JP2011225796A - Antistatic coating composition - Google Patents
Antistatic coating composition Download PDFInfo
- Publication number
- JP2011225796A JP2011225796A JP2010119958A JP2010119958A JP2011225796A JP 2011225796 A JP2011225796 A JP 2011225796A JP 2010119958 A JP2010119958 A JP 2010119958A JP 2010119958 A JP2010119958 A JP 2010119958A JP 2011225796 A JP2011225796 A JP 2011225796A
- Authority
- JP
- Japan
- Prior art keywords
- antistatic
- solvent
- compound
- weight
- alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、帯電防止性、耐擦傷性、透明性、耐久性に優れた光硬化性のコーティング用組成物、およびこのコーティング用組成物を用いた帯電防止層を形成してなる帯電防止フィルムに関する。 The present invention relates to a photocurable coating composition excellent in antistatic properties, scratch resistance, transparency and durability, and an antistatic film formed by forming an antistatic layer using the coating composition. .
従来、プラスチックフィルムを基材として用いる製品には、プラスチックフィルムの表面保護を目的にハードコート処理が施されている。 Conventionally, products using a plastic film as a base material have been subjected to a hard coat treatment for the purpose of protecting the surface of the plastic film.
しかしながら、一般に、プラスチックフィルム表面のハードコート処理に用いられる、紫外線などの活性エネルギー線にて硬化する、分子中に（メタ）アクリロイル基を有する化合物（以下、「光硬化性化合物」ともいう）から形成される硬化塗膜は、固有表面抵抗値が高く静電気が発生し易いため、粉塵の吸着および静電気に起因したトラブルを生じる。
例えば、ＬＣＤやＰＤＰなどのディスプレイの表面には、傷つき防止のためのハードコート処理や、各種光学処理がされたＴＡＣフィルムやＰＥＴフィルムが使用されているが、ホコリの付着により画像の視認性が著しく損なわれたり、生産工程中に静電気の発生によりトラブルが発生し、生産性が著しく損なわれたりする等の問題が生じる。
これらの問題を解決するため、フィルムへ帯電防止性を付与するために、多くの検討が試みられてきた。例えば、４級アンモニウム塩基含有ポリマーを使用した帯電防止性コーティング組成物をプラスチックフィルムに塗布して、帯電防止性とハードコート性を両立する方法が知られている。
However, in general, from a compound having a (meth) acryloyl group in a molecule (hereinafter, also referred to as a “photo-curable compound”) that is cured by an active energy ray such as ultraviolet rays, which is used for a hard coat treatment of a plastic film surface. The formed cured coating film has a high intrinsic surface resistance value and is likely to generate static electricity, which causes trouble due to dust adsorption and static electricity.
For example, the surface of a display such as an LCD or PDP uses a TAC film or PET film that has been subjected to a hard coat treatment for preventing scratches or various optical treatments. Problems such as significant damage, troubles due to generation of static electricity during the production process, and significant loss of productivity.
In order to solve these problems, many studies have been made to impart antistatic properties to the film. For example, a method is known in which an antistatic coating composition using a quaternary ammonium base-containing polymer is applied to a plastic film to achieve both antistatic properties and hard coat properties.
しかしながら、一般的に４級アンモニウム塩基含有ポリマーは、吸湿性が高く、疎水性の高いハードコート性の光硬化性化合物と相溶性が悪いため、塗膜を形成する際、組成物中に多くの水分が含まれ、析出ブツ、硬化ムラ、品質ムラが発生する場合があった。
このような問題を解決するため、帯電防止剤として四級アンモニウム塩基含有モノマーとアルキレンオキサイド構造含有モノマーの共重合物と、極性基を含有する単官能モノマーを使用した、帯電防止性コーティング用組成物の提案がなされている（特許文献１〜４参照）。
However, since quaternary ammonium base-containing polymers generally have high hygroscopicity and poor compatibility with hard-coating photocurable compounds having high hydrophobicity, many polymers are contained in the composition when forming a coating film. In some cases, moisture was contained, causing precipitation, uneven curing, and uneven quality.
In order to solve such a problem, an antistatic coating composition using a copolymer of a quaternary ammonium base-containing monomer and an alkylene oxide structure-containing monomer as an antistatic agent and a monofunctional monomer containing a polar group Has been proposed (see Patent Documents 1 to 4).
しかしながら、上述の方法では、吸湿による析出ブツ、硬化ムラ、品質ムラは改善するものの、極性基を含有する単官能モノマーを使用するため、塗膜の架橋密度が低下し、ハードコートとして必要な塗膜硬度が不足する。
また、近年、携帯機器に関するディスプレイ分野においては、高い防水性が求められているが、上述の方法により得られた塗膜を温水中に浸漬した場合、加水分解により４級アンモニウム塩が溶出し、帯電防止性が損なわれる場合があった。
However, although the above-described method improves precipitation blur, curing unevenness, and quality unevenness due to moisture absorption, since a monofunctional monomer containing a polar group is used, the crosslinking density of the coating film is reduced, and the coating required as a hard coat is required. Film hardness is insufficient.
In recent years, in the display field related to portable devices, high waterproofness is required, but when the coating film obtained by the above method is immersed in warm water, the quaternary ammonium salt is eluted by hydrolysis, In some cases, the antistatic property is impaired.
本発明は、帯電防止性を有すると共に、ハードコートとして十分な耐擦傷性、透明性を備え、さらには、近年、要求の増加している防水性にも応えることができるような耐久性に優れた光硬化性のコーティング用組成物、およびこのコーティング用組成物を用いた帯電防止層を形成してなる帯電防止フィルムを提供する事を目的とする。 The present invention has antistatic properties, has sufficient scratch resistance and transparency as a hard coat, and is excellent in durability that can meet the increasing waterproof properties in recent years. Another object of the present invention is to provide a photocurable coating composition and an antistatic film formed by forming an antistatic layer using the coating composition.
本発明者らは、前記問題を解決するため、鋭意検討した結果、本発明に達した。
即ち、本発明は、帯電防止性共重合体（Ａ）、3つ以上のエチレン性不飽和基を有する化合物（Ｂ）、光重合開始剤（Ｃ）及び溶剤（Ｄ）を含む帯電防止用コーティング組成物であって、
前記帯電防止性共重合体（Ａ）が、下記一般式（１）で表される４級アンモニウム塩基を有する化合物（ａ−１）及び下記一般式（２）で表されるアルキレンオキサイド鎖を有する化合物（ａ−２）を必須の構成成分とする共重合体であり、
前記溶剤（Ｄ）が、アルコール系溶剤（ｄ−１）及び炭素数３〜５のアセテート系溶剤（ｄ−２）を含むことを特徴とする帯電防止用コーティング組成物に関する。
一般式（１）
ＣＨ２＝Ｃ（Ｒ１）ＣＯＺ（ＣＨ２）ｋＮ＋（Ｒ２）（Ｒ３）Ｒ４・Ｘ−
（式中、Ｒ１はＨまたはＣＨ３ 、Ｒ２〜Ｒ４はＨまたは炭素数が１〜９の炭化水素基、Ｚは酸素原子またはＮＨ基、ｋは１〜１０の整数、Ｘ−は１価のアニオンを表す。）
一般式（２）
ＣＨ２＝Ｃ（Ｒ５）ＣＯＯ（ＡＯ）ｎＲ６
（式中、Ｒ５はＨまたはＣＨ３、Ｒ６は水素または炭素数が１〜２２の炭化水素基、ｎは２〜２００の整数、Ａは炭素数が２〜４のアルキレン基を表す。）
The inventors of the present invention have arrived at the present invention as a result of intensive studies to solve the above problems.
That is, the present invention relates to an antistatic coating comprising an antistatic copolymer (A), a compound (B) having three or more ethylenically unsaturated groups, a photopolymerization initiator (C) and a solvent (D). A composition comprising:
The antistatic copolymer (A) has a compound (a-1) having a quaternary ammonium base represented by the following general formula (1) and an alkylene oxide chain represented by the following general formula (2). A copolymer comprising the compound (a-2) as an essential constituent,
The solvent (D) relates to an antistatic coating composition comprising an alcohol solvent (d-1) and an acetate solvent (d-2) having 3 to 5 carbon atoms.
General formula (1)
CH 2 = C (R 1) COZ (CH 2) k N + (R 2) (R 3) R 4 · X -
(In the formula, R 1 is H or CH 3 , R 2 to R 4 are H or a hydrocarbon group having 1 to 9 carbon atoms, Z is an oxygen atom or NH group, k is an integer of 1 to 10, and X − is Represents a monovalent anion.)
General formula (2)
CH 2 = C (R 5) COO (AO) n R 6
(In the formula, R 5 represents H or CH 3 , R 6 represents hydrogen or a hydrocarbon group having 1 to 22 carbon atoms, n represents an integer of 2 to 200, and A represents an alkylene group having 2 to 4 carbon atoms. )
また、本発明は、一般式（１）におけるＲ２〜Ｒ４がＨまたは無置換の炭素数が１〜９のアルキル基であり、一般式（２）Ｒ６は水素または無置換の炭素数が１〜２２のアルキル基であることを特徴とする上記発明に記載の帯電防止用コーティング組成物に関する。 In the present invention, R 2 to R 4 in the general formula (1) are H or an unsubstituted alkyl group having 1 to 9 carbon atoms, and the general formula (2) R 6 is hydrogen or an unsubstituted carbon number. The present invention relates to the antistatic coating composition according to the invention, wherein is an alkyl group of 1 to 22.
また、本発明は、3つ以上のエチレン性不飽和基を有する化合物（Ｂ）１００重量部に対して、帯電防止性共重合体（Ａ）を１〜２０重量部、光重合開始剤（Ｃ）を０．１〜２０重量部を含有し、
（Ａ）〜（Ｄ）の合計１００重量％中に、溶剤（Ｄ）を３０〜８０重量％含有し、
前記溶剤（Ｄ）の１００重量％中、アルコール系溶剤（ｄ−１）の含有量が５〜２５重量％、炭素数３〜５のアセテート系溶剤（ｄ−２）の含有量が５５〜９０重量％であることを特徴とする上記発明に記載の帯電防止用コーティング組成物に関する。
In addition, the present invention provides 1 to 20 parts by weight of an antistatic copolymer (A) to 100 parts by weight of a compound (B) having three or more ethylenically unsaturated groups, a photopolymerization initiator (C ) 0.1-20 parts by weight,
In a total of 100% by weight of (A) to (D), 30 to 80% by weight of the solvent (D) is contained,
In 100% by weight of the solvent (D), the content of the alcohol solvent (d-1) is 5 to 25% by weight, and the content of the acetate solvent (d-2) having 3 to 5 carbon atoms is 55 to 90%. The antistatic coating composition according to the invention as described above, wherein the coating composition is wt%.
また、本発明は、アルコール系溶剤（ｄ−１）が、メチルアルコール、エチルアルコール、イソプロピルアルコール、ｎ−ブチルアルコール、イソブチルアルコール、シクロヘキシルアルコール、
２−メトキシエタノール、２−エトキシエタノール、２−プロポキシエタノール、２−ブトキシエタノール、
１−メトキシ−２−プロパノール、３−メトキシ−１−プロパノール、１−エトキシ−２−プロノール、２−エトキシ−１−プロノール及び３−エトキシ−１−プロノールからなる群より選ばれることを特徴とする上記発明のいずれか記載の帯電防止用コーティング組成物に関する。
In the present invention, the alcohol solvent (d-1) is methyl alcohol, ethyl alcohol, isopropyl alcohol, n-butyl alcohol, isobutyl alcohol, cyclohexyl alcohol,
2-methoxyethanol, 2-ethoxyethanol, 2-propoxyethanol, 2-butoxyethanol,
It is selected from the group consisting of 1-methoxy-2-propanol, 3-methoxy-1-propanol, 1-ethoxy-2-pronol, 2-ethoxy-1-pronol and 3-ethoxy-1-pronol The present invention relates to an antistatic coating composition according to any one of the above inventions.
