JP2013001649A - Toothpaste composition - Google Patents

Toothpaste composition Download PDF

Info

Publication number
JP2013001649A
JP2013001649A JP2011131699A JP2011131699A JP2013001649A JP 2013001649 A JP2013001649 A JP 2013001649A JP 2011131699 A JP2011131699 A JP 2011131699A JP 2011131699 A JP2011131699 A JP 2011131699A JP 2013001649 A JP2013001649 A JP 2013001649A
Authority
JP
Japan
Prior art keywords
dentifrice composition
fatty acid
component
divalent metal
mass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
JP2011131699A
Other languages
Japanese (ja)
Inventor
Noritaka Takahashi
典敬 高橋
Atsushi Yamagishi
敦 山岸
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kao Corp
Original Assignee
Kao Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kao Corp filed Critical Kao Corp
Priority to JP2011131699A priority Critical patent/JP2013001649A/en
Publication of JP2013001649A publication Critical patent/JP2013001649A/en
Withdrawn legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide a toothpaste composition for immediately and sufficiently sealing openings in dentinal tubules in the surface of exposed dentine and capable of effectively preventing pain caused by dentine hypersensitivity.SOLUTION: The toothpaste composition includes the following components (A), (B) and (C). They are: (A) a low water-soluble powder selected from a fatty acid divalent metal salt (A-1) derived from a 12-18C saturated fatty acid, a fatty acid acyllysine (A-2) having an acyl group derived from a 12-18C saturated fatty acid, and a fatty acid acyltaurine divalent metal salt (A-3) having an acyl group derived from a 12-18C saturated fatty acid; (B) powder cellulose (B-1), or carboxymethylcellulose having an etherification degree of 0.1 to 0.6 or its salt (B-2); and (C) water.

Description

本発明は、特定の水難溶性粉体を含有する歯磨組成物に関する。   The present invention relates to a dentifrice composition containing a specific poorly water-soluble powder.

象牙質知覚過敏症は、歯面に機械的、温度的或いは化学的刺激が与えられた際に疼痛が誘発される疾患である。歯周炎の進行や加齢、強い歯磨処理等によって、歯肉の退縮や歯牙のエナメル質の損傷が生じ、これらに被覆されていた歯牙の象牙質が露出することが要因となる。従来より、このような象牙質知覚過敏症を予防又は治療するために種々の提案がなされている。   Dentine hypersensitivity is a disease in which pain is induced when a mechanical, thermal or chemical stimulus is applied to the tooth surface. The progression of periodontitis, aging, strong dentifrice treatment, etc. cause gingival retraction and tooth enamel damage, and this is due to the exposure of the dentin of the covered tooth. Conventionally, various proposals have been made to prevent or treat such dentin hypersensitivity.

例えば、特許文献1には、重炭酸カリウム及び塩化カリウムの中から選択されたカリウム塩を有効量で施用する方法が開示されており、カリウムイオンの作用によって知覚神経自体の活動の低下を図り、疼痛を緩和させるものである。   For example, Patent Document 1 discloses a method of applying an effective amount of a potassium salt selected from potassium bicarbonate and potassium chloride, and the activity of the sensory nerve itself is reduced by the action of potassium ions. It relieves pain.

一方、再石灰化を促進して歯を元の健康な状態に戻すことも、象牙質知覚過敏症の発症を抑制するのに寄与し得る。例えば、特許文献2には、再石灰化成分として、フッ素化合物と、酸化亜鉛やクエン酸亜鉛、ステアリン酸亜鉛等の水難溶性亜鉛化合物を含有する口腔用組成物が開示されている。   On the other hand, promoting remineralization to return the teeth to their original healthy state can also contribute to suppressing the onset of dentine hypersensitivity. For example, Patent Document 2 discloses an oral composition containing, as a remineralization component, a fluorine compound and a poorly water-soluble zinc compound such as zinc oxide, zinc citrate, and zinc stearate.

他方、象牙質知覚過敏症の発症メカニズムとしては、動水力学説、すなわち、露出した象牙質の表面では象牙質細管が開口し、外部からの刺激がこの開口部から象牙質細管内の組織液へと伝達され、組織液の流動が細管内の奥端部に位置する歯髄神経に到達して、疼痛が知覚されるという説が支持されている。こうした説に基づき、象牙質知覚過敏症の発症を抑制すべく、例えば、特許文献3には、アルミニウム化合物を含有する第一液と、リン酸化合物等を含有する助剤とに分離構成した知覚過敏症用塗布剤が開示されており、第一液と助剤との反応によってアルミニウム塩を沈着させることで、象牙質細管の開口部を物理的に封鎖する試みがなされている。また、特許文献4に開示されている象牙質知覚過敏予防・治療剤は、乳酸アルミニウム等の金属塩とポリオールリン酸エステル等との反応により形成されるコロイドによって、特許文献2に開示された口腔用組成物と同様に、象牙質細管の開口部の封鎖を図っている。   On the other hand, the onset mechanism of hypersensitivity of the dentin is the hydrodynamic theory, that is, the dentinal tubule opens on the exposed surface of the dentin, and external stimuli pass from this opening to the tissue fluid in the dentinal tubule. The theory that the flow of tissue fluid is transmitted and reaches the pulp nerve located at the innermost end in the tubule and pain is perceived is supported. Based on these theories, for example, Patent Document 3 discloses a perception that is separated into a first liquid containing an aluminum compound and an auxiliary containing a phosphoric acid compound and the like in order to suppress the onset of dentin hypersensitivity. An application agent for hypersensitivity has been disclosed, and an attempt has been made to physically seal the opening of a dentin tubule by depositing an aluminum salt by a reaction between a first liquid and an auxiliary agent. Moreover, the agent for preventing and treating dentine hypersensitivity disclosed in Patent Document 4 is an oral cavity disclosed in Patent Document 2 by a colloid formed by a reaction between a metal salt such as aluminum lactate and a polyol phosphate. As with the composition for use, the opening of the dentinal tubule is blocked.

特表昭61−501389号公報JP-T 61-501389 特開2000−247852号公報Japanese Patent Laid-Open No. 2000-247852 特開平6−116153号公報JP-A-6-116153 特開平5−117157号公報JP-A-5-117157

しかしながら、特許文献1に記載の知覚神経の活動を低下させる方法は、知覚神経周辺のイオンバランスを変化させて神経を鈍感にさせるため、充分に疼痛を低減できないおそれがある。また、特許文献2に記載の口腔用組成物がもたらす再石灰化は緩和な作用であるため、象牙質知覚過敏症の発症を即効的に抑制するのは困難である。   However, since the method of reducing the activity of sensory nerves described in Patent Document 1 changes the ion balance around the sensory nerves and makes the nerves insensitive, there is a possibility that pain cannot be reduced sufficiently. Moreover, since the remineralization which the composition for oral cavity of patent document 2 brings about is a mild effect, it is difficult to suppress onset of dentine hypersensitivity promptly.

こうしたことから、象牙質知覚過敏症の発現を防止する手段として、特許文献3〜4に記載の剤のように、象牙質細管の開口部を封鎖して、象牙質細管内の組織液の流動を抑制することが提案されている。しかしながら、特許文献3は乳酸アルミニウム塩を形成させるため、この塩を象牙質細管の開口部に効果的に沈着させることは難しく、特許文献4に記載のコロイドによっても、象牙質細管の開口部を充分に封鎖することは難しい。   Therefore, as a means for preventing the development of dentinal hypersensitivity, like the agents described in Patent Documents 3 to 4, the openings of the dentinal tubules are blocked, and the flow of tissue fluid in the dentinal tubules is prevented. It has been proposed to suppress. However, since Patent Document 3 forms an aluminum lactate salt, it is difficult to effectively deposit this salt on the opening of the dentinal tubule, and the opening of the dentinal tubule is also formed by the colloid described in Patent Document 4. It is difficult to fully block it.

したがって、本発明の課題は、露出した象牙質の表面における象牙質細管の開口部を即効的かつ充分に封鎖して、象牙質知覚過敏症に起因する痛みを効果的に防止することのできる歯磨組成物を提供することにある。   Accordingly, an object of the present invention is to provide a dentifrice that can quickly and sufficiently seal the opening of the dentin tubule on the surface of the exposed dentin, thereby effectively preventing pain caused by dentine hypersensitivity. It is to provide a composition.

