JP2013086451A - Heat shield decorative sheet - Google Patents
Heat shield decorative sheet Download PDFInfo
- Publication number
- JP2013086451A JP2013086451A JP2011231515A JP2011231515A JP2013086451A JP 2013086451 A JP2013086451 A JP 2013086451A JP 2011231515 A JP2011231515 A JP 2011231515A JP 2011231515 A JP2011231515 A JP 2011231515A JP 2013086451 A JP2013086451 A JP 2013086451A
- Authority
- JP
- Japan
- Prior art keywords
- film layer
- layer
- decorative sheet
- resin
- overlay film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、主に住居や店舗、船舶等の外装扉の表層に用いるのをはじめとし、窓枠、テラス、車庫等の屋外に使われる、耐侯性が高く、光線遮蔽効果を有する遮熱化粧シートに関する。 The present invention is mainly used for the outer layer of exterior doors of houses, stores, ships, etc., and is used for outdoor such as window frames, terraces, garages, etc. Regarding the sheet.
従来、玄関扉の表層等については耐候性のあるオレフィン系化粧シートが使われてきたが、実際の屋外暴露や促進耐候性試験にて耐侯性は評価しており、太陽光の紫外光領域に対しては処方を施した設計ではあったが、赤外光領域の熱の吸収に対しては、考慮されていなかった。 Conventionally, olefin-based decorative sheets with weather resistance have been used for the surface of entrance doors, etc., but weather resistance has been evaluated by actual outdoor exposure and accelerated weather resistance tests, and in the ultraviolet region of sunlight. On the other hand, although it was the design which gave the prescription, it was not considered about the absorption of the heat | fever of an infrared region.
実際に使用されていると、耐候性としては満足されるものであったが、太陽光の赤外光領域の熱の吸収によって、蓄熱作用が発生し、結果として基材に伝わる事で、熱膨張が発生し、表裏の温度差によって反りが発生する慢性的な問題については、解決されないままであった。 When actually used, the weather resistance was satisfactory, but the heat storage effect occurred due to the absorption of heat in the infrared light region of sunlight, and as a result, it was transferred to the base material. The chronic problem of swelling and warping due to temperature differences between the front and back remained unresolved.
本発明はこのような問題を解決するためになされたものであり、すなわちその課題とするところは、短納期で安価に製造可能であり、耐候性や耐摩耗性、耐水性等の各物性に優れ、かつ光線遮蔽効果を有しながら、しかも絵柄の深み等の意匠性にも優れた遮熱化粧シートを提供することにある。 The present invention has been made to solve such a problem, that is, the problem is that it can be manufactured at a low cost with a short delivery time, and has various physical properties such as weather resistance, wear resistance, and water resistance. An object of the present invention is to provide a heat-insulating decorative sheet that has an excellent light shielding effect and also has excellent design properties such as the depth of a pattern.
本発明はこの課題を解決したものであり、すなわちその請求項1記載の発明は、着色ベースフィルム層、印刷層、オーバーレイフィルム層を少なくともこの順に積層してなる遮熱化粧シートにおいて、前記着色ベースフィルム層の着色顔料として酸化チタンを用い、前記印刷層の顔料としてイソインドリノン、ジスアゾ、ポリアゾ、ジケトピロロピロール、キイナクリドン、フタロシアニン、酸化チタンの少なくとも一つ以上を用いることを特徴とする遮熱化粧シートである。 The present invention solves this problem, that is, the invention according to claim 1 is a heat-shielding decorative sheet in which a colored base film layer, a printed layer, and an overlay film layer are laminated in this order. Titanium oxide is used as a coloring pigment for the film layer, and at least one of isoindolinone, disazo, polyazo, diketopyrrolopyrrole, quinacridone, phthalocyanine, and titanium oxide is used as the pigment for the printing layer. It is a decorative sheet.