また、本発明は、トリアセチルセルロース透明支持体の少なくとも一方の面へ、上記発明のいずれか記載の帯電防止コーティング用組成物を用いた帯電防止層を形成してなる帯電防止フィルムに関する。 The present invention also relates to an antistatic film obtained by forming an antistatic layer using the antistatic coating composition according to any one of the above inventions on at least one surface of a triacetylcellulose transparent support.
本発明の帯電防止用コーティング組成物から形成される帯電防止層は、十分な帯電防止性を有すると共に、優れた耐擦傷性、透明性を示し、さらに温水浸漬試験においても高い耐久性を有する。従って、本発明の帯電防止コーティング組成物は、ディスプレイ等の表面層、プラスチック成型品の表面コート用など、帯電防止性に加えてハードコート性と透明性が要求される各種用途に好適に使用できる。 The antistatic layer formed from the antistatic coating composition of the present invention has sufficient antistatic properties, exhibits excellent scratch resistance and transparency, and has high durability even in a hot water immersion test. Therefore, the antistatic coating composition of the present invention can be suitably used for various applications that require hard coat properties and transparency in addition to antistatic properties, such as surface layers for displays and the like, and surface coatings for plastic molded products. .
以下に本発明の実施の形態を詳細に説明するが、以下に記載する構成要件の説明は、本発明の実施態様の一例（代表例）であり、本発明はその要旨を超えない限りこれらの内容に特定されない。 Embodiments of the present invention will be described in detail below, but the description of the constituent elements described below is an example (representative example) of an embodiment of the present invention, and the present invention does not exceed the gist thereof. Not specific to the content.
本発明で用いられる帯電防止性共重合体（Ａ）は、下記一般式（１）で表される４級アンモニウム塩基を有する化合物（ａ−１）と下記一般式（２）で表されるアルキレンオキサイド鎖を有する化合物（ａ−２）とを必須の構成成分とし、さらに必要に応じて前記（ａ−１）、（ａ−２）と共重合可能な化合物（ａ−３）をアルコール系溶剤（ｄ−１）中でラジカル共重合して得られる。 The antistatic copolymer (A) used in the present invention includes a compound (a-1) having a quaternary ammonium base represented by the following general formula (1) and an alkylene represented by the following general formula (2). The compound (a-2) having an oxide chain as an essential component, and if necessary, the compound (a-3) copolymerizable with the above (a-1) and (a-2) is an alcohol solvent. Obtained by radical copolymerization in (d-1).
一般式（１）
ＣＨ２＝Ｃ（Ｒ１）ＣＯＺ（ＣＨ２）ｋＮ＋（Ｒ２）（Ｒ３）Ｒ４・Ｘ−
（式中、Ｒ１はＨまたはＣＨ３ 、Ｒ２〜Ｒ４はＨまたは炭素数が１〜９の炭化水素基、Ｚは酸素原子またはＮＨ基、ｋは１〜１０の整数、Ｘ−は１価のアニオンを表す。）
General formula (1)
CH 2 = C (R 1) COZ (CH 2) k N + (R 2) (R 3) R 4 · X -
(In the formula, R 1 is H or CH 3 , R 2 to R 4 are H or a hydrocarbon group having 1 to 9 carbon atoms, Z is an oxygen atom or NH group, k is an integer of 1 to 10, and X − is Represents a monovalent anion.)
一般式（２）
ＣＨ２＝Ｃ（Ｒ５）ＣＯＯ（ＡＯ）ｎＲ６
（式中、Ｒ５はＨまたはＣＨ３、Ｒ６は水素または炭素数が１〜２２の炭化水素基、ｎは２〜２００の整数、Ａは炭素数が２〜４のアルキレン基を表す。）
General formula (2)
CH 2 = C (R 5) COO (AO) n R 6
(In the formula, R 5 represents H or CH 3 , R 6 represents hydrogen or a hydrocarbon group having 1 to 22 carbon atoms, n represents an integer of 2 to 200, and A represents an alkylene group having 2 to 4 carbon atoms. )
＜４級アンモニウム塩基を有する化合物（ａ−１）＞
本発明における４級アンモニウム塩基を有する化合物（ａ−１）は、前記一般式（１）で表され、一般式（１）におけるＲ２〜Ｒ４が、炭素数が１〜９の炭化水素基の場合、前記炭化水素基は置換又は無置換のものが選択でき、無置換のものが好ましく、無置換のアルキル基が好ましい。無置換のアルキル基としては、分岐を有するもの、有しないもの、いずれをも使うことができる。これらは、は２種類以上を併用しても良い。
Ｒ２〜Ｒ４の炭素数が１０よりも大きい場合、生成される帯電防止性共重合体（Ａ）の疎水性が高まる結果、前記帯電防止性共重合体（Ａ）を含有する帯電防止層の吸湿性が低下し、良好な帯電防止性能を得られない場合がある。
一般式（１）におけるＲ２〜Ｒ４のうち、無置換のアルキル基としては、炭素数１〜３のアルキル基が好ましく、メチル基、エチル基、ｎ−プロピル基、ｉｓｏ−プロピル基、等の無置換のアルキル基を有するものが入手し易いという点で好ましい。
<Compound (a-1) having a quaternary ammonium base>
The compound (a-1) having a quaternary ammonium base in the present invention is represented by the general formula (1), and R 2 to R 4 in the general formula (1) are hydrocarbon groups having 1 to 9 carbon atoms. In this case, the hydrocarbon group can be selected from a substituted or unsubstituted group, an unsubstituted group is preferred, and an unsubstituted alkyl group is preferred. As the unsubstituted alkyl group, any having or not having a branch can be used. These may be used in combination of two or more.
When the carbon number of R 2 to R 4 is larger than 10, the resulting antistatic copolymer (A) is increased in hydrophobicity, and as a result, the antistatic layer containing the antistatic copolymer (A) is produced. In some cases, the hygroscopicity of the resin decreases and good antistatic performance cannot be obtained.
Of the R 2 to R 4 in the general formula (1), the unsubstituted alkyl group is preferably an alkyl group having 1 to 3 carbon atoms, such as a methyl group, an ethyl group, an n-propyl group, an iso-propyl group, and the like. Those having an unsubstituted alkyl group are preferred in that they are easily available.
４級アンモニウム塩基を有する化合物（ａ−１）は、例えば、アミノ基を有する（メタ）アクリレート類、もしくは（メタ）アクリルアミド類を、４級化剤により４級化することにより得られる。また、市販の４級アンモニウム塩基を有する（メタ）アクリレート類や（メタ）アクリルアミド類も使用することができる。 The compound (a-1) having a quaternary ammonium base can be obtained by, for example, quaternizing an amino group-containing (meth) acrylate or (meth) acrylamide with a quaternizing agent. Further, (meth) acrylates and (meth) acrylamides having a commercially available quaternary ammonium base can also be used.
一般式（１）におけるＺが酸素原子の４級アンモニウム塩基を有する化合物（ａ−１）を形成するためのアミノ基を有する（メタ）アクリレート類の例としては、ジメチルアミノエチル（メタ）アクリレート、ジメチルアミノプロピル（メタ）アクリレート、ジメチルアミノブチル（メタ）アクリレート、ジエチルアミノエチル（メタ）アクリレート、ジエチルアミノプロピル（メタ）アクリレート、ジプロピルアミノエチル（メタ）アクリレート、ジブチルアミノエチル（メタ）アクリレート、ジヒドロキシエチルアミノエチル（メタ）アクリレート等を挙げることができる。 Examples of (meth) acrylates having an amino group for forming a compound (a-1) in which Z in the general formula (1) has a quaternary ammonium base having an oxygen atom include dimethylaminoethyl (meth) acrylate, Dimethylaminopropyl (meth) acrylate, dimethylaminobutyl (meth) acrylate, diethylaminoethyl (meth) acrylate, diethylaminopropyl (meth) acrylate, dipropylaminoethyl (meth) acrylate, dibutylaminoethyl (meth) acrylate, dihydroxyethylamino Examples thereof include ethyl (meth) acrylate.
一般式（１）におけるＺがＮＨ基の４級アンモニウム塩基を有する化合物（ａ−１）を形成するためのアミノ基を有する（メタ）アクリルアミド類の例としては、ジメチルアミノエチル（メタ）アクリルアミド、ジメチルアミノプロピル（メタ）アクリルアミド、ジメチルアミノブチル（メタ）アクリルアミド、ジエチルアミノエチル（メタ）アクリルアミド、ジエチルアミノプロピル（メタ）アクリルアミド、ジプロピルアミノエチル（メタ）アクリルアミド、ジブチルアミノエチル（メタ）アクリルアミド、ジヒドロキシエチルアミノエチル（メタ）アクリルアミド等を挙げることができる。 Examples of (meth) acrylamides having an amino group for forming a compound (a-1) in which Z in the general formula (1) has a quaternary ammonium base of an NH group include dimethylaminoethyl (meth) acrylamide, Dimethylaminopropyl (meth) acrylamide, dimethylaminobutyl (meth) acrylamide, diethylaminoethyl (meth) acrylamide, diethylaminopropyl (meth) acrylamide, dipropylaminoethyl (meth) acrylamide, dibutylaminoethyl (meth) acrylamide, dihydroxyethylamino Examples thereof include ethyl (meth) acrylamide.
前記アミノ基を有する（メタ）アクリレート類や前記アミノ基を有する（メタ）アクリルアミド類を４級塩化するための４級化剤としては、アルキルベンジルクロライド、ベンジルクロライド、アルキルクロライド、アルキルブロマイド等の各種ハライド類、ジメチル硫酸、ジエチル硫酸、ジプロピル硫酸等のアルキル硫酸類、ｐ−トルエンスルホン酸メチル、ベンゼンスルホン酸メチル等のスルホン酸エステル類、トリメチルホスファイト等のアルキルリン酸類が用いられる。 As a quaternizing agent for quaternizing the (meth) acrylates having an amino group and the (meth) acrylamides having an amino group, various kinds of alkylbenzyl chloride, benzyl chloride, alkyl chloride, alkyl bromide, etc. Halides, alkyl sulfates such as dimethyl sulfate, diethyl sulfate, and dipropyl sulfate, sulfonate esters such as methyl p-toluenesulfonate and methyl benzenesulfonate, and alkyl phosphates such as trimethyl phosphite are used.
＜アルキレンオキサイド鎖を有する化合物（ａ−２）＞
次に、本発明で用いられる帯電防止性共重合体（Ａ）の形成に用いられるもう１つの必須成分、アルキレンオキサイド鎖を有する化合物（ａ−２）について説明する。
アルキレンオキサイド鎖を有する化合物（ａ−２）は、前記一般式（２）で表され、例えば、エチレンオキシドのアルキルアルコールによる開環重合後、（メタ）アクリル酸メチルとのエステル交換反応、もしくは（メタ）アクリル酸クロライドとの反応により得ることができる。
<Compound (a-2) having an alkylene oxide chain>
Next, another essential component used for forming the antistatic copolymer (A) used in the present invention, compound (a-2) having an alkylene oxide chain, will be described.
The compound (a-2) having an alkylene oxide chain is represented by the general formula (2). For example, after ring-opening polymerization of ethylene oxide with an alkyl alcohol, transesterification with methyl (meth) acrylate, or (meta ) It can be obtained by reaction with acrylic acid chloride.
前記一般式（２）において、アルキレンオキサイド基（ＡＯ）は、炭素数２〜４のアルキレンオキサイド基であり、例えば、エチレンオキサイド基、プロピレンオキサイド基、ブチレンオキサイド基が挙げられる。また、同一モノマー内に、炭素数が異なるアルキレンオキサイド基が存在していてもよい。
アルキレンオキサイド基数（ｎ）は２〜２００の整数であり、好ましくは１０〜１００の整数である。２以下、または１０１以上の場合は、後述する、分子中に３つ以上のエチレン性不飽和基を有する化合物（Ｂ）との十分な相溶性が得られない場合がある。
Ｒ６は水素または炭素数１〜２２の炭化水素基である。炭素数２３以上では、原料が高価であるため実用的ではない。
炭素数１〜２２の炭化水素基としては、置換又は無置換のものが選択でき、無置換のものが好ましく、無置換のアルキル基が好ましい。無置換のアルキル基としては、分岐を有するもの、有しないもの、いずれをも使うことができる。これらは、２種類以上を併用しても良い。
In the general formula (2), the alkylene oxide group (AO) is an alkylene oxide group having 2 to 4 carbon atoms, and examples thereof include an ethylene oxide group, a propylene oxide group, and a butylene oxide group. Moreover, the alkylene oxide group from which carbon number differs may exist in the same monomer.