そこで本発明者らは、特定の脂肪酸二価金属塩、脂肪酸アシルリシン、脂肪酸アシルタウリン二価金属塩から選ばれる水難溶性粉体と、粉末セルロース又は特定のカルボキシメチルセルロースとを水とともに併用することで、象牙質細管の開口部を即効的かつ充分に封鎖することのできる歯磨組成物が得られることを見出した。   Therefore, the present inventors, by using a water-insoluble powder selected from a specific fatty acid divalent metal salt, fatty acid acyl lysine, fatty acid acyl taurine divalent metal salt, and powdered cellulose or specific carboxymethyl cellulose together with water, It has been found that a dentifrice composition capable of immediately and sufficiently sealing the opening of the dentin tubule is obtained.

すなわち、本発明は、次の成分(A)、(B)並びに(C):
(A)炭素数12〜18の飽和脂肪酸を由来とする脂肪酸二価金属塩(A−1)、炭素数12〜18の飽和脂肪酸を由来とするアシル基を有する脂肪酸アシルリシン(A−2)、及び炭素数12〜18の飽和脂肪酸を由来とするアシル基を有する脂肪酸アシルタウリン二価金属塩(A−3)から選ばれる水難溶性粉体、
(B)粉末セルロース(B−1)又はエーテル化度が0.1〜0.6のカルボキシメチルセルロース若しくはその塩(B−2)、並びに
(C)水
を含有する歯磨組成物を提供するものである。
That is, the present invention includes the following components (A), (B) and (C):
(A) a fatty acid divalent metal salt (A-1) derived from a saturated fatty acid having 12 to 18 carbon atoms, a fatty acid acyl lysine (A-2) having an acyl group derived from a saturated fatty acid having 12 to 18 carbon atoms, And a poorly water-soluble powder selected from fatty acid acyl taurine divalent metal salts (A-3) having an acyl group derived from a saturated fatty acid having 12 to 18 carbon atoms,
(B) Powdered cellulose (B-1) or carboxymethylcellulose having a degree of etherification of 0.1 to 0.6 or a salt thereof (B-2), and (C) a dentifrice composition containing water. is there.

本発明の歯磨組成物によれば、歯ブラシ等を用いてブラッシングすることにより、露出した象牙質の表面に存在する象牙質細管の開口部を即効的かつ充分に封鎖することができる。したがって、本発明の歯磨組成物を用いれば、象牙質知覚過敏症に起因する痛みを効果的に防止することが可能である。   According to the dentifrice composition of the present invention, the opening of the dentin tubule present on the exposed dentin surface can be immediately and sufficiently sealed by brushing with a toothbrush or the like. Therefore, if the dentifrice composition of this invention is used, it is possible to prevent effectively the pain resulting from dentine hypersensitivity.

図1(a)は、象牙質細管の開口部の殆どが露出している象牙質の表面のマイクロスコープ写真であり、図1(b)は、象牙質の開口部の殆どが封鎖されている象牙質の表面のマイクロスコープ写真である。FIG. 1 (a) is a microscopic photograph of the surface of the dentin where most of the openings of the dentinal tubules are exposed, and FIG. 1 (b) is where most of the openings of the dentin are blocked. It is a microscope photograph of the surface of dentin.

以下、本発明について詳細に説明する。
本発明の歯磨組成物は、炭素数12〜18の飽和脂肪酸を由来とする脂肪酸二価金属塩(A−1)、炭素数12〜18の飽和脂肪酸を由来とするアシル基を有する脂肪酸アシルリシン(A−2)、及び炭素数12〜18の飽和脂肪酸を由来とするアシル基を有する脂肪酸アシルタウリン二価金属塩(A−3)から選ばれる水難溶性粉体(A)を含有する。本発明で用いる水難溶性粉体(A)は、25℃において100gの水に対して溶解する量が0.1g未満である粉体であり、好ましくは溶解する量が0.05g未満である粉体、又は水に実質的に溶解しない粉体である。また、かかる水難溶性粉体(A)は、延展性に優れており、ブラッシングの際、歯ブラシ等の毛先が露出した象牙質の表面に直接的又は間接的に負荷をかけながら接触することで、歯磨組成物に含まれる水難溶性粉体(A)が象牙質細管の開口部を封鎖することができる。水難溶性粉体(A)は、延展して伸びが良いことから、本発明の歯磨組成物の使用により、象牙質細管の開口部の周辺に展着しながら延展すると考えられ、象牙質細管の開口部を効果的に封鎖することができる。
Hereinafter, the present invention will be described in detail.
The dentifrice composition of the present invention comprises a fatty acid divalent metal salt (A-1) derived from a saturated fatty acid having 12 to 18 carbon atoms and a fatty acid acyl lysine having an acyl group derived from a saturated fatty acid having 12 to 18 carbon atoms (A-1). A-2) and a poorly water-soluble powder (A) selected from fatty acid acyl taurine divalent metal salts (A-3) having an acyl group derived from a saturated fatty acid having 12 to 18 carbon atoms. The poorly water-soluble powder (A) used in the present invention is a powder that dissolves in 100 g of water at 25 ° C. in an amount of less than 0.1 g, and preferably dissolves in an amount of less than 0.05 g. It is a powder that does not substantially dissolve in the body or water. In addition, the poorly water-soluble powder (A) is excellent in spreadability, and is in contact with a direct or indirect load on the surface of dentin where the hair tips such as a toothbrush are exposed during brushing. The poorly water-soluble powder (A) contained in the dentifrice composition can block the opening of the dentinal tubule. Since the poorly water-soluble powder (A) spreads and has a good elongation, it is considered that the powder is spread while spreading around the opening of the dentinal tubule by using the dentifrice composition of the present invention. The opening can be effectively sealed.

本発明の歯磨組成物は、脂肪酸二価金属塩(A−1)、脂肪酸アシルリシン(A−2)、脂肪酸アシルタウリン二価金属塩(A−3)から選ばれる水難溶性粉体(A)を、1種単独で含有することも2種以上で含有することも可能である。水難溶性粉体(A)の合計含有量は、象牙質細管の開口部の封鎖性及び良好な味を確保する点から、本発明の歯磨組成物中に、好ましくは0.1〜2質量%であり、より好ましくは0.2〜1.5質量%であり、さらに好ましくは0.4〜1.2質量%である。   The dentifrice composition of the present invention comprises a poorly water-soluble powder (A) selected from a fatty acid divalent metal salt (A-1), a fatty acid acyl lysine (A-2), and a fatty acid acyl taurine divalent metal salt (A-3). It can be contained singly or in combination of two or more. The total content of the poorly water-soluble powder (A) is preferably 0.1 to 2% by mass in the dentifrice composition of the present invention from the viewpoint of securing the sealing property of the opening of the dentin tubule and good taste. More preferably, it is 0.2-1.5 mass%, More preferably, it is 0.4-1.2 mass%.

成分(A−1)の脂肪酸二価金属塩は、炭素数12〜18の飽和脂肪酸を由来とするものであり、2つの飽和脂肪酸と二価金属とから構成される。かかる飽和脂肪酸としては、具体的には、ラウリン酸、ミリスチン酸、ペンタデシル酸、パルミチン酸、マルガリン酸、ステアリン酸が挙げられる。なかでも、ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸が好ましく、ラウリン酸、ミリスチン酸、ステアリン酸がより好ましい。成分(A−1)を構成する2つの飽和脂肪酸は、同一であることが好ましい。また、二価金属としては、具体的には、亜鉛、カルシウム、マグネシウム、ストロンチウム、バリウムが挙げられる。なかでも、口腔内への適用性、延展性及びコスト面の点から、亜鉛、カルシウム、マグネシウムが好ましく、亜鉛、カルシウムがより好ましい。   The fatty acid divalent metal salt of component (A-1) is derived from a saturated fatty acid having 12 to 18 carbon atoms, and is composed of two saturated fatty acids and a divalent metal. Specific examples of such saturated fatty acids include lauric acid, myristic acid, pentadecylic acid, palmitic acid, margaric acid, and stearic acid. Of these, lauric acid, myristic acid, palmitic acid, and stearic acid are preferable, and lauric acid, myristic acid, and stearic acid are more preferable. The two saturated fatty acids constituting the component (A-1) are preferably the same. Specific examples of the divalent metal include zinc, calcium, magnesium, strontium, and barium. Of these, zinc, calcium, and magnesium are preferable, and zinc and calcium are more preferable in terms of applicability to the oral cavity, spreadability, and cost.

