と機能層を合計した塗膜厚さが、防眩ハードコート層を構成する微粒子の平均粒径の0.5〜1.5倍であることが必要である。   Further, in the antiglare hard coat film of the present invention, in addition to the antiglare hard coat layer containing fine particles and a resin, a functional layer such as an antireflection layer or an antistatic layer is contained on the transparent film. When provided on the antiglare hard coat layer, when the coating thickness of the antiglare hard coat layer is set below the average particle size of the fine particles constituting the antiglare hard coat layer, it functions as an antiglare hard coat layer. The total coating thickness of the layers needs to be 0.5 to 1.5 times the average particle size of the fine particles constituting the antiglare hard coat layer.

なお、本発明の防眩ハードコートフィルムは、透明フィルム上の微粒子および樹脂を含有する防眩ハードコート層の上に、反射防止層や帯電防止層のような機能層を設けた場合においては、防眩ハードコートフィルムの表面、つまり機能層の表面の評価領域内の高さの平均値をゼロ(零)としたときの、評価領域内の高さ最大値と評価領域内の高さ最小値との差で表わす最大断面高さが1.0〜3.0μmであり、かつ該機能層の表面の凹凸の平均傾斜角が1度以下であることが必要である。   In addition, when the antiglare hard coat film of the present invention is provided with a functional layer such as an antireflection layer or an antistatic layer on the antiglare hard coat layer containing the fine particles and the resin on the transparent film, The maximum height in the evaluation area and the minimum height in the evaluation area when the average height in the evaluation area of the surface of the antiglare hard coat film, that is, the surface of the functional layer is zero. It is necessary that the maximum cross-sectional height represented by the difference between the thickness of the functional layer is 1.0 to 3.0 μm and the average inclination angle of the irregularities on the surface of the functional layer is 1 degree or less.

以下、実施例にて本発明を例証するが、本発明を限定することを意図するものではない。なお、微粒子の平均粒径は、レーザー回折粒度測定器SALD2200(島津製作所製)で測定した。塗膜厚さは、キーエンス(株)製の走査型電子顕微鏡にて断面を観察し、計測した。また、特に断らない限り、以下に記載する「部」及び「%」は、それぞれ「重量部」及び「重量%」を表す。   The following examples illustrate the invention, but are not intended to limit the invention. The average particle size of the fine particles was measured with a laser diffraction particle size analyzer SALD2200 (manufactured by Shimadzu Corporation). The thickness of the coating film was measured by observing the cross section with a scanning electron microscope manufactured by Keyence Corporation. Unless otherwise specified, “parts” and “%” described below represent “parts by weight” and “% by weight”, respectively.

[実施例1]
<塗料調製>
酢酸ブチル45.00gにアクリル─スチレン共重合粒子(積水化成品工業(株)社製、平均粒径4.0μm、屈折率:1.525)0.17gを添加し十分攪拌した。この液にアクリル系紫外線硬化樹脂(日本合成化学工業(株)社製、屈折率:1.52)50.83gとイルガキュア184(光重合開始剤、(株)チバスペシャリティーケミカル社製)2.75g、含フッ素重合性化合物(DIC(株)社製)0.50gを添加し十分攪拌し塗料を調製した。
<防眩フィルム作製>
Fuji TAC(トリアセチルセルロースフィルム、富士フィルム(株)社製)に上記塗料をマイヤーバー#4(RDS社製)で塗工し、80℃で1分間乾燥後、350mJ/cmの紫外線(光源:Fusion Japan社製UVランプ)を照射し硬化した。得られた塗膜の厚さは3.6μmであった。
[Example 1]
<Preparation of paint>
0.17 g of acrylic-styrene copolymer particles (manufactured by Sekisui Plastics Co., Ltd., average particle size 4.0 μm, refractive index: 1.525) was added to 45.00 g of butyl acetate and sufficiently stirred. 50.83 g of acrylic ultraviolet curable resin (manufactured by Nippon Synthetic Chemical Industry Co., Ltd., refractive index: 1.52) and Irgacure 184 (photopolymerization initiator, manufactured by Ciba Specialty Chemical Co., Ltd.) 75 g and 0.50 g of a fluorine-containing polymerizable compound (manufactured by DIC Corporation) were added and sufficiently stirred to prepare a coating material.
<Preparation of antiglare film>
The above-mentioned paint was applied to Fuji TAC (triacetylcellulose film, manufactured by Fuji Film Co., Ltd.) with Meyer bar # 4 (manufactured by RDS), dried at 80 ° C. for 1 minute, and then irradiated with 350 mJ / cm 2 ultraviolet light (light source) : UV lamp manufactured by Fusion Japan) and cured. The thickness of the obtained coating film was 3.6 μm.