The number (n) of alkylene oxide groups is an integer of 2 to 200, preferably an integer of 10 to 100. In the case of 2 or less, or 101 or more, sufficient compatibility with the compound (B) having 3 or more ethylenically unsaturated groups in the molecule, which will be described later, may not be obtained.
R 6 is hydrogen or a hydrocarbon group having 1 to 22 carbon atoms. A carbon number of 23 or more is not practical because the raw material is expensive.
As the hydrocarbon group having 1 to 22 carbon atoms, a substituted or unsubstituted group can be selected, an unsubstituted group is preferable, and an unsubstituted alkyl group is preferable. As the unsubstituted alkyl group, any having or not having a branch can be used. Two or more of these may be used in combination.
アルキレンオキサイド鎖を有する化合物（ａ−２）としては、具体的には例えば、ポリエチレングリコールモノ（メタ）アクリレート、ポリプロピレングリコールモノ（メタ）アクリレート、ポリブチレングリコールモノ（メタ）アクリレート、ポリ（エチレングリコール−プロピレングリコール）モノ（メタ）アクリレート、ポリ（エチレングリコール−テトラメチレングリコール）モノ（メタ）アクリレート、ポリ（プロピレングリコール−テトラメチレングリコール）モノ（メタ）アクリレート、ポリエチレングリコールモノ（メタ）アクリレートモノメチルエーテル、ポリエチレングリコールモノ（メタ）アクリレートモノブチルエーテル、ポリエチレングリコールモノ（メタ）アクリレートモノオクチルエーテル、ポリエチレングリコールモノ（メタ）アクリレートモノベンジルエーテル、ポリエチレングリコールモノ（メタ）アクリレートモノフェニルエーテル、ポリエチレングリコールモノ（メタ）アクリレートモノデシルエーテル、ポリエチレングリコールモノ（メタ）アクリレートモノドデシルエーテル、ポリエチレングリコールモノ（メタ）アクリレートモノテトラデシルエーテル、ポリエチレングリコールモノ（メタ）アクリレートモノヘキサデシルエーテル、ポリエチレングリコールモノ（メタ）アクリレートモノオクタデシルエーテルポリ（エチレングリコール−プロピレングリコール）モノ（メタ）アクリレートオクチルエーテル、ポリ（エチレングリコール−プロピレングリコール）モノ（メタ）アクリレートオクタデシルエーテル、ポリ（エチレングリコール−プロピレングリコール）モノ（メタ）アクリレートノニルフェニルエーテル等が挙げられる。また、化合物（Ｂ）は２種類以上を併用しても良い。 Specific examples of the compound (a-2) having an alkylene oxide chain include, for example, polyethylene glycol mono (meth) acrylate, polypropylene glycol mono (meth) acrylate, polybutylene glycol mono (meth) acrylate, poly (ethylene glycol- Propylene glycol) mono (meth) acrylate, poly (ethylene glycol-tetramethylene glycol) mono (meth) acrylate, poly (propylene glycol-tetramethylene glycol) mono (meth) acrylate, polyethylene glycol mono (meth) acrylate monomethyl ether, polyethylene Glycol mono (meth) acrylate monobutyl ether, polyethylene glycol mono (meth) acrylate monooctyl ether, polyethylene glycol Cole mono (meth) acrylate monobenzyl ether, polyethylene glycol mono (meth) acrylate monophenyl ether, polyethylene glycol mono (meth) acrylate monodecyl ether, polyethylene glycol mono (meth) acrylate monododecyl ether, polyethylene glycol mono (meth) acrylate Monotetradecyl ether, polyethylene glycol mono (meth) acrylate monohexadecyl ether, polyethylene glycol mono (meth) acrylate monooctadecyl ether poly (ethylene glycol-propylene glycol) mono (meth) acrylate octyl ether, poly (ethylene glycol-propylene glycol) ) Mono (meth) acrylate octadecyl ether, poly (ethylene) Glycol - propylene glycol) mono (meth) acrylate nonylphenyl ether. Two or more kinds of compounds (B) may be used in combination.
＜（ａ−１）、（ａ−２）と共重合可能な化合物（ａ−３）＞
本発明で用いられる帯電防止性共重合体（Ａ）は、４級アンモニウム塩基を有する化合物（ａ−１）とアルキレンオキサイド鎖を有する化合物（ａ−２）とを必須の構成成分とし、さらに必要に応じて任意に前記（ａ−１）、（ａ−２）と共重合可能な化合物（ａ−３）をアルコール系溶剤（ｄ−１）中でラジカル共重合して得られる。
本発明における（ａ−１）、（ａ−２）と共重合可能な化合物（ａ−３）は、１つのエチレン性不飽和基を有する化合物であればよく、特に限定されるものでないが、例えば、メチル（メタ）アクリレート、エチル（メタ）アクリレート、プロピル（メタ）アクリレート、ブチル（メタ）アクリレート、２−エチルヘキシル（メタ）アクリレート、ドデシル（メタ）アクリレート、オクタデシル（メタ）アクリレート等のアルキル（メタ）アクリレート；ヒドロキシエチル（メタ）アクリレート、ヒドロキシプロピル（メタ）アクリレート、ヒドロキシブチル（メタ）アクリレート等のヒドロキシアルキル（メタ）アクリレート；ベンジル（メタ）アクリレート、シクロヘキシル（メタ）アクリレート、イソボルニル（メタ）アクリレート、ジシクロペンテニル（メタ）アクリレート、ジシクロペンテニルオキシエチル（メタ）アクリレート、エトキシエチル（メタ）アクリレート、エチルカルビトール（メタ）アクリレート、ブトキシエチル（メタ）アクリレート、シアノエチル（メタ）アクリレート、グリシジル（メタ）アクリレート等の各種（メタ）アクリレートやスチレン、メチルスチレン等が挙げられる。
<Compound (a-3) copolymerizable with (a-1) and (a-2)>
The antistatic copolymer (A) used in the present invention comprises the compound (a-1) having a quaternary ammonium base and the compound (a-2) having an alkylene oxide chain as essential constituent components, and further necessary. Depending on the above, the compound (a-3) copolymerizable with the above (a-1) and (a-2) can be obtained by radical copolymerization in an alcohol solvent (d-1).
The compound (a-3) copolymerizable with (a-1) and (a-2) in the present invention may be a compound having one ethylenically unsaturated group and is not particularly limited. For example, alkyl (meta) such as methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, dodecyl (meth) acrylate, octadecyl (meth) acrylate, etc. ) Acrylate; hydroxyalkyl (meth) acrylate such as hydroxyethyl (meth) acrylate, hydroxypropyl (meth) acrylate, hydroxybutyl (meth) acrylate; benzyl (meth) acrylate, cyclohexyl (meth) acrylate, isobornyl (meth) acrylate, Cyclopentenyl (meth) acrylate, dicyclopentenyloxyethyl (meth) acrylate, ethoxyethyl (meth) acrylate, ethyl carbitol (meth) acrylate, butoxyethyl (meth) acrylate, cyanoethyl (meth) acrylate, glycidyl (meth) acrylate And various (meth) acrylates such as styrene, methylstyrene and the like.
本発明で用いられる帯電防止性共重合体（Ａ）は、化合物（ａ−１）、（ａ−２）及び任意に（ａ−３）をアルコール系溶剤（ｄ−１）中でラジカル共重合して得ることができる。化合物（ａ−１）、（ａ−２）及び（ａ−３）の使用量は、ラジカル重合性化合物の合計１００重量％中、化合物（ａ−１）は、帯電防止性能の観点から、３０〜６０重量％、化合物（ａ−２）は、後述する３つ以上のエチレン性不飽和基を有する化合物（Ｂ）との相溶性の観点から、１０〜５０重量％であるのが好ましい。化合物（ａ−３）は、生成される帯電防止性共重合体（Ａ）の帯電防止性、溶解性、剛直性を整える目的で、必要に応じて０〜５０重量％の範囲で使用される。 The antistatic copolymer (A) used in the present invention is a radical copolymer of the compounds (a-1), (a-2) and optionally (a-3) in an alcohol solvent (d-1). Can be obtained. The compound (a-1), (a-2) and (a-3) are used in an amount of 30% in total of 100% by weight of the radical polymerizable compound, and the compound (a-1) is 30 from the viewpoint of antistatic performance. From 60 to 60% by weight, the compound (a-2) is preferably 10 to 50% by weight from the viewpoint of compatibility with the compound (B) having three or more ethylenically unsaturated groups described later. Compound (a-3) is used in the range of 0 to 50% by weight as necessary for the purpose of adjusting the antistatic property, solubility and rigidity of the resulting antistatic copolymer (A). .
帯電防止性共重合体（Ａ）は、前記量比で混合ざれた化合物（ａ−１）、（ａ−２）及び任意に（ａ−３）を、パーオキサイド系やアゾビス系等の重合開始剤を用いた溶液重合法等により得ることができる。
重合に際して用いる溶剤としては特に限定されないが、メチルアルコール、エチルアルコール、イソプロピルアルコール、ｎ−ブチルアルコール、イソブチルアルコール、シクロヘキシルアルコール、２−メトキシエタノール、２−エトキシエタノール、２−プロポキシエタノール、２−ブトキシエタノール、１−メトキシ−２−プロパノール、３−メトキシ−１−プロパノール、１−エトキシ−２−プロノール、２−エトキシ−１−プロノール及び３−エトキシ−１−プロノールからなる群より選ばれるアルコール系溶剤（ｄ−１）が好適に用いられる。これらは、１種単独であるいは２種以上を組み合わせて用いることができる。
The antistatic copolymer (A) is prepared by mixing the compounds (a-1), (a-2) and optionally (a-3) mixed at the above-mentioned quantitative ratios, such as peroxide-based or azobis-based polymers. It can be obtained by a solution polymerization method using an agent.
Although it does not specifically limit as a solvent used in superposition | polymerization, Methyl alcohol, ethyl alcohol, isopropyl alcohol, n-butyl alcohol, isobutyl alcohol, cyclohexyl alcohol, 2-methoxyethanol, 2-ethoxyethanol, 2-propoxyethanol, 2-butoxyethanol An alcohol solvent selected from the group consisting of 1-methoxy-2-propanol, 3-methoxy-1-propanol, 1-ethoxy-2-pronol, 2-ethoxy-1-pronol and 3-ethoxy-1-pronol ( d-1) is preferably used. These can be used alone or in combination of two or more.
帯電防止性共重合体（Ａ）の使用量は、後述する３つ以上のエチレン性不飽和基を有する化合物（Ｂ）１００重量部に対し、１〜２０重量部が好ましく、３〜１０重量部がより好ましい。１重量部未満では十分な帯電防止性能を得ることができず、２０重量部を超えると形成される帯電防止層の耐擦傷性や強靱性が低下する。 The amount of the antistatic copolymer (A) used is preferably 1 to 20 parts by weight, preferably 3 to 10 parts by weight, based on 100 parts by weight of the compound (B) having three or more ethylenically unsaturated groups described later. Is more preferable. If it is less than 1 part by weight, sufficient antistatic performance cannot be obtained, and if it exceeds 20 parts by weight, the scratch resistance and toughness of the antistatic layer formed are lowered.