成分(A−2)の炭素数12〜18の飽和脂肪酸を由来とするアシル基を有する脂肪酸アシルリシンは、上述のような炭素数12〜18の飽和脂肪酸を由来とするアシル基を分子内に有しており、なかでもN-飽和脂肪酸を由来とするアシル基を有するアシルリシンが好ましい。かかる脂肪酸アシルリシン(A−2)としては、例えば、N−ラウロイルリシン、N−ミリストイルリシン、N−パルミトイルリシン、N−ステアロイルリシン等が挙げられ、このうち、感触に優れるN−ラウロイルリシンが好ましい。N−ラウロイルリシンは、市販品ではNε−ラウロイル−L−リシンとして、商品名アミホープLL(味の素(株))等を入手することができる。   The fatty acid acyl lysine having an acyl group derived from a saturated fatty acid having 12 to 18 carbon atoms of the component (A-2) has an acyl group derived from a saturated fatty acid having 12 to 18 carbon atoms in the molecule as described above. Among them, acyl lysine having an acyl group derived from an N-saturated fatty acid is preferable. Examples of the fatty acyl lysine (A-2) include N-lauroyl lysine, N-myristoyl lysine, N-palmitoyl lysine, and N-stearoyl lysine. Among these, N-lauroyl lysine having excellent feel is preferable. As N-lauroyl lysine, a commercial name, Amihope LL (Ajinomoto Co., Inc.), etc. can be obtained as Nε-lauroyl-L-lysine.

成分(A−3)の炭素数12〜18の飽和脂肪酸を由来とするアシル基を有する脂肪酸アシルタウリン二価金属塩は、上述のような炭素数が12〜18の飽和脂肪酸を由来とするアシル基と、タウリン基とからなる脂肪酸アシルタウリン基を分子内に有しており、なかでも脂肪酸アシルタウリン基は、N-飽和脂肪酸アシルタウリン基が好ましい。かかる脂肪酸アシルタウリン基としては、例えば、N-ラウロイルタウリン、N-ミリストイルタウリン、N-パルミトイルタウリン、N-ステアリロイルタウリン等が挙げられ、使用感、象牙質細管の開口部封鎖性の点からN-ラウロイルタウリン基が好ましい。かかる脂肪酸アシルタウリン二価金属塩(A−3)の二価金属としては、カルシウム、亜鉛、マグネシウム等が好ましく、使用感、象牙質細管の開口部封鎖性の点から亜鉛、カルシウムが好ましく、さらにカルシウムが好ましい。   The fatty acid acyl taurine divalent metal salt having an acyl group derived from a saturated fatty acid having 12 to 18 carbon atoms of component (A-3) is an acyl derived from a saturated fatty acid having 12 to 18 carbon atoms as described above. And a fatty acid acyl taurine group consisting of a taurine group in the molecule, and the fatty acid acyl taurine group is preferably an N-saturated fatty acid acyl taurine group. Examples of such fatty acyltaurine groups include N-lauroyl taurine, N-myristoyl taurine, N-palmitoyl taurine, N-stearylloyl taurine and the like. -Lauroyl taurine group is preferred. As the divalent metal of the fatty acid acyl taurine divalent metal salt (A-3), calcium, zinc, magnesium and the like are preferable, and zinc and calcium are preferable from the viewpoint of feeling of use and opening of the dentinal tubule. Calcium is preferred.

本発明の歯磨組成物は、粉末セルロース又はエーテル化度が0.1〜0.6のカルボキシメチルセルロース若しくはその塩(B)を含有する。以下、成分(B)について、粉末セルロースを成分(B−1)、エーテル化度が0.1〜0.6のカルボキシメチルセルロース若しくはその塩を成分(B−2)と称する。   The dentifrice composition of the present invention contains powdered cellulose, carboxymethylcellulose having a degree of etherification of 0.1 to 0.6, or a salt thereof (B). Hereinafter, regarding component (B), powdered cellulose is referred to as component (B-1), and carboxymethylcellulose having a degree of etherification of 0.1 to 0.6 or a salt thereof is referred to as component (B-2).

本発明で用いる粉末セルロース(B−1)は、平均重合度が440〜2250であり、平均重合度が350以下の結晶セルロースと比べ、重合度及び結晶化度が異なるのみならず、物性が顕著に異なる。例えば、結晶セルロースはピーリング剤等としても用いられるように適度な研磨性を有するが、粉末セルロースには研磨性は殆どない。また、粉末セルロース(B−1)は水に難溶であるが、吸水性を有しており、保水効果を発揮する。水分を保持した粉末セルロース(B−1)は、適度な柔軟性(柔らかさ)を有するため、歯ブラシの先端を介して水難溶性粉体(A)を連れ込み、ブラッシング時における歯ブラシ等の毛先の負荷力が四方へ分散するのを防止しながら、負荷力を効率的に水難溶性粉体(A)へ作用させ、水難溶性粉体(A)を良好に延展させることができる。   The powdered cellulose (B-1) used in the present invention has an average degree of polymerization of 440 to 2250, and not only has a different degree of polymerization and a higher degree of crystallinity than crystalline cellulose having an average degree of polymerization of 350 or less, but also has remarkable physical properties. Different. For example, crystalline cellulose has an appropriate abrasiveness so that it can also be used as a peeling agent and the like, but powdered cellulose has little abrasiveness. Moreover, although powdered cellulose (B-1) is hardly soluble in water, it has water absorption and exhibits a water retention effect. Since the powdered cellulose (B-1) retaining moisture has an appropriate flexibility (softness), the water-soluble powder (A) is brought in via the tip of the toothbrush, and the tip of a toothbrush such as a toothbrush at the time of brushing is used. While preventing the load force from spreading in all directions, the load force can be efficiently applied to the hardly water-soluble powder (A), and the hardly water-soluble powder (A) can be spread well.

本発明で用いるエーテル化度が0.1〜0.6のカルボキシメチルセルロース又はその塩(B−2)は、水に難溶であるが、吸水性を有しており、水の存在下で膨潤して適度な柔軟性を発現することができる。また、カルボキシメチルセルロース又はその塩(B−2)は、粘結剤として用いられるエーテル化度が上記範囲外のカルボキシメチルセルロース又はその塩のような増粘機能をもたず、25℃において1%の水溶液の粘度が200mPa・s未満であるものが好ましく、1〜150mPa・sであるものがより好ましく、10〜150mPa・sであるものがさらに好ましい。市販品としては、日本製紙ケミカル製のサンローズSLD-F1、サンローズSLD-FMが挙げられる。   Carboxymethylcellulose having a degree of etherification of 0.1 to 0.6 or a salt thereof (B-2) used in the present invention is hardly soluble in water, but has water absorption and swells in the presence of water. Therefore, moderate flexibility can be expressed. In addition, carboxymethylcellulose or a salt thereof (B-2) does not have a thickening function like carboxymethylcellulose or a salt thereof whose degree of etherification used as a binder is outside the above range, and is 1% at 25 ° C. The aqueous solution preferably has a viscosity of less than 200 mPa · s, more preferably 1 to 150 mPa · s, and still more preferably 10 to 150 mPa · s. Examples of commercially available products include Sunrose SLD-F1 and Sunrose SLD-FM manufactured by Nippon Paper Chemicals.

このような上記カルボキシメチルセルロース又はその塩(B−2)は、ブラッシング時に歯ブラシ等の毛先と象牙質の表面との空隙に存在して水難溶性粉体(A)を連れ込み、歯ブラシ等の毛先の負荷力が四方へ分散するのを抑制することで、負荷力を効率的に水難溶性粉体(A)へ作用させ、水難溶性粉体(A)を良好に延展させることができると考えられる。   Such carboxymethylcellulose or a salt thereof (B-2) is present in the gap between the tip of the toothbrush and the dentin during brushing and brings in the water-insoluble powder (A), and the tip of the toothbrush and the like. It is considered that the load force can be efficiently applied to the poorly water-soluble powder (A) and the poorly water-soluble powder (A) can be satisfactorily spread by suppressing the dispersion of the load force in all directions. .