[実施例2]
<塗料調製>
酢酸ブチル45.00gにアクリル─スチレン共重合粒子(積水化成品工業(株)社製、平均粒径4.0μm、屈折率:1.525)0.17gを添加し十分攪拌した。この液にアクリル系紫外線硬化樹脂(日本合成化学工業(株)社製、屈折率:1.52)51.33gとイルガキュア184(光重合開始剤、(株)チバスペシャリティーケミカル社製)2.75g、含フッ素重合性化合物(DIC(株)社製)0.75gを添加し十分攪拌し塗料を調製した。
<防眩フィルム作製>
実施例1と同様の方法で防眩フィルムを作製した。得られた塗膜の厚さは3.6μmであった。
[Example 2]
<Preparation of paint>
0.17 g of acrylic-styrene copolymer particles (manufactured by Sekisui Plastics Co., Ltd., average particle size 4.0 μm, refractive index: 1.525) was added to 45.00 g of butyl acetate and sufficiently stirred. 51.33 g of an acrylic ultraviolet curable resin (manufactured by Nippon Synthetic Chemical Industry Co., Ltd., refractive index: 1.52) and Irgacure 184 (photopolymerization initiator, manufactured by Ciba Specialty Chemicals Co., Ltd.) 75 g and 0.75 g of a fluorine-containing polymerizable compound (manufactured by DIC Corporation) were added and sufficiently stirred to prepare a coating material.
<Preparation of antiglare film>
An antiglare film was produced in the same manner as in Example 1. The thickness of the obtained coating film was 3.6 μm.

[実施例3]
<塗料調製>
酢酸ブチル45.00gにアクリル─スチレン共重合粒子(積水化成品工業(株)社製、平均粒径4.0μm、屈折率:1.525)0.17gを添加し十分攪拌した。この液にアクリル系紫外線硬化樹脂(日本合成化学工業(株)社製、屈折率:1.52)50.33gとイルガキュア184(光重合開始剤、(株)チバスペシャリティーケミカル社製)2.75g、含フッ素重合性化合物(DIC(株)社製)1.75gを添加し十分攪拌し塗料を調製した。
<防眩フィルム作製>
実施例1と同様の方法で防眩フィルムを作製した。得られた塗膜の厚さは3.6μmであった。
[Example 3]
<Preparation of paint>
0.17 g of acrylic-styrene copolymer particles (manufactured by Sekisui Plastics Co., Ltd., average particle size 4.0 μm, refractive index: 1.525) was added to 45.00 g of butyl acetate and sufficiently stirred. 50.33 g of an acrylic UV curable resin (manufactured by Nippon Synthetic Chemical Industry Co., Ltd., refractive index: 1.52) and Irgacure 184 (photopolymerization initiator, manufactured by Ciba Specialty Chemical Co., Ltd.) 75 g and 1.75 g of a fluorine-containing polymerizable compound (manufactured by DIC Corporation) were added and sufficiently stirred to prepare a coating material.
<Preparation of antiglare film>
An antiglare film was produced in the same manner as in Example 1. The thickness of the obtained coating film was 3.6 μm.

[比較例1]
<塗料調製>
酢酸ブチル45.00gにアクリル─スチレン共重合粒子(積水化成品工業(株)社製、平均粒径4.0μm、屈折率:1.525)0.17gを添加し十分攪拌した。この液にアクリル系紫外線硬化樹脂(日本合成化学工業(株)社製、屈折率:1.52)52.08gとイルガキュア184(光重合開始剤、(株)チバスペシャリティーケミカル社製)2.75g、を添加し十分攪拌し塗料を調製した。
<防眩フィルム作製>
実施例1と同様の方法で防眩フィルムを作製した。得られた塗膜の厚さは3.6μmであった。
[Comparative Example 1]
<Preparation of paint>
0.17 g of acrylic-styrene copolymer particles (manufactured by Sekisui Plastics Co., Ltd., average particle size 4.0 μm, refractive index: 1.525) was added to 45.00 g of butyl acetate and sufficiently stirred. In this liquid, 52.08 g of an acrylic UV curable resin (manufactured by Nippon Synthetic Chemical Industry Co., Ltd., refractive index: 1.52) and Irgacure 184 (photopolymerization initiator, manufactured by Ciba Specialty Chemicals Co., Ltd.) 75 g was added and stirred well to prepare a paint.
<Preparation of antiglare film>
An antiglare film was produced in the same manner as in Example 1. The thickness of the obtained coating film was 3.6 μm.

