JP2011161701A - Nonskid wooden floor covering for pet - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide wooden flooring which is a coated wooden article for breeding and provided with light weight as well as a finish really close to solid wood in feel, appearance and texture, which is a floor covering using a plate like base body of 50-200 mm width, and which is a narrow planar strip-like wooden flooring with a nonskid coating on the surface. <P>SOLUTION: This article is a wooden flooring for a house or the like, with nonskid coating applied to the surface. As wooden flooring, it is selected from wood, plywood, and MDF, and is 2-5 mm thick, After undercoating is applied to the surface of the wooden strip article of the narrow planar structure for a pet, the wooden base material of the strip article is irradiated with ultraviolet rays on the film and applied with a nonskid effect. Having a sheet surface with a fabric or nonwoven fabric lining. the floor covering has designability in the planar base body. <P>COPYRIGHT: (C)2011,JPO&INPIT

Description

The present invention is obtained by performing a non-slip treatment on a surface-feeling coated article having a good quality feeling for pets, particularly a woodware base material, obtained by pre-treatment painting of wooden products in indoor pet breeding. A non-slip processed wooden rug for pets.

  2. Description of the Related Art Conventionally, non-slip processed wooden pet floor materials have been applied to, for example, indoor floors, stairs, pet goods, and the like from the viewpoint that a wooden feel can be imparted to articles. However, when an excellent wooden material is used for pet breeding, slip prevention is not sufficient, and it is not strong against mechanical impacts, which is a great limitation. Anti-slip on wooden products, but not by painting, but by changing the grain and type of wood.

It becomes a limited product depending on the choice of materials and wood types. As described above, it is desired that the pet breeding floor has a favorable touch feeling. In particular, a technique has been proposed in which a floor plate or a staircase is prevented from slipping (see Patent Documents 2 to 4).

  On the other hand, from the viewpoints of moldability and impact resistance, resins such as polymethyl methacrylate and polycarbonate are used for wooden products, but there is a problem in that a high-class feeling cannot be expressed and scratch resistance is also a problem. One of the methods of painting wood products instead of resin is a finishing method for touching the painted surface.

    In general, wood is good to the touch, and surface-treated paints have good matte properties and inorganic or organic extender pigments are used as a component for expressing touch. In addition, examples of extender pigments that have a good inorganic feel and a matte appearance include amorphous silica powder and calcium carbonate powder. Examples of organic pigments that have an organic feel and are suitable for matting include organic powders such as polyethylene and polycarbonate.

Further, spherical acrylic resin particles, urethane resin particles, and the like are also used as organic powders for the purpose of matting, but these are widely used for paints having a pattern-like feel. There is disclosed a technique for applying a satin pattern decoration by electrostatic coating to a resin composition obtained by blending a spherical solid silicone resin of 5 to 100 μm on a wooden surface. (See Patent Document 1)

However, with a simple coating composition according to the above technique, it has been extremely difficult to obtain a matte coating composition on a wood surface that satisfies all of the touch feeling, appearance, and texture.
For example, when organic powders such as polyethylene are used as extender pigments, it is difficult to obtain a touch and texture because the filler itself is soft, and silica powder was used as a prescription to solve this point. A paint that has a good feel and can be matted is conceivable, but in this case the feel and appearance are close to the finish, but are easily scratched by external mechanical shocks and scratches, and the texture is extremely low. There was a problem that it was a high-quality finish.

Japanese Patent Laid-Open No. 10-329840 JP-A-11-303350 Japanese Patent Laid-Open No. 10-227119 JP 2001-123627 A

  Since the floor surface of pet indoor flooring has increased rapidly, it is a carpet type new wooden flooring that does not impair the appearance and functionality of the flooring by placing it on the floor surface of the flooring. The purpose of the development of a flat plate-like substrate having a width of 50 mm to 200 mm is a wooden floor material that has been subjected to anti-slip coating.

The wooden flooring of this wooden flooring, the wooden flooring having a non-slip coating on the surface, is intended to have a form in which a flat plate-like substrate having a width of 50 mm to 200 mm has an improved wood carpet. did.