次に本発明の帯電防止用コーティング組成物に用いられる３つ以上のエチレン性不飽和基を有する化合物（Ｂ）について説明する。
３つ以上のエチレン性不飽和基を有する化合物（Ｂ）は、分子中に少なくとも３つの以上の（メタ）アクリロイル基を有する架橋反応性化合物であり、その分子内にエーテル結合、チオエーテル結合、エステル結合、アミド結合、ウレタン結合等を含むことができる。
Next, the compound (B) having three or more ethylenically unsaturated groups used in the antistatic coating composition of the present invention will be described.
The compound (B) having three or more ethylenically unsaturated groups is a cross-linking reactive compound having at least three or more (meth) acryloyl groups in the molecule, and has an ether bond, a thioether bond, an ester in the molecule. Bonds, amide bonds, urethane bonds and the like can be included.
３つ以上のエチレン性不飽和基を有する化合物（Ｂ）としては、具体的には例えば、ペンタエリスリトールトリ（メタ）アクリレート、ペンタエリスリトールテトラ（メタ）アクリレート、トリメチロールプロパントリ（メタ）アクリレート、ＥＯ変性トリメチロールプロパントリ（メタ）アクリレート、ＰＯ変性トリメチロールプロパントリ（メタ）アクリレート、トリス（アクリロキシエチル）イソシアヌレート、カプロラクトン変性トリス（アクリロキシエチル）イソシアヌレート、トリメチロールエタントリ（メタ）アクリレート、ジペンタエリスリトールテトラ（メタ）アクリレート、ジペンタエリスリトールペンタ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート、アルキル変性ジペンタエリスリトールトリ（メタ）アクリレート、アルキル変性ジペンタエリスリトールテトラ（メタ）アクリレート、アルキル変性ジペンタエリスリトールペンタ（メタ）アクリレート、カプロラクトン変性ジペンタエリスリトールヘキサ（メタ）アクリレート、１，２，３−シクロヘキサンテトラ（メタ）アクリレート等の、多価アルコールと（メタ）アクリル酸とのエステル化合物；
ポリウレタンポリ（メタ）アクリレート、ポリエステルポリ（メタ）アクリレート、ポリエーテルポリ（メタ）アクリレート、ポリアクリルポリ（メタ）アクリレート、ポリアルキッドポリ（メタ）アクリレート、ポリエポキシポリ（メタ）アクリレート、ポリスピロアセタールポリ（メタ）アクリレート、ポリブタジエンポリ（メタ）アクリレート、ポリチオールポリエンポリ（メタ）アクリレート、ポリシリコンポリ（メタ）アクリレート等の多官能化合物のポリ（メタ）アクリレート化合物；
多価アルコールと多塩基酸および（メタ）アクリル酸とから合成されるエステル化合物、例えばトリメチロールエタン／コハク酸／アクリル酸＝２／１／４（モル比）から合成されるエステル化合物等が挙げられる。
なお、本発明において、（メタ）アクリレートとは、アクリレート、メタクリレートの併記を略したものである。化合物（ａ−１）、（ａ−２）に関する説明においても同様である。
Specific examples of the compound (B) having three or more ethylenically unsaturated groups include pentaerythritol tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, trimethylolpropane tri (meth) acrylate, and EO. Modified trimethylolpropane tri (meth) acrylate, PO modified trimethylolpropane tri (meth) acrylate, tris (acryloxyethyl) isocyanurate, caprolactone modified tris (acryloxyethyl) isocyanurate, trimethylolethane tri (meth) acrylate, Dipentaerythritol tetra (meth) acrylate, dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate, alkyl-modified dipentaerythritol Rutri (meth) acrylate, alkyl-modified dipentaerythritol tetra (meth) acrylate, alkyl-modified dipentaerythritol penta (meth) acrylate, caprolactone-modified dipentaerythritol hexa (meth) acrylate, 1,2,3-cyclohexanetetra (meth) Ester compounds of polyhydric alcohols and (meth) acrylic acid, such as acrylates;
Polyurethane poly (meth) acrylate, polyester poly (meth) acrylate, polyether poly (meth) acrylate, polyacryl poly (meth) acrylate, polyalkyd poly (meth) acrylate, polyepoxy poly (meth) acrylate, polyspiroacetal poly Poly (meth) acrylate compounds of polyfunctional compounds such as (meth) acrylate, polybutadiene poly (meth) acrylate, polythiol polyene poly (meth) acrylate, polysilicon poly (meth) acrylate;
An ester compound synthesized from a polyhydric alcohol, a polybasic acid and (meth) acrylic acid, such as an ester compound synthesized from trimethylolethane / succinic acid / acrylic acid = 2/4 (molar ratio), etc. It is done.
In the present invention, (meth) acrylate is an abbreviation of acrylate and methacrylate. The same applies to the description of the compounds (a-1) and (a-2).
これら３つ以上のエチレン性不飽和基を有する化合物（Ｂ）は、単独または２種以上の混合物として用いることができる。
なお、２つ以下のエチレン性不飽和基を有する化合物も、形成される帯電防止層に要求される耐擦傷性や強靱性を満足する範囲で使用することができる。
These compounds (B) having three or more ethylenically unsaturated groups can be used alone or as a mixture of two or more.
A compound having two or less ethylenically unsaturated groups can also be used within the range satisfying the scratch resistance and toughness required for the antistatic layer to be formed.
本発明における光重合開始剤（Ｃ）は、光励起によってラジカル重合を開始できる機能を有するものであれば特に限定はなく、例えばアセトフェノン化合物、ベンゾイン化合物、ベンゾフェノン化合物、ホスフィンオキシド化合物、ケタール化合物、アントラキノン化合物、チオキサントン化合物等が挙げられる。具体的には、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインイソプロピルエーテル、ベンゾインブチルエーテル、ジエトキシアセトフェノン、ベンジルジメチルケタール、１−ヒドロキシシクロヘキシルフェニルケトン、ベンゾフェノン、２，４，６−トリメチルベンゾインジフェニルホスフィンオキシド、Ｎ，Ｎ−ジメチルアミノ安息香酸イソアミル、２−クロロチオキサントン、２，４−ジエチルチオキサントン等が挙げられる。また、増感剤として公知の有機アミンを加えることもできる。 The photopolymerization initiator (C) in the present invention is not particularly limited as long as it has a function capable of initiating radical polymerization by photoexcitation. For example, acetophenone compound, benzoin compound, benzophenone compound, phosphine oxide compound, ketal compound, anthraquinone compound And thioxanthone compounds. Specifically, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, benzoin butyl ether, diethoxyacetophenone, benzyldimethyl ketal, 1-hydroxycyclohexyl phenyl ketone, benzophenone, 2,4,6-trimethylbenzoin diphenylphosphine oxide, N , N-dimethylaminobenzoate isoamyl, 2-chlorothioxanthone, 2,4-diethylthioxanthone and the like. Moreover, a well-known organic amine can also be added as a sensitizer.
光重合開始剤（Ｃ）の使用量は、前述の３つ以上のエチレン性不飽和基を有する化合物（Ｂ）１００重量部に対し、０．１〜２０重量部が好ましく、１〜１０重量部がより好ましい。０．１重量％未満では重合開始効果が得られず、２０重量％を超えるとハードコート性が低下する恐れがある。 The amount of the photopolymerization initiator (C) used is preferably 0.1 to 20 parts by weight, preferably 1 to 10 parts by weight with respect to 100 parts by weight of the compound (B) having three or more ethylenically unsaturated groups. Is more preferable. If it is less than 0.1% by weight, the polymerization initiation effect cannot be obtained, and if it exceeds 20% by weight, the hard coat property may be lowered.
次に、本発明における溶剤（Ｄ）について説明する。
従来、帯電防止用コーティング組成物に使用される溶剤は、親水性の高い帯電防止性共重合体と疎水性の高い光硬化性組成物を相溶させるため、アルコール等の高極性溶剤とエーテル、ケトン、エステル、炭化水素等の低極性溶剤を混合するのが一般的であった。
本発明では、帯電防止性共重合体（Ａ）と３つ以上のエチレン性不飽和基を有する化合物（Ｂ）との相溶性の観点から、高極性溶剤としてアルコール系溶剤（ｄ−１）と、低極性溶剤として炭素数３〜５のアセテート系溶剤（ｄ−２）を併用することによって、十分な帯電防止性能を保ちつつハードコート性能を大きく向上させることができるようになった。
Next, the solvent (D) in the present invention will be described.
Conventionally, the solvent used for the antistatic coating composition is a highly polar solvent such as alcohol and ether, in order to make the highly hydrophilic antistatic copolymer and the highly hydrophobic photocurable composition compatible. It has been common to mix low polar solvents such as ketones, esters and hydrocarbons.
In the present invention, from the viewpoint of compatibility between the antistatic copolymer (A) and the compound (B) having three or more ethylenically unsaturated groups, the alcohol solvent (d-1) Further, by using the acetate solvent (d-2) having 3 to 5 carbon atoms as a low polarity solvent, the hard coat performance can be greatly improved while maintaining sufficient antistatic performance.
即ち、低極性溶剤として、アセテート以外の溶剤、例えばエステル、エーテル、ケトン、炭化水素系溶剤等を用いると、耐擦傷性が低下したり、温水浸漬試験で帯電防止性が低下したりする場合がある。この現象は特に透明支持体として、トリアセチルセルロースを用いた場合に顕著である。原因は明確ではないが、アセテート以外の上記の低極性溶剤を多量に用いると、乾燥の工程で帯電防止性共重合体（Ａ）が塗膜表面に著しく局在化し、塗膜表面の架橋密度が低下するためと推察される。
また、アセテート系溶剤であっても炭素数６以上のアセテート系溶剤では、アルコール系溶剤（ｄ−１）に比べ、エステルの揮発速度が遅く、帯電防止性共重合体（Ａ）の表面局在化が上手く起こらず、帯電防止性が低下したり、膜が白化したりするなどの不具合が生じる。
That is, if a solvent other than acetate, such as an ester, ether, ketone, or hydrocarbon solvent, is used as the low-polarity solvent, the scratch resistance may decrease or the antistatic property may decrease in the hot water immersion test. is there. This phenomenon is particularly remarkable when triacetyl cellulose is used as the transparent support. Although the cause is not clear, when a large amount of the above low-polarity solvent other than acetate is used, the antistatic copolymer (A) is remarkably localized on the coating surface in the drying step, and the crosslinking density on the coating surface Is presumed to decrease.
Moreover, even if it is an acetate type solvent, in the case of an acetate type solvent having 6 or more carbon atoms, the volatilization rate of the ester is slower than that of the alcohol type solvent (d-1), and the surface localization of the antistatic copolymer (A). Does not occur well, resulting in problems such as reduced antistatic properties and whitening of the film.
本発明におけるアルコール系溶剤（ｄ−１）としては、帯電防止性共重合体（Ａ）を得る際に用い得る溶剤として例示したものが同様に例示でき、１種単独であるいは２種以上を組み合わせて用いることができる。 As the alcohol solvent (d-1) in the present invention, those exemplified as the solvent that can be used in obtaining the antistatic copolymer (A) can be exemplified in the same manner, one kind alone or a combination of two or more kinds. Can be used.
炭素数３〜５のアセテート系溶剤（ｄ−２）としては、酢酸メチル、酢酸エチル、酢酸プロピルが挙げられる。これらは、１種単独であるいは２種以上を組み合わせて用いることができる。 Examples of the acetate solvent (d-2) having 3 to 5 carbon atoms include methyl acetate, ethyl acetate, and propyl acetate. These can be used alone or in combination of two or more.