カルボキシメチルセルロース又はその塩(B−2)のより好ましいエーテル化度は0.1〜0.5であり、さらに0.2〜0.4であることが好ましい。ここでエーテル化度とは、グルコース単位あたりのカルボキシメチル基の置換度をいう。エーテル化度は、例えばCMC工業会分析法(灰化法)に従い得ることができる。カルボキシメチルセルロースナトリウム1gを精秤し、磁性ルツボに入れて600℃で灰化し、灰化によって生成した酸化ナトリウムをN/10硫酸でフェノールフタレインを指示薬として滴定し、カルボキシメチルセルロースナトリウム1gあたりの滴定量YmLを次式に入れて計算し、求めたエーテル化度を示すことができる。
エーテル化度=(162×Y)/(10,000−80×Y)
The more preferable degree of etherification of carboxymethylcellulose or a salt thereof (B-2) is 0.1 to 0.5, and further preferably 0.2 to 0.4. Here, the degree of etherification refers to the degree of substitution of carboxymethyl groups per glucose unit. The degree of etherification can be obtained, for example, according to the CMC industry association analysis method (ashing method). Weigh precisely 1 g of sodium carboxymethylcellulose, put it in a magnetic crucible, incinerate at 600 ° C., titrate sodium oxide produced by incineration with N / 10 sulfuric acid using phenolphthalein as an indicator, and titrate per 1 g of sodium carboxymethylcellulose. YmL can be calculated by putting it in the following formula and the obtained degree of etherification can be shown.
Degree of etherification = (162 × Y) / (10,000-80 × Y)

カルボキシメチルセルロースの塩(B−2)としては、ナトリウム、カリウムなどのアルカリ金属塩、アンモニウム塩などが挙げられ、口腔内への適用、コスト面や入手容易性、水難溶性粉体(A)の良好な延展を図る点から、カルボキシメチルセルロースナトリウムが好ましい。   Examples of the salt of carboxymethyl cellulose (B-2) include alkali metal salts such as sodium and potassium, ammonium salts, etc., application to the oral cavity, cost and availability, and poorly water-soluble powder (A). From the standpoint of easy extension, sodium carboxymethylcellulose is preferred.

上記粉末セルロース(B−1)又は上記カルボキシメチルセルロース若しくはその塩(B−2)の含有量は、保水性をもち、適度な柔軟性をもって水難溶性粉体(A)の延展を図り、象牙質細管を効果的に封鎖する点から、本発明の歯磨組成物中に、好ましくは0.05質量%以上であり、より好ましくは0.1質量%以上であり、さらに好ましくは0.2質量%以上である。また、これら成分(B−1)又は成分(B−2)の含有量は、適度な柔軟性をもって水難溶性粉体(A)の延展を図り象牙質細管を効果的に封鎖する点から、本発明の歯磨組成物中に、好ましくは5質量%以下であり、より好ましくは2.5質量%以下であり、さらに好ましくは1質量%以下であり、またさらに好ましくは0.8質量%以下である。なお、これら成分(B−1)及び成分(B−2)は、1種単独で用いてもよく、2種以上組み合わせて用いてもよい。   Content of the said powdered cellulose (B-1) or the said carboxymethylcellulose or its salt (B-2) has water retention, aims at extension of a poorly water-soluble powder (A) with moderate flexibility, and a dentinal tubule In the dentifrice composition of the present invention, it is preferably 0.05% by mass or more, more preferably 0.1% by mass or more, and further preferably 0.2% by mass or more. It is. In addition, the content of these components (B-1) or (B-2) is from the point of spreading the hardly water-soluble powder (A) with appropriate flexibility and effectively sealing the dentinal tubules. In the dentifrice composition of the present invention, it is preferably 5% by mass or less, more preferably 2.5% by mass or less, further preferably 1% by mass or less, and further preferably 0.8% by mass or less. is there. In addition, these component (B-1) and component (B-2) may be used individually by 1 type, and may be used in combination of 2 or more type.

成分(B)の平均粒径は、良好な保水性を保持し、ブラッシング時に歯ブラシ等の毛先と象牙質の表面との狭小な空隙に有効に存在させる点から、好ましくは10〜200μmであり、より好ましくは15〜100μmであり、さらに好ましくは20〜80μmである。   The average particle size of the component (B) is preferably 10 to 200 μm from the viewpoint that it retains good water retention and is effectively present in a narrow gap between the tip of a toothbrush and the dentin surface during brushing. More preferably, it is 15-100 micrometers, More preferably, it is 20-80 micrometers.

また、成分(A)の水難溶性粉体と成分(B)の粉末セルロース(B−1)又はエーテル化度が0.1〜0.6のカルボキシメチルセルロース若しくはその塩(B−2)の質量比(A/B)は、成分(B)によって適度な柔軟性を発現させながら成分(A)を良好に延展させる点から、好ましくは0.02〜20であり、より好ましくは0.1〜10であり、さらに好ましくは0.5〜7である。   Moreover, the mass ratio of the poorly water-soluble powder of the component (A) and the powdered cellulose (B-1) of the component (B), or carboxymethylcellulose having a degree of etherification of 0.1 to 0.6 or a salt thereof (B-2) (A / B) is preferably 0.02 to 20 and more preferably 0.1 to 10 from the viewpoint of spreading the component (A) satisfactorily while expressing appropriate flexibility by the component (B). More preferably, it is 0.5-7.

本発明の歯磨組成物は、水(C)を含有する。これにより、成分(B)に水(C)を吸収させ、これら成分(B)によって適度な柔軟性を発現させて、ブラッシング時における歯ブラシ等の毛先の負荷力が四方へ分散するのを防止しながら、成分(A)の水難溶性粉体を良好に延展させることができる。   The dentifrice composition of the present invention contains water (C). As a result, water (C) is absorbed in the component (B), and appropriate flexibility is expressed by the component (B), so that the load force of the bristles such as a toothbrush at the time of brushing is prevented from being dispersed in all directions. However, the poorly water-soluble powder of component (A) can be spread well.

水(C)は、成分(B)を膨潤させ、かつ適度な柔軟性を発現させ、水難溶性粉体(A)による象牙質細管の封鎖性を向上する点から、本発明の歯磨組成物中に、好ましくは10〜55質量%含有し、より好ましくは12〜50質量%含有する。   In the dentifrice composition of the present invention, the water (C) swells the component (B) and exhibits appropriate flexibility, and improves the sealing performance of the dentinal tubules with the poorly water-soluble powder (A). Preferably, it contains 10-55 mass%, More preferably, it contains 12-50 mass%.

なお、歯磨組成物の水分量は、配合した水分量及び配合した成分中の水分量から計算によって算出することもできるが、例えばカールフィッシャー水分計で測定することができる。カールフィッシャー水分計としては、例えば、微量水分測定装置(平沼産業(株))を用いることができる。この装置では、歯磨組成物を5gとり、無水メタノール25gに懸濁させ、この懸濁液0.02gを分取して水分量を測定することができる。   In addition, although the water content of a dentifrice composition can also be computed by calculation from the water content mix | blended and the water content in the mix | blended component, it can measure with a Karl Fischer moisture meter, for example. As the Karl Fischer moisture meter, for example, a trace moisture measuring device (Hiranuma Sangyo Co., Ltd.) can be used. In this apparatus, 5 g of the dentifrice composition can be taken and suspended in 25 g of anhydrous methanol, and 0.02 g of this suspension can be collected to measure the amount of water.