A wooden flooring made of wooden flooring, in which a plurality of vertically long wooden flat plates are placed adjacent to each other in parallel, and the surface of the flat plates is cut to the required size. The flooring has a structure in which flat plate-like substrates having a width of 50 mm to 200 mm are bonded together. Due to the moderate weight of this flat plate, it is difficult to slip even when laid on the floor of the flooring, and when not in use, the entire rug can be rolled up compactly if it is rolled up with the back side of the sheet inside. Is to have it.

The wooden flooring of this new wooden flooring, which has a non-slip coating on the surface, is developing a flat plate substrate having a width of 50 mm to 200 mm. It was a wooden flooring of wooden flooring that was cut into a long and thin shape.

The wooden flooring that is coated with anti-slip coating on the surface is made by laminating a flat plate-like substrate having a width of 50 mm to 200 mm, and is a wooden flooring of this wooden flooring, and is coated with anti-slip coating on the surface. In the case of a flat plate base having a width of 50 mm to 200 mm, the wooden flooring is mainly formed along the longitudinal direction of the flat plate on both ends in the width direction of each flat plate.

    Further, the present invention is a wooden flooring of wooden flooring, and the wooden flooring which is coated with anti-slip on the surface prevents the original texture and texture of a flat plate-like substrate having a width of 50 mm to 200 mm from being damaged. This is a new carpet flooring wooden flooring that has been laid on the flooring of the flooring, etc., without changing its functionality and appearance. It is an object of the present invention to provide a rug that prevents the occurrence of ticks only.

  Furthermore, it is a wooden flooring made of wooden flooring that is excellent in water resistance, stain resistance and hygiene resistance, and that can achieve the above-mentioned purpose. A rug using a flat plate-like substrate of 50 mm to 200 mm, and a wooden flooring of a wooden flooring used for the rug, and the wooden flooring coated with a non-slip coating on the surface has a flat plate-like substrate structure with a width of 50 mm to 200 mm The object of the present invention is to provide a rug treated sheet, and further, the interior of the rug and the lining.

The object of the present invention has been made by paying attention to such conventional problems, and is lightweight as a pet rug, and has a good feeling of limbs on furniture, the floor of a house, wooden furniture, It is to provide an article having a finish that is very close to the floor in appearance and texture, such as a floor. In particular, by applying such a coating treatment to the surface of a wooden product, it is more comfortable to touch and durable. It is to provide painted rugs of high surface touch wooden products.

It is a wooden flooring of wooden flooring in a house, etc., and the surface of the wooden flooring is coated with anti-slip coating, and the lining is made of non-slip or non-woven fabric with anti-slip effect on the lining, An anti-slip wooden pet rug having a structure in which a plurality of elongated flat wooden plates are joined adjacent to the surface of a sheet.

A wooden flooring of a wooden flooring such as a house, the wooden flooring having a non-slip coating on the surface, a flat plate-like substrate having a width of 50 mm to 200 mm, a surface joined to each of the flat plate-like substrates, and the above A non-woven fabric or a woven fabric sheet having a non-slip effect on the lining, and has a thickness of 0.1 mm to 3 mm and a non-slip effect on the back surface.

The wooden flooring of a wooden flooring of a house or the like, and the wooden flooring that is anti-slip coated on the surface is selected from wood, plywood, and MDF, and has a thickness of 2 mm to 5 mm, A plurality of flat plate-like substrates having a width of 50 mm to 200 mm and a length of 500 mm to 2000 mm are pasted together.

A woven sheet with a non-slip effect on the lining is a non-slip wooden pet rug with a non-slip finish on the back surface.

The wooden flooring is prepared by pre-treating the surface, and after applying a binder having an acrylic group to the pre-treated wooden surface in a thickness of 3 to 10 microns, the average particle size is 1.5 to 12 microns. A surface-sensitive coating composition comprising 10 to 60% by weight of the silicone resin particles (a) and 90 to 40% by weight of a binder (b) having an acrylic group is applied to the surface of the treated substrate with a thickness of 5 to 15 microns. Formed into a film thickness and cured.

Pretreatment of the surface of the wooden flooring is a non-slip process that uses a pretreatment technique by an ester-based oligomer containing a hydroxyl group and a polyfunctional isocyanate-based oligomer impregnation coating method in order to increase the bondability between the wood surface and the resin component. The wooden pet flooring.