本発明の帯電防止用コーティング組成物は、帯電防止性共重合体（Ａ）の溶液に、帯電防止性共重合体（Ａ）生成時に用いたのと同じアルコール系溶剤（ｄ−１）及びアセテート系溶剤（ｄ−２）を加えて得ることもできるし、共重合体（Ａ）生成時に用いたのとは異なるアルコール系溶剤（ｄ−１）及びアセテート系溶剤（ｄ−２）を加えて得ることもできる。あるいは、帯電防止性共重合体（Ａ）のアルコール系溶剤（ｄ−１）溶液に、アセテート系溶剤（ｄ−２）を加えることで、塗工に好適な粘度の帯電防止用コーティング組成物を得ることもできる。 The antistatic coating composition of the present invention comprises the same alcohol solvent (d-1) and acetate used in the solution of the antistatic copolymer (A) as used in the production of the antistatic copolymer (A). It can also be obtained by adding a system solvent (d-2), or by adding an alcohol solvent (d-1) and an acetate solvent (d-2) different from those used in the production of the copolymer (A). It can also be obtained. Alternatively, an antistatic coating composition having a viscosity suitable for coating is obtained by adding an acetate solvent (d-2) to an alcohol solvent (d-1) solution of the antistatic copolymer (A). It can also be obtained.
本発明の帯電防止用コーティング組成物は、溶剤（Ｄ）として、前記アルコール系溶剤（ｄ−１）及び炭素数３〜５のアセテート系溶剤（ｄ−２）と共に、任意のエーテル、ケトン、エステル、炭化水素等の溶剤を、本発明の目的を損なわない範囲で用いることができる。具体的には、溶剤１００重量％中に、その他の溶剤は２０重量％以下であることが好ましい。
例えば、トリアセチルセルロース支持体を溶解し、密着性を付与する溶剤として、１，３−ジオキソラン、１，４−ジオキサン、テトラヒドロフラン等のエーテル類；アセトン、メチルエチルケトン、シクロヘキサノン、ジアセトンアルコール等のケトン類；ジメチルカーボネート、ジエチルカーボネート等の炭酸エステル類等が知られている。これらを、１種単独であるいは２種以上を組み合わせて用いることができる。
The antistatic coating composition of the present invention comprises an arbitrary ether, ketone or ester as the solvent (D) together with the alcohol solvent (d-1) and the acetate solvent (d-2) having 3 to 5 carbon atoms. A solvent such as hydrocarbon can be used as long as the object of the present invention is not impaired. Specifically, the other solvent is preferably 20% by weight or less in 100% by weight of the solvent.
For example, as a solvent for dissolving a triacetyl cellulose support and imparting adhesion, ethers such as 1,3-dioxolane, 1,4-dioxane and tetrahydrofuran; ketones such as acetone, methyl ethyl ketone, cyclohexanone and diacetone alcohol Carbonic acid esters such as dimethyl carbonate and diethyl carbonate are known. These can be used alone or in combination of two or more.
帯電防止用コーティング組成物中の溶剤（Ｄ）の含有量は、特に制限はないが、一般的に、組成物の粘度、レベリング性、乾燥性の観点から、（Ａ）〜（Ｄ）の合計１００重量％中に、３０〜８０重量％含まれるのが好ましく、３０〜６０重量％含まれることがより好ましい。
そして、前記溶剤（Ｄ）の１００重量％中、アルコール系溶剤（ｄ−１）の含有量は５〜２５重量％、炭素数３〜５のアセテート系溶剤（ｄ−２）の含有量が５５〜９０重量％であることが好ましく、アルコール系溶剤（ｄ−１）は１０〜２０重量％、アセテート系溶剤（ｄ−２）は６５〜８５重量％であることがより好ましい。
Although there is no restriction | limiting in particular in content of the solvent (D) in the coating composition for antistatic, Generally, it is the sum total of (A)-(D) from a viewpoint of the viscosity of a composition, leveling property, and drying property. It is preferable that 30 to 80% by weight is contained in 100% by weight, and more preferably 30 to 60% by weight.
In 100% by weight of the solvent (D), the content of the alcohol solvent (d-1) is 5 to 25% by weight, and the content of the acetate solvent (d-2) having 3 to 5 carbon atoms is 55%. It is preferable that it is -90 weight%, It is more preferable that alcoholic solvent (d-1) is 10-20 weight%, and acetate-based solvent (d-2) is 65-85 weight%.
アルコール系溶剤（ｄ−１）の含有量が５重量％未満では帯電防止性共重合体（Ａ）の溶解度が不足し、コーティング組成物中で沈殿物を生じたり、塗膜中で析出し、ゆず肌や白化などの不具合を生じる場合がある。一方、２５重量％を超えると、３つ以上のエチレン性不飽和基を有する化合物（Ｂ）の溶解度が不足し、コーティング組成物の粘度が高くなり塗工適性が低下したり、帯電防止性共重合体（Ａ）の表面局在化が起こりにくく、帯電防止性能が低下したりする恐れがある。 When the content of the alcoholic solvent (d-1) is less than 5% by weight, the solubility of the antistatic copolymer (A) is insufficient, and precipitates are formed in the coating composition or deposited in the coating film. May cause problems such as cirrhosis and whitening. On the other hand, if it exceeds 25% by weight, the solubility of the compound (B) having three or more ethylenically unsaturated groups is insufficient, the viscosity of the coating composition is increased, the coating suitability is lowered, and the antistatic property is not improved. The surface localization of the polymer (A) hardly occurs, and the antistatic performance may be lowered.
また、炭素数３〜５のアセテート系溶剤（ｄ−２）が５５重量％未満の場合、（ｄ−１）及び（ｄ−２）と共に用いられる任意のその他の溶剤の量が相対的に多くなる結果、硬化塗膜の耐擦傷性が低下したり、温水浸漬試験で帯電防止性が低下したりする場合がある。アセテート系溶剤（ｄ−２）が９０重量％を超えると帯電防止性共重合体（Ａ）の溶解度が不足し、コーティング組成物中で沈殿物を生じたり、塗膜中で析出し、ゆず肌になったり、白化したりするなどの不具合を生じる場合がある。 Further, when the amount of the C3-C5 acetate solvent (d-2) is less than 55% by weight, the amount of any other solvent used together with (d-1) and (d-2) is relatively large. As a result, the scratch resistance of the cured coating film may decrease, or the antistatic property may decrease in the hot water immersion test. If the acetate solvent (d-2) exceeds 90% by weight, the solubility of the antistatic copolymer (A) is insufficient, and precipitates are formed in the coating composition or deposited in the coating film. May cause problems such as becoming white or whitening.
本発明の帯電防止コーティング用組成物には必要に応じて、光増感剤、光安定剤、紫外線吸収剤、触媒、着色剤、滑剤、レベリング剤、消泡剤、重合禁止剤、重合促進剤、酸化防止剤、難燃剤、赤外線吸収剤、界面活性剤、表面改質剤、チキソトロピー剤、球状フィラー等を添加することができる。 If necessary, the antistatic coating composition of the present invention includes a photosensitizer, a light stabilizer, an ultraviolet absorber, a catalyst, a colorant, a lubricant, a leveling agent, an antifoaming agent, a polymerization inhibitor, and a polymerization accelerator. Antioxidants, flame retardants, infrared absorbers, surfactants, surface modifiers, thixotropic agents, spherical fillers, and the like can be added.
本発明の帯電防止コーティング用組成物は、各種の支持体へ塗工し、帯電防止層付き部材を得ることができる。本発明の帯電防止コーティング用組成物は、プラスチックフィルムに塗工し帯電防止フィルムとして使用することが好ましい。また、必要に応じて、高屈折率層、低屈折率層、近赤外吸収層、電磁波シールド層など公知の機能層が帯電防止層の上層や下層に形成されていてもよい。 The antistatic coating composition of the present invention can be applied to various supports to obtain a member with an antistatic layer. The antistatic coating composition of the present invention is preferably applied to a plastic film and used as an antistatic film. Further, a known functional layer such as a high refractive index layer, a low refractive index layer, a near infrared absorption layer, and an electromagnetic wave shielding layer may be formed in the upper layer or the lower layer of the antistatic layer as necessary.
本発明において基材上に帯電防止層を形成する方法としては、帯電防止コーティング用組成物を、バーコーティング、ブレードコーティング、スピンコーティング、リバースコーティング、ダイティング、スプレーコーティング、ロールコーティング、グラビアコーティング、マイクログラビアコーティング、リップコーティング、エアーナイフコーティング、ディッピング法等の塗工方法で基材樹脂表面に塗工した後、必要に応じ溶剤を乾燥させ、さらに紫外線等の活性エネルギー線を照射し、塗工した帯電防止コーティング組成物を架橋硬化させる方法が挙げられる。
前記活性エネルギー線としては、キセノンランプ、低圧水銀灯、高圧水銀灯、超高圧水銀灯、メタルハライドランプ、カーボンアーク灯、タングステンランプ等の光源から発せられる紫外線あるいは、通常２０〜２０００ＫｅＶのコックロフワルトン型、バンデグラフ型、共振変圧型、絶縁コア変圧器型、直線型、ダイナミトロン型、高周波型等の電子線加速器から取り出される電子線、α線、β線、γ等を用いることができる。
In the present invention, the antistatic layer is formed on the substrate by coating the antistatic coating composition with a bar coating, a blade coating, a spin coating, a reverse coating, a diting, a spray coating, a roll coating, a gravure coating, a micro coating. After coating on the surface of the base resin with a coating method such as gravure coating, lip coating, air knife coating, dipping method, etc., the solvent was dried if necessary, and further irradiated with active energy rays such as ultraviolet rays. A method of crosslinking and curing the antistatic coating composition is exemplified.
Examples of the active energy ray include ultraviolet rays emitted from a light source such as a xenon lamp, a low-pressure mercury lamp, a high-pressure mercury lamp, an ultra-high pressure mercury lamp, a metal halide lamp, a carbon arc lamp, and a tungsten lamp, or a Cockrowalton type or a bandegraph type usually 20 to 2000 KeV. Electron beams extracted from electron beam accelerators such as resonance transformer type, insulated core transformer type, linear type, dynamitron type, and high frequency type, α rays, β rays, γ, etc. can be used.
前記方法で得られる帯電防止層の膜厚は、特に限定されないが、通常１〜２０μｍ、好ましくは３〜１０μｍである。帯電防止層の膜厚が３μｍ未満では鉛筆硬度や耐擦傷性が低下する恐れがあり、１０μｍを超える場合は、クラックが発生するおそれがある。 Although the film thickness of the antistatic layer obtained by the said method is not specifically limited, Usually, 1-20 micrometers, Preferably it is 3-10 micrometers. If the film thickness of the antistatic layer is less than 3 μm, the pencil hardness and scratch resistance may be reduced, and if it exceeds 10 μm, cracks may occur.
本発明において、支持体（基材ともいう）としては、特に限定はなく、ガラス、合成樹脂成型物、フィルム支持体などが挙げられる。
合成樹脂成型物としては、ポリメチルメタクリレートまたはメチルメタクリレートを主構成成分とする共重合体製、ポリスチレン製、スチレン−メチルメタクリレート共重合体製、スチレン−アクリロニトリル共重合体製、ポリカーボネート製、セルロースアセテートブチレート樹脂製、ポリアリルジグリコールカーボネート樹脂製、ポリ塩化ビニル樹脂製、ポリエステル樹脂製のフィルム以外の成型物等が挙げられる。
また、フィルム支持体としては、例えば、ポリエステルフィルム、ポリエチレンフィルム、ポリプロピレンフィルム、セロファンフィルム、ジアセチルセルロースフィルム、トリアセチルセルロースフィルム、アセチルセルロースブチレートフィルム、ポリ塩化ビニルフィルム、ポリ塩化ビニリデンフィルム、ポリビニルアルコールフィルム、エチレンビニルアルコールフィルム、ポリオレフィンフィルム、ポリスチレンフィルム、ポリカーボネートフィルム、ポリメチルペンテルフィルム、ポリスルフォンフィルム、ポリエーテルエーテルケトンフィルム、ポリエーテルスルフォンフィルム、ポリエーテルイミドフィルム、ポリイミドフィルム、フッ素樹脂フィルム、ナイロンフィルム、アクリルフィルム等が挙げられる。
なお、フィルムを支持体として使用する場合、フィルムに更にアクリル系樹脂、共重合ポリエステル系樹脂、ポリウレタン系樹脂、スチレン−マレイン酸グラフトポリエステル樹脂、アクリルグラフトポリエステル樹脂等の樹脂層を設けたいわゆる易接着タイプのフィルムも用いることができる。
In the present invention, the support (also referred to as a base material) is not particularly limited, and examples thereof include glass, a synthetic resin molded product, and a film support.