本発明の歯磨組成物は、さらに粘結剤(D)を含有することが好ましい。粘結剤としては、アルギン酸ナトリウム、エーテル化度が0.7〜2.0のカルボキシメチルセルロースナトリウム、カラギーナン、キサンタンガム、ポリアクリル酸ナトリウム、ヒドロキシエチルセルロース、ヒドロキシプロピルセルロース、ペクチン、トラガントガム、アラビアガム、グアーガム、カラヤガム、ローカストビーンガム、ジェランガム、タマリンドガム、サイリウムシードガム、ポリビニルアルコール、コンドロイチン硫酸ナトリウム及びメトキシエチレン無水マレイン酸共重合体等からなる群より選ばれる1種又は2種以上を用いることができる。このうち、エーテル化度が0.7〜2.0のカルボキシメチルセルロースナトリウム、カラギーナン、キサンタンガムが好ましい。また、保形性や糸引き性、及び使用感の面から2種以上、さらには3種以上を使用することができる。粘結剤(D)は、歯磨組成物中に、好ましくは0.1〜3質量%含有し、より好ましくは0.2〜2質量%が、さらに好ましくは0.3〜1.5質量%含有する。なお、粘結剤(D)として含有するカルボキシメチルセルロースナトリウムのエーテル化度は、一般的に0.7以上であって、0.7〜2.0であるものが好ましく、適度な粘性を得る点から1.0〜1.5であるものが好ましい。   The dentifrice composition of the present invention preferably further contains a binder (D). As a binder, sodium alginate, sodium carboxymethylcellulose having a degree of etherification of 0.7 to 2.0, carrageenan, xanthan gum, sodium polyacrylate, hydroxyethylcellulose, hydroxypropylcellulose, pectin, tragacanth gum, gum arabic, guar gum, One type or two or more types selected from the group consisting of karaya gum, locust bean gum, gellan gum, tamarind gum, psyllium seed gum, polyvinyl alcohol, sodium chondroitin sulfate and methoxyethylene maleic anhydride copolymer can be used. Among these, sodium carboxymethylcellulose, carrageenan, and xanthan gum having a degree of etherification of 0.7 to 2.0 are preferable. Moreover, 2 or more types, Furthermore, 3 or more types can be used from the surface of shape retention property, stringing property, and usability. The binder (D) is preferably contained in the dentifrice composition in an amount of 0.1 to 3% by mass, more preferably 0.2 to 2% by mass, and still more preferably 0.3 to 1.5% by mass. contains. The degree of etherification of sodium carboxymethylcellulose contained as the binder (D) is generally 0.7 or more, preferably 0.7 to 2.0, and obtains an appropriate viscosity. To 1.0 to 1.5 is preferable.

なお、本発明の歯磨組成物は、歯ブラシによるブラッシングに適用するための良好な保形性及び使用感を確保する点から、25℃における粘度が1000〜7000dPa・sであるものが好ましく、さらに1500〜5000dPa・sであるものが好ましい。歯磨組成物の粘度は、製造から3日以上経過後の歯磨組成物を測定することが好ましく、ヘリパス型粘度計を用いて、25℃、ロータT-C、(回転数)2.5rpm、1分間の条件で測定することができる。   The dentifrice composition of the present invention preferably has a viscosity at 25 ° C. of 1000 to 7000 dPa · s, more preferably 1500, from the viewpoint of ensuring good shape retention and usability for brushing with a toothbrush. What is -5000dPa * s is preferable. The viscosity of the dentifrice composition is preferably measured for a dentifrice composition after 3 days or more from the production, using a helipath viscometer at 25 ° C., rotor TC, (rotation number) 2.5 rpm, 1 It can be measured in minutes.

本発明の歯磨組成物は、上記成分の他、本発明の効果を損なわない範囲内で、甘味剤、香料、pH調整剤、色素、硝酸カリウム等の薬効成分等を適宜含有することができる。このように、本発明の歯磨組成物によれば、象牙質知覚過敏症に罹患したために歯牙の象牙質が露出したような場合にも、象牙質の表面に存在する象牙質細管の開口部を即効的にしかも充分に封鎖することができるので、象牙質知覚過敏症に起因する痛みを即効的に防止することが可能であり、象牙質知覚過敏用の歯磨組成物として最適である。   The dentifrice composition of the present invention can appropriately contain, in addition to the above components, medicinal components such as sweeteners, fragrances, pH adjusters, pigments, potassium nitrate, and the like within a range not impairing the effects of the present invention. Thus, according to the dentifrice composition of the present invention, even when the dentin of the tooth is exposed because it suffered from hypersensitivity of the dentin, the opening of the dentin tubule present on the surface of the dentin is removed. Since it can be instantly and sufficiently sealed, it is possible to immediately prevent pain caused by dentine hypersensitivity, and it is optimal as a dentifrice composition for dentin hypersensitivity.

本発明の歯磨組成物は、常法による歯磨組成物を用いたブラッシングによって、象牙質知覚過敏症に起因する痛みを防止することができる。象牙質知覚過敏症に起因する痛みをより効果的に防止する観点から、歯磨組成物の使用方法は、1日1〜5回使用することが好ましく、これを1ヶ月間のうち1日以上又は1〜2週間継続して使用することが好ましい。   The dentifrice composition of the present invention can prevent pain caused by dentin hypersensitivity by brushing using a dentifrice composition according to a conventional method. From the viewpoint of more effectively preventing pain caused by dentine hypersensitivity, the method of using the dentifrice composition is preferably used 1 to 5 times a day, and this is used for 1 day or more in a month or It is preferable to use it continuously for 1 to 2 weeks.

本発明の歯磨組成物は、象牙質細管の表面を物理的に刺激しない観点、及び象牙質細管の開口部を封鎖した水難溶性粉体(A)の剥離を防止する観点から、15g/個以上の崩壊強度の顆粒、及び結晶セルロースなどの研磨性の高い粉体又は粒子の含有量は、本発明の歯磨組成物中に2質量%以下であることが好ましく、1質量%以下であることがより好ましく、0.5質量%以下がさらに好ましく、実質的に含有しないことが好ましい。なお、崩壊強度とは、微小圧縮試験機((株)島津製作所、MCTM−500)を用いて、粒子径(180〜200μm)の顆粒を10個〜20個測定した平均値で表される値を意味する。また、崩壊強度は歯磨組成物に含有されている湿潤状態における強度である。   The dentifrice composition of the present invention is not less than 15 g / piece from the viewpoint of not physically stimulating the surface of the dentinal tubule and from preventing peeling of the poorly water-soluble powder (A) blocking the opening of the dentinal tubule. The content of highly disintegrating granules and highly abrasive powders or particles such as crystalline cellulose is preferably 2% by mass or less in the dentifrice composition of the present invention, and preferably 1% by mass or less. More preferably, 0.5 mass% or less is further more preferable, and it is preferable not to contain substantially. The collapse strength is a value represented by an average value obtained by measuring 10 to 20 granules having a particle diameter (180 to 200 μm) using a micro compression tester (Shimadzu Corporation, MCTM-500). Means. The disintegration strength is the strength in a wet state contained in the dentifrice composition.

本発明の歯磨組成物は、本発明の効果を阻害しない範囲で研磨剤を含有することができる。研磨剤としては、例えばリン酸カルシウム、リン酸水素カルシウム、炭酸カルシウム、水酸化アルミニウム、ケイ酸アルミニウム、ケイ酸ジルコニウム、ピロリン酸カルシウム、無水ケイ酸(研磨性シリカ:JIS K5101−13−2に準ずる方法により測定される吸油量が、50〜150mL/100g)等が挙げられる。研磨剤は、RDA値(Radioactive Dentine Abrasion values、ISO11609研磨性の試験方法 付随書Aにより測定される値)が20〜250のものが一般に用いられる。研磨剤の含有量は、本発明の歯磨組成物中に0〜20質量%であることが好ましく、15質量%以下であることがより好ましく、12質量%以下であることがさらに好ましい。上記RDA値が250を超える研磨剤の含有量は、本発明の歯磨組成物中に1質量%以下であることが好ましく、0.5質量%以下であることがより好ましく、0.1質量%以下であることがさらに好ましく、実質的に配合しないことがさらに好ましい。   The dentifrice composition of the present invention can contain an abrasive as long as the effects of the present invention are not impaired. As an abrasive, for example, calcium phosphate, calcium hydrogen phosphate, calcium carbonate, aluminum hydroxide, aluminum silicate, zirconium silicate, calcium pyrophosphate, anhydrous silicic acid (abrasive silica: measured by a method according to JIS K5101-13-2) The oil absorption is 50 to 150 mL / 100 g). As the abrasive, one having an RDA value (Radioactive Dentine Abrasion values, a value measured by ISO 11609 abrasive test method appendix A) of 20 to 250 is generally used. The content of the abrasive is preferably 0 to 20% by mass, more preferably 15% by mass or less, and further preferably 12% by mass or less in the dentifrice composition of the present invention. The content of the abrasive having an RDA value exceeding 250 is preferably 1% by mass or less, more preferably 0.5% by mass or less, and more preferably 0.1% by mass in the dentifrice composition of the present invention. More preferably, it is more preferable not to mix substantially.