A surface-tactile paint in which a binder having an acrylic group is applied in advance to a thickness of 3 to 10 microns on a painted surface of a pretreated wood product, and then the viscosity of the paint is 8 to 11 seconds with a viscometer of food cup # 4 The paint of the composition has the appearance, texture and feel by the spray gun applicator.

The binder of the surface tactile paint composition applied to the wooden flooring is a compound having a (meth) acrylic group mainly composed of (meth) acrylic acid; methyl (meth) acrylate and butyl (meth) acrylate.
The surface-tactile-sensitive coating composition is cured by crosslinking while maintaining the surface temperature of the wood product in the range of 20 ° C. to 40 ° C. by irradiating ultraviolet rays with an integrated energy of 500 mj / cm 2 using a halogen lamp type irradiation device. Non-slip wooden pet flooring.

After pre-treating the surface of the wood product and applying a binder having an acrylic group to the thickness of 3 to 10 microns in advance on the pre-treated wood surface, the silicone resin particles (with an average particle size of 1.5 to 12 microns) A surface touch coating composition comprising 10 to 60% by weight of a) and a binder having an acrylic group (b) 90 to 40% by weight is formed on the surface of the treated substrate to a coating thickness of 5 to 15 microns. It is a rug of surface-feeling paint for wooden products that forms and hardens.

In the present invention, the surface pretreatment of the wood product is pretreated with a coating of an ester oligomer containing a hydroxyl group and a polyfunctional isocyanate oligomer in order to increase the bondability between the wood interface and the resin component interface.

After applying a binder having an acrylic group to a thickness of 3 to 10 microns on the painted surface of a wooden product, the appearance and texture of the paint whose viscosity is 8 to 11 seconds with a food cup # 4 viscometer with a spray gun And has a tactile sensation.

The surface-tactile paint composition for wood products contains 0.01 to 2.0% by weight of pigment.
The binder in the surface tactile paint composition of the wood product is made of a compound having a (meth) acryl group. It is a coated rug in which the surface touch-sensitive coating composition is cured by crosslinking while maintaining the surface temperature of the wood product in the range of 20 ° C. to 40 ° C. by irradiation with ultraviolet rays.

The present invention relates to a surface touch-sensitive paint composition having an average particle size of 1.5 to 12 microns, comprising 10 to 60% by weight of silicone resin particles (a) and 90 to 40% by weight of a binder (b) having an acrylic group. This is a surface-feeling paint rug for wooden products in which an object is coated with an applicator so as to form a 5-15 micron thick coating on the surface of a wooden substrate.

As the silicone resin particles (a), Tospearl 130 (spherical; average particle diameter 3.0 μm), Tospearl 145A (spherical; average particle diameter 4.5 μm), Tospearl 2000B (spherical; average particle) manufactured by GE Toshiba Silicone Co., Ltd. Examples include diameter 6.0 μm) and Tospearl 3120 (GE Toshiba Silicone Co., Ltd.).

After the primer is applied to the painted surface of the wood product, the paint whose viscosity is 8 to 11 seconds with a viscometer of food cup # 4 has an appearance, texture and touch by a spray gun.
It is preferable to contain a pigment component in an amount of 0.01 to 2.0% by weight in the surface-tactile paint composition for wood products. The surface touch-sensitive paint rug of a wooden product, wherein the binder in the surface-sensitive coating composition of the wooden product is made of a compound having a (meth) acrylic group.

As the compound (m) having a (meth) acrylic group, (meth) acrylic acid; alkyl such as methyl (meth) acrylate, butyl (meth) acrylate, stearyl (meth) acrylate (C1-18) (meth) An acrylate, 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, etc. can be mentioned.
These can be used alone or in combination of two or more.

This is a surface-feeling paint rug for wooden products in which the surface-friendly coating composition is crosslinked and cured while maintaining the surface temperature of the wooden products in the range of 20 ° C. to 40 ° C. by irradiation with ultraviolet rays.
As the binder used in the present invention, a binder used for an acrylic curable coating containing a binder that is cured by irradiation with ultraviolet active energy rays, more preferably a UV curable coating. It is.