Synthetic resin moldings include polymethyl methacrylate or methyl methacrylate copolymer, polystyrene, styrene-methyl methacrylate copolymer, styrene-acrylonitrile copolymer, polycarbonate, cellulose acetate butyrate Examples include molded products other than films made of rate resins, polyallyl diglycol carbonate resins, polyvinyl chloride resins, and polyester resins.
Examples of the film support include polyester film, polyethylene film, polypropylene film, cellophane film, diacetyl cellulose film, triacetyl cellulose film, acetyl cellulose butyrate film, polyvinyl chloride film, polyvinylidene chloride film, and polyvinyl alcohol film. , Ethylene vinyl alcohol film, polyolefin film, polystyrene film, polycarbonate film, polymethylpentel film, polysulfone film, polyetheretherketone film, polyethersulfone film, polyetherimide film, polyimide film, fluororesin film, nylon film, An acrylic film etc. are mentioned.
In addition, when using a film as a support, a so-called easy adhesion in which a resin layer such as an acrylic resin, a copolyester resin, a polyurethane resin, a styrene-maleic acid graft polyester resin, or an acrylic graft polyester resin is further provided on the film. A type of film can also be used.
本発明の帯電防止コーティング剤は透明性、帯電防止性、耐擦傷性に優れ、さらに、浸水後の耐久性にも優れている。
透明性は、ＨＡＺＥで評価することができ、１０％以下が好ましく、より好ましくは５％以下である。
帯電防止性は、表面抵抗値で評価することができ、５×１０１２Ω／□以下が好ましい。
また、耐擦傷性は傷の本数で評価することができ、５本以下が好ましく、より好ましくは０本である。
また、本発明によれば、温水浸後にこれらの諸物性を保つことが可能である。これらの効果は、支持体としてトリアセチルセルロース（ＴＡＣ）フィルムを使用した場合に特に耐擦傷性の点で顕著であり、本発明の帯電防止コーティング組成物は、ＬＣＤやＰＤＰ等の光学ディスプレイ用途、プラスチック成型品の表面コート用途など、帯電防止性に加えてハードコート性と透明性が要求される各種用途に好適に使用できる。
The antistatic coating agent of the present invention is excellent in transparency, antistatic properties, and scratch resistance, and is also excellent in durability after water immersion.
Transparency can be evaluated by HAZE, preferably 10% or less, more preferably 5% or less.
The antistatic property can be evaluated by a surface resistance value, and is preferably 5 × 10 12 Ω / □ or less.
The scratch resistance can be evaluated by the number of scratches, preferably 5 or less, more preferably 0.
Further, according to the present invention, it is possible to maintain these physical properties after immersion in warm water. These effects are particularly remarkable in terms of scratch resistance when a triacetyl cellulose (TAC) film is used as a support, and the antistatic coating composition of the present invention is used for optical displays such as LCD and PDP, It can be suitably used for various applications that require hard coat properties and transparency in addition to antistatic properties, such as surface coating applications for plastic molded products.
以下に、実施例により、本発明をさらに具体的に説明するが、以下の実施例は本発明の権利範囲を何ら制限するものではない。なお、実施例における「部」は、「重量部」を表す。 The present invention will be described more specifically with reference to the following examples. However, the following examples do not limit the scope of rights of the present invention. In the examples, “part” represents “part by weight”.
（合成例１）
〈アルキレンオキサイド鎖を有する化合物（ａ−２−１）の製造〉
攪拌装置、温度計、アルキレンオキサイド導入管、並びに、窒素ガス導入管を備えたオートクレーブに、ドデカノール３５２．５部、トルエン７１３部、および、水酸化カリウム２部を仕込み、系中を窒素ガスにて置換した後、反応容器内圧力８ｋｇｆ／ｃｍ２以下、温度９０℃以下でエチレンオキサイド２５００部（ドデカノールに対して３０倍モル）を４時間かけて圧入し、さらに９０℃で５時間反応させた。次に空気を通じて未反応のエチレンオキサイドを除去した後、協和化学工業（株）製キョーワード６００［アルカリ（土類）金属水酸化物の吸着除剤］を４２．０部加え、乾燥空気５ｋＰａ、３０℃の条件にて２時間処理後、濾別し、得られた濾液からトルエンを加熱減圧によって除去し、ポリエチレンオキサイド付加アルコールを得た。
得られたポリエチレンオキサイド付加アルコール３００．９部を攪拌装置、温度計、空気導入管、液体添加ラインおよび精留塔を取り付けたフラスコに移し、メタクリル酸メチル２００部（ポリエチレンオキサイド付加アルコールに対して１０倍モル）、ヒドロキノンモノメチルエーテル０．０４部仕込み、乾燥空気を吹き込みながら、８０℃に加熱した後、オルトチタン酸テトライソプロピル０．２部を１時間毎に加え、エステル交換反応させた。反応中、必要に応じて副生するメタノールとメタクリル酸メチルを共沸混合物として反応系外へ留去させた。４時間後、アルコール転化率が９５％になったところで反応を終了した。
得られた溶液を冷却し、水洗、脱水、濃縮を行い、濾過してエチレンオキサイド基数３０とドデシル基を有する化合物（ａ−２−１）を得た。
なお、アルキレンオキサイド基数は、アルキレンオキサイド付加工程において使用したアルキレンオキサイドとアルコールとのモル比（理論値）をもって表す。
(Synthesis Example 1)
<Production of Compound (a-2-1) Having Alkylene Oxide Chain>
An autoclave equipped with a stirrer, thermometer, alkylene oxide introduction tube, and nitrogen gas introduction tube was charged with 352.5 parts of dodecanol, 713 parts of toluene, and 2 parts of potassium hydroxide, and the system was filled with nitrogen gas. After the substitution, 2500 parts of ethylene oxide (30-fold mol with respect to dodecanol) was injected over 4 hours at an internal pressure of the reaction vessel of 8 kgf / cm 2 or less and a temperature of 90 ° C. or less, and further reacted at 90 ° C. for 5 hours. Next, after removing unreacted ethylene oxide through air, Kyowa Chemical Industry Co., Ltd. Kyoward 600 [adsorption remover of alkali (earth) metal hydroxide] 42.0 parts, dry air 5kPa, After treatment for 2 hours at 30 ° C., filtration was performed, and toluene was removed from the obtained filtrate by heating under reduced pressure to obtain polyethylene oxide-added alcohol.
300.9 parts of the resulting polyethylene oxide-added alcohol was transferred to a flask equipped with a stirrer, thermometer, air introduction tube, liquid addition line, and rectification column, and 200 parts of methyl methacrylate (10 parts per 10 parts of polyethylene oxide-added alcohol). 2 times mol), 0.04 part of hydroquinone monomethyl ether was charged, heated to 80 ° C. while blowing dry air, and then 0.2 part of tetraisopropyl orthotitanate was added every 1 hour for ester exchange reaction. During the reaction, methanol and methyl methacrylate, which are by-produced as necessary, were distilled out of the reaction system as an azeotropic mixture. After 4 hours, the reaction was terminated when the alcohol conversion reached 95%.
The obtained solution was cooled, washed with water, dehydrated and concentrated, and filtered to obtain a compound (a-2-1) having 30 ethylene oxide groups and a dodecyl group.
In addition, the number of alkylene oxide groups is represented by the molar ratio (theoretical value) of the alkylene oxide and alcohol used in the alkylene oxide addition step.
〈帯電防止性共重合体（Ａ−１）の製造（共重合過程）〉
攪拌翼、還流冷却器、およびガス導入口を供えたフラスコに、前記で合成した（ａ−２−１）３０部、メタクリロイルオキシエチルトリメチルアンモニウムクロライド５０部、メチルメタクリレート２０部、アゾビスイソブチロニトリル１．５部、エタノール２３３部を仕込み、窒素気流下、７０℃で８時間反応した。反応終了後、冷却し、帯電防止性共重合体（Ａ−１）のエタノール溶液（固形分３０重量％）を得た。
<Production of antistatic copolymer (A-1) (copolymerization process)>
In a flask equipped with a stirring blade, a reflux condenser, and a gas inlet, 30 parts of (a-2-1) synthesized above, 50 parts of methacryloyloxyethyltrimethylammonium chloride, 20 parts of methyl methacrylate, azobisisobutyro 1.5 parts of nitrile and 233 parts of ethanol were charged and reacted at 70 ° C. for 8 hours under a nitrogen stream. After completion of the reaction, the mixture was cooled to obtain an ethanol solution (solid content 30% by weight) of the antistatic copolymer (A-1).
（合成例２）
合成例１のアルキレンオキサイド付加工程において、ドデカノールの代わりにオクタノールを２４６．４部使用し、トルエンの量を３９３．０部に変更した。また、エチレンオキサイド２５００部の代わりに、エチレンオキサイド６６６．７部（オクタノールに対して８倍モル）を２時間かけて圧入後、続いてプロピレンオキサイド６５９．２部（オクタノールに対して６倍モル）を２時間かけて圧入した。また、エステル化工程において、前記アルキレンオキサイド付加工程で得られたポリエチレン・ポリプロピレンオキサイド付加アルコールを１６５．８部用いた以外は合成例１と同様の操作を行い、エチレンオキサイド基数8、プロピレンオキサイド基数６とオクチル基を有する化合物（ａ−２−２）を得た。さらに共重合過程において、化合物（ａ−２−１）を前記化合物（ａ−２−２）へ変更した以外は、合成例１と同様の操作を行い、帯電防止性共重合体（Ａ−２）のエタノール溶液（固形分３０重量％）を得た。
(Synthesis Example 2)
In the alkylene oxide addition step of Synthesis Example 1, 246.4 parts of octanol was used instead of dodecanol, and the amount of toluene was changed to 393.0 parts. Also, instead of 2500 parts of ethylene oxide, 666.7 parts of ethylene oxide (8-fold mol with respect to octanol) was injected over 2 hours, and then 659.2 parts of propylene oxide (6-fold mol with respect to octanol). Was pressed in over 2 hours. In the esterification step, the same operation as in Synthesis Example 1 was performed except that 165.8 parts of the polyethylene / polypropylene oxide addition alcohol obtained in the alkylene oxide addition step was used, and the number of ethylene oxide groups was 8, and the number of propylene oxide groups was 6. And a compound (a-2-2) having an octyl group. Further, in the copolymerization process, the same operation as in Synthesis Example 1 was carried out except that the compound (a-2-1) was changed to the compound (a-2-2), and the antistatic copolymer (A-2) ) Ethanol solution (solid content 30% by weight).
（合成例３）
合成例１の共重合過程において、メチルメタクリレートをラウリルメタクリレートへ変更した以外は、合成例１と同様の操作を行い、帯電防止性共重合体（Ａ−３）のエタノール溶液（固形分３０重量％）を得た。
(Synthesis Example 3)
In the copolymerization process of Synthesis Example 1, the same operation as in Synthesis Example 1 was performed except that methyl methacrylate was changed to lauryl methacrylate, and an antistatic copolymer (A-3) solution in ethanol (solid content 30 wt%) )
（合成例４）
合成例１のアルキレンオキサイド付加工程において、ドデカノールの代わりにオクタノールを２４６．４部使用し、エチレンオキサイド８３３．３部（オクタノールに対して１０倍モル）、トルエンの量を２６９．９部に変更、また、エステル化工程において、ポリエチレンオキサイド付加アルコールの量を１１３．９部とした以外は合成例１と同様の操作を行い、エチレンオキサイド基数１０とオクチル基を有する化合物（ａ−２−３）を得た。さらに共重合過程において、化合物（ａ−２−１）を前記化合物（ａ−２−３）に、メチルメタクリレートをラウリルメタクリレートへ変更した以外は、合成例１と同様の操作を行い、帯電防止性共重合体（Ａ−４）のエタノール溶液（固形分３０重量％）を得た。
(Synthesis Example 4)
In the alkylene oxide addition step of Synthesis Example 1, 246.4 parts of octanol was used instead of dodecanol, 833.3 parts of ethylene oxide (10-fold mol relative to octanol), and the amount of toluene was changed to 269.9 parts. In the esterification step, the same procedure as in Synthesis Example 1 was performed except that the amount of polyethylene oxide-added alcohol was 113.9 parts, and the compound (a-2-3) having 10 ethylene oxide groups and an octyl group was obtained. Obtained. Further, in the copolymerization process, the same operation as in Synthesis Example 1 was carried out except that the compound (a-2-1) was changed to the compound (a-2-3) and methyl methacrylate was changed to lauryl methacrylate. An ethanol solution (solid content: 30% by weight) of copolymer (A-4) was obtained.