本発明の歯磨組成物は、上記成分の他、本発明の効果を損なわない範囲内で、グリセリン、ソルビトール、ポリエチレングリコール等の湿潤剤、ラウリル硫酸ナトリウム、ラウロイルメチルタウリンナトリウム等の発泡剤、サッカリンナトリウム等の甘味剤、メントール等の香料、水酸化ナトリウム等のpH調整剤、色素、薬効成分等を適宜含有することができる。このように、本発明の歯磨組成物によれば、象牙質知覚過敏症に罹患したために歯牙の象牙質が露出したような場合にも、象牙質の表面に存在する象牙質細管の開口部を即効的にしかも充分に封鎖することができるので、象牙質知覚過敏症に起因する痛みを即効的かつ持続的に防止することができるため、象牙質知覚過敏用の歯磨組成物として最適である。   In addition to the above components, the dentifrice composition of the present invention includes a wetting agent such as glycerin, sorbitol, and polyethylene glycol, a foaming agent such as sodium lauryl sulfate and sodium lauroylmethyl taurine, and saccharin sodium. Sweeteners, perfumes such as menthol, pH adjusters such as sodium hydroxide, pigments, medicinal ingredients and the like. Thus, according to the dentifrice composition of the present invention, even when the dentin of the tooth is exposed because it suffered from hypersensitivity of the dentin, the opening of the dentin tubule present on the surface of the dentin is removed. Since it can be instantly and sufficiently sealed, it is possible to prevent pain caused by dentine hypersensitivity immediately and continuously, and is therefore optimal as a dentifrice composition for dentin hypersensitivity.

本発明の歯磨組成物は、<1>(A)炭素数12〜18の飽和脂肪酸を由来とする脂肪酸二価金属塩(A−1)、炭素数12〜18の飽和脂肪酸を由来とするアシル基を有する脂肪酸アシルリシン(A−2)、及び炭素数12〜18の飽和脂肪酸を由来とするアシル基を有する脂肪酸アシルタウリン二価金属塩(A−3)から選ばれる水難溶性粉体、(B)粉末セルロース(B−1)又はエーテル化度が0.1〜0.6のカルボキシメチルセルロース若しくはその塩(B−2)、及び(C)水を含有する歯磨組成物である。   The dentifrice composition of the present invention includes <1> (A) a fatty acid divalent metal salt (A-1) derived from a saturated fatty acid having 12 to 18 carbon atoms, and an acyl derived from a saturated fatty acid having 12 to 18 carbon atoms. A poorly water-soluble powder selected from a fatty acid acyl lysine having a group (A-2) and a fatty acid acyl taurine divalent metal salt (A-3) having an acyl group derived from a saturated fatty acid having 12 to 18 carbon atoms, (B ) A dentifrice composition containing powdered cellulose (B-1) or carboxymethylcellulose having a degree of etherification of 0.1 to 0.6 or a salt thereof (B-2), and (C) water.

本発明は、さらに以下の歯磨組成物又は方法、或いは用途が好ましい。
<2>成分(A−1)又は成分(A−3)の二価金属が、亜鉛、カルシウム及びマグネシウムから選ばれる前記<1>の歯磨組成物。
<3>成分(A−1)又は成分(A−3)の二価金属が、亜鉛及びカルシウムから選ばれる前記<1>又は<2>の歯磨組成物。
<4>成分(A−1)が、ラウリン酸二価金属塩、ミリスチン酸二価金属塩及びステアリン酸二価金属塩から選ばれる前記<1>から<3>の歯磨組成物。
<5>成分(A−1)が、ステアリン酸二価金属塩である前記<1>から<3>の歯磨組成物。
<6>成分(A−1)の二価金属が、亜鉛である前記<4>又は<5>の歯磨組成物。
<7>成分(A−1)が、ラウリン酸二価金属塩である前記<1>から<3>の歯磨組成物。
<8>成分(A−2)が、N-ラウロイルリシン、N-ミリストイルリシン、N-パルミトイルリシン及びN-ステアロイルリシンから選ばれる前記<1>から<7>の歯磨組成物。
<9>成分(A−2)が、N−ラウロイルリシンである前記<1>から<7>の歯磨組成物。
<10>成分(A−3)の二価金属が、カルシウムである前記<1>から<9>の歯磨組成物。
<11>成分(A−3)が、N-ラウロイルタウリン二価金属塩、N−ミリストイルタウリン二価金属塩、N−パルミトイルタウリン二価金属塩及びN−ステアロイルタウリン二価金属塩から選ばれる前記<1>から<10>の歯磨組成物。
<12>成分(A−3)が、N-ラウロイルタウリン二価金属塩である前記<1>から<11>の歯磨組成物。
<13>成分(A)を0.1〜2質量%、成分(B)を0.05〜5質量%含有する前記<1>から<12>の歯磨組成物。
<14>成分(A)を0.4〜1.2質量%、成分(B)を0.2〜1質量%含有する前記<1>から<12>の歯磨組成物。
<15>成分(A)と成分(B)の質量比(A/B)が、0.02〜20である前記<1>から<14>の歯磨組成物。
<16>成分(A)と成分(B)の質量比(A/B)が、0.5〜7である前記<1>から<14>の歯磨組成物。
<17>さらに、(D)粘結剤を0.1〜3質量%含有する前記<1>から<16>の歯磨組成物。
<18>15g/個以上の崩壊強度の顆粒の含有量が2質量%以下である前記<1>から<17>の歯磨組成物。
<19>RDA値が25〜250の研磨剤の含有量が15質量%以下である前記<1>から<18>の歯磨組成物。
<20>RDA値が250より大きい研磨剤の含有量が2質量%以下である前記<1>〜<19>の歯磨組成物。
<21>25℃における粘度が、1000〜7000dPa・sである前記<1>から<20>の歯磨組成物。
<22>象牙質知覚過敏用歯磨組成物である前記<1>〜<21>の歯磨組成物。
<23>前記<1>〜<21>の歯磨組成物の象牙質知覚過敏症に起因する痛み防止のための使用。
<24>象牙質知覚過敏防止剤の製造のための前記<1>〜<21>記載の歯磨組成物の使用。
<25>前記<1>〜<21>の歯磨組成物を口腔内に適用する象牙質知覚過敏を防止する方法。
In the present invention, the following dentifrice composition or method or use is further preferable.
<2> The dentifrice composition of <1>, wherein the divalent metal of the component (A-1) or the component (A-3) is selected from zinc, calcium and magnesium.
<3> The dentifrice composition of <1> or <2>, wherein the divalent metal of the component (A-1) or the component (A-3) is selected from zinc and calcium.
<4> The dentifrice composition of <1> to <3>, wherein the component (A-1) is selected from lauric acid divalent metal salt, myristic acid divalent metal salt and stearic acid divalent metal salt.
<5> The dentifrice composition of <1> to <3>, wherein the component (A-1) is a divalent metal salt of stearic acid.
<6> The dentifrice composition of <4> or <5>, wherein the divalent metal of the component (A-1) is zinc.
<7> The dentifrice composition of <1> to <3>, wherein the component (A-1) is a divalent metal salt of lauric acid.
<8> The dentifrice composition according to <1> to <7>, wherein the component (A-2) is selected from N-lauroyl lysine, N-myristoyl lysine, N-palmitoyl lysine and N-stearoyl lysine.
<9> The dentifrice composition of <1> to <7>, wherein the component (A-2) is N-lauroyl lysine.
<10> The dentifrice composition according to <1> to <9>, wherein the divalent metal of the component (A-3) is calcium.
<11> The component (A-3) is selected from N-lauroyl taurine divalent metal salt, N-myristoyl taurine divalent metal salt, N-palmitoyl taurine divalent metal salt and N-stearoyl taurine divalent metal salt <1> to <10> dentifrice composition.
<12> The dentifrice composition according to the above <1> to <11>, wherein the component (A-3) is an N-lauroyl taurine divalent metal salt.
<13> The dentifrice composition according to <1> to <12>, containing 0.1 to 2% by mass of the component (A) and 0.05 to 5% by mass of the component (B).
<14> The dentifrice composition of <1> to <12>, containing 0.4 to 1.2% by mass of the component (A) and 0.2 to 1% by mass of the component (B).
<15> The dentifrice composition of <1> to <14>, wherein the mass ratio (A / B) of the component (A) to the component (B) is 0.02 to 20.
<16> The dentifrice composition according to the above <1> to <14>, wherein the mass ratio (A / B) of the component (A) to the component (B) is 0.5 to 7.
<17> The dentifrice composition according to <1> to <16>, further comprising (D) 0.1 to 3% by mass of a binder.
<18> The dentifrice composition according to the above <1> to <17>, wherein the content of granules having a disintegration strength of 15 g / piece or more is 2% by mass or less.
<19> The dentifrice composition according to <1> to <18>, wherein the content of the abrasive having an RDA value of 25 to 250 is 15% by mass or less.
<20> The dentifrice composition of <1> to <19>, wherein the content of the abrasive having an RDA value greater than 250 is 2% by mass or less.
<21> The dentifrice composition according to the above <1> to <20>, wherein the viscosity at 25 ° C is 1000 to 7000 dPa · s.
<22> The dentifrice composition according to the above <1> to <21>, which is a dentifrice composition for hypersensitivity to dentin.
<23> Use of the dentifrice composition of <1> to <21> for preventing pain caused by dentin hypersensitivity.
Use of the dentifrice composition as described in said <1>-<21> for manufacture of a <24> dentine hypersensitivity prevention agent.
<25> A method of preventing dentin hypersensitivity by applying the dentifrice composition of <1> to <21> to the oral cavity.