  Examples of compounds that generate active chemical species (sensitizers) upon irradiation with active energy rays include acetophenones such as acetophenone, 2,2-diethoxyacetophenone, p-dimethylacetophenone, and benzophenone.

These compounds may be used individually by 1 type, and can also be used in combination of 2 or more type. In addition, a compound that does not act as a photopolymerization initiator per se, but that can increase the ability of the photopolymerization initiator by using it in combination with the above-mentioned compound can also be added.

  10 to 60% by weight of silicone resin particles (a) having an average particle diameter of 1.5 to 12 microns and a pencil hardness F or higher, and a binder having a coating film hardness of only the binder (b) having a pencil hardness F or higher. (B) It has been found that the above-mentioned problems can be solved by coating a coating composition comprising 90 to 40% by weight on the surface of an article such as a wooden product, and the present invention has been completed.

In the present invention, 10 to 60% by weight of silicone resin particles having an average particle diameter of 1.5 to 12 microns and a pencil hardness F or more, and a binder 90 to which the hardness of a coating film of only a binder is a pencil hardness F or more is used. Provided is a coated wooden article obtained by coating a surface of a wooden substrate with a coating composition comprising 40% by weight.
Moreover, this invention improves adhesiveness with the said coating material by pre-processing a woody and a coating-film interface.

Furthermore, the functional coating composition provides a coated wooden article having a good touch and containing 0.01 to 2.0% by weight of a pigment. Provided is a functional coated wooden article which is a binder in which a binder in a functional coating composition is composed of a compound having a (meth) acrylic group and an active chemical species generating compound and is cured by generation of active chemical species.

Provided is a functionally coated wooden article obtained by crosslinking and curing a coating composition by ultraviolet irradiation. Provided is a coated wooden article in which the silicone resin particles in the functional coating composition have a pencil hardness of F or more when only the silicone resin particles are formed into a film.

In pet breeding, the wooden flooring of this wooden flooring, which is coated with a non-slip coating on the surface, can be used by laying a flat plate-like substrate with a width of 50 mm to 200 mm in the room. The wooden flooring of the wooden flooring arranged side by side, and the wooden flooring whose surface is coated with a non-slip coating is made of wooden flooring even if the flat plate-like base members having a width of 50 mm to 200 mm rub against each other. A wooden flooring which is a flooring and has a non-slip coating on the surface can prevent a flat plate-like substrate having a width of 50 mm to 200 mm from being torn.

According to the present invention, it is possible to obtain a wooden painted article having a coating film having a touch and a texture that is very close in appearance and touch to a wooden product using solid wood in pet breeding.
In particular, when painting a light, high-strength wooden material for pet breeding, it is possible to impart a texture that is very close to that of a solid wooden product, with extremely low damage caused by impact, and excellent durability. And a wooden coated article having a coating film having an appearance.

Further, since the beads made of silicon resin protrude from the surface of the coating film, the surface is not only a touch feeling but also has a high level of water breakage. Therefore, water, urine, coffee, even though a flat plate substrate with a width of 50 mm to 200 mm is bonded on the back with non-woven fabric or woven fabric and the joints of each plate are in contact but not integrated. Exhibits high water resistance to liquid spilled on the surface of the rug.

The perspective view of the product in this invention Plan view (A) and sectional view (B) of the product in the present invention Cross-sectional schematic diagram of the coating surface Product specification state diagram in the present invention

Wooden rugs with touch-sensitive paint according to the present invention not only improve and stabilize the walking and living habits of pets kept indoors, but also have a non-slip surface to help prevent the elderly from falling or flooring. The feeling of bare feet is very good. Therefore, it is necessary to deal with a wide size to spread the entire living room.

This specific example is merely representative and is not particularly limited thereto.

Hereinafter, the present invention will be described by way of examples, but will be described in more detail based on the examples shown in the drawings. This was done to stop the color on the surface and to prevent warping caused by painting on the back.