またその請求項2記載の発明は、前記オーバーレイフィフィルム層としてホモまたはランダムポリプロピレン系樹脂に紫外線吸収剤とヒンダードアミン系光安定剤を添加したものを用い、さらに前記オーバーレイフィフィルム層の表面側に、アクリルポリオールとヘキサメチレンジイソシアネートに紫外線吸収剤とヒンダードアミン系光安定剤を添加したコーティング層を設けてなることを特徴とする請求項1記載の遮熱化粧シートである。 Further, the invention according to claim 2 uses, as the overlay film layer, a homo- or random polypropylene resin added with an ultraviolet absorber and a hindered amine light stabilizer, and further on the surface side of the overlay film layer, 2. The heat-shielding decorative sheet according to claim 1, wherein a coating layer obtained by adding an ultraviolet absorber and a hindered amine light stabilizer to acrylic polyol and hexamethylene diisocyanate is provided.
またその請求項3記載の発明は、前記オーバーレイフィフィルム層としてポリメチルメタアクリル樹脂に紫外線吸収剤とヒンダードフェノール系酸化防止剤を添加したものを用い、さらに前記印刷層とオーバーレイフィルム層の間にアクリル樹脂、ポリエステル樹脂、塩化ビニル=酢酸ビニル共重合樹脂の少なくとも1つ以上からなる接着剤層を設けてなることを特徴とする請求項1記載の遮熱化粧シートである。 The invention according to claim 3 uses, as the overlay film layer, a polymethylmethacrylic resin added with an ultraviolet absorber and a hindered phenol antioxidant, and further between the print layer and the overlay film layer. The thermal insulation decorative sheet according to claim 1, wherein an adhesive layer comprising at least one of acrylic resin, polyester resin, and vinyl chloride = vinyl acetate copolymer resin is provided.
太陽光の赤外光領域の熱の吸収によって、蓄熱作用が発生し、結果として基材に伝わる事で、熱膨張が発生し、表裏の温度差によって反りが発生する。本発明はその請求項1記載の発明により、着色ベースフィルム層と印刷層に特定の顔料を用いる事で、赤外光領域の反射率を一定以上に上げる事が可能となり、光線遮蔽効果を得て、反りの発生を防止することを可能とする。 Thermal absorption occurs due to the absorption of heat in the infrared light region of sunlight, and as a result, thermal expansion occurs due to transmission to the base material, and warpage occurs due to a temperature difference between the front and back sides. According to the first aspect of the present invention, by using a specific pigment for the colored base film layer and the printing layer, the reflectance in the infrared light region can be increased to a certain level or more, and a light shielding effect is obtained. Therefore, it is possible to prevent warping.
またその請求項2記載の発明により、オーバーレイフィルム層の樹脂を特定しさらにその表面側に特定の樹脂のコーティング層を設けることで経時の耐候性と光線遮蔽効果の維持とを可能とした。 According to the invention described in claim 2, the weather resistance over time and the light shielding effect can be maintained by specifying the resin of the overlay film layer and further providing a coating layer of the specific resin on the surface side.
またその請求項3記載の発明により、オーバーレイフィルム層の樹脂を特定しさらに印刷層とオーバーレイフィルム層との間に特定の樹脂の接着剤層を設けることで経時の層間強度と光線遮蔽効果の維持とを可能とした。 According to the invention of claim 3, by specifying the resin of the overlay film layer and further providing an adhesive layer of the specific resin between the printing layer and the overlay film layer, the interlayer strength over time and the light shielding effect can be maintained. And made it possible.
以下、本発明を図面に基づき詳細に説明する。図1に本発明の遮熱化粧シートの一実施例の断面の形状を示す。着色ベースフィルム層1、印刷層2、オーバーレイフィルム層3からなり、適宜接着剤層4やコーティング層5を設けてなる。 Hereinafter, the present invention will be described in detail with reference to the drawings. FIG. 1 shows a cross-sectional shape of one embodiment of the heat-shielding decorative sheet of the present invention. It consists of a colored base film layer 1, a printing layer 2, and an overlay film layer 3, and is provided with an adhesive layer 4 and a coating layer 5 as appropriate.