以下、本発明について、実施例に基づき具体的に説明する。なお、表中に特に示さない限り、各成分の含有量は質量%を示す。   Hereinafter, the present invention will be specifically described based on examples. In addition, unless otherwise indicated in a table | surface, content of each component shows the mass%.

[実施例1〜9、比較例1〜6]
表1に示す組成の歯磨組成物を常法にしたがって調製した。得られた各歯磨組成物を用い、下記に示す象牙質細管の開口部封鎖状態の評価を行った。また、表2に示す組成の歯磨組成物を調製し、得られた各歯磨組成物を用い、同様に象牙質細管の開口部封鎖状態の評価、及び象牙質知覚過敏症の改善効果の評価を行った。評価結果を表1及び表2にそれぞれ示す。なお、実施例1〜9、比較例1〜6の歯磨組成物は、調製1ヶ月後に25℃で3500〜4500dPa・sとなるものとし、実施例1の歯磨組成物は、調整1ヶ月後25℃の粘度が3800dPa・sであった(測定条件:ヘリパス粘度計、ロータT-C、(回転数)2.5rpm、1分間)。
[Examples 1-9, Comparative Examples 1-6]
A dentifrice composition having the composition shown in Table 1 was prepared according to a conventional method. Each dentifrice composition thus obtained was used to evaluate the blocked state of the opening of the dentinal tubule shown below. In addition, a dentifrice composition having the composition shown in Table 2 was prepared, and each dentifrice composition thus obtained was used to similarly evaluate the occlusion state of the opening of the dentinal tubule and evaluate the improvement effect of the dentinal hypersensitivity. went. The evaluation results are shown in Table 1 and Table 2, respectively. In addition, the dentifrice composition of Examples 1-9 and Comparative Examples 1-6 shall be 3500-4500 dPa * s at 25 degreeC after one month of preparation, and the dentifrice composition of Example 1 is 25 months after adjustment 1 month. The viscosity at 0 ° C. was 3800 dPa · s (measurement conditions: helipath viscometer, rotor TC, (rotation speed) 2.5 rpm, 1 minute).

[象牙質細管の開口部封鎖状態の評価]
牛歯の象牙質を試料とし、試料を0.5%リン酸水溶液にて室温で30分脱灰し、砥粒サイズ40μmのサンドペーパー、及び砥粒サイズ3μmのサンドペーパーで表面を研磨処理した。この試料の表面を、実施例、比較例の歯磨組成物1gを歯ブラシ(ディープクリーン超コンパクト 普通・花王(株)製)を用いて5往復ブラッシングし、試料を蒸留水で30秒間洗浄した。洗浄後の試料の表面における象牙質細管の開口部をデジタルマイクロスコープ(VHX−1000、(株)キーエンス製)を用いて倍率2000倍で観察し、目視で象牙質細管の開口状態を確認した。図1(a)は、比較例4の歯磨組成物で処理した後の試料の状態を示すマイクロスコープ写真である。図1(a)に示すように、象牙質細管の開口部のほぼ全てが黒く、開口していることが認められる。図1(b)は、実施例2の歯磨組成物で処理した後の試料の状態を示すマイクロスコープ写真である。図1(b)に示すように、象牙質細管の開口部のほぼ全てが白く、開口部を歯磨組成物が封鎖している状態が認められる。
[Evaluation of occluded state of dentinal tubule]
Using bovine dentin as a sample, the sample was decalcified with a 0.5% aqueous phosphoric acid solution at room temperature for 30 minutes, and the surface was polished with sandpaper having an abrasive grain size of 40 μm and sandpaper having an abrasive grain size of 3 μm. . The surface of this sample was brushed 5 times with a toothbrush (Deep Clean Ultra Compact Ordinary, Kao Co., Ltd.) using 1 g of the dentifrice compositions of Examples and Comparative Examples, and the sample was washed with distilled water for 30 seconds. The opening of the dentinal tubule on the surface of the sample after washing was observed at a magnification of 2000 using a digital microscope (VHX-1000, manufactured by Keyence Corporation), and the opening state of the dentinal tubule was visually confirmed. FIG. 1A is a microscope photograph showing the state of the sample after being treated with the dentifrice composition of Comparative Example 4. As shown in FIG. 1 (a), it can be seen that almost all the openings of the dentinal tubules are black and open. FIG. 1 (b) is a microscope photograph showing the state of the sample after being treated with the dentifrice composition of Example 2. As shown in FIG. 1 (b), almost all the openings of the dentin tubule are white, and a state in which the dentifrice composition seals the openings is observed.

歯磨組成物による象牙質細管の開口部の封鎖状態の評価は、図1(a)の状態を5、図1(b)の状態を1とし、図1(b)に比べて一部の象牙質細管の開口部が開いていると認められる状態を2、さらに象牙質細管の開口部が開いていると認められる状態を3、図1(a)に比べて一部の象牙質細管の開口部が封鎖されていると認められる状態、又は過半数の象牙質細管の開口部が封鎖されていない状態を4として評価した。評価結果を表1及び表2に示す。   The evaluation of the sealed state of the opening of the dentin tubule by the dentifrice composition is that the state of FIG. 1 (a) is 5 and the state of FIG. 1 (b) is 1, and a part of ivory is compared with FIG. 1 (b) 2 for the state where the opening of the tubule is recognized as being open, 3 for the state where the opening of the dentinal tubule is recognized as being open, and the opening of some of the dentinal tubules compared to FIG. The state where the part was recognized as being blocked, or the state where the majority of the openings of the dentinal tubules were not blocked was evaluated as 4. The evaluation results are shown in Tables 1 and 2.

[象牙質知覚過敏症状に起因する痛み改善の評価]
表2の実施例2、比較例4〜5の歯磨組成物について、象牙質知覚過敏症状に起因する痛み防止、又は抑制の程度を評価した。評価対象者は最近1ヶ月の間に歯がしみる頻度が毎日、又は週に数回ある者をパネラーとした。各歯磨組成物にパネラー11名、2週間の期間、1日3回の歯磨組成物を使用した後に、象牙質知覚過敏症に起因する痛みが防止されたか、又は抑制されたかを評価した。具体的には、2週間の使用継続後に「しみなくなった感じがするか」について、3:そう思う、2:ややそう思う、1:そう思わない又はわからない の中から回答を得た。パネラーの回答の合計値を象牙質知覚過敏症に起因する痛みの評価として表2に示す。この評価は、数値が大きいほど、象牙質知覚過敏症に起因する痛みが抑制又は低減されたことを意味する。
[Evaluation of pain improvement caused by dentinal hypersensitivity symptoms]
About the dentifrice composition of Example 2 of Table 2, and Comparative Examples 4-5, the degree of the pain prevention or suppression resulting from a dentine hypersensitivity symptom was evaluated. The subjects of evaluation were panelists who had a frequency of teething every day or several times a week during the last month. Each toothpaste composition was evaluated for whether the pain caused by dentin hypersensitivity was prevented or suppressed after using 11 toothpaste compositions for 11 panelists, for a period of 2 weeks, 3 times a day. Specifically, after 2 weeks of use, “I feel no more smudged” was answered: 3: Yes, 2: Yes, 1: No, I don't know. The total value of the panelists' responses is shown in Table 2 as an evaluation of pain caused by dentine hypersensitivity. This evaluation means that the larger the numerical value, the more the pain caused by dentine hypersensitivity was suppressed or reduced.

