JP2012246340A - 接着シート - Google Patents
接着シート Download PDFInfo
- Publication number
- JP2012246340A JP2012246340A JP2011117017A JP2011117017A JP2012246340A JP 2012246340 A JP2012246340 A JP 2012246340A JP 2011117017 A JP2011117017 A JP 2011117017A JP 2011117017 A JP2011117017 A JP 2011117017A JP 2012246340 A JP2012246340 A JP 2012246340A
- Authority
- JP
- Japan
- Prior art keywords
- adhesive
- epoxy resin
- adhesive sheet
- adhesive layer
- meth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本実施形態に係るエポキシ樹脂は、分子内に少なくとも2個のエポキシ基を有するものであれば特に限定されない。エポキシ樹脂としては、例えば、ビスフェノールA型エポキシ樹脂、ビスフェノールF型エポキシ樹脂、ビスフェノールS型エポキシ樹脂等の二官能エポキシ樹脂、フェノールノボラック型エポキシ樹脂、クレゾールノボラック型エポキシ樹脂等のノボラック型エポキシ樹脂、多官能エポキシ樹脂及び脂環式エポキシ樹脂が挙げられる。これらは、1種を単独で又は2種以上を組み合わせて用いることができる。
本実施形態に係るエポキシ樹脂硬化剤は、下記式(1)で表されるフェノール樹脂を含有する。
本実施形態に係るエポキシ基含有(メタ)アクリル共重合体は、グリシジルアクリレート又はグリシジルメタクリレート等の官能性モノマーを含有するモノマーを重合して得ることができる。上記官能性モノマーはエポキシ樹脂と非相溶であるため、硬化後にエポキシ樹脂と(メタ)アクリル共重合体とがそれぞれ分離し、接着剤層の耐リフロークラック性及び耐熱性を向上することができる。
本実施形態の接着剤組成物には、無機フィラーを更に含有することができる。無機フィラーとしては、例えば、水酸化アルミニウム、水酸化マグネシウム、炭酸カルシウム、炭酸マグネシウム、ケイ酸カルシウム、ケイ酸マグネシウム、酸化カルシウム、酸化マグネシウム、酸化アルミニウム、窒化アルミニウム、ホウ酸アルミウィスカ、窒化ホウ素及び結晶性シリカ、非晶性シリカが挙げられる。これらは、1種又は2種以上を併用することができる。接着剤層の熱伝導性を向上する観点から、無機フィラーとして、酸化アルミニウム、窒化アルミニウム、窒化ホウ素、結晶性シリカ又は非晶性シリカを含有することが好ましい。接着剤層の溶融粘度の調整や、接着剤組成物にチキソトロピック性を付与する観点からは、水酸化アルミニウム、水酸化マグネシウム、炭酸カルシウム、炭酸マグネシウム、ケイ酸カルシウム、ケイ酸マグネシウム、酸化カルシウム、酸化マグネシウム、酸化アルミニウム、結晶性シリカ又は非晶性シリカを含有することが好ましい。
表1に示す配合割合(質量部)で各成分を配合して、接着剤組成物を調製した。まず、エポキシ樹脂として、クレゾールノボラック型エポキシ樹脂(東都化成(株)製、商品名:YDCN−700−10、エポキシ当量:210)50.0質量部、エポキシ樹脂硬化剤として、式(1)で表される構造を有するフェノール樹脂(エア・ウォーター(株)製、商品名:HE910−20、CAS番号:304859−44−7)24.0質量部、シランカップリング剤として、3−メルカプトプロピルトリメトキシシラン(モーメンティブ・パフォーマンス・マテリアルズ・ジャパン合同会社製、商品名:A−189)2.0質量部及び3−ウレイドプロピルトリエトキシシラン(モーメンティブ・パフォーマンス・マテリアルズ・ジャパン合同会社製、商品名:A−1160)6.0質量部、無機フィラーとして、真球状シリカ(株式会社アドマテックス製、商品名:アドマナノ、平均粒径:約0.050μm)37.0質量部及びシクロヘキサノン1900質量部を攪拌混合した。ここに、エポキシ基含有(メタ)アクリル共重合体として、アクリルゴム(ナガセケムテック(株)製、商品名:HTR−860P−3、Mw:80万、Tg:15℃、ブチルアクリレート/エチルアクリレート/アクリロニトリル/グリシジルメタクリレートの質量比:39.4/29.3/30.3/3)210.0質量部を加え、混合した後、真空脱気して接着剤組成物のワニスを得た。
アクリルゴムの配合量を270.0質量部に変更した以外は、実施例1と同様にして接着シートを作製した。
アクリルゴムの配合量を410.0質量部に変更した以外は、実施例1と同様にして接着シートを作製した。
エポキシ樹脂硬化剤を、式(1)で表される構造を有しないフェノール樹脂(三井化学株式会社製、商品名:XLC−LL)に変更した以外は、実施例1と同様にして接着シートを作製した。
接着シートの接着剤層の溶融粘度は回転式粘弾性測定装置(ティー・エイ・インスツルメント・ジャパン(株)製、商品名:ARES−RDA〕を用いて測定した。
接着シートの接着剤層面にダイシングシートを貼り付け、基材フィルムを剥離した後、もう一方の接着剤層面に100μm厚の半導体ウェハを熱板上でラミネートする。その後、ダイシング工程を経て半導体ウェハを個片化して、7.5mm×7.5mmの接着層付き半導体チップとした。
Claims (4)
- 前記エポキシ基含有(メタ)アクリル共重合体は、エポキシ基を有するモノマーに由来する構造単位を0.5〜3.0質量%含有し、ガラス転移温度が−50〜30℃であり、重量平均分子量が10万〜300万である、請求項1記載の接着シート。
- 前記エポキシ基含有(メタ)アクリル共重合体の質量に対する、前記エポキシ樹脂及び前記エポキシ樹脂硬化剤の合計量の比が、0.05〜0.40である、請求項1又は2記載の接着シート。
- 前記接着剤組成物が、無機フィラーを更に含む、請求項1〜3のいずれか一項に記載の接着シート。