本発明における着色ベースフィルム層1としては、塩化ビニル樹脂代替として取り扱いが容易なホモまたはランダムポリプロピレン系樹脂またはポリエチレン樹脂が好適に用いられる。また、ヒンダートフェノール系酸化防止剤、紫外線吸収剤、ヒンダートアミン系光安定剤などを適宜するのが好適である。 As the colored base film layer 1 in the present invention, a homo- or random polypropylene-based resin or polyethylene resin that is easy to handle as a substitute for vinyl chloride resin is preferably used. In addition, it is preferable to appropriately use a hindered phenol-based antioxidant, an ultraviolet absorber, a hindered amine-based light stabilizer, and the like.
本発明における着色ベースフィルム層1に用いる顔料としては、酸化チタンが用いられる。これにより、赤外光領域の反射率を一定以上に上げる事が可能となる。 Titanium oxide is used as the pigment used for the colored base film layer 1 in the present invention. Thereby, the reflectance in the infrared light region can be increased to a certain level or more.
本発明における印刷層2としては、前記着色ベースフィルム層1に好適なインキを用いて設ければ良い。具体的には前記ベースフィルム層1がポリプロピレン樹脂であれば、ウレタン樹脂と塩化ビニル=酢酸ビニル共重合樹脂の混合物が好適に用いられる。 What is necessary is just to provide the printing layer 2 in this invention using the ink suitable for the said colored base film layer 1. FIG. Specifically, if the base film layer 1 is a polypropylene resin, a mixture of urethane resin and vinyl chloride = vinyl acetate copolymer resin is preferably used.
本発明における印刷層2に用いる顔料としては、イソインドリノン、ジスアゾ、ポリアゾ、ジケトピロロピロール、キイナクリドン、フタロシアニン、酸化チタンの少なくとも一つ以上を用いる。これにより、赤外光領域の反射率を一定以上に上げる事が可能となる。 As the pigment used for the printing layer 2 in the present invention, at least one of isoindolinone, disazo, polyazo, diketopyrrolopyrrole, quinacridone, phthalocyanine, and titanium oxide is used. Thereby, the reflectance in the infrared light region can be increased to a certain level or more.
本発明におけるオーバーフィルム層3としては、さらにこの表面にコーティング層5を設ける場合は、前記着色ベースフィルム層1や印刷層2との層間密着を考慮して樹脂を選択すればよく、具体的には前記着色ベースフィルム層1がホモまたはランダムポリプロピレン系樹脂またはポリエチレン樹脂であるなら同様のホモまたはランダムポリプロピレン系樹脂またはポリエチレン樹脂が好ましく、紫外線吸収剤とヒンダードアミン系光安定剤を添加するのが好適である。
一方、オーバーレイフィルム層3が表面層となる場合は、ポリメチルメタアクリル樹脂を用いるのが好ましく、紫外線吸収剤とヒンダードフェノール系酸化防止剤を添加するのが好適であり、層間密着を考慮して印刷層2との間にアクリル樹脂、ポリエステル樹脂、塩化ビニル=酢酸ビニル共重合樹脂の少なくとも1つ以上からなる接着剤層4を設けるのが好ましい。
As the over film layer 3 in the present invention, when the coating layer 5 is further provided on the surface, a resin may be selected in consideration of interlayer adhesion with the colored base film layer 1 and the printing layer 2. If the colored base film layer 1 is a homo- or random polypropylene resin or polyethylene resin, the same homo- or random polypropylene resin or polyethylene resin is preferable, and it is preferable to add an ultraviolet absorber and a hindered amine light stabilizer. is there.
On the other hand, when the overlay film layer 3 is a surface layer, it is preferable to use a polymethylmethacrylic resin, and it is preferable to add an ultraviolet absorber and a hindered phenol-based antioxidant, considering interlayer adhesion. It is preferable to provide an adhesive layer 4 made of at least one of acrylic resin, polyester resin, and vinyl chloride = vinyl acetate copolymer resin between the printing layer 2 and the printed layer 2.