A material having a size of 3 × 6 (900 × 1800) having a 3 mm thick water-resistant MDF and a 0.3 mm plate attached to the surface was used. After coloring the surface plate with a solvent-based pigment to give a predetermined color, the back, front, and the whole are coated with a film thickness of about 20 microns with a non-yellowing urethane sanding, and then the pretreatment is performed. It was. This was done to stop the color on the surface and to prevent warping caused by painting on the back.
After the paint dried, the whole was lightly polished with # 240 paper and cut to a length of 1800 mm with a width of 70 mm. For the 900 × 900 mm size, 1800 mm was cut in half to 900 mm and then cut to a width of 70 mm.

After removing the polishing debris by air blow, the entire coating including the forehead was applied twice with a non-yellowing urethane sanding with a film thickness of about 20 microns. After the coated film was dried, it was completely polished with # 600 paper.

Next, after air blow was performed to remove polishing debris, the surface was kept clean, and a touch-sensitive paint was applied to the surface with a thickness of 10 to 15 microns. This coating film was solidified and dried by UV irradiation to produce a strip-shaped decorative plate whose surface was treated with a touch-sensitive paint.
A strip-like plate finished with a touch-sensitive paint was arranged in a number of sheets close to 900 mm width, and a sheet having a width of 900 × 1800 was attached to the back surface with an adhesive to produce a carpet-like rug.

A material having a size of 3 × 6 (900 × 1800) having a 3 mm thick water-resistant MDF and a 0.3 mm plate attached to the surface was used. After coloring the surface plate with a solvent-based pigment to give a predetermined color, the back, front, and the whole are coated with a film thickness of about 20 microns with a non-yellowing urethane sanding, and then the pretreatment is performed. It was. This was done to stop the color on the surface and to prevent warping caused by painting on the back.

After the paint dried, the whole was lightly polished with # 240 paper and cut to a length of 1800 mm with a width of 70 mm. For the 900 × 900 mm size, 1800 mm was cut in half to 900 mm and then cut to a width of 70 mm.

After removing the polishing debris by air blow, coating was performed twice with a non-yellowing urethane sanding used for the entire time including the front edge at a film thickness of about 20 microns.
After the paint was dried, the entire surface including the edge was completely polished with # 600 paper. Next, after air blow was performed to remove polishing debris, the surface was cleaned to a clean state, and then a touch-sensitive paint was applied to the surface in a thickness of 10 to 15 microns.

This coating film is solidified and dried by UV irradiation, and a strip-like plate whose surface is treated with a touch-sensitive paint is prepared. A strip-like plate finished with a touch-sensitive paint was arranged in a number of sheets close to a width of 900 mm, and a sheet having a width of 900 × 1800 mm was attached to the back surface with an adhesive to produce a carpet-like rug.
This carpet-like rug was used in a living room as shown in FIG. Pet dogs were bred comfortably.

・ Strip wooden board ・ Anti-slip fiber ・ Anti-slip coating ・ Silicone particles ・ Undercoat layer ・ Conventional wooden flooring

Claims (3)

It is a wooden flooring of wooden flooring such as a house, and the surface of the wooden flooring is subjected to anti-slip coating, and the wooden flooring is selected from wood, plywood and MDF, and has a thickness of 2 mm to An anti-slip wooden pet rug, which is 5 mm and is a vertical plate-like substrate. Anti-slip coating on the surface of the wooden flooring is performed by pretreating the elongated strip-shaped planar wooden plate-like surface, and adding 3 to 10 binders having an acrylic group in advance on each of the elongated planar wooden plate-like wooden surfaces that have been pretreated. After coating to a thickness of micron, the average particle diameter is 1.5 to 12 microns, the silicone resin particles (a) are 10 to 60% by weight, and the binder (b) having an acrylic group is 90 to 40% by weight. The non-slip processed wooden pet rug according to claim 1, wherein the surface touch-sensitive coating composition is formed and cured on the surface of the treated substrate so as to have a coating thickness of 5 to 15 microns. . In order to have the appearance, texture and touch, the painted surface of the pre-treated wood product was previously coated with a binder having an acrylic group to a thickness of 3 to 10 microns, and then the viscosity of the paint was measured with a viscometer of Food Cup # 4. The anti-slip material according to claim 1, wherein the surface touch-sensitive paint composition is applied for 8 to 11 seconds using a spray gun applicator, and the coating film is irradiated with ultraviolet rays. Processed wooden pet rug.

Images