（合成例５）
合成例１の共重合過程において、化合物（ａ−２−１）を合成例４で得られた化合物（ａ−２−３）に、メチルメタクリレートをシクロヘキシルメタクリレートへ変更した以外は、合成例１と同様の操作を行い、帯電防止性共重合体（Ａ−５）のエタノール溶液（固形分３０重量％）を得た。
(Synthesis Example 5)
In the copolymerization process of Synthesis Example 1, except that Compound (a-2-1) was changed to Compound (a-2-3) obtained in Synthesis Example 4 and methyl methacrylate was changed to cyclohexyl methacrylate, Synthesis Example 1 and The same operation was performed to obtain an ethanol solution (solid content: 30% by weight) of the antistatic copolymer (A-5).
（合成例６）
合成例１のアルキレンオキサイド付加工程において、ドデカノールの代わりにステアリルアルコールを５１１．７部使用し（ステアリルアルコールに対して３０倍モルのエチレンオキサイドを使用）、トルエンの量を７５２．９部に変更、また、エステル化工程において、ポリエチレンオキサイド付加アルコールの量を３１７．７部とした以外は合成例１と同様の操作を行い、エチレンオキサイド基数３０とオクタデシル基を有する化合物（ａ−２−４）を得た。さらに共重合過程において、化合物（ａ−２−１）を前記化合物（ａ−２−４）に、メチルメタクリレートをシクロヘキシルメタクリレートへ変更した以外は、合成例１と同様の操作を行い、帯電防止性共重合体（Ａ−６）のエタノール溶液（固形分３０重量％）を得た。
(Synthesis Example 6)
In the alkylene oxide addition step of Synthesis Example 1, 511.7 parts of stearyl alcohol was used instead of dodecanol (30 moles of ethylene oxide was used relative to stearyl alcohol), and the amount of toluene was changed to 752.9 parts. In the esterification step, the same procedure as in Synthesis Example 1 was performed except that the amount of polyethylene oxide-added alcohol was 317.7 parts, and the compound (a-2-4) having 30 ethylene oxide groups and an octadecyl group was obtained. Obtained. Further, in the copolymerization process, the same operation as in Synthesis Example 1 was conducted except that the compound (a-2-1) was changed to the compound (a-2-4) and methyl methacrylate was changed to cyclohexyl methacrylate. An ethanol solution (solid content: 30% by weight) of copolymer (A-6) was obtained.
（合成例７）
合成例１の共重合過程において、メチルメタクリレートをベンジルメタクリレートへ変更した以外は、合成例１と同様の操作を行い、帯電防止性共重合体（Ａ−７）のエタノール溶液（固形分３０重量％）を得た。
(Synthesis Example 7)
The same operation as in Synthesis Example 1 was performed except that methyl methacrylate was changed to benzyl methacrylate in the copolymerization process of Synthesis Example 1, and an antistatic copolymer (A-7) ethanol solution (solid content: 30% by weight) )
（合成例８）
合成例１の共重合過程において、化合物（ａ−２−１）を合成例２で得られた化合物（ａ−２−２）に、メチルメタクリレートをベンジルメタクリレートへ変更した以外は、合成例１と同様の操作を行い、帯電防止性共重合体（Ａ−８）のエタノール溶液（固形分３０重量％）を得た。
(Synthesis Example 8)
In the copolymerization process of Synthesis Example 1, except that Compound (a-2-1) was changed to Compound (a-2-2) obtained in Synthesis Example 2 and methyl methacrylate was changed to benzyl methacrylate, Synthesis Example 1 and The same operation was performed to obtain an ethanol solution (solid content: 30% by weight) of the antistatic copolymer (A-8).
（実施例１）
ペンタエリスリトールトリアクリレートヘキサメチレンジイソシアネートウレタンプレポリマー（共栄社化学（株）製：ＵＡ−３０６Ｈ）５０重量部、ジペンタエリスリトールヘキサアクリレート（日本化薬（株）製：ＫＡＹＡＲＡＤ ＤＰＨＡ）４０重量部、ペンタエリスリトールテトラアクリレート（日本化薬（株）製：ＫＡＹＡＲＡＤ ＰＥＴ３０）１０重量部に、合成例１で合成した帯電防止性共重合体のエタノール溶液を、帯電防止性共重合体が固形分で５重量部となるように加え、さらに光重合開始剤としてイルガキュアー１８４（チバスペシャリティケミカルズ製）５重量部添加してなる組成物を、酢酸メチル、エタノール及び１−メトキシ−２−プロパノールで希釈し、溶媒組成が酢酸メチル／エタノール／１−メトキシ−２−プロパノール＝８０／１５／５（重量比）の溶剤を５０重量％含有する帯電防止組成物を調製した。（溶剤組成中のエタノールの一部は帯電防止性共重合体溶液由来で混入した。）
Example 1
50 parts by weight of pentaerythritol triacrylate hexamethylene diisocyanate urethane prepolymer (manufactured by Kyoeisha Chemical Co., Ltd .: UA-306H), 40 parts by weight of dipentaerythritol hexaacrylate (manufactured by Nippon Kayaku Co., Ltd .: KAYARAD DPHA), pentaerythritol tetra An ethanol solution of the antistatic copolymer synthesized in Synthesis Example 1 is added to 10 parts by weight of acrylate (manufactured by Nippon Kayaku Co., Ltd .: KAYARAD PET30), and the antistatic copolymer is 5 parts by weight in solid content. In addition, a composition obtained by adding 5 parts by weight of Irgacure 184 (manufactured by Ciba Specialty Chemicals) as a photopolymerization initiator was diluted with methyl acetate, ethanol and 1-methoxy-2-propanol, and the solvent composition was acetic acid. Methyl / ethanol / 1-methoxy-2 The solvent propanol = 80/15/5 (weight ratio) was prepared antistatic composition containing 50 wt%. (A part of ethanol in the solvent composition was mixed from the antistatic copolymer solution.)
この組成物を厚さ約８０μｍのトリアセチルセルロースフィルム（富士写真フィルム社製）、あるいは表面易接着処理ポリエチレンテレフタレートフィルム（東洋紡製：コスモシャインＡ４１００）上にバーコーターを用いて塗布し、熱風オーブンで溶剤を除去した後、出力８０ｗ／ｃｍの高圧水銀ランプで紫外線を照射し、塗布層を硬化させ、膜厚６μｍの帯電防止ハードコートフィルムを得た。 This composition was applied onto a triacetylcellulose film (Fuji Photo Film Co., Ltd.) having a thickness of about 80 μm or a surface-adhesion-treated polyethylene terephthalate film (Toyobo Cosmo Shine A4100) using a bar coater and heated in a hot air oven. After removing the solvent, ultraviolet rays were irradiated with a high-pressure mercury lamp with an output of 80 w / cm to cure the coating layer, and an antistatic hard coat film with a film thickness of 6 μm was obtained.
得られた帯電防止ハードコート層を有するフィルムについて次の評価方法により評価を行い、結果を表１に示した。 The film having the obtained antistatic hard coat layer was evaluated by the following evaluation method, and the results are shown in Table 1.
（１）塗膜の外観：帯電防止層の外観を目視にて評価した。評価基準は以下のように行った。
○：凝集物の発生、ゆず肌や白化がない。
×：凝集物の発生、ゆず肌や白化が見られる。
(1) Appearance of coating film: The appearance of the antistatic layer was visually evaluated. The evaluation criteria were as follows.
◯: There is no generation of aggregates, no yuzu skin or whitening.
X: Occurrence of aggregates, yuzu skin and whitening are observed.
（２）表面抵抗率：２５℃、相対湿度４０％雰囲気下で２４時間放置した後、ＴＯＡ社製表面抵抗率計（ＳＭ−８０００ｓｅｒｉｅｓ ＳＭＥ−８３１０）を用い、温度２５℃、相対湿度４０％の条件で、印加電圧１００Ｖをかけて１分後の表面抵抗率（Ω／□）を測定した。評価基準は以下のように行った。
◎：１．０Ｅ+１０Ω／□以下
○：１．０Ｅ＋１０Ω／□〜１．０Ｅ＋１１Ω／□未満
△：１．０Ｅ＋１１Ω／□〜１．０Ｅ＋１２Ω／□未満
×：１．０Ｅ＋１２Ω／□以上
(2) Surface resistivity: 25 ° C., left in an atmosphere with a relative humidity of 40% for 24 hours, and then a surface resistivity meter (SM-8000 series SME-8310) manufactured by TOA was used at a temperature of 25 ° C. and a relative humidity of 40%. Under the conditions, the surface resistivity (Ω / □) after 1 minute was measured by applying an applied voltage of 100V. The evaluation criteria were as follows.
◎: 1.0E + 10Ω / □ or less ○: 1.0E + 10Ω / □ to less than 1.0E + 11Ω / □ Δ: 1.0E + 11Ω / □ to less than 1.0E + 12Ω / □ ×: 1.0E + 12Ω / □ or more
（３）ヘイズ値・全光線透過率：日本電色社製Ｈａｚｅ Ｍｅｔｅｒ ＮＤＨ２０００でヘイズ値（Ｈｚ）および全光線透過率（ＴＴ）を測定した。 (3) Haze value / total light transmittance: The haze value (Hz) and the total light transmittance (TT) were measured with Haze Meter NDH2000 manufactured by Nippon Denshoku.
（４）耐擦傷性：＃００００のスチールウールを装着した１平方センチメートルの角形パッドを試料表面上に置き、荷重５００ｇで１０回往復させた後、外観を目視で評価し、傷の本数を測定した (4) Scratch resistance: A square pad of 1 cm 2, fitted with # 0000 steel wool, was placed on the sample surface, reciprocated 10 times with a load of 500 g, the appearance was visually evaluated, and the number of scratches was measured.
（５）鉛筆硬度：ＪＩＳ Ｋ５４００に従って評価した。 (5) Pencil hardness: evaluated according to JIS K5400.
（６）密着性試験：ＪＩＳ Ｋ５４００碁盤目剥離法に準じて、帯電防止層にカッターナイフで１ミリ間隔の碁盤目状の切り傷を１００ますつけ、セロハンテープ（ニチバン社製）を貼り付け、一気に引きはがした後、剥離しないで残った帯電防止層のます目を数え、ｎ／１００で表した。例）１００／１００：剥離なし。０／１００：全て剥離。 (6) Adhesion test: In accordance with JIS K5400 cross-cutting method, apply 100 mm grid cuts with a cutter knife to the antistatic layer and apply cellophane tape (made by Nichiban Co., Ltd.) at once. After peeling, the antistatic layer remaining without peeling was counted and expressed in n / 100. Example) 100/100: No peeling. 0/100: All peeled.
（７）高温・高湿度耐久試験後の表面抵抗率：ガラス板に帯電防止ハードコートフィルムの裏面（帯電防止層とは反対側、即ちトリアセチルセルロースフィルム面、あるいはポリエチレンテレフタレートフィルム面）を粘着テープで貼り付けた試料を、８５℃、８５％ＲＨの環境下に１００時間放置した後、前記（２）同様の方法で表面抵抗率を測定し評価した。 (7) Surface resistivity after high-temperature / high-humidity durability test: Adhesive tape on the back side of the antistatic hard coat film on the glass plate (the side opposite to the antistatic layer, that is, the triacetyl cellulose film side or the polyethylene terephthalate film side) The sample pasted in (1) was left in an environment of 85 ° C. and 85% RH for 100 hours, and then the surface resistivity was measured and evaluated in the same manner as in (2) above.