着色ベースフィルム層1として、ポリエチレン樹脂100重量部に、ヒンダードフェノール系酸化防止剤を3重量部、紫外線吸収剤を1重量部、ヒンダードアミン系光安定剤を1重量部、酸化チタンを23重量部添加して、厚み55μmに製膜した。 As colored base film layer 1, 100 parts by weight of polyethylene resin, 3 parts by weight of hindered phenol antioxidant, 1 part by weight of UV absorber, 1 part by weight of hindered amine light stabilizer, 23 parts by weight of titanium oxide This was added to form a film having a thickness of 55 μm.
前記着色ベースフィルム1の表面に印刷層2として、ウレタン樹脂と塩化ビニル=酢酸ビニル共重合樹脂を7:3の割合で混合したもの100重量部に、ヘキサメチレンジイソシアネートとイソホロンジイソシアネートを2:8の混合からなる硬化剤を3重量部添加して、イソインドリノン、ポリアゾ、フタロシアニンからなる顔料を3重量部添加してインキとし、木目柄をグラビア印刷にて印刷した。 As a printed layer 2 on the surface of the colored base film 1, a mixture of urethane resin and vinyl chloride = vinyl acetate copolymer resin in a ratio of 7: 3 is mixed with 100 parts by weight of hexamethylene diisocyanate and isophorone diisocyanate in a ratio of 2: 8. 3 parts by weight of a curing agent composed of a mixture was added, 3 parts by weight of a pigment composed of isoindolinone, polyazo, and phthalocyanine was added to form an ink, and a wood grain pattern was printed by gravure printing.
前記着色ベースフィルム1の印刷層2を設けた面に、オーバーレイフィルム層3として、ランダムポリプロピレン系樹脂を用い100重量部に対して紫外線吸収剤0.5重量部とヒンダードアミン系光安定剤0.3重量部を添加したものを溶融押出により設け、乾燥後の厚みが70μmとなるようにして設けた。 On the surface of the colored base film 1 on which the printing layer 2 is provided, as an overlay film layer 3, a random polypropylene resin is used and 0.5 parts by weight of an ultraviolet absorber and a hindered amine light stabilizer 0.3 with respect to 100 parts by weight. What added a weight part was provided by melt extrusion, and it provided so that the thickness after drying might be set to 70 micrometers.
最後に、前記オーバーレイフィルム層3の表面にアクリルポリオール100重量部に対してヘキサメチレンジイソシアネート10重量部と紫外線吸収剤5重量部とヒンダードアミン系光安定剤5重量部を添加したものをコーティングにより9μmとなるようにして設け、遮熱化粧シートを作成した。 Finally, the surface of the overlay film layer 3 was added with 10 parts by weight of hexamethylene diisocyanate, 5 parts by weight of an ultraviolet absorber and 5 parts by weight of a hindered amine light stabilizer with respect to 100 parts by weight of an acrylic polyol. Thus, a thermal insulation decorative sheet was prepared.
着色ベースフィルム1と印刷層2は実施例1と同様に作成した。前記印刷層2の表面にアクリル−ポリエステル−塩化ビニル=酢酸ビニル共重合樹脂系接着剤(アクリル/ポリエステル/塩酢ビ=30/30/30)をグラビアコート法により乾燥後の塗布量1.5g/m2に塗工して接着剤層4を形成し、オーバーレイフィルム層3としてポリメチルメタアクリル樹脂100重量部に紫外線吸収剤3重量部とヒンダードフェノール系酸化防止剤1重量部からなる厚さ50μmのガラス転移点が104℃の透明アクリル樹脂フィルムを、フィルム表面温度120℃の条件で熱ラミネートして、遮熱化粧シートを作成した。 The colored base film 1 and the printing layer 2 were prepared in the same manner as in Example 1. 1.5 g of coating amount after drying acrylic-polyester-vinyl chloride = vinyl acetate copolymer resin adhesive (acrylic / polyester / vinyl acetate = 30/30/30) on the surface of the printing layer 2 by a gravure coating method. / M2 is applied to form an adhesive layer 4, and the overlay film layer 3 is composed of 100 parts by weight of polymethylmethacrylic resin, 3 parts by weight of an ultraviolet absorber and 1 part by weight of a hindered phenolic antioxidant. A transparent acrylic resin film having a glass transition point of 50 ° C. having a glass transition temperature of 50 μm was heat-laminated under the condition of a film surface temperature of 120 ° C. to prepare a heat insulating decorative sheet.