以上のようにして作製された実施例及び比較例の各防眩ハードコートフィルムを次の項目について評価し、その結果を纏めて後記表に示した。   The antiglare hard coat films of Examples and Comparative Examples produced as described above were evaluated for the following items, and the results are summarized in the table below.

(1)最大断面高さ
(株)菱化システム製の三次元表面粗計「VertScan2.0」を用いて測定した。測定により得られた領域断面曲線パラメータの評価領域内の高さの平均値(Ave)がゼロのときの、評価領域内の高さ最大値(P)と評価領域内の高さ最小値(V)との差から最大断面高さ(Pt)を求めた。測定条件の設定は以下のとおりである。
<光学条件>
Camera:SONY HR−50 1/3型
Objective:10×(10倍)
Tube:1×Body
Relay:No Relay
Filter:530white
・光量調節:Lampの値が50〜95の範囲内に入るよう自動で実施。
<測定条件>
Mode:Wave
Size:640×480
Range(μm):Start(5)、Stop(−10)
(1) Maximum cross-sectional height It was measured using a three-dimensional surface roughness meter “VertScan2.0” manufactured by Ryoka System Co., Ltd. The maximum height value (P) in the evaluation region and the minimum height value (V) in the evaluation region when the average value (Ave) of the height in the evaluation region of the region cross-sectional curve parameter obtained by measurement is zero. ) To determine the maximum cross-sectional height (Pt). The measurement conditions are set as follows.
<Optical conditions>
Camera: SONY HR-50 1/3 type Objective: 10 x (10 times)
Tube: 1 x Body
Relay: No Relay
Filter: 530 white
-Light quantity adjustment: Automatically performed so that the value of Lamp falls within the range of 50-95.
<Measurement conditions>
Mode: Wave
Size: 640 × 480
Range (μm): Start (5), Stop (−10)

(2)平均傾斜角
(株)菱化システム製の三次元表面粗計「VertScan2.0」を用いて、フィルム表面の凹凸部の平均傾斜角を測定した。
(2) Average inclination angle The average inclination angle of the concavo-convex portions on the film surface was measured using a three-dimensional surface roughness meter “VertScan2.0” manufactured by Ryoka System Co., Ltd.

(3)ヘイズ値
村上色彩技術研究所製ヘイズメーター「HM150」を用いて測定した。
(3) Haze value The haze value was measured using a haze meter “HM150” manufactured by Murakami Color Research Laboratory.

(4)視感透過率(透過Y値)
村上色彩技術研究所製「積分球高速分光透過測定システムDOT-3」を用い、JISZ8722に順ずる方法にて測定を実施した。
(4) Luminous transmittance (transmission Y value)
Murakami Color Research Laboratory “integrated sphere high-speed spectral transmission measurement system DOT-3” was used, and the measurement was carried out according to JISZ8722.

ここで視感透過率とは、Y=K∫S(λ)y(λ)T(λ)dλから求められる。なお、S(λ):波長400〜700nmの分光分布、y(λ):等色関数、T(λ):分光立体角透過率、Y:視感透過率である。   Here, the luminous transmittance is obtained from Y = K∫S (λ) y (λ) T (λ) dλ. S (λ): spectral distribution of wavelength 400 to 700 nm, y (λ): color matching function, T (λ): spectral solid angle transmittance, Y: luminous transmittance.

(5)透過鮮明度
スガ試験機(株)製写像性測定器「ICM−1DP」を使用し測定を実施した。測定は2mm、1mm、0.5mm、0.125mmの巾をもつ光学櫛を用いて行い、各巾における測定値とその総和を算出した。
(5) Transmission clarity Measurement was carried out using a Suga Test Instruments Co., Ltd. image clarity measuring device “ICM-1DP”. The measurement was performed using an optical comb having widths of 2 mm, 1 mm, 0.5 mm, and 0.125 mm, and the measured values at each width and the sum thereof were calculated.