*1:アミホープLL (味の素(株))
*2:KCフロックW-400(日本製紙ケミカル(株)) 平均粒子径24μm
*3:サンローズSLD-F1(日本製紙ケミカル(株))エーテル化度0.2〜0.3、平均粒子径50〜60μm
*4:サイロピュア25(富士シリシア化学(株)) 吸油量:310ml/100g
*5:ソーボシル AC77(PT PQ Sillicas Indonesia) RDA値:125
*6:サンローズF35SH(日本製紙ケミカル(株)) エーテル化度1.0〜1.15
* 1: Amihope LL (Ajinomoto Co., Inc.)
* 2: KC Flock W-400 (Nippon Paper Chemical Co., Ltd.) Average particle size 24μm
* 3: Sunrose SLD-F1 (Nippon Paper Chemical Co., Ltd.) Degree of etherification 0.2-0.3, average particle size 50-60μm
* 4: Silo Pure 25 (Fuji Silysia Chemical Co., Ltd.) Oil absorption: 310ml / 100g
* 5: Sobosil AC77 (PT PQ Sillicas Indonesia) RDA value: 125
* 6: Sunrose F35SH (Nippon Paper Chemical Co., Ltd.) Degree of etherification 1.0 to 1.15

*2:KCフロックW-400(日本製紙ケミカル(株)) 平均粒子径24μm
*4:サイロピュア25(富士シリシア化学(株)) 吸油量:310ml/100g
*5:ソーボシル AC77(PT PQ Sillicas Indonesia) RDA値:125
*6:サンローズF35SH(日本製紙ケミカル(株)) エーテル化度1.0〜1.15
* 2: KC Flock W-400 (Nippon Paper Chemical Co., Ltd.) Average particle size 24μm
* 4: Silo Pure 25 (Fuji Silysia Chemical Co., Ltd.) Oil absorption: 310ml / 100g
* 5: Sobosil AC77 (PT PQ Sillicas Indonesia) RDA value: 125
* 6: Sunrose F35SH (Nippon Paper Chemical Co., Ltd.) Degree of etherification 1.0 to 1.15

表1に示すように、本発明の水難溶性粉体(A)と成分(B)を含有する実施例1〜9は、象牙質細管の開口部がほぼ封鎖されている、又は概ね封鎖されていることが認められた。一方、水難溶性粉体(A)及び/又は成分(B)を含有しない比較例1〜2、4は、象牙質細管の開口部が殆ど封鎖されていないか、封鎖状態が不十分であることが認められた。また、水難溶性粉体であるが、本願の粉体(A)ではない酸化亜鉛を含有する比較例3についても、象牙質細管の開口部が封鎖されていないことが認められた。   As shown in Table 1, in Examples 1 to 9 containing the poorly water-soluble powder (A) and the component (B) of the present invention, the openings of the dentinal tubules are almost sealed or almost sealed. It was recognized that On the other hand, Comparative Examples 1-2, 4 which do not contain the poorly water-soluble powder (A) and / or the component (B) are that the openings of the dentinal tubules are hardly blocked or the sealed state is insufficient. Was recognized. Moreover, it was recognized that the opening part of a dentin tubule is not blocked also about the comparative example 3 containing the zinc oxide which is a powder with poor water solubility but not the powder (A) of this application.

表2に示すように、充分に象牙質細管が封鎖されている実施例2は、使用後に象牙質知覚過敏症に起因する痛みが抑制されている評価が得られたが、比較例5は象牙質細管の開口部の封鎖が一部であるため、象牙質知覚過敏症に起因する痛みはやや抑制されている程度であり、比較例6の象牙質細管の開口部が殆ど封鎖されていない歯磨組成物については、象牙質知覚過敏症に起因する痛みが殆ど抑制されていない評価が得られた。この結果より、象牙質細管の封鎖状態は、象牙質知覚過敏症に起因する痛み抑制との相関があると認められ、象牙質細管の封鎖性の高い本発明の実施例は、象牙質知覚過敏症に起因する痛みの抑制効果が高いと判断できる。   As shown in Table 2, in Example 2, in which the dentinal tubules were sufficiently blocked, evaluation was obtained in which the pain caused by dentine hypersensitivity was suppressed after use. Tooth brushing in which the opening of the dentinal tubule of Comparative Example 6 is hardly blocked because the opening of the tubule is partially blocked, and the pain caused by dentine hypersensitivity is somewhat suppressed. About the composition, evaluation by which the pain resulting from dentine hypersensitivity was hardly suppressed was obtained. From these results, it is recognized that the sealed state of the dentinal tubules has a correlation with the suppression of pain caused by the hypersensitivity of the dentinal tubules. It can be judged that the effect of suppressing the pain caused by the disease is high.

Claims (8)

次の成分(A)、(B)並びに(C):
(A)炭素数12〜18の飽和脂肪酸を由来とする脂肪酸二価金属塩(A−1)、炭素数12〜18の飽和脂肪酸を由来とするアシル基を有する脂肪酸アシルリシン(A−2)、及び炭素数12〜18の飽和脂肪酸を由来とするアシル基を有する脂肪酸アシルタウリン二価金属塩(A−3)から選ばれる水難溶性粉体、
(B)粉末セルロース(B−1)又はエーテル化度が0.1〜0.6のカルボキシメチルセルロース若しくはその塩(B−2)、並びに
(C)水
を含有する歯磨組成物。
The following components (A), (B) and (C):
(A) a fatty acid divalent metal salt (A-1) derived from a saturated fatty acid having 12 to 18 carbon atoms, a fatty acid acyl lysine (A-2) having an acyl group derived from a saturated fatty acid having 12 to 18 carbon atoms, And a poorly water-soluble powder selected from fatty acid acyl taurine divalent metal salts (A-3) having an acyl group derived from a saturated fatty acid having 12 to 18 carbon atoms,
(B) A dentifrice composition containing powdered cellulose (B-1) or carboxymethyl cellulose having a degree of etherification of 0.1 to 0.6 or a salt thereof (B-2), and (C) water.
成分(A−1)又は成分(A−3)の二価金属が、亜鉛、カルシウム及びマグネシウムから選ばれる請求項1に記載の歯磨組成物。   The dentifrice composition according to claim 1, wherein the divalent metal of component (A-1) or component (A-3) is selected from zinc, calcium and magnesium. 成分(A−2)が、N-ラウロイルリシン、N-ミリストイルリシン、N-パルミトイルリシン及びN-ステアロイルリシンから選ばれる請求項1に記載の歯磨組成物。   The dentifrice composition according to claim 1, wherein component (A-2) is selected from N-lauroyl lysine, N-myristoyl lysine, N-palmitoyl lysine and N-stearoyl lysine. 成分(A)を0.1〜2質量%、成分(B)を0.05〜5質量%含有する請求項1〜3のいずれか1項に記載の歯磨組成物。   The dentifrice composition of any one of Claims 1-3 which contains a component (A) 0.1-2 mass% and a component (B) 0.05-5 mass%. 成分(A)と成分(B)の質量比(A/B)が、0.02〜20である請求項1〜4のいずれか1項に記載の歯磨組成物。   The dentifrice composition of any one of Claims 1-4 whose mass ratio (A / B) of a component (A) and a component (B) is 0.02-20. さらに、(D)粘結剤を0.1〜3質量%含有する請求項1〜5のいずれか1項に記載の歯磨組成物。   Furthermore, the dentifrice composition of any one of Claims 1-5 which contains 0.1-3 mass% of (D) binder. 25℃における粘度が、1000〜7000dPa・sである請求項1〜6のいずれか1項に記載の歯磨組成物。   The dentifrice composition of any one of Claims 1-6 whose viscosity in 25 degreeC is 1000-7000 dPa * s. 象牙質知覚過敏用歯磨組成物である請求項1〜7のいずれか1項に記載の歯磨組成物。   The dentifrice composition according to any one of claims 1 to 7, which is a dentifrice-sensitive dentifrice composition.
JP2011131699A 2011-06-13 2011-06-13 Toothpaste composition Withdrawn JP2013001649A (en)