<比較例>
着色ベースフィルム層1に用いる顔料をカーボンブラック、印刷層2に用いる顔料をカーボンブラックとし、その他の材料構成は実施例1と同様のものを用いて遮熱化粧シートを作成した。
<Comparative example>
The pigment used for the colored base film layer 1 was carbon black, the pigment used for the printing layer 2 was carbon black, and the other material configurations were the same as in Example 1 to produce a heat shield decorative sheet.
<性能比較1>
実施例1と実施例2と比較例1の遮熱化粧シートに関し、(株)日立ハイテクノロジーズ製U−4100形分光光度計を用い、遮熱化粧シートについて、波長340nm〜2500nmの光に対する反射率を測定した。結果を表1に示す。
<Performance comparison 1>
About the heat-insulating decorative sheet of Example 1, Example 2 and Comparative Example 1, using a U-4100 type spectrophotometer manufactured by Hitachi High-Technologies Corporation, the heat-insulating decorative sheet is reflected with respect to light having a wavelength of 340 nm to 2500 nm. Was measured. The results are shown in Table 1.
<性能比較2>
また、縦20cm横11cm厚みが0.6mmの無塗装鋼板に対して、接着剤を用いて、片面のみ遮熱化粧シートを貼り合わせたものについて、ハロゲン球を真上から15cm離したところから、遮熱化粧シートが照射面になるよう30分間照射し続け、鋼板表裏を1分毎に温度を記録し、最大値を測定した。結果を表2に示す。
<Performance comparison 2>
In addition, for a non-coated steel sheet having a length of 20 cm and a width of 11 cm and a thickness of 0.6 mm, using an adhesive, only one side of the heat-shielding decorative sheet was bonded, from where the halogen bulb was separated from the top by 15 cm, Irradiation was continued for 30 minutes so that the heat-shielding decorative sheet became the irradiated surface, the temperature was recorded on the front and back of the steel sheet every minute, and the maximum value was measured. The results are shown in Table 2.
表1より、近赤外光領域(780nm〜2000nm)においての反射率が高く、遮熱性に優れている事が確認された。表2より、遮熱性に優れている事が確認された。 From Table 1, it was confirmed that the reflectance in the near-infrared light region (780 nm to 2000 nm) is high and the heat shielding property is excellent. From Table 2, it was confirmed that the heat shielding property was excellent.
本発明の遮熱化粧シートは、主に住居や店舗、船舶等の外装扉の表層に用いるのをはじめとし、窓枠、テラス、車庫等の屋外に利用可能である。 The heat-insulating decorative sheet of the present invention can be used not only for the surface layer of exterior doors of residences, stores, ships, etc., but also outdoors such as window frames, terraces, and garages.
1…着色ベースフィルム層
2…印刷層
3…オーバーレイフィルム層
4…接着剤層
5…コーティング層
DESCRIPTION OF SYMBOLS 1 ... Colored base film layer 2 ... Printing layer 3 ... Overlay film layer 4 ... Adhesive layer 5 ... Coating layer
Claims (3)
前記着色ベースフィルム層の着色顔料として酸化チタンを用い、
前記印刷層の顔料としてイソインドリノン、ジスアゾ、ポリアゾ、ジケトピロロピロール、キイナクリドン、フタロシアニン、酸化チタンの少なくとも一つ以上を用いることを特徴とする遮熱化粧シート。 In the heat insulating decorative sheet formed by laminating at least the coloring base film layer, the printing layer, and the overlay film layer in this order,
Titanium oxide is used as a color pigment for the colored base film layer,
At least one or more of isoindolinone, disazo, polyazo, diketopyrrolopyrrole, quinacridone, phthalocyanine, and titanium oxide is used as a pigment for the printing layer.