(6)光沢度(20度、60度)
村上色彩技術研究所製グロスメーター(GM−3D)を使用し、塗工反対面に黒色のビニールテープ(日東ビニールテープ、PROSELFNo.21(幅広))を貼り20度または、60度光沢度を測定した。
(6) Glossiness (20 degrees, 60 degrees)
Using a gloss meter (GM-3D) manufactured by Murakami Color Research Laboratory, apply a black vinyl tape (Nitto Vinyl Tape, PROSELF No. 21 (wide)) to the opposite side of the coating and measure the glossiness at 20 or 60 degrees. did.

(7)鉛筆硬度
新東科学社製HEIDON14 を使用し、JIS K 5400に準拠して実施した。
(7) Pencil hardness It carried out based on JISK5400 using HEIDON14 by Shinto Scientific.

(8)ギラツキ
全面緑色表示させた解像度150ppiの液晶表示体(LCD)の上に各防眩フィルムを重ね、画面のキラキラ光る輝きの発生度合いを目視で評価した。なお、LCD表面には予めギラツキの発生しないクリアタイプのハードコートフィルムを設置した。ギラツキがないもの及びギラツキがわずかであるものを「○」、ギラツキが大きく視認性が悪化するものを「×」とした。
(8) Glitter Each anti-glare film was layered on a liquid crystal display (LCD) having a resolution of 150 ppi that was displayed in green on the entire surface, and the degree of occurrence of glittering screen was visually evaluated. In addition, a clear type hard coat film which does not generate glare was previously set on the LCD surface. The case where there was no glare and the case where the glare was slight was designated as “◯”, and the case where the glare was large and the visibility deteriorated was designated as “X”.

(9)白ボケ、白っぽさ
外光の写り込みによる白ボケは、塗工反対面に黒色のビニールテープ(日東ビニールテープ、PROSELFNo.21(幅広))を貼りマクベス濃度計で黒濃度として測定した。2.15以上を「○」、2.10以上2.15未満を「△」、2.10未満を「×」とした。また、透過光による塗膜の白っぽさは、塗工面を観測者側にして防眩ハードコートフィルムを介して、白色蛍光灯を見たときの、内部ヘイズによりフィルム中で光が拡散し塗膜が白っぽくなる状態を目視で評価した。白っぽさがないもの及びわずかなものを「○」、白っぽさが若干強いものを「△」、塗膜が白っぽくなるものを「×」とした。
(9) White bokeh, whitish White bokeh due to reflection of external light is applied with a black vinyl tape (Nitto Vinyl Tape, PROSELF No. 21 (wide)) on the opposite side of the coating as black density using a Macbeth densitometer. It was measured. 2.15 or more is “◯”, 2.10 or more and less than 2.15 is “Δ”, and less than 2.10 is “x”. In addition, the whitishness of the coating film due to transmitted light is that light diffuses in the film due to internal haze when the white fluorescent lamp is viewed through an anti-glare hard coat film with the coated surface facing the observer. The state in which the coating became whitish was visually evaluated. Those with no whiteness and slight whiteness were indicated with “◯”, those with a slight whiteness were indicated with “△”, and those with a white coating film were indicated with “X”.

(10)防眩性
防眩性は幅1mm間隔で直線を10本引いたものを防眩ハードコートフィルムの塗工面に写り込ませ、塗工面を観測者側にして防眩ハードコートフィルムを介して線幅を見たときの、光の散乱により線幅がぼやけて見え難くなる状態を目視で評価した。線幅を認識できないものを「○」、線幅を認識できるものを「×」とした。
(10) Anti-glare property The anti-glare property is obtained by reflecting 10 lines drawn at 1 mm width on the coated surface of the anti-glare hard coat film, with the coated surface facing the observer, and through the anti-glare hard coat film. When the line width was viewed, the state in which the line width was blurred and difficult to see due to light scattering was visually evaluated. “◯” indicates that the line width cannot be recognized, and “X” indicates that the line width can be recognized.

(11)耐擦傷性試験
#0000のスチールウールを用いて1000gf/cmの荷重をかけながら10往復し、傷の発生の有無を確認した。
(11) Scratch resistance test Using a # 0000 steel wool, it was reciprocated 10 times while applying a load of 1000 gf / cm 2 , and the presence or absence of scratches was confirmed.