（８）耐温水性試験後の表面抵抗率：上記（７）と同様の試料を８５℃の水中で２０分間浸漬後、前記（２）同様の方法で、表面抵抗率を測定し評価した。 (8) Surface resistivity after hot water resistance test: A sample similar to the above (7) was immersed in water at 85 ° C. for 20 minutes, and then the surface resistivity was measured and evaluated by the same method as in (2) above.
（実施例２〜１２、比較例１〜３）
使用する帯電防止性共重合体を、表１および表２に示すように合成例１〜８で得られた帯電防止性共重合体（Ａ−１〜８）エタノール溶液とし、溶剤組成を表１および表２に示す割合とした以外は実施例１と同様にして帯電防止組成物を得た。さらに同様の評価を行い、その結果を表１および表２に示した。
(Examples 2 to 12, Comparative Examples 1 to 3)
As shown in Tables 1 and 2, the antistatic copolymer to be used is an antistatic copolymer (A-1 to 8) ethanol solution obtained in Synthesis Examples 1 to 8, and the solvent composition is shown in Table 1. An antistatic composition was obtained in the same manner as in Example 1 except that the ratios shown in Table 2 were used. Further, the same evaluation was performed, and the results are shown in Tables 1 and 2.
（実施例１３）
合成例２で得られた帯電防止性共重合体（Ａ−２）のエタノール溶液をヘキサン中に投入し、析出物を濾別後、乾燥することで帯電防止性共重合体（Ａ−２）の固体を得た。得られた帯電防止性共重合体（Ａ−２）の固体５重量部に、エタノール１０重量部、酢酸エチル８５重量部、メチルエチルケトン５重量部を加え、さらにペンタエリスリトールトリアクリレートヘキサメチレンジイソシアネートウレタンプレポリマー（共栄社化学（株）製：ＵＡ−３０６Ｈ）５０重量部、ジペンタエリスリトールヘキサアクリレート（日本化薬（株）製：ＫＡＹＡＲＡＤ ＤＰＨＡ）４０重量部、ペンタエリスリトールテトラアクリレート（日本化薬（株）製：ＫＡＹＡＲＡＤ ＰＥＴ３０）１０重量部、光重合開始剤としてイルガキュアー１８４（チバスペシャリティケミカルズ製）５重量部を添加し、溶媒組成が酢酸メチル／エタノール／メチルエチルケトン＝８５／１０／５（重量比）である固形分５２重量％の帯電防止組成物を調製した。さらに実施例１と同様の評価を行い、その結果を表１に示した。
(Example 13)
The antistatic copolymer (A-2) obtained in Synthesis Example 2 is put into hexane, and the precipitate is filtered off and dried. A solid was obtained. 10 parts by weight of ethanol, 85 parts by weight of ethyl acetate and 5 parts by weight of methyl ethyl ketone are added to 5 parts by weight of the solid of the obtained antistatic copolymer (A-2), and further pentaerythritol triacrylate hexamethylene diisocyanate urethane prepolymer. (Kyoeisha Chemical Co., Ltd .: UA-306H) 50 parts by weight, dipentaerythritol hexaacrylate (Nippon Kayaku Co., Ltd .: KAYARAD DPHA) 40 parts by weight, pentaerythritol tetraacrylate (Nippon Kayaku Co., Ltd .: KAYARAD PET30) 10 parts by weight, Irgacure 184 (manufactured by Ciba Specialty Chemicals) as a photopolymerization initiator is added, and the solvent composition is methyl acetate / ethanol / methyl ethyl ketone = 85/10/5 (weight ratio) 52% by weight antistatic The composition was prepared. Further, the same evaluation as in Example 1 was performed, and the results are shown in Table 1.
表１、２中の略号は以下の通り。
溶剤（Ｄ）
ＥｔＯＨ：エチルアルコール
ＰＧＭ：１−メトキシ−２−プロパノール
ＭＥＫ：メチルエチルケトン
ＭｅＡｃ：酢酸メチル
ＥｔＡｃ：酢酸エチル
ｎ−ＰｒＡｃ：酢酸−ｎ−プロピル
１，３−ＤＯＸ：１，３−ジオキソラン
Abbreviations in Tables 1 and 2 are as follows.
Solvent (D)
EtOH: ethyl alcohol PGM: 1-methoxy-2-propanol MEK: methyl ethyl ketone MeAc: methyl acetate EtAc: ethyl acetate n-PrAc: acetic acid-n-propyl 1,3-DOX: 1,3-dioxolane
表１の結果より、比較例１では、溶剤（Ｄ）がアルコール系溶剤（ｄ−１）のみのため、ゆず肌、耐温水性試験後の帯電防止性の低下などの不具合が生じており、さらに、トリアセチルセルロース支持体フィルムでは、密着性も低い結果となった。
比較例２では、溶剤（Ｄ）がアルコール系溶剤（ｄ−１）とケトン系溶剤のため、トリアセチルセルロース支持体フィルムにおいて、耐擦傷性が低く、耐温水試験後の帯電防止性が低下する結果となった。
また、比較例３では、溶剤（Ｄ）がアルコール系溶剤（ｄ−１）と炭素数６のアセテート系溶剤のため、帯電防止性が低い結果となった。
これに対して、実施例１〜１２はいずれも、溶剤（Ｄ）にアルコール系溶剤（ｄ−１）と炭素数３〜５のアセテート系溶剤（ｄ−２）を使用しており、透明性・帯電防止性・硬度のバランスの良い膜が得られた。実施例４〜６より分かるように、溶剤（Ｄ）には、アルコール系溶剤（ｄ−１）及び炭素数３〜５のアセテート系溶剤（ｄ−２）と共に、エーテル、ケトン、等の溶剤を用いることができる。また、実施例４および６と実施例５の比較から、溶剤（Ｄ）中の炭素数３〜５のアセテート系溶剤（ｄ−２）は５５重量％以上が好ましい事が分かる。
From the results of Table 1, in Comparative Example 1, since the solvent (D) is only the alcohol solvent (d-1), defects such as deterioration of the antistatic property after the yuzu skin and the hot water resistance test have occurred, Furthermore, the triacetyl cellulose support film also resulted in low adhesion.
In Comparative Example 2, since the solvent (D) is an alcohol solvent (d-1) and a ketone solvent, the triacetyl cellulose support film has low scratch resistance and lowers antistatic properties after a hot water resistance test. As a result.
In Comparative Example 3, since the solvent (D) was an alcohol solvent (d-1) and an acetate solvent having 6 carbon atoms, the antistatic property was low.
On the other hand, all Examples 1-12 use the alcohol solvent (d-1) and the C3-C5 acetate solvent (d-2) for the solvent (D), and are transparent. A film with a good balance of antistatic properties and hardness was obtained. As can be seen from Examples 4 to 6, the solvent (D) includes an alcohol solvent (d-1) and an acetate solvent (d-2) having 3 to 5 carbon atoms, and a solvent such as ether, ketone or the like. Can be used. Further, from comparison between Examples 4 and 6 and Example 5, it is found that the content of the acetate solvent (d-2) having 3 to 5 carbon atoms in the solvent (D) is preferably 55% by weight or more.
Claims (5)
前記帯電防止性共重合体（Ａ）が、下記一般式（１）で表される４級アンモニウム塩基を有する化合物（ａ−１）及び下記一般式（２）で表されるアルキレンオキサイド鎖を有する化合物（ａ−２）を必須の構成成分とする共重合体であり、
前記溶剤（Ｄ）が、アルコール系溶剤（ｄ−１）及び炭素数３〜５のアセテート系溶剤（ｄ−２）を含むことを特徴とする帯電防止用コーティング組成物。
一般式（１）
ＣＨ２＝Ｃ（Ｒ１）ＣＯＺ（ＣＨ２）ｋＮ＋（Ｒ２）（Ｒ３）Ｒ４・Ｘ−
（式中、Ｒ１はＨまたはＣＨ３ 、Ｒ２〜Ｒ４はＨまたは炭素数が１〜９の炭化水素基、Ｚは酸素原子またはＮＨ基、ｋは１〜１０の整数、Ｘ−は１価のアニオンを表す。）
一般式（２）
ＣＨ２＝Ｃ（Ｒ５）ＣＯＯ（ＡＯ）ｎＲ６
（式中、Ｒ５はＨまたはＣＨ３、Ｒ６は水素または炭素数が１〜２２の炭化水素基、ｎは２〜２００の整数、Ａは炭素数が２〜４のアルキレン基を表す。） An antistatic coating composition comprising an antistatic copolymer (A), a compound (B) having three or more ethylenically unsaturated groups, a photopolymerization initiator (C) and a solvent (D),
The antistatic copolymer (A) has a compound (a-1) having a quaternary ammonium base represented by the following general formula (1) and an alkylene oxide chain represented by the following general formula (2). A copolymer comprising the compound (a-2) as an essential constituent,
The antistatic coating composition, wherein the solvent (D) contains an alcohol solvent (d-1) and an acetate solvent (d-2) having 3 to 5 carbon atoms.
General formula (1)
CH 2 = C (R 1) COZ (CH 2) k N + (R 2) (R 3) R 4 · X -
(In the formula, R 1 is H or CH 3 , R 2 to R 4 are H or a hydrocarbon group having 1 to 9 carbon atoms, Z is an oxygen atom or NH group, k is an integer of 1 to 10, and X − is Represents a monovalent anion.)
General formula (2)
CH 2 = C (R 5) COO (AO) n R 6
(In the formula, R 5 represents H or CH 3 , R 6 represents hydrogen or a hydrocarbon group having 1 to 22 carbon atoms, n represents an integer of 2 to 200, and A represents an alkylene group having 2 to 4 carbon atoms. )
（Ａ）〜（Ｄ）の合計１００重量％中に、溶剤（Ｄ）を３０〜８０重量％含有し、
前記溶剤（Ｄ）の１００重量％中、アルコール系溶剤（ｄ−１）の含有量が５〜２５重量％、炭素数３〜５のアセテート系溶剤（ｄ−２）の含有量が５５〜９０重量％であることを特徴とする請求項１又は２記載の帯電防止用コーティング組成物。 1 to 20 parts by weight of the antistatic copolymer (A) and 0.1 to 0.1% of the photopolymerization initiator (C) with respect to 100 parts by weight of the compound (B) having three or more ethylenically unsaturated groups. Containing 20 parts by weight,
In a total of 100% by weight of (A) to (D), 30 to 80% by weight of the solvent (D) is contained,
In 100% by weight of the solvent (D), the content of the alcohol solvent (d-1) is 5 to 25% by weight, and the content of the acetate solvent (d-2) having 3 to 5 carbon atoms is 55 to 90%. The antistatic coating composition according to claim 1 or 2, wherein the coating composition is in wt%.
２−メトキシエタノール、２−エトキシエタノール、２−プロポキシエタノール、２−ブトキシエタノール、
１−メトキシ−２−プロパノール、３−メトキシ−１−プロパノール、１−エトキシ−２−プロノール、２−エトキシ−１−プロノール及び３−エトキシ−１−プロノールからなる群より選ばれることを特徴とする請求項１〜３いずれか記載の帯電防止用コーティング組成物。 Alcohol solvent (d-1) is methyl alcohol, ethyl alcohol, isopropyl alcohol, n-butyl alcohol, isobutyl alcohol, cyclohexyl alcohol,
2-methoxyethanol, 2-ethoxyethanol, 2-propoxyethanol, 2-butoxyethanol,
It is selected from the group consisting of 1-methoxy-2-propanol, 3-methoxy-1-propanol, 1-ethoxy-2-pronol, 2-ethoxy-1-pronol and 3-ethoxy-1-pronol The antistatic coating composition according to any one of claims 1 to 3.