(12)防汚性
防汚性は防眩ハードコートフィルムの塗工面にマジックで線を引き、マジックで引いた線を布で拭き取ったときに容易に拭き取れるものを「◎」、拭き取れるものを「○」、拭き取り難いものを「△」、拭き取れないものを「×」とした。
(12) Antifouling The antifouling property is “◎”, which can be wiped off easily when a line is drawn with a magic on the coated surface of the antiglare hard coat film and the line drawn with the magic is wiped off with a cloth. Was “◯”, those that were difficult to wipe off were “Δ”, and those that could not be wiped were “X”.

Figure 2013257359
Figure 2013257359

また、実施例1〜3はいずれも、防眩ハードコート層に用いる微粒子の平均粒径、その配合量、防眩ハードコート層の塗膜厚さ及び防眩ハードコートフィルムのヘイズ値、含フッ素重合性化合物の配合量がそれぞれ本発明の所望の範囲内であり、良好な像鮮明度、視感透過率、光沢度、良好な耐擦傷性、防汚性を有し、なお且つギラツキ、白ボケ、白っぽさを抑制した防眩ハードコートフィルムが得られた。これに対して、防眩ハードコート層に用いる微粒子の平均粒径、その配合量、防眩ハードコート層の塗膜厚さ及び防眩ハードコートフィルムのヘイズ値が本発明の所望の範囲であるが、含フッ素重合性化合物を含有していない比較例1では耐擦傷性が得られなかった。   Also, in all of Examples 1 to 3, the average particle diameter of fine particles used in the antiglare hard coat layer, the blending amount thereof, the coating thickness of the antiglare hard coat layer, the haze value of the antiglare hard coat film, and fluorine content The compounding amount of the polymerizable compound is within the desired range of the present invention, and has good image definition, luminous transmittance, glossiness, good scratch resistance and antifouling property, and also has glare, white An anti-glare hard coat film with reduced blur and whitishness was obtained. On the other hand, the average particle diameter of the fine particles used for the antiglare hard coat layer, the blending amount thereof, the coating thickness of the antiglare hard coat layer, and the haze value of the antiglare hard coat film are within the desired ranges of the present invention. However, in Comparative Example 1 containing no fluorine-containing polymerizable compound, no scratch resistance was obtained.

Claims (3)

透明フィルム上に、微粒子、樹脂及び含フッ素重合性化合物を含有する防眩ハードコート層を設けてなる防眩ハードコートフィルムであって、該防眩ハードコートフィルムの表面の評価領域内の高さの平均値をゼロ(零)としたときの、評価領域内の高さ最大値と評価領域内の高さ最小値との差で表わす最大断面高さが1.0〜3.0μmであるとともに、該防眩ハードコートフィルム表面の凹凸の平均傾斜角が1度以下であり、かつ該防眩ハードコートフィルムのJIS K 7105−1981に基づく透過鮮明度測定装置を用いて4つの光学櫛(巾2mm、1mm、0.5mm、0.125mm)を通して測定される透過鮮明度の値が各々70%以上であることを特徴とする防眩ハードコートフィルム。   An anti-glare hard coat film comprising an anti-glare hard coat layer containing fine particles, a resin and a fluorine-containing polymerizable compound on a transparent film, the height within the evaluation region of the surface of the anti-glare hard coat film And the maximum cross-sectional height represented by the difference between the maximum height value in the evaluation region and the minimum height value in the evaluation region when the average value is zero (zero) is 1.0 to 3.0 μm The optical antiglare hard coat film surface has an average inclination angle of 1 degree or less, and four optical combs (widths) using a transmission sharpness measuring device based on JIS K 7105-1981 of the antiglare hard coat film. An anti-glare hard coat film characterized by having a transmission sharpness value measured through 2 mm, 1 mm, 0.5 mm, and 0.125 mm) of 70% or more. 前記含フッ素重合性化合物が、フッ素フルオロ脂肪族基及び親水性基を有することを特徴とする請求項記載の防眩ハードコートフィルム。 The antiglare hard coat film according to claim 1, wherein the fluorine-containing polymerizable compound has a fluorine fluoroaliphatic group and a hydrophilic group. 前記含フッ素重合性化合物の含有量がハードコート層中の樹脂100重量部に対して、0.1〜10重量部(固形分)であることを特徴とする請求項1〜2記載の防眩ハードコートフィルム。 The antiglare according to claim 1 or 2, wherein the content of the fluorine-containing polymerizable compound is 0.1 to 10 parts by weight (solid content) with respect to 100 parts by weight of the resin in the hard coat layer. Hard coat film.
JP2012131660A 2012-06-11 2012-06-11 Antidazzle hard coat film Pending JP2013257